JP2009247802A - Nail chip and nail chip aggregate

Info

Publication number: JP2009247802A
Application number: JP2008102770A
Authority: JP
Inventors: Masami Yamamoto; 政美山本; Mikiko Yamamoto; 美貴子山本
Original assignee: Individual
Current assignee: Individual
Priority date: 2008-04-10
Filing date: 2008-04-10
Publication date: 2009-10-29

Abstract

<P>PROBLEM TO BE SOLVED: To provide a nail chip which combines to ensure easiness of decorating the nail chip and to be gentle to a nail of a user while reducing a burden by such as external force and prevents breakage or a whitening phenomenon of the nail chip, and a nail chip aggregate. <P>SOLUTION: A the nail chip body 10 is used by decorating an external surface and is attached by bonding an internal surface to the nail of the user. A plastic, soft resin material such as elastomer or a vinyl chloride resin is used as a material of the nail chip body 10, and the nail chip is formed to have hardness which is close to that of the nail of a human body and to be softer than the nail chip imitating the hardness of the nail of the human body. A double structure having an external surface part 11 only that is hardened and an internal surface part 12 keeping plasticity is obtained by applying a chemical liquid 15 for imparting hardenability to the external surface part 11 at the time of use. Consequently, the nail chip achieves the double structure which facilitates the decoration by hardening the external surface part 11 and reduces the burden on the nail of the user by softening the internal surface part 12. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

本発明はネイルチップおよび複数個のネイルチップを備えたネイルチップ集合体に関する。ネイルチップは、手の爪、足の爪などの表面に貼り付けて装着するものである。 The present invention relates to a nail chip and a nail chip assembly including a plurality of nail chips. The nail tip is attached to a surface such as a fingernail or a fingernail.

近年、ネイルチップが若い女性を中心に流行し、ファッションに欠かせないものとなってきている。ネイルチップは爪に沿う湾曲形状を持っており、使用者の爪の外表面に沿わせるように載せ置いて接着することにより装着する。ネイルチップの外表面に装飾を施すなどしてお洒落を楽しむことが可能となる。 In recent years, nail chips have become popular with young women and become an essential part of fashion. The nail tip has a curved shape along the nail, and is mounted by being placed and adhered along the outer surface of the user's nail. It is possible to enjoy the fashion by decorating the outer surface of the nail tip.

従来のネイルチップ一枚一枚の形状は、利用者の爪の外表面に沿うような湾曲形状を備え、使用者の爪の外表面に接着する形状をしている。しかし、従来のネイルチップは、一枚一枚を個別に押し出し成形などにより製造するのではなく、製造過程において図１６に示したようなネイルチップ集合体の形で複数個のネイルチップをまとめて製造する。このネイルチップ集合体は金型を用いた押し出し成形により製造される。
従来のネイルチップ集合体１００は、図１６に示すように、複数個のネイルチップ本体１０１と軸体１０２と橋梁部１０３を持った樹状構造をしている（特許文献１：特開２００５−３４９１８３号公報、特許文献２：特開２００６−１４１９３９号公報）。 The shape of each conventional nail chip has a curved shape that conforms to the outer surface of the user's nails, and is bonded to the outer surface of the user's nails. However, conventional nail chips are not manufactured individually by extrusion, but a plurality of nail chips are gathered in the form of a nail chip assembly as shown in FIG. 16 in the manufacturing process. To manufacture. This nail chip assembly is manufactured by extrusion molding using a mold.
A conventional nail chip assembly 100 has a tree-like structure having a plurality of nail chip bodies 101, a shaft body 102, and a bridge portion 103 as shown in FIG. 349183, Patent Document 2: JP-A-2006-141939).

従来のネイルチップの製造では、図１６に示したネイルチップ集合体１００から一枚一枚ネイルチップ本体１０１を切り離してネイルチップ本体１０１を製造していた。販売も基本的にはネイルチップ本体１０１は切り離された状態で販売されている。
なお、図１６に示したようなネイルチップ集合体１００の形のまま販売されることもあった。このようにネイルチップ集合体１００のまま販売された場合、購入者自らがハサミやカッターにより切り分けて一枚一枚のネイルチップ本体１０１とする必要がある。 In the manufacture of conventional nail chips, the nail chip body 101 is manufactured by separating the nail chip bodies 101 one by one from the nail chip assembly 100 shown in FIG. Basically, the nail chip body 101 is sold in a state of being separated.
In some cases, the nail chip assembly 100 as shown in FIG. In this way, when the nail chip assembly 100 is sold as it is, it is necessary for the purchaser himself to cut it with scissors or a cutter to make the nail chip body 101 one by one.

なお、従来のネイルチップは、実際の人体の爪の硬さや質感を模倣するため、近しい硬度を持つように成形できるＡＢＳ樹脂素材で製造されていた。ＡＢＳ樹脂とはアクリロニトリル(Acrylonitrile)、ブタジエン(Butadiene)、スチレン(Styrene)の共重合合成樹脂であり、剛性、硬度、加工性、耐衝撃性、曲げ疲労性など機械的特性のバランスに優れ、薄肉への成形性が良いとされている素材とされている。ＡＢＳ樹脂で成形した場合、ネイルチップの硬さや質感がちょうど実際の人体の爪の硬さや質感に近いものが得られる。
ＡＢＳ素材で成形されたネイルチップを手にとると実際の人体の爪に近い硬度と質感が得られていることが分かる。いわゆる実際の爪を模倣したつけ爪である以上、実際の人体の爪に近い硬度と質感が得られていることが重視されていた。 In addition, the conventional nail chip is manufactured from an ABS resin material that can be molded to have a similar hardness in order to imitate the hardness and texture of an actual human nail. ABS resin is a copolymer synthetic resin of acrylonitrile, butadiene (Butadiene) and styrene (Styrene). It is considered as a material that has good moldability. When molded with ABS resin, it is possible to obtain a nail chip having a hardness and texture close to those of an actual human nail.
When you take a nail chip molded from ABS material, you can see that it has hardness and texture close to those of the actual human nails. Since it is a false nail that imitates a so-called actual nail, it was emphasized that hardness and texture similar to those of an actual human nail were obtained.

特開２００５−３４９１８３号公報JP 2005-349183 A 特開２００６−１４１９３９号公報JP 2006-141939 A

従来のネイルチップにおける第１の問題点は、使用者の爪へネイルチップを介した外力による負荷がかかりやすいことである。
従来のネイルチップは実際の人体の爪の硬さや質感を模倣するため、近しい硬度を持つように成形できるＡＢＳ樹脂素材で製造されており、人体の爪に近い硬度で人体の爪の硬さを模したネイルチップとなっている。実際の人体の爪の硬さや質感に近いネイルチップであればネイルチップへの装飾は実際の人体の爪に施す感覚で行うことができる。また、従来のネイルチップを使用者の爪に接着して装着した場合もあたかも自分の爪が長く伸びたように一体感も得られる。 A first problem with the conventional nail tip is that the user's nails are likely to be loaded by an external force via the nail tip.
Conventional nail tips are made of ABS resin material that can be molded to have similar hardness to imitate the hardness and texture of actual human nails, and the hardness of human nails is similar to that of human nails. It is a simulated nail chip. If the nail tip is close to the hardness and texture of an actual human nail, the decoration on the nail tip can be performed as if applied to the actual human nail. In addition, when a conventional nail chip is attached to a user's nail, it is possible to obtain a sense of unity as if the nail is extended for a long time.

しかし、そのように人体の爪に近い硬度で人体の爪の硬さを模したネイルチップを実際の使用者の爪表面に接着して装着すれば、自分の爪が長く伸びた状態と近くなり、使用時にネイルチップに外力がかかってネイルチップが割れたときに使用者の爪が傷む場合があった。また、ネイルチップに外力がかかってネイルチップが剥離したときにも使用者の爪が傷む場合があった。 However, if you attach a nail tip imitating the hardness of a human nail to the surface of the actual user's nail with a hardness close to that of the human nail, it will be close to the state where your nails are extended for a long time. When the nail tip is cracked due to external force applied to the nail tip during use, the user's nails may be damaged. Also, the user's nails may be damaged when the nail tip is peeled off due to an external force applied to the nail tip.

従来のネイルチップの第２の問題点は、ネイルチップ内面の湾曲と使用者の爪の湾曲とのずれが存在する場合は、無理にネイルチップを使用者の爪に貼り付けると歪みが生じ、ネイルチップや使用者の爪に無理な力がかかってしまうことである。
上記したように人体の爪に近い硬度で人体の爪の硬さを模したネイルチップとなっており、その内面の湾曲も人体の爪表面の湾曲とできるだけ合致するように製作されている。 The second problem of the conventional nail tip is that if there is a deviation between the curvature of the inner surface of the nail tip and the curvature of the user's nail, distortion occurs when the nail tip is forcibly applied to the user's nail, It is that excessive force is applied to the nail tip and the user's nails.
As described above, it is a nail chip that simulates the hardness of a human nail with a hardness close to that of the human nail, and the curvature of the inner surface of the nail chip is made to match the curvature of the surface of the nail of the human body as much as possible.

しかし、人体の爪表面の湾曲は千差万別であるため、オーダーメードのネイルチップでない以上は従来のネイルチップ内面の湾曲と使用者の爪の湾曲とのずれが存在する。個人差はあるものの、このずれは接着剤で取り付ければ装着できる程度のずれであるので従来のネイルチップではそのまま接着剤で取り付けていた。ネイルチップ内面の湾曲と使用者の爪の湾曲とのずれが存在する状態でそのまま接着剤により装着した場合、ネイルチップに歪みが生じ、ネイルチップや使用者の爪に無理な力がかかってしまう。そのため、使用者の爪が傷む場合があった。 However, since the curvature of the nail surface of the human body is various, there is a difference between the conventional curvature of the inner surface of the nail tip and the curvature of the user's nail as long as it is not a custom-made nail tip. Although there are differences among individuals, this shift is a shift that can be mounted if attached with an adhesive, so the conventional nail chip is attached as it is with an adhesive. If the adhesive is attached as it is in the state where there is a deviation between the curvature of the inner surface of the nail tip and the curvature of the user's nail, the nail tip is distorted and an excessive force is applied to the nail tip and the user's nail. . For this reason, the user's nails may be damaged.

従来のネイルチップにおける第３の問題点は、割れやすく折り曲げに弱くいわゆる「白化現象」が起こることであった。
従来のネイルチップは、人体の爪に近い硬度で人体の爪の硬さを模したものとして、ＡＢＳ素材を使用するものがほとんどであったが、人体の爪の硬さを模したＡＢＳ素材のネイルチップでは折れや曲げが発生した場合に「白化現象」が発生したりするおそれがあった。割れないまでも折り目がついてその折り目部分が白く変色するいわゆる「白化現象」が起こってしまうともはや装飾用途をなさない。 A third problem with conventional nail tips is that they are easily broken and weak against bending, so-called “whitening” occurs.
Most conventional nail tips use ABS material to simulate the hardness of a human nail with a hardness close to that of the human nail, but the ABS material that simulates the hardness of a human nail When the nail tip is bent or bent, a “whitening phenomenon” may occur. If a so-called “whitening phenomenon” occurs in which a crease is formed even if it does not break and the crease part turns white, it is no longer used for decoration.

上記問題点に鑑み、本発明は、ネイルチップへの装飾が施しやすさは確保しつつ使用者の爪に優しく外力などの負荷を軽減せしめることを両立させ、ネイルチップの内面の湾曲と使用者の爪の表面の湾曲とのずれにより発生する歪みの影響を低減せしめ、ネイルチップの切り分け時や使用時において割れたり白化現象が発生したりしないネイルチップおよびネイルチップ集合体を提供することを目的とする。 In view of the above problems, the present invention is capable of reducing the load of the external force and the like gently on the user's nails while ensuring the ease of decoration on the nail tip, and the curvature of the inner surface of the nail tip and the user The purpose of the present invention is to provide a nail chip and a nail chip assembly that reduce the influence of distortion caused by deviation from the surface of the nail surface and that do not crack or whiten when the nail chip is cut or used. And

上記目的を達成するため、本発明のネイルチップは、前記ネイルチップ本体の素材を柔らかい軟質樹脂素材とし、人体の爪に近い硬度で人体の爪の硬さを模したネイルチップよりも柔らかく形成しておき、使用時に前記外面に対して硬化性を与える薬液をコーティングすることにより前記外面に前記ネイルチップ本体の硬度よりも硬いコーティング層を形成し、前記内面の柔軟性は保たせた二重構造とすることにより、前記外面を硬くして装飾を行いやすくすると同時に前記内面の柔らかさを維持して前記使用者の爪への負担を軽減せしめるネイルチップである。 In order to achieve the above object, the nail chip of the present invention is formed of a soft soft resin material as the material of the nail chip body, and is softer than a nail chip imitating the hardness of a human nail with a hardness close to that of a human nail. In addition, a double layer structure in which a coating layer harder than the hardness of the nail tip body is formed on the outer surface by coating a chemical solution that gives curability to the outer surface during use, and the flexibility of the inner surface is maintained. By doing so, the outer surface is hardened to facilitate decoration, and at the same time, the softness of the inner surface is maintained to reduce the burden on the user's nails.

また、本発明のネイルチップは、人体の爪に近い硬度で人体の爪の硬さを模したネイルチップよりも柔らかい軟質樹脂素材により形成したネイルチップ本体と、前記ネイルチップ本体の外面を覆い、前記ネイルチップ本体の硬度よりも硬い硬度であるコーティング層とを備え、前記外面は前記コーティング層によって硬く、前記内面は前記軟質樹脂素材によって柔軟とした二重構造とし、前記外面への装飾を行いやすくすると同時に前記内面の柔らかさを維持して前記使用者の爪への負担を軽減せしめたネイルチップである。 Further, the nail chip of the present invention covers a nail chip body formed of a soft resin material softer than a nail chip imitating the hardness of a human nail with a hardness close to that of a human body, and an outer surface of the nail chip body, A coating layer that is harder than the hardness of the nail chip body, the outer surface is hardened by the coating layer, and the inner surface is made flexible by the soft resin material to decorate the outer surface At the same time, it is a nail tip that reduces the burden on the user's nails while maintaining the softness of the inner surface.

ここで、前記軟質樹脂素材が、エラストマーまたは塩化ビニル樹脂のいずれかであることが好ましい。さらには、今後開発される新素材であっても硬度がエラストマーや塩化ビニル樹脂に近しいものであれば適用できる。 Here, it is preferable that the soft resin material is either an elastomer or a vinyl chloride resin. Furthermore, even if it is a new material developed in the future, it can be applied if the hardness is close to that of an elastomer or a vinyl chloride resin.

例えば、前記軟質樹脂素材の柔軟性が、プラスチックのデュロメータ硬さ試験方法のタイプＤの測定において、ＨＤＤ値５０以下の柔軟性であることが好ましい。 For example, the soft resin material preferably has a HDD value of 50 or less in the type D measurement of the plastic durometer hardness test method.

また、前記ネイルチップ本体が前記外面を上にして上方から３ｍｍ以上押し込んでも白化現象が起きない柔軟性を確保せしめたものとすることが好ましい。 Moreover, it is preferable that the nail chip body has ensured flexibility that does not cause a whitening phenomenon even if it is pushed in from the upper side by 3 mm or more with the outer surface facing up.

次に、上記目的を達成するため、本発明のネイルチップ集合体は、
外面に装飾を施し、内面を使用者の爪に接着して装着する複数個のネイルチップ本体と、
横たわった基本姿勢にて安定自立し、全体を支える土台となる軸体と、
個々の前記ネイルチップ本体に対応して適当な間隔をおいて前記軸体の軸方向に対して側方に設けられた、前記軸体と前記ネイルチップ本体とをつなぐ橋梁部とを備えたネイルチップ集合体であって、
前記ネイルチップ本体の素材を柔らかい軟質樹脂素材とし、前記ネイルチップ本体を、人体の爪に近い硬度で人体の爪の硬さを模したネイルチップよりも柔らかく形成し、
使用に際して前記ネイルチップ本体の外面に対して硬化性を与える薬液をコーティングして前記外面に前記ネイルチップ本体の硬度よりも硬いコーティング層を形成して前記内面の柔軟性は保たせた二重構造を備えたものとし、前記ネイルチップ本体が、前記外面を硬くして装飾を行いやすくすると同時に前記内面の柔らかさを維持して前記使用者の爪への負担を軽減せしめるものである。 Next, in order to achieve the above object, the nail chip assembly of the present invention is
A plurality of nail tip bodies that are decorated on the outer surface and are attached by attaching the inner surface to the user's nails,
A shaft that will be stable and independent in the basic posture,
A nail comprising a bridge portion that is provided laterally with respect to the axial direction of the shaft body at an appropriate interval corresponding to each of the nail chip bodies and that connects the shaft body and the nail chip body. A chip assembly,
The material of the nail chip body is a soft soft resin material, and the nail chip body is formed softer than a nail chip imitating the hardness of a human nail with a hardness close to that of the human nail,
In use, a dual structure in which the inner surface is kept flexible by coating the outer surface of the nail tip body with a chemical solution that imparts curability to form a coating layer harder than the hardness of the nail tip body on the outer surface. The nail tip body hardens the outer surface to facilitate decoration, and at the same time maintains the softness of the inner surface to reduce the burden on the user's nails.

また、本発明のネイルチップ集合体は、
外面に装飾を施し、内面を使用者の爪に接着して装着する複数個のネイルチップ本体であって、人体の爪に近い硬度で人体の爪の硬さを模したネイルチップよりも柔らかい軟質樹脂素材により形成したネイルチップ本体部分と、
前記ネイルチップ本体の外面を覆い、前記ネイルチップ本体の硬度よりも硬い硬度であるコーティング層と、
横たわった基本姿勢にて安定自立し、全体を支える土台となる軸体と、
個々の前記ネイルチップ本体に対応して適当な間隔をおいて前記軸体の軸方向に対して側方に設けられた、前記軸体と前記ネイルチップ本体とをつなぐ橋梁部とを備えたネイルチップ集合体であって、
前記ネイルチップ本体が、前記外面は前記コーティング層によって硬く、前記内面は前記軟質樹脂素材によって柔軟である二重構造とし、前記外面への装飾を行いやすくすると同時に前記内面の柔らかさを維持して前記使用者の爪への負担を軽減せしめたものである。 The nail chip assembly of the present invention is
A plurality of nail tip bodies that are decorated on the outer surface and attached to the user's nails by attaching the inner surface, and are softer than a nail tip that mimics the hardness of human nails with a hardness close to that of the human nails A nail chip body portion formed of a resin material;
A coating layer that covers the outer surface of the nail tip body and has a hardness that is harder than the hardness of the nail tip body;
A shaft that will be stable and independent in the basic posture,
A nail comprising a bridge portion that is provided laterally with respect to the axial direction of the shaft body at an appropriate interval corresponding to each of the nail chip bodies and that connects the shaft body and the nail chip body. A chip assembly,
The nail chip body has a double structure in which the outer surface is hardened by the coating layer and the inner surface is flexible by the soft resin material, and it is easy to decorate the outer surface while maintaining the softness of the inner surface. This reduces the burden on the user's nails.

なお、上記ネイルチップ集合体において、前記橋梁部が前記軸体から前記ネイルチップ本体にかけて斜め上方に設けられ、前記基本姿勢において前記ネイルチップ本体が前記軸体に対して上方に維持され、前記基本姿勢において前記ネイルチップ本体が前記橋梁部との接点のみを介して支えられ、空中に維持されることが好ましい。 In the nail chip assembly, the bridge portion is provided obliquely upward from the shaft body to the nail chip body, and the nail chip body is maintained above the shaft body in the basic posture. In the posture, it is preferable that the nail tip main body is supported only through a contact point with the bridge portion and maintained in the air.

また、上記ネイルチップ集合体において、前記橋梁部が前記軸体の軸方向に対して側方に設けられ、前記軸体における前記橋梁部から底面までの高さが前記ネイルチップ本体の厚みよりも十分に大きく、前記基本姿勢において前記ネイルチップ本体が前記橋梁部との接点のみを介して支えられ、空中に維持されることが好ましい。 Further, in the nail chip assembly, the bridge portion is provided laterally with respect to the axial direction of the shaft body, and the height from the bridge portion to the bottom surface of the shaft body is larger than the thickness of the nail chip body. It is preferable that the nail tip main body is sufficiently large and is supported in the basic posture only through the contact point with the bridge portion and maintained in the air.

また、上記ネイルチップ集合体において、個々の前記ネイルチップ本体のサイズが、親指用の大きなサイズから小指用の小さなサイズまで多様なサイズとなっており、個々のネイルチップ本体の軸体に対する配置において、前記軸体の一方から他方にかけてサイズの大きなものから小さなものへとサイズ順に配置され、前記軸体の太さと前記橋梁部の太さが、前記軸体の一方から他方にかけて小さくなるように調整されていることが好ましい。 Further, in the nail chip assembly, the sizes of the individual nail chip main bodies are various sizes from a large size for the thumb to a small size for the little finger. The shaft body is arranged in order of size from one to the other from the largest to the smallest, and the thickness of the shaft body and the thickness of the bridge portion are adjusted so as to decrease from one to the other of the shaft body. It is preferable that

また、上記ネイルチップ集合体において、前記軸体の太さの調整が、前記軸体の水平方向の幅のみならず垂直方向の高さの調整を含み、前記軸体の高さの調整が、前記軸体の上面を下げるのではなく前記軸体の底面を上げることによる調整であり、前記底面を上げる調整を施した軸体部分の底面に、前記調整にかかる高さに相当する柱状突起を複数個設け、前記底面を上げる調整を施さなかった軸体の底面と前記柱状突起の底面により全体が自立安定しやすい構造とすることが好ましい。 Further, in the nail chip assembly, the adjustment of the thickness of the shaft body includes adjustment of not only the horizontal width of the shaft body but also the height in the vertical direction, and adjustment of the height of the shaft body, It is an adjustment by raising the bottom surface of the shaft body instead of lowering the top surface of the shaft body, and a columnar projection corresponding to the height required for the adjustment is formed on the bottom surface of the shaft body portion that has been adjusted to raise the bottom surface. It is preferable to provide a structure in which a plurality are provided and the entire bottom surface of the shaft body that has not been adjusted to raise the bottom surface and the bottom surface of the columnar protrusions are easily stabilized independently.

本発明のネイルチップおよびネイルチップ集合体は、コーティングにより外面部分は人体の爪を模した硬度に近い硬さを持つのでネイルチップ外面部分への装飾が施しやすさは確保され、内面部分は柔らかい状態が確保されるので、ネイルチップ全体が緩衝能を備えることができ、使用者の爪に優しく外力などの負荷を軽減せしめることが両立できる。 In the nail chip and nail chip assembly of the present invention, the outer surface portion has a hardness similar to that of a human nail by coating, so that the decoration on the outer surface portion of the nail chip can be easily applied and the inner surface portion is soft. Since the state is ensured, the entire nail tip can be provided with a buffering capacity, and it is possible to reduce the load such as external force gently on the user's nails.

また、ネイルチップの内面が柔らかく、ネイルチップの内面の湾曲が実際の使用者の爪の表面の湾曲に沿うように変形してくれるので、ネイルチップの内面の湾曲と使用者の爪の表面の湾曲とのずれにより発生する歪みの影響を低減せしめることができる。 Also, since the inner surface of the nail tip is soft and the curvature of the inner surface of the nail tip is deformed so as to follow the curvature of the surface of the actual user's nail, the curvature of the inner surface of the nail tip and the surface of the user's nail It is possible to reduce the influence of distortion caused by deviation from the curvature.

また、ネイルチップの使用時において割れたり白化現象が発生したりすることがない。
また、ネイルチップ集合体からのネイルチップの切り分け時において割れたり白化現象が発生したりすることがない。 Further, there is no occurrence of cracking or whitening when using the nail tip.
Further, no cracking or whitening phenomenon occurs when the nail chip is separated from the nail chip assembly.

以下、図面を参照しつつ、本発明のネイルチップの実施例を説明する。ただし、本発明の範囲は以下の実施例に示した具体的な用途、形状、個数などには限定されない。 Embodiments of a nail tip according to the present invention will be described below with reference to the drawings. However, the scope of the present invention is not limited to the specific application, shape, number and the like shown in the following examples.

実施例１にかかる本発明のネイルチップの構成例を示す。
図１は、実施例１にかかる本発明のネイルチップ本体１０の構成例を示す図である。
図１（ａ）は平面図、図１（ｂ）は正面図、図１（ｃ）は右側面図である。
ネイルチップ本体１０は、外面１１に装飾を施し、内面１２を使用者の爪に接着して装着するものであり、押し出し成形により成形されている。 The structural example of the nail chip | tip of this invention concerning Example 1 is shown.
FIG. 1 is a diagram illustrating a configuration example of a nail chip body 10 according to the first embodiment of the present invention.
1A is a plan view, FIG. 1B is a front view, and FIG. 1C is a right side view.
The nail tip main body 10 is provided with a decoration on the outer surface 11 and attached by attaching the inner surface 12 to the user's nails, and is formed by extrusion molding.

ネイルチップ本体１０全体の素材は柔らかい軟質樹脂素材、例えば、エラストマーや塩化ビニル樹脂により形成されており、その硬度は、従来のネイルチップよりも柔らかいものとなっている。従来のネイルチップはＡＢＳ樹脂素材などで人体の爪に近い硬度で人体の爪の硬さを模したネイルチップとなっているが、本発明のネイルチップ本体１０は人体の爪の硬度よりも柔らかく形成されている。 The whole material of the nail chip body 10 is made of a soft soft resin material such as an elastomer or a vinyl chloride resin, and the hardness thereof is softer than that of a conventional nail chip. A conventional nail chip is an ABS resin material or the like, which is a nail chip that simulates the hardness of a human nail with a hardness close to that of a human nail, but the nail chip body 10 of the present invention is softer than the hardness of a human nail. Is formed.

以下、本発明のネイルチップ本体１０の柔らかさと二重構造について説明する。
本発明のネイルチップ本体１０は、ネイルチップ本体１０全体の素材は柔らかい軟質樹脂素材で形成されているが、使用時には外面部分において硬化する薬液をコーティングすることにより外面部分のみを硬化させ、内面部分の柔軟性は保たせた二重構造とする。このように二重構造とすることにより、外面部分を硬くして人体の爪を模した硬度に近い硬度を実現して装飾を施しやすくすると同時に、人体の爪と接する内面部分は柔らかく保つこととして使用者の爪への負担を軽減せしめることを実現する。 Hereinafter, the softness and double structure of the nail tip body 10 of the present invention will be described.
In the nail chip body 10 of the present invention, the entire material of the nail chip body 10 is formed of a soft soft resin material. However, when used, only the outer surface portion is cured by coating a chemical solution that hardens on the outer surface portion, and the inner surface portion. A double structure is maintained while maintaining flexibility. By adopting a double structure in this way, the outer surface part is hardened to achieve a hardness close to that of a human nail, making it easier to decorate, and at the same time keeping the inner surface part in contact with the human nail soft It is possible to reduce the burden on the user's nails.

図２は、本発明のネイルチップ本体１０において二重構造を実現する原理を模式的に示す図であり、図２（ａ）はネイルチップ本体１０の縦断面を模式的に示した図である。上が外面部分１１、下が内面部分１２に相当する。ネイルチップ本体１０全体はエラストマー素材や塩化ビニルで柔らかく形成されている。 FIG. 2 is a diagram schematically showing the principle of realizing a dual structure in the nail tip body 10 of the present invention, and FIG. 2A is a diagram schematically showing a longitudinal section of the nail tip body 10. . The upper portion corresponds to the outer surface portion 11, and the lower portion corresponds to the inner surface portion 12. The entire nail tip body 10 is softly formed of an elastomer material or vinyl chloride.

次に、図２（ｂ）に示すように、外面部分に装飾を施す前にネイルチップ本体１０の外面部分１１に対して薬液１５をコーティングする。たとえば、下地となるベースコート剤（爪に対するネイルカラーの色素沈着を防ぎ、ネイルカラーの乗りを良くする下地コーティング剤）、ネイルカラー剤（ネイルエナメル、ネイルポリッシュ、ネイルラッカーと呼ばれることもあるネイルアート用の装飾剤）、表面保護のトップコート剤（ネイルカラー、ネイルアートを施した仕上げとして、ネイルカラーを保護したり、ツヤ出しの為に塗る薬剤）、スカルプチュア剤（アクリルパウダーとアクリルリキッドを使って硬化させる人工爪用の薬剤）、ジェルネイル剤（ネイルエクステンションで用いられるものであり、ジェル素材に装飾物を施して紫外線で硬化させる人工爪用の薬剤）などがある。このように外面部分に塗布された薬液１５が硬化してコーティング層が形成される。硬化した結果、人体の爪の硬度と近しいものとなれば、外面部分はネイルアートなどの装飾を施しやすくなる。 Next, as shown in FIG. 2B, the chemical solution 15 is coated on the outer surface portion 11 of the nail tip body 10 before decorating the outer surface portion. For example, base coat agent (base coat agent that prevents nail color pigmentation on nails and improves nail color riding), nail color agent (nail enamel, nail polish, nail lacquer, sometimes called nail lacquer) ), Surface-protecting top coat agent (nail color, nail art finish, protecting nail color and applying for gloss), sculpture agent (using acrylic powder and acrylic liquid) Drugs for artificial nails to be cured) and gel nail agents (agents for artificial nails that are used in nail extensions and are decorated with gel material and cured with ultraviolet rays). Thus, the chemical | medical solution 15 apply | coated to the outer surface part hardens | cures, and a coating layer is formed. As a result of curing, if the hardness of the nail of the human body is close, the outer surface portion can easily be decorated with nail art or the like.

一方、図２（ｂ）に示すように、薬液１５が塗布されていない部分、つまり、外面部分以外の内面部分１２は柔らかい軟質樹脂素材のままである。ネイルチップの縦断面から明らかなように外面部分１１は硬く内面部分１２は柔らかいという二重構造が実現できる。 On the other hand, as shown in FIG. 2B, the portion where the chemical solution 15 is not applied, that is, the inner surface portion 12 other than the outer surface portion remains a soft soft resin material. As is apparent from the longitudinal section of the nail tip, a double structure can be realized in which the outer surface portion 11 is hard and the inner surface portion 12 is soft.

図２（ｃ）は使用者の爪に本発明のネイルチップ本体１０を接着して装着した様子を縦断面において模式的に示した図である。使用者の爪２００に対して内面部分１２が接しており、内面部分１２は柔らかいものとなっている。つまり、ネイルチップ本体１０を装着した状態では図２（ｃ）に見るように、上から順に、人体の爪に近い硬度を持つ硬い外面部分１１、柔らかい内面部分１２、硬い人体の爪２００と並び、硬い上下の層の中に柔らかい中間層を設けたような構造となる。ここで、使用者の爪付近に何らかの外力がかかった場合を想定すると、硬い外面部分１１と硬い使用者の爪２００の間に柔らかい内面部分１２が緩衝材として機能するので使用者の爪２００に対する影響が緩和され、負荷を低減させることができる。 FIG. 2 (c) is a diagram schematically showing, in a longitudinal section, a state in which the nail tip body 10 of the present invention is attached to a user's nail and attached. The inner surface portion 12 is in contact with the user's nails 200, and the inner surface portion 12 is soft. That is, in the state where the nail chip body 10 is mounted, as shown in FIG. 2C, the hard outer surface portion 11, the soft inner surface portion 12, and the hard human nail 200 having hardness close to that of the human nail are arranged in order from the top. The structure is such that a soft intermediate layer is provided between the hard upper and lower layers. Here, assuming that some external force is applied in the vicinity of the user's nails, the soft inner surface portion 12 functions as a cushioning material between the hard outer surface portion 11 and the hard user's nails 200. The impact is mitigated and the load can be reduced.

このように、本発明のネイルチップ本体１０を使用することにより、装飾を施す点からは従来の硬いネイルチップを用いる場合と同様に外面部分は硬く扱いやすくなっており、使用者の爪２００を外力から保護する点からは従来にはない二重構造により柔らかい緩衝力を提供することができ、二重構造ゆえのメリットが得られる。 As described above, by using the nail tip body 10 of the present invention, the outer surface portion is hard and easy to handle in the same manner as in the case of using the conventional hard nail tip in terms of decoration, and the user's nails 200 In terms of protection from external force, a soft cushioning force can be provided by a double structure that has not been used in the past, and the advantages of the double structure can be obtained.

ここで、本発明のネイルチップ本体１０の柔らかさについて説明する。
上記したように本発明のネイルチップ本体１０全体が柔らかい素材として提供されるが、どの程度の柔らかさを持つかを数値として確かめた。従来の人体の爪の硬さを模したネイルチップと、本発明の軟質樹脂素材のネイルチップ本体１０を用意し、実験を通じて硬度の違いを比較した。 Here, the softness of the nail tip body 10 of the present invention will be described.
As described above, the entire nail chip body 10 of the present invention is provided as a soft material, and the degree of softness was confirmed as a numerical value. A nail chip simulating the hardness of a conventional human nail and a nail chip body 10 of the soft resin material of the present invention were prepared, and the difference in hardness was compared through experiments.

［製作した試料］
同じ金型を使用して３種類の素材で同じ形のネイルチップ試料を製作した。
ネイルチップ１：ＡＢＳ樹脂素材
ネイルチップ本体１０ａ：塩化ビニル素材
ネイルチップ本体１０ｂ：エラストマー素材
ネイルチップ１は、ＡＢＳ樹脂により従来型の人体の爪の硬さを模したネイルチップとなっている。ネイルチップ本体１０ａは塩化ビニル素材により人体の爪の硬さより柔らかく成型されたネイルチップとなっている。ネイルチップ本体１０ｂはエラストマー素材により人体の爪の硬さより柔らかく成型されたネイルチップとなっている。 [Samples made]
Using the same mold, nail tip samples of the same shape were made from three types of materials.
Nail chip 1: ABS resin material Nail chip body 10a: Vinyl chloride material Nail chip body 10b: Elastomer material The nail chip 1 is a nail chip that mimics the hardness of a conventional human nail using ABS resin. The nail tip body 10a is a nail tip that is made of a vinyl chloride material softer than the hardness of a human nail. The nail tip body 10b is a nail tip that is made of an elastomer material and is softer than the hardness of the nail of the human body.

［試験１］押し込みによる軟性試験
図３は押し込みによる軟性試験の試験方法の概略を示す図である。速度２ｍｍ／ｓｅｃにより圧子を押し下げて所定深さまで押し込む。その過程で白化または割れが生じるか否かを検証する。なお、所定深さまで押し込むために必要な負荷を計測した。 [Test 1] Softness test by indentation FIG. 3 is a diagram showing an outline of a test method for a softness test by indentation. The indenter is pushed down to a predetermined depth at a speed of 2 mm / sec. It is verified whether whitening or cracking occurs in the process. In addition, the load required in order to push in to the predetermined depth was measured.

使用試料型：
ＡＢＳ樹脂製ネイルチップ１の親指用のネイルチップ
塩化ビニル製ネイルチップ本体１０ａの親指用のネイルチップ
エラストマー製ネイルチップ本体１０ｂの親指用のネイルチップ
使用機材：「Stable Micro Systems社」製「TA.TX-plus Texture Analyzer」
実験委託先：兵庫県立工業技術センター Sample type used:
ABS resin nail tip 1 nail tip for thumb Nail tip for thumb of vinyl chloride nail tip body 10a Nail tip for thumb of elastomeric nail tip body 10b Equipment used: “TA. TX-plus Texture Analyzer "
Test contractor: Hyogo Prefectural Industrial Technology Center

押し込みによる軟性試験の実験結果を図４に示す。図４に示す実験結果から分かるように、ＡＢＳ樹脂素材のネイルチップ１は２ｍｍ押し込みの時点では白化現象は起きていないが、３ｍｍ押し込みまでに白化現象が起きることが検証された。塩化ビニル素材のネイルチップ本体１０ａおよびエラストマー素材のネイルチップ本体１０ｂは４ｍｍ押し込みを経ても白化現象は起きないことが検証された。押し込みに必要な負荷を見ても塩化ビニル素材のネイルチップ本体１０ａおよびエラストマー素材のネイルチップ本体１０ｂの柔軟性が優れていることが検証できた。 The experimental result of the softness test by indentation is shown in FIG. As can be seen from the experimental results shown in FIG. 4, the nail chip 1 made of ABS resin material has not been whitened at the time of 2 mm indentation, but it has been verified that the whitening phenomenon occurs by 3 mm indentation. It has been verified that the whitening phenomenon does not occur in the nail chip body 10a made of a vinyl chloride material and the nail chip body 10b made of an elastomer material even after being pushed in by 4 mm. It was verified that the flexibility of the vinyl chloride material nail tip body 10a and the elastomer material nail tip body 10b was excellent even when looking at the load required for pushing.

［試験２］スプリング式硬度計による調査
試験１により３種類の素材の柔軟性の優劣は検証済みであるが、プラスチック素材の柔軟性の試験方法はＪＩＳ規格により定まっているので同規格に沿った硬度試験も行った。
試験はＪＩＳ規格のＫ７２１５「プラスチックのデュロメータ硬さ試験方法」を用いた。 [Test 2] Investigation using a spring type hardness tester The superiority or inferiority of the flexibility of three types of materials has been verified in Test 1, but the test method for the flexibility of plastic materials is determined by the JIS standard, so it conforms to the standard. A hardness test was also performed.
The test used JIS standard K7215 “Plastic Durometer Hardness Test Method”.

図５はプラスチックのデュロメータ硬さ試験方法の概略を示す図である。
デュロメータ硬さとは、圧子を用いてくぼみ深さに対応して変化する試験荷重を試料に負荷し、生じたくぼみ深さｈから求めた値である。
デュロメータ硬さの計測にはタイプＡとタイプＤの２通りがあり、タイプＡのデュロメータにて計測して計測値が９０以上のときはタイプＤに切り替えて行うことが好ましく、タイプＤのデュロメータにて計測して計測値が２０以下のときはタイプＡのデュロメータを用いることが好ましい。今回の試験では、タイプＤのデュロメータで計測して良い範囲であったのでタイプＤのデュロメータで計測した。 FIG. 5 is a diagram showing an outline of a plastic durometer hardness test method.
The durometer hardness is a value obtained from the indentation depth h generated by applying a test load that changes in accordance with the indentation depth to the sample using an indenter.
There are two types of durometer hardness measurement: Type A and Type D. When the measured value is 90 or more, it is preferable to switch to Type D. When the measured value is 20 or less, it is preferable to use a type A durometer. In this test, since it was in the range that can be measured with a type D durometer, it was measured with a type D durometer.

試験試料：プラスチックのデュロメータ硬さ試験方法で用いる使用試料は６ｍｍ厚以上の素材を用いる必要があるので、ＡＢＳ樹脂、塩化ビニル樹脂、エラストマーの各素材で成形したネイルチップ集合体の軸体を用いて計測した。
実験委託先：［兵庫県立工業技術センター］ Test sample: Since the material used in the plastic durometer hardness test method must be made of a material with a thickness of 6 mm or more, a shaft of a nail chip assembly molded from ABS resin, vinyl chloride resin, or elastomer material is used. Measured.
Test contractor: [Hyogo Prefectural Industrial Technology Center]

プラスチックのデュロメータ硬さ試験の実験結果を図６に示す。実験結果から分かるように、やはりＡＢＳ樹脂素材がもっとも硬く塩化ビニルとエラストマーは比較的柔らかいことが検証できた。 The experimental results of the plastic durometer hardness test are shown in FIG. As can be seen from the experimental results, it was verified that the ABS resin material was the hardest and the vinyl chloride and the elastomer were relatively soft.

図６の実験結果によれば、従来のネイルチップに用いられるＡＢＳ樹脂素材はＨＤＤ値で７０〜８０近くあるが、本発明のネイルチップに用いられる塩化ビニル素材とエラストマー素材はＨＤＤ値で４５〜５０近くであることが分かった。この実験結果では、従来の人体の爪の硬さを模したネイルチップの硬度に比べて本発明のネイルチップの硬度は６割〜７割程度の硬度である。このように本発明のネイルチップは、従来のネイルチップ硬度の６割〜７割程度の硬度の素材を用いているので、使用者みずからも手に取れば、本発明のネイルチップは従来品のネイルチップとは明らかに違う柔らかさを持っていることを実感できるであろう。 According to the experimental results of FIG. 6, the ABS resin material used for the conventional nail chip has an HDD value of 70-80, but the vinyl chloride material and the elastomer material used for the nail chip of the present invention have an HDD value of 45-50. It was found to be close to 50. In this experimental result, the hardness of the nail tip of the present invention is about 60% to 70% compared to the hardness of the nail tip simulating the hardness of a conventional human nail. As described above, since the nail tip of the present invention uses a material having a hardness of about 60% to 70% of the conventional nail tip hardness, the nail tip of the present invention is a conventional product if taken by the user. You will realize that it has a softness that is clearly different from nail tips.

次に、素材の透明度を検証しておく。
ネイルチップ本体１０は装飾を施すため下地の色がない方が好ましい。実際の人体の爪も透明度が高い。可視光に属する３００ｎｍから８００ｎｍの光を照射し、透過率を求めた。透過率が高い方が透明度が高いこととなる。 Next, the transparency of the material is verified.
Since the nail chip body 10 is decorated, it is preferable that the nail chip body 10 has no base color. The actual human nails are also highly transparent. Irradiation with light of 300 nm to 800 nm belonging to visible light was performed to determine the transmittance. The higher the transmittance, the higher the transparency.

図７（ａ）はＡＢＳ樹脂の透明度、図７（ｂ）は塩化ビニルの透明度、図８（ａ）はエラストマーの透明度を示す図である。
図７、図８に示すように、概ね、ＡＢＳ樹脂と塩化ビニルは８０％程度の透過率、エラストマーは９０％程度の透過率と言える。目視するとエラストマーがもっともクリアな透明に見える。透明度の面からもエラストマーはネイルチップに適した素材であると言える。 FIG. 7A shows the transparency of the ABS resin, FIG. 7B shows the transparency of vinyl chloride, and FIG. 8A shows the transparency of the elastomer.
As shown in FIG. 7 and FIG. 8, it can be said that ABS resin and vinyl chloride generally have a transmittance of about 80%, and elastomer has a transmittance of about 90%. When viewed visually, the elastomer appears to be the clearest and transparent. From the viewpoint of transparency, elastomer can be said to be a material suitable for nail chips.

以上、実験１、実験２、実験３の結果からは、本発明のネイルチップ素材としてはエラストマーと塩化ビニル樹脂が適するという結論を得た。
以上、実証実験を経て、出願人は本発明のネイルチップの素材としてエラストマー、塩化ビニルを用いるのが適しているとの結論に至った。 As described above, from the results of Experiment 1, Experiment 2, and Experiment 3, it was concluded that elastomer and vinyl chloride resin are suitable as the nail chip material of the present invention.
As described above, through the verification experiment, the applicant has come to the conclusion that it is suitable to use an elastomer or vinyl chloride as a material for the nail chip of the present invention.

出願人が実際に検証を重ねた結果、軟質樹脂としてエラストマーまたは塩化ビニルを素材として用いれば外表面を上にして上方から３ｍｍ以上押し込んでも割れにくく折り曲げてもいわゆる「白化現象」が生じにくいという結論を得られている。また、実際の装着した状態において、外力をかけた実証を行ったが、本発明のネイルチップ本体１０では内面部分１２が緩衝材として働き、人体の爪２００への負荷が軽減されることが確認できた。 As a result of the applicant's actual verification, it is concluded that if an elastomer or vinyl chloride is used as a soft resin, the so-called “whitening phenomenon” is unlikely to occur even if the outer surface is pushed upwards by 3 mm or more and it is difficult to break or bend. Have been gained. In addition, in the actual wearing state, it was demonstrated that an external force was applied. However, in the nail tip body 10 of the present invention, it was confirmed that the inner surface portion 12 functions as a cushioning material and the load on the human nail 200 is reduced. did it.

なお、本発明のネイルチップとして、軟質樹脂素材のネイルチップ本体の外面にコーティング層を形成する前の状態で利用者に提供し、利用者が使用に際して薬液をコーティングしてコーティング層を形成してから使用するものでも良く、軟質樹脂素材のネイルチップ本体の外面にコーティング層を形成した二重構造を備えた状態で提供し、利用者がそのまま利用できるものであっても良い。 In addition, as a nail chip of the present invention, it is provided to a user in a state before forming a coating layer on the outer surface of a soft resin material nail chip body, and the user coats a chemical solution when used to form a coating layer. It is also possible to use a soft resin material nail chip body provided with a double structure in which a coating layer is formed on the outer surface of the nail chip body, and the user can use it as it is.

実施例２にかかる本発明のネイルチップ集合体１００の構成例を示す。
図９は、実施例２にかかる本発明のネイルチップ集合体１００の構成例を示す図である。
図９（ａ）は平面図、図９（ｂ）は正面図、図９（ｃ）は右側面図である。
ネイルチップ集合体１００は、複数個のネイルチップ本体１０と、軸体２０と、橋梁部３０を備え、押し出し成形により一体成形されている。本発明のネイルチップ集合体１００のネイルチップ本体は軟質樹脂素材で形成されており、軸体２０、橋梁部３０も軟質樹脂素材で形成されていても良い。 The structural example of the nail chip | tip aggregate | assembly 100 of this invention concerning Example 2 is shown.
FIG. 9 is a diagram illustrating a configuration example of the nail chip assembly 100 according to the second embodiment of the present invention.
9A is a plan view, FIG. 9B is a front view, and FIG. 9C is a right side view.
The nail chip assembly 100 includes a plurality of nail chip bodies 10, a shaft body 20, and a bridge portion 30, and is integrally formed by extrusion molding. The nail chip body of the nail chip assembly 100 of the present invention is formed of a soft resin material, and the shaft body 20 and the bridge portion 30 may also be formed of a soft resin material.

ネイルチップ本体１０は実施例１に示したネイルチップ本体であり、個々のネイルチップ本体１０のサイズは親指用の大きなサイズから小指用の小さなサイズまで多様なサイズのものがある。 The nail chip body 10 is the nail chip body shown in the first embodiment, and the size of each nail chip body 10 varies from a large size for the thumb to a small size for the little finger.

軸体２０は、底面が平面となっており、横たわった基本姿勢にて安定自立し全体を支える土台となる。 The shaft body 20 has a flat bottom surface and serves as a foundation that supports the entire body in a stable and independent manner.

橋梁部３０は、個々のネイルチップ本体１０に対応して適当な間隔をおいて軸体２０の軸方向に対して側方に設けられており、軸体２０とネイルチップ本体１０とをつなぐ役割を果たしている。 The bridge portion 30 is provided laterally with respect to the axial direction of the shaft body 20 at an appropriate interval corresponding to each nail chip body 10, and serves to connect the shaft body 20 and the nail chip body 10. Plays.

本発明のネイルチップ集合体１００の利用は図１０に示す手順で行うことができる。
まず、図１０（ａ）に示すように、個々のネイルチップ本体１０が橋梁部３０を介して軸体２０により支えられている状態のまま、個々のネイルチップ本体１０の外面部分１１に対して薬液１５をコーティングして外面部分１１のみを硬化させる。本発明のネイルチップ集合体１００全体はエラストマーや塩化ビニルなど柔らかい軟質樹脂素材で形成されており、薬液１５を塗布乾燥することにより硬いコーティング層が形成される。 The use of the nail chip assembly 100 of the present invention can be performed by the procedure shown in FIG.
First, as shown in FIG. 10A, the individual nail tip bodies 10 are supported by the shaft body 20 via the bridge portions 30, and the outer surface portions 11 of the individual nail tip bodies 10 are supported. Only the outer surface portion 11 is cured by coating the chemical solution 15. The entire nail chip assembly 100 of the present invention is formed of a soft soft resin material such as an elastomer or vinyl chloride, and a hard coating layer is formed by applying and drying the chemical solution 15.

次に、図１０（ｂ）に示すように、個々のネイルチップ本体１０が橋梁部３０を介して軸体２０により支えられている状態のまま、個々のネイルチップ本体１０の外面部分１１にネイルアートなどの装飾を施す。個々のネイルチップ本体１０の外面部分１１は硬化しているのでネイルアートなどの装飾を施しやすくなっている。 Next, as shown in FIG. 10B, the nail tip body 10 is nailed on the outer surface portion 11 of each nail tip body 10 while being supported by the shaft body 20 via the bridge portion 30. Apply art and other decorations. Since the outer surface portion 11 of each nail tip body 10 is hardened, it is easy to apply decoration such as nail art.

次に、図１０（ｃ）に示すように、個々のネイルチップ本体１０を橋梁部３０において切り離し、単体のネイルチップ本体１０を得る。 Next, as shown in FIG. 10 (c), the individual nail tip bodies 10 are separated at the bridge portion 30 to obtain a single nail tip body 10.

なお、橋梁部３０はエラストマーや塩化ビニルなど柔らかい軟質樹脂素材で形成されておれば優しく切り離すことができ、切り離しの際に生じる圧力などによりネイルチップ本体１０が割れたり弾けたりするおそれが低減する。従来のＡＢＳ樹脂素材の場合、橋梁部３０からネイルチップ本体１０を切り離す際にネイルチップ本体１０が割れたり弾けたりすることがあった。本発明のネイルチップ集合体１００ではネイルチップ本体１０の軸体２０からの切り離しにおいてもメリットがあることが理解されよう。 In addition, if the bridge part 30 is formed with soft soft resin materials, such as an elastomer and vinyl chloride, it can detach easily, and the possibility that the nail tip main body 10 will be cracked or flipped due to the pressure generated during the detachment is reduced. In the case of a conventional ABS resin material, when the nail tip body 10 is separated from the bridge portion 30, the nail tip body 10 may be cracked or flipped. It will be understood that the nail chip assembly 100 of the present invention has advantages in separating the nail chip body 10 from the shaft body 20.

次に、本発明のネイルチップ集合体１００の構成において、ネイルチップ本体１０と軸体２０と橋梁部３０の形状や関係における種々の工夫について述べる。 Next, in the configuration of the nail chip assembly 100 of the present invention, various ideas regarding the shapes and relationships of the nail chip body 10, the shaft body 20, and the bridge portion 30 will be described.

第１の工夫は、橋梁部３０を軸体２０からネイルチップ本体１０にかけて斜め上方に設け、ネイルチップ本体１０が上方に維持されるようにする工夫である。
図９に示したネイルチップ集合体１００の例はこの第１の工夫が施された例である。
図９（ｂ）、図９（ｃ）に示したように、橋梁部３０が斜め上方に構成され、ネイルチップ本体１０が上方に維持されている。この理由は、ネイルチップ集合体１００が机上などに載せ置かれた基本姿勢において、ネイルチップ本体１０が軸体２０に対して上方に維持され、ネイルチップ本体１０が橋梁部３０との接点のみを介して空中に浮いた状態で維持されるように工夫するためである。 The first device is a device in which the bridge portion 30 is provided obliquely upward from the shaft body 20 to the nail chip body 10 so that the nail chip body 10 is maintained upward.
The example of the nail chip assembly 100 shown in FIG. 9 is an example in which the first device is applied.
As shown in FIGS. 9B and 9C, the bridge portion 30 is configured obliquely upward, and the nail tip body 10 is maintained upward. This is because, in a basic posture in which the nail chip assembly 100 is placed on a desk or the like, the nail chip body 10 is maintained above the shaft body 20, and the nail chip body 10 only has a contact point with the bridge portion 30. It is for devising so that it may be maintained in the state of floating in the air.

図１１は比較上、橋梁部３０が軸体２０から水平に設けられている場合を想定した構成例の図である。図１１（ａ）は平面図、図１１（ｂ）は正面図、図１１（ｃ）は右側面図である。図１１の例では軸体２０と橋梁部３０とネイルチップ本体１０が略同一平面内に設けられているため、ネイルチップ集合体１００全体を机上などに載せ置いた場合に、図１１（ｂ）、図１１（ｃ）に示すようにネイルチップ本体１０も机上に触れてしまう。このようにネイルチップ本体１０が机上に触れてしまうと、ネイルチップ本体１０の周辺部に対する装飾が施しにくくなり装飾工程に不都合である上、ペインティング塗料の乾燥やストーンの接着剤の乾燥がしにくくなり乾燥工程に不都合である。 FIG. 11 is a diagram of a configuration example assuming that the bridge portion 30 is provided horizontally from the shaft body 20 for comparison. 11A is a plan view, FIG. 11B is a front view, and FIG. 11C is a right side view. In the example of FIG. 11, the shaft body 20, the bridge portion 30, and the nail tip body 10 are provided in substantially the same plane. Therefore, when the entire nail tip assembly 100 is placed on a desk or the like, FIG. As shown in FIG. 11C, the nail tip body 10 also touches the desk. If the nail chip body 10 touches the desk in this way, it is difficult to decorate the periphery of the nail chip body 10, which is inconvenient for the decoration process, and the painting paint or the stone adhesive is dried. It becomes difficult and inconvenient for the drying process.

図９（ｂ）、図９（ｃ）に示すように、橋梁部３０が斜め上方に構成されておればネイルチップ本体１０が軸体２０に対して上方に維持され、ネイルチップ本体１０が橋梁部３０との接点のみを介して空中に浮いた状態で維持され、ネイルチップ本体１０の周辺部に対する装飾が施しやすくなり装飾工程に好都合である上、ペインティング塗料の乾燥やストーンの接着剤の乾燥がしやすくなり乾燥工程に好都合である。 As shown in FIGS. 9B and 9C, if the bridge portion 30 is configured obliquely upward, the nail tip body 10 is maintained above the shaft body 20, and the nail tip body 10 is bridged. It is maintained in a state of floating in the air only through the contact point with the part 30, and it is easy to decorate the peripheral part of the nail chip body 10 and is convenient for the decoration process. It is easy to dry and is convenient for the drying process.

第２の工夫は、軸体２０の高さを高くすることにより、ネイルチップ本体１０が上方に維持されるようにする工夫である。
図１２は第２の工夫を取り込んだネイルチップ集合体１００ａの例である。図１２（ａ）は平面図、図１２（ｂ）は正面図、図１２（ｃ）は右側面図である。
ネイルチップ集合体１００ａは、複数個のネイルチップ本体１０と、軸体２０ａと、橋梁部３０を備えている。ネイルチップ本体１０は実施例１のネイルチップ本体１０と同様で良く、ここでの説明は省略する。 The second device is a device that allows the nail tip body 10 to be maintained upward by increasing the height of the shaft body 20.
FIG. 12 is an example of a nail chip assembly 100a incorporating the second device. 12A is a plan view, FIG. 12B is a front view, and FIG. 12C is a right side view.
The nail chip assembly 100 a includes a plurality of nail chip bodies 10, a shaft body 20 a, and a bridge portion 30. The nail chip body 10 may be the same as the nail chip body 10 of the first embodiment, and a description thereof is omitted here.

橋梁部３０ａは、軸体の軸方向に対して側方へ水平に設けられており、実施例１のように斜め上方に持ち上がる形態となっていない。ただし、軸体２０ａの厚みが実施例１よりも厚くなっており、軸体２０ａにおける橋梁部３０ａから底面までの高さがネイルチップ本体１０の厚みよりも十分に大きいものとなっている。軸体２０ａの厚さが十分に厚いために基本姿勢においてネイルチップ本体１０が橋梁部３０ａとの接点のみを介して支えられ、ネイルチップ本体１０が空中に維持され、第１の工夫と同様の効果が得られる。
ネイルチップ本体１０が空中に維持された状態であるので、薬液１５を塗布乾燥して硬いコーティング層を形成する工程、続いてネイルアートなどの装飾を施した後に乾燥する工程が行いやすくなる。 The bridge portion 30a is provided horizontally to the side with respect to the axial direction of the shaft body, and is not lifted obliquely upward as in the first embodiment. However, the thickness of the shaft body 20a is thicker than that of the first embodiment, and the height from the bridge portion 30a to the bottom surface of the shaft body 20a is sufficiently larger than the thickness of the nail tip body 10. Since the shaft body 20a is sufficiently thick, the nail tip body 10 is supported in the basic posture only through the contact with the bridge portion 30a, and the nail tip body 10 is maintained in the air, which is the same as the first device. An effect is obtained.
Since the nail tip body 10 is maintained in the air, the step of applying and drying the chemical solution 15 to form a hard coating layer, and subsequently the step of drying after applying decoration such as nail art are facilitated.

次に、第３の工夫は、ネイルチップ集合体１００が一層安定自立しやすいように軸体２０の底面積を大きくしておく工夫である。
図１３は、第３の工夫を取り込んだネイルチップ集合体１００ｂの例である。
図１３（ａ）は平面図、図１３（ｂ）は正面図、図１３（ｃ）は右側面図である。
ネイルチップ集合体１００ｂは、複数個のネイルチップ本体１０と、軸体２０ｂと、橋梁部３０ａを備えている。ネイルチップ本体１０は実施例１のネイルチップ本体１０と同様で良く、ここでの説明は省略する。
図１３に見るように軸体２０ｂの底面部分が大きくなっており、ネイルチップ集合体１００ｂ全体がより一層安定自立しやすい構造となっている。ネイルチップ集合体１００ｂが安定して自立しやすくなるため、ネイルチップ本体１０に対して薬液１５を塗布乾燥して硬いコーティング層を形成する工程、ネイルアートなどの装飾を施した後に乾燥する工程が行いやすくなる。 Next, the third device is a device that increases the bottom area of the shaft body 20 so that the nail chip assembly 100 is more stable and independent.
FIG. 13 is an example of a nail chip assembly 100b incorporating the third device.
13A is a plan view, FIG. 13B is a front view, and FIG. 13C is a right side view.
The nail chip assembly 100b includes a plurality of nail chip bodies 10, a shaft body 20b, and a bridge portion 30a. The nail chip body 10 may be the same as the nail chip body 10 of the first embodiment, and a description thereof is omitted here.
As shown in FIG. 13, the bottom portion of the shaft body 20b is large, and the entire nail chip assembly 100b has a structure that is more likely to be more stable and independent. Since the nail chip assembly 100b is stable and easily becomes independent, a process of applying and drying the chemical solution 15 on the nail chip body 10 to form a hard coating layer, and a process of drying after applying decoration such as nail art It becomes easier to do.

次に、ネイルチップ本体１０の配置の工夫として、軸体２０や橋梁部３０の体積を減らし、押し出し成形において流し込む素材を少なくする工夫について述べる。
まず、軸体２０の太さや橋梁部３０の太さはネイルチップ本体１０のサイズに応じて決めてよい。つまり、親指用の大きなサイズのネイルチップ本体１０を支える軸体２０や橋梁部３０は比較的太いものとする必要がある一方、小指用の小さなサイズのネイルチップ本体１０を支える軸体２０や橋梁部３０は比較的細いもので良い。 Next, as a device for disposing the nail tip body 10, a device for reducing the volume of the shaft body 20 and the bridge portion 30 and reducing the material to be poured in the extrusion molding will be described.
First, the thickness of the shaft body 20 and the thickness of the bridge portion 30 may be determined according to the size of the nail tip body 10. That is, the shaft body 20 and the bridge portion 30 that support the large-sized nail tip body 10 for the thumb need to be relatively thick, while the shaft body 20 and the bridge that support the small-sized nail tip body 10 for the little finger. The portion 30 may be relatively thin.

次に、個々のネイルチップ本体１０の軸体２０に対する配置において、軸体２０の一端から他端にかけてサイズの大きなものから小さなものへとサイズ順の配置とし、軸体２０の太さを一端側が太く他端側にかけて細くなってゆくように工夫する。このようにサイズ順に並べておくことにより軸体２０や橋梁部３０の太さの調整が容易となる。 Next, in the arrangement of the individual nail chip main body 10 with respect to the shaft body 20, the arrangement is made in order of size from the largest to the smallest from one end of the shaft body 20 to the other end. Try to be thicker and thinner toward the other end. By arranging in this order in size, the thickness of the shaft body 20 and the bridge portion 30 can be easily adjusted.

なお、軸体２０の太さを一端側が太く他端側にかけて細くする工夫において、軸体２０の太さの調整として、軸体２０の水平方向の幅のみならず垂直方向の高さの調整を含むことも可能である。このように水平方向の幅を小さくして行くとともに垂直方向の高さも小さくして行くことにより素材の量をより一層小さくできるからである。 It should be noted that in the idea of reducing the thickness of the shaft body 20 from one end to the other end, the thickness of the shaft 20 is adjusted by adjusting not only the horizontal width of the shaft 20 but also the vertical height. It can also be included. This is because the amount of material can be further reduced by reducing the horizontal width and the vertical height in this way.

ここで、軸体２０の高さの調整が、軸体２０の上面を下げるのではなく軸体２０の底面を上げることによる調整とすることが好ましい。図１４（ａ）は軸体２０の上面を下げることによる調整をした場合を示す正面図、一方、図１４（ｂ）は軸体２０の底面を上げることによる調整をした場合を示す正面図である。図１４（ａ）に示すように軸体２０の上面を下げることによる調整をした場合にはネイルチップ本体１０が比較的底面近くに位置することとなるが、図１４（ｂ）に示すように軸体２０の底面を上げることによる調整をした場合にはネイルチップ本体１０が比較的高くに位置することとなり、ネイルチップ本体１０に対して薬液１５を塗布乾燥して硬いコーティング層を形成する工程、ネイルアートなどの装飾を施した後に乾燥する工程が行いやすくなる。なお、図１４（ｂ）に示すように軸体２０の底面を上げる調整を施した軸体部分の底面に、調整にかかる高さに相当する柱状突起２１を複数個設ける。このように柱状突起２１を設けておくことにより、底面を上げる調整を施さなかった軸体２０の底面と柱状突起２４の底面が同一平面の底面を形成し、全体が自立安定しやすい構造となっている。 Here, the height of the shaft body 20 is preferably adjusted by raising the bottom surface of the shaft body 20 instead of lowering the upper surface of the shaft body 20. FIG. 14A is a front view showing a case where the adjustment is performed by lowering the upper surface of the shaft body 20, while FIG. 14B is a front view showing a case where the adjustment is performed by raising the bottom surface of the shaft body 20. is there. When adjustment is performed by lowering the upper surface of the shaft body 20 as shown in FIG. 14 (a), the nail tip body 10 is positioned relatively near the bottom surface, but as shown in FIG. 14 (b). When the adjustment is performed by raising the bottom surface of the shaft body 20, the nail tip body 10 is positioned relatively high, and the liquid 15 is applied to the nail tip body 10 and dried to form a hard coating layer. It becomes easy to perform a drying process after applying decoration such as nail art. As shown in FIG. 14B, a plurality of columnar protrusions 21 corresponding to the height required for adjustment are provided on the bottom surface of the shaft body portion that has been adjusted to raise the bottom surface of the shaft body 20. By providing the columnar protrusions 21 in this way, the bottom surface of the shaft body 20 and the bottom surface of the columnar protrusions 24 that have not been adjusted to raise the bottom surface form a bottom surface in the same plane, and the whole structure is easily self-supporting and stable. ing.

なお、押し出し成形時に素材を流す方向としては特に限定されることはなく、前記軸体の一方の端から素材を流し込んでも良く、また他方の端から素材を流し込んでも良く、また、軸の途中から素材を流し込んでも良い。金型と射出速度の関係などを考慮して製造工程において調整すれば良い。 The direction in which the material flows during extrusion is not particularly limited, and the material may be poured from one end of the shaft body, the material may be poured from the other end, or from the middle of the shaft. Material may be poured. The manufacturing process may be adjusted in consideration of the relationship between the mold and the injection speed.

以上、本発明の好ましい実施形態を図示して説明してきたが、本発明の技術的範囲を逸脱することなく種々の変更が可能であることは理解されるであろう。従って本発明の技術的範囲は添付された特許請求の範囲の記載によってのみ限定されるものである。 While preferred embodiments of the invention have been illustrated and described, it will be appreciated that various changes can be made without departing from the scope of the invention. Therefore, the technical scope of the present invention is limited only by the description of the appended claims.

本発明のネイルチップおよびネイルチップ集合体は、手の爪用、足の爪用などのネイルチップに広く適用することができる。 The nail chip and the nail chip assembly of the present invention can be widely applied to nail chips for hand nails and toenails.

本発明のネイルチップ本体１０の構成例を示す図The figure which shows the structural example of the nail tip main body 10 of this invention. ネイルチップ本体１０において二重構造を実現する原理を模式的に示す図The figure which shows typically the principle which implement | achieves a double structure in the nail tip main body 10 押し込みによる軟性試験の試験方法の概略を示す図The figure which shows the outline of the test method of the softness test by indentation 押し込みによる軟性試験の実験結果を示す図The figure which shows the experimental result of the softness test by indentation プラスチックのデュロメータ硬さ試験方法の概略を示す図Diagram showing outline of plastic durometer hardness test method プラスチックのデュロメータ硬さ試験の実験結果を示す図The figure which shows the experimental result of the durometer hardness test of plastic （ａ）はＡＢＳ樹脂の透明度、（ｂ）は塩化ビニルの透明度を示す図(A) shows the transparency of ABS resin, (b) shows the transparency of vinyl chloride エラストマーの透明度を示す図Diagram showing transparency of elastomer 実施例２にかかる本発明のネイルチップ集合体１００の構成例を示す図The figure which shows the structural example of the nail chip | tip aggregate | assembly 100 of this invention concerning Example 2. FIG. 本発明のネイルチップ集合体１００の利用手順を示す図The figure which shows the utilization procedure of the nail chip | tip aggregate | assembly 100 of this invention. 比較として橋梁部３０が軸体２０から水平に設けられている従来のネイルチップ集合体の構成例を示す図The figure which shows the structural example of the conventional nail chip | tip aggregate | assembly in which the bridge part 30 is provided horizontally from the shaft body 20 as a comparison. 軸体２０の高さを高くしてネイルチップを空中に維持する構成例を示す図The figure which shows the structural example which raises the height of the shaft body 20 and maintains a nail tip in the air ネイルチップ集合体１００が一層安定自立しやすいように軸体２０の底面積を大きくした構成例を示す図The figure which shows the structural example which enlarged the bottom area of the shaft body 20 so that the nail chip | tip aggregate | assembly 100 may be stabilized more easily. （ａ）は軸体２０の上面を下げることによる調整をした場合を示す側面図、（ｂ）は軸体２０の底面を上げることによる調整をした場合を示す側面図、(A) is a side view showing a case where an adjustment is made by lowering the upper surface of the shaft body 20, (b) is a side view showing a case where an adjustment is made by raising the bottom surface of the shaft body 20, 従来のネイルチップ集合体の形状を示す図The figure which shows the shape of the conventional nail chip assembly

符号の説明Explanation of symbols

１０ネイルチップ本体
１１外面部分
１２内面部分
２０軸体
２１柱状突起
３０橋梁部
１００ネイルチップ集合体 DESCRIPTION OF SYMBOLS 10 Nail chip body 11 Outer surface part 12 Inner surface part 20 Shaft body 21 Columnar protrusion 30 Bridge part 100 Nail chip assembly

Claims

外面に装飾を施し、内面を使用者の爪に接着して装着するネイルチップであって、
前記ネイルチップ本体の素材を柔らかい軟質樹脂素材とし、人体の爪に近い硬度で人体の爪の硬さを模したネイルチップよりも柔らかく形成しておき、
使用時に前記外面に対して硬化性を与える薬液をコーティングすることにより前記外面に前記ネイルチップ本体の硬度よりも硬いコーティング層を形成し、前記内面の柔軟性は保たせた二重構造とすることにより、前記外面を硬くして装飾を行いやすくすると同時に前記内面の柔らかさを維持して前記使用者の爪への負担を軽減せしめるネイルチップ。 It is a nail chip that is decorated on the outer surface and is attached by attaching the inner surface to the user's nails,
The material of the nail chip body is a soft soft resin material, and is formed softer than a nail chip imitating the hardness of a human nail with a hardness close to that of a human nail,
A coating layer that is harder than the hardness of the nail tip body is formed on the outer surface by coating a chemical solution that imparts curability to the outer surface during use, and the inner surface has a flexible structure that retains flexibility. Thus, the nail tip that hardens the outer surface and facilitates decoration and at the same time maintains the softness of the inner surface and reduces the burden on the user's nails.

外面に装飾を施し、内面を使用者の爪に接着して装着するネイルチップであって、
人体の爪に近い硬度で人体の爪の硬さを模したネイルチップよりも柔らかい軟質樹脂素材により形成したネイルチップ本体と、
前記ネイルチップ本体の外面を覆い、前記ネイルチップ本体の硬度よりも硬い硬度であるコーティング層とを備え、
前記外面は前記コーティング層によって硬く、前記内面は前記軟質樹脂素材によって柔軟とした二重構造とし、前記外面への装飾を行いやすくすると同時に前記内面の柔らかさを維持して前記使用者の爪への負担を軽減せしめたネイルチップ。 It is a nail chip that is decorated on the outer surface and is attached by attaching the inner surface to the user's nails,
A nail tip body formed of a soft resin material softer than a nail tip imitating the hardness of a human nail with a hardness close to that of a human nail,
Covering the outer surface of the nail tip body, and having a coating layer that is harder than the hardness of the nail tip body,
The outer surface is hardened by the coating layer, and the inner surface is made flexible by the soft resin material to facilitate decoration on the outer surface and at the same time maintain the softness of the inner surface to the user's nails. Nail tips that reduce the burden on the skin.

前記軟質樹脂素材が、エラストマーまたは塩化ビニル樹脂のいずれかであることを特徴とする請求項１または２に記載のネイルチップ。 The nail chip according to claim 1 or 2, wherein the soft resin material is either an elastomer or a vinyl chloride resin.

前記軟質樹脂素材の柔軟性が、プラスチックのデュロメータ硬さ試験方法のタイプＤの測定において、ＨＤＤ値５０以下の柔軟性であることを特徴とする請求項１から３のいずれか１項に記載のネイルチップ。 4. The soft resin material according to claim 1, wherein the soft resin material has a HDD value of 50 or less in the measurement of the type D of the plastic durometer hardness test method. 5. Nail tip.

前記ネイルチップ本体が前記外面を上にして上方から３ｍｍ以上押し込んでも白化現象が起きない柔軟性を確保せしめたものであることを特徴とした請求項１から４のいずれか１項に記載のネイルチップ。 The nail according to any one of claims 1 to 4, wherein the nail tip body has a flexibility that does not cause a whitening phenomenon even when the outer surface is pushed upward by 3 mm or more from above. Chip.

外面に装飾を施し、内面を使用者の爪に接着して装着する複数個のネイルチップ本体と、
横たわった基本姿勢にて安定自立し、全体を支える土台となる軸体と、
個々の前記ネイルチップ本体に対応して適当な間隔をおいて前記軸体の軸方向に対して側方に設けられた、前記軸体と前記ネイルチップ本体とをつなぐ橋梁部とを備えたネイルチップ集合体であって、
前記ネイルチップ本体の素材を柔らかい軟質樹脂素材とし、前記ネイルチップ本体を、人体の爪に近い硬度で人体の爪の硬さを模したネイルチップよりも柔らかく形成し、
使用に際して前記ネイルチップ本体の外面に対して硬化性を与える薬液をコーティングして前記外面に前記ネイルチップ本体の硬度よりも硬いコーティング層を形成して前記内面の柔軟性は保たせた二重構造を備えたものとし、前記ネイルチップ本体が、前記外面を硬くして装飾を行いやすくすると同時に前記内面の柔らかさを維持して前記使用者の爪への負担を軽減せしめるものである、ネイルチップ集合体。 A plurality of nail tip bodies that are decorated on the outer surface and are attached by attaching the inner surface to the user's nails,
A shaft that will be stable and independent in the basic posture,
A nail comprising a bridge portion that is provided laterally with respect to the axial direction of the shaft body at an appropriate interval corresponding to each of the nail chip bodies and that connects the shaft body and the nail chip body. A chip assembly,
The material of the nail chip body is a soft soft resin material, and the nail chip body is formed softer than a nail chip imitating the hardness of a human nail with a hardness close to that of the human nail,
In use, a dual structure in which the inner surface is kept flexible by coating the outer surface of the nail tip body with a chemical solution that imparts curability to form a coating layer harder than the hardness of the nail tip body on the outer surface. The nail tip body is designed to make the outer surface harder and easier to decorate, while at the same time maintaining the softness of the inner surface and reducing the burden on the user's nails. Aggregation.

外面に装飾を施し、内面を使用者の爪に接着して装着する複数個のネイルチップ本体であって、人体の爪に近い硬度で人体の爪の硬さを模したネイルチップよりも柔らかい軟質樹脂素材により形成したネイルチップ本体部分と、
前記ネイルチップ本体の外面を覆い、前記ネイルチップ本体の硬度よりも硬い硬度であるコーティング層と、
横たわった基本姿勢にて安定自立し、全体を支える土台となる軸体と、
個々の前記ネイルチップ本体に対応して適当な間隔をおいて前記軸体の軸方向に対して側方に設けられた、前記軸体と前記ネイルチップ本体とをつなぐ橋梁部とを備えたネイルチップ集合体であって、
前記ネイルチップ本体が、前記外面は前記コーティング層によって硬く、前記内面は前記軟質樹脂素材によって柔軟である二重構造とし、前記外面への装飾を行いやすくすると同時に前記内面の柔らかさを維持して前記使用者の爪への負担を軽減せしめたものである、ネイルチップ集合体。 A plurality of nail tip bodies that are decorated on the outer surface and attached to the user's nails by attaching the inner surface, and are softer than a nail tip that mimics the hardness of human nails with a hardness close to that of the human nails A nail chip body portion formed of a resin material;
A coating layer that covers the outer surface of the nail tip body and has a hardness that is harder than the hardness of the nail tip body;
A shaft that will be stable and independent in the basic posture,
A nail comprising a bridge portion that is provided laterally with respect to the axial direction of the shaft body at an appropriate interval corresponding to each of the nail chip bodies and that connects the shaft body and the nail chip body. A chip assembly,
The nail chip body has a double structure in which the outer surface is hardened by the coating layer and the inner surface is flexible by the soft resin material, and it is easy to decorate the outer surface while maintaining the softness of the inner surface. A nail chip assembly that reduces the burden on the user's nails.

前記軟質樹脂素材が、エラストマーまたは塩化ビニル樹脂のいずれかであることを特徴とする請求項６または７に記載のネイルチップ集合体。 The nail chip assembly according to claim 6 or 7, wherein the soft resin material is either an elastomer or a vinyl chloride resin.

前記軟質樹脂素材の柔軟性が、プラスチックのデュロメータ硬さ試験方法のタイプＤの測定において、ＨＤＤ値５０以下の柔軟性であることを特徴とする請求項６から８のいずれか１項に記載のネイルチップ集合体。 9. The soft resin material according to claim 6, wherein the soft resin material has a HDD value of 50 or less in the measurement of type D in the plastic durometer hardness test method. 10. Nail chip assembly.

前記ネイルチップ本体が前記外面を上にして上方から３ｍｍ以上押し込んでも白化現象が起きない柔軟性を確保せしめたものであることを特徴とした請求項６から９のいずれか１項に記載のネイルチップ集合体。 The nail according to any one of claims 6 to 9, wherein the nail chip main body is secured so as not to cause a whitening phenomenon even if the outer surface is pushed upward by 3 mm or more from above. Chip assembly.

前記橋梁部が前記軸体から前記ネイルチップ本体にかけて斜め上方に設けられ、前記基本姿勢において前記ネイルチップ本体が前記軸体に対して上方に維持され、前記基本姿勢において前記ネイルチップ本体が前記橋梁部との接点のみを介して支えられ、空中に維持されることを特徴とした請求項６から１０のいずれか１項に記載のネイルチップ集合体。 The bridge portion is provided obliquely upward from the shaft body to the nail chip body, and the nail chip body is maintained upward with respect to the shaft body in the basic posture, and the nail chip body is bridged in the basic posture. The nail chip assembly according to any one of claims 6 to 10, wherein the nail chip assembly is supported only through a contact point with the portion and maintained in the air.

前記橋梁部が前記軸体の軸方向に対して側方に設けられ、前記軸体における前記橋梁部から底面までの高さが前記ネイルチップ本体の厚みよりも十分に大きく、前記基本姿勢において前記ネイルチップ本体が前記橋梁部との接点のみを介して支えられ、空中に維持されることを特徴とした請求項６から１１のいずれか１項に記載のネイルチップ集合体。 The bridge portion is provided laterally with respect to the axial direction of the shaft body, and the height from the bridge portion to the bottom surface of the shaft body is sufficiently larger than the thickness of the nail tip body, and in the basic posture, The nail tip assembly according to any one of claims 6 to 11, wherein the nail tip body is supported only through a contact point with the bridge portion and is maintained in the air.

個々の前記ネイルチップ本体のサイズが、親指用の大きなサイズから小指用の小さなサイズまで多様なサイズとなっており、
個々の前記ネイルチップ本体の前記軸体に対する配置において、前記軸体の一方から他方にかけてサイズの大きなものから小さなものへとサイズ順に配置され、
前記軸体の太さと前記橋梁部の太さが、前記軸体の一方から他方にかけて小さくなるように調整されていることを特徴とする請求項６から１２のいずれか１項に記載のネイルチップ集合体。 The size of each of the nail chip bodies varies from a large size for the thumb to a small size for the little finger,
In the arrangement of the individual nail tip main body with respect to the shaft body, the nail chip body is arranged in order of size from one of the shaft bodies to the other in the order of size from one to the other.
The nail tip according to any one of claims 6 to 12, wherein a thickness of the shaft body and a thickness of the bridge portion are adjusted so as to decrease from one side of the shaft body to the other. Aggregation.

前記軸体の太さの調整が、前記軸体の水平方向の幅のみならず垂直方向の高さの調整を含み、前記軸体の高さの調整が、前記軸体の上面を下げるのではなく前記軸体の底面を上げることによる調整であり、
前記底面を上げる調整を施した軸体部分の底面に、前記調整にかかる高さに相当する柱状突起を複数個設け、
前記底面を上げる調整を施さなかった軸体の底面と前記柱状突起の底面により全体が自立安定しやすい構造とした請求項１３に記載のネイルチップ集合体。 The adjustment of the thickness of the shaft includes adjustment of the height in the vertical direction as well as the horizontal width of the shaft, and the adjustment of the height of the shaft does not lower the upper surface of the shaft. And adjustment by raising the bottom surface of the shaft body,
A plurality of columnar protrusions corresponding to the height required for the adjustment are provided on the bottom surface of the shaft body portion that has been adjusted to raise the bottom surface,
14. The nail tip assembly according to claim 13, wherein the nail chip assembly as a whole is easily self-supportingly stabilized by the bottom surface of the shaft body that has not been adjusted to raise the bottom surface and the bottom surface of the columnar protrusion.