JP2009166877A - Air-permeable packaging material - Google Patents
Air-permeable packaging material Download PDFInfo
- Publication number
- JP2009166877A JP2009166877A JP2008008051A JP2008008051A JP2009166877A JP 2009166877 A JP2009166877 A JP 2009166877A JP 2008008051 A JP2008008051 A JP 2008008051A JP 2008008051 A JP2008008051 A JP 2008008051A JP 2009166877 A JP2009166877 A JP 2009166877A
- Authority
- JP
- Japan
- Prior art keywords
- air
- packaging material
- breathable
- layer
- air permeability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、通気性を有する包装材料に関し、脱酸素剤、除湿剤、炭酸ガス吸収剤、防錆剤、防臭剤等の包装に適した通気性包装材料に関するものである。 The present invention relates to a breathable packaging material, and relates to a breathable packaging material suitable for packaging of oxygen scavengers, dehumidifiers, carbon dioxide absorbents, rust inhibitors, deodorants, and the like.
近年、食品の酸化、変色、カビ、腐敗などの品質低下や変質の防止、また衣類や紙製品の防虫や品質保持、或いは金属部品、精密機器の錆やカビ発生を防止するため乾燥剤、脱酸素剤、除湿剤、防錆剤等の機能性剤が多く用いられている。この機能性剤は、通気性を有する包装材料からなる袋状の包装袋内に封入したものが一般に用いられ、包装内の酸素や湿気を吸収してその品質を長期間維持するものである。 In recent years, desiccants and removal of foods have been prevented to prevent quality deterioration and deterioration such as oxidation, discoloration, mold and decay, and to prevent insects and quality of clothing and paper products, and to prevent rust and mold generation of metal parts and precision equipment. Many functional agents such as oxygen agents, dehumidifiers, and rust inhibitors are used. This functional agent is generally used in a bag-like packaging bag made of a breathable packaging material, and absorbs oxygen and moisture in the packaging to maintain its quality for a long period of time.
上記の通気性包装材料としては、通気性を有する紙や不織布等の通気性シート材料に、包装材料の透気度をコントロールするために所定の配列で多数の細孔が開孔されたポリエステルやポリエチレン、ナイロン、ポリプロピレン等のヒートシール性を有する合成樹脂製有孔フィルムを両面に貼り合わせた通気性を有する積層体が主に用いられてきた（例えば、特許文献１）。 As the above-mentioned breathable packaging material, polyester or a breathable sheet material such as breathable paper or nonwoven fabric, in which a large number of pores are opened in a predetermined arrangement in order to control the air permeability of the packaging material, A laminate having air permeability in which a synthetic resin perforated film having heat sealing properties such as polyethylene, nylon, and polypropylene is bonded to both surfaces has been mainly used (for example, Patent Document 1).
このような従来の通気性包装材料の１例としては、「厚み１２μｍポリエステル（ＰＥＴ１２）／印刷層／厚み１５μｍのポリエチレン（ＰＥ１５）／熱ラミネート／撥水撥油紙／熱ラミネート／厚み３０μｍのポリエチレン（ＰＥ３０）」、からなる積層体が一般的な構成として挙げられ、積層体の表裏面から通気孔が開孔されていた。 As an example of such a conventional air-permeable packaging material, “12 μm thick polyester (PET12) / printing layer / 15 μm thick polyethylene (PE15) / thermal laminate / water / oil repellent paper / thermal laminate / 30 μm thick polyethylene ( PE30) ", and the like. As a general configuration, a laminate was formed, and vents were opened from the front and back surfaces of the laminate.
上記の従来の通気性包装材料の製造方法では、その工程が、
１．ＰＥＴ１２の裏面層に文字、図柄等を印刷する。
２．「ＰＥＴ１２／印刷層」にＰＥ１５を押出しラミネートし、「ＰＥＴ１２／印刷層／ＰＥ１５」の積層体を形成する。
３．「ＰＥＴ１２／印刷層／ＰＥ１５」の積層体に有孔加工を行い、所定パターンの通気孔を開孔する…（Ａ）とする。
４．ＰＥ３０に有孔加工を行い通気孔を開孔する…（Ｂ）とする。
５．撥水撥油紙と（Ａ）を熱ラミネートで貼り合わせ積層体「ＰＥＴ１２／印刷層／ＰＥ１５／撥水撥油紙」…（Ｃ）を形成する。
６．（Ｃ）に（Ｂ）を熱ラミネートし積層体を形成して通気性包装材料とする。
という６工程により製造されるものであった。
In the conventional method for manufacturing a breathable packaging material, the process includes
1. Characters, designs, etc. are printed on the back layer of PET12.
2. PE15 is extruded and laminated on “PET12 / printing layer” to form a laminate of “PET12 / printing layer / PE15”.
3. A perforated process is performed on the laminate of “PET12 / printing layer / PE15” to open a predetermined pattern of air holes (A).
4). A perforated process is performed on PE30 to open a vent hole.
5. The water- and oil-repellent paper and (A) are bonded together by thermal lamination to form a laminate “PET12 / printing layer / PE15 / water / oil-repellent paper” (C).
6). (B) is heat laminated to (C) to form a laminate to obtain a breathable packaging material.
It was manufactured by the six processes.
また、プラスチックフィルム層と接着層と強化材層と酢酸ビニル含有率が６〜３０重量％のエチレン−酢酸ビニル共重合体層からなり、プラスチックフィルム層と接着層に細孔が形成され、エチレン−酢酸ビニル共重合体層は通気性を有するため細孔の形成が不要である通気性包装材料が開示されている（特許文献２）。
上記従来の通気性包装材料では、次のような問題点が挙げられる。
Ａ）製造工程が多い（６工程）ことによる時間的損失とコストアップが大きい。
Ｂ）熱針による有孔加工が一般的で、特殊な装置を必要としコストに影響する。
Ｃ）熱で熱可塑性樹脂フィルムを溶かして孔を空けるので、溶けた孔の大きさが不安定になりがちで、設計通りの孔を形成するのが困難である。
Ｄ）熱可塑性樹脂に熱針で孔を空けるので、針に溶融樹脂が絡まりやすく加工が困難となり、孔の大きさが不安定となったり、メンテナンス頻度が高くなる。
Ｅ）熱ラミネートは熱のかかったロール間に基材を通して貼り合わせる加工で、上記構成では、ＰＥを半溶融状態にして撥水撥油紙や不織布等の繊維にめり込ませる形となり、加工速度及び温度管理の調整が困難であり、そのため一般的な熱ラミネートの加工速度は約５０ｍ／分と遅く、生産性が低い。
Ｆ）熱ラミネートは樹脂を溶かして撥水撥油紙などと貼り合わせるため、溶けた樹脂が孔を塞ぎ透気度が不安定になるおそれがある。
The conventional breathable packaging material has the following problems.
A) Time loss and cost increase due to many manufacturing processes (six processes) are large.
B) Perforated machining with a hot needle is common, requires special equipment, and affects cost.
C) Since the hole is formed by melting the thermoplastic resin film with heat, the size of the melted hole tends to become unstable, and it is difficult to form a hole as designed.
D) Since a hole is made in the thermoplastic resin with a hot needle, the molten resin is easily entangled with the needle, making it difficult to process, making the hole size unstable and increasing the maintenance frequency.
E) Thermal laminating is a process in which a base material is bonded between heated rolls. In the above configuration, PE is in a semi-molten state and is embedded in fibers such as water and oil repellent paper and nonwoven fabric. In addition, it is difficult to adjust the temperature control. Therefore, the processing speed of a general thermal laminate is as low as about 50 m / min, and the productivity is low.
F) Since the heat laminate melts the resin and bonds it to water- and oil-repellent paper or the like, the melted resin may block the holes and the air permeability may become unstable.
また、特許文献２に記載のものは、材料費や製造工程は削減されるが、エチレン−酢酸ビニル共重合体層が熱溶融押出ラミネーションにより形成されるため、工程が煩雑になっていた。
Moreover, although the material cost and the manufacturing process of the thing of
そこで本発明は、製造が容易であって工程数が低減でき大幅なコストダウンを達成すると共に、安定した狙いの透気度が得られ、かつ製造時及び使用時の安全性、衛生面で優れた通気性包装材料を提供することを目的とする。 Therefore, the present invention is easy to manufacture, can reduce the number of processes, achieves a significant cost reduction, obtains a stable target air permeability, and is excellent in safety and hygiene during manufacturing and use. An object of the present invention is to provide a breathable packaging material.
すなわち、本発明の通気性包装材料は、合成樹脂フィルム層と通気性シート基材と通気性コート層とを積層した積層体からなり、前記合成樹脂フィルム層は前記通気性シート基材に達する通気孔を形成し、前記通気性コート層がヒートシール性と通気性とを有する水系エマルジョン型コーティング剤を塗布して形成された塗膜からなることを特徴とする。 That is, the breathable packaging material of the present invention comprises a laminate in which a synthetic resin film layer, a breathable sheet base material, and a breathable coat layer are laminated, and the synthetic resin film layer passes through the breathable sheet base material. The pores are formed, and the air-permeable coating layer is formed of a coating film formed by applying a water-based emulsion type coating agent having heat sealability and air permeability.
本発明の通気性包装材料においては、前記水系エマルジョン型コーティング剤が、エチレン−酢酸ビニル共重合体及び／又はエチレン−メタクリル酸共重合体を含む水系エマルジョンであることが好ましい。 In the breathable packaging material of the present invention, the aqueous emulsion type coating agent is preferably an aqueous emulsion containing an ethylene-vinyl acetate copolymer and / or an ethylene-methacrylic acid copolymer.
さらに、本発明の通気性包装材料は、ＪＩＳ Ｌ１０９６に規定のガーレー法に準じて測定される透気度が、５００〜１２，０００秒／１００ｃｃであることが好ましい。 Further, the breathable packaging material of the present invention preferably has an air permeability measured according to the Gurley method defined in JIS L1096 of 500 to 12,000 seconds / 100 cc.
本発明の通気性包装材料によれば、積層体の積層工程、開孔工程が簡略化され、エマルジョン型コーティング剤をコーティングし乾燥させることで通気層を形成するので、製造が容易になり、かつ安定した透気度を得ることができ、さらに水系エマルジョンを用いることで包装材料の製造時及び包装袋など使用時の安全性、衛生面で優れるものとなる。 According to the breathable packaging material of the present invention, the laminating step and the opening step of the laminate are simplified, and the breathable layer is formed by coating and drying the emulsion type coating agent. A stable air permeability can be obtained, and the use of an aqueous emulsion further improves safety and hygiene when manufacturing packaging materials and packaging bags.
以下、本発明にかかる実施形態について説明する。 Embodiments according to the present invention will be described below.
図１は、本発明の１実施形態に係る通気性包装材料（以下、単に「包装材料」という）１０の断面図である。包装材料１０は、通気性シート基材１と合成樹脂フィルム層２を接着層３を介して積層し、前記シート基材１の他面に水系エマルジョン型コーティング剤を塗布し乾燥させた塗膜からなる通気性コート層４を形成し、前記合成樹脂フィルム層２の表面から通気性シート基材１に達するまでの通気孔５を形成した積層体８である。
FIG. 1 is a cross-sectional view of a breathable packaging material (hereinafter simply referred to as “packaging material”) 10 according to an embodiment of the present invention. The
通気性を有するシート基材１としては、透気度が１〜２０秒／１００ｃｃ、好ましくは５〜１０秒／１００ｃｃである、撥水撥油処理あるいは耐水耐油処理を施したパルプ紙やポリエチレン、ポリプロピレン、ポリエステル等を抄紙した合成繊維混抄紙等の紙類、又はポリエチレンやポリエステルなどの合成樹脂からなるスパンボンド法やスパンレース法による不織布等の繊維質層、ポリエチレン系合成樹脂等を材料として微細有孔処理を施した微多孔性フィルム等の通気性素材が用いられ、乾燥剤、脱酸素剤等の成分である鉄粉等の固体微粉末を通過させず、また常圧で水及び油を通しにくいものが用いられる。 As the sheet base material 1 having air permeability, pulp paper or polyethylene subjected to water / oil repellent treatment or water / oil resistance treatment having an air permeability of 1 to 20 seconds / 100 cc, preferably 5 to 10 seconds / 100 cc, Paper made of synthetic fiber mixed paper made of polypropylene, polyester, etc., or fiber layers such as non-woven fabric by spunbond method or spunlace method made of synthetic resin such as polyethylene and polyester, polyethylene synthetic resin, etc. Breathable material such as microporous film that has been subjected to perforation treatment is used, and it does not pass solid fine powder such as iron powder, which is a component of desiccant, oxygen scavenger, etc. Something that is difficult to pass through is used.
シート基材１の厚みは、特に限定されないが、強度と通気性を確保するために５０〜１００μｍ程度が好ましく、撥水撥油紙の場合は秤量５０ｇ／ｍ２ 、厚さ８０μｍ、透気度８〜１０秒／１００ｃｃにあるものが例示される。 The thickness of the sheet substrate 1 is not particularly limited, but is preferably about 50 to 100 μm in order to ensure strength and air permeability. In the case of water and oil repellent paper, the weight is 50 g / m 2 , the thickness is 80 μm, and the air permeability is 8 Examples are those at 10 seconds / 100 cc.
合成樹脂フィルム層２としては、ポリエチレンテレフタレート（ＰＥＴ）やポリブチレンテレフタレート（ＰＢＴ）などのポリエステル樹脂、ナイロン６やナイロン６６などのポリアミド樹脂、ポリエチレンやポリプロピレン等のオレフィン系樹脂、ポリエチレン酢酸ビニル共重合体などの熱可塑性樹脂が用いられ、２軸延伸法により製膜されたＰＥＴ樹脂やナイロン樹脂からなるフィルムが強度、光沢性、印刷適性などに優れ好適に使用することができる。
The synthetic
樹脂フィルム層２の厚みは、特に限定されないが、例えば、ＰＥＴの場合は強度と非通水性を確保するために１０〜３０μｍ程度であることが好ましい。
The thickness of the
また、シート基材１あるいは樹脂フィルム層２の表面には、「脱酸素剤」、「ＤＯ ＮＯＴ ＥＡＴ」等の文字や絵柄を印刷することができる。
Further, on the surface of the sheet substrate 1 or the
前記シート基材１と樹脂フィルム層２は接着層３を介して積層される。接着層３としては、水系または溶剤系の接着剤を用いて樹脂フィルム層２とシート基材１とを貼り合わされるが、残留溶剤や引火性、毒性等の安全性の問題から、水系接着剤を使用することが好ましい。水系接着剤としては、酢酸ビニル樹脂、エチレン−酢酸ビニル共重合樹脂、アクリル樹脂あるいはウレタン樹脂等を主成分とするエマルジョン型接着剤等が挙げられる。
The sheet substrate 1 and the
また、ポリエチレン（ＰＥ）等のポリオレフィン樹脂の溶融押出層を接着層３とすることもでき、ＰＥの押出ラミネーションによりシート基材１と樹脂フィルム層２を積層することもできる。
Moreover, the melt-extruded layer of polyolefin resin, such as polyethylene (PE), can also be used as the
通気性コート層４は、乾燥すると通気性を有するようになる水系エマルジョン型コーティング剤を塗布し形成された塗膜からなる。
The air-
前記エマルジョン型コーティング剤としては、例えば、酢酸ビニル系、アクリル酸エステル系、メタクリル酸エステル系、アイオノマー系、及びスチレン−ブタジエンなどのゴム系の水系エマルジョンが挙げられる。これらのコーティング剤は、乾燥すると非通水性を示し、かつ通気性とヒートシール性を有し、水系であるので製造時及び包装袋など使用時に引火性や毒性などがなく安全性、衛生面で優れるものとなり、食品の乾燥剤や除湿剤の包装袋にも好適に使用できるが、特に、エチレン−酢酸ビニル共重合体（ＥＶＡ）及び／又はエチレン−メタクリル酸共重合体（ＥＭＡＡ）を含む水系エマルジョンが、均一な塗布性、塗布量の調整しやすさ（透気度の調整）が良く好ましい。 Examples of the emulsion-type coating agent include vinyl acetate-based, acrylic ester-based, methacrylic ester-based, ionomer-based, and rubber-based aqueous emulsions such as styrene-butadiene. These coating agents are non-water-permeable when dried, have breathability and heat-sealability, and are water-based, so there is no flammability or toxicity during production or use of packaging bags, etc., in terms of safety and hygiene. It is excellent and can be suitably used for packaging bags for food desiccants and dehumidifiers. In particular, an aqueous system containing ethylene-vinyl acetate copolymer (EVA) and / or ethylene-methacrylic acid copolymer (EMAA). Emulsions are preferable because of their uniform coatability and ease of adjusting the coating amount (adjustment of air permeability).
コート層４は、シート基材１の全面に上記水系エマルジョン型コーティング剤を塗布し乾燥させた塗膜層からなり、安定した塗布量が得られることで透気度の調整のしやすさ、その安定化が図られ、またシート基材１に露出面がないので製袋時の安定したヒートシール強度が得られる。
The
例えば、上記ＥＶＡを用いたコーティング剤としては、酢酸ビニル含有率が１０〜３０重量％のＥＶＡが使用でき、このエマルジョンをシート基材１に塗布することで通気性とヒートシール性を有するコート層４を形成することができるので、通気孔５を形成しなくとも乾燥剤等を包装するために必要な通気性と袋を製造するヒートシール性が得られる。 For example, as the coating agent using EVA, EVA having a vinyl acetate content of 10 to 30% by weight can be used. By applying this emulsion to the sheet substrate 1, a coating layer having air permeability and heat sealability. 4 can be formed, the air permeability necessary for packaging the desiccant and the like and the heat seal property for manufacturing the bag can be obtained without forming the air holes 5.
上記ＥＶＡは、酢酸ビニル含有率が１０重量％未満のものでは透気度が小さくなり通気性包装材として好ましくない。一方、酢酸ビニル含有率が３０重量％以上のものでは、コート層４の皮膜の滑性が悪く製袋化が困難であり、また酢酸ビニル臭が強くなるために好ましくない。酢酸ビニル含有率が１０〜３０重量％のＥＶＡを使用することにより通気性、加工性が優れるとともに、通気孔を形成しなくとも通気性包装材に必要な適度な通気性が得られる。
When the EVA has a vinyl acetate content of less than 10% by weight, the air permeability becomes small, which is not preferable as a breathable packaging material. On the other hand, a vinyl acetate content of 30% by weight or more is not preferable because the film of the
また、コーティング剤は、ＥＶＡを固形分として２０〜５０重量％含む水溶液が好ましく、固形分が２０重量％未満では透気度の調整やヒートシール性が劣り、５０重量％を超えると粘度が増加し塗布作業がしずらくなったり、必要な通気性が得られなくなる。さらに、乳化剤としてカチオン界面活性剤や非イオン界面活性剤、水溶性の重合開始剤などを添加してもよい。 The coating agent is preferably an aqueous solution containing 20 to 50% by weight of EVA as a solid content. If the solid content is less than 20% by weight, the air permeability adjustment and heat sealability are inferior, and if it exceeds 50% by weight, the viscosity increases. However, it becomes difficult to perform the coating operation and necessary air permeability cannot be obtained. Furthermore, you may add a cationic surfactant, a nonionic surfactant, a water-soluble polymerization initiator, etc. as an emulsifier.
コーティング剤の塗布量は、ＥＶＡ固形分として１〜１２ｇ／ｍ２・ｄｒｙであり、好ましくは３〜６ｇ／ｍ２・ｄｒｙである。塗布量が少ないとヒートシール強度が低くなり製袋加工が困難になり、また袋が破損しやすくなる。逆に塗布量が多くなると通気性が低下し、目的の透気度が得られなくなる。 The coating amount of the coating agent is 1~12g / m 2 · dry as EVA solids, preferably 3~6g / m 2 · dry. When the coating amount is small, the heat seal strength is low, making the bag making process difficult, and the bag is easily damaged. On the other hand, if the coating amount increases, the air permeability decreases and the desired air permeability cannot be obtained.
なお、コーティング剤の塗布方法は、特に制限されず、グラビア、エアナイフ、スプレー、リバース、クローズド法など、各種のコーティングによることができる。 In addition, the coating method of a coating agent is not specifically limited, It can be based on various coatings, such as a gravure, an air knife, a spray, a reverse, and a closed method.
樹脂フィルム層２側に形成される通気孔５は、樹脂フィルム層２と接着層３に予め通気孔５を開孔したものをシート基材１に積層しても、樹脂フィルム層２とシート基材１を積層した後、あるいはコート層４を形成した後に開孔してもよい。また、シート基材１の内部まで達するハーフカット（図１参照）状のものでも、また全貫通（図２参照）するものでもよい。このように樹脂フィルム層２と接着層３に通気孔５を形成することにより、ＥＶＡなどのコート層４は通気孔を形成しなくとも通気性が得られ、乾燥剤、脱酸素剤等を包装するために必要な通気性を得ることができる。
The
この通気孔５の開孔方法は特に限定されることなく、例えば、積層体８の表面からシート基材１に向かって所定の配列で開孔されるもので、例えば先端部に刃部を有する細長い刃物、細幅の刃物、針又は熱針を用いる機械的手段、レーザー照射、電子線照射等の各種の穿孔方法により開孔することができる。
The method for opening the
通気孔の径、深さ或いは開孔密度は、前記各種の穿孔方法に従い、目的の透気度が得られるように、例えば刃物や針の形状や配置、侵入深さ、或いはレーザー、電子線の照射電圧、電流、照射時間等の穿孔条件により適宜決めることができ、また、通気孔の形状は、横断面は円形、三角、四角等の方形、楕円径等、縦断面も柱状、先細りの円錐、角錐状等であり、特に限定されるものではない。 The diameter, depth or hole density of the air holes is determined according to the above-mentioned various drilling methods, for example, the shape and arrangement of the blades and needles, the penetration depth, or the laser and electron beam so that the desired air permeability can be obtained. It can be determined appropriately according to the drilling conditions such as irradiation voltage, current, irradiation time, etc. The shape of the air vent is circular, triangular, square, etc. in the transverse section, elliptical diameter, etc., the longitudinal section is also columnar, tapered cone The shape is a pyramid or the like and is not particularly limited.
上記のようにして得られた積層体８からなる包装材料は、ＪＩＳ Ｌ１０９６に規定のガーレー法に準じて測定される透気度が、５００〜１２，０００秒／１００ｃｃであることが好ましく、より好ましくは２，０００〜６，０００秒／１００ｃｃである。この透気度の調整はコート層４の透気度と上記通気孔５の大きさ、開孔密度、配列等により容易に実施することができる。
The packaging material comprising the
上記構成による包装材料は、次のような特長が挙げられる。
（１）コーティング層４自体に通気性とヒートシール性があり、通気孔の形成と熱シール層を別途設ける必要がない。
（２）コーティング剤は水系エマルジョンが使用できるので、溶剤系に比べて引火性、安全性、衛生面（非毒性）等に優れ、水で希釈できるので塗布量の調整が容易である。
（３）シート基材の全面にコーティングされるので、パターンコーティングのようにパターン版が不要であり、コーティング方法の幅が増える。グラビア、エアナイフ、スプレー、リバース、クローズド法などがある。また、塗布量が安定するので、安定した目的の透気度を得られ、ヒートシール強度も安定する。さらに、内容物が漏れ出すおそれがない。
（４）樹脂フィルム層とシート基材の積層体に全貫通で通気孔を開孔し、これにコーティング層を設ける製法では、ハーフカットのような微妙な開孔手段が省け、製法を簡易にすることができる。
The packaging material according to the above configuration has the following features.
(1) The
(2) Since a water-based emulsion can be used as the coating agent, it is excellent in flammability, safety, hygiene (non-toxicity) and the like as compared with the solvent system, and can be diluted with water, so that the coating amount can be easily adjusted.
(3) Since the entire surface of the sheet base material is coated, a pattern plate is not required unlike pattern coating, and the width of the coating method increases. There are gravure, air knife, spray, reverse and closed methods. Further, since the coating amount is stabilized, a stable target air permeability can be obtained, and the heat seal strength is also stabilized. Furthermore, there is no risk of the contents leaking out.
(4) In the manufacturing method in which a ventilation hole is opened through the laminated body of the resin film layer and the sheet base material and a coating layer is provided on this, a delicate opening means such as half cut is omitted, and the manufacturing method is simplified. can do.
上記包装材料によって、乾燥剤等の包装袋を形成するには、方形状の一対の包装材料のヒートシール性を有するコート層４同士が対向するように重ね合わせ、その周縁部の３方をヒートシールして１方が開孔された包装袋を作製し、或いは１枚の方形状の包装材料のコート層４同士が対向するように折り重ね、その周縁部をヒートシールして１方が開孔された包装袋を作製し、粉末状や粒状の乾燥剤を収納した後開口部をヒートシールするもの、また筒状の包装体を作製し連続的に乾燥剤を収納し、包装体の中間部分をヒートシールして包装袋を形成することもできる。 In order to form a packaging bag made of the desiccant or the like with the packaging material described above, the pair of rectangular packaging materials are superposed so that the coat layers 4 having heat-sealing properties face each other, and the three peripheral edges are heated. Make a sealed packaging bag with one side opened, or fold it so that the coat layers 4 of one rectangular packaging material face each other, and heat seal the periphery to open one side Create a perforated packaging bag, store powdery or granular desiccant and then heat seal the opening, or create a cylindrical package and continuously store the desiccant in the middle of the package It is also possible to heat seal the part to form a packaging bag.
以上説明した本発明に係る通気性包装材料の具体例を以下に説明する。 Specific examples of the breathable packaging material according to the present invention described above will be described below.
通気性包装材料の構成は、「ＰＥＴ１２／印刷層／水系接着剤層（ウェットラミネート（ＷＬ））／撥水撥油紙／水系エマルジョン型コーティング層」、からなる積層体である。 The structure of the breathable packaging material is a laminate composed of “PET12 / printing layer / water-based adhesive layer (wet laminate (WL)) / water / oil repellent paper / water-based emulsion type coating layer”.
上記の通気性包装材料の製造方法では、その工程が、
１．ＰＥＴ１２の裏面層に文字、図柄等を印刷する。
２．「ＰＥＴ１２／印刷層」と撥水撥油紙や不織布等をＷＬする…（Ｄ）とする。
３．（Ｄ）の撥水撥油紙、不織布等面に水系エマルジョン型コーティング層をコーティングする。
４．ＰＥＴ１２面から有孔加工を行い通気孔を開孔する。
という４工程により製造することができる。
In the manufacturing method of the breathable packaging material, the process includes:
1. Characters, designs, etc. are printed on the back layer of PET12.
2. WL “PET12 / printing layer” and water / oil repellent paper, non-woven fabric, etc. (D).
3. A water-based emulsion-type coating layer is coated on the surface of the water- and oil-repellent paper (D), non-woven fabric and the like.
4). A perforated process is performed from the surface of the PET 12 to open a vent hole.
It can be manufactured by four processes.
以上よりなる通気性包装材料は、従来構成に比較して次の改善点を得ることができる。
Ａ）製造工程数が減るので（６工程→４工程）、大幅なコストダウンが実現できる。
Ｂ）刃物によるカット加工が可能となり、熱針のような特殊な装置が不要となる。
Ｃ）刃物によるカット加工により、孔の大きさ、パターンが均一で、設計通りの加工が可能となり安定した透気度が得られる。
Ｄ）刃物に熱がかからないため、刃物への樹脂の絡まりが無くスムーズな加工ができる。
Ｅ）カット加工では、約１００ｍ／分の高速加工が可能であり、生産性が大幅に向上する。
Ｆ）積層体に貼り合わせた後にカット加工を施すので、孔が塞がるおそれがなく、透気度が安定する。
The breathable packaging material composed as described above can obtain the following improvements compared to the conventional configuration.
A) Since the number of manufacturing steps is reduced (6 steps → 4 steps), a significant cost reduction can be realized.
B) Cutting with a blade is possible, and a special device such as a hot needle is not required.
C) By cutting with a blade, the size and pattern of the holes are uniform, processing as designed is possible, and stable air permeability is obtained.
D) Since the blade is not heated, there is no entanglement of resin on the blade and smooth processing can be performed.
E) In the cutting process, high speed machining of about 100 m / min is possible, and the productivity is greatly improved.
F) Since the cut process is performed after bonding to the laminate, there is no possibility that the hole is blocked, and the air permeability is stabilized.
また、その他の改善点としては、次ぎの事項が挙げられる。
・コーティング剤はヒートシール性と通気性の機能を有しているので、シール面への有孔フィルムの熱ラミネート、およびシール面からのカット加工が不要になる。
・従来の熱針による有孔加工では、針に溶融樹脂が絡まるおそれがあり使用するシーラントフィルムにも制約があったが、本発明ではその心配が無く、コート剤の選定も自由となる。また、使用時の機械充填適性を考慮して、低温シールタイプのコート剤を使用することも可能となる。
・コーティング量を変えることで、シール強度の調整が容易に可能となる。
・ウェットラミネート（ＷＬ）は、水系の接着性樹脂を使用して貼り合わせる手法で、基材であるＰＥＴ等に接着性樹脂を塗り、紙等を貼り合わせてから乾燥させて仕上げるので、接着性樹脂は紙の繊維に吸収され接着膜を形成しない形で貼り合わされる。このことは、後にカット加工を行う上で有利に働く。すなわち、押出しラミネートのようにＰＥを接着剤代わりに貼り合わせる手法だと、ＰＥＴ／ＰＥ／紙という形でＰＥの接着膜を介している。そのためＰＥＴ／ＰＥまでカットを入れる必要があり、本発明のようにＰＥＴにだけカットを入れる方法に比べると加工が困難であった。また、ドライラミネートは溶剤系の接着剤を使用するため、環境面、衛生面で考えるとウェットラミネートのほうが有利である。
Other improvements include the following items.
-Since the coating agent has functions of heat sealing and breathability, thermal lamination of the perforated film on the sealing surface and cutting processing from the sealing surface are unnecessary.
In conventional perforated processing with a hot needle, there is a possibility that the molten resin may be entangled with the needle, and there are restrictions on the sealant film to be used. However, in the present invention, there is no concern about this, and the selection of the coating agent is also free. Moreover, it becomes possible to use a low-temperature seal type coating agent in consideration of machine filling suitability during use.
-By changing the coating amount, the seal strength can be easily adjusted.
・ Wet laminate (WL) is a method of bonding using water-based adhesive resin. Adhesive resin is applied to PET, which is a base material, and paper is pasted and dried to finish. The resin is bonded together in a form that is absorbed by the paper fibers and does not form an adhesive film. This is advantageous for the subsequent cutting process. That is, in the case of a technique in which PE is bonded instead of an adhesive as in the case of extrusion lamination, the adhesive film of PE is interposed in the form of PET / PE / paper. Therefore, it is necessary to make a cut up to PET / PE, and processing is difficult as compared with the method of making a cut only into PET as in the present invention. In addition, since dry lamination uses a solvent-based adhesive, wet lamination is more advantageous in terms of environment and hygiene.
本発明の通気性包装材料は、食品分野のみならず、金属部品や精密機械部品、医薬品、衣料品等、広い分野において各種機能性剤の包装に有効に利用できるものである。 The breathable packaging material of the present invention can be effectively used for packaging various functional agents not only in the food field but also in a wide range of fields such as metal parts, precision machine parts, pharmaceuticals, and clothing.
以下、本発明の実施例について説明するが、本発明はこれらの実施例により何ら制限されるものではない。 Examples of the present invention will be described below, but the present invention is not limited to these examples.
［実施例１］
印刷層６を印刷したＰＥＴフィルム層（厚み１２μｍ）２と撥水撥油紙１（５０ｇ／ｍ２、透気度５秒／１００ｃｃ）とをＥＶＡ系水性接着剤３により接着一体化し、撥水撥油紙１の裏面にＥＶＡ系エマルジョン型コーティング剤（ＥＶＡ固形分３６重量％）を４．３ｇ／ｍ２・ｄｒｙの塗布量で塗布した通気性コート層４を形成した図１に示す積層体８を作製した。図１に示すように、ＰＥＴフィルム層２の表面から撥水撥油紙１に達する通気孔５を、先端部に刃部を有する刃物を用いて図３に示すカットパターンにて開孔した包装材料１０を製造した。得られた包装材料１０の透気度をＪＩＳ Ｌ１０９６に規定のガーレー法に準じて測定した結果、透気度は２，２５０秒／１００ｃｃであった。また、ヒートシール強度は、ヒートシールの熱板温度が１１０℃からの立ち上がりで、４．０〜６．０Ｎ／１５ｍｍの強度を得ることができた（圧力：０．２ＭＰａ、時間：０．５秒）。１１０℃以下の立ち上がりでは、強度は低いものの（１．０〜３．０Ｎ／１５ｍｍ）、接着はされている。
[Example 1]
The PET film layer (thickness 12 μm) 2 on which the printing layer 6 is printed and the water- and oil-repellent paper 1 (50 g / m 2 ,
［実施例２］
上記と同様の積層体８に、図２に示すように、ＰＥＴフィルム層２の表面から撥水撥油紙１を貫通する通気孔７を、先端部に刃部を有する刃物を用いて図３に示すカットパターンにて開孔した包装材料２０を製造した。得られた包装材料２０の透気度を上記と同様にして測定した結果、透気度は２，５００秒／１００ｃｃであった。また、ヒートシール強度は、実施例１と同様に、ヒートシール時の熱板温度が１１０℃からの立ち上がりで、４．０〜６．０Ｎ／１５ｍｍの強度を得ることができた（圧力：０．２ＭＰａ、時間：０．５秒）。１１０℃以下の立ち上がりでは、強度は低いものの（１．０〜３．０Ｎ／１５ｍｍ）、接着はされている。
[Example 2]
As shown in FIG. 2, an
［比較例］
比較例の通気性包装材料は、図４の断面図に示す「ＰＥＴ１２／印刷層／ＰＥ１５／撥水撥油紙（秤量５０ｇ／ｍ２、透気度５秒／１００ｃｃ）／ＰＥ３０」の積層体に、図３に示すカットパターンにて表裏面から通気孔を開孔した従来の包装材料である。透気度は２，５００秒／１００ｃｃであった。また、ヒートシール強度は、ヒートシール時の熱板温度が１２０℃からの立ち上がりで、４．０〜６．０Ｎ／１５ｍｍの強度であり、（圧力：０．２ＭＰａ、時間：０．５秒）、１２０℃以下の立ち上がりでは、強度は０Ｎ／１５ｍｍで全くシール強度がでなかった。
[Comparative example]
The breathable packaging material of the comparative example is a laminate of “PET12 / printing layer / PE15 / water / oil repellent paper (weighing 50 g / m 2 ,
以上のことから、実施例の包装材料は比較例と比べて、同等の透気度を確保しながら、ヒートシール時のシール熱板温度の立ち上がりが１０℃低い温度でシール強度が得られ、それより低い温度でも接着されていることから、低温シール性・ホットタック性に優れ、機械充填適性が向上することが分かる。 From the above, the packaging material of the example can obtain the sealing strength at a temperature lower by 10 ° C. than the comparative example, while ensuring the same air permeability, and the rise of the temperature of the sealing hot plate during heat sealing is 10 ° C. Since it is bonded even at a lower temperature, it can be seen that the low-temperature sealing property and hot tack property are excellent, and the machine filling suitability is improved.
本発明の通気性を有する包装材料は、脱酸素剤、除湿剤、炭酸ガス吸収剤、防錆剤、防臭剤等の機能性を有する組成物を包装する包装材料に好適に用いられる。 The air-permeable packaging material of the present invention is suitably used as a packaging material for packaging a composition having functionality such as a deoxidizer, a dehumidifier, a carbon dioxide absorbent, a rust inhibitor, and a deodorizer.
１……通気性シート基材
２……樹脂フィルム層
４……通気性コート層
５……通気孔
８……積層体
１０……通気性包装材料
DESCRIPTION OF SYMBOLS 1 ... Breathable
Claims (3)
前記合成樹脂フィルム層は前記通気性シート基材に達する通気孔を形成し、前記通気性コート層がヒートシール性と通気性とを有する水系エマルジョン型コーティング剤を塗布して形成された塗膜からなる
ことを特徴とする通気性包装材料。 Consists of a laminate in which a synthetic resin film layer, a breathable sheet base material, and a breathable coat layer are laminated,
The synthetic resin film layer forms a vent hole reaching the breathable sheet substrate, and the breathable coat layer is formed from a coating film formed by applying a water-based emulsion type coating agent having heat sealability and breathability. A breathable packaging material characterized by comprising:
ことを特徴とする請求項１に記載の通気性包装材料。 The breathable packaging material according to claim 1, wherein the aqueous emulsion type coating agent is an aqueous emulsion containing an ethylene-vinyl acetate copolymer and / or an ethylene-methacrylic acid copolymer.
ことを特徴とする請求項１又は２に記載の通気性包装材料。 The air-permeable packaging material according to claim 1 or 2, wherein the air permeability measured according to the Gurley method defined in JIS L1096 is 500 to 12,000 seconds / 100cc.