JP2009214098A - Honeycomb structure, apparatus for cleaning exhaust gas and method for manufacturing the honeycomb structure - Google Patents
Honeycomb structure, apparatus for cleaning exhaust gas and method for manufacturing the honeycomb structure Download PDFInfo
- Publication number
- JP2009214098A JP2009214098A JP2009021389A JP2009021389A JP2009214098A JP 2009214098 A JP2009214098 A JP 2009214098A JP 2009021389 A JP2009021389 A JP 2009021389A JP 2009021389 A JP2009021389 A JP 2009021389A JP 2009214098 A JP2009214098 A JP 2009214098A
- Authority
- JP
- Japan
- Prior art keywords
- honeycomb
- honeycomb structure
- sealing portion
- sealing
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、ハニカム構造体、排ガス浄化装置、及び、ハニカム構造体の製造方法に関する。 The present invention relates to a honeycomb structure, an exhaust gas purification device, and a method for manufacturing a honeycomb structure.
従来、ディーゼルエンジン等の内燃機関から排出される排ガス中には、パティキュレートマター（以下、ＰＭともいう）が含まれており、近年、このＰＭが環境や人体に害を及ぼすことが問題となっている。
そこで、排ガス中のＰＭを捕集して排ガスを浄化するフィルタとして、例えば、多孔質セラミックを用いたハニカム構造体からなるハニカムフィルタが種々提案されている。
Conventionally, exhaust gas discharged from an internal combustion engine such as a diesel engine contains particulate matter (hereinafter also referred to as PM). In recent years, it has been a problem that this PM is harmful to the environment and the human body. ing.
Therefore, various types of honeycomb filters made of a honeycomb structure using a porous ceramic have been proposed as filters for collecting PM in the exhaust gas and purifying the exhaust gas.
このようなハニカム構造体として、特許文献１には、多孔質セラミック焼結体からなる複数のフィルタの外周面同士をシール材層を介して接着することにより、各フィルタを一体化したハニカム構造体が開示されている（例えば、特許文献１参照）。 As such a honeycomb structure, Patent Document 1 discloses a honeycomb structure in which each filter is integrated by bonding the outer peripheral surfaces of a plurality of filters made of a porous ceramic sintered body through a sealing material layer. Is disclosed (for example, see Patent Document 1).
このようなハニカム構造体は、下記のような方法により製造することができる。
まず、セラミック粉末とバインダと分散媒液等とを混合して湿潤混合物を調製する。
次に、この湿潤混合物を押出成形し、押し出された成形体を所定の長さに切断することにより、柱状のハニカム成形体を作製する。
その後、ハニカム成形体の各セルのいずれか一方の端部が封止されるように各セルの所定の端部に封止材ペーストを充填する。次に、封止材ペーストが充填されたハニカム成形体に、脱脂処理及び焼成処理を施し、フィルタとして機能するハニカム焼成体を作製する。
次に、複数のハニカム焼成体をシール材層（接着材層）を介して結束させてハニカム焼成体の集合体を作製し、その後、必要に応じて、ハニカム焼成体の集合体の外周に切削加工を施したり、この集合体の外周にコート層を形成したりすることによりハニカム構造体を製造する。
Such a honeycomb structure can be manufactured by the following method.
First, a ceramic powder, a binder, a dispersion medium liquid, and the like are mixed to prepare a wet mixture.
Next, this wet mixture is extruded, and the extruded molded body is cut into a predetermined length to produce a columnar honeycomb molded body.
Thereafter, a predetermined paste of each cell is filled with a sealing material paste so that any one end of each cell of the honeycomb formed body is sealed. Next, the honeycomb formed body filled with the sealing material paste is subjected to a degreasing process and a firing process, thereby manufacturing a honeycomb fired body that functions as a filter.
Next, a plurality of honeycomb fired bodies are bundled through a sealing material layer (adhesive layer) to produce a honeycomb fired body aggregate, and then, if necessary, cut to the outer periphery of the honeycomb fired body aggregate A honeycomb structure is manufactured by processing or forming a coat layer on the outer periphery of the aggregate.
特許文献１に記載されたハニカム構造体の製造方法では、押出成形によりハニカム成形体を作製する時点で、作製するハニカム焼成体と略同形のハニカム成形体を作製し、このハニカム成形体に、封止、脱脂、焼成等の各種処理を施してハニカム焼成体を作製している。
このような製造方法において、ハニカム焼成体のサイズは、焼成処理を経ることにより、ハニカム成形体のサイズよりも若干小さくなる。そして、このようなサイズの縮小は避けることができない。
そのため、ハニカム成形体を作製する際には、サイズの縮小を見込んで、ハニカム焼成体のサイズよりも若干大きいハニカム成形体を作製する必要があった。
しかしながら、サイズの縮小量は予想値であり、焼成条件のバラツキ等により作製したハニカム焼成体のサイズにバラツキが生じることがあった。
そして、ハニカム焼成体のサイズにバラツキが生じると、複数個のハニカム焼成体を結束させてハニカム構造体を製造した場合に、ハニカム構造体の端面に凹凸が生じることとなり、場合によっては、端面研磨を行う必要があった。
しかしながら、端面研磨は、可能であれば省略が望まれる工程である。なぜなら、研磨処理を行うことにより、ハニカム構造体の端面に欠けが発生する、ハニカム構造体のセル壁の気孔に研磨粉が入り込む等の不都合が生じる場合があるからである。また、端面研磨、セル壁の気孔に入り込んだ研磨粉を除去するための洗浄等の工程の増加がそのままコストの増加に繋がるからである。
In the method for manufacturing a honeycomb structure described in Patent Document 1, a honeycomb formed body having substantially the same shape as the honeycomb fired body to be manufactured is manufactured at the time of manufacturing the honeycomb formed body by extrusion molding. A honeycomb fired body is manufactured by performing various treatments such as stopping, degreasing, and firing.
In such a manufacturing method, the size of the honeycomb fired body is slightly smaller than the size of the honeycomb formed body through the firing treatment. And such a reduction in size cannot be avoided.
Therefore, when manufacturing a honeycomb formed body, it was necessary to manufacture a honeycomb formed body slightly larger than the size of the honeycomb fired body in anticipation of size reduction.
However, the amount of size reduction is an expected value, and there may be variations in the size of the honeycomb fired body produced due to variations in the firing conditions.
If the honeycomb fired bodies vary in size, when the honeycomb structure is manufactured by bundling a plurality of honeycomb fired bodies, the end faces of the honeycomb structure are uneven. Had to do.
However, the end surface polishing is a process that should be omitted if possible. This is because the polishing process may cause inconveniences such as chipping of the end face of the honeycomb structure and the introduction of polishing powder into the pores of the cell wall of the honeycomb structure. Further, the increase in processes such as end face polishing and cleaning for removing the polishing powder that has entered the pores of the cell wall directly leads to an increase in cost.
また、上述したハニカム構造体の製造方法のように、作製するハニカム焼成体と略同形のハニカム成形体を作製して各種処理を行う場合、生産性が低くなる場合があった。特に、長手方向の長さの短いハニカム構造体を製造する場合には、この傾向が顕著であった。
これについて、もう少し詳しく説明する。
上述したようなハニカム構造体の製造方法において、ハニカム成形体に焼成処理を施す際には、通常、複数個のハニカム成形体を１個の焼成用治具に収納した状態で行う。ここで、成形体の焼結を確実かつ均一に進行させるには、ハニカム成形体を焼成用治具内に収納する際に、ハニカム成形体同士をある程度離間させて収納する必要がある。
そのため、焼成用治具の大きさが同一である場合、ハニカム成形体が小さくなると、ハニカム成形体同士の間のスペース（空間）が占める割合が増加することとなり、その結果、ハニカム焼成体の生産性が低下することとなる。
別の言い方をすると、焼成用治具の大きさが同一である場合、例えば、ハニカム成形体のサイズが１／２になっても、焼成用治具内に収納することできるハニカム成形体の数が焼成用治具内に収納することができる通常のサイズのハニカム成形体の数の２倍になるわけではなく、収納することできるハニカム成形体の数は２倍未満となる。
また、焼成用治具は、ハニカム成形体の大きさに合せて最適な大きさのものを用いることが望ましく、ハニカム成形体の大きさに合せて、大きさの異なる焼成用治具を準備することが望ましいが、このような大きさの異なる焼成用治具を準備することは、製造コストの増加に繋がる。
In addition, when the honeycomb formed body that is substantially the same shape as the honeycomb fired body to be manufactured is manufactured and subjected to various treatments as in the above-described method for manufacturing a honeycomb structure, productivity may be lowered. This tendency was particularly remarkable when a honeycomb structure having a short length in the longitudinal direction was manufactured.
This will be explained in a little more detail.
In the method for manufacturing a honeycomb structured body as described above, when the honeycomb formed body is subjected to the firing treatment, usually, a plurality of honeycomb formed bodies are stored in a single firing jig. Here, in order to advance the sintering of the formed body reliably and uniformly, when the honeycomb formed body is stored in the firing jig, it is necessary to store the honeycomb formed bodies apart from each other to some extent.
Therefore, when the size of the firing jig is the same, if the honeycomb formed body becomes smaller, the proportion of the space (space) between the honeycomb formed bodies increases. As a result, the production of the honeycomb fired body The performance will be reduced.
In other words, when the size of the firing jig is the same, for example, the number of honeycomb molded bodies that can be accommodated in the firing jig even if the size of the honeycomb molded body is halved. However, the number of honeycomb formed bodies of normal size that can be stored in the firing jig is not doubled, and the number of honeycomb formed bodies that can be stored is less than double.
In addition, it is desirable to use a firing jig having an optimum size according to the size of the honeycomb formed body, and prepare firing jigs having different sizes according to the size of the honeycomb formed body. It is desirable, however, to prepare such firing jigs having different sizes leads to an increase in manufacturing cost.
そこで、本発明者らは上記課題を解決するために鋭意検討を行い、本発明を完成した。
請求項１に記載のハニカム構造体は、
複数のセルがセル壁を隔てて長手方向に並設され、上記セルのいずれか一方の端部が封止材ペーストにより形成された封止部により封止された柱状のハニカム焼成体からなるハニカムブロックを備えたハニカム構造体であって、
上記封止部のうち、上記ハニカム焼成体の一方の端面側の封止部は焼成された第一の封止部であり、上記ハニカム焼成体の他方の端面側の封止部は未焼成の第二の封止部であることを特徴とするハニカム構造体である。
Therefore, the present inventors have intensively studied to solve the above-mentioned problems, and completed the present invention.
The honeycomb structure according to claim 1,
A honeycomb composed of a columnar honeycomb fired body in which a plurality of cells are arranged side by side in the longitudinal direction across a cell wall, and one of the ends of the cells is sealed by a sealing portion formed of a sealing material paste A honeycomb structure with blocks,
Among the sealing parts, the sealing part on one end face side of the honeycomb fired body is a fired first sealing part, and the sealing part on the other end face side of the honeycomb fired body is unfired. The honeycomb structure is a second sealing portion.
請求項１に記載のハニカム構造体は、後述する本発明のハニカム構造体の製造方法により、効率よく製造することができる。
また、請求項１に記載のハニカム構造体では、このハニカム構造体を構成するハニカム焼成体において、一方の端面側の封止部が焼成された封止部であり、他方の端面側の封止部が未焼成の封止部である。そのため、未焼成の封止部では、熱応力を緩和することができ、焼成された封止部では、高温下でもクラックや剥がれが発生しにくく、ＰＭの漏れが発生しにくい。
The honeycomb structure according to claim 1 can be efficiently manufactured by the method for manufacturing a honeycomb structure of the present invention described later.
In the honeycomb structured body according to claim 1, in the honeycomb fired body constituting the honeycomb structured body, the sealing portion on one end face side is a fired sealing portion, and the sealing on the other end face side is performed. The part is an unfired sealing part. Therefore, thermal stress can be relieved in the unsealed sealing portion, and cracks and peeling are unlikely to occur even at high temperatures, and PM leakage is unlikely to occur in the fired sealing portion.
請求項２に記載のハニカム構造体は、請求項１に記載のハニカム構造体において、
上記未焼成の第二の封止部が、加熱処理により固化された封止部である。
このように、未焼成の封止部が固化された封止部である場合、上述した熱応力を緩和する効果を維持しつつ、セルの端部をより確実に封止することができる。
The honeycomb structure according to
The unfired second sealing portion is a sealing portion solidified by heat treatment.
Thus, when the unfired sealing portion is a solidified sealing portion, the end portion of the cell can be more reliably sealed while maintaining the effect of relieving the thermal stress described above.
請求項３に記載のハニカム構造体は、請求項１又は２に記載のハニカム構造体において、
上記第二の封止部が、少なくとも無機粒子と無機バインダとを含む封止材ペーストを用いて形成されている。
このような封止材ペーストは、セル壁との密着性に優れるとともに、必要な強度を備え、未焼成の封止部を形成するのに特に適している。
The honeycomb structure according to claim 3 is the honeycomb structure according to
The second sealing portion is formed using a sealing material paste including at least inorganic particles and an inorganic binder.
Such a sealing material paste is excellent in adhesion to the cell wall, has a required strength, and is particularly suitable for forming an unfired sealing portion.
請求項４に記載のハニカム構造体は、請求項１〜３のいずれかに記載のハニカム構造体において、
上記ハニカムブロックが、複数個のハニカム焼成体が接着材層を介して結束されてなる。
請求項５に記載のハニカム構造体は、請求項４に記載のハニカム構造体において、
上記第二の封止部の組成が、上記接着材層の組成と略同一である。
このように第二の封止部の組成と、接着材層の組成とが略同一であると、構成部材の熱膨張係数の差に起因した内部応力が発生しにくく、より信頼性に優れる。
The honeycomb structure according to claim 4, in the honeycomb structure according to any one of claims 1 to 3,
The honeycomb block is formed by binding a plurality of honeycomb fired bodies through an adhesive layer.
The honeycomb structure according to claim 5, in the honeycomb structure according to claim 4,
The composition of the second sealing portion is substantially the same as the composition of the adhesive layer.
Thus, when the composition of the second sealing portion and the composition of the adhesive layer are substantially the same, internal stress due to the difference in the thermal expansion coefficients of the constituent members is less likely to occur, and the reliability is further improved.
また、請求項６に記載のハニカム構造体は、請求項１〜３のいずれに記載のハニカム構造体において、
上記ハニカムブロックが、１個のハニカム焼成体からなる。
Moreover, the honeycomb structure according to claim 6 is the honeycomb structure according to any one of claims 1 to 3,
The honeycomb block is composed of one honeycomb fired body.
請求項７に記載のハニカム構造体は、請求項１〜６のいずれかに記載のハニカム構造体において、
上記ハニカムブロックの外周部にコート層が形成されている。
請求項７に記載のハニカム構造体では、外周側面からのＰＭの漏れがより発生しにくいため、より信頼性に優れることとなる。また、コート層を形成することにより、ハニカム構造体の外周精度（外周側面の寸法精度）を高めることができる。
The honeycomb structure according to claim 7, in the honeycomb structure according to any one of claims 1 to 6,
A coat layer is formed on the outer periphery of the honeycomb block.
In the honeycomb structure according to the seventh aspect, since PM leakage from the outer peripheral side surface is less likely to occur, the reliability is further improved. Further, by forming the coat layer, it is possible to increase the outer peripheral accuracy (dimensional accuracy of the outer peripheral side surface) of the honeycomb structure.
請求項８に記載のハニカム構造体は、請求項７に記載のハニカム構造体において、
上記第二の封止部の組成が、上記コート層の組成と略同一である。
このように第二の封止部の組成と、コート層の組成とが略同一であると、構成部材の熱膨張係数の差に起因した内部応力が発生しにくく、より信頼性に優れる。
The honeycomb structure according to claim 8 is the honeycomb structure according to claim 7,
The composition of the second sealing portion is substantially the same as the composition of the coat layer.
As described above, when the composition of the second sealing portion and the composition of the coat layer are substantially the same, internal stress due to the difference in thermal expansion coefficients of the constituent members hardly occurs, and the reliability is further improved.
請求項９に記載のハニカム構造体は、請求項１〜８のいずれかに記載のハニカム構造体において、
上記第一の封止部の組成が、上記ハニカム焼成体の組成と略同一である。
このように第一の封止部の組成と、ハニカム焼成体の組成とが略同一であると、構成部材の熱膨張係数の差に起因した内部応力が発生しにくく、より信頼性に優れる。特に、１０００℃近くの高温になった場合にも劣化しにくく、強度を保つことができ、信頼性に優れる。
The honeycomb structure according to claim 9 is the honeycomb structure according to any one of claims 1 to 8,
The composition of the first sealing portion is substantially the same as the composition of the honeycomb fired body.
As described above, when the composition of the first sealing portion and the composition of the honeycomb fired body are substantially the same, internal stress due to the difference in the thermal expansion coefficients of the constituent members hardly occurs, and the reliability is further improved. In particular, even when the temperature becomes close to 1000 ° C., it is difficult to deteriorate, can maintain strength, and is excellent in reliability.
また、請求項５、８又は９に記載のハニカム構造体では、封止部の組成が、接着材層、コート層、ハニカム焼成体のいずれかの組成と略同一である。そのため、ハニカム構造体を製造する際に、封止部を形成するための封止材ペーストを別途調製する必要がない。 In the honeycomb structure according to claim 5, 8 or 9, the composition of the sealing portion is substantially the same as any of the composition of the adhesive layer, the coat layer, and the honeycomb fired body. Therefore, when manufacturing a honeycomb structure, it is not necessary to separately prepare a sealing material paste for forming a sealing portion.
請求項１０に記載のハニカム構造体は、請求項１〜９のいずれかに記載のハニカム構造体において、
上記ハニカム焼成体に形成された複数のセルは、上記長手方向に垂直なセルの断面が相対的に大きい大容積セルと相対的に小さい小容積セルとからなり、
上記大容積セルには、上記第一の封止部が形成され、
上記小容積セルには、上記第二の封止部が形成されている。
このようなセルを備えたハニカム構造体は、圧力損失を上昇を抑えつつ、多量のＰＭを捕集するのに適している。
The honeycomb structure according to
The plurality of cells formed in the honeycomb fired body includes a large volume cell and a relatively small small volume cell in which the cross section of the cell perpendicular to the longitudinal direction is relatively large,
In the large-capacity cell, the first sealing portion is formed,
The second sealing portion is formed in the small volume cell.
A honeycomb structure including such cells is suitable for collecting a large amount of PM while suppressing an increase in pressure loss.
請求項１１に記載の排ガス浄化装置は、
請求項１〜１０のいずれかに記載のハニカム構造体が、保持シール材を介して金属容器内に配置された排ガス浄化装置であって、
上記ハニカム構造体が、上記第一の封止部が形成された端面側が排ガス流出側、上記第二の封止部が形成された側が排ガス流入側となるように配置されていることを特徴とする排ガス浄化装置である。
An exhaust gas purifying apparatus according to
The honeycomb structure according to any one of claims 1 to 10, wherein the honeycomb structure is disposed in a metal container via a holding sealing material,
The honeycomb structure is arranged such that an end surface side on which the first sealing portion is formed is an exhaust gas outflow side, and a side on which the second sealing portion is formed is an exhaust gas inflow side. This is an exhaust gas purifying device.
請求項１１に記載の排ガス浄化装置は、ハニカム構造体として、請求項１〜１０のいずれかに記載のハニカム構造体を備えており、第一の封止部（焼成された封止部）が排ガス流出側、第二の封止部（未焼成の封止部）が排ガス流入側に位置しているため、排ガス流入側に生じる高温の排ガスによる熱応力を緩和することができるとともに、再生処理を行った際に、さらに高温になる排ガス流出側での封止部のクラックや、ハニカム焼成体と封止部と剥離を防止することができる。 An exhaust gas purifying apparatus according to an eleventh aspect includes the honeycomb structure according to any one of the first to tenth aspects as a honeycomb structure, and the first sealing portion (fired sealing portion) is provided. Since the exhaust gas outflow side and the second sealing part (unfired sealing part) are located on the exhaust gas inflow side, it is possible to relieve the thermal stress due to the high temperature exhaust gas generated on the exhaust gas inflow side, and to regenerate When this is performed, cracks in the sealing portion on the exhaust gas outflow side, which become higher in temperature, and separation of the honeycomb fired body from the sealing portion can be prevented.
請求項１２に記載のハニカム構造体の製造方法は、
セラミック原料を成形することにより、複数のセルがセル壁を隔てて長手方向に並設された柱状のハニカム成形体を作製する工程と、
上記ハニカム成形体の両端部の所定箇所のセルが封止されるように封止材ペーストを充填する工程と、
このハニカム成形体に焼成処理を施して、第一の封止部が形成されたハニカム焼成体を作製する工程と、
少なくとも１つの上記ハニカム焼成体からなるハニカムブロックを作製する工程とを含み、
さらに、上記第一の封止部が所定箇所に形成されたハニカム焼成体を切断する工程と、
切断された上記ハニカム焼成体の上記第一の封止部が形成された側と反対側の端部の所定箇所のセルに封止材ペーストを充填し、加熱処理を施して上記封止材ペーストを固化して第二の封止部を形成する工程とを含むことを特徴とするハニカム構造体の製造方法である。
A method for manufacturing a honeycomb structured body according to
Forming a columnar honeycomb formed body in which a plurality of cells are arranged in parallel in the longitudinal direction across the cell wall by molding a ceramic raw material;
Filling a plug material paste so that cells at predetermined locations on both ends of the honeycomb molded body are sealed;
The honeycomb formed body is fired to produce a honeycomb fired body having a first sealing portion formed;
Producing a honeycomb block comprising at least one of the above honeycomb fired bodies,
Furthermore, the step of cutting the honeycomb fired body in which the first sealing portion is formed in a predetermined location;
The sealing material paste is filled with a sealing material paste in a predetermined portion of the end of the cut honeycomb honeycomb body opposite to the side where the first sealing portion is formed, and subjected to heat treatment. And a step of forming a second sealing portion by solidifying the structure of the honeycomb structure.
請求項１２に記載のハニカム構造体の製造方法では、請求項１〜１０に記載のハニカム構造体を好適に製造することができる。
また、請求項１２に記載のハニカム構造体の製造方法では、ハニカム成形体に焼成処理を施してハニカム焼成体を作製した後、得られたハニカム焼成体を切断している。
このように、焼成処理後に切断処理を行うことにより、作製する各ハニカム焼成体の長手方向の寸法精度が優れることとなり、各ハニカム焼成体の大きさのバラツキを小さくすることができる。
In the method for manufacturing a honeycomb structure according to
In the method for manufacturing a honeycomb structured body according to
Thus, by performing the cutting process after the firing process, the dimensional accuracy in the longitudinal direction of each honeycomb fired body to be manufactured is excellent, and the variation in the size of each honeycomb fired body can be reduced.
また、請求項１２に記載のハニカム構造体の製造方法は、長手方向の長さが短いハニカム構造体を製造するのに特に適している。
ハニカム構造体の製造方法においては、焼成用治具にハニカム成形体を収納して焼成処理を行うが、同一サイズの焼成用治具を使用する場合、上述したように、ハニカム成形体のサイズが小さくなると生産性が低下していく傾向にある。
これに対して、請求項１２に記載のハニカム構造体の製造方法では、ハニカム成形体に焼成処理を施した後、得られたハニカム焼成体に切断処理を行うことにより、所定の長さのハニカム焼成体を作製している。
そのため、長手方向の長さの短いハニカム構造体を製造する場合であっても、優れた生産性を備えることとなる。
また、例えば、長手方向の長さが、従来の長さの半分の長さのハニカム構造体を製造する場合にも、従来と同様の焼成用治具を用いて焼成を行うことができる。
従って、ハニカム焼成体を切断する際には、２等分することが望ましい。勿論、３つ以上に切断してもよい。また、３つ以上に切断した場合には、両端以外（中央にある）のハニカム焼成体を別のハニカム構造体の製造に使用することができる。
The method for manufacturing a honeycomb structure according to
In the manufacturing method of the honeycomb structure, the honeycomb molded body is accommodated in the firing jig and fired, and when the same size firing jig is used, as described above, the size of the honeycomb molded body is As it becomes smaller, productivity tends to decrease.
On the other hand, in the method for manufacturing a honeycomb structured body according to
Therefore, even when a honeycomb structure having a short length in the longitudinal direction is manufactured, excellent productivity is provided.
Also, for example, when manufacturing a honeycomb structure having a length in the longitudinal direction that is half of the conventional length, firing can be performed using a firing jig similar to the conventional one.
Therefore, when the honeycomb fired body is cut, it is desirable to divide it into two equal parts. Of course, it may be cut into three or more. Moreover, when cut into three or more, the honeycomb fired body other than both ends (in the center) can be used for manufacturing another honeycomb structure.
請求項１３に記載のハニカム構造体の製造方法は、請求項１２に記載のハニカム構造体の製造方法において、
上記第一の封止部が形成されたハニカム焼成体を作製する工程を行った後、上記ハニカム焼成体を切断する工程を行い、
上記第二の封止部を形成する工程を行った後、上記ハニカムブロックを作製する工程を行う。
The method for manufacturing a honeycomb structure according to claim 13, wherein the method for manufacturing the honeycomb structure according to
After performing the step of producing the honeycomb fired body in which the first sealing portion is formed, performing the step of cutting the honeycomb fired body,
After performing the step of forming the second sealing portion, the step of manufacturing the honeycomb block is performed.
請求項１４に記載のハニカム構造体の製造方法は、請求項１２又は１３に記載のハニカム構造体の製造方法において、
上記ハニカムブロックを、１つのハニカム焼成体で作製する。
また、請求項１５に記載のハニカム構造体の製造方法は、請求項１２又は１３に記載のハニカム構造体の製造方法において、
上記ハニカムブロックは、複数個のハニカム焼成体を接着材層を介して結束して作製する。
The method for manufacturing a honeycomb structure according to claim 14, wherein the method for manufacturing a honeycomb structure according to claim 12 or 13,
The honeycomb block is manufactured with one honeycomb fired body.
Moreover, the manufacturing method of the honeycomb structure according to
The honeycomb block is manufactured by binding a plurality of honeycomb fired bodies through an adhesive layer.
請求項１６に記載のハニカム構造体の製造方法は、請求項１２に記載のハニカム構造体の製造方法において、
上記第一の封止部が形成されたハニカム焼成体を作製した後、複数の上記ハニカム焼成体を接着材層を介して結束させて、両端部に上記第一封止部が形成されたハニカムブロックを作製し、
次に、この接着材層を介して結束されたハニカムブロックを切断した後、上記ハニカムブロックの上記第一の封止部が形成された側と反対側の端部に、上記第二の封止部を形成する工程を行う。
請求項１７に記載のハニカム構造体の製造方法は、請求項１５又は１６に記載のハニカム構造体の製造方法において、
上記第二の封止部の組成が、上記接着材層の組成と略同一である。
このように、第二の封止部の組成が、ハニカム構造体の他の構成部材の組成と略同一であると、製造したハニカム構造体において、構成部材の熱膨張係数の差に起因した内部応力が発生しにくくなる。
The method for manufacturing a honeycomb structure according to claim 16, wherein the method for manufacturing the honeycomb structure according to
A honeycomb fired body in which the first sealing portion is formed, and then a plurality of the honeycomb fired bodies are bundled through an adhesive layer to form the first sealing portion at both ends. Make a block,
Next, after cutting the honeycomb block bound through the adhesive layer, the second sealing is provided at the end of the honeycomb block opposite to the side where the first sealing portion is formed. The process of forming a part is performed.
The method for manufacturing a honeycomb structure according to claim 17, wherein the method for manufacturing the honeycomb structure according to claim 15 or 16,
The composition of the second sealing portion is substantially the same as the composition of the adhesive layer.
As described above, when the composition of the second sealing portion is substantially the same as the composition of the other constituent members of the honeycomb structure, in the manufactured honeycomb structure, the internal components caused by the difference in the thermal expansion coefficients of the constituent members Stress is less likely to occur.
請求項１８に記載のハニカム構造体の製造方法は、請求項１２〜１７のいずれかに記載のハニカム構造体の製造方法において、
上記ハニカム焼成体は、複数のセルが、上記長手方向に垂直なセルの断面が相対的に大きい大容積セルと相対的に小さい小容積セルとからなるように形成し、
上記大容積セルには、上記第一の封止部を形成し、
上記小容積セルには、上記第二の封止部を形成する。
請求項１８に記載のハニカム構造体の製造方法では、圧力損失の上昇を抑えつつ、多量のＰＭを捕集するのに適したハニカム構造体を製造することができる。
A method for manufacturing a honeycomb structure according to claim 18, wherein the method for manufacturing a honeycomb structure according to any one of
The honeycomb fired body is formed such that a plurality of cells are composed of a large volume cell having a relatively large cross section of the cell perpendicular to the longitudinal direction and a relatively small volume cell.
In the large-capacity cell, the first sealing portion is formed,
The second sealing portion is formed in the small volume cell.
In the method for manufacturing a honeycomb structure according to claim 18, a honeycomb structure suitable for collecting a large amount of PM can be manufactured while suppressing an increase in pressure loss.
請求項１９に記載のハニカム構造体の製造方法は、請求項１２〜１８のいずれかに記載のハニカム構造体の製造方法において、
上記ハニカムブロックを形成する工程を行った後、さらに、上記ハニカムブロックの外周にコート材ペーストを塗布し、その後、上記コート材ペーストを固化させることによりコート層を形成する工程を行う。
このように、ハニカムブロックの外周にコート層を形成することにより、より信頼性に優れたハニカム構造体を製造することができる。また、コート層を形成することにより、外周精度（外周側面の寸法精度）の高いハニカム構造体を製造することができる。
The method for manufacturing a honeycomb structure according to claim 19, wherein the method for manufacturing a honeycomb structure according to any one of
After the step of forming the honeycomb block, a coating material paste is applied to the outer periphery of the honeycomb block, and then the coating material paste is solidified to form a coating layer.
Thus, by forming the coat layer on the outer periphery of the honeycomb block, it is possible to manufacture a honeycomb structure having higher reliability. In addition, by forming the coat layer, it is possible to manufacture a honeycomb structure having high outer peripheral accuracy (dimensional accuracy of the outer peripheral side surface).
また、請求項２０に記載のハニカム構造体の製造方法は、請求項１９に記載のハニカム構造体の製造方法において、
上記第二の封止部の組成が、上記コート層の組成と略同一である。
このように、第二の封止部の組成が、ハニカム構造体の他の構成部材の組成と略同一であると、製造したハニカム構造体において、構成部材の熱膨張係数の差に起因した内部応力が発生しにくくなる。
Further, the method for manufacturing a honeycomb structure according to
The composition of the second sealing portion is substantially the same as the composition of the coat layer.
As described above, when the composition of the second sealing portion is substantially the same as the composition of the other constituent members of the honeycomb structure, in the manufactured honeycomb structure, the internal components caused by the difference in the thermal expansion coefficients of the constituent members Stress is less likely to occur.
請求項２１に記載のハニカム構造体の製造方法は、請求項１２〜２０のいずれかに記載のハニカム構造体の製造方法において、
上記第二の封止部を形成する封止材ペーストが、少なくとも無機粒子と無機バインダとを含む。
このような組成の封止材ペーストは、セル壁との密着性に優れるとともに、必要な強度を備え、第二の封止部（未焼成の封止部）を形成するのに、特に適している。
The method for manufacturing a honeycomb structure according to
The sealing material paste that forms the second sealing portion includes at least inorganic particles and an inorganic binder.
The sealing material paste having such a composition is excellent in adhesion to the cell wall, has a necessary strength, and is particularly suitable for forming the second sealing portion (unfired sealing portion). Yes.
請求項２２に記載のハニカム構造体の製造方法は、請求項１２〜２１のいずれかに記載のハニカム構造体の製造方法において、
上記第一の封止部の組成が、上記ハニカム焼成体の組成と略同一である。
このように、第一の封止部の組成が、ハニカム構造体の他の構成部材の組成と略同一であると、製造したハニカム構造体において、構成部材の熱膨張係数の差に起因した内部応力が発生しにくくなる。特に、１０００℃近くの高温になった場合にも劣化しにくく、強度を保つことができ、信頼性に優れる。
A method for manufacturing a honeycomb structure according to claim 22, wherein the method for manufacturing a honeycomb structure according to any one of
The composition of the first sealing portion is substantially the same as the composition of the honeycomb fired body.
As described above, when the composition of the first sealing portion is substantially the same as the composition of the other constituent members of the honeycomb structure, in the manufactured honeycomb structure, the internal components caused by the difference in the thermal expansion coefficients of the constituent members Stress is less likely to occur. In particular, even when the temperature becomes close to 1000 ° C., it is difficult to deteriorate, can maintain strength, and is excellent in reliability.
また、請求項１７、２０又は２２に記載のハニカム構造体の製造方法では、封止部の組成が、接着材層、コート層、ハニカム焼成体のいずれかの組成と略同一である。そのため、ハニカム構造体を製造する際に、封止材ペーストを別途調製する必要がなく、接着材ペーストやコート材ペースト、ハニカム成形体を作製するための湿潤混合物を封止材ペーストとして用いることができる。
In the method for manufacturing a honeycomb structured body according to
以下、本発明の実施形態について説明する。
（第一実施形態）
まず、本実施形態におけるハニカム構造体の製造方法について工程順に説明する。
図１（ａ）〜図１（ｈ）は、第一実施形態の製造工程を説明するための説明図である。
（１）セラミック原料として平均粒子径の異なる炭化ケイ素粉末と有機バインダと可塑剤と潤滑剤と水とを混合して湿潤混合物を調製する。
Hereinafter, embodiments of the present invention will be described.
(First embodiment)
First, the manufacturing method of the honeycomb structure in the present embodiment will be described in the order of steps.
Fig.1 (a)-FIG.1 (h) are explanatory drawings for demonstrating the manufacturing process of 1st embodiment.
(1) A wet mixture is prepared by mixing silicon carbide powder having a different average particle size, an organic binder, a plasticizer, a lubricant and water as ceramic raw materials.
（２）上記湿潤混合物を押出成形機に投入し、上記湿潤混合物を押出成形することにより所定の形状のハニカム成形体１３０を作製する（図１（ａ）参照）。ここでは、各セル１２１が所定の形状となるよう押出成形用金型を選定する。
なお、ここで作製するハニカム成形体１３０は、長手方向の長さが、製造するハニカム構造体の設計値の長手方向の長さの約２倍の長さを有する。このとき、ハニカム成形体の長さは、焼成時の収縮量と、切断される切り代とを考慮して決定する。
さらに、ハニカム成形体を乾燥機を用いて乾燥させる。
(2) The wet mixture is put into an extruder, and the wet mixture is extruded to produce a honeycomb formed
Note that the honeycomb formed
Further, the honeycomb formed body is dried using a dryer.
（３）次に、ハニカム成形体１３０の各セル１２１の所定の端部に、封止材ペースト１２２を所定量充填し、各セル１２１を封止する。セルを封止する際には、ハニカム成形体の端面に封止用のマスクを当てて、封止の必要なセルにのみ封止材ペーストを充填する（図１（ｂ）参照）。
ここで、封止材ペーストは、最終的に出来上がるハニカム構造体において、各端面においてセルが市松模様に封止され、かつ、各セルはいずれか一方の端部のみが封止されるように充填されている。
ここで、封止材ペーストとしては、上記湿潤混合物と略同一の組成（ハニカム成形体と略同一の組成）の組成物を使用する。
ここで、上記封止材ペーストは、上記湿潤混合物と同一の組成であってもよいが、例えば、セルへの充填性を考慮して粘度を調製してもよい。粘度の調整は、有機溶媒や、水等の配合量を変更することにより行えばよい。
(3) Next, a predetermined amount of the sealing
Here, the sealing material paste is filled so that the cells are sealed in a checkered pattern at each end face in the honeycomb structure finally obtained, and each cell is sealed only at one end. Has been.
Here, as the sealing material paste, a composition having substantially the same composition as the wet mixture (substantially the same composition as the honeycomb formed body) is used.
Here, the sealing material paste may have the same composition as the wet mixture, but the viscosity may be adjusted in consideration of, for example, the filling properties into the cells. The adjustment of the viscosity may be performed by changing the blending amount of an organic solvent or water.
（４）各セルの所定の端部が封止されたハニカム成形体１３０を焼成用治具に載置した後、脱脂炉中で加熱し、ハニカム成形体中の有機物を除去する脱脂処理を行う。
続いて、上記脱脂処理を施したハニカム成形体を焼成用治具に載置したまま、焼成炉内に投入し、所定の温度（例えば、２２００〜２３００℃）で焼成処理を行い、ハニカム焼成体１２０を作製する（図１（ｃ）参照）。
なお、本発明において焼成処理を経て形成された封止部２２ｂを第一封止部という。
また、本発明において、「ハニカム成形体」には、押出成形直後の生形成体は勿論のこと、乾燥処理や脱脂処理を施した後の成形体もハニカム成形体に含むこととする。
(4) After placing the honeycomb formed
Subsequently, the honeycomb formed body that has been subjected to the degreasing treatment is placed in a firing furnace while being placed on a firing jig, and fired at a predetermined temperature (for example, 2200 to 2300 ° C.) to obtain a honeycomb fired body. 120 is manufactured (see FIG. 1C).
In the present invention, the sealing
In the present invention, the “honeycomb formed body” includes not only a green formed body immediately after extrusion molding but also a formed body after drying treatment and degreasing treatment.
（５）次に、上記（４）の工程で作製したハニカム焼成体１２０を長手方向に２等分に切断し、ハニカム焼成体２０とする（図１（ｄ）参照）。
上記ハニカム焼成体の切断は、ダイヤモンドカッター、外周型ダイヤモンド砥石、内周型ダイヤモンド砥石、マルチワイヤ、マルチブレード等を用いて行う。
このような切断処理を行うことにより、長手方向の長さが製造するハニカム構造体の設計値と同一のハニカム焼成体２０を作製することができる。
また、切断して得たハニカム焼成体２０は、一方の端面側の所定のセルのみ封止されていることとなる。
(5) Next, the honeycomb fired
The honeycomb fired body is cut using a diamond cutter, an outer peripheral diamond grindstone, an inner peripheral diamond grindstone, a multi-wire, a multi-blade or the like.
By performing such a cutting process, a honeycomb fired
In addition, the honeycomb fired
（６）次に、上記（５）の工程で作製したハニカム焼成体について、各セルのいずれか一方の端部が封止されるように、ハニカム焼成体の未だ封止されていない側の端部の所定のセルに封止材ペーストを充填する。
なお、ここで充填する封止材ペーストは、例えば、無機バインダと有機バインダと無機粒子とからなるものを使用する。この封止材ペーストはさらに無機繊維及び／又はウィスカを含んでいてもよい。
そして、この工程で充填した封止材ペーストを加熱して固化させることにより未焼成の封止部（固化された封止部）２２ａとする（図１（ｅ）参照）。なお、本発明において未焼成（固化された）の封止部を第二封止部という。
なお、上記（３）の工程で充填した封止材ペーストは、上記（４）の工程の焼成処理を経ることにより焼成された封止部２２ｂとなる。
(6) Next, for the honeycomb fired body manufactured in the step (5), the end of the honeycomb fired body that has not been sealed so that either one end of each cell is sealed A predetermined paste cell is filled with a sealing material paste.
In addition, the sealing material paste filled here uses what consists of an inorganic binder, an organic binder, and an inorganic particle, for example. This sealing material paste may further contain inorganic fibers and / or whiskers.
Then, the sealing material paste filled in this step is heated and solidified to form an unfired sealing portion (solidified sealing portion) 22a (see FIG. 1E). In the present invention, an unfired (solidified) sealing portion is referred to as a second sealing portion.
The sealing material paste filled in the step (3) becomes the fired sealing
（７）次に、各セルの所定の端部が封止された上記ハニカム焼成体２０の側面に、接着材層となる接着材ペーストを塗布して接着材ペースト層を形成し、この接着材ペースト層の上に、順次他のハニカム焼成体を積層する工程を繰り返して所定数のハニカム焼成体２０が結束されたハニカム焼成体の集合体１１０を作製する。この際、複数のハニカム焼成体は、第一封止部同士が同一の端面側に位置するように（第二封止部同士がもう一方の端面側に位置するように）積層する。
ここで、接着材ペーストとしては、上記（６）の工程で充填した封止材ペーストと略同一の組成を有するものを使用する。
続いて、上記ハニカム焼成体の集合体１１０を加熱して接着材ペースト層を固化させて接着材層１１とする（図１（ｆ）、図１（ｇ）参照）。
なお、図１（ｇ）は、図１（ｆ）のＡ−Ａ線断面における部分拡大断面図である。
(7) Next, an adhesive paste layer serving as an adhesive layer is applied to the side surface of the honeycomb fired
Here, as the adhesive paste, a paste having substantially the same composition as the sealing material paste filled in the step (6) is used.
Subsequently, the
In addition, FIG.1 (g) is the fragmentary expanded sectional view in the AA sectional view of FIG.1 (f).
（８）その後、ダイヤモンドカッターを用いてハニカム焼成体の集合体１１０に、図１（ｆ）中の破線に沿って切削加工を施してハニカムブロックとし、ハニカムブロックの外周面にコート材ペーストを塗布し、コート材ペーストを固化させてコート層１２を形成することによりハニカム構造体１０とする（図１（ｈ）参照）。
ここで、コート材ペーストとしては、例えば、上記接着材ペーストと略同一の組成をペースト状組成物を使用する。
(8) Thereafter, the honeycomb fired
Here, as the coating material paste, for example, a paste-like composition having substantially the same composition as the adhesive paste is used.
次に、このような製造方法を経て製造されるハニカム構造体について、図面を参照しながら説明する。
図２は、第一実施形態のハニカム構造体の一例を模式的に示す斜視図であり、図３（ａ）は、第一実施形態のハニカム構造体を構成するハニカム焼成体の一例を模式的に示す斜視図であり、図３（ｂ）は、図３（ａ）のＢ−Ｂ線断面図である。
Next, a honeycomb structure manufactured through such a manufacturing method will be described with reference to the drawings.
FIG. 2 is a perspective view schematically showing an example of the honeycomb structure of the first embodiment, and FIG. 3A is a schematic example of the honeycomb fired body constituting the honeycomb structure of the first embodiment. FIG. 3B is a cross-sectional view taken along line BB in FIG.
本実施形態のハニカム構造体１０は、図２に示すようにハニカム焼成体２０が接着材層１１を介して複数個結束されてハニカムブロック１５を構成し、さらに、このハニカムブロック１５の外周にコート層１２が形成されている。
また、ハニカム焼成体２０は、図３（ａ）及び図３（ｂ）に示すように、長手方向（図３（ａ）中、矢印ａの方向）に多数のセル２１が並設され、セル２１同士を隔てるセル壁２３がフィルタとして機能するようになっている。
In the
Further, as shown in FIGS. 3A and 3B, the honeycomb fired
即ち、ハニカム焼成体２０に形成されたセル２１は、図３（ｂ）に示すように、排ガスの入口側の端部が封止材ペーストを用いて形成された封止部２２ａで封止されるか、又は、排ガスの出口側の端部が封止材ペーストを用いて形成された封止部２２ｂで封止され、排ガスの出口側の端部が封止されたセル２１に流入した排ガスは、必ずセル２１を隔てるセル壁２３を通過した後、ガスの入口側の端部が封止されたセル２１から流出するようになっており、排ガスがこのセル壁２３を通過する際、ＰＭがセル壁２３部分で捕捉され、排ガスが浄化される。
ここで、排ガスの出口側の端部を封止する封止部２２ｂは、封止材ペーストに焼成処理を施して形成した焼成された封止部（第一封止部）である。一方、排ガスの入口側の端部を封止する封止部２２ａは、焼成処理を施すことなく、封止材ペーストを固化させて形成した未焼成の封止部（第二封止部）である。
また、ハニカム構造体１０では、コート層１２と、封止部２２ａとが、接着材層１１を形成するペーストと略同一のペーストを用いて形成されている。
なお、図３（ｂ）中、矢印は排ガスの流れを示す。
That is, the
Here, the sealing
In the
In addition, in FIG.3 (b), the arrow shows the flow of exhaust gas.
ハニカム構造体１０では、上述したように封止部２２ｂが焼成処理を経て形成された封止部であり、封止部２２ａが焼成処理を経ずに形成された封止部であるため、封止部２２ｂと封止部２２ａとは、硬度（例えば、ビッカーズ硬度、ロックウェル硬度等）、強度（曲げ強度、圧縮強度、破壊強度等）、ヤング率、弾性率、熱伝導率等の機械的特性が異なることとなる。
本発明の実施形態では、ハニカム構造体の一方の端部に強度が低く、熱伝導率の小さい封止部を形成し、他方の端部に強度が高く、熱伝導率の大きい封止部を形成していることとなる。そして、ハニカム構造体の強度が低く、熱伝導率の小さい封止部が形成された端部を排ガス浄化装置の入口側、強度が高く、熱伝導率の大きい封止部が形成された端部を排ガス浄化装置の出口側に配置することが望ましい。
In the
In the embodiment of the present invention, a sealing portion having low strength and low thermal conductivity is formed at one end of the honeycomb structure, and a sealing portion having high strength and high thermal conductivity is formed at the other end. It will be formed. Then, the end portion where the honeycomb structure has a low strength and a sealing portion having a small thermal conductivity is formed on the inlet side of the exhaust gas purification apparatus, and the end portion where the sealing portion having a high strength and a high thermal conductivity is formed. Is preferably disposed on the outlet side of the exhaust gas purification device.
なお、本明細書において、焼成とは、成形体中の不安定成分（水分、バインダ等）を分解、除去し、各成分間の反応（再結晶を含む）を進行させて安定な化合物を形成することをいい、強度が一段と向上する。一方、固化とは、組成物中の各成分間での反応は起こさず、組成物中の水分等を除去することにより、物理的作用によって組成物の状態が変化し接着特性を発現させる（組成物の硬さを向上させる）ことをいう。 In this specification, firing means decomposing and removing unstable components (moisture, binder, etc.) in the molded product, and forming a stable compound by advancing reactions (including recrystallization) between the components The strength is further improved. On the other hand, solidification means that the reaction between each component in the composition does not occur, and by removing moisture and the like in the composition, the state of the composition is changed due to physical action to develop adhesive properties (composition To improve the hardness of an object).
次に、このようなハニカム構造体を用いた排ガス浄化装置について、図面を参照しながら説明する。
図４は、ハニカム構造体が設置された本実施形態の排ガス浄化装置の一例を模式的に示した断面図である。
Next, an exhaust gas purification apparatus using such a honeycomb structure will be described with reference to the drawings.
FIG. 4 is a cross-sectional view schematically showing an example of the exhaust gas purification apparatus of the present embodiment in which a honeycomb structure is installed.
図４に示したように、排ガス浄化装置４０は、主に、ハニカム構造体１０、ハニカム構造体１０の外方を覆うケーシング（金属容器）４１、ハニカム構造体１０とケーシング４１との間に配置されるアルミナ製の保持シール材４２から構成されており、ケーシング４１の排ガスが導入される側の端部には、エンジン等の内燃機関に連結された導入管４３が接続されており、ケーシング４１の他端部には、外部に連結された排出管４４が接続されている。
ここで、ハニカム構造体１０は、封止部２２ａ（未焼成の封止部）が形成された側が排ガス流入側となり、封止部２２ｂ（焼成された封止部）が形成された側が排ガス流出側となるように、ケーシング４１内に配置されている。従って、排ガス浄化装置４０では、機械的特性の大きい封止部２２ｂが排ガス流出側に位置することとなる。
なお、図４中、矢印は排ガスの流れを示している。
As shown in FIG. 4, the exhaust
Here, in the
In FIG. 4, arrows indicate the flow of exhaust gas.
このような構成からなる排ガス浄化装置４０では、エンジン等の内燃機関から排出された排ガスは、導入管４３を通ってケーシング４１内に導入され、入口側が開口したセルからハニカム構造体１０の内部に流入し、セル壁を通過し、このセル壁でＰＭが捕集されて浄化された後、出口側が開口したセルからハニカム構造体外に排出され、排出管４４を通って外部へ排出されることとなる。
In the exhaust
また、排ガス浄化装置４０では、ハニカム構造体１０のセル壁に大量のＰＭが堆積し、圧力損失が高くなると、ハニカム構造体１０の再生処理が行われる。
上記再生処理では、図示しない加熱手段を用いて加熱されたガスをハニカム構造体のセルの内部へ流入させることで、ハニカム構造体１０を加熱し、セル壁に堆積したＰＭを燃焼除去する。また、ポストインジェクション方式を用いてＰＭを燃焼除去してもよい。
特に、ハニカム構造体の排ガス流出側は、排ガス流入側に比べてＰＭの堆積量が多くなる傾向にあり、ＰＭを燃焼除去した場合に、ハニカム構造体の排ガス流出側は、排ガス流入側に比べて高温になりやすい傾向にある。よって、本実施形態では、より高温になりやすい排ガス流出側を機械的特性が大きい封止部とし、排ガス流入側を機械的特性が小さい封止部としている。
Further, in the exhaust
In the regeneration process, the
In particular, the exhaust gas outflow side of the honeycomb structure tends to have a larger amount of accumulated PM than the exhaust gas inflow side, and when the PM is burned and removed, the exhaust gas outflow side of the honeycomb structure is larger than the exhaust gas inflow side. Tend to be hot. Therefore, in this embodiment, the exhaust gas outflow side, which is likely to become higher in temperature, is a sealing portion having a large mechanical characteristic, and the exhaust gas inflow side is a sealing portion having a small mechanical characteristic.
以下、第一実施形態の作用効果について説明する。
（１）本実施形態では、ハニカム構造体を製造する際に、ハニカム成形体に焼成処理を施してハニカム焼成体を作製した後、得られたハニカム焼成体を切断している。
このように、焼成処理後に切断処理を行うことにより、作製する各ハニカム焼成体の長手方向の寸法精度が優れることとなり、各ハニカム焼成体の大きさのバラツキを小さくすることができる。従って、本実施形態は、特に研磨処理を行うことなく、端面の凹凸の少ないハニカム構造体を製造するのに適している。
具体的には、設計値よりも大きな寸法で焼成体を作製しておき、両端面側から設計値の寸法で切断を行い、２つのハニカム焼成体を作製する。このとき、中央部は切断でなくなるようにしてもよいし、切り代として破棄してもよい。また、中央部のハニカム焼成体を破棄しない場合、これを他のハニカム構造体の作製に使用することもできる。
また、本実施形態では、作製した焼成体を設計値の寸法で切断するため、ハニカム焼成体の端面研磨を行う必要がなく、ハニカム焼成体のセル壁の気孔に研磨粉が残存することもないため、端面研磨工程にともなう洗浄工程も行う必要がない。
Hereinafter, the effect of the first embodiment will be described.
(1) In the present embodiment, when the honeycomb structure is manufactured, the honeycomb formed body is fired to produce a honeycomb fired body, and then the obtained honeycomb fired body is cut.
Thus, by performing the cutting process after the firing process, the dimensional accuracy in the longitudinal direction of each honeycomb fired body to be manufactured is excellent, and the variation in the size of each honeycomb fired body can be reduced. Therefore, the present embodiment is suitable for manufacturing a honeycomb structure with less unevenness on the end face without performing a polishing process.
Specifically, a fired body having a size larger than the design value is prepared, and cutting is performed from the both end surface sides with the design value, thereby producing two honeycomb fired bodies. At this time, the central portion may not be cut or may be discarded as a cutting allowance. Further, when the honeycomb fired body at the central portion is not discarded, it can be used for manufacturing another honeycomb structure.
Further, in the present embodiment, since the manufactured fired body is cut at a design value dimension, it is not necessary to polish the end face of the honeycomb fired body, and no abrasive powder remains in the pores of the cell wall of the honeycomb fired body. Therefore, it is not necessary to perform a cleaning process accompanying the end face polishing process.
また、ハニカム焼成体を作製した後、得られたハニカム焼成体を切断しているため、１つのハニカム成形体から２つのハニカム焼成体を作製することとなり、ハニカム焼成体を効率良く作製することができる。その結果、ハニカム構造体の生産効率が向上し、単位時間あたりのハニカム構造体の生産個数を増やすことができるので、製造コストを低減させることにつながる。 Further, since the obtained honeycomb fired body is cut after the honeycomb fired body is produced, two honeycomb fired bodies are produced from one honeycomb molded body, and the honeycomb fired body can be efficiently produced. it can. As a result, the production efficiency of the honeycomb structure is improved and the number of honeycomb structures produced per unit time can be increased, leading to a reduction in manufacturing cost.
（２）本実施形態では、セルの端部を封止する封止部について、封止材ペーストを充填した後、焼成処理を施すか、又は、加熱により固化させているため、各セルの所定の端部が確実に封止されることとなる。 (2) In the present embodiment, the sealing portion for sealing the end portion of the cell is filled with the sealing material paste and then subjected to a baking treatment or solidified by heating. The end portion of this is surely sealed.
（３）本実施形態では、ハニカム構造体の外周にコート層が形成されているため、ハニカム構造体を用いて、排ガスを浄化した際に、ハニカム構造体の外周側面からＰＭが漏れることがなく、信頼性に優れることとなる。また、コート層を形成することにより、ハニカム構造体の外周側面の寸法精度が向上する。 (3) In this embodiment, since the coat layer is formed on the outer periphery of the honeycomb structure, when exhaust gas is purified using the honeycomb structure, PM does not leak from the outer peripheral side surface of the honeycomb structure. It will be excellent in reliability. In addition, by forming the coat layer, the dimensional accuracy of the outer peripheral side surface of the honeycomb structure is improved.
（４）本実施形態では、ハニカム構造体を構成する未焼成の封止部と、接着材層及びコート層とが略同一の材料を用いて形成されているため、ハニカム構造体において構成部材の熱膨張係数の差に起因した内部応力が発生しにくく、より信頼性に優れることとなる。
また、ハニカム構造体を構成する焼成された封止部は、ハニカム焼成体と略同一の組成で形成されているため、再生処理時に熱衝撃があっても、セル壁と封止部との間でクラック、剥がれ等が発生しにくく、信頼性に優れ、ススの漏れを確実に防止することができる。
(4) In the present embodiment, since the unfired sealing portion constituting the honeycomb structure, the adhesive layer, and the coat layer are formed using substantially the same material, Internal stress due to the difference in thermal expansion coefficient is unlikely to occur and the reliability is further improved.
In addition, since the fired sealing portion constituting the honeycomb structure is formed with substantially the same composition as the honeycomb fired body, even if there is a thermal shock during the regeneration process, the space between the cell wall and the sealing portion is Therefore, cracks, peeling, etc. are hardly generated, the reliability is excellent, and soot leakage can be surely prevented.
（５）本実施形態の排ガス浄化装置では、焼成処理を経て形成された封止部（第一封止部）が排ガス流出側に位置し、焼成処理を経ずに形成された封止部（第二封止部）が排ガス流入側に位置しているため、上記（４）に記載した効果が最も効果的に現れ、排ガス流入側で、排ガスの温度による内部応力が緩和されやすく、排ガス流出側では、ＰＭの堆積量が多くなり、再生処理を行った際に高温になりやすい傾向にあるが、焼成された封止部のためセル壁との間にクラックが発生しにくく、ＰＭを確実に捕集することができる。 (5) In the exhaust gas purification apparatus of this embodiment, the sealing part (first sealing part) formed through the firing process is located on the exhaust gas outflow side, and the sealing part (without the firing process) ( Since the second sealing part) is located on the exhaust gas inflow side, the effect described in (4) above is most effective, and on the exhaust gas inflow side, internal stress due to the temperature of the exhaust gas is easily relaxed, and the exhaust gas outflow On the side, the accumulated amount of PM tends to increase, and it tends to become high temperature when the regeneration process is performed. Can be collected.
以下、本発明の第一実施形態をより具体的に開示した実施例を示す。なお、本発明はこの実施例のみに限定されるものではない。
（実施例１）
（１）平均粒子径２２μｍを有する炭化ケイ素の粗粉末５２．８重量％と、平均粒子径０．５μｍの炭化ケイ素の微粉末２２．６重量％とを混合し、得られた混合物に対して、アクリル樹脂２．１重量％、有機バインダ（メチルセルロース）４．６重量％、潤滑剤（日油社（日本油脂社）製 ユニルーブ）２．８重量％、グリセリン１．３重量％、及び、水１３．８重量％を加えて混練して湿潤混合物を得た後、押出成形する押出成形工程を行い、図３（ａ）に示した形状と略同様の形状であって、セルの封止をしていない生のハニカム成形体を作製した。
Examples that more specifically disclose the first embodiment of the present invention will be described below. In addition, this invention is not limited only to this Example.
Example 1
(1) 52.8% by weight of silicon carbide coarse powder having an average particle size of 22 μm and 22.6% by weight of fine powder of silicon carbide having an average particle size of 0.5 μm are mixed, and the resulting mixture is mixed. 2.1% by weight of acrylic resin, 4.6% by weight of organic binder (methyl cellulose), 2.8% by weight of lubricant (Unilube manufactured by NOF Corporation (Nippon Oil & Fats Co., Ltd.)), 1.3% by weight of glycerin, and water After 13.8% by weight is added and kneaded to obtain a wet mixture, an extrusion molding step is performed to perform extrusion molding. The shape is substantially the same as the shape shown in FIG. A raw honeycomb formed body was prepared.
（２）次いで、マイクロ波乾燥機を用いて上記生のハニカム成形体を乾燥させ、ハニカム成形体の乾燥体を作製した。その後、上記ハニカム成形体の乾燥体の所定のセルに上記湿潤混合物と同一の組成のペーストに充填した。具体的には、各セルにおいて、いずれか一方の端部が封止されるように、上記湿潤混合物と同一の組成のペーストを封止材ペーストとして充填した。その後、再び乾燥機を用いて乾燥させた。 (2) Next, the raw honeycomb formed body was dried using a microwave dryer to prepare a dried honeycomb formed body. Thereafter, a predetermined cell of the dried honeycomb molded body was filled with a paste having the same composition as the wet mixture. Specifically, in each cell, a paste having the same composition as that of the wet mixture was filled as a sealing material paste so that either one end was sealed. Then, it dried again using the dryer.
（３）次に、ハニカム成形体の乾燥体を焼成用治具に載置した後、４００℃で脱脂処理を行い、さらに、常圧のアルゴン雰囲気下２２００℃、３時間の条件で焼成処理を行うことにより、気孔率が４５％、平均気孔径が１５μｍ、大きさが３４．３ｍｍ×３４．３ｍｍ×３００．５ｍｍ、セルの数（セル密度）が３００個／ｉｎｃｈ２、セル壁の厚さが０．２５ｍｍ（１０ｍｉｌ）の炭化ケイ素焼結体からなるハニカム焼成体を製造した。 (3) Next, after placing the dried honeycomb molded body on a firing jig, degreasing treatment is performed at 400 ° C., and further, firing treatment is performed under conditions of 2200 ° C. and 3 hours in an argon atmosphere at normal pressure. By performing, the porosity is 45%, the average pore diameter is 15 μm, the size is 34.3 mm × 34.3 mm × 300.5 mm, the number of cells (cell density) is 300 cells / inch 2 , and the cell wall thickness Produced a honeycomb fired body made of a silicon carbide sintered body having a thickness of 0.25 mm (10 mil).
（４）次に、上記ハニカム焼成体を板厚０．５ｍｍの外周型ダイヤモンド砥石を用いて２等分し、所定のセルの一方の端面側のみ封止された大きさが３４．３ｍｍ×３４．３ｍｍ×１５０ｍｍのハニカム焼成体を作製した。 (4) Next, the honeycomb fired body is divided into two equal parts using a peripheral diamond grindstone having a plate thickness of 0.5 mm, and the size of only one end face side of a predetermined cell is 34.3 mm × 34. A honeycomb fired body of 3 mm × 150 mm was produced.
（５）上記（４）の工程で得たハニカム焼成体について、各セルのいずれか一方の端部が封止されるように、未だ封止されていないセルの端部に封止材ペーストを充填した。
ここで、封止材ペーストとしては、平均粒径０．６μｍの炭化ケイ素粒子３０．０重量％、シリカゾル２１．４重量％、カルボキシメチルセルロース８．０重量％、及び、水４０．６重量％からなる封止材ペーストを使用した。
その後、この工程で充填した封止材ペーストを１８０℃の熱風を用いた加熱を１５分間行うことにより固化させて封止部とした。
(5) With respect to the honeycomb fired body obtained in the step (4), a sealing material paste is applied to the end portions of the cells that have not been sealed so that any one end portion of each cell is sealed. Filled.
Here, as the sealing material paste, from 30.0% by weight of silicon carbide particles having an average particle diameter of 0.6 μm, 21.4% by weight of silica sol, 8.0% by weight of carboxymethylcellulose, and 40.6% by weight of water. An encapsulant paste was used.
Then, the sealing material paste filled in this step was solidified by heating with hot air at 180 ° C. for 15 minutes to obtain a sealing portion.
（６）次に、上記（１）〜（５）の工程を経て作製したハニカム焼成体の側面に接着材ペーストを塗布し、この接着材ペーストを介して上記ハニカム焼成体１６個を接着させ、さらに、１８０℃で２０分間の加熱で接着材ペーストを固化させることにより、四角柱状のハニカム焼成体の集合体を作製した。続いて、ダイヤモンドカッターを用いて、ハニカム焼成体の集合体の外周を切断することにより、接着材層の厚さ１ｍｍの円柱状のハニカムブロックを作製した。
ここで、接着材ペーストとしては、上記（５）の工程で使用した封止材ペーストと同一の組成のペーストを使用した。
(6) Next, an adhesive paste is applied to the side surface of the honeycomb fired body manufactured through the above steps (1) to (5), and the 16 honeycomb fired bodies are bonded via the adhesive paste, Further, the adhesive paste was solidified by heating at 180 ° C. for 20 minutes to produce a quadrangular prism honeycomb fired body aggregate. Subsequently, a cylindrical honeycomb block having an adhesive layer thickness of 1 mm was manufactured by cutting the outer periphery of the aggregate of honeycomb fired bodies using a diamond cutter.
Here, a paste having the same composition as the sealing material paste used in the step (5) was used as the adhesive paste.
（７）次に、ハニカムブロックの外周部にコート材ペーストを塗布し、コート材ペースト層を形成した。そして、このコート材ペースト層を１２０℃で固化して、外周にコート層が形成された直径１４３．８ｍｍ×長さ１５０ｍｍの円柱状のハニカム構造体を製造した。
ここで、コート材ペーストとしては、上記（５）の工程で使用した封止材ペーストと同一の組成のペーストを使用した。
(7) Next, a coating material paste was applied to the outer peripheral portion of the honeycomb block to form a coating material paste layer. Then, this coating material paste layer was solidified at 120 ° C. to produce a cylindrical honeycomb structure having a diameter of 143.8 mm and a length of 150 mm, on which the coating layer was formed on the outer periphery.
Here, as the coating material paste, a paste having the same composition as that of the sealing material paste used in the step (5) was used.
（比較例１）
（１）押出形成工程を経て作製する生のハニカム成形体の長手方向の長さを、焼成後に１５０ｍｍになる寸法とした以外は、実施例１の（１）の工程と同様にして、図３（ａ）に示した形状と略同様の形状であって、セルの封止をしていない生のハニカム成形体を作製した。
(Comparative Example 1)
(1) Except that the length in the longitudinal direction of the raw honeycomb formed body produced through the extrusion forming step is set to a dimension that becomes 150 mm after firing, in the same manner as in the step (1) of Example 1, FIG. A raw honeycomb molded body having substantially the same shape as that shown in (a) and without cell sealing was produced.
（２）次に、マイクロ波乾燥機を用いて上記生のハニカム成形体を乾燥させ、ハニカム成形体の乾燥体を作製した。その後、各セルのいずれか一方の端部が封止されるように、所定のセルの端部に封止材ペーストを充填した。
ここで、封止材ペーストとしては、上記湿潤混合物と同一の組成の組成物を使用した。
(2) Next, the raw honeycomb molded body was dried using a microwave dryer to prepare a dried honeycomb molded body. Thereafter, the end portion of a predetermined cell was filled with a sealing material paste so that either one end portion of each cell was sealed.
Here, as the sealing material paste, a composition having the same composition as that of the wet mixture was used.
（３） 次に、封止材ペーストを充填したハニカム成形体に、実施例１の（３）の工程と同様の条件で、脱脂処理及び焼成処理を行い、ハニカム焼成体を作製した。
ここで、作製したハニカム焼成体は、気孔率が４５％、平均気孔径が１５μｍ、大きさが３４．３ｍｍ×３４．３ｍｍ×１５０ｍｍ、セルの数（セル密度）が３００個／ｉｎｃｈ２、セル壁の厚さが０．２５ｍｍ（１０ｍｉｌ）の炭化ケイ素焼結体からなるハニカム焼成体である。
(3) Next, the honeycomb molded body filled with the sealing material paste was subjected to a degreasing process and a firing process under the same conditions as in the step (3) of Example 1 to produce a honeycomb fired body.
Here, the manufactured honeycomb fired body has a porosity of 45%, an average pore diameter of 15 μm, a size of 34.3 mm × 34.3 mm × 150 mm, a number of cells (cell density) of 300 / inch 2 , cells This is a honeycomb fired body made of a silicon carbide sintered body having a wall thickness of 0.25 mm (10 mil).
（４）次に、上記（３）の工程で作製したハニカム焼成体を用いて、実施例１の（６）及び（７）の工程と同様の方法を用いることにより、複数個のハニカム焼成体が接着材層を介して結束したハニカム構造体を作製した。 (4) Next, by using the honeycomb fired body manufactured in the above step (3) and using the same method as in the steps (6) and (7) of Example 1, a plurality of honeycomb fired bodies are obtained. Produced a honeycomb structure bound together through an adhesive layer.
（ハニカム構造体の評価）
（１）圧力損失の測定
実施例１及び比較例１のそれぞれで製造したハニカム構造体を用いて、図４に示した排ガス浄化装置４０を組み上げた。そして、排ガス浄化装置４０の導入管４３に２Ｌのコモンレール式ディーゼルエンジンを接続した。さらに、ハニカム構造体の前後に圧力計を取り付けた。
そして、エンジンを回転数１５００ｍｉｎ−１、トルク５０Ｎｍで運転し、運転開始から５分後の差圧を測定した。
(Evaluation of honeycomb structure)
(1) Measurement of pressure loss Using the honeycomb structures manufactured in Example 1 and Comparative Example 1, the exhaust
The engine was operated at a rotational speed of 1500 min −1 and a torque of 50 Nm, and the differential pressure after 5 minutes from the start of operation was measured.
その結果、実施例１のハニカム構造体の圧力損失は、２．３ｋＰａであり、比較例１のハニカム構造体の圧力損失は、２．４ｋＰａであった。
このように、実施例１で作製したハニカム構造体の圧力損失は、比較例１（従来の方法）で作製したハニカム構造体と同程度であった。
As a result, the pressure loss of the honeycomb structure of Example 1 was 2.3 kPa, and the pressure loss of the honeycomb structure of Comparative Example 1 was 2.4 kPa.
Thus, the pressure loss of the honeycomb structure manufactured in Example 1 was almost the same as that of the honeycomb structure manufactured in Comparative Example 1 (conventional method).
（２）再生限界値の測定
実施例１及び比較例１のそれぞれで製造したハニカム構造体を用いて、図４に示した排ガス浄化装置４０を組み上げた。そして、排ガス浄化装置４０の導入管４３に２Ｌのコモンレール式ディーゼルエンジンを接続した。
そして、エンジンを回転数２０００ｍｉｎ−１、トルク５０Ｎｍで所定時間運転し、その後、再生処理を行う実験を、運転時間を増加させながら継続して行い、ハニカム構造体（特に封止部）にクラックが発生するか否かを観察した。
そして、クラックが発生した際に捕集していたＰＭの量を再生限界値とした。
(2) Measurement of regeneration limit value Using the honeycomb structures manufactured in Example 1 and Comparative Example 1, the exhaust
Then, the engine is operated at a rotational speed of 2000 min −1 and a torque of 50 Nm for a predetermined time, and then an experiment for performing the regeneration process is continuously performed while increasing the operation time. It was observed whether it occurred.
Then, the amount of PM collected when the crack occurred was taken as the regeneration limit value.
その結果、実施例１のハニカム構造体の再生限界値は、７．９ｇ／ｌであり、比較例１のハニカム構造体の再生限界値は、７．７ｇ／ｌであった。
このように、実施例１で作製したハニカム構造体の再生限界値は、比較例１（従来の方法）で作製したハニカム構造体と同程度であった。
As a result, the regeneration limit value of the honeycomb structure of Example 1 was 7.9 g / l, and the regeneration limit value of the honeycomb structure of Comparative Example 1 was 7.7 g / l.
Thus, the regeneration limit value of the honeycomb structure manufactured in Example 1 was almost the same as that of the honeycomb structure manufactured in Comparative Example 1 (conventional method).
（第二実施形態）
本実施形態では、ハニカム構造体の製造方法の工程順序が第一実施形態におけるハニカム構造体の製造方法の工程順序と異なる。
図５（ａ）〜図５（ｆ）は、第二実施形態の製造工程を説明するための説明図である。
（１）本実施形態のハニカム構造体の製造方法では、第一実施形態のハニカム構造体の製造方法の（１）〜（４）の方法と同様の方法を用いて、ハニカム焼成体１２０を作製する（図５（ａ）参照）。
(Second embodiment)
In the present embodiment, the process sequence of the honeycomb structure manufacturing method is different from the process sequence of the honeycomb structure manufacturing method in the first embodiment.
Fig.5 (a)-FIG.5 (f) are explanatory drawings for demonstrating the manufacturing process of 2nd embodiment.
(1) In the honeycomb structure manufacturing method of the present embodiment, the honeycomb fired
（２）次に、作製したハニカム焼成体１２０の側面に、接着材層となる接着材ペーストを塗布して接着材ペースト層を形成し、この接着材ペースト層の上に、順次他のハニカム焼成体を積層する工程を繰り返して所定数のハニカム焼成体１２０が結束されたハニカム焼成体の集合体１１０′を作製する。
ここで、接着材ペーストとしては、下記（４）の工程で使用する封止材ペーストと略同一の組成を有するものを使用する。
また、この工程では、ハニカム焼成体を結束させた後、上記ハニカム焼成体の集合体を加熱することにより、接着材ペースト層を固化させて接着材層１１とする（図５（ｂ）参照）。
(2) Next, an adhesive paste serving as an adhesive layer is applied to the side surface of the manufactured honeycomb fired
Here, as the adhesive paste, a paste having substantially the same composition as the sealing material paste used in the step (4) below is used.
In this step, after the honeycomb fired bodies are bundled, the aggregate of the honeycomb fired bodies is heated to solidify the adhesive paste layer to form the adhesive layer 11 (see FIG. 5B). .
（３）次に、上記（２）の工程で作製したハニカム焼成体の集合体１１０′を長手方向に２等分に切断し、ハニカム焼成体の集合体１１０とする（図５（ｃ）参照）。
上記ハニカム焼成体の切断は、ダイヤモンドカッター、外周型ダイヤモンド砥石、内周型ダイヤモンド砥石、マルチワイヤ、マルチブレード等を用いて行う。
このような切断処理を行うことにより、長手方向の長さが製造するハニカム構造体の設計値の長手方向の長さと同一のハニカム焼成体の集合体１１０を作製することができる。
(3) Next, the honeycomb fired
The honeycomb fired body is cut using a diamond cutter, an outer peripheral diamond grindstone, an inner peripheral diamond grindstone, a multi-wire, a multi-blade or the like.
By performing such a cutting process, a honeycomb fired
（４）次に、上記（３）の工程で切断したハニカム焼成体の集合体１１０について、各セルのいずれか一方の端部が封止されるように、封止する必要のあるセルの端部のうち、未だ封止されていないセルの端部に封止材ペーストを充填する。
その後、充填した封止材ペーストを加熱により固化させて、封止部２２ａとする（図５（ｄ）、図５（ｅ）参照）。
なお、図５（ｅ）は、図５（ｄ）のＣ−Ｃ線断面における部分拡大断面図である。
ここで、封止材ペーストとしては、例えば、無機バインダと有機バインダと無機粒子とからなるものを使用する。この封止材ペーストはさらに無機繊維及び／又はウィスカを含んでいてもよい。
(4) Next, for the honeycomb fired
Thereafter, the filled sealing material paste is solidified by heating to form a sealing
FIG. 5E is a partially enlarged cross-sectional view taken along the line CC of FIG. 5D.
Here, as a sealing material paste, what consists of an inorganic binder, an organic binder, and an inorganic particle is used, for example. This sealing material paste may further contain inorganic fibers and / or whiskers.
（５）その後、ダイヤモンドカッターを用いてハニカム焼成体の集合体１１０に、図５（ｄ）中の破線に沿った切削加工を施してハニカムブロックとし、ハニカムブロックの外周面にコート材ペーストを塗布し、コート材ペーストを加熱により固化させてコート層１２を形成することによりハニカム構造体１０とする（図５（ｆ）参照）。
ここで、コート材ペーストとしては、例えば、上記（４）の工程で使用する封止材ペーストと略同一の組成を有するものを使用する。
(5) Thereafter, the honeycomb fired
Here, as the coating material paste, for example, a coating material paste having substantially the same composition as that of the sealing material paste used in the step (4) is used.
本実施形態では、このような工程を経ることによりハニカム構造体を製造することができる。
また、本実施形態の製造方法により製造されるハニカム構造体の構成は、第一実施形態のハニカム構造体の構成と同様である。また、本実施形態の製造方法により製造されたハニカム構造体を用いた排ガス浄化装置の構成は、第一実施形態の排ガス浄化装置の構成と同様である。
In the present embodiment, a honeycomb structure can be manufactured through such steps.
The configuration of the honeycomb structure manufactured by the manufacturing method of the present embodiment is the same as the configuration of the honeycomb structure of the first embodiment. The configuration of the exhaust gas purification apparatus using the honeycomb structure manufactured by the manufacturing method of the present embodiment is the same as the configuration of the exhaust gas purification apparatus of the first embodiment.
第二実施形態に係るハニカム構造体、排ガス浄化装置、及び、ハニカム構造体の製造方法では、第一実施形態と同様の作用効果を享受することができる。 In the honeycomb structure, the exhaust gas purification device, and the method for manufacturing the honeycomb structure according to the second embodiment, the same operational effects as those of the first embodiment can be obtained.
以下、本発明の第二実施形態をより具体的に開示した実施例を示す。なお、本発明はこの実施例のみに限定されるものではない。
（実施例２）
（１）実施例１の（１）〜（３）の工程と同様にして、気孔率が４５％、平均気孔径が１５μｍ、大きさが３４．３ｍｍ×３４．３ｍｍ×３００．５ｍｍ、セルの数（セル密度）が３００個／ｉｎｃｈ２、セル壁の厚さが０．２５ｍｍ（１０ｍｉｌ）の炭化ケイ素焼結体からなるハニカム焼成体を製造した。
Examples that more specifically disclose the second embodiment of the present invention will be described below. In addition, this invention is not limited only to this Example.
(Example 2)
(1) In the same manner as in the steps (1) to (3) of Example 1, the porosity is 45%, the average pore diameter is 15 μm, the size is 34.3 mm × 34.3 mm × 300.5 mm, A honeycomb fired body made of a silicon carbide sintered body having a number (cell density) of 300 / inch 2 and a cell wall thickness of 0.25 mm (10 mil) was manufactured.
（２）次に、上記（１）の工程で作製したハニカム焼成体の側面に接着材ペーストを塗布し、この接着材ペーストを介して上記ハニカム焼成体１６個を接着させ、さらに、１８０℃、２０分の加熱処理で接着材ペーストを固化させることにより、四角柱状のハニカム焼成体の集合体を作製した。
その後、上記ハニカム焼成体の集合体を、板厚０．５ｍｍの外周型ダイヤモンド砥石を用いて２等分し、長手方向の長さが１５０ｍｍで所定のセルの一方の端面側のみ封止されたハニカム焼成体の集合体とした。
この工程で、上記接着材ペーストとしては、平均粒径０．６μｍの炭化ケイ素粒子３０．０重量％、シリカゾル２１．４重量％、カルボキシメチルセルロース８．０重量％、及び、水４０．６重量％からなる接着材ペーストを使用した。
(2) Next, an adhesive paste is applied to the side surface of the honeycomb fired body manufactured in the step (1), and the 16 honeycomb fired bodies are bonded through the adhesive paste, and further, 180 ° C., The adhesive paste was solidified by heat treatment for 20 minutes to produce a quadrangular columnar honeycomb fired body aggregate.
Thereafter, the aggregate of the honeycomb fired bodies was divided into two equal parts using a peripheral diamond grindstone having a plate thickness of 0.5 mm, and the length in the longitudinal direction was 150 mm, and only one end face side of a predetermined cell was sealed. An aggregate of honeycomb fired bodies was obtained.
In this step, the adhesive paste includes 30.0% by weight of silicon carbide particles having an average particle diameter of 0.6 μm, 21.4% by weight of silica sol, 8.0% by weight of carboxymethylcellulose, and 40.6% by weight of water. An adhesive paste consisting of was used.
（３）次に、上記（２）の工程で得たハニカム焼成体の集合体について、各セルのいずれか一方の端部が封止されるように、未だ封止されていないセルの端部に封止材ペーストを充填した。その後、充填した封止材ペーストを１８０℃の熱風を用いた加熱を１５分間行うことにより固化させて封止部とした。
ここで、封止材ペーストとしては、上記（２）の工程で用いた接着材ペーストと同一の組成のペーストを使用した。
(3) Next, for the aggregate of honeycomb fired bodies obtained in the step (2), the end portions of the cells that have not been sealed so that any one end portion of each cell is sealed Was filled with a sealing material paste. Thereafter, the filled sealing material paste was solidified by heating with hot air at 180 ° C. for 15 minutes to obtain a sealing portion.
Here, as the sealing material paste, a paste having the same composition as that of the adhesive paste used in the step (2) was used.
（４）次に、ダイヤモンドカッターを用いて集合体の外周を切断することにより、接着材層の厚さ１ｍｍの円柱状のハニカムブロックを作製した。
その後、ハニカムブロックの外周部にコート材ペーストを塗布し、コート材ペースト層を形成した。そして、このコート材ペースト層を１８０℃で２０分間乾燥して、外周にコート層が形成された直径１４３．８ｍｍ×長さ１５０ｍｍの円柱状のハニカム構造体を製造した。
ここで、コート材ペーストとしては、上記（２）の工程で使用した接着材ペーストと同一の組成のペーストを使用した。
(4) Next, the outer periphery of the aggregate was cut using a diamond cutter to produce a cylindrical honeycomb block with an adhesive layer thickness of 1 mm.
Thereafter, a coating material paste was applied to the outer periphery of the honeycomb block to form a coating material paste layer. Then, this coating material paste layer was dried at 180 ° C. for 20 minutes to produce a cylindrical honeycomb structure having a diameter of 143.8 mm and a length of 150 mm with a coating layer formed on the outer periphery.
Here, a paste having the same composition as the adhesive paste used in the step (2) was used as the coating material paste.
このような実施例２で作製したハニカム構造体では、一方の端面側の封止部は焼成処理を経て形成されており、他方の端面側の封止部は焼成処理を経ずに形成されていることとなる。
また、本実施例で製造したハニカム構造体について、実施例１と同様の方法で、圧力損失、及び、再生限界値を測定したところ、それぞれ、２．３ｋＰａ及び７．９ｇ／ｌであった。
このように、実施例２で作製したハニカム構造体の圧力損失及び再生限界値は、比較例１（従来の方法）で作製したハニカム構造体と同程度であった。
In such a honeycomb structure manufactured in Example 2, the sealing portion on one end face side is formed through a firing process, and the sealing portion on the other end face side is formed without undergoing a firing process. Will be.
Further, the pressure loss and the regeneration limit value of the honeycomb structure manufactured in this example were measured by the same method as in Example 1, and found to be 2.3 kPa and 7.9 g / l, respectively.
Thus, the pressure loss and the regeneration limit value of the honeycomb structure manufactured in Example 2 were approximately the same as those of the honeycomb structure manufactured in Comparative Example 1 (conventional method).
（第三実施形態）
本実施形態では、ハニカム構造体の製造方法の工程順序が第一実施形態におけるハニカム構造体の製造方法の工程順序と異なる。
図６（ａ）〜図６（ｇ）は、第三実施形態の製造工程を説明するための説明図である。
（１）本実施形態のハニカム構造体の製造方法では、第一実施形態のハニカム構造体の製造方法の（１）〜（５）の方法と同様の方法を用いて、長手方向の長さが製造するハニカム構造体の設計値の長手方向の長さと同一のハニカム焼成体２０を作製する（図６（ａ）、図６（ｂ）参照）。
(Third embodiment)
In the present embodiment, the process sequence of the honeycomb structure manufacturing method is different from the process sequence of the honeycomb structure manufacturing method in the first embodiment.
FIG. 6A to FIG. 6G are explanatory diagrams for explaining the manufacturing process of the third embodiment.
(1) In the manufacturing method of the honeycomb structure of the present embodiment, the length in the longitudinal direction is the same as the method of (1) to (5) of the manufacturing method of the honeycomb structure of the first embodiment. A honeycomb fired
（２）次に、上記（１）の工程で作製したハニカム焼成体２０の側面に、接着材ペーストを塗布して接着材ペースト層を形成し、この接着材ペースト層の上に、順次他のハニカム焼成体を積層する工程を繰り返して所定数のハニカム焼成体が結束されたハニカム焼成体の集合体１１０を作製する。
また、この工程では、ハニカム焼成体を結束させた後、上記ハニカム焼成体の集合体を加熱することにより、接着材ペースト層を固化させて接着材層１１とする（図６（ｃ）、図６（ｄ）参照）。
なお、図６（ｄ）は、図６（ｃ）のＤ−Ｄ線断面における部分拡大断面図である。
ここで、接着材ペーストとしては、下記（３）の工程で使用する封止材ペーストと略同一の組成のペーストを使用する。
(2) Next, an adhesive paste is applied to the side surface of the honeycomb fired
In this step, after the honeycomb fired bodies are bundled, the aggregate of the honeycomb fired bodies is heated to solidify the adhesive paste layer to form the adhesive layer 11 (FIG. 6 (c), FIG. 6 (d)).
In addition, FIG.6 (d) is the elements on larger scale in the DD sectional view of FIG.6 (c).
Here, as the adhesive paste, a paste having substantially the same composition as the sealing material paste used in the following step (3) is used.
（３）次に、上記（２）の工程で作製したハニカム焼成体の集合体１１０について、各セル２１のいずれか一方の端部が封止されるように、封止する必要のあるセルの端部のうち、未だ封止されていないセルの端部に封止材ペーストを充填する。
その後、充填した封止材ペーストを加熱により固化させ、封止部２２ａとする（図６（ｅ）、図６（ｆ）参照）。
なお、図６（ｆ）は、図６（ｅ）のＥ−Ｅ線断面における部分拡大断面図である。
ここで、封止材ペーストとしては、例えば、無機バインダと有機バインダと無機粒子とからなるものを使用する。この封止材ペーストは、さらに無機繊維及び／又はウィスカを含んでいてもよい。
(3) Next, for the honeycomb fired
Thereafter, the filled sealing material paste is solidified by heating to form a sealing
In addition, FIG.6 (f) is the fragmentary expanded sectional view in the EE sectional view of FIG.6 (e).
Here, as a sealing material paste, what consists of an inorganic binder, an organic binder, and an inorganic particle is used, for example. This sealing material paste may further contain inorganic fibers and / or whiskers.
（４）その後、ダイヤモンドカッターを用いてハニカム焼成体の集合体１１０に、図６（ｅ）中の破線に沿った切削加工を施してハニカムブロックとし、ハニカムブロックの外周面にコート材ペーストを塗布し、コート材ペーストを加熱処理により固化させてコート層１２を形成することによりハニカム構造体１０とする（図６（ｇ）参照）。
ここで、コート材ペーストとしては、例えば、上記（３）の工程で充填した封止材ペーストと略同一の組成を有するものを使用する。
(4) Thereafter, the honeycomb fired
Here, as the coating material paste, for example, a coating material paste having substantially the same composition as the sealing material paste filled in the step (3) is used.
本実施形態では、このような工程を経ることによりハニカム構造体を製造することができる。
また、本実施形態の製造方法により製造されるハニカム構造体の構成は、第一実施形態のハニカム構造体の構成と同様である。また、本実施形態の製造方法により製造されたハニカム構造体を用いた排ガス浄化装置の構成は、第一実施形態の排ガス浄化装置の構成と同様である。
In the present embodiment, a honeycomb structure can be manufactured through such steps.
The configuration of the honeycomb structure manufactured by the manufacturing method of the present embodiment is the same as the configuration of the honeycomb structure of the first embodiment. The configuration of the exhaust gas purification apparatus using the honeycomb structure manufactured by the manufacturing method of the present embodiment is the same as the configuration of the exhaust gas purification apparatus of the first embodiment.
第三実施形態に係るハニカム構造体、排ガス浄化装置、及び、ハニカム構造体の製造方法では、第一実施形態と同様の作用効果を享受することができる。 In the honeycomb structure, the exhaust gas purification device, and the method for manufacturing the honeycomb structure according to the third embodiment, the same functions and effects as those of the first embodiment can be enjoyed.
以下、本発明の第三実施形態をより具体的に開示した実施例を示す。なお、本発明はこの実施例のみに限定されるものではない。
（実施例３）
（１）まず、実施例１の（１）〜（５）の工程と同様にして、所定のセルの一方の端面側のみ封止された大きさが３４．３ｍｍ×３４．３ｍｍ×１５０ｍｍのハニカム焼成体を作製
した。
Hereinafter, examples that more specifically disclose the third embodiment of the present invention will be described. In addition, this invention is not limited only to this Example.
(Example 3)
(1) First, in the same manner as in the steps (1) to (5) of the first embodiment, a honeycomb in which only one end face side of a predetermined cell is sealed is 34.3 mm × 34.3 mm × 150 mm A fired body was produced.
（２）次に、実施例２の（２）の工程と同様にして、上記（１）の工程で作製したハニカム焼成体の側面に接着材ペーストを塗布し、この接着材ペーストを介して上記ハニカム焼成体１６個を接着させ、さらに、１８０℃、２０分間の加熱処理で接着材ペーストを固化させることにより、四角柱状のハニカム焼成体の集合体を作製した。
ここで、接着材ペーストとしては、平均粒径０．６μｍの炭化ケイ素粒子３０．０重量％、シリカゾル２１．４重量％、カルボキシメチルセルロース８．０重量％、及び、水４０．６重量％からなる接着材ペーストを使用した。
(2) Next, in the same manner as in the step (2) of Example 2, an adhesive paste was applied to the side surface of the honeycomb fired body produced in the step (1), and the adhesive paste was passed through the adhesive paste. The 16 honeycomb fired bodies were bonded, and the adhesive paste was solidified by a heat treatment at 180 ° C. for 20 minutes to produce a quadrangular prism-shaped honeycomb fired body aggregate.
Here, the adhesive paste is composed of 30.0% by weight of silicon carbide particles having an average particle diameter of 0.6 μm, 21.4% by weight of silica sol, 8.0% by weight of carboxymethylcellulose, and 40.6% by weight of water. Adhesive paste was used.
（３）次に、実施例２の（３）の工程と同様にして、各セルのいずれか一方の端部が封止されるように封止部を形成した。
ここで、封止部を形成するための封止材ペーストとしては、上記（２）の工程で用いた接着材ペーストと同一の組成のペーストを使用した。
(3) Next, in the same manner as in the step (3) of Example 2, a sealing portion was formed so that either one end of each cell was sealed.
Here, as the sealing material paste for forming the sealing portion, a paste having the same composition as that of the adhesive paste used in the step (2) was used.
（４）次に、実施例２の（４）の工程と同様にして、ハニカム焼成体の集合体の外周加工と、コート層の形成とを行い、外周にコート層が形成された直径１４３．８ｍｍ×長さ１５０ｍｍの円柱状のハニカム構造体を製造した。
ここで、コート層を形成するためのコート材ペーストとしては、上記（２）の工程で使用した接着材ペーストと同一の組成のペーストを使用した。
(4) Next, in the same manner as in the step (4) of Example 2, the outer periphery processing of the aggregate of honeycomb fired bodies and the formation of the coat layer were performed, and the diameter 143. A columnar honeycomb structure of 8 mm × length 150 mm was manufactured.
Here, as the coating material paste for forming the coating layer, a paste having the same composition as the adhesive paste used in the step (2) was used.
このような実施例３で作製したハニカム構造体では、一方の端面側の封止部は焼成処理を経て形成されており、他方の端面側の封止部は焼成処理を経ずに形成されていることとなる。
また、本実施例で製造したハニカム構造体について、実施例１と同様の方法で、圧力損失、及び、再生限界値を測定したところ、それぞれ、２．５ｋＰａ及び７．９ｇ／ｌであった。
このように、実施例３で作製したハニカム構造体の圧力損失及び再生限界値は、比較例１（従来の方法）で作製したハニカム構造体と同程度であった。
In such a honeycomb structure manufactured in Example 3, the sealing portion on one end face side is formed through a firing process, and the sealing portion on the other end face side is formed without undergoing a firing process. Will be.
Moreover, when the pressure loss and the regeneration limit value of the honeycomb structure manufactured in this example were measured by the same method as in Example 1, they were 2.5 kPa and 7.9 g / l, respectively.
As described above, the pressure loss and the regeneration limit value of the honeycomb structure manufactured in Example 3 were almost the same as those of the honeycomb structure manufactured in Comparative Example 1 (conventional method).
ここまで説明した第一〜第三の実施形態は、ハニカム構造体の製造方法が異なるものの、製造されるハニカム構造体、及び、このハニカム構造体を用いた排ガス浄化装置は、同様の構成を備えることとなる。
そして、各実施形態に係るハニカム構造体の製造方法の工程は、図７に示す通りである。
Although the first to third embodiments described so far differ in the manufacturing method of the honeycomb structure, the manufactured honeycomb structure and the exhaust gas purification apparatus using the honeycomb structure have the same configuration. It will be.
And the process of the manufacturing method of the honeycomb structure which concerns on each embodiment is as showing in FIG.
図７は、第一〜第三の実施形態に係るハニカム構造体の製造方法における工程図である。
図７に示すように、第一〜第三の実施形態に係るハニカム構造体の製造方法では、ハニカム焼成体を切断するタイミング、ハニカム焼成体を複数個結束させるタイミング、及び、切断して得たハニカム焼成体のセルに封止材ペーストを充填するタイミングが異なることとなる。
FIG. 7 is a process diagram in the method for manufacturing a honeycomb structure according to the first to third embodiments.
As shown in FIG. 7, in the manufacturing method of the honeycomb structure according to the first to third embodiments, the timing for cutting the honeycomb fired body, the timing for binding a plurality of honeycomb fired bodies, and the cutting were obtained. The timing at which the cells of the honeycomb fired body are filled with the sealing material paste is different.
（第四実施形態）
第一〜第三の実施形態に係るハニカム構造体において、各セルのハニカム焼成体の長手方向に垂直な断面の形状は、全て同一で、かつ、４角形であるが、本発明の実施形態のハニカム構造体において、各セルのハニカム焼成体の長手方向に垂直な断面の形状は、例えば、８角形と４角形であってもよい。
図８（ａ）は、本発明の実施形態のハニカム構造体を構成するハニカム焼成体の別の一例を模式的に示す斜視図であり、図８（ｂ）は、図８（ａ）のＢ−Ｂ線断面図である。
(Fourth embodiment)
In the honeycomb structures according to the first to third embodiments, the shapes of the cross sections perpendicular to the longitudinal direction of the honeycomb fired bodies of the respective cells are all the same and are quadrangular. In the honeycomb structure, the shape of the cross section perpendicular to the longitudinal direction of the honeycomb fired body of each cell may be, for example, an octagon and a quadrangle.
Fig. 8 (a) is a perspective view schematically showing another example of the honeycomb fired body constituting the honeycomb structure of the embodiment of the present invention, and Fig. 8 (b) is a diagram B of Fig. 8 (a). FIG.
図８（ａ）、（ｂ）に示したハニカム焼成体７０は、多数のセル７１ａ、７１ｂがセル壁７３を隔てて長手方向（図８（ａ）中、矢印ｂの方向）に並設されており、セル７１ａ、７１ｂはいずれか一方の端部が封止部により封止されている。具体的には、セル７１ａは、排ガスの流入側の端部が未焼成の封止部（第二の封止部）７２ａで封止されており、セル７１ｂは、排ガスの流出側の端部が焼成された封止部（第一の封止部）により封止されている。
ここで、セル７１ａの上記長手方向に垂直な断面の形状は４角形であり、セル７１ｂの上記長手方向に垂直な断面の形状は８角形である。
In the honeycomb fired
Here, the shape of the cross section perpendicular to the longitudinal direction of the
従って、ハニカム焼成体７０に形成された複数のセルは、上記長手方向に垂直なセルの断面が相対的に大きい大容積セルと相対的に小さい小容積セルとからなり、上記大容積セルには、上記第一の封止部が形成され、上記小容積セルには、上記第二の封止部が形成されていることとなる。
Therefore, the plurality of cells formed in the honeycomb fired
ハニカム焼成体７０においても、セル７１ｂに流入した排ガスは、必ずセル壁７３を通過した後、セル７１ａから流出するようになっている。
従って、ハニカム焼成体７０でも、セル壁７３がＰＭ等を補集するためのフィルタとして機能する。
そして、ハニカム焼成体７０は、排ガス流入側が開口したセル（断面の形状が８角形のセル７１ｂ）の容積が、排ガス流出側が開口したセル（断面の形状が４角形のセル７１ａ）の容積に比べて大きいため、圧力損失を上昇を抑えつつ、多量のＰＭを捕集するのに適している。
Also in the honeycomb fired
Therefore, also in the honeycomb fired
In the honeycomb fired
また、ハニカム焼成体が、上記大容積セルと上記小容積セルとを備える場合、上記大容積セル及び上記小容積セルの上記断面の形状の組合せは、８角形と４角形とに限定されるわわけではなく、断面積が異なる２種類の４角形の組合せ等、任意の形状の組合せであればよい。 Further, when the honeycomb fired body includes the large volume cell and the small volume cell, the combination of the cross-sectional shapes of the large volume cell and the small volume cell is limited to an octagon and a quadrangle. However, it may be a combination of arbitrary shapes such as a combination of two types of quadrangles having different cross-sectional areas.
（その他の実施形態） (Other embodiments)
第一〜第四の実施形態のハニカム構造体の製造方法では、四角柱状のハニカム焼成体を複数個結束させて、ハニカム焼成体の集合体を作製した後、切削加工を施してハニカムブロックを作製しているが、本発明の実施形態のハニカム構造体の製造方法では、予め、所定の形状で作製したハニカム焼成体を複数個結束してハニカムブロックとしてもよい。 In the method for manufacturing a honeycomb structure according to the first to fourth embodiments, a plurality of square pillar-shaped honeycomb fired bodies are bundled to produce an aggregate of honeycomb fired bodies, and then a cutting process is performed to produce a honeycomb block. However, in the method for manufacturing a honeycomb structure according to the embodiment of the present invention, a plurality of honeycomb fired bodies manufactured in advance with a predetermined shape may be bundled to form a honeycomb block.
図９（ａ）〜（ｃ）は、本発明の実施形態のハニカム構造体の製造方法で作製するハニカム焼成体の別の一例を模式的に示す斜視図である。
即ち、図９（ａ）〜（ｃ）に示したような、複数のセル２２１、２３１、２４１がセル壁２２３、２３３、２４３を隔てて形成されたハニカム焼成体２２０、２３０、２４０を所定の個数ずつ結束させてハニカムブロックとしてもよい。
なお、図２に示したハニカムブロック１５を作製する場合は、ハニカム焼成体２２０、２４０をそれぞれ４個、ハニカム焼成体２３０を８個使用すればよい。
FIGS. 9A to 9C are perspective views schematically showing another example of the honeycomb fired body manufactured by the method for manufacturing a honeycomb structure according to the embodiment of the present invention.
That is, as shown in FIGS. 9A to 9C, honeycomb fired
When the
ここまで説明した本発明の実施形態に係るハニカム構造体では、ハニカム構造体に触媒を担持させることは記載していないが、本発明の実施形態では、ハニカム構造体に触媒を担持させてもよい。
そして、ハニカム構造体に触媒を担持させることにより、触媒が担持されたハニカム構造体や、このハニカム構造体を用いた排ガス浄化装置では排ガスに含有されるＣＯ、ＨＣ及びＮＯｘ等の有害成分を浄化することができる。また、担持させた触媒により、ＰＭの燃焼温度を低下させることもできる。
In the honeycomb structure according to the embodiment of the present invention described so far, it is not described that the catalyst is supported on the honeycomb structure. However, in the embodiment of the present invention, the catalyst may be supported on the honeycomb structure. .
Then, by supporting the catalyst on the honeycomb structure, the honeycomb structure on which the catalyst is supported and the exhaust gas purification apparatus using the honeycomb structure purifies harmful components such as CO, HC and NOx contained in the exhaust gas. can do. Moreover, the combustion temperature of PM can also be lowered by the supported catalyst.
上記触媒としては、貴金属、アルカリ金属、アルカリ土類金属、それらの酸化物等を含む触媒が挙げられる。そして、これらの触媒は、比表面積の高いアルミナ等からなる酸化物膜の表面に付与されてハニカム構造体に担持されていることが望ましい。 Examples of the catalyst include catalysts containing noble metals, alkali metals, alkaline earth metals, oxides thereof, and the like. These catalysts are desirably applied to the surface of an oxide film made of alumina or the like having a high specific surface area and supported on the honeycomb structure.
本発明の実施形態で使用する封止材ペーストが少なくとも無機粒子と無機バインダとを含むペーストである場合、無機粒子としては、例えば、炭化物粒子、窒化物粒子等を挙げることができ、具体的には、炭化ケイ素、窒化ケイ素、窒化ホウ素からなる無機粉末等が挙げられる。これらは、単独で用いてもよく、２種以上を併用してもよい。無機粒子のなかでは、熱伝導性に優れる炭化ケイ素粒子が望ましい。
また、無機バインダとしては、例えば、シリカゾル、アルミナゾル等が挙げられる。これらは、単独で用いてもよく、２種以上を併用してもよい。無機バインダのなかでは、シリカゾルが望ましい。
When the sealing material paste used in the embodiment of the present invention is a paste containing at least inorganic particles and an inorganic binder, examples of the inorganic particles include carbide particles and nitride particles. Specifically, Includes inorganic powders composed of silicon carbide, silicon nitride, boron nitride, and the like. These may be used alone or in combination of two or more. Among the inorganic particles, silicon carbide particles having excellent thermal conductivity are desirable.
Examples of the inorganic binder include silica sol and alumina sol. These may be used alone or in combination of two or more. Among inorganic binders, silica sol is desirable.
また、上記封止材ペーストは、さらに無機繊維及び／又はウィスカを含んでいてもよく、この場合、無機繊維及び／又はウィスカとしては、例えば、シリカ−アルミナ、ムライト、アルミナ、シリカ等のセラミックファイバー等が挙げられる。これらは、単独で用いてもよく、２種以上を併用してもよい。無機繊維及び／又はウィスカのなかでは、アルミナファイバが望ましい。 The sealing material paste may further contain inorganic fibers and / or whiskers. In this case, examples of the inorganic fibers and / or whiskers include ceramic fibers such as silica-alumina, mullite, alumina, silica, and the like. Etc. These may be used alone or in combination of two or more. Among inorganic fibers and / or whiskers, alumina fibers are desirable.
また、上記封止材ペーストについては既に説明したように、ハニカム焼成体を押出成形にて作製する際に使用する湿潤混合物と略同一の組成を有するものであってもよい。
そして、焼成処理を経ることなく形成した封止部の形成に使用する封止材ペーストは、前者（少なくとも無機粒子と無機バインダとを含む封止材ペースト）が望ましく、焼成処理を経て形成した封止部の形成に使用する封止材ペーストは、後者（湿潤混合物と略同一の組成のペースト）が望ましい。
ただし、前者の封止材ペーストを焼成処理を経て形成する封止部の材料として用いてもよいし、後者の封止材ペーストを焼成処理を経ることなく形成する封止部の材料として用いてもよい。
Further, as described above, the sealing material paste may have substantially the same composition as the wet mixture used when the honeycomb fired body is produced by extrusion molding.
The sealing material paste used for forming the sealing part formed without undergoing the firing treatment is desirably the former (a sealing material paste containing at least inorganic particles and an inorganic binder), and the sealing paste formed through the firing treatment. The latter (paste having substantially the same composition as the wet mixture) is desirable for the sealing material paste used for forming the stopper.
However, the former sealing material paste may be used as a material for a sealing part formed through a baking process, or the latter sealing material paste may be used as a material for a sealing part formed without undergoing a baking process. Also good.
また、第一〜第四の実施形態では、焼成処理を経ることなく形成した封止部、接着材層及びコート層は全て略同一の組成のペーストを使用して形成することとしているが、これらは必ずしも略同一でなくてもよい。 In the first to fourth embodiments, the sealing part, the adhesive layer, and the coating layer formed without undergoing the firing treatment are all formed using pastes having substantially the same composition. Are not necessarily substantially the same.
本発明の実施形態のハニカム構造体の形状は、図２に示した円柱状に限定されるものではなく、楕円柱状、多角柱状等の任意の柱の形状であればよい。 The shape of the honeycomb structure of the embodiment of the present invention is not limited to the columnar shape shown in FIG. 2, and may be any columnar shape such as an elliptical columnar shape or a polygonal columnar shape.
本発明の実施形態に係るハニカム焼成体の気孔率は特に限定されないが、３５〜６０％であることが望ましい。
上記ハニカム焼成体の平均気孔径は５〜３０μｍであることが望ましい。
なお、上記気孔率及び気孔径は、例えば、水銀圧入法、アルキメデス法、走査型電子顕微鏡（ＳＥＭ）による測定等の従来公知の方法により測定することができる。
The porosity of the honeycomb fired body according to the embodiment of the present invention is not particularly limited, but is desirably 35 to 60%.
The honeycomb fired body preferably has an average pore diameter of 5 to 30 μm.
The porosity and pore diameter can be measured by a conventionally known method such as a mercury intrusion method, an Archimedes method, or a measurement using a scanning electron microscope (SEM).
本発明の実施形態のハニカム焼成体の構成材料の主成分は、炭化ケイ素に限定されるわけではなく、他の構成材料の主成分として、例えば、窒化アルミニウム、窒化ケイ素、窒化ホウ素、窒化チタン等の窒化物セラミック、炭化ジルコニウム、炭化チタン、炭化タンタル、炭化タングステン等の炭化物セラミック、アルミナ、ジルコニア、コージェライト、ムライト、チタン酸アルミニウム等の酸化物セラミック等が挙げられる。
これらのなかでは、非酸化物セラミックが好ましく、炭化ケイ素が特に好ましい。耐熱性、機械強度、熱伝導率等に優れるからである。なお、上述したセラミックに金属ケイ素を配合したケイ素含有セラミック、ケイ素やケイ酸塩化合物で結合されたセラミック等も構成材料の主成分として挙げられ、これらのなかでは、炭化ケイ素に金属ケイ素が配合されたもの（ケイ素含有炭化ケイ素）が望ましい。
特に、炭化ケイ素を６０ｗｔ％以上含むケイ素含有炭化ケイ素質セラミックが望ましい。
The main component of the constituent material of the honeycomb fired body of the embodiment of the present invention is not limited to silicon carbide, and examples of main components of other constituent materials include aluminum nitride, silicon nitride, boron nitride, and titanium nitride. Nitride ceramics, carbide ceramics such as zirconium carbide, titanium carbide, tantalum carbide, and tungsten carbide, and oxide ceramics such as alumina, zirconia, cordierite, mullite, and aluminum titanate.
Of these, non-oxide ceramics are preferred, and silicon carbide is particularly preferred. It is because it is excellent in heat resistance, mechanical strength, thermal conductivity and the like. In addition, silicon-containing ceramics in which metallic silicon is blended with the above-mentioned ceramics, ceramics bonded with silicon or a silicate compound, and the like are also cited as the main components of the constituent materials, and among these, silicon carbide is blended with silicon carbide. (Silicon-containing silicon carbide) is desirable.
In particular, a silicon-containing silicon carbide ceramic containing 60 wt% or more of silicon carbide is desirable.
本発明の実施形態のハニカム構造体の製造方法において、押出成形する湿潤混合物に含まれるセラミック粉末の粒径は特に限定されないが、後の焼成工程を経て作製されたハニカム焼成体の大きさが、脱脂されたハニカム成形体の大きさに比べて小さくなる場合が少ないものが好ましい。
例えば、１．０〜５０μｍの平均粒径を有する粉末１００重量部と０．１〜１．０μｍの平均粒径を有する粉末５〜６５重量部とを組み合わせたものが好ましい。
In the method for manufacturing a honeycomb structured body of the embodiment of the present invention, the particle size of the ceramic powder contained in the wet mixture to be extruded is not particularly limited, but the size of the honeycomb fired body produced through the subsequent firing step is Those that are less likely to be smaller than the size of the defatted honeycomb molded body are preferred.
For example, a combination of 100 parts by weight of powder having an average particle diameter of 1.0 to 50 μm and 5 to 65 parts by weight of powder having an average particle diameter of 0.1 to 1.0 μm is preferable.
本発明の実施形態のハニカム構造体の製造方法において、押出成形する湿潤混合物に含まれる有機バインダとしては特に限定されず、例えば、メチルセルロース、カルボキシメチルセルロース、ヒドロキシエチルセルロース、ポリエチレングリコール等が挙げられる。これらのなかでは、メチルセルロースが望ましい。
また、上記湿潤混合物に含まれる可塑剤としては特に限定されず、例えば、グリセリン等が挙げられる。
また、上記湿潤混合物に含まれる潤滑剤としては特に限定されず、例えば、ポリオキシエチレンアルキルエーテル、ポリオキシプロピレンアルキルエーテル等のポリオキシアルキレン系化合物等が挙げられる。
上記潤滑剤の具体例としては、例えば、ポリオキシエチレンモノブチルエーテル、ポリオキシプロピレンモノブチルエーテル等が挙げられる。
なお、可塑剤、潤滑剤は、場合によっては、湿潤混合物に含まれていなくてもよい。
In the method for manufacturing a honeycomb structure of the embodiment of the present invention, the organic binder contained in the wet mixture to be extruded is not particularly limited, and examples thereof include methyl cellulose, carboxymethyl cellulose, hydroxyethyl cellulose, and polyethylene glycol. Of these, methylcellulose is desirable.
Moreover, it does not specifically limit as a plasticizer contained in the said wet mixture, For example, glycerol etc. are mentioned.
Further, the lubricant contained in the wet mixture is not particularly limited, and examples thereof include polyoxyalkylene compounds such as polyoxyethylene alkyl ether and polyoxypropylene alkyl ether.
Specific examples of the lubricant include polyoxyethylene monobutyl ether and polyoxypropylene monobutyl ether.
In some cases, the plasticizer and the lubricant may not be contained in the wet mixture.
また、上記湿潤混合物を調製する際には、分散媒液を使用してもよく、分散媒液としては、例えば、水、ベンゼン等の有機溶媒、メタノール等のアルコール等が挙げられる。
さらに、上記湿潤混合物中には、成形助剤が添加されていてもよい。
上記成形助剤としては特に限定されず、例えば、エチレングリコール、デキストリン、脂肪酸、脂肪酸石鹸、ポリアルコール等が挙げられる。
In preparing the wet mixture, a dispersion medium liquid may be used. Examples of the dispersion medium liquid include water, an organic solvent such as benzene, and an alcohol such as methanol.
Furthermore, a molding aid may be added to the wet mixture.
The molding aid is not particularly limited, and examples thereof include ethylene glycol, dextrin, fatty acid, fatty acid soap, polyalcohol and the like.
さらに、上記湿潤混合物には、必要に応じて酸化物系セラミックを成分とする微小中空球体であるバルーンや、球状アクリル粒子、グラファイト等の造孔剤を添加してもよい。
バルーンとしては特に限定されず、例えば、アルミナバルーン、ガラスマイクロバルーン、シラスバルーン、フライアッシュバルーン（ＦＡバルーン）、ムライトバルーン等が挙げられる。これらのなかでは、アルミナバルーンが望ましい。
Furthermore, a pore-forming agent such as balloons that are fine hollow spheres containing oxide-based ceramics, spherical acrylic particles, and graphite may be added to the wet mixture as necessary.
The balloon is not particularly limited, and examples thereof include an alumina balloon, a glass micro balloon, a shirasu balloon, a fly ash balloon (FA balloon), and a mullite balloon. Of these, alumina balloons are desirable.
また、第一〜第四の実施形態では、複数個のハニカム焼成体を結束させる際に、各ハニカム焼成体の側面に接着材ペーストを塗布し、ハニカム焼成体を順次積層する方法を採用している。しかしながら、複数個のハニカム焼成体を結束させる際には、例えば、ハニカム焼成体間のスペースを確保するために、ハニカム焼成体の表面に空隙保持材を貼り付け、空隙保持材を介して複数個のハニカム焼成体を組み合わせた後、ハニカム焼成体間の空隙に接着材ペーストを注入する方法を用いて、ハニカム焼成体を結束させてもよい。 In the first to fourth embodiments, when a plurality of honeycomb fired bodies are bundled, an adhesive paste is applied to the side surface of each honeycomb fired body, and the honeycomb fired bodies are sequentially stacked. Yes. However, when bundling a plurality of honeycomb fired bodies, for example, in order to secure a space between the honeycomb fired bodies, a gap holding material is attached to the surface of the honeycomb fired bodies, and a plurality of gaps are disposed via the gap holding material. After the honeycomb fired bodies are combined, the honeycomb fired bodies may be bound using a method of injecting an adhesive paste into the gaps between the honeycomb fired bodies.
また、第一〜第四の実施形態において、ハニカムブロックは複数個のハニカム焼成体が結束されているが、本発明の実施形態のハニカム構造体及び排ガス浄化装置では、必ずしもハニカムブロックが複数個のハニカム焼成体から構成されている必要はなく、ハニカムブロックが１個のハニカム焼成体から構成されていてもよい。
そして、このようなハニカムブロックが１個のハニカム焼成体から構成されたハニカム構造体を製造する際には、湿潤混合物を押出成形する工程において、長手方向に垂直な断面の形状が、ハニカムブロックの長手方向に垂直な断面と略同一のハニカム成形体を作製すればよい。
In the first to fourth embodiments, the honeycomb block has a plurality of honeycomb fired bodies bound together. However, in the honeycomb structure and the exhaust gas purification apparatus of the embodiment of the present invention, the honeycomb block does not necessarily have a plurality of honeycomb blocks. The honeycomb fired body need not be constituted, and the honeycomb block may be constituted by one honeycomb fired body.
And when manufacturing such a honeycomb structure in which the honeycomb block is composed of one honeycomb fired body, in the step of extruding the wet mixture, the shape of the cross section perpendicular to the longitudinal direction is What is necessary is just to produce the honeycomb molded body substantially the same as the cross section perpendicular to the longitudinal direction.
１０ ハニカム構造体
１１ 接着材層
１２ コート層
１５ ハニカムブロック
２０ ハニカム焼成体
２１ セル
２２ａ 未焼成の封止部（第二の封止部）
２２ｂ 焼成された封止部（第一の封止部）
２３ セル壁
DESCRIPTION OF
22b Firing sealing part (first sealing part)
23 cell wall
Claims (22)
前記封止部のうち、前記ハニカム焼成体の一方の端面側の封止部は焼成された第一の封止部であり、前記ハニカム焼成体の他方の端面側の封止部は未焼成の第二の封止部であることを特徴とするハニカム構造体。 A honeycomb composed of a pillar-shaped honeycomb fired body in which a plurality of cells are arranged in parallel in the longitudinal direction across a cell wall, and either one end of the cells is sealed by a sealing portion formed of a sealing material paste A honeycomb structure with blocks,
Among the sealing parts, the sealing part on one end face side of the honeycomb fired body is a fired first sealing part, and the sealing part on the other end face side of the honeycomb fired body is unfired. A honeycomb structure characterized by being a second sealing portion.
前記大容積セルには、前記第一の封止部が形成され、
前記小容積セルには、前記第二の封止部が形成されている請求項１〜９のいずれかに記載のハニカム構造体。 The plurality of cells formed in the honeycomb fired body includes a large volume cell and a relatively small small volume cell in which the cross section of the cell perpendicular to the longitudinal direction is relatively large,
In the large-capacity cell, the first sealing portion is formed,
The honeycomb structure according to any one of claims 1 to 9, wherein the second sealing portion is formed in the small volume cell.
前記ハニカム構造体が、前記第一の封止部が形成された端面側が排ガス流出側、前記第二の封止部が形成された側が排ガス流入側となるように配置されていることを特徴とする排ガス浄化装置。 The honeycomb structure according to any one of claims 1 to 10, wherein the honeycomb structure is disposed in a metal container via a holding sealing material,
The honeycomb structure is arranged such that an end surface side on which the first sealing portion is formed is an exhaust gas outflow side, and a side on which the second sealing portion is formed is an exhaust gas inflow side. Exhaust gas purification device.
前記ハニカム成形体の両端部の所定箇所のセルが封止されるように封止材ペーストを充填する工程と、
このハニカム成形体に焼成処理を施して、第一の封止部が形成されたハニカム焼成体を作製する工程と、
少なくとも１つの前記ハニカム焼成体からなるハニカムブロックを作製する工程とを含み、
さらに、前記第一の封止部が所定箇所に形成されたハニカム焼成体を切断する工程と、
切断された前記ハニカム焼成体の前記第一の封止部が形成された側と反対側の端部の所定箇所のセルに封止材ペーストを充填し、加熱処理を施して前記封止材ペーストを固化して第二の封止部を形成する工程とを含むことを特徴とするハニカム構造体の製造方法。 Forming a columnar honeycomb formed body in which a plurality of cells are arranged in parallel in the longitudinal direction across the cell wall by molding a ceramic raw material;
Filling a plug material paste so that cells at predetermined locations on both ends of the honeycomb molded body are sealed;
The honeycomb formed body is fired to produce a honeycomb fired body having a first sealing portion formed;
Producing a honeycomb block comprising at least one of the honeycomb fired bodies,
Furthermore, the step of cutting the honeycomb fired body in which the first sealing portion is formed in a predetermined location;
The sealing material paste is filled with a sealing material paste in a predetermined portion of the end of the cut honeycomb honeycomb body opposite to the side where the first sealing portion is formed, and subjected to heat treatment. And a step of solidifying the substrate to form a second sealing portion.
前記第二の封止部を形成する工程を行った後、前記ハニカムブロックを作製する工程を行う請求項１２に記載のハニカム構造体の製造方法。 After performing the step of producing the honeycomb fired body in which the first sealing portion is formed, performing the step of cutting the honeycomb fired body,
The method for manufacturing a honeycomb structured body according to claim 12, wherein the step of forming the honeycomb block is performed after the step of forming the second sealing portion.
次に、この接着材層を介して結束されたハニカムブロックを切断した後、前記ハニカムブロックの前記第一の封止部が形成された側と反対側の端部に、前記第二の封止部を形成する工程を行う請求項１２に記載のハニカム構造体の製造方法。 After producing the honeycomb fired body in which the first sealing portion was formed, a plurality of the honeycomb fired bodies were bound through an adhesive layer, and the first sealing portion was formed at both ends. Make a honeycomb block,
Next, after cutting the honeycomb block bound through the adhesive layer, the second sealing is provided at the end of the honeycomb block opposite to the side where the first sealing portion is formed. The method for manufacturing a honeycomb structured body according to claim 12, wherein the step of forming the portion is performed.
前記大容積セルには、前記第一の封止部を形成し、
前記小容積セルには、前記第二の封止部を形成する請求項１２〜１７のいずれかに記載のハニカム構造体の製造方法。 The honeycomb fired body is formed such that a plurality of cells are composed of a large volume cell having a relatively large cross section of the cell perpendicular to the longitudinal direction and a relatively small volume cell.
In the large-capacity cell, the first sealing portion is formed,
The method for manufacturing a honeycomb structure according to any one of claims 12 to 17, wherein the second sealing portion is formed in the small volume cell.