JP2010120997A - Active ray-curable inkjet ink and inkjet recording method - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide active ray-curable inkjet ink which can be printed on various types of recording media, has excellent printed image quality and excellent fixability particularly on coated printing paper, and is improved in storage stability and ejection stability of the ink, and to provide an inkjet recording method using the above ink. <P>SOLUTION: The active ray-curable inkjet ink contains a compound represented by general formula (I) in amount of 0.1 mass% or more and less than 20 mass%. In the formula, R<SB>1</SB>and R<SB>4</SB>each represents a linear or branched alkyl group or linear or branched alkenyl group, R<SB>2</SB>represents a linear alkylene group having 1 to 5 carbon atoms, and R<SB>3</SB>represents a linear or branched alkyl group having 1 to 5 carbon atoms. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

本発明は、新規の活性光線硬化型インクジェットインク、中でも温度によりゾルゲル相転移することを特徴とする活性光線硬化型インクジェット用インクとそれを用いたインクジェット記録方法に関する。   The present invention relates to a novel actinic radiation curable inkjet ink, and more particularly to an actinic radiation curable inkjet ink characterized by a sol-gel phase transition depending on temperature, and an inkjet recording method using the same.

近年、インクジェット記録方式は簡便、安価に画像を作成できるため、写真、各種印刷、マーキング、カラーフィルター等の特殊印刷など、様々な印刷分野に応用されてきている。特に、微細なドットを出射、制御する記録装置や、色再現域、耐久性、出射適性等を改善したインク及びインクの吸収性、色材の発色性、表面光沢などを飛躍的に向上させた専用紙を用い、銀塩写真に匹敵する画質を得ることも可能となっている。   In recent years, the ink jet recording method can easily and inexpensively create an image, and thus has been applied to various printing fields such as photographs, various printing, marking, and special printing such as a color filter. In particular, a recording device that emits and controls fine dots, ink that has improved color reproduction gamut, durability, and emission suitability, and ink absorbability, coloring material color development, surface gloss, etc. have been dramatically improved. It is also possible to obtain image quality comparable to silver halide photography using special paper.

しかしながら、専用紙を必要とするインクジェットシステムでは、用いることのできる記録媒体が制限されることと、記録媒体のコストが高くなることが問題となる。   However, in an inkjet system that requires dedicated paper, there are problems that the recording medium that can be used is limited and the cost of the recording medium is high.

一方、オフィス及び軽印刷分野においては、記録媒体（例えば、普通紙、コート紙、アート紙、普通紙両面印刷等）の制約を受けずに高速フルカラー印字が行えるシステムのニーズが益々高まりつつある。電子写真方式では、１分当たりＡ４サイズで１００枚の印字が可能な高速タイプがあるが、装置の簡便性、コスト、消費電力等のいずれの要求を満たし、且つ様々な記録媒体に高画質で印字するためには、その技術的な課題が未だ多く、ユーザーの要望を満足するには至っていないのが現状である。   On the other hand, in the office and light printing fields, there is an increasing need for a system that can perform high-speed full-color printing without being restricted by recording media (for example, plain paper, coated paper, art paper, double-sided printing on plain paper, etc.). In the electrophotographic system, there is a high-speed type that can print 100 sheets at A4 size per minute. However, it meets all requirements such as simplicity, cost, and power consumption of the device, and high image quality on various recording media. In order to print, there are still many technical problems, and the present situation is that the user's request has not been satisfied.

インクジェット方式においても、水性インクを用いた場合、普通紙などの吸収性の高い記録媒体では、インクが記録媒体に滲み広がるフェザリングや、記録媒体の背面側まで浸透してしまう裏抜けが生じるといった問題があり、またインク吸収層を持たない印刷コート紙等の記録媒体ではインク液滴同士が合一し、画像がまだらになる液寄り現象や、インクの乾燥不良及び定着不良が生じるといった問題がある。   Even in the ink jet system, when water-based ink is used, a recording medium with high absorbency such as plain paper causes feathering in which the ink spreads into the recording medium, or see-through that penetrates to the back side of the recording medium. There are problems, and in recording media such as print-coated paper that does not have an ink absorbing layer, ink droplets coalesce and liquid drip phenomenon that causes an image to be mottled, and problems such as poor ink drying and poor fixing occur. is there.

また、近年、高速印字を目的として、ライン方式により画像を一筆書きで形成するシングルパス方式によるインクジェット印字が検討されているが、水系インクを適用した場合、印刷コート紙上の液寄りや定着不良は多パス方式よりも悪くなる傾向にあり、且つシングルパス方式ではより速やかな乾燥が求められるため、乾燥に多大なエネルギーを必要とし、消費電力が高くなるという問題がある。   In recent years, for the purpose of high-speed printing, inkjet printing by a single pass method in which an image is formed with a single stroke by the line method has been studied. The single-pass method tends to be worse than the multi-pass method, and quicker drying is required. Therefore, there is a problem that a large amount of energy is required for drying and the power consumption is increased.

上記課題を踏まえて、専用紙とは異なる様々な記録媒体へインクジェット記録方式により画像記録する方法が提案されている。例えば、記録後に紫外線（ＵＶ）光などの活性光線を照射して架橋させる紫外線硬化型インクジェット方式や、室温で固形のワックスインクを用いる相変化インクジェット方式などである。   Based on the above problems, a method for recording an image on various recording media different from dedicated paper by an ink jet recording method has been proposed. For example, there are an ultraviolet curable ink jet method in which actinic rays such as ultraviolet light (UV) light are irradiated after crosslinking and a phase change ink jet method using a solid wax ink at room temperature.

具体的には、有機溶媒、着色剤、紫外線硬化組成物を含むインクジェットインクを、ポリエチレンテレフタレートフィルム、塩化ビニルシート等に印字して、紫外線照射装置により紫外線を照射して硬化させ、指触乾燥評価によるインク定着性、メタノールラビング評価による耐溶剤性を向上させる技術が開示されている（例えば、特許文献１参照）。   Specifically, an inkjet ink containing an organic solvent, a colorant, and an ultraviolet curable composition is printed on a polyethylene terephthalate film, a vinyl chloride sheet, etc., cured by irradiating ultraviolet rays with an ultraviolet irradiation device, and evaluated for touch dryness. Discloses a technique for improving the ink fixing property and solvent resistance by methanol rubbing evaluation (see, for example, Patent Document 1).

この構成により様々な記録媒体に高い定着性で印字が可能になるが、紫外線照射方式ではインク着滴から紫外線照射までにタイムラグが生じ、そのタイムラグ中にインクが濡れ広がるために、記録ドットの大きさがタイムラグの長さ、つまり装置構成や記録速度に左右されるという問題が生じる。また、これらの構成を印刷用コート紙などの非吸収性記録媒体に適用した場合、記録媒体の種類によりインクの濡れ広がりが異なるため、記録媒体の種類によって記録ドットの大きさに差異が生じ、結果として画像品質が記録媒体の種類に左右されるといった問題が生じる。   This configuration makes it possible to print on various recording media with high fixability. However, in the ultraviolet irradiation method, there is a time lag between ink landing and ultraviolet irradiation, and the ink spreads out during the time lag. There arises a problem that the length of time is affected by the length of the time lag, that is, the apparatus configuration and the recording speed. In addition, when these configurations are applied to a non-absorbent recording medium such as a coated paper for printing, the ink wetting and spreading differs depending on the type of the recording medium, resulting in a difference in the size of the recording dot depending on the type of the recording medium, As a result, there arises a problem that the image quality depends on the type of the recording medium.

更に活性光線硬化型インクジェットシステムをシングルパス方式に適用する場合、活性光線を照射する前に液滴同士の合一が生じるため、液寄りが発生して画像品質が劣化するといった問題がある。   Further, when the actinic ray curable ink jet system is applied to the single pass method, the droplets are coalesced before being irradiated with the actinic ray.

一方、低融点ワックスを含む常温固体インクを加熱（例えば、１２０℃以上）、溶融させ、溶融した状態で該インクを出射し、記録媒体上で瞬時に固化させる方法が知られている。   On the other hand, there is known a method in which a normal temperature solid ink containing a low melting point wax is heated (for example, 120 ° C. or higher), melted, ejected in the melted state, and instantly solidified on a recording medium.

この方法によれば、普通紙等のインク吸収能を有する記録媒体でもほどほどの品位を有する画像を得ることはできるが、形成された画像の擦過耐性を高めるためには、固化したインクの硬度を高める必要があるが、所望の硬度を得るためには融点の高いワックスの使用が必要となる。例えば、融点が１２０℃以上のワックスを用いた場合、１２０℃以上という高温に加熱するため、インクジェット印字装置のヘッドの耐熱性、インク供給系の部材に負荷がかかり、印字装置の耐久性に難があり、その装置も大型にせざるを得ないという課題を抱えている。特に記録ヘッドにピエゾ素子を使用した方式では、高温限界点としてキュリー温度があり、自ずと加熱できる温度に上限が存在する。   According to this method, it is possible to obtain an image having a moderate quality even with a recording medium having ink absorbing ability such as plain paper, but in order to increase the scratch resistance of the formed image, the hardness of the solidified ink is reduced. Although it is necessary to increase, it is necessary to use a wax having a high melting point in order to obtain a desired hardness. For example, when a wax having a melting point of 120 ° C. or higher is used, the head is heated to a high temperature of 120 ° C. or higher, so that the heat resistance of the head of the ink jet printing apparatus and the members of the ink supply system are overloaded, making the printing apparatus difficult to be durable. There is a problem that the apparatus must be large. In particular, in a method using a piezo element in the recording head, there is a Curie temperature as a high temperature limit point, and there is an upper limit on the temperature that can be heated naturally.

また、インク中にゲル化剤としてアルキルアリールシクロアルカノールを含み、ゲル化剤の固化能を利用して、インクの色ドット間での滲みを改良する方法が開示されている（例えば、特許文献２参照）。   Further, a method is disclosed in which an alkylarylcycloalkanol is included as a gelling agent in the ink and the blurring between the color dots of the ink is improved by utilizing the solidification ability of the gelling agent (for example, Patent Document 2). reference).

しかしながら、上記提案されている方法ではインク固化能としてゲル化剤のみを使用しており、インク固化能が十分ではないため、特に高速印字において普通紙等を用いて高速で搬送した場合、記録媒体上からインク画像が剥離してしまう問題点を抱えている。また、上記特許文献１においては、インク中にゲル化剤と共に活性光線硬化型組成物を用いることに関し、一切の言及がなされていない。   However, in the above proposed method, only the gelling agent is used as the ink solidifying ability, and the ink solidifying ability is not sufficient. Therefore, when the medium is transported at high speed using plain paper or the like particularly in high-speed printing, the recording medium There is a problem that the ink image is peeled off from above. Moreover, in the said patent document 1, no reference is made | formed regarding using an actinic-light curable composition with a gelatinizer in an ink.

また、有機溶剤をゲル化する機能を持った所謂油ゲル化剤をインクに添加することにより、普通紙に記録した場合の裏抜け耐性や印字画像品質を改善する技術や、油ゲル化剤として特定構造の化合物が開示されている（例えば、特許文献３、４参照）が、ゲル化剤の種類によってインクにチクソトロピー性が出る場合があることや、インクを０℃で低温保存した時にゲル化剤と思われる物質の析出が見られる場合があるなどの問題があった。
特開２００２−２４１６５４号公報 特開平１１−３１５２４５号公報 特開２００５−１２６５０７号公報 特開２００５−２５５８２１号公報 In addition, by adding a so-called oil gelling agent with the function of gelling an organic solvent to the ink, the technology for improving the through-through resistance and printed image quality when recording on plain paper, as an oil gelling agent Although compounds having a specific structure are disclosed (for example, see Patent Documents 3 and 4), there are cases where the thixotropy of the ink may appear depending on the type of gelling agent, and gelation occurs when the ink is stored at 0 ° C. at a low temperature. There were problems such as the precipitation of substances that seemed to be agents.
JP 2002-241654 A JP-A-11-315245 JP 2005-126507 A JP 2005-255821 A

本発明は上記課題に鑑みなされたものであり、その目的は、様々な記録媒体に印字が可能で、特に印刷用コート紙での印字画像品質や定着性に優れ、併せてインク自体の保存安定性及び出射安定性が改良された活性光線硬化型インクジェットインクとそれを用いたインクジェット記録方法を提供することである。   The present invention has been made in view of the above-mentioned problems, and its purpose is to enable printing on various recording media, particularly excellent print image quality and fixability on coated paper for printing, and storage stability of the ink itself. The present invention provides an actinic ray curable inkjet ink having improved properties and emission stability and an inkjet recording method using the same.

本発明の上記目的は、以下の構成により達成される。   The above object of the present invention is achieved by the following configurations.

１．下記一般式（Ｉ）で表される化合物をインク全質量に対して０．１質量％以上、２０質量％未満含有することを特徴とする活性光線硬化型インクジェットインク。   1. An actinic ray curable inkjet ink comprising a compound represented by the following general formula (I) in an amount of 0.1% by mass to less than 20% by mass with respect to the total mass of the ink.

（式中、Ｒ_１及びＲ_４は直鎖もしくは分岐のアルキル基、または直鎖もしくは分岐のアルケニル基を表し、Ｒ_２は炭素数１〜５の直鎖のアルキレン基を表し、Ｒ_３は炭素数１〜５の直鎖もしくは分岐のアルキル基を表す。）
２．前記一般式（Ｉ）で表される化合物中のＲ_２がテトラメチレン基であり、Ｒ_１及びＲ_４がそれぞれ炭素数２〜３０の直鎖のアルキル基であって、末端がビニル基または水素原子であることを特徴とする前記１に記載の活性光線硬化型インクジェットインク。 (In the formula, R ₁ and R ₄ represent a linear or branched alkyl group or a linear or branched alkenyl group, R ₂ represents a linear alkylene group having 1 to 5 carbon atoms, and R ₃ represents carbon. Represents a linear or branched alkyl group of formula 1-5.)
2. R ₂ in the compound represented by the general formula (I) is a tetramethylene group, R ₁ and R ₄ are each a linear alkyl group having 2 to 30 carbon atoms, and the terminal is a vinyl group or hydrogen. 2. The actinic ray curable inkjet ink according to 1 above, which is an atom.

３．着色剤として顔料を含有することを特徴とする前記１または２に記載の活性光線硬化型インクジェットインク。   3. 3. The actinic ray curable inkjet ink according to 1 or 2 above, which contains a pigment as a colorant.

４．温度により可逆的にゾルゲル相転移することを特徴とし、ゾルゲル相転移温度が３０℃以上、１００℃未満であることを特徴とする前記１〜３のいずれか１項に記載の活性光線硬化型インクジェットインク。   4). 4. The actinic ray curable inkjet according to any one of 1 to 3 above, wherein the sol-gel phase transition is reversibly changed depending on a temperature, and the sol-gel phase transition temperature is 30 ° C. or higher and lower than 100 ° C. ink.

５．前記１〜４のいずれか１項に記載の活性光線硬化型インクジェットインクを記録ヘッドを用いて記録媒体上に記録を行うインクジェット記録方法において、記録ヘッド内での活性光線硬化型インクジェットインクの温度が記録媒体の温度より２５℃以上、１００℃未満高いことを特徴とするインクジェット記録方法。   5. In the inkjet recording method of recording the actinic ray curable inkjet ink according to any one of 1 to 4 on a recording medium using a recording head, the temperature of the actinic ray curable inkjet ink in the recording head is An ink jet recording method characterized by being 25 ° C. or more and less than 100 ° C. higher than the temperature of the recording medium.

６．前記活性光線硬化型インクジェットインクを記録ヘッド内で加熱することを特徴とする前記５に記載のインクジェット記録方法。   6). 6. The inkjet recording method described in 5 above, wherein the actinic ray curable inkjet ink is heated in a recording head.

７．前記活性光線硬化型インクジェットインクの記録ヘッド内での加熱の温度が活性光線硬化型インクジェットインクのゾルゲル相転移温度よりも１０℃以上、４０℃未満高いことを特徴とする前記６に記載のインクジェット記録方法。   7). 7. The ink jet recording according to 6 above, wherein the heating temperature of the actinic radiation curable inkjet ink in the recording head is 10 ° C. or more and less than 40 ° C. higher than the sol-gel phase transition temperature of the actinic radiation curable inkjet ink. Method.

本発明によれば、様々な記録媒体に印字が可能で、特に印刷用コート紙での印字画像品質や定着性に優れ、併せてインク自体の保存安定性及び出射安定性が改良された活性光線硬化型インクジェットインクとそれを用いたインクジェット記録方法を提供できる。   According to the present invention, actinic rays can be printed on various recording media, particularly excellent in print image quality and fixability on a coated paper for printing, and also improved in the storage stability and emission stability of the ink itself. A curable inkjet ink and an inkjet recording method using the same can be provided.

本発明者らは、上記課題に鑑みて鋭意検討を行った結果、前記一般式（Ｉ）で表される化合物を含有する活性光線硬化型インクジェットインクにより、様々な記録媒体に印字が可能で、特に印刷用コート紙での印字画像品質や定着性に優れ、併せてインク自体の保存安定性及び出射安定性が改良された活性光線硬化型インクジェットインクを実現できることを見出し、本発明に至った。   As a result of intensive studies in view of the above problems, the present inventors are capable of printing on various recording media with the actinic ray curable inkjet ink containing the compound represented by the general formula (I), In particular, the present inventors have found that an actinic ray curable inkjet ink having excellent print image quality and fixability on a coated paper for printing, and improved storage stability and emission stability of the ink itself can be realized.

前記一般式（Ｉ）で表される化合物を含有する本発明の活性光線硬化型インクジェットインクは、出射時には低粘度で良好な流動性を有する。しかし、記録媒体への着弾は、主にインク温度の低下により速やかにインク粘性の増加またはゾルからゲルへの相転移が起こり、流動性が著しく低下することにより、印刷用コート紙上での濡れ広がりによる記録ドットの拡大を抑制し、なお且つ液滴同士の合一を抑える作用が働き、印刷用コート紙での印字画像品質を飛躍的に改良できたものと考えられる。   The actinic ray curable inkjet ink of the present invention containing the compound represented by the general formula (I) has a low viscosity and good fluidity when emitted. However, when landing on the recording medium, wetting spreads on the coated paper for printing mainly due to the rapid increase in ink viscosity or phase transition from sol to gel due to a decrease in ink temperature, resulting in a significant decrease in fluidity. It is considered that the print image quality on the coated paper for printing was drastically improved by the action of suppressing the expansion of the recording dots due to the ink and also suppressing the coalescence of the droplets.

以下、本発明の詳細について説明する。   Details of the present invention will be described below.

本発明の活性光線硬化型インクジェットインク（以下、単にインクとも言う）においては、少なくとも前記一般式（Ｉ）で表される少なくとも１種の化合物を含有することが特徴である。   The actinic ray curable inkjet ink of the present invention (hereinafter also simply referred to as ink) is characterized by containing at least one compound represented by the general formula (I).

一般式（Ｉ）において、Ｒ_１及びＲ_４は直鎖もしくは分岐のアルキル基、または直鎖もしくは分岐のアルケニル基を表し、Ｒ_２は炭素数１〜５の直鎖のアルキレン基を表し、Ｒ_３は炭素数１〜５の直鎖もしくは分岐のアルキル基を表す。 In the general formula (I), R ₁ and R ₄ represent a linear or branched alkyl group or a linear or branched alkenyl group, R ₂ represents a linear alkylene group having 1 to 5 carbon atoms, R ₃ represents a linear or branched alkyl group having 1 to 5 carbon atoms.

Ｒ_１及びＲ_４が表すアルキル基、アルケニル基は置換基を有してもよく、置換基としては、シクロアルキル基（例えば、シクロペンチル基、シクロヘキシル基等）、アルキニル基（例えば、エチニル基、プロパルギル基等）、アリール基（例えば、フェニル基、ナフチル基等）、芳香族複素環基（例えば、フリル基、チエニル基、ピリジル基、ピリダジニル基、ピリミジニル基、ピラジニル基、トリアジニル基、イミダゾリル基、ピラゾリル基、チアゾリル基、キナゾリニル基、フタラジニル基等）、複素環基（例えば、ピロリジル基、イミダゾリジル基、モルホリル基、オキサゾリジル基等）、アルコキシ基（例えば、メトキシ基、エトキシ基、プロピルオキシ基、ペンチルオキシ基、ヘキシルオキシ基、オクチルオキシ基、ドデシルオキシ基等）、シクロアルコキシ基（例えば、シクロペンチルオキシ基、シクロヘキシルオキシ基等）、アリールオキシ基（例えば、フェノキシ基、ナフチルオキシ基等）、アルキルチオ基（例えば、メチルチオ基、エチルチオ基、プロピルチオ基、ペンチルチオ基、ヘキシルチオ基、オクチルチオ基、ドデシルチオ基等）、シクロアルキルチオ基（例えば、シクロペンチルチオ基、シクロヘキシルチオ基等）、アリールチオ基（例えば、フェニルチオ基、ナフチルチオ基等）、アルコキシカルボニル基（例えば、メチルオキシカルボニル基、エチルオキシカルボニル基、ブチルオキシカルボニル基、オクチルオキシカルボニル基、ドデシルオキシカルボニル基等）、アリールオキシカルボニル基（例えば、フェニルオキシカルボニル基、ナフチルオキシカルボニル基等）、スルファモイル基（例えば、アミノスルホニル基、メチルアミノスルホニル基、ジメチルアミノスルホニル基、ブチルアミノスルホニル基、ヘキシルアミノスルホニル基、シクロヘキシルアミノスルホニル基、オクチルアミノスルホニル基、ドデシルアミノスルホニル基、フェニルアミノスルホニル基、ナフチルアミノスルホニル基、２−ピリジルアミノスルホニル基等）、アシル基（例えば、アセチル基、エチルカルボニル基、プロピルカルボニル基、ペンチルカルボニル基、シクロヘキシルカルボニル基、オクチルカルボニル基、２−エチルヘキシルカルボニル基、ドデシルカルボニル基、フェニルカルボニル基、ナフチルカルボニル基、ピリジルカルボニル基等）、アシルオキシ基（例えば、アセチルオキシ基、エチルカルボニルオキシ基、ブチルカルボニルオキシ基、オクチルカルボニルオキシ基、ドデシルカルボニルオキシ基、フェニルカルボニルオキシ基等）、アミド基（例えば、メチルカルボニルアミノ基、エチルカルボニルアミノ基、ジメチルカルボニルアミノ基、プロピルカルボニルアミノ基、ペンチルカルボニルアミノ基、シクロヘキシルカルボニルアミノ基、２−エチルヘキシルカルボニルアミノ基、オクチルカルボニルアミノ基、ドデシルカルボニルアミノ基、フェニルカルボニルアミノ基、ナフチルカルボニルアミノ基等）、カルバモイル基（例えば、アミノカルボニル基、メチルアミノカルボニル基、ジメチルアミノカルボニル基、プロピルアミノカルボニル基、ペンチルアミノカルボニル基、シクロヘキシルアミノカルボニル基、オクチルアミノカルボニル基、２−エチルヘキシルアミノカルボニル基、ドデシルアミノカルボニル基、フェニルアミノカルボニル基、ナフチルアミノカルボニル基、２−ピリジルアミノカルボニル基等）、ウレイド基（例えば、メチルウレイド基、エチルウレイド基、ペンチルウレイド基、シクロヘキシルウレイド基、オクチルウレイド基、ドデシルウレイド基、フェニルウレイド基ナフチルウレイド基、２−ピリジルアミノウレイド基等）、スルフィニル基（例えば、メチルスルフィニル基、エチルスルフィニル基、ブチルスルフィニル基、シクロヘキシルスルフィニル基、２−エチルヘキシルスルフィニル基、ドデシルスルフィニル基、フェニルスルフィニル基、ナフチルスルフィニル基、２−ピリジルスルフィニル基等）、アルキルスルホニル基（例えば、メチルスルホニル基、エチルスルホニル基、ブチルスルホニル基、シクロヘキシルスルホニル基、２−エチルヘキシルスルホニル基、ドデシルスルホニル基等）、アリールスルホニル基（例えば、フェニルスルホニル基、ナフチルスルホニル基、２−ピリジルスルホニル基等）、アミノ基（例えば、アミノ基、エチルアミノ基、ジメチルアミノ基、ブチルアミノ基、シクロペンチルアミノ基、２−エチルヘキシルアミノ基、ドデシルアミノ基、アニリノ基、ナフチルアミノ基、２−ピリジルアミノ基等）、ハロゲン原子（例えば、フッ素原子、塩素原子、臭素原子等）、フッ化炭化水素基（例えば、フルオロメチル基、トリフルオロメチル基、ペンタフルオロエチル基、ペンタフルオロフェニル基等）、シアノ基、ニトロ基、ヒドロキシ基、メルカプト基、シリル基（例えば、トリメチルシリル基、トリイソプロピルシリル基、トリフェニルシリル基、フェニルジエチルシリル基等）、ビニル基、アリル基等が挙げられる。 The alkyl group and alkenyl group represented by R ₁ and R ₄ may have a substituent. Examples of the substituent include a cycloalkyl group (eg, cyclopentyl group, cyclohexyl group, etc.), an alkynyl group (eg, ethynyl group, propargyl). Group), aryl group (for example, phenyl group, naphthyl group, etc.), aromatic heterocyclic group (for example, furyl group, thienyl group, pyridyl group, pyridazinyl group, pyrimidinyl group, pyrazinyl group, triazinyl group, imidazolyl group, pyrazolyl group) Group, thiazolyl group, quinazolinyl group, phthalazinyl group, etc.), heterocyclic group (eg, pyrrolidyl group, imidazolidyl group, morpholyl group, oxazolidyl group, etc.), alkoxy group (eg, methoxy group, ethoxy group, propyloxy group, pentyloxy) Group, hexyloxy group, octyloxy group, dodecyloxy group Si group etc.), cycloalkoxy group (eg cyclopentyloxy group, cyclohexyloxy group etc.), aryloxy group (eg phenoxy group, naphthyloxy group etc.), alkylthio group (eg methylthio group, ethylthio group, propylthio group, Pentylthio group, hexylthio group, octylthio group, dodecylthio group, etc.), cycloalkylthio group (eg, cyclopentylthio group, cyclohexylthio group, etc.), arylthio group (eg, phenylthio group, naphthylthio group, etc.), alkoxycarbonyl group (eg, methyl Oxycarbonyl group, ethyloxycarbonyl group, butyloxycarbonyl group, octyloxycarbonyl group, dodecyloxycarbonyl group, etc.), aryloxycarbonyl group (for example, phenyloxycarbonyl group, naphthi) Ruoxycarbonyl group, etc.), sulfamoyl group (for example, aminosulfonyl group, methylaminosulfonyl group, dimethylaminosulfonyl group, butylaminosulfonyl group, hexylaminosulfonyl group, cyclohexylaminosulfonyl group, octylaminosulfonyl group, dodecylaminosulfonyl group) Phenylaminosulfonyl group, naphthylaminosulfonyl group, 2-pyridylaminosulfonyl group, etc.), acyl group (for example, acetyl group, ethylcarbonyl group, propylcarbonyl group, pentylcarbonyl group, cyclohexylcarbonyl group, octylcarbonyl group, 2-ethylhexyl) Carbonyl group, dodecylcarbonyl group, phenylcarbonyl group, naphthylcarbonyl group, pyridylcarbonyl group, etc.), acyloxy group (for example, acetyloxy group) Group, ethylcarbonyloxy group, butylcarbonyloxy group, octylcarbonyloxy group, dodecylcarbonyloxy group, phenylcarbonyloxy group, etc.), amide group (for example, methylcarbonylamino group, ethylcarbonylamino group, dimethylcarbonylamino group, propyl) Carbonylamino group, pentylcarbonylamino group, cyclohexylcarbonylamino group, 2-ethylhexylcarbonylamino group, octylcarbonylamino group, dodecylcarbonylamino group, phenylcarbonylamino group, naphthylcarbonylamino group, etc.), carbamoyl group (for example, aminocarbonyl) Group, methylaminocarbonyl group, dimethylaminocarbonyl group, propylaminocarbonyl group, pentylaminocarbonyl group, cyclohexylaminocarbonyl Nyl group, octylaminocarbonyl group, 2-ethylhexylaminocarbonyl group, dodecylaminocarbonyl group, phenylaminocarbonyl group, naphthylaminocarbonyl group, 2-pyridylaminocarbonyl group, etc.), ureido group (for example, methylureido group, ethylureido group) Pentylureido group, cyclohexylureido group, octylureido group, dodecylureido group, phenylureido group, naphthylureido group, 2-pyridylaminoureido group, etc.), sulfinyl group (for example, methylsulfinyl group, ethylsulfinyl group, butylsulfinyl group, cyclohexyl) Sulfinyl group, 2-ethylhexylsulfinyl group, dodecylsulfinyl group, phenylsulfinyl group, naphthylsulfinyl group, 2-pyridylsulfinyl group, etc.), Alkylsulfonyl groups (for example, methylsulfonyl group, ethylsulfonyl group, butylsulfonyl group, cyclohexylsulfonyl group, 2-ethylhexylsulfonyl group, dodecylsulfonyl group, etc.), arylsulfonyl groups (for example, phenylsulfonyl group, naphthylsulfonyl group, 2- Pyridylsulfonyl group, etc.), amino group (for example, amino group, ethylamino group, dimethylamino group, butylamino group, cyclopentylamino group, 2-ethylhexylamino group, dodecylamino group, anilino group, naphthylamino group, 2-pyridylamino group) Group), halogen atom (eg, fluorine atom, chlorine atom, bromine atom), fluorinated hydrocarbon group (eg, fluoromethyl group, trifluoromethyl group, pentafluoroethyl group, pentafluorophenyl group), cyan Group, nitro group, hydroxy group, a mercapto group, a silyl group (e.g., trimethylsilyl group, triisopropylsilyl group, triphenylsilyl group, a phenyl diethyl silyl group and the like), vinyl group, allyl group and the like.

Ｒ_２が表すアルキレン基、Ｒ_３が表すアルキル基もまた上記置換基で置換されてもよい。 The alkylene group represented by R _{2 and the} alkyl group represented by R ₃ may also be substituted with the above substituents.

一般式（Ｉ）においては、Ｒ_２がテトラメチレン基であり、Ｒ_１及びＲ_４がそれぞれ炭素数２〜３０の直鎖のアルキル基であって、末端がビニル基または水素原子であることが好ましい。 In the general formula (I), R ₂ is a tetramethylene group, R ₁ and R ₄ are each a linear alkyl group having 2 to 30 carbon atoms, and the terminal is a vinyl group or a hydrogen atom. preferable.

本発明に係る前記一般式（Ｉ）で表される化合物をインクに添加することにより、温度降下に伴いインクの増粘あるいはゲル化させることが可能となる。   By adding the compound represented by the general formula (I) according to the present invention to the ink, the ink can be thickened or gelled as the temperature drops.

インクを増粘させるか、あるいはゲル化させるかについては、インクに対する前記一般式（Ｉ）で表される化合物の添加量で調整することが可能である。記録媒体上での印字品質や裏抜け性能を最大限に発揮するためには、インクは記録媒体上でゲル化することが好ましい。本発明で言うゲル化とは、ラメラ構造、共有結合や水素結合した高分子網目、物理的な凝集状態によって形成される高分子網目、微粒子の凝集構造などの相互作用により、物質が独立した運動を失って集合した構造を持ち、急激な粘度上昇や弾性増加を伴って固化した、または半固化した状態のことを言う。   Whether the ink is thickened or gelled can be adjusted by the amount of the compound represented by formula (I) added to the ink. In order to maximize the print quality and back-through performance on the recording medium, the ink is preferably gelled on the recording medium. Gelation as used in the present invention refers to the independent movement of substances due to interactions such as lamellar structure, covalently or hydrogen-bonded polymer network, polymer network formed by physical aggregation state, and fine particle aggregation structure. It has a structure that has been aggregated by losing and solidified with a sudden increase in viscosity or elasticity, or a semi-solidified state.

本発明のインクが温度によりゾルゲル相転移を起こす場合、そのゾルゲル転移温度は任意に設定されるが、３０℃以上、１００℃未満であることが好ましい。インクの相転移温度が３０℃未満では、記録ヘッドからインク液滴を出射する際に印字環境温度に影響されて、安定した出射性を得ることが難しく、また１００℃以上では、インクジェット記録装置を過度の高温に加熱する必要があり、インクジェット記録装置のヘッドやインク供給系の部材への負荷がかかり、耐久性に問題を生じると共に装置全体の大型化やそれに伴う高コスト化を招く結果となる。   When the ink of the present invention causes a sol-gel phase transition depending on the temperature, the sol-gel transition temperature is arbitrarily set, but is preferably 30 ° C. or higher and lower than 100 ° C. If the phase transition temperature of the ink is less than 30 ° C., it is difficult to obtain a stable ejection property due to the influence of the printing environment temperature when ejecting the ink droplets from the recording head. It is necessary to heat to an excessively high temperature, and a load is applied to the head of the ink jet recording apparatus and the members of the ink supply system. This causes a problem in durability and results in an increase in the size of the entire apparatus and the associated increase in cost. .

本発明で言うゾルゲルによる相転移温度とは、流動性のある溶液状態から急激に粘度が変化してゲル状態になる温度のことを言い、ゲル転移温度、ゲル溶解温度、ゲル軟化温度、ゾルゲル転移点、ゲル化点と称される用語と同義である。   The phase transition temperature by sol-gel in the present invention refers to the temperature at which the viscosity suddenly changes from a fluid solution state to a gel state. Gel transition temperature, gel dissolution temperature, gel softening temperature, sol-gel transition It is synonymous with the term called point, gel point.

インクにおける相転移温度の測定方法は、例えば、ヒートプレート上にゲル状の試験片を置き、ヒートプレートを加熱していき、試験片の形状が崩れる温度を測定し、これをゾルゲル相転移温度として求めることができる。また、ゾルゲル転移温度は記録ヘッド内でのインク温度と記録媒体の温度の間であることが好ましい。本発明のインクのゾルゲル転移温度は、本発明に係る前記一般式（Ｉ）で表される化合物の添加量により調整が可能である。   The method of measuring the phase transition temperature in ink is, for example, placing a gel-like test piece on a heat plate, heating the heat plate, measuring the temperature at which the shape of the test piece collapses, and using this as the sol-gel phase transition temperature. Can be sought. The sol-gel transition temperature is preferably between the ink temperature in the recording head and the temperature of the recording medium. The sol-gel transition temperature of the ink of the present invention can be adjusted by the amount of the compound represented by the general formula (I) according to the present invention.

次に、本発明のインクに係る前記一般式（Ｉ）で表される化合物の具体例を示すが、本発明はこれらの化合物に限定されるものではない。   Next, specific examples of the compound represented by the general formula (I) according to the ink of the present invention are shown, but the present invention is not limited to these compounds.

本発明に係る前記一般式（Ｉ）で表される化合物のインク中への添加量は、インク全質量に対して０．１質量％以上、２０質量％未満であることを特徴とする。本発明のインクにおいて、インク全質量に対して、前記一般式（Ｉ）で表される化合物の添加量が０．１質量％未満である場合には、記録媒体に着弾した際の増粘やゲル化が不十分となるため、記録媒体上での印字品質や裏抜け性能が十分に満たされない結果となる。また、インク全質量に対し、前記一般式（Ｉ）で表される化合物の添加量が２０質量％以上の場合には、出射が不安定なる場合があり、また色材に顔料を使用した場合には、顔料の分散安定性を損なう場合がある。   The amount of the compound represented by the general formula (I) according to the present invention added to the ink is 0.1% by mass or more and less than 20% by mass with respect to the total mass of the ink. In the ink of the present invention, when the amount of the compound represented by the general formula (I) is less than 0.1% by mass with respect to the total mass of the ink, Since the gelation is insufficient, the printing quality on the recording medium and the through-through performance are not sufficiently satisfied. In addition, when the amount of the compound represented by the general formula (I) is 20% by mass or more with respect to the total mass of the ink, the emission may be unstable, and when a pigment is used as the coloring material In some cases, the dispersion stability of the pigment is impaired.

インク全質量に対する前記一般式（Ｉ）で表される化合物の添加量は、０．１質量％以上、２０質量％未満であれば顕著な効果が見られるが、より好ましくは０．５質量％以上、２０質量％未満であり、更に好ましくは１．０質量％以上、１５質量％未満である。   If the amount of the compound represented by the general formula (I) is 0.1% by mass or more and less than 20% by mass relative to the total mass of the ink, a remarkable effect is seen, but more preferably 0.5% by mass. As mentioned above, it is less than 20 mass%, More preferably, it is 1.0 mass% or more and less than 15 mass%.

本発明に係る前記一般式（Ｉ）で表される化合物は、それぞれ単独で用いてもよいし、２種類以上を併用して用いてもよい。２種類以上用いる時にはその総量がインク全質量に対して２０質量％未満であることが好ましい。   The compounds represented by the general formula (I) according to the present invention may be used alone or in combination of two or more. When two or more types are used, the total amount is preferably less than 20% by mass with respect to the total mass of the ink.

次いで、本発明のインクについて、上記項目を除いた各構成要素について説明する。   Next, the components of the ink of the present invention excluding the above items will be described.

本発明のインクにおいては、インクを構成する色材としては、染料あるいは顔料を制限なく用いることができるが、インク成分に対し良好な分散安定性を有し、且つ耐候性に優れた顔料を用いることが好ましい。顔料としては特に限定されるわけではないが、本発明には、例えば、カラーインデックスに記載される下記の番号の有機または無機顔料が使用できる。   In the ink of the present invention, a dye or a pigment can be used without limitation as a colorant constituting the ink, but a pigment having good dispersion stability with respect to the ink component and excellent weather resistance is used. It is preferable. Although it does not necessarily limit as a pigment, For example, the organic or inorganic pigment of the following number described in a color index can be used for this invention.

赤あるいはマゼンタ顔料としては、Ｐｉｇｍｅｎｔ Ｒｅｄ ３、５、１９、２２、３１、３８、４３、４８：１、４８：２、４８：３、４８：４、４８：５、４９：１、５３：１、５７：１、５７：２、５８：４、６３：１、８１、８１：１、８１：２、８１：３、８１：４、８８、１０４、１０８、１１２、１２２、１２３、１４４、１４６、１４９、１６６、１６８、１６９、１７０、１７７、１７８、１７９、１８４、１８５、２０８、２１６、２２６、２５７、Ｐｉｇｍｅｎｔ Ｖｉｏｌｅｔ ３、１９、２３、２９、３０、３７、５０、８８、Ｐｉｇｍｅｎｔ Ｏｒａｎｇｅ １３、１６、２０、３６、青またはシアン顔料としては、Ｐｉｇｍｅｎｔ Ｂｌｕｅ １、１５、１５：１、１５：２、１５：３、１５：４、１５：６、１６、１７−１、２２、２７、２８、２９、３６、６０、緑顔料としては、Ｐｉｇｍｅｎｔ Ｇｒｅｅｎ ７、２６、３６、５０、黄顔料としては、Ｐｉｇｍｅｎｔ Ｙｅｌｌｏｗ １、３、１２、１３、１４、１７、３４、３５、３７、５５、７４、８１、８３、９３、９４，９５、９７、１０８、１０９、１１０、１３７、１３８、１３９、１５３、１５４、１５５、１５７、１６６、１６７、１６８、１８０、１８５、１９３、黒顔料としては、Ｐｉｇｍｅｎｔ Ｂｌａｃｋ ７、２８、２６などが目的に応じて使用できる。   Examples of red or magenta pigments include Pigment Red 3, 5, 19, 22, 31, 38, 43, 48: 1, 48: 2, 48: 3, 48: 4, 48: 5, 49: 1, and 53: 1. 57: 1, 57: 2, 58: 4, 63: 1, 81, 81: 1, 81: 2, 81: 3, 81: 4, 88, 104, 108, 112, 122, 123, 144, 146 149, 166, 168, 169, 170, 177, 178, 179, 184, 185, 208, 216, 226, 257, Pigment Violet 3, 19, 23, 29, 30, 37, 50, 88, Pigment Orange 13 16, 20, 36, blue or cyan pigments include Pigment Blue 1, 15, 15: 1, 15: 2, 15: 3, 15: 4, 15: 6, 16 , 17-1, 22, 27, 28, 29, 36, 60, Pigment Green 7, 26, 36, 50 as a green pigment, Pigment Yellow 1, 3, 12, 13, 14, 17 as a yellow pigment , 34, 35, 37, 55, 74, 81, 83, 93, 94, 95, 97, 108, 109, 110, 137, 138, 139, 153, 154, 155, 157, 166, 167, 168, 180 , 185, 193, and black pigments such as Pigment Black 7, 28, 26 can be used depending on the purpose.

具体的に商品名を示すと、例えば、クロモファインイエロー２０８０、５９００、５９３０、ＡＦ−１３００、２７００Ｌ、クロモファインオレンジ３７００Ｌ、６７３０、クロモファインスカーレット６７５０、クロモファインマゼンタ６８８０、６８８６、６８９１Ｎ、６７９０、６８８７、クロモファインバイオレット ＲＥ、クロモファインレッド６８２０、６８３０、クロモファインブルーＨＳ−３、５１８７、５１０８、５１９７、５０８５Ｎ、ＳＲ−５０２０、５０２６、５０５０、４９２０、４９２７、４９３７、４８２４、４９３３ＧＮ−ＥＰ、４９４０、４９７３、５２０５、５２０８、５２１４、５２２１、５０００Ｐ、クロモファイングリーン２ＧＮ、２ＧＯ、２Ｇ−５５０Ｄ、５３１０、５３７０、６８３０、クロモファインブラックＡ−１１０３、セイカファストエロー１０ＧＨ、Ａ−３、２０３５、２０５４、２２００、２２７０、２３００、２４００（Ｂ）、２５００、２６００、ＺＡＹ−２６０、２７００（Ｂ）、２７７０、セイカファストレッド８０４０、Ｃ４０５（Ｆ）、ＣＡ１２０、ＬＲ−１１６、１５３１Ｂ、８０６０Ｒ、１５４７、ＺＡＷ−２６２、１５３７Ｂ、ＧＹ、４Ｒ−４０１６、３８２０、３８９１、ＺＡ−２１５、セイカファストカーミン６Ｂ１４７６Ｔ−７、１４８３ＬＴ、３８４０、３８７０、セイカファストボルドー１０Ｂ−４３０、セイカライトローズＲ４０、セイカライトバイオレットＢ８００、７８０５、セイカファストマルーン４６０Ｎ、セイカファストオレンジ９００、２９００、セイカライトブルーＣ７１８、Ａ６１２、シアニンブルー４９３３Ｍ、４９３３ＧＮ−ＥＰ、４９４０、４９７３（大日精化工業製）、ＫＥＴ Ｙｅｌｌｏｗ ４０１、４０２、４０３、４０４、４０５、４０６、４１６、４２４、ＫＥＴ Ｏｒａｎｇｅ ５０１、ＫＥＴ Ｒｅｄ ３０１、３０２、３０３、３０４、３０５、３０６、３０７、３０８、３０９、３１０、３３６、３３７、３３８、３４６、ＫＥＴ Ｂｌｕｅ １０１、１０２、１０３、１０４、１０５、１０６、１１１、１１８、１２４、ＫＥＴ Ｇｒｅｅｎ ２０１（大日本インキ化学製）、Ｃｏｌｏｒｔｅｘ Ｙｅｌｌｏｗ ３０１、３１４、３１５、３１６、Ｐ−６２４、３１４、Ｕ１０ＧＮ、Ｕ３ＧＮ、ＵＮＮ、ＵＡ−４１４、Ｕ２６３、Ｆｉｎｅｃｏｌ Ｙｅｌｌｏｗ Ｔ−１３、Ｔ−０５、Ｐｉｇｍｅｎｔ Ｙｅｌｌｏｗ １７０５、Ｃｏｌｏｒｔｅｘ Ｏｒａｎｇｅ ２０２、Ｃｏｌｏｒｔｅｘ Ｒｅｄ １０１、１０３、１１５、１１６、Ｄ３Ｂ、Ｐ−６２５、１０２、Ｈ−１０２４、１０５Ｃ、ＵＦＮ、ＵＣＮ、ＵＢＮ、Ｕ３ＢＮ、ＵＲＮ、ＵＧＮ、ＵＧ２７６、Ｕ４５６、Ｕ４５７、１０５Ｃ、ＵＳＮ、Ｃｏｌｏｒｔｅｘ Ｍａｒｏｏｎ６０１、Ｃｏｌｏｒｔｅｘ ＢｒｏｗｎＢ６１０Ｎ、Ｃｏｌｏｒｔｅｘ Ｖｉｏｌｅｔ６００、Ｐｉｇｍｅｎｔ Ｒｅｄ １２２、Ｃｏｌｏｒｔｅｘ Ｂｌｕｅ５１６、５１７、５１８、５１９、Ａ８１８、Ｐ−９０８、５１０、Ｃｏｌｏｒｔｅｘ Ｇｒｅｅｎ ４０２、４０３、Ｃｏｌｏｒｔｅｘ Ｂｌａｃｋ ７０２、Ｕ９０５（山陽色素製）、Ｌｉｏｎｏｌ Ｙｅｌｌｏｗ１４０５Ｇ、Ｌｉｏｎｏｌ Ｂｌｕｅ ＦＧ７３３０、ＦＧ７３５０、ＦＧ７４００Ｇ、ＦＧ７４０５Ｇ、ＥＳ、ＥＳＰ−Ｓ（東洋インキ製）、Ｔｏｎｅｒ Ｍａｇｅｎｔａ Ｅ０２、Ｐｅｒｍａｎｅｎｔ Ｒｕｂｉｎ Ｆ６Ｂ、Ｔｏｎｅｒ Ｙｅｌｌｏｗ ＨＧ、Ｐｅｒｍａｎｅｎｔ Ｙｅｌｌｏｗ ＧＧ−０２、Ｈｏｓｔａｐｅａｍ ＢｌｕｅＢ２Ｇ（ヘキストインダストリ製）、Ｎｏｖｏｐｅｒｍ Ｐ−ＨＧ、Ｈｏｓｔａｐｅｒｍ Ｐｉｎｋ Ｅ、Ｈｏｓｔａｐｅｒｍ Ｂｌｕｅ Ｂ２Ｇ（クラリアント製）、カーボンブラック＃２６００、＃２４００、＃２３５０、＃２２００、＃１０００、＃９９０、＃９８０、＃９７０、＃９６０、＃９５０、＃８５０、ＭＣＦ８８、＃７５０、＃６５０、ＭＡ６００、ＭＡ７、ＭＡ８、ＭＡ１１、ＭＡ１００、ＭＡ１００Ｒ、ＭＡ７７、＃５２、＃５０、＃４７、＃４５、＃４５Ｌ、＃４０、＃３３、＃３２、＃３０、＃２５、＃２０、＃１０、＃５、＃４４、ＣＦ９（三菱化学製）などが挙げられる。   Specific product names include, for example, chromofine yellow 2080, 5900, 5930, AF-1300, 2700L, chromofine orange 3700L, 6730, chromofine scarlet 6750, chromofine magenta 6880, 6886, 6891N, 6790, 6887. , Chromofine Violet RE, Chromofine Red 6820, 6830, Chromofine Blue HS-3, 5187, 5108, 5197, 5085N, SR-5020, 5026, 5050, 4920, 4927, 4937, 4824, 4933GN-EP, 4940, 4973, 5205, 5208, 5214, 5221, 5000P, Chromofine Green 2GN, 2GO, 2G-550D, 5310, 5370, 6830, Ku Mofine Black A-1103, Seika Fast Yellow 10GH, A-3, 2035, 2054, 2200, 2270, 2300, 2400 (B), 2500, 2600, ZAY-260, 2700 (B), 2770, Seika Fast Red 8040 , C405 (F), CA120, LR-116, 1531B, 8060R, 1547, ZAW-262, 1537B, GY, 4R-4016, 3820, 3891, ZA-215, Seika Fast Carmine 6B1476T-7, 1483LT, 3840, 3870 , Seika Fast Bordeaux 10B-430, Seica Light Rose R40, Seika Light Violet B800, 7805, Seika Fast Maroon 460N, Seika Fast Orange 900, 2900, Seika Light Blue C7 18, A612, cyanine blue 4933M, 4933GN-EP, 4940, 4973 (manufactured by Dainichi Seika Kogyo), KET Yellow 401, 402, 403, 404, 405, 406, 416, 424, KET Orange 501, KET Red 301, 302 , 303, 304, 305, 306, 307, 308, 309, 310, 336, 337, 338, 346, KET Blue 101, 102, 103, 104, 105, 106, 111, 118, 124, KET Green 201 (large Nippon Ink Chemical Co., Ltd.), Colortex Yellow 301, 314, 315, 316, P-624, 314, U10GN, U3GN, UNN, UA-414, U263, Finecol Yellow T-13, T-05, Pi gment Yellow 1705, Colortex Orange 202, Colortex Red 101, 103, 115, 116, D3B, P-625, 102, H-1024, 105C, UFN, UCN, UBN, U3BN, URN, UGN, UG276, U456, U457 105C, USN, Colortex Maroon 601, Colortex Brown B610N, Colortex Violet 600, Pigment Red 122, Colortex Blue 516, 517, 518, 519, A818, P-908, 510, Colortex Green 402, Colortex Green 403 , Lionol Yellow 1405G, Liono l Blue FG7330, FG7350, FG7400G, FG7405G, ES, ESP-S (manufactured by Toyo Ink), Toner Magenta E02, Permanent Rubin F6B, Toner Yellow HG, Permanent Yellow GG-02, Hoge -HG, Hostaperm Pink E, Hostaperm Blue B2G (manufactured by Clariant), carbon black # 2600, # 2400, # 2350, # 2200, # 1000, # 990, # 980, # 970, # 960, # 950, # 850, MCF88, # 750, # 650, MA600, MA7, MA8, MA11, MA100, MA100R, M 77, # 52, # 50, # 47, # 45, # 45L, # 40, # 33, # 32, # 30, # 25, # 20, # 10, # 5, # 44, CF9 (Mitsubishi Chemical) Etc.

また、顔料を予め水、溶剤、重合性モノマー等に高濃度分散した分散液を使用することもできる。   Further, it is also possible to use a dispersion in which the pigment is dispersed in high concentration in advance in water, a solvent, a polymerizable monomer or the like.

本発明のインクにおいては、顔料を分散するための顔料分散剤を用いることが好ましい。本発明で用いることのできる分散剤としては、例えば、高級脂肪酸塩、アルキル硫酸塩、アルキルエステル硫酸塩、アルキルスルホン酸塩、スルホコハク酸塩、ナフタレンスルホン酸塩、アルキルリン酸塩、ポリオキシアルキレンアルキルエーテルリン酸塩、ポリオキシアルキレンアルキルフェニルエーテル、ポリオキシエチレンポリオキシプロピレングリコール、グリセリンエステル、ソルビタンエステル、ポリオキシエチレン脂肪酸アミド、アミンオキシド等の活性剤、あるいは、スチレン、スチレン誘導体、ビニルナフタレン誘導体、アクリル酸、アクリル酸誘導体、マレイン酸、マレイン酸誘導体、イタコン酸、イタコン酸誘導体、フマル酸、フマル酸誘導体から選ばれた２種以上の単量体からなるブロック共重合体、ランダム共重合体及びこれらの塩を挙げることができる。   In the ink of the present invention, it is preferable to use a pigment dispersant for dispersing the pigment. Examples of the dispersant that can be used in the present invention include higher fatty acid salts, alkyl sulfates, alkyl ester sulfates, alkyl sulfonates, sulfosuccinates, naphthalene sulfonates, alkyl phosphates, and polyoxyalkylene alkyls. Activators such as ether phosphate, polyoxyalkylene alkylphenyl ether, polyoxyethylene polyoxypropylene glycol, glycerin ester, sorbitan ester, polyoxyethylene fatty acid amide, amine oxide, or styrene, styrene derivatives, vinyl naphthalene derivatives, Block copolymer consisting of two or more monomers selected from acrylic acid, acrylic acid derivatives, maleic acid, maleic acid derivatives, itaconic acid, itaconic acid derivatives, fumaric acid, fumaric acid derivatives, random copolymer It can be given body and the salts thereof.

顔料の分散には、ボールミル、サンドミル、アトライター、ロールミル、アジテータ、ヘンシェルミキサ、コロイドミル、超音波ホモジナイザー、パールミル、湿式ジェットミル、ペイントシェーカー等を用いることができる。また、顔料の分散を行う際に分散剤を添加することも可能である。   For the dispersion of the pigment, a ball mill, a sand mill, an attritor, a roll mill, an agitator, a Henschel mixer, a colloid mill, an ultrasonic homogenizer, a pearl mill, a wet jet mill, a paint shaker, or the like can be used. It is also possible to add a dispersant when dispersing the pigment.

本発明においては、顔料分散剤の添加量としては、顔料に対し１０〜１００質量％であることが好ましい。   In the present invention, the addition amount of the pigment dispersant is preferably 10 to 100% by mass with respect to the pigment.

上記方法で得られる顔料の平均分散粒子径は、５０ｎｍ以上、１５０ｎｍ以下であることが好ましい。顔料の平均分散粒子径が上記で規定する範囲であれば、インクの分散安定性を向上させることができ、その結果、ヘッドノズルの詰まりを抑制し、出射安定性がより一層向上させるとともに、インク透明性の向上に伴い、後述する活性光線硬化型組成物を含有させた際の活性光線の硬化効率を高めることができる。本発明のインクにおいて、顔料の平均分散粒子径を上記で規定する範囲に調整する手段としては、例えば、顔料、分散剤、分散媒体の選定、分散条件、ろ過条件を適宜選択あるいは組み合わせることにより達成することができる。   The average dispersed particle size of the pigment obtained by the above method is preferably 50 nm or more and 150 nm or less. If the average dispersed particle size of the pigment is within the range specified above, the dispersion stability of the ink can be improved. As a result, clogging of the head nozzle is suppressed, and the emission stability is further improved. With the improvement of transparency, the curing efficiency of actinic rays when an actinic ray curable composition described later is contained can be increased. In the ink of the present invention, the means for adjusting the average dispersed particle size of the pigment to the range specified above is achieved by, for example, appropriately selecting or combining pigment, dispersant, dispersion medium selection, dispersion conditions, and filtration conditions. can do.

また、本発明のインクにおいては、従来公知の染料、好ましくは油溶性染料の必要に応じて用いることができる。本発明で用いることのできる油溶性染料として、以下にその具体例を挙げるが、本発明はこれらにのみ限定されるものではない。   In the ink of the present invention, conventionally known dyes, preferably oil-soluble dyes, can be used as required. Specific examples of oil-soluble dyes that can be used in the present invention are given below, but the present invention is not limited to these.

〈マゼンタ染料〉
ＭＳ Ｍａｇｅｎｔａ ＶＰ、ＭＳ Ｍａｇｅｎｔａ ＨＭ−１４５０、ＭＳ Ｍａｇｅｎｔａ ＨＳｏ−１４７（以上、三井東圧製）、ＡＩＺＥＮＳＯＴ Ｒｅｄ−１、ＡＩＺＥＮ ＳＯＴ Ｒｅｄ−２、ＡＩＺＥＮ ＳＯＴＲｅｄ−３、ＡＩＺＥＮ ＳＯＴ Ｐｉｎｋ−１、ＳＰＩＲＯＮ Ｒｅｄ ＧＥＨ ＳＰＥＣＩＡＬ（以上、保土谷化学製）、ＲＥＳＯＬＩＮ Ｒｅｄ ＦＢ ２００％、ＭＡＣＲＯＬＥＸ Ｒｅｄ Ｖｉｏｌｅｔ Ｒ、ＭＡＣＲＯＬＥＸ ＲＯＴ５Ｂ（以上、バイエルジャパン製）、ＫＡＹＡＳＥＴ Ｒｅｄ Ｂ、ＫＡＹＡＳＥＴ Ｒｅｄ １３０、ＫＡＹＡＳＥＴ Ｒｅｄ ８０２（以上、日本化薬製）、ＰＨＬＯＸＩＮ、ＲＯＳＥ ＢＥＮＧＡＬ、ＡＣＩＤ Ｒｅｄ（以上、ダイワ化成製）、ＨＳＲ−３１、ＤＩＡＲＥＳＩＮ Ｒｅｄ Ｋ（以上、三菱化成製）、Ｏｉｌ Ｒｅｄ（ＢＡＳＦジャパン製）。 <Magenta dye>
MS Magenta VP, MS Magenta HM-1450, MS Magenta HSo-147 (manufactured by Mitsui Toatsu), AIZENSOT Red-1, AIZEN SOT Red-2, AIZEN SOTRed-3, AIZEN SOT PinGE, SPIRONSPEC GE (Above, manufactured by Hodogaya Chemical Co., Ltd.), RESOLIN Red FB 200%, MACROLEX Red Violet R, MACROLEX ROT5B (above, manufactured by Bayer Japan), KAYASET Red B, KAYASET Red 130, KAYASET Red 802 (above, Nippon Kayaku) PHLOXIN, ROSE BENGAL, ACID Red (Daiwa Kasei), HSR-31, DIARESIN Red K (Mitsubishi) Ltd.), Oil Red (manufactured by BASF Japan).

〈シアン染料〉
ＭＳ Ｃｙａｎ ＨＭ−１２３８、ＭＳ Ｃｙａｎ ＨＳｏ−１６、Ｃｙａｎ ＨＳｏ−１４４、ＭＳ Ｃｙａｎ ＶＰＧ（以上、三井東圧製）、ＡＩＺＥＮ ＳＯＴ Ｂｌｕｅ−４（保土谷化学製）、ＲＥＳＯＬＩＮ ＢＲ．Ｂｌｕｅ ＢＧＬＮ ２００％、ＭＡＣＲＯＬＥＸ Ｂｌｕｅ ＲＲ、ＣＥＲＥＳ Ｂｌｕｅ ＧＮ、ＳＩＲＩＵＳ ＳＵＰＲＡＴＵＲＱ．Ｂｌｕｅ Ｚ−ＢＧＬ、ＳＩＲＩＵＳ ＳＵＰＲＡ ＴＵＲＱ．Ｂｌｕｅ ＦＢ−ＬＬ ３３０％（以上、バイエルジャパン製）、ＫＡＹＡＳＥＴ Ｂｌｕｅ ＦＲ、ＫＡＹＡＳＥＴ Ｂｌｕｅ Ｎ、ＫＡＹＡＳＥＴ Ｂｌｕｅ ８１４、Ｔｕｒｑ．Ｂｌｕｅ ＧＬ−５ ２００、Ｌｉｇｈｔ Ｂｌｕｅ ＢＧＬ−５ ２００（以上、日本化薬製）、ＤＡＩＷＡ Ｂｌｕｅ ７０００、Ｏｌｅｏｓｏｌ Ｆａｓｔ Ｂｌｕｅ ＧＬ（以上、ダイワ化成製）、ＤＩＡＲＥＳＩＮ Ｂｌｕｅ Ｐ（三菱化成製）、ＳＵＤＡＮ Ｂｌｕｅ ６７０、ＮＥＯＰＥＮ Ｂｌｕｅ ８０８、ＺＡＰＯＮ Ｂｌｕｅ ８０６（以上、ＢＡＳＦジャパン製）。 <Cyan dye>
MS Cyan HM-1238, MS Cyan HSo-16, Cyan HSo-144, MS Cyan VPG (manufactured by Mitsui Toatsu), AIZEN SOT Blue-4 (Hodogaya Chemical), RESOLIN BR. Blue BGLN 200%, MACROLEX Blue RR, CERES Blue GN, SIRIUS SUPRATURQ. Blue Z-BGL, SIRIUS SUTRA TURQ. Blue FB-LL 330% (manufactured by Bayer Japan), KAYASET Blue FR, KAYASET Blue N, KAYASET Blue 814, Turq. Blue GL-5 200, Light Blue BGL-5 200 (above, manufactured by Nippon Kayaku), DAIWA Blue 7000, Oleosol Fast Blue GL (above, manufactured by Daiwa Kasei), DIARESIN Blue P (produced by Mitsubishi Kasei), SUDAN Blue 70 NEOPEN Blue 808, ZAPON Blue 806 (above, manufactured by BASF Japan).

〈イエロー染料〉
ＭＳ Ｙｅｌｌｏｗ ＨＳｍ−４１、Ｙｅｌｌｏｗ ＫＸ−７、Ｙｅｌｌｏｗ ＥＸ−２７（三井東圧）、ＡＩＺＥＮ ＳＯＴ Ｙｅｌｌｏｗ−１、ＡＩＺＥＮ ＳＯＴ ＹｅｌｌｏＷ−３、ＡＩＺＥＮ ＳＯＴ Ｙｅｌｌｏｗ−６（以上、保土谷化学製）、ＭＡＣＲＯＬＥＸ Ｙｅｌｌｏｗ ６Ｇ、ＭＡＣＲＯＬＥＸ ＦＬＵＯＲ．Ｙｅｌｌｏｗ １０ＧＮ（以上、バイエルジャパン製）、ＫＡＹＡＳＥＴ Ｙｅｌｌｏｗ ＳＦ−Ｇ、ＫＡＹＡＳＥＴ Ｙｅｌｌｏｗ２Ｇ、ＫＡＹＡＳＥＴ Ｙｅｌｌｏｗ Ａ−Ｇ、ＫＡＹＡＳＥＴ Ｙｅｌｌｏｗ Ｅ−Ｇ（以上、日本化薬製）、ＤＡＩＷＡ Ｙｅｌｌｏｗ ３３０ＨＢ（ダイワ化成製）、ＨＳＹ−６８（三菱化成製）、ＳＵＤＡＮ Ｙｅｌｌｏｗ １４６、ＮＥＯＰＥＮ Ｙｅｌｌｏｗ ０７５（以上、ＢＡＳＦジャパン製）。 <Yellow dye>
MS Yellow HSm-41, Yellow KX-7, Yellow EX-27 (Mitsui Toatsu), AIZEN SOT Yellow-1, AIZEN SOT YellowW-3, AIZEN SOT Yellow-6 (above, manufactured by Hodogaya Chemical), MACROLEX Yellow 6G MACROLEX FLUOR. Yellow 10GN (above, manufactured by Bayer Japan), KAYASET Yellow SF-G, KAYASET Yellow 2G, KAYASET Yellow AG, KAYASET Yellow EG (above, manufactured by Nippon Kayaku), DAIWA Yellow Chemical Y 68 (manufactured by Mitsubishi Kasei), SUDAN Yellow 146, NEOPEN Yellow 075 (above, manufactured by BASF Japan).

〈ブラック染料〉
ＭＳ Ｂｌａｃｋ ＶＰＣ（三井東圧製）、ＡＩＺＥＮ ＳＯＴ Ｂｌａｃｋ−１、ＡＩＺＥＮ ＳＯＴ Ｂｌａｃｋ−５（以上、保土谷化学製）、ＲＥＳＯＲＩＮ Ｂｌａｃｋ ＧＳＮ ２００％、ＲＥＳＯＬＩＮ ＢｌａｃｋＢＳ（以上、バイエルジャパン製）、ＫＡＹＡＳＥＴ Ｂｌａｃｋ Ａ−Ｎ（日本化薬製）、ＤＡＩＷＡ Ｂｌａｃｋ ＭＳＣ（ダイワ化成製）、ＨＳＢ−２０２（三菱化成製）、ＮＥＰＴＵＮＥ Ｂｌａｃｋ Ｘ６０、ＮＥＯＰＥＮ Ｂｌａｃｋ Ｘ５８（以上、ＢＡＳＦジャパン製）等である。 <Black dye>
MS Black VPC (Mitsui Toatsu), AIZEN SOT Black-1, AIZEN SOT Black-5 (above, manufactured by Hodogaya Chemical), RESOLIN Black GSN 200%, RESOLIN Black BS (above, made by Bayer Japan), KAYASET BlackA N (manufactured by Nippon Kayaku), DAIWA Black MSC (manufactured by Daiwa Kasei), HSB-202 (manufactured by Mitsubishi Kasei), NEPTUNE Black X60, NEOPEN Black X58 (manufactured by BASF Japan) and the like.

顔料あるいは油溶性染料の添加量は０．１〜２０質量％が好ましく、更に好ましくは０．４〜１０質量％である。０．１質量％以上であれば、良好な画像品質を得ることができ、２０質量％以下であれば、インク出射における適正なインク粘度を得ることができる。また、色の調整等で２種類以上の着色剤を適時混合して使用できる。   The amount of pigment or oil-soluble dye added is preferably 0.1 to 20% by mass, more preferably 0.4 to 10% by mass. If it is 0.1% by mass or more, good image quality can be obtained, and if it is 20% by mass or less, an appropriate ink viscosity in ink ejection can be obtained. In addition, two or more kinds of colorants can be mixed and used in a timely manner for color adjustment or the like.

本発明のインクにおいては、前記一般式（Ｉ）から選ばれる化合物、色材と共に、活性光線で硬化する活性光線硬化型組成物を含有することを特徴とする。   The ink of the present invention is characterized by containing an actinic ray curable composition that is cured with actinic rays together with a compound selected from the general formula (I) and a colorant.

本発明に用いられる活性光線硬化型組成物（以下、光重合性化合物とも言う）について説明する。   The actinic ray curable composition (hereinafter also referred to as a photopolymerizable compound) used in the present invention will be described.

本発明で言う活性光線とは、例えば、電子線、紫外線、α線、γ線、エックス線等が挙げられるが、人体への危険性や、取り扱いが容易で、工業的にもその利用が普及している紫外線また電子線が好ましい。   The actinic rays referred to in the present invention include, for example, electron beams, ultraviolet rays, α rays, γ rays, X rays, and the like. Preferred are ultraviolet rays and electron beams.

本発明において、活性光線の照射により架橋または重合する光重合性化合物としては、特に制限なく用いることができるが、中でも光カチオン重合性化合物またはラジカル重合性化合物を用いることが好ましく、特に好ましくは光カチオン重合性化合物である。   In the present invention, the photopolymerizable compound that is crosslinked or polymerized by irradiation with actinic rays can be used without any particular limitation. Among them, it is preferable to use a photocationic polymerizable compound or a radical polymerizable compound, particularly preferably light. It is a cationically polymerizable compound.

光カチオン重合性モノマーとしては、各種公知のカチオン重合性のモノマーが使用できる。例えば、特開平６−９７１４号、特開２００１−３１８９２号、特開２００１−４００６８号、特開２００１−５５５０７号、特開２００１−３１０９３８号、特開２００１−３１０９３７号、特開２００１−２２０５２６号の各公報に例示されているエポキシ化合物、ビニルエーテル化合物、オキセタン化合物などが挙げられる。   As the photo cationic polymerizable monomer, various known cationic polymerizable monomers can be used. For example, JP-A-6-9714, JP-A-2001-31892, JP-A-2001-40068, JP-A-2001-55507, JP-A-2001-310938, JP-A-2001-310937, JP-A-2001-220526 Epoxy compounds, vinyl ether compounds, oxetane compounds and the like exemplified in each of the above publications.

本発明においては、インク硬化の際の記録媒体の収縮を抑える目的で、光重合性化合物として少なくとも１種のオキセタン化合物と、エポキシ化合物及びビニルエーテル化合物から選ばれる少なくとも１種の化合物とを含有することが好ましい。   In the present invention, for the purpose of suppressing the shrinkage of the recording medium during ink curing, it contains at least one oxetane compound as a photopolymerizable compound and at least one compound selected from an epoxy compound and a vinyl ether compound. Is preferred.

芳香族エポキシドとして好ましいものは、少なくとも１個の芳香族核を有する多価フェノールあるいはそのアルキレンオキサイド付加体とエピクロルヒドリンとの反応によって製造されるジまたはポリグリシジルエーテルであり、例えば、ビスフェノールＡあるいはそのアルキレンオキサイド付加体のジまたはポリグリシジルエーテル、水素添加ビスフェノールＡあるいはそのアルキレンオキサイド付加体のジまたはポリグリシジルエーテル、並びにノボラック型エポキシ樹脂等が挙げられる。ここでアルキレンオキサイドとしては、エチレンオキサイド及びプロピレンオキサイド等が挙げられる。   A preferable aromatic epoxide is a di- or polyglycidyl ether produced by the reaction of a polyhydric phenol having at least one aromatic nucleus or an alkylene oxide adduct thereof and epichlorohydrin, such as bisphenol A or an alkylene thereof. Examples thereof include di- or polyglycidyl ethers of oxide adducts, di- or polyglycidyl ethers of hydrogenated bisphenol A or alkylene oxide adducts thereof, and novolak-type epoxy resins. Here, examples of the alkylene oxide include ethylene oxide and propylene oxide.

脂環式エポキシドとしては、少なくとも１個のシクロへキセンまたはシクロペンテン環等のシクロアルカン環を有する化合物を、過酸化水素、過酸等の適当な酸化剤でエポキシ化することにより得られる、シクロヘキセンオキサイドまたはシクロペンテンオキサイド含有化合物が好ましい。   As the alicyclic epoxide, cyclohexene oxide obtained by epoxidizing a compound having at least one cycloalkane ring such as cyclohexene or cyclopentene ring with a suitable oxidizing agent such as hydrogen peroxide or peracid. Or a cyclopentene oxide containing compound is preferable.

脂肪族エポキシドの好ましいものとしては、脂肪族多価アルコールあるいはそのアルキレンオキサイド付加体のジまたはポリグリシジルエーテル等があり、その代表例としては、エチレングリコールのジグリシジルエーテル、プロピレングリコールのジグリシジルエーテルまたは１，６−ヘキサンジオールのジグリシジルエーテル等のアルキレングリコールのジグリシジルエーテル、グリセリンあるいはそのアルキレンオキサイド付加体のジまたはトリグリシジルエーテル等の多価アルコールのポリグリシジルエーテル、ポリエチレングリコールあるいはそのアルキレンオキサイド付加体のジグリシジルエーテル、ポリプロピレングリコールあるいはそのアルキレンオキサイド付加体のジグリシジルエーテル等のポリアルキレングリコールのジグリシジルエーテル等が挙げられる。ここでアルキレンオキサイドとしては、エチレンオキサイド及びプロピレンオキサイド等が挙げられる。   Preferred aliphatic epoxides include di- or polyglycidyl ethers of aliphatic polyhydric alcohols or alkylene oxide adducts thereof, and typical examples thereof include diglycidyl ether of ethylene glycol, diglycidyl ether of propylene glycol or Diglycidyl ether of alkylene glycol such as diglycidyl ether of 1,6-hexanediol, polyglycidyl ether of polyhydric alcohol such as di- or triglycidyl ether of glycerin or alkylene oxide adduct thereof, polyethylene glycol or alkylene oxide adduct thereof Of polyalkylene glycols such as diglycidyl ether, polypropylene glycol or diglycidyl ether of its alkylene oxide adduct Glycidyl ether, and the like. Here, examples of the alkylene oxide include ethylene oxide and propylene oxide.

これらのエポキシドの内、速硬化性を考慮すると、芳香族エポキシド及び脂環式エポキシドが好ましく、特に脂環式エポキシドが好ましい。本発明では、上記エポキシドの１種を単独で使用してもよいが、２種以上を適宜組み合わせて使用してもよい。   Of these epoxides, aromatic epoxides and alicyclic epoxides are preferable, and alicyclic epoxides are particularly preferable in consideration of fast curability. In the present invention, one of the epoxides may be used alone, or two or more may be used in appropriate combination.

ビニルエーテル化合物としては、例えば、エチレングリコールジビニルエーテル、ジエチレングリコールジビニルエーテル、トリエチレングリコールジビニルエーテル、プロピレングリコールジビニルエーテル、ジプロピレングリコールジビニルエーテル、ブタンジオールジビニルエーテル、ヘキサンジオールジビニルエーテル、シクロヘキサンジメタノールジビニルエーテル、トリメチロールプロパントリビニルエーテル等のジまたはトリビニルエーテル化合物、エチルビニルエーテル、ｎ−ブチルビニルエーテル、イソブチルビニルエーテル、オクタデシルビニルエーテル、シクロヘキシルビニルエーテル、ヒドロキシブチルビニルエーテル、２−エチルヘキシルビニルエーテル、シクロヘキサンジメタノールモノビニルエーテル、ｎ−プロピルビニルエーテル、イソプロピルビニルエーテル、イソプロペニルエーテル−ｏ−プロピレンカーボネート、ドデシルビニルエーテル、ジエチレングリコールモノビニルエーテル、オクタデシルビニルエーテル等のモノビニルエーテル化合物等が挙げられる。   Examples of the vinyl ether compound include ethylene glycol divinyl ether, diethylene glycol divinyl ether, triethylene glycol divinyl ether, propylene glycol divinyl ether, dipropylene glycol divinyl ether, butanediol divinyl ether, hexanediol divinyl ether, cyclohexanedimethanol divinyl ether, Di- or trivinyl ether compounds such as methylolpropane trivinyl ether, ethyl vinyl ether, n-butyl vinyl ether, isobutyl vinyl ether, octadecyl vinyl ether, cyclohexyl vinyl ether, hydroxybutyl vinyl ether, 2-ethylhexyl vinyl ether, cyclohexane dimethanol monovinyl ether, n- B pills vinyl ether, isopropyl vinyl ether, isopropenyl ether -o- propylene carbonate, dodecyl vinyl ether, diethylene glycol monovinyl ether, and octadecyl vinyl ether.

これらのビニルエーテル化合物の内、硬化性、密着性、表面硬度を考慮するとジまたはトリビニルエーテル化合物が好ましく、特にジビニルエーテル化合物が好ましい。本発明では、上記ビニルエーテル化合物の１種を単独で使用してもよいが、２種以上を適宜組み合わせて使用してもよい。   Of these vinyl ether compounds, a di- or trivinyl ether compound is preferable in consideration of curability, adhesion, and surface hardness, and a divinyl ether compound is particularly preferable. In the present invention, one of the above vinyl ether compounds may be used alone, or two or more thereof may be used in appropriate combination.

本発明に係るオキセタン化合物はオキセタン環を有する化合物のことであり、特開２００１−２２０５２６号、特開２００１−３１０９３７号の各公報に記載されているような公知のあらゆるオキセタン化合物を使用できる。   The oxetane compound according to the present invention is a compound having an oxetane ring, and any known oxetane compound as described in JP-A Nos. 2001-220526 and 2001-310937 can be used.

本発明で用いることのできるオキセタン化合物において、オキセタン環を５個以上有する化合物を使用するとインク組成物の粘度が高くなるため、取り扱いが困難になること、またインク組成物のガラス転移温度が高くなるため、得られる硬化物の粘着性が十分でなくなることがある。本発明で使用するオキセタン環を有する化合物は、オキセタン環を１〜４個有する化合物が好ましい。   In the oxetane compound that can be used in the present invention, if a compound having 5 or more oxetane rings is used, the viscosity of the ink composition increases, which makes it difficult to handle and increases the glass transition temperature of the ink composition. For this reason, the obtained cured product may not have sufficient tackiness. The compound having an oxetane ring used in the present invention is preferably a compound having 1 to 4 oxetane rings.

本発明で好ましく用いることのできるオキセタン環を有する化合物としては、特開２００５−２５５８２１号公報の段落番号００８９に記載されている、一般式（１）で表される化合物、同じく同号公報の段落番号００９２に記載されている、一般式（２）、段落番号０１０７の一般式（７）、段落番号０１０９の一般式（８）、段落番号０１６６の一般式（９）等で表される化合物を挙げることができる。   Examples of the compound having an oxetane ring that can be preferably used in the present invention include compounds represented by general formula (1) described in paragraph No. 0089 of JP-A No. 2005-255821, and also paragraphs of the same publication. Compounds represented by general formula (2), general formula (7) of paragraph number 0107, general formula (8) of paragraph number 0109, general formula (9) of paragraph number 0166 and the like described in number 0092 Can be mentioned.

具体的には、同号公報の段落番号０１０４〜０１１９に記載されている例示化合物１〜６及び段落番号０１２１に記載されている化合物を挙げることができる。   Specific examples thereof include the exemplified compounds 1 to 6 described in paragraph numbers 0104 to 0119 and the compound described in paragraph number 0121 of the publication.

次いで、ラジカル重合性化合物について説明する。   Next, the radical polymerizable compound will be described.

本発明のインクにおいては、ラジカル重合性化合物の使用を制限するものではなく、ラジカル重合性化合物としては、例えば、特開平７−１５９９８３号、特公平７−３１３９９号、特開平８−２２４９８２号、特開平１０−８６３号の各公報に記載されている光重合性組成物を用いた光硬化型材料と、カチオン重合系の光硬化性樹脂が知られており、最近では可視光以上の長波長域に増感された光カチオン重合系の光硬化性樹脂も、例えば、特開平６−４３６３３号公報、特開平８−３２４１３７号公報等に公開されている。   In the ink of the present invention, the use of the radical polymerizable compound is not limited. Examples of the radical polymerizable compound include JP-A-7-159983, JP-B-7-31399, JP-A-8-224982, A photocurable material using a photopolymerizable composition described in JP-A-10-863 and a cationic polymerization type photocurable resin are known, and recently, a long wavelength longer than visible light. Photo-cationic polymerization type photo-curing resins sensitized to the region are also disclosed in, for example, JP-A-6-43633 and JP-A-8-324137.

ラジカル重合性化合物は、ラジカル重合可能なエチレン性不飽和結合を有する化合物であり、分子中にラジカル重合可能なエチレン性不飽和結合を少なくとも１つ有する化合物であればどの様なものでもよく、モノマー、オリゴマー、ポリマー等の化学形態を持つものが含まれる。ラジカル重合性化合物は１種のみ用いてもよく、また目的とする特性を向上するために任意の比率で２種以上を併用してもよい。   The radical polymerizable compound is a compound having an ethylenically unsaturated bond capable of radical polymerization, and may be any compound as long as it has at least one ethylenically unsaturated bond capable of radical polymerization in the molecule. , Oligomers, polymers and the like having a chemical form. Only one kind of radically polymerizable compound may be used, or two or more kinds thereof may be used in combination at an arbitrary ratio in order to improve desired properties.

本発明のインクにおいて、活性光線として紫外線等を用いる場合には、少なくとも１種の光重合開始剤を含有することが好ましい。但し、活性光線として電子線を用いる場合には、多くの場合、光重合開始剤を必要としない。   In the ink of the present invention, when ultraviolet rays or the like are used as the active light, it is preferable to contain at least one photopolymerization initiator. However, when an electron beam is used as the actinic ray, a photopolymerization initiator is not required in many cases.

光重合開始剤としては、分子内結合開裂型と分子内水素引き抜き型の２種に大別できる。   Photopolymerization initiators can be broadly classified into two types: intramolecular bond cleavage type and intramolecular hydrogen abstraction type.

分子内結合開裂型の光重合開始剤としては、例えば、ジエトキシアセトフェノン、２−ヒドロキシ−２−メチル−１−フェニルプロパン−１−オン、ベンジルジメチルケタール、１−（４−イソプロピルフェニル）−２−ヒドロキシ−２−メチルプロパン−１−オン、４−（２−ヒドロキシエトキシ）フェニル−（２−ヒドロキシ−２−プロピル）ケトン、１−ヒドロキシシクロヘキシル−フェニルケトン、２−メチル−２−モルホリノ（４−チオメチルフェニル）プロパン−１−オン、２−ベンジル−２−ジメチルアミノ−１−（４−モルホリノフェニル）−ブタノンの如きアセトフェノン系；ベンゾイン、ベンゾインメチルエーテル、ベンゾインイソプロピルエーテルの如きベンゾイン類；２，４，６−トリメチルベンゾインジフェニルホスフィンオキシドの如きアシルホスフィンオキシド系；ベンジル、メチルフェニルグリオキシエステルなどが挙げられる。   Examples of the intramolecular bond cleavage type photopolymerization initiator include diethoxyacetophenone, 2-hydroxy-2-methyl-1-phenylpropan-1-one, benzyldimethyl ketal, 1- (4-isopropylphenyl) -2. -Hydroxy-2-methylpropan-1-one, 4- (2-hydroxyethoxy) phenyl- (2-hydroxy-2-propyl) ketone, 1-hydroxycyclohexyl-phenylketone, 2-methyl-2-morpholino (4 Acetophenones such as -thiomethylphenyl) propan-1-one, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -butanone; benzoins such as benzoin, benzoin methyl ether, benzoin isopropyl ether; 2 , 4,6-Trimethylbenzoindiphenyl Scan fins oxides such acylphosphine oxide of; benzyl, and methyl phenylglyoxylate ester.

一方、分子内水素引き抜き型の光重合開始剤としては、例えば、ベンゾフェノン、ｏ−ベンゾイル安息香酸メチル−４−フェニルベンゾフェノン、４，４′−ジクロロベンゾフェノン、ヒドロキシベンゾフェノン、４−ベンゾイル−４′−メチル−ジフェニルサルファイド、アクリル化ベンゾフェノン、３，３′，４，４′−テトラ（ｔ−ブチルペルオキシカルボニル）ベンゾフェノン、３，３′−ジメチル−４−メトキシベンゾフェノンの如きベンゾフェノン系；２−イソプロピルチオキサントン、２，４−ジメチルチオキサントン、２，４−ジエチルチオキサントン、２，４−ジクロロチオキサントンの如きチオキサントン系；ミヒラ−ケトン、４，４′−ジエチルアミノベンゾフェノンの如きアミノベンゾフェノン系；１０−ブチル−２−クロロアクリドン、２−エチルアンスラキノン、９，１０−フェナンスレンキノン、カンファーキノンなどが挙げられる。   On the other hand, as an intramolecular hydrogen abstraction type photopolymerization initiator, for example, benzophenone, methyl 4-phenylbenzophenone, o-benzoylbenzoate, 4,4'-dichlorobenzophenone, hydroxybenzophenone, 4-benzoyl-4'-methyl Benzophenones such as diphenyl sulfide, acrylated benzophenone, 3,3 ', 4,4'-tetra (t-butylperoxycarbonyl) benzophenone, 3,3'-dimethyl-4-methoxybenzophenone; 2-isopropylthioxanthone, 2 Thioxanthone series such as 1,4-dimethylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone; amino benzophenone series such as Michler-ketone, 4,4'-diethylaminobenzophenone; 10-butyl- - chloro acridone, 2-ethyl anthraquinone, 9,10-phenanthrenequinone, and a camphorquinone.

光重合開始剤を使用する場合の配合量は、活性光線硬化型組成物の０．０１〜１０．００質量％の範囲が好ましい。   The amount of the photopolymerization initiator used is preferably in the range of 0.01 to 10.00% by mass of the actinic ray curable composition.

また、ラジカル重合開始剤としては、特公昭５９−１２８１号、特公昭６１−９６２１号、及び特開昭６０−６０１０４号等の各公報記載のトリアジン誘導体、特開昭５９−１５０４号及び特開昭６１−２４３８０７号等の各公報に記載の有機過酸化物、特公昭４３−２３６８４号、特公昭４４−６４１３号、特公昭４４−６４１３号及び特公昭４７−１６０４号等の各公報並びに米国特許第３，５６７，４５３号明細書に記載のジアゾニウム化合物、米国特許第２，８４８，３２８号、同２，８５２，３７９号及び同２，９４０，８５３号各明細書に記載の有機アジド化合物、特公昭３６−２２０６２号、特公昭３７−１３１０９号、特公昭３８−１８０１５号、特公昭４５−９６１０号等の各公報に記載のオルト−キノンジアジド類、特公昭５５−３９１６２号、特開昭５９−１４０２３号等の各公報及び「マクロモレキュルス（Ｍａｃｒｏｍｏｌｅｃｕｌｅｓ）、第１０巻、第１３０７頁（１９７７年）に記載の各種オニウム化合物、特開昭５９−１４２２０５号公報に記載のアゾ化合物、特開平１−５４４４０号公報、ヨーロッパ特許第１０９，８５１号、ヨーロッパ特許第１２６，７１２号等の各明細書、「ジャーナル・オブ・イメージング・サイエンス」（Ｊ．Ｉｍａｇ．Ｓｃｉ．）」、第３０巻、第１７４頁（１９８６年）に記載の金属アレン錯体、特許第２７１１４９１号及び特許第２８０３４５４号明細書に記載の（オキソ）スルホニウム有機ホウ素錯体、特開昭６１−１５１１９７号公報に記載のチタノセン類、「コーディネーション・ケミストリー・レビュー（Ｃｏｏｒｄｉｎａｔｉｏｎ Ｃｈｅｍｉｓｔｒｙ Ｒｅｖｉｅｗ）」、第８４巻、８５〜２７７頁（１９８８年）及び特開平２−１８２７０１号公報に記載のルテニウム等の遷移金属を含有する遷移金属錯体、特開平３−２０９４７７号公報に記載の２，４，５−トリアリールイミダゾール二量体、四臭化炭素や特開昭５９−１０７３４４号公報記載の有機ハロゲン化合物等が挙げられる。これらの重合開始剤はラジカル重合可能なエチレン不飽和結合を有する化合物１００質量部に対して０．０１から１０質量部の範囲で含有されるのが好ましい。   Examples of radical polymerization initiators include triazine derivatives described in JP-B-59-1281, JP-B-61-9621, JP-A-60-60104, JP-A-59-1504, and JP-A-59-1504. Organic peroxides described in JP-A-61-243807, JP-B-43-23684, JP-B-44-6413, JP-B-44-6413, JP-B-47-1604, etc., and the United States Diazonium compounds described in Japanese Patent No. 3,567,453, organic azide compounds described in US Pat. Nos. 2,848,328, 2,852,379 and 2,940,853 Ortho-quinonediazides described in JP-B 36-22062, JP-B 37-13109, JP-B 38-18015, JP-B 45-9610, and the like. Various onium compounds described in JP-A-55-39162, JP-A-59-14023 and the like, and “Macromolecules, Vol. 10, page 1307 (1977); No. 142205, JP-A-1-54440, European Patent No. 109,851, European Patent No. 126,712, etc., “Journal of Imaging Science” (J. Imag. Sci.), Vol. 30, page 174 (1986), (oxo) sulfonium organoboron complexes described in Japanese Patent Nos. 2711491 and 2803454, 61-151197, titanocenes, “Coordination Chemistry Review” (Coordination Chemistry Review), Vol. 84, pages 85-277 (1988) and transition metal complexes containing transition metals such as ruthenium described in JP-A-2-182701, JP-A-3-209477 Examples include 2,4,5-triarylimidazole dimer, carbon tetrabromide, and organic halogen compounds described in JP-A-59-107344. These polymerization initiators are preferably contained in the range of 0.01 to 10 parts by mass with respect to 100 parts by mass of the compound having an ethylenically unsaturated bond capable of radical polymerization.

また、本発明のインクにおいては光酸発生剤も用いることができる。光酸発生剤としては、例えば、化学増幅型フォトレジストや光カチオン重合に利用される化合物が用いられる（有機エレクトロニクス材料研究会編、「イメージング用有機材料」、ぶんしん出版（１９９３年）、１８７〜１９２頁参照）。本発明に好適な化合物の例を以下に挙げる。   In the ink of the present invention, a photoacid generator can also be used. As the photoacid generator, for example, a chemically amplified photoresist or a compound used for photocationic polymerization is used (edited by Organic Electronics Materials Research Group, “Organic Materials for Imaging”, Bunshin Publishing (1993), 187. To page 192). Examples of compounds suitable for the present invention are listed below.

第１に、ジアゾニウム、アンモニウム、ヨードニウム、スルホニウム、ホスホニウムなどの芳香族オニウム化合物のＢ（Ｃ_６Ｆ_５）_４ ⁻、ＰＦ_６ ⁻、ＡｓＦ_６ ⁻、ＳｂＦ_６ ⁻、ＣＦ_３ＳＯ_３ ⁻塩を挙げることができる。本発明で用いることのできるオニウム化合物の具体的な例としては、特開２００５−２５５８２１号公報の段落番号０１３４に記載されている化合物を挙げることができる。 First, diazonium, ammonium, iodonium, sulfonium, aromatic onium compounds such as phosphonium ^{_{B (C 6 F 5) 4}} -, PF 6 -, AsF 6 -, SbF 6 -, CF 3 SO 3 - and salts be able to. Specific examples of the onium compound that can be used in the present invention include the compounds described in paragraph No. 0134 of JP-A No. 2005-255821.

第２に挙げられるスルホン酸を発生するスルホン化物の具体的な化合物としては、特開２００５−２５５８２１号公報の段落番号０１３６に記載されている化合物を挙げることができる。   Specific examples of the sulfonated compound that generates sulfonic acid include compounds described in paragraph No. 0136 of JP-A No. 2005-255821.

第３にハロゲン化水素を光発生するハロゲン化物も用いることができ、その具体的な化合物としては、特開２００５−２５５８２１号公報の段落番号０１３８に記載されている化合物を挙げることができる。   Thirdly, a halide that generates hydrogen halide can also be used, and specific examples thereof include compounds described in paragraph No. 0138 of JP-A No. 2005-255821.

第４に、特開２００５−２５５８２１号公報の段落番号０１４０に記載されている鉄アレン錯体を挙げることができる。   Fourthly, an iron allene complex described in paragraph No. 0140 of JP-A-2005-255821 can be mentioned.

本発明のインクでは、上記説明した以外に必要に応じて、出射安定性、プリントヘッドやインクカートリッジ適合性、保存安定性、画像保存性、その他の諸性能向上の目的に応じて、公知の各種添加剤、例えば、粘度調整剤、比抵抗調整剤、皮膜形成剤、紫外線吸収剤、酸化防止剤、退色防止剤、防バイ剤、防錆剤等を適宜選択して用いることができる。   In the ink of the present invention, in addition to the above description, various known types may be used depending on the purpose of improving the emission stability, compatibility with the print head and ink cartridge, storage stability, image storage stability, and other various performances. Additives such as viscosity modifiers, specific resistance modifiers, film forming agents, ultraviolet absorbers, antioxidants, fading inhibitors, antibacterial agents, and rust inhibitors can be appropriately selected and used.

本発明のインクによる画像形成に用いることのできる記録媒体としては、特に制限はなく、コピー等で使用されている普通紙、アート紙等の紙製の基材、通常の非コート紙、基紙の両面を樹脂等で被覆したコート紙などの他、所謂軟包装に用いられる各種非吸収性のプラスチック及びそのフィルムを用いることができ、各種プラスチックフィルムとしては、例えば、ＰＥＴフィルム、ＯＰＳフィルム、ＯＰＰフィルム、ＯＮＹフィルム、ＰＶＣフィルム、ＰＥフィルム、ＴＡＣフィルムを挙げることができる。また、金属類やガラス類にも適用可能である。   The recording medium that can be used for image formation with the ink of the present invention is not particularly limited, and is made of a paper base such as plain paper or art paper used for copying, ordinary uncoated paper, base paper, etc. In addition to coated paper with both sides coated with resin, various non-absorbable plastics and films used for so-called soft packaging can be used. Examples of various plastic films include PET film, OPS film, and OPP. Examples include films, ONY films, PVC films, PE films, and TAC films. Moreover, it is applicable also to metals and glass.

次いで、本発明のインクジェット記録方法について説明する。   Next, the ink jet recording method of the present invention will be described.

本発明のインクジェット記録方法において好ましい形態の１つは、本発明に係る一般式（Ｉ）で表される化合物を含むインクを用いて、記録ヘッド内でのインク温度と記録媒体の温度に差を付けた状態で画像形成を行うインクジェット記録方法であって、記録媒体上に着弾した本発明のインクを温度低下により増粘あるいはゲル化する固化手段を用いる方法であり、記録ヘッド内での活性光線硬化型インクジェットインクの温度が、記録媒体の温度より２５℃以上、１００℃未満高いことが特徴である。   One of the preferred forms in the ink jet recording method of the present invention is to use the ink containing the compound represented by the general formula (I) according to the present invention to make a difference between the ink temperature in the recording head and the temperature of the recording medium. An ink jet recording method in which an image is formed in a state where the ink is applied, and a method using a solidifying means for thickening or gelling the ink of the present invention landed on a recording medium by lowering the temperature. It is characterized in that the temperature of the curable inkjet ink is 25 ° C. or more and less than 100 ° C. higher than the temperature of the recording medium.

上記の増粘またはゲル化による固定化手段としては、例えば、インクジェット記録に用いるインクジェット記録装置を、室温等の比較的低温度環境下において所定の温度に加熱した後、記録媒体上に着弾させて、環境温度により自然冷却して固定化させる方法や、記録媒体を予め冷却したり、あるいは冷風を強制的に着弾部に吹き付けて固定化したりする方法等を適宜選択して用いることができるが、記録ヘッド内のインクを室内温度よりも高く加熱する方法が簡便であり好ましい。記録ヘッド内のインクを加熱する方法としては、記録ヘッドの内部または外部にヒーターを付けて直接または間接的にインクを加熱する方法、記録ヘッド駆動時に発生する発熱を利用する方法などを挙げることができる。   As the fixing means by the above thickening or gelling, for example, an inkjet recording apparatus used for inkjet recording is heated to a predetermined temperature in a relatively low temperature environment such as room temperature, and then landed on a recording medium. The method of natural cooling by the ambient temperature and fixing, the method of cooling the recording medium in advance, or the method of fixing by blowing cold air to the landing part can be appropriately selected and used. A method of heating the ink in the recording head higher than the room temperature is simple and preferable. Examples of the method for heating the ink in the recording head include a method for heating the ink directly or indirectly by attaching a heater inside or outside the recording head, a method for utilizing heat generated when the recording head is driven, and the like. it can.

また、本発明のインクジェット記録方法において好ましい他の形態は、本発明に係る一般式（Ｉ）で表される化合物を含むインクを用いて、記録ヘッド内でのインク温度と記録媒体の温度に２５℃以上、１００℃未満の温度差を付けた状態で画像形成を行うインクジェット記録方法であって、記録媒体上に着弾した該インクジェット用インクを、２つ以上の固定化手段を有し、且つ該固定化手段の少なくとも１つが上記で説明した増粘またはゲル化による固定化手段である方法である。更に２つ以上の固定化手段がゲル化による固定化手段と活性光線照射によりインクを硬化する固定化手段であることが好ましい。   In another preferred embodiment of the ink jet recording method of the present invention, the ink containing the compound represented by the general formula (I) according to the present invention is used and the ink temperature in the recording head and the temperature of the recording medium are 25. An inkjet recording method for forming an image with a temperature difference of not less than 100 ° C. and less than 100 ° C., the inkjet ink having landed on a recording medium having two or more fixing means, and In this method, at least one of the immobilization means is the immobilization means by thickening or gelation described above. Further, it is preferable that two or more immobilization means are an immobilization means by gelation and an immobilization means for curing ink by irradiation with actinic rays.

本発明のインクジェット記録方法においては、本発明に係る一般式（Ｉ）で表される化合物を含むインクを記録媒体上に出射して描画し、次いで、本発明に係る一般式（Ｉ）で表される化合物を含むインク液滴を増粘またはゲル化した後、紫外線あるいは電子線等の活性光線を照射してインクを硬化させる方法である。   In the inkjet recording method of the present invention, an ink containing a compound represented by the general formula (I) according to the present invention is drawn on a recording medium and then drawn, and then represented by the general formula (I) according to the present invention. In this method, the ink droplet containing the compound is thickened or gelled, and then the ink is cured by irradiation with an actinic ray such as an ultraviolet ray or an electron beam.

（インク着弾後の総インク膜厚）
本発明では、記録媒体上にインクが着弾し、活性光線を照射して硬化した後の総インク膜厚が２〜２５μｍであることが好ましい。なお、ここで「総インク膜厚」とは記録媒体に描画されたインクの膜厚の最大値を意味し、単色でも、それ以外の２色重ね（２次色）、３色重ね、４色重ね（白インクベース）のインクジェット記録方式で記録を行った場合でも総インク膜厚の意味するところは同様である。 (Total ink film thickness after ink landing)
In the present invention, the total ink film thickness after the ink has landed on the recording medium and cured by irradiation with actinic rays is preferably 2 to 25 μm. Here, “total ink film thickness” means the maximum value of the film thickness of the ink drawn on the recording medium, and even in a single color, other two colors are superimposed (secondary color), three colors are superimposed, four colors Even when recording is performed by the overlapping (white ink base) inkjet recording method, the meaning of the total ink film thickness is the same.

（インクの吐出条件）
インクの吐出条件としては、記録ヘッド及びインクを本発明のインクのゾルゲル相転移温度よりも１０℃以上、４０℃未満高い温度で加熱し、吐出することが吐出安定性及び画質向上の点で好ましい。インクの吐出温度をゾルゲル相転移温度よりも１０℃以上高くすることで、温度変動による記録ヘッド内におけるインクのゲル化を防ぐことができ、吐出不良を抑えることが可能となる。また、４０℃未満とすることで記録媒体に着弾後にインクがゾルゲル相転移温度に達するまでの時間を短くでき、ゲル化速度を高めることが可能となるため、結果として高い画像品質が得られる。 (Ink ejection conditions)
As the ink discharge conditions, it is preferable from the viewpoint of improving discharge stability and image quality that the recording head and the ink are heated at a temperature of 10 ° C. or more and less than 40 ° C. higher than the sol-gel phase transition temperature of the ink of the present invention. . By making the ink ejection temperature 10 ° C. or more higher than the sol-gel phase transition temperature, it is possible to prevent the ink from gelling in the recording head due to temperature fluctuations, and to suppress ejection defects. Further, by setting the temperature to less than 40 ° C., the time until the ink reaches the sol-gel phase transition temperature after landing on the recording medium can be shortened, and the gelation speed can be increased. As a result, high image quality can be obtained.

また、記録ヘッド内の活性光線硬化型インクジェットインクと記録媒体の温度差を２５℃以上とすることで、活性光線硬化型インクジェットインクのゾルゲル相転移温度と記録媒体の温度に十分な温度差を設けることができ、増粘あるいはゲル化の効果をより一層高めることができる。また、１００℃未満とすることで該インクが記録媒体に着弾した際にインクの熱が速やかに記録媒体に拡散し、インクが速やかに冷却されるため、増粘あるいはゲル化の効果をより一層高めることができる。   Further, by setting the temperature difference between the actinic ray curable inkjet ink in the recording head and the recording medium to 25 ° C. or more, a sufficient temperature difference is provided between the sol-gel phase transition temperature of the actinic ray curable inkjet ink and the temperature of the recording medium. And the effect of thickening or gelation can be further enhanced. In addition, when the temperature is less than 100 ° C., when the ink lands on the recording medium, the heat of the ink is quickly diffused to the recording medium, and the ink is quickly cooled. Can be increased.

本発明のインクは、温度変動による粘度変動幅が大きく、粘度変動はそのまま液滴サイズ、液滴出射速度に大きく影響を与え、画質劣化を起こすため、インク温度を上げながらその温度を所定の範囲内に保ち、その状態で出射することが好ましい。この所定の温度範囲としては、好ましくは設定温度±５℃、より好ましくは設定温度±２℃、更に好ましくは設定温度±１℃である。ここで言う設定温度とは、インクを出射する際のインクの温度として設定された基準の温度を言う。   The ink of the present invention has a large viscosity fluctuation range due to temperature fluctuation, and the viscosity fluctuation directly affects the droplet size and droplet ejection speed, causing image quality degradation. It is preferable to keep in and emit in that state. The predetermined temperature range is preferably set temperature ± 5 ° C., more preferably set temperature ± 2 ° C., and further preferably set temperature ± 1 ° C. The set temperature here refers to a reference temperature set as the temperature of ink when ink is ejected.

また、本発明では、記録ヘッドの各ノズルより吐出する液滴量が１〜１５ｐｌであることが好ましい。本来、高精細画像を形成するためには、液滴量がこの範囲であることが必要であるが、この液滴量で吐出する場合、前述した吐出安定性が特に厳しくなる。本発明によれば、インクの液滴量が１〜１５ｐｌのような小液滴量で吐出を行っても吐出安定性は向上し、高精細画像が安定して形成できる。   In the present invention, the amount of liquid droplets ejected from each nozzle of the recording head is preferably 1 to 15 pl. Originally, in order to form a high-definition image, it is necessary for the amount of droplets to be within this range, but when discharging with this amount of droplets, the above-described discharge stability becomes particularly severe. According to the present invention, even when ejection is performed with a small droplet amount such as 1 to 15 pl, the ejection stability is improved and a high-definition image can be stably formed.

（インク着弾後の光照射条件）
本発明のインクジェット記録方法においては、活性光線の照射条件として、インク着弾後１０秒以内に活性光線が照射されることが好ましく、より好ましくは０．００１〜５秒であり、更に好ましくは０．００１〜２秒である。高精細な画像を形成するためには、照射タイミングが出来るだけ早いことが重要な要件となる。 (Light irradiation conditions after ink landing)
In the ink jet recording method of the present invention, the actinic ray is preferably irradiated within 10 seconds after ink landing, more preferably 0.001 to 5 seconds, and still more preferably 0. 001 to 2 seconds. In order to form a high-definition image, it is an important requirement that the irradiation timing be as early as possible.

活性光線の照射方法として、その基本的な方法が特開昭６０−１３２７６７号公報に開示されている。これによると、記録ヘッドユニットの両側に光源を設け、シャトル方式で記録ヘッドと光源を走査する。照射は、インク着弾後、一定時間を置いて行われることになる。更に、駆動を伴わない別光源によって硬化を完了させる。米国特許第６，１４５，９７９号明細書では、照射方法として、光ファイバーを用いた方法や、コリメートされた光源を記録ヘッドユニット側面に設けた鏡面に当て、記録部へ紫外線を照射する方法が開示されている。本発明のインクジェット記録方法においては、これらのいずれの照射方法も用いることができる。   As a method for irradiating actinic rays, the basic method is disclosed in JP-A-60-132767. According to this, the light source is provided on both sides of the recording head unit, and the recording head and the light source are scanned by the shuttle method. Irradiation is performed after a certain period of time after ink landing. Further, the curing is completed by another light source that is not driven. In US Pat. No. 6,145,979, as an irradiation method, a method using an optical fiber or a method of irradiating a recording unit with ultraviolet rays by applying a collimated light source to a mirror surface provided on the side of the recording head unit is disclosed. Has been. Any of these irradiation methods can be used in the inkjet recording method of the present invention.

また、活性光線の照射を２段階に分け、まずインク着弾後０．００１〜２．０秒の間に前述の方法で活性光線を照射し、且つ全印字終了後、更に活性光線を照射する方法も好ましい態様の１つである。活性光線の照射を２段階に分けることで、よりインク硬化の際に起こる記録媒体の収縮を抑えることが可能となる。   Also, the method of irradiating actinic rays in two stages, first irradiating actinic rays by the above-described method within 0.001 to 2.0 seconds after ink landing, and further irradiating actinic rays after completion of all printing Is also a preferred embodiment. By dividing the irradiation of actinic rays into two stages, it is possible to further suppress the shrinkage of the recording medium that occurs during ink curing.

（電子線照射）
電子線の照射方法としては、例えば、スキャニング方式、カーテンビーム方式、ブロードビーム方式などがあるが、処理能力の観点からカーテンビーム方式が好ましい。 (Electron beam irradiation)
Examples of the electron beam irradiation method include a scanning method, a curtain beam method, and a broad beam method. The curtain beam method is preferable from the viewpoint of processing capability.

電子線照射の加速電圧は、３０〜２５０ｋＶの範囲に設定することにより硬化皮膜の形成が可能であるが、より低い被照射線量で同等な硬化性が得られる３０〜１００ｋＶに設定するのが好ましい。加速電圧が３０〜１００ｋＶの電子線を照射することにより、硬化阻害を生じやすい記録媒体表面に電子線が集中し、硬化性を向上させることができる。よって、高酸素濃度下での高硬化性を得るためには、３０〜１００ｋＶの加速電圧の電子線を照射することが好ましい。   The acceleration voltage of electron beam irradiation can be set to a range of 30 to 250 kV, and a cured film can be formed. However, it is preferable to set the acceleration voltage to 30 to 100 kV, which can obtain the same curability with a lower irradiation dose. . By irradiating an electron beam with an acceleration voltage of 30 to 100 kV, the electron beam concentrates on the surface of the recording medium where inhibition of curing tends to occur, and the curability can be improved. Therefore, in order to obtain high curability under a high oxygen concentration, it is preferable to irradiate an electron beam with an acceleration voltage of 30 to 100 kV.

また、電子線照射の加速電圧を３０〜１００ｋＶの範囲に設定した場合には、電子線の被照射線量を通常より低い値とし、高エネルギー効率による省エネルギー化と、印字速度の高速化による生産効率向と上を図ることも可能である。加速電圧が１００〜２５０ｋＶの通常の電子線照射では、電子線照射量としては３０〜１００ｋＧｙであることが好ましく、より好ましくは３０〜６０ｋＧｙである。なお、電子線照射量の測定は、例えば、厚さ４４．５μｍの線量測定フィルム（ＦＡＲＷＥＳＴ製ＲＡＤＩＡＣＨＲＯＭＩＣ ＦＩＬＭ ＦＷＴ−６０−００）にＣｏ６０のγ線を標準線源として照射し、フィルム着色による吸光度と線量との関係を求めた検量線を作成し、この検量線と吸光度により電子線照射線量を求めることができる。   In addition, when the acceleration voltage of electron beam irradiation is set in the range of 30 to 100 kV, the irradiation dose of the electron beam is set to a value lower than normal, energy saving by high energy efficiency, and production efficiency by increasing printing speed. It is also possible to plan upward and downward. In normal electron beam irradiation with an acceleration voltage of 100 to 250 kV, the electron beam irradiation amount is preferably 30 to 100 kGy, more preferably 30 to 60 kGy. In addition, the measurement of the electron beam irradiation amount is performed, for example, by irradiating a 44.5 μm-thick dose measurement film (RADIACHROMIC FILM FWT-60-00 manufactured by FARWEST) with Co60 γ rays as a standard radiation source, A calibration curve for determining the relationship with the dose can be prepared, and the electron beam irradiation dose can be determined from the calibration curve and the absorbance.

本発明で用いることのできる電子線照射手段としては、例えば、日新ハイボルテージ（株）製の「キュアトロンＥＢＣ−２００−２０−３０」、ＡＩＴ（株）製の「Ｍｉｎ−ＥＢ」等を挙げることができる。   Examples of electron beam irradiation means that can be used in the present invention include “Curetron EBC-200-20-30” manufactured by Nissin High Voltage Co., Ltd., “Min-EB” manufactured by AIT Co., Ltd., and the like. Can be mentioned.

本発明のインクジェット記録方法においては、１０００ｐｐｍ以下の酸素濃度雰囲気下で電子線を照射することが好ましく、より好ましくは５００ｐｐｍ以下である。本発明における１０００ｐｐｍ以下の酸素濃度とは、窒素やアルゴン等の不活性ガスによるイナーティングを行うことにより達成された濃度範囲を含んでいる。   In the ink jet recording method of the present invention, it is preferable to irradiate an electron beam under an oxygen concentration atmosphere of 1000 ppm or less, and more preferably 500 ppm or less. The oxygen concentration of 1000 ppm or less in the present invention includes a concentration range achieved by inerting with an inert gas such as nitrogen or argon.

（紫外線照射）
紫外線の光源としては、例えば、数１００Ｐａから１ＭＰａまでの動作圧力を有する低圧、中圧、高圧水銀ランプ、メタルハライドランプ等が用いられるが、光源の波長分布という観点で高圧水銀灯、メタルハライドランプが好ましく、メタルハライドランプがより好ましい。また、３００ｎｍ以下の波長光をカットするフィルターを設けることが好ましい。ランプの出力としては４００Ｗ〜３０ｋＷ、照度としては１０ｍＷ／ｃｍ^２〜１０ｋＷ／ｃｍ^２、照射エネルギーとしては０．１〜５００ｍＪ／ｃｍ^２が好ましく、１〜１００ｍＪ／ｃｍ^２がより好ましい。 (UV irradiation)
As the ultraviolet light source, for example, low pressure, medium pressure, high pressure mercury lamp, metal halide lamp and the like having an operating pressure of several hundred Pa to 1 MPa are used, but high pressure mercury lamp and metal halide lamp are preferable from the viewpoint of wavelength distribution of the light source, A metal halide lamp is more preferable. Moreover, it is preferable to provide a filter that cuts light having a wavelength of 300 nm or less. The output of the lamp ^{400W~30kW, 10mW / cm 2 ~10kW /} cm 2 as illuminance, preferably 0.1~500mJ / cm ² as irradiation energy, 1 to 100 mJ / cm ² is more preferable.

光源波長に３００ｎｍ以下の紫外線が含まれる場合や、照射エネルギーとして５００ｍＪ／ｃｍ^２を超える場合は、活性光線架橋性樹脂の母核、または共存させる各種添加剤紫外線により分解してしまい、本発明の効果を得られないだけでなく、分解物に由来する臭気などの問題を起こす可能性があるので好ましくない。 When the light source wavelength includes ultraviolet rays of 300 nm or less, or when the irradiation energy exceeds 500 mJ / cm ² , it is decomposed by the active nucleus of the actinic ray crosslinkable resin or various additive ultraviolet rays that coexist. Not only can the effect not be obtained, but there is a possibility of causing problems such as odor derived from the decomposition product, which is not preferable.

照射エネルギーが０．１ｍＪ／ｃｍ^２に満たない場合は架橋効率が不足し、本発明の効果が十分にえられない。 When the irradiation energy is less than 0.1 mJ / cm ² , the crosslinking efficiency is insufficient and the effect of the present invention cannot be obtained sufficiently.

紫外線照射の際の照度は０．１ｍＷ／ｃｍ^２〜１Ｗ／ｃｍ^２好ましい。照度が１Ｗ／ｃｍ^２を超える場合、塗膜の表面硬化性は向上するが、深部硬化性が低下し、表面のみ硬い膜が得られる。その場合は、膜の深度方向の硬さのバランスが崩れ、カールなどが起こり、好ましくない。照度が０．１ｍＷ／ｃｍ^２より低い場合は、膜中の散乱等により架橋が十分進まず、本発明の効果が得られないため好ましくない。 Illuminance at the time of ultraviolet irradiation is preferably 0.1 mW / cm ^{2 to 1} W / cm ² . When the illuminance exceeds 1 W / cm ² , the surface curability of the coating film is improved, but the deep curability is lowered, and a film having a hard surface only is obtained. In that case, the balance of hardness in the depth direction of the film is lost and curling occurs, which is not preferable. When the illuminance is lower than 0.1 mW / cm ^{2, the} crosslinking does not proceed sufficiently due to scattering in the film and the effect of the present invention cannot be obtained, which is not preferable.

同一積算光量（ｍＪ／ｃｍ^２）を与える場合、照度に好ましい範囲があることは、その光の透過率が変化することに起因する。紫外線の透過性により発生した架橋反応種の濃度分布が異なり、紫外線照度が高い場合、塗膜表層に高濃度の架橋反応種が発生し、塗膜表層に堅い緻密な膜が形成されてしまう。 When giving the same integrated light quantity (mJ / cm ² ), the preferable range of illuminance is due to the change in the light transmittance. When the concentration distribution of the cross-linking reactive species generated due to the ultraviolet light transmittance is different and the ultraviolet illuminance is high, a high concentration of the cross-linking reactive species is generated on the surface of the coating film, and a firm and dense film is formed on the surface of the coating film.

次いで、本発明のインクジェット記録方法で用いることのできるインクジェット記録装置（以下、単に記録装置と言う）について、紫外線照射方式の装置を一例として説明する。   Next, an ink jet recording apparatus (hereinafter simply referred to as a recording apparatus) that can be used in the ink jet recording method of the present invention will be described using an ultraviolet irradiation apparatus as an example.

以下、本発明で用いることのできる記録装置について、図面を適宜参照しながら説明する。なお、図面の記録装置はあくまでも本発明で好ましく用いることのできる記録装置の一態様であり、本発明はこの図面に限定されない。   Hereinafter, a recording apparatus that can be used in the present invention will be described with reference to the drawings as appropriate. Note that the recording apparatus shown in the drawings is merely an embodiment of the recording apparatus that can be preferably used in the present invention, and the present invention is not limited to this drawing.

図１は本発明で用いることのできるインクジェット記録装置の要部の構成を示す正面図である。記録装置１は、記録ヘッドキャリッジ２、記録ヘッド３、紫外線を照射する手段としての照射手段４、プラテン部５等を備えて構成される。この記録装置１は、記録媒体Ｐの下にプラテン部５が設置されている。プラテン部５は、紫外線を吸収する機能を有しており、記録媒体Ｐを通過してきた余分な紫外線を吸収する。その結果、高精細な画像を非常に安定に再現できる。   FIG. 1 is a front view showing a configuration of a main part of an ink jet recording apparatus that can be used in the present invention. The recording apparatus 1 includes a recording head carriage 2, a recording head 3, irradiation means 4 as means for irradiating ultraviolet rays, a platen unit 5, and the like. In the recording apparatus 1, the platen unit 5 is installed under the recording medium P. The platen unit 5 has a function of absorbing ultraviolet rays, and absorbs excess ultraviolet rays that have passed through the recording medium P. As a result, a high-definition image can be reproduced very stably.

記録媒体Ｐは、ガイド部材６に案内され、搬送手段（図示せず）の作動により、図１における手前から奥の方向に移動する。記録ヘッド走査手段（図示せず）は、記録ヘッドキャリッジ２を図１におけるＹ方向に往復移動させることにより、記録ヘッドキャリッジ２に保持された記録ヘッド３の走査を行う。   The recording medium P is guided by the guide member 6 and moves from the near side to the far side in FIG. 1 by the operation of the conveying means (not shown). The recording head scanning means (not shown) scans the recording head 3 held by the recording head carriage 2 by reciprocating the recording head carriage 2 in the Y direction in FIG.

記録ヘッドキャリッジ２は記録媒体Ｐの上側に設置され、記録媒体Ｐ上の画像印刷に用いる色の数に応じて後述する記録ヘッド３を複数個、吐出口（ノズル）を下側に配置して収納する。記録ヘッドキャリッジ２は、図１におけるＹ方向に往復自在な形態で記録装置１本体に対して設置されており、記録ヘッド走査手段の駆動により、図１におけるＹ方向に往復移動する。   The recording head carriage 2 is installed on the upper side of the recording medium P, and has a plurality of recording heads 3 to be described later and discharge ports (nozzles) on the lower side according to the number of colors used for image printing on the recording medium P. Store. The recording head carriage 2 is installed on the main body of the recording apparatus 1 in such a manner that it can reciprocate in the Y direction in FIG. 1, and reciprocates in the Y direction in FIG. 1 by driving the recording head scanning means.

なお、図１では記録ヘッドキャリッジ２がホワイト（Ｗ）、イエロー（Ｙ）、マゼンタ（Ｍ）、シアン（Ｃ）、ブラック（Ｋ）、ライトイエロー（Ｌｙ）、ライトマゼンタ（Ｌｍ）、ライトシアン（Ｌｃ）、ライトブラック（Ｌｋ）、ホワイト（Ｗ）用の記録ヘッド３を収納するものとして描図を行っているが、実施の際には記録ヘッドキャリッジ２に収納される記録ヘッド３の数やそれに収容されるインクの色は適宜決められるものである。   In FIG. 1, the recording head carriage 2 is white (W), yellow (Y), magenta (M), cyan (C), black (K), light yellow (Ly), light magenta (Lm), and light cyan (Lc). ), The drawing is carried out in such a way that the recording heads 3 for light black (Lk) and white (W) are accommodated. The color of the ink to be stored is determined as appropriate.

記録ヘッド３は、インク供給手段（図示せず）により供給された本発明のインクを、内部に複数個備えられた吐出手段（図示せず）の作動により、吐出口から記録媒体Ｐに向けて吐出する。記録ヘッド３により吐出されるインクは本発明に係るゲル化剤の他に、色材、重合性モノマー、開始剤等を含んで組成されており、記録媒体Ｐ上に着弾した後冷却されてゲル化し、次いで、この例では照射手段として、紫外線の照射を受けることで光重合開始剤が触媒として作用することに伴うモノマーの架橋、重合反応によって硬化する性質を有する。   The recording head 3 is directed from the discharge port toward the recording medium P by the operation of a plurality of discharge means (not shown) provided inside the ink of the present invention supplied by the ink supply means (not shown). Discharge. The ink ejected by the recording head 3 is composed of a colorant, a polymerizable monomer, an initiator, and the like in addition to the gelling agent according to the present invention. After landing on the recording medium P, the ink is cooled and gelled. Then, in this example, as an irradiation means, it has a property of being cured by crosslinking of a monomer and a polymerization reaction when the photopolymerization initiator acts as a catalyst by being irradiated with ultraviolet rays.

記録ヘッド３は記録媒体Ｐの幅方向の一端から記録ヘッド走査手段の駆動により、図１におけるＹ方向に記録媒体Ｐの他端まで移動するという走査の間に、記録媒体Ｐにおける一定の領域（着弾可能領域）に対して本発明のインクをインク滴として吐出し、該着弾可能領域にインク滴を着弾させる。   The recording head 3 moves from one end in the width direction of the recording medium P to the other end of the recording medium P in the Y direction in FIG. The ink of the present invention is ejected as ink droplets onto the landable region), and the ink droplets are landed on the landable region.

上記走査を適宜回数行い、１領域の着弾可能領域に向けて本発明のインクの吐出を行った後、搬送手段で記録媒体Ｐを図１における手前から奥方向に適宜移動させ、再び記録ヘッド走査手段による走査を行いながら、記録ヘッド３により上記着弾可能領域に対し、図１における奥方向に隣接した次の着弾可能領域に対して本発明のインクの吐出を行う。   The above scanning is performed as many times as necessary, and after the ink of the present invention is ejected toward one landable area, the recording medium P is appropriately moved from the front to the back in FIG. While performing scanning by the means, the recording head 3 discharges the ink of the present invention to the next landable area adjacent to the rearward direction in FIG.

上述の操作を繰り返し、記録ヘッド走査手段及び搬送手段と連動して記録ヘッド３から本発明のインクを吐出することにより、記録媒体Ｐ上に本発明のインクの集合体からなる画像が形成される。   By repeating the above operation and ejecting the ink of the present invention from the recording head 3 in conjunction with the recording head scanning means and the conveying means, an image composed of the ink aggregate of the present invention is formed on the recording medium P. .

照射手段４は特定の波長領域の紫外線を安定した露光エネルギーで発光する紫外線ランプ及び特定の波長の紫外線を透過するフィルターを備えて構成される。ここで、紫外線ランプとしては、水銀ランプ、メタルハライドランプ、エキシマーレーザー、紫外線レーザー、冷陰極管、熱陰極管、ブラックライト、ＬＥＤ（ｌｉｇｈｔ ｅｍｉｔｔｉｎｇ ｄｉｏｄｅ）等が適用可能であり、帯状のメタルハライドランプ、冷陰極管、熱陰極管、水銀ランプもしくはブラックライトが好ましい。特に波長２５４ｎｍの紫外線を発光する低圧水銀ランプ、熱陰極管、冷陰極管及び殺菌灯が滲み防止、ドット径制御を効率よく行うことができ好ましい。ブラックライトを照射手段４の活性光源に用いることで、ＵＶインクを硬化するための照射手段４を安価に作製することができる。   The irradiation unit 4 includes an ultraviolet lamp that emits ultraviolet light in a specific wavelength region with stable exposure energy and a filter that transmits ultraviolet light of a specific wavelength. Here, as the ultraviolet lamp, a mercury lamp, a metal halide lamp, an excimer laser, an ultraviolet laser, a cold cathode tube, a hot cathode tube, a black light, an LED (light emitting diode), and the like can be applied. A cathode tube, a hot cathode tube, a mercury lamp or black light is preferred. In particular, a low-pressure mercury lamp, a hot cathode tube, a cold cathode tube, and a germicidal lamp that emit ultraviolet light having a wavelength of 254 nm are preferable because they can prevent bleeding and efficiently control the dot diameter. By using black light as the active light source of the irradiation means 4, the irradiation means 4 for curing the UV ink can be produced at low cost.

照射手段４は、記録ヘッド３が記録ヘッド走査手段の駆動による１回の走査によってＵＶインクを吐出する着弾可能領域の内、記録装置１で設定できる最大のものとほぼ同じ形状か、着弾可能領域よりも大きな形状を有する。   The irradiating means 4 has the same shape as the maximum possible area that can be set by the recording apparatus 1 among the possible landing areas in which the recording head 3 ejects UV ink by one scan driven by the recording head scanning means. Has a larger shape.

照射手段４は、記録ヘッドキャリッジ２の両脇に、記録媒体Ｐに対してほぼ平行に固定して設置される。   The irradiation unit 4 is installed on both sides of the recording head carriage 2 so as to be fixed substantially parallel to the recording medium P.

前述したようにインク吐出部の照度を調整する手段としては、記録ヘッド３全体を遮光することはもちろんであるが、加えて照射手段４と記録媒体Ｐの距離ｈ１より、記録ヘッド３のインク吐出部３１と記録媒体Ｐとの距離ｈ２を大きくしたり（ｈ１＜ｈ２）、記録ヘッド３と照射手段４とを離間したり、両者間の距離を大きくしたりすることが有効である。また、記録ヘッド３と照射手段４の間を蛇腹構造７にすると更に好ましい。   As described above, as a means for adjusting the illuminance of the ink discharge portion, not only the entire recording head 3 is shielded, but in addition, the ink discharge of the recording head 3 is determined from the distance h1 between the irradiation means 4 and the recording medium P. It is effective to increase the distance h2 between the portion 31 and the recording medium P (h1 <h2), to separate the recording head 3 from the irradiation means 4, or to increase the distance between them. Further, it is more preferable that a bellows structure 7 is provided between the recording head 3 and the irradiation means 4.

ここで、照射手段４で照射される紫外線の波長は、照射手段４に備えられた紫外線ランプまたはフィルターを交換することで適宜変更することができる。   Here, the wavelength of the ultraviolet rays irradiated by the irradiation unit 4 can be changed as appropriate by exchanging the ultraviolet lamp or the filter provided in the irradiation unit 4.

本発明のインクは非常に吐出安定性が優れており、ラインヘッドタイプの記録装置を用いて画像形成する場合に特に有効である。   The ink of the present invention has very excellent ejection stability and is particularly effective when an image is formed using a line head type recording apparatus.

図２は、本発明で用いることのできるラインヘッドタイプのインクジェット記録装置の要部の構成の一例を示す上面図である。図１に示したものと同様の機能を有するものについては、図１と同様の符号を用いて説明する。   FIG. 2 is a top view illustrating an example of a configuration of a main part of a line head type ink jet recording apparatus that can be used in the present invention. Those having the same functions as those shown in FIG. 1 will be described using the same reference numerals as those in FIG.

図２で示したインクジェット記録装置は、ラインヘッド方式と呼ばれており、記録ヘッドキャリッジ２に、各色のインクジェット記録ヘッド３を、それぞれ記録媒体Ｐの全幅をカバーするようにして、複数個、固定配置されている。   The ink jet recording apparatus shown in FIG. 2 is called a line head system, and a plurality of ink jet recording heads 3 of each color are fixed to a recording head carriage 2 so as to cover the entire width of the recording medium P. Has been placed.

一方、記録ヘッドキャリッジ２の下流側には、同じく記録媒体Ｐの全幅をカバーするようにして、インク印字面の幅方向全域をカバーするように配置されている照射手段４が設けられている。照明手段４に用いられる紫外線ランプは、図１に記載したのと同様のものを用いることができる。   On the other hand, on the downstream side of the recording head carriage 2, there is provided irradiation means 4 arranged so as to cover the entire width of the ink printing surface so as to cover the entire width of the recording medium P. As the ultraviolet lamp used in the illuminating means 4, the same one as described in FIG. 1 can be used.

この図２に示したラインヘッド方式では、記録ヘッドキャリッジ２及び照射手段４は固定され、記録媒体Ｐのみが、搬送されて、インク出射及び硬化を行って画像形成を行う。   In the line head system shown in FIG. 2, the recording head carriage 2 and the irradiation means 4 are fixed, and only the recording medium P is transported, and ink is ejected and cured to form an image.

以下、実施例を挙げて本発明を具体的に説明するが、本発明はこれらに限定されるものではない。なお、実施例において「部」あるいは「％」の表示を用いるが、特に断りがない限り「質量部」あるいは「質量％」を表す。   EXAMPLES Hereinafter, the present invention will be specifically described with reference to examples, but the present invention is not limited thereto. In addition, although the display of "part" or "%" is used in an Example, unless otherwise indicated, "part by mass" or "mass%" is represented.

実施例１
《活性光線硬化型インクジェットインクの調製》
（顔料分散液１の調製）
顔料：ブラック顔料 Ｐｉｇｍｅｎｔ Ｂｌａｃｋ ７（三菱化学製＃５２）２０部
顔料分散剤：ＰＢ８２２（味の素ファインテクノ製） ９部
重合性化合物：オキセタン２２１（ＯＸＴ２２１ 東亞合成製） ７１部
上記を混合した後、ビーズミルを用いて練肉して、顔料分散液１を調製した。このブラック顔料を含む顔料分散液１の顔料粒子の体積平均粒子径は、ゼータサイザー１０００（マルバーン製）を用いて測定した結果、８０ｎｍであった。 Example 1
<< Preparation of actinic ray curable inkjet ink >>
(Preparation of pigment dispersion 1)
Pigment: Black pigment Pigment Black 7 (Mitsubishi Chemical # 52) 20 parts Pigment dispersant: PB822 (Ajinomoto Finetechno) 9 parts Polymerizable compound: Oxetane 221 (OXT221 Toagosei) 71 parts After mixing the above, bead mill Pigment dispersion 1 was prepared by kneading with The volume average particle diameter of the pigment particles of the pigment dispersion 1 containing the black pigment was 80 nm as a result of measurement using a Zetasizer 1000 (manufactured by Malvern).

〔インク１の調製〕
下記を順次混合し、８０℃に加熱して攪拌した後、得られた液体を加熱下、＃３０００の金属メッシュフィルターでろ過し、冷却してブラックインクであるインク１を調製した。 [Preparation of Ink 1]
The following were mixed in order, heated to 80 ° C. and stirred, and then the resulting liquid was heated and filtered through a # 3000 metal mesh filter and cooled to prepare ink 1 as a black ink.

重合性化合物：オキセタン２２１（ＯＸＴ２２１ 東亞合成製） ６０部
重合性化合物：セロキサイド２０２１Ｐ（Ｃ２０２１Ｐ ダイセル化学工業製）
２５部
光重合開始剤：ＵＶ１６９９２（ダウ・ケミカル製） ５部
顔料分散液１ １０部
〔インク２の調製〕
上記インク１の調製において、添加剤として１２−ヒドロキシステアリン酸（表１にはＨＳＡと表記、特開２００５−１２６５０７号公報記載のＯＧ−２）を表１に記載の量を添加し、加熱温度を９０℃に変更した以外は同様にして、インク２を調製した。 Polymerizable compound: Oxetane 221 (OXT221 manufactured by Toagosei Co., Ltd.) 60 parts Polymerizable compound: Celoxide 2021P (C2021P manufactured by Daicel Chemical Industries)
25 parts Photopolymerization initiator: UV16992 (manufactured by Dow Chemical) 5 parts Pigment dispersion 1 10 parts [Preparation of ink 2]
In the preparation of the ink 1, 12-hydroxystearic acid (indicated as HSA in Table 1, OG-2 described in JP-A-2005-126507) as an additive was added in the amount shown in Table 1, and the heating temperature Ink 2 was prepared in the same manner except that was changed to 90 ° C.

〔インク３、４の調製〕
上記インク１の調製において、添加剤としてＮ−ラウロイル−Ｌ−グルタミン酸−α，γ−ジブチルアミド（表１にはＬＧＢＡと表記、特開２００５−１２６５０７号公報記載のＯＧ−３）を表１に記載の量添加し、加熱温度を１３０℃に変更した以外は同様にして、インク３、４を調製した。 [Preparation of inks 3 and 4]
In the preparation of the ink 1, N-lauroyl-L-glutamic acid-α, γ-dibutyramide (indicated as LGBA in Table 1, OG-3 described in JP-A-2005-126507) as an additive is shown in Table 1. Inks 3 and 4 were prepared in the same manner except that the indicated amount was added and the heating temperature was changed to 130 ° C.

〔インク５〜１４の調製〕
上記インク１の調製において、各種添加剤及び添加量を表１に記載のように例示化合物Ｉ、II及びIVに変更し、加熱温度を１３０℃に変更した以外は同様にして、インク番号５〜１４を調製した。 [Preparation of inks 5 to 14]
In the preparation of the ink 1, various additives and addition amounts were changed to Exemplified Compounds I, II and IV as shown in Table 1, and the heating temperature was changed to 130 ° C. 14 was prepared.

なお、表１に記載のＯＸＴ２２１はオキサタン化合物、Ｃ２０２１Ｐはエポキシ化合物である。   In addition, OXT221 of Table 1 is an oxatan compound, and C2021P is an epoxy compound.

（顔料分散液２の調製）
顔料：ブラック顔料 Ｐｉｇｍｅｎｔ Ｂｌａｃｋ ７（三菱化学製＃５２）２０部
顔料分散剤：ＰＢ８２２（味の素ファインテクノ製） ９部
重合性化合物：テトラエチレングリコールジアクリレート（ＴＥＧＤＡ） ７１部
上記を混合した後、ビーズミルを用いて練肉して、顔料分散液２を調製した。 (Preparation of pigment dispersion 2)
Pigment: Black pigment Pigment Black 7 (Mitsubishi Chemical # 52) 20 parts Pigment dispersant: PB822 (Ajinomoto Finetechno) 9 parts Polymerizable compound: Tetraethylene glycol diacrylate (TEGDA) 71 parts After mixing the above, bead mill Pigment dispersion 2 was prepared by kneading with

〔インク１５の調製〕
下記を順次混合し、８０℃に加熱して攪拌した後、得られた液体を加熱下、＃３０００の金属メッシュフィルターでろ過し、冷却してブラックインクであるインク番号１６を調製した。 [Preparation of Ink 15]
The following were sequentially mixed, heated to 80 ° C. and stirred, and then the obtained liquid was filtered with a # 3000 metal mesh filter under heating and cooled to prepare ink number 16 as a black ink.

重合性化合物：テトラエチレングリコールジアクリレート（ＴＥＧＤＡ） ３０部
重合性化合物：ラウリルアクリレート（ＲＡ） ３０部
重合性化合物：ＮＫエステル（Ａ−４００ 新中村化学工業製） ２５部
光重合開始剤：ＩＲＧＡＣＵＲＥ９０７（Ｉ−９０７ チバ・ジャパン製） ５部
顔料分散液２ １０部
〔インク１６、１７の調製〕
上記インク１５の調製において、各種添加剤及び添加量を表２に記載のように例示化合物Ｉ及びIVに変更し、加熱温度を１３０℃に変更した以外は同様にして、インク１６、１７を調製した。 Polymerizable compound: Tetraethylene glycol diacrylate (TEGDA) 30 parts Polymerizable compound: Lauryl acrylate (RA) 30 parts Polymerizable compound: NK ester (A-400 manufactured by Shin-Nakamura Chemical Co., Ltd.) 25 parts Photopolymerization initiator: IRGACURE907 ( I-907 manufactured by Ciba Japan) 5 parts Pigment dispersion 2 10 parts [Preparation of inks 16 and 17]
In the preparation of the ink 15, inks 16 and 17 were prepared in the same manner except that various additives and addition amounts were changed to Exemplified Compounds I and IV as shown in Table 2 and the heating temperature was changed to 130 ° C. did.

《インクの各特性値の測定》
以上により調製したインク１〜１７について、以下の方法により相転移温度の測定を行った。得られた結果を表１、２に示す。 <Measurement of each characteristic value of ink>
About the inks 1-17 prepared by the above, the phase transition temperature was measured with the following method. The obtained results are shown in Tables 1 and 2.

〔相転移温度の測定〕
融点測定機（アズワン製 ＡＴＭ−０１）にゲル状の各インクの試験片を置き、昇温速度５℃／分以下で加熱し、試験片が溶融した温度を測定し、この操作を３回繰り返して平均値を求め、その平均値の小数点第一位を四捨五入して、これをインクの相転移温度とした。 (Measurement of phase transition temperature)
Place a test piece of each gel-like ink on a melting point measuring machine (ATM1 ATM-01), heat at a heating rate of 5 ° C./min or less, measure the temperature at which the test piece melts, and repeat this operation three times. The average value was obtained, and the first decimal place was rounded off to obtain the ink phase transition temperature.

《インクジェット画像の形成》
ピエゾ型インクジェットノズルを備えたラインヘッド方式のインクジェット記録装置に、上記調製した各インクを装填し、ＰＰＣ用紙（Ｊ ＰＡＰＥＲ コニカミノルタビジネスソリューションズ製）、印刷用アート紙（ＳＡ金藤 王子製紙製）、印刷用キャストコート紙（ミラーコート・ゴールド 王子製紙製）、及び印刷用コート紙（ＯＫマットコートグリーン１００ 王子製紙製）に、４、５、６ポイントのＭＳ明朝体で文字「口、四、日、回、因、困、固、国、目、図、國」の文字、黒ベタ画像、及び画素を３６０ｄｐｉ間隔で配置したドット径測定用画像を印字して画像１〜１７を得た。 << Inkjet image formation >>
Each of the inks prepared above is loaded into a line head type ink jet recording apparatus equipped with a piezo type ink jet nozzle, and PPC paper (manufactured by J PAPER Konica Minolta Business Solutions), art paper for printing (manufactured by SA Kanou Oji Paper), printing Cast coated paper (mirror coated gold, made by Oji Paper) and printing coated paper (OK mat coated green 100, made by Oji Paper) with the characters “Mouth, Four, Day” , Times, cause, trouble, solid, country, eyes, figure, country ", black solid images, and dot diameter measurement images in which pixels are arranged at 360 dpi intervals to obtain images 1-17.

インク供給系は、インクタンク、供給パイプ、記録ヘッド直前の前室インクタンク、フィルター付き配管、ピエゾヘッドからなり、前室タンクから記録ヘッド部分まで断熱してインクの相転移温度＋２０℃に加温した。また、ピエゾヘッドもヒーターを内蔵させ、記録ヘッド内のインク温度を相転移温度＋２０℃に加温した。また、ゲル化を生じないインクについては、一律８０℃にインクを加熱した。ピエゾヘッドはノズル径２５μｍ、ノズル数２５６ノズル（１２８ノズル×２列、千鳥配列、１列のノズルピッチ３６０ｄｐｉ）で、各々１滴の液滴量が４ｐｌとなる条件で、液滴速度約８ｍ／ｓｅｃで出射させて、１４４０ｄｐｉ×１４４０ｄｐｉの記録解像度で印字した。各記録媒体は室温（２５℃）とした。   The ink supply system consists of an ink tank, a supply pipe, a front chamber ink tank immediately before the print head, a pipe with a filter, and a piezo head. The ink is insulated from the front chamber tank to the print head and heated to the ink phase transition temperature + 20 ° C did. The piezo head also has a built-in heater, and the ink temperature in the recording head is heated to the phase transition temperature + 20 ° C. For the ink that does not cause gelation, the ink was uniformly heated to 80 ° C. The piezo head has a nozzle diameter of 25 μm, 256 nozzles (128 nozzles × 2 rows, staggered arrangement, 1 row nozzle pitch of 360 dpi), and a droplet velocity of about 8 m / droplet under the condition that the amount of each droplet is 4 pl. It was emitted in sec and printed with a recording resolution of 1440 dpi × 1440 dpi. Each recording medium was at room temperature (25 ° C.).

各インクが着弾した後、キャリッジ上部に配置したランプユニットにより、インクが着弾した０．５秒後に、高圧水銀ランプＶＺｅｒｏ０８５（ＩＮＴＥＧＲＡＴＩＯＮ ＴＥＣＨＮＯＬＯＧＹ製）により、１４０Ｗ／ｃｍ^２のエネルギー密度、照度２０ｍＪ／ｃｍ^２（積算光量）で紫外線を照射してインクを硬化した。なお、照射光源の照度は、岩崎電機製のＵＶＰＦ−Ａ１を用いて２５４ｎｍの積算照度を測定して表示した。また、上記の画像形成は２５℃、５５％ＲＨの環境下で行った。なお、本発明で言うｄｐｉとは、２．５４ｃｍ当たりのドット数を表す。 After each ink has landed, 0.5 seconds after the ink has landed by a lamp unit disposed on the upper part of the carriage, a high-pressure mercury lamp VZero085 (manufactured by INTEGRATION TECHNOLOGY) has an energy density of 140 W / cm ² and an illuminance of 20 mJ / cm ^2. The ink was cured by irradiating with ultraviolet rays at (integrated light amount). The illuminance of the irradiation light source was displayed by measuring the integrated illuminance of 254 nm using UVPF-A1 manufactured by Iwasaki Electric. The above image formation was performed in an environment of 25 ° C. and 55% RH. In the present invention, dpi refers to the number of dots per 2.54 cm.

《形成画像の評価》
上記作成した画像１〜１７について、以下の方法に従って、普通紙裏抜け耐性、文字品質、ドット径ばらつき、ＵＶ硬化性、インクチクソ性、インク保存性及び出射安定性の評価を行った。 <Evaluation of formed image>
The images 1 to 17 created above were evaluated in terms of plain paper back-through resistance, character quality, dot diameter variation, UV curability, ink thixotropy, ink storage stability and emission stability according to the following methods.

〔普通紙裏抜け耐性の評価〕
上記方法により、ＰＰＣ用紙（Ｊ ＰＡＰＥＲ コニカミノルタビジネスソリューションズ製）上に作成した黒ベタ画像部の裏面濃度を、光学濃度計（Ｘ−Ｒｉｔｅ製９３８分光濃度計）を用いて測定した、また同紙の非記録部の濃度も同様に測定した。次いで、（黒ベタ画像部の裏面濃度）−（非画像部の濃度）を求め、下記の評価基準に従って裏抜け耐性の評価を行った。 [Evaluation of resistance to slipping out of plain paper]
By the above method, the density of the back surface of the black solid image portion prepared on PPC paper (manufactured by JP PAPER Konica Minolta Business Solutions) was measured using an optical densitometer (938 spectral densitometer made by X-Rite). The density of the non-recorded part was measured in the same manner. Next, (the density of the back surface of the black solid image portion) − (the density of the non-image portion) was determined, and the strike through resistance was evaluated according to the following evaluation criteria.

◎：濃度差が０．０５ 未満である
○：濃度差が０．０５ 以上、０．０８未満である
△：濃度差が０．０８ 以上、０．１２未満である
×：濃度差が０．１２ 以上である。 A: Density difference is less than 0.05 O: Density difference is 0.05 or more and less than 0.08 Δ: Density difference is 0.08 or more and less than 0.12 ×: Density difference is 0.00. 12 or more.

〔文字品質の評価〕
上記方法により、印刷用アート紙（ＳＡ金藤 王子製紙製）に対して解像度１４００ｄｐｉ×１４４０ｄｐｉで、３ポイント、４ポイント及び５ポイントのＭＳ明朝体で漢字「口、四、日、回、因、困、固、国、目、図、國」の文字を印字し、印字した文字画像を目視観察し、下記の評価基準に従って文字品質の評価を行った。 [Evaluation of character quality]
According to the above method, the kanji characters “mouth, four, day, times, cause, with a resolution of 1400 dpi × 1440 dpi and 3 points, 4 points and 5 points of MS Mincho with a resolution of 1400 dpi × 1440 dpi for art paper for printing (made by SA Kinfuji Oji Paper) The characters “Kan, Tsuki, Koku, Koku, Koku, Kōchi, Figu, Kuni” were printed, the printed character images were visually observed, and the character quality was evaluated according to the following evaluation criteria.

◎：４ポイントの文字全てが、細部にまで明瞭に記録されている
○：４ポイントの文字は一部しか判読できないが、５ポイントの文字全てが判読可能である
△：４、５ポイントの文字は一部しか判読できないが、６ポイントの文字全てが判読可能である
×：６ポイントの文字の中にも判読できないものがある。 ◎: All four-point characters are clearly recorded in detail ○: Four-point characters are readable only partially, but all five-point characters are readable △: 4, 5-point characters Can be read only partially, but all 6-point characters can be read. ×: Some 6-point characters cannot be read.

〔ドット径ばらつきの評価〕
上記方法により、アート紙（ＳＡ金藤 王子製紙製）、キャストコート紙（ミラーコート・ゴールド 王子製紙製）、及びコート紙（ＯＫマットコートグリーン１００ 王子製紙製）の三種類の用紙に、画素を３６０ｄｐｉ間隔で配置したドット径測定用画像を印字して、光学顕微鏡（ＫＥＹＥＮＣＥ製 ＶＨＸ−５００）を用いて各種用紙のドット径を２０点ずつ測定し、平均ドット径を求めた。次いで下記により計算されるドット径ばらつき指標を用いてドット径ばらつきを評価した。 [Evaluation of dot diameter variation]
According to the above method, the pixel is set to 360 dpi on three types of paper, art paper (SA Kinfuji Oji Paper), cast coated paper (Mirror Coat Gold Oji Paper), and coated paper (OK Matte Coat Green 100, Oji Paper). The dot diameter measurement images arranged at intervals were printed, and the dot diameters of various papers were measured 20 points at a time using an optical microscope (VHX-500 manufactured by KEYENCE) to obtain the average dot diameter. Next, the dot diameter variation was evaluated using the dot diameter variation index calculated as follows.

ドット径ばらつき指標＝（最も平均ドット径の大きい用紙の平均ドット径）／（最も平均ドット径の小さい用紙の平均ドット径）
◎：ドット径ばらつき指標が１．００以上１．１５未満である
○：ドット径ばらつき指標が１．１５以上１．３０未満である
△：ドット径ばらつき指標が１．３０以上１．５０未満である
×：ドット径ばらつき指標が１．５０以上である。 Dot diameter variation index = (average dot diameter of paper having the largest average dot diameter) / (average dot diameter of paper having the smallest average dot diameter)
A: The dot diameter variation index is from 1.00 to less than 1.15. O: The dot diameter variation index is from 1.15 to less than 1.30. Δ: The dot diameter variation index is from 1.30 to less than 1.50. Yes: The dot diameter variation index is 1.50 or more.

〔紫外線硬化性の評価〕
上記アート紙に形成したベタ画像上に、セロテープ（登録商標）を貼り付けた後、垂直方法に剥離した時の画像状態を目視観察し、下記のように判定した。 [Evaluation of UV curing]
After the cellotape (registered trademark) was pasted on the solid image formed on the art paper, the image state when peeled off by the vertical method was visually observed and judged as follows.

◎：画像の剥離は認められないし、画像の表面性にも変化がない
○：画像の剥離は認められないが、画像の少なくとも一部に曇りが見られる
△：画像の端などに僅かに剥離が認められた
×：明らかに画像の剥離が認められた。 A: Image peeling is not observed, and the surface property of the image is not changed. ○: Image peeling is not observed, but at least part of the image is cloudy. Δ: Slight peeling at the edge of the image. X: Image peeling was clearly observed.

《インクの特性評価》
〔インクチクソ性の評価〕
インク１〜１７を粘弾性測定装置（ＵＤＳ−３００；ＰａａｒＰｈｙｓｉｃａ製）を用いて、シェアレート１ｓｅｃ及び１０００ｓｅｃでの粘度を測定した。測定時のインク温度は、ゲル化するインクについては相転移温度＋２０℃とし、ゲル化しないインクについては一律８０℃とした。次いで、下式により計算されるチクソ指標を用いてインクのチクソ性を判定した。 <Evaluation of ink characteristics>
[Evaluation of ink thixotropy]
The viscoelasticity measuring device (UDS-300; manufactured by Paar Physica) was used to measure the viscosity of the inks 1 to 17 at a share rate of 1 sec and 1000 sec. The ink temperature at the time of measurement was set to the phase transition temperature + 20 ° C. for the ink that gels, and uniformly 80 ° C. for the ink that does not gel. Next, the thixotropy of the ink was determined using the thixo index calculated by the following equation.

チクソ指標＝（シェアレート１ｓｅｃでの粘度）／（シェアレート１０００ｓｅｃでの粘度）
◎：チクソ指標が０．９８以上、１．０２未満である
○：チクソ指標が０．９０以上、０．９８未満、あるいは１．０２以上、１．１０未満である
△：チクソ指標が０．７５以上、０．９０未満、あるいは１．１０以上、１．２５未満である
×：チクソ指標が０．７５未満あるいは１．２５以上である。 Thixo index = (viscosity at 1 sec share rate) / (viscosity at 1000 sec share rate)
A: The thixo index is 0.98 or more and less than 1.02. B: The thixo index is 0.90 or more and less than 0.98, or 1.02 or more and less than 1.10. Δ: The thixo index is 0.00. 75 or more, less than 0.90, or 1.10 or more, and less than 1.25. X: The thixo index is less than 0.75 or 1.25 or more.

〔インク保存性の評価〕
インク１〜１７をガラス製のサンプル瓶に入れて密栓し、０℃と２３℃の環境下で各々１４日間保存した。保存終了後、０℃で保存したものは室温に戻して、２つのインク状態を比較観察し、下記の基準に従ってインク保存性を評価した。 [Evaluation of ink storage stability]
Inks 1 to 17 were put in glass sample bottles, sealed, and stored at 0 ° C. and 23 ° C. for 14 days. After storage, the one stored at 0 ° C. was returned to room temperature, the two ink states were compared and observed, and the ink storage stability was evaluated according to the following criteria.

◎：２種のインクに全く差異は認められない
○：０℃保存したインクの表面に、僅かに分離した液体が認められる
△：０℃保存したインク全体に、僅かに分離が見られる
×：０℃保存したインク全体に、分離が見られる。 A: No difference is observed between the two inks. O: A slightly separated liquid is observed on the surface of the ink stored at 0.degree. C. A: A slight separation is observed in the whole ink stored at 0.degree. C .: Separation is observed throughout the ink stored at 0 ° C.

〔出射安定性の評価〕
上記調製した各インクを搭載したプリンターを、１サイクルが１２時間で１０〜４０℃の温度範囲で変化させ、これを３サイクル繰り返した後、画像出射を行い、ノズル欠及び出射曲がりの有無について目視観察を行い、下記の基準に則り、出射安定性の評価を行った。 [Evaluation of output stability]
The printer equipped with each of the inks prepared above was changed in a temperature range of 10 to 40 ° C. in 12 hours, and after repeating this for 3 cycles, the image was emitted and visually checked for the presence of nozzle shortage and emission bending. Observation was performed, and emission stability was evaluated according to the following criteria.

◎：ノズル欠の発生が全く認められなかった
○：全ノズル２５６中、１〜６個のノズルで出射方向の曲がりが認められた
△：全ノズル２５６中、１〜２個のノズルで出射不良が認められた
×：全ノズル２５６中、３個以上のノズルで出射不良が認められた。 ◎: No nozzle missing was found. ○: Out of all nozzles 256, 1 to 6 nozzles were bent in the emitting direction. △: Out of all nozzles 256, 1 to 2 nozzles were poorly emitting. X: Out of all the nozzles 256, 3 or more nozzles were found to have poor emission.

以上により得られた結果を、表３に示す。   The results obtained as described above are shown in Table 3.

表３の結果より明らかなように、本発明に係る一般式（Ｉ）で表される化合物を含有する本発明の活性光線硬化型インクジェットインクは、比較例に対し、形成した画像の文字品質と耐裏抜け性に優れ、更にインクとしてチクソ性が殆どなく、出射安定性、保存安定性が良好で、加えて形成した画像の紫外線硬化性に優れていることが分かる。   As is clear from the results in Table 3, the actinic ray curable inkjet ink of the present invention containing the compound represented by the general formula (I) according to the present invention has the character quality of the formed image as compared with the comparative example. It can be seen that the film has excellent anti-through-through resistance, has almost no thixotropy as an ink, has good emission stability and storage stability, and is excellent in ultraviolet curability of the formed image.

実施例２
実施例１のラインヘッド方式のインクジェットプリンターを用い、ラインヘッドプリンターに実施例１のインク２及びインク１０を詰め、記録ヘッド及び記録ヘッド内のインクの温度と記録媒体の温度を表４に記載の温度とした以外は実施例１と同様にして、ＰＰＣ用紙（Ｊ ＰＡＰＥＲ コニカミノルタビジネスソリューションズ製）及びアート紙（ＳＡ金藤 王子製紙製）及び印刷用キャストコート紙（ミラーコート・ゴールド 王子製紙製）、及び印刷用コート紙（ＯＫマットコートグリーン１００ 王子製紙製）に画像１８〜２４をプリントし、実施例１に記載の方法と同様にして、文字品質の評価、ドット径ばらつきの評価、出射安定性の評価を行った。得られた結果を表４に示す。 Example 2
Using the line head type ink jet printer of Example 1, the line head printer was filled with ink 2 and ink 10 of Example 1, and the temperature of the recording head and the ink in the recording head and the temperature of the recording medium are shown in Table 4. PPC paper (manufactured by J PAPER Konica Minolta Business Solutions) and art paper (manufactured by SA Kinfuji Oji Paper) and cast coated paper for printing (made by Mirror Coat Gold Oji Paper), except for the temperature, Images 18 to 24 were printed on coated paper for printing (OK mat coated green 100 made by Oji Paper Co., Ltd.), and in the same manner as described in Example 1, evaluation of character quality, evaluation of dot diameter variation, emission stability Was evaluated. Table 4 shows the obtained results.

表４の結果より明らかなように、本発明の活性光線硬化型インクジェットインクは比較例に対し、形成した画像の文字品質が良好で、ドット径ばらつきが少なく、更に出射安定性に優れていることが分かる。更に記録ヘッドと記録媒体の加熱温度を本発明の好ましい形態に係るよう調整することで、より良好な文字品質が得られ、ドット径ばらつきが少なく、優れた出射安定性が得られることが分かる。   As is clear from the results in Table 4, the actinic radiation curable ink-jet ink of the present invention has better character quality of the formed image, less variation in dot diameter, and better emission stability than the comparative example. I understand. Furthermore, it can be seen that by adjusting the heating temperature of the recording head and the recording medium so as to be according to the preferred embodiment of the present invention, better character quality can be obtained, dot diameter variation is small, and excellent emission stability can be obtained.

実施例３
《顔料分散液の調製》
〔イエロー顔料分散液１の調製〕
顔料：イエロー顔料（Ｎｏｖｏｐｅｒｍ Ｐ−ＨＧ クラリアント製） １５部
顔料分散剤：ＰＢ８２２（味の素ファインテクノ製） ５部
オキセタン化合物（ＯＸＴ２２１ 東亞合成製） ８０部
上記を混合した後、ビーズミルを用いて練肉して、イエロー顔料分散液１を調製した。このイエロー顔料分散液１の顔料粒子の体積平均粒子径は、ゼータサイザー１０００（マルバーン製）を用いて測定した結果、１２０ｎｍであった。 Example 3
<< Preparation of pigment dispersion >>
[Preparation of Yellow Pigment Dispersion 1]
Pigment: Yellow pigment (manufactured by Novoperm P-HG Clariant) 15 parts Pigment dispersant: PB822 (manufactured by Ajinomoto Fine Techno) 5 parts Oxetane compound (manufactured by OXT221 Toagosei Co., Ltd.) 80 parts After mixing the above, kneading using a bead mill A yellow pigment dispersion 1 was prepared. The volume average particle diameter of the pigment particles of this yellow pigment dispersion 1 was 120 nm as a result of measurement using a Zetasizer 1000 (manufactured by Malvern).

〔マゼンタ顔料分散液１の調製〕
顔料：マゼンタ顔料（Ｈｏｓｔａｐｅｒｍ Ｐｉｎｋ Ｅ クラリアント製）１５部
顔料分散剤：ＰＢ８２２（味の素ファインテクノ製） ５部
オキセタン化合物（ＯＸＴ２２１ 東亞合成製） ８０部
上記を混合した後、ビーズミルを用いて練肉して、マゼンタ顔料分散液１を調製した。このマゼンタ顔料分散液１の顔料粒子の体積平均粒子径は、ゼータサイザー１０００（マルバーン製）を用いて測定した結果、１００ｎｍであった。 [Preparation of magenta pigment dispersion 1]
Pigment: Magenta pigment (Hostaperm Pink E, Clariant) 15 parts Pigment dispersant: PB822 (Ajinomoto Fine Techno) 5 parts Oxetane compound (OXT221, manufactured by Toagosei Co., Ltd.) 80 parts A magenta pigment dispersion 1 was prepared. The volume average particle diameter of the pigment particles of this magenta pigment dispersion 1 was 100 nm as a result of measurement using a Zetasizer 1000 (manufactured by Malvern).

〔シアン顔料分散液１の調製〕
顔料：シアン顔料（Ｈｏｓｔａｐｅｒｍ Ｂｌｕｅ Ｂ２Ｇ クラリアント製）
２０部
顔料分散剤：ＰＢ８２２（味の素ファインテクノ製） ５部
オキセタン化合物（ＯＸＴ２２１ 東亞合成製） ７５部
上記を混合した後、ビーズミルを用いて練肉して、シアン顔料分散液１を調製した。このシアン顔料分散液１の顔料粒子の体積平均粒子径は、ゼータサイザー１０００（マルバーン製）を用いて測定した結果、８５ｎｍであった。 [Preparation of Cyan Pigment Dispersion 1]
Pigment: Cyan pigment (manufactured by Hostaperm Blue B2G Clariant)
20 parts Pigment dispersant: PB822 (manufactured by Ajinomoto Finetechno Co., Ltd.) 5 parts Oxetane compound (OXT221 manufactured by Toagosei Co., Ltd.) 75 parts After mixing the above, the mixture was kneaded using a bead mill to prepare cyan pigment dispersion 1. The volume average particle diameter of the pigment particles of the cyan pigment dispersion 1 was 85 nm as a result of measurement using a Zetasizer 1000 (manufactured by Malvern).

〔ブラック顔料分散液１〕
実施例１に記載のブラック顔料分散液１を用いた。 [Black pigment dispersion 1]
The black pigment dispersion 1 described in Example 1 was used.

《インクセットの調製》
下記の各色インクからなるインクセットを調製した。 <Preparation of ink set>
An ink set comprising the following color inks was prepared.

〔イエローインクの調製〕
下記を順次混合し、１３０℃に加熱、攪拌した後、得られた液体を加熱下、＃３０００の金属メッシュフィルターでろ過した後、冷却して、イエローインクを調製した。 [Preparation of yellow ink]
The following were mixed in order, heated to 130 ° C. and stirred, and the resulting liquid was filtered with a # 3000 metal mesh filter under heating and then cooled to prepare a yellow ink.

重合性化合物：オキセタン２２１（ＯＸＴ２２１ 東亞合成製） ３５部
重合性化合物：セロキサイド２０２１Ｐ（Ｃ２０２１Ｐ ダイセル化学工業製）
２０部
光重合開始剤：ＵＶ１６９９２（ダウ・ケミカル製） ５部
イエロー顔料分散液１ ３０部
例示化合物Ｉ １０部
〔マゼンタインクの調製〕
下記を順次混合し、１３０℃に加熱、攪拌した後、得られた液体を加熱下、＃３０００の金属メッシュフィルターでろ過した後冷却して、マゼンタインクを調製した。 Polymerizable compound: Oxetane 221 (OXT221 manufactured by Toagosei Co., Ltd.) 35 parts Polymerizable compound: Celoxide 2021P (C2021P manufactured by Daicel Chemical Industries)
20 parts Photopolymerization initiator: UV16992 (manufactured by Dow Chemical) 5 parts Yellow pigment dispersion 1 30 parts Illustrative compound I 10 parts [Preparation of magenta ink]
The following were mixed in order, heated and stirred at 130 ° C., and the resulting liquid was filtered through a # 3000 metal mesh filter under heating and then cooled to prepare a magenta ink.

重合性化合物：オキセタン２２１ （ＯＸＴ２２１ 東亞合成製） ４５部
重合性化合物：セロキサイド２０２１Ｐ（Ｃ２０２１Ｐ ダイセル化学工業製）
２０部
光重合開始剤：ＵＶ１６９９２（ダウ・ケミカル製） ５部
マゼンタ顔料分散液１ ２０部
例示化合物Ｉ １０部
〔シアンインクの調製〕
下記を順次混合し、１３０℃に加熱、攪拌した後、得られた液体を加熱下、＃３０００の金属メッシュフィルターでろ過した後、冷却して、シアンインクを調製した。 Polymerizable compound: Oxetane 221 (OXT221 manufactured by Toagosei Co., Ltd.) 45 parts Polymerizable compound: Celoxide 2021P (C2021P manufactured by Daicel Chemical Industries)
20 parts Photopolymerization initiator: UV16992 (manufactured by Dow Chemical) 5 parts Magenta pigment dispersion 1 20 parts Illustrative compound I 10 parts [Preparation of cyan ink]
The following were mixed in order, heated and stirred at 130 ° C., and the resulting liquid was filtered through a # 3000 metal mesh filter under heating and then cooled to prepare a cyan ink.

重合性化合物：オキセタン２２１（ＯＸＴ２２１ 東亞合成製） ５５部
重合性化合物：セロキサイド２０２１Ｐ（Ｃ２０２１Ｐ ダイセル化学工業製）
２０部
光重合開始剤：ＵＶ１６９９２（ダウ・ケミカル製） ５部
シアン顔料分散液１ １０部
例示化合物Ｉ １０部
〔ブラックインクの調製〕
下記を順次混合し、１３０℃に加熱、攪拌した後、得られた液体を加熱下、＃３０００の金属メッシュフィルターでろ過した後、冷却して、ブラックインクを調製した。 Polymerizable compound: Oxetane 221 (OXT221 manufactured by Toagosei Co., Ltd.) 55 parts Polymerizable compound: Celoxide 2021P (C2021P manufactured by Daicel Chemical Industries)
20 parts Photopolymerization initiator: UV16992 (manufactured by Dow Chemical) 5 parts Cyan pigment dispersion 1 10 parts Illustrative compound I 10 parts [Preparation of black ink]
The following were mixed in order, heated to 130 ° C. and stirred, and the resulting liquid was filtered through a # 3000 metal mesh filter under heating, and then cooled to prepare a black ink.

重合性化合物：オキセタン２２１（ＯＸＴ２２１ 東亞合成製） ４５部
重合性化合物：セロキサイド２０２１Ｐ（Ｃ２０２１Ｐ ダイセル化学工業製）
２０部
光重合開始剤：ＵＶ１６９９２（ダウ・ケミカル製） ５部
ブラック顔料分散液１ ２０部
例示化合物Ｉ １０部
〔ライトマゼンタインクの調製〕
下記を順次混合し、１３０℃に加熱、攪拌した後、得られた液体を加熱下、＃３０００の金属メッシュフィルターでろ過した後、冷却して、ライトマゼンタインクを調製した。 Polymerizable compound: Oxetane 221 (OXT221 manufactured by Toagosei Co., Ltd.) 45 parts Polymerizable compound: Celoxide 2021P (C2021P manufactured by Daicel Chemical Industries)
20 parts Photopolymerization initiator: UV16992 (manufactured by Dow Chemical) 5 parts Black pigment dispersion 1 20 parts Illustrative compound I 10 parts [Preparation of light magenta ink]
The following were mixed in order, heated to 130 ° C. and stirred, and the resulting liquid was filtered with a # 3000 metal mesh filter under heating and then cooled to prepare a light magenta ink.

重合性化合物：オキセタン２２１（ＯＸＴ２２１ 東亞合成製） ５５部
重合性化合物：セロキサイド２０２１Ｐ（Ｃ２０２１Ｐ ダイセル化学工業製）
２５部
光重合開始剤：ＵＶ１６９９２（ダウ・ケミカル製） ５部
マゼンタ顔料分散液１ ５部
例示化合物Ｉ １０部
〔ライトシアンインクの調製〕
下記を順次混合し、１３０℃に加熱、攪拌した後、得られた液体を加熱下、＃３０００の金属メッシュフィルターでろ過した後、冷却して、ライトシアンインクを調製した。 Polymerizable compound: Oxetane 221 (OXT221 manufactured by Toagosei Co., Ltd.) 55 parts Polymerizable compound: Celoxide 2021P (C2021P manufactured by Daicel Chemical Industries)
25 parts Photopolymerization initiator: UV16992 (manufactured by Dow Chemical) 5 parts Magenta pigment dispersion 1 5 parts Exemplary compound I 10 parts [Preparation of light cyan ink]
The following were mixed in order, heated to 130 ° C. and stirred, and the resulting liquid was filtered with a # 3000 metal mesh filter under heating and then cooled to prepare a light cyan ink.

重合性化合物：オキセタン２２１（ＯＸＴ２２１ 東亞合成製） ５８部
重合性化合物：セロキサイド２０２１Ｐ（Ｃ２０２１Ｐ ダイセル化学工業製）
２５部
光重合開始剤：ＵＶ１６９９２（ダウ・ケミカル製） ５部
シアン顔料分散液１ ２部
例示化合物Ｉ １０部
《インクの各特性値の測定》
以上により調製した各色インクについて、実施例１に記載の方法と同様にして相転移温度の測定を行い、得られた結果を表５に示す。 Polymerizable compound: Oxetane 221 (OXT221 manufactured by Toagosei Co., Ltd.) 58 parts Polymerizable compound: Celoxide 2021P (C2021P manufactured by Daicel Chemical Industries)
25 parts Photopolymerization initiator: UV16992 (manufactured by Dow Chemical) 5 parts Cyan pigment dispersion 1 2 parts Exemplary compound I 10 parts << Measurement of each characteristic value of ink >>
For each color ink prepared as described above, the phase transition temperature was measured in the same manner as in the method described in Example 1, and the obtained results are shown in Table 5.

《インクジェット画像の形成及び評価》
実施例１のラインヘッド方式のインクジェットプリンターを用い、紙搬送方向に６列並べたラインヘッドプリンターに上記６色のインクを詰め、記録条件は実施例１と同様に、ＰＰＣ用紙（Ｊ ＰＡＰＥＲ コニカミノルタビジネスソリューションズ製）及びアート紙（ＳＡ金藤 王子製紙製）及び印刷用キャストコート紙（ミラーコート・ゴールド 王子製紙社製）、及び印刷用コート紙（ＯＫマットコートグリーン１００ 王子製紙製）に、３Ｐ明朝体の文字画像及びＪＩＳ／ＳＣＩＤ Ｎ５「自転車」画像をプリントし、実施例１に記載の方法と同様にして、文字品質の評価、裏抜け耐性の評価、ドット径ばらつきの評価、紫外線硬化性の評価、出射安定性の評価を行った結果、全ての評価項目において優れた効果を確認することができた。 << Formation and evaluation of inkjet image >>
Using the line head type ink jet printer of the first embodiment, the above-mentioned six colors of ink are packed in a line head printer arranged in six rows in the paper transport direction, and the recording conditions are the same as in the first embodiment, and the PPC paper (JPAPER Konica Minolta) is used. Business Solutions), art paper (SA Kinfuji Oji Paper), cast coated paper for printing (Mirror Coat Gold Oji Paper Co., Ltd.), and coated paper for printing (OK Matte Coat Green 100, Oji Paper Co., Ltd.) A morning character image and a JIS / SCID N5 “bicycle” image were printed, and in the same manner as described in Example 1, evaluation of character quality, evaluation of back-through resistance, evaluation of dot diameter variation, ultraviolet curing property As a result of evaluating the above and the output stability, it was possible to confirm excellent effects in all the evaluation items.

また、作製したＪＩＳ／ＳＣＩＤ Ｎ５「自転車」画像を目視観察した結果、液滴同士の合一による画像劣化がなく、鮮鋭性に優れ、また高い光学濃度が得られることを確認することができた。   Moreover, as a result of visually observing the produced JIS / SCID N5 “bicycle” image, it was confirmed that there was no image deterioration due to coalescence of droplets, excellent sharpness, and high optical density was obtained. .

本発明で用いることのできるインクジェット記録装置の要部の構成の一例を示す正面図である。1 is a front view illustrating an example of a configuration of a main part of an ink jet recording apparatus that can be used in the present invention. 本発明で用いることのできるラインヘッド方式のインクジェット記録装置の要部の構成の他の一例を示す上面図である。It is a top view which shows another example of a structure of the principal part of the line head type inkjet recording device which can be used by this invention.

符号の説明Explanation of symbols

１ インクジェット記録装置
２ 記録ヘッドキャリッジ
３ 記録ヘッド
３１ インク吐出口
４ 照射手段
５ プラテン部
６ ガイド部材
７ 蛇腹構造
Ｐ 記録媒体 DESCRIPTION OF SYMBOLS 1 Inkjet recording device 2 Recording head carriage 3 Recording head 31 Ink ejection port 4 Irradiation means 5 Platen part 6 Guide member 7 Bellows structure P Recording medium

Claims (7)

下記一般式（Ｉ）で表される化合物をインク全質量に対して０．１質量％以上、２０質量％未満含有することを特徴とする活性光線硬化型インクジェットインク。

（式中、Ｒ_１及びＲ_４は直鎖もしくは分岐のアルキル基、または直鎖もしくは分岐のアルケニル基を表し、Ｒ_２は炭素数１〜５の直鎖のアルキレン基を表し、Ｒ_３は炭素数１〜５の直鎖もしくは分岐のアルキル基を表す。） An actinic ray curable inkjet ink comprising a compound represented by the following general formula (I) in an amount of 0.1% by mass to less than 20% by mass with respect to the total mass of the ink.

(In the formula, R ₁ and R ₄ represent a linear or branched alkyl group or a linear or branched alkenyl group, R ₂ represents a linear alkylene group having 1 to 5 carbon atoms, and R ₃ represents carbon. Represents a linear or branched alkyl group of formula 1-5.) 前記一般式（Ｉ）で表される化合物中のＲ_２がテトラメチレン基であり、Ｒ_１及びＲ_４がそれぞれ炭素数２〜３０の直鎖のアルキル基であって、末端がビニル基または水素原子であることを特徴とする請求項１に記載の活性光線硬化型インクジェットインク。 R ₂ in the compound represented by the general formula (I) is a tetramethylene group, R ₁ and R ₄ are each a linear alkyl group having 2 to 30 carbon atoms, and the terminal is a vinyl group or hydrogen. The actinic ray curable inkjet ink according to claim 1, which is an atom. 着色剤として顔料を含有することを特徴とする請求項１または２に記載の活性光線硬化型インクジェットインク。 The actinic ray curable ink jet ink according to claim 1, further comprising a pigment as a colorant. 温度により可逆的にゾルゲル相転移することを特徴とし、ゾルゲル相転移温度が３０℃以上、１００℃未満であることを特徴とする請求項１〜３のいずれか１項に記載の活性光線硬化型インクジェットインク。 The actinic ray curable type according to any one of claims 1 to 3, wherein the sol-gel phase transition reversibly depends on temperature, and the sol-gel phase transition temperature is 30 ° C or higher and lower than 100 ° C. Inkjet ink. 請求項１〜４のいずれか１項に記載の活性光線硬化型インクジェットインクを記録ヘッドを用いて記録媒体上に記録を行うインクジェット記録方法において、記録ヘッド内での活性光線硬化型インクジェットインクの温度が記録媒体の温度より２５℃以上、１００℃未満高いことを特徴とするインクジェット記録方法。 The temperature of the actinic radiation curable inkjet ink in a recording head in the inkjet recording method which records the actinic radiation curable inkjet ink of any one of Claims 1-4 on a recording medium using a recording head. An ink jet recording method, wherein the temperature is 25 ° C. or more and less than 100 ° C. higher than the temperature of the recording medium. 前記活性光線硬化型インクジェットインクを記録ヘッド内で加熱することを特徴とする請求項５に記載のインクジェット記録方法。 The inkjet recording method according to claim 5, wherein the actinic ray curable inkjet ink is heated in a recording head. 前記活性光線硬化型インクジェットインクの記録ヘッド内での加熱の温度が活性光線硬化型インクジェットインクのゾルゲル相転移温度よりも１０℃以上、４０℃未満高いことを特徴とする請求項６に記載のインクジェット記録方法。 The inkjet according to claim 6, wherein the temperature of heating in the recording head of the actinic radiation curable inkjet ink is 10 ° C or more and less than 40 ° C higher than the sol-gel phase transition temperature of the actinic radiation curable inkjet ink. Recording method.

Images