JP2012001792A - Rust prevention composition and rust prevention film using the same - Google Patents
Rust prevention composition and rust prevention film using the same Download PDFInfo
- Publication number
- JP2012001792A JP2012001792A JP2010139826A JP2010139826A JP2012001792A JP 2012001792 A JP2012001792 A JP 2012001792A JP 2010139826 A JP2010139826 A JP 2010139826A JP 2010139826 A JP2010139826 A JP 2010139826A JP 2012001792 A JP2012001792 A JP 2012001792A
- Authority
- JP
- Japan
- Prior art keywords
- rust
- rust preventive
- film
- silicate
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、金属に対して防錆作用を有する防錆組成物およびこれを用いた防錆フィルムに関する。 The present invention relates to a rust preventive composition having a rust preventive action on metals and a rust preventive film using the same.
気相中に存在する金属体の腐食は、空気中に存在する気体状の水分（水蒸気）が金属の表面に吸着することにより発生及び進行する。空気中から水蒸気を完全に除去することは困難であるため、金属体の表面を腐食から保護するための処理が必要となる。 Corrosion of the metal body existing in the gas phase is generated and proceeds by the adsorption of gaseous moisture (water vapor) existing in the air on the surface of the metal. Since it is difficult to completely remove water vapor from the air, a treatment for protecting the surface of the metal body from corrosion is required.
気相中で防錆効果を発揮するものには、例えば気化性防錆剤がある。この気化性防錆剤は、例えば樹脂フィルムに練り込まれ、防錆フィルムとして用いられる。この防錆フィルムで金属体を包装すると、フィルムに含有された気化性防錆剤が包装内部に気散して防錆剤が金属体の表面に付着し、皮膜を形成する。この皮膜により、気相中の水分や酸素を遮断し、防錆効果が発揮される。 For example, there are vaporizable rust preventives that exhibit a rust preventive effect in the gas phase. This vaporizable rust preventive is kneaded into a resin film, for example, and used as a rust preventive film. When the metal body is packaged with this rust-proof film, the vaporizable rust preventive agent contained in the film is diffused inside the package and the rust preventive agent adheres to the surface of the metal body to form a film. By this film, moisture and oxygen in the gas phase are blocked, and the antirust effect is exhibited.
しかし、温度及び湿度の変化が激しい環境下に金属が晒された場合、金属の表面に結露水が発生することがあり（特に防錆フィルムと金属との接触部分は、毛細管現象により結露水が発生しやすい）、その部分が腐食してしまう。従って、結露水のような液体状の水分が金属表面に接触した状態においても腐食を防止する必要がある。 However, when the metal is exposed to an environment where the temperature and humidity change drastically, condensed water may be generated on the surface of the metal (especially the contact portion between the rust-proof film and the metal may be condensed due to capillary action). It tends to occur) and the part is corroded. Therefore, it is necessary to prevent corrosion even in a state where liquid water such as condensed water is in contact with the metal surface.
それ故に、本発明では、気体状の水分（水蒸気）に対してだけでなく、液体状の水分が付着した場合でも防錆効果を発揮できる防錆組成物およびそれを用いた防錆フィルムを提供することを目的とする。 Therefore, the present invention provides a rust preventive composition capable of exhibiting a rust preventive effect not only with respect to gaseous moisture (water vapor) but also when liquid moisture adheres, and a rust preventive film using the same. The purpose is to do.
本発明は、防錆作用を有する防錆組成物に関するものである。防錆組成物は、少なくとも１種類の防錆剤と、オルトケイ酸ナトリウム以外の少なくとも１種類のケイ酸塩とを含む。 The present invention relates to a rust preventive composition having a rust preventive action. The rust preventive composition contains at least one rust preventive agent and at least one silicate other than sodium orthosilicate.
また、本発明は、防錆フィルムに関する。防錆フィルムは、樹脂フィルムと、樹脂フィルムに含有される少なくとも１種類の防錆剤と、樹脂フィルムに含有される、オルトケイ酸ナトリウム以外の少なくとも１種類のケイ酸塩と、樹脂フィルムに含有される不飽和脂肪酸アミドとを備える。 The present invention also relates to a rust prevention film. The rust preventive film is contained in the resin film, at least one rust preventive agent contained in the resin film, at least one silicate other than sodium orthosilicate contained in the resin film, and the resin film. An unsaturated fatty acid amide.
本発明に係る防錆組成物は、ケイ酸塩が水に溶解して金属体の表面に防錆剤の皮膜及び不動態皮膜を形成するので、防錆対象となる金属体が吸着水や結露水に接触した場合でも防錆作用を発揮することができる。 In the rust preventive composition according to the present invention, the silicate dissolves in water to form a rust preventive film and a passive film on the surface of the metal body. Even when it comes into contact with water, it can exhibit an anti-rust effect.
本発明の実施形態に係る防錆組成物は、鉄、銅、アルミニウム等の単体または組み合わせよりなる金属部品や金属製品（以下、単に「金属体」という）の表面を防錆するために用いられる。この防錆組成物を用いるには、例えば、防錆組成物を溶媒に溶かして、金属体を収容する容器の内面への塗布、樹脂フィルムへの塗布又は練り込み、紙・木材・不織布への含侵・塗布・すき込み等、様々な方法がある。 The rust preventive composition according to the embodiment of the present invention is used to rust prevent the surface of a metal part or metal product (hereinafter simply referred to as “metal body”) made of a simple substance or a combination of iron, copper, aluminum and the like. . In order to use this rust preventive composition, for example, the rust preventive composition is dissolved in a solvent, applied to the inner surface of a container containing a metal body, applied to a resin film or kneaded, applied to paper, wood or nonwoven fabric. There are various methods such as impregnation, application and penetration.
防錆組成物は、少なくとも１種類の防錆剤と、オルトケイ酸ナトリウム以外の少なくとも１種類のケイ酸塩とを含む。また防錆組成物は、防錆助剤として不飽和脂肪酸アミドを含むことが好ましい。 The rust preventive composition contains at least one rust preventive agent and at least one silicate other than sodium orthosilicate. Moreover, it is preferable that an antirust composition contains unsaturated fatty acid amide as an antirust agent.
防錆組成物を樹脂フィルムに練り込んで作製される防錆フィルムは、樹脂フィルムと、少なくとも１種類の防錆剤と、オルトケイ酸ナトリウム以外の少なくとも１種類のケイ酸塩と、不飽和脂肪酸アミドとを備える。尚、樹脂フィルムには、例えばポリエチレンやポリプロピレン等、フィルム状に形成できる様々な樹脂を用いることができる。 A rust-proof film produced by kneading a rust-proof composition into a resin film comprises a resin film, at least one rust-proofing agent, at least one silicate other than sodium orthosilicate, and an unsaturated fatty acid amide. With. In addition, various resin which can be formed in film shape, such as polyethylene and a polypropylene, can be used for a resin film, for example.
防錆剤は、例えば、安息香酸ナトリウムや安息香酸アンモニウムのような安息香酸塩、有機アミン−安息香酸塩（ジイソプロピルアミン-安息香酸塩、ジベンジルアミン-安息香酸塩、シクロヘキシルアミン-安息香酸塩など）、亜硝酸ナトリウム、亜硝酸カリウム、亜硝酸カルシウム、亜硝酸マグネシウム又はジシクロヘキシルアンミニウム亜硝酸塩又はジイソプロピルアンモニウム亜硝酸塩のような亜硝酸塩、ベンゾトリアゾールを使用できる。 Examples of rust preventives include benzoates such as sodium benzoate and ammonium benzoate, organic amine-benzoates (diisopropylamine-benzoate, dibenzylamine-benzoate, cyclohexylamine-benzoate, etc. ), Nitrites such as sodium nitrite, potassium nitrite, calcium nitrite, magnesium nitrite or dicyclohexylammonium nitrite or diisopropylammonium nitrite, benzotriazole.
ケイ酸塩は、例えば、ケイ酸リチウム、ケイ酸ナトリウム、ケイ酸カリウム、ケイ酸カルシウム、ケイ酸バリウムを使用することができ、特に、ケイ酸ナトリウムを好適に用いることができる。尚、本明細書において、ケイ酸ナトリウムとは、オルトケイ酸ナトリウム以外のケイ酸ナトリウムであって、例えば、メタケイ酸ナトリウムやメタ二ケイ酸ナトリウムである。 As the silicate, for example, lithium silicate, sodium silicate, potassium silicate, calcium silicate, and barium silicate can be used. In particular, sodium silicate can be preferably used. In this specification, sodium silicate is sodium silicate other than sodium orthosilicate, and is, for example, sodium metasilicate or sodium metadisilicate.
不飽和脂肪酸アミドは、例えば、クロトン酸アミド、バルトミン酸アミド、オレイン酸アミド、エライジン酸アミド、バクセン酸アミド、ガドレイン酸アミド、エイコセン酸アミド、エルカ酸アミド、リノール酸アミド、リノレン酸アミドを使用できる。 As the unsaturated fatty acid amide, for example, crotonic acid amide, baltimic acid amide, oleic acid amide, elaidic acid amide, vaccenic acid amide, gadoleic acid amide, eicosenoic acid amide, erucic acid amide, linoleic acid amide, linolenic acid amide can be used. .
防錆剤は、気化して、金属体の表面に物理的又は化学的に可逆吸着することにより皮膜を形成する。また、防錆剤が溶解した水溶液に接触する金属体の表面にも皮膜が形成される。これら防錆剤の皮膜は、水分や酸素が金属体の表面へ接触することを抑制し、金属体に対して防錆効果を発揮する。 The rust inhibitor vaporizes and forms a film by reversibly adsorbing physically or chemically on the surface of the metal body. Moreover, a film is also formed on the surface of the metal body that comes into contact with the aqueous solution in which the rust inhibitor is dissolved. These rust preventive coatings inhibit moisture and oxygen from coming into contact with the surface of the metal body and exhibit a rust preventive effect on the metal body.
ケイ酸塩は、水に溶解してアルカリ水溶液となる。アルカリ水溶液に接触した金属体の表面には、緻密な酸化膜である不動態皮膜が形成される。この不動態皮膜は、水や酸素が不動態皮膜の内部の金属体の表面に接触することを効果的に抑制し、金属体に対する防錆効果が発揮される。 Silicate is dissolved in water to become an alkaline aqueous solution. A passive film, which is a dense oxide film, is formed on the surface of the metal body in contact with the alkaline aqueous solution. This passive film effectively suppresses water and oxygen from coming into contact with the surface of the metal body inside the passive film, and exhibits a rust preventive effect on the metal body.
また、水溶液がアルカリ性である場合、防錆剤の溶解度を高めることができる。防錆剤の溶解量が多いほど、水溶液に接触する金属体の表面に対する防錆効果が高くなる。このように、防錆剤及びケイ酸塩を共存させることで、防錆剤による防錆効果が助長されるという効果を奏する。 Moreover, when aqueous solution is alkaline, the solubility of a rust preventive agent can be improved. The more the amount of the rust inhibitor dissolved, the higher the rust prevention effect on the surface of the metal body in contact with the aqueous solution. Thus, there exists an effect that the rust prevention effect by a rust inhibitor is promoted by making a rust inhibitor and a silicate coexist.
金属体を防錆フィルムで包装した場合には、温度や湿度の変化により、包装内部の金属体の表面に吸着水が発生し、更に、金属体と防錆フィルムとの接触部分には結露水が発生する。ケイ酸塩は、防錆フィルムから防錆剤が包装内部に気化する際に同時に運ばれて金属体表面の吸着水や結露水に溶解したり、防錆フィルムから直接結露水に溶解したりして、金属体の表面に不動態皮膜を形成する。このように、ケイ酸塩によって、吸着水や結露水に接触する金属体に対しても防錆効果が発揮される。 When a metal body is packaged with a rust-proof film, adsorbed water is generated on the surface of the metal body inside the package due to changes in temperature and humidity, and dew condensation water is generated at the contact portion between the metal body and the rust-proof film. Will occur. Silicates are transported from the rust preventive film at the same time when the rust preventive agent is vaporized inside the package, and dissolved in the adsorbed water and condensed water on the metal surface, or dissolved directly in the condensed water from the rust preventive film. Then, a passive film is formed on the surface of the metal body. Thus, the rust-proofing effect is exerted on the metal body that comes into contact with the adsorbed water or the condensed water by the silicate.
更に、防錆組成物に不飽和脂肪酸アミドが含まれる場合、防錆剤と不飽和脂肪酸アミドとの間で反応が起こり、防錆剤の成分が外部に放出される。このように、防錆剤の気化性が促進されることで、防錆剤の防錆効果が助長される。特に、防錆組成物を樹脂成形品に練り込んだ形態の防錆フィルムにおいては、包装した金属体を防錆するには、防錆フィルムに含まれる防錆剤を外部に気化させる必要があるため、防錆組成物に不飽和脂肪酸アミドを加えることが、防錆剤の防錆効果を助長するのに特に有効となる。 Furthermore, when an unsaturated fatty acid amide is contained in the rust preventive composition, a reaction occurs between the rust preventive and the unsaturated fatty acid amide, and the components of the rust preventive are released to the outside. Thus, the rust preventive effect of a rust preventive agent is promoted by promoting the vaporization property of a rust preventive agent. In particular, in the case of a rust preventive film in which a rust preventive composition is kneaded into a resin molded product, it is necessary to vaporize the rust preventive agent contained in the rust preventive film to rust the packaged metal body. Therefore, adding an unsaturated fatty acid amide to the rust preventive composition is particularly effective for promoting the rust preventive effect of the rust preventive agent.
以上説明したように、本実施形態に係る防錆組成物及び防錆フィルムによれば、防錆剤とケイ酸塩と相乗効果により、気相中の水分のみならず、温度変化によって生じる吸着水や結露水に対しても効果的に金属体を防錆し、かつ、防錆効果の持続時間を向上させることが可能となる。また、複数種類の金属に対する防錆作用を有する防錆剤を使用することで、金属部品や金属製品に含まれる複数種類の金属に対して同時に防錆効果を発揮することができる。 As described above, according to the rust preventive composition and the rust preventive film according to the present embodiment, due to the synergistic effect with the rust preventive agent and the silicate, not only the moisture in the gas phase but also the adsorbed water generated by the temperature change. It is possible to effectively rust the metal body even against dew condensation water and to improve the duration of the rust prevention effect. In addition, by using a rust inhibitor having a rust preventive action on a plurality of types of metals, a rust prevention effect can be exerted simultaneously on a plurality of types of metals contained in metal parts and metal products.
以下、本発明を具体的に実施した実施例について説明する。尚、実施例１及び比較例１〜３では防錆組成物を蒸留水に溶解させて用い、実施例２及び比較例４〜６では防錆組成物を樹脂フィルムに含有させて用いた。 Examples in which the present invention is specifically implemented will be described below. In Example 1 and Comparative Examples 1 to 3, the rust preventive composition was dissolved in distilled water and used, and in Example 2 and Comparative Examples 4 to 6, the rust preventive composition was used in a resin film.
（実施例１）
実施例１に係る防錆組成物は、安息香酸ナトリウムとメタケイ酸ナトリウムを１対１の重量比で配合したものである。蒸留水１００ｍｌに対して、０．００１重量％、０．０１重量％、０．１重量％の防錆組成物を添加し、３種類の水溶液を作製した。
Example 1
The rust preventive composition according to Example 1 is a mixture of sodium benzoate and sodium metasilicate in a weight ratio of 1: 1. 0.001% by weight, 0.01% by weight, and 0.1% by weight of an antirust composition were added to 100 ml of distilled water to prepare three types of aqueous solutions.
（比較例１）
比較例１では安息香酸ナトリウムのみを用いた。蒸留水１００ｍｌに対して、０．００１重量％、０．０１重量％、０．１重量％の安息香酸ナトリウムを添加し、３種類の水溶液を作製した。
(Comparative Example 1)
In Comparative Example 1, only sodium benzoate was used. 0.001 wt%, 0.01 wt%, and 0.1 wt% sodium benzoate were added to 100 ml of distilled water to prepare three types of aqueous solutions.
（比較例２）
比較例２ではメタケイ酸ナトリウムのみを用いた。蒸留水１００ｍｌに対して、０．００１重量％、０．０１重量％、０．１重量％のケイ酸ナトリウムを添加し、３種類の水溶液を作製した。
(Comparative Example 2)
In Comparative Example 2, only sodium metasilicate was used. 0.001 wt%, 0.01 wt%, and 0.1 wt% sodium silicate were added to 100 ml of distilled water to prepare three types of aqueous solutions.
（比較例３）
比較例３では、蒸留水のみを用いた。
(Comparative Example 3)
In Comparative Example 3, only distilled water was used.
ガラス瓶に実施例１及び比較例１〜３の水溶液を満たし、その中に、３０×４０×３ｍｍの鉄製プレート、銅製プレート及びアルミニウム製プレートを浸漬した。その後、ガラス瓶を密封し、２５℃の環境下で放置した。そして、所定期間経過後、各プレートを水溶液から取り出し、表面を目視観察し、[○：腐食なし、△：僅かに腐食、×：腐食有り]で評価した。各実施例及び各比較例の試験結果を、プレートの種類及び蒸留水に対する防錆組成物の重量％毎に表１〜９に示す。 A glass bottle was filled with the aqueous solutions of Example 1 and Comparative Examples 1 to 3, and a 30 × 40 × 3 mm iron plate, copper plate, and aluminum plate were immersed therein. Thereafter, the glass bottle was sealed and left in an environment of 25 ° C. Then, after elapse of a predetermined period, each plate was taken out from the aqueous solution, and the surface was visually observed, and evaluated by [◯: no corrosion, Δ: slight corrosion, x: corrosion). The test result of each Example and each comparative example is shown to Tables 1-9 for every weight% of the rust prevention composition with respect to the kind of plate and distilled water.
表１〜３には、実施例１及び比較例１〜３の水溶液に鉄製プレートを浸漬した結果を示す。 Tables 1 to 3 show the results of immersing the iron plate in the aqueous solutions of Example 1 and Comparative Examples 1 to 3.
表４〜６には、実施例１及び比較例１〜３の水溶液に銅製プレートを浸漬した結果を示す。 Tables 4 to 6 show the results of immersing the copper plate in the aqueous solutions of Example 1 and Comparative Examples 1 to 3.
表７〜９には、実施例１及び比較例１〜３の水溶液にアルミニウム製プレートを浸漬した結果を示す。 Tables 7 to 9 show the results of immersing aluminum plates in the aqueous solutions of Example 1 and Comparative Examples 1 to 3.
表１〜９を参照して、実施例１と比較例１〜３とを比較すると、安息香酸ナトリウムと、メタケイ酸ナトリウムとを併用した実施例では、比較例に比べて、水溶液中の全ての金属プレート（鉄、銅及びアルミニウム）に対する防錆効果の持続期間が長くなることが確認された。特に、防錆組成物の添加量が０．０１重量％以上の場合、比較例１〜３の防錆効果の持続期間が１週間〜１ヶ月であるのに対して、実施例１では１年以上の長期に渡り防錆効果を発揮しており、防錆剤とケイ酸ナトリウムとの相乗効果が確認された。 With reference to Tables 1-9, when Example 1 and Comparative Examples 1-3 are compared, in the Example which used sodium benzoate and sodium metasilicate together, compared with a comparative example, all the solutions in aqueous solution were compared. It was confirmed that the duration of the rust prevention effect on the metal plate (iron, copper and aluminum) was increased. In particular, when the addition amount of the rust preventive composition is 0.01% by weight or more, the duration of the rust preventive effect of Comparative Examples 1 to 3 is 1 week to 1 month, whereas Example 1 is 1 year. The antirust effect was demonstrated over the above long period, and the synergistic effect of the antirust agent and sodium silicate was confirmed.
（実施例２）
実施例２に係る防錆組成物は、安息香酸ナトリウムとメタケイ酸ナトリウムとオレイン酸アミドとを１対１対１の重量比で配合したものである。この防錆組成物を樹脂フィルムに含有させて防錆フィルムを作製した。具体的には、まず、低密度ポリエチレンと安息香酸ナトリウムの重量比が１００対２０であるマスターバッチと、低密度ポリエチレンとメタケイ酸ナトリウムの重量比が１００対２０であるマスターバッチと、低密度ポリエチレンとオレイン酸アミドの重量比が１００対２０であるマスターバッチとを作製した。そして、低密度ポリエチレンにこれらのマスターバッチの添加量を変えて混練し、押出し成形により、低密度ポリエチレンに対する安息香酸ナトリウムの添加比率が、１重量％、０．１重量％、０．０１重量％となる３種類の防錆フィルムを作製した。
(Example 2)
The rust preventive composition according to Example 2 is obtained by blending sodium benzoate, sodium metasilicate, and oleic amide at a weight ratio of 1: 1 to 1: 1. This rust preventive composition was contained in a resin film to produce a rust preventive film. Specifically, first, a masterbatch in which the weight ratio of low density polyethylene to sodium benzoate is 100: 20, a masterbatch in which the weight ratio of low density polyethylene to sodium metasilicate is 100: 20, and low density polyethylene And a master batch in which the weight ratio of oleic amide is 100: 20. Then, the addition amount of these master batches is kneaded into low density polyethylene, and the addition ratio of sodium benzoate to low density polyethylene is 1% by weight, 0.1% by weight, 0.01% by weight by extrusion molding. Three types of rust preventive films were prepared.
（比較例４）
比較例４では安息香酸ナトリウムのみを樹脂フィルムに含有させて防錆フィルムを作製した。具体的には、低密度ポリエチレンと安息香酸ナトリウムの重量比が１００対２０であるマスターバッチを作製し、低密度ポリエチレンとマスターバッチの比率を変えて混練し、押出成形により、低密度ポリエチレンに対する安息香酸ナトリウムの濃度が、１重量％、０．１重量％、０．０１重量％となる３種類の防錆フィルムを作製した。
(Comparative Example 4)
In Comparative Example 4, a rust preventive film was prepared by containing only sodium benzoate in the resin film. Specifically, a masterbatch in which the weight ratio of low density polyethylene to sodium benzoate is 100: 20 is prepared, kneaded by changing the ratio of the low density polyethylene and masterbatch, and benzoa to the low density polyethylene by extrusion molding. Three types of rust preventive films having a sodium acid concentration of 1% by weight, 0.1% by weight, and 0.01% by weight were produced.
（比較例５）
比較例５ではメタケイ酸ナトリウムのみを樹脂フィルムに含有させて防錆フィルムを作製した。具体的には、低密度ポリエチレンとメタケイ酸ナトリウムの重量比が１００対２０であるマスターバッチを作製した。そして、低密度ポリエチレンとマスターバッチの比率を変えて混練し、押出成形により、低密度ポリエチレンに対するメタケイ酸ナトリウムの濃度が、１重量％、０．１重量％、０．０１重量％となる３種類の防錆フィルムを作製した。
(Comparative Example 5)
In Comparative Example 5, a rust preventive film was prepared by containing only sodium metasilicate in the resin film. Specifically, a master batch in which the weight ratio of low density polyethylene to sodium metasilicate was 100: 20 was prepared. Then, the ratio of the low density polyethylene and the master batch is changed and kneaded, and by extrusion molding, the concentration of sodium metasilicate with respect to the low density polyethylene becomes 1% by weight, 0.1% by weight, and 0.01% by weight. An anticorrosive film was prepared.
（比較例６）
比較例６では、低密度ポリエチレン単体を押出成形したフィルムを用いた。
(Comparative Example 6)
In Comparative Example 6, a film obtained by extrusion molding a low density polyethylene simple substance was used.
実施例２及び比較例４〜６の防錆フィルムは、押出時にインフレーション成膜することにより、厚み１００μｍ、径６００ｍｍのチューブ形状に成形した。作製した各チューブの内部に鉄製、銅製及びアルミニウム製の金属部品を入れ、端部をヒートシールにより封止した。その後、金属部品の表面に結露が発生するように、「温度１５℃・湿度５０％の環境下で６時間放置、その後、温度５０℃・湿度９５％の環境下で６時間放置」を１サイクルとして、繰り返しのサイクル試験を実施した。所定回数のサイクルを経た後、防錆フィルムから各金属部品を取り出し、表面の腐食の発生を目視観察し、上記サイクルにおいて、金属部品の表面において、気相に晒された箇所（以下「気相部」という）と、結露水が発生した箇所（以下「液接触部」という）とについて、夫々の表面状態を目視観察し、[○：腐食なし、×：腐食有り]で評価した。実施例及び各比較例の試験結果を、防錆フィルムに対する安息香酸ナトリウム（比較例５ではケイ酸ナトリウム）の重量％毎に表１０、１１及び１２に示す。尚、表１０〜１２では、腐食が生じたサンプルについての結果を示している。 The rust preventive films of Example 2 and Comparative Examples 4 to 6 were formed into a tube shape having a thickness of 100 μm and a diameter of 600 mm by forming an inflation film during extrusion. Metal parts made of iron, copper, and aluminum were placed inside each of the produced tubes, and the ends were sealed by heat sealing. Then, one cycle of “Leave for 6 hours in an environment with a temperature of 15 ° C. and a humidity of 50% and then leave for 6 hours in an environment with a temperature of 50 ° C. and a humidity of 95%” so that condensation occurs on the surface of the metal part. As a result, a repeated cycle test was conducted. After a predetermined number of cycles, each metal part is taken out from the anticorrosive film, and the occurrence of corrosion on the surface is visually observed. In the above cycle, the surface of the metal part exposed to the gas phase (hereinafter referred to as “gas phase”). The surface state of each of the portions where the condensed water was generated (hereinafter referred to as “liquid contact portion”) was visually observed and evaluated by [◯: no corrosion, x: corrosion). The test results of Examples and Comparative Examples are shown in Tables 10, 11 and 12 for each weight% of sodium benzoate (sodium silicate in Comparative Example 5) with respect to the anticorrosive film. Tables 10 to 12 show the results for samples in which corrosion occurred.
表１０〜１２を参照して、実施例２及び比較例４〜６を比較すると、安息香酸ナトリウムと、メタケイ酸ナトリウムと、オレイン酸アミドとを併用した実施例では、比較例に比べて、気相部及び液接触部の両方において、鉄製の金属部品に対する防錆効果の持続サイクルが長くなることが確認された。特に、防錆フィルム中の安息香酸ナトリウムが０．１重量％以上の場合、実施例２では４０サイクル以上に渡り防錆効果が持続されているように、比較例４〜６に比べて格段に長く防錆効果が持続されており、防錆剤とケイ酸塩（ケイ酸ナトリウム）との相乗効果が発揮され、かつ、オレイン酸アミド添加により防錆剤の防錆効果が助長されることが確認された。 When comparing Example 2 and Comparative Examples 4 to 6 with reference to Tables 10 to 12, the Example using sodium benzoate, sodium metasilicate, and oleic acid amide in comparison with Comparative Example, It was confirmed that in both the phase part and the liquid contact part, the sustained cycle of the anticorrosive effect on the iron metal part was lengthened. In particular, when the amount of sodium benzoate in the rust-preventing film is 0.1% by weight or more, in Example 2, the rust-preventing effect is maintained over 40 cycles or more, compared with Comparative Examples 4-6. The anti-rust effect has been maintained for a long time, the synergistic effect of the anti-rust agent and silicate (sodium silicate) is demonstrated, and the addition of oleic acid amide promotes the anti-rust effect of the anti-rust agent. confirmed.
本発明は、自動車部品等の金属体の防錆に利用できる。 The present invention can be used for rust prevention of metal bodies such as automobile parts.
Claims (5)
少なくとも１種類の防錆剤と、
オルトケイ酸ナトリウム以外の少なくとも１種類のケイ酸塩とを含む、防錆組成物。 A rust preventive composition having a rust preventive action,
At least one rust inhibitor;
A rust preventive composition comprising at least one silicate other than sodium orthosilicate.
樹脂フィルムと、
前記樹脂フィルムに含有される少なくとも１種類の防錆剤と、
前記樹脂フィルムに含有される、オルトケイ酸ナトリウム以外の少なくとも１種類のケイ酸塩と、
前記樹脂フィルムに含有される不飽和脂肪酸アミドとを備える、防錆フィルム。 A rust-proof film,
A resin film;
At least one rust inhibitor contained in the resin film;
At least one silicate other than sodium orthosilicate, contained in the resin film;
A rust-proof film comprising an unsaturated fatty acid amide contained in the resin film.