JP2008308512A - Polyamide resin composition - Google Patents
Polyamide resin composition Download PDFInfo
- Publication number
- JP2008308512A JP2008308512A JP2007154888A JP2007154888A JP2008308512A JP 2008308512 A JP2008308512 A JP 2008308512A JP 2007154888 A JP2007154888 A JP 2007154888A JP 2007154888 A JP2007154888 A JP 2007154888A JP 2008308512 A JP2008308512 A JP 2008308512A
- Authority
- JP
- Japan
- Prior art keywords
- polyamide
- resin composition
- compound
- polyamide resin
- melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明はメタキシリレン基を含有するポリアミドと他のポリアミドからなる組成物を利用したポリアミド樹脂組成物に関する。詳しくは、色調が良好でゲルが少なく、長時間に渡り安定した溶融押出加工が可能なポリアミド樹脂組成物に関する。 The present invention relates to a polyamide resin composition using a composition comprising a polyamide containing a metaxylylene group and another polyamide. Specifically, the present invention relates to a polyamide resin composition having a good color tone, less gel, and capable of stable melt extrusion over a long period of time.
ポリマー主鎖にメタキシリレン基を含有するポリアミドは剛性が高く、熱的性質にも優れるため、エンジニアリングプラスチックとして広く利用されている。またメタキシリレン基をポリマー主鎖に持つことにより、酸素や炭酸ガス等を遮断する性能にも優れているため、フィルム、ボトル、シート等の様々な包装材料のガスバリア材料としても利用されている。包装材料として利用されるポリマーに求められる特性としては、着色が少なく透明で、異物やゲルが少ないことであり、さらには長時間に渡る溶融押出加工において安定運転が可能なことである。 Polyamides containing metaxylylene groups in the polymer main chain are widely used as engineering plastics because of their high rigidity and excellent thermal properties. Further, by having a metaxylylene group in the polymer main chain, it is also excellent in the performance of blocking oxygen, carbon dioxide gas, etc., so it is also used as a gas barrier material for various packaging materials such as films, bottles, sheets and the like. The properties required for the polymer used as a packaging material are that it is transparent with little coloration and has few foreign matters and gels, and furthermore, stable operation is possible in melt extrusion over a long period of time.
メタキシリレン基を含有するポリアミドは、ベンゼン環のα位の炭素(ベンジル炭素)がラジカル化し易く、ナイロン6等の一般的なポリアミドと比較して熱安定性が低い。このため、従来からポリマー製造時あるいは押出成形加工時における熱安定性向上に関わる提案が多くなされてきた。 In the polyamide containing a metaxylylene group, the α-position carbon (benzyl carbon) of the benzene ring is easily radicalized, and the thermal stability is lower than that of a general polyamide such as nylon 6. For this reason, many proposals related to the improvement of thermal stability at the time of polymer production or extrusion molding have been made.
例えば、ポリマー製造工程においてゲルの少ないポリアミドを得るためには、ポリアミドの製造工程における熱履歴を極力少なくしつつ速やかに所望の分子量に到達するよう重縮合を進めることが重要である。ポリアミドの製造工程における熱履歴を少なく方法としてはアミド化反応を速やかに進行させるため、重縮合系内に触媒効果を有する化合物を添加することが効果的である。 For example, in order to obtain a polyamide with less gel in the polymer production process, it is important to proceed polycondensation so as to reach a desired molecular weight quickly while minimizing the heat history in the polyamide production process. As a method for reducing the heat history in the polyamide production process, it is effective to add a compound having a catalytic effect in the polycondensation system in order to rapidly advance the amidation reaction.
アミド化反応に対して触媒効果を有する化合物としては、リン原子含有化合物が広く知られている。ポリアミドの重縮合に際してリン原子含有化合物およびアルカリ金属化合物を添加する方法が過去に提案されている(例えば、特許文献1参照)。リン原子含有化合物はポリアミドのアミド化反応を促進するだけではなく、重縮合系内に存在する酸素によるポリアミドの着色を防止する酸化防止剤としての効果を発揮するため、黄色度の低いポリアミドを得ることができるものの、場合によってはポリアミドの3次元化(ゲル化)を引き起こすこともあるため、適切な添加量を選択する必要がある。 As compounds having a catalytic effect on the amidation reaction, phosphorus atom-containing compounds are widely known. In the past, a method of adding a phosphorus atom-containing compound and an alkali metal compound during polycondensation of polyamide has been proposed (see, for example, Patent Document 1). The phosphorus atom-containing compound not only accelerates the amidation reaction of the polyamide, but also exhibits an effect as an antioxidant that prevents the polyamide from being colored by oxygen present in the polycondensation system, so that a polyamide having a low yellowness is obtained. However, depending on the case, it may cause three-dimensionalization (gelation) of the polyamide, so it is necessary to select an appropriate addition amount.
一方、メタキシリレン基を含有するポリアミドは非常に剛性が高いため、フィルム等の柔軟性を求められる用途にそのままで使用するには種々問題があった。これまでこの性質を改善するためにメタキシリレン基を含有するポリアミドに対してナイロン6やナイロン666等の柔軟性に優れる一般的なポリアミドを溶融混合したものを利用したり、それらと多層構造を形成してガスバリア性と柔軟性を兼ね備えたものとして利用する方法が種々提案されている(例えば、特許文献2〜4参照)。 On the other hand, since the polyamide containing a metaxylylene group has very high rigidity, there have been various problems in using it as it is for applications requiring flexibility such as a film. In order to improve this property, a polyamide containing a metaxylylene group and a general polyamide having excellent flexibility such as nylon 6 and nylon 666 are melt-mixed or a multilayer structure is formed with them. Various methods have been proposed for use as those having both gas barrier properties and flexibility (see, for example, Patent Documents 2 to 4).
しかしながら、メタキシリレン基を含有するポリアミドと他のポリアミドを溶融混合すると、算術平均を遙かに超えた溶融粘度の上昇が起こることがある。この現象を防止する方法として、溶融混合後のポリアミド樹脂組成物の末端基カルボキシル基と末端アミノ基の濃度差と溶融混合後のポリアミド組成物中に含まれるリン原子濃度が特定の関係になるように使用するポリアミドを選択する方法が提案されている(例えば、特許文献5参照)。この方法は、溶融状態においてアミド化が進行しにくくするために、ポリアミドの末端基のバランスを一方が過剰になるように設定する、もしくはアミド化触媒となりうるリン化合物を減らすことで、分子量の増加による溶融粘度上昇を防ぐという考え方に基づくものであるが、通常包装材料等に用いられるポリアミドは反応モル比を極力1に近づけなければ十分な重合度を有する材料が得られないことから、この方法では事実上ポリアミド中のリン原子濃度を低く抑えるということが必須となる。このような状況でポリアミドを得ようとすると、重合工程において十分な分子量を得るための反応時間が長くなったり、重合系内のリン化合物が少ないことからポリマーの酸化が進み、得られるポリアミドは黄色度が高いものであったり、ゲルが多いものになってしまうため、結果としてこの方法によって得られる包装材料等の製品の商品価値は低いものであった。 However, when a polyamide containing a metaxylylene group and another polyamide are melt-mixed, an increase in melt viscosity far exceeding the arithmetic average may occur. As a method of preventing this phenomenon, the concentration difference between the terminal carboxyl group and terminal amino group of the polyamide resin composition after melt mixing has a specific relationship with the concentration of phosphorus atoms contained in the polyamide composition after melt mixing. A method of selecting a polyamide to be used for the above has been proposed (for example, see Patent Document 5). In this method, in order to prevent amidation from proceeding in the molten state, the molecular weight is increased by setting the balance of the end groups of the polyamide so that one is excessive or by reducing the number of phosphorus compounds that can serve as amidation catalysts. This method is based on the idea of preventing an increase in melt viscosity due to the fact that the polyamide usually used for packaging materials or the like cannot obtain a material having a sufficient degree of polymerization unless the reaction molar ratio is as close to 1 as possible. Therefore, it is essential to keep the phosphorus atom concentration in the polyamide low. When trying to obtain a polyamide in such a situation, the reaction time for obtaining a sufficient molecular weight in the polymerization process becomes long, or the oxidation of the polymer proceeds because there are few phosphorus compounds in the polymerization system, and the resulting polyamide is yellow As a result, the product value of products such as packaging materials obtained by this method is low.
本発明者が種々検討を行った中で、メタキシリレン基を含有するポリアミドと他のポリアミドの溶融混合物の溶融粘度は、原料それぞれの溶融粘度、リン原子濃度、末端基濃度差が同じであっても、組成物を構成するメタキシリレン基を含有するポリアミドの製造履歴や保管状態、保管期間等によって、混合物の溶融粘度が異なる場合があることを認めた。これについては特許文献5はもとより、どの文献にも一切記載されていないことであると同時に、押出加工安定性の観点からも解決すべき課題であると言える。
本発明の目的は、上記課題を解決し、メタキシリレン基を含有するポリアミドと他のポリアミドを溶融混合して得られるもので、色調が良好でありかつ押出加工性の良好なポリアミド樹脂組成物を提供することにある。
Among various studies conducted by the present inventor, the melt viscosity of the polyamide-containing polyamide and other polyamide-containing polyamide melts is the same as the melt viscosity, phosphorus atom concentration, and end group concentration difference of each raw material. It was recognized that the melt viscosity of the mixture may vary depending on the production history, storage state, storage period, etc. of the polyamide containing the metaxylylene group constituting the composition. This is not described in any document as well as Patent Document 5, and at the same time, it can be said that this is a problem to be solved from the viewpoint of extrusion stability.
The object of the present invention is to solve the above-mentioned problems and to obtain a polyamide resin composition having good color tone and good extrudability, which is obtained by melt-mixing a polyamide containing a metaxylylene group and another polyamide. There is to do.
本発明者らは、上記ポリアミド樹脂組成物について鋭意研究を重ねた結果、リン原子含有化合物の存在下で重縮合を行い得られるメタキシリレン基を含有するポリアミドと他のポリアミドを溶融混合する際に、特定量の増粘防止化合物を添加して得たポリアミド樹脂組成物が、溶融粘度の異常な上昇もなく、かつ長時間に渡り安定して成形加工ができ、さらに得られた成形品は着色やゲルの少ない外観良好なものとなることを見出し、本発明を完成するに到った。 As a result of intensive research on the polyamide resin composition, the present inventors have melt-mixed a polyamide containing a metaxylylene group obtained by polycondensation in the presence of a phosphorus atom-containing compound with another polyamide. The polyamide resin composition obtained by adding a specific amount of the thickening prevention compound can be stably molded for a long time without an abnormal increase in melt viscosity. It has been found that the appearance is good with little gel, and the present invention has been completed.
すなわち本発明は、メタキシリレンジアミンを70モル%以上含むジアミン成分とα,ω−直鎖状脂肪族ジカルボン酸を70モル%以上含むジカルボン酸成分をリン原子含有化合物(A)の存在下で溶融重縮合して得られるポリアミド(1)1〜99重量部と、ポリアミド(1)以外のポリアミド(2)99〜1重量部と(ここで、ポリアミド(1)とポリアミド(2)の合計重量は100重量部である)、増粘防止化合物(B)の少なくとも3成分を溶融混合してなるポリアミド樹脂組成物であって、ポリアミド(1)が、ポリアミド(1)中のリン原子濃度が50〜400ppmとなるようにリン原子含有化合物(A)を重縮合系内に添加して得られたものであり、増粘防止化合物(B)のモル数をリン原子含有化合物(A)のモル数で除した値が0.05〜0.5であり、270℃、剪断速度100s−1におけるポリアミド樹脂組成物の溶融粘度が、同条件下におけるポリアミド(1)とポリアミド(2)それぞれの溶融粘度から下式(1)を使用して求められる算術平均値の1.20倍以下であるポリアミド樹脂組成物、ならびに該樹脂組成物からなる層を1層以上積層してなる構造物に関する。
MVA=MV1/(W1/100)+MV2/(W2/100) ・・・(1)
MVA;溶融粘度の算術平均値(Pa・s)
MV1;ポリアミド(1)の溶融粘度(Pa・s)
MV2;ポリアミド(2)の溶融粘度(Pa・s)
W1;ポリアミド樹脂組成物におけるポリアミド(1)の重量比(重量%)
W2;ポリアミド樹脂組成物におけるポリアミド(2)の重量比(重量%)
That is, the present invention provides a diamine component containing 70 mol% or more of metaxylylenediamine and a dicarboxylic acid component containing 70 mol% or more of an α, ω-linear aliphatic dicarboxylic acid in the presence of the phosphorus atom-containing compound (A). 1 to 99 parts by weight of polyamide (1) obtained by melt polycondensation, 99 to 1 part by weight of polyamide (2) other than polyamide (1) (here, the total weight of polyamide (1) and polyamide (2)) Is a polyamide resin composition obtained by melt-mixing at least three components of the thickening prevention compound (B), wherein the polyamide (1) has a phosphorus atom concentration of 50 in the polyamide (1). It was obtained by adding the phosphorus atom-containing compound (A) to the polycondensation system so as to be ˜400 ppm, and the number of moles of the thickening prevention compound (B) was the number of moles of the phosphorus atom-containing compound (A). Divided by The melt viscosity of the polyamide resin composition at 270 ° C. and a shear rate of 100 s −1 is lower than the melt viscosities of the polyamide (1) and the polyamide (2) under the same conditions. The present invention relates to a polyamide resin composition that is not more than 1.20 times the arithmetic average value obtained using formula (1), and a structure obtained by laminating one or more layers made of the resin composition.
MVA = MV1 / (W1 / 100) + MV2 / (W2 / 100) (1)
MVA: arithmetic average value of melt viscosity (Pa · s)
MV1; Polyamide (1) melt viscosity (Pa · s)
MV2: Polyamide (2) melt viscosity (Pa · s)
W1: weight ratio (% by weight) of polyamide (1) in the polyamide resin composition
W2: Weight ratio (% by weight) of polyamide (2) in the polyamide resin composition
本発明のポリアミド樹脂組成物は、色調が良好でゲルが少なく、さらにそれを用いた成形加工において長時間に渡る連続運転を可能としたものであり、ガスバリア材料として各種包装材料に利用できる非常に有用なものであり、その工業的価値は非常に高い。 The polyamide resin composition of the present invention has a good color tone and a small amount of gel, and further enables continuous operation for a long time in molding using the same, and can be used for various packaging materials as a gas barrier material. It is useful and its industrial value is very high.
本発明のポリアミド樹脂組成物を構成するポリアミド(1)は、メタキシリレンジアミンを70モル%以上含むジアミン成分とα,ω−直鎖状脂肪族ジカルボン酸を70モル%以上含むジカルボン酸成分とを溶融重縮合して得られるポリアミドである。 The polyamide (1) constituting the polyamide resin composition of the present invention comprises a diamine component containing 70 mol% or more of metaxylylenediamine and a dicarboxylic acid component containing 70 mol% or more of an α, ω-linear aliphatic dicarboxylic acid. Is a polyamide obtained by melt polycondensation.
ポリアミド(1)を構成するジアミン成分としては、メタキシリレンジアミンが70モル%以上含まれることが好ましく、より好ましくは75モル%以上、さらに好ましくは80モル%以上、特に好ましくは90モル%以上である。ジアミン成分中のメタキシリレンジアミンが70モル%以上であると、それから得られるポリアミドは優れたガスバリア性を発現することができる。メタキシリレンジアミン以外に使用できるジアミンとしては、パラキシリレンジアミン、1,3−ビス(アミノメチル)シクロヘキサン、1,4−ビス(アミノメチル)シクロヘキサン、テトラメチレンジアミン、ヘキサメチレンジアミン、ノナメチレンジアミン、2−メチル−1,5−ペンタンジアミン等が例示できるが、これらに限定されるものではない。 The diamine component constituting the polyamide (1) preferably contains 70 mol% or more of metaxylylenediamine, more preferably 75 mol% or more, still more preferably 80 mol% or more, particularly preferably 90 mol% or more. It is. When the metaxylylenediamine in the diamine component is 70 mol% or more, the polyamide obtained therefrom can exhibit excellent gas barrier properties. Examples of diamines that can be used in addition to metaxylylenediamine include paraxylylenediamine, 1,3-bis (aminomethyl) cyclohexane, 1,4-bis (aminomethyl) cyclohexane, tetramethylenediamine, hexamethylenediamine, and nonamethylenediamine. , 2-methyl-1,5-pentanediamine and the like, but are not limited thereto.
ポリアミド(1)を構成するジカルボン酸成分としては、α,ω−直鎖状脂肪族ジカルボン酸が70モル%以上含まれることが好ましく、より好ましくは75モル%以上、さらに好ましくは80モル%以上、特に好ましくは90モル%以上である。α,ω−直鎖状脂肪族ジカルボン酸が70モル%以上であると、ガスバリア性の低下や結晶性の過度の低下を避けることができる。α,ω−直鎖状脂肪族ジカルボン酸としては、炭素数4〜20のα,ω−直鎖状脂肪族ジカルボン酸のうち1種以上が好ましく使用され、特に好ましくはアジピン酸である。その他セバシン酸、スベリン酸、アゼライン酸、ウンデカンジカルボン酸、ウンデカン二酸、ダイマー酸等の脂肪族ジカルボン酸、1,4−シクロヘキサンジカルボン酸等の脂環族ジカルボン酸、テレフタル酸、イソフタル酸、オルソフタル酸、キシリレンジカルボン酸、ナフタレンジカルボン酸などの芳香族ジカルボン酸等が例示できるが、これらに限定されるものではない。 The dicarboxylic acid component constituting the polyamide (1) preferably contains α, ω-linear aliphatic dicarboxylic acid in an amount of 70 mol% or more, more preferably 75 mol% or more, and further preferably 80 mol% or more. Especially preferably, it is 90 mol% or more. When the α, ω-linear aliphatic dicarboxylic acid is 70 mol% or more, it is possible to avoid a decrease in gas barrier properties and an excessive decrease in crystallinity. As the α, ω-linear aliphatic dicarboxylic acid, one or more of α, ω-linear aliphatic dicarboxylic acids having 4 to 20 carbon atoms are preferably used, and adipic acid is particularly preferable. Other sebacic acid, suberic acid, azelaic acid, undecane dicarboxylic acid, undecanedioic acid, dimer acid and other aliphatic dicarboxylic acids, 1,4-cyclohexanedicarboxylic acid and other alicyclic dicarboxylic acids, terephthalic acid, isophthalic acid, orthophthalic acid Aromatic dicarboxylic acids such as xylylene dicarboxylic acid and naphthalene dicarboxylic acid can be exemplified, but are not limited thereto.
前記のジアミン成分、ジカルボン酸成分以外にも、ポリアミド(1)を構成する成分として、本発明の効果を損なわない範囲でε−カプロラクタムやラウロラクタム等のラクタム類、アミノカプロン酸、アミノウンデカン酸等の脂肪族アミノカルボン酸類、パラ−アミノメチル安息香酸のような芳香族アミノカルボン酸等も共重合成分として使用できる。 In addition to the above diamine component and dicarboxylic acid component, as a component constituting the polyamide (1), lactams such as ε-caprolactam and laurolactam, aminocaproic acid, aminoundecanoic acid and the like as long as the effects of the present invention are not impaired. Aliphatic aminocarboxylic acids, aromatic aminocarboxylic acids such as para-aminomethylbenzoic acid, and the like can also be used as copolymerization components.
ポリアミド(1)は、リン原子含有化合物(A)の存在下において溶融重縮合(溶融重合)法により製造される。溶融重縮合法としては、例えばジアミン成分とジカルボン酸成分からなるナイロン塩を水の存在下に、加圧下で昇温し、加えた水および縮合水を除きながら溶融状態で重合させる方法がある。また、ジアミン成分を溶融状態のジカルボン酸成分に直接加えて、重縮合する方法によっても製造される。この場合、反応系を均一な液状状態に保つために、ジアミン成分をジカルボン酸成分に連続的に加え、その間、反応温度が生成するオリゴアミドおよびポリアミドの融点よりも下回らないように反応系を昇温しつつ、重縮合が進められる。 The polyamide (1) is produced by a melt polycondensation (melt polymerization) method in the presence of the phosphorus atom-containing compound (A). As the melt polycondensation method, for example, there is a method in which a nylon salt composed of a diamine component and a dicarboxylic acid component is heated in the presence of water under pressure, and polymerized in a molten state while removing added water and condensed water. It can also be produced by a method in which a diamine component is directly added to a molten dicarboxylic acid component and polycondensed. In this case, in order to keep the reaction system in a uniform liquid state, the diamine component is continuously added to the dicarboxylic acid component, and the reaction system is heated up so that the reaction temperature does not fall below the melting point of the generated oligoamide and polyamide. However, polycondensation proceeds.
ポリアミド(1)の重縮合系内に添加されるリン原子含有化合物(A)としては、ジメチルホスフィン酸、フェニルメチルホスフィン酸、次亜リン酸、次亜リン酸ナトリウム、次亜リン酸カリウム、次亜リン酸リチウム、次亜リン酸エチル、フェニル亜ホスホン酸、フェニル亜ホスホン酸ナトリウム、フェニル亜ホスホン酸カリウム、フェニル亜ホスホン酸リチウム、フェニル亜ホスホン酸エチル、フェニルホスホン酸、エチルホスホン酸、フェニルホスホン酸ナトリウム、フェニルホスホン酸カリウム、フェニルホスホン酸リチウム、フェニルホスホン酸ジエチル、エチルホスホン酸ナトリウム、エチルホスホン酸カリウム、亜リン酸、亜リン酸水素ナトリウム、亜リン酸ナトリウム、亜リン酸トリエチル、亜リン酸トリフェニル、ピロ亜リン酸等が挙げられ、これらの中でも特に次亜リン酸ナトリウム、次亜リン酸カリウム、次亜リン酸リチウム等の次亜リン酸金属塩がアミド化反応を促進する効果が高く、かつ着色防止効果にも優れるため好ましく用いられ、特に次亜リン酸ナトリウムが好ましい。本発明で使用できるリン原子含有化合物(A)はこれらの化合物に限定されない。 Examples of the phosphorus atom-containing compound (A) added to the polycondensation system of the polyamide (1) include dimethylphosphinic acid, phenylmethylphosphinic acid, hypophosphorous acid, sodium hypophosphite, potassium hypophosphite, Lithium phosphite, ethyl hypophosphite, phenylphosphonic acid, sodium phenylphosphonite, potassium phenylphosphonite, lithium phenylphosphonite, ethyl phenylphosphonite, phenylphosphonic acid, ethylphosphonic acid, phenylphosphone Sodium phosphate, potassium phenylphosphonate, lithium phenylphosphonate, diethyl phenylphosphonate, sodium ethylphosphonate, potassium ethylphosphonate, phosphorous acid, sodium hydrogen phosphite, sodium phosphite, triethyl phosphite, phosphorus phosphite Triphenyl acid, pyro-a Among these, metal hypophosphite such as sodium hypophosphite, potassium hypophosphite, and lithium hypophosphite is particularly effective in promoting the amidation reaction and prevents coloration. It is preferably used because of its excellent effect, and sodium hypophosphite is particularly preferred. The phosphorus atom-containing compound (A) that can be used in the present invention is not limited to these compounds.
ポリアミド(1)の重縮合系内に添加するリン原子含有化合物(A)の添加量は、ポリアミド(1)中のリン原子濃度換算で50〜400ppmであることが好ましく、より好ましくは60〜350ppmであり、さらに好ましくは70〜300ppmである。50ppmを下回る場合、重合中にポリアミドが着色する傾向にあり好ましくない。また400ppmを超える場合、ポリアミドのゲル化反応が促進される場合があり、成形品の外観が悪化する傾向があるため好ましくない。 The addition amount of the phosphorus atom-containing compound (A) added in the polycondensation system of the polyamide (1) is preferably 50 to 400 ppm, more preferably 60 to 350 ppm in terms of the phosphorus atom concentration in the polyamide (1). More preferably, it is 70-300 ppm. If it is less than 50 ppm, the polyamide tends to be colored during the polymerization, which is not preferable. On the other hand, if it exceeds 400 ppm, the gelation reaction of polyamide may be accelerated, and the appearance of the molded product tends to deteriorate, which is not preferable.
また、ポリアミド(1)の重縮合系内には、リン原子含有化合物(A)と併用してアルカリ金属化合物(C)を添加することが好ましい。重縮合中のポリアミドの着色を防止するためにはリン原子含有化合物(A)を十分な量存在させる必要があるが、場合によってはポリアミドのゲル化を招く恐れがあるため、アミド化反応速度を調整するためにもアルカリ金属化合物(C)を共存させることが好ましい。アルカリ金属化合物(C)としては、アルカリ金属水酸化物やアルカリ金属酢酸塩が好ましい。
本発明で用いることのできるアルカリ金属化合物(C)としては、水酸化リチウム、水酸化ナトリウム、水酸化カリウム、水酸化ルビジウム、水酸化セシウム、酢酸リチウム、酢酸ナトリウム、酢酸カリウム、酢酸ルビジウム、酢酸セシウム等が挙げられるが、これらの化合物に限定されることなく用いることができる。
Further, it is preferable to add the alkali metal compound (C) in combination with the phosphorus atom-containing compound (A) in the polycondensation system of the polyamide (1). In order to prevent the polyamide from being colored during the polycondensation, a sufficient amount of the phosphorus atom-containing compound (A) needs to be present, but in some cases, the gelation of the polyamide may be caused. In order to adjust, it is preferable to allow the alkali metal compound (C) to coexist. As the alkali metal compound (C), an alkali metal hydroxide or an alkali metal acetate is preferable.
Examples of the alkali metal compound (C) that can be used in the present invention include lithium hydroxide, sodium hydroxide, potassium hydroxide, rubidium hydroxide, cesium hydroxide, lithium acetate, sodium acetate, potassium acetate, rubidium acetate, cesium acetate. However, it can be used without being limited to these compounds.
ポリアミド(1)の重縮合系内にアルカリ金属化合物(C)を添加する場合、該化合物のモル数をリン原子含有化合物(A)のモル数で除した値が0.5〜1となるようにすることが好ましく、より好ましくは0.55〜0.95であり、さらに好ましくは0.6〜0.9である。上記範囲内であると、リン原子含有化合物のアミド化反応促進を抑制する効果が適度であり、従って、抑制し過ぎによる重縮合反応速度が低下し、ポリアミドの熱履歴が増加してポリアミドのゲル化が増大することを避けることができる。 When the alkali metal compound (C) is added to the polycondensation system of the polyamide (1), the value obtained by dividing the number of moles of the compound by the number of moles of the phosphorus atom-containing compound (A) is 0.5 to 1. Preferably, it is 0.55 to 0.95, more preferably 0.6 to 0.9. Within the above range, the effect of suppressing the acceleration of the amidation reaction of the phosphorus atom-containing compound is moderate. Therefore, the polycondensation reaction rate due to excessive suppression decreases, the thermal history of the polyamide increases, and the polyamide gel increases. An increase in crystallization can be avoided.
溶融重縮合で得られたポリアミド(1)は一旦取り出され、ペレット化された後、乾燥して使用される。また更に重合度を高めるために固相重合しても良い。乾燥乃至固相重合で用いられる加熱装置としては、連続式の加熱乾燥装置やタンブルドライヤー、コニカルドライヤー、ロータリードライヤー等と称される回転ドラム式の加熱装置およびナウタミキサーと称される内部に回転翼を備えた円錐型の加熱装置が好適に使用できるが、これらに限定されることなく公知の方法、装置を使用することができる。特にポリアミドの固相重合を行う場合は、上述の装置の中で回分式加熱装置が、系内を密閉化でき、着色の原因となる酸素を除去した状態で重縮合を進めやすいことから好ましく用いられる。 The polyamide (1) obtained by melt polycondensation is once taken out, pelletized, and dried before use. In order to further increase the degree of polymerization, solid phase polymerization may be performed. As a heating device used in drying or solid phase polymerization, a continuous heating drying device, a rotary drum type heating device called a tumble dryer, a conical dryer, a rotary dryer or the like, and a rotating blade inside a nauta mixer are used. Although a conical heating apparatus provided with can be used suitably, a well-known method and apparatus can be used without being limited to these. Particularly in the case of solid-phase polymerization of polyamide, a batch heating apparatus is preferably used because it can seal the inside of the system and easily proceed with polycondensation in a state where oxygen causing coloring is removed. It is done.
上述の工程を経て得られるポリアミド(1)は着色やゲルが少ないものであるが、本発明では上述の工程を経て得られたポリアミドのうち、JIS−K−7105の色差試験におけるb*値が3以下のものが好ましく用いられ、特に好ましくは2以下のものであり、さらに好ましくは1以下のものである。ポリアミドのb*値が3を超えるものは、後加工によって得られる成形品の黄色味強いものとなり、その商品価値が低下するため好ましくない。 The polyamide (1) obtained through the above-mentioned steps has little coloring and gel, but in the present invention, among the polyamides obtained through the above-mentioned steps, the b * value in the color difference test of JIS-K-7105 is Those of 3 or less are preferably used, particularly preferably 2 or less, and more preferably 1 or less. A polyamide having a b * value exceeding 3 is not preferable because the molded product obtained by post-processing has a strong yellowish color and its commercial value is lowered.
ポリアミド(1)の重合度の指標としてはいくつかあるが、相対粘度は一般的に使われるものである。ポリアミド(1)において好ましい相対粘度は1.5〜4.2であり、より好ましくは1.7〜4.0、さらに好ましくは2.0〜3.8である。ポリアミド(1)の相対粘度が1.5以上であると、溶融したポリアミドの流動性が安定で外観が良好な成形品が得られる。またポリアミド(1)の相対粘度が4.2以下であると、ポリアミドの溶融粘度が適度であり成形加工を安定に行うことができる。
尚、ここで言う相対粘度は、ポリアミド1gを96%硫酸100mLに溶解し、キャノンフェンスケ型粘度計にて25℃で測定した落下時間(t)と、同様に測定した96%硫酸そのものの落下時間(t0)の比であり、次式で示される。
相対粘度=t/t0 ・・・(イ)
There are several indices for the degree of polymerization of the polyamide (1), but the relative viscosity is generally used. In the polyamide (1), the preferred relative viscosity is 1.5 to 4.2, more preferably 1.7 to 4.0, and still more preferably 2.0 to 3.8. When the relative viscosity of the polyamide (1) is 1.5 or more, a molded product having a stable fluidity and a good appearance can be obtained. Further, when the relative viscosity of the polyamide (1) is 4.2 or less, the melt viscosity of the polyamide is appropriate and the molding process can be performed stably.
The relative viscosity here refers to the drop time (t) measured by dissolving 1 g of polyamide in 100 mL of 96% sulfuric acid at 25 ° C. using a Canon Fenske viscometer, and the drop of 96% sulfuric acid itself measured in the same manner. It is the ratio of time (t0) and is given by the following equation.
Relative viscosity = t / t0 (A)
ポリアミド(1)には、本発明の効果を損なわない範囲で艶消剤、耐熱安定剤、耐候安定剤、紫外線吸収剤、核剤、可塑剤、難燃剤、帯電防止剤、着色防止剤、ゲル化防止剤等の添加剤、末端封止のための各種有機化合物、層状珪酸塩等のクレイやナノフィラー等を加えることもできるが、以上に示したものに限定されることなく、種々の材料を重合系内または重合後に混合しても良い。 The polyamide (1) includes a matting agent, a heat stabilizer, a weather stabilizer, a UV absorber, a nucleating agent, a plasticizer, a flame retardant, an antistatic agent, an anti-coloring agent and a gel as long as the effects of the present invention are not impaired. Additives such as antioxidants, various organic compounds for end-capping, clays such as layered silicates, nanofillers, etc. can be added, but not limited to those shown above, various materials May be mixed in the polymerization system or after the polymerization.
本発明のポリアミド樹脂組成物を構成するポリアミド(2)は、様々な包装材料に適した性質とするために利用される。ポリアミド(2)としては、メタキシリレンジアミン単位を含まないポリアミドを使用することが、ポリアミド(1)との混合に使用するという目的から好ましい。例えば、ナイロン6、ナイロン66、ナイロン666、ナイロン46、ナイロン610、ナイロン612等の脂肪族ポリアミドや、ナイロン6T、ナイロン6IT、ナイロン9T等の半芳香族ポリアミド、更にこれらに対してコモノマーを使用した共重合物、各種添加剤を添加したもの等、種々のポリアミドを例示することができ、目的に応じて選択することができる。またポリアミド(2)としては、上述のうち1種類でも良いし、目的に応じて2種類以上を混合したものでも良い。
目的に応じた混合例を挙げると、例えば柔軟性を要求する場合、ナイロン6やナイロン666を使用することが好ましい。またポリアミド(1)の結晶化速度を速めるためにはナイロン6やナイロン66の様な結晶性のポリアミド、逆に遅くするためにはナイロン6ITの様な非晶性乃至難晶性のポリアミドを混合する方法が挙げられる。
The polyamide (2) that constitutes the polyamide resin composition of the present invention is used to make the properties suitable for various packaging materials. As the polyamide (2), it is preferable to use a polyamide that does not contain a metaxylylenediamine unit for the purpose of being used for mixing with the polyamide (1). For example, Nylon 6, Nylon 66, Nylon 666, Nylon 46, Nylon 610, Nylon 612 and other aliphatic polyamides, Nylon 6T, Nylon 6IT, Nylon 9T and other semi-aromatic polyamides, and comonomer were used for these. Various polyamides, such as a copolymer and what added various additives, can be illustrated and can be selected according to the objective. Moreover, as polyamide (2), one type may be sufficient among the above-mentioned, and what mixed 2 or more types according to the objective may be used.
When the example of mixing according to the purpose is given, for example, when flexibility is required, it is preferable to use nylon 6 or nylon 666. In order to increase the crystallization speed of the polyamide (1), a crystalline polyamide such as nylon 6 or nylon 66 is mixed, and on the contrary, an amorphous or hardly crystalline polyamide such as nylon 6IT is mixed. The method of doing is mentioned.
ポリアミド(2)は、溶融重縮合(溶融重合)法により製造される。ポリアミド(2)の重縮合においてもアミド化反応速度を高めるためにリン原子含有化合物(A)を添加しても良い。また更に重合度を高めるためにポリアミド(1)と同様にして固相重合しても良い。 The polyamide (2) is produced by a melt polycondensation (melt polymerization) method. In the polycondensation of the polyamide (2), the phosphorus atom-containing compound (A) may be added in order to increase the amidation reaction rate. In order to further increase the degree of polymerization, solid phase polymerization may be performed in the same manner as in the polyamide (1).
ポリアミド(2)の重合度については、ポリアミド(1)と溶融混合する際の温度における溶融粘度を指標として選択することが好ましい。ポリアミド(1)とポリアミド(2)を溶融混合した場合、そのモルホロジーは海島構造を形成するが、島部分の分散粒子径が小さい程、得られる組成物の特性は優れたものとなる傾向がある。具体的には、ポリアミド(1)とポリアミド(2)を溶融混合する際、多量成分の溶融粘度が少量成分の溶融粘度よりも高くなるように選択することが好ましく、より好ましくは多量成分の溶融粘度が少量成分の溶融粘度よりも1.2倍以上、さらに好ましくは1.5倍以上になるように選択する。 The degree of polymerization of the polyamide (2) is preferably selected using as an index the melt viscosity at the temperature when melt mixed with the polyamide (1). When the polyamide (1) and the polyamide (2) are melt-mixed, the morphology forms a sea-island structure, but the smaller the dispersed particle size of the island portion, the better the properties of the resulting composition tend to be. . Specifically, when the polyamide (1) and the polyamide (2) are melt-mixed, it is preferable to select so that the melt viscosity of the major component is higher than the melt viscosity of the minor component, more preferably the melt of the major component. The viscosity is selected to be 1.2 times or more, more preferably 1.5 times or more than the melt viscosity of the minor component.
ポリアミド(2)には、本発明の効果を損なわない範囲で艶消剤、耐熱安定剤、耐候安定剤、紫外線吸収剤、核剤、可塑剤、難燃剤、帯電防止剤、着色防止剤、ゲル化防止剤等の添加剤、末端封止のための各種有機化合物、層状珪酸塩等のクレイやナノフィラー等を加えることもできるが、以上に示したものに限定されることなく、種々の材料を重合系内または重合後に混合しても良い。 The polyamide (2) includes a matting agent, a heat stabilizer, a weather stabilizer, an ultraviolet absorber, a nucleating agent, a plasticizer, a flame retardant, an antistatic agent, an anti-coloring agent and a gel as long as the effects of the present invention are not impaired. Additives such as antioxidants, various organic compounds for end-capping, clays such as layered silicates, nanofillers, etc. can be added, but not limited to those shown above, various materials May be mixed in the polymerization system or after the polymerization.
本発明のポリアミド樹脂組成物において、ポリアミド(1)とポリアミド(2)の混合比率は、ポリアミド(1):ポリアミド(2)=1〜99:99〜1(重量部、合計量は100重量部である)の範囲とすることが好ましく、より好ましくは5〜95:95〜5(重量部)であり、さらに好ましくは10〜90:90〜10(重量部)である。いずれかのポリアミドの配合比率が1重量部を下回ると(あるいは99重量部を超えると)、少量成分の性質が発現しにくくなるため、組成物の性質がほぼ多量成分そのものになり、十分な改質効果が得られない。 In the polyamide resin composition of the present invention, the mixing ratio of polyamide (1) and polyamide (2) is polyamide (1): polyamide (2) = 1 to 99:99 to 1 (parts by weight, total amount is 100 parts by weight) It is preferably within the range of 5 to 95:95 to 5 (parts by weight), and more preferably 10 to 90:90 to 10 (parts by weight). If the blending ratio of any of the polyamides is less than 1 part by weight (or more than 99 parts by weight), the properties of the minor components are difficult to develop. Quality effect cannot be obtained.
本発明のポリアミド樹脂組成物を構成する増粘防止化合物(B)は、ポリアミド(1)とポリアミド(2)の混合物の溶融粘度が算術平均を超えて大きく上昇することを防止する役割を有する。増粘防止化合物(B)を添加しない場合、ポリアミド(1)とポリアミド(2)を溶融混合した際に、算術平均を遙かに超えた高い溶融粘度を示すことがある。溶融粘度が大幅に上昇する原因は定かではないが、ポリアミド樹脂組成物中のリン原子含有化合物(A)の量が非常に少ない場合はこのような現象が見られないことから、リン原子含有化合物(A)のアミド化触媒効果により、ポリアミド(1)とポリアミド(2)の間でアミド交換反応がすすみ、高分子量のポリアミドが生成するためと推定される。 The thickening prevention compound (B) constituting the polyamide resin composition of the present invention has a role of preventing the melt viscosity of the mixture of the polyamide (1) and the polyamide (2) from significantly increasing beyond the arithmetic average. When the thickening prevention compound (B) is not added, when the polyamide (1) and the polyamide (2) are melt-mixed, a high melt viscosity far exceeding the arithmetic average may be exhibited. The cause of the significant increase in melt viscosity is not clear, but when the amount of the phosphorus atom-containing compound (A) in the polyamide resin composition is very small, such a phenomenon is not observed. It is presumed that due to the amidation catalytic effect of (A), an amide exchange reaction proceeds between the polyamide (1) and the polyamide (2), and a high molecular weight polyamide is produced.
増粘防止化合物(B)としては、水酸化リチウム、水酸化ナトリウム、水酸化カリウム、水酸化ルビジウム、水酸化セシウム等の金属水酸化物;酢酸リチウム、酢酸ナトリウム、酢酸カリウム、酢酸ルビジウム、酢酸セシウム等の金属酢酸塩;ナトリウムメトキシド、ナトリウムエトキシド、ナトリウムプロポキシド、ナトリウムブトキシド、カリウムメトキシド、リチウムメトキシド等の金属アルコキシド;炭酸ナトリウム等の金属炭酸塩;脂肪酸、脂肪酸金属塩等の各種脂肪酸系化合物等が挙げられるが、これらに限定されない。 Anti-thickening compounds (B) include metal hydroxides such as lithium hydroxide, sodium hydroxide, potassium hydroxide, rubidium hydroxide, cesium hydroxide; lithium acetate, sodium acetate, potassium acetate, rubidium acetate, cesium acetate Metal alkoxides such as sodium methoxide, sodium ethoxide, sodium propoxide, sodium butoxide, potassium methoxide, lithium methoxide, etc .; metal carbonates such as sodium carbonate; various fatty acids such as fatty acids and fatty acid metal salts Examples of such compounds are not limited to these.
特に本発明では各種脂肪酸系化合物が好ましく用いられ、好ましくは炭素数(C)10以上、より好ましくは10〜50、さらに好ましくは18〜34の脂肪酸系化合物であり、例えば脂肪酸としてはステアリン酸(C18)、エイコ酸(C20)、ベヘン酸(C22)、モンタン酸(C28)、トリアコンタン酸(C30)などの直鎖飽和脂肪酸が挙げられ、さらに脂肪酸と塩を形成する金属としてはナトリウム、カリウム、リチウム、カルシウム、バリウム、マグネシウム、ストロンチウム、アルミニウム、亜鉛等が挙げられるが、特にこれらに限定されるものではない。増粘防止化合物(B)は、上記のうち1種類でもよいし、2種以上を併用してもよい。
なお、前述の脂肪酸金属塩は水酸化物や酢酸塩と比較してハンドリング性に優れ、この中でもステアリン酸金属塩は安価である上、滑剤としての効果を有しており、成形加工をより安定化することができるため好ましい。
In particular, various fatty acid compounds are preferably used in the present invention, preferably fatty acid compounds having 10 or more carbon atoms (C), more preferably 10 to 50, and still more preferably 18 to 34. Linear saturated fatty acids such as C18), eicoic acid (C20), behenic acid (C22), montanic acid (C28), triacontanoic acid (C30), and the metals that form salts with fatty acids are sodium, potassium , Lithium, calcium, barium, magnesium, strontium, aluminum, zinc and the like, but are not particularly limited thereto. One type of the anti-thickening compound (B) may be used, or two or more types may be used in combination.
The above-mentioned fatty acid metal salts are superior in handling properties compared to hydroxides and acetates. Among them, stearic acid metal salts are inexpensive and have an effect as a lubricant, making the molding process more stable. It is preferable because
なお、ポリアミド(1)を製造する際に添加可能なアルカリ金属化合物(C)は増粘防止化合物(B)と同じ化合物も例示されるが、アルカリ金属化合物(C)は重縮合系内でイオン化し、重縮合反応を進めるための脱水工程においてアルカリ金属化合物(C)から生成した負のイオン(例えば−OH−、CH3COO−)が水や酢酸となって、或いは水と共に系外へ流去されてしまうために、ポリアミド(1)中ではアルカリ金属化合物(C)は元の形で存在していないと考えられる。実際に、酢酸ナトリウムをアルカリ金属化合物(C)として重縮合系内に添加しても、増粘防止化合物(B)として添加した場合のようなポリアミド樹脂組成物の溶融粘度増加を抑制する効果は発現しない。 The alkali metal compound (C) that can be added when the polyamide (1) is produced is exemplified by the same compound as the thickening prevention compound (B), but the alkali metal compound (C) is ionized in the polycondensation system. In the dehydration process for proceeding the polycondensation reaction, negative ions (for example, —OH − , CH 3 COO − ) generated from the alkali metal compound (C) flow into the water or acetic acid, or flow out of the system together with water. It is considered that the alkali metal compound (C) does not exist in the original form in the polyamide (1) because it is left behind. Actually, even when sodium acetate is added as an alkali metal compound (C) in the polycondensation system, the effect of suppressing the increase in the melt viscosity of the polyamide resin composition as when added as the thickening prevention compound (B) is Not expressed.
増粘防止化合物(B)は、ポリアミド(1)とポリアミド(2)を溶融混合する際に添加することが好ましい。増粘防止化合物(B)の添加方法は従来公知の方法を用いることができるが、例えば、ポリアミド(1)および/またはポリアミド(2)と増粘防止化合物(B)を乾式混合で混合した後に、成形加工に供する方法や、ポリアミド(1)、ポリアミド(2)またはそれ以外の熱可塑性樹脂に増粘防止化合物(B)を練り込んだマスターバッチとして添加する方法が挙げられる。
ポリアミド(1)および/またはポリアミド(2)と乾式混合する際は、例えば、タンブラーにポリアミド(1)と増粘防止化合物(B)を入れ、回転させることで混合する方法が挙げられる。本発明では増粘防止化合物(B)の形状に特に制限はないが、粉体でかつその粒径が小さい方が乾式混合にて樹脂組成物中に均一に分散させることが容易であるため、その粒径は0.2mm以下が好ましい。また本発明では乾式混合後のポリアミド(1)および/またはポリアミド(2)と増粘防止化合物(B)の分級を防止するために粘性のある液体を展着剤としてポリアミド(1)および/またはポリアミド(2)に付着させた後、増粘防止化合物(B)を添加、混合する方法を採ることもできる。展着剤としては、界面活性剤等が挙げられるが、これに限定されることなく公知のものを使用することができる。
次にマスターバッチとして添加する際は、ポリアミド樹脂組成物の性質を大きく変化させるような性質を持たない熱可塑性樹脂を基材として使用することが好ましいが、特に好ましいのはポリアミド(1)又はポリアミド(2)を基材とすることである。ただし、マスターバッチの配合量がそれほど多くないのであれば、特に限定することなく種々の熱可塑性樹脂の中から選択することができる。
The thickening preventing compound (B) is preferably added when the polyamide (1) and the polyamide (2) are melt-mixed. As a method for adding the thickening prevention compound (B), a conventionally known method can be used. For example, after the polyamide (1) and / or the polyamide (2) and the thickening prevention compound (B) are mixed by dry mixing. And a method of subjecting to a molding process and a method of adding as a master batch in which the thickening prevention compound (B) is kneaded into the polyamide (1), the polyamide (2) or other thermoplastic resin.
When dry-mixing with the polyamide (1) and / or the polyamide (2), for example, there is a method of mixing the polyamide (1) and the thickening prevention compound (B) in a tumbler and rotating them. In the present invention, there is no particular limitation on the shape of the thickening prevention compound (B), but since the powder and the smaller particle size are easier to uniformly disperse in the resin composition by dry mixing, The particle size is preferably 0.2 mm or less. In the present invention, the polyamide (1) and / or the polyamide (1) and / or the polyamide (2) and the thickening prevention compound (B) after dry mixing are prevented by using a viscous liquid as a spreading agent. After making it adhere to a polyamide (2), the method of adding and mixing a thickening prevention compound (B) can also be taken. Examples of the spreading agent include a surfactant and the like, but a known one can be used without being limited thereto.
Next, when adding as a masterbatch, it is preferable to use a thermoplastic resin that does not have properties that greatly change the properties of the polyamide resin composition as the base material, and particularly preferred is polyamide (1) or polyamide. (2) is a base material. However, if there are not so many compounding quantities of a masterbatch, it can select from various thermoplastic resins, without specifically limiting.
増粘防止化合物(B)の添加量は、増粘防止化合物(B)のモル数をポリアミドに添加したリン原子含有化合物(A)のモル数で除した値が0.05〜0.5の範囲内となるようにすることが好ましく、より好ましくは0.07〜0.4であり、さらに好ましくは0.1〜0.3である。0.05を下回る場合、溶融粘度の上昇を十分に抑制することができないことがある。また0.5を超える場合、増粘防止化合物(B)によりポリアミド(1)やポリアミド(2)が成形加工中に加水分解したり、場合によっては着色することがあるため好ましくない。
なお脂肪酸金属塩のような滑剤としての効果を有するものを添加する場合は、上述の添加量の範囲内を考慮した上で、ポリアミド(1)とポリアミド(2)の合計量を100重量部とした場合、増粘防止化合物(B)は0.5重量部以下となるように添加することが好ましく、より好ましくは0.4重量部以下、さらに好ましくは0.3重量部以下である。増粘防止化合物(B)は必要量以上添加すると、ポリアミドペレットが押出機に食い込まなくなり成形不良を起こすことがある。
The addition amount of the thickening prevention compound (B) is a value obtained by dividing the number of moles of the thickening prevention compound (B) by the number of moles of the phosphorus atom-containing compound (A) added to the polyamide is 0.05 to 0.5. It is preferable to be within the range, more preferably 0.07 to 0.4, and still more preferably 0.1 to 0.3. When it is less than 0.05, an increase in melt viscosity may not be sufficiently suppressed. On the other hand, when it exceeds 0.5, the thickening prevention compound (B) is not preferable because the polyamide (1) or the polyamide (2) may be hydrolyzed during the molding process or may be colored in some cases.
In addition, when adding what has the effect as a lubricant like a fatty acid metal salt, after considering the inside of the range of the above-mentioned addition amount, the total amount of polyamide (1) and polyamide (2) is 100 weight part. In this case, the thickening prevention compound (B) is preferably added so as to be 0.5 parts by weight or less, more preferably 0.4 parts by weight or less, and still more preferably 0.3 parts by weight or less. If the thickening prevention compound (B) is added more than the necessary amount, the polyamide pellets may not bite into the extruder and cause molding defects.
ポリアミドに含まれるリン原子含有化合物(A)は前述の通り、ポリアミドの酸化を防止する効果を有しているため、例えば製造後、一定期間保管したポリアミドや大気中に暴露されていたポリアミドを本発明のポリアミド樹脂組成物を構成する材料として使用すると、リン原子濃度や末端基濃度が同じであっても溶融粘度の上昇度が変化することがある。これはリン原子含有化合物(A)が周辺の酸素と反応して化学変化を起こし、アミド化反応に対する触媒効果を失ってしまうため、他のポリアミドと混合された際にアミド交換反応を促進する効果を徐々に失っているためと推測される。しかしながら、本発明のように増粘防止化合物(B)を適当量配合すれば、ポリアミドの保存状態に関わらず、ポリアミド(1)とポリアミド(2)それぞれの溶融粘度から算出される算術平均値に近い溶融粘度を安定して実現することができる。もちろん、増粘防止化合物(B)を配合する本発明の方法によれば、ポリアミド(1)もしくはポリアミド(2)に含まれるリン原子含有化合物の量や、それぞれのポリアミドの末端基濃度による溶融粘度への影響は小さいものであり、ポリアミドの末端基濃度やリン原子濃度を気にすることなく、目的に応じた物性を有するポリアミドを選択してポリアミド樹脂組成物を製造することができる。 As described above, the phosphorus atom-containing compound (A) contained in the polyamide has the effect of preventing the oxidation of the polyamide. For example, the polyamide stored for a certain period after the production or the polyamide exposed to the atmosphere is used. When used as a material constituting the polyamide resin composition of the invention, the degree of increase in melt viscosity may change even when the phosphorus atom concentration and the terminal group concentration are the same. This is because the phosphorus atom-containing compound (A) reacts with the surrounding oxygen to cause a chemical change and loses the catalytic effect on the amidation reaction, so that it promotes the amide exchange reaction when mixed with other polyamides. Is estimated to be gradually lost. However, when an appropriate amount of the thickening prevention compound (B) is blended as in the present invention, the arithmetic average value calculated from the melt viscosity of each of the polyamide (1) and the polyamide (2) is obtained regardless of the storage state of the polyamide. Close melt viscosity can be realized stably. Of course, according to the method of the present invention in which the thickening prevention compound (B) is blended, the amount of the phosphorus atom-containing compound contained in the polyamide (1) or the polyamide (2) and the melt viscosity depending on the end group concentration of each polyamide. The polyamide resin composition can be produced by selecting a polyamide having physical properties according to the purpose without worrying about the end group concentration or phosphorus atom concentration of the polyamide.
本発明のポリアミド樹脂組成物は、270℃、剪断速度100s−1におけるポリアミド樹脂組成物の溶融粘度が、同条件下におけるポリアミド(1)とポリアミド(2)それぞれの溶融粘度から下式(1)を使用して求められる算術平均値の1.20倍以下であることが好ましく、1〜1.15倍であるのがより好ましい。
MVA=MV1/(W1/100)+MV2/(W2/100) ・・・(1)
MVA;溶融粘度の算術平均値(Pa・s)
MV1;ポリアミド(1)の溶融粘度(Pa・s)
MV2;ポリアミド(2)の溶融粘度(Pa・s)
W1;ポリアミド樹脂組成物におけるポリアミド(1)の重量比(重量%)
W2;ポリアミド樹脂組成物におけるポリアミド(2)の重量比(重量%)
In the polyamide resin composition of the present invention, the melt viscosity of the polyamide resin composition at 270 ° C. and a shear rate of 100 s −1 represents the following formula (1) from the melt viscosities of the polyamide (1) and the polyamide (2) under the same conditions. It is preferable that it is 1.20 times or less of the arithmetic mean value calculated | required using, and it is more preferable that it is 1-1.15 times.
MVA = MV1 / (W1 / 100) + MV2 / (W2 / 100) (1)
MVA: arithmetic average value of melt viscosity (Pa · s)
MV1; Polyamide (1) melt viscosity (Pa · s)
MV2: Polyamide (2) melt viscosity (Pa · s)
W1: weight ratio (% by weight) of polyamide (1) in the polyamide resin composition
W2: Weight ratio (% by weight) of polyamide (2) in the polyamide resin composition
本発明のポリアミド樹脂組成物はフィルム、シート、ボトル等の各種包装材料はもちろん、モノフィラメント、成形材料等様々なものに使用することができる。また包装材料を形成する際には他の熱可塑性樹脂材料や金属箔、板紙等と組み合わせて使用することができ、さらに必要に応じて本発明のポリアミド樹脂組成物に対してさらに他の熱可塑性樹脂を溶融混合して使用することもできる。 The polyamide resin composition of the present invention can be used for various materials such as monofilaments and molding materials as well as various packaging materials such as films, sheets and bottles. Further, when forming a packaging material, it can be used in combination with other thermoplastic resin materials, metal foil, paperboard, etc., and further, if necessary, further thermoplastic resin for the polyamide resin composition of the present invention. It is also possible to melt and mix the resin.
以下実施例及び比較例により、本発明を更に詳細に説明するが本発明はこれら実施例に限定されるものではない。なお、本実施例において各種測定は以下の方法により行った。
(1)ポリアミドの相対粘度
ポリアミド1gを精秤し、96%硫酸100mlに20〜30℃で攪拌溶解した。完全に溶解した後、速やかにキャノンフェンスケ型粘度計に溶液5mlを取り、25℃の恒温漕中で10分間放置後、落下速度(t)を測定した。また、96%硫酸そのものの落下速度(t0)も同様に測定した。tおよびt0から次式(イ)により相対粘度を算出した。
相対粘度=t/t0 ・・・(イ)
(2)ポリアミドペレットのb*値
JIS−K−7105に準じて、反射法によりb*値を測定した。b*値が高い値を示すほど、黄色く着色しているものと判断される。b*値の測定装置は、日本電色工業社製の色差測定装置(型式:Z−Σ80 Color Measuring System)を使用した。
(3)各ポリアミドの溶融粘度
東洋精機製作所製キャピログラフ1−Dを使用し、直径1mm、長さ10mmのキャピラリをセットして、260℃、溶融保持時間5分乃至15分の条件において溶融粘度を測定した。
Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples, but the present invention is not limited to these Examples. In this example, various measurements were performed by the following methods.
(1) Relative viscosity of polyamide 1 g of polyamide was precisely weighed and stirred and dissolved in 100 ml of 96% sulfuric acid at 20 to 30 ° C. After completely dissolving, 5 ml of the solution was quickly taken into a Cannon-Fenceke viscometer, and left for 10 minutes in a constant temperature bath at 25 ° C., and then the dropping speed (t) was measured. Further, the dropping rate (t0) of 96% sulfuric acid itself was measured in the same manner. The relative viscosity was calculated from t and t0 according to the following formula (A).
Relative viscosity = t / t0 (A)
(2) b * value of polyamide pellets The b * value was measured by a reflection method according to JIS-K-7105. The higher the b * value, the more yellow the color is judged. As a b * value measuring apparatus, a color difference measuring apparatus (model: Z-Σ80 Color Measuring System) manufactured by Nippon Denshoku Industries Co., Ltd. was used.
(3) Melt viscosity of each polyamide Using Capillograph 1-D manufactured by Toyo Seiki Seisakusho, a capillary with a diameter of 1 mm and a length of 10 mm was set, and the melt viscosity was adjusted under the conditions of 260 ° C. and a melt holding time of 5 to 15 minutes. It was measured.
<実施例1>
(ポリアミドの溶融重合)
攪拌機、分縮器、全縮器、温度計、滴下ロート及び窒素導入管、ストランドダイを備えた内容積50リットルの反応容器に、精秤したアジピン酸15000g(102.6mol)、次亜リン酸ナトリウム5.174g(0.0488mol)、酢酸ナトリウム2.803g(0.0342mol)を入れ、十分に窒素置換した後、さらに少量の窒素気流下で系内を攪拌しながら170℃まで加熱した。これにメタキシリレンジアミン13974g(102.6mol)を攪拌下に滴下し、生成する縮合水を系外へ除きながら系内を連続的に昇温した。メタキシリレンジアミンの滴下終了後、内温を260℃として40分反応を継続した。その後、系内を窒素で加圧し、ストランドダイからポリマーを取り出してこれをペレット化し、約24kgのポリアミドを得た。
(ポリアミドの固相重合)
窒素ガス導入管、真空ライン、真空ポンプ、内温測定用の熱電対を設けたジャケット付きのタンブルドライヤーに前記ポリアミドを仕込み、一定速度で回転させつつ、タンブルドライヤー内部を純度が99容量%以上の窒素ガスで十分に置換した後、同窒素ガス気流下でタンブルドライヤーを加熱し、約150分かけてペレット温度を150℃に昇温した。ペレット温度が150℃に達した時点で系内の圧力を1torr以下に減圧した。さらに昇温を続け、約70分かけてペレット温度を200℃まで昇温した後、200℃で30分保持した。次いで、系内に純度が99容量%以上の窒素ガスを導入して、タンブルドライヤーを回転させたまま冷却して相対粘度が2.6のポリアミド1を得た。得られたポリアミド1のb*値は1.1であった。また、ポリアミド1の溶融粘度を表1に示す。
(ポリアミド樹脂組成物の調製)
20kgのポリアミド1に対して、ステアリン酸カルシウム3.9g(0.0065mol)を加え、タンブラーで10分間撹拌混合した。次いで、この混合物30重量部と、70重量部のナイロン6(宇部興産製、グレード:1030B、溶融粘度を表1に示す)からなる混合ペレットを、タンブラーを使用して撹拌混合した。次に、30mmφ単軸押出機を使用して、260℃にて前記混合物を溶融混練し、混合ペレット−1を作製した。次いで混合ペレットを減圧乾燥し、水分を0.03%に調整し、ポリアミド樹脂組成物を得た。ポリアミド1とナイロン6の溶融粘度の算術平均値と、ポリアミド樹脂組成物の溶融粘度(実測値)を表2に示す。
<Example 1>
(Polymer melt polymerization)
15000 g (102.6 mol) of adipic acid weighed precisely in a reaction vessel having an internal volume of 50 liters equipped with a stirrer, a partial condenser, a full condenser, a thermometer, a dropping funnel and a nitrogen introduction tube, and a strand die, hypophosphorous acid 5.174 g (0.0488 mol) of sodium and 2.803 g (0.0342 mol) of sodium acetate were added, and after sufficient nitrogen substitution, the system was heated to 170 ° C. with stirring in a small amount of nitrogen stream. To this was added 13974 g (102.6 mol) of metaxylylenediamine under stirring, and the inside of the system was continuously heated while removing the condensed water produced. After completion of the dropwise addition of metaxylylenediamine, the internal temperature was 260 ° C. and the reaction was continued for 40 minutes. Thereafter, the inside of the system was pressurized with nitrogen, and the polymer was taken out from the strand die and pelletized to obtain about 24 kg of polyamide.
(Polyamide solid phase polymerization)
The polyamide is charged into a tumble dryer with a jacket provided with a nitrogen gas introduction tube, a vacuum line, a vacuum pump, and a thermocouple for measuring the internal temperature, and the purity inside the tumble dryer is 99 volume% or more while rotating at a constant speed. After sufficiently replacing with nitrogen gas, the tumble dryer was heated under the same nitrogen gas stream, and the pellet temperature was raised to 150 ° C. over about 150 minutes. When the pellet temperature reached 150 ° C., the pressure in the system was reduced to 1 torr or less. The temperature was further raised, and the pellet temperature was raised to 200 ° C. over about 70 minutes, and then held at 200 ° C. for 30 minutes. Next, nitrogen gas having a purity of 99% by volume or more was introduced into the system, and the tumble dryer was rotated while being cooled to obtain polyamide 1 having a relative viscosity of 2.6. The obtained polyamide 1 had a b * value of 1.1. Table 1 shows the melt viscosity of polyamide 1.
(Preparation of polyamide resin composition)
To 20 kg of polyamide 1, 3.9 g (0.0065 mol) of calcium stearate was added and stirred and mixed with a tumbler for 10 minutes. Subsequently, 30 parts by weight of this mixture and 70 parts by weight of nylon 6 (manufactured by Ube Industries, grade: 1030B, melt viscosity is shown in Table 1) were stirred and mixed using a tumbler. Next, using a 30 mmφ single screw extruder, the mixture was melt-kneaded at 260 ° C. to prepare mixed pellet-1. Subsequently, the mixed pellet was dried under reduced pressure, the water content was adjusted to 0.03%, and a polyamide resin composition was obtained. Table 2 shows the arithmetic average value of the melt viscosity of polyamide 1 and nylon 6 and the melt viscosity (measured value) of the polyamide resin composition.
<実施例2>
次亜リン酸ナトリウムを12.953g(0.1220mol)、酢酸ナトリウムを7.008g(0.0854mol)とした以外は実施例1と同様にして溶融重合と固相重合を行って相対粘度が2.6、b*値が−2.0のポリアミド2を得た。なお、ペレット温度を200℃で保持した時間は20分であった。ポリアミド2の溶融粘度を表1に示す。
次いで、20kgのポリアミド2に対して、ステアリン酸カルシウム7.6g(0.0126mol)を加え、タンブラーで10分間撹拌混合した。この混合物30重量部と、70重量部のナイロン6(宇部興産製、グレード:1030B)からなる混合ペレットを、タンブラーを使用して撹拌混合した。次に、30mmφ単軸押出機を使用して、260℃にて前記混合物を溶融混練し、混合ペレット−1を作製した。次いで混合ペレットを減圧乾燥し、水分を0.03%に調整し、ポリアミド樹脂組成物を得た。結果を表2に示す。
<Example 2>
Except for using sodium hypophosphite at 12.953 g (0.1220 mol) and sodium acetate at 7.008 g (0.0854 mol), melt polymerization and solid phase polymerization were carried out in the same manner as in Example 1 to obtain a relative viscosity of 2 .6, and a polyamide 2 having a b * value of −2.0 was obtained. In addition, the time which hold | maintained pellet temperature at 200 degreeC was 20 minutes. The melt viscosity of polyamide 2 is shown in Table 1.
Next, 7.6 g (0.0126 mol) of calcium stearate was added to 20 kg of polyamide 2, and the mixture was stirred and mixed with a tumbler for 10 minutes. A mixed pellet composed of 30 parts by weight of this mixture and 70 parts by weight of nylon 6 (manufactured by Ube Industries, grade: 1030B) was stirred and mixed using a tumbler. Next, using a 30 mmφ single screw extruder, the mixture was melt-kneaded at 260 ° C. to prepare mixed pellet-1. Subsequently, the mixed pellet was dried under reduced pressure, the water content was adjusted to 0.03%, and a polyamide resin composition was obtained. The results are shown in Table 2.
<比較例1>
30重量部のポリアミド1と、70重量部のナイロン6(宇部興産製、グレード:1030B)からなる混合ペレットを、タンブラーを使用して撹拌混合した。次に、30mmφ単軸押出機を使用して、260℃にて前記混合物を溶融混練し、混合ペレット−1を作製した。次いで混合ペレットを減圧乾燥し、水分を0.03%に調整し、ポリアミド樹脂組成物を得た。結果を表2に示す。
<Comparative Example 1>
A mixed pellet composed of 30 parts by weight of polyamide 1 and 70 parts by weight of nylon 6 (manufactured by Ube Industries, grade: 1030B) was stirred and mixed using a tumbler. Next, using a 30 mmφ single screw extruder, the mixture was melt-kneaded at 260 ° C. to prepare mixed pellet-1. Subsequently, the mixed pellet was dried under reduced pressure, the water content was adjusted to 0.03%, and a polyamide resin composition was obtained. The results are shown in Table 2.
<比較例2>
ステアリン酸カルシウムを1.8g(0.0029mol)を加えたこと以外は実施例2と同様にしてポリアミド樹脂組成物を得た。結果を表2に示す。
<Comparative example 2>
A polyamide resin composition was obtained in the same manner as in Example 2 except that 1.8 g (0.0029 mol) of calcium stearate was added. The results are shown in Table 2.
Claims (9)
MVA=MV1/(W1/100)+MV2/(W2/100) ・・・(1)
MVA;溶融粘度の算術平均値(Pa・s)
MV1;ポリアミド(1)の溶融粘度(Pa・s)
MV2;ポリアミド(2)の溶融粘度(Pa・s)
W1;ポリアミド樹脂組成物におけるポリアミド(1)の重量比(重量%)
W2;ポリアミド樹脂組成物におけるポリアミド(2)の重量比(重量%) A diamine component containing 70 mol% or more of metaxylylenediamine and a dicarboxylic acid component containing 70 mol% or more of an α, ω-linear aliphatic dicarboxylic acid are melt polycondensed in the presence of the phosphorus atom-containing compound (A). 1 to 99 parts by weight of the obtained polyamide (1), 99 to 1 part by weight of the polyamide (2) other than the polyamide (1) (here, the total weight of the polyamide (1) and the polyamide (2) is 100 parts by weight) A polyamide resin composition obtained by melt-mixing at least three components of the thickening prevention compound (B) so that the polyamide (1) has a phosphorus atom concentration of 50 to 400 ppm in the polyamide (1). The phosphorus atom-containing compound (A) was added to the polycondensation system, and the value obtained by dividing the number of moles of the thickening prevention compound (B) by the number of moles of the phosphorus atom-containing compound (A) was 0.05 ~ The melt viscosity of the polyamide resin composition at 270 ° C. and a shear rate of 100 s −1 is 0.5, and the following formula (1) is used from the melt viscosities of the polyamide (1) and the polyamide (2) under the same conditions. The polyamide resin composition which is 1.20 times or less of the arithmetic average value obtained by the above.
MVA = MV1 / (W1 / 100) + MV2 / (W2 / 100) (1)
MVA: arithmetic average value of melt viscosity (Pa · s)
MV1; Polyamide (1) melt viscosity (Pa · s)
MV2: Polyamide (2) melt viscosity (Pa · s)
W1: weight ratio (% by weight) of polyamide (1) in the polyamide resin composition
W2: Weight ratio (% by weight) of polyamide (2) in the polyamide resin composition