JP2011099108A

JP2011099108A - Highly conductive molding compound, and fuel cell bipolar plate containing the same

Info

Publication number: JP2011099108A
Application number: JP2010288956A
Authority: JP
Inventors: Kurt I Butler; アイ．バトラーカート
Original assignee: Quantum Composites Inc
Current assignee: Quantum Composites Inc
Priority date: 1999-03-19
Filing date: 2010-12-24
Publication date: 2011-05-19

Abstract

<P>PROBLEM TO BE SOLVED: To provide a highly conductive polymer to be suitably used as a bipolar plate of an electrochemical cell. <P>SOLUTION: The conductive polymer is disclosed which is suitable for use in applications requiring corrosion resistance when subjected to acidic flow at temperature ranging from -40 to 140°F and which can be molded into highly intricate and thin specimens that exhibit consistent conductivity, sufficient strength and flexibility, and appropriate surface characteristics. In particular, the invention involves molding unsaturated prepolymer resin compositions, which have high loadings of conductive fillers. Further, to acquire necessary characteristics, the compositions include rheological modifiers and polyethylene. Ostensibly, these modifiers act to alter the apparent molecular weight and three dimensional prepolymer network structures correcting rheological deficiencies. The composition is disclosed for use in the electrochemical cell (for example, a fuel cell). <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

本特許出願は、１９９９年３月１９日に出願された米国仮特許出願第６０／１２５，１３８号に基づいている。 This patent application is based on US Provisional Patent Application No. 60 / 125,138, filed Mar. 19, 1999.

（発明の分野）
本発明の分野は、熱硬化性バルク成形組成物を使用する方法のような成形方法に特に有用な高導電性組成物である。これらの成形組成物は、高解像度複合構造に形成できる。例えば、それらは、薄板様試験片（例えば、千分の６０〜２００インチ）に成形でき、これらは、非常に狭く比較的に滑らかな流路の複雑に模様を付けたネットワークを有する。これらの試験片は、電気化学セル双極プレートとして使用される。これらのプレートは、望ましくは、少なくとも４０、５０、６０、７０、８０、９０または９６Ｓ／ｃｍのバルク導電率を有する。それらはまた、所望の表面特性；熱、温度、薬品耐性および収縮耐性；強度；および価格を有する。 (Field of Invention)
The field of the invention is highly conductive compositions that are particularly useful for molding methods, such as those using thermosetting bulk molding compositions. These molding compositions can be formed into high resolution composite structures. For example, they can be formed into sheet-like specimens (e.g., 60-200 inches), which have a complex patterned network of very narrow and relatively smooth flow paths. These specimens are used as electrochemical cell bipolar plates. These plates desirably have a bulk conductivity of at least 40, 50, 60, 70, 80, 90 or 96 S / cm. They also have the desired surface properties; heat, temperature, chemical and shrink resistance; strength; and price.

（発明の背景）
導電性重合体は、伝統的な導電性材料の代替物を提供する際に用途があり、これらは、しばしば、複雑な部品を製造するのに、多大な労働費が関与している。特に、多量の製品が要求されている場合、重合体の成形費用は、他の材料に対する同程度の機械切削にかかる費用よりも、ずっと費用効率が高いことが判明され得る。しかしながら、過去において、高レベルの導電率および所望の成形特性の両方を達成することは、困難であることが判明している。一般に、十分なレベルの導電率を達成するためには、重合体マトリックス中にて、適当な充填剤の高レベルの重量割合が存在することが必要である。しかしながら、これらの高装填レベルは、得られる組成物の強度、耐久性および成形性に伴う問題を引き起こす。 (Background of the Invention)
Conductive polymers have applications in providing an alternative to traditional conductive materials, which often involve significant labor costs in producing complex parts. In particular, when large quantities of product are required, the polymer molding costs can be found to be much more cost effective than the cost of comparable mechanical cutting on other materials. However, in the past, it has proven difficult to achieve both high levels of conductivity and desired molding characteristics. In general, to achieve a sufficient level of conductivity, it is necessary that a high level weight fraction of a suitable filler be present in the polymer matrix. However, these high loading levels cause problems with the strength, durability and moldability of the resulting composition.

特に、先に言及した強度、耐久性および成形の問題を解決することが有益な１領域には、燃料電池での応用がある。電気化学的燃料電池は、清浄で環境にやさしい潜在的に無限なエネルギー源として、非常に魅力がある。これらの燃料電池は、それに加えて、小規模なエネルギー消費（例えば、家庭での用途）、または工業規模の用途、および商用発電にさえ、適当な規模で、構築できる。それらは、電力の小さい電気器具（例えば、コンピューターまたはキャップ設備）、または自動車および他の輸送形態のための携帯用途を有する。これらの異なる用途は、サイズが異なるものの、その基本的な構造は、１キロワット未満から数千キロワットまでの発電用に対して、同じである。 In particular, one area where it is beneficial to solve the strength, durability and molding problems referred to above is in fuel cell applications. Electrochemical fuel cells are very attractive as a potentially endless energy source that is clean and environmentally friendly. In addition, these fuel cells can be built on a suitable scale for small-scale energy consumption (eg, home use), or industrial scale applications, and even commercial power generation. They have low power electrical appliances (eg, computers or cap equipment), or portable applications for automobiles and other forms of transport. Although these different applications differ in size, their basic structure is the same for power generation from less than 1 kilowatt to thousands of kilowatts.

基本的には、燃料電池は、ガルバーニ電池であり、ここで、燃料の化学エネルギーは、電気化学的プロセスによって、直接的に電気エネルギーに変換される。この燃料電池の基本的な成分は、アノードおよびカソードを含む電極、電極触媒、および電解質である。液体および固体の両方の電解質燃料電池を完成する作業が行われており、本発明は、両方の型の燃料電池において、用途が見出され得る。 Basically, the fuel cell is a galvanic cell, where the chemical energy of the fuel is converted directly into electrical energy by an electrochemical process. The basic components of this fuel cell are an electrode including an anode and a cathode, an electrocatalyst, and an electrolyte. Work has been done to complete both liquid and solid electrolyte fuel cells, and the present invention can find use in both types of fuel cells.

固体電解質には、高分子膜が挙げられ、これらは、典型的には、水素で燃料供給される陽子交換膜として作用する。これらの膜は、通常、過フッ素化スルホン酸高分子膜を含み、これは、２個の触媒化電極（これは、電極触媒として、炭素上に支持された白金を利用し得る）間で挟まれている。水素燃料電池は、反応チャンバを形成し、これは、そのアノードにおいて、水素を消費する。このカソードでは、酸素は、その電極触媒部位において、陽子および電子と反応して、その反応生成物として、水を生じる。この電極の領域では、三相界面が形成され、この電極、電解質および気相の間では、微妙なバランスが維持されなければならない。 Solid electrolytes include polymer membranes, which typically act as proton exchange membranes fueled with hydrogen. These membranes typically include a perfluorinated sulfonic acid polymer membrane, which is sandwiched between two catalyzed electrodes (which can utilize platinum supported on carbon as an electrocatalyst). It is. The hydrogen fuel cell forms a reaction chamber that consumes hydrogen at its anode. At this cathode, oxygen reacts with protons and electrons at its electrocatalytic sites to produce water as its reaction product. In the region of this electrode, a three-phase interface is formed and a delicate balance must be maintained between this electrode, the electrolyte and the gas phase.

他の電極の使用が関与しているシステムもまた、研究されている。これらには、アルカリ燃料電池、リン酸燃料電池、溶融炭酸塩燃料電池、および固形酸化物燃料電池が挙げられる。しかしながら、それらの原理は、これらの製品を完成する際の一部の問題と同様に、類似している。 Systems that involve the use of other electrodes are also being investigated. These include alkaline fuel cells, phosphate fuel cells, molten carbonate fuel cells, and solid oxide fuel cells. However, their principles are similar, as are some of the problems in completing these products.

燃料電池反応器は、単一電池または複数電池の積み重ねを含み得る。いずれの場合でも、この電池は、少なくとも２枚の非常に導電性の流動フィールドプレートを含み、これには、複数の機能を果たす。これらのプレートは、電流収集器として機能し得、これは、この燃料電池の電圧端子と電極との間で、電気的な連続性を与える。これらはまた、機械的な支持（例えば、その膜／電極のアセンブリに対して）を与える。それに加えて、これらのプレートは、これらの電極へと反応物を輸送するように作用し、先に言及した微妙な相バランスを確立するのに必須である。 The fuel cell reactor may include a single cell or a stack of multiple cells. In any case, the battery includes at least two highly conductive flow field plates that serve multiple functions. These plates can function as current collectors, which provide electrical continuity between the voltage terminals and electrodes of the fuel cell. They also provide mechanical support (eg, for the membrane / electrode assembly). In addition, these plates act to transport reactants to these electrodes and are essential to establish the delicate phase balance referred to above.

典型的には、この燃料電池プレートは、薄くて比較的に平らなプレート部材であり、これらは、相互連絡しているチャンネルの非常に複雑なネットワークを含み、このネットワークは、このプレートの流動フィールド領域を形成する。これらのチャンネルの構造は、反応物の正常な流れを維持するために、また、チャンネル形成または停滞領域の形成（これは、燃料電池の性能を悪化させる）を回避するために、非常によく開発されている。これらの反応物の流れを正しく管理すること、およびこれらの電極触媒を反応物の適当なバランスと共に正確に連続的に供給することは、重大である。それゆえ、これらのプレートが、非常にうまく設計した流れ迷路内で、明瞭な流路を規定し維持することは、必須である。さらに、適当な寿命を保証するために、これらのプレートは、種々の条件下において、表面腐食に抵抗できなければならない。例えば、燃料電池は、外部に配置されて外の天候の影響を受け得る。それゆえ、これらの電池は、４０〜２００°Ｆの範囲の温度で、応力割れおよび腐食に対して抵抗性でなければならない。さらに、この電池内の状態は、腐食性であるので、これらの電池はまた、これらの温度での種々の腐食物質からの化学的な攻撃に対して抵抗性でなければならない。例えば、これらのプレートは、この燃料電池の型に依存して、脱イオン水、メタノール、ギ酸、ホルムアルデヒド、ヘビーナフサ、フッ化水素酸、テトラフルオロエチレン、およびヘキサフルオロプロピレンの影響を受け得る。さらに、この燃料電池内の状態は、高温（すなわち、１５０〜２００°Ｆ）だけでなく、高圧（すなわち、常圧〜３０ｐ．ｓ．ｉ．）に至り得る。腐食分解は、この燃料電池内での流動パターンを変えることにより殆ど確実にシステムの故障を引き起こすので、回避されなければならない。 Typically, the fuel cell plates are thin and relatively flat plate members that contain a very complex network of interconnecting channels that are connected to the flow field of the plate. Form a region. The structure of these channels is very well developed to maintain normal flow of reactants and to avoid channel formation or stagnant region formation (which degrades fuel cell performance) Has been. It is critical to properly manage the flow of these reactants and to supply these electrocatalysts accurately and continuously with an appropriate balance of reactants. It is therefore essential that these plates define and maintain a clear flow path within a very well designed flow maze. In addition, these plates must be able to resist surface corrosion under a variety of conditions in order to ensure a reasonable life. For example, the fuel cell may be disposed outside and be affected by outside weather. Therefore, these batteries must be resistant to stress cracking and corrosion at temperatures in the range of 40-200 ° F. In addition, since the conditions within this battery are corrosive, these batteries must also be resistant to chemical attack from various corrosive substances at these temperatures. For example, these plates can be affected by deionized water, methanol, formic acid, formaldehyde, heavy naphtha, hydrofluoric acid, tetrafluoroethylene, and hexafluoropropylene, depending on the type of fuel cell. Further, the conditions within this fuel cell can reach not only high temperatures (ie, 150-200 ° F.), but also high pressures (ie, normal pressure to 30 p.s.i.). Corrosion decomposition must be avoided because changing the flow pattern in the fuel cell almost certainly causes system failure.

燃料電池プレートに対する種々の要件を解決する過去の試行には、金属および機械切削したグラファイトのプレートを使用することが挙げられる。金属プレートを使用すると、１電池あたりの重量が重くなり、機械切削のコストが大きくなり、おそらく、腐食の問題が起こる。機械切削したグラファイトプレートは、この重量および腐食の問題を解決するが、機械切削のコストが高く、特に、非常に薄いプレートとして作製したとき、脆い製品ができる。グラファイト／ポリ（フッ化ビニリデン）プレートが一部で使用されているが、これらは、高価で脆弱であって長いサイクル時間がかかるという特徴がある。 Past attempts to solve various requirements for fuel cell plates include the use of metal and machined graphite plates. The use of a metal plate increases the weight per cell, increases the cost of machine cutting, and possibly causes corrosion problems. Machined graphite plates solve this weight and corrosion problem, but they are expensive to machine, especially when made as very thin plates, resulting in brittle products. Graphite / poly (vinylidene fluoride) plates are used in part, but they are expensive, fragile and take a long cycle time.

特許文献１の内容は、電気化学セルの作業および組成物の教示について、本明細書中で参考として援用されている。特許文献２の内容は、電気化学セル用のグラファイトベースの分離器の教示について、本明細書中で参考として援用されている。 The contents of U.S. Pat. No. 6,057,086 are incorporated herein by reference for the work of the electrochemical cell and the teaching of the composition. The contents of U.S. Pat. No. 6,057,056 are incorporated herein by reference for the teaching of graphite-based separators for electrochemical cells.

米国特許第４，１９７，１７８号明細書U.S. Pat. No. 4,197,178 米国特許第４，３０１，２２２号明細書US Pat. No. 4,301,222

（発明の要旨）
過去において、従来公知のバルク成形化合物は、多量の導電性充填剤（例えば、グラファイト）を添加することにより、導電性になるように調節されている。成形中にて、その液体樹脂相は、この充填剤から分離されて、この成形から除外されることが観察された。さらに、この発生は、薄い成形試験片で割れを引き起こす傾向があることが観察された。さらに、これらの試験片内の異なる位置でのバルク導電性の測定は、矛盾していた。本発明に従って、前述の問題を解決する組成物が調合できることが発見された。特に、これらの調合は、高い装填量の導電性充填剤を備えた樹脂マトリックスの使用；種々の追加添加剤（例えば、開始剤、離型剤、およびカーボンブラック）；および１種またはそれ以上のレオロジー剤（これは、第ＩＩ族の酸化物、アルカリ金属酸化物、カルボジアミド、ポリイソシアネート、ポリエチレンおよびポリテトラエチレンフルオロエチレンからなる群から選択される）を含む。この成形剤が作用する機構の１つに考えられる説明には、このプレポリマー（例えば、ビニルエステル樹脂または不飽和ポリエステル樹脂）の見かけ分子量を確立するように作用することがある。あるいは、これらの試薬は、例えば、成形中の剪断を少なくすることにより、流動を促進し得る。これらのレオロジー剤を使用すると、相分離だけでなく、割れおよび矛盾した導電性測定がなくなる。これらの問題は、非常に高濃度の導電性充填剤と共に成形される試験片の複雑な構造の結果であると予想されている。 (Summary of the Invention)
In the past, previously known bulk molding compounds have been adjusted to be conductive by adding large amounts of conductive fillers (eg, graphite). During molding, it was observed that the liquid resin phase was separated from the filler and excluded from the molding. Furthermore, it has been observed that this occurrence tends to cause cracking in thin molded specimens. In addition, measurements of bulk conductivity at different locations within these specimens were inconsistent. In accordance with the present invention, it has been discovered that compositions can be formulated that solve the aforementioned problems. In particular, these formulations use a resin matrix with a high loading of conductive filler; various additional additives (eg, initiators, mold release agents, and carbon black); and one or more A rheology agent, which is selected from the group consisting of Group II oxides, alkali metal oxides, carbodiamides, polyisocyanates, polyethylenes and polytetraethylene fluoroethylenes. A possible explanation for one of the mechanisms by which the molding agent acts may be to establish the apparent molecular weight of the prepolymer (eg, vinyl ester resin or unsaturated polyester resin). Alternatively, these reagents can facilitate flow, for example, by reducing shear during molding. The use of these rheological agents eliminates not only phase separation, but also cracking and inconsistent conductivity measurements. These problems are expected to be a result of the complex structure of the test specimens molded with very high concentrations of conductive filler.

成形および割れの問題を解決することに加えて、他の特性（例えば、熱膨張率、導電率および熱伝導率、収縮抵抗および機械的特性）は、本発明を使用する結果として、さらに均一になるかおよび／または改良され得る。前述の改良に加えて、本発明の樹脂組成物は、高いガラス転移温度を示し、成形部分の熱強度が改良されることが見出された。開始剤の種類および量ならびに禁止剤の種類および量を制御することにより、このプレポリマーに対してゲル化時間および硬化時間の両方を最適化することによって、さらに改良することもまた、可能である。 In addition to solving the forming and cracking problems, other properties (eg, thermal expansion, conductivity and thermal conductivity, shrinkage resistance and mechanical properties) are more uniform as a result of using the present invention. And / or can be improved. In addition to the improvements described above, it has been found that the resin composition of the present invention exhibits a high glass transition temperature and improves the heat strength of the molded part. Further improvements are also possible by optimizing both gel time and cure time for this prepolymer by controlling the type and amount of initiator and the type and amount of inhibitor. .

これらの組成物から成形した試験片における前述の改良により、本発明の追加実施態様として、双極プレートの低価格大量生産が可能となる。これらは、固定動力装置だけでなく、携帯型燃料電池に使用できる。
本発明は、例えば、以下を提供する。
（項目１）組成物であって、以下
ａ）不飽和プレポリマー樹脂であって、該プレポリマー樹脂は、不飽和ポリエステルおよびビニルエステル樹脂のうちの１種またはそれ以上を含有する；
ｂ）該樹脂と共重合可能な不飽和物質であって、該不飽和物質は、末端エチレン基を含有する；
ｃ）該組成物の全重量の少なくとも５０％を占める導電性充填剤；
ｄ）開始剤であって、該開始剤は、該共重合を開始する；ならびに
ｅ）有効量のレオロジー改質剤であって、該レオロジー改質剤は、成形中において、該樹脂と該導電性充填剤との間の相分離を防止し、該レオロジー改質剤は、第ＩＩ族の酸化物および水酸化物、カルボジアミド、アジリジン、ポリイソシアネート、ポリテトラフルオロエチレン、パーフルオロポリエーテル、ポリエチレン、粘土およびヒュームドシリカからなる群から選択される１種またはそれ以上の組成物である、
を含む、組成物。
（項目２）前記レオロジー改質剤の有効量が該系の全重量の約０．５％〜約１５％である、項目１に記載の組成物。
（項目３）前記導電性充填剤は、粒子状充填剤または薄片状充填剤であり、該導電性充填剤の量は、少なくとも６０重量％である、項目２に記載の組成物。
（項目４）前記導電性充填剤が、グラファイト充填剤であり、該導電性充填剤の量が少なくとも６５重量％である、項目３に記載の組成物。
（項目５）前記レオロジー改質剤が酸化マグネシウムおよび／または酸化カルシウムを含み、前記有効量が該組成物の重量に基づいて約０．１〜約２重量％である、項目１に記載の組成物。
（項目６）前記レオロジー改質剤がアジリジン、カルボジアミド、およびポリイソシアネートのうちの１つ以上であり、前記有効量が該組成物の重量に基づいて約１重量％〜約１０重量％である、項目１に記載の組成物。
（項目７）前記レオロジー改質剤の有効量が約４００ｐｓｉ〜約２０００ｐｓｉの圧力で約０．０５０インチ〜約０．２００インチの厚さに成形される部品の破壊を妨げるのに有効な量である、項目１に記載の組成物。
（項目８）前記改質剤が、ポリテトラフルオロエチレン、パーフルオロポリエーテルのうちの１つ以上を含み、前記有効量が該成形組成物の重量に基づいて約０．１重量％〜約５重量％である、項目１に記載の組成物。
（項目９）前記レオロジー改質剤がポリイソシアネートであり、前記有効量が該成形組成物の重量に基づいて約２重量％〜約８重量％である、項目１に記載の組成物。
（項目１０）前記導電性充填剤が合成結晶性グラファイト粒子であり、前記不飽和プレポリマー樹脂がエポキシビニル樹脂、ビスフェノールフマレート樹脂、変性ビスフェノールフマレートポリエステル樹脂、不飽和ポリエステル樹脂、ウレタン変性ビニルエステル樹脂、ウレタン変性ビニルエステル樹脂、ビスフェノール−エポキシビニルエステル樹脂、エラストマー変性ビニルエステル樹脂、エポキシノボラックビニルエステル樹脂および不飽和イソシアヌレートビニルエステル樹脂からなる群から選択される１つ以上の樹脂である、項目４に記載の組成物。
（項目１１）前記共重合可能物質が、スチレン、α−メチルスチレン、クロロスチレン、ビニルトルエン、ジビニルベンゼン、ジアリルフタレート、およびメタクリル酸メチル、およびそれらの混合物からなる群から選択される１種またはそれ以上の単量体である、項目１０に記載の組成物。
（項目１２）前記共重合可能物質が、スチレンおよびメタクリル酸メチルからなる群から選択される１種またはそれ以上の単量体である、項目１１に記載の組成物。
（項目１３）前記開始剤が遊離ラジカル開始剤である、項目１２に記載の組成物。
（項目１４）前記開始剤が過酸化物、ヒドロペルオキシド、レドックス系、ジアゾ化合物、過硫酸塩、および過安息香酸塩からなる群より選択され、該系の全重量に基づいて約０．０５重量％〜約５重量％の量で使用される、項目１３に記載の組成物。
（項目１５）カーボンブラックをさらに含む、項目１４に記載の組成物。
（項目１６）強化充填剤をさらに含む、項目１４に記載の組成物。
（項目１７）以下を含有する電気化学セル流動フィールドプレート：
成形熱硬化性樹脂組成物であって、該成形樹脂組成物は、約０．０５０〜約０．２００インチの厚さおよび少なくとも５５Ｓ／ｃｍのバルク導電率を有し、該成形樹脂組成物は、少なくとも、以下の反応生成物である：
ａ）不飽和プレポリマー樹脂であって、該プレポリマー樹脂は、不飽和ポリエステルおよびビニルエステル樹脂のうちの１種またはそれ以上を含有する；
ｂ）該樹脂と共重合可能な不飽和物質であって、該不飽和物質は、末端エチレン基を含有する；
ｃ）該組成物の全重量の少なくとも５０％を占める導電性充填剤；
ｄ）開始剤であって、該開始剤は、該共重合を開始する；ならびに
ｅ）有効量のレオロジー改質剤であって、該レオロジー改質剤は、成形中において、該樹脂と該導電性充填剤との間の相分離を防止し、該レオロジー改質剤は、第ＩＩ族の酸化物および水酸化物、カルボジアミド、アジリジン、ポリイソシアネート、ポリテトラフルオロエチレン、パーフルオロポリエーテル、ポリエチレン、粘土およびヒュームドシリカからなる群から選択される１種またはそれ以上の組成物である、
電気化学セル流動フィールドプレート。
（項目１８）前記レオロジー改質剤の有効量が該系の全重量の約０．５％〜１５％である、項目１７に記載の電気化学セル流動フィールドプレート。
（項目１９）前記導電性充填剤は、粒子状充填剤または薄片状充填剤であり、該導電性充填剤の量は、少なくとも６０重量％である、項目１８に記載の電気化学セル流動フィールドプレート。
（項目２０）前記導電性充填剤が、グラファイト充填剤であり、該導電性充填剤の量が少なくとも６５重量％である、項目１９に記載の電気化学セル流動フィールドプレート。
（項目２１）前記レオロジー改質剤が酸化マグネシウムおよび／または酸化カルシウムを含み、前記有効量が該組成物の重量に基づいて約０．１〜約２重量％である、項目１７に記載の電気化学セル流動フィールドプレート。
（項目２２）前記レオロジー改質剤がアジリジンおよびポリイソシアネートのうちの１つ以上であり、前記有効量が該組成物の重量に基づいて約１〜約１０重量％である、項目１７に記載の電気化学セル流動フィールドプレート。
（項目２３）前記レオロジー改質剤の有効量が約４００ｐｓｉ〜約５０００ｐｓｉの圧力で約０．０５０インチ〜約０．２００インチの厚さに成形される部品の破壊を妨げるのに有効な量である、項目１７に記載の電気化学セル流動フィールドプレート。
（項目２４）前記改質剤が、ポリテトラフルオロエチレン、パーフルオロポリエーテルのうちの１つ以上を含み、前記有効量が該成形組成物の重量に基づいて約０．１重量％〜約５重量％である、項目１７に記載の電気化学セル流動フィールドプレート。
（項目２５）前記レオロジー改質剤がポリイソシアネートであり、前記有効量が該成形組成物の重量に基づいて約２重量％〜約８重量％である、項目１７に記載の電気化学セル流動フィールドプレート。
（項目２６）前記導電性充填剤が合成結晶性グラファイト粒子であり、前記不飽和プレポリマー樹脂がエポキシビニル樹脂、ビスフェノールフマレート樹脂、変性ビスフェノールフマレートポリエステル樹脂、不飽和ポリエステル樹脂、ウレタン変性ビニルエステル樹脂、ウレタン変性ビニルエステル樹脂、ビスフェノール−エポキシビニルエステル樹脂、エラストマー変性ビニルエステル樹脂、エポキシノボラックビニルエステル樹脂および不飽和イソシアヌレートビニルエステル樹脂からなる群から選択される１つ以上の樹脂である、項目２０に記載の電気化学セル流動フィールドプレート。
（項目２７）前記共重合可能物質が、スチレン、α−メチルスチレン、クロロスチレン、ビニルトルエン、ジビニルベンゼン、ジアリルフタレート、およびメタクリル酸メチル、およびそれらの混合物からなる群から選択される１種またはそれ以上の単量体である、項目２６に記載の電気化学セル流動フィールドプレート。
（項目２８）前記共重合可能物質が、スチレンおよびメタクリル酸メチルからなる群から選択される１種またはそれ以上の単量体である、項目２７に記載の電気化学セル流動フィールドプレート。
（項目２９）前記開始剤が遊離ラジカル開始剤である、項目２８に記載の電気化学セル流動フィールドプレート。
（項目３０）前記開始剤が過酸化物、ヒドロペルオキシド、レドックス系、ジアゾ化合物、過硫酸塩、および過安息香酸塩からなる群より選択され、該系の全重量に基づいて約０．０５重量％〜約５重量％の量で使用される、項目２９に記載の電気化学セル流動フィールドプレート。
（項目３１）カーボンブラックをさらに含む、項目３０に記載の電気化学セル流動フィールドプレート。
（項目３２）強化充填剤をさらに含む、項目３０に記載の電気化学セル流動フィールドプレート。
（項目３３）以下のａ）、ｂ）、ｃ）、ｄ）およびｅ）を含有する、導電性成形組成物：
ａ）１００部の不飽和プレポリマー樹脂であって、該不飽和プレポリマー樹脂は、不飽和ポリエステルおよびビニルエステル樹脂の１種またはそれ以上を含有する；
ｂ）不飽和単量体であって、該不飽和単量体は、スチレン、α−メチルスチレン、クロロスチレン、ビニルトルエン、ジビニルベンゼン、ジアリルフタレート、およびメタクリル酸メチル、およびそれらの混合物からなる群から選択される；ここで、該単量体と該不飽和プレポリマー樹脂との比は、該ａ）およびｂ）の重量基準で、約４０：６０〜約７２：２５である；
ｃ）少なくとも約２２５ｐｈｒの導電性充填剤であって、該組成物から製造した成形生成物は、ＡＳＴＭＴｅｓｔＮｏ．Ｆ１５２９−９７に従って測定したとき、少なくとも約５５Ｓ／ｃｍのバルク導電率を有する；
ｄ）約０．５〜約４．０ｐｈｒの開始剤であって、該開始剤は、該共重合を開始する；ならびに
ｅ）約０．５〜約２０ｐｈｒのレオロジー改質剤であって、該レオロジー改質剤は、第ＩＩ族の酸化物および水酸化物、カルボジアミド、アジリジン、ポリイソシアネート、ポリテトラフルオロエチレン、パーフルオロポリエーテル、ポリエチレン、粘土およびヒュームドシリカおよびそれらの混合物からなる群から選択される１種またはそれ以上の組成物である、
導電性成形組成物。
（項目３４）前記プレポリマー樹脂が、エポキシビニル樹脂、ビスフェノールフマレート樹脂、変性ビスフェノールフマレートポリエステル樹脂、不飽和ポリエステル樹脂、ウレタン変性ビニルエステル樹脂、ウレタン変性ビニルエステル樹脂、ビスフェノール−エポキシビニルエステル樹脂、エラストマー変性ビニルエステル樹脂、エポキシノボラックビニルエステル樹脂および不飽和イソシアヌレートビニルエステル樹脂からなる群から選択される、項目３３に記載の導電性成形組成物。
（項目３５）前記導電性充填剤は、粒子状充填剤または薄片状充填剤であり、該導電性充填剤の量は、少なくとも２５０ｐｈｒである、項目３４に記載の導電性成形組成物。
（項目３６）前記導電性充填剤が、グラファイト充填剤であり、該導電性充填剤の量が少なくとも２７５ｐｈｒである、項目３５に記載の導電性成形組成物。
（項目３７）前記レオロジー改質剤が酸化マグネシウムおよび／または酸化カルシウムを含み、前記有効量が約０．５ｐｈｒ〜約２０ｐｈｒである、項目３３に記載の導電性成形組成物。
（項目３８）前記レオロジー改質剤がアジリジン、カルボジアミド、およびポリイソシアネートのうちの１つ以上であり、前記有効量が０．５ｐｈｒ〜２０ｐｈｒである、項目３３に記載の導電性成形組成物。
（項目３９）前記改質剤が、ポリテトラフルオロエチレン、パーフルオロポリエーテルのうちの１つ以上を含み、前記有効量が約０．５ｐｈｒ〜約２０ｐｈｒである、項目３３に記載の導電性成形組成物。
（項目４０）前記レオロジー改質剤がポリイソシアネートであり、前記有効量が約０．５ｐｈｒ〜約２０ｐｈｒである、項目３３に記載の導電性成形組成物。
（項目４１）前記共重合可能物質が、スチレンおよびメタクリル酸メチルからなる群から選択される１種またはそれ以上の単量体である、項目３３に記載の導電性成形組成物。
（項目４２）前記開始剤が過酸化物、ヒドロペルオキシド、レドックス系、ジアゾ化合物、過硫酸塩、および過安息香酸塩からなる群より選択され、約０．０５ｐｈｒ〜約２０ｐｈｒの量で使用される、項目３３に記載の導電性成形組成物。
（項目４３）カーボンブラックをさらに含む、項目４２に記載の導電性成形組成物。
（項目４４）強化充填剤をさらに含む、項目４３に記載の導電性成形組成物。
（項目４５）以下のａ）、ｂ）、ｃ）、ｄ）およびｅ）の硬化反応生成物を含む導電性成形品：
ａ）１００部の不飽和プレポリマー樹脂であって、該不飽和プレポリマー樹脂は、不飽和ポリエステルおよびビニルエステル樹脂の１種またはそれ以上を含有する；
ｂ）不飽和単量体であって、該不飽和単量体は、スチレン、α−メチルスチレン、クロロスチレン、ビニルトルエン、ジビニルベンゼン、ジアリルフタレート、およびメタクリル酸メチル、およびそれらの混合物からなる群から選択される；ここで、該単量体と該不飽和プレポリマー樹脂との比は、該ａ）およびｂ）の重量基準で、約４０：６０〜約７２：２５である；
ｃ）少なくとも約２２５ｐｈｒの導電性充填剤であって、該組成物から製造した成形生成物は、ＡＳＴＭＴｅｓｔＮｏ．Ｆ１５２９−９７に従って測定したとき、少なくとも約５５Ｓ／ｃｍのバルク導電率を有する；
ｄ）約０．５〜約４．０ｐｈｒの開始剤であって、該開始剤は、該共重合を開始する；ならびに
ｅ）約０．５〜約２０ｐｈｒのレオロジー改質剤であって、該レオロジー改質剤は、第ＩＩ族の酸化物および水酸化物、カルボジアミド、アジリジン、ポリイソシアネート、ポリテトラフルオロエチレン、パーフルオロポリエーテル、ポリエチレン、粘土およびヒュームドシリカおよびそれらの混合物からなる群から選択される１種またはそれ以上の組成物である、
導電性成形品。
（項目４６）前記開始剤が過酸化物、ヒドロペルオキシド、レドックス系、ジアゾ化合物、過硫酸塩、および過安息香酸塩からなる群より選択され、約０．５ｐｈｒ〜約４ｐｈｒの量で使用される、項目４５に記載の導電性成形品。
（項目４７）カーボンブラックをさらに含む、項目４６に記載の導電性成形品。
（項目４８）強化充填剤をさらに含む、項目４６に記載の導電性成形品。
（項目４９）前記不飽和プレポリマー樹脂がエポキシビニル樹脂、ビスフェノールフマレート樹脂、変性ビスフェノールフマレートポリエステル樹脂、不飽和ポリエステル樹脂、ウレタン変性ビニルエステル樹脂、ウレタン変性ビニルエステル樹脂、ビスフェノール−エポキシビニルエステル樹脂、エラストマー変性ビニルエステル樹脂、エポキシノボラックビニルエステル樹脂および不飽和イソシアヌレートビニルエステル樹脂からなる群から選択される１つ以上の樹脂である、項目４５に記載の導電性成形品。
（項目５０）以下ａ）〜ｄ）
ａ）不飽和プレポリマー樹脂であって、該プレポリマー樹脂は、１種またはそれ以上の不飽和ポリエステルおよびビニルエステル樹脂を含有する；
ｂ）該樹脂と共重合可能な不飽和物質であって、該不飽和物質は、末端エチレン基を含有する；
ｃ）該組成物の全重量の少なくとも５０％を占める導電性充填剤；
ｄ）開始剤であって、該開始剤は、該共重合を開始する、
を含む組成物の反応生成物である高充填ポリマーを成形する方法であって、
該方法が、第ＩＩ族の酸化物および水酸化物、カルボジアミド、アジリジン、ポリイソシアネート、ポリテトラフルオロエチレン（ＰＴＦＥ）、パーフルオロポリエーテル（ＰＥＰＥ）、ポリエチレン、粘土およびヒュームドシリカからなる群から選択されるレオロジー剤の硬化の前に添加する工程；および続いて、該組成物を、硬化を開始する熱及び圧力下で成形し、該製品を形成する工程を包含する、方法。
（項目５１）前記成形が、圧縮成形または射出成形のいずれかである、項目５０に記載の方法。 The aforementioned improvements in specimens molded from these compositions allow for low cost mass production of bipolar plates as an additional embodiment of the present invention. These can be used not only for fixed power devices but also for portable fuel cells.
For example, the present invention provides the following.
(Item 1) A composition comprising:
a) an unsaturated prepolymer resin, the prepolymer resin containing one or more of unsaturated polyester and vinyl ester resins;
b) an unsaturated material copolymerizable with the resin, the unsaturated material containing terminal ethylene groups;
c) a conductive filler comprising at least 50% of the total weight of the composition;
d) an initiator that initiates the copolymerization; and
e) an effective amount of a rheology modifier, wherein the rheology modifier prevents phase separation between the resin and the conductive filler during molding; One or more compositions selected from the group consisting of Group II oxides and hydroxides, carbodiamides, aziridines, polyisocyanates, polytetrafluoroethylenes, perfluoropolyethers, polyethylenes, clays and fumed silicas. Is,
A composition comprising:
2. The composition of claim 1, wherein the effective amount of the rheology modifier is from about 0.5% to about 15% of the total weight of the system.
(Item 3) The composition according to item 2, wherein the conductive filler is a particulate filler or a flaky filler, and the amount of the conductive filler is at least 60% by weight.
(Item 4) The composition according to item 3, wherein the conductive filler is a graphite filler, and the amount of the conductive filler is at least 65% by weight.
5. The composition of claim 1, wherein the rheology modifier comprises magnesium oxide and / or calcium oxide and the effective amount is from about 0.1 to about 2% by weight based on the weight of the composition. object.
6. The rheology modifier is one or more of aziridine, carbodiamide, and polyisocyanate, and the effective amount is from about 1% to about 10% by weight based on the weight of the composition. The composition according to Item 1.
7. An effective amount of the rheology modifier is an amount effective to prevent failure of a part molded to a thickness of about 0.050 inch to about 0.200 inch at a pressure of about 400 psi to about 2000 psi. The composition according to item 1, wherein:
(Item 8) The modifier comprises one or more of polytetrafluoroethylene, perfluoropolyether, and the effective amount is from about 0.1 wt% to about 5 based on the weight of the molding composition. Item 2. The composition according to Item 1, wherein the composition is% by weight.
9. The composition of claim 1, wherein the rheology modifier is a polyisocyanate and the effective amount is from about 2% to about 8% by weight based on the weight of the molding composition.
(Item 10) The conductive filler is synthetic crystalline graphite particles, and the unsaturated prepolymer resin is epoxy vinyl resin, bisphenol fumarate resin, modified bisphenol fumarate polyester resin, unsaturated polyester resin, urethane modified vinyl ester. Item, which is one or more resins selected from the group consisting of resins, urethane-modified vinyl ester resins, bisphenol-epoxy vinyl ester resins, elastomer-modified vinyl ester resins, epoxy novolac vinyl ester resins and unsaturated isocyanurate vinyl ester resins 5. The composition according to 4.
(Item 11) The copolymerizable material is one or more selected from the group consisting of styrene, α-methylstyrene, chlorostyrene, vinyltoluene, divinylbenzene, diallyl phthalate, and methyl methacrylate, and mixtures thereof. Item 11. The composition according to Item 10, which is the above monomer.
(Item 12) The composition according to item 11, wherein the copolymerizable substance is one or more monomers selected from the group consisting of styrene and methyl methacrylate.
(Item 13) The composition of item 12 whose said initiator is a free radical initiator.
14. The initiator is selected from the group consisting of peroxides, hydroperoxides, redox systems, diazo compounds, persulfates, and perbenzoates, and about 0.05 weight based on the total weight of the system. 14. A composition according to item 13, which is used in an amount of from about 5% to about 5% by weight.
(Item 15) The composition according to item 14, further comprising carbon black.
(Item 16) The composition according to item 14, further comprising a reinforcing filler.
(Item 17) Electrochemical cell flow field plate containing:
A molded thermosetting resin composition, wherein the molded resin composition has a thickness of about 0.050 to about 0.200 inches and a bulk conductivity of at least 55 S / cm, the molded resin composition comprising: At least the following reaction products:
a) an unsaturated prepolymer resin, the prepolymer resin containing one or more of unsaturated polyester and vinyl ester resins;
b) an unsaturated material copolymerizable with the resin, the unsaturated material containing terminal ethylene groups;
c) a conductive filler comprising at least 50% of the total weight of the composition;
d) an initiator that initiates the copolymerization; and
e) an effective amount of a rheology modifier, wherein the rheology modifier prevents phase separation between the resin and the conductive filler during molding; One or more compositions selected from the group consisting of Group II oxides and hydroxides, carbodiamides, aziridines, polyisocyanates, polytetrafluoroethylenes, perfluoropolyethers, polyethylenes, clays and fumed silicas. Is,
Electrochemical cell flow field plate.
18. The electrochemical cell flow field plate of claim 17, wherein an effective amount of the rheology modifier is about 0.5% to 15% of the total weight of the system.
(Item 19) The electrochemical cell flow field plate according to item 18, wherein the conductive filler is a particulate filler or a flaky filler, and the amount of the conductive filler is at least 60 wt%. .
(Item 20) The electrochemical cell flow field plate according to item 19, wherein the conductive filler is a graphite filler, and the amount of the conductive filler is at least 65 wt%.
21. The electricity of claim 17, wherein the rheology modifier comprises magnesium oxide and / or calcium oxide and the effective amount is from about 0.1 to about 2% by weight based on the weight of the composition. Chemical cell flow field plate.
22. The rheology modifier is one or more of aziridine and polyisocyanate, and the effective amount is from about 1 to about 10% by weight based on the weight of the composition. Electrochemical cell flow field plate.
23. An effective amount of the rheology modifier is an amount effective to prevent failure of a part molded to a thickness of about 0.050 inch to about 0.200 inch at a pressure of about 400 psi to about 5000 psi. Item 18. The electrochemical cell flow field plate according to Item 17.
24. The modifier comprises one or more of polytetrafluoroethylene, perfluoropolyether, and the effective amount is from about 0.1 wt% to about 5 based on the weight of the molding composition. Item 18. The electrochemical cell flow field plate of item 17, wherein the field cell plate is weight percent.
25. The electrochemical cell flow field of claim 17, wherein the rheology modifier is a polyisocyanate and the effective amount is from about 2% to about 8% by weight based on the weight of the molding composition. plate.
(Item 26) The conductive filler is synthetic crystalline graphite particles, and the unsaturated prepolymer resin is epoxy vinyl resin, bisphenol fumarate resin, modified bisphenol fumarate polyester resin, unsaturated polyester resin, urethane modified vinyl ester. Item, which is one or more resins selected from the group consisting of resins, urethane-modified vinyl ester resins, bisphenol-epoxy vinyl ester resins, elastomer-modified vinyl ester resins, epoxy novolac vinyl ester resins and unsaturated isocyanurate vinyl ester resins 21. Electrochemical cell flow field plate according to 20.
(Item 27) The copolymerizable substance is one or more selected from the group consisting of styrene, α-methylstyrene, chlorostyrene, vinyltoluene, divinylbenzene, diallyl phthalate, and methyl methacrylate, and mixtures thereof. 27. The electrochemical cell flow field plate according to item 26, which is the above monomer.
28. The electrochemical cell flow field plate according to claim 27, wherein the copolymerizable material is one or more monomers selected from the group consisting of styrene and methyl methacrylate.
29. The electrochemical cell flow field plate of claim 28, wherein the initiator is a free radical initiator.
30. The initiator is selected from the group consisting of peroxides, hydroperoxides, redox systems, diazo compounds, persulfates, and perbenzoates, and about 0.05 weight based on the total weight of the system 30. The electrochemical cell flow field plate of item 29, used in an amount of from about 5% to about 5% by weight.
(Item 31) The electrochemical cell flow field plate according to item 30, further comprising carbon black.
32. The electrochemical cell flow field plate of claim 30, further comprising a reinforcing filler.
(Item 33) A conductive molding composition containing the following a), b), c), d) and e):
a) 100 parts of an unsaturated prepolymer resin, the unsaturated prepolymer resin containing one or more of unsaturated polyester and vinyl ester resins;
b) an unsaturated monomer, the unsaturated monomer comprising styrene, α-methyl styrene, chlorostyrene, vinyl toluene, divinyl benzene, diallyl phthalate, and methyl methacrylate, and mixtures thereof; Wherein the ratio of the monomer to the unsaturated prepolymer resin is from about 40:60 to about 72:25, based on the weight of the a) and b);
c) At least about 225 phr of conductive filler, and the molded product made from the composition is ASTM Test No. Has a bulk conductivity of at least about 55 S / cm when measured according to F1529-97;
d) about 0.5 to about 4.0 phr of initiator, which initiates the copolymerization; and
e) from about 0.5 to about 20 phr of a rheology modifier comprising a Group II oxide and hydroxide, carbodiamide, aziridine, polyisocyanate, polytetrafluoroethylene, One or more compositions selected from the group consisting of fluoropolyethers, polyethylenes, clays and fumed silicas and mixtures thereof;
Conductive molding composition.
(Item 34) The prepolymer resin is an epoxy vinyl resin, bisphenol fumarate resin, modified bisphenol fumarate polyester resin, unsaturated polyester resin, urethane modified vinyl ester resin, urethane modified vinyl ester resin, bisphenol-epoxy vinyl ester resin, Item 34. The conductive molding composition according to Item 33, selected from the group consisting of an elastomer-modified vinyl ester resin, an epoxy novolac vinyl ester resin, and an unsaturated isocyanurate vinyl ester resin.
(Item 35) The conductive molding composition according to item 34, wherein the conductive filler is a particulate filler or a flaky filler, and the amount of the conductive filler is at least 250 phr.
(Item 36) The conductive molding composition according to item 35, wherein the conductive filler is a graphite filler, and the amount of the conductive filler is at least 275 phr.
(Item 37) The conductive molding composition according to item 33, wherein the rheology modifier comprises magnesium oxide and / or calcium oxide, and the effective amount is from about 0.5 phr to about 20 phr.
(Item 38) The conductive molding composition according to item 33, wherein the rheology modifier is one or more of aziridine, carbodiamide, and polyisocyanate, and the effective amount is 0.5 phr to 20 phr.
39. The conductive molding of claim 33, wherein the modifier comprises one or more of polytetrafluoroethylene, perfluoropolyether, and the effective amount is from about 0.5 phr to about 20 phr. Composition.
40. The conductive molding composition of claim 33, wherein the rheology modifier is a polyisocyanate and the effective amount is from about 0.5 phr to about 20 phr.
(Item 41) The conductive molding composition according to item 33, wherein the copolymerizable substance is one or more monomers selected from the group consisting of styrene and methyl methacrylate.
42. The initiator is selected from the group consisting of peroxides, hydroperoxides, redox systems, diazo compounds, persulfates, and perbenzoates and is used in an amount of about 0.05 phr to about 20 phr. 34. The conductive molding composition according to item 33.
(Item 43) The conductive molding composition according to Item 42, further comprising carbon black.
(Item 44) The electroconductive molding composition according to item 43, further comprising a reinforcing filler.
(Item 45) An electroconductive molded article containing the curing reaction products of a), b), c), d) and e) below:
a) 100 parts of an unsaturated prepolymer resin, the unsaturated prepolymer resin containing one or more of unsaturated polyester and vinyl ester resins;
b) an unsaturated monomer, the unsaturated monomer comprising styrene, α-methyl styrene, chlorostyrene, vinyl toluene, divinyl benzene, diallyl phthalate, and methyl methacrylate, and mixtures thereof; Wherein the ratio of the monomer to the unsaturated prepolymer resin is from about 40:60 to about 72:25, based on the weight of the a) and b);
c) At least about 225 phr of conductive filler, and the molded product made from the composition is ASTM Test No. Has a bulk conductivity of at least about 55 S / cm when measured according to F1529-97;
d) about 0.5 to about 4.0 phr of initiator, which initiates the copolymerization; and
e) from about 0.5 to about 20 phr of a rheology modifier comprising a Group II oxide and hydroxide, carbodiamide, aziridine, polyisocyanate, polytetrafluoroethylene, One or more compositions selected from the group consisting of fluoropolyethers, polyethylenes, clays and fumed silicas and mixtures thereof;
Conductive molded product.
46. The initiator is selected from the group consisting of peroxides, hydroperoxides, redox systems, diazo compounds, persulfates, and perbenzoates and is used in an amount of about 0.5 phr to about 4 phr. 46. The conductive molded article according to item 45.
(Item 47) The conductive molded article according to item 46, further comprising carbon black.
(Item 48) The conductive molded article according to item 46, further comprising a reinforcing filler.
(Item 49) The unsaturated prepolymer resin is epoxy vinyl resin, bisphenol fumarate resin, modified bisphenol fumarate polyester resin, unsaturated polyester resin, urethane modified vinyl ester resin, urethane modified vinyl ester resin, bisphenol-epoxy vinyl ester resin. Item 46. The conductive molded article according to Item 45, which is one or more resins selected from the group consisting of an elastomer-modified vinyl ester resin, an epoxy novolac vinyl ester resin, and an unsaturated isocyanurate vinyl ester resin.
(Item 50) The following a) to d)
a) an unsaturated prepolymer resin, the prepolymer resin containing one or more unsaturated polyester and vinyl ester resins;
b) an unsaturated material copolymerizable with the resin, the unsaturated material containing terminal ethylene groups;
c) a conductive filler comprising at least 50% of the total weight of the composition;
d) an initiator that initiates the copolymerization;
A method of molding a highly filled polymer that is a reaction product of a composition comprising:
The method is from the group consisting of Group II oxides and hydroxides, carbodiamides, aziridines, polyisocyanates, polytetrafluoroethylene (PTFE), perfluoropolyether (PEPE), polyethylene, clays and fumed silica. Adding the selected rheological agent prior to curing; and subsequently molding the composition under heat and pressure to initiate curing to form the product.
(Item 51) A method according to item 50, wherein the molding is either compression molding or injection molding.

図１は、双極電池プレートを利用する燃料電池アセンブリの図示である。FIG. 1 is an illustration of a fuel cell assembly utilizing bipolar cell plates. 図２は、本発明に従って製造できる双極燃料電池プレートの図示である。FIG. 2 is an illustration of a bipolar fuel cell plate that can be manufactured in accordance with the present invention.

（発明の詳細な説明）
本発明は、導電性成形組成物での改良に関する。特に、これらの組成物は、圧縮成形プロセスおよび射出成形プロセスで使用できる。さらに、これらの組成物により、高濃度の導電性充填剤を有する薄くて複雑な試験片の製造が可能となる。 (Detailed description of the invention)
The present invention relates to improvements in conductive molding compositions. In particular, these compositions can be used in compression molding and injection molding processes. In addition, these compositions allow for the production of thin and complex test strips with a high concentration of conductive filler.

シート成形組成物およびバルク成形組成物は、米国特許第５，９９８，５１０号；第５，３４２，５５４号；第５，８５４，３１７号；第５，７４４，８１６号；および第５，２６８，４００号で記述されている；これらの全ての内容は、当該技術分野で公知の成形組成物の種々の改良に関するそれらの教示について、本明細書中で参考として援用されている。 Sheet molding compositions and bulk molding compositions are described in U.S. Pat. Nos. 5,998,510; 5,342,554; 5,854,317; 5,744,816; and 5,268. All of which are hereby incorporated by reference for their teachings on various modifications of molding compositions known in the art.

成形樹脂組成物の１成分には、架橋可能プレポリマー（例えば、不飽和ポリエステル樹脂またはビニルエステル樹脂）がある。望ましくは、このプレポリマーは、比較的に低い分子量（例えば、約２００〜約５０００（重量平均））を有する。それらは、上記特許（その内容は、本明細書中で参考として援用されている）の実施例で、詳細に記述されている。これらのポリエステル樹脂は、不飽和多塩基酸および／または無水物とポリオール（例えば、ジヒドロキシまたはトリヒドロキシ化合物）との縮合から誘導された縮合生成物である。望ましくは、これらのポリエステル樹脂は、二酸または二酸無水物（これは、一般に、約３個〜約１２個の炭素原子、さらに好ましくは、約４個〜約８個の炭素原子を有する）とポリオールまたは環状エーテル（これは、約２個〜約１２個の炭素原子、さらに好ましくは、約２個〜約６個の炭素原子を有する）とのエステル化反応生成物である。 One component of the molded resin composition is a crosslinkable prepolymer (eg, an unsaturated polyester resin or vinyl ester resin). Desirably, the prepolymer has a relatively low molecular weight (eg, from about 200 to about 5000 (weight average)). They are described in detail in the examples of the above patent, the contents of which are incorporated herein by reference. These polyester resins are condensation products derived from the condensation of unsaturated polybasic acids and / or anhydrides with polyols (eg, dihydroxy or trihydroxy compounds). Desirably, these polyester resins are diacids or dianhydrides (which generally have from about 3 to about 12 carbon atoms, more preferably from about 4 to about 8 carbon atoms). Is an esterification reaction product of a polyol or a cyclic ether, which has from about 2 to about 12 carbon atoms, more preferably from about 2 to about 6 carbon atoms.

一般に、使用できるビニルエステル樹脂は、エポキシ樹脂と一官能性エチレン性不飽和カルボン酸との反応生成物である。さらに具体的には、これらのビニルエステル樹脂は、エポキシ末端オリゴマー（例えば、エポキシ官能化ビスフェノールＡ）とアクリル酸またはメタクリル酸との反応生成物であり、このオリゴマー上でアクリル末端基を形成する。これらのビニルエステルは、大部分は、末端不飽和を有するのに対して、これらの不飽和ポリエステルは、大部分は、内部不飽和を有する。 Generally, the vinyl ester resin that can be used is the reaction product of an epoxy resin and a monofunctional ethylenically unsaturated carboxylic acid. More specifically, these vinyl ester resins are the reaction product of an epoxy-terminated oligomer (eg, epoxy-functionalized bisphenol A) and acrylic acid or methacrylic acid that forms acrylic end groups on the oligomer. Most of these vinyl esters have terminal unsaturation, whereas these unsaturated polyesters have mostly internal unsaturation.

この成形組成物の別の成分は、この樹脂と共重合可能な１種またはそれ以上の不飽和単量体である。望ましくは、この成分は、室温で、この樹脂成分を溶解できる。それゆえ、１実施態様では、この樹脂は、残りの成分と配合する前に、この単量体成分に溶解される。適当な単量体の例には、スチレン、α−メチルスチレン、クロロスチレン、ビニルトルエン、ジビニルベンゼン、ジアリルフタレート、メタクリル酸メチル、およびこれらの混合物があり、好ましい単量体は、スチレンおよびメタクリル酸メチルである。単量体と樹脂との比は、重量基準で、望ましくは、約４０：６０〜約７５：２５、好ましくは、約４０：６０〜約６５：３５である。 Another component of the molding composition is one or more unsaturated monomers copolymerizable with the resin. Desirably, this component can dissolve the resin component at room temperature. Thus, in one embodiment, the resin is dissolved in the monomer component prior to blending with the remaining components. Examples of suitable monomers include styrene, α-methyl styrene, chlorostyrene, vinyl toluene, divinyl benzene, diallyl phthalate, methyl methacrylate, and mixtures thereof, with preferred monomers being styrene and methacrylic acid. Methyl. The ratio of monomer to resin is desirably about 40:60 to about 75:25, preferably about 40:60 to about 65:35, on a weight basis.

この成形組成物の別の成分は、充填剤である。本発明によれば、その主な充填剤は、最終成形品のに導電性を与えるための導電性充填剤である。好ましい充填剤は、グラファイト粒子、特に、合成結晶性グラファイト粒子（例えば、現在、Ａｓｂｕｒｙ，ＮｅｗＪｅｒｓｅｙのＡｓｂｕｒｙＧｒａｐｈｉｔｅにより、Ａｓｂｕｒｙ４０１２の名称で調達したもの）である。このグラファイトは、直径１５０ミクロンより大きい粒子を１０％未満で有し、直径４４ミクロンより小さい粒子を１０％未満で有することにより、特徴付けられる。他のグラファイト充填剤には、以下が挙げられる：ＡｓｈｂｕｒｙＡ９９、Ａｓｈｂｕｒｙ
３２４３、Ａｓｈｂｕｒｙ変性４０１２、Ａｓｈｂｕｒｙ３２８５、Ａｓｈｂｕｒｙ２３０Ｕ；ＴｉｍｒｅｘＲＫＳ７５および１５０、ＴｉｍｒｅｘＲＫＣ４４（全て、ＷｅｓｔｌａｋｅのＴＩＭＣＡＬにより販売されている）、Ｏｈｉｏ；およびＣａｌｇｒａｐｈ（これは、Ｖａｌｅｎｃｉａ，ＣａｌｉｆｏｒｎｉａのＳＧＬＴｅｃｈｎｉｃＩｎｃから販売されている）。この充填剤は、少なくとも５０重量％の装填量で使用される。他の導電性充填剤（例えば、他の型のグラファイト（グラファイトピッチベースの繊維を含めて）、金属粒子、または金属被覆粒子）は、グラファイト充填剤と共に、または単独でさえ、使用され得る。望ましくは、導電性充填剤は、この成形組成物の少なくとも約５０重量％、約６０重量％、または約６５重量％である。さらに望ましくは、この充填剤は、この成形組成物の約７０〜７１重量％または約７８重量％よりも多い。あるいは、この量は、少なくとも約２５０ｐｈｒ、さらに好ましくは、少なくとも約２７５ｐｈｒ、または３００ｐｈｒでさえ、表わすことができる。あるいは、これらの導電性充填剤は、約０．０６０〜約０．２００インチの厚さを有する成形品について、ＡＳＴＭＴｅｓｔＳｔａｎｄａｒｄＮｏ．Ｆ１５２９−９７に従って測定したとき、少なくとも約４０、約５０、約６０、約７０、約８０、約８５、約９０または約９６Ｓ／ｃｍのバルク導電率を生じる有効量で、存在する。燃料電池プレートにおける現在の技術は、少なくとも約５５、好ましくは、少なくとも約７０のバルク導電率を使用する。 Another component of the molding composition is a filler. According to the present invention, the main filler is a conductive filler for imparting conductivity to the final molded product. Preferred fillers are graphite particles, especially synthetic crystalline graphite particles (for example, those currently procured under the name Asbury 4012 by Asbury Graphite, Asbury, New Jersey). The graphite is characterized by having less than 10% particles larger than 150 microns in diameter and less than 10% particles smaller than 44 microns in diameter. Other graphite fillers include: Ashbury A99, Ashbury
3243, Ashbury modified 4012, Ashbury 3285, Ashbury 230U; TimrexR KS 75 and 150, TimrexR KC 44 (all sold by Westlake's TIMCAL), Ohio; and Calgraph SG Sold). This filler is used at a loading of at least 50% by weight. Other conductive fillers (eg, other types of graphite (including graphite pitch-based fibers), metal particles, or metal-coated particles) can be used with or even alone with the graphite filler. Desirably, the conductive filler is at least about 50%, about 60%, or about 65% by weight of the molding composition. More desirably, the filler is greater than about 70-71% or about 78% by weight of the molding composition. Alternatively, this amount can represent at least about 250 phr, more preferably at least about 275 phr, or even 300 phr. Alternatively, these conductive fillers are available from ASTM Test Standard No. for molded articles having a thickness of about 0.060 to about 0.200 inches. It is present in an effective amount that results in a bulk conductivity of at least about 40, about 50, about 60, about 70, about 80, about 85, about 90 or about 96 S / cm, as measured according to F1529-97. Current technology in fuel cell plates uses a bulk conductivity of at least about 55, preferably at least about 70.

開始剤は、この成形組成物の他の成分である。この開始剤は、この樹脂および単量体の共重合を開始する。開始剤には、成形条件下にて、正しい濃度で、ラジカルを形成できる任意の遊離ラジカル開始剤が挙げられる。それらには、過酸化物、ヒドロペルオキシド、レドックス系、ジアゾ化合物、過硫酸塩、過安息香酸塩などが挙げられ得る。これらの開始剤は、典型的には、約０．０５〜約５重量％の量、さらに好ましくは、約０．１〜約２重量％の量で、使用される。あるいは、これらの量は、樹脂１００重量部あたりの部、すなわち、約０．５〜約４．０ｐｈｒ、好ましくは、約０．７〜約３．０ｐｈｒ、最も好ましくは、約０．８〜約２．２５ｐｈｒで、表わされ得る。あるいは、成形用途には、高温開始剤（例えば、Ｄｉｃｕｐ、例えば、過酸化ジクミル）が使用でき、この場合、さらに高い開始温度が望ましい。 The initiator is another component of this molding composition. The initiator initiates copolymerization of the resin and monomer. Initiators include any free radical initiator capable of forming radicals at the correct concentration under molding conditions. They may include peroxides, hydroperoxides, redox systems, diazo compounds, persulfates, perbenzoates and the like. These initiators are typically used in an amount of about 0.05 to about 5% by weight, more preferably about 0.1 to about 2% by weight. Alternatively, these amounts are in parts per 100 parts by weight resin, i.e. from about 0.5 to about 4.0 phr, preferably from about 0.7 to about 3.0 phr, most preferably from about 0.8 to about It can be expressed at 2.25 phr. Alternatively, high temperature initiators (e.g., Dicup, e.g., dicumyl peroxide) can be used for molding applications, where higher onset temperatures are desirable.

この改良成形組成物の必須成分には、レオロジー改質剤があり、これは、例えば、この樹脂プレポリマーの鎖伸長により、その分子量を大きくするように作用し得る。適当な改質剤には、第ＩＩ族の酸化物および水酸化物（例えば、酸化カルシウムまたはマグネシウム）；カルボジアミド；アジリジン；およびポリイソシアネートが挙げられる。前述の改質剤は、カルボキシ部位またはヒドロキシ部位において、その重合体骨格に共に反応させることにより、化学的に作用すると考えられている。他の適当な改質剤には、ポリテトラフルオロエチレン（ＰＴＦＥ）；パーフルオロポリエーテル（ＰＦＰＥ）、およびポリエチレンが挙げられる。これらの改質剤は、剪断を低くして、それにより、成形中において、この組成物中の流れを促進するように作用し得る。ヒュームドシリカは、物質の一例であり、これは、機械的に作用して、成形粘度を高めるように作用し得、従って、本発明の適当なレオロジー改質剤であり得る。２種またはそれ以上のレオロジー改質剤の組合せは、最適な特性のために、望まれ得る。この用途では、それらは、（特に、この導電性充填剤の高い装填量（すなわち、グラファイトの５０重量％を超え、６５重量％でさえ）を考慮して）、この導電性充填剤からの樹脂の相分離を防止するために、この樹脂構造を変性するように使用される。これらの改質剤は、さらに、一般に、高解像度の導電性重合体燃料電池プレートが完成できるようにするために、使用される。 An essential component of the improved molding composition is a rheology modifier, which can act to increase its molecular weight, for example, by chain extension of the resin prepolymer. Suitable modifiers include Group II oxides and hydroxides (eg, calcium or magnesium oxide); carbodiamides; aziridines; and polyisocyanates. The aforementioned modifiers are believed to act chemically by reacting together with the polymer backbone at the carboxy or hydroxy moiety. Other suitable modifiers include polytetrafluoroethylene (PTFE); perfluoropolyether (PFPE), and polyethylene. These modifiers can act to lower shear and thereby promote flow in the composition during molding. Fumed silica is an example of a material that can act mechanically to increase the molding viscosity and thus can be a suitable rheology modifier of the present invention. A combination of two or more rheology modifiers may be desired for optimal properties. In this application, they are (especially taking into account the high loading of the conductive filler (ie more than 50% and even 65% by weight of the graphite)) resin from the conductive filler. It is used to modify this resin structure in order to prevent phase separation. These modifiers are also generally used to allow high resolution conducting polymer fuel cell plates to be completed.

望ましくは、これらのレオロジー改質剤は、成形中の相分離を防止する有効量で、使用される。この用途の目的のために、成形は、望ましくは、約４００〜約５０００ｐｓｉ、好ましくは、約２０００〜約３５００ｐｓｉ、最も好ましくは、約２５００〜約３０００ｐｓｉの圧力でなされる。第ＩＩ族酸化物（第ＩＩ族水酸化物およびこれらの化合物の混合物を含めて）の望ましい量は、約０．１〜約１または約２重量％、さらに望ましくは、約０．２または約０．３〜約０．７または約０．８重量％である。これはまた、約０．５〜約４．０ｐｈｒ、好ましくは、約１．０〜約３．０ｐｈｒ、最も好ましくは、約１．５〜約２．５ｐｈｒとして、表わすことができる。好ましい具体的な化合物には、酸化マグネシウム、または水酸化マグネシウムまたは酸化カルシウムが挙げられる。適当な酸化マグネシウム添加剤の例には、Ｄａｎｖｅｒ，ＭＡのＭｏｒｔｏｎＴｈｉｏｋｏｌから「Ｅｌａｓｔｏｍａｇ」の商品名で販売されている９９％純粋酸化マグネシウムがある。他の例には、Ｐｌａｓｔｉｃｏｌｏｒｓにより「ｐｇ−９０３３」の商品名で販売されている酸化マグネシウム分散体、および「ｐｇ−９１１４６」の商品名でまたＰｌａｓｔｉｃｏｌｏｒｓにより販売されている水酸化マグネシウム分散体が挙げられる。別の適当な水酸化マグネシウムには、Ｂａｒｃｒｏｆｔがあり、これは、粉末化した型である。アジリジン化合物の例としては、ＸＡＭＡの商品名称でＥＩＴ，Ｉｎｃ．から調達した多官能性アジリジン（ＸＡＭＡ−２（これは、トリメチロールプロパン−トリス（β−（Ｎ−アジリジニル）プロピオネートとして同定されている））、特に、ＸＡＭＡ−７（これは、ペンタエリスリトール−トリス−（β−（アジリジニル）プロピオネート）として同定されている））；ＰＦＡＺ３２２（これは、三官能性アジリジンとして同定されている）を含めたｌｏｎａｃの商品名のＳｙｂｒｏｎＣｈｅｍｉｃａｌｓの製品、ＣＸ−１００を含めたＺｅｎｅｃａＲｅｓｉｎｓの製品（これは、多官能性アジリジンとして同定されている）が挙げられる。アジリジンおよび／またはポリイソシアネート改質剤の望ましい量は、約１〜約１０または約１５重量％であり、さらに望ましくは、約２または約３〜約８または約９重量％である。これはまた、約０．５〜約２０ｐｈｒ、好ましくは、約１〜約１７ｐｈｒ、最も好ましくは、約２〜約１５ｐｈｒとして、表わすことができる。ポリイソシアネートは、一般に、米国特許第５，２６８，４００号、６欄、５９行〜７欄、１７行で、さらに詳細に記述されている。使用できる具体的なジイソシアネートには、ジフェニルメタンジイソシアネート（例えば、「Ｒｕｂｉｎａｔｅ」ＲＭＦ−１７８０の商品名で、ＷｅｓｔＤｅｐｔｆｏｌｄ，ＮｅｗＪｅｒｓｅｙのＩＣＩＡｍｅｒｉｃａｓから販売されているもの）がある。それに加えて、適当なジイソシアネートには、ＬｕｐｒａｎａｔｅＭＰ−１０２（ＢＡＳＦ製の溶媒無しのウレタン変性ジフェニルメタンジイソシアネート）がある。ポリテトラフルオロエチレン（ＰＴＦＥ）（および／またはパーフルオロポリエーテル（ＰＦＰＥ））の所望量は、約０．５〜約１または約２重量％、さらに好ましくは、約０．６または約０．７〜約１．８または約１．３重量％である。これはまた、約０．５〜約２０ｐｈｒ、好ましくは、約３〜約１５ｐｈｒ、最も好ましくは、約５〜約１２ｐｈｒとして、表わすことができる。適当な微粒子ＰＴＦＥ粉末（これは、ＣｏｕｌｔｅｒＣｏｕｎｔｅｒにより、ミクロン未満の平均粒径を有する）は、ＷｅｓｔＣｈｅｓｔｅｒ，ＰｅｎｎｓｙｌｖａｎｉａのＭａｒｓｈａｌｌＰｒｏｄｕｃｔｓＣｏｍｐａｎｙから、「Ｍａｒｚｏｎ＃５」の商品名で販売されている。直鎖状低密度ポリエチレン（例えば、ＦＮ５１０の商品名で、ＨｏｕｓｔｏｎＴｅｘａｓのＥｑｕｉｓｔａｒから販売されているもの）を使用するのが好ましい。それを、約３〜約２０ｐｈｒ、さらに好ましくは、約４〜約１７ｐｈｒ、最も好ましくは、約５〜約１５ｐｈｒの量で使用するのが好ましい。ヒュームドシリカは、約０．５〜約２０ｐｈｒ、好ましくは、約１〜約１０ｐｈｒで使用できる。 Desirably, these rheology modifiers are used in an effective amount that prevents phase separation during molding. For purposes of this application, the molding is desirably done at a pressure of about 400 to about 5000 psi, preferably about 2000 to about 3500 psi, and most preferably about 2500 to about 3000 psi. The desired amount of Group II oxide (including Group II hydroxides and mixtures of these compounds) is about 0.1 to about 1 or about 2% by weight, more preferably about 0.2 or about 0.3 to about 0.7 or about 0.8% by weight. This can also be expressed as about 0.5 to about 4.0 phr, preferably about 1.0 to about 3.0 phr, most preferably about 1.5 to about 2.5 phr. Preferred specific compounds include magnesium oxide, or magnesium hydroxide or calcium oxide. An example of a suitable magnesium oxide additive is 99% pure magnesium oxide sold under the name “Elastomag” by Morton Thiokol of Danver, MA. Other examples include a magnesium oxide dispersion sold under the trade name “pg-9033” by Plasticcolors and a magnesium hydroxide dispersion sold under the trade name “pg-91146” and also by Plasticcolors. It is done. Another suitable magnesium hydroxide is Barcroft, which is a powdered form. Examples of aziridine compounds include EIT, Inc. under the trade name XAMA. Multifunctional aziridines (XAMA-2, which has been identified as trimethylolpropane-tris (identified as β- (N-aziridinyl) propionate)), in particular XAMA-7 (which is pentaerythritol-tris -(Identified as [beta]-(aziridinyl) propionate))); including the product of Symon Chemicals under the trade name of Lonac, including PFAZ322 (which has been identified as a trifunctional aziridine), including CX-100 Zeneca Resins products, which have been identified as multifunctional aziridines. The desired amount of aziridine and / or polyisocyanate modifier is from about 1 to about 10 or about 15% by weight, and more desirably from about 2 or about 3 to about 8 or about 9% by weight. This can also be expressed as about 0.5 to about 20 phr, preferably about 1 to about 17 phr, most preferably about 2 to about 15 phr. Polyisocyanates are generally described in further detail in US Pat. No. 5,268,400, column 6, lines 59-7, line 17. Specific diisocyanates that can be used include diphenylmethane diisocyanate (for example, sold under the trade name “Rubinate” RMF-1780 from ICI Americas, West Deptfold, New Jersey). In addition, a suitable diisocyanate is Lupranate MP-102 (a solvent-free urethane-modified diphenylmethane diisocyanate from BASF). The desired amount of polytetrafluoroethylene (PTFE) (and / or perfluoropolyether (PFPE)) is about 0.5 to about 1 or about 2% by weight, more preferably about 0.6 or about 0.7. To about 1.8 or about 1.3% by weight. This can also be expressed as about 0.5 to about 20 phr, preferably about 3 to about 15 phr, and most preferably about 5 to about 12 phr. Appropriate particulate PTFE powder (this is by Coulter Counter, (With an average particle size of less than a micron) is sold under the trade name “Marzon # 5” by Marshall Products Company of West Chester, Pennsylvania. It is preferred to use linear low density polyethylene (for example, the product name FN510 sold by Equistar of Houston Texas). It is preferred to use it in an amount of about 3 to about 20 phr, more preferably about 4 to about 17 phr, and most preferably about 5 to about 15 phr. Fumed silica can be used at about 0.5 to about 20 phr, preferably about 1 to about 10 phr.

成形組成物への他の任意の成分には、ウレタンベースまたはウレタン含有オリゴマーまたは重合体、ポリ酢酸ビニルまたはポリエチレンのような低収縮添加剤；繊維状強化剤（例えば、綿ガラスマイクロファイバーまたはグラファイトマイクロファイバー）；可撓化剤；離型剤；保存中または成形の初期段階での早期重合を禁止する重合禁止剤；ヒュームドシリカのような粘度調節剤；およびカルシウム、亜鉛またはマグネシウムのステアリン酸塩のような金型潤滑剤が挙げられる。その表面導電性に影響を及ぼし成形品の外観を変えるために、カーボンブラックが添加され得る。適当なカーボンブラックには、２７０ｍ²／ｇの窒素表面積、１４５ｍ²／ｇのＳＴＳＡ表面積、３５メッシュで０ｐｐｍおよび３２５メッシュで２０ｐｐｍのふるい残渣を有する導電性低残渣カーボンブラックが挙げられ、これは、例えば、Ｊａｍｅｓｂｕｒｇ，ＮＪのＣｏｌｕｍｂｉａＣｈｅｍｉｃａｌｓからＣｏｎｄｕｃｔｅｘ９７５の商品名で販売されている。また、適当な導電性カーボンブラックは、ＫｅｔｊｅｎｂｌａｃｋＥＣ−３００ＪおよびＥＣ−６００ＪＤの商品名で、Ｃｈｉｃａｇｏ，ＩｌｌｉｎｏｉｓのＡｋｚｏＮｏｂｅｌＣｈｅｍｉｃａｌｓから調達される。ＢｏｓｔｏｎＭＡのＣａｂｏｔＣｏｒｐｏｒａｔｉｏｎもまた、導電性カーボンブラックを提供している。ポリエチレンおよびヒュームドシリカは、前述の機能に加えて、レオロジー改質剤として機能できることが注目される。 Other optional ingredients to the molding composition include urethane-based or urethane-containing oligomers or polymers, low shrink additives such as polyvinyl acetate or polyethylene; fibrous reinforcing agents (eg cotton glass microfiber or graphite micro Fiber); flexibilizers; mold release agents; polymerization inhibitors that inhibit premature polymerization during storage or in the early stages of molding; viscosity modifiers such as fumed silica; and stearates of calcium, zinc or magnesium And a mold lubricant such as Carbon black can be added to affect the surface conductivity and change the appearance of the molded article. Suitable carbon black, nitrogen surface area of 270m ² / g, STSA surface area of 145m ² / g, include conductive low residue carbon black having a 20ppm sieve residue 0ppm and 325 mesh 35 mesh, which, For example, it is sold under the product name of Conductex 975 from Columbia Chemicals of Jamesburg, NJ. Suitable conductive carbon blacks are also procured from Akzo Nobel Chemicals of Chicago, Illinois under the trade names Ketjenblack EC-300J and EC-600JD. Boston MA's Cabot Corporation also offers conductive carbon black. It is noted that polyethylene and fumed silica can function as rheology modifiers in addition to the functions described above.

これらの成形組成物は、連続法またはバッチ法のいずれかを含めた種々の混合条件を使用して、また、種々の公知の混合設備を使用して、調合され混合され得る。具体的な例は、実施例の項目で述べる。これらの組成物は、有利には、成形前、適当な時間にわたって保存され得る。これらの組成物は、圧縮成形および射出成形を含めた種々の方法により、成形できる。これらの組成物は、これらの種類の成形に典型的な条件（約４００〜約５０００ｐｓｉ、好ましくは、約２０００〜約３５００ｐｓｉ、最も好ましくは、約２５００〜約３０００ｐｓｉの圧力、および約２２５〜約４００°Ｆの温度を含めて）下にて、成形できる。滞留時間は、約７０秒間〜約４分間である。これらの組成物は、薄いまたは複雑な導電性製品を含めた複雑な形状（例えば、約０．０５０〜約０．２００インチ、さらに好ましくは、約０．０６０〜約０．１５０インチの厚さを有するもの）を成形するのに有用である。これらの組成物は、上で示した厚さで、少なくとも４０、５０、６０、７０、８０、８５、９０または９６Ｓ／ｃｍのバルク導電率を有する製品に有用である。この組成物に由来の製品は、望ましくは、ＡＳＴＭ試験Ｎｏ．Ｄ６３８に従って測定した約１５００〜約５０００ｐｓｉの引張り強度およびＡＳＴＭ試験ｎｏ．Ｄ７９０に従って試験したとき、約２５００〜約１０，０００ｐｓｉの曲げ弾性率を有する。 These molding compositions can be formulated and mixed using various mixing conditions, including either continuous or batch processes, and using various known mixing equipment. A specific example will be described in the item of the embodiment. These compositions can advantageously be stored for a suitable time before molding. These compositions can be molded by a variety of methods including compression molding and injection molding. These compositions are prepared under conditions typical for these types of moldings (about 400 to about 5000 psi, preferably about 2000 to about 3500 psi, most preferably about 2500 to about 3000 psi, and about 225 to about 400 (Including temperatures of ° F) The residence time is about 70 seconds to about 4 minutes. These compositions are complex shapes, including thin or complex conductive products (e.g., about 0.050 to about 0.200 inches, more preferably about 0.060 to about 0.150 inches thick). It is useful for molding a material having These compositions are useful for products having a bulk conductivity of at least 40, 50, 60, 70, 80, 85, 90 or 96 S / cm at the thicknesses indicated above. The product derived from this composition is preferably ASTM test no. Tensile strength of about 1500 to about 5000 psi measured according to D638 and ASTM test no. When tested in accordance with D790, it has a flexural modulus of about 2500 to about 10,000 psi.

本発明の組成物から製造した成形品は、複雑な形状、導電性だけでなく強度および腐食耐性が要求される種々の用途に有用である。圧縮成形で製造できる１つの特に有利な製品には、燃料電池で使用する双極プレートがある。このようなプレートの一例は、図１で示されている。このプレートの図面は、本発明の導電性化合物の成形性能を図示することを意図している。それは、必ずしも、最適な、または操作可能なフィールド流動設計を提供する目的ではない。それは、いずれの様式でも、本発明を限定するべきではない。プレート１０は、１個またはそれ以上の略平行および／または蛇行したフローチャンネル１２を備えた流体流れ面を含む。これらのフローチャンネルは、ポート１４および１６（これらは、対応する入口と流体連絡しており、マニホルド１８および１９を出ていく）を通って、流体を受容し移送する。このプレートは、長さおよび幅が１〜２０インチで変わる寸法を有し、０．０２〜０．３インチの厚さを有し、このフローチャンネルの断面深さは、約０．００５〜０．０８０インチの範囲である。隣接フローチャンネル部分を隔てているランドの断面幅は、０．０１〜０．１インチの範囲である。このプレートは、多数の周辺スルーホール２０を含み得、これらは、燃料輸送用のマニホルドとして作用する。 Molded articles produced from the composition of the present invention are useful for various applications that require not only complex shapes and conductivity, but also strength and corrosion resistance. One particularly advantageous product that can be produced by compression molding is a bipolar plate for use in fuel cells. An example of such a plate is shown in FIG. The drawing of this plate is intended to illustrate the molding performance of the conductive compound of the present invention. It is not necessarily the purpose of providing an optimal or operable field flow design. It should not limit the invention in any way. Plate 10 includes a fluid flow surface with one or more generally parallel and / or serpentine flow channels 12. These flow channels receive and transfer fluid through ports 14 and 16 (which are in fluid communication with corresponding inlets and exit manifolds 18 and 19). The plate has dimensions that vary in length and width from 1 to 20 inches, has a thickness of 0.02 to 0.3 inches, and the cross-sectional depth of the flow channel is about 0.005 to 0. .080 inch range. The land cross-sectional width separating adjacent flow channel portions is in the range of 0.01 to 0.1 inches. The plate may include a number of peripheral through holes 20, which act as a manifold for fuel transport.

図２は、燃料電池の未組み立て部品を図示している。この燃料電池は、ベースユニット１２（これは、改質装置１４を受容する陰刻手段を含む）および燃料電池スタック１６（これは、複数の双極プレート２０から構成されており、これらのプレートは、スタックキャップ２２とスタックベース２４との間に挟まれている）を有する。この燃料電池は、さらに、熱交換器２６を含む。囲壁３０は、このユニットに対して、漏れ防止ハウジングを提供する。 FIG. 2 illustrates unassembled parts of the fuel cell. The fuel cell is comprised of a base unit 12 (which includes intaglio means for receiving the reformer 14) and a fuel cell stack 16 (which comprises a plurality of bipolar plates 20 that are stacked. Between the cap 22 and the stack base 24). The fuel cell further includes a heat exchanger 26. The enclosure 30 provides a leak-proof housing for this unit.

（実施例）
以下の実施例は、以下で述べる成分を使用する。 (Example)
The following examples use the ingredients described below.

樹脂Ａは、Ｃｏｌｕｍｂｕｓ，ＯｈｉｏのＡｓｈｌａｎｄＣｈｅｍｉｃａｌ
Ｃｏ．から入手できるＨｅｔｒｏｎ９２２である。それは、低粘度のエポキシビニルエステル樹脂である。それは、約５５重量％の固形分および約４５重量％の反応性単量体である。 Resin A is Ashland Chemical, Columbus, Ohio
Co. Hetron 922 available from It is a low viscosity epoxy vinyl ester resin. It is about 55 wt% solids and about 45 wt% reactive monomer.

樹脂Ｂは、ＲｅｓｅａｒｃｈＴｒｉａｎｇｌｅＰａｒｋ，ＮＣのＲｅｉｃｈｈｏｌｄＣｈｅｍｉｃａｌｓ，Ｉｎｃ．製のＡｔｌａｃ３８２ＥＳである。それは、ビスフェノールフマレート樹脂として、特徴付けられる。それを、スチレンで、約５５重量％の固形分まで希釈した。 Resin B was purchased from Reichhold Chemicals, Inc. of Research Triangle Park, NC. It is made by Atlac 382ES. It is characterized as a bisphenol fumarate resin. It was diluted with styrene to a solids content of about 55% by weight.

樹脂Ｃは、スチレンで５５重量％の固形分まで希釈したＤｉｏｎ６６９４である。それは、ＲｅｉｃｈｈｏｌｄＣｈｅｍｉｃａｌｓ，Ｉｎｃ．から入手できる。それは、変性ビスフェノールフマレートポリエステルとして特徴付けられる。 Resin C is Dion 6694 diluted with styrene to a solid content of 55% by weight. It is available from Reichhold Chemicals, Inc. Available from It is characterized as a modified bisphenol fumarate polyester.

樹脂Ｄは、ＫａｎｓａｓＣｉｔｙ，ＭＯのＣｏｏｋＣｏｍｐｏｓｉｔｅｓ
ａｎｄＰｏｌｙｍｅｒｓ製の４２−２６４１である。それは、スチレンで、５５重量％の固形分まで希釈した。それは、不飽和ポリエステル樹脂として、特徴付けられる。 Resin D is Cook Compositions of Kansas City, MO.
and Polymers 42-2641. It was diluted with styrene to a solid content of 55% by weight. It is characterized as an unsaturated polyester resin.

樹脂Ｅは、ＲｅｉｃｈｈｏｌｄＣｈｅｍｉｃａｌｓ，Ｉｎｃ．製のＡＴＬＡＣ３５８１−６１である。それは、５０重量％のスチレンと組み合わせた１９重量％のビニルエステル樹脂、２７重量％のポリエステルおよび４重量％のウレタン重合体として、特徴付けられる。それゆえ、それは、スチレンで５０重量％の固形分まで希釈した。 Resin E was purchased from Reichhold Chemicals, Inc. ATLAC 3581-61 manufactured by It is characterized as 19% vinyl ester resin, 27% polyester and 4% urethane polymer combined with 50% styrene. Therefore, it was diluted to 50 wt% solids with styrene.

樹脂Ｆは、ＲｅｉｃｈｈｏｌｄＣｈｅｍｉｃａｌｓ，Ｉｎｃ．製の５８０−０５である。それは、ウレタン変性ビニルエステル樹脂として、特徴付けられる。それは、スチレンで５４重量％の固形分まで希釈した。 Resin F was purchased from Reichhold Chemicals, Inc. 580-05 made by It is characterized as a urethane-modified vinyl ester resin. It was diluted to 54 wt% solids with styrene.

樹脂Ｇは、ＲｅｉｃｈｈｏｌｄＣｈｅｍｉｃａｌｓ，Ｉｎｃ．製の９１００である。それは、ビスフェノール−エポキシビニルエステルとして、特徴付けられる。それは、スチレンで５４〜５８重量％の固形分まで希釈した。 Resin G was purchased from Reichhold Chemicals, Inc. 9100 made. It is characterized as a bisphenol-epoxy vinyl ester. It was diluted with styrene to a solids content of 54-58% by weight.

樹脂Ｈは、ＤｏｗＣｈｅｍｉｃａｌｓ，Ｉｎｃ．製のＤｏｗＤｅｒａｋａｎｅＲ８０８４である。それは、エラストマー変性ビニルエステル樹脂として、特徴付けられる。それは、スチレンで５０〜６０重量％の固形分まで希釈した。 Resin H was purchased from Dow Chemicals, Inc. It is Dow Derekane R8084. It is characterized as an elastomer modified vinyl ester resin. It was diluted with styrene to a solid content of 50-60% by weight.

樹脂Ｉは、ＲｅｉｃｈｈｏｌｄＣｈｅｍｉｃａｌｓ，Ｉｎｃ．製の９４８０−００である。それは、エポキシノボラックビニルエステルとして、特徴付けられる。それは、スチレンで５３．５重量％の固形分まで希釈した。 Resin I was obtained from Reichhold Chemicals, Inc. 9480-00 made by It is characterized as an epoxy novolac vinyl ester. It was diluted to 53.5 wt% solids with styrene.

樹脂Ｊは、ＲｅｉｃｈｈｏｌｄＣｈｅｍｉｃａｌｓ，Ｉｎｃ．製のＡｔｌａｃ３１−６３２である。それは、不飽和イソシアヌレートビニルエステル樹脂である。 Resin J was purchased from Reichhold Chemicals, Inc. Atlac 31-632 made. It is an unsaturated isocyanurate vinyl ester resin.

レオロジー改質剤Ａは、Ｄａｎｖｅｒｓ，ＭＡのＭｏｒｔｏｎＴｈｉｏｋｏｌ，Ｉｎｃ．製のＥｌａｓｔｏｍａｇである。それは、９９％純粋酸化マグネシウムとして、特徴付けられる。 Rheology modifier A is available from Morton Thiokol, Inc. of Danvers, MA. Elastomag. It is characterized as 99% pure magnesium oxide.

レオロジー改質剤Ｂは、ポリイソシアネートである。これらの実験で使用した物質は、ＣｏｏｋＣｏｍｐｏｓｉｔｅｓａｎｄＰｏｌｙｍｅｒｓ製の４０−７２６３である。それは、１７．７〜２０．９のＮＣＯ含量、１１０〜１７０の粘度、８７°Ｆの引火点および゜４０°Ｆの結晶化点により、特徴付けられる。 Rheology modifier B is a polyisocyanate. The material used in these experiments is 40-7263 from Cook Composites and Polymers. It is characterized by an NCO content of 17.7-20.9, a viscosity of 110-170, a flash point of 87 ° F. and a crystallization point of 40 ° F.

レオロジー改質剤Ｃは、Ｒｅｉｃｈｈｏｌｄ，Ｉｎｃ．製のＲＣＩＲＤＴＨＬ５５（これはまた、ＲＤ−１０７０としても知られている）である。それは、具体的には、ポリウレタン樹脂である。 Rheology modifier C is available from Reichhold, Inc. RCI RD THL55 (also known as RD-1070). Specifically, it is a polyurethane resin.

レオロジー改質剤Ｄは、ＩＣＩから入手できるＲｕｂｉｎａｔｅ１７８０である。それは、重合体メチレンジフェニルジイソシアネートとして、特徴付けられる。 Rheology modifier D is Rubinate 1780 available from ICI. It is characterized as a polymer methylene diphenyl diisocyanate.

レオロジー改質剤Ｅは、ＷｅｓｔＣｈｅｓｔｅｒ，ＰｅｎｎｓｙｌｖａｎｉａのＭａｒｓｈａｌｌＰｒｏｄｕｃｔｓＣｏｍｐａｎｙ製のＭａｒｚｏｎ＃５である。それは、細かく分割した粉末ポリテトラフルオロエチレンとして、特徴付けられる。 Rheology modifier E is Marzon # 5 from Marshall Products Company of West Chester, Pennsylvania. It is characterized as finely divided powder polytetrafluoroethylene.

レオロジー改質剤Ｆは、ＦＮ−５１０であり、これは、低密度直鎖状ポリエチレンである。 Rheology modifier F is FN-510, which is a low density linear polyethylene.

開始剤Ａは、Ｄｕｐｏｎｔ，Ｉ＆ＢＩｎｄｕｓｔｒｉａｌａｎｄＢｉｏｃｈｅｍｉｃａｌＤｅｐｔ，ＷｉｌｍｉｎｇｔｏｎＤＥから入手できるＶａｚｏ（２，２−アゾビスイソブチロニトリル）である。 Initiator A is Vazo (2,2-azobisisobutyronitrile) available from Dupont, I & B Industrial and Biochemical Dept, Wilmington DE.

開始剤Ｂは、Ｐｉｔｔｓｂｕｒｇｈ，ＰＡのＤｕｒｒＭａｒｋｅｔｉｎｇから入手できる第三級ブチルパーオキシイソプロピルカーボネート（ＴｒｉｇｉｎｏｘＢＰＩＣ）である。 Initiator B is tertiary butyl peroxyisopropyl carbonate (Triginox BPIC) available from Durr Marketing of Pittsburgh, PA.

開始剤Ｃは、ＤｕｒｒＭａｒｋｅｔｉｎｇから入手できる過安息香酸ｔ−ブチル（ＴＢＰＢ）である。 Initiator C is t-butyl perbenzoate (TBPB) available from Durr Marketing.

開始剤Ｄは、ＤｕｒｒＭａｒｋｅｔｉｎｇから入手できる１，３ジ−ｔ−ブチルパーオキシ−３，５，５−トリメチルシクロヘキサン触媒（Ｔｒｉｇ２９Ｂ７５）である。 Initiator D is a 1,3 di-t-butylperoxy-3,5,5-trimethylcyclohexane catalyst (Trig 29B75) available from Durr Marketing.

この離型剤は、ステアリン酸カルシウムである。 This mold release agent is calcium stearate.

グラファイトＡは、Ａｓｂｕｒｙ，ＮＪのＡｓｂｕｒｙＧｒａｐｈｉｔｅから入手できる合成結晶性グラファイトである。それは、直径１５０ミクロンより大きい粒子を１０％未満で有しかつ直径４４ミクロンより小さい粒子を１０％未満で有することにより、特徴付けられる。それは、４０１２の名称で入手できる。 Graphite A is a synthetic crystalline graphite available from Asbury Graphite, Asbury, NJ. It is characterized by having less than 10% particles larger than 150 microns in diameter and less than 10% particles smaller than 44 microns in diameter. It is available under the name 4012.

グラファイトＢは、ＳＧＬ０２の商品名称で、Ｖａｌｅｎｃｉａ，ＣａｌｉｆｏｒｎｉａのＳＧＬＴｅｃｈｎｉｃから入手できる非常に細かい導電性微粒子グラファイトである。 Graphite B is a very fine conductive particulate graphite available under the trade name SGL 02 and available from SGL Technic, Valencia, California.

グラファイトＣは、ＳＧＬＶＦＩＮＥの商品名称でＶａｌｅｎｃｉａ，ＣａｌｉｆｏｒｎｉａのＳＧＬＴｅｃｈｎｉｃから入手できる導電性微粒子グラファイトである。 Graphite C is a conductive particulate graphite available from SGL Technic, Valencia, California under the trade name SGLVFINE.

グラファイトＤは、Ａｓｂｕｒｙ，ＮＪのＡｓｂｕｒｙＧｒａｐｈｉｔｅから入手できる。それは、改良型の４０１２製品である。 Graphite D is available from Asbury Graphite, Asbury, NJ. It is an improved 4012 product.

グラファイトＥは、３２４３の商品名称でＡｓｂｕｒｙ，ＮＪのＡｓｂｕｒｙ
Ｇｒａｐｈｉｔｅから入手できる導電性薄片グラファイトである。それは、直径７５ミクロンより大きい粒子を１８％未満で有しかつ直径４４ミクロンより小さい粒子を６５％未満で有することにより、特徴付けられる。 Graphite E is an Asbury, NJ Asbury under the trade name 3243
Conductive flake graphite available from Graphite. It is characterized by having less than 18% particles greater than 75 microns in diameter and less than 65% particles smaller than 44 microns in diameter.

グラファイトＦは、２３０Ｕの商品名称でＡｓｂｕｒｙ，ＮＪのＡｓｂｕｒｙ
Ｇｒａｐｈｉｔｅから入手できる導電性薄片グラファイトである。それは、直径４４ミクロンより小さい粒子を１００％有することにより、特徴付けられる。 Graphite F is an Asbury, NJ Asbury under the 230U product name.
Conductive flake graphite available from Graphite. It is characterized by having 100% particles smaller than 44 microns in diameter.

グラファイトＧは、商品名称Ａ９９でＡｓｂｕｒｙ，ＮＪのＡｓｂｕｒｙＧｒａｐｈｉｔｅから入手できる合成グラファイトである。それは、直径４４ミクロンより大きい粒子を３％未満で有しかつ直径４４ミクロンより小さい粒子を９９％未満で有することにより、特徴付けられる。 Graphite G is a synthetic graphite available under the trade name A99 from Asbury Graphite, Asbury, NJ. It is characterized by having less than 3% particles larger than 44 microns in diameter and less than 99% particles smaller than 44 microns in diameter.

グラファイトＨは、ＫＳ７５の名称でＴｉｍｒｅｘＡｍｅｒｉｃａ，Ｉｎｃ．から入手できる合成グラファイトである。それは、直径９６ミクロンより大きい粒子を９５％未満で有しかつ直径７５ミクロンより小さい粒子を９５％未満で有することにより、特徴付けられる。 Graphite H is named KS 75 under the name Timrex America, Inc. Synthetic graphite available from It is characterized by having less than 95% particles larger than 96 microns in diameter and less than 95% particles smaller than 75 microns in diameter.

グラファイトＩは、ＫＳ１５０の名称でＴｉｍｒｅｘＡｍｅｒｉｃａ，Ｉｎｃ．から入手できる合成グラファイトである。それは、直径１８０ミクロンより小さい粒子を少なくとも９５％で有することにより、特徴付けられる。 Graphite I is a trade name of TIM 150 America, Inc. Synthetic graphite available from It is characterized by having at least 95% particles smaller than 180 microns in diameter.

グラファイトＪは、ＫＣ４４の名称でＴｉｍｒｅｘＡｍｅｒｉｃａ，Ｉｎｃ．から入手できる合成グラファイトである。それは、直径４８ミクロンより小さい粒子を少なくとも９０％で有することにより、特徴付けられる。 Graphite J is the name of KC 44, Timmex America, Inc. Synthetic graphite available from It is characterized by having at least 90% particles smaller than 48 microns in diameter.

カーボンブラックＢは、２７０ｍ²／ｇの窒素表面積、１４５ｍ²／ｇのＳＴＳＡ表面積、３５メッシュで０ｐｐｍおよび３２５メッシュで２０ｐｐｍのふるい残渣を有する電気的導電性低残渣カーボンブラックとして特徴付けられ、これは、Ｊａｍｅｓｂｕｒｇ，ＮＪのＣｏｌｕｍｂｉａＣｈｅｍｉｃａｌｓからＣｏｎｄｕｃｔｅｘ９７５の商品名で販売されている。 Carbon Black B is nitrogen surface area of 270m ² / g, STSA surface area of 145m ² / g, characterized as electrically conductive low residue carbon black having a sieve residue of 20ppm at 0ppm and 325 mesh 35 mesh, which is , Jamesburg, NJ, under the trade name Conductex 975 from Columbia Chemicals.

カーボンブラックＣは、ＢｌａｃｋＰｅａｒｌｓの商品名でＢｏｓｔｏｎ，ＭＡのＣａｂｏｔＣｏｒｐｏｒａｔｉｏｎから調達した導電性カーボンブラックであるのに対して、グラファイトＤは、商品ＸＣ−７２でこの企業から調達した。 Carbon Black C is a conductive carbon black procured from Cabot Corporation of Boston, MA under the trade name Black Pearls, whereas Graphite D was procured from this company under the merchandise XC-72.

カーボンブラックＥは、ＫｅｔｊｅｎｂｌａｃｋＥＣ−３００ＪおよびＥＣ−６００ＪＤの商品名でＣｈｉｃａｇｏ，ＩｌｌｉｎｏｉｓのＡｋｚｏＮｏｂｅｌＣｈｅｍｉｃａｌｓから調達した導電性カーボンブラックである。ＥＣ−３００Ｊは、７４０〜８４０ｍｇ／ｇのヨウ素吸収；３１０〜３４５ｃｍ³／１００ｇの細孔容量および１２５〜１４５ｋｇ／ｍ³の見かけバルク密度を有する。ＥＣ−６００ＪＤは、１０００〜１１５０ｍｇ／ｇのヨウ素吸収；４８０〜５１０ｃｍ³／１００ｇの細孔容量および１００〜１２０ｋｇ／ｍ³の見かけバルク密度を有する。 Carbon Black E is a conductive carbon black procured from Akzo Nobel Chemicals of Chicago, Illinois under the trade names Ketjenblack EC-300J and EC-600JD. EC-300 J has an iodine absorption of 740~840mg / g; has an apparent bulk density of pore volume and 125~145kg / m ³ of 310~345cm ³ / 100g. EC-600JD are iodine absorption of 1000~1150mg / g; has an apparent bulk density of pore volume and 100~120kg / m ³ of 480~510cm ³ / 100g.

それらのガラス繊維は、Ｏｗｅｎｓ−ＣｏｒｎｉｎｇＦｉｂｅｒｇｌａｓｓ製であり、特定長にハンマー製粉された連続ガラスフィラメントとして特徴付けられ、強化充填剤媒体として使用される。 These glass fibers are from Owens-Corning Fiberglass and are characterized as continuous glass filaments that are hammer milled to a specific length and are used as reinforcing filler media.

その禁止剤は、２，６−ジ−第三級ブチル−ｐ−クレゾール（ビニルトルエン中で２５％）であった。 The inhibitor was 2,6-di-tert-butyl-p-cresol (25% in vinyl toluene).

これらの成形組成物は、一般に、この樹脂、単量体開始剤、禁止剤、離型剤およびレオロジー改質剤（もし存在するなら）を高剪断カウ（ｃｏｗｅｌｓ）調合器に添加して２分間ブレンドすることにより、調製される。ＢａｋｅｒＰｅｒｋｉｎＭｉｘｅｒにて、この混合物に、この導電性充填剤を添加し、そして１５分間混合する。混合が完了すると、この組成物を適当なバリアバッグに入れ、そして成形前、およそ１日間にわたって、熟成させる。 These molding compositions are typically added to the high shear cows compounder for 2 minutes with the resin, monomer initiator, inhibitor, mold release agent and rheology modifier (if present). It is prepared by blending. The conductive filler is added to the mixture on a Baker Perkin Mixer and mixed for 15 minutes. When mixing is complete, the composition is placed in a suitable barrier bag and aged for approximately 1 day prior to molding.

これらの成形組成物の成形パラメータは、以下のようである：飾り板用には、成形温度は、２９５°Ｆであり、３分間の成形時間および１７３ｇの充填重量
であった。新型双極プレートの成形温度は、２９０°Ｆであり、３分間の成形時間および３００ｇの充填重量であった。種々のレオロジー添加剤（濃厚剤）と組み合わせて導電性充填剤と共に特定の熱硬化性樹脂を使用すると、電気化学的（例えば、燃料電池双極）プレートの大量生産で使用できる製品を有することに関して、双極プレート組成物を改良することが認められた。 The molding parameters of these molding compositions were as follows: For the decorative board, the molding temperature was 295 ° F., a molding time of 3 minutes and a filling weight of 173 g. The molding temperature of the new bipolar plate was 290 ° F. with a molding time of 3 minutes and a filling weight of 300 g. Using certain thermosetting resins with conductive fillers in combination with various rheological additives (thickeners) for having products that can be used in mass production of electrochemical (eg, fuel cell bipolar) plates, It has been found to improve the bipolar plate composition.

その調合を変えた成果には、割れのない成形化合物、金型からの良好な熱強度、低い製造コスト、短いサイクル時間、良好な全体的電気的導電率、高い機械的特性、および良好なレオロジー特性が挙げられる。 The results of this formulation change include crack-free molding compounds, good heat strength from the mold, low manufacturing costs, short cycle times, good overall electrical conductivity, high mechanical properties, and good rheology Characteristics.

表１Ａでは、ＣｏｎｔｒｏｌＬ−２３０１２は、プレートの成形中に割れを受け、そして成形中に導電性充填剤が相分離するために、このプレートの表面に沿って不均一な導電率および抵抗率を有した。ＳａｍｐｌｅｓＬ−２３１８５、Ｌ−２３１２０、Ｌ−２３１１９およびＬ−２３１２６は、所望の特性を有していた。 In Table 1A, Control L-23012 exhibits non-uniform conductivity and resistivity along the surface of the plate due to cracking during molding of the plate and phase separation of the conductive filler during molding. Had. Samples L-23185, L-23120, L-23119 and L-23126 had the desired properties.

表１Ｂでは、ＳａｍｐｌｅｓＬ−２３１２５、Ｌ−２３１８６、Ｌ−２３０３９は、所望の特性を有していた。ＳａｍｐｌｅｓＬ−２３１８４およびＬ−２３０２２は、最適なバルク導電率よりも低い導電率および最適な抵抗率よりも高い抵抗率を有していた。 In Table 1B, Samples L-23125, L-23186, L-23039 had the desired characteristics. Samples L-23184 and L-23022 had a lower conductivity than the optimal bulk conductivity and a higher resistivity than the optimal resistivity.

表１Ｃでは、ＳａｍｐｌｅｓＬ−２３０２３、Ｌ−２３０６３、Ｌ−２３０２４、Ｌ−３２３０２７およびＬ２３０２６は、最適なバルク導電率よりも低い導電率および最適な抵抗率よりも高い抵抗率を有していた。 In Table 1C, Samples L-23023, L-23063, L-23024, L-323027 and L23026 had a lower conductivity than the optimal bulk conductivity and a higher resistivity than the optimal resistivity.

表１Ｄでは、ＳａｍｐｌｅｓＬ−２３２０９およびＬ−２３２１５は、良好な特性を有していた。ＳａｍｐｌｅｓＬ−２３０２８、Ｌ−２３２１０およびＬ−２３２１１は、最適なバルク導電率よりも低い導電率および最適な抵抗率よりも高い抵抗率を有していた。 In Table 1D, Samples L-23209 and L-23215 had good properties. Samples L-23028, L-23210 and L-23211 had a lower conductivity than the optimum bulk conductivity and a higher resistivity than the optimum resistivity.

特許規則に従って、最良の様式および好ましい実施形態が示されてきたが、本発明の範囲は、それに限定されず、むしろ添付の特許請求の範囲によって制限される。

Although the best mode and preferred embodiments have been shown according to the patent rules, the scope of the present invention is not limited thereto but rather is limited by the appended claims.

Claims