JP2009281109A - Method for removing asbestos-contained coating layer on wall face of tunnel or the like - Google Patents
Method for removing asbestos-contained coating layer on wall face of tunnel or the like Download PDFInfo
- Publication number
- JP2009281109A JP2009281109A JP2008136938A JP2008136938A JP2009281109A JP 2009281109 A JP2009281109 A JP 2009281109A JP 2008136938 A JP2008136938 A JP 2008136938A JP 2008136938 A JP2008136938 A JP 2008136938A JP 2009281109 A JP2009281109 A JP 2009281109A
- Authority
- JP
- Japan
- Prior art keywords
- asbestos
- liquid
- stripping
- coating layer
- wall surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、吸音、耐火などのために、自動車や電車などが走るトンネルや道路などの壁面に施されたアスベスト含有被覆層を安全に剥ぎ取り処理するための方法に関する。 The present invention relates to a method for safely stripping off an asbestos-containing coating layer applied to a wall surface of a tunnel or a road where automobiles, trains, and the like run for sound absorption and fire resistance.
アスベストは，断熱性、耐熱性、吸音性など工業的に優れた特性を持っているために、建築、土木関係などで、被覆材として広く採用されてきた。自動車や電車などが通るトンネル、地下鉄などの壁面や道路などの壁にも、吸音性や耐火性を上げる目的で被覆材として使用されてきた。かし、最近になって、アスベストに起因すると思われる肺ガン、中皮腫患者が増加して大きな社会問題になっている。そして、アスベスト含有量がある値以上のものは使用禁止になっているが、すでに用いられているものについても安全に剥ぎ取り、最終処分することが必要とされている。 Asbestos has been widely adopted as a coating material in construction and civil engineering because it has industrially superior characteristics such as heat insulation, heat resistance, and sound absorption. It has been used as a covering material for the purpose of improving sound absorption and fire resistance on tunnels through which cars and trains pass, walls of subways, and road walls. However, recently, the number of patients with lung cancer and mesothelioma, which are thought to be caused by asbestos, has become a major social problem. And asbestos content exceeding a certain value is forbidden to use, but already used one is required to be peeled off safely and finally disposed.
建物の場合には、普通、剥ぎ取りを行う場所を養生シートで隔離して、密閉された空間内で剥ぎ取り作業が行われるが、本発明が対象とするトンネルなどの壁面の場合には、交通への影響から作業可能時間が限定されていて迅速に作業を進めなければならないという要求があり、また、密閉することがむつかしいという問題がある。特許文献１には、トンネルなどの長大構造物内で、人力によるアスベスト含有層を剥ぎ取る作業を密閉された空間内で行う方法として、複数の着脱自在の遮蔽パネルで覆う工程と、長大構造物の延伸方向に移動可能に載置された前記遮蔽パネルに対向する面が開口可能な作業函体を所定の位置に移動させる工程と、前記遮蔽パネル方向に作業函体を移動させるとともに養生シートを展開して形成した作業エリア内から遮蔽パネルを外す工程と、作業エリアに連通する範囲内のアスベストを含有する被覆層を除去する工程と、その後に遮蔽パネルを元の位置に戻して取り付ける工程からなる方法が示されている。これは移動可能な作業函体の中でアスベスト含有物の剥ぎ取り作業を行う方法であり、作業効率や作業者への負荷などに課題が残されている。
建築物でのアスベスト含有被覆層の剥ぎ取りについては、従来、ヘラ、ブラシ、スクレーパーなどを用いた手作業で行われてきた。これに対して、より効率的に行うために高圧液体を使う方法が示されている。たとえば、特許文献２には、圧縮エアーと高圧水の混合ジェット噴流による直接洗浄を行う手段によって剥離するとともに、隔離養生内を噴霧状態にして剥離された石綿（アスベスト）と噴霧水滴が交じり合って落下することによって泥状になる方法が示されている。また、特許文献３には、耐火性被覆材を剥離する水の周囲を、同じく耐火性被覆材に吹き付けられる圧力水によって形成される水カーテンで囲み、剥離された耐火被覆材を水カーテンで外に飛散しないようにして、剥離した耐火被覆材を水とともに回収して固液分離処理する方法が示されている。しかし、これらの方法は、トンネル壁面などに対して行なうには剥ぎ取り物や水の処理などに多くの課題が残されている。
特許文献４には、走行しながらトンネルなどの壁面に高圧ノズルから噴出させた液体を作用させる方法が示されている。しかし、これは壁面の汚れを洗浄することを目的とするものであって、アスベスト含有被覆層の剥離作業に適用できるものではない。
The stripping of the asbestos-containing coating layer in a building has been conventionally performed manually using a spatula, a brush, a scraper, or the like. On the other hand, a method of using a high-pressure liquid to perform more efficiently is shown. For example, in
Patent Document 4 discloses a method in which a liquid ejected from a high-pressure nozzle acts on a wall surface of a tunnel or the like while traveling. However, this is intended to clean the dirt on the wall surface and is not applicable to the asbestos-containing coating layer peeling operation.
本発明は、トンネル、地下鉄、道路などの壁面に施されたアスベスト含有被覆層を、走行しながらアスベストの飛散を防止しつつ液体ジェットで剥ぎ取り、剥ぎ取り物の回収、圧縮、減容、搾り出された液体の浄化と剥ぎ取り処理への循環使用などを可能にし、効率的な作業、アスベストの飛散防止および発生物の処理を合わせて行うための方法である。 The present invention is an asbestos-containing coating layer applied to the walls of tunnels, subways, roads, etc., and stripped with a liquid jet while preventing asbestos from being scattered while traveling, and recovery, compression, volume reduction, and squeezing of the stripped material This is a method for purifying the discharged liquid and circulating it for the stripping process, etc., and performing efficient work, prevention of asbestos scattering and treatment of generated products.
上記の課題を解決するための具体的手段の第1は、トンネルなどの壁面のアスベスト含有被覆物の除去処理を、移動できる台車に載せられた２連あるいは３連以上の液体ジェット吹き付け装置、そのジェットで剥ぎ取られたアスベスト含有物を受け止める器具、受け止められたものを移送して圧縮、成型する装置を用いて、走行しながら液体ジェットによるアスベスト含有物の第１次剥ぎ取り（粗剥ぎ取り）と、第１次剥ぎ取りされた後の面の仕上げのための処理を並行して行うことである。 The first of the concrete means for solving the above-mentioned problem is to remove the asbestos-containing coating on the wall surface of a tunnel or the like, a liquid jet spraying device having two or three or more liquid jets mounted on a movable carriage, Primary stripping (coarse stripping) of asbestos-containing material with a liquid jet while running using a device that receives the asbestos-containing material stripped by the jet, and a device that transports and compresses the received asbestos-containing material. And processing for finishing the surface after the first stripping is performed in parallel.
具体的手段の第２は、０００５において、ジェットに使用する液体としてシリコーン樹脂乳化液を用い、シリコーン樹脂の濃度は第１次剥ぎ取り（粗剥ぎ取り）に用いる液体よりも、第１次剥ぎ取りされた後の面の仕上げのための処理に用いる液体の方を高くすることである。 The second specific means is that in 0005, a silicone resin emulsion is used as the liquid used in the jet, and the concentration of the silicone resin is higher than the liquid used for the first peeling (rough peeling). The liquid used for finishing the finished surface is made higher.
具体的手段の第３は、０００５あるいは０００６において、アスベスト含有物剥ぎ取り作業が終了後、一般の交通が再開されるまでの間に、作業対象になった箇所に対して熱風吹き付けによる乾燥作業が行なわれることである。 The third specific means is that in 0005 or 0006, after the asbestos-containing material stripping operation is completed, until the general traffic is resumed, a drying operation by hot air blowing is performed on the target site. Is to be done.
具体的手段の第４は、０００５において、ジェットで剥ぎ取られたアスベスト含有物を受け止める器具と処理対象の壁面の間の空間を吸引することによって、アスベスト繊維の飛散を防止することである。 A fourth specific means is to prevent scattering of asbestos fibers by sucking a space between a device receiving the asbestos-containing material peeled off by the jet and a wall surface to be treated in 0005.
具体的手段の第５は、圧縮時に搾り出され液を回収して中性凝集剤を加えて固体分の凝集、沈殿を行い、分離された液体をジェット吹き付けに循環使用することである。 The fifth specific means is to collect the liquid squeezed during compression, add a neutral flocculant to agglomerate and precipitate the solid, and circulate and use the separated liquid for jet spraying.
具体的な手段の第６は、０００９で凝集、沈殿したものを、０００５での剥ぎ取り物の圧縮、成型時に加えて処理することである。 The sixth specific means is to treat the material agglomerated and precipitated in 0009 at the time of compression and molding of the peeled material in 0005.
０００５の方法によって、トンネル、地下鉄などの壁面に施されたアスベスト含有被覆層を、走行しながらアスベストの飛散を防止しながら液体ジェットで剥ぎ取り、剥ぎ取り物の回収、圧縮、減容、搾り出された液体の浄化と剥ぎ取り処理への循環使用を可能にし、効率的な作業、アスベストの飛散防止および発生物の処理を合わせて行うことができる。特に０００６の方法によって、剥ぎ取り時のアスベストの飛散を防止でき、また、わずかにアスベスト含有物が残存したとしてもシリコーン樹脂の硬化によって完全封じ込めが行える。０００７の方法によって、液体に起因する電気事故を防止するとともに、わずかにアスベスト含有物が残存したとしてもシリコン樹脂の硬化によって完全封じ込めが行える。また、０００８の方法によって、アスベストの破砕片が存在しているおそれがある空間を局限できる。０００９の方法によって、剥ぎ取り物の重量、容積の減少ができ、また発生した液体を循環使用できる。００１０の方法によって、水分含有量が多いために廃棄処分しにくいものの発生しないようにできる。以上、０００５〜００１０の方法によって、本発明が目的とする、トンネルなどの壁面に施されたアスベスト含有被覆層を、走行しながらアスベストの飛散を防止しつつ液体ジェットで剥ぎ取り、剥ぎ取り物の回収、圧縮、減容、搾りだされた液体の浄化と剥ぎ取り処理への循環使用を可能にし、効率的な作業、アスベストの飛散防止および発生物の処理を合わせて行うことが可能になる。 Using the method of 0005, the asbestos-containing coating layer applied to the walls of tunnels, subways, etc. is stripped off with a liquid jet while preventing the asbestos from scattering while traveling, and the stripped material is recovered, compressed, reduced in volume, and squeezed out. It is possible to recycle the used liquid and to circulate it for the stripping process, and to perform efficient work, prevention of asbestos scattering and treatment of generated products. In particular, according to the method 0006, asbestos can be prevented from being scattered at the time of stripping, and even if a slight amount of asbestos-containing material remains, it can be completely contained by curing the silicone resin. According to the method of 0007, an electrical accident caused by a liquid can be prevented, and even if an asbestos-containing material remains slightly, complete containment can be performed by curing the silicone resin. In addition, the method 0008 can localize a space in which asbestos fragments may exist. By the method of 0009, the weight and volume of the scraped material can be reduced, and the generated liquid can be recycled. According to the method 0010, it is possible to prevent generation of a material that is difficult to dispose of because of its high water content. As described above, by the method of 0005 to 0010, the asbestos-containing coating layer applied to the wall surface of a tunnel or the like, which is the object of the present invention, is peeled off with a liquid jet while preventing asbestos from being scattered while traveling, Recovery, compression, volume reduction, purification of squeezed liquid and circulation use for stripping processing are possible, and it is possible to perform efficient work, asbestos scattering prevention, and processing of generated products.
本発明が処理の対象とするのは、自動車や電車が通過するトンネル、地下鉄の壁面や、道路の横に立てられた壁面などのうち、アスベスト含有物による被覆が施されているものである。本発明の目的は、その大部分の剥ぎ取り、後処理を自動的に、作業効率高く行うことである。したがって、壁面に照明などの器具や換気扇、電気系統の配線や器具が存在する部分は、本発明の処理の前あるいは後で、たとえば通常法を用いて行われるものとする。したがって、事前に壁面の状況が調査されて、本発明によりトンネルなどの長さ方向に移動する台車によって剥ぎ取り処理が行える部分が特定され、作られた作業計画にしたがって、以下に述べる剥ぎ取りなどの作業が行われる。 The subject of the present invention is the one that is covered with an asbestos-containing material, such as a tunnel through which an automobile or a train passes, a wall surface of a subway, or a wall surface set up beside a road. An object of the present invention is to perform most of the stripping and post-processing automatically and with high work efficiency. Therefore, the part where the lighting device, the ventilation fan, the electrical wiring, and the device are present on the wall surface is performed before or after the processing of the present invention, for example, using a normal method. Therefore, the situation of the wall surface is investigated in advance, and a portion that can be stripped by a carriage moving in the length direction of a tunnel or the like according to the present invention is specified, and stripping described below according to the created work plan, etc. Work is done.
交通量が多いトンネル、地下鉄、道路などでは、交通への影響を極力、抑制しながら安
全に作業を行うことが要請される。そこで、たとえば、毎日、夜間の限られた時間のみの交通を止めて、その時間帯が過ぎれば交通を再開するという形で作業が行われる。交通を止める時間の範囲内でいかにして剥ぎ取りなどの作業効率を上げることと安全確保の両立が本発明の最大の課題である。そのためには、まず、作業開始からできるだけ短い時間でアスベスト含有被覆層の剥ぎ取りが始められるようにすること、つぎに剥ぎ取り作業が迅速に進行すること、さらに、剥ぎ取り作業が一段落した後、短い時間で交通を再開しても、安全が確保できるようにすることが重要である。その方策として、従来のように養生シートで隔離して、その中で剥ぎ取り作業を行うということは採用できない。また、剥ぎ取り物や副生物を散乱しないようにし、作業現場で迅速に取り扱いしやすいものに変換することが必要である。そのためには従来法のように、剥ぎ取りを行った後、剥ぎ取り物を集めてビニール袋に入れるというような作業形態は採用することができない。
Tunnels, subways, roads, etc. with heavy traffic are required to work safely while minimizing the impact on traffic. Therefore, for example, work is carried out in such a way that traffic is stopped every day for a limited time only, and the traffic is resumed after that time period. The greatest challenge of the present invention is how to improve work efficiency such as stripping within the range of time to stop traffic and to ensure safety. For that purpose, first, to start the stripping of the asbestos-containing coating layer in as short a time as possible from the start of the work, then that the stripping work proceeds quickly, and further, after the stripping work has settled down, It is important to ensure safety even if traffic is resumed in a short time. As a measure for this, it is not possible to use a conventional method of separating with a curing sheet and performing a stripping operation in the sheet. Moreover, it is necessary to prevent the stripped material and by-products from being scattered and to convert them into something that can be easily handled at the work site. For this purpose, it is not possible to adopt a work form in which the peeled material is collected and placed in a plastic bag after peeling off as in the conventional method.
本発明では、剥ぎ取り作業を迅速に進めるために、液体ジェットを用いる。液体ジェットを用いる剥ぎ取りは、第1次剥ぎ取り（粗剥ぎ取り）と仕上げ処理からなる。ここで言う第1次剥ぎ取り（粗剥ぎ取り）とは被覆層に対して行い、その大部分を剥がす作業である。一方、仕上げ処理とは、部分的に残ったアスベスト含有物を剥ぎ取り、必要によってはそこに液体を吹き付けて塗膜を形成して、ごくわずかに残ったアスベストの飛散を防止できるようにすることである。普通は、第1次剥ぎ取り（粗剥ぎ取り）と仕上げ処理が別々に行なわれる。しかし、本発明では時間的に対応するために、第１次剥ぎ取り（粗剥ぎ取り）と仕上げ剥ぎ取りを並行して行えるようにする。また、用いた液体を迅速に回収、処理できるようにしなければならない。さらに、用いた液体が電気系統に降りかかったりしていると、本発明の対象にように迅速に交通を再開する必要がある場合には、電気事故の原因になるおそれがあるので、その対応も必要である。 In the present invention, a liquid jet is used in order to proceed the stripping operation quickly. Stripping using a liquid jet consists of primary stripping (rough stripping) and a finishing process. The first stripping (rough stripping) referred to here is an operation performed on the coating layer and stripping most of it. On the other hand, the finishing treatment is to remove the partially remaining asbestos-containing material, and if necessary, spray a liquid on it to form a coating film so that only a small amount of remaining asbestos can be prevented from scattering. It is. Normally, the first stripping (rough stripping) and the finishing process are performed separately. However, in the present invention, the first stripping (rough stripping) and the finish stripping can be performed in parallel in order to cope with time. In addition, the used liquid must be collected and processed quickly. In addition, if the liquid used falls on the electrical system, it may cause an electrical accident when it is necessary to quickly resume traffic as in the subject of the present invention. Is also necessary.
そのために、本発明の特色の第１は図１示すような、移動できる台車１に載せられた２連あるいは３連以上の液体ジェット吹き付け装置２、２´、そのジェットで剥ぎ取られたアスベスト含有物を受け止める器具３、受け止められたものを移送する器具４．それを圧縮、成型する装置５（その詳細は図２，３に示す）を用いることである。液体ジェット吹き付け装置について言う「連」とはノズルによってきまる液体ジェットの数は複数であっても、それに供給される液体の条件、すなわち液体の種類、圧力などが同じものを意味する。本発明においては、少なくとも第１次剥ぎ取り（粗剥ぎ取り）を行う１連と、仕上げ剥ぎ取りを１連からなり、必要によって、さらに、第１次剥ぎ取り（粗剥ぎ取り）などを行うものの連の数をふやして、1回の走行、通過による剥ぎ取り面積を増やすことができる。液体ジェットの吹きつけ器具の位置は任意に設定して固定でき、液体ジェットを壁面に吹き付けながら台車が移動し、アスベスト含有物の第１次剥ぎ取り（粗剥ぎ取り）と、第１次剥ぎ取りされた後の面の仕上げのための処理を並行して進められる。
For this purpose, the first feature of the present invention is that two or three or more liquid
剥ぎ取られる面積は第１次剥ぎ取り（粗剥ぎ取り）の液体ジェットの幅と移動速度によって決まる。たとえば剥ぎ取ろうとするアスベスト被覆層の厚さが２０ｍｍの場合、１ｍ２を約２リットルの液体量のジェットで剥ぎ取ることができる。第１次剥ぎ取り（粗剥ぎ取り）液体ジェット吹き付け装置の各ノズルは、たとえば液体量６リットル／分で、回転ノズルを用いてたとえば約１０ｃｍの幅の剥ぎ取り処理が行える。たとえば、このノズルが１０ｃｍ間隔で１０本並べられたのが１連の液体ジェット吹き付け装置で、このノズルの角度は剥ぎ取ろうとする場所に向けて自由に設定、固定できるようになっている。これがたとえば３０ｍ／分で移動すれば幅１ｍの剥ぎ取りが行われることになる。必要により、この第１次剥ぎ取り（粗剥ぎ取り）用液体ジェット吹き付け装置２を２連、あるいはそれ以上にすることで１回の通過による剥ぎ取り面積を増やすことができる。この第１次剥ぎ取り（粗剥ぎ取り）用液体ジェット吹き付け装置２の後にたとえば、２５〜３０ｃｍの間隔をおいて仕上げ用液体ジェット吹き付け装置２´が追従する。その役割は、粗剥ぎ取りで残ったアスベスト含有物を剥離するとともに、壁面にわずかに残るおそれのあるアスベストを飛散しないように封じ込めることである。そのためには、液体ジェットの力は、粗剥ぎ取りの１／３程度でよく、粗剥ぎ取りに比べて各ノズルの液体量を減らすか、あるいは回転ノズルによりジェットの広がりを大きくして、ノズル本数を減らすことができる。本発明では粗剥ぎ取り後の残留アスベストの状況を目視で確認できないので、たとえば第１次剥ぎ取り（粗剥ぎ取り）用液体ジェット吹き付け装置２と仕上げ用液体ジェット吹き付け装置２´のノズルの位置をずらすことで剥ぎ取り残留物を少なくする。
The area to be stripped is determined by the width of the liquid jet and the moving speed of the first stripping (rough stripping). For example, when the thickness of the asbestos coating layer to be peeled off is 20 mm, 1 m 2 can be peeled off by a jet having a liquid amount of about 2 liters. Each nozzle of the primary stripping (rough stripping) liquid jet spraying apparatus has a liquid amount of, for example, 6 liters / minute, and can perform stripping processing of, for example, a width of about 10 cm using a rotating nozzle. For example, 10 nozzles arranged at intervals of 10 cm are a series of liquid jet spraying devices, and the angle of the nozzles can be freely set and fixed toward the place to be peeled off. If this moves at, for example, 30 m / min, stripping with a width of 1 m is performed. If necessary, the stripping area by one pass can be increased by providing two or more liquid
本発明の第２の特徴は、ジェットに使用する液体にシリコーン樹脂乳化液を用いることである。シリコーン樹脂はシリコーンを含む高分子（ポリマー）で、このシリコーン樹脂のベースポリマー、架橋ポリマーに触媒を加え、さらに乳化剤を加え、水に乳化した状態にしたものがシリコーン樹脂の乳化液である。この状態では高分子はマイクロカプセル状である。これは、水が存在する限り乳化状態、すなわち液体として安定しており、アスベストを含む吹き付け層などに対して濡れ性をもっているので、アスベストを含む層に浸透、湿潤が起こる。この乳化した状態の液体から水の蒸発がしてしまうと、マイクロカプセルが壊れて架橋が起こり、硬化が進行する。シリコーン樹脂には、通常オイル型、オイルコンパウンド型、溶液型、エマルジョン型、自己乳化型などがある。制限されないが、本発明で用いられるシリコーン樹脂は、好ましくは水と併用することができるエマルジョン型（Ｏ／Ｗ型エマルジョン）および自己乳化型である。特に好ましくはエマルジョン型であり、中でも架橋反応により硬化し、シリコーン皮膜を形成する反応性のエマルジョン型シリコーン樹脂が好適に使用できる。商業的に入手できる反応性のシリコーン樹脂（エマルジョン型）としては、制限されないが、信越化学工業株式会社のＰｏｌｏｎ ＭＦ−２０（商品名）、Ｐｏｌｏｎ ＭＦ−２３（商品名）、Ｐｏｌｏｎ ＭＦ−５６（商品名）、Ｐｏｌｏｎ ＭＫ−２０６（商品名）、Ｐｏｌｏｎ ＭＷＳ（商品名）、ＫＭ２００２Ｔ（商品名）、およびＫＭ２０００２Ｌ−１（商品名）などを例示することができる。 The second feature of the present invention is that a silicone resin emulsion is used as the liquid used in the jet. A silicone resin is a polymer containing silicone. A silicone resin emulsion is obtained by adding a catalyst to a base polymer and a crosslinked polymer of this silicone resin, further adding an emulsifier, and emulsifying it in water. In this state, the polymer is in the form of a microcapsule. This is stable as an emulsified state, that is, as a liquid as long as water is present, and has wettability with respect to a sprayed layer containing asbestos, so that permeation and wetting occur in the layer containing asbestos. When water evaporates from this emulsified liquid, the microcapsules are broken and cross-linking occurs, and curing proceeds. Silicone resins usually include oil type, oil compound type, solution type, emulsion type, and self-emulsifying type. Although not limited, the silicone resin used in the present invention is preferably an emulsion type (O / W type emulsion) and a self-emulsifying type that can be used in combination with water. Particularly preferred is an emulsion type, and among them, a reactive emulsion type silicone resin that cures by a crosslinking reaction and forms a silicone film can be suitably used. Commercially available reactive silicone resin (emulsion type) is not limited, but Shin-Etsu Chemical Co., Ltd. Polon MF-20 (trade name), Polon MF-23 (trade name), Polon MF-56 ( Product name), Polon MK-206 (product name), Polon MWS (product name), KM2002T (product name), KM20002L-1 (product name), and the like.
ジェットに使用する液体としては、シリコーン樹脂の濃度は第１次剥ぎ取りに用いる液体より、第１次剥ぎ取りされた後の面の仕上げのための処理に用いる液体の方が高くする。
仕上げ処理は乾燥により硬化後に、わずかにでも残るおそれのあるアスベスト繊維を完全に封じ込めることが必要であるので、シリコーン樹脂分の濃度が１０％以上、望ましくは、２０〜４０％とする。一方、１次剥ぎ取り（粗剥ぎ取り）用は、剥ぎ取られたアスベスト含有物が圧縮、成型されたものを硬化させるためのものであり、濃度が高すぎとアスベスト含有層への湿潤には不利になるのでシリコーン樹脂の濃度は２％以上、望ましくは、５〜２０％とする。このように、第１次剥ぎ取り（粗剥ぎ取り）に比べて、仕上げ処理の方が用いる液体のシリコーン濃度を高くする。
As the liquid used for the jet, the concentration of the silicone resin is higher in the liquid used in the treatment for finishing the surface after the first stripping than in the liquid used in the first stripping.
Since it is necessary for the finishing treatment to completely enclose asbestos fibers that may remain even after curing by drying, the concentration of the silicone resin content is 10% or more, preferably 20 to 40%. On the other hand, for primary stripping (rough stripping), the stripped asbestos-containing material is for curing the compressed and molded material. If the concentration is too high, the asbestos-containing layer may be wetted. Since this is disadvantageous, the concentration of the silicone resin is 2% or more, preferably 5 to 20%. In this way, the liquid silicone concentration used in the finishing process is increased as compared with the first stripping (rough stripping).
剥ぎ取られたアスベスト含有物は、本発明では、３で受け止められる。この３は、鋼などによって作られており、周辺にはスポンジ製のクッションなどが取り付けられている。この３によって、剥ぎ取り場所に対する作業者の視界がさえぎられているが、３によって剥ぎ取り物の回収する手間が省ける。さらに、３をクッションを介して壁面９に押し付け、この内部を吸引することによって、アスベストが飛散するおそれがある空間を壁面と３で囲まれた空間に限定できる。ジェットで剥ぎ取られたアスベスト含有物を受け止める器具３と処理対象の壁面９の間の空間を吸引することによって、アスベスト繊維の飛散を防止できる。
The stripped asbestos-containing material is received at 3 in the present invention. This 3 is made of steel or the like, and a sponge cushion or the like is attached to the periphery. Although the operator's view of the stripping place is blocked by 3, the labor for collecting the stripped material can be saved by 3. Further, by pressing 3 against the wall surface 9 through the cushion and sucking the inside, the space in which asbestos may be scattered can be limited to the space surrounded by the wall surface and 3. Asbestos fibers can be prevented from scattering by sucking the space between the
３の中に受け止められた剥ぎ取りアスベスト含有物（固体、液体）は、屈曲可能な管状の移送装置４の中をガス吸引によって移動し、５内に置かれたアスベスト含有物の圧縮、成型装置の中の槽１１に入る。一方、ガスはさらに吸引されて７の集塵機に入る。そこで、集塵処理された後、１部は液体ジェット用のガスに用いられ、他は外気に放散される。
The stripped asbestos-containing material (solid, liquid) received in 3 moves in the bendable tubular transfer device 4 by gas suction, and the asbestos-containing material placed in 5 is compressed and molded.
次に、搬送されてきたアスベスト含有剥ぎ取り物を圧縮・成型する工程についてのべる。圧縮、成型に用いる装置５の１例を図２、図３に示す。剥ぎ取り物が入れられる槽１１の部分、そのアスベスト含有物をスクリューコンベア１５により所定量ずつ切り出し供給する部分１２、およびそのアスベスト含有物を受け、押圧機で圧縮する収容体１３の部分から構成される。槽１１は支持台１６によって支持されている。収容体１３は、槽１１およびスクリューコンベア１５により所定量ずつ切り出し供給する部分１２が１つに対して３つ設けて、回転によって、収容、プレスによる圧縮、および圧縮成型物の取り出しを並行して行えるようにする。具体的には、収容体１３は、軸線が鉛直方向を向くように配置されており、円形の回転板２３０に貫通孔１４を設けて取り付けられ軸線周りに回転可能に構成されている。収容体１３の下面は固定された基板２４０に接しており、回転時には摺動する。回転板２３０が回転することによって収容体１３が軸線周りに回転し、収容体１３は、３つの位置に配置されるようになっている。第１の位置は、スクリューコンベア１５内に投入される。第２の位置は、第１の位置で投入されたアスベスト含有体がこの位置で圧縮される。つまり、第２の位置の上方には、プレスのような押圧具２５０が配置されており、上方から収容体１３に進入可能となっている。そして、第２の位置に隣接する第３の位置の下方には、ベルトコンベア２７０が配置されている。一方、第３の位置の上方には、上下動可能に支持された押し出し具２８０が配置されており、第３の位置に収容体１３内に進入し、圧縮成型物をベルトコンベア２７０上に押し出すようになっている。なお、基板２４０の圧縮成型物が下方へと押し出されるようになっている。また、液体分の回収容器２６０、ベルトコンベア２７０、及び収容体１３を回転させるモーター２９０は、支持台１６の内部に収容されている。まず、収容体１３は鉄などの金属で作られた円柱体であるが、その壁面に複数個の孔を設けられている。その孔は、圧縮時に液体分をスムースに排出するとともに、できるだけアスベスト含有物が収容体の外に出るのを抑制するという役割をする。そのために、その孔１７の断面積は、収容体の壁面の内部より外部の方が大きいものとする。このように孔の断面積を変えるには、孔に断面が円形でテーパーを設けても、あるいは2段階あるいはそれ以上の階段状であってもよい。収容体の内面に開いた部分の直径は、１ｍｍ以上、３ｍｍ以下（円形でない場合は断面積として、３．２ｍｍ２以上、２８．８ｍｍ２ 以下とする。一方、収容体３の外面に開けられた孔の部分は、２ｍｍ以上、８ｍｍ以下（円形でない場合は断面積として、１２．８ｍｍ２以上、２０５ｍｍ２以下とする。このように、収容体から出てきた一部、泥状のアスベスト含有物を含む固液混合物は、基板２４０に取り付けられた遮蔽板２２によって、基板から外に流れ出るのを押さえられ、基板２４０に設けられた開口部から下に流れ落ち、回収装置２６０に集められる。なお、収容体１３を支える基板２４０にも同様の孔２０を設けて液体分を排出する。図１の５には圧縮、成型のための装置がたとえば２台搭載されている。
Next, the process of compressing and molding the asbestos-containing peeled material that has been conveyed will be described. An example of the apparatus 5 used for compression and molding is shown in FIGS. It consists of a portion of the
次に上記のように構成された処理装置を用いた圧縮、成型の処理工程について説明する。槽１１にアスベスト含有被覆層の剥ぎ取り物を投入すると、このアスベスト含有体は、スクリューコンベア１５によって所定量ずつ下方に落下していき収容体１３において第１の位置にある収容体１３に投入される。所定量のアスベスト含有体が投入されると、収容体１３は回転板２３０とともに回転し、アスベスト含有体が収容された収容体１３が第２の位置に移動される。続いて、第２の位置では、押圧具２５０が下降し、収容体１３内のアスベスト含有体を圧縮する。この過程において、アスベスト含有体に含有されていた液体分が、収容体１３の壁面に設けられ孔などを通して絞り出され、基板２４０の開口部から流れ出し、回収容器２６０で回収される。所定の圧縮が完了すれば、収容体１３がさらに回転し、成型物が入っている収容体１３が第３の位置へ移動される。そして、この位置においては、押し出し具２８０が下降して、収容体１３内の成型物をベルトコンベア２７０上に落下させる。こうして、圧縮成型物６０はベルトコンベア２７０によって搬送されていく。各収容体１３でこの処理が１つづつずれて並行して行われる。そのため、アスベスト含有体の圧縮は、半連続的に行われる。斯くしてアスベスト含有物（乾燥時の見かけ比重：０．３〜０．４程度）であったものを、見かけ比重１.５以上、好ましくは１.８〜２.１程度にまで増すことができ、アスベスト含有物の見かけ容積（乾燥時）を１／３〜１／５程度まで減らすことができる。
Next, compression and molding processing steps using the processing apparatus configured as described above will be described. When the asbestos-containing coating layer is peeled off into the
圧縮、成型された物は、ビニール袋に入れて図１の１０に仮置きされ、逐次、別の車に積み代えられ、埋め立てのために管理型最終処分場か、焼成あるいは溶融してアスベストを無害化する装置が設置されている場所に搬送される。搬送についていえば、通常のように剥ぎ取られたままではなく、圧縮、成型されていることによって、容積が減少していること（たとえば１／３〜１／５）、液体ジェットで剥ぎ取ったままのものに比べて水分含有量が１５〜２５％に低下しているので重量が減少し、かつ遊離の液体が存在しないことで、ビニール袋にいれても袋を取り扱いやすくするなどの効果がある。さらに、搬送先で、焼成あるいは溶融してアスベストを無害化する場合には、加熱処理を行いやすいという効果がある。 The compacted and molded product is put in a plastic bag and temporarily placed in 10 of FIG. 1, and is sequentially transferred to another car. It is transported to a place where a detoxifying device is installed. Speaking of transportation, it is not peeled off as usual, but is compressed and molded, so that the volume is reduced (for example, 1/3 to 1/5), and it is peeled off with a liquid jet. Since the moisture content is reduced to 15-25% compared to the untreated one, the weight is reduced, and since there is no free liquid, it is easy to handle the bag even if it is put in a plastic bag. is there. Furthermore, when the asbestos is rendered harmless by baking or melting at the transport destination, there is an effect that the heat treatment is easy to perform.
次に、００２２で搾り出された、固体を１部含む液体の処理方法について述べる。本発明では回収装置２６０に集められた固液混合物には中性凝集剤が加えられて、固体の凝集、沈澱を促進する。中性の凝集剤を用いる理由は、分離された液体が、００２６に後述のように、液体ジェット用に循環使用する場合にシリコーン樹脂乳化液の性状（硬化能など）を阻害しないためである。この中性凝集材としては、たとえば、半水石膏の粉末を主体とするもので、これに凝集促進のために 全体量の５％以下の無機系の凝集剤；ポリ塩化アルミニウム、硫酸アルミニウムなど、あるいは有機系の凝集剤；ポリアクリルアミド系などが加えられたものを用いることができる。この場合、中性凝集材の添加量は、処理対象物の重量の０．３〜２．０％の範囲が適している。中性凝集剤を添加して混合すると迅速に、固体分の凝集、沈澱が進行する。この上澄み液は抜き出して、必要に応じてフィルターを通してから、第１次（粗剥ぎ取り）のジェット用の液に加えて循環使用される。
Next, a method for treating a liquid squeezed at 0022 and containing 1 part of solid will be described. In the present invention, a neutral flocculant is added to the solid-liquid mixture collected in the
一方、凝集、沈澱させて得られた固体分は、液体の分離の仕方にもよるが、ある量の遊離液体を伴っている。これをビニール袋などに入れて最終処分場に運ぶには、取り扱いなどに問題がある。そこで本発明では、この凝集、沈澱させて得られた固体分は、剥ぎ取り物の圧縮、成型工程に加えて処理をする。それによって、固体分は最終的に圧縮、成型物になる。 On the other hand, the solid content obtained by agglomeration and precipitation is accompanied by a certain amount of free liquid, depending on how the liquid is separated. There is a problem in handling etc. when putting this in a plastic bag etc. and carrying it to the final disposal site. Therefore, in the present invention, the solid content obtained by this aggregation and precipitation is processed in addition to the compression and molding process of the stripped material. As a result, the solid content is finally compressed and molded.
剥ぎ取り処理後、一般の交通が再開されるまでの間に、作業対象になった場所に対して熱風吹き付けによる乾燥作業が行われる。これによって送電再開時に電気系統など濡れていることによって生じる漏電などの電気トラブルを回避するとともに、壁面にアスベスト含有物がわずかに残っている場合、あるいは剥ぎ取られたものの1部が完全に回収されていなかった場合に、仕上げ処理時に塗布したシリコーン樹脂を硬化させることでアスベスト繊維の飛散を完全に防止できる。すなわち、この工程の目的は第１次剥ぎ取り（粗剥ぎ取り）と仕上げ処理に用いた液体の水分を蒸発させることである。なお、この時点で、剥ぎ取りの残留物が見つけられた場合には、人力による局所手直しが行われるが、それまでの間、硬化したシリコーン樹脂によってアスベストは完全に封じ込めておくことができる。 After the stripping process and before general traffic is resumed, a drying operation by blowing hot air is performed on a place that is a work target. This avoids electrical troubles such as electric leakage caused by getting wet when the electric power transmission resumes, and when a small amount of asbestos-containing material remains on the wall, or a part of the stripped material is completely recovered. If not, it is possible to completely prevent the asbestos fibers from scattering by curing the silicone resin applied during the finishing process. That is, the purpose of this step is to evaporate the water content of the liquid used for the first stripping (rough stripping) and the finishing process. At this point, when a residue of peeling is found, local rework is performed by human power. Until that time, asbestos can be completely contained by the cured silicone resin.
以上の工程により、アスベスト含有被覆層の剥ぎ取り作業を液体ジェットで効率的に行うとともに、その液体に起因する問題、すなわち剥ぎ取り物の散乱や剥ぎ取り物に多量の液体が含まれていることにより最終処分物の重量、嵩が多く、取り扱いにくいことなどを解決し、また液体の流れ出しや、剥ぎ取り回収物の遊離液体が存在することによるトラブルを防止し、かつ液体のプロセス内での循環使用が可能になる。 By the above process, the asbestos-containing coating layer is efficiently stripped with a liquid jet, and problems caused by the liquid, that is, scattering of the stripped material or the stripped material contains a large amount of liquid. Solves the problem that the final waste is heavy, bulky and difficult to handle, prevents troubles due to the liquid flowing out and the presence of free liquid in the stripped collection, and circulates the liquid in the process. Can be used.
対象となったのは長さ１１００ｍ、断面の壁面長さが１７ｍのトンネルの内面に施された、厚さ２ｍｍの、アスベストを１５％含む吹き付け被覆層（残りはロックウール）である。事前調査により、突起物などがあって走行しながらの液体ジェットでの剥ぎ取りに適さない場所を特定した。本発明の走行しながらの剥ぎ取りが可能な部分は、断面の壁面長さが１２ｍであった。本発明の走行台車による作業は、午後１１時から午前６時までの間、一般の交通を停止して行われた。
剥ぎ取りなどに用いられた装置は図１に示したものである。液体ジェット吹き付け装置は、１０本のノズルが１０ｃｍ間隔で並べられた第１次剥ぎ取り（粗剥ぎ取り）用吹き付け装置を１連（各ノズルは液量が６リットル／分で、回転ノズルにより約１０ｃｍの幅が処理できる）と、５本のノズルが２０ｃｍ間隔で並べられた仕上げ処理用吹き付け装置を１連（各ノズルは液量が４リットル／分で、回転ノズルにより約２０ｃｍの幅が処理できる）が、２５ｃｍの間隔を置いて設置されている。供給する液体は、シリコーン樹脂（信越化学工業製Ｐｏｌｏｎ ＭＦ５６）を、第１次剥ぎ取り（粗剥ぎ取り）用には５％、仕上げ処理用には２２％含むものが用いられた。そして走行１回につき、剥ぎ取り幅が１ｍ 、移動速度１８００ｍ／ｈで、平均４００ｍ連続して剥ぎ取り処理が行われた。この作業を１日約５時間（中断を含む）２日間かけて行われた。剥ぎ取り物の受け止めから、圧縮成型装置までの流れは、００１９，００２０に述べたとおりである。なお、作業中に、剥ぎ取られたアスベスト含有物の受け止める器具３の外側の空気の試料を採取して調べた結果、１ミクロン以上のアスベスト繊維は検出されなかった。剥ぎ取られたアスベストは図２、図３に示した装置２台を用いて、００２２で述べた方法で圧縮、成型され、水平断面積７０ｃｍ２、高さ ３０〜５０ｃｍの成型物にした。この水分含有量は平均２５％であった。
この成型物はビニール袋に入れて密閉し、１０の部分に仮置きし、順次、トラックに積み替えて、埋め立て処分のため管理型最終処分場に搬送した。圧縮、成型時に搾り出された液には、００２４で述べた石膏系凝集剤を１．１％加えて、固形分を凝集、沈殿させ、上澄み液は、フィルターを通して第１次剥ぎ取り（粗剥ぎ取り）用の液に加えて循環使用した。また、凝集、沈殿物は、剥ぎ取り物に加えて圧縮、成型した。剥ぎ取り物を１１の槽１１まで運んだ後の、吸引ガスは集塵機を通した後、排出した。
剥ぎ取り後、交通再開前に、剥ぎ取りを行った壁面に１００〜１２０℃の熱風を吹きつけて、水分の乾燥を行い、シリコーン樹脂の硬化、封じ込めを行った。その作業中に肉眼で見つけられたアスベスト被覆層の残留物の存在場所は調査、記録され、後述の人力による作業時に剥ぎ取り、およびシリコーン樹脂の吹きつけの作業が行われた。
上記の走行方式の剥ぎ取り作業が終了後、７日間かけて、壁面に突起物などが存在する、断面の壁面長さが５ｍの部分は、養生シートを貼っての従来型のヘラ、ブラシ、スクレーパーを用いた人力による剥ぎ取り作業が行われた。なお、その作業でも、本発明と同じ、圧縮、成型の設備が使用された。
The object was a spray coating layer containing 15% of asbestos (the rest is rock wool) having a thickness of 2 mm and applied to the inner surface of a tunnel having a length of 1100 m and a wall surface length of 17 m. Pre-investigation identified areas that were not suitable for stripping with a liquid jet while running due to protrusions. In the portion of the present invention that can be peeled off while traveling, the wall length of the cross section was 12 m. The work with the traveling carriage of the present invention was performed by stopping general traffic from 11:00 pm to 6:00 am.
The apparatus used for stripping or the like is the one shown in FIG. The liquid jet spraying device is a series of primary stripping (rough stripping) spraying devices in which 10 nozzles are arranged at intervals of 10 cm (each nozzle has a liquid volume of 6 liters / minute, and is approximately about 30% by rotating nozzles). 10 cm width) and one finish spraying device with 5 nozzles arranged at 20 cm intervals (each nozzle has a liquid volume of 4 liters / minute, and a rotary nozzle can process about 20 cm width) Can be), but are installed at a distance of 25 cm. As the liquid to be supplied, a silicone resin (Polon MF56 manufactured by Shin-Etsu Chemical Co., Ltd.) containing 5% for primary peeling (rough peeling) and 22% for finishing treatment was used. Then, the stripping process was performed continuously for 400 m on average at a stripping width of 1
This molded product was put in a plastic bag, sealed, temporarily placed in 10 part, sequentially loaded onto a truck, and transported to a managed final disposal site for landfill disposal. To the liquid squeezed during compression and molding, 1.1% of the gypsum flocculant described in 0024 is added to agglomerate and precipitate the solid content, and the supernatant liquid is first stripped (roughly stripped) through the filter. In addition to the liquid for removal, it was recycled. Further, the agglomeration and precipitate were compressed and molded in addition to the peeled material. The suction gas after the peeled material was transported to 11
After stripping, before resuming traffic, hot air of 100 to 120 ° C. was blown onto the stripped wall surface to dry the moisture, and the silicone resin was cured and contained. During the work, the presence location of the residue of the asbestos coating layer, which was found with the naked eye, was investigated and recorded, and it was stripped off during the work by human power described later and sprayed with silicone resin.
After the above stripping operation of the traveling method is completed, a portion having protrusions and the like on the wall surface for 7 days and a wall surface length of 5 m is a conventional spatula, brush, A human scraping work was performed using a scraper. In this operation, the same compression and molding equipment as in the present invention was used.
本発明は、トンネル、地下鉄、道路など、自動車や電車などが走る施設の壁面などに施されたアスベスト含有被覆層を迅速かつ安全に剥ぎ取り処理するために用いることができる。アスベストが含有されていない被覆層の剥ぎ取りにも利用することができる。 INDUSTRIAL APPLICABILITY The present invention can be used for quickly and safely stripping an asbestos-containing coating layer applied to a wall surface of a facility such as a tunnel, subway, or road where a car or a train runs. It can also be used for stripping a coating layer that does not contain asbestos.
１． 移動できる台車
２． 液体ジェット吹き付け装置（第１次剥ぎ取り用）
２´．液体ジェット吹き付け装置（仕上げ処理用）
３． 剥ぎ取られたアスベスト含有物を受け止める器具
４． 受け止められたアスベスト含有物を移送する装置
５． アスベスト含有物を圧縮、成型する装置
６． 圧縮時に搾り出された液体を回収して処理する装置およびジェット用液体の調整装置
７． ガスの集塵装置
８． 運転台
９． トンネルなどの壁面
１０．圧縮、成型物の仮置き場
１１．槽
１２．所定量づつ切り出し供給する部分
１３．収容体
１４．貫通孔
１５．スクリューコンベア
１６．支持台
１７．収容体3の壁面に設けられた孔
２０．収容体１０を支える基板に設けられた孔
６０．圧縮、減容物
２３０．回転板
２４０．基板
２５０．押圧具
２６０．回収容器
２７０．ベルトコンベア
２８０．押し出し具
２９０．モーター
1. 1. A movable carriage Liquid jet spraying device (for primary stripping)
2 '. Liquid jet spraying device (for finishing treatment)
3. 3. Device for receiving stripped asbestos-containing material 4. Device for transferring received asbestos-containing material 5. Equipment for compressing and molding asbestos-containing material Apparatus for recovering and processing liquid squeezed during compression and apparatus for adjusting liquid for jet
7). 7. Gas dust collector Cab 9 Wall surfaces such as tunnels10. 10. Temporary storage place for compression and molding Tank 12. A portion for cutting out and supplying a
15.
Claims (6)