JP2011184718A

JP2011184718A - Method for reducing iron oxide-contained material with micro-wave heating, method for producing raw material for producing sintered ore, and method for producing raw material in blast furnace

Info

Publication number: JP2011184718A
Application number: JP2010048805A
Authority: JP
Inventors: Hideaki Yabe; 英昭矢部; Hatsuo Taira; 初雄平; Masaji Miyake; 正司三宅; Tasaburo Saji; 他三郎佐治
Original assignee: Nippon Steel Corp
Current assignee: Nippon Steel Corp
Priority date: 2010-03-05
Filing date: 2010-03-05
Publication date: 2011-09-22
Anticipated expiration: 2030-03-05
Also published as: JP5445230B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a method for reducing iron oxide-contained material by further efficiently heat-treating with a micro-wave irradiation to the iron oxide-contained material including hematite and goethite as the main components or the method that the same result can be obtained by using the above heat-treatment with the micro-wave irradiation even in the case that a reducing agent seldom exists. <P>SOLUTION: The method for reducing the iron oxide-contained material with the micro-wave heating is the followings that the iron oxide containing at least anyone in the hematite and the goethite contained in the iron oxide-contained material is reduced with the micro-wave irradiation having the frequency in the range of 20-30 GHz to the iron oxide-contained material containing at least anyone of the hematite and the goethite. <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

本発明は、周波数領域が２０〜３０GHzのマイクロ波を照射することによって酸化鉄含有物質を加熱・還元する方法に関するものであり、また、この方法を用いて製鉄所における焼結鉱製造用原料や高炉原料を製造する方法に関するものである。 The present invention relates to a method for heating and reducing an iron oxide-containing substance by irradiating a microwave having a frequency range of 20 to 30 GHz, and using this method, The present invention relates to a method for producing a blast furnace raw material.

近年、電磁波の一種であるマイクロ波を照射することによる加熱現象（すなわち、電子レンジの技術）を各種工業プロセスに応用しようという試みが各方面で検討されている。マイクロ波加熱は、従来の加熱プロセスと比較した場合、（１）マイクロ波を吸収する物質自身を内部から迅速に加熱することが可能である（急速加熱、内部加熱）、（２）マイクロ波を吸収する物質のみを選択して加熱することが可能である（選択加熱）、（３）通常の電気炉等による加熱では生じ得ない非熱的効果（マイクロ波による温度上昇以外によると考えられる効果）が発生する等、様々な特徴を併せ持つため、従来から検討されていた乾燥分野のみならず、近年では、鉄鉱石を始めとする各種金属酸化物の還元反応へマイクロ波加熱を適用することによって、従来よりも高効率な還元プロセスを確立しようとする検討が盛んに行われている。 In recent years, attempts have been made in various fields to apply a heating phenomenon (that is, microwave oven technology) by irradiating a microwave, which is a kind of electromagnetic wave, to various industrial processes. Compared with the conventional heating process, microwave heating can (1) rapidly heat the substance itself that absorbs the microwave from the inside (rapid heating, internal heating), (2) microwave It is possible to select and heat only the substance to be absorbed (selective heating). (3) Non-thermal effects that cannot be produced by heating with a normal electric furnace or the like (effects other than temperature rise caused by microwaves) In addition to the drying field that has been studied in the past, in recent years, by applying microwave heating to the reduction reactions of various metal oxides including iron ore. Consideration has been actively made to establish a reduction process that is more efficient than before.

例えば、特許文献１には、粉状の鉄酸化物原料に、還元剤たる炭剤と炭酸塩を配合して、マイクロ波を照射することにより、鉄酸化物を還元して鉄粉を製造する方法が提案されている。 For example, in Patent Document 1, a powdered iron oxide raw material is mixed with a charcoal and carbonate as a reducing agent, and irradiated with microwaves to reduce iron oxide to produce iron powder. A method has been proposed.

また、特許文献２には、金属含有材料と還元剤を混合して充填したコンテナへマイクロ波照射し、加えて電気アーク等のエネルギーを付加することによって金属を製造する方法が提案されている。 Further, Patent Document 2 proposes a method for producing a metal by irradiating a container filled with a metal-containing material and a reducing agent with microwaves and additionally applying energy such as an electric arc.

特開平06-279,824号公報JP 06-279,824 特表2004-526,864号公報Special table 2004-526,864

重見彰利、「製銑ハンドブック」地人書館、昭和54年12月10日、P.73Akinori Shigemi, “Seikan Handbook” Jinshokan, December 10, 1979, p. 73

ところで、マイクロ波による加熱を実施する場合、当然被加熱物質（物質そのものが内部から加熱される物質）はマイクロ波を吸収する物質でなくてはならない。そして、対象物がマイクロ波を照射することによってどの程度加熱できるかを示す式（１）として以下が定義されている。 By the way, when heating by a microwave is carried out, naturally the to-be-heated substance (substance in which the substance itself is heated from the inside) must be a substance that absorbs microwaves. And the following is defined as Formula (1) which shows how much an object can be heated by irradiating a microwave.

Ｐ：物質に吸収されるマイクロ波エネルギー[W/m³]
Ｅ：電場[V/m]
Ｈ：磁場[A/m]
σ：導電率[S/m]
ｆ：周波数[Hz]
ε₀：真空の誘電率[F/m]
ε^"：誘電損失
μ₀：真空の透磁率[H/m]
μ^"：磁気損失

P: Microwave energy absorbed by the substance [W / m ³ ]
E: Electric field [V / m]
H: Magnetic field [A / m]
σ: Conductivity [S / m]
f: Frequency [Hz]
ε ₀ : Vacuum dielectric constant [F / m]
ε ^" : Dielectric loss μ ₀ : Vacuum permeability [H / m]
μ ^" : Magnetic loss

この式（１）に基づけば、ある一定のマイクロ波電磁場において、導電率、誘電損失、磁気損失等の物性定数の大きな物質は、マイクロ波を良好に吸収してマイクロ波加熱し易い物質であると定義される。例えば、酸化鉄にはヘマタイト（酸化第二鉄／Fe₂O₃）、マグネタイト（四三酸化鉄／Fe₃O₄）、ウスタイト（酸化第一鉄／FeO）といった形態が存在するが、電子レンジで一般的に用いられている周波数（2.45GHz）のマイクロ波の使用を前提とした場合、ヘマタイトに関してはマイクロ波の吸収性が悪いため、それ単独ではマイクロ波による加熱を行うことが難しいことが知られている。 Based on this formula (1), a substance having a large physical constant such as conductivity, dielectric loss, magnetic loss, etc. in a certain microwave electromagnetic field is a substance that absorbs microwave well and is easily heated by microwave. Is defined. For example, there are forms of iron oxide such as hematite (ferric oxide / Fe ₂ O ₃ ), magnetite (triiron tetroxide / Fe ₃ O ₄ ), and wustite (ferrous oxide / FeO). Assuming the use of microwaves with a frequency (2.45 GHz) generally used in Japan, it is difficult to heat by microwave alone because hematite has poor microwave absorption Are known.

従って、製鉄業における主要原料である鉄鉱石の場合、マグネタイトを主成分とする磁鉄鉱であれば何ら問題なくマイクロ波による加熱を行うことが可能であるが、埋蔵量が多く、現在の主流となっているヘマタイトあるいはヘマタイトと同様の３価鉄ベースの水酸化鉄（ゲーサイト／Fe₂O₃・3H₂O）を主成分とする鉄鉱石（赤鉄鉱、褐鉄鉱）に関しては、基本的にはそれ単独ではマイクロ波による加熱を効果的に行うことはできない。また、製鉄所において発生する副産物（高炉ダスト、転炉ダスト、中和スラッジ等）を製鉄原料として再利用することも多く見受けられるが、これらの主要成分もヘマタイトあるいはゲーサイトであるため、やはりこれらの副産物についても単独ではマイクロ波によって効果的に加熱することはできない場合が多い。 Therefore, in the case of iron ore, which is the main raw material in the iron and steel industry, heating with microwaves can be carried out without any problem if it is a magnetite mainly composed of magnetite, but the reserves are large and the current mainstream. For iron ore (hematite, limonite) mainly composed of hematite or trivalent iron-based iron hydroxide (goethite / Fe ₂ O ₃ · 3H ₂ O) similar to hematite Alone, heating by microwaves cannot be performed effectively. In addition, by-products generated at steelworks (blast furnace dust, converter dust, neutralized sludge, etc.) are often reused as raw materials for iron making, but these main components are also hematite or goethite. In many cases, it is not possible to effectively heat these by-products alone by microwaves.

そのため、特許文献１及び特許文献２においては、ヘマタイトを原料として使用する場合には、マイクロ波の吸収性の高い物質（炭素あるいはマグネタイト等）を別途混合する必要があると述べられている。 Therefore, in Patent Document 1 and Patent Document 2, it is stated that when hematite is used as a raw material, it is necessary to separately mix a substance having high microwave absorptivity (such as carbon or magnetite).

ここで、酸化鉄を還元するためには、いずれにしても還元剤としての炭素を添加する必要があるのは当然であるが、特許文献１によれば、ヘマタイトを良好にマイクロ波加熱するためには、酸化鉄の還元のために必要な当量に対して２倍以上の余分な炭素を加える必要があるものと述べられており、還元剤に関わるコストを浪費する観点から問題があった。また、還元反応に何ら寄与しない余分な炭素を酸化鉄と同等以上の温度にまで昇温させることになるため、その分マイクロ波の出力を高める必要があり、結果としてマイクロ波の発生に必要な電力を多量に消費するという問題もあった。 Here, in order to reduce iron oxide, it is natural that in any case it is necessary to add carbon as a reducing agent. However, according to Patent Document 1, hematite is favorably microwave-heated. Describes that it is necessary to add more than twice as much extra carbon to the equivalent amount required for the reduction of iron oxide, and there was a problem from the viewpoint of wasting costs related to the reducing agent. In addition, since excess carbon that does not contribute to the reduction reaction is heated to a temperature equal to or higher than that of iron oxide, it is necessary to increase the microwave output accordingly, and as a result, it is necessary to generate microwaves. There was also a problem of consuming large amounts of power.

また、常温においてはマイクロ波吸収性が悪い物質であっても、温度の上昇に伴ってマイクロ波吸収性が改善される物質が存在することが知られており、諸説が存在するもののヘマタイトもこのような温度依存性の大きな物質であると一部では報告されている。そこで、特許文献２においては、電気炉加熱等の方法によって被加熱物質をマイクロ波吸収性が向上する臨界温度にまで予熱した後に、マイクロ波による加熱並びに金属の還元を行う方法も提案されている。しかし、この方法では、金属の還元に必要なマイクロ波加熱によるリアクター単独では還元処理を実施することができず、何ら還元反応には寄与しない予熱用のリアクターが別途必要になる。 In addition, it is known that there are substances that improve microwave absorption with increasing temperature, even if the substance has poor microwave absorption at room temperature. Some have been reported to be highly temperature-dependent. Therefore, Patent Document 2 also proposes a method of heating by a microwave and reducing a metal after preheating the material to be heated to a critical temperature at which microwave absorption is improved by a method such as electric furnace heating. . However, in this method, the reduction treatment cannot be carried out with a single reactor by microwave heating necessary for metal reduction, and a preheating reactor that does not contribute to any reduction reaction is required separately.

ところで、本発明者らは、ヘマタイトあるいはゲーサイトを含有する物質を還元性ガスによってマグネタイト主体の物質へと還元処理した後に、当該還元物質を炭素（還元剤）と混合し、得られた混合物にマイクロ波を照射して加熱することにより、金属鉄を得る方法を提案している（特願2009-073,169号出願）。この方法においても、マイクロ波加熱の前処理として還元性ガスを用いた事前還元が必要であるため、マイクロ波による加熱設備とは別に、還元性ガスによる事前還元を行うためのリアクターが必要になる。 By the way, the present inventors reduced a substance containing hematite or goethite to a substance mainly composed of magnetite with a reducing gas, and then mixed the reducing substance with carbon (reducing agent). A method for obtaining metallic iron by heating by irradiation with microwaves has been proposed (filed in Japanese Patent Application No. 2009-073,169). Also in this method, since pre-reduction using a reducing gas is necessary as a pretreatment for microwave heating, a reactor for performing pre-reduction using a reducing gas is required separately from the heating equipment using microwaves. .

そこで、本発明者らは、マイクロ波照射によりヘマタイトやゲーサイトを主成分とする酸化鉄含有物質をより効率良く加熱処理し、酸化鉄含有物質を還元する方法について、更に以下のような考えの下に検討を行った。 Therefore, the present inventors have further considered the following idea regarding a method for more efficiently heat-treating an iron oxide-containing substance mainly composed of hematite or goethite by microwave irradiation and reducing the iron oxide-containing substance. The investigation was conducted below.

一般的に、マイクロ波とは、３００MHz〜３００GHz程度の範囲の周波数を持つ電磁波である、と定義されている。しかし実際には、現在マイクロ波加熱用途に利用されているマイクロ波の周波数はかなり限定されており、電子レンジ用に普及して安価な発振機（マグネトロン）が出力する２．４５GHz以外の周波数に関してはほとんど使用されていないのが現実である。極僅かに、短波長側の０．９１５GHzの周波数が使用された例はあるが、２．４５GHzよりも高周波側（波長としては短波長側）の領域（ミリ波、サブミリ波と呼称される場合が多い）の利用に関しては、係る高周波のマイクロ波を出力する発振機（クライストロン、ジャイロトロン等）があまり普及しておらず、高価なことも手伝って、あまり検討が行われていないのが現実である。 Generally, a microwave is defined as an electromagnetic wave having a frequency in the range of about 300 MHz to 300 GHz. In practice, however, the frequency of microwaves currently used for microwave heating applications is quite limited. Regarding frequencies other than 2.45 GHz that are widely used in microwave ovens and output from inexpensive oscillators (magnetrons) The reality is that is almost never used. There is an example in which the frequency of 0.915 GHz on the short wavelength side is used very slightly, but the region on the high frequency side (short wavelength side as the wavelength) than 2.45 GHz (called millimeter wave, submillimeter wave) In many cases, oscillators that output such high-frequency microwaves (klystrons, gyrotrons, etc.) are not widely used, and the fact that they are expensive has helped them not be studied. It is.

また、電磁波は、そのエネルギーの大きさに比例して様々な形で物質と相互作用をするといわれている。電磁波のエネルギーは波長が短くなるにつれて（周波数が大きくなるにつれて）大きくなるため、γ線やＸ線のようないわゆる高エネルギーの電磁波は、原子核や原子内電子と相互作用することができ、それらより低いエネルギーを持つ紫外線、可視光、近赤外線は主に固体内電子の遷移に影響を及ぼすことができ、更にエネルギーが低い電磁波である赤外線は分子の振動や回転に影響を及ぼすことができる。一方、これらの電磁波よりも更にエネルギーが低いマイクロ波は、主に物質中の電気双極子と相互作用し、配向分極を誘起する程度のレベルであるといわれている。しかし、マイクロ波加熱に付随するいわゆる非熱的効果は、これらマイクロ波と物質との相互作用に起因して生じる現象であるとも考えられている。 Electromagnetic waves are said to interact with substances in various forms in proportion to their energy levels. Since the energy of electromagnetic waves increases as the wavelength decreases (as the frequency increases), so-called high-energy electromagnetic waves such as γ-rays and X-rays can interact with nuclei and electrons inside the atom. Ultraviolet rays, visible light, and near infrared rays having low energy can mainly affect the transition of electrons in the solid, and infrared rays, which are electromagnetic waves having lower energy, can affect the vibration and rotation of molecules. On the other hand, microwaves having lower energy than these electromagnetic waves are said to be at a level that mainly interacts with electric dipoles in the substance and induces orientational polarization. However, the so-called non-thermal effect associated with microwave heating is also considered to be a phenomenon caused by the interaction between these microwaves and substances.

そこで、本発明者らは、同じマイクロ波領域の電磁波であっても、２．４５GHzのマイクロ波よりも更に短波長側（高周波数側）のマイクロ波を用いることにより物質との相互作用が促進され、更に非熱的効果が増幅されることが期待できるのではないかとの考えに到達し、また、既に述べたように、２０〜３０℃程度の常温状態において、ヘマタイト又はゲーサイトのような３価鉄をベースとした酸化鉄へ２．４５GHzのマイクロ波を照射した場合、ほとんどマイクロ波は吸収されないため、ごく僅かな昇温幅でしか加熱できないことが広く一般的に知られてはいるが、先に式（１）において示した通り、マイクロ波加熱に関係した物性定数（誘電損失、磁気損失等）は周波数に依存した関数であり、また、マイクロ波加熱（マイクロ波の吸収）は、より高い周波数及び強い電磁場雰囲気下において一層促進されるため、マイクロ波の周波数を従来の２．４５GHzよりも更に高周波側へシフトすることによって、これまでは加熱することさえできなかったヘマタイトやゲーサイトのような物質が容易に加熱されるようになり、加えて非熱的効果も増幅される可能性があるとの考えに到達した。 Therefore, the present inventors have promoted interaction with a substance by using microwaves on the shorter wavelength side (high frequency side) than microwaves of 2.45 GHz even for electromagnetic waves in the same microwave region. And reached the idea that a non-thermal effect can be expected to be further amplified, and as already mentioned, at room temperature of about 20-30 ° C., such as hematite or goethite It is widely known that when iron oxide based on trivalent iron is irradiated with microwaves of 2.45 GHz, microwaves are hardly absorbed and can be heated with only a slight temperature rise. However, as shown in the equation (1) above, the physical constants related to microwave heating (dielectric loss, magnetic loss, etc.) are functions depending on the frequency, and microwave heating (microwave absorption) Is further promoted at higher frequencies and in a strong electromagnetic field atmosphere, so by shifting the microwave frequency to a higher frequency side than the conventional 2.45 GHz, hematite or It came to the idea that materials such as goethite could easily be heated and in addition non-thermal effects could be amplified.

本発明者らは、上記の考え方の下に幾多の検討を重ねた結果、現在汎用されている２．４５GHzではほとんど温度が上昇しないヘマタイトやゲーサイトを主体とする酸化鉄含有物質に対して、１０倍程度の周波数を有するマイクロ波を照射したところ、驚くべきことに、短時間で１０００℃以上まで加熱できることを見出し、本発明をした。 As a result of many examinations based on the above-mentioned idea, the present inventors, as a result of the iron oxide-containing substance mainly composed of hematite and goethite, which does not increase in temperature at 2.45 GHz, which is currently widely used, When microwaves having a frequency of about 10 times were irradiated, it was surprisingly found that it was possible to heat to 1000 ° C. or higher in a short time, and the present invention was made.

従って、本発明の目的は、赤鉄鉱等のヘマタイトやゲーサイトを主成分とする酸化鉄含有物質を、マイクロ波照射によって、より効率良く加熱処理して、酸化鉄含有物質を還元する方法を提供することである。 Therefore, an object of the present invention is to provide a method for reducing an iron oxide-containing substance by heat-treating an iron oxide-containing substance mainly composed of hematite such as hematite or goethite by microwave irradiation. It is to be.

また、本発明は、赤鉄鉱等のヘマタイトやゲーサイトを主成分とする酸化鉄含有物質を、還元剤が殆どない状態であっても、マイクロ波照射によって、効率良く加熱処理して、酸化鉄含有物質を還元する方法を提供することも目的とする。 In addition, the present invention is an iron oxide-containing substance mainly composed of hematite or goethite such as hematite, even in a state where there is almost no reducing agent. It is also an object to provide a method for reducing contained substances.

更にまた、本発明は、左記マイクロ波照射による酸化鉄含有物質の還元方法により、鉄鋼製造プロセスにおける焼結鉱原料や高炉原料を製造する方法を提供することを目的とする。 Still another object of the present invention is to provide a method for producing a sintered ore raw material or a blast furnace raw material in a steel production process by the method for reducing an iron oxide-containing substance by microwave irradiation described on the left.

上記目的を達成するための本発明の要旨は次の通りである。
(1) ヘマタイト及びゲーサイトのうちの少なくともいずれか一方を含む酸化鉄含有物質に対して２０〜３０GHzの領域の周波数を持つマイクロ波を照射することにより、前記酸化鉄含有物質を加熱し、前記酸化鉄含有物質中に含有される前記ヘマタイト及びゲーサイトのうちの少なくともいずれかを含む酸化鉄を還元することを特徴とするマイクロ波加熱による酸化鉄含有物質の還元方法。 In order to achieve the above object, the gist of the present invention is as follows.
(1) heating the iron oxide-containing substance by irradiating the iron oxide-containing substance containing at least one of hematite and goethite with a microwave having a frequency in a range of 20 to 30 GHz; A method for reducing an iron oxide-containing material by microwave heating, comprising reducing iron oxide containing at least one of the hematite and goethite contained in the iron oxide-containing material.

(2) 前記酸化鉄含有物質への前記マイクロ波の照射を、還元剤と共存する状態で行うことを特徴とする前記(1)に記載のマイクロ波による酸化鉄含有物質の還元方法。 (2) The method for reducing an iron oxide-containing substance by microwave according to (1), wherein the microwave irradiation to the iron oxide-containing substance is performed in a state of coexisting with a reducing agent.

(3) 前記還元剤が炭素含有物質であり、この還元剤を前記酸化鉄含有物質に添加して得られた混合物へマイクロ波を照射することを特徴とする前記(2)に記載のマイクロ波加熱による酸化鉄含有物質の還元方法。 (3) The microwave according to (2), wherein the reducing agent is a carbon-containing substance, and the mixture obtained by adding the reducing agent to the iron oxide-containing substance is irradiated with microwaves. A method for reducing iron oxide-containing substances by heating.

(4) 前記還元剤が還元性ガスであり、前記酸化鉄含有物質への前記マイクロ波の照射を前記還元性ガス中で行うことを特徴とする前記(2)又は(3)に記載のマイクロ波による酸化鉄含有物質の還元方法。 (4) The reducing agent according to (2) or (3), wherein the reducing agent is a reducing gas, and the microwave irradiation to the iron oxide-containing substance is performed in the reducing gas. Reduction method of iron oxide-containing substances by waves.

(5) 前記(1)〜(4)のいずれか１項に記載のマイクロ波加熱により酸化鉄含有物質の還元処理を行い、この還元処理された酸化鉄含有物質を、焼結鉱製造プロセスにおける原料とすることを特徴とする焼結鉱製造用原料の製造方法。 (5) The iron oxide-containing substance is reduced by microwave heating according to any one of (1) to (4), and the reduced iron oxide-containing substance is used in a sinter ore production process. A method for producing a raw material for producing sintered ore, characterized in that the raw material is used as a raw material.

(6) 前記(1)〜(4)のいずれか１項に記載のマイクロ波加熱により酸化鉄含有物質の還元処理を行い、この還元処理された酸化鉄含有物質を、高炉プロセスにおける原料とすることを特徴とする高炉原料の製造方法。 (6) The iron oxide-containing substance is reduced by microwave heating according to any one of (1) to (4), and the reduced iron oxide-containing substance is used as a raw material in a blast furnace process. A method of producing a blast furnace raw material characterized by the above.

ヘマタイトやゲーサイトを主成分とする酸化鉄含有物質であっても、マイクロ波加熱によって効率良く加熱処理を行い、酸化鉄含有物質を還元することが可能となる。また、ヘマタイトやゲーサイトを主成分とする酸化鉄含有物質であっても、マイクロ波加熱による還元により、鉄鋼製造プロセスにおける焼結鉱製造用原料や、高炉プロセスにおける高炉原料を製造することが可能となる。 Even an iron oxide-containing substance mainly composed of hematite or goethite can be efficiently heat-treated by microwave heating to reduce the iron oxide-containing substance. In addition, even iron oxide-containing substances mainly composed of hematite and goethite can be produced by raw material for sinter ore production in the steel production process or blast furnace raw material in the blast furnace process by reduction by microwave heating. It becomes.

図１は、本発明の方法を実施するためのマイクロ波加熱処理装置の１例を示す説明図である。FIG. 1 is an explanatory diagram showing an example of a microwave heat treatment apparatus for carrying out the method of the present invention.

図２は、本発明と従来技術とのマイクロ波加熱特性を比較したグラフ図である。FIG. 2 is a graph comparing the microwave heating characteristics of the present invention and the prior art. 図３は、別の条件における本発明と従来技術とのマイクロ波加熱特性を比較したグラフ図である。FIG. 3 is a graph comparing the microwave heating characteristics of the present invention and the prior art under different conditions.

図４は、更に別の条件における本発明と従来技術とのマイクロ波加熱特性を比較したグラフ図である。FIG. 4 is a graph comparing the microwave heating characteristics of the present invention and the prior art under still another condition. 図５は、非特許文献１に記載された「温度と酸化鉄の解離との関係を示すグラフ」を紹介するグラフ図である。FIG. 5 is a graph showing the “graph showing the relationship between temperature and iron oxide dissociation” described in Non-Patent Document 1.

図６は、本発明の実施例で使用したマイクロ波加熱処理装置を示す説明図である。FIG. 6 is an explanatory view showing the microwave heat treatment apparatus used in the example of the present invention. 図７は、比較例で使用したマイクロ波加熱処理装置を示す説明図である。FIG. 7 is an explanatory view showing the microwave heat treatment apparatus used in the comparative example.

以下、本発明を詳細に説明する。
図１に、本発明に係るマイクロ波加熱処理装置の１例を示す。ここで、本装置は、本発明に係る２０〜３０GHzのマイクロ波のうち２４GHzのマイクロ波を照射可能としているほか、比較のために、２．４５GHzのマイクロ波の照射も可能としている。すなわち、アプリケーター（反応器）１内に設置された被加熱物質２に対して、異なる２種類の周波数のマイクロ波を照射することが可能である。マイクロ波の種類としては２．４５GHz及び２４GHzの２種類の周波数が選択可能であり（発振機の特性上、±500MHz程度の誤差は生じ得る。以下同様）、各々のマイクロ波はマグネトロン３、ジャイロトロン４という個別の専用発振機を用いて発生させ、マイクロ波が特定の位置に集束することなく、ランダムかつ非定常にアプリケーター１内を飛び回っている状態（マルチモード）とし、被加熱物質２全体をなるべく均一に加熱できるようになっている。また、アプリケーター１内の雰囲気は、外部から雰囲気ガス５を添加することによって任意に調節することが可能であり、更に、被加熱物質２の温度に関しては、外径８mmの金属管シースで保護された熱電対７を粉体である試料中へ挿入し、この粉体内部の平均温度を測定できるようになっている。 Hereinafter, the present invention will be described in detail.
FIG. 1 shows an example of a microwave heat treatment apparatus according to the present invention. Here, the present apparatus can irradiate microwaves of 24 GHz out of microwaves of 20 to 30 GHz according to the present invention, and can also irradiate microwaves of 2.45 GHz for comparison. That is, it is possible to irradiate the to-be-heated substance 2 installed in the applicator (reactor) 1 with microwaves of two different frequencies. As the types of microwaves, two frequencies of 2.45 GHz and 24 GHz can be selected (an error of about ± 500 MHz can occur due to the characteristics of the oscillator. The same applies hereinafter), and each microwave is magnetron 3, gyro. It is generated using an individual dedicated oscillator called TRON 4, and the microwave is not focused on a specific position, but is randomly and unsteadily flying around the applicator 1 (multi-mode), and the heated material 2 as a whole Can be heated as uniformly as possible. The atmosphere in the applicator 1 can be arbitrarily adjusted by adding an atmospheric gas 5 from the outside. Further, the temperature of the heated material 2 is protected by a metal tube sheath having an outer diameter of 8 mm. The thermocouple 7 is inserted into a powder sample, and the average temperature inside the powder can be measured.

本装置を用いて、各種のサンプルにマイクロ波を照射して加熱・還元を行う試験を行った。以下に、これら試験例の結果を示す。
なお、以下の試験例において、鉄(Fe)還元率とは、ヘマタイトを金属鉄（M-Fe）まで還元する際に除去される理論酸素量に対して、実際にどの程度の割合の酸素が除去されたかを表す指標であり、マイクロ波照射後の酸化鉄含有物質の全てがヘマタイトの場合は還元率＝０%、全てがマグネタイトの場合は還元率＝１１．１%、全てがウスタイト（FeO）の場合還元率＝３３．３%、全てが金属鉄の場合は還元率＝１００%となる。すなわち、還元率１１．１%というのはすべてのヘマタイトがマグネタイトまで還元された状態であり、還元率５%とはヘマタイトとマグネタイトが混合（ウスタイト以降の還元が起きていないと想定した場合）している状態である。 Using this device, various samples were irradiated with microwaves and tested for heating and reduction. The results of these test examples are shown below.
In the following test examples, the iron (Fe) reduction rate is the actual oxygen content that is removed when hematite is reduced to metallic iron (M-Fe). It is an index indicating whether it has been removed. When all of the iron oxide-containing materials after microwave irradiation are hematite, the reduction rate is 0%, when all are magnetite, the reduction rate is 11.1%, and all are wustite (FeO ), The reduction rate = 33.3%, and when all are metallic iron, the reduction rate = 100%. In other words, a reduction rate of 11.1% means that all hematite has been reduced to magnetite, and a reduction rate of 5% means that hematite and magnetite are mixed (assuming no reduction after wustite occurs). It is in a state.

また、以下の試験例において、鉄の形態の定量分析（M-Fe、FeO、Fe₂O₃）に関しては、蛍光Ｘ線分析法、容量法（JIS M8213）等の分析手法によって実施した。これら分析手法ではマグネタイト（Fe₃O₄＝FeO・Fe₂O₃）の含有量を定量することができないため、ウスタイト、マグネタイト、ヘマタイトの各々の含有割合を正確に把握することは不可能である。そこで、これら定量分析の結果から算出したFe還元率及びＸ線回折分析法による鉄形態の定性分析の結果から、試料中に存在する酸化鉄の形態（ウスタイト、マグネタイト、ヘマタイト）を推定した。 Further, in the following test examples, the quantitative analysis of the iron form (M-Fe, FeO, Fe ₂ O ₃ ) was carried out by an analytical method such as a fluorescent X-ray analysis method or a volumetric method (JIS M8213). Since these analytical methods cannot quantify the content of magnetite (Fe ₃ O ₄ = FeO · Fe ₂ O ₃ ), it is impossible to accurately grasp the content of each of wustite, magnetite, and hematite. . Therefore, the form of iron oxide (wustite, magnetite, hematite) present in the sample was estimated from the Fe reduction rate calculated from the results of quantitative analysis and the results of qualitative analysis of iron form by X-ray diffraction analysis.

［試験例１］
最初に、被加熱物質２としてヘマタイト試薬（特級／純度99.0%以上、100g）を用い、アプリケーター１内の雰囲気をアルゴン（供給したアルゴンガス中に不純物として含有される酸素の分圧は10^-4MPa）として、被加熱物質２には、マグネトロン３によって発生させた２．４５GHzのマイクロ波、又はジャイロトロン４によって発生させた２４GHzのマイクロ波をそれぞれ４００Wの出力で照射した。図２にその際のヘマタイト試薬の温度変化を示す。 [Test Example 1]
First, a hematite reagent (special grade / purity 99.0% or more, 100 g) is used as the substance 2 to be heated, and the atmosphere in the applicator 1 is argon (the partial pressure of oxygen contained as an impurity in the supplied argon gas is 10 ^−4. The material 2 to be heated was irradiated with a 2.45 GHz microwave generated by the magnetron 3 or a 24 GHz microwave generated by the gyrotron 4 at an output of 400 W, respectively. FIG. 2 shows the temperature change of the hematite reagent at that time.

２．４５GHzのマイクロ波を照射した場合（マイクロ波照射時間255分）は、これまでの知見の通り、ヘマタイト試薬は極僅かの温度上昇（最高温度80℃）が認められたにすぎなかったが、２４GHzの周波数を照射した場合（マイクロ波照射時間70分）には、ヘマタイト試薬単独であっても、極めて急速に１０００℃以上の温度（最高温度1200℃）にまで加熱できることが判明した。
表１に上記において加熱した後のヘマタイトの組成およびＦｅの還元率を示す。 When irradiated with a 2.45 GHz microwave (microwave irradiation time of 255 minutes), the hematite reagent showed only a slight increase in temperature (maximum temperature of 80 ° C.), as known to date. When the frequency of 24 GHz was irradiated (microwave irradiation time 70 minutes), it was found that even the hematite reagent alone could be heated to a temperature of 1000 ° C. or higher (maximum temperature 1200 ° C.) very rapidly.
Table 1 shows the composition of hematite and the reduction rate of Fe after heating in the above.

表１に示す結果から明らかなように、２．４５GHzのマイクロ波を照射した場合のヘマタイト試薬は、高々８０℃程度までにしか加熱されなかったため、当然にヘマタイトの還元はほとんど起きていなかったが、２４GHzのマイクロ波で加熱した場合には、有為的にヘマタイトの還元が進行しているのが判明した。 As is clear from the results shown in Table 1, the hematite reagent when irradiated with the 2.45 GHz microwave was only heated up to about 80 ° C., and naturally, hematite was hardly reduced. It was found that when heating with microwaves at 24 GHz, the reduction of hematite progressed significantly.

［試験例２］
次に、被加熱物質２として表２に示す組成のローブリバー鉱石（粒径0.25mm以下、150g）をを用い、アプリケーター１内の雰囲気をアルゴン（供給したアルゴンガス中に不純物として含有される酸素の分圧は10^-4MPa）として、先のヘマタイト試薬を用いた試験例１と同様に、２．４５GHzのマイクロ波又は２４GHzのマイクロ波をそれぞれ４００Wの出力で照射した。図３に、その際のローブリバー鉱石の温度変化を示す。 [Test Example 2]
Next, lobe river ore (particle size: 0.25 mm or less, 150 g) having the composition shown in Table 2 is used as the material to be heated 2, and the atmosphere in the applicator 1 is argon (oxygen contained as an impurity in the supplied argon gas). as partial pressure 10 ^-4 MPa) for, in the same manner as in test example 1 using the previous hematite reagent, a microwave 2.45GHz microwave or 24GHz was irradiated at an output of 400W, respectively. FIG. 3 shows the temperature change of the lobe river ore at that time.

ローブリバー鉱石を用いた試験例２の場合、ヘマタイト以外の成分（ヘマタイトとはマイクロ波吸収性が異なる）が含有されるため、ある程度時間は要するものの、２．４５GHzのマイクロ波を照射した場合（マイクロ波照射時間240分）であっても１０００℃以上の高温（最高温度1320℃）にまで加熱することが可能であった。しかし、２４GHzのマイクロ波を照射した場合（マイクロ波照射時間70分）には、２．４５GHzの周波数を用いた場合よりも、極めて迅速に１０００℃以上の温度（最高温度1230℃）にまで加熱することが可能であった。
表３に、上記において加熱した後のローブリバー鉱石の組成及びFe還元率を示す。 In the case of Test Example 2 using lobliber ore, since components other than hematite (microwave absorption is different from hematite) are contained, it takes a certain amount of time, but when 2.45 GHz microwave is irradiated ( Even with a microwave irradiation time of 240 minutes, it was possible to heat to a high temperature of 1000 ° C. or higher (maximum temperature 1320 ° C.). However, when irradiated with 24 GHz microwaves (microwave irradiation time 70 minutes), heating to a temperature of 1000 ° C. or higher (maximum temperature 1230 ° C.) is much faster than when using a frequency of 2.45 GHz. It was possible to do.
Table 3 shows the composition of the lobe river ore and the Fe reduction rate after heating in the above.

表３に示す結果から明らかなように、２４GHzのマイクロ波で加熱した場合のローブリバー鉱石の方が、２．４５GHzのマイクロ波で加熱した場合よりも、Fe還元率が大きく、ウスタイト（FeO）レベルまでの還元が進行していることが判明した。また、ローブリバー鉱石の中の結晶水も除去されていた。 As is apparent from the results shown in Table 3, the lobe river ore when heated with microwaves at 24 GHz has a higher Fe reduction rate than when heated with microwaves at 2.45 GHz, and wustite (FeO). It turned out that the reduction to the level was progressing. The crystal water in the lobe river ore was also removed.

［試験例３］
次に、被加熱物質２として表４に示す組成の中和スラッジ（製鉄所副産物であって乾燥機によって乾燥した後のサンプル：平均粒径30μm、50g）を用い、アプリケーター１内の雰囲気をアルゴン（供給したアルゴンガス中に不純物として含有される酸素の分圧は10^-4MPa）として、先のヘマタイト試薬を用いた試験例１と同様に、２．４５GHzのマイクロ波又は２４GHzのマイクロ波をそれぞれ４００Ｗの出力で照射した。図４に、その際の中和スラッジの温度変化を示す。 [Test Example 3]
Next, neutralized sludge having the composition shown in Table 4 is used as the material to be heated 2 (sample of ironworks by-product and dried by a dryer: average particle size 30 μm, 50 g), and the atmosphere in the applicator 1 is argon. (The partial pressure of oxygen contained as an impurity in the supplied argon gas is 10 ⁻⁴ MPa) As in Test Example 1 using the previous hematite reagent, a 2.45 GHz microwave or a 24 GHz microwave was applied. Irradiation was performed at an output of 400 W each. In FIG. 4, the temperature change of the neutralization sludge in that case is shown.

中和スラッジを用いた試験例３の場合、ヘマタイト以外の成分（ヘマタイトとはマイクロ波吸収性が異なる）が多量に含有されるため、２．４５GHzのマイクロ波を照射した場合（マイクロ波照射時間240分）であっても、２４GHzのマイクロ波を照射した場合（マイクロ波照射時間60分）であっても、ほとんど同様の昇温速度によって１０００℃以上の温度（2.45GHz：最高温度1360℃、２４GHz：1200℃）にまで加熱することが可能であった。
表５に、上記において加熱した後の中和スラッジの組成およびＦｅの還元率を示す。 In the case of Test Example 3 using neutralized sludge, since a large amount of components other than hematite (differing in microwave absorption from hematite) is contained, when 2.45 GHz microwave is irradiated (microwave irradiation time) 240 minutes), even when 24 GHz microwaves are irradiated (microwave irradiation time 60 minutes), a temperature of 1000 ° C or higher (2.45 GHz: maximum temperature 1360 ° C, 24 GHz: 1200 ° C.).
Table 5 shows the composition of the neutralized sludge and the reduction rate of Fe after heating in the above.

表５に示す結果から明らかなように、２．４５GHzのマイクロ波で加熱した中和スラッジがマグネタイトレベルまでへの還元しか起きていないのに対して（Fe還元率とＸ線回折分析結果から推定）、２４GHzのマイクロ波で加熱した中和スラッジの場合にはFe還元率が大幅に大きく、ウスタイトレベルまで、また一部に関しては金属Feレベルまでの還元が進行していることが判明した（Fe還元率とＸ線回折分析結果から推定）。また、中和スラッジ中に含有される塩素の除去率に関しても、２４GHzのマイクロ波で加熱した場合の方が大きかった。 As is clear from the results shown in Table 5, neutralized sludge heated with 2.45 GHz microwaves was only reduced to the magnetite level (estimated from Fe reduction rate and X-ray diffraction analysis results). ), In the case of neutralized sludge heated by microwaves at 24 GHz, the Fe reduction rate was significantly large, and it was found that the reduction to the wustite level, and partly to the metallic Fe level (Fe) Estimated from reduction rate and X-ray diffraction analysis results). Also, the removal rate of chlorine contained in the neutralized sludge was larger when heated by microwaves at 24 GHz.

上記試験例１〜３において、ヘマタイト試薬及びローブリバー鉱石をマイクロ波加熱する際に還元剤（炭素）は全く共存しない状態であり、また雰囲気ガスはアルゴンであって還元性のガス成分も全く含有されていない。従って、マイクロ波加熱によって生じた還元現象は、専ら酸化鉄を高温に加熱したことに付随する熱分解（酸素解離）反応に由来するものであると推定される。また、中和スラッジ中には、元来極僅かな量の炭素が含有されているが、実際の２４GHzのマイクロ波加熱後のサンプルは、その炭素を還元剤として理論上起り得る最大の還元率（C＋2O→CO₂までの還元が起きるものと想定）を超えるまで、還元反応が進行しているため、ローブリバー鉱石の場合と同様に、酸化鉄の熱分解反応が主体となっているものと推定される。 In Test Examples 1 to 3, when the hematite reagent and the lobe river ore are heated by microwave, the reducing agent (carbon) is not present at all, and the atmospheric gas is argon and contains no reducing gas component. It has not been. Therefore, the reduction phenomenon caused by microwave heating is presumed to originate solely from the thermal decomposition (oxygen dissociation) reaction accompanying heating of iron oxide to a high temperature. The neutralized sludge originally contains a very small amount of carbon, but the actual sample after 24 GHz microwave heating has the maximum reduction rate that can theoretically occur using that carbon as a reducing agent. Since the reduction reaction proceeds until exceeding (assuming that the reduction from C + 2O to CO ₂ occurs), the thermal decomposition reaction of iron oxide is the main component as in the case of lobe river ore. Presumed.

図５に、非特許文献１に記載された「温度と酸化鉄の解離との関係を示すグラフ」が紹介されている。この図５から、今回の試験例１〜３で使用されたアルゴンガス中の酸素分圧（10^-4MPa≒10^-3atm、logPo₂＝-3[atm]；炭素等の共存物質と酸素が平衡することによって、アプリケーター内の酸素分圧はこれよりも若干低くなっている可能性はある。）付近においては、理論上、２４GHzのマイクロ波加熱において到達した温度（1200〜1230℃程度）では、ヘマタイトからマグネタイトまでの熱分解（還元）は起りうるが、マグネタイトからウスタイトまでの熱分解（還元）は起り得ないことが解かる。 FIG. 5 introduces a “graph showing the relationship between temperature and iron oxide dissociation” described in Non-Patent Document 1. From FIG. 5, the oxygen partial pressure (10 ⁻⁴ MPa≈10 ⁻³ atm, logPo ₂ = −3 [atm] in argon gas used in Test Examples 1 to 3 this time; coexisting substances such as carbon and oxygen It is possible that the oxygen partial pressure in the applicator is slightly lower than this due to the equilibrium of the temperature.) Nearly, the temperature reached in the microwave heating at 24 GHz (about 1200 to 1230 ° C) Then, it can be seen that thermal decomposition (reduction) from hematite to magnetite can occur, but thermal decomposition (reduction) from magnetite to wustite cannot occur.

試験例２の場合のローブリバー鉱石と試験例３の場合の中和スラッジに関して、２．４５GHzよりも２４GHzのマイクロ波を用いた場合に（しかも、最高温度は２４GHzのマイクロ波で加熱した場合の方が低いのにもかかわらず）、酸化鉄の還元（熱分解反応）が大幅に促進され、しかも、理論上起り得るレベル以上にまで還元が進行している原因に関しては不明であるが、例えば、要因(1) ２４GHzのマイクロ波の強い電磁場が何らかのメカニズムによって酸素の解離現象を促進したこと、要因(2) マイクロ波加熱の特徴である内部加熱が２４GHzのマイクロ波では更に増幅され、ローブリバー鉱石や中和スラッジ粒子の内部温度が熱電対による測定温度（各粒子表面の平均温度を測定しているにすぎない）よりも大幅に高温となっていたこと、等の理由が考えられる。しかし、試験例１の場合のヘマタイト試薬に関しては、２４GHzのマイクロ波で加熱した場合であっても、ほとんど還元が進行していないことから、ローブリバー粉鉱石及び中和スラッジ中に含有されるFe以外の物質の影響（マイクロ波加熱特性上Feよりも更に高温に加熱され、それらと隣接するFeも局所的に同等レベルの温度にまで加熱される）も含め、要因(2)が理由として大きいのではないかと推定される。 With respect to the lobe river ore in Test Example 2 and the neutralized sludge in Test Example 3, when microwaves of 24 GHz rather than 2.45 GHz were used (and the maximum temperature was when heated by microwaves of 24 GHz) Although it is lower), the reduction of iron oxide (pyrolysis reaction) is greatly promoted, and the reason why the reduction is proceeding beyond the theoretically possible level is unclear. (1) The strong electromagnetic field of microwaves at 24 GHz promoted the oxygen dissociation phenomenon by some mechanism. The internal temperature of the ore and neutralized sludge particles was significantly higher than the temperature measured by the thermocouple (only the average temperature of each particle surface was measured) It can be considered. However, with respect to the hematite reagent in the case of Test Example 1, even when heated with a microwave of 24 GHz, since the reduction hardly progresses, Fe contained in the lobe river powder ore and neutralized sludge Factor (2) is large as a reason, including the effects of substances other than (including heating to a higher temperature than Fe due to microwave heating characteristics, and the adjacent Fe is also heated locally to a similar level) It is estimated that.

このように還元剤を外部から何ら添加しない場合、アプリケーター１内の雰囲気は不活性ガス雰囲気、特に不純物として含有される酸素の分圧ができる限り低い雰囲気とした方が、酸化鉄の還元が進行する。しかし、Fe還元率が不活性ガス雰囲気下において還元を行った場合よりも低くても構わないということであれば、特に雰囲気ガス中の酸素分圧は限定される訳ではなく、通常の空気雰囲気下において２４GHzのマイクロ波による加熱を実施しても構わない。 Thus, when no reducing agent is added from the outside, reduction of iron oxide proceeds in an atmosphere of the applicator 1 that is an inert gas atmosphere, particularly an atmosphere in which the partial pressure of oxygen contained as an impurity is as low as possible. To do. However, the oxygen partial pressure in the atmosphere gas is not particularly limited as long as the Fe reduction rate may be lower than that in the case of performing the reduction in an inert gas atmosphere, and the normal air atmosphere Below, heating by microwaves of 24 GHz may be performed.

これら酸化鉄含有物質（上述の試験例１〜３では、ヘマタイト試薬、ローブリバー鉱石、中和スラッジ等）のマイクロ波加熱後のFe還元率を更に高めるためには、酸化鉄含有物質が還元剤と共存する状態において、前記マイクロ波を前記酸化鉄含有物質へ照射することが有効である。特に、酸化鉄含有物質に炭素等の還元性物質が含まれていない場合は、何らかの還元剤を外部から添加するとより有効である。この場合の還元剤としては、固体状の還元剤（石炭、コークス、チャー、カーボンブラック、黒鉛、木質バイオマス、下水汚泥、廃プラスチック、廃タイヤ等）、液体状の還元剤（コールタール、メタノール、エタノール等）、あるいは、ガス状の還元剤（水素、一酸化炭素、メタン、コークス炉ガス、高炉ガス、石炭ガス化ガス、メタン改質ガス、コークス炉ガス改質ガス、高炉ガス改質ガス等）等が挙げられ、何を使用しても構わない。固体状及び液体状の還元剤を使用する場合には、酸化鉄含有物質と事前に混合すればよく、また、ガス状の還元剤を使用する場合には、アプリケーター内の雰囲気ガスをこれらガス状の還元剤雰囲気にすればよい。 In order to further increase the Fe reduction rate after microwave heating of these iron oxide-containing substances (in the above-described Test Examples 1 to 3, hematite reagent, lobe river ore, neutralized sludge, etc.), the iron oxide-containing substance is a reducing agent. It is effective to irradiate the iron oxide-containing substance with the microwave in a state where it coexists with the iron oxide. In particular, when the iron oxide-containing substance does not contain a reducing substance such as carbon, it is more effective to add some reducing agent from the outside. In this case, as the reducing agent, solid reducing agent (coal, coke, char, carbon black, graphite, woody biomass, sewage sludge, waste plastic, waste tire, etc.), liquid reducing agent (coal tar, methanol, Ethanol etc.) or gaseous reducing agent (hydrogen, carbon monoxide, methane, coke oven gas, blast furnace gas, coal gasification gas, methane reformed gas, coke oven gas reformed gas, blast furnace gas reformed gas, etc. ), Etc., and anything may be used. When solid and liquid reducing agents are used, they may be mixed in advance with an iron oxide-containing substance, and when a gaseous reducing agent is used, the atmospheric gas in the applicator may be mixed with these gaseous substances. The reducing agent atmosphere may be used.

一般的に、鉄鉱石等の酸化鉄から還元鉄を製造するプロセスにおいては、安価な固体状の還元剤を使用する場合や、還元速度が速くより低温で還元を行うことができるガス状の還元剤を使用する場合が多いが、酸化鉄含有物質と一様に混合した状態にすることができれば、液体状の還元剤を使用しても構わない。また、固体状又は液体状の還元剤を使用する場合、これら還元剤が燃焼して消失しないように、アプリケーター１内の雰囲気ガスを、酸素を含まない不活性ガス（窒素、アルゴン等）雰囲気とする必要がある。勿論、不活性ガス雰囲気中に若干（3vol%程度以下）の酸素が含まれていても構わないが、その酸素は還元剤を燃焼させ、消失させてしまうため、その消失分を見込んだ分の還元剤を余分に添加する必要がある。更に、固体状、液体状、ガス状の還元剤をいくつか組み合わせて使用しても何ら問題とはならない。 In general, in the process of producing reduced iron from iron oxides such as iron ore, when using an inexpensive solid reducing agent, or when the reduction rate is high, the reduction rate can be reduced at a lower temperature. In many cases, an agent is used, but a liquid reducing agent may be used as long as it can be uniformly mixed with the iron oxide-containing substance. Further, when using a solid or liquid reducing agent, the atmospheric gas in the applicator 1 is changed to an inert gas (nitrogen, argon, etc.) atmosphere not containing oxygen so that the reducing agent does not burn and disappear. There is a need to. Of course, the inert gas atmosphere may contain some (less than 3vol%) oxygen, but the oxygen burns the reducing agent and disappears. It is necessary to add extra reducing agent. Furthermore, there is no problem even if some combinations of solid, liquid and gaseous reducing agents are used.

ジャイロトロン４から発生させるマイクロ波の周波数としては、何ら２４GHzに限定される訳ではなく、２．４５GHzの１０倍程度のエネルギー密度（電磁場強度）を持つ２０GHz以上３０GHz以下程度、好ましくは２４GHz以上２８GHz以下程度の範囲内の周波数であれば何れでも構わない。なお、３０GHzよりも更に大きな周波数領域のマイクロ波を用いることも可能ではあるが、以下の式（２）に示す通り、マイクロ波の浸透深さ（侵入深さ）は逆に高周波側のマイクロ波を用いることによって浅くなるため、３０GHzより大きな周波数のマイクロ波を用いた場合、被加熱物質全体を均一に加熱できなくなる恐れがあるため好ましくない。また、２４GHzおよび２８GHzの周波数のマイクロ波発信装置は、比較的入手し易く、コストも比較的安いため、好ましい。 The frequency of the microwave generated from the gyrotron 4 is not limited to 24 GHz, and is 20 GHz to 30 GHz, preferably 24 GHz to 28 GHz, having an energy density (electromagnetic field strength) about 10 times that of 2.45 GHz. Any frequency within the following range may be used. Although it is possible to use microwaves in a frequency region larger than 30 GHz, as shown in the following formula (2), the microwave penetration depth (penetration depth) is conversely the microwave on the high frequency side. When microwaves with a frequency higher than 30 GHz are used, there is a possibility that the whole heated material cannot be heated uniformly, which is not preferable. In addition, microwave transmission devices with frequencies of 24 GHz and 28 GHz are preferable because they are relatively easy to obtain and the cost is relatively low.

δ：浸透深さ[m]
ｆ：周波数[Hz]
μ：透磁率[H/m]
σ：導電率[S/m]

δ: penetration depth [m]
f: Frequency [Hz]
μ: Permeability [H / m]
σ: Conductivity [S / m]

本発明において、酸化鉄含有物質としては、前述したヘマタイト試薬、ローブリバー鉱石、中和スラッジのみに限定される訳ではなく、ローブリバー以外の鉄鉱石、製鉄所から発生する中和スラッジ以外の副産物（含油スラッジ、高炉ダスト、転炉ダスト等）等、ヘマタイトやゲーサイトを含む酸化鉄を含有するものであればよく、何を用いても構わない。また、これら酸化鉄含有物質を他の前処理設備（乾燥設備、予熱設備、予備還元設備等）で予め一度処理した後のものを、本発明の酸化鉄含有物質として、マイクロ波加熱処理しても構わない。 In the present invention, the iron oxide-containing substance is not limited to the aforementioned hematite reagent, lobe river ore, and neutralized sludge, but iron ore other than lobe river and by-products other than neutralized sludge generated from steelworks. Any material may be used as long as it contains iron oxide containing hematite or goethite (oil-containing sludge, blast furnace dust, converter dust, etc.). In addition, after these iron oxide-containing substances have been treated once in other pretreatment equipment (drying equipment, preheating equipment, prereduction equipment, etc.), they are subjected to microwave heat treatment as the iron oxide-containing substance of the present invention. It doesn't matter.

本発明の方法により酸化鉄含有物質をマイクロ波加熱処理して得られた処理物は、製鉄所原料として使用可能である。M-Feの含有割合が大きく、Fe還元率も高い本発明の処理物に関しては、ブリケットに成型した後に高炉原料として用いることが望ましい。また、ブリケットに成型せずに粉体のまま高炉の羽口から吹き込むことによって高炉原料として用いることも可能である。これら還元後の試料を原料として用いることによって、高炉での還元剤（コークス、微粉炭等）の使用量を削減することが可能となる。また、M-Feがほとんど含有されず、ウスタイト又はマグネタト程度までの還元しか生じていない試料に関しては、粉体のままの状態で焼結機原料として用いることが望ましい。これら還元後の本発明の処理物を原料として用いることによって、焼結機での燃料（粉コークス、無煙炭等）の使用量を削減することが可能となる。 The processed product obtained by subjecting the iron oxide-containing substance to microwave heat treatment by the method of the present invention can be used as a raw material for ironworks. Regarding the treated product of the present invention having a high M-Fe content ratio and a high Fe reduction rate, it is desirable to use it as a blast furnace raw material after being formed into briquettes. Moreover, it is also possible to use it as a blast furnace raw material by blowing it from a tuyere of a blast furnace without forming it into a briquette. By using these reduced samples as raw materials, the amount of reducing agent (coke, pulverized coal, etc.) used in the blast furnace can be reduced. In addition, it is desirable to use the sample as a raw material for the sintering machine in a powder state with respect to a sample that hardly contains M-Fe and that has been reduced only to the extent of wustite or magnetite. By using the processed product of the present invention after reduction as a raw material, it is possible to reduce the amount of fuel (powder coke, anthracite, etc.) used in the sintering machine.

（実施例１）
図６に示した図１と同様のマイクロ波加熱処理装置を用いて、実施例１に係る本発明例を実施した。
アプリケーター１内には、被加熱物質２としてヘマタイト試薬（特級：純度99.0%以上、100g）を配置すると共に、このアプリケーター１内に雰囲気ガス５として水素を流通させ、ジャイロトロン４から２４GHzのマイクロ波を発振させて被加熱物質２に対して２４GHzのマイクロ波照射（出力400W、マルチモード）を行ったところ、２０分間で９００℃にまで急速に昇温したため、その温度のまま３０分間加熱処理を行った。なお、温度測定には熱電対７を用い、ヘマタイト試薬の粉体と熱電対測温部が充分接触した状態にて測定した。 Example 1
The present invention example according to Example 1 was carried out using the same microwave heat treatment apparatus as shown in FIG. 1 shown in FIG.
In the applicator 1, a hematite reagent (special grade: purity 99.0% or more, 100 g) is disposed as the material to be heated 2, and hydrogen is circulated in the applicator 1 as an atmospheric gas 5, and a microwave of 24 GHz from the gyrotron 4 is used. Was oscillated and 24GHz microwave irradiation (output 400W, multimode) was applied to the material 2 to be heated. The temperature was rapidly raised to 900 ° C in 20 minutes. went. In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder of the hematite reagent and the thermocouple temperature-measurement part contacted sufficiently.

表６に、マイクロ波加熱処理後のヘマタイト試薬の組成及びFe還元率を示す。この表６に示す結果から明らかなように、実施例１においては、ヘマタイト試薬中のヘマタイトの大部分を金属鉄にまで効率良く還元することができた。 Table 6 shows the composition of the hematite reagent and the Fe reduction rate after the microwave heat treatment. As apparent from the results shown in Table 6, in Example 1, most of the hematite in the hematite reagent could be efficiently reduced to metallic iron.

（実施例２）
図６に示した図１と同様のマイクロ波加熱処理装置を用いて、実施例２に係る本発明例を実施した。
アプリケーター１内には、被加熱物質２として表２に示す組成のローブリバー粉鉱石（粒径1〜3mm、150g）を配置すると共に、雰囲気ガス５として窒素（不純物として含有される酸素の分圧は10^-4MPa）を流通させ、ジャイロトロン４から２４GHzのマイクロ波を発振させて被加熱物質２に対して２４GHzのマイクロ波照射（出力400W、マルチモード）を行ったところ、３０分間で１２００℃にまで急速に昇温したため、その温度のまま３０分間加熱処理を行った。なお、温度測定には熱電対７を用い、ローブリバー粉鉱石の粉体と熱電対測温部が充分接触した状態にて測定した。 (Example 2)
The present invention example according to Example 2 was carried out using the same microwave heat treatment apparatus as shown in FIG. 1 shown in FIG.
In the applicator 1, lobe river powder ore (particle size 1 to 3 mm, 150 g) having the composition shown in Table 2 is arranged as the material to be heated 2, and nitrogen (partial pressure of oxygen contained as an impurity) is used as the atmosphere gas 5. 10 ^-4 MPa) was circulated, and a microwave of 24 GHz was oscillated from the gyrotron 4 to irradiate the material 2 to be heated with a microwave of 24 GHz (output 400 W, multimode). Since the temperature was rapidly raised to 0 ° C., heat treatment was performed for 30 minutes at that temperature. In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder of the lobe river powder ore and the thermocouple temperature-measurement part contacted sufficiently.

表７に、マイクロ波加熱処理後のローブリバー粉鉱石の組成及びFe還元率を示す。この表７に示す結果から明らかなように、実施例２においては、ローブリバー粉鉱石中のヘマタイト（あるいはゲーサイト）をマグネタイトとウスタイトの混合状態にまで還元（Fe還元率とＸ線回折分析結果から推定）することができた。また、これらマイクロ波加熱処理後の粉鉱石は、製鉄所における焼結機原料として使用することによって、焼結機で使用する燃料（粉コークス、無煙炭等）を削減することができた。 Table 7 shows the composition of the lobe river powder ore after the microwave heat treatment and the Fe reduction rate. As is apparent from the results shown in Table 7, in Example 2, hematite (or goethite) in lobe river powder ore is reduced to a mixed state of magnetite and wustite (Fe reduction rate and X-ray diffraction analysis results). It was possible to estimate). Moreover, by using the powdered ore after the microwave heat treatment as a raw material for a sintering machine at an ironworks, it was possible to reduce fuel (powder coke, anthracite, etc.) used in the sintering machine.

（実施例３）
図６に示した図１と同様のマイクロ波加熱処理装置を用いて、実施例３に係る本発明例を実施した。
アプリケーター１内には、被加熱物質２として表２に示す組成のローブリバー粉鉱石（粒径1〜3mm、150g）を配置すると共に、雰囲気ガス５として水素を流通させ、ジャイロトロン４から２４GHzのマイクロ波を発振させて被加熱物質２に対して２４GHzのマイクロ波照射（出力400W、マルチモード）を行ったところ、２０分間で９００℃にまで急速に昇温したため、その温度のまま３０分間加熱処理を行った。なお、温度測定には熱電対７を用い、ローブリバー粉鉱石の粉体と熱電対測温部が充分接触した状態にて測定した。 (Example 3)
The present invention example according to Example 3 was carried out using the same microwave heat treatment apparatus as shown in FIG. 1 shown in FIG.
In the applicator 1, lobe river powder ore (particle size 1 to 3 mm, 150 g) having the composition shown in Table 2 is disposed as the heated material 2, and hydrogen is circulated as the atmosphere gas 5, and the gyrotron 4 has a frequency of 24 GHz. Microwave was oscillated and 24GHz microwave irradiation (output 400W, multimode) was applied to the material 2 to be heated. The temperature rapidly increased to 900 ° C in 20 minutes. Processed. In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder of the lobe river powder ore and the thermocouple temperature-measurement part contacted sufficiently.

表８に、マイクロ波加熱処理後のローブリバー粉鉱石の組成及びFe還元率を示す。この表８に示す結果から明らかなように、実施例３においては、ローブリバー粉鉱石中のヘマタイト（あるいはゲーサイト）をほぼ金属鉄の状態にまで迅速に還元することが可能であった。また、これらマイクロ波加熱処理後の粉鉱石は、ブリケットに成型した後、製鉄所における高炉原料として使用することによって、高炉で使用する燃料あるいは還元剤（コークス、微粉炭等）を削減することができた。 Table 8 shows the composition of the lobe river powder ore after the microwave heat treatment and the Fe reduction rate. As is clear from the results shown in Table 8, in Example 3, hematite (or goethite) in the lobe river powder ore could be rapidly reduced to almost the state of metallic iron. In addition, the powdered ore after the microwave heat treatment is formed into briquettes and then used as a blast furnace raw material in an ironworks, thereby reducing the fuel or reducing agent (coke, pulverized coal, etc.) used in the blast furnace. did it.

（実施例４）
図６に示した図１と同様のマイクロ波加熱処理装置を用いて、実施例４に係る本発明例を実施した。
アプリケーター１内には、被加熱物質２として表２に示す組成のローブリバー粉鉱石（粒径1〜3mm、150g）と表９に示す組成の粉コークス（粒径3mm以下、平均粒径0.7mm、38g）との混合物（質量比としてローブリバー粉鉱石100：粉コークス25）を配置すると共に、雰囲気ガス５として窒素（不純物として含有される酸素の分圧は10^-4MPa）を流通させ、ジャイロトロン４から２４GHzのマイクロ波を発振させて被加熱物質２に対して２４GHzのマイクロ波照射（出力400W、マルチモード）を行ったところ、２５分間で１３００℃にまで急速に昇温したため、その温度のまま３０分間加熱処理を行った。なお、温度測定には熱電対７を用い、ローブリバー粉鉱石と粉コークスの混合物からなる粉体と熱電対測温部が充分接触した状態にて測定した。 Example 4
The present invention example according to Example 4 was carried out using the same microwave heat treatment apparatus as shown in FIG. 1 shown in FIG.
In the applicator 1, the lobe river powder ore having the composition shown in Table 2 (particle size 1 to 3 mm, 150 g) and the powdered coke having the composition shown in Table 9 (particle size 3 mm or less, average particle size 0.7 mm) , 38 g) (lobe river fine ore 100: fine coke 25 as mass ratio) and nitrogen (the partial pressure of oxygen contained as impurities is 10 ⁻⁴ MPa) as an atmospheric gas 5 circulates, When the microwave of 24 GHz was oscillated from the gyrotron 4 and the microwave irradiation of 24 GHz was applied to the heated material 2 (output 400 W, multimode), the temperature rapidly increased to 1300 ° C. in 25 minutes. The heat treatment was performed for 30 minutes while maintaining the temperature. In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder and the thermocouple temperature-measurement part which consisted of the mixture of lobe river powder ore and powder coke fully contacted.

表１０に、マイクロ波加熱処理後のローブリバー粉鉱石と粉コークスとの混合物について、その組成及びFe還元率を示す。この表１０に示す結果から明らかなように、実施例４においては、ローブリバー粉鉱石中のヘマタイト（あるいはゲーサイト）の多くを金属鉄の状態にまで迅速に還元することが可能であった。これら加熱後の粉鉱石は、ブリケットに成型した後、製鉄所における高炉原料として使用することによって、高炉で使用する燃料あるいは還元剤（コークス、微粉炭等）を削減することができた。 In Table 10, the composition and Fe reduction | restoration rate are shown about the mixture of the lobe river powder ore and the powder coke after a microwave heat processing. As is clear from the results shown in Table 10, in Example 4, it was possible to quickly reduce most of the hematite (or goethite) in the lobe river powder ore to the state of metallic iron. The powdered ore after heating was formed into briquettes and then used as a blast furnace raw material in an ironworks, thereby reducing the fuel or reducing agent (coke, pulverized coal, etc.) used in the blast furnace.

（実施例５）
図６に示した図１と同様のマイクロ波加熱処理装置を用いて、実施例５に係る本発明例を実施した。
アプリケーター１内には、被加熱物質２として表４に示す組成の中和スラッジ（事前に別途乾燥機によって水分5%以下にまで乾燥したもの、平均粒径30μm、50g）を配置すると共に、雰囲気ガス５として窒素（不純物として含有される酸素の分圧は10^-4MPa）を流通させ、ジャイロトロン４から２４GHzのマイクロ波を発振させて被加熱物質２に対して２４GHzのマイクロ波照射（出力400W、マルチモード）を行ったところ、３０分間で１２００℃にまで急速に昇温したため、その温度のまま３０分間加熱処理を行った。なお、温度測定には熱電対７を用い、ローブリバー粉鉱石と粉コークスの混合物からなる粉体と熱電対測温部が充分接触した状態にて測定した。 (Example 5)
The present invention example according to Example 5 was carried out using the same microwave heat treatment apparatus as shown in FIG. 1 shown in FIG.
In the applicator 1, neutralized sludge having the composition shown in Table 4 (substance previously dried to a moisture content of 5% or less by a dryer, average particle size of 30 μm, 50 g) is arranged as the substance to be heated 2 and the atmosphere. Nitrogen (partial pressure of oxygen contained as an impurity is 10 ⁻⁴ MPa) is circulated as gas 5, and a microwave of 24 GHz is oscillated from the gyrotron 4 to irradiate the heated material 2 with microwaves of 24 GHz (output) (400W, multimode), the temperature was rapidly raised to 1200 ° C. in 30 minutes, and heat treatment was performed for 30 minutes at that temperature. In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder and the thermocouple temperature-measurement part which consisted of the mixture of lobe river powder ore and powder coke fully contacted.

表１１に、マイクロ波加熱処理後の中和スラッジの組成及びFe還元率を示す。この表１１に示す結果から明らかなように、実施例５においては、中和スラッジ中のヘマタイト（あるいはゲーサイト）をウスタイト程度にまで還元（Fe還元率とＸ線回折分析結果から推定）することができた。また、これらマイクロ波加熱処理後の中和スラッジは、製鉄所における焼結機原料として使用することによって、焼結機で使用する燃料（粉コークス、無煙炭等）を削減することができた。 Table 11 shows the composition and Fe reduction rate of the neutralized sludge after the microwave heat treatment. As is clear from the results shown in Table 11, in Example 5, hematite (or goethite) in the neutralized sludge is reduced to the level of wustite (estimated from the Fe reduction rate and X-ray diffraction analysis results). I was able to. Further, by using the neutralized sludge after the microwave heat treatment as a raw material for a sintering machine at an ironworks, it was possible to reduce fuel (powder coke, anthracite, etc.) used in the sintering machine.

（比較例１）
図７に示した図１と同様のマイクロ波加熱処理装置を用いて、比較例１に係るマイクロ波加熱処理を実施した。
アプリケーター１内には、被加熱物質２としてヘマタイト試薬（特級：純度99.0%以上、100g）を配置すると共に、雰囲気ガス５として水素を流通させ、マグネトロン３から２．４５GHzのマイクロ波を発振させて実施例１と同じ出力（出力400W、マルチモード）でマイクロ波照射をしたところ、６０分間照射しても４０℃までにしか昇温しなかった。なお、温度測定には熱電対７を用い、ヘマタイト試薬の粉体と熱電対測温部が充分接触した状態にて測定した。
マイクロ波加熱処理後のヘマタイト試薬に関しては全く還元が進行していなかった。 (Comparative Example 1)
The microwave heat treatment according to Comparative Example 1 was performed using the same microwave heat treatment apparatus as in FIG. 1 shown in FIG.
In the applicator 1, a hematite reagent (special grade: purity 99.0% or more, 100 g) is arranged as the material to be heated 2, hydrogen is circulated as the atmosphere gas 5, and a 2.45 GHz microwave is oscillated from the magnetron 3. When microwave irradiation was performed with the same output as in Example 1 (output 400 W, multimode), the temperature increased only to 40 ° C. even after 60 minutes of irradiation. In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder of the hematite reagent and the thermocouple temperature-measurement part contacted sufficiently.
Regarding the hematite reagent after the microwave heat treatment, the reduction did not proceed at all.

（比較例２）
図７に示した図１と同様のマイクロ波加熱処理装置を用いて、比較例２に係るマイクロ波加熱処理を実施した。
アプリケーター１内には、被加熱物質２として表２に示す組成のローブリバー粉鉱石（粒径1〜3mm、150g）を配置すると共に、雰囲気ガス５として窒素（不純物として含有される酸素の分圧は10^-4MPa）を流通させ、マグネトロン３から２．４５GHzのマイクロ波を発振させて実施例２と同じ出力（出力400W、マルチモード）でマイクロ波照射をしたところ、１２０分間で１２００℃にまで昇温したため、その温度のまま３０分間加熱処理を行った。なお、温度測定には熱電対７を用い、ローブリバー粉鉱石の粉体と熱電対測温部が充分接触した状態にて測定した。 (Comparative Example 2)
Using the same microwave heat treatment apparatus as FIG. 1 shown in FIG. 7, the microwave heat treatment according to Comparative Example 2 was performed.
In the applicator 1, lobe river powder ore (particle size 1 to 3 mm, 150 g) having the composition shown in Table 2 is arranged as the material to be heated 2, and nitrogen (partial pressure of oxygen contained as an impurity) is used as the atmosphere gas 5. 10 ⁻⁴ MPa) was circulated, and a 2.45 GHz microwave was oscillated from the magnetron 3 and was irradiated with microwaves at the same output (output 400 W, multimode) as in Example 2; Therefore, the heat treatment was performed for 30 minutes at that temperature. In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder of the lobe river powder ore and the thermocouple temperature-measurement part contacted sufficiently.

表１２に、マイクロ波加熱処理後のローブリバー粉鉱石の組成及びFe還元率を示す。この表１２に示す結果から明らかなように、比較例２においては、実施例２と比較して、昇温に時間を要したため全体の処理時間が大幅に長くなった。また、ローブリバー粉鉱石中のヘマタイト（あるいはゲーサイト）は極一部がマグネタイトにまで還元（Fe還元率とＸ線回折分析結果から推定）したに過ぎなかった。 Table 12 shows the composition and Fe reduction rate of the lobe river powder ore after the microwave heat treatment. As is clear from the results shown in Table 12, in Comparative Example 2, compared with Example 2, it took time to raise the temperature, so the entire processing time was significantly increased. In addition, hematite (or goethite) in lobe river powder ore was only partially reduced to magnetite (estimated from Fe reduction rate and X-ray diffraction analysis results).

（比較例３）
図７に示した図１と同様のマイクロ波加熱処理装置を用いて、比較例３に係るマイクロ波加熱処理を実施した。
アプリケーター１内には、被加熱物質２として表２に示す組成のローブリバー粉鉱石（粒径1〜3mm、150g）を配置すると共に、雰囲気ガス５として水素を流通させ、マグネトロン３から２．４５GHzのマイクロ波を発振させて実施例３と同じ出力（出力400W、マルチモード）でマイクロ波照射をしたところ、８５分間で９００℃にまで昇温したため、その温度のまま３０分間加熱処理を行った。なお、温度測定には熱電対７を用い、ローブリバー粉鉱石の粉体と熱電対測温部が充分接触した状態にて測定した。 (Comparative Example 3)
Using the same microwave heat treatment apparatus as FIG. 1 shown in FIG. 7, the microwave heat treatment according to Comparative Example 3 was performed.
In the applicator 1, lobe river powder ore (particle size 1 to 3 mm, 150 g) having the composition shown in Table 2 is arranged as the material to be heated 2, and hydrogen is circulated as the atmosphere gas 5, and 2.45 GHz from the magnetron 3. When microwave irradiation was performed with the same output (output 400 W, multimode) as in Example 3 and the temperature was raised to 900 ° C. in 85 minutes, heat treatment was performed for 30 minutes at that temperature. . In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder of the lobe river powder ore and the thermocouple temperature-measurement part contacted sufficiently.

表１３に、マイクロ波加熱処理後のローブリバー粉鉱石の組成及びFe還元率を示す。この表１３に示す結果から明らかなように、比較例３においては、実施例３と比較して、昇温に時間を要したため全体の処理時間が大幅に長くなった。また、ローブリバー粉鉱石中のヘマタイト（あるいはゲーサイト）をほぼ金属鉄の状態にまで還元することが可能であったが、還元率は実施例３よりも小さかった。 Table 13 shows the composition of the lobe river powder ore after the microwave heat treatment and the Fe reduction rate. As is apparent from the results shown in Table 13, in Comparative Example 3, compared with Example 3, it took a long time to raise the temperature, so that the entire processing time was significantly increased. Moreover, although it was possible to reduce the hematite (or goethite) in the lobe river powder ore to almost the metallic iron state, the reduction rate was smaller than that in Example 3.

（比較例４）
図７に示した図１と同様のマイクロ波加熱処理装置を用いて、比較例４に係るマイクロ波加熱処理を実施した。
アプリケーター１内には、被加熱物質２として表２に示す組成のローブリバー粉鉱石（粒径1〜3mm、150g）と表９に示す組成の粉コークス（粒径3mm以下、平均粒径0.7mm、38g）との混合物（質量比としてローブリバー粉鉱石100：粉コークス25）を配置すると共に、雰囲気ガス５として窒素（不純物として含有される酸素の分圧は10^-4MPa）を流通させ、マグネトロン３から２．４５GHzのマイクロ波を発振させて実施例４と同じ出力（出力400W、マルチモード）でマイクロ波照射をしたところ、４０分間で１３００℃にまで昇温したため、その温度のまま３０分間加熱処理を行った。なお、温度測定には熱電対７を用い、ローブリバー粉鉱石と粉コークスの混合物の粉体と熱電対測温部が充分接触した状態にて測定した。 (Comparative Example 4)
The microwave heat treatment according to Comparative Example 4 was performed using the same microwave heat treatment apparatus as in FIG. 1 shown in FIG.
In the applicator 1, the lobe river powder ore having the composition shown in Table 2 (particle size 1 to 3 mm, 150 g) and the powdered coke having the composition shown in Table 9 (particle size 3 mm or less, average particle size 0.7 mm) , 38 g) (lobe river fine ore 100: fine coke 25 as mass ratio) and nitrogen (the partial pressure of oxygen contained as impurities is 10 ⁻⁴ MPa) as an atmospheric gas 5 circulates, When a microwave of 2.45 GHz was oscillated from the magnetron 3 and was irradiated with microwaves at the same output (output 400 W, multimode) as in Example 4, the temperature was raised to 1300 ° C. in 40 minutes. Heat treatment was performed for a minute. In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder of the mixture of the lobe river powder ore and the powder coke, and the thermocouple temperature-measurement part fully contacted.

表１４に、マイクロ波加熱処理後のローブリバー粉鉱石と粉コークのとの混合物について、その組成及びFe還元率を示す。この表１４に示す結果から明らかなように、比較例４においては、ローブリバー粉鉱石中のヘマタイト（あるいはゲーサイト）の多くを金属鉄の状態にまで迅速に還元することが可能であったが、実施例４よりも若干処理時間は長くなり、かつFe還元率は小さかった。 In Table 14, the composition and Fe reduction | restoration rate are shown about the mixture of the lobe river powder ore and the powder coke after a microwave heat processing. As is apparent from the results shown in Table 14, in Comparative Example 4, it was possible to quickly reduce most of the hematite (or goethite) in the lobe river powder ore to the state of metallic iron. The treatment time was slightly longer than in Example 4, and the Fe reduction rate was small.

（比較例５）
図７に示した図１と同様のマイクロ波加熱処理装置を用いて、比較例５に係るマイクロ波加熱処理を実施した。
アプリケーター１内には、被加熱物質２として表４に示す組成の中和スラッジ（事前に別途乾燥機によって水分5%以下にまで乾燥したもの、平均粒径30μm）を配置すると共に、雰囲気ガス５として窒素（不純物として含有される酸素の分圧は10^-4MPa）を流通させ、マグネトロン３から２．４５GHzのマイクロ波を発振させて実施例５と同じ出力（出力400W、マルチモード）でマイクロ波照射をしたところ、３０分間で１２００℃にまで昇温したため、その温度のまま３０分間加熱処理を行った。なお、温度測定には熱電対７を用い、中和スラッジの粉体と熱電対測温部が充分接触した状態にて測定した。 (Comparative Example 5)
The microwave heat treatment according to Comparative Example 5 was performed using the same microwave heat treatment apparatus as in FIG. 1 shown in FIG.
In the applicator 1, neutralized sludge having the composition shown in Table 4 (substance previously dried to a moisture content of 5% or less by a dryer, average particle size of 30 μm) is disposed as the substance to be heated 2, and the atmosphere gas 5 As a result, nitrogen (the partial pressure of oxygen contained as an impurity is 10 ⁻⁴ MPa) was circulated, and a 2.45 GHz microwave was oscillated from the magnetron 3, and the same output (output 400 W, multimode) as in Example 5 was used. When wave irradiation was performed, the temperature was raised to 1200 ° C. in 30 minutes, and heat treatment was performed at that temperature for 30 minutes. In addition, the thermocouple 7 was used for temperature measurement, and it measured in the state which the powder of neutralization sludge and the thermocouple temperature-measurement part contacted sufficiently.

表１５に、マイクロ波加熱処理後の中和スラッジの組成及びFe還元率を示す。この表１４に示す結果から明らかなように、比較例５においては、実施例５と比較して還元率は小さく、中和スラッジ中のヘマタイト（あるいはゲーサイト）をマグネタイト程度にしか還元（Fe還元率とＸ線回折分析結果から推定）することができなかった。 Table 15 shows the composition of the neutralized sludge after the microwave heat treatment and the Fe reduction rate. As is apparent from the results shown in Table 14, in Comparative Example 5, the reduction rate is small compared to Example 5, and hematite (or goethite) in the neutralized sludge is reduced only to the extent of magnetite (Fe reduction). Rate and X-ray diffraction analysis result).

１…アプリケーター（反応器）、２…被加熱物質、３…マグネトロン、４…ジャイロトロン、５…雰囲気ガス、６…排ガス、７…熱電対。 DESCRIPTION OF SYMBOLS 1 ... Applicator (reactor), 2 ... Heated material, 3 ... Magnetron, 4 ... Gyrotron, 5 ... Atmospheric gas, 6 ... Exhaust gas, 7 ... Thermocouple.

Claims

ヘマタイト及びゲーサイトのうちの少なくともいずれか一方を含む酸化鉄含有物質に対して２０〜３０GHzの領域の周波数を持つマイクロ波を照射することにより、前記酸化鉄含有物質を加熱し、前記酸化鉄含有物質中に含有される前記ヘマタイト及びゲーサイトのうちの少なくともいずれかを含む酸化鉄を還元することを特徴とするマイクロ波加熱による酸化鉄含有物質の還元方法。 The iron oxide-containing substance is heated by irradiating the iron oxide-containing substance containing at least one of hematite and goethite with a microwave having a frequency in a range of 20 to 30 GHz, and the iron oxide-containing substance is heated. A method for reducing an iron oxide-containing substance by microwave heating, comprising reducing iron oxide containing at least one of the hematite and goethite contained in the substance.

前記酸化鉄含有物質への前記マイクロ波の照射を、還元剤と共存する状態で行うことを特徴とする請求項１記載のマイクロ波による酸化鉄含有物質の還元方法。 The method for reducing an iron oxide-containing substance by microwave according to claim 1, wherein the microwave irradiation to the iron oxide-containing substance is performed in a state of coexisting with a reducing agent.

前記還元剤が炭素含有物質であり、この還元剤を前記酸化鉄含有物質に添加して得られた混合物へマイクロ波を照射することを特徴とする請求項２に記載のマイクロ波加熱による酸化鉄含有物質の還元方法。 The iron oxide by microwave heating according to claim 2, wherein the reducing agent is a carbon-containing substance, and the mixture obtained by adding the reducing agent to the iron oxide-containing substance is irradiated with microwaves. Reduction method of contained substances.

前記還元剤が還元性ガスであり、前記酸化鉄含有物質への前記マイクロ波の照射を前記還元性ガス中で行うことを特徴とする請求項２又は３に記載のマイクロ波による酸化鉄含有物質の還元方法。 4. The microwave-containing iron oxide-containing material according to claim 2, wherein the reducing agent is a reducing gas, and the microwave irradiation to the iron oxide-containing material is performed in the reducing gas. Reduction method.

請求項１〜４のいずれか１項に記載のマイクロ波加熱により酸化鉄含有物質の還元処理を行い、この還元処理された酸化鉄含有物質を、焼結鉱製造プロセスにおける原料とすることを特徴とする焼結鉱製造用原料の製造方法。 The iron oxide-containing substance is reduced by microwave heating according to any one of claims 1 to 4, and the reduced iron oxide-containing substance is used as a raw material in a sintered ore production process. The manufacturing method of the raw material for sinter ore production.

請求項１〜４のいずれか１項に記載のマイクロ波加熱により酸化鉄含有物質の還元処理を行い、この還元処理された酸化鉄含有物質を、高炉プロセスにおける原料とすることを特徴とする高炉原料の製造方法。 A blast furnace characterized in that the iron oxide-containing substance is reduced by microwave heating according to any one of claims 1 to 4, and the reduced iron oxide-containing substance is used as a raw material in a blast furnace process. Raw material manufacturing method.