JP2011147949A - Method and device for deciding breakage in press forming simulation of sheet - Google Patents
Method and device for deciding breakage in press forming simulation of sheet Download PDFInfo
- Publication number
- JP2011147949A JP2011147949A JP2010009584A JP2010009584A JP2011147949A JP 2011147949 A JP2011147949 A JP 2011147949A JP 2010009584 A JP2010009584 A JP 2010009584A JP 2010009584 A JP2010009584 A JP 2010009584A JP 2011147949 A JP2011147949 A JP 2011147949A
- Authority
- JP
- Japan
- Prior art keywords
- fracture
- strain
- gauge length
- limit strain
- determination
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、薄板のプレス成形シミュレーションにおける破断判定方法および破断判定装置に関する。 The present invention relates to a fracture determination method and a fracture determination apparatus in press molding simulation of a thin plate.
金属薄板のプレス成形加工により例えば、自動車部品を製造する際の成形不具合として、材料破断現象である割れが発生することがある。これを加工前に予測することは非常に重要であり、今日、有限要素法等によるシミュレーション計算を利用して割れを予測することが定常的に行われている。具体的には、板厚限界線や成形限界線図(以下、FLDと記す)等の限界歪を実験的あるいは理論的に導出しておき、その限界歪状態とシミュレーションにより計算上得られる歪状態とを比較することにより、割れ発生の有無を判定することが実施されており、割れ発生箇所および発生時点の予測には、ある程度定量性が得られている。 For example, a crack that is a material rupture phenomenon may occur as a molding defect in manufacturing an automobile part by press forming of a thin metal plate. Predicting this before machining is very important, and today, it is routine to predict cracks using simulation calculation by a finite element method or the like. Specifically, a limit strain such as a plate thickness limit line or a forming limit diagram (hereinafter referred to as FLD) is derived experimentally or theoretically, and the limit strain state and the strain state obtained by simulation are calculated. Is used to determine the presence or absence of cracks, and a certain degree of quantification has been obtained in predicting the location and time of occurrence of cracks.
薄板のプレス成形シミュレーションにおける破断判定方法に関しては、従来から種々の提案がなされており、例えば、特開2000−107818号公報(下記特許文献1)には、塑性加工シミュレーションにおいて塑性加工材料が変形させられる過程で、歪応力変化率算出手段(歪応力変化率算出工程)により塑性加工材料の歪εの変化率dε/dtが逐次算出され、破断判定手段(破断判定工程)により、その歪εの変化率dε/dtに基づいて、その塑性加工材料の破断が判定されるので、動的に或いは時間的に変化する歪みの集中度合を考慮でき、塑性加工材料の破断が正確に判定できる方法を提供することが記載されている。
Various proposals have hitherto been made regarding the method for determining fracture in a press forming simulation of a thin plate. For example, Japanese Patent Laid-Open No. 2000-107818 (
また、特開2009−61477号公報(下記特許文献2)には、予め材料の剪断面比率γと限界引張歪εcrとの関係を求めた後、実部品の成形前の剪断面比率γpartを測定する。剪断面比率γpartから実部品の限界歪εcr partを求める。次に、有限要素法で実部品の成形解析を行い、有限要素法の要素毎に算出されたフランジ部の引張歪εと実部品の限界歪εcr partを比較して、伸びフランジ割れの有無を推定することにより、自動車用実部品の伸びフランジ形状設計指針又は設計限界を策定するために、シミュレーション上で伸びフランジ割れを事前予測する方法を提供する方法が記載されている。
Japanese Patent Laid-Open No. 2009-61477 (
また、薄板の成形限界線図の測定方法については、塑性と加工、第47巻、第548号(下記非特許文献1)に記載されている。
The method for measuring the forming limit diagram of the thin plate is described in Plasticity and Processing, Vol. 47, No. 548 (Non-patent
従来、薄板の成形限界は、破断をもって評価することが主に行なわれており、有限要素法を用いた成形シミュレーションでは、板厚減少率やひずみ量で破断判定を行なっている。 Conventionally, the forming limit of a thin plate has been mainly evaluated by breakage, and in a forming simulation using a finite element method, breakage determination is performed by a plate thickness reduction rate or a strain amount.
しかし、成形限界歪の評価に関しては、ひずみを評価する際のゲージ長さ(GL:Gage Length)に注意を払う必要がある。すなわち、成形解析で得られるひずみ量は解析条件である各要素寸法(メッシュサイズ)に依存するため、メッシュサイズの大小により破断判定が異なってくるという問題点があった。 However, regarding the evaluation of the forming limit strain, it is necessary to pay attention to the gauge length (GL) when evaluating the strain. That is, since the amount of strain obtained by forming analysis depends on each element size (mesh size) which is an analysis condition, there is a problem that the determination of breakage differs depending on the size of the mesh size.
本発明は、前述のような従来技術の問題点を解決し、有限要素法を用いた薄板のプレス成形シミュレーションにおいて、各要素寸法(メッシュサイズ)に依存せず正確な破断判定を行うことができる薄板のプレス成形シミュレーションにおける破断判定方法および破断判定装置を提供することを課題とする。 The present invention solves the problems of the prior art as described above, and can perform accurate fracture determination without depending on each element size (mesh size) in press forming simulation of a thin plate using the finite element method. It is an object of the present invention to provide a rupture determination method and a rupture determination device in press molding simulation of a thin plate.
本発明は前述の課題を解決するために鋭意検討の結果、特定のゲージ長さにおける破断限界歪ε1に基づいて、任意のゲージ長さにおける破断限界歪εf1を計算して破断判定を行なうことにより、各要素寸法(メッシュサイズ)に依存せず正確な破断判定を行うことができる薄板のプレス成形シミュレーションにおける破断判定方法および破断判定装置を提供するものであり、その要旨とするところは特許請求の範囲に記載した通りの下記内容である。
(1)有限要素法を用いた薄板のプレス成形シミュレーションにおいて、
特定のゲージ長さにおける破断限界歪ε1に基づいて、任意のゲージ長さにおける破断限界歪εf1を計算し、
該任意のゲージ長さにおける破断限界歪εf1と、有限要素法を用いて計算した各要素の歪量εとを比較することにより、破断判定を行うことを特徴とする、薄板のプレス成形シミュレーションにおける破断判定方法。
(2)前記有限要素法において各要素寸法を自動的に算出し、該各要素寸法と各要素の歪量εに基づいて、各要素の歪がゼロとなる要素寸法である初期相当寸法を計算してゲージ長さを求めることを特徴とする(1)に記載の、薄板のプレス成形シミュレーションにおける破断判定方法。
(3)前記特定のゲージ長さにおける破断限界歪ε1は、素材にサークルまたはグリッドを転写した実験により求めることを特徴とする(1)または(2)に記載の、薄板のプレス成形シミュレーションにおける破断判定方法。
(4)前記特定のゲージ長さにおける破断限界歪ε1は、理論計算により算出することを特徴とする(1)または(2)に記載の、薄板のプレス成形シミュレーションにおける破断判定方法。
(5)(1)乃至(4)のいずれか一項に記載の破断判定方法を実施するための装置であって、
特定のゲージ長さにおける破断限界歪ε1に基づいて、任意のゲージ長さにおける破断限界歪εf1を計算する破断限界歪計算手段と、
該任意のゲージ長さにおける破断限界歪εf1と、有限要素法を用いて計算した各要素の歪量εとを比較することにより破断判定を行う破断判定手段とを有することを特徴とする、薄板のプレス成形シミュレーションにおける破断判定装置。
<作用>
(1)の発明によれば、有限要素法を用いた薄板のプレス成形シミュレーションにおいて、特定のゲージ長さにおける破断限界歪ε1に基づいて、任意のゲージ長さにおける破断限界歪εf1を計算し、該任意のゲージ長さにおける破断限界歪εf1と、有限要素法を用いて計算した各要素の歪量εとを比較することにより破断判定を行うので、従来のように各要素寸法(メッシュサイズ)に依存せず正確な破断判定を行うことができる薄板のプレス成形シミュレーションにおける破断判定方法を提供することができる。
(2)の発明によれば、有限要素法において各要素寸法を自動的に算出し、該各要素寸法と各要素の歪量εに基づいて、各要素の歪がゼロとなる要素寸法である初期相当寸法を計算してゲージ長さを求めることにより、該任意のゲージ長さにおける破断限界歪εf1をさらに正確に求めることができる。
(3)の発明によれば、特定のゲージ長さにおける破断限界歪ε1は、素材にサークルまたはグリッドを転写した実験により求めることにより、実験値に即してゲージ長さにおける破断限界歪εf1を求めることができる。
(4)の発明によれば、特定のゲージ長さにおける破断限界歪ε1は、理論計算により算出することにより、実験をすることなくゲージ長さにおける破断限界歪εf1を求めることができる。
(5)の発明によれば、該任意のゲージ長さにおける破断限界歪εf1と、有限要素法を用いて計算した各要素の歪量εとを比較することにより破断判定を行う破断判定手段とを有することにより、従来のように各要素寸法(メッシュサイズ)に依存せず正確な破断判定を行うことができる薄板のプレス成形シミュレーションにおける破断判定装置を提供することができる。
As a result of intensive studies to solve the above-mentioned problems, the present invention calculates a fracture limit strain ε f1 at an arbitrary gauge length based on the fracture limit strain ε 1 at a specific gauge length and performs a fracture determination. Accordingly, the present invention provides a breakage determination method and a breakage determination apparatus in a press forming simulation of a thin plate that can accurately determine a breakage without depending on each element size (mesh size). It is the following contents as described in the claims.
(1) In the press forming simulation of a thin plate using the finite element method,
Based on the fracture limit strain ε 1 at a specific gauge length, calculate the fracture limit strain ε f1 at an arbitrary gauge length,
A thin plate press-forming simulation characterized by performing fracture determination by comparing the fracture limit strain ε f1 at the arbitrary gauge length and the strain amount ε of each element calculated using a finite element method Break determination method in
(2) Each element dimension is automatically calculated in the finite element method, and an initial equivalent dimension, which is an element dimension at which the distortion of each element becomes zero, is calculated based on each element dimension and the distortion amount ε of each element. Then, the gauge length is obtained, and the fracture determination method in the press molding simulation of the thin plate according to (1).
(3) The fracture limit strain ε 1 at the specific gauge length is obtained by an experiment in which a circle or a grid is transferred to a material, and in the press forming simulation of a thin plate according to (1) or (2) Breaking judgment method.
(4) The fracture determination method in a press molding simulation of a thin plate according to (1) or (2), wherein the fracture limit strain ε 1 at the specific gauge length is calculated by theoretical calculation.
(5) An apparatus for carrying out the fracture determination method according to any one of (1) to (4),
Breaking limit strain calculating means for calculating the breaking limit strain ε f1 at an arbitrary gauge length based on the breaking limit strain ε 1 at a specific gauge length;
It has a fracture determination means for performing fracture determination by comparing the fracture limit strain ε f1 at the arbitrary gauge length and the strain amount ε of each element calculated using a finite element method, Break determination device in thin plate press forming simulation.
<Action>
According to the invention of (1), in the press forming simulation of a thin plate using the finite element method, the fracture limit strain ε f1 at an arbitrary gauge length is calculated based on the fracture limit strain ε 1 at a specific gauge length. Since the fracture determination is performed by comparing the fracture limit strain ε f1 at the arbitrary gauge length with the strain amount ε of each element calculated using the finite element method, each element dimension ( It is possible to provide a fracture determination method in a press forming simulation of a thin plate that can perform accurate fracture determination without depending on the mesh size.
According to the invention of (2), each element dimension is automatically calculated in the finite element method, and the element dimension is such that the distortion of each element becomes zero based on each element dimension and the distortion amount ε of each element. By calculating the initial equivalent dimension and obtaining the gauge length, the fracture limit strain ε f1 at the arbitrary gauge length can be obtained more accurately.
According to the invention of (3), the breaking limit strain ε 1 at a specific gauge length is obtained by an experiment in which a circle or a grid is transferred to the material, and thereby the breaking limit strain ε at the gauge length in accordance with the experimental value. f1 can be obtained.
According to the invention of (4), breakage threshold strain epsilon 1 in a specific gauge length, by calculating the theoretical calculation, it is possible to obtain the fracture limit strain epsilon f1 in gauge length without the experiment.
According to the invention of (5), the fracture determination means for determining fracture by comparing the fracture limit strain ε f1 at the arbitrary gauge length with the strain amount ε of each element calculated using the finite element method. As described above, it is possible to provide a breakage determination device in press molding simulation of a thin plate that can perform accurate breakage determination without depending on each element size (mesh size) as in the prior art.
本発明によれば、特定のゲージ長さにおける破断限界歪ε1に基づいて、任意のゲージ長さにおける破断限界歪εf1を計算して破断判定を行なうことにより、各要素寸法(メッシュサイズ)に依存せず正確な破断判定を行うことができる薄板のプレス成形シミュレーションにおける破断判定方法および破断判定装置を提供することができ、その結果、プレス成形に用いる金型の製作工期の短縮やコスト削減につながる等、産業上有用な著しい効果を奏する。 According to the present invention, each element size (mesh size) is determined by calculating the breaking limit strain ε f1 at an arbitrary gauge length and performing a rupture determination based on the breaking limit strain ε 1 at a specific gauge length. It is possible to provide a fracture determination method and a fracture determination apparatus in a press molding simulation of a thin plate that can perform accurate fracture determination without depending on the process, and as a result, shorten the production period and cost reduction of the mold used for press molding. It has a significant industrially useful effect.
発明を実施するための形態について図1〜図5を用いて詳細に説明する。図1は、本発明の薄板のプレス成形シミュレーションにおける破断判定方法の処理フローを例示する図である。 DESCRIPTION OF EMBODIMENTS Embodiments for carrying out the invention will be described in detail with reference to FIGS. FIG. 1 is a diagram illustrating a processing flow of a fracture determination method in a press molding simulation of a thin plate according to the present invention.
まず、有限要素法を用いた薄板のプレス成形シミュレーションにおいて、特定のゲージ長さにおける破断限界歪ε1を、素材にサークルまたはグリッドまたはグリッドを転写した実験、もしくは、理論計算によりにより求める(S−1)。 First, in a press forming simulation of a thin plate using a finite element method, a fracture limit strain ε 1 at a specific gauge length is obtained by an experiment in which a circle, a grid, or a grid is transferred to a material, or by theoretical calculation (S− 1).
ここに、ゲージ長さ(GL:Gage Length)とは、ひずみを評価する際の基準長さであり,実験においては成形前に転写するサークル径またはグリッドの寸法をいう。 Here, the gauge length (GL: Gage Length) is a reference length for evaluating strain, and in an experiment, refers to a circle diameter or a grid dimension to be transferred before forming.
本発明においては破断限界歪ε1の決定方法は問わないが、例えば、図2に示す成形限界線(FLC)の測定方法−Nakajima法−のように、球頭パンチを用いて張り出し成形を行なって破断する限界歪(最大主歪ε1、最小主歪ε2)を測定することが好ましく、試験片幅を変更してひずみ比を変えた限界歪を測定する。歪の測定は変形前の素材にスクライブドサークルまたはグリッドの格子をエッチングで転写し,例えばゲージ長さ10mmで測定する。サークル径やグリッドの格子寸法を変えることでゲージ長さを変えた限界歪も測定可能であれば,ゲージ長さ6mm以下では測定時のばらつきが大きくなるため,ゲージ長さ6〜10mmで測定することが通常である。 In the present invention, there is no limitation on the method for determining the breaking limit strain ε 1. For example, as shown in FIG. 2, a forming limit line (FLC) measurement method—Nakajima method—is performed by using a ball head punch. It is preferable to measure the critical strain (maximum principal strain ε 1 , minimal principal strain ε 2 ) that breaks, and the critical strain is measured by changing the specimen width to change the strain ratio. Strain is measured by transferring a scribed circle or grid of lattice to the material before deformation by etching, for example, with a gauge length of 10 mm. If the limit strain with the gauge length changed by changing the circle diameter or grid dimensions can be measured, the gauge variation will be larger if the gauge length is 6mm or less. It is normal.
図3は、実験から得られた破断限界歪線(FLC:Forming Line Curve)を例示する図である。実験で測定された破断の際の歪量をプロットし、曲線で結ぶことによって実線で示すような破断限界歪線(FLC)を得ることができる。 FIG. 3 is a diagram illustrating a fracture limit strain line (FLC) obtained from an experiment. By plotting the amount of strain at the time of rupture measured in an experiment and connecting with a curve, a fracture limit strain line (FLC) as indicated by a solid line can be obtained.
なお、この破断限界歪線(FLC)は、例えば、Storen-Riceの理論式によりも求めることができ、この場合は前述のように破断限界歪ε1を実験で求める必要がない。 Note that the fracture limit strain line (FLC) can be obtained by, for example, the Storen-Rice theoretical formula, and in this case, it is not necessary to obtain the fracture limit strain ε 1 by experiment as described above.
図4は、破断限界歪線(FLC)のゲージ長さ依存性を示す実験結果を例示する図である。 FIG. 4 is a diagram illustrating experimental results showing the gauge length dependence of the fracture limit strain line (FLC).
後述の実施例1に用いた鉄連規格JSC270Dについて、ゲージ長さに対する破断ひずみの推移を測定した結果、ゲージ長さが小さいと破断限界歪ε1は大きくなる一方で、ゲージ長さが大きいと破断限界歪ε1は小さくなることが分わかった。 As a result of measuring the transition of the breaking strain with respect to the gauge length of the iron standard JSC270D used in Example 1 to be described later, the fracture limit strain ε 1 increases when the gauge length is small, whereas the fracture occurs when the gauge length is large. It has been found that the critical strain ε 1 becomes smaller.
そこで、前記特定のゲージ長さにおける破断限界歪ε1に基づいて、任意のゲージ長さにおける破断限界歪εf1を計算する(S−2)。例えば、破断判定装置に以下の式を組み込み,特定の基準ゲージ長さの破断限界歪線(FLC)から任意のゲージ長さの破断限界歪線(FLC)に換算することにより、任意のゲージ長さにおける破断限界歪を算出することができ、例えば、以下の実験式を用いてゲージ長さが初期のメッシュ寸法2mmの場合の限界歪に換算することができる。 Therefore, the fracture limit strain ε f1 at an arbitrary gauge length is calculated based on the fracture limit strain ε 1 at the specific gauge length (S-2). For example, by incorporating the following equation into the rupture determination device and converting from a rupture limit strain line (FLC) of a specific reference gauge length to a rupture limit strain line (FLC) of an arbitrary gauge length, an arbitrary gauge length The fracture limit strain at the height can be calculated. For example, it can be converted into the limit strain when the gauge length is the initial mesh size of 2 mm using the following empirical formula.
L:ゲージ長さ
ρ:基準ゲージ長さにおけるひずみ比(ε2/ε1)
ε1:最大主ひずみ
ε2:最小主ひずみ
α:材料ごとの限界歪から得られるパラメータ
β:材料によらずρで決定される関数
次に、前記任意のゲージ長さにおける破断限界歪εf1と、有限要素法を用いて計算した各要素の歪量εとを比較することにより、破断判定を行う(S−3)。
L: Gauge length ρ: Strain ratio at the reference gauge length (ε 2 / ε 1 )
ε 1 : Maximum principal strain ε 2 : Minimum principal strain α: Parameter obtained from limit strain for each material β: Function determined by ρ regardless of material Next, fracture limit strain ε f1 at the arbitrary gauge length Is determined by comparing the strain amount ε of each element calculated using the finite element method (S-3).
即ち、各要素ごとに変形前相当のゲージ長さに換算した破断限界歪線(FLC)と比較し,各要素のひずみ量εが対応する破断限界歪線(FLC)上のεf1を超えているかどうか計算し、超えている場合に破断と判定する。 That is, the strain amount ε of each element exceeds ε f1 on the corresponding fracture limit strain line (FLC) as compared with the fracture limit strain line (FLC) converted into a gauge length equivalent to that before deformation for each element. It is determined whether it is broken or not.
そして、破断判定要素の表示・出力を行なう(S−4)。 Then, the break determination element is displayed / output (S-4).
各要素の歪や応力は、有限要素法を用いた既存のプログラムにより成形解析を行なうことによって算定することができる(S−5)。 The strain and stress of each element can be calculated by performing molding analysis using an existing program using the finite element method (S-5).
各要素寸法は、有限要素法において予め入力したプレス金型の形状から各要素寸法を自動的に算出することによって、より正確な歪や応力を算定することができる(S−6)。 More accurate distortion and stress can be calculated for each element size by automatically calculating each element size from the shape of the press die input in advance in the finite element method (S-6).
また、該各要素寸法と各要素の歪量εに基づいて、各要素の歪がゼロとなる要素寸法である初期相当寸法を計算してゲージ長さを求めることができる(S−7)。 Further, based on the element dimensions and the strain amount ε of each element, the gauge length can be obtained by calculating an initial equivalent dimension that is an element dimension at which the distortion of each element becomes zero (S-7).
図5は、変形前相当の要素寸法を例示する図である。 FIG. 5 is a diagram illustrating the element dimensions corresponding to those before deformation.
解析の各要素のゲージ長さの算出方法は、有限要素法で解析した結果を破断判定装置に読み込み、メッシュ上の各節点座標から各要素の辺長(L1,L2)を算出する。 As a method for calculating the gauge length of each element in the analysis, the result analyzed by the finite element method is read into the fracture determination device, and the side length (L1, L2) of each element is calculated from each node coordinate on the mesh.
また各要素の真歪量(ε1,ε2)を用いて以下式により変形前に相当する要素寸法を算出し、各要素に対してゲージ長さGLを求めることができる。
GL=L1/(1+ε1)
ここではL1>L2とし、L1方向の真歪をε1とする。
Further, by using the true strain amount (ε 1 , ε 2 ) of each element, an element dimension corresponding to that before deformation is calculated by the following equation, and a gauge length GL can be obtained for each element.
GL = L1 / (1 + ε 1 )
Here, the L1> L2, the true strain in the direction of L1 and epsilon 1.
本発明を用いて角筒工具による深絞りの解析を下記に示す条件で行ない、実験結果と比較した。図6は、実施例1に用いた成形品を例示する図である。
<解析条件>
ポンチ寸法70×70mm,コーナーR10mm,パンチ肩R8mm
ダイ寸法74×74mm,コーナーR12mm,パンチ肩R5mm
初期素材寸法170×170mm
しわ押さえ力200kN
材料特性:鉄連規格JSC270D(下記表1)
初期メッシュサイズ:2×2mm
Using the present invention, deep drawing analysis with a square tube tool was performed under the following conditions and compared with the experimental results. FIG. 6 is a diagram illustrating a molded product used in Example 1.
<Analysis conditions>
Punch size 70 × 70mm, corner R10mm, punch shoulder R8mm
Die size 74 × 74mm, corner R12mm, punch shoulder R5mm
Initial material size 170 × 170mm
Wrinkle holding force 200kN
Material characteristics: Iron standard JSC270D (Table 1 below)
Initial mesh size: 2 x 2mm
解析は対称性を考慮し4分の1の領域で実施した.解析の各ステップごとの歪に対し実験による破断限界歪ε1を使って破断判定を行った。図7は、実験で得たゲージ長さ10mmの破断限界歪ε1を用いた場合に破断と判定したステップでの変形形状及び破断と判定された要素の位置を示す図である。矢印は破断と判定された要素を示し、この方法で破断判定を行った結果、成形高さ23.8mmで破断となった。
The analysis was performed in a quarter of the area considering symmetry. The fracture was determined using the experimental fracture limit strain ε 1 for the strain at each step of the analysis. FIG. 7 is a diagram illustrating a deformed shape and a position of an element determined to be broken at a step determined to be broken when a fracture limit strain ε 1 having a gauge length of 10 mm obtained in an experiment is used. The arrow indicates the element determined to be broken, and as a result of determining the fracture by this method, the fracture occurred at a molding height of 23.8 mm.
次に数1の式を用いてゲージ長さ10mmの破断限界歪ε1をゲージ長さ2mmの破断限界歪εf1に換算計算を行い,破断限界歪εf1を使って破断判定を行った。図8は、ゲージ長さ2mmの破断限界歪εf1を用いた場合に破断と判定したステップでの変形形状及び破断と判定された要素の位置を示す図である。矢印は破断と判定された要素を示し、この方法で破断判定を行った結果、成形高さ35.7mmで破断となった。実験結果は35.2mmで破断しており、ε1に比べεf1を用いることで破断の予測精度が格段に向上したことにより、本発明の効果が確認された。
Then perform conversion calculation the breakage threshold strain epsilon 1 of gauge length 10mm to breakage threshold strain epsilon f1 gauge length
本発明を用いて、図9に示すエンボスパネルの深絞り解析の解析を下記に示す条件で行行ない、実験結果と比較した。素材の解析モデル(変形前)を図10に示す。
<解析条件>
パネル寸法:300×450×25mm,コーナーR20mm,肩R4mm
エンボス深さ:4mm
初期素材寸法:370×520mm
しわ押さえ荷重200kN
材料特性:鉄連規格JAC440W(下記表2)
メッシュサイズ:初期24×24mm
(各要素寸法を自動的に計算するアダプティブメッシュを使用し,変形後の最小要素は初期サイズで1.5×1.5mm相当となる。)
Using the present invention, the deep drawing analysis of the embossed panel shown in FIG. 9 was performed under the following conditions and compared with the experimental results. A material analysis model (before deformation) is shown in FIG.
<Analysis conditions>
Panel dimensions: 300 × 450 × 25mm, corner R20mm, shoulder R4mm
Emboss depth: 4mm
Initial material dimensions: 370 x 520mm
Wrinkle holding load 200kN
Material characteristics: Iron standard JAC440W (Table 2 below)
Mesh size: Initial 24 × 24mm
(Adaptive mesh that automatically calculates each element size is used, and the minimum element after deformation is equivalent to 1.5 x 1.5 mm in the initial size.)
理論FLC計算プログラムを用いて供試材の引張試験値を入力し,ゲージ長さ10mmでの破断限界歪を算出した。
(本理論FLC計算プログラムはあらかじめ各種の鋼板においてゲージ長さ10mmの実験結果と定量的に一致することを確認した。)
<解析結果>
解析は全領域のモデルを作成し,実施した.解析の各ステップごとの歪に対し実験による破断限界歪ε1を使って破断判定を行った。図11に解析結果による変形後のメッシュ形状を示す.アダプティブメッシュの使用により要素ごとに寸法が異なった。この結果に,理論FLCから得られた10mmのゲージ長さの破断限界歪ε1を用いて破断判定を行った結果,成形高さ24.5mmでエンボス縦壁部が破断と評価され、図12に示すように、中央のエンボスの縦壁部で破断と判定した。 次に、数1の式を用いて各要素ごとに変形前相当のゲージ長さに換算したFLCから求めた破断限界歪εf1を用いて破断判定を行った結果,成形終了(高さ25mm)まで破断と判定された要素はなかった。実験結果では破断を起こさずに成形できることから,ε1に比べεf1を用いることで正確な破断の予測が可能となったことにより、本発明の効果が確認された。
Using the theoretical FLC calculation program, the tensile test value of the specimen was input, and the fracture limit strain at a gauge length of 10 mm was calculated.
(This theoretical FLC calculation program was confirmed in advance to quantitatively agree with the experimental results of a gauge length of 10 mm in various steel plates.)
<Analysis results>
The analysis was performed by creating a model of the entire region. The fracture was determined using the experimental fracture limit strain ε 1 for the strain at each step of the analysis. Figure 11 shows the mesh shape after deformation based on the analysis results. Due to the use of adaptive mesh, the dimensions were different for each element. As a result of the fracture determination using the fracture limit strain ε 1 of the gauge length of 10 mm obtained from the theoretical FLC, the embossed vertical wall portion was evaluated as fractured at a molding height of 24.5 mm. As shown, it was determined as a break at the vertical wall of the central emboss. Next, as a result of rupture determination using the rupture limit strain ε f1 obtained from the FLC converted into the gauge length equivalent to the deformation for each element using the formula (1), the end of molding (height 25 mm) No element was determined to be broken. Since the experimental results show that molding can be performed without causing breakage, the use of ε f1 compared to ε 1 makes it possible to accurately predict rupture, thereby confirming the effects of the present invention.
Claims (5)
特定のゲージ長さにおける破断限界歪ε1に基づいて、任意のゲージ長さにおける破断限界歪εf1を計算し、
該任意のゲージ長さにおける破断限界歪εf1と、有限要素法を用いて計算した各要素の歪量εとを比較することにより、破断判定を行うことを特徴とする、薄板のプレス成形シミュレーションにおける破断判定方法。 In press forming simulation of thin plates using the finite element method,
Based on the fracture limit strain ε 1 at a specific gauge length, calculate the fracture limit strain ε f1 at an arbitrary gauge length,
A thin plate press-forming simulation characterized by performing fracture determination by comparing the fracture limit strain ε f1 at the arbitrary gauge length and the strain amount ε of each element calculated using a finite element method Break determination method in
特定のゲージ長さにおける破断限界歪ε1に基づいて、任意のゲージ長さにおける破断限界歪εf1を計算する破断限界歪計算手段と、
該任意のゲージ長さにおける破断限界歪εf1と、有限要素法を用いて計算した各要素の歪量εとを比較することにより破断判定を行う破断判定手段とを有することを特徴とする、薄板のプレス成形シミュレーションにおける破断判定装置。
An apparatus for carrying out the fracture determination method according to any one of claims 1 to 4,
Breaking limit strain calculating means for calculating the breaking limit strain ε f1 at an arbitrary gauge length based on the breaking limit strain ε 1 at a specific gauge length;
It has a fracture determination means for performing fracture determination by comparing the fracture limit strain ε f1 at the arbitrary gauge length and the strain amount ε of each element calculated using a finite element method, Break determination device in thin plate press forming simulation.