JP2010069527A - 高Al鋼の連続鋳造用モールドフラックス及び鋳片の製造方法 - Google Patents
高Al鋼の連続鋳造用モールドフラックス及び鋳片の製造方法 Download PDFInfo
- Publication number
- JP2010069527A JP2010069527A JP2008242898A JP2008242898A JP2010069527A JP 2010069527 A JP2010069527 A JP 2010069527A JP 2008242898 A JP2008242898 A JP 2008242898A JP 2008242898 A JP2008242898 A JP 2008242898A JP 2010069527 A JP2010069527 A JP 2010069527A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- concentration
- slab
- steel
- mold flux
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】sol.Al濃度が0.1〜1.5質量%、Si濃度が0.3〜2.0質量%、C濃度が0.05〜0.18質量%である普通鋼の連続鋳造に用いるモールドフラックスである。CaO含有率をSiO2含有率で除した比(CaO/SiO2)が1.0〜2.0で、P2O5が1.0〜8.0質量%、B2O3が0.5〜5.0質量%のうちの1種または2種を含有し、かつ、凝固温度が1050〜1200℃、1300℃における粘度が0.5〜2.5dPa・sで、一旦溶融させたフラックスを毎分10℃の速度で冷却した常温試料中の主な結晶相がカスピダインである。
【効果】sol.Al濃度が0.1質量%以上の高Al鋼を連続鋳造する場合にも、高圧水等によるスケール除去を促進でき、島状スケールの少ない熱延鋼板が得られる。
【選択図】なし
Description
すなわち、粗圧延後に再加熱した後のスケール剥離性を高める方法として、特許文献2に開示された方法を適用するにあたって、その効果を高める連続鋳造用モールドフラックスを提供するものである。また、鋳造中におけるモールドフラックス物性値の変化を小さく抑え、安定した操業と高品質な鋳片を製造する方法を提供するものである。
ここで、モールドフラックスは、通常、化学組成として、CaOおよびSiO2を主成分とし、Al2O3、MgO、Na2O等のアルカリ金属酸化物やフッ素(F)等を含有して適正な凝固温度に調整し、滓化速度調整剤としてカーボンを1〜5質量%程度添加したものである。
sol.Al濃度が0.1〜1.5質量%、Si濃度が0.3〜2.0質量%、C濃度が0.05〜0.18質量%である普通鋼を対象とし、
粗圧延後に鋼板を加熱してスケールを厚く生成させた後、高圧水スプレーによってスケールを除去する際に、連続鋳造用モールドフラックスを活用してスケール剥離性を高めるために、
CaO/SiO2が1.0〜2.0であり、
P2O5が1.0〜8.0質量%、B2O3が0.5〜5.0質量%のうちの1種または2種を含有し、
かつ、凝固温度が1050〜1200℃、1300℃における粘度が0.5〜2.5dPa・sであり、
一旦溶融させたフラックスを毎分10℃の速度で冷却した常温試料中の主な結晶相がカスピダインであることを最も主要な特徴としている。
さらに、対象とする普通鋼を40m以上連続鋳造した際の鋳型内溶融層の凝固温度が、第1の本発明に規定した元組成の前記凝固温度に対し、20℃〜200℃高く、かつ1300℃以下であり、
かつ、第1の本発明に規定した元組成の前記粘度に対して、鋳型内溶融層の1300℃における粘度の上昇が2.5dPa・s以下としたのが第2の本発明モールドフラックスである。
前記何れかの本発明モールドフラックスを用いて連続鋳造した鋳片を熱間圧延して鋳片を製造する方法であって、
前記連続鋳造鋳片を素材として熱間圧延する際の粗圧延後に該鋳片を再加熱し、その後、高圧水によって該鋳片の表面スケールを除去して熱間圧延を継続するに際して、
連続鋳造後から熱間圧延を開始するまでの間に、該鋳片の表層部を溶削または研削する手入れを行わないことを最も主要な特徴としたものである。
第1の本発明モールドフラックスは、
sol.Al濃度が0.1〜1.5質量%、Si濃度が0.3〜2.0質量%、C濃度が0.05〜0.18質量%である普通鋼の連続鋳造に用いられるモールドフラックスであって、
CaO/SiO2が1.0〜2.0であり、
P2O5が1.0〜8.0質量%、B2O3が0.5〜5.0質量%のうちの1種または2種を含有し、
かつ、凝固温度が1050〜1200℃、1300℃における粘度が0.5〜2.5dPa・sであり、
一旦溶融させたフラックスを毎分10℃の速度で冷却した常温試料中の主な結晶相がカスピダインであることを特徴とするものである。
かつ、第1の本発明に規定した元組成の前記粘度に対して、鋳型内溶融層の1300℃における粘度の上昇が2.5dPa・s以下であることを特徴とするものである。
連続鋳造後から熱間圧延を開始するまでの間に、該鋳片の表層部を溶削または研削する手入れを行わないこととしたのが、本発明の鋳片の製造方法である。
下記表1に示した組成を含有し残部が鉄からなる鋼種を、下記表2に示した本発明の実施例及び比較例のモールドフラックスを用いて鋳造した。下記表2において、A〜Cは本発明の実施例、D〜Eは比較例である。
Claims (3)
- sol.Al濃度が0.1〜1.5質量%、Si濃度が0.3〜2.0質量%、C濃度が0.05〜0.18質量%である普通鋼の連続鋳造に用いられるモールドフラックスであって、
CaO含有率をSiO2含有率で除した比(CaO/SiO2)が1.0〜2.0であり、
P2O5が1.0〜8.0質量%、B2O3が0.5〜5.0質量%のうちの1種または2種を含有し、
かつ、凝固温度が1050〜1200℃、1300℃における粘度が0.5〜2.5dPa・sであり、
一旦溶融させたフラックスを毎分10℃の速度で冷却した常温試料中の主な結晶相がカスピダインであることを特徴とする高Al鋼の連続鋳造用モールドフラックス。 - sol.Al濃度が0.1〜1.5質量%、Si濃度が0.3〜2.0質量%、C濃度が0.05〜0.18質量%である普通鋼を40m以上連続鋳造した際の鋳型内溶融層の凝固温度が、請求項1に規定した元組成の前記凝固温度に対し、20℃〜200℃高く、かつ1300℃以下であり、
かつ、請求項1に規定した元組成の前記粘度に対して、鋳型内溶融層の1300℃における粘度の上昇が、2.5dPa・s以下であることを特徴とする請求項1に記載の高Al鋼の連続鋳造用モールドフラックス。 - 請求項1又は2に記載のモールドフラックスを用いて連続鋳造した鋳片を熱間圧延して鋳片を製造する方法であって、
前記連続鋳造鋳片を素材として熱間圧延する際の粗圧延後に該鋳片を再加熱し、その後、高圧水によって該鋳片の表面スケールを除去して熱間圧延を継続するに際して、
連続鋳造後から熱間圧延を開始するまでの間に、該鋳片の表層部を溶削または研削する手入れを行わないことを特徴とする鋳片の製造方法。