JP2009522100A - Electrocatalysts containing platinum and titanium - Google Patents

Electrocatalysts containing platinum and titanium Download PDF

Info

Publication number
JP2009522100A
JP2009522100A JP2008549565A JP2008549565A JP2009522100A JP 2009522100 A JP2009522100 A JP 2009522100A JP 2008549565 A JP2008549565 A JP 2008549565A JP 2008549565 A JP2008549565 A JP 2008549565A JP 2009522100 A JP2009522100 A JP 2009522100A
Authority
JP
Japan
Prior art keywords
atomic percent
metal
platinum
titanium
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2008549565A
Other languages
Japanese (ja)
Other versions
JP5425472B2 (en
JP2009522100A5 (en
Inventor
ハ、ティン
クレイドラー、エリック、ローランド
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Honda Motor Co Ltd
Original Assignee
Honda Motor Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US11/326,350 external-priority patent/US7740975B2/en
Priority claimed from US11/370,991 external-priority patent/US7691522B2/en
Priority claimed from US11/429,252 external-priority patent/US7704628B2/en
Priority claimed from US11/429,251 external-priority patent/US7318977B2/en
Application filed by Honda Motor Co Ltd filed Critical Honda Motor Co Ltd
Publication of JP2009522100A publication Critical patent/JP2009522100A/en
Publication of JP2009522100A5 publication Critical patent/JP2009522100A5/ja
Application granted granted Critical
Publication of JP5425472B2 publication Critical patent/JP5425472B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

【課題】 プラチナ、チタン、および追加の金属を含有することを必須とし、燃料電池の用途において５種類までの金属を含有する電極触媒の組成物を提供する。
【解決手段】 この電極触媒の組成物は、プラチナとチタンと第三金属の含有を必須とし、実施形態によっては、さらに、第四金属および第五金属とを適宜含むようにしてもよい。この第三金属として可能なものは、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から選択される少なくとも１つの金属である。追加の第四金属および第五金属はそれぞれ、第三金属とは異なる金属であり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から選択するようにしてもよい。
【選択図】なしPROBLEM TO BE SOLVED: To provide an electrocatalyst composition containing up to five kinds of metals in a fuel cell application, which must contain platinum, titanium, and an additional metal.
The composition of the electrocatalyst essentially contains platinum, titanium, and a third metal, and may further include a fourth metal and a fifth metal depending on the embodiment. Possible third metals are at least one metal selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. . Each of the additional fourth and fifth metals is a different metal than the third metal, scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, You may make it select from the group which consists of hafnium, a tantalum, and rhenium.
[Selection figure] None

Description

本願は、米国特許出願第１１／３２６３５０号（出願日：２００６年１月６日）、米国特許出願第１１／３７０９９１号（出願日：２００６年３月９日）、米国特許出願第１１／４２９２５１号（出願日：２００６年５月８日）および米国特許出願第１１／４２９２５２号（出願日：２００６年５月８日）の利益を請求するものであり、これら出願のすべての記載をここに引用するものである。   The present application includes US patent application No. 11/326350 (filing date: January 6, 2006), US patent application number 11/370991 (filing date: March 9, 2006), and US patent application number 11/429251. No. (Application Date: May 8, 2006) and US Patent Application No. 11/429252 (Application Date: May 8, 2006), all of which are hereby incorporated by reference To quote.

本開示は、プラチナ、チタンおよび第三金属を必須とする電極触媒の組成物について教示し、具体的には、約５５〜８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属の含有を必須とする電極触媒の組成物に関する。この第三金属は、ニッケル、バナジウムおよびモリブデンからなる群から選ばれる少なくとも１つの金属である。   The present disclosure teaches an electrocatalytic composition comprising platinum, titanium and a third metal, specifically, about 55 to 85 atomic percent platinum, about 1 to about 30 atomic percent titanium, The present invention relates to an electrocatalyst composition which requires inclusion of about 1 to about 30 atomic percent of a third metal. This third metal is at least one metal selected from the group consisting of nickel, vanadium and molybdenum.

さらに、本開示は、プラチナ、チタンおよび第三金属を必須とする電極触媒の組成物に関し、具体的には、約５５〜９５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属の含有を必須とする電極触媒の組成物に関する。この第三金属は、銅、マンガンおよび鉄からなる群から選ばれる少なくとも１つの金属である。   The present disclosure further relates to an electrocatalytic composition comprising platinum, titanium and a third metal, specifically, about 55 to 95 atomic percent platinum, about 1 to about 30 atomic percent titanium, The present invention relates to an electrocatalyst composition which requires inclusion of about 1 to about 30 atomic percent of a third metal. This third metal is at least one metal selected from the group consisting of copper, manganese and iron.

さらに、本開示は、プラチナ、チタンおよび第三金属の含有を必須とする電極触媒の組成物に関し、具体的には、約５０〜８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属の含有を必須とする電極触媒の組成物について教示する。
この第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から選ばれる少なくとも１つの金属である。 The present disclosure further relates to electrocatalyst compositions that require the inclusion of platinum, titanium and a third metal, specifically about 50 to 85 atomic percent platinum and about 5 to about 30 atomic percent titanium. And electrocatalyst compositions that require inclusion of about 1 to about 30 atomic percent of a third metal.
This third metal is at least one metal selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold.

さらに、本開示は、プラチナ、チタン、第三金属、第四金属および第五金属の含有を必須とする電極触媒の組成物を教示する。
具体的には、約３０〜８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属と、約１％〜約３０％の第四金属と、約１％〜約３０％の第五金属が含まれる。
この第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択するようにしてもよい。
また、この第四金属と第五金属とは互いに異なる金属であり、さらに第三金属とも異なる金属であって、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタラムおよびレニウムからなる群から少なくとも１つを選択するようにしてもよい。 Furthermore, the present disclosure teaches an electrocatalyst composition that requires the inclusion of platinum, titanium, third metal, fourth metal and fifth metal.
Specifically, about 30 to 85 atomic percent platinum, about 5 to about 30 atomic percent titanium, about 1 to about 30 atomic percent third metal, and about 1% to about 30% quaternary metal. And about 1% to about 30% of the fifth metal.
The third metal may be selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold.
Further, the fourth metal and the fifth metal are different from each other, and are also different from the third metal, and scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium. , Molybdenum, cadmium, tin, hafnium, tantalum, and rhenium may be selected.

電極触媒の所望の性能を確保しつつ、高価なプラチナ系金属の必要量を低減しようとする試みは、電極触媒に必須となる各種の装置設計や手順において、従来、操作パラメータとして扱われるものである。   Attempts to reduce the required amount of expensive platinum-based metals while ensuring the desired performance of the electrocatalyst have been conventionally treated as operating parameters in various equipment designs and procedures essential for electrocatalysts. is there.

プラチナに各種の安価な金属を組み合わせることで触媒性能の向上を図る手法は、プラチナの必要量を低減し、触媒反応の効率性を促進するために有効な手段の１つである。目的のプラチナ系電極触媒に関する１応用例として、例えば、酸素還元反応に触媒作用を及ぼすプラチナ系電極触媒を含有する電極としての利用が可能である、典型的な固体高分子系燃料電池（PEMFC）のカソード反応がある。   The technique of improving the catalyst performance by combining various inexpensive metals with platinum is one of the effective means for reducing the required amount of platinum and promoting the efficiency of the catalytic reaction. For example, a typical polymer electrolyte fuel cell (PEMFC) that can be used as an electrode containing a platinum-based electrocatalyst that catalyzes an oxygen reduction reaction. There is a cathodic reaction.

したがって、所望の性能レベルを達成するのに必要なプラチナの量を低減する電極触媒の組成物および薄膜型燃料電池の電極触媒が求められている。   Accordingly, there is a need for electrocatalyst compositions and thin film fuel cell electrocatalysts that reduce the amount of platinum necessary to achieve the desired performance level.

本開示は、プラチナの量を低減するような電極触媒の組成物、特に燃料電池の電極触媒、具体的には、薄膜型燃料電池の電極触媒に対する要求を満たすものである。   The present disclosure fulfills the need for electrode catalyst compositions that reduce the amount of platinum, particularly fuel cell electrode catalysts, specifically thin film fuel cell electrode catalysts.

本開示は、プラチナ、タンタルおよび第三金属の含有を必須とする金属成分を含んだ電極触媒の組成物を教示するものである。この電極触媒の組成物は、約５５〜約８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、ニッケル、バナジウムおよびモリブデンからなる群から少なくとも１つを選択する。   The present disclosure teaches an electrocatalyst composition that includes a metal component that requires the inclusion of platinum, tantalum and a third metal. The electrocatalyst composition may include from about 55 to about 85 atomic percent platinum, from about 1 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of nickel, vanadium and molybdenum.

さらに、本開示は、プラチナと、チタンと、第三金属の含有を必須とする組成物を含んだ燃料電池の電極触媒を教示する。この電極触媒の組成物は、約５５〜約８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、ニッケル、バナジウムおよびモリブデンからなる群から少なくとも１つを選択する。   Furthermore, the present disclosure teaches a fuel cell electrocatalyst comprising a composition that requires the inclusion of platinum, titanium, and a third metal. The electrocatalyst composition may include from about 55 to about 85 atomic percent platinum, from about 1 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of nickel, vanadium and molybdenum.

本開示は、さらに、少なくとも１つの薄膜型電極触媒と、膜と、少なくとも１つの電極とを備える燃料電池アッセンブリをさらに教示する。この薄膜型電極触媒は、プラチナ、チタンおよび第三金属の含有を必須とする組成物を含む。この電極触媒の組成物は、約５５〜約８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、ニッケル、バナジウムおよびモリブデンからなる群から少なくとも１つを選択する。   The present disclosure further teaches a fuel cell assembly comprising at least one thin film electrocatalyst, a membrane, and at least one electrode. The thin film type electrocatalyst includes a composition that essentially contains platinum, titanium, and a third metal. The electrocatalyst composition may include from about 55 to about 85 atomic percent platinum, from about 1 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of nickel, vanadium and molybdenum.

さらに、本開示は、プラチナ、チタンおよび第三金属の含有を必須とする金属成分を含んだ、別の電極触媒の組成物を教示する。この電極触媒の組成物は、約５５〜約９５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、銅、マンガンおよび鉄からなる群から少なくとも１つを選択する。   In addition, the present disclosure teaches another electrocatalyst composition that includes a metal component that requires inclusion of platinum, titanium, and a third metal. The electrocatalyst composition may comprise about 55 to about 95 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of copper, manganese and iron.

さらに、本開示は、プラチナ、チタンおよび第三金属の含有を必須とする組成物を含んでいる、燃料電池の電極触媒の組成物を教示する。この電極触媒の組成物は、約５５〜約９５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、銅、マンガンおよび鉄からなる群から少なくとも１つを選択する。   In addition, the present disclosure teaches a fuel cell electrocatalyst composition comprising a composition that requires the inclusion of platinum, titanium and a third metal. The electrocatalyst composition may comprise about 55 to about 95 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of copper, manganese and iron.

さらに、本開示は、少なくとも１つの薄膜型電極触媒と、膜と、少なくとも１つの電極を備える燃料電池アッセンブリについて教示する。この薄膜型電極触媒は、プラチナ、チタンおよび第三金属の含有を必須とする組成物を含む。この電極触媒の組成物は、約５５〜約９５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、銅、マンガンおよび鉄からなる群から少なくとも１つを選択する。   Furthermore, the present disclosure teaches a fuel cell assembly comprising at least one thin film type electrocatalyst, a membrane, and at least one electrode. The thin film type electrocatalyst includes a composition that essentially contains platinum, titanium, and a third metal. The electrocatalyst composition may comprise about 55 to about 95 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of copper, manganese and iron.

本開示は、さらに、プラチナ、チタンおよび第三金属の含有を必須とする金属成分を含んでいる、追加的な電極触媒の組成物について教示する。この電極触媒の組成物は、約５０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択する。   The present disclosure further teaches an additional electrocatalytic composition that includes a metal component that requires inclusion of platinum, titanium, and a third metal. The electrocatalyst composition may include from about 50 to about 85 atomic percent platinum, from about 5 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold.

さらに、本開示は、プラチナ、チタンおよび第三金属の含有を必須とする組成物を含んでいる、燃料電池の電極触媒について教示する。
この電極触媒の組成物は、約５０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択する。 Furthermore, the present disclosure teaches a fuel cell electrocatalyst comprising a composition that requires the inclusion of platinum, titanium and a third metal.
The electrocatalyst composition may include from about 50 to about 85 atomic percent platinum, from about 5 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold.

さらに、本開示は、少なくとも１つの薄膜型電極触媒と、膜と、少なくとも１つの電極を備える燃料電池アッセンブリについて教示する。この薄膜型電極触媒は、本開示に教示されるプラチナ、チタンおよび第三金属の含有を必須とする組成物を含む。この電極触媒の組成物は、約５０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択する。   Furthermore, the present disclosure teaches a fuel cell assembly comprising at least one thin film type electrocatalyst, a membrane, and at least one electrode. The thin film type electrocatalyst comprises a composition that requires the inclusion of platinum, titanium, and a third metal taught in the present disclosure. The electrocatalyst composition may include from about 50 to about 85 atomic percent platinum, from about 5 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold.

さらに、本開示は、プラチナ、チタン、第三金属、第四金属および第五金属の含有を必須とする金属成分を含んでいる、別の電極触媒の組成物を教示する。この電極触媒の組成物は、約３０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属と、約１〜約３０原子パーセントの第四金属と、約１〜約３０原子パーセントの第五金属とを含むようにしてもよい。この第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択する。この第四金属は第三金属とは異なるものであり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から少なくとも１つを選択する。この第五金属は第三金属と第四金属とは異なるものであり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から少なくとも１つを選択する。   In addition, the present disclosure teaches another electrocatalyst composition that includes a metal component that requires inclusion of platinum, titanium, a third metal, a fourth metal, and a fifth metal. The electrocatalyst composition comprises about 30 to about 85 atomic percent platinum, about 5 to about 30 atomic percent titanium, about 1 to about 30 atomic percent third metal, and about 1 to about 30 atomic percent. And about 1 to about 30 atomic percent of the fifth metal. This third metal is at least one selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. This fourth metal is different from the third metal and consists of scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium Select at least one from the group. This fifth metal is different from the third and fourth metals, scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum And at least one selected from the group consisting of rhenium.

本開示は、さらに、プラチナ、チタン、第三金属および第四金属の含有を必須とする金属成分を含んでいる電極触媒について教示する。この金属成分は、約３０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属と、約１〜約３０原子パーセントの第四金属とを含むようにしてもよい。この第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択する。この第四金属は第三金属とはことなるものであり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から少なくとも１つを選択する。   The present disclosure further teaches an electrocatalyst comprising a metal component that requires the inclusion of platinum, titanium, a third metal and a fourth metal. The metal component includes about 30 to about 85 atomic percent platinum, about 5 to about 30 atomic percent titanium, about 1 to about 30 atomic percent third metal, and about 1 to about 30 atomic percent fourth. You may make it contain a metal. This third metal is at least one selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. This fourth metal is different from the third metal, from scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium At least one is selected from the group consisting of

さらに、本開示は、少なくとも１つの電極触媒と、膜と、少なくとも１つの電極とを備えた燃料電池アッセンブリについて教示する。この電極触媒は、プラチナ、チタン、第三金属、第四金属および第五金属の含有を必須とする組成物を含んでいる。この金属成分は、約３０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属と、約１〜約３０原子パーセントの第四金属と、約１〜約３０原子パーセントの第五金属とを含むようにしてもよい。この第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択する。この第四金属は第三金属とはことなるものであり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から少なくとも１つを選択する。この第五金属は第三金属と第四金属とは異なるものであり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から少なくとも１つを選択する。   Furthermore, the present disclosure teaches a fuel cell assembly that includes at least one electrocatalyst, a membrane, and at least one electrode. The electrocatalyst includes a composition that essentially contains platinum, titanium, a third metal, a fourth metal, and a fifth metal. The metal component includes about 30 to about 85 atomic percent platinum, about 5 to about 30 atomic percent titanium, about 1 to about 30 atomic percent third metal, and about 1 to about 30 atomic percent fourth. It may include a metal and from about 1 to about 30 atomic percent of a fifth metal. This third metal is at least one selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. This fourth metal is different from the third metal, from scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium At least one is selected from the group consisting of This fifth metal is different from the third and fourth metals, scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum And at least one selected from the group consisting of rhenium.

さらに、本開示は、プラチナ、チタン、コバルトおよびパラジウムの含有を必須とする金属成分を含んでいる電極触媒の組成物について教示する。この電極触媒の組成物は、約３０〜約６０原子パーセントのプラチナと、約５〜約２０原子パーセントのチタンと、約１〜約２０原子パーセントのコバルトと、約１５〜約３０原子パーセントのパラジウムとを含むようにしてもよい。   Furthermore, the present disclosure teaches an electrocatalyst composition that includes a metal component that is required to contain platinum, titanium, cobalt, and palladium. The electrocatalyst composition comprises about 30 to about 60 atomic percent platinum, about 5 to about 20 atomic percent titanium, about 1 to about 20 atomic percent cobalt, and about 15 to about 30 atomic percent palladium. May be included.

さらに、本開示が教示する電極触媒は薄膜型電極触媒であってもよく、この薄膜電極触媒は、高表面積担体上に担持される、プラチナ、チタンおよび追加の金属の含有を必須とする粉体組成物を含むようにしてもよい。
代替の実施形態によっては、この電極触媒は、担持されたナノ粒子含有粉体であってもよい。 In addition, the electrocatalyst taught by the present disclosure may be a thin film type electrocatalyst, which is a powder essentially comprising platinum, titanium and additional metals supported on a high surface area support. A composition may be included.
In some alternative embodiments, the electrocatalyst may be a supported nanoparticle-containing powder.

本発明をよりよく理解するために提供され引用された、本明細書を構成する付属の図面は、本発明の最良の実施形態を例示するものであり、詳細な記載とともに本発明の原理を説明するためのものである。   The accompanying drawings, which are provided and referred to for a better understanding of the invention, and constitute the specification, illustrate the best embodiment of the invention and, together with the detailed description, explain the principles of the invention. Is to do.

本開示の教示は、プラチナ、チタンおよび第三金属を必須の含有とする金属成分を含む電極触媒の組成物に関する。この電極触媒の組成物は、約５５〜約８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、ニッケル、バナジウムおよびモリブデンからなる群から少なくとも１つを選択する。   The teachings of the present disclosure relate to an electrocatalyst composition comprising a metal component that essentially contains platinum, titanium, and a third metal. The electrocatalyst composition may include from about 55 to about 85 atomic percent platinum, from about 1 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of nickel, vanadium and molybdenum.

別の実施形態の電極触媒の組成物では、約６０〜約８０原子パーセントのプラチナと、約５〜約２５原子パーセントのチタンと、約５〜約２５原子パーセントの第三金属とを含むようにしてもよい。さらに別の実施形態の電極触媒の組成物では、約６０〜約７０原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、約１０〜約２０原子パーセントの第三金属とを含むようにしてもよい。さらに別の実施形態の電極触媒の組成物では、約６０〜約８０原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約２５原子パーセントの第三金属とを含むようにしてもよい。また、別の事例の電極触媒の組成物は、約６０〜約７０原子パーセントのプラチナと、約１０〜約３０原子パーセントのチタンと、約１〜約２０原子パーセントの第三金属とを含むようにしてもよい。   Another embodiment of the electrocatalyst composition may comprise from about 60 to about 80 atomic percent platinum, from about 5 to about 25 atomic percent titanium, and from about 5 to about 25 atomic percent third metal. Good. Yet another embodiment of the electrocatalyst composition comprises about 60 to about 70 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 10 to about 20 atomic percent tertiary metal. Also good. Yet another embodiment of the electrocatalyst composition comprises from about 60 to about 80 atomic percent platinum, from about 5 to about 30 atomic percent titanium, and from about 1 to about 25 atomic percent tertiary metal. Also good. Another example electrocatalyst composition includes about 60 to about 70 atomic percent platinum, about 10 to about 30 atomic percent titanium, and about 1 to about 20 atomic percent tertiary metal. Also good.

本開示のこの他の実施形態に係る電極触媒の組成物では、約５５〜約８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１０〜約２０原子パーセントの第三金属として、ニッケル、バナジウムあるいはモリブデンを含んでいてもよい。さらに、追加的な電極触媒の組成物では、約５５〜８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約２０原子パーセントの第三金属として、ニッケル、バナジウムあるいはモリブデンを含んでいてもよい。   In the composition of the electrocatalyst according to other embodiments of the present disclosure, from about 55 to about 85 atomic percent platinum, from about 1 to about 30 atomic percent titanium, and from about 10 to about 20 atomic percent third metal. As an alternative, nickel, vanadium or molybdenum may be included. Further, additional electrocatalyst compositions include nickel, vanadium, or about 55 to 85 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 1 to about 20 atomic percent tertiary metal. Molybdenum may be included.

さらに本開示の教示は、電極触媒の組成物からなる燃料電池の電極触媒を提供し、この電極触媒の組成物は、約５５〜約８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属の含有を必須とする。この第三金属は、ニッケル、バナジウムおよびモリブデンからなる群から少なくとも１つを選択する。   The teachings of the present disclosure further provide a fuel cell electrocatalyst comprising an electrocatalyst composition, the electrocatalyst composition comprising about 55 to about 85 atomic percent platinum and about 1 to about 30 atomic percent. The inclusion of titanium and about 1 to about 30 atomic percent of a third metal is essential. The third metal is at least one selected from the group consisting of nickel, vanadium and molybdenum.

膜と、薄膜型あるいは担持型の電極触媒と、この薄膜型電極触媒とは異なる電極とからなる燃料電池アッセンブリを提供する。薄膜型あるいは担持型の電極触媒は、プラチナ、チタンおよび第三金属の含有を必須とする組成物で構成されるようにしてもよい。この電極触媒の組成物には、約５５〜約８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属が含まるようにしてもよい。この第三金属は、ニッケル、バナジウムおよびモリブデンからなる群から少なくとも１つを選択するようにしてもよい。   Provided is a fuel cell assembly comprising a membrane, a thin-film or supported electrode catalyst, and an electrode different from the thin-film electrode catalyst. The thin film-type or supported-type electrode catalyst may be composed of a composition essential to contain platinum, titanium, and a third metal. The electrocatalyst composition may include about 55 to about 85 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 1 to about 30 atomic percent third metal. . The third metal may be at least one selected from the group consisting of nickel, vanadium and molybdenum.

さらに別の実施形態に係る燃料電池アッセンブリは、約６０〜約８０原子パーセントのプラチナと、約５〜約２５原子パーセントのチタンと、約５〜約２５原子パーセントの第三金属が含まれていてもよい。さらに別の実施形態の燃料電池アッセンブリには、約６０〜８０原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約２５原子パーセントの第三金属が含まれるようにしてもよい。   A fuel cell assembly according to yet another embodiment includes about 60 to about 80 atomic percent platinum, about 5 to about 25 atomic percent titanium, and about 5 to about 25 atomic percent third metal. Also good. Yet another embodiment of the fuel cell assembly includes about 60 to 80 atomic percent platinum, about 5 to about 30 atomic percent titanium, and about 1 to about 25 atomic percent third metal. Also good.

別の実施形態に係る燃料電池アッセンブリでは、約６０〜約７０原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、約１０〜約２０原子パーセントの第三金属が含まれるようにしてもよい。さらに別の実施形態に係る燃料電池アッセンブリでは、約６０〜約７０原子パーセントのプラチナと、約１０〜約３０原子パーセントのチタンと、約１〜約２０原子パーセントの第三金属が含まれるようにしてもよい。   In another embodiment, a fuel cell assembly includes about 60 to about 70 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 10 to about 20 atomic percent third metal. Also good. In yet another embodiment, the fuel cell assembly includes from about 60 to about 70 atomic percent platinum, from about 10 to about 30 atomic percent titanium, and from about 1 to about 20 atomic percent third metal. May be.

さらに別の実施形態に係る燃料電池アッセンブリでは、約５５〜約８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１０〜約２０原子パーセントの第三金属としてニッケル、バナジウムあるいはモリブデンが含まれる組成物からなる電極触媒を含むようにしてもよい。さらに実施形態によっては、燃料電池アッセンブリは、約５５〜約８５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属として、ニッケル、バナジウムあるいはモリブデンとの含有を必須とする組成物により構成されるようにしてもよい。   In a fuel cell assembly according to yet another embodiment, about 55 to about 85 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 10 to about 20 atomic percent of a third metal such as nickel, vanadium, or You may make it contain the electrode catalyst which consists of a composition containing molybdenum. Further, in some embodiments, the fuel cell assembly includes about 55 to about 85 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 1 to about 30 atomic percent third metal, such as nickel, vanadium, or You may make it comprise with the composition which requires inclusion with molybdenum.

本開示は、プラチナ、チタンおよび第三金属からなる金属成分を含む電極触媒の組成物に関する。この電極触媒の組成物は、約５５〜約９５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属を含むようにしてもよい。この第三金属は、銅、マンガンおよび鉄から成る群から少なくとも１つを選択する。   The present disclosure relates to an electrocatalyst composition comprising a metal component comprising platinum, titanium and a third metal. The electrocatalyst composition may comprise from about 55 to about 95 atomic percent platinum, from about 1 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of copper, manganese and iron.

さらに別の実施形態に係る組成物では、約５５〜約７５原子パーセントのプラチナと、約１０〜約２５原子パーセントのチタンと、約１０〜約２５原子パーセントの第三金属を含むようにしてもよい。さらに、別の実施形態に係る電極触媒の組成物では、約５５〜約９０原子パーセントのプラチナと、約３〜約２５原子パーセントのチタンと、約５〜約２５原子パーセントの銅を含むようにしてもよい。さらに別の実施形態に係る電極触媒の組成物は、約５５〜約７０原子パーセントのプラチナと、約１５〜約２０原子パーセントのチタンと、約１０〜約２５原子パーセントの銅を含むようにしてもよい。   Yet another embodiment of the composition may include about 55 to about 75 atomic percent platinum, about 10 to about 25 atomic percent titanium, and about 10 to about 25 atomic percent third metal. Further, the electrocatalyst composition according to another embodiment may comprise about 55 to about 90 atomic percent platinum, about 3 to about 25 atomic percent titanium, and about 5 to about 25 atomic percent copper. Good. The composition of the electrocatalyst according to yet another embodiment may include about 55 to about 70 atomic percent platinum, about 15 to about 20 atomic percent titanium, and about 10 to about 25 atomic percent copper. .

さらに別の実施形態に係る電極触媒の組成物は、約５５〜約８０原子パーセントのプラチナと、約１０〜約２５原子パーセントのチタンと、約１０〜約２１原子パーセントのマンガンを含むようにしてもよい。
さらに、追加的な実施形態の電極触媒の組成物は、約６０〜約８０原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、約１０〜約３６原子パーセントのマンガンを含むようにしてもよい。 The composition of the electrocatalyst according to yet another embodiment may comprise about 55 to about 80 atomic percent platinum, about 10 to about 25 atomic percent titanium, and about 10 to about 21 atomic percent manganese. .
Further, the electrocatalyst composition of additional embodiments may comprise about 60 to about 80 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 10 to about 36 atomic percent manganese. Good.

さらに別の実施形態に係る電極触媒の組成物では、約６０〜約８０原子パーセントのプラチナと、約９〜約２５原子パーセントのチタンと、約７〜約２２原子パーセントの鉄を含むようにしてもよい。さらに追加的な実施形態に係る電極触媒の組成物では、約６０〜約７５原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、約１４〜約２２原子パーセントの鉄を含むようにしてもよい。   In yet another embodiment, the electrocatalyst composition may comprise about 60 to about 80 atomic percent platinum, about 9 to about 25 atomic percent titanium, and about 7 to about 22 atomic percent iron. . Still further, the electrocatalyst composition according to additional embodiments may comprise from about 60 to about 75 atomic percent platinum, from about 10 to about 20 atomic percent titanium, and from about 14 to about 22 atomic percent iron. Good.

本開示が教示する追加的な電極触媒の組成物では、約５５〜約７５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約５〜約２５原子パーセントの第三金属として銅、マンガンまたは鉄を含むようにしてもよい。   Additional electrocatalytic compositions taught by the present disclosure include about 55 to about 75 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 5 to about 25 atomic percent of the third metal, copper. Further, manganese or iron may be included.

さらに、本開示は燃料電池の電極触媒を提供し、この電極触媒の組成物は、約５５〜約９５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属の含有を必須とする構成である。この第三金属は、銅、マンガンおよび鉄からなる群から少なくとも１つを選択する。   Further, the present disclosure provides a fuel cell electrocatalyst, the electrocatalyst composition comprising about 55 to about 95 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 1 to about 30 atoms. It is the structure which requires content of the third metal of percent. The third metal is at least one selected from the group consisting of copper, manganese and iron.

膜と、薄膜型あるいは薄膜担持型の電極触媒と、薄膜型電極触媒とは異なる電極とで構成される燃料電池アッセンブリを提供する。薄膜型あるいは薄膜担持型の電極触媒は、プラチナ、チタンおよび第三金属の含有を必須とする組成物で構成するようにしてもよい。この電極触媒の組成物は、約５５〜約９５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属を含有するようにしてもよい。この第三金属は、銅、マンガンおよび鉄からなる群から少なくとも１つを選択してもよい。   Provided is a fuel cell assembly comprising a membrane, a thin film type or thin film supported type electrode catalyst, and an electrode different from the thin film type electrode catalyst. The thin film-type or thin film-supported electrode catalyst may be composed of a composition that essentially contains platinum, titanium, and a third metal. The electrocatalyst composition may include from about 55 to about 95 atomic percent platinum, from about 1 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal may be at least one selected from the group consisting of copper, manganese and iron.

追加的な実施形態の燃料電池アッセンブリでは、約５５〜約７５原子パーセントのプラチナと、約１０〜約２５原子パーセントのチタンと、約１０〜約２５原子パーセントの第三金属とを含有する組成物であってもよい。   In an additional embodiment fuel cell assembly, the composition comprises from about 55 to about 75 atomic percent platinum, from about 10 to about 25 atomic percent titanium, and from about 10 to about 25 atomic percent third metal. It may be.

さらに別の実施形態に係る燃料電池アッセンブリでは、約５５〜約９０原子パーセントのプラチナと、約３〜約２５原子パーセントのチタンと、約５〜約２５原子パーセントの銅とを含有する組成物であってもよい。さらに、追加的な実施形態の燃料電池アッセンブリでは、約５５〜約７０原子パーセントのプラチナと、約１５〜約２０原子パーセントのチタンと、約１０〜約２５原子パーセントの銅とを含有する組成物であってもよい。   In a fuel cell assembly according to yet another embodiment, a composition comprising about 55 to about 90 atomic percent platinum, about 3 to about 25 atomic percent titanium, and about 5 to about 25 atomic percent copper. There may be. Further, in an additional embodiment fuel cell assembly, a composition comprising about 55 to about 70 atomic percent platinum, about 15 to about 20 atomic percent titanium, and about 10 to about 25 atomic percent copper. It may be.

さらに別の実施形態の燃料電池アッセンブリでは、約５５〜約８０原子パーセントのプラチナと、約１０〜約２５原子パーセントのチタンと、約１０〜約２１原子パーセントのマンガンとを含有する組成物であってもよい。さらに、別の実施形態によっては、燃料電池アッセンブリは、約６０〜８０原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、約１０〜約１６原子パーセントのマンガンとを含有する組成物であってもよい。   In yet another embodiment of the fuel cell assembly, the composition comprises from about 55 to about 80 atomic percent platinum, from about 10 to about 25 atomic percent titanium, and from about 10 to about 21 atomic percent manganese. May be. Further, in some other embodiments, the fuel cell assembly includes a composition comprising about 60 to 80 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 10 to about 16 atomic percent manganese. It may be.

さらに別の実施形態の燃料電池アッセンブリでは、約６０〜約８０原子パーセントのプラチナと、約９〜約２５原子パーセントのチタンと、約７〜約２２原子パーセントの鉄とを含有する組成物であってもよい。さらに、追加的な実施形態の燃料電池アッセンブリでは、約６０〜約７５原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、約１４〜約２２原子パーセントの鉄とを含有する組成物であってもよい。   Yet another embodiment of a fuel cell assembly is a composition comprising about 60 to about 80 atomic percent platinum, about 9 to about 25 atomic percent titanium, and about 7 to about 22 atomic percent iron. May be. Further, in an additional embodiment fuel cell assembly, a composition comprising about 60 to about 75 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 14 to about 22 atomic percent iron. It may be.

本開示が教示する追加的な燃料電池アッセンブリでは、約５５〜約７５原子パーセントのプラチナと、約１〜約３０原子パーセントのチタンと、約５〜約２５原子パーセントの第三金属からなる組成物であってもよい。   In an additional fuel cell assembly taught by the present disclosure, a composition comprising about 55 to about 75 atomic percent platinum, about 1 to about 30 atomic percent titanium, and about 5 to about 25 atomic percent third metal. It may be.

さらに、本開示は、プラチナとチタンと第三金属の含有を必須とする金属成分を含む電極触媒の組成物に関する。この電極触媒の組成物には、約５０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属を含むようにしてもよい。この第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択する。   Furthermore, this indication is related with the composition of the electrocatalyst containing the metal component which requires inclusion of platinum, titanium, and a 3rd metal. The electrocatalyst composition may include about 50 to about 85 atomic percent platinum, about 5 to about 30 atomic percent titanium, and about 1 to about 30 atomic percent third metal. The third metal is at least one selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold.

追加的な実施形態の電極触媒の組成物では、約６０〜約７５原子パーセントのプラチナと、約５〜約２５原子パーセントのチタンと、約１０〜約２０原子パーセントの第三金属を含むようにしてもよい。さらに別の実施形態に係る電極触媒の組成物では、約６０〜約７５原子パーセントのプラチナと、約８〜約２１原子パーセントのチタンと、約１５〜約２５原子パーセントの第三金属を含むようにしてもよい。
さらに追加的な実施形態の電極触媒の組成物では、約６０〜約７５原子パーセントのプラチナと、約８〜約２１原子パーセントのチタンと、約１５〜約２５原子パーセントのコバルトを含むようにしてもよい。 Additional embodiments of the electrocatalyst composition may comprise about 60 to about 75 atomic percent platinum, about 5 to about 25 atomic percent titanium, and about 10 to about 20 atomic percent third metal. Good. In another embodiment of the electrocatalyst composition, the composition comprises about 60 to about 75 atomic percent platinum, about 8 to about 21 atomic percent titanium, and about 15 to about 25 atomic percent third metal. Also good.
Still further embodiments of the electrocatalyst composition may comprise about 60 to about 75 atomic percent platinum, about 8 to about 21 atomic percent titanium, and about 15 to about 25 atomic percent cobalt. .

さらに別の実施形態に係る電極触媒の組成物では、約５０〜約６５原子パーセントのプラチナと、約１５〜約２５原子パーセントのチタンと、約１０〜約３０原子パーセントのパラジウムを含むようにしてもよい。   In yet another embodiment, the electrocatalyst composition may comprise about 50 to about 65 atomic percent platinum, about 15 to about 25 atomic percent titanium, and about 10 to about 30 atomic percent palladium. .

本開示は、燃料電池の電極触媒を提供し、この燃料電池の電極触媒は、約５０〜８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属の含有を必須とする電極触媒の組成物で構成される。この第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択する。   The present disclosure provides a fuel cell electrocatalyst comprising about 50 to 85 atomic percent platinum, about 5 to about 30 atomic percent titanium, and about 1 to about 30 atomic percent. It is comprised with the composition of the electrocatalyst which requires containing of a 3rd metal. The third metal is at least one selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold.

膜、薄膜型あるいは薄膜担持型の電極触媒と、薄膜型電極触媒とは異なる電極とからなる燃料電池アッセンブリを提供する。薄膜あるいは薄膜担持型の電極触媒は、プラチナと、チタンと、第三金属の含有を必須とする組成物で構成するようにしてもよい。この電極触媒の組成物は、約５０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属を含むようにしてもよい。この第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択するようにしてもよい。   Provided is a fuel cell assembly comprising a membrane, a thin film type or thin film supported type electrode catalyst, and an electrode different from the thin film type electrode catalyst. The thin-film or thin-film-supported electrode catalyst may be composed of a composition that essentially contains platinum, titanium, and a third metal. The electrocatalyst composition may comprise from about 50 to about 85 atomic percent platinum, from about 5 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal may be at least one selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold.

追加的な実施形態の燃料電池アッセンブリでは、電極触媒の組成物は、約６０〜約７５原子パーセントのプラチナと、約５〜約２５原子パーセントのチタンと、約１０〜約２０原子パーセントの第三金属を含むようにしてもよい。   In an additional embodiment fuel cell assembly, the electrocatalyst composition comprises about 60 to about 75 atomic percent platinum, about 5 to about 25 atomic percent titanium, and about 10 to about 20 atomic percent third. You may make it contain a metal.

別の実施形態の燃料電池アッセンブリでは、約６０〜約７５原子パーセントのプラチナと、約８〜約２１原子パーセントのチタンと、約１５〜約２５原子パーセントの第三金属を含むようにしてもよい。   Another embodiment fuel cell assembly may include about 60 to about 75 atomic percent platinum, about 8 to about 21 atomic percent titanium, and about 15 to about 25 atomic percent third metal.

さらに別の実施形態に係る燃料電池アッセンブリでは、電極触媒の組成物は、約６０〜約７５原子パーセントのプラチナと、約８〜約２１原子パーセントのチタンと、約１５〜約２５原子パーセントのコバルトを含むようにしてもよい。
さらに別の実施形態の燃料電池アッセンブリでは、電極触媒の組成物は、約５０〜約６５原子パーセントのプラチナと、約１５〜約２５原子パーセントのチタンと、約１０〜約３０原子パーセントのパラジウムを含むようにしてもよい。 In yet another embodiment of a fuel cell assembly, the electrocatalyst composition comprises about 60 to about 75 atomic percent platinum, about 8 to about 21 atomic percent titanium, and about 15 to about 25 atomic percent cobalt. May be included.
In yet another embodiment of the fuel cell assembly, the electrocatalyst composition comprises about 50 to about 65 atomic percent platinum, about 15 to about 25 atomic percent titanium, and about 10 to about 30 atomic percent palladium. It may be included.

さらに、本開示は、プラチナとチタンと第三金属と第四金属の含有を必須とし、さらに、オプションで第五金属を含有する金属成分を含む電極触媒の組成物に関する。この電極触媒の組成物は、約３０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属を含むようにしてもよい。この第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金から成る群から少なくとも１つを選択する。また、第四金属は約１〜約３０原子パーセントであってもよく、第５金属は約１〜約３０原子パーセントであってもよい。第四金属は、第三金属とは異なる金属であり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムから成る群から少なくとも１つを選択するようにしてもよい。オプションで追加する第五金属は、第三金属と第四金属とは異なる金属であって、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムから成る群から少なくとも１つを選択するようにしてもよい。   Furthermore, the present disclosure relates to a composition of an electrocatalyst that includes a metal component that essentially contains platinum, titanium, a third metal, and a fourth metal, and optionally includes a fifth metal. The electrocatalyst composition may include about 30 to about 85 atomic percent platinum, about 5 to about 30 atomic percent titanium, and about 1 to about 30 atomic percent of a third metal. The third metal is at least one selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. The fourth metal may also be about 1 to about 30 atomic percent and the fifth metal may be about 1 to about 30 atomic percent. The fourth metal is different from the third metal and consists of scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium. At least one may be selected from the group. The optional fifth metal is a different metal from the third and fourth metals, scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, At least one may be selected from the group consisting of tin, hafnium, tantalum and rhenium.

電極触媒の組成物の追加的な実施形態では、約６０〜約７０原子パーセントのプラチナと、約１０〜約３０原子パーセントのチタンと、約１〜約２０原子パーセントの第三金属を含むようにしてもよい。また、本開示の事例によっては、電極触媒の組成物は、第三金属として約１〜約２０原子パーセントのバナジウムを含有する、もしくは、第三金属として約１〜約２０原子パーセントのモリブデンを含む。   Additional embodiments of the electrocatalyst composition may include from about 60 to about 70 atomic percent platinum, from about 10 to about 30 atomic percent titanium, and from about 1 to about 20 atomic percent third metal. Good. Also, in some cases of the present disclosure, the electrocatalyst composition contains about 1 to about 20 atomic percent vanadium as the third metal, or contains about 1 to about 20 atomic percent molybdenum as the third metal. .

別の実施形態の電極触媒の組成物では、約５５〜約７０原子パーセントのプラチナと、約１５〜約２０原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントの銅を含むようにしてもよい。   In another embodiment, the electrocatalyst composition comprises from about 55 to about 70 atomic percent platinum, from about 15 to about 20 atomic percent titanium, and from about 10 to about 25 atomic percent copper as the third metal. Also good.

さらに別の実施形態では、電極触媒の組成物は、約６０〜８０原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントのマンガンを含むようにしてもよい。   In yet another embodiment, the electrocatalyst composition comprises about 60 to 80 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 10 to about 25 atomic percent manganese as the third metal. You may make it.

さらに、別の実施形態の電極触媒の組成物では、約６０〜約７５原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントの鉄を含むようにしてもよい。   Furthermore, another embodiment of the electrocatalyst composition comprises about 60 to about 75 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 10 to about 25 atomic percent iron as the third metal. It may be included.

さらに別の実施形態によっては、電極触媒の組成物は、約６０〜約７５原子パーセントのプラチナと、約５〜約２５原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントのコバルトを含むようにしてもよい。   In yet another embodiment, the electrocatalyst composition comprises about 60 to about 75 atomic percent platinum, about 5 to about 25 atomic percent titanium, and about 10 to about 25 atomic percent cobalt as the third metal. May be included.

別の実施形態の電極触媒の組成物では、第三金属として約１０〜約３０原子パーセントのパラジウムと、約５０〜約６５原子パーセントのプラチナと、約１５〜約２５原子パーセントのチタンとを含むようにしてもよい。   In another embodiment of the electrocatalyst composition, the third metal includes about 10 to about 30 atomic percent palladium, about 50 to about 65 atomic percent platinum, and about 15 to about 25 atomic percent titanium. You may make it.

本開示の追加的な実施形態では、プラチナとチタンとコバルトとパラジウムの含有を必須とする金属成分を含んでいる電極触媒の組成物に関する。この場合、プラチナは約３０〜約６０原子パーセント、チタンは約５〜約２０原子パーセント、コバルトは約４〜約２０原子パーセント、さらにパラジウムは約１５〜約３０原子パーセントがそれぞれ含まれるようにしてもよい。   An additional embodiment of the present disclosure relates to an electrocatalyst composition that includes a metal component that requires inclusion of platinum, titanium, cobalt, and palladium. In this case, platinum is included in an amount of about 30 to about 60 atomic percent, titanium is about 5 to about 20 atomic percent, cobalt is about 4 to about 20 atomic percent, and palladium is about 15 to about 30 atomic percent. Also good.

別の実施形態に係る電極触媒の組成物では、約４０〜約５５原子パーセントのプラチナと、約１３〜約２０原子パーセントのチタンと、約９〜約１６原子パーセントのコバルトと、約１８〜約２６原子パーセントのパラジウムとを含むようにしてもよい。   In an electrocatalyst composition according to another embodiment, about 40 to about 55 atomic percent platinum, about 13 to about 20 atomic percent titanium, about 9 to about 16 atomic percent cobalt, and about 18 to about It may contain 26 atomic percent palladium.

本開示は、プラチナ、チタン、第三金属、第四金属、オプションで第五金属の含有を必須とする電極触媒の組成物で構成される燃料電池の電極触媒を提供する。この電極触媒の組成物では、約３０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金から成る群から少なくとも１つを選択する。第四金属は約１〜約３０原子パーセント、第五金属は約１〜約３０原子パーセントが含まれるようにしてもよい。第四金属は、第三金属とは異なる金属で、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から少なくとも１つを選択するようにしてもよい。電極触媒の組成物にオプションの第五金属が含まれる場合、この第五金属は第三金属と第四金属とは異なる金属であり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から少なくとも１つを選択するようにしてもよい。   The present disclosure provides a fuel cell electrocatalyst comprising a composition of an electrocatalyst that requires the inclusion of platinum, titanium, third metal, fourth metal, and optionally fifth metal. The electrocatalyst composition may include from about 30 to about 85 atomic percent platinum, from about 5 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. The third metal is selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. The fourth metal may include from about 1 to about 30 atomic percent and the fifth metal from about 1 to about 30 atomic percent. The fourth metal is a metal different from the third metal, and is composed of scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium. You may make it select at least one from. If the composition of the electrocatalyst includes an optional fifth metal, the fifth metal is a different metal from the third and fourth metals, scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc At least one may be selected from the group consisting of yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium.

追加的な実施形態に係る燃料電池の電極触媒は、約６０〜約７０原子パーセントのプラチナと、約１０〜３０原子パーセントのチタンと、第三金属として約１〜約２０原子パーセントのニッケルとを含むようにしてもよい。さらに、本開示の事例によっては、第三金属として約１〜約２０原子パーセントのバナジウムを含んだ燃料電池の電極触媒、あるいは、第三金属として約１〜約２０原子パーセントのモリブデンを含んだ燃料電池の電極触媒を提供する。   The fuel cell electrocatalyst according to an additional embodiment comprises about 60 to about 70 atomic percent platinum, about 10 to 30 atomic percent titanium, and about 1 to about 20 atomic percent nickel as the third metal. It may be included. Further, in some cases of the present disclosure, fuel cell electrode catalysts containing about 1 to about 20 atomic percent vanadium as the third metal, or fuels containing about 1 to about 20 atomic percent molybdenum as the third metal. A battery electrode catalyst is provided.

別の実施形態の燃料電池の電極触媒では、約５５〜約７０原子パーセントのプラチナと、約１５〜２０原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントの銅とを含むようにしてもよい。   In another embodiment, the fuel cell electrocatalyst comprises about 55 to about 70 atomic percent platinum, about 15 to 20 atomic percent titanium, and about 10 to about 25 atomic percent copper as the third metal. Also good.

さらに追加的な実施形態に係る燃料電池の電極触媒では、約６０〜約８０原子パーセントのプラチナと、約１０〜２０原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントのマンガンとを含むようにしてもよい。   In a fuel cell electrocatalyst according to yet additional embodiments, about 60 to about 80 atomic percent platinum, about 10 to 20 atomic percent titanium, and about 10 to about 25 atomic percent manganese as a third metal. May be included.

さらに別の実施形態の燃料電池の電極触媒では、約６０〜約７５原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントの鉄とを含むようにしてもよい。   In yet another embodiment of the fuel cell electrocatalyst, about 60 to about 75 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 10 to about 25 atomic percent iron as the third metal. It may be included.

さらに、実施形態によっては、燃料電池の電極触媒は、約６０〜約７５原子パーセントのプラチナと、約５〜２５原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントのコバルトとを含むようにしてもよい。   Further, in some embodiments, the fuel cell electrocatalyst comprises about 60 to about 75 atomic percent platinum, about 5 to 25 atomic percent titanium, and about 10 to about 25 atomic percent cobalt as the third metal. It may be included.

別の実施形態に係る燃料電池の電極触媒では、第三金属として約１０〜約３０原子パーセントのパラジウムを含み、約５０〜約６５原子パーセントのプラチナと、約１５〜約２５原子パーセントのチタンとを含むようにしてもよい。   In another embodiment, the fuel cell electrocatalyst comprises from about 10 to about 30 atomic percent palladium as the third metal, from about 50 to about 65 atomic percent platinum, and from about 15 to about 25 atomic percent titanium. May be included.

また、燃料電池アッセンブリでは、約３０〜約６０原子パーセントのプラチナと、約５〜約２０原子パーセントのチタンと、約４〜約２０原子パーセントのコバルトと、約１５〜約３０原子パーセントのパラジウムの含有を必須とする電極触媒の組成物を利用する。別の実施形態の燃料電池アッセンブリでは、電極触媒の組成物は、約４０〜約５５原子パーセントのプラチナと、約１３〜約２０原子パーセントのチタンと、約９〜約１６原子パーセントのコバルトと、約１８〜約２６原子パーセントのパラジウムとを含むようにしてもよい。   The fuel cell assembly also includes about 30 to about 60 atomic percent platinum, about 5 to about 20 atomic percent titanium, about 4 to about 20 atomic percent cobalt, and about 15 to about 30 atomic percent palladium. An electrocatalyst composition that must be contained is used. In another embodiment of the fuel cell assembly, the electrocatalyst composition comprises about 40 to about 55 atomic percent platinum, about 13 to about 20 atomic percent titanium, about 9 to about 16 atomic percent cobalt, About 18 to about 26 atomic percent palladium.

膜、薄膜型あるいは薄膜担持型の電極触媒と、薄膜電極触媒とは異なる電極からなる燃料電池アッセンブリを提供する。薄膜型あるいは薄膜担持型の電極触媒は、プラチナ、チタン、第三金属、第四金属、さらに、オプションの第五金属の含有を必須とした金属成分で構成するようにしてもよい。この電極触媒の組成物には、約３０〜約８５原子パーセントのプラチナと、約５〜約３０原子パーセントのチタンと、約１〜約３０原子パーセントの第三金属とを含むようにしてもよい。この第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択する。第四金属は約１〜約３０原子パーセント含まれ、第五金属は約１〜約３０原子パーセント含まれるようにしてもよい。第四金属は第三金属とは異なる金属であり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から少なくとも１つを選択するようにしてもよい。第五金属が電極触媒の組成物に含まれる場合は、この第五金属は第三金属と第四金属とは異なる金属であり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタル、およびレニウムからなる群の少なくとも１つであってもよい。   Provided is a fuel cell assembly comprising a membrane, thin film type or thin film supported type electrode catalyst, and an electrode different from the thin film electrode catalyst. The thin-film or thin-film-supported electrode catalyst may be composed of a metal component that essentially contains platinum, titanium, a third metal, a fourth metal, and an optional fifth metal. The electrocatalyst composition may include from about 30 to about 85 atomic percent platinum, from about 5 to about 30 atomic percent titanium, and from about 1 to about 30 atomic percent third metal. This third metal is at least one selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. The fourth metal may comprise about 1 to about 30 atomic percent and the fifth metal may comprise about 1 to about 30 atomic percent. The fourth metal is a metal different from the third metal, and is composed of scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium. You may make it select at least one from. When the fifth metal is included in the composition of the electrocatalyst, the fifth metal is a metal different from the third metal and the fourth metal, scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, It may be at least one of the group consisting of yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum, and rhenium.

追加的な実施形態によっては、燃料電池アッセンブリの電極触媒の組成物は、約６０〜約７０原子パーセントのプラチナと、約１０〜約３０原子パーセントのチタンと、第三金属として約１〜約２０原子パーセントのニッケルを含むようにしてもよい。さらに、本開示の事例によっては、燃料電池アッセンブリは、第三金属として約１〜約２０原子パーセントのバナジウムを含む電極触媒の組成物、あるいは、第三金属として約１〜約２０原子パーセントのモリブデンを含む電極触媒の組成物が含まれる。   In some additional embodiments, the composition of the fuel cell assembly electrocatalyst comprises about 60 to about 70 atomic percent platinum, about 10 to about 30 atomic percent titanium, and about 1 to about 20 as the third metal. Atomic percent nickel may be included. Further, in some instances of the present disclosure, the fuel cell assembly comprises an electrocatalyst composition comprising about 1 to about 20 atomic percent vanadium as the third metal, or about 1 to about 20 atomic percent molybdenum as the third metal. A composition of an electrocatalyst comprising

さらに別の実施形態の燃料電池アッセンブリでは、電極触媒の組成物は、約５５〜約７０原子パーセントのプラチナと、約１５〜約２０原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントの銅を含むようにしてもよい。   In yet another embodiment of the fuel cell assembly, the electrocatalyst composition comprises about 55 to about 70 atomic percent platinum, about 15 to about 20 atomic percent titanium, and about 10 to about 25 atoms as the third metal. Percent copper may be included.

さらに追加的な実施形態の燃料電池アッセンブリは、電極触媒の組成物は、約６０〜約８０原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントのマンガンを含むようにしてもよい。   In yet an additional embodiment of the fuel cell assembly, the electrocatalyst composition comprises about 60 to about 80 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 10 to about 25 as the third metal. It may contain atomic percent manganese.

さらに別の実施形態の燃料電池アッセンブリでは、電極触媒の組成物は、約６０〜約７５原子パーセントのプラチナと、約１０〜約２０原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントの鉄を含むようにしてもよい。   In yet another embodiment of the fuel cell assembly, the electrocatalyst composition comprises about 60 to about 75 atomic percent platinum, about 10 to about 20 atomic percent titanium, and about 10 to about 25 atoms as the third metal. Percent iron may be included.

さらに別の実施形態に係る燃料電池アッセンブリでは、電極触媒の組成物は、約６０〜約７５原子パーセントのプラチナと、約５〜約２５原子パーセントのチタンと、第三金属として約１０〜約２５原子パーセントのコバルトを含むようにしてもよい。   In yet another embodiment of the fuel cell assembly, the electrocatalyst composition comprises about 60 to about 75 atomic percent platinum, about 5 to about 25 atomic percent titanium, and about 10 to about 25 as the third metal. It may contain atomic percent cobalt.

さらに、別の実施形態に係る燃料電池アッセンブリでは、電極触媒の組成物は、第三金属として約１０〜約３０原子パーセントのパラジウムと、約５０〜約６５原子パーセントのプラチナと、約１５〜約２５原子パーセントのチタンを含むようにしてもよい。   Further, in a fuel cell assembly according to another embodiment, the composition of the electrocatalyst comprises about 10 to about 30 atomic percent palladium, about 50 to about 65 atomic percent platinum, and about 15 to about It may contain 25 atomic percent titanium.

さらに、電極触媒の組成物と燃料電池の電極触媒は、ナノ粒子を含有する担持粉体の形態であってもよい。担持された粉体に含有されるナノ粒子の大きさは約０．５ｎｍ〜約１００ｎｍであり、前記の電極触媒の組成物からなるナノ粒子で構成されるようにしてもよい。   Further, the electrode catalyst composition and the fuel cell electrode catalyst may be in the form of a supported powder containing nanoparticles. The size of the nanoparticles contained in the supported powder is about 0.5 nm to about 100 nm, and may be composed of nanoparticles composed of the composition of the electrode catalyst.

実施形態に係る燃料電池の電極触媒の形態は様々なものが可能であり、例えば、薄膜、担体に担持された粉体、あるいは担持されたナノ粒子含有の粉体であってもよい。粉体の電極触媒およびナノ粒子含有の燃料電池の電極触媒は、例えば、カーボン黒などの高表面積炭素などの担体上に担持されるようにしてもよい。燃料電池の電極触媒の担体として、高表面積導電性の担体を用いてもよい。   Various forms of the electrode catalyst of the fuel cell according to the embodiment are possible, and for example, a thin film, a powder supported on a carrier, or a supported nanoparticle-containing powder may be used. The electrode catalyst of the powder and the electrode catalyst of the fuel cell containing nanoparticles may be supported on a carrier such as high surface area carbon such as carbon black. A high surface area conductive support may be used as a support for the electrode catalyst of the fuel cell.

燃料電池の電極触媒を、例えば、物理蒸着法で作成してもよい。物理蒸着法は、プラズマガンなどの所定の手段によって発生させたプラズマであってもよい。さらに、蒸着法の事例としては、例えば、イオンめっき、イオン注入、エバポレーション、レーザ表面合金化などがある。   The electrode catalyst of the fuel cell may be prepared by physical vapor deposition, for example. The physical vapor deposition may be plasma generated by a predetermined means such as a plasma gun. Further, examples of the vapor deposition method include ion plating, ion implantation, evaporation, and laser surface alloying.

燃料電池の電極触媒は、例えば、プラチナ金属とチタン金属に金属を追加して、これらを同時に蒸着して作成するようにしてもよい。あるいは、薄膜型の燃料電池を、各種金属の逐次蒸着法により作成してもよく、あるいは、電極触媒の組成物に含まれる各種金属を各種に組み合わせて同時に蒸着させたり、あるいは逐次蒸着させて作成するようにしてもよい。   For example, the electrode catalyst of the fuel cell may be formed by adding metal to platinum metal and titanium metal and vapor-depositing them simultaneously. Alternatively, a thin-film fuel cell may be prepared by a sequential deposition method of various metals, or it may be deposited by combining various metals contained in the composition of the electrode catalyst in various ways, or by sequential deposition. You may make it do.

担持型の電極触媒は粉体組成物であってもよい。粉体組成物は、湿式化学法などの所定の製造方法により作成するようにしてもよい。粉体は、所定の高表面積担体に担持されるようにしてもよい。高表面積担体は、例えば、炭素やアルミニウムであってもよい。高表面積とは、約１００ｍ２／ｇ以上の表面積を有する担体のことをいう。薄膜型電極触媒は、PEMFCのカソードでもよく、PEMFCの酸素還元反応を誘発するようにしてもよい。 The supported electrode catalyst may be a powder composition. The powder composition may be prepared by a predetermined manufacturing method such as a wet chemical method. The powder may be supported on a predetermined high surface area carrier. The high surface area support may be, for example, carbon or aluminum. High surface area refers to a carrier having a surface area of about 100 m 2 / g or more. The thin film type electrocatalyst may be a cathode of PEMFC or may induce an oxygen reduction reaction of PEMFC.

電極触媒の組成物は、薄膜型の組成物であってもよい。この薄膜型電極触媒は、薄膜の厚さがナノメートルからマイクロメートルであり、所定の基材に物理蒸着法や電気化学めっきを施して作成したものや、所望成分のインクを塗布して作成したものであってもよい。所望の薄膜を作成する方法は物理蒸着法でもよい。物理蒸着法とは、例えば、加熱、プラズマ、電子ビームなどによる蒸気成分を蒸着させる方法をいう。蒸着成分、この場合では、プラチナ、チタン、およびこれらに追加する金属を、同時にあるいは逐次に蒸着させるようにしてもよい。所定の作成方法は、米国特許公開公報第２００５−０１５０７６０号（２００５年７月１４日公開）に記載されている。   The composition of the electrode catalyst may be a thin film type composition. This thin film type electrocatalyst has a thin film thickness of nanometer to micrometer, and is prepared by applying a physical vapor deposition method or electrochemical plating to a predetermined base material, or by applying an ink of a desired component. It may be a thing. A physical vapor deposition method may be used as a method of forming a desired thin film. The physical vapor deposition method refers to a method of vapor-depositing a vapor component by heating, plasma, electron beam or the like, for example. The vapor deposition components, in this case, platinum, titanium, and the metal added thereto may be vapor deposited simultaneously or sequentially. The predetermined creation method is described in US Patent Publication No. 2005-0150760 (published July 14, 2005).

薄膜型の電極触媒はPEMFCのカソードであってもよく、PEMFCの酸化還元反応を誘発するようにしてもよい。   The thin film type electrocatalyst may be a cathode of PEMFC or may induce a redox reaction of PEMFC.

ここに記載される組成物すべてについてであるが、この電極触媒の組成物に含まれる金属の濃度は、電極触媒の性能を最適化するために変更してもよい。さらに、電極触媒の組成物は、作業環境や性能要求などの要因に応じて変更してもよい。   As for all of the compositions described herein, the concentration of metal contained in the composition of the electrocatalyst may be varied to optimize the performance of the electrocatalyst. Furthermore, the composition of the electrode catalyst may be changed according to factors such as work environment and performance requirements.

実施形態によっては、この電極触媒の組成物は、約６０〜約８０原子パーセントのプラチナ、あるいは、約６０〜約７０原子パーセントのプラチナを含むようにしてもよい。さらに、実施形態によっては、この電極触媒の組成物は、約５〜約２５原子パーセント、約１０〜約２０原子パーセント、約５〜約３０原子パーセント、または、約１０〜約３０原子パーセントのチタンを含むようにしてもよい。さらに、実施形態によっては、この電極触媒の組成物は、約１〜約２５原子パーセント、約５〜約２５原子パーセント、約１０〜約２０原子パーセント、または、約１〜約２０原子パーセントのニッケルを含むようにしてもよいし、あるいは、約１〜約２５原子パーセント、約５〜約２５原子パーセント、約１０〜約２０原子パーセント、または、約１〜約２０原子パーセントのモリブデンを含むようにしてもよいし、もしくは、約１〜約２５原子パーセント、約５〜約２５原子パーセント、約１０〜約２０原子パーセント、または、約１〜約２０原子パーセントのバナジウムを含むようにしてもよい。   In some embodiments, the electrocatalyst composition may include about 60 to about 80 atomic percent platinum, or about 60 to about 70 atomic percent platinum. Further, in some embodiments, the composition of the electrocatalyst is about 5 to about 25 atomic percent, about 10 to about 20 atomic percent, about 5 to about 30 atomic percent, or about 10 to about 30 atomic percent titanium. May be included. Further, in some embodiments, the composition of the electrocatalyst is about 1 to about 25 atomic percent, about 5 to about 25 atomic percent, about 10 to about 20 atomic percent, or about 1 to about 20 atomic percent nickel. Or about 1 to about 25 atomic percent, about 5 to about 25 atomic percent, about 10 to about 20 atomic percent, or about 1 to about 20 atomic percent molybdenum. Or about 1 to about 25 atomic percent, about 5 to about 25 atomic percent, about 10 to about 20 atomic percent, or about 1 to about 20 atomic percent vanadium.

別の実施形態によっては、この電極触媒の組成物は、約５５〜約７５原子パーセント、または約６０〜約７０原子パーセントのプラチナを含むようにしてもよい。さらに、この電極触媒の組成物は、約１０〜約２５原子パーセント、約１０〜約２０原子パーセント、約５〜約３０原子パーセント、または、約１０〜約３０原子パーセントのチタンを含むようにしてもよい。さらに、実施形態によっては、この電極触媒の組成物は、約１〜約２５原子パーセント、約５〜約２５原子パーセント、約１０〜約２０原子パーセント、または、約１〜約２０原子パーセントの銅を含むようにしてもよいし；約１〜約２５原子パーセント、約５〜約２５原子パーセント、約１０〜約２０原子パーセント、または、約１〜約２０原子パーセントのマンガンを含むようにしてもよいし；約１〜約２５原子パーセント、約５〜約２５原子パーセント、約１０〜約２０原子パーセント、または、約１〜約２０原子パーセントの鉄を含むようにしてもよい。   In other embodiments, the electrocatalyst composition may comprise about 55 to about 75 atomic percent, or about 60 to about 70 atomic percent of platinum. Further, the electrocatalyst composition may comprise about 10 to about 25 atomic percent, about 10 to about 20 atomic percent, about 5 to about 30 atomic percent, or about 10 to about 30 atomic percent titanium. . Further, in some embodiments, the electrocatalyst composition comprises about 1 to about 25 atomic percent, about 5 to about 25 atomic percent, about 10 to about 20 atomic percent, or about 1 to about 20 atomic percent copper. About 1 to about 25 atomic percent, about 5 to about 25 atomic percent, about 10 to about 20 atomic percent, or about 1 to about 20 atomic percent manganese; 1 to about 25 atomic percent, about 5 to about 25 atomic percent, about 10 to about 20 atomic percent, or about 1 to about 20 atomic percent of iron may be included.

さらに別の実施形態によっては、この電極触媒の組成物は、約３０原子パーセント、約４０原子パーセント、約５０原子パーセント、約６０原子パーセントのいずれかの低濃度から、約５５原子パーセント、約６０原子パーセント、約６５原子パーセント、約７５原子パーセント、約８５原子パーセントのいずれかの高濃度までの範囲でプラチナを含むようにしてもよい。また別の実施形態によっては、この電極触媒の組成物は、約５原子パーセント、約８原子パーセント、約１５原子パーセントのいずれかの低濃度から、約２０原子パーセント、約２１原子パーセント、約２５原子パーセント、約３０原子パーセントのいずれかの高濃度までの範囲でチタンを含むようにしてもよい。また、電極触媒に含有される第三金属は、実施形態によっては、約１原子パーセント、約１０原子パーセント、約１５原子パーセントのいずれかの低濃度から、約２０原子パーセント、約２５原子パーセント、約３０原子パーセントのいずれかの高濃度までの範囲で含有されるようにしてもよい。この第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から少なくとも１つを選択するようにしてもよい。好ましい実施形態によっては、この第三金属はコバルトまたはパラジウムであってもよい。コバルトは、約１原子パーセント、約４原子パーセント、約９原子パーセント、約１０原子パーセントのいずれかの低濃度から、約１６原子パーセント、約２０原子パーセント、約２５原子パーセントのいずれかの高濃度までの範囲で含有されるようにしてもよい。パラジウムは、約１原子パーセント、約１０原子パーセント、約１５原子パーセント、約１８原子パーセントのいずれかの低濃度から、約２０原子パーセント、約２５原子パーセント、約２６原子パーセント、約３０原子パーセントのいずれかの高濃度までの範囲で電極触媒の組成物に含有されるようにしてもよい。   In yet another embodiment, the composition of the electrocatalyst is from any low concentration of about 30 atomic percent, about 40 atomic percent, about 50 atomic percent, about 60 atomic percent, to about 55 atomic percent, about 60 atomic percent. Platinum may be included in ranges up to any high concentration of atomic percent, about 65 atomic percent, about 75 atomic percent, or about 85 atomic percent. In yet another embodiment, the electrocatalyst composition has a low concentration of any of about 5 atomic percent, about 8 atomic percent, or about 15 atomic percent, to about 20 atomic percent, about 21 atomic percent, about 25 atomic percent. Titanium may be included in a range up to a high concentration of either atomic percent or about 30 atomic percent. The third metal contained in the electrocatalyst, in some embodiments, can be as low as about 1 atomic percent, about 10 atomic percent, or about 15 atomic percent, to about 20 atomic percent, about 25 atomic percent, It may be contained in a range up to any high concentration of about 30 atomic percent. The third metal may be at least one selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. In some preferred embodiments, the third metal may be cobalt or palladium. Cobalt can be as low as any one of about 1 atomic percent, about 4 atomic percent, about 9 atomic percent, or about 10 atomic percent to any high concentration of about 16 atomic percent, about 20 atomic percent, or about 25 atomic percent. You may make it contain in the range up to. Palladium can be from any low concentration of about 1 atomic percent, about 10 atomic percent, about 15 atomic percent, about 18 atomic percent, to about 20 atomic percent, about 25 atomic percent, about 26 atomic percent, about 30 atomic percent. You may make it contain in the composition of an electrode catalyst in the range to any high concentration.

さらに別の実施形態では、電極触媒の組成物には、約３０原子パーセント、約４０原子パーセント、約５０原子パーセント、約５５原子パーセント、約６０原子パーセントのいずれかの低濃度から、約５５原子パーセント、約６０原子パーセント、約６５原子パーセント、約７０原子パーセント、約７５原子パーセント、約８０原子パーセント、約８５原子パーセントのいずれかの高濃度までの範囲でプラチナが含まれるようにしてもよい。実施形態によっては、電極触媒の組成物には、約５原子パーセント、約１０原子パーセント、約１３原子パーセント、約１５原子パーセントのいずれかの低濃度から、約２０原子パーセント、約２５原子パーセント、約３０原子パーセントのいずれかの高濃度までの範囲でチタンが含有されるようにしてもよい。また、実施形態によっては、電極触媒の組成物に含まれる第三金属は、約１原子パーセント、約１０原子パーセントのいずれかの低濃度から、約２０原子パーセント、約２５原子パーセント、約３０原子パーセントのいずれかの高濃度の範囲で含有されるようにしてもよい。第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群の少なくとも１つであってもよい。第四金属およびオプションの第五金属は、約１原子パーセントの低濃度から約３０原子パーセントの高濃度までの範囲で含有されるようにしてもよい。この第四金属およびオプションの第五金属は、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から少なくとも１つを選択するようにしてもよい。また、第四金属およびオプションの第五金属はそれぞれ、第三金属とは異なる金属である。コバルトは、約１原子パーセント、約４原子パーセント、約９原子パーセント、約１０原子パーセント、約１５原子パーセントのいずれかの低濃度から、約１６原子パーセント、約２０原子パーセント、約２５原子パーセント、約３０原子パーセントのいずれかの高濃度までの範囲で含有されるようにしてもよい。また、パラジウムは、約１原子パーセント、約１０原子パーセント、約１５原子パーセント、約１８原子パーセントのいずれかの低濃度から、約２０原子パーセント、約２５原子パーセント、約２６原子パーセント、約３０原子パーセントのいずれかの高濃度までの範囲で電極触媒の組成物に含有されるようにしてもよい。   In yet another embodiment, the electrocatalyst composition comprises from a low concentration of any of about 30 atomic percent, about 40 atomic percent, about 50 atomic percent, about 55 atomic percent, about 60 atomic percent, to about 55 atomic percent. Platinum may be included in a range up to any concentration of percent, about 60 atomic percent, about 65 atomic percent, about 70 atomic percent, about 75 atomic percent, about 80 atomic percent, about 85 atomic percent. . In some embodiments, the electrocatalyst composition includes any low concentration of about 5 atomic percent, about 10 atomic percent, about 13 atomic percent, about 15 atomic percent, to about 20 atomic percent, about 25 atomic percent, Titanium may be included in a range up to any high concentration of about 30 atomic percent. Also, in some embodiments, the third metal included in the electrocatalyst composition is from a low concentration of either about 1 atomic percent or about 10 atomic percent to about 20 atomic percent, about 25 atomic percent, or about 30 atoms. It may be contained in any high concentration range of percent. The third metal may be at least one of the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. The fourth metal and optional fifth metal may be contained in a range from a low concentration of about 1 atomic percent to a high concentration of about 30 atomic percent. The fourth metal and optional fifth metal are at least from the group consisting of scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium. One may be selected. The fourth metal and the optional fifth metal are different from the third metal, respectively. Cobalt can be from any low concentration of about 1 atomic percent, about 4 atomic percent, about 9 atomic percent, about 10 atomic percent, about 15 atomic percent to about 16 atomic percent, about 20 atomic percent, about 25 atomic percent, It may be contained in a range up to any high concentration of about 30 atomic percent. Palladium can also be from any low concentration of about 1 atomic percent, about 10 atomic percent, about 15 atomic percent, or about 18 atomic percent to about 20 atomic percent, about 25 atomic percent, about 26 atomic percent, about 30 atomic percent. It may be contained in the composition of the electrocatalyst in a range up to any high concentration of percent.

電極触媒の組成物に含有される金属は、いくつかの可能な酸化状態および構造のうち、任意の酸化状態および構造で存在することが可能である。この金属の酸化状態および構造は、例えば、化学構造、熱処理、水素含有かつまたは酸素含有の環境への暴露など、各種要因に依存する。可能な金属構造には、例えば、合金、混合酸化物、水素酸化物、混合水素化物、青銅、ぺロブスカイトなどが含まれてもよい。電極触媒の表面上の金属の構造は、電極触媒のバルク内に位置する金属の構造と異なっていてもよく、あるいは同じであってもよい。電極触媒の表面上にある金属の濃度は、電極触媒のバルク内に位置する金属の濃度と異なっていてもよく、あるいは同じであってもよい。   The metal contained in the electrocatalyst composition can be present in any of several possible oxidation states and structures. The oxidation state and structure of the metal depends on various factors such as chemical structure, heat treatment, exposure to hydrogen-containing and / or oxygen-containing environments. Possible metal structures may include, for example, alloys, mixed oxides, hydrogen oxides, mixed hydrides, bronze, perovskites, and the like. The structure of the metal on the surface of the electrocatalyst may be different from or the same as the structure of the metal located in the bulk of the electrocatalyst. The concentration of the metal on the surface of the electrocatalyst may be different from or the same as the concentration of the metal located in the bulk of the electrocatalyst.

組成物の金属成分は、電極触媒の表面あるいは表面上に存在するようにしてもよい。この金属成分は、酸化物と金属のいずれであってもよく、本開示に係る電極触媒の組成物構造の任意の位置に配置されるようにしてもよい。   The metal component of the composition may be present on or on the surface of the electrode catalyst. This metal component may be either an oxide or a metal, and may be disposed at an arbitrary position in the composition structure of the electrode catalyst according to the present disclosure.

本願明細書に記載される原子パーセントは、後述の実施例で説明する回転円盤電極により評価を行った後に、薄膜型の電極触媒組成物のＥＤＸ解析によって判定したものである。   The atomic percentage described in the specification of the present application is determined by EDX analysis of a thin film type electrocatalyst composition after being evaluated by a rotating disk electrode described in Examples described later.

ここに引用する刊行物、雑誌、書誌、特許、特許公報およびこの他の文献は、目的とするすべての内容をここに引用する。   All publications, journals, bibliographies, patents, patent publications and other references cited herein are hereby incorporated by reference in their entirety.

前記の記載内容は、本開示の好ましい実施形態に関するものであるが、この他の変形や修正は当業者には明らかであり、本開示の範囲から逸脱しない限りにおいて行うことができる。   Although the foregoing description relates to preferred embodiments of the present disclosure, other variations and modifications will be apparent to those skilled in the art and may be made without departing from the scope of the present disclosure.

以下の実施例は、本開示をより具体的に理解するために提示するものである。本開示の原理を例示する具体的な手法、条件、材料および報告のデータは、事例的なものであり、本開示の範囲を限定するものとして解釈されるべきではない。   The following examples are presented for a more specific understanding of the present disclosure. The specific techniques, conditions, materials, and reporting data illustrating the principles of the present disclosure are exemplary and should not be construed as limiting the scope of the present disclosure.

＜実施例＞
プラチナ、チタンと、これらに追加する金属の配分を各種変化させた組成物の薄膜試料を、プラズマで発生させた金属蒸気の物理蒸着法で作成した。なお、好ましい作成方法については、米国特許公開公報第２００５−０１５０７６０号（２００５年７月１４日公開）に記載されている。 <Example>
Thin film samples of compositions with various changes in the distribution of platinum and titanium and the metal added to these were prepared by physical vapor deposition of metal vapor generated by plasma. A preferable production method is described in US Patent Publication No. 2005-0150760 (published July 14, 2005).

プラチナ、チタンおよび追加の金属を含んだ電極触媒の酸化還元反応の活性度レベルについて、多数の材料の組成物を一度にスクリーニングできる流体力学的な回転円盤電極装置を用いて、電気化学的なスクリーニングを行った。なお、好ましいスクリーニング法については、米国特許公開公報第２００５−０１０３６４５号（２００５年５月１９日公開）に記載されている。   Electrochemical screening using a hydrodynamic rotating disk electrode device capable of screening a large number of material compositions at once for the redox activity level of electrocatalysts containing platinum, titanium and additional metals Went. A preferred screening method is described in US Patent Publication No. 2005-0103645 (published May 19, 2005).

直径５ｍｍのガラスカーボン電極（glassy carbon electrodes）に薄膜試料をコートした。電気化学的なクリーニングを行った後に、これらの試料を酸化還元反応セルの作用電極として用いて、その結果を以下の表１から表３までに示した。   A thin film sample was coated on glassy carbon electrodes having a diameter of 5 mm. After electrochemical cleaning, these samples were used as the working electrode of the redox reaction cell, and the results are shown in Tables 1 to 3 below.

表１から表５には、プラチナ、チタンおよび追加の金属それぞれの原子パーセントの一覧を示した。さらに、半波電位のシフト量（ΔE1/2）（単位：ｍＶ）と、純プラチナ薄膜に対するプラチナの質量分率ベースの相対活性度（R-Act）を、電圧が０．７Ｖの場合と０．８Ｖの場合とについて、試料ごとに表１から表５に示した。 Tables 1-5 list the atomic percentages for each of platinum, titanium, and additional metals. Furthermore, the amount of shift of the half-wave potential (ΔE 1/2 ) (unit: mV) and the relative activity (R-Act) based on the mass fraction of platinum with respect to the pure platinum thin film, when the voltage is 0.7V, Tables 1 to 5 show the case of 0.8 V for each sample.

図１から図４は、電圧が０．８Ｖの場合の、表３の各試料の純プラチナ薄膜に対する相対活性度と、評価済の薄膜電極に含まれるプラチナ、チタン、コバルト、パラジウムの原子パーセントとの関係をそれぞれ示したものである。   1 to 4 show the relative activities of each sample in Table 3 with respect to pure platinum thin film when the voltage is 0.8 V, and the atomic percentages of platinum, titanium, cobalt, and palladium contained in the evaluated thin film electrode. Each of these relationships is shown.

Figure 2009522100
Figure 2009522100

Figure 2009522100
Figure 2009522100

Figure 2009522100
Figure 2009522100

Figure 2009522100
Figure 2009522100

Figure 2009522100
Figure 2009522100

本開示の各種実施形態に関する前記の詳細な説明は、例示的かつ説明的な目的から行ったものである。したがって、本開示を包括的に説明したり、本開示を開示された実施形態に厳密に限定する意図からではない。多数の修正や変形が可能であることは当業者には明らかであろう。前記の実施形態は、本開示の原理や実用例を最適に説明するために記載されたものであり、本開示の各種実施形態を当業者が理解できるようにするためのものである。特定の用途に適するように各種修正をもって、本開示は付属の特許請求の範囲およびその均等物によって定義されることを意図したものである。   The foregoing detailed description of various embodiments of the present disclosure has been presented for purposes of illustration and description. Therefore, it is not intended to be exhaustive or to limit the present disclosure to the precise embodiments disclosed. It will be apparent to those skilled in the art that many modifications and variations are possible. The above embodiments are described in order to optimally explain the principles and practical examples of the present disclosure, and are intended to allow those skilled in the art to understand the various embodiments of the present disclosure. With various modifications to suit a particular application, the present disclosure is intended to be defined by the appended claims and their equivalents.

電圧が０．８Ｖの場合の、表５の各試料の純プラチナ薄膜に対する相対活性度と、プラチナの原子パーセントとの関係を示したものである。The relationship between the relative activity with respect to the pure platinum thin film of each sample of Table 5 in case a voltage is 0.8V, and the atomic percent of platinum is shown.

電圧が０．８Ｖの場合の、表５の各試料の純プラチナ薄膜に対する相対活性度と、チタンの原子パーセントとの関係を示したものである。The relationship between the relative activity with respect to the pure platinum thin film of each sample of Table 5 in case a voltage is 0.8V, and the atomic percent of titanium is shown.

電圧が０．８Ｖの場合の、表５の各試料の純プラチナ薄膜に対する相対活性度と、コバルトの原子パーセントとの関係を示したものである。The relationship between the relative activity with respect to the pure platinum thin film of each sample of Table 5 in case a voltage is 0.8V, and the atomic percent of cobalt is shown.

電圧が０．８Ｖの場合の、表５の各試料の純プラチナ薄膜に対する相対活性度と、パラジウムの原子パーセントとの関係を示したものである。The relationship between the relative activity with respect to the pure platinum thin film of each sample of Table 5 in case a voltage is 0.8V, and the atomic percent of palladium is shown.

Claims (90)

プラチナ、チタンおよび第三金属を含有する金属成分を含む電極触媒の組成物であって、
プラチナを５５〜８５原子パーセント、チタンを１〜３０原子パーセント、第三金属を１〜３０原子パーセント含み、
前記第三金属は、ニッケル、バナジウムおよびモリブデンからなる群から選ばれる少なくとも１つの金属である
ことを特徴とする電極触媒の組成物。 An electrocatalyst composition comprising a metal component comprising platinum, titanium and a third metal,
Containing 55-85 atomic percent platinum, 1-30 atomic percent titanium, 1-30 atomic percent tertiary metal,
The composition of an electrode catalyst, wherein the third metal is at least one metal selected from the group consisting of nickel, vanadium and molybdenum. プラチナを６０〜８０原子パーセント、チタンを５〜２５原子パーセント、前記第三金属を５〜２５原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, comprising 60 to 80 atomic percent of platinum, 5 to 25 atomic percent of titanium, and 5 to 25 atomic percent of said third metal. プラチナを６０〜８０原子パーセント、チタンを５〜３０原子パーセント、前記第三金属を１〜２５原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, comprising 60 to 80 atomic percent of platinum, 5 to 30 atomic percent of titanium, and 1 to 25 atomic percent of said third metal. プラチナを６０〜７０原子パーセント、チタンを１０〜２０原子パーセント、前記第三金属を１０〜２０原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, comprising 60 to 70 atomic percent of platinum, 10 to 20 atomic percent of titanium, and 10 to 20 atomic percent of said third metal. プラチナを６０〜７０原子パーセント、チタンを１０〜３０原子パーセント、前記第三金属を１〜２０原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, comprising 60 to 70 atomic percent of platinum, 10 to 30 atomic percent of titanium, and 1 to 20 atomic percent of said third metal. 前記第三金属はニッケルであり、１０〜２０原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, wherein the third metal is nickel and contains 10 to 20 atomic percent. 前記第三金属はニッケルであり、１〜２０原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, wherein the third metal is nickel and contains 1 to 20 atomic percent. 前記第三金属はバナジウムであり、１０〜２０原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, wherein the third metal is vanadium and contains 10 to 20 atomic percent. 前記第三金属はバナジウムであり、１〜２０原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, wherein the third metal is vanadium and contains 1 to 20 atomic percent. 前記第三金属はモリブデンであり、１０〜２０原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, wherein the third metal is molybdenum and contains 10 to 20 atomic percent. 前記第三金属はモリブデンであり、１〜２０原子パーセント含むことを特徴とする請求項１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 1, wherein the third metal is molybdenum and contains 1 to 20 atomic percent. 請求項１に記載の電極触媒の組成物を含むことを特徴とする薄膜型電極触媒。   A thin film type electrocatalyst comprising the composition of the electrocatalyst according to claim 1. 電極触媒と、膜と、電極とを備える燃料電池アッセンブリであって、
前記電極触媒は、プラチナ、チタンおよび第三金属を含有する組成物を含み、
プラチナを５５〜８５原子パーセント、チタンを１〜３０原子パーセント、前記第三金属を１〜３０原子パーセント含み、
前記第三金属は、ニッケル、バナジウムおよびモリブデンからなる群から選ばれる少なくとも１つの金属である
ことを特徴とする燃料電池アッセンブリ。 A fuel cell assembly comprising an electrode catalyst, a membrane, and an electrode,
The electrocatalyst includes a composition containing platinum, titanium, and a third metal,
Containing 55 to 85 atomic percent of platinum, 1 to 30 atomic percent of titanium, and 1 to 30 atomic percent of the third metal;
The fuel cell assembly, wherein the third metal is at least one metal selected from the group consisting of nickel, vanadium and molybdenum. プラチナを６０〜８０原子パーセント、チタンを５〜３０原子パーセント、前記第三金属を１〜２５原子パーセント含む
ことを特徴とする請求項１３に記載の燃料電池アッセンブリ。 The fuel cell assembly according to claim 13, comprising 60 to 80 atomic percent of platinum, 5 to 30 atomic percent of titanium, and 1 to 25 atomic percent of the third metal. プラチナを６０〜７０原子パーセント、チタンを１０〜３０原子パーセント、前記第三金属を１〜２０原子パーセント含む
ことを特徴とする請求項１３に記載の燃料電池アッセンブリ。 14. The fuel cell assembly according to claim 13, comprising 60 to 70 atomic percent of platinum, 10 to 30 atomic percent of titanium, and 1 to 20 atomic percent of the third metal. 前記第三金属はニッケルであり、１〜２０原子パーセント含むことを特徴とする請求項１３に記載の燃料電池アッセンブリ。   14. The fuel cell assembly according to claim 13, wherein the third metal is nickel and contains 1 to 20 atomic percent. 前記第三金属はバナジウムであり、１〜２０原子パーセント含むことを特徴とする請求項１３に記載の燃料電池アッセンブリ。   14. The fuel cell assembly according to claim 13, wherein the third metal is vanadium and contains 1 to 20 atomic percent. 前記第三金属はモリブデンであり、１〜２０原子パーセント含むことを特徴とする請求項１３に記載の燃料電池アッセンブリ。   14. The fuel cell assembly of claim 13, wherein the third metal is molybdenum and includes 1 to 20 atomic percent. 前記電極触媒は薄膜型電極触媒を含むことを特徴とする請求項１３に記載の燃料電池アッセンブリ。   14. The fuel cell assembly according to claim 13, wherein the electrode catalyst includes a thin film type electrode catalyst. 前記電極触媒は、担持された、ナノ粒子含有粉体からなる電極触媒を含むことを特徴とする請求項１３に記載の燃料電池アッセンブリ。   The fuel cell assembly according to claim 13, wherein the electrode catalyst includes a supported electrode catalyst made of powder containing nanoparticles. プラチナ、チタンおよび第三金属を含有する金属成分を含む電極触媒の組成物であって、
プラチナを５５〜９５原子パーセント、チタンを１〜３０原子パーセント、第三金属を１〜３０原子パーセント含み、
前記第三金属は、銅、マンガンおよび鉄からなる群から選ばれる少なくとも１つの金属である
ことを特徴とする電極触媒の組成物。 An electrocatalyst composition comprising a metal component comprising platinum, titanium and a third metal,
Containing 55-95 atomic percent platinum, 1-30 atomic percent titanium, 1-30 atomic percent tertiary metal,
The composition of an electrode catalyst, wherein the third metal is at least one metal selected from the group consisting of copper, manganese, and iron. プラチナを５５〜７５原子パーセント、チタンを１０〜２５原子パーセント、前記第三金属を１０〜２５原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, comprising 55 to 75 atomic percent of platinum, 10 to 25 atomic percent of titanium, and 10 to 25 atomic percent of said third metal. プラチナを５５〜９０原子パーセント、チタンを３〜２５原子パーセント、銅を５〜２５原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, comprising 55 to 90 atomic percent of platinum, 3 to 25 atomic percent of titanium, and 5 to 25 atomic percent of copper. プラチナを５５〜７０原子パーセント、チタンを１５〜２０原子パーセント、銅を１０〜２５原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, comprising 55 to 70 atomic percent of platinum, 15 to 20 atomic percent of titanium, and 10 to 25 atomic percent of copper. プラチナを５５〜８０原子パーセント、チタンを１０〜２５原子パーセント、マンガンを１０〜２１原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, comprising 55 to 80 atomic percent of platinum, 10 to 25 atomic percent of titanium, and 10 to 21 atomic percent of manganese. プラチナを６０〜８０原子パーセント、チタンを１０〜２０原子パーセント、マンガンを１０〜１６原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, comprising 60 to 80 atomic percent of platinum, 10 to 20 atomic percent of titanium, and 10 to 16 atomic percent of manganese. プラチナを６０〜８０原子パーセント、チタンを９〜２５原子パーセント、鉄を７〜２２原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, comprising 60 to 80 atomic percent of platinum, 9 to 25 atomic percent of titanium, and 7 to 22 atomic percent of iron. プラチナを６０〜７５原子パーセント、チタンを１０〜２０原子パーセント、鉄を１４〜２２原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, comprising 60 to 75 atomic percent of platinum, 10 to 20 atomic percent of titanium, and 14 to 22 atomic percent of iron. 前記第三金属は銅であり、１０〜２５原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, wherein the third metal is copper and comprises 10 to 25 atomic percent. 前記第三金属はマンガンであり、１０〜２５原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, wherein the third metal is manganese and contains 10 to 25 atomic percent. 前記第三金属は鉄であり、１０〜２５原子パーセント含むことを特徴とする請求項２１に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 21, wherein the third metal is iron and comprises 10 to 25 atomic percent. 請求項２１に記載の電極触媒の組成物を含むことを特徴とする薄膜型電極触媒。   A thin film type electrocatalyst comprising the composition of the electrocatalyst according to claim 21. 電極触媒と、膜と、電極とを備える燃料電池アッセンブリであって、
前記電極触媒は、プラチナ、チタンおよび第三金属を含有する組成物を含み、
プラチナを５５〜９５原子パーセント、チタンを１〜３０原子パーセント、前記第三金属を１〜３０原子パーセント含み、
前記第三金属は、銅、マンガンおよび鉄からなる群から選ばれる少なくとも１つの金属である
ことを特徴とする燃料電池アッセンブリ。 A fuel cell assembly comprising an electrode catalyst, a membrane, and an electrode,
The electrocatalyst includes a composition containing platinum, titanium, and a third metal,
Containing 55 to 95 atomic percent of platinum, 1 to 30 atomic percent of titanium, and 1 to 30 atomic percent of the third metal;
The fuel cell assembly, wherein the third metal is at least one metal selected from the group consisting of copper, manganese, and iron. プラチナを５５〜７５原子パーセント、チタンを１０〜２５原子パーセント、前記第三金属を１０〜２５原子パーセント含むことを特徴とする請求項３３に記載の燃料電池アッセンブリ。   34. The fuel cell assembly of claim 33, comprising 55 to 75 atomic percent of platinum, 10 to 25 atomic percent of titanium, and 10 to 25 atomic percent of the third metal. プラチナを５５〜９０原子パーセント、チタンを３〜２５原子パーセント、銅を５〜２５原子パーセント含むことを特徴とする請求項３３に記載の燃料電池アッセンブリ。   34. The fuel cell assembly of claim 33, comprising 55 to 90 atomic percent platinum, 3 to 25 atomic percent titanium, and 5 to 25 atomic percent copper. プラチナを５５〜７０原子パーセント、チタンを１５〜２０原子パーセント、銅を１０〜２５原子パーセント含むことを特徴とする請求項３３に記載の燃料電池アッセンブリ。   34. The fuel cell assembly of claim 33, comprising 55 to 70 atomic percent platinum, 15 to 20 atomic percent titanium, and 10 to 25 atomic percent copper. プラチナを５５〜８０原子パーセント、チタンを１０〜２５原子パーセント、マンガンを１０〜２１原子パーセント含むことを特徴とする請求項３３に記載の燃料電池アッセンブリ。   34. The fuel cell assembly of claim 33, comprising 55-80 atomic percent platinum, 10-25 atomic percent titanium, and 10-21 atomic percent manganese. プラチナを６０〜８０原子パーセント、チタンを１０〜２０原子パーセント、マンガンを１０〜１６原子パーセント含むことを特徴とする請求項３３に記載の燃料電池アッセンブリ。   34. The fuel cell assembly of claim 33, comprising 60 to 80 atomic percent platinum, 10 to 20 atomic percent titanium, and 10 to 16 atomic percent manganese. プラチナを６０〜８０原子パーセント、チタンを９〜２５原子パーセント、鉄を７〜２２原子パーセント含むことを特徴とする請求項３３に記載の燃料電池アッセンブリ。   34. The fuel cell assembly of claim 33, comprising 60-80 atomic percent platinum, 9-25 atomic percent titanium, and 7-22 atomic percent iron. プラチナを６０〜７５原子パーセント、チタンを１０〜２０原子パーセント、鉄を１４〜２２原子パーセント含むことを特徴とする請求項３３に記載の燃料電池アッセンブリ。   34. The fuel cell assembly of claim 33, comprising 60-75 atomic percent platinum, 10-20 atomic percent titanium, and 14-22 atomic percent iron. 前記電極触媒は薄膜型電極触媒を含むことを特徴とする請求項３３に記載の燃料電池アッセンブリ。   34. The fuel cell assembly according to claim 33, wherein the electrode catalyst includes a thin film type electrode catalyst. 前記電極触媒は、担持された、ナノ粒子含有粉体からなる電極触媒を含むことを特徴とする請求項３３に記載の燃料電池アッセンブリ。   34. The fuel cell assembly according to claim 33, wherein the electrode catalyst includes a supported electrode catalyst made of powder containing nanoparticles. プラチナ、チタンおよび第三金属を含有する金属成分を含む電極触媒の組成物であって、
プラチナを５０〜８５原子パーセント、チタンを５〜３０原子パーセント、第三金属を１〜３０原子パーセント含み、
前記第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から選ばれる少なくとも１つの金属である
ことを特徴とする電極触媒の組成物。 An electrocatalyst composition comprising a metal component comprising platinum, titanium and a third metal,
50 to 85 atomic percent platinum, 5 to 30 atomic percent titanium, 1 to 30 atomic percent third metal,
The composition of an electrode catalyst, wherein the third metal is at least one metal selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. プラチナを６０〜７５原子パーセント、チタンを５〜２５原子パーセント、前記第三金属を１０〜２０原子パーセント含むことを特徴とする請求項４３に記載の電極触媒の組成物。   44. The electrocatalyst composition of claim 43, comprising 60 to 75 atomic percent platinum, 5 to 25 atomic percent titanium, and 10 to 20 atomic percent of the third metal. 前記第三金属はコバルトであることを特徴とする請求項４４に記載の電極触媒の組成物。   45. The composition of an electrocatalyst according to claim 44, wherein the third metal is cobalt. プラチナを６０〜７５原子パーセント、チタンを８〜２１原子パーセント、前記第三金属を１５〜２５原子パーセント含むことを特徴とする請求項４３に記載の電極触媒の組成物。   44. The composition of an electrocatalyst according to claim 43, comprising 60 to 75 atomic percent of platinum, 8 to 21 atomic percent of titanium, and 15 to 25 atomic percent of said third metal. 前記第三金属はコバルトであることを特徴とする請求項４６に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 46, wherein the third metal is cobalt. プラチナを５０〜６５原子パーセント、チタンを１５〜２５原子パーセント、パラジウムを１０〜３０原子パーセント含むことを特徴とする請求項４３に記載の電極触媒の組成物。   44. The composition of an electrocatalyst according to claim 43, comprising 50 to 65 atomic percent of platinum, 15 to 25 atomic percent of titanium, and 10 to 30 atomic percent of palladium. 請求項４３に記載の電極触媒の組成物を含むことを特徴とする薄膜型電極触媒。   44. A thin film type electrocatalyst comprising the composition of the electrocatalyst according to claim 43. 電極触媒と、膜と、電極を備える燃料電池アッセンブリであって、
前記電極触媒は、プラチナ、チタンおよび第三金属を含有する金属成分を含み、
プラチナを５０〜８５原子パーセント、チタンを５〜３０原子パーセント、前記第三金属を１〜３０原子パーセント含み、
前記第三金属は、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から選ばれる少なくとも１つの金属である
ことを特徴とする燃料電池アッセンブリ。 A fuel cell assembly comprising an electrode catalyst, a membrane, and an electrode,
The electrocatalyst includes a metal component containing platinum, titanium, and a third metal,
Containing 50 to 85 atomic percent of platinum, 5 to 30 atomic percent of titanium, and 1 to 30 atomic percent of the third metal;
The fuel cell assembly, wherein the third metal is at least one metal selected from the group consisting of cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold. 前記金属成分は、プラチナを６０〜７５原子パーセント、チタンを５〜２５原子パーセント、前記第三金属を１０〜２０原子パーセント含むことを特徴とする請求項５０に記載の燃料電池アッセンブリ。   51. The fuel cell assembly of claim 50, wherein the metal component comprises 60 to 75 atomic percent of platinum, 5 to 25 atomic percent of titanium, and 10 to 20 atomic percent of the third metal. 前記第三金属はコバルトであることを特徴とする請求項５１に記載の燃料電池アッセンブリ。   52. The fuel cell assembly of claim 51, wherein the third metal is cobalt. 前記金属成分は、プラチナを６０〜７５原子パーセント、チタンを８〜２１原子パーセント、前記第三金属を１５〜２５原子パーセント含むことを特徴とする請求項５０に記載の燃料電池アッセンブリ。   51. The fuel cell assembly of claim 50, wherein the metal component comprises 60 to 75 atomic percent platinum, 8 to 21 atomic percent titanium, and 15 to 25 atomic percent third metal. 前記第三金属はコバルトであることを特徴とする請求項５３に記載の燃料電池アッセンブリ。   54. The fuel cell assembly of claim 53, wherein the third metal is cobalt. 前記金属成分は、プラチナを５０〜６５原子パーセント、チタンを１５〜２５原子パーセント、前記第三金属を１０〜３０原子パーセント含むことを特徴とする請求項５０に記載の燃料電池アッセンブリ。   51. The fuel cell assembly according to claim 50, wherein the metal component includes 50 to 65 atomic percent of platinum, 15 to 25 atomic percent of titanium, and 10 to 30 atomic percent of the third metal. 前記電極触媒は薄膜型電極触媒を含むことを特徴とする請求項５０に記載の燃料電池アッセンブリ。   51. The fuel cell assembly according to claim 50, wherein the electrode catalyst includes a thin film type electrode catalyst. 前記電極触媒は、担持された、ナノ粒子含有粉体からなる電極触媒を含むことを特徴とする請求項５０に記載の燃料電池アッセンブリ。   51. The fuel cell assembly according to claim 50, wherein the electrode catalyst includes a supported electrode catalyst made of nanoparticle-containing powder. プラチナ、チタン、第三金属および第四金属を含有する金属成分を含む電極触媒の組成物であって、
プラチナを３０〜８５原子パーセント、チタンを５〜３０原子パーセント、前記第三金属を１〜３０原子パーセント、前記第四金属を１〜３０原子パーセント含み、
前記第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から選択される少なくとも１つの金属であり、
前記第四金属は前記第三金属とは異なり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から選択される少なくとも１つの金属である
ことを特徴とする電極触媒の組成物。 A composition of an electrocatalyst comprising a metal component containing platinum, titanium, a third metal and a fourth metal,
30 to 85 atomic percent of platinum, 5 to 30 atomic percent of titanium, 1 to 30 atomic percent of the third metal, and 1 to 30 atomic percent of the fourth metal,
The third metal is at least one metal selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold,
The fourth metal is different from the third metal, and is composed of scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium. An electrocatalyst composition characterized in that it is at least one metal selected. 前記金属成分は、さらに、第五金属を１〜３０原子パーセント含み、
前記第五金属は、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から選択される少なくとも１つの金属であり、
前記第三金属と前記第四金属と前記第五金属とはそれぞれ異なる金属である
ことを特徴とする請求項５８に記載の電極触媒の組成物。 The metal component further comprises 1 to 30 atomic percent of a fifth metal;
The fifth metal is at least one metal selected from the group consisting of scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium. And
59. The composition of an electrode catalyst according to claim 58, wherein the third metal, the fourth metal, and the fifth metal are different from each other. プラチナを６０〜７０原子パーセント、チタンを１０〜３０原子パーセント含み、前記第三金属はニッケルであり、１〜２０原子パーセント含むことを特徴とする請求項５９に記載の電極触媒の組成物。   60. The composition of an electrocatalyst according to claim 59, comprising 60 to 70 atomic percent of platinum, 10 to 30 atomic percent of titanium, and said third metal being nickel and 1 to 20 atomic percent. 前記第三金属はバナジウムであり、１〜２０原子パーセント含むことを特徴とする請求項６０に記載の電極触媒の組成物。   61. The composition of an electrocatalyst according to claim 60, wherein the third metal is vanadium and contains 1 to 20 atomic percent. 前記第三金属はモリブデンであり、１〜２０原子パーセント含むことを特徴とする請求項６０に記載の電極触媒の組成物。   61. The composition of an electrocatalyst according to claim 60, wherein the third metal is molybdenum and comprises 1 to 20 atomic percent. プラチナを５５〜７０原子パーセント、チタンを１５〜２０原子パーセント含み、前記第三金属は銅であり、１０〜２５原子パーセント含むことを特徴とする請求項５９に記載の電極触媒の組成物。   60. The composition of an electrocatalyst according to claim 59, comprising 55 to 70 atomic percent of platinum, 15 to 20 atomic percent of titanium, and said third metal being copper and 10 to 25 atomic percent. プラチナを６０〜８０原子パーセント、チタンを１０〜２０原子パーセント含み、前記第三金属はマンガンであり、１０〜２５原子パーセント含むことを特徴とする請求項５９に記載の電極触媒の組成物。   60. The composition of an electrocatalyst according to claim 59, comprising 60-80 atomic percent of platinum, 10-20 atomic percent of titanium, and said third metal being manganese, comprising 10-25 atomic percent. プラチナを６０〜７５原子パーセント、チタンを１０〜２０原子パーセント含み、前記第三金属は鉄であり、１０〜２５原子パーセント含むことを特徴とする請求項５９に記載の電極触媒の組成物。   60. The composition of an electrocatalyst according to claim 59, comprising 60 to 75 atomic percent of platinum, 10 to 20 atomic percent of titanium, and said third metal being iron and 10 to 25 atomic percent. プラチナを６０〜７５原子パーセント、チタンを５〜２５原子パーセント含み、前記第三金属はコバルトであり、１０〜２５原子パーセント含むことを特徴とする請求項５９に記載の電極触媒の組成物。   60. The composition of an electrocatalyst according to claim 59, comprising 60 to 75 atomic percent of platinum, 5 to 25 atomic percent of titanium, and said third metal being cobalt and 10 to 25 atomic percent. プラチナを５０〜６５原子パーセント、チタンを１５〜２５原子パーセント含み、前記第三金属はパラジウムであり、１０〜３０原子パーセント含むことを特徴とする請求項５９に記載の電極触媒の組成物。   60. The composition of an electrocatalyst according to claim 59, comprising 50 to 65 atomic percent of platinum, 15 to 25 atomic percent of titanium, and said third metal being palladium, comprising 10 to 30 atomic percent. 請求項５８に記載の電極触媒の組成物を含むことを特徴とする薄膜型電極触媒。   59. A thin film type electrocatalyst comprising the composition of the electrocatalyst according to claim 58. プラチナ、チタン、第三金属、第四金属および第五金属を含有する金属成分を含む電極触媒の組成物であって、
プラチナを３０〜８５原子パーセント、チタンを５〜３０原子パーセント、前記第三金属を１〜３０原子パーセント、前記第四金属を１〜３０原子パーセント、前記第五金属を１〜３０原子パーセント含み、
前記第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から選ばれる少なくとも１つの金属であり、
前記第四金属は前記第三金属とは異なり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から選ばれる少なくとも１つの金属であり、
前記第五金属は、前記第三金属および前記第四金属とは異なり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から選ばれる少なくとも１つの金属である
ことを特徴とする電極触媒の組成物。 A composition of an electrocatalyst comprising a metal component containing platinum, titanium, third metal, fourth metal and fifth metal,
30 to 85 atomic percent of platinum, 5 to 30 atomic percent of titanium, 1 to 30 atomic percent of the third metal, 1 to 30 atomic percent of the fourth metal, and 1 to 30 atomic percent of the fifth metal,
The third metal is at least one metal selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold,
The fourth metal is different from the third metal, and is composed of scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium. At least one metal selected,
Unlike the third metal and the fourth metal, the fifth metal is scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum. And at least one metal selected from the group consisting of rhenium. プラチナを６０〜７０原子パーセント、チタンを１０〜３０原子パーセント含み、前記第三金属はニッケルであり、１〜２０原子パーセント含むことを特徴とする請求項６９に記載の電極触媒の組成物。   70. The composition of an electrocatalyst according to claim 69, comprising 60-70 atomic percent platinum, 10-30 atomic percent titanium, and said third metal being nickel, comprising 1-20 atomic percent. 前記第三金属はバナジウムであり、１〜２０原子パーセント含むことを特徴とする請求項７０に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 70, wherein the third metal is vanadium and contains 1 to 20 atomic percent. 前記第三金属はモリブデンであり、１〜２０原子パーセント含むことを特徴とする請求項７０に記載の電極触媒の組成物。   The composition of an electrocatalyst according to claim 70, wherein the third metal is molybdenum and contains 1 to 20 atomic percent. プラチナを５５〜７０原子パーセント、チタンを１５〜２０原子パーセント含み、前記第三金属は銅であり、１０〜２５原子パーセント含むことを特徴とする請求項６９に記載の電極触媒の組成物。   70. The composition of an electrocatalyst according to claim 69, comprising 55 to 70 atomic percent platinum, 15 to 20 atomic percent titanium, and said third metal being copper and 10 to 25 atomic percent. プラチナを６０〜８０原子パーセント、チタンを１０〜２０原子パーセント含み、前記第三金属はマンガンであり、１０〜２５原子パーセント含むことを特徴とする請求項６９に記載の電極触媒の組成物。   70. The composition of an electrocatalyst according to claim 69, comprising 60 to 80 atomic percent of platinum, 10 to 20 atomic percent of titanium, and said third metal being manganese, comprising 10 to 25 atomic percent. プラチナを６０〜７５原子パーセント、チタンを１０〜２０原子パーセント含み、前記第三金属は鉄であり、１０〜２５原子パーセント含むことを特徴とする請求項６９に記載の電極触媒の組成物。   70. The composition of an electrocatalyst according to claim 69, comprising 60 to 75 atomic percent of platinum, 10 to 20 atomic percent of titanium, and said third metal being iron and 10 to 25 atomic percent. プラチナを６０〜７５原子パーセント、チタンを５〜２５原子パーセント含み、前記第三金属はコバルトであり、１０〜２５原子パーセント含むことを特徴とする請求項６９に記載の電極触媒の組成物。   70. The composition of an electrocatalyst according to claim 69, comprising 60-75 atomic percent platinum, 5-25 atomic percent titanium, and said third metal being cobalt, comprising 10-25 atomic percent. プラチナを５０〜６５原子パーセント、チタンを１５〜２５原子パーセント含み、前記第三金属はパラジウムであり、１０〜３０原子パーセント含むことを特徴とする請求項６９に記載の電極触媒の組成物。   70. The composition of an electrocatalyst according to claim 69, comprising 50 to 65 atomic percent of platinum, 15 to 25 atomic percent of titanium, and said third metal being palladium, comprising 10 to 30 atomic percent. 請求項６９に記載の電極触媒を含むことを特徴とする薄膜型電極触媒。   70. A thin film electrode catalyst comprising the electrode catalyst according to claim 69. プラチナ、チタン、コバルトおよびパラジウムを含有する金属成分を含む電極触媒の組成物であって、
プラチナを３０〜６０原子パーセント、チタンを５〜２０原子パーセント、コバルトを４〜２０原子パーセント、パラジウムを１５〜３０原子パーセント含むことを特徴とする電極触媒の組成物。 An electrocatalyst composition comprising a metal component containing platinum, titanium, cobalt and palladium,
An electrocatalyst composition comprising 30 to 60 atomic percent of platinum, 5 to 20 atomic percent of titanium, 4 to 20 atomic percent of cobalt, and 15 to 30 atomic percent of palladium. 前記金属成分は、プラチナを４０〜５５原子パーセント、チタンを１３〜２０原子パーセント、コバルトを９〜１６原子パーセント、パラジウムを１８〜２６原子パーセント含むことを特徴とする請求項７９に記載の電極触媒の組成物。   80. The electrocatalyst of claim 79, wherein the metal component comprises 40-55 atomic percent platinum, 13-20 atomic percent titanium, 9-16 atomic percent cobalt, and 18-26 atomic percent palladium. Composition. 電極触媒と、膜と、電極とを備える燃料電池アッセンブリであって、
前記電極触媒は、プラチナ、チタン、第三金属、第四金属および第五金属を含有する金属成分を含む組成物を含み、
プラチナを３０〜８５原子パーセント、チタンを５〜３０原子パーセント、前記第三金属を１〜３０原子パーセント、前記第四金属を１〜３０原子パーセント、前記第五金属を１〜３０原子パーセント含み、
前記第三金属は、ニッケル、バナジウム、モリブデン、銅、マンガン、鉄、コバルト、ルテニウム、ロジウム、パラジウム、銀、オスミウム、イリジウムおよび金からなる群から選ばれる少なくとも１つの金属であり、
前記第四金属は前記第三金属とは異なり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から選らばれる少なくとも１つの金属であり、
前記第五金属は前記第三金属および第四金属とは異なり、スカンジウム、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、イットリウム、ジルコニウム、ニオビウム、モリブデン、カドミウム、スズ、ハフニウム、タンタルおよびレニウムからなる群から選ばれる少なくとも１つの金属である
ことを特徴とする燃料電池アッセンブリ。 A fuel cell assembly comprising an electrode catalyst, a membrane, and an electrode,
The electrocatalyst comprises a composition comprising a metal component containing platinum, titanium, a third metal, a fourth metal and a fifth metal,
30 to 85 atomic percent of platinum, 5 to 30 atomic percent of titanium, 1 to 30 atomic percent of the third metal, 1 to 30 atomic percent of the fourth metal, and 1 to 30 atomic percent of the fifth metal,
The third metal is at least one metal selected from the group consisting of nickel, vanadium, molybdenum, copper, manganese, iron, cobalt, ruthenium, rhodium, palladium, silver, osmium, iridium and gold,
The fourth metal is different from the third metal, and is composed of scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium. At least one metal selected,
The fifth metal is different from the third metal and the fourth metal, and is scandium, vanadium, chromium, manganese, iron, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, cadmium, tin, hafnium, tantalum and rhenium. A fuel cell assembly comprising at least one metal selected from the group consisting of: プラチナを６０〜７０原子パーセント、チタンを１０〜３０原子パーセント含み、前記第三金属はニッケルであり、１〜２０原子パーセント含むことを特徴とする請求項８１に記載の燃料電池アッセンブリ。   82. The fuel cell assembly of claim 81, comprising 60-70 atomic percent platinum, 10-30 atomic percent titanium, and the third metal being nickel, comprising 1-20 atomic percent. 前記第三金属はバナジウムであり、１〜２０原子パーセント含むことを特徴とする請求項８２に記載の燃料電池アッセンブリ。   83. The fuel cell assembly of claim 82, wherein the third metal is vanadium and includes 1 to 20 atomic percent. 前記第三金属はモリブデンであり、１〜２０原子パーセント含むことを特徴とする請求項８２に記載の燃料電池アッセンブリ。   83. The fuel cell assembly of claim 82, wherein the third metal is molybdenum and contains 1 to 20 atomic percent. プラチナを５５〜７０原子パーセント、チタンを１５〜２０原子パーセント含み、前記第三金属は銅であり、１０〜２５原子パーセント含むことを特徴とする請求項８１に記載の燃料電池アッセンブリ。   82. The fuel cell assembly of claim 81, comprising 55 to 70 atomic percent platinum, 15 to 20 atomic percent titanium, and the third metal being copper, comprising 10 to 25 atomic percent. プラチナを６０〜８０原子パーセント、チタンを１０〜２０原子パーセント含み、前記第三金属はマンガンであり、１０〜２５原子パーセント含むことを特徴とする請求項８１に記載の燃料電池アッセンブリ。   82. The fuel cell assembly of claim 81, comprising 60-80 atomic percent platinum, 10-20 atomic percent titanium, and the third metal being manganese, comprising 10-25 atomic percent. プラチナを６０〜７５原子パーセント、チタンを１０〜２０原子パーセント含み、前記第三金属は鉄であり、１０〜２５原子パーセント含むことを特徴とする請求項８１に記載の燃料電池アッセンブリ。   82. The fuel cell assembly of claim 81, comprising 60 to 75 atomic percent platinum, 10 to 20 atomic percent titanium, and the third metal being iron and 10 to 25 atomic percent. プラチナを６０〜７５原子パーセント、チタンを５〜２５原子パーセント含み、前記第三金属はコバルトであり、１０〜２５原子パーセント含むことを特徴とする請求項８１に記載の燃料電池アッセンブリ。   82. The fuel cell assembly of claim 81, comprising 60 to 75 atomic percent platinum, 5 to 25 atomic percent titanium, and the third metal being cobalt and 10 to 25 atomic percent. プラチナを５０〜６５原子パーセント、チタンを１５〜２５原子パーセント含み、前記第三金属はパラジウムであり、１０〜３０原子パーセント含むことを特徴とする請求項８１に記載の燃料電池アッセンブリ。   82. The fuel cell assembly of claim 81, comprising 50 to 65 atomic percent platinum, 15 to 25 atomic percent titanium, and the third metal being palladium, comprising 10 to 30 atomic percent. 前記電極触媒は薄膜型電極触媒を含むことを特徴とする請求項８１に記載の燃料電池アッセンブリ。
82. The fuel cell assembly of claim 81, wherein the electrode catalyst includes a thin film type electrode catalyst.
JP2008549565A 2006-01-06 2007-01-05 Electrocatalysts containing platinum and titanium Active JP5425472B2 (en)