JP2011125540A - Golf club head - Google Patents

Golf club head Download PDF

Info

Publication number
JP2011125540A
JP2011125540A JP2009287878A JP2009287878A JP2011125540A JP 2011125540 A JP2011125540 A JP 2011125540A JP 2009287878 A JP2009287878 A JP 2009287878A JP 2009287878 A JP2009287878 A JP 2009287878A JP 2011125540 A JP2011125540 A JP 2011125540A
Authority
JP
Japan
Prior art keywords
golf club
club head
adhesive material
sole
hosel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2009287878A
Other languages
Japanese (ja)
Inventor
Ko Saka
航 坂
Kozue Wada
梢 和田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bridgestone Sports Co Ltd
Original Assignee
Bridgestone Sports Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bridgestone Sports Co Ltd filed Critical Bridgestone Sports Co Ltd
Priority to JP2009287878A priority Critical patent/JP2011125540A/en
Priority to US12/970,064 priority patent/US20110152004A1/en
Publication of JP2011125540A publication Critical patent/JP2011125540A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a golf club head which makes an exhilarating sound when it hits a ball. <P>SOLUTION: The golf club head 1 includes: a face part 2; a crown part 3; a sole part 4; a side part 5; and a hosel part 6. A protruded strip 8 is arranged on the sole 4 so that a lower region at the lower end of the hosel part 6 may be a region for arranging an adhesive material 7. Preferably, the adhesive material 7 is arranged by passing an injection nozzle through the hosel part 6 and injecting it from the injection nozzle to the region for arranging. <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

本発明は中空のゴルフクラブヘッドに係り、特に内部に異物を付着させるための粘着材を設けたゴルフクラブヘッドに関する。   The present invention relates to a hollow golf club head, and more particularly to a golf club head provided with an adhesive material for adhering foreign matter inside.

ドライバーやフェアウェーウッドなどのウッド型ゴルフクラブヘッドとして、中空の金属製のものが広く用いられている。一般に、中空のウッド型のゴルフクラブヘッドは、ボールをヒットするためのフェース部と、ゴルフクラブヘッドの上面部を構成するクラウン部と、ゴルフクラブヘッドの底面部を構成するソール部と、ゴルフクラブヘッドのトウ側、バック側及びヒール側の側面部を構成するサイド部と、ホゼル部とを有している。このホゼル部にシャフトが挿入され、接着剤等によってシャフトがゴルフクラブヘッドに固定されることにより、ゴルフクラブが構成される。   Hollow metal golf club heads such as drivers and fairway woods are widely used. In general, a hollow wood-type golf club head includes a face portion for hitting a ball, a crown portion constituting an upper surface portion of the golf club head, a sole portion constituting a bottom surface portion of the golf club head, and a golf club. It has a side part constituting a side part on the toe side, back side and heel side of the head, and a hosel part. A shaft is inserted into the hosel portion, and the shaft is fixed to the golf club head with an adhesive or the like, thereby forming a golf club.

この中空ゴルフクラブヘッドを構成する金属としては、アルミニウム合金、ステンレスやチタン合金が用いられている。なお、ゴルフクラブヘッドの一部を繊維強化合成樹脂にて構成することもある。   As a metal constituting the hollow golf club head, an aluminum alloy, stainless steel, or titanium alloy is used. A part of the golf club head may be made of fiber reinforced synthetic resin.

中空ゴルフクラブヘッドの内部に金属の微小片等よりなる異物が存在すると、ゴルフクラブを動かしたときに該異物がゴルフクラブヘッド内を移動し、チリチリあるいはカラカラといった異音が発生する。このような異物としては、金属製ゴルフクラブヘッドの鋳造滓などが挙げられる。   If there is a foreign object such as a fine metal piece inside the hollow golf club head, the foreign object will move in the golf club head when the golf club is moved, and an abnormal noise such as a dusty or an unevenness will be generated. An example of such a foreign material is a cast iron of a metal golf club head.

特開平７−１４８２８８には、ゴルフクラブヘッド内に粘着材層を設けることにより異物粒子を付着させて捕獲することが記載されている。この特開平７−１４８２８８では、粘着材層はソール部やクラウン部の内面に広い範囲にわたって設けられている。   Japanese Patent Application Laid-Open No. 7-148288 describes that foreign particles are attached and captured by providing an adhesive layer in a golf club head. In JP-A-7-148288, the adhesive material layer is provided over a wide range on the inner surface of the sole portion or the crown portion.

特開平７−１４８２８８JP 7-148288 A

粘着材層を中空ゴルフクラブヘッドの内部に付着させた場合、ボールを打ったときのゴルフクラブヘッドの一次固有振動数が低下し、打球音の周波数が小さくなり、打球音の音域が低音となる。特に、上記特開平７−１４８２８８のように粘着材層をソール部の広い範囲に設けた場合、ソール部の一次固有振動数が小さくなり、「カキーン」というメタルヘッド特有の甲高い爽快な打球音が生じなくなる。そのため、ゴルフクラブ使用者（プレーヤー）は、ナイスショットをしている場合であってもミスショットをしたのではないかという誤解を抱くことがある。   When the adhesive layer is attached to the inside of the hollow golf club head, the primary natural frequency of the golf club head when the ball is hit is reduced, the frequency of the hitting sound is reduced, and the sound range of the hitting sound is low. . In particular, when the adhesive material layer is provided in a wide range of the sole portion as in JP-A-7-148288, the primary natural frequency of the sole portion is reduced, and a high-pitched and refreshing hitting sound peculiar to a metal head called “Kakeen” is produced. No longer occurs. Therefore, the golf club user (player) may have a misunderstanding that he / she has made a miss shot even if he / she is a nice shot.

本発明は、このような問題点を解決し、爽快な打球音を発するゴルフクラブヘッドを提供することを目的とする。   An object of the present invention is to provide a golf club head that solves such problems and emits a refreshing hitting sound.

本発明（請求項１）のゴルフクラブヘッドは、少なくともフェース部、ソール部、サイド部、クラウン部及びホゼル部を有する中空のゴルフクラブヘッドであって、該ゴルフクラブヘッドの内面の一部に、異物を付着させるための粘着材が設けられているゴルフクラブヘッドにおいて、該ソール部に、該粘着材の配置領域を区画するための凸条部を設け、該粘着材を該配置領域に配置したことを特徴とするものである。   The golf club head of the present invention (Claim 1) is a hollow golf club head having at least a face portion, a sole portion, a side portion, a crown portion, and a hosel portion, and a part of the inner surface of the golf club head, In the golf club head provided with an adhesive material for adhering foreign matter, the sole portion is provided with a ridge for partitioning the placement area of the adhesive material, and the adhesive material is placed in the placement area. It is characterized by this.

請求項２のゴルフクラブヘッドは、請求項１において、前記凸条部は前記フェース部から離隔していることを特徴とするものである。   According to a second aspect of the present invention, the golf club head according to the first aspect is characterized in that the protruding portion is separated from the face portion.

請求項３のゴルフクラブヘッドは、請求項１において、前記凸条部は、前記フェース部のうちヒール側に連なっていることを特徴とするものである。   A golf club head according to a third aspect of the present invention is the golf club head according to the first aspect, wherein the ridge portion is connected to the heel side of the face portion.

請求項４のゴルフクラブヘッドは、請求項１ないし３のいずれか１項において、前記ホゼル部は、ゴルフクラブヘッド内外を連通するように貫通しており、前記配置領域は、該ホゼル部の下方領域であることを特徴とするものである。   A golf club head according to a fourth aspect of the present invention is the golf club head according to any one of the first to third aspects, wherein the hosel portion passes through the golf club head so as to communicate with the inside and outside of the golf club head, It is a region.

請求項５のゴルフクラブヘッドは、請求項１ないし４のいずれか１項において、前記凸条部は、その全体が、前記ソール部のトウ・ヒール方向の中間よりもヒール側に設けられていることを特徴とするものである。   According to a fifth aspect of the present invention, in the golf club head according to any one of the first to fourth aspects, the entire protrusion is provided on the heel side with respect to the middle of the sole portion in the toe-heel direction. It is characterized by this.

本発明のゴルフクラブヘッドは、内部に粘着材を備えており、異物が付着して捕集されるので、異物が動くことによる異音が防止される。   The golf club head of the present invention includes an adhesive material inside, and foreign matter adheres and is collected, so that noise due to the movement of the foreign matter is prevented.

本発明では、ソール部に凸条部を設けて粘着材の配置領域を区画し、粘着材をこの配置領域に配置しているので、粘着材はソール部のうち限られた範囲のみ存在する。そのため、粘着材を設けたことによるボールヒット時におけるソール部の一次固有振動数の低下が抑制され、粘着材を入れていないゴルフクラブヘッドと大差ない打球音が発生するようになる。   In the present invention, the protruding portion is provided in the sole portion to partition the adhesive material arrangement area, and the adhesive material is arranged in the arrangement area. Therefore, the adhesive material is present only in a limited range of the sole portion. Therefore, a decrease in the primary natural frequency of the sole portion at the time of a ball hit due to the provision of the adhesive material is suppressed, and a hitting sound that is not much different from a golf club head not containing an adhesive material is generated.

この凸条部をフェース部から離隔させた場合、ボールヒット時におけるフェース部の撓みに影響がなく、ボール打ち出し速度が大きいものとなる。ただし、凸条部がフェース部のヒール側に連なるようにした場合にも、ボールヒット時におけるフェース部の撓みに殆ど影響がなく、ボール打ち出し速度が大きいものとなる。   When the convex portion is separated from the face portion, the deflection of the face portion at the time of a ball hit is not affected, and the ball launch speed is high. However, even when the ridges are connected to the heel side of the face part, there is almost no effect on the deflection of the face part at the time of a ball hit, and the ball launch speed is high.

なお、ホゼル部が貫通穴状である場合、ホゼル部にシャフトを差し込む際などにホゼル部内面やシャフト先端に付着していた異物がゴルフクラブヘッド内に入り込むおそれがある。粘着材配置領域をホゼル部の下方領域に設定しておくと、ホゼル部から落下してきた異物がそのまま粘着材上に落下して捕集されるので、異物に起因した異音発生が確実に防止される。また、ホゼル部から加熱溶融状態の粘着材をゴルフクラブヘッド内に注入したときに、粘着材が凸条部で堰止められ、凸条部よりもヒール側の粘着材配置領域に粘着材が配置される。   In the case where the hosel portion has a through hole shape, there is a possibility that foreign matter adhering to the inner surface of the hosel portion or the shaft tip may enter the golf club head when the shaft is inserted into the hosel portion. If the adhesive material placement area is set in the lower area of the hosel part, the foreign matter that has fallen from the hosel part will fall onto the adhesive material as it is and be collected, so it is possible to reliably prevent the generation of abnormal noise caused by the foreign matter. Is done. In addition, when a hot-melt adhesive material is injected into the golf club head from the hosel part, the adhesive material is blocked by the ridges, and the adhesive material is arranged in the adhesive material arrangement region on the heel side of the ridges. Is done.

実施の形態に係るゴルフクラブヘッドを示すものであり、クラウン部を破断した状態の後方かつ上方からの斜視図である。BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 shows a golf club head according to an embodiment, and is a perspective view from the rear and above in a state where a crown portion is broken. 実施の形態に係るゴルフクラブヘッドを示すものであり、クラウン部を破断した状態の上面図である。BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a top view of a golf club head according to an embodiment, with a crown portion broken away. 実施の形態に係るゴルフクラブヘッドの図２におけるIII−III線に沿う断面図である。It is sectional drawing which follows the III-III line | wire in FIG. 2 of the golf club head which concerns on embodiment. 別の実施の形態に係るゴルフクラブヘッドを示すものであり、クラウン部を破断した状態の後方かつ上方からの斜視図である。FIG. 7 is a perspective view showing a golf club head according to another embodiment, from the rear and from the top in a state where a crown portion is broken. さらに別の実施の形態に係るゴルフクラブヘッドを示すものであり、クラウン部を破断した状態の上面図である。FIG. 7 is a top view showing a golf club head according to another embodiment, with a crown portion broken. 異なる実施の形態に係るゴルフクラブヘッドを示すものであり、クラウン部を破断した状態の上面図である。FIG. 5 is a top view showing a golf club head according to another embodiment, with a crown portion broken.

以下、図面を参照して実施の形態について説明する。第１図〜第３図は第１の実施の形態に係るゴルフクラブヘッドを示している。なお、ゴルフクラブヘッド１の構造を明確にするために、第１図では粘着材の図示が省略されている。   Hereinafter, embodiments will be described with reference to the drawings. 1 to 3 show a golf club head according to a first embodiment. In order to clarify the structure of the golf club head 1, the adhesive material is not shown in FIG.

このゴルフクラブヘッド１は、フェース部２と、クラウン部３と、ソール部４と、サイド部５と、ホゼル部６とを有する中空形状であり、全体としてチタン合金などの金属にて一体に構成されている。金属としては、チタン、チタン合金、アルミ合金、ステンレスなど各種のものを用いることができる。ゴルフクラブヘッドの容積は３５０ｃｃ以上例えば４００〜４６０ｃｃ程度であることが好ましい。   This golf club head 1 has a hollow shape having a face portion 2, a crown portion 3, a sole portion 4, a side portion 5, and a hosel portion 6, and is constituted integrally by a metal such as a titanium alloy as a whole. Has been. Various metals such as titanium, titanium alloy, aluminum alloy, and stainless steel can be used as the metal. The volume of the golf club head is preferably 350 cc or more, for example, about 400 to 460 cc.

ホゼル部６は、第３図の通り貫通穴形状である。このホゼル部６の下端の下方領域を粘着材７の配置領域とするために、ソール部４に凸条部８が突設されている。この実施の形態では、凸条部８は、平面視において前部８ａと後部８ｂとが略々直交状に交わったＬ字形状である。前部８ａと後部８ｂとの交わり部が最もヒール１ｈから遠い（トウ１ｔに近い）ものとなっており、前端側及び後端側ほどヒール１ｈに近づいている。   The hosel portion 6 has a through-hole shape as shown in FIG. In order to make the area below the lower end of the hosel part 6 an area where the adhesive material 7 is disposed, a protruding strip part 8 is projected from the sole part 4. In this embodiment, the ridge portion 8 has an L-shape in which the front portion 8a and the rear portion 8b intersect each other substantially orthogonally in a plan view. The intersection of the front portion 8a and the rear portion 8b is the farthest from the heel 1h (closer to the toe 1t), and is closer to the heel 1h toward the front end side and the rear end side.

この凸条部８の前端はフェース部２との間から若干（例えば１〜１０ｍｍ特に２〜５ｍｍ）離隔している。この凸条部８の後端は、ヒール１ｈ側のサイド部５に連なっているが、若干（例えば２〜５ｍｍ程度）離隔していてもよい。この凸条部８よりもヒール１ｈ側が粘着材７の配置領域である。この凸条部８は、その全体が、ゴルフクラブヘッド１のトウ１ｔとヒール１ｈとを結ぶトウ・ヒール方向の中間Ｃよりもヒール１ｈ側に位置している。容積４００〜４６０ｃｃ程度のゴルフクラブヘッドの場合、この中間Ｃから凸条部８の最もトウ側までの距離Ｌ（第３図）は１０ｍｍ以上例えば１２〜３０ｍｍ程度が好ましい。   The front end of the ridge 8 is slightly separated from the face 2 (for example, 1 to 10 mm, particularly 2 to 5 mm). The rear end of the ridge portion 8 is continuous with the side portion 5 on the heel 1h side, but may be slightly separated (for example, about 2 to 5 mm). The heel 1 h side is an arrangement region of the adhesive material 7 with respect to the protruding portion 8. The entire protrusion 8 is positioned on the heel 1 h side from the middle C in the toe-heel direction connecting the toe 1 t and the heel 1 h of the golf club head 1. In the case of a golf club head having a volume of about 400 to 460 cc, the distance L (FIG. 3) from the middle C to the toe side of the ridge 8 is preferably 10 mm or more, for example, about 12 to 30 mm.

凸条部８はソール部４と一体の金属製の壁状である。壁の最も高い部分のソール部４からの高さは１〜１０ｍｍ特に２〜５ｍｍ程度が好適である。凸条部８の壁の厚さは３ｍｍ以下、例えば０．５〜１．５ｍｍ程度が好適である。   The ridge portion 8 has a metal wall shape integral with the sole portion 4. The height of the highest part of the wall from the sole part 4 is preferably about 1 to 10 mm, particularly about 2 to 5 mm. The thickness of the wall of the ridge portion 8 is preferably 3 mm or less, for example, about 0.5 to 1.5 mm.

粘着材７としては、粘着付与剤と熱可塑性エラストマーの混合物が好ましく、例えば、粘着付与剤としては、ロジンエステル樹脂、ロジンエステル樹脂、テルペンフェノール樹脂、テルペン樹脂、低分子量のブチルゴム、ポリブテン樹脂などを用い、これに、熱可塑性樹脂または、ポリスチレン系エラストマー、ポリウレタンエラストマーなどの各種エラストマーを混ぜたものが好ましい。ゴルフクラブヘッド１の重量を徒に増大させないようにするために、粘着材７の重量は１５ｇ以下例えば２〜１２ｇ程度であることが好ましい。   The adhesive 7 is preferably a mixture of a tackifier and a thermoplastic elastomer. Examples of the tackifier include rosin ester resin, rosin ester resin, terpene phenol resin, terpene resin, low molecular weight butyl rubber, polybutene resin, and the like. It is preferable to use a thermoplastic resin or a mixture of various elastomers such as polystyrene elastomer and polyurethane elastomer. In order not to increase the weight of the golf club head 1 undesirably, the weight of the adhesive 7 is preferably 15 g or less, for example, about 2 to 12 g.

この粘着材７は、好ましくは、注入ノズル（図示略）をホゼル部６に通し、加温して粘度を低くして該注入ノズルから配置領域に注入されることにより設けられる。凸条部８を設けてあるので、この粘着材７はソール部４の中心側にまで広がることはなく、粘着材７は前記配置領域に配置される。   This adhesive material 7 is preferably provided by passing an injection nozzle (not shown) through the hosel portion 6 and heating it to lower the viscosity to be injected from the injection nozzle into the arrangement region. Since the protruding portion 8 is provided, the adhesive material 7 does not spread to the center side of the sole portion 4, and the adhesive material 7 is arranged in the arrangement region.

ソール部４の厚さは０．５〜１．２ｍｍ程度が好適である。   The thickness of the sole part 4 is preferably about 0.5 to 1.2 mm.

このように構成されたゴルフクラブヘッド１は、内部に粘着材７を備えており、異物が付着して捕集されるので、異物が動くことによる異音が防止される。また、ソール部４に凸条部８を設けて粘着材７の配置領域を区画し、粘着材７をこの配置領域にのみ配置しているので、粘着材７はソール部４のうち限られた範囲にのみ存在する。そのため、粘着材を設けたことによるボールヒット時におけるソール部４の一次固有振動数の低下が抑制され、粘着材を入れていないゴルフクラブヘッドと大差ない打球音が発生するようになる。   The golf club head 1 configured as described above includes an adhesive 7 inside, and foreign matter adheres and is collected, so that abnormal noise due to the movement of the foreign matter is prevented. Further, the protruding portion 8 is provided on the sole portion 4 to partition the arrangement area of the adhesive material 7, and the adhesive material 7 is arranged only in this arrangement area, so the adhesive material 7 is limited in the sole portion 4. Exists only in range. Therefore, a decrease in the primary natural frequency of the sole portion 4 at the time of a ball hit due to the provision of the adhesive material is suppressed, and a hitting sound that is not significantly different from a golf club head not containing an adhesive material is generated.

なお、本発明者の研究によると、打球音の発生部位としてはソール部４が主要部となる。そのため、ソール部４の一次固有振動数を高目に保つことにより、「カキーン」というメタルヘッド特有の甲高い爽快な金属音が強く発生するようになる。   According to the research of the present inventor, the sole portion 4 is a main portion as a hitting sound generation site. For this reason, by keeping the primary natural frequency of the sole portion 4 high, a high-pitched exhilarating metal sound peculiar to the metal head called “Kakeen” is strongly generated.

この実施の形態では、凸条部８をフェース部２から離隔させているので、ボールヒット時におけるフェース部２の撓みに影響がなく、ボール打ち出し速度（初速）が大きいものとなる。ただし、図示はしないが、凸条部８がフェース部２のヒール１ｈ側に連なるようにした場合にも、ボールヒット時におけるフェース部２の撓みに殆ど影響がなく、ボール打ち出し速度が大きいものとなる。   In this embodiment, since the protruding portion 8 is separated from the face portion 2, there is no influence on the bending of the face portion 2 at the time of a ball hit, and the ball launch speed (initial speed) is high. However, although not shown in the figure, even when the ridges 8 are connected to the heel 1h side of the face part 2, there is almost no influence on the deflection of the face part 2 at the time of a ball hit, and the ball launch speed is high. Become.

この実施の形態では、ホゼル部６が貫通穴状であるので、ホゼル部６にシャフト（図示略）を差し込む際などにホゼル部６の内面やシャフトの先端部に付着していた異物がホゼル部６から落下してゴルフクラブヘッド１内に入り込むおそれがある。この実施の形態では、粘着材７をホゼル部６の下方領域に設けているので、ホゼル部６から落下してきた異物がそのまま粘着材７上に落下して直ちに捕集されるので、異物に起因した異音発生が確実に防止される。   In this embodiment, since the hosel portion 6 has a through-hole shape, foreign matter attached to the inner surface of the hosel portion 6 or the tip end portion of the shaft when the shaft (not shown) is inserted into the hosel portion 6 or the like. There is a risk of falling from 6 and entering the golf club head 1. In this embodiment, since the adhesive material 7 is provided in the lower region of the hosel portion 6, the foreign matter dropped from the hosel portion 6 falls on the adhesive material 7 as it is and is immediately collected. Generation of abnormal noise is reliably prevented.

上記実施の形態では、凸条部８は、平面視においてＬ字形に屈曲した形状となっているが、第４図のゴルフクラブヘッド１Ａの凸条部８Ａのようにソール部４の中央側に向って膨出する弧形状に湾曲していてもよい。また、第５図のゴルフクラブヘッド１Ｂの凸条部８Ｂのように、前部８ａと後部８ｂとが鈍角状に交わる「く」字形状であってもよく、第６図のゴルフクラブヘッド１Ｃの凸条部８Ｃのように一直線状に延在してもよい。第４図〜第６図のゴルフクラブヘッドのその他の構成は第１図〜第３図のゴルフクラブヘッドと同じであり、同一符号は同一部分を示している。図示は省略するが、凸条部の平面視形状は、ジグザグ形、波線形などであってもよい。   In the above embodiment, the ridge portion 8 is bent in an L shape in plan view, but on the center side of the sole portion 4 like the ridge portion 8A of the golf club head 1A in FIG. You may curve in the arc shape which bulges toward. Further, like the convex portion 8B of the golf club head 1B in FIG. 5, the front portion 8a and the rear portion 8b may have an oblong shape, and the golf club head 1C in FIG. You may extend in a straight line like the protruding line part 8C. Other configurations of the golf club head of FIGS. 4 to 6 are the same as those of the golf club head of FIGS. 1 to 3, and the same reference numerals denote the same parts. Although illustration is omitted, the plan view shape of the ridges may be a zigzag shape, a wave shape, or the like.

上記実施の形態では、ゴルフクラブヘッドは全体として金属製であるが、一部例えばクラウン部の一部又は全体を繊維強化合成樹脂など金属以外の材料で構成してもよい。   In the above-described embodiment, the golf club head is entirely made of metal, but a part, for example, a part or the whole of the crown portion may be made of a material other than metal such as fiber reinforced synthetic resin.

実施例１
容積が４６０ｃｃの第１図〜第３図に図示の構成のゴルフクラブヘッド１を４個製作した。ゴルフクラブヘッドのフェース部２以外の本体部はインベストメント鋳造法により作られた（Ｔｉ−６Ａｌ−４Ｖ）α−β型チタン合金で作成した。フェース部２はβ型チタン合金を鍛造して製作し、本体部に対しレーザ溶接した。 Example 1
Four golf club heads 1 having a volume of 460 cc and having the structure shown in FIGS. 1 to 3 were manufactured. The main body portion other than the face portion 2 of the golf club head was made of (Ti-6Al-4V) α-β type titanium alloy made by an investment casting method. The face portion 2 was manufactured by forging a β-type titanium alloy and laser-welded to the main body portion.

ゴルフクラブヘッドの各部分の厚さについては、クラウン部は０．７ｍｍ、サイド部は０．８ｍｍ、ソール部は０．８ｍｍとした。フェース部の肉厚は、周縁部で２．２ｍｍとし、中央部に向って徐々に肉厚を大きくし、中央部で３．０ｍｍとした。   Regarding the thickness of each part of the golf club head, the crown part was 0.7 mm, the side part was 0.8 mm, and the sole part was 0.8 mm. The thickness of the face portion was 2.2 mm at the peripheral portion, the thickness was gradually increased toward the central portion, and 3.0 mm at the central portion.

凸条部８の長さは、前部８ａを１９ｍｍ、後部８ｂを５０ｍｍとした。前部８ａと後部８ｂとの交わり角度を約９０°とし、この交わり部から中央Ｃまでの距離Ｌを２４ｍｍとし、凸条部８の高さは交わり部付近で１０ｍｍとし、壁の肉厚は１ｍｍとした。   The length of the protruding portion 8 was 19 mm for the front portion 8a and 50 mm for the rear portion 8b. The intersection angle between the front portion 8a and the rear portion 8b is about 90 °, the distance L from the intersection portion to the center C is 24 mm, the height of the ridge portion 8 is 10 mm near the intersection portion, and the wall thickness is It was 1 mm.

ホゼル部６に注入ノズルを差し込み、１５０℃に加温した粘着剤（スチレン系エラストマーとロジンエステル樹脂やポリブテン樹脂を混ぜたもの）を３．４ｇ配置領域に注入した。ファイバースコープをホゼル部６からゴルフクラブヘッド１内に差し込んで観察したところ、粘着材は凸条部８よりもヒール側の配置領域にのみ薄く広がっていることが確認された。   An injection nozzle was inserted into the hosel part 6, and an adhesive (mixed with a styrene elastomer and a rosin ester resin or polybutene resin) heated to 150 ° C. was injected into the region where 3.4 g was disposed. When the fiberscope was inserted into the golf club head 1 from the hosel portion 6 and observed, it was confirmed that the adhesive material spread thinly only in the arrangement region on the heel side with respect to the ridge portion 8.

このゴルフクラブヘッドに長さ４５インチのカーボンシャフトを装着してゴルフクラブを製作し、ゴルフクラブヘッドのソール部の一次固有振動数を測定した。参考のために、粘着材注入前のゴルフクラブヘッドを用いたゴルフクラブについてもソール部の一次固有振動数を測定した。   A golf club was manufactured by attaching a carbon shaft having a length of 45 inches to this golf club head, and the primary natural frequency of the sole portion of the golf club head was measured. For reference, the primary natural frequency of the sole portion was also measured for the golf club using the golf club head before injection of the adhesive material.

ソール部の一次固有振動数の測定は、ソール部に加速度計を接着剤で取り付け、ソール部をインパルスハンマーで叩いたときの一次固有振動数をデータステーションを介してパソコン（ＰＣ）に入力し、解析することにより行った。ＰＣには、周波数応答関数を算出するＦＦＴ解析ソフトおよびモーダルパラメータを算出するモーダル解析ソフトがインストールされている。   To measure the primary natural frequency of the sole part, an accelerometer is attached to the sole part with an adhesive, and the primary natural frequency when the sole part is hit with an impulse hammer is input to a personal computer (PC) via a data station, This was done by analysis. The PC is installed with FFT analysis software for calculating a frequency response function and modal analysis software for calculating a modal parameter.

具体的には、各機器として以下のものを用いた。
・データステーション：小野測器（株）製ＤＳ２０００
・インパルスハンマー：ＤＹＴＲＡＮ社製５８００ＳＬ
・加速度計：小野測器（株）製ＮＰ３２１０
・ＦＦＴ解析ソフト：小野測器（株）製ＤＳ０２２１
・モーダル解析ソフト：VibrantTechnology社製Ｖｉｓｕａｌ Ｍｏｄａｌ Specifically, the following devices were used.
・ Data station: DS2000 manufactured by Ono Sokki Co., Ltd.
・ Impulse hammer: DYTRAN 5800SL
Accelerometer: NP3210 manufactured by Ono Sokki Co., Ltd.
-FFT analysis software: DS0221 manufactured by Ono Sokki Co., Ltd.
-Modal analysis software: Visual Model made by VibrantTechnology

実施例２
凸条部の高さを１５ｍｍとし、粘着材の注入量を６．１ｇとしたこと以外は実施例１と同様とし、ソール部の一次固有振動数を測定した。参考のために、粘着材注入前のゴルフクラブヘッドを用いたゴルフクラブについてもソール部の一次固有振動数を測定した。 Example 2
The primary natural frequency of the sole portion was measured in the same manner as in Example 1 except that the height of the protruding portion was 15 mm and the injection amount of the adhesive material was 6.1 g. For reference, the primary natural frequency of the sole portion was also measured for the golf club using the golf club head before injection of the adhesive material.

比較例１
リブを設けず、粘着材をソール部の中央付近に注入したこと以外は実施例１と同様とし、ソール部の一次固有振動数を測定した。参考のために、粘着材注入前のゴルフクラブヘッドを用いたゴルフクラブについてもソール部の一次固有振動数を測定した。 Comparative Example 1
The primary natural frequency of the sole portion was measured in the same manner as in Example 1 except that the rib was not provided and the adhesive material was injected near the center of the sole portion. For reference, the primary natural frequency of the sole portion was also measured for the golf club using the golf club head before injection of the adhesive material.

比較例２
リブを設けず、粘着材をソール部の中央付近に注入したこと以外は実施例２と同様とし、ソール部の一次固有振動数を測定した。参考のために、粘着材注入前のゴルフクラブヘッドを用いたゴルフクラブについてもソール部の一次固有振動数を測定した。 Comparative Example 2
The primary natural frequency of the sole portion was measured in the same manner as in Example 2 except that no rib was provided and the adhesive material was injected near the center of the sole portion. For reference, the primary natural frequency of the sole portion was also measured for the golf club using the golf club head before injection of the adhesive material.

Figure 2011125540
Figure 2011125540

表１の実施例１と比較例１との対比及び実施例２と比較例２との対比から明らかな通り、粘着材をヒール側に注入した場合、ソール部中央付近に注入した場合に比べてソール部の一次固有振動数の低下が少なくなることが認められる。なお、ソール部の一次固有振動数と打球音とには強い相関関係があり、ソール部の一次固有振動数が小さいほど打球音の周波数は低音側となる。   As is clear from the comparison between Example 1 and Comparative Example 1 in Table 1 and the comparison between Example 2 and Comparative Example 2, when the adhesive material was injected on the heel side, compared with the case where it was injected near the center of the sole part. It can be seen that the decrease in the primary natural frequency of the sole portion is reduced. Note that there is a strong correlation between the primary natural frequency of the sole portion and the hitting sound, and the lower the primary natural frequency of the sole portion, the lower the frequency of the hitting sound.

１ ゴルフクラブヘッド
１ｈ ヒール
１ｔ トウ
２ フェース部
３ クラウン部
４ ソール部
５ サイド部
６ ホゼル部
７ 粘着材
８ 凸条部 DESCRIPTION OF SYMBOLS 1 Golf club head 1h Heel 1t Toe 2 Face part 3 Crown part 4 Sole part 5 Side part 6 Hosel part 7 Adhesive material 8 Projection part

Claims (5)

少なくともフェース部、ソール部、サイド部、クラウン部及びホゼル部を有する中空のゴルフクラブヘッドであって、
該ゴルフクラブヘッドの内面の一部に、異物を付着させるための粘着材が設けられているゴルフクラブヘッドにおいて、
該ソール部に、該粘着材の配置領域を区画するための凸条部を設け、
該粘着材を該配置領域に配置したことを特徴とするゴルフクラブヘッド。 A hollow golf club head having at least a face portion, a sole portion, a side portion, a crown portion, and a hosel portion,
In the golf club head provided with an adhesive material for attaching foreign matter to a part of the inner surface of the golf club head,
Providing the sole part with a protruding line part for partitioning the arrangement region of the adhesive material,
A golf club head, wherein the adhesive material is arranged in the arrangement region. 請求項１において、前記凸条部は前記フェース部から離隔していることを特徴とするゴルフクラブヘッド。   The golf club head according to claim 1, wherein the ridge portion is separated from the face portion. 請求項１において、前記凸条部は、前記フェース部のうちヒール側に連なっていることを特徴とするゴルフクラブヘッド。   2. The golf club head according to claim 1, wherein the ridge portion is connected to the heel side of the face portion. 請求項１ないし３のいずれか１項において、前記ホゼル部は、ゴルフクラブヘッド内外を連通するように貫通しており、
前記配置領域は、該ホゼル部の下方領域であることを特徴とするゴルフクラブヘッド。 In any 1 item | term of the Claims 1 thru | or 3, The said hosel part has penetrated so that the inside and outside of a golf club head may be connected,
The golf club head according to claim 1, wherein the arrangement region is a region below the hosel portion. 請求項１ないし４のいずれか１項において、前記凸条部は、その全体が、前記ソール部のトウ・ヒール方向の中間よりもヒール側に設けられていることを特徴とするゴルフクラブヘッド。   5. The golf club head according to claim 1, wherein the protruding portion is entirely provided on a heel side with respect to a middle of the sole portion in a toe-heel direction. 6.
JP2009287878A 2009-12-18 2009-12-18 Golf club head Pending JP2011125540A (en)