JP2012062650A - Woody floor material and building - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a woody floor material whose abrasion resistance and scratch resistance are improved even when a finish material is soft wood such as cider and which is easily restored even when a finish surface is damaged, and a highly durable building.SOLUTION: A woody floor material 100 includes a wooden base material 10, a wooden base material strengthening protective layer 40 coated on the wooden base material, and a surface protective layer 50 coated on the wooden base material strengthening protective layer. The wooden base material strengthening protective layer 40 is formed of a base resin coating material containing 0.5 to 25 pts.wt. of wood fibers in a cellulose structure whose average fiber length is 300 to 2000 μm. For the building whose floor is configured by the wooden floor material, even when the wooden base material 10 is the soft wood such as cider, the abrasion resistance and the scratch resistance are improved, a finish state is easily restored even when the finish surface is damaged, and the building becomes highly durable.

Description

本発明は、耐磨耗性及び耐傷性に優れた木質系床材及びこれを用いた建物に関する。   The present invention relates to a wooden floor material excellent in wear resistance and scratch resistance, and a building using the same.

建物の床材には、樹脂系や木質系の材料が使用されている。木質系床材は直接接触する面として、触感・意匠性・断熱性の点で、樹脂系の床材に優れ、居住性が求められる住宅や学校などの用途の建物に使われている。また、木質系床材としては、一枚の板材からなる単層板材とともに、複数の合板を重ね合わせた上に、表層に０．２５〜４．０ｍｍの木製単板を仕上板として張った複層板材も用いられている。   Resin-based and wood-based materials are used for building flooring. Wood-based flooring is used as a direct contact surface in buildings such as houses and schools that are superior in resin-based flooring in terms of touch, design, and heat insulation, and that require comfort. In addition, as a wood-based flooring, a single-layer board made of a single board and a plurality of plywoods are stacked, and a wooden single board of 0.25 to 4.0 mm is stretched as a finishing board on the surface layer. Layer board materials are also used.

従来から、単層板材の樹種としては、椅子や家具などを移動させても傷がつきにくいことから、なら、かば、ぶな、チーク、花梨などの無垢の硬質の板材が用いられてきた。一方、複層板材は、表層の木製単板の厚さを超える損傷が発生した場合には、著しく見栄えが低下し、床材の一部を取り替える必要が生じるという欠点があるにも関わらず、価格面や施工性が優れていることから、表層に上記単層板材の樹種の仕上げに似せた木製単板を張ったものが使用されてきた。   Conventionally, solid hard board materials such as beaks, beech, teak and quince have been used as tree species for single-layer board materials because they are less likely to be damaged even when chairs or furniture are moved. On the other hand, the multi-layer board material has a disadvantage that when the damage exceeding the thickness of the surface wooden veneer occurs, the appearance is remarkably deteriorated, and a part of the floor material needs to be replaced. Because of its excellent price and workability, the surface layer has been used with a wooden veneer resembling the finish of the tree species of the single-layer plate material.

そして、学校の教室や体育館などのように、学習机や体育器具などの移動が日常的に行われ、仕上げ表面が傷つきやすい用途の居室では単層板材が使用され、家具の移動などが少ない住宅の居室などでは複層板材が使用され使い分けられてきた。ところが、スギなどの針葉樹はその繊維質が柔らかいため、家具を載せたり、引きずったりする用途の居室の床材としては、その表面に傷がつき易く、磨耗し易いことから、上述のような体育館や教室の床では使うことができないという問題があった。   And, like a classroom in a school or a gymnasium, where a learning desk or gym equipment is moved on a daily basis, a single-layer board is used in a room where the finish surface is easily damaged, and there is little movement of furniture, etc. Multi-layered board materials have been used in various rooms. However, since soft fibers such as cedar are soft in fiber, they are easy to be damaged and worn as flooring for living rooms where furniture is placed or dragged. There was a problem that it could not be used on the floor of the classroom.

一方、地域で生産された原材料を活かして用いるという地産地消のニーズから、国内の多くの地域で生産されているスギやヒノキなどを床材料として使うことを可能にする技術が開発されている。まず、スギなどの木材を圧縮して硬化した上で、その表面に硬化皮膜を形成する技術があるが、木材を圧縮硬化する技術は、加工コストが高価であるため普及が進んでいない。また、樹種の表面に硬化皮膜を形成させる技術としては、例えば、木質基板の表面に、アミノアルキッド樹脂液に炭化珪素やホワイトアルミナなどの無機質充填剤を配合し混合させた下塗り塗料を塗装し、この上に上塗り塗料を塗装して、耐磨耗性を向上させる技術が知られている。   On the other hand, technology that enables the use of cedar and cypress produced in many regions in Japan as flooring materials has been developed in response to the need for local production for local consumption, using raw materials produced in the region. . First, there is a technique for compressing and curing wood such as cedar and forming a cured film on the surface thereof. However, the technique for compressing and curing wood has not been widely used because of its high processing cost. In addition, as a technique for forming a cured film on the surface of the tree species, for example, an undercoat paint in which an inorganic alkyd resin liquid is mixed and mixed with an inorganic filler such as silicon carbide or white alumina is applied to the surface of a wooden substrate, A technique for improving the wear resistance by applying a top coating on this is known.

しかしながら、この従来技術によった場合には、木質基板の下塗り塗料に配合される上記無機質充填剤の比重が大きいため、下塗りの塗装工程において無機質充填剤が沈殿し均一に分散されないことがあり、これにより表面における耐磨耗性にばらつきが生じ、耐傷性は確保できるものの、耐磨耗性が十分に得られない場合があるという課題があった。   However, according to this prior art, because the specific gravity of the inorganic filler blended in the undercoat paint of the wooden substrate is large, the inorganic filler may precipitate and not be uniformly dispersed in the undercoat coating process, As a result, the wear resistance on the surface varies, and although scratch resistance can be ensured, there is a problem that sufficient wear resistance may not be obtained.

更に、特開平１−１０５８６１号公報には、木質基板の表面に下塗り塗料により下塗膜層を形成し、この下塗膜層に無機質充填剤を含有する中塗り塗料により中塗膜層を形成し、この中塗膜層の上に粉末樹脂系ワックスを含有する上塗り塗料により上塗膜層を設けた木質床材に関する技術が開示されている。この技術は、中塗膜層には耐磨耗性及び耐傷性を確保し、更に上塗膜層により耐磨耗性を向上させるものである。   Further, JP-A-1-105861 discloses that an undercoat layer is formed on the surface of a wooden substrate by an undercoat paint, and an intermediate coat layer is formed on the undercoat layer by an intermediate coat containing an inorganic filler. And the technique regarding the wooden flooring which provided the upper-coat-film layer with the top-coat paint containing a powder resin-type wax on this middle-coat-film layer is disclosed. This technique ensures wear resistance and scratch resistance for the middle coating layer, and further improves the wear resistance by the upper coating layer.

また、木質系材料に硬化皮膜を形成する別の従来技術としては、木質系材料に紫外線硬化型塗装をするという技術がある。この技術は、溶剤を用いず、紫外線照射により短期間で塗膜が硬化し、価格も安価であることから普及が進んでいる。しかし、その効果は塗装の厚さの範囲内にとどまり、その塗膜は木材が持っている伸縮性に追従することができず、塗装に微細なひび割れが入り易く、傷がついた場合には、傷周辺において美観が損なわれた状態となり易く、傷が木質材に及びやすく、その復元が困難であるという課題があった。   As another conventional technique for forming a cured film on a wood-based material, there is a technique of applying an ultraviolet curable coating to a wood-based material. This technique is spreading because a coating is cured in a short period of time by ultraviolet irradiation without using a solvent, and the price is low. However, the effect remains within the thickness range of the paint, and the paint film cannot follow the elasticity of the wood, and the paint is prone to fine cracks and is damaged. There is a problem that the appearance of the wound is likely to be impaired in the vicinity of the wound, the scratch is easily applied to the wooden material, and the restoration thereof is difficult.

特開平１−１０５８６１号公報JP-A-1-105861

本願発明は、上記背景技術に鑑みてなされたものであり、その課題は、スギやヒノキなどの軟質の木質材料を使用した耐磨耗性及び耐傷性に優れた床材、及びこれを用いた建物を提供することを目的とする。   This invention is made | formed in view of the said background art, The subject used the floor material excellent in abrasion resistance and scratch resistance using soft wooden materials, such as a cedar and a cypress, and this. The purpose is to provide buildings.

本発明の第１の発明は、木質基材と、前記木質基材に塗装された木質基材強化保護層と、前記木質基材強化保護層に塗装された表面保護層と、を含む木質系床材であって、
前記木質基材強化保護層が、少なくとも前記木質基材の室内面側に、平均繊維長３００〜２０００μｍのセルロース構造の木材繊維を０．５〜２５重量部を含んだ下地樹脂塗料を塗装したことにより形成されている、ことを特徴としている。 A first aspect of the present invention is a wood system comprising: a wood base material; a wood base material reinforced protective layer coated on the wood base material; and a surface protective layer coated on the wood base material reinforced protective layer. Flooring,
The wooden substrate reinforced protective layer is coated with a base resin coating containing 0.5 to 25 parts by weight of wood fibers having an average fiber length of 300 to 2000 μm on the indoor surface side of the wooden substrate. It is characterized by being formed by.

本発明の木質系床材は、木質基材に繊維長３００〜２０００μｍのセルロース構造の木材繊維を含んだ下地樹脂塗料により塗装されて木質基材強化保護層が形成されている。下地樹脂塗料に含まれている木材繊維の平均繊維長が３００〜２０００μｍであるため、塗装面に耐磨耗性及び耐傷性を付与する。平均繊維長が３００μｍ未満の場合は、十分に表面硬度を上げることができず、塗装面に十分な耐磨耗性及び耐傷性を付与することが困難であり、平均繊維長が２０００μｍを超えると凸凹が大きくなり平滑性が劣ることになる。また木材繊維が下地樹脂塗料に対して０．５重量部未満である場合には床材としての表面硬度を確保することが困難になり、木材繊維が下地樹脂塗料に対して２５重量部を超える場合には塗装表面の平滑性が劣ることになる。   The wood-based flooring of the present invention is coated with a base resin coating containing a wood fiber having a cellulose structure with a fiber length of 300 to 2000 μm on a wood substrate to form a wood substrate-reinforced protective layer. Since the average fiber length of the wood fibers contained in the base resin coating is 300 to 2000 μm, wear resistance and scratch resistance are imparted to the painted surface. When the average fiber length is less than 300 μm, the surface hardness cannot be sufficiently increased, and it is difficult to impart sufficient abrasion resistance and scratch resistance to the painted surface. When the average fiber length exceeds 2000 μm The unevenness becomes large and the smoothness is inferior. Further, when the wood fiber is less than 0.5 parts by weight with respect to the base resin paint, it becomes difficult to ensure the surface hardness as a flooring material, and the wood fiber exceeds 25 parts by weight with respect to the base resin paint. In this case, the smoothness of the painted surface is inferior.

木質基材強化保護層に含まれる木材繊維は変形に対応可能であるため木質基材の変形に追従して木質基材の表面を覆い、木質基材の節を脱落させることもなく、木質基材の節が脱落して穴があくことを防止する。また木質基材強化保護層には、表面保護層が塗装されているため、下地樹脂塗料に含まれている木材繊維により木質基材強化保護層に凸凹ができても、それを表面保護層が平滑に保ち、高い意匠性を保持する。   The wood fiber contained in the reinforced protective layer of the wooden base material can cope with the deformation, so that the surface of the wooden base material is covered following the deformation of the wooden base material, so that the nodes of the wooden base material are not dropped off. Prevents timber nodes from falling off and making holes. Moreover, since the surface protective layer is coated on the wood base material reinforced protective layer, even if the wood base material reinforced protective layer is uneven due to the wood fiber contained in the base resin coating, the surface protective layer is Keeps it smooth and maintains high design.

これにより、木質系床材に高い耐磨耗性及び耐傷性を付与することができる。また、木質系床材が節を含んだ床材である場合であっても、硬い節だけが残り柔らかい部分だけが減ることがなく、美しい状態で木質系床材が長期間耐用可能となる。   Thereby, high abrasion resistance and scratch resistance can be imparted to the wooden floor material. Moreover, even when the wooden flooring is a flooring containing a knot, only the hard knot remains and only the soft part does not decrease, and the wooden flooring can be used for a long time in a beautiful state.

また、木質基材強化保護層には表面保護層が形成されているため、表面保護層に擦り傷がついた場合であっても、木質基材は強化保護層により保護され擦り傷がつきにくい。そして、所定の年月が経過し、表面保護層の一部が擦り減り、表面保護層の美観が低下した場合には、表面保護層の擦り減った劣化部分を研磨して削除して、再度、表面保護層を塗り足すことにより、美観を復元するとともに、木質系床材を長期間使用可能とする。   In addition, since the surface protective layer is formed on the wooden substrate reinforced protective layer, even when the surface protective layer is scratched, the wooden substrate is protected by the reinforced protective layer and is not easily scratched. Then, when a predetermined period of time has passed and a part of the surface protective layer has been worn away, and the aesthetics of the surface protective layer has deteriorated, the worn-down deteriorated portion of the surface protective layer has been polished and removed, and again By applying a surface protective layer, the aesthetics are restored and the wooden flooring can be used for a long time.

本発明の第２の発明は、第１の発明の前記木質系床材において、下地樹脂塗料がウレタン樹脂系塗料であることを特徴としている。ウレタン樹脂系塗料としては、例えば、ＯＨ基を持つポリエステル、アルキド、アクリルなどのポリオール樹脂を主成分とする塗料主剤に、ＮＣＯ基を持つポリイソシアネート樹脂を主成分とする硬化剤を混合することによりウレタン結合を形成し、常温で硬化乾燥する２液型ポリウレタン樹脂塗料によると好適である。これにより、安価に且つ容易に耐磨耗性及び耐傷性に優れた塗膜を形成することができる。   A second invention of the present invention is characterized in that, in the wood-based flooring of the first invention, the base resin paint is a urethane resin paint. As a urethane resin-based paint, for example, by mixing a curing agent mainly containing a polyisocyanate resin having an NCO group into a coating agent mainly containing a polyol resin such as polyester having OH group, alkyd, or acrylic. A two-pack type polyurethane resin paint that forms a urethane bond and is cured and dried at room temperature is preferred. Thereby, the coating film excellent in abrasion resistance and scratch resistance can be formed inexpensively and easily.

本発明の第３の発明は、第１又は第２の発明の前記木質系床材において、前記木質基材強化保護層の乾燥状態膜厚さが２５０〜４００μｍであることを特徴としている。すなわち、塗膜厚さが２００μｍ未満となると、スギなどの軟質木材を床材として使用するに十分な表面硬度を確保するのが困難となるおそれがある。また、塗膜厚さが４００μｍを超えると、塗装作業工程上、多大な時間を要したり、コストアップになるとともに塗膜内に気泡を発生させるおそれもある。すなわち、乾燥状態膜厚さを２５０〜４００μｍとすることにより、木質基材に効率的に高い耐磨耗性及び耐傷性を備えた塗装をすることが可能になる。   According to a third aspect of the present invention, in the wood-based flooring of the first or second aspect, the dry thickness of the wood base reinforced protective layer is 250 to 400 μm. That is, when the coating thickness is less than 200 μm, it may be difficult to ensure sufficient surface hardness to use soft wood such as cedar as a flooring. On the other hand, if the thickness of the coating film exceeds 400 μm, it takes a lot of time in the coating operation process, and the cost may increase and bubbles may be generated in the coating film. That is, by setting the dry state film thickness to 250 to 400 μm, it is possible to efficiently apply a coating having high wear resistance and scratch resistance to a wooden substrate.

本発明の第４の発明は、第１乃至第３の発明の前記木質系床材において、前記木質基材強化保護層が少なくとも２層からなることを特徴としている。木質基材強化保護層が複層で構成されることにより、気泡の発生の可能性を抑えて、作業効率を向上させ、所定の厚さの木質基材強化保護層を構成することが容易になる。   The fourth invention of the present invention is characterized in that, in the wood-based flooring of the first to third inventions, the wood substrate reinforced protective layer comprises at least two layers. The wood base reinforced protective layer is composed of multiple layers, which can reduce the possibility of air bubbles, improve work efficiency, and make it easy to construct a wood base reinforced protective layer with a predetermined thickness. Become.

本発明の第５の発明は、第２乃至第４の発明の前記木質系床材において、前記表面保護層がウレタン樹脂系塗料であり、乾燥塗膜厚さが６０〜１００μｍであることを特徴としている。表面保護層が木質基材強化保護層と同一材質のウレタン塗装であるため、層間の馴染みがよく、塗装が一体化し、基材強化保護層と表面保護層とが同一の変形性を有する。木質系床材の美観を保つ乾燥塗膜厚さが木質基材強化保護層よりも薄く形成され、耐磨耗性及び耐傷性の高い塗装を少量の塗料で、高い作業効率で実現することができる。   According to a fifth aspect of the present invention, in the wood-based flooring according to the second to fourth aspects, the surface protective layer is a urethane resin-based paint, and a dry coating thickness is 60 to 100 μm. It is said. Since the surface protective layer is a urethane coating made of the same material as that of the wood base reinforced protective layer, the familiarity between the layers is good, the coating is integrated, and the base reinforced protective layer and the surface protective layer have the same deformability. The dry coating thickness that keeps the aesthetics of the wooden flooring is thinner than the reinforced protective layer of the wooden base material, and it is possible to achieve high abrasion resistance and scratch resistance painting with a small amount of paint with high work efficiency it can.

本発明の第６の発明は、第１乃至第５の発明の前記木質系床材において、前記木質基材が、無垢板であることを特徴としている。第６の発明においては、木質基材は無垢板としている。スギなどの針葉樹のように柔らかい木質の無垢板、又は節が多く散在する間伐材の無垢板に本発明を適用すれば、それらの柔らかい樹種の無垢板を耐磨耗性及び耐傷性に優れた単層床材として使用することができる。これにより、建物に使用する床材の木質基材が、建物建設地に近い場所で伐採された柔らかい樹種の針葉樹からなっている場合であっても、それを用いて、柔らかいけれども割れにくい耐磨耗性及び耐傷性に優れた単層床材が提供できる。   According to a sixth aspect of the present invention, in the wooden flooring according to the first to fifth aspects, the wooden base material is a solid board. In the sixth invention, the wooden substrate is a solid board. If the present invention is applied to a soft wooden solid board such as a conifer such as cedar or a thinned wooden board with many knots, the soft wooden solid board has excellent wear resistance and scratch resistance. Can be used as a single layer flooring. As a result, even if the wooden base material for flooring used in a building is made of soft conifers of soft tree species that have been cut close to the building construction site, it is used to make it soft but hard to break. A single-layer flooring material excellent in wear and scratch resistance can be provided.

本発明の第７の発明は、第１乃至第５の発明の前記木質系床材において、前記木質基材が、複数の木質部材を貼り合わせた木質基材であることを特徴としている。第７の発明においては、木質基材は複層板材又は集成材から成る。複層板材は、ラワン材などに代表される南洋材やマツ材、スギ材、ヒノキ材などからなる合板を、繊維方向が異なるようにして、複数層重ね合わせて形成し、その表層に仕上げ突板を張設した合板である。また、集成材は、断面寸法の小さい木材を再構成したものである。これらの木質基材の表層に本発明を適用し、表層に基材強化保護層と表面保護層を設けるだけで所定の耐磨耗性及び耐傷性に優れた木質系床材を提供することができる。これにより複層板材の間に硬化層を形成するなどの複雑な構成をすることなく、安価に簡単な工程で耐磨耗性及び耐傷性に優れた複層床材を提供することができる。   According to a seventh aspect of the present invention, in the wooden flooring according to the first to fifth aspects, the wooden base material is a wooden base material obtained by bonding a plurality of wooden members. In 7th invention, a wooden base material consists of a multilayer board | plate material or a laminated material. Multi-layer boards are made of laminated plywood made of South Sea wood, pine wood, cedar wood, cypress wood, etc., typified by lauan wood, etc., with multiple layers stacked, and the finished veneer on the surface layer It is a plywood that stretches. The laminated lumber is a reconstructed wood having a small cross-sectional dimension. By applying the present invention to the surface layer of these woody base materials, and providing a base material reinforcing protective layer and a surface protective layer on the surface layer, it is possible to provide a wooden flooring material excellent in predetermined abrasion resistance and scratch resistance. it can. Thus, it is possible to provide a multi-layer flooring material excellent in wear resistance and scratch resistance by a simple and inexpensive process without forming a hardened layer between the multi-layer plate materials.

本発明の第８の発明は、第１乃至第７の発明の前記木質系床材を用いた建物である。耐磨耗性及び耐傷性の高い木質系床材を使用しているので、例えば、学校の教室又は体育館のように、机などを日常的に移動する用途に使う居室の建物に使用した場合でも、床が傷つきにくく且つ擦り減りにくい。長期間の使用によって、木質系床材の表面保護層が擦り減った場合には、表面保護層を塗り足していけば床の張替えを必要としない。これにより木質の柔軟性、木質の風合いの意匠性に加えて、耐磨耗性及び耐傷性の物性に優れた床を備えた、耐久性の高い維持管理の容易な建物を提供することができる。   An eighth invention of the present invention is a building using the wood floor material of the first to seventh inventions. Because wooden flooring with high wear resistance and scratch resistance is used, even if it is used in a building in a living room that is used for daily movement such as a classroom or gymnasium in a school, for example The floor is not easily damaged and is not easily worn away. If the surface protective layer of the wood-based flooring is worn out by long-term use, it is not necessary to replace the floor if the surface protective layer is applied. As a result, it is possible to provide a highly durable and easy-to-maintain building that has a floor with excellent wear resistance and scratch resistance in addition to the wooden flexibility and the design of the wooden texture. .

木質系床材が軟質のものであっても、木質系床材に高い耐磨耗性及び耐傷性を付与することができる。また、木質系床材が節を含んだ床材である場合であっても、節などの硬い部分だけが残り柔らかい部分だけが減ることがなく、所定の期間毎に表面保護層を塗り足すことにより、美観を復元するとともに、木質系床材を長期間使用可能とする。また、本発明の木質床材により床を構成した建物は、床仕上材がスギなどの軟質木材であっても、その耐磨耗性及び耐傷性を向上させると共に、仕上げ面が傷ついた場合であっても仕上げ状態の復元が容易で且つ耐久性が高い建物とすることができる。   Even if the wooden flooring is soft, high wear resistance and scratch resistance can be imparted to the wooden flooring. In addition, even when the wooden flooring is a flooring material that contains nodes, only hard parts such as nodes remain and only soft parts do not decrease, and a surface protective layer is added every predetermined period. As a result, the aesthetics are restored and the wooden flooring can be used for a long time. In addition, the building comprising the floor made of the wood floor material of the present invention improves the wear resistance and scratch resistance even if the floor finish material is soft wood such as cedar and the finished surface is damaged. Even if it exists, it can be set as the building where restoration of a finishing state is easy and durability is high.

図１は、単層木質基材を説明する断面図である。FIG. 1 is a cross-sectional view illustrating a single-layered wood base material. 図２は、木質系床材と塗装塗膜を説明する要部断面図である。FIG. 2 is a cross-sectional view of a main part for explaining the wooden floor material and the paint film. 図３は、単層木質系床材の斜視図である。FIG. 3 is a perspective view of a single-layer wooden flooring. 図４は、複層木質系床材を説明する断面図である。FIG. 4 is a cross-sectional view illustrating a multi-layered wood floor material. 図５は、スギを木質基材とした耐磨耗性試験の結果の写真である。FIG. 5 is a photograph of the results of an abrasion resistance test using cedar as a wooden substrate. 図６は、スギを木質基材とした耐傷性試験の結果の写真である。FIG. 6 is a photograph of the results of a scratch resistance test using cedar as a wooden substrate. 図７は、ヒノキを木質基材とした耐磨耗性試験の結果の写真である。FIG. 7 is a photograph of the results of an abrasion resistance test using cypress as a wood base material. 図８は、ヒノキを木質基材とした耐傷性試験の結果の写真である。FIG. 8 is a photograph of the results of a scratch resistance test using cypress as a woody base material.

以下、木質系床材としてスギ板、ヒノキ板を木質基材とした本発明の実施形態について、図面を参照して詳細に説明する。
（実施例１）
実施例１の木質系床材１００は、木質基材１０として無垢のスギ板を用いて長尺の単層床板としている。実施例１について、図１乃至図３を参照して説明する。図１は断面図を示し、図２は木質系床材の木質基材と塗装部の要部断面図を示し、図３は斜視図を示している。 Hereinafter, embodiments of the present invention in which cedar boards and cypress boards are used as wooden base materials as wooden floor materials will be described in detail with reference to the drawings.
Example 1
The wooden flooring 100 of Example 1 is a long single-layer floor board using a solid cedar board as the wooden base material 10. Example 1 will be described with reference to FIGS. 1 to 3. FIG. 1 shows a cross-sectional view, FIG. 2 shows a cross-sectional view of the main parts of a wooden base material and a coating portion of a wooden floor material, and FIG. 3 shows a perspective view.

まず、図１、図３を参照して実施例１の木質系床材１００を詳細に説明する。木質基材１０は、幅が約７０〜９０ｍｍ、長さが約１．８〜３．６ｍ、厚さが約１５〜１８ｍｍであり、一本のスギ材から切り出された板材である。表層には、硬い木質１１と柔らかい木質１２が交互に年輪として形成され、板目又は木目といわれる木質基材の模様が表れている。また、木質基材には、幹から伸びていた枝の跡が節１３として、木質基材本体の所々に散在している。   First, the wooden flooring 100 of the first embodiment will be described in detail with reference to FIGS. The wooden substrate 10 has a width of about 70 to 90 mm, a length of about 1.8 to 3.6 m, a thickness of about 15 to 18 mm, and is a plate material cut out from a single cedar material. On the surface layer, hard wood material 11 and soft wood material 12 are alternately formed as annual rings, and a pattern of a wood base material called a grain or wood grain appears. Further, in the wooden base material, the traces of the branches extending from the trunk are scattered as nodes 13 in various places on the main body of the wooden base material.

節１３は、木質基材本体より硬く、木質基材本体と連続性もないため、樹木の乾燥により脱落して穴を形成することがある。大きな節がある木質基材は製品としては使用されず、小さな節が脱落した穴はパテ処理により穴埋めされ、小さく且つ脱落していない節は、木質基材１０に含まれたまま、単層木質系床板１００として加工される。（図３参照）   The knots 13 are harder than the wood base body and are not continuous with the wood base body, and may fall off due to drying of the trees to form holes. A wood base material having a large node is not used as a product, and a hole from which a small node has fallen is filled by putty processing, and a small and non-dropped node is included in the wood base material 10 while being a single layer wood. It is processed as a system floor board 100. (See Figure 3)

ここで図１を参照して木質基材１０の断面形状を説明する。木質基材１０の断面形状は、その基材長辺の側面には、一方の側面に沿って雄ざね２０（図３参照）が、他方の側面には雌ざね３０（図３参照）が形成されている。木質基材の雄ざね２０は、その隣に並べられた木質基材の雌ざね３０と嵌め合わされて建物の床を構成する。雄ざね２０は木質基材１０の厚さ方向において、その厚さの略半分よりも下方に形成され、木質基材の側面から断面視において台形形状に凸部として突出している。雄ざね２０の下方の切り立ち部２１は、雄ざねの上方の切り立ち部２２よりも外方とされている。これにより、釘を打設した際に雄ざね部が割れることを防止することができる。   Here, the cross-sectional shape of the wooden substrate 10 will be described with reference to FIG. As for the cross-sectional shape of the wooden substrate 10, a male ridge 20 (see FIG. 3) is formed along one side surface on the side surface of the long side of the substrate, and a female ridge 30 (see FIG. 3) is formed on the other side surface. Has been. The wooden base male ridge 20 is fitted with the wooden base female ridge 30 arranged next to it to constitute the floor of the building. The male ridge 20 is formed below substantially half of the thickness in the thickness direction of the wooden base material 10, and protrudes from the side surface of the wooden base material as a convex portion in a trapezoidal shape in a cross-sectional view. The cut-away portion 21 below the male ridge 20 is outward from the cut-away portion 22 above the male ridge. Thereby, when a nail is nailed, a male ridge part can be prevented from cracking.

また、雄ざねの上方の切り立ち部２２の下方には、窪み溝２３が形成されて、木質系床材を床下地材に固定する釘２４の釘頭２５の格納空間とされている。これにより、その釘頭２５が前記格納空間に格納されるように、木質基材１０を図示しない根太などの下地材に釘２４を斜めに打ち込むことができる。釘２４が斜めに打ち込まれているため、床の上を人が移動して、床が上下に変形しても木質基材２０が床下地材から弛んで外れることがなく、また釘頭２５が格納空間に格納されているため、隣に並べられた木質基材１０の雌ざね部３０と干渉することがなく、高い精度で所定の位置に木質基材１０を敷き並べることができる。   In addition, a recessed groove 23 is formed below the cut portion 22 above the male ridge, and serves as a storage space for the nail head 25 of the nail 24 that fixes the wooden floor material to the floor base material. Thereby, the nail 24 can be driven diagonally into a base material such as joist (not shown) so that the nail head 25 is stored in the storage space. Since the nail 24 is driven diagonally, even if a person moves on the floor and the floor is deformed up and down, the wooden base material 20 does not loosen and come off from the floor base material, and the nail head 25 Since it is stored in the storage space, the wood base material 10 can be laid in a predetermined position with high accuracy without interfering with the female ridges 30 of the wood base material 10 arranged next to each other.

また、雌ざね部３０は前記雄ざね部２０の台形凸部形状と整合するように凹溝３１が形成されている。雄ざね部の凸部と雌ざねの凹溝は傾斜面を介して当接しているため、所定の位置に敷き並べられる際に、後から敷き並べられる木質基材の側方から軽打して加力することにより、隙間なく密着して敷き並べられる。また、雄ざね上部の切り欠き部２２の傾斜と雌ざね上部の傾斜３２は、雄ざねと雌ざねの頂部近傍で密着し、雄ざね凸部の裾部３３で離間するように、各々の切り欠き部に傾斜が形成されている。また、木質基材の突合せ頂部には、木質基材の接合部がささくれ立たないように面取り３４が形成されている。   Further, the female ridge portion 30 is formed with a concave groove 31 so as to match the trapezoidal convex shape of the male ridge portion 20. Since the convex portion of the male ridge and the concave groove of the female ridge are in contact with each other through an inclined surface, when laying in a predetermined position, lightly strike from the side of the wooden substrate laid out later. By applying force, it is placed in close contact with no gap. In addition, the slope of the notch 22 at the top of the male ridge and the slope 32 at the top of the female ridge are in close contact with each other in the vicinity of the top of the male ridge and the female ridge, and are separated from each other by the skirt 33 of the convex portion of the male ridge. A slope is formed in the notch. Further, a chamfer 34 is formed at the butt top of the wooden base material so that the joint portion of the wooden base material does not stand up.

また、木質基材１０の少なくとも室内面に、木質基材強化保護層４０及び表面保護層５０が塗装されている。なお、塗装範囲は塗装方法により異なってもよく、少なくとも室内の居室用途側に面する木質系床材１００の表面に塗装されていればよい。   Moreover, the wooden base material reinforcement | strengthening protection layer 40 and the surface protection layer 50 are painted on the indoor surface of the wooden base material 10 at least. In addition, the coating range may differ with a coating method, and should just be painted on the surface of the wooden flooring 100 facing the indoor room use side at least.

次に、実施例１で木質基材に塗装される塗料について説明する。
木質基材強化保護層をなす下地樹脂塗料としては、例えば、２液型ポリウレタン樹脂塗料とする。２液型ポリウレタン樹脂塗料以外では、湿気硬化型ポリウレタン樹脂塗料、油変性ポリウレタン樹脂塗料、不飽和ポリエステル樹脂塗料、ＵＶ硬化型塗料、フタル酸樹脂塗料、酸硬化型アミノアルキド樹脂塗料、水性塗料などを用いることができる。しかし、２液型のポリウレタン樹脂塗料は、ポリオール樹脂を主成分とする塗料主剤に、ポリイソシアネート樹脂を主成分とする硬化剤を混合することによりウレタン結合を形成し、常温で硬化が進行し、安価なうえ非常に強固で強靭な塗膜を形成することから好適である。 Next, the coating material coated on the wood base material in Example 1 will be described.
As the base resin paint that forms the wooden substrate reinforced protective layer, for example, a two-component polyurethane resin paint is used. Other than two-component polyurethane resin paints, moisture curable polyurethane resin paints, oil-modified polyurethane resin paints, unsaturated polyester resin paints, UV curable paints, phthalic acid resin paints, acid curable amino alkyd resin paints, aqueous paints, etc. Can be used. However, the two-component polyurethane resin paint forms a urethane bond by mixing a curing agent mainly composed of a polyisocyanate resin with a coating material mainly composed of a polyol resin, and curing proceeds at room temperature. It is preferable because it is inexpensive and forms a very strong and tough coating film.

さて、木材繊維としては、セルロース構造の木材繊維を有するものであればよく、例えば、木材から直接削りだした木粉、漂白処理した白色の木材繊維などを使用することができる。木材繊維の平均繊維長は３００〜２０００μｍであり、木材繊維直径は１５〜４０μｍである。なお、木材繊維の精製は、特に必要ではない。木材繊維の原料となる木質材としては、樹種や形状に特に制限はなく、木粉、木材繊維、木材チップなどの木材を粉砕したものや、セルロース、パルプなどの植物繊維を粉砕したものなどを挙げることができる。   Any wood fiber may be used as long as it has a cellulose fiber having a cellulose structure. For example, wood powder directly cut from wood, white wood fiber bleached, and the like can be used. The average fiber length of the wood fibers is 300 to 2000 μm, and the wood fiber diameter is 15 to 40 μm. Note that the purification of wood fibers is not particularly necessary. The wood material used as the raw material for wood fiber is not particularly limited in terms of tree species and shape, such as pulverized wood such as wood flour, wood fiber and wood chips, and pulverized plant fibers such as cellulose and pulp. Can be mentioned.

下地樹脂塗料に含まれている木材繊維の平均繊維長が３００〜２０００μｍであるため、塗装面に耐磨耗性及び耐傷性を付与する。平均繊維長が３００μｍ未満の場合は、十分に表面硬度を上げることができず塗装面に十分な耐磨耗性及び耐傷性を付与することが困難であり、平均繊維長が２０００μｍを超えると凸凹が大きくなり平滑性が劣ることになる。また木材繊維が下地樹脂塗料に対して０．５重量部未満である場合には床材としての表面硬度を確保することが困難になり、木材繊維が下地樹脂塗料に対して２５重量部を超える場合には塗装表面の平滑性が劣ることになる。また、木材繊維直径は１５〜４０μｍであるため、容易に平滑で硬質の塗膜を形成することができる。   Since the average fiber length of the wood fibers contained in the base resin coating is 300 to 2000 μm, wear resistance and scratch resistance are imparted to the painted surface. When the average fiber length is less than 300 μm, it is difficult to sufficiently increase the surface hardness, and it is difficult to give sufficient abrasion resistance and scratch resistance to the painted surface. Becomes larger and the smoothness becomes inferior. Further, when the wood fiber is less than 0.5 parts by weight with respect to the base resin paint, it becomes difficult to ensure the surface hardness as a flooring material, and the wood fiber exceeds 25 parts by weight with respect to the base resin paint. In this case, the smoothness of the painted surface is inferior. Moreover, since a wood fiber diameter is 15-40 micrometers, a smooth and hard coating film can be formed easily.

木質基材強化保護層４０は、前記下地塗料を３層塗りしている。塗装は、カーテンフローコーター又は吹付塗装のいずれによってもよい。乾燥塗装厚さが２５０〜４００μｍとなるように３層４１，４２，４３に分けて塗装される。この乾燥塗膜厚さが確保されれば、塗り分けの回数に制限はないが、作業性と、塗膜に発泡を生じさせないことから３層とするのが好適である。   The wood base reinforced protective layer 40 is coated with three layers of the base paint. The painting may be either a curtain flow coater or spray painting. The coating is divided into three layers 41, 42, and 43 so that the dry coating thickness is 250 to 400 μm. If this dry coating film thickness is secured, there is no limit to the number of coatings, but it is preferable to have three layers because workability and foaming of the coating film do not occur.

表面保護層５０は、下地樹脂塗料と同じ樹脂塗料とするのが好適であり、実施例１では２液型ポリウレタン樹脂塗料により表面保護層５０を塗装している。表面保護層５０は、２液型ポリウレタン樹脂塗料を２層塗り５１，５２している。１層目の下塗り５２はカーテンフローコーターにより、木質基材強化保護層を形成した木質基材全体に、偏りなく塗装される。これにより、基材強化保護層４０に含まれている木材繊維によって生じた表面の僅かな凸凹があっても、それを均一な面とすることができる。２層目の仕上げ塗り５２の塗装方法については、刷毛、ロールコーター、フローコーター、あるいは吹付けなどのいずれの塗装方法によってもよい。   The surface protective layer 50 is preferably the same resin paint as the base resin paint. In Example 1, the surface protective layer 50 is coated with a two-component polyurethane resin paint. The surface protective layer 50 is coated with two layers 51 and 52 of a two-component polyurethane resin paint. The first undercoat 52 is applied to the entire wood base material on which the wood base material reinforced protective layer is formed by a curtain flow coater. Thereby, even if there is a slight unevenness on the surface caused by the wood fibers contained in the base material reinforcing protective layer 40, it can be made a uniform surface. The coating method of the second finish coating 52 may be any coating method such as brush, roll coater, flow coater or spraying.

ここで、スギ及びヒノキを単層木質基材について、本発明の塗装を適用した木質系床材と、従来の紫外線硬化型塗料（以下ＵＶ塗装という。）又は２液性ウレタン樹脂系塗料（以下ウレタン塗装という。）を塗装した木質系床材とを形成して、その一部を試験体として比較・実施した耐磨耗性及び耐傷性試験について説明する。耐磨耗性試験としては、複合合板用の規格試験であるＪＡＳ（日本農林規格）フローリング規格磨耗性試験Ａ試験とＪＡＳフローリング規格磨耗性試験Ｂ試験とを、前記の単層板材を木質基材とし木質系床材に適用して実施した。また、耐傷性試験としては、前記木質系床材に、ＪＩＳ（日本工業規格）Ｋ５６００に基づく鉛筆硬度試験と、デュポン衝撃試験により耐衝撃性試験を行った。   Here, a cedar and a cypress are applied to a single-layer wood base material, a wood-based flooring to which the coating of the present invention is applied, and a conventional ultraviolet curable paint (hereinafter referred to as UV coating) or a two-component urethane resin-based paint (hereinafter referred to as a paint). A wear-resistant and scratch-resistant test will be described in which a wooden floor material coated with urethane coating is formed and a part of the floor is compared and implemented as a test specimen. As the abrasion resistance test, JAS (Japanese Agricultural Standards) flooring standard abrasion test A and JAS flooring standard abrasion test B test, which are standard tests for composite plywood, are used. And applied to wooden flooring. Further, as a scratch resistance test, an impact resistance test was performed on the wooden floor material by a pencil hardness test based on JIS (Japanese Industrial Standard) K5600 and a DuPont impact test.

前記Ａ試験とＢ試験について、簡単に紹介すると以下のとおりである。
・Ａ試験：
定められた試験装置の回転盤に試験体を水平に固定し、研磨紙（ＪＩＳ−Ａ１４５３）＃１８０ペーパーを巻きつけたゴム製円盤２個で５００回転を行い磨耗試験を行い、５００回転後の表面状態が試験前と著しく変化していない事と、１００回転あたりの減磨耗量が０．１５ｇｒ以下であることが合格の条件である。（通常は突板・単板が削れ、台板のベニアが露出するところを終点としているが、本試験では木質基材が露出したところを終点とした。）
・Ｂ試験：
定められた試験装置の回転盤に試験体を水平に固定し、研磨紙（ＪＩＳ−Ａ１４５３）＃１８０ペーパーを巻きつけたゴム製円盤２個で１００回転を行い磨耗試験を行い、１００回転後の表面状態が試験前と著しく変化していない事が合格の条件である。 The A test and the B test are briefly described as follows.
・ A test:
A test specimen is fixed horizontally on a rotating disk of a predetermined test apparatus, and a wear test is performed by performing 500 rotations with two rubber disks wrapped with abrasive paper (JIS-A1453) # 180 paper. The conditions for success are that the surface state is not significantly different from that before the test and that the amount of wear reduction per 100 revolutions is 0.15 gr or less. (Normally, the end point is where the veneer of the base plate is exposed when the veneer / single plate is shaved, but in this test, the end point is where the wooden substrate is exposed.)
・ B test:
A test piece is fixed horizontally on a rotating disk of a predetermined test apparatus, and a wear test is performed by performing 100 rotations with two rubber disks wound with abrasive paper (JIS-A1453) # 180 paper. The condition for success is that the surface condition has not changed significantly from that before the test.

具体的に説明すると、厚さ１５ｍｍのスギの無垢板を木質基材として、本発明の前記塗装を適用した木質系床材の実験結果の状態を、耐磨耗性について図５、耐衝撃性について図６に示し、厚さ１５ｍｍのヒノキの無垢板を木質基材として、本発明の前記塗装を適用した実験結果の状態を、耐磨耗性について図７、耐衝撃性について図８に示し、これらを参照して説明する。各図（ａ）図は、本発明を適用した試験体の実験結果の状態を、各図（ｂ）図は従来技術によるウレタン塗装を行った試験体の実験結果の状態を写真で示したものである。   Specifically, the state of the experimental results of the wood-based flooring to which the above-described coating of the present invention is applied using a solid cedar board with a thickness of 15 mm as a wooden substrate, FIG. 5 with respect to wear resistance, impact resistance FIG. 6 shows the results of an experiment in which the above-described coating of the present invention was applied using a solid wood of cypress having a thickness of 15 mm as a wooden substrate, and FIG. 8 shows the abrasion resistance and FIG. 8 shows the impact resistance. These will be described with reference to these. Each figure (a) shows the state of the experimental result of the test specimen to which the present invention was applied, and each figure (b) shows the state of the experimental result of the test specimen subjected to urethane coating according to the prior art. It is.

まず、スギを木質基材とした木質系床材について説明すると、耐磨耗性試験については、前記従来技術例のウレタン塗装をした試験体は４０回転の時点で、ＵＶ塗装をした試験体は７０回転の時点で、木質基材が露出する状態となりＢ試験不合格となった。これに対して、本発明を適用した試験体は、５００回転の時点でも木質基材が露出することなく、１００回転時点の磨耗減量が０．０８２ｇｒとなりＡ試験合格であった。また、前記鉛筆硬度試験については、前記従来技術例のウレタン塗装及びＵＶ塗装の試験体は６Ｂ以下でも凹みができるのに対して、本発明を適用した試験体は５Ｈまでは異常が無い状態であった。デュポン衝撃試験については、前記従来技術例の試験体は塗装に割れが発生したが、本発明の適用試験体については異常がなかった。（図５、図６参照）   First, the wood-based flooring using cedar as a wooden base material will be described. For the abrasion resistance test, the urethane-coated test body of the above-mentioned prior art example is 40 revolutions, and the UV-coated test body is At the time of 70 rotations, the woody base material was exposed and the B test was rejected. On the other hand, the test specimen to which the present invention was applied passed the A test with a loss of wear at 100 revolutions of 0.082 gr without exposing the wood base material even at 500 revolutions. As for the pencil hardness test, the urethane coating and UV coating specimens of the prior art example can be recessed even at 6B or less, while the specimen to which the present invention is applied is in a state of no abnormality up to 5H. there were. Regarding the DuPont impact test, the specimen of the prior art example had cracks in the coating, but the applied specimen of the present invention was not abnormal. (See FIGS. 5 and 6)

次に、ヒノキを木質基材とした木質系床材について説明すると、耐磨耗性試験については、前記従来技術例のウレタン塗装をした試験体は３０回転の時点で、ＵＶ塗装をした試験体は１００回転の時点で、木質基材が露出する状態となりＢ試験不合格となった。これに対して、本発明を適用した試験体は、８００回転の時点でも木質基材が露出することなく、１００回転時点の磨耗減量が０．０８６ｇｒとなりＡ試験合格であった。また、前記鉛筆硬度試験については、前記従来技術例のウレタン塗装及びＵＶ塗装の試験体は６Ｂ以下でも凹みができるのに対して、本発明を適用した試験体は５Ｈまでは異常が無い状態であった。デュポン衝撃試験については、前記従来技術例の試験体は塗装に割れが発生したが、本発明の適用試験体については異常がなかった。（図７、図８参照）   Next, a wooden floor material using cypress as a wooden base material will be described. For the abrasion resistance test, the urethane-coated test specimen of the above-mentioned prior art example is a UV-coated test specimen at 30 revolutions. At 100 revolutions, the woody substrate was exposed and the B test was rejected. On the other hand, the test specimen to which the present invention was applied passed the A test with a loss of wear at 100 revolutions of 0.086 gr without exposing the wooden substrate even at 800 revolutions. As for the pencil hardness test, the urethane coating and UV coating specimens of the prior art example can be recessed even at 6B or less, while the specimen to which the present invention is applied is in a state of no abnormality up to 5H. there were. Regarding the DuPont impact test, the specimen of the prior art example had cracks in the coating, but the applied specimen of the present invention was not abnormal. (See Figs. 7 and 8)

上記の試験の比較結果をまとめて下記表１に示した。表１にまとめたように、本発明を適用した試験体は、従来技術によるウレタン塗装及びＵＶ塗装をした試験体と比較して、耐磨耗性及び耐傷性いずれの点においても優れた結果が得られた。
The comparison results of the above tests are summarized in Table 1 below. As summarized in Table 1, the specimens to which the present invention was applied showed superior results in both wear resistance and scratch resistance compared to the specimens subjected to urethane coating and UV coating according to the prior art. Obtained.

（実施例２）
実施例２では、表層仕上単板６１を下地合板６２〜６６に張り付けた複層木質系床材６０を、図２及び図４を参照して説明する。合板としては、たとえば、ラワン材などに代表される南洋材やマツ材、スギ材、ヒノキ材などからなる合板を挙げることができ、繊維方向が異なる単板を一層毎に複数層、たとえば、３層、５層、７層を配置したものであって、表層の繊維方向が合板の長手方向と平行に構成されたもの、あるいは、表層の繊維方向が合板の長手方向と直交する方向に構成されたものの、いずれであってもよい。実施例２では５層を配置した例を示している（図４参照）が、層数に限定がないことは勿論のことである。 (Example 2)
In Example 2, a multilayer wooden flooring 60 in which a surface layer finished single plate 61 is attached to base plywoods 62 to 66 will be described with reference to FIGS. 2 and 4. As the plywood, for example, plywood made of South Sea wood, pine wood, cedar wood, cypress wood, and the like typified by lauan wood can be mentioned. Layers, 5 layers, and 7 layers, wherein the fiber direction of the surface layer is configured in parallel with the longitudinal direction of the plywood, or the fiber direction of the surface layer is configured in a direction orthogonal to the longitudinal direction of the plywood. However, either may be sufficient. In the second embodiment, an example in which five layers are arranged (see FIG. 4) is shown, but it goes without saying that the number of layers is not limited.

実施例２においては、表層の突板６１は２．５ｍｍの厚さであり、下地合板を成す５層６２〜６６の各層も２．５ｍｍであり、木質基材の厚さとしては１５ｍｍである（図４参照）。その木質基材に、木質基材強化保護層４０と表面保護層５０を形成している点については、実施例１と同様である。実施例１と同様に、図２に参照されるように、表層仕上単板に３層の木質基材強化保護層４１，４２，４３と２層の表面保護層５１，５２を塗装により形成している。塗料の材質、木質繊維などの構成についても実施例１と同様であるので、説明を省略する。   In Example 2, the protruding plate 61 of the surface layer has a thickness of 2.5 mm, each of the five layers 62 to 66 constituting the base plywood is also 2.5 mm, and the thickness of the wooden substrate is 15 mm ( (See FIG. 4). The point that the wood base material reinforced protective layer 40 and the surface protective layer 50 are formed on the wood base material is the same as in Example 1. As in Example 1, as shown in FIG. 2, three layers of woody substrate reinforced protective layers 41, 42, 43 and two surface protective layers 51, 52 were formed on the surface finished veneer by painting. ing. Since the configuration of the material of the coating material, the wood fiber, etc. is the same as that of the first embodiment, the description thereof is omitted.

（実施例３）
実施例３では、学校の体育館の床材に、実施例１で説明した木質系床材１００を張っている。学校の体育館の床は、生徒が体育授業において跳び箱を移動させ、行事の際に椅子を配置し移動させるため傷がつきやすい。しかし、本発明を適用すれば、床は傷つきにくく、且つ擦り減りにくく耐久性が向上する。そして、その使用状況に応じて、例えば３年毎に表層塗装５０を塗り足すことにより、床の意匠性も維持することができる。 Example 3
In Example 3, the wooden flooring 100 described in Example 1 is stretched on the flooring of a school gymnasium. The floor of the school gymnasium is easily scratched because students move jump boxes in physical education classes and place and move chairs during events. However, if the present invention is applied, the floor is less likely to be scratched and less likely to be worn away, thereby improving durability. And according to the use condition, the design property of a floor can also be maintained, for example by applying the surface coating 50 every 3 years.

（その他の実施例）
・上記の実施例は、床材として説明したが、床に限定するものではなく、例えば人が出入りし、物を搬入する際に擦り傷を発生させる可能性のある壁に使用することもできる。
・上記の実施例は、スギ、ヒノキの実施例で説明したが、木質基材を成す樹種は針葉樹に限定する必要はなく、硬質の木質基材である場合には、更に木質基材に耐磨耗性及び耐傷性を付与するのは勿論のことである。
・実施例２の複層床材の木質基材に、中密度繊維板（ＭＤＦ）やパーティクルボードなどの他の木質基材と積層した複合板を用いることもできる。また、垂直方向に木片を積層した集成材であってもよい。
・実施例３では体育館の床に使用する実施例を説明したが、体育館に限定されず教室の床、住宅の床や商店など、建物の用途に限らず本発明が適用できることは勿論のことである。
・なお、本発明は上記各実施例に限定されず、本発明の技術思想の範囲内において、各実施例は適宜変更され得ることは明らかである。 (Other examples)
Although the above embodiment has been described as a flooring material, the present invention is not limited to a flooring material, and can be used for a wall that may cause a scratch when a person enters and exits and loads an object, for example.
-Although the above-mentioned examples have been described in the examples of cedar and cypress, the tree species forming the wood base material need not be limited to conifers. Of course, wear and scratch resistance are imparted.
-The composite board laminated | stacked with other wooden base materials, such as a medium density fiber board (MDF) and a particle board, can also be used for the wooden base material of the multilayer flooring of Example 2. FIG. Moreover, the laminated material which laminated | stacked the wood piece in the perpendicular direction may be sufficient.
-Although Example 3 demonstrated the Example used for the floor of a gymnasium in Example 3, it is needless to say that this invention is applicable not only to the use of buildings, such as a classroom floor, a house floor, and a shop, but is not limited to a gymnasium. .
The present invention is not limited to the above-described embodiments, and it is obvious that each embodiment can be appropriately changed within the scope of the technical idea of the present invention.

１００…木質系床材、
１０…単層木質基材、
４０…木質基材強化保護層、
５０…表面保護層、
６０…複層木質基材、
２０…雄ざね部、
３０…雌ざね部、
１１…硬い木質、１２…柔らかい木質、１３…節、
２１…下方の切り立ち部、２２…上方の切り立ち部、２３…窪み溝、
２４…釘、２５…釘頭、
３１…凹溝、３２…雌ざね上部の傾斜、３３…裾部、
３４…面取り、
４１，４２，４３…木質基材強化保護層の各層、
５１，５２…表面保護層の各層、
６１…表層の突板、６２，６３，６４，６５，６６…合板の各層 100 ... Wooden flooring,
10: Single-layer woody base material,
40 ... wooden substrate reinforced protective layer,
50 ... Surface protective layer,
60 ... Multi-layer woody base material,
20 ... male ridge,
30 ... Female ridge,
11 ... Hard wood, 12 ... Soft wood, 13 ... Section,
21 ... Lower cut-out portion, 22 ... Upper cut-out portion, 23 ... Recessed groove,
24 ... nails, 25 ... nail heads,
31 ... concave groove, 32 ... slope of upper part of female ridge, 33 ... hem part,
34 ... Chamfering,
41, 42, 43 ... each layer of the wood substrate reinforced protective layer,
51, 52 ... each layer of the surface protective layer,
61 ... Surface protrusions, 62, 63, 64, 65, 66 ... Plywood layers

Claims (8)

木質基材と、前記木質基材に塗装された木質基材強化保護層と、前記木質基材強化保護層に塗装された表面保護層と、を含む木質系床材であって、
前記木質基材強化保護層が、少なくとも前記木質基材の室内面側に、平均繊維長３００〜２０００μｍのセルロース構造の木材繊維を０．５〜２５重量部を含んだ下地樹脂塗料を塗装したことにより形成されている、
ことを特徴とする木質系床材。 A wood-based flooring material comprising a wood base material, a wood base material reinforced protective layer painted on the wood base material, and a surface protective layer painted on the wood base material reinforced protective layer,
The wooden substrate reinforced protective layer is coated with a base resin coating containing 0.5 to 25 parts by weight of wood fibers having an average fiber length of 300 to 2000 μm on the indoor surface side of the wooden substrate. Formed by,
This is a wooden flooring. 前記下地樹脂塗料がウレタン樹脂系塗料である、ことを特徴とする請求項１に記載の木質系床材。   The wood-based flooring material according to claim 1, wherein the base resin coating material is a urethane resin-based coating material. 前記木質基材強化保護層の乾燥状態膜厚さが２５０〜４００μｍである、ことを特徴とする請求項１又は請求項２に記載の木質系床材。   The woody flooring according to claim 1 or 2, wherein the dry thickness of the woody substrate reinforced protective layer is 250 to 400 µm. 前記木質基材強化保護層が少なくとも２層からなる、ことを特徴とする請求項１乃至請求項３のいずれか１項に記載の木質系床材。   The woody flooring material according to any one of claims 1 to 3, wherein the woody substrate reinforcing protective layer comprises at least two layers. 前記表面保護層がウレタン樹脂系塗料であり、乾燥塗膜厚さが６０〜１００μｍである、ことを特徴とする請求項１乃至請求項４のいずれか１項に記載の木質系床材。   The woody flooring according to any one of claims 1 to 4, wherein the surface protective layer is a urethane resin-based paint, and a dry coating thickness is 60 to 100 µm. 前記木質基材が無垢板である、ことを特徴とする請求項１乃至請求項５のいずれか１項に記載の木質系床材。   The wooden flooring material according to any one of claims 1 to 5, wherein the wooden base material is a solid board. 前記木質基材が、複数の木質部材を貼り合わせた木質基材である、ことを特徴とする請求項１乃至請求項５のいずれか１項に記載の木質系床材。   The woody flooring material according to any one of claims 1 to 5, wherein the woody base material is a woody base material in which a plurality of wood members are bonded together. 前記請求項１乃至請求項７のいずれか１項に記載の木質系床材を用いた、ことを特徴とする建物。   A building using the wooden flooring material according to any one of claims 1 to 7.