JP2012099526A - Separator for aluminum electrolytic capacitor and aluminum electrolytic capacitor - Google Patents

Separator for aluminum electrolytic capacitor and aluminum electrolytic capacitor Download PDF

Info

Publication number
JP2012099526A
JP2012099526A JP2010243466A JP2010243466A JP2012099526A JP 2012099526 A JP2012099526 A JP 2012099526A JP 2010243466 A JP2010243466 A JP 2010243466A JP 2010243466 A JP2010243466 A JP 2010243466A JP 2012099526 A JP2012099526 A JP 2012099526A
Authority
JP
Japan
Prior art keywords
separator
electrolytic capacitor
aluminum electrolytic
aluminum
sound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2010243466A
Other languages
Japanese (ja)
Inventor
Susumu Yonezawa
晋 米沢
Jae-Ho Kim
在虎 金
Naoto Iwano
直人 岩野
Tadahiro Nakamura
忠浩 中村
Hidetaka Kitamura
英貴 北村
Yasuhiko Soga
靖彦 曽我
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Elna Co Ltd
University of Fukui NUC
Original Assignee
Elna Co Ltd
University of Fukui NUC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Elna Co Ltd, University of Fukui NUC filed Critical Elna Co Ltd
Priority to JP2010243466A priority Critical patent/JP2012099526A/en
Publication of JP2012099526A publication Critical patent/JP2012099526A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide an aluminum electrolytic capacitor for audio that reduces change of the sound pressure and change of the sound quality due to oscillation and obtains high-quality reproduction sound.SOLUTION: In an aluminum electrolytic capacitor an anode foil and a cathode foil are wound in a spiral manner through a separator. In the separator, a dielectric powder of titanium dioxide (TiO2) or barium titanate (BaTiO3) that has the particle size of 1 nm to 5 μm and does not dissolve in electrolyte is included in a fiber base material that is a craft pulp fiber or a manila hemp fiber.

Description

本発明は、アルミニウム電解コンデンサ用セパレータおよびアルミニウム電解コンデンサに関し、さらに詳しく言えば、音響機器のコンデンサとして好適なアルミニウム電解コンデンサに関するものである。   The present invention relates to a separator for an aluminum electrolytic capacitor and an aluminum electrolytic capacitor. More specifically, the present invention relates to an aluminum electrolytic capacitor suitable as a capacitor for an acoustic device.

アルミニウム電解コンデンサは、ともにアルミニウム材からなる電極箔としての陽極箔と陰極箔とを、それらの間にセパレータを挟んで渦巻き状に巻回してなるコンデンサ素子に所定の電解液を含浸して有底筒状の金属ケース内に収納し、そのケース開口部を封口ゴム等の封口部材にて封止し、陽極箔と陰極箔とに接続されている一対のタブ端子を封口部材に穿設されている貫通孔を通して外部に引き出してなる構造を備えている。   An aluminum electrolytic capacitor has a bottomed surface by impregnating a predetermined electrolytic solution into a capacitor element formed by winding an anode foil and a cathode foil as electrode foils made of an aluminum material in a spiral shape with a separator between them. It is housed in a cylindrical metal case, the case opening is sealed with a sealing member such as a sealing rubber, and a pair of tab terminals connected to the anode foil and the cathode foil are formed in the sealing member. It has a structure that is pulled out through the through-hole.

この種のアルミニウム電解コンデンサにおいて、セパレータには、通常、クラフトパルプ繊維やマニラ麻繊維等の繊維を抄製してなる繊維基材が用いられている。   In this type of aluminum electrolytic capacitor, a fiber substrate formed by making fibers such as kraft pulp fiber and Manila hemp fiber is usually used for the separator.

アルミニウム電解コンデンサは、多くの電子・電気機器に採用されているが、音響機器の電源平滑コンデンサやカップリング用コンデンサ等に用いられる音響用途の場合、スピーカから発せられる音圧の変化や実装回路基板から伝播される振動によってコンデンサ素子の電極箔のセパレータへの締め付け力が変化し、音響機器の音質が劣化するという問題がある。   Aluminum electrolytic capacitors are used in many electronic and electrical devices, but for acoustic applications used for power supply smoothing capacitors, coupling capacitors, etc. for acoustic devices, changes in sound pressure emitted from speakers and mounted circuit boards Therefore, there is a problem in that the sound quality of the acoustic device is deteriorated by changing the tightening force of the electrode foil of the capacitor element to the separator due to vibration propagated from the sound device.

特に、電解液が含浸されているセパレータは、繊維間の機械的な結合が弱い膨潤状態にあるため、図３に示すアルミニウム電解コンデンサの等価回路において、セパレータ自体の抵抗とセパレータに含浸されている電解液の抵抗とを含むセパレータの抵抗Ｒｅが上記したような音圧の変化や振動等によって変化し、これによってアルミニウム電解コンデンサの電気的定数が変動することがある。   In particular, since the separator impregnated with the electrolyte is in a swollen state where the mechanical bond between the fibers is weak, the resistance of the separator itself and the separator are impregnated in the equivalent circuit of the aluminum electrolytic capacitor shown in FIG. The resistance Re of the separator including the resistance of the electrolytic solution may change due to the change in sound pressure, vibration, or the like as described above, and thereby the electrical constant of the aluminum electrolytic capacitor may fluctuate.

なお、図３の等価回路において、Ｒｆは皮膜抵抗，Ｌはコンデンサの巻き構造やタブ端子によるインダクタンス成分，Ｄは皮膜の極性，Ｃ＋は陽極酸化皮膜の静電容量，Ｃ−は陰極の自然空気酸化皮膜の静電容量である。   In the equivalent circuit of FIG. 3, Rf is the film resistance, L is the inductance structure due to the winding structure of the capacitor and the tab terminal, D is the polarity of the film, C + is the capacitance of the anodized film, and C- is the natural air of the cathode. This is the capacitance of the oxide film.

したがって、このようなセパレータを有するアルミニウム電解コンデンサを音響機器の電源平滑コンデンサやカップリング用コンデンサに使用した場合、音圧の変化や内部振動および外的振動等により、オーディオ信号の劣化や音質の歪みが生じやすくなる。   Therefore, when an aluminum electrolytic capacitor having such a separator is used as a power supply smoothing capacitor or a coupling capacitor for an acoustic device, the audio signal is deteriorated or the sound quality is distorted due to a change in sound pressure, internal vibration or external vibration. Is likely to occur.

そこで、特許文献１に記載された発明では、音響用のアルミニウム電解コンデンサにおいて、セパレータの膨潤状態における機械的強度を補強するため、セパレータの繊維基材にフッ素雲母粒子を含有させるようにしている。   Therefore, in the invention described in Patent Document 1, in the acoustic aluminum electrolytic capacitor, in order to reinforce the mechanical strength of the separator in the swollen state, the fiber base material of the separator is made to contain fluorine mica particles.

特開２００１−６９８０号公報JP 2001-6980 A

特許文献１に記載された発明によれば、フッ素雲母粒子をセパレータに含有させることによってある程度オーディオ信号の劣化や音質の歪みを少なくすることができるが、十分な効果が得られるまでに至っていない。   According to the invention described in Patent Document 1, although it is possible to reduce the deterioration of the audio signal and the distortion of the sound quality to some extent by including the fluorine mica particles in the separator, a sufficient effect has not yet been obtained.

したがって、本発明の課題は、音響用途のアルミニウム電解コンデンサにおいて、音圧の変化や振動による音質の変化がより少なく、より品質の高い再生音が得られるようにすることにある。   Accordingly, an object of the present invention is to make it possible to obtain a higher quality reproduced sound with less change in sound quality due to a change in sound pressure or vibration in an aluminum electrolytic capacitor for acoustic applications.

上記課題を解決するため、本発明は、アルミニウム電解コンデンサ用セパレータにおいて、その繊維基材に電解液に溶解しない誘電体粉末を含有させたことを特徴としている。   In order to solve the above-mentioned problems, the present invention is characterized in that in the separator for an aluminum electrolytic capacitor, the fiber base material contains a dielectric powder that does not dissolve in the electrolytic solution.

本発明において、上記誘電体粉末の粒径は１ｎｍ〜５μｍで、上記繊維基材に対する上記誘電体粉末の含有率は０．０１〜１．０ｗｔ％であることが好ましい。   In the present invention, the dielectric powder preferably has a particle size of 1 nm to 5 μm, and the content of the dielectric powder with respect to the fiber substrate is preferably 0.01 to 1.0 wt%.

また、上記誘電体粉末として、二酸化チタン（ＴｉＯ２）もしくはチタン酸バリウム（ＢａＴｉＯ３）が好ましく採用され、上記繊維基材には、クラフトパルプ繊維もしくはマニラ麻繊維が用いられてよい。 Moreover, titanium dioxide (TiO 2 ) or barium titanate (BaTiO 3 ) is preferably employed as the dielectric powder, and kraft pulp fiber or Manila hemp fiber may be used as the fiber base material.

本発明には、アルミニウム電解コンデンサも含まれる。すなわち、本発明のアルミニウム電解コンデンサは、ともにアルミニウム材からなる陽極箔と陰極箔とをセパレータを介して渦巻き状に巻回し所定の電解液が含浸されたコンデンサ素子を有底筒状の金属ケース内に収納し、上記金属ケースの開口部を封口部材にて封止してなるアルミニウム電解コンデンサで、上記セパレータとして、繊維基材に電解液に溶解しない誘電体粉末を含有させたセパレータを用いることを特徴としており、特に、音響機器のコンデンサとして好適である。   The present invention also includes an aluminum electrolytic capacitor. That is, the aluminum electrolytic capacitor of the present invention includes an anode foil and a cathode foil both made of an aluminum material spirally wound through a separator and a capacitor element impregnated with a predetermined electrolytic solution in a bottomed cylindrical metal case. And an aluminum electrolytic capacitor in which the opening of the metal case is sealed with a sealing member, and a separator containing a dielectric powder that does not dissolve in an electrolyte solution is used as the separator. In particular, it is suitable as a capacitor for audio equipment.

本発明によれば、アルミニウム電解コンデンサのセパレータに、電解液に溶解しない誘電体粉末を含有させたセパレータを用いることにより、音響用途のアルミニウム電解コンデンサにおいて、音圧の変化や振動による音質の変化がより少なく、より品質の高い再生音を得ることができる。   According to the present invention, by using a separator containing a dielectric powder that does not dissolve in an electrolytic solution as a separator of an aluminum electrolytic capacitor, in an aluminum electrolytic capacitor for acoustic use, a change in sound quality due to a change in sound pressure or a vibration is not caused. Less and higher quality reproduced sound can be obtained.

アルミニウム電解コンデンサの基本的な構成を示す模式的な断面図。FIG. 3 is a schematic cross-sectional view showing a basic configuration of an aluminum electrolytic capacitor. コンデンサ素子の構成要素を図解した模式的な斜視図。The typical perspective view which illustrated the component of the capacitor | condenser element. アルミニウム電解コンデンサの等価回路図。The equivalent circuit diagram of an aluminum electrolytic capacitor.

次に、図１ないし図３を参照して、本発明の実施形態を説明するが、本発明はこれに限定されるものではない。   Next, an embodiment of the present invention will be described with reference to FIGS. 1 to 3, but the present invention is not limited to this.

まず、図１に示すように、本発明のアルミニウム電解コンデンサは、基本的な構成として、コンデンサ素子１０と、その収納容器である有底筒状の金属ケース２０と、金属ケース２０の開口部を封止する封口部材３０とを備える。   First, as shown in FIG. 1, an aluminum electrolytic capacitor of the present invention has, as a basic configuration, a capacitor element 10, a bottomed cylindrical metal case 20 as a storage container, and an opening of the metal case 20. And a sealing member 30 to be sealed.

図２に示すように、コンデンサ素子１０は、陽極箔１１と陰極箔１２とを、それらの間にセパレータ１３（１３ａ，１３ｂ）を介在させて渦巻き状に巻回することにより構成される。   As shown in FIG. 2, the capacitor element 10 is configured by winding an anode foil 11 and a cathode foil 12 in a spiral shape with a separator 13 (13a, 13b) interposed therebetween.

図示の例では、セパレータ１３ａ，陽極箔１１，セパレータ１３ｂ，陰極箔１２を重ねた状態で巻回される。なお、セパレータ１３ａ，１３ｂは同一の素材からなるため、特に区別する必要がない場合には、セパレータ１３とする。   In the illustrated example, the separator 13a, the anode foil 11, the separator 13b, and the cathode foil 12 are wound in a stacked state. Since the separators 13a and 13b are made of the same material, the separator 13 is used when it is not necessary to distinguish between them.

陽極箔１１と陰極箔１２は、ともにアルミニウム材からなり、陽極箔１１には、アルミニウム材をエッチングし、さらに陽極化成したものが用いられ、また、陰極箔１２には、アルミニウム材をエッチングしてなるエッチド箔が好ましく用いられる。   The anode foil 11 and the cathode foil 12 are both made of an aluminum material. The anode foil 11 is formed by etching an aluminum material and then anodized, and the cathode foil 12 is etched by an aluminum material. An etched foil is preferably used.

陽極箔１１と陰極箔１２は、テープ状であって巻回する前に、その各々に引出リードとしてのタブ端子１４，１５が例えばかしめ針等の接続手段によって電気的・機械的に取り付けられる。   The anode foil 11 and the cathode foil 12 are in the form of a tape, and before being wound, tab terminals 14 and 15 as lead leads are attached to each of them electrically and mechanically by connecting means such as caulking needles.

詳しくは図示しないが、タブ端子１４，１５は、アルミニウム材の丸棒からなり、その一端側をプレス等により扁平に押し潰して羽子板状とした端子本体と、端子本体の他端側に残されている丸棒の端部に溶接等により一体的に接続されたＣＯＰ線（銅被覆鋼線）とから構成されてよい。   Although not shown in detail, the tab terminals 14 and 15 are made of a round bar made of aluminum material, and one end side of the tab terminals 14 and 15 is flattened by a press or the like to be flattened, and left on the other end side of the terminal body. It may be composed of a COP wire (copper-coated steel wire) integrally connected to the end of the round bar that is connected by welding or the like.

金属ケース２０は、アルミニウム材のプレス成型品よりなる。この実施形態において、封口部材３０には、ブチルゴム等からなる封口ゴムが用いられている。   The metal case 20 is made of a press-molded product made of aluminum. In this embodiment, a sealing rubber made of butyl rubber or the like is used for the sealing member 30.

封口部材３０には、タブ端子１４，１５を貫通する貫通孔が穿設されており、タブ端子１４，１５に取り付けられた状態でコンデンサ素子１０とともに金属ケース２０内に挿入され、金属ケース２０の開口端縁のかしめにより固着される。   The sealing member 30 has through holes penetrating the tab terminals 14 and 15, and is inserted into the metal case 20 together with the capacitor element 10 while being attached to the tab terminals 14 and 15. It is fixed by caulking the opening edge.

コンデンサ素子１０には、電解液が含浸される。電解液の含浸は、金属ケース２０に収納する前もしくは収納後のいずれに行われてもよい。   The capacitor element 10 is impregnated with an electrolytic solution. The impregnation with the electrolytic solution may be performed either before or after storage in the metal case 20.

電解液には、溶質として例えば無機酸や、芳香族カルボン酸および脂肪族カルボン酸等の有機酸を使用でき、また、溶媒としては、γ−ブチロラクトン等の非プロトン溶媒や、エチレングリコール等のプロトン溶媒を使用できるが、これに限定されるものではない。   In the electrolytic solution, for example, an inorganic acid or an organic acid such as an aromatic carboxylic acid or an aliphatic carboxylic acid can be used as a solute, and a solvent such as an aprotic solvent such as γ-butyrolactone or a proton such as ethylene glycol. Although a solvent can be used, it is not limited to this.

また、電解液には、初期の損失角の正接（ｔａｎδ）を改善するためにケトン類を添加したり、ｐＨを調整するためにｐＨ調整剤を添加する等、その他の添加剤が添加されてよい。   In addition, other additives such as ketones are added to the electrolyte to improve the initial loss angle tangent (tan δ), and pH adjusters are added to adjust the pH. Good.

セパレータ１３には、繊維を紙のように抄製したものが用いられる。繊維としては、クラフトパルプ繊維やマニラ麻繊維等の植物繊維やポリプロピレン，ビニロン，レーヨン，ポリエチレン，ポリエステル等の合成繊維を単独で用いたり、あるいはこれらにガラス繊維を混抄させたものが使用される。   As the separator 13, a fiber made of paper like paper is used. As the fiber, a plant fiber such as kraft pulp fiber or manila hemp fiber, or a synthetic fiber such as polypropylene, vinylon, rayon, polyethylene, polyester or the like, or a mixture of these with glass fiber is used.

本発明では、音響用途のアルミニウム電解コンデンサにおいて、音圧の変化や振動による音質の変化がより少なく、品質の高い再生音が得られるようにするため、セパレータ１３の繊維基材に、電解液に溶解しない誘電体粉末（図示省略）を含有させる。   In the present invention, in an aluminum electrolytic capacitor for acoustic use, in order to obtain a high quality reproduced sound with less change in sound pressure and sound quality due to vibration, the separator 13 has a fibrous base material and an electrolytic solution. A dielectric powder (not shown) that does not dissolve is contained.

誘電体粉末の粒径は１ｎｍ〜５μｍであることが好ましい。すなわち、１ｎｍ未満では、音圧の変化や振動による音質の変化に改善が見られず、他方において、５μｍを超えると、かえって音質が損なわれるおそれがあるので好ましくない。   The particle size of the dielectric powder is preferably 1 nm to 5 μm. That is, when the thickness is less than 1 nm, no improvement is seen in the change in sound pressure or the change in sound quality due to vibration. On the other hand, when the thickness exceeds 5 μm, the sound quality may be impaired.

また、繊維基材に対する誘電体粉末４０の含有率は０．０１〜１．０ｗｔ％であることが好ましい。すなわち、含有率が０．０１ｗｔ％未満と少なすぎても、また、１．０ｗｔ％超と多すぎても、所期の効果が得られないので好ましくない。   Moreover, it is preferable that the content rate of the dielectric powder 40 with respect to a fiber base material is 0.01-1.0 wt%. That is, if the content is too small, less than 0.01 wt%, or too much, more than 1.0 wt%, the desired effect cannot be obtained, which is not preferable.

誘電体粉末には、二酸化チタン（ＴｉＯ２）もしくはチタン酸バリウム（ＢａＴｉＯ３）が好ましく採用される。 For the dielectric powder, titanium dioxide (TiO 2 ) or barium titanate (BaTiO 3 ) is preferably employed.

二酸化チタンについて説明すれば、二酸化チタンには、アナターゼ型二酸化チタン，ルチル型二酸化チタン，ブルッカイト型二酸化チタン，アモルファス型二酸化チタン等が知られているが、これらの中では、アナターゼ型二酸化チタンが好ましい。   As for titanium dioxide, anatase-type titanium dioxide, rutile-type titanium dioxide, brookite-type titanium dioxide, amorphous-type titanium dioxide and the like are known as titanium dioxide. Among these, anatase-type titanium dioxide is preferable. .

二酸化チタン粒子は、乾燥させた二酸化チタン粒子であってよいが、二酸化チタンゲル，二酸化チタンゾル等であってもよい。   The titanium dioxide particles may be dried titanium dioxide particles, but may be a titanium dioxide gel, a titanium dioxide sol, or the like.

二酸化チタンゲル，二酸化チタンゾル等の二酸化チタンの分散体を用いる場合には、その分散体に含まれている溶媒を除去して使用する。商業的に入手できる二酸化チタンには、例えば石原産業社製の品番ＳＴ−２１等が挙げられる。   When using a titanium dioxide dispersion such as titanium dioxide gel or titanium dioxide sol, the solvent contained in the dispersion is removed before use. Examples of commercially available titanium dioxide include product number ST-21 manufactured by Ishihara Sangyo Co., Ltd.

厚さ９０μｍのアルミニウム箔（純度４Ｎ）をエッチングし化成処理したものを陽極箔とし、厚さ５０μｍのアルミニウム箔（純度２Ｎ）をエッチングしたものを陰極箔とし、これらの間に表１のように仕様が異なるセパレータを挟んで巻回してコンデンサ素子を作成した。そして、各コンデンサ素子にエチレングリコール系の電解液を含浸させた後、有底筒状のアルミニウムケースに入れ、各タブ端子を封口ゴムの貫通孔を貫通させて外部に引き出しながら、アルミニウムケースの開口部を密封することにより、直径１０ｍｍ，高さ１０ｍｍ，定格１６Ｖ２２０μＦの音響用アルミニウム電解コンデンサ（実施例１〜８，比較例１〜１０および特許文献１に記載のもの）を作成した。   An aluminum foil (purity 4N) having a thickness of 90 μm etched and chemically treated is used as an anode foil, and an aluminum foil (purity 2N) having a thickness of 50 μm is etched as a cathode foil. Capacitor elements were created by winding separators with different specifications. After each capacitor element is impregnated with an ethylene glycol-based electrolyte, it is placed in a bottomed cylindrical aluminum case, and each tab terminal is opened through the through-hole of the sealing rubber while being pulled out. By sealing the part, acoustic aluminum electrolytic capacitors (those described in Examples 1 to 8, Comparative Examples 1 to 10 and Patent Document 1) having a diameter of 10 mm, a height of 10 mm, and a rating of 16 V 220 μF were prepared.

Figure 2012099526
Figure 2012099526

実施例１〜８，比較例１〜１０およびフッ素雲母粒子含有のセパレータを用いた特許文献１に記載のアルミニウム電解コンデンサを音響機器の電源平滑用コンデンサとして用い、音楽の再生音を６名で試聴して、その音質を帯域，質感，解像度，音像および音場に分けて１０点満点で評価した。その結果を表２に示す。   Example 1-8, Comparative Examples 1-10, and an aluminum electrolytic capacitor described in Patent Document 1 using a separator containing fluorine mica particles were used as power source smoothing capacitors for audio equipment, and music playback sounds were listened to by six people Then, the sound quality was divided into band, texture, resolution, sound image, and sound field and evaluated with a maximum of 10 points. The results are shown in Table 2.

Figure 2012099526
Figure 2012099526

ここで、帯域とは、周波数特性であり、高得点のものほど再現できる音の周波数帯域が広いことを意味している。質感とは、音のＳ／Ｎ比で、音の伸びの再現性を意味している。解像度とは、音の分解能であり、例えば重なった旋律をそれぞれ把握できる度合いを意味している。音像とは、音の美しさであり、音の透明感や輪郭を意味し、音場とは、音の厚み、すなわち音の収束感を意味している。   Here, the band is a frequency characteristic, and means that the higher the score, the wider the frequency band of the sound that can be reproduced. The texture is the S / N ratio of sound and means the reproducibility of sound expansion. The resolution is the resolution of the sound and means, for example, the degree to which the overlapping melody can be grasped. The sound image is the beauty of sound, meaning the transparency and outline of the sound, and the sound field is the thickness of the sound, that is, the sense of convergence of the sound.

表２から分かるように、本発明の実施例１〜８によれば、帯域，質感，解像度，音像および音場ともに７点以上（特に、実施例５〜８はすべてが１０点）の高得点であるのに対して、比較例１〜１０ではいずれも５点評価であり、また、特許文献１の場合は６点評価であり、本発明の繊維基材にフッ素皮膜を有する誘電体粉末を含有させたセパレータを用いたアルミニウム電解コンデンサの優位性が検証された。   As can be seen from Table 2, according to Examples 1 to 8 of the present invention, the band, texture, resolution, sound image and sound field are all 7 points or more (especially, Examples 5 to 8 are all 10 points). On the other hand, in Comparative Examples 1 to 10, all are evaluated by 5 points, and in the case of Patent Document 1, it is evaluated by 6 points, and the dielectric powder having a fluorine film on the fiber base material of the present invention The superiority of the aluminum electrolytic capacitor using the contained separator was verified.

以上説明したように、本発明のアルミニウム電解コンデンサは、音響用途に好適であるが、これ以外の用途に適用されてもよいことは勿論である。   As described above, the aluminum electrolytic capacitor of the present invention is suitable for acoustic applications, but it goes without saying that it may be applied to other applications.

１０ コンデンサ素子
１１ 陽極箔
１２ 陰極箔
１３（１３ａ，１３ｂ） セパレータ
１４，１５ タブ端子
２０ 金属ケース（アルミニウムケース）
３０ 封口部材 DESCRIPTION OF SYMBOLS 10 Capacitor element 11 Anode foil 12 Cathode foil 13 (13a, 13b) Separator 14,15 Tab terminal 20 Metal case (aluminum case)
30 Sealing member

Claims (7)

繊維基材に電解液に溶解しない誘電体粉末を含有させたことを特徴とするアルミニウム電解コンデンサ用セパレータ。   A separator for an aluminum electrolytic capacitor, wherein a dielectric powder that does not dissolve in an electrolytic solution is contained in a fiber base material. 上記誘電体粉末の粒径が１ｎｍ〜５μｍであることを特徴とする請求項１に記載のアルミニウム電解コンデンサ用セパレータ。   2. The aluminum electrolytic capacitor separator according to claim 1, wherein the dielectric powder has a particle size of 1 nm to 5 [mu] m. 上記繊維基材に対する上記誘電体粉末の含有率が０．０１〜１．０ｗｔ％であることを特徴とする請求項１または２に記載のアルミニウム電解コンデンサ用セパレータ。   The separator for an aluminum electrolytic capacitor according to claim 1 or 2, wherein the content of the dielectric powder with respect to the fiber base material is 0.01 to 1.0 wt%. 上記誘電体粉末が二酸化チタン（ＴｉＯ２）もしくはチタン酸バリウム（ＢａＴｉＯ３）であることを特徴とする請求項１ないし３のいずれか１項に記載のアルミニウム電解コンデンサ用セパレータ。 4. The separator for an aluminum electrolytic capacitor according to claim 1, wherein the dielectric powder is titanium dioxide (TiO 2 ) or barium titanate (BaTiO 3 ). 5. 上記繊維基材がクラフトパルプ繊維もしくはマニラ麻繊維であることを特徴とする請求項１ないし４のいずれか１項に記載のアルミニウム電解コンデンサ用セパレータ。   5. The separator for an aluminum electrolytic capacitor according to claim 1, wherein the fiber base material is kraft pulp fiber or Manila hemp fiber. ともにアルミニウム材からなる陽極箔と陰極箔とをセパレータを介して渦巻き状に巻回し所定の電解液が含浸されたコンデンサ素子を有底筒状の金属ケース内に収納し、上記金属ケースの開口部を封口部材にて封止してなるアルミニウム電解コンデンサにおいて、
上記セパレータに請求項１ないし５のいずれか１項によるセパレータを用いたことを特徴とするアルミニウム電解コンデンサ。 A capacitor element impregnated with a predetermined electrolytic solution by winding an anode foil and a cathode foil both made of an aluminum material in a spiral shape through a separator is housed in a bottomed cylindrical metal case, and an opening of the metal case In an aluminum electrolytic capacitor formed by sealing with a sealing member,
An aluminum electrolytic capacitor using the separator according to any one of claims 1 to 5 as the separator. 音響機器のコンデンサとして用いられることを特徴とする請求項６に記載のアルミニウム電解コンデンサ。   The aluminum electrolytic capacitor according to claim 6, wherein the aluminum electrolytic capacitor is used as a capacitor of an acoustic device.
JP2010243466A 2010-10-29 2010-10-29 Separator for aluminum electrolytic capacitor and aluminum electrolytic capacitor Pending JP2012099526A (en)