JP2011137375A - Method of regenerating surface body - Google Patents
Method of regenerating surface body Download PDFInfo
- Publication number
- JP2011137375A JP2011137375A JP2011091161A JP2011091161A JP2011137375A JP 2011137375 A JP2011137375 A JP 2011137375A JP 2011091161 A JP2011091161 A JP 2011091161A JP 2011091161 A JP2011091161 A JP 2011091161A JP 2011137375 A JP2011137375 A JP 2011137375A
- Authority
- JP
- Japan
- Prior art keywords
- surface layer
- sand
- roadbed
- aqueous emulsion
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、特に、馬場、野球場、サッカー場、ラグビー場などのスポーツフィールドの表面に形成される表層体の再生方法に関する。 In particular, the present invention relates to a method for reproducing a surface layer formed on the surface of a sports field such as a Baba, a baseball field, a soccer field, and a rugby field.
例えば、従来の馬場用舗装構造は、路床の上に敷設された路盤と、当該路盤の上に敷設された表層体とから主に構成されている。前記路盤は、例えば、透水性アスファルトコンクリートからなり、透水性を高めるとともに、馬場用舗装構造の強度を確保する役割を担っている。また、前記表層体は、例えば、芝や砂もしくは砂とゴムチップ等の混合物からなり、クッション性を高める役割を担っている。 For example, a conventional pavement structure for Baba is mainly composed of a roadbed laid on a roadbed and a surface layer laid on the roadbed. The said roadbed consists of water-permeable asphalt concrete, for example, and has the role which ensures the intensity | strength of the pavement structure for Baba while improving water permeability. The surface layer is made of, for example, turf, sand, or a mixture of sand and rubber chips, and plays a role of improving cushioning properties.
近年、砂とゴムチップ等の弾性を有する粒状物質とを混合した表層材料を用いて、表層体を形成することが注目されている。このような表層体は、クッション性に優れるとともに、芝に比べて施工コスト、メンテナンスコストが廉価であるため、例えば、競馬場やトレーニングセンター等で利用されている。通常、前記した表層体は、砂やゴムチップ等の粒状物質が、風雨によって散飛したり、流出したりするのを防止するために、また、表層体内の所定の空隙を確保するためにバインダを介して一体化されている。 In recent years, attention has been focused on forming a surface layer body using a surface layer material in which sand and a granular material having elasticity such as a rubber chip are mixed. Such a surface layer body has excellent cushioning properties and is cheaper in construction cost and maintenance cost than turf, and is used, for example, at a racetrack or a training center. Usually, the above-mentioned surface layer body has a binder to prevent particulate matter such as sand and rubber chips from being scattered or discharged by wind and rain, and to secure a predetermined gap in the surface layer body. It is integrated through.
バインダは、常温で固形(半固形)又は液体であって、表層材料の種類や用途に応じて様々な種類のものが用いられている。従来のバインダとしては、例えば、ポリウレタン樹脂などが挙げられる(特許文献1参照)。 The binder is solid (semi-solid) or liquid at room temperature, and various types of binders are used depending on the type and application of the surface layer material. As a conventional binder, a polyurethane resin etc. are mentioned, for example (refer patent document 1).
しかし、常温で液体のバインダは、硬化後の耐久性が弱く、さらには経年劣化によりバインダの成分が外部に流出しやすいという問題があった。
一方、常温で固形のバインダを用いて、当該固形のバインダと表層材料とを混合する際には、アスファルトプラント等で加熱しながら混合しなければならないが、表層材料にゴムチップ等の弾性を有する粒状物質が混在していると、加熱する際にこれらの粒状物質が変性する可能性があった。このように、弾性を有する粒状物質が変性すると、クッション性及び透水性が低下するという問題があった。
However, a binder that is liquid at room temperature has a problem that durability after curing is weak, and further, components of the binder easily flow out due to aging.
On the other hand, when using a solid binder at room temperature and mixing the solid binder and the surface layer material, they must be mixed while heating in an asphalt plant or the like, but the surface layer material has elasticity such as rubber chips. When substances are mixed, there is a possibility that these particulate substances are denatured during heating. As described above, when the granular material having elasticity is denatured, there is a problem that cushioning properties and water permeability are lowered.
本発明はかかる問題を解決するためになされたものであり、耐久性が高く、かつ、バインダの流出を防止するとともに、表層材料に弾性を有する粒状物質が混在してもこれらの物質が施工工程中に変性することのない表層体の再生方法を提供することを課題とする。 The present invention has been made to solve such a problem, and has high durability and prevents outflow of the binder, and even if the granular material having elasticity is mixed in the surface layer material, these substances are applied in the construction process. It is an object of the present invention to provide a method for regenerating a surface layer that does not denature inside.
このような課題を解決するために本発明は、固形又は半固形のバインダを乳化して生成された水性エマルジョンを既設の表層体に散布する散布工程と、前記既設の表層体及び前記水性エマルジョンを攪拌機で攪拌する攪拌工程と、を含むことを特徴とする。 In order to solve such a problem, the present invention includes a spraying step of dispersing an aqueous emulsion produced by emulsifying a solid or semi-solid binder on an existing surface layer body, and the existing surface layer body and the aqueous emulsion. A stirring step of stirring with a stirrer.
かかる方法によれば、固形又は半固形のバインダを乳化して生成された水性エマルジョンは、水分を多く含むため、既存の表層体と混ざりやすい(馴染みやすい)。これにより、攪拌工程後には水分が蒸発して既存の表層体とバインダとが強固に結合して一体化するため、耐久性の高い新たな表層体を形成することができる。また、固形又は半固形のバインダを用いることにより、バインダの流出を防止することができる。また、既存の表層体と水性エマルジョンとを例えば常温で混合させることができるため、再生作業を効率よく行うことができる。 According to such a method, an aqueous emulsion produced by emulsifying a solid or semi-solid binder contains a large amount of moisture, so that it easily mixes with an existing surface layer (is easy to become familiar with). Thereby, after a stirring process, since water | moisture content evaporates and the existing surface layer body and a binder couple | bond together firmly and can be integrated, a new surface layer body with high durability can be formed. Further, by using a solid or semi-solid binder, the binder can be prevented from flowing out. Moreover, since the existing surface layer and the aqueous emulsion can be mixed, for example, at room temperature, the regeneration operation can be performed efficiently.
また、前記既設の表層体は、少なくとも砂と弾性を有する粒状物質とを含んだ表層材料で構成されていることが好ましい。また、前記既設の表層体に、新たに砂や弾性を備えた粒状物質を加えた後、前記散布工程及び前記攪拌工程を行うことが好ましい。 Moreover, it is preferable that the existing surface layer body is composed of a surface layer material including at least sand and a granular material having elasticity. Moreover, it is preferable to perform the said dispersion | distribution process and the said stirring process, after adding the granular material which newly provided sand and elasticity to the said existing surface layer body.
本発明に係る表層体の再生方法によれば、耐久性が高く、かつ、バインダの流出を防止するとともに、表層材料に弾性を有する粒状物質が混在してもこれらの物質が施工工程中に変性することのない表層体を提供することができる。 According to the method for regenerating a surface layer body according to the present invention, the durability is high and the outflow of the binder is prevented, and even if a granular material having elasticity is mixed in the surface layer material, these materials are modified during the construction process. The surface layer body which does not do can be provided.
[第一実施形態]
本発明の最良の実施形態について図面を参照して詳細に説明する。図1は、第一実施形態に係る舗装構造を示した断面図である。
[First embodiment]
The best embodiment of the present invention will be described in detail with reference to the drawings. FIG. 1 is a cross-sectional view showing a pavement structure according to the first embodiment.
本実施形態に係る表層体10は、図1に示すように、舗装構造Hの表面に形成される舗装体である。舗装構造Hは、主として馬場、野球場、サッカー場、ラグビー場などのスポーツフィールドの舗装構造として採用することができるが、本実施形態では、馬場に採用した場合を例にして説明する。 As shown in FIG. 1, the surface layer body 10 according to the present embodiment is a pavement formed on the surface of the pavement structure H. The pavement structure H can be mainly used as a pavement structure for sports fields such as a Baba, a baseball field, a soccer field, and a rugby field. In the present embodiment, a case where the pavement structure H is used for a Baba will be described as an example.
舗装構造Hは、地面の上に形成された路床2と、路床2に埋設されたドレンパイプ3と、路床2の上に設けられた透水シート4と、透水シート4の上に設けられた下層路盤5と、下層路盤5の上に設けられた透水性アスファルト舗装6と、透水性アスファルト舗装6の上に設けられた上層路盤7と、上層路盤7の上に設けられた表層体10とを有する。
The pavement structure H is provided on the road bed 2 formed on the ground, the
路床2は、図示しない地面の上に設けられ、舗装構造Hの最下層を構成する部分である。路床2は、本実施形態では主に路床土を用いて形成されているが、セメント固化材等を用いて強度を高めてもよい。路床2の表面には、断面視略矩形の凹溝Lが切り欠いて形成されており、凹溝Lには、ドレンパイプ3が挿入されている。
The roadbed 2 is a part that is provided on the ground (not shown) and constitutes the lowest layer of the pavement structure H. Although the roadbed 2 is mainly formed using roadbed soil in this embodiment, the strength may be increased using a cement solidifying material or the like. A concave groove L having a substantially rectangular cross-sectional view is formed on the surface of the road bed 2, and a
ドレンパイプ3は、断面視円形状を呈する筒状部材であって、下層路盤5に流れ込んだ水の排水を担う部材である。ドレンパイプ3は、本実施形態では、フィルタ材を巻いたポーラス管を用いている。ドレンパイプ3の一端側は、図示しない排水溝や排水口に開口して形成されている。なお、凹溝L及びドレンパイプ3は、必要に応じて適宜設ければよい。
The
透水シート4は、路床2の上に設けられており、下層路盤5に流れ込む水を下方に透水させるとともに、下層路盤5の砕石の流出や路床2の路床土の流入を防止するための部材である。透水シート4は、例えば厚さが2〜5mm程度の不織布からなり、微細な孔を備えている。即ち、下層路盤5に流入した水は、透水シート4に備えられた上下方向に貫通する微細な孔を通ってドレンパイプ3に流入し、排水される。なお、透水シート4は、必要に応じて適宜設ければよい。
The water permeable sheet 4 is provided on the road bed 2 to allow water flowing into the lower road bed 5 to flow downward, and to prevent the crushed stone from the lower road bed 5 from flowing out and the road bed soil from flowing into the road bed 2. It is a member. The water permeable sheet 4 is made of a nonwoven fabric having a thickness of about 2 to 5 mm, for example, and includes fine holes. That is, the water that has flowed into the lower layer roadbed 5 flows into the
下層路盤5は、透水シート4の上に設けられ、主に支持機能を備える部分である。即ち、下層路盤5は、透水性アスファルト舗装6及び上層路盤7が受ける馬(馬蹄)の衝撃や管理車両の荷重を受けて分散させる役割を担う。下層路盤5は、本実施形態では、例えば粒径が40mm程度の単粒砕石又はクラッシャランC−40からなる。下層路盤5は、本実施形態では例えば150mm厚で形成されている。下層路盤5の厚みや石の粒径は、用途に応じて適宜設定すればよい。 The lower layer roadbed 5 is a part provided on the water-permeable sheet 4 and mainly having a support function. That is, the lower roadbed 5 plays a role of receiving and dispersing the impact of the horse (horseshoe) received by the water-permeable asphalt pavement 6 and the upper roadbed 7 and the load of the management vehicle. In the present embodiment, the lower layer roadbed 5 is made of, for example, single-grain crushed stone or crusheran C-40 having a particle size of about 40 mm. In this embodiment, the lower layer roadbed 5 is formed with a thickness of 150 mm, for example. What is necessary is just to set suitably the thickness of the lower layer roadbed 5, and the particle size of a stone according to a use.
透水性アスファルト舗装6は、下層路盤5の上に設けられ、上層路盤7を支持する部分である。透水性アスファルト舗装6は、本実施形態では、ポーラスアスファルトによって形成されている。ポーラスアスファルトによれば、適度な強度を有するとともに、ポーラスアスファルトを構成する骨材同士の間隙に水が流れるため、透水性を高めることができる。透水性アスファルト舗装6は、本実施形態では約50mm厚で形成されているが、厚みは適宜設定すればよい。 The water permeable asphalt pavement 6 is a portion that is provided on the lower layer roadbed 5 and supports the upper layer roadbed 7. In this embodiment, the water permeable asphalt pavement 6 is formed of porous asphalt. According to the porous asphalt, water has an appropriate strength and water can flow through the gap between the aggregates constituting the porous asphalt, so that the water permeability can be increased. The permeable asphalt pavement 6 is formed with a thickness of about 50 mm in this embodiment, but the thickness may be set as appropriate.
上層路盤7は、透水性アスファルト舗装6の上に設けられ、表層体10を支持する部分である。上層路盤7は、本実施形態では砂入り人工芝からなる。砂入り人工芝は、上層路盤用人工芝7aと上層路盤用人工芝7aに充填された上層路盤用砂7dとを有する。上層路盤用人工芝7aは、板状の基板部7bと、基板部7bから略垂直に立設されたパイル部7cとを有する。上層路盤用砂7dは、基板部7bと、隣り合うパイル部7c,7c間に充填され、締め固められている。上層路盤7によれば、上層路盤用人工芝7aに上層路盤用砂7dが締め固められているため、所定の強度を確保するとともに、透水性を高めることができる。また、上層路盤7は、馬が推進力を生むための必要な強度を備えるとともに、例えば馬蹄が深く入り込んで上層路盤7に触れたとしても、上層路盤7に人工芝7aを含んでいるため、馬蹄の損傷を防止することができる。
The upper layer roadbed 7 is a part that is provided on the water-permeable asphalt pavement 6 and supports the surface layer body 10. In this embodiment, the upper layer roadbed 7 is made of sand-containing artificial turf. The artificial grass with sand has an
なお、上層路盤用砂7dに用いる砂の種類は特に限定されるものではないが、川砂、レイクサンド、海砂、砂丘砂、火山砂利などの天然骨材及び珪砂、洗い砂、スラグなどの人工骨材からなる砂等を適宜選択して用いればよい。
The type of sand used for the
表層体10は、上層路盤7の上に設けられ、舗装構造Hの表面に現れる部分である。表層体10は、主にクッション性を高める機能を有する。表層体10は、本実施形態では、砂11及びゴムチップ13からなる表層材料14と、表層材料14を一体化させるバインダ(図示省略)とを有する。表層体10は、本実施形態では、砂11とゴムチップ13の重量の比率が約8:2であって、100mm厚で形成されている。表層体10の配合や厚さ等は馬場の用途等に応じて適宜設定すればよい。
The surface layer 10 is a portion that is provided on the upper layer roadbed 7 and appears on the surface of the pavement structure H. The surface layer 10 mainly has a function of improving cushioning properties. In the present embodiment, the surface layer body 10 includes a
砂11の種類は、特に限定されるものではないが、川砂、レイクサンド、海砂、砂丘砂、火山砂利などの天然骨材及び珪砂、洗い砂、スラグなどの人工骨材からなる砂等を適宜選択して用いればよい。また、ゴムチップ13は、粒径が約1mm〜3mmのものを採用している。ゴムチップ13を表層体10に含ませることにより、表層体10のクッション性をより高めることができる。ゴムチップ13の粒径、性状、混合量等は、表層体10の用途に応じて適宜設定すればよい。
The type of sand 11 is not particularly limited, but natural sand such as river sand, lake sand, sea sand, dune sand, volcanic gravel and sand made of artificial aggregate such as quartz sand, washing sand, slag, etc. What is necessary is just to select and use suitably. The
なお、本実施形態では、弾性を有する粒状物質としてゴムチップ13を用いたが、これに限定されるものではなく、例えば、ウッドチップ、細かく裁断された人工芝、電線被覆材、その他粒状の樹脂製品等を採用してもよい。弾性を有する粒状物質の粒径は、表層体10の用途や選択した材料に応じて適宜設定すればよい。また、本実施形態では、砂11をベースに表層材料14を構成したが、砂11に替えてウッドチップや樹脂製の粒状物質をベースに表層材料14を構成してもよい。
In this embodiment, the
バインダは、本実施形態では、半固形のペトロラタムを主成分としたものを用いている。即ち、本実施形態では、半固形のペトロラタム、低分子量ポリエチレン及び水を乳化剤によって乳化させたペトロラタムの水性エマルジョンを表層材14と混合させた後、水を蒸発させている。水を蒸発させると、バインダ(ペトロラタム)が表層材14と強固に結合するとともに、表層体10内において所定の空隙を確保することができる。
In the present embodiment, the binder is a binder mainly composed of semisolid petrolatum. That is, in this embodiment, water is evaporated after the semi-solid petrolatum, low molecular weight polyethylene, and an aqueous emulsion of petrolatum obtained by emulsifying water with an emulsifier are mixed with the
なお、本実施形態では、半固形のバインダとしてペトロラタムを用いたが、これに限定されるものではなく、例えば、アスファルト、クリスタリンワックス、マイクロワックス、パラフィンワックス等を所定の乳化剤で乳化させてもよい。また、公知の固形のバインダを用いて乳化させてもよい。
また、乳化剤は、公知の乳化剤を用いればよく、例えば、α−オレフィンスルフォン化物、アルキルサルフェート、脂肪酸石けんなどの乳化剤を用いればよい。
In this embodiment, petrolatum is used as a semi-solid binder. However, the present invention is not limited to this, and for example, asphalt, crystallin wax, microwax, paraffin wax or the like may be emulsified with a predetermined emulsifier. . Moreover, you may emulsify using a well-known solid binder.
Moreover, what is necessary is just to use a well-known emulsifier as an emulsifier, for example, emulsifiers, such as (alpha) -olefin sulfonated substance, an alkyl sulfate, and a fatty acid soap.
次に、図1を参照して本実施形態に係る舗装構造Hの施工方法について説明する。
まず、路床土を用いて所定の厚みで路床2を形成した後、表面を掘削して凹溝Lを形成する。次に、凹溝Lにドレンパイプ3を挿入する。ドレンパイプ3の少なくとも一端側は、図示しない排水溝に開口するように形成する。そして、路床2の上面に透水シート4を敷設した後、所定の厚みで砕石を敷設して下層路盤5を形成する。
Next, with reference to FIG. 1, the construction method of the pavement structure H which concerns on this embodiment is demonstrated.
First, the road bed 2 is formed with a predetermined thickness using road bed soil, and then the surface is excavated to form the groove L. Next, the
次に、下層路盤5の上に砕石を敷設し、ポーラスアスファルトバインダと骨材とを混合してなる透水性アスファルト舗装6を形成する。 Next, crushed stone is laid on the lower roadbed 5, and a water-permeable asphalt pavement 6 formed by mixing a porous asphalt binder and aggregate is formed.
次に、下層路盤5の上に上層路盤用人工芝7aを敷設し、上層路盤用人工芝7aの内部に所定の厚みで上層路盤用砂7dを充填して上層路盤7を形成する。上層路盤用砂7dを充填する際には、振動機を用いて振動を加えながら充填するのが好ましい。なお、上層路盤7は、他の場所で形成したものを透水性アスファルト舗装6の上に配置してもよい。
Next, the upper-layer roadbed
次に、上層路盤7の上に表層体10を形成する。
表層体10の施工方法は、本実施形態では、半固形のバインダを乳化して水性エマルジョンを生成する水性エマルジョン生成工程と、水性エマルジョンと表層材料14を常温で混合する混合工程と、混合工程で混合された混合物を施工面に敷き均す敷設工程と、敷き均された混合物の水分を蒸発させる養生工程と、を含む。
Next, the surface layer body 10 is formed on the upper layer roadbed 7.
In this embodiment, the construction method of the surface layer body 10 includes an aqueous emulsion generation step of emulsifying a semi-solid binder to generate an aqueous emulsion, a mixing step of mixing the aqueous emulsion and the
(水性エマルジョン生成工程)
水性エマルジョン生成工程では、半固形のペトロラタム、低分子量ポリエチレン、乳化剤及び水を公知の乳化機で混合し、ペトロラタムの水性エマルジョンを生成する。配合割合は、例えば、ペトロラタム20〜40%重量、低分子量ポリエチレン1〜10%重量、乳化剤3〜10%重量、水40〜60%重量の範囲で適宜設定する。
(Aqueous emulsion production process)
In the aqueous emulsion production step, semisolid petrolatum, low molecular weight polyethylene, emulsifier and water are mixed with a known emulsifier to produce an aqueous emulsion of petrolatum. The blending ratio is appropriately set in the range of, for example, petrolatum 20 to 40% weight, low molecular weight polyethylene 1 to 10% weight,
(混合工程)
混合工程では、表層材料14とペトロラタムの水性エマルジョンをアスファルトプラントにて公知のミキサーを用いて常温で混合する。本実施形態では、表層材料14とペトロラタムの水性エマルジョンとの重量比が例えば、8:2になるように混ぜ合わせる。各材料が十分に攪拌されたら、例えば、アスファルトフィニッシャ等の敷き均し機に混合物を投入する。
(Mixing process)
In the mixing step, the
なお、混合工程は、必ずしもアスファルトプラントで行う必要はなく、公知のミキサー等を用いて現場で混合してもよい。また、本実施形態に係る混合工程では、常温(5℃〜35℃)で各材料を混合したが、例えば、ゴムチップ13が変性しない温度で温めながら混合工程を行ってもよい。
The mixing step is not necessarily performed in an asphalt plant, and may be performed on site using a known mixer or the like. In the mixing step according to the present embodiment, each material is mixed at normal temperature (5 ° C. to 35 ° C.). For example, the mixing step may be performed while warming at a temperature at which the
(敷設工程)
敷設工程では、混合工程で混合された混合物を例えば、アスファルトフィニッシャ等の敷き均し機で施工面(本実施形態では、上層路盤7)に敷き均す。
(Laying process)
In the laying step, the mixture mixed in the mixing step is spread on the construction surface (in this embodiment, the upper layer roadbed 7) with a spreader such as an asphalt finisher.
(養生工程)
養生工程では、敷設工程で敷き均された混合物を所定の期間放置して、水分を蒸発させる。これにより、表層体10が完成する。
(Curing process)
In the curing process, the mixture leveled in the laying process is allowed to stand for a predetermined period to evaporate water. Thereby, the surface layer body 10 is completed.
以上説明した、表層体10によれば、ペトロラタムを乳化して形成されたペトロラタムの水性エマルジョンは、水分を多く含むため、表層材料14と混ざりやすい(馴染みやすい)。これにより、敷設工程後に水分が蒸発して表層材料14とバインダ(ペトロラタム)とが強固に結合して一体化するため、耐久性の高い表層体10を形成することができる。また、固形又は半固形のバインダを用いることにより、バインダの流出を防止することができる。また、本実施形態にように、表層材料14にゴムチップ13が混在している場合でも、常温で表層材料14とペトロラタムの水性エマルジョンとを混合させるため、ゴムチップ13が変性することなく混合することができる。これにより、クッション性及び透水性の高い表層体10を形成することができる。
According to the surface layer 10 described above, the aqueous emulsion of petrolatum formed by emulsifying petrolatum contains a lot of water, and thus is easily mixed with the surface layer material 14 (easy to adapt). As a result, the water evaporates after the laying step, and the
また、ペトロラタムの水性エマルジョンを用いることで、混合工程の際に加熱することなく常温で混合することができるため、CO2の排出がなく地球環境に対しても好ましい。 Further, by using an aqueous emulsion of petrolatum, it is possible to mix at normal temperature without heating during the mixing step, and therefore, it is preferable for the global environment without CO 2 emission.
[第二実施形態]
次に、本発明の第二実施形態について説明する。第二実施形態に係る表層体の施工方法は、前記した表層体10の施工方法であって、二種類の混合工程を含む点で第一実施形態と相違する。
[Second Embodiment]
Next, a second embodiment of the present invention will be described. The construction method of the surface layer body according to the second embodiment is the construction method of the surface layer body 10 described above, and is different from the first embodiment in that it includes two kinds of mixing steps.
第二実施形態に係る施工方法は、半固形のバインダを乳化して水性エマルジョンを生成する水性エマルジョン生成工程と、熱可塑性バインダと砂11とを加熱して混合する第一混合工程と、第一混合工程で混合された混合物と、ペトロラタムの水性エマルジョンと、ゴムチップ13を常温で混合する第二混合工程と、第二混合工程で混合された混合物を施工面に敷き均す敷設工程と、敷き均された混合物の水分を蒸発させる養生工程と、を含む。
なお、水性エマルジョン生成工程は、第一実施形態と同等であるため説明を省略する。
The construction method according to the second embodiment includes an aqueous emulsion generating step of emulsifying a semi-solid binder to generate an aqueous emulsion, a first mixing step of heating and mixing the thermoplastic binder and the sand 11, and a first A second mixing step in which the mixture mixed in the mixing step, the aqueous emulsion of petrolatum, and the rubber chips 13 are mixed at room temperature; a laying step in which the mixture mixed in the second mixing step is spread on the construction surface; And a curing step for evaporating the water in the mixed mixture.
In addition, since an aqueous | water-based emulsion production | generation process is equivalent to 1st embodiment, description is abbreviate | omitted.
(第一混合工程)
第一混合工程では、熱可塑性バインダと、砂11とを例えば、アスファルトプラントで加熱しながら混合する。熱可塑性バインダは、本実施形態では、例えば固形パラフィンを用いる。砂11と熱可塑性バインダとを加熱しながら混合することで、より均一に混合することができる。砂11と熱可塑性バインダとの配合は、例えば、重量比が9:1となるように設定する。なお、熱可塑性バインダは、他の公知のバインダを用いてもよい。また、固形のバインダに限られず、半固形のバインダを用いてもよい。
(First mixing step)
In the first mixing step, the thermoplastic binder and the sand 11 are mixed while being heated in, for example, an asphalt plant. In this embodiment, for example, solid paraffin is used as the thermoplastic binder. By mixing the sand 11 and the thermoplastic binder while heating, it is possible to mix more uniformly. The composition of the sand 11 and the thermoplastic binder is set so that the weight ratio is 9: 1, for example. Note that other known binders may be used as the thermoplastic binder. Moreover, it is not restricted to a solid binder, You may use a semi-solid binder.
(第二混合工程)
第二混合工程では、第一混合工程で混合された混合物と、ペトロラタムの水性エマルジョン及びゴムチップ13を、例えばアスファルトプラントで常温で混合する。第一混合工程で混合された混合物と、ペトロラタムの水性エマルジョンと、ゴムチップ13との配合は、例えば、重量比が8:1:1となるように設定する。各材料が十分に攪拌されたら、例えば、アスファルトフィニッシャ等の敷き均し機に混合物を投入する。なお、第二混合工程は、現場で公知のミキサーを用いて混合してもよい。
なお、本実施形態に係る混合工程では、常温(5℃〜35℃)で各材料を混合したが、例えば、ゴムチップ13が変性しない温度で温めながら混合工程を行ってもよい。
(Second mixing step)
In the second mixing step, the mixture mixed in the first mixing step, the aqueous emulsion of petrolatum and the rubber chips 13 are mixed at room temperature in an asphalt plant, for example. The mixture of the mixture mixed in the first mixing step, the aqueous emulsion of petrolatum, and the
In the mixing step according to the present embodiment, each material is mixed at normal temperature (5 ° C. to 35 ° C.). For example, the mixing step may be performed while warming at a temperature at which the
(敷設工程)
敷設工程では、第二混合工程で混合された混合物を例えば、アスファルトフィニッシャで施工面(本実施形態では、上層路盤7)に敷き均す。
(Laying process)
In the laying step, the mixture mixed in the second mixing step is spread on the construction surface (in this embodiment, the upper layer roadbed 7) with, for example, an asphalt finisher.
(養生工程)
養生工程では、敷設工程で敷き均された混合物を所定の期間放置して、水分を蒸発させる。これにより、表層体10が完成する。
(Curing process)
In the curing process, the mixture leveled in the laying process is allowed to stand for a predetermined period to evaporate water. Thereby, the surface layer body 10 is completed.
以上説明した表層体の施工方法のように、加熱しても変性しない砂11と、加熱すると変性しやすいゴムチップ13とを分けて混合してもよい。即ち、砂11と熱可塑性バインダとを加熱して混合(第一混合工程)することにより、砂11と熱可塑性バインダとを十分に混合することができる。また、第二混合工程では、第一混合工程で混合された混合物と、熱に弱いゴムチップ13とを常温で混合することができるため、ゴムチップ13が変性することを防止することができる。これにより、表層体10のクッション性及び透水性を高めることができる。
Like the surface layer construction method described above, the sand 11 that does not denature even when heated and the
[第三実施形態]
次に、本発明の第三実施形態に係る表層体の再生方法ついて説明する。表層体は、長期間使用すると、砂が締め固められたり、ゴムチップ等のクッション材が風雨によって流出したりして性能が低下する。したがって、所定の期間が経過したら、既設の表層体に対して再生処理を行う必要がある。
第三実施形態に係る表層体の再生方法は、水性エマルジョンを用いる点を特徴とする。
[Third embodiment]
Next, a method for regenerating a surface layer body according to the third embodiment of the present invention will be described. When the surface layer is used for a long period of time, the sand is compacted, or the cushioning material such as a rubber chip flows out due to wind and rain, and the performance deteriorates. Therefore, when a predetermined period has elapsed, it is necessary to perform a regeneration process on the existing surface layer body.
The surface layer regeneration method according to the third embodiment is characterized in that an aqueous emulsion is used.
第三実施形態に係る表層体の再生方法は、半固形のバインダを乳化して水性エマルジョンを生成する水性エマルジョン生成工程と、既設の表層体に水性エマルジョンを散布する散布工程と、既設の表層体及び水性エマルジョンを攪拌機で攪拌する攪拌工程と、攪拌された混合物の水分を蒸発させる養生工程と、を含む。
なお、水性エマルジョン生成工程は、第一実施形態と同等であるため、説明を省略する。
The method for regenerating a surface layer body according to the third embodiment includes an aqueous emulsion generation step of emulsifying a semi-solid binder to generate an aqueous emulsion, a spraying step of spraying the aqueous emulsion on the existing surface layer body, and an existing surface layer body And a stirring step of stirring the aqueous emulsion with a stirrer, and a curing step of evaporating the water in the stirred mixture.
In addition, since an aqueous | water-based emulsion production | generation process is equivalent to 1st embodiment, description is abbreviate | omitted.
(散布工程)
散布工程では、水性エマルジョン生成工程で生成されたペトロラタムの水性エマルジョンを、公知のディストリビューダ等の散布車両を用いて既設の表層体に略均一に散布する。
(Spraying process)
In the spraying step, the aqueous emulsion of petrolatum generated in the aqueous emulsion generation step is sprayed substantially uniformly on the existing surface layer body using a spraying vehicle such as a known distributor.
(攪拌工程)
攪拌工程では、既設の表層体及び散布されたペトロラタムの水性エマルジョンを公知の攪拌機を用いて攪拌する。
(Stirring process)
In the stirring step, the existing surface layer body and the dispersed aqueous emulsion of petrolatum are stirred using a known stirrer.
(養生工程)
養生工程では、攪拌工程で攪拌された混合物を所定の期間放置して、水分を蒸発させる。これにより、表層体の再生を行うことができる。
(Curing process)
In the curing process, the mixture stirred in the stirring process is allowed to stand for a predetermined period to evaporate moisture. Thereby, reproduction | regeneration of a surface layer body can be performed.
以上のような表層体の再生方法によれば、半固形のペトロラタムを乳化して形成されたペトロラタムの水性エマルジョンは、水分を多く含むため扱いやすく、ディストリビュータ等で散布しやすい。また、ペトロラタムの水性エマルジョンは、既設の表層体と混ざりやすく、攪拌工程後に水分が蒸発して既設の表層体の表層体材料とバインダ(ペトロラタム)とが強固に結合して一体化する。これにより、耐久性の高い再生表層材を形成することができる。また、固形又は半固形のバインダを用いることにより、バインダの流出を防止することができる。また、常温でペトロラタムの水性エマルジョンを用いて再生作業を行うことができるため作業性がよい。 According to the surface layer regeneration method as described above, the aqueous emulsion of petrolatum formed by emulsifying semisolid petrolatum is easy to handle because it contains a large amount of water, and is easily sprayed by a distributor or the like. In addition, the aqueous emulsion of petrolatum is easily mixed with the existing surface layer, and after the stirring step, the water evaporates and the surface layer material of the existing surface layer and the binder (petrolatum) are firmly bonded and integrated. Thereby, a highly durable recycled surface layer material can be formed. Further, by using a solid or semi-solid binder, the binder can be prevented from flowing out. In addition, the workability is good because the regeneration work can be performed using an aqueous emulsion of petrolatum at room temperature.
なお、表層体の再生方法は、前記した方法に限定されるものではない。例えば、既設の表層体に、新たに砂や弾性を備えた粒状物質を加えた後に散布工程及び攪拌工程を行ってもよい。また、既設の表層体に、新たに砂、弾性を有する粒状物質及びペトロラタムの水性エマルジョンを混合させた混合物を敷き均した後に、当該混合物と既存の表層体とを攪拌させてもよい。 In addition, the reproduction | regeneration method of a surface layer body is not limited to an above described method. For example, you may perform a dispersion | distribution process and a stirring process, after adding the granular material which newly provided sand and elasticity to the existing surface layer body. In addition, after the existing surface layer body is spread with a mixture of sand, an elastic granular material, and an aqueous emulsion of petrolatum, the mixture and the existing surface layer body may be stirred.
以上、本発明の実施形態について説明したが、本発明の趣旨を逸脱しない範囲において適宜変更が可能である。例えば、舗装構造Hの路盤の構造は、本実施形態のものに限定されるものではなく、用途に応じて適宜変更してもよい。 While the embodiments of the present invention have been described above, modifications can be made as appropriate without departing from the spirit of the present invention. For example, the structure of the roadbed of the pavement structure H is not limited to that of the present embodiment, and may be appropriately changed according to the application.
また、本実施形態では、舗装構造Hを馬場に採用した場合を例にしたが、これに限定されず、他の運動場、さらには、公園や広場の散歩道、遊歩道、駐車場、屋上の歩道、ゴルフ場等の舗装として用いてもよい。 Moreover, in this embodiment, although the case where the pavement structure H was employ | adopted as a Baba was taken as an example, it is not limited to this, Other playgrounds, Furthermore, a walkway of a park or a square, a promenade, a parking lot, a rooftop sidewalk, It may be used as paving for golf courses and the like.
2 路床
3 ドレンパイプ
4 透水シート
5 下層路盤
6 透水性アスファルト舗装
7 上層路盤
10 表層体
11 砂
13 ゴムチップ(弾性を有する粒状物質)
14 表層材料
H 舗装構造
2
14 Surface material H Pavement structure
Claims (3)
前記既設の表層体及び前記水性エマルジョンを攪拌機で攪拌する攪拌工程と、
を含むことを特徴とする表層体の再生方法。 A spraying step of spreading an aqueous emulsion produced by emulsifying a solid or semi-solid binder on an existing surface layer; and
A stirring step of stirring the existing surface layer body and the aqueous emulsion with a stirrer;
A method for regenerating a surface layer, comprising: