JP2008291205A - Rubber composition for belt, rubber belt, and toothed belt for driving motorcycle - Google Patents
Rubber composition for belt, rubber belt, and toothed belt for driving motorcycle Download PDFInfo
- Publication number
- JP2008291205A JP2008291205A JP2007296038A JP2007296038A JP2008291205A JP 2008291205 A JP2008291205 A JP 2008291205A JP 2007296038 A JP2007296038 A JP 2007296038A JP 2007296038 A JP2007296038 A JP 2007296038A JP 2008291205 A JP2008291205 A JP 2008291205A
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- belt
- mass
- parts
- hydrogenated nitrile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、ベルト用ゴム組成物及びゴムベルトに係り、詳しくは不飽和カルボン酸金属塩を含有した水素化ニトリルゴムを用いたベルトにおいて硬度を上げると共に圧延等の加工性に優れたベルト用ゴム組成物及びゴムベルトに関する。 TECHNICAL FIELD The present invention relates to a rubber composition for a belt and a rubber belt, and more particularly to a belt rubber composition using a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt and having high workability such as rolling and the like. Articles and rubber belts.
近年、エンジンの高出力化、高回転化に伴い動力を伝達するベルトの使用環境温度が上昇し、ベルトに求められる負荷も大きくなっている。従来のベルトとしては主としてクロロプレンゴムを素材としていたが、クロロプレンゴムでは高雰囲気下で硬化しやすく早期に硬化によるクラックを生じたり、また、高温雰囲気下での側圧剛性不足によりベルトがプーリ内へ落ち込むように変形しディッシングと呼ばれる座屈変形を起こしてしまい動力の伝達ができなくなったり、心線と接着ゴムとの剥離が発生することによって心線が飛び出すポップアウトなどの故障を引き起こしベルト寿命に至ることがあった。 In recent years, with the increase in engine output and rotation, the operating environment temperature of the belt for transmitting power has increased, and the load required for the belt has increased. Conventional belts are mainly made of chloroprene rubber. However, chloroprene rubber is easy to cure under high atmosphere, and cracks due to curing occur early, or the belt falls into the pulley due to insufficient side pressure rigidity under high temperature atmosphere. This causes a buckling deformation called dishing, which makes it impossible to transmit power, or causes a failure such as pop-out where the core wire pops out due to the separation of the core wire and adhesive rubber, leading to the belt life There was a thing.
そこで特許文献１に開示されているように、耐摩耗性及び耐熱性に優れたベルトとして水素化ニトリルゴム（Ｈ−ＮＢＲ）にメタクリル酸亜鉛などの不飽和カルボン酸金属塩を分散させたゴムを使用したベルトが提案されている。 Therefore, as disclosed in Patent Document 1, a rubber in which an unsaturated carboxylic acid metal salt such as zinc methacrylate is dispersed in hydrogenated nitrile rubber (H-NBR) as a belt excellent in wear resistance and heat resistance. Used belts have been proposed.
又、特許文献２には水素化ニトリルゴムにメタクリル酸亜鉛などの不飽和カルボン酸金属塩を分散させて強度を向上させたゴムに、シリカとトリアリルイソシアヌレートを配合しても良いということが開示されている。
しかし、高負荷伝動の要求は更に高まっている。又、単に不飽和カルボン酸金属塩を含んだ水素化ニトリルゴムを用いるだけでは、未加硫ゴムの粘度が高くなってしまって加工性に劣るなどの不具合もあることから、ゴムの硬度は今までのものよりも高く、しかも圧延性などの加工性を低下させることなく、硬度を高くすることのできるベルト用ゴム組成物が特許文献３に開示している。
However, the demand for high load transmission is further increased. Also, simply using a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt has the disadvantage that the viscosity of the unvulcanized rubber becomes high and the processability is inferior.
しかし、高負荷伝動の要求は更に高まっている。又、単に不飽和カルボン酸金属塩を含んだ水素化ニトリルゴムを用いるだけでは、未加硫ゴムの粘度が高くなってしまって加工性に劣るなどの不具合もある。 However, the demand for high load transmission is further increased. Further, simply using a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt has a problem that the viscosity of the unvulcanized rubber becomes high and the processability is poor.
又、自動二輪車に使用される歯付ベルトは、さらに高負荷のより厳しい条件で使用され、高硬度でかつモジュラスの高い歯部を有するベルトが要求されてきた。 Further, a toothed belt used in a motorcycle is used under more severe conditions under a high load, and a belt having a tooth portion with high hardness and high modulus has been demanded.
そこで、これらのゴムを用いるとともに、配合内に短繊維、例えば耐熱性繊維等を含有するゴム組成物及びゴムベルトの提供を行う。 Therefore, while using these rubbers, a rubber composition and a rubber belt containing short fibers such as heat-resistant fibers in the blend are provided.
本発明は、不飽和カルボン酸金属塩を含有した水素化ニトリルゴムをマトリックスゴムとし、該マトリックスゴム１００質量部に対してシリカを２０〜８０質量部添加し、有機過酸化物を０.２〜１０質量部添加し、さらに耐熱性短繊維を添加したベルト用ゴム組成物にある。 In the present invention, a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt is used as a matrix rubber, 20 to 80 parts by mass of silica is added to 100 parts by mass of the matrix rubber, and 0.2 to 0.2 organic peroxide is added. The rubber composition for belts is added with 10 parts by mass and further added with heat-resistant short fibers.
請求項２に記載の発明は、前記耐熱性短繊維が、アクリル酸化繊維、アラミド繊維、フェノール繊維、フッ素系繊維、ＰＰＳ繊維、ＰＢＩ繊維の中から、少なくとも一つ選ばれてなる請求項１に記載のベルト用ゴム組成物にある。 According to a second aspect of the present invention, in the first aspect, the heat-resistant short fiber is selected from at least one selected from acrylic oxidation fiber, aramid fiber, phenol fiber, fluorine-based fiber, PPS fiber, and PBI fiber. It is in the rubber composition for belts of description.
請求項３に記載の発明は、前記アラミド繊維がメタ系アラミド繊維である請求項２に記載のベルト用ゴム組成物にある。
The invention according to
請求項４に記載の発明は、前記耐熱性短繊維を１．０質量部〜１０質量部添加する請求項１から３のいずれかに記載のベルト用ゴム組成物にある。
Invention of
請求項５に記載の発明は、マトリックスゴムは不飽和カルボン酸金属塩を含有した水素化ニトリルゴムと水素化ニトリルゴムを７：３〜１：９の割合で混合したものである請求項１から４のいずれかに記載のベルト用ゴム組成物にある。 According to a fifth aspect of the present invention, the matrix rubber is a mixture of a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt and a hydrogenated nitrile rubber in a ratio of 7: 3 to 1: 9. 4. The rubber composition for a belt according to any one of 4 above.
請求項６に記載の発明は、シリカの配合量が３０〜６０質量部である請求項１から５のいずれかに記載のベルト用ゴム組成物にある。
The invention according to
請求項７に記載の発明は、前記ゴム組成物にフェノール樹脂を配合した請求項１から６のいずれかに記載のベルト用ゴム組成物にある。 The invention according to claim 7 is the rubber composition for belts according to any one of claims 1 to 6, wherein a phenol resin is blended with the rubber composition.
請求項８に記載の発明は、前記ベルト用ゴム組成物が歯付ベルトの歯ゴムに使用される請求項１から７のいずれかに記載のベルト用ゴム組成物にある。 The invention according to claim 8 is the rubber composition for belt according to any one of claims 1 to 7, wherein the rubber composition for belt is used for tooth rubber of a toothed belt.
請求項９に記載の発明は、前記水素化ニトリルゴムのアクリロニトリル含有量が分布の中心値で水素化ニトリルゴム１００質量部のうち４０〜５０質量部含まれる請求項１から８のいずれかに記載のベルト用ゴム組成物にある。 The invention according to claim 9 is the invention according to any one of claims 1 to 8, wherein the acrylonitrile content of the hydrogenated nitrile rubber is 40 to 50 parts by mass out of 100 parts by mass of the hydrogenated nitrile rubber at the center value of the distribution. The rubber composition for belts.
請求項１０に記載の発明は、不飽和カルボン酸金属塩を含有した水素化ニトリルゴムを主成分とした伝動若しくは搬送用途に用いられるベルトにおいて、不飽和カルボン酸金属塩を含有した水素化ニトリルゴムをマトリックスゴムとし、該マトリックスゴム１００質量部に対してシリカを２０〜８０質量部添加し、さらに耐熱性短繊維を含み、有機過酸化物により架橋したゴムからなるゴムベルトにある。 The invention according to claim 10 is a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt in a belt used for power transmission or conveyance, the main component of which is a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt. Is a rubber belt made of rubber containing 20 to 80 parts by mass of silica added to 100 parts by mass of the matrix rubber, further containing heat-resistant short fibers and crosslinked with an organic peroxide.
請求項１１に記載の発明は、前記耐熱性短繊維が、アクリル酸化繊維、アラミド繊維、フェノール繊維、フッ素系繊維、ＰＰＳ繊維、ＰＢＩ繊維の中から、少なくとも一つ選ばれてなる請求項１０に記載のゴムベルトにある。 According to an eleventh aspect of the present invention, in the tenth aspect, the heat-resistant short fibers are selected from at least one selected from acrylic oxidized fibers, aramid fibers, phenol fibers, fluorine-based fibers, PPS fibers, and PBI fibers. It is in the rubber belt of description.
請求項１２に記載の発明は、前記アラミド繊維がメタ系アラミド繊維である請求項１１に記載のゴムベルトにある。 The invention described in claim 12 is the rubber belt according to claim 11, wherein the aramid fiber is a meta-aramid fiber.
請求項１３に記載の発明は、前記耐熱性短繊維１．０質量部〜１０質量部添加する請求項１０から１２のいずれかに記載のゴムベルトにある。 The invention according to claim 13 is the rubber belt according to any one of claims 10 to 12, wherein 1.0 to 10 parts by mass of the heat-resistant short fibers are added.
請求項１４に記載の発明は、マトリックスゴムは不飽和カルボン酸金属塩を含有した水素化ニトリゴムと水素化ニトリルゴムとを７：３〜１：９の割合で混合したものである請求項１０から１３のいずれかに記載のゴムベルトにある。 In the invention described in claim 14, the matrix rubber is a mixture of hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt and hydrogenated nitrile rubber in a ratio of 7: 3 to 1: 9. The rubber belt according to any one of 13 above.
請求項１５に記載の発明は、シリカの添加量が３０〜６０質量部である請求項１０から１４のいずれかに記載のゴムベルトにある。 The invention according to claim 15 is the rubber belt according to any one of claims 10 to 14, wherein the addition amount of silica is 30 to 60 parts by mass.
請求項１６に記載の発明は、前記マトリックスゴムにフェノール樹脂を添加した請求項１０から１５のいずれかに記載のゴムベルトにある。 The invention according to claim 16 is the rubber belt according to any one of claims 10 to 15, wherein a phenol resin is added to the matrix rubber.
請求項１７に記載の発明は、前記ゴムベルトが歯付ベルトである請求項１０から１６のいずれかに記載のゴムベルトにある。 The invention according to claim 17 is the rubber belt according to any one of claims 10 to 16, wherein the rubber belt is a toothed belt.
請求項１８に記載の発明は、前記水素化ニトリルゴムのアクリロニトリル含有量が分布の中心値で水素化ニトリルゴム１００質量部のうち４０〜５０質量部含まれる請求項１０から１７に記載のゴムベルトにある。 The invention according to claim 18 is the rubber belt according to claims 10 to 17, wherein the acrylonitrile content of the hydrogenated nitrile rubber is 40 to 50 parts by mass out of 100 parts by mass of the hydrogenated nitrile rubber at the center value of the distribution. is there.
請求項１９に記載の発明は、ベルト長手方向に沿って所定間隔で配置された複数の歯部と、心線が埋設された背部と、前記歯部と前記背部との間に設けられた接着層と、前記複数の歯部を被覆する歯布と、を備え、少なくとも前記歯部が不飽和カルボン酸金属塩を含有した水素化ニトリルゴムをマトリックスゴムとし、該マトリックスゴム１００質量部に対して補強材としてシリカを３０〜６０質量部、着色材としてのカーボンブラックを０〜５質量部添加したゴム組成物からなる自動二輪車駆動用歯付ベルトである。 According to the nineteenth aspect of the present invention, there are provided a plurality of tooth portions arranged at predetermined intervals along the belt longitudinal direction, a back portion in which a core wire is embedded, and an adhesive provided between the tooth portion and the back portion. A layer and a tooth cloth covering the plurality of teeth, wherein at least the teeth include a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt as a matrix rubber, and 100 parts by mass of the matrix rubber A toothed belt for driving a motorcycle comprising a rubber composition to which 30 to 60 parts by mass of silica as a reinforcing material and 0 to 5 parts by mass of carbon black as a coloring material are added.
請求項２０に記載の発明は、前記ゴム組成物にさらに有機過酸化物を０．２〜１０質量部、耐熱性短繊維を１．０質量部〜１０質量部添加した請求項１９に記載の自動二輪車駆動用歯付ベルトにある。 The invention according to claim 20 is according to claim 19, wherein 0.2 to 10 parts by mass of organic peroxide and 1.0 to 10 parts by mass of heat-resistant short fibers are further added to the rubber composition. It is in a toothed belt for motorcycle driving.
請求項２１に記載の発明は、前記耐熱性短繊維がメタ系アラミド繊維である請求項２０に記載の自動二輪車駆動用歯付ベルトにある。
The invention according to
請求項２２に記載の発明は、前記マトリックスゴムは不飽和カルボン酸金属塩を含有した水素化ニトリルゴムと水素化ニトリルゴムを７：３〜１：９の割合で混合したものである請求項１９から２１のいずれかに記載の自動二輪車駆動用歯付ベルトにある。 According to a twenty-second aspect of the present invention, the matrix rubber is a mixture of a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt and a hydrogenated nitrile rubber in a ratio of 7: 3 to 1: 9. To the toothed belt for driving a motorcycle according to any one of.
請求項２３に記載の発明は、ベルト長手方向に沿って所定間隔で配置された複数の歯部と、心線が埋設された背部と、前記複数の歯部を被覆する歯布と、を備え、少なくとも前記歯部を構成するゴムが、１ｍｍせん断変形させるのに２０ｍｍ幅当たり５００Ｎから１０００Ｎの力が必要である自動二輪車駆動用歯付ベルトにある。
The invention described in
請求項２４に記載の発明は、前記心線と前記接着層との接着力が１５０Ｎ／２５ｍｍ〜 Ｎ／２５ｍｍである請求項２３に記載の自動二輪車駆動用歯付ベルトにある。
The invention described in
本発明によると、不飽和カルボン酸金属塩を含有した水素化ニトリルゴムをマトリックスゴムとし、該マトリックスゴム１００質量部に対してシリカを１０〜６０質量部添加し、有機過酸化物を０.２〜１０質量部添加し、さらに耐熱性短繊維を添加したベルト用ゴム組成物であることから、不飽和カルボン酸金属塩を含有したＨ−ＮＢＲにシリカを配合する、未架橋時には粘度が上がることが無く圧延や成形などの加工が容易であり、架橋後は非常に高硬度で強度の高いベルトを得ることができると共に、接着性及び耐屈曲性に優れるという効果がある。 According to the present invention, hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt is used as a matrix rubber, 10 to 60 parts by mass of silica is added to 100 parts by mass of the matrix rubber, and 0.2% of organic peroxide is added. Since it is a rubber composition for belts to which 10 parts by mass is added and heat-resistant short fibers are further added, silica is added to H-NBR containing an unsaturated carboxylic acid metal salt, and the viscosity increases when uncrosslinked. There is no problem, and processing such as rolling and molding is easy, and after crosslinking, an extremely high hardness and high strength belt can be obtained, and there is an effect that adhesion and bending resistance are excellent.
請求項２に記載の発明によると、前記耐熱性短繊維が、アクリル酸化繊維、アラミド繊維、フェノール繊維、フッ素系繊維、ＰＰＳ繊維、ＰＢＩ繊維の中から、少なくとも一つ選ばれてなる請求項１に記載のベルト用ゴム組成物であることから、高温雰囲気下での強度維持に優れるという効果がある。
According to the invention described in
請求項３に記載の発明によると、前記アラミド繊維がメタ系アラミド繊維である請求項２に記載のベルト用ゴム組成物にあることから、耐摩耗性に優れるという効果がある。
According to the invention described in
請求項４に記載の発明によると、前記耐熱性短繊維を１．０質量部〜１０質量部添加する請求項１から３のいずれかに記載のベルト用ゴム組成物にあることから、耐屈曲性を損なうことなく、高硬度の配合物が得られるという効果がある。
According to invention of
請求項５に記載の発明によると、マトリックスゴムは不飽和カルボン酸金属塩を含有した水素化ニトリルゴムと水素化ニトリルゴムを１：１〜１：９の割合で混合したものである請求項１から４のいずれかに記載のベルト用ゴム組成物にあることから、必要に応じて不飽和カルボン酸金属塩を含有した水素化ニトリルゴムと不飽和カルボン酸金属塩を含んでいない水素化ニトリルゴムをブレンドして用いることが可能となる効果がある。
According to the invention described in
請求項６に記載の発明によると、シリカの配合量が３０〜６０質量部である請求項１から５のいずれかに記載のベルト用ゴム組成物にあることから、シリカの配合量をより多い範囲に限定することによって、より高硬度なベルトを得ることができる。
According to invention of
請求項７に記載の発明によると、前記ゴム組成物にフェノール樹脂を配合した請求項１から６のいずれかに記載のベルト用ゴム組成物であることから、ゴム組成物と心線との接着性が向上するという効果がある。 According to invention of Claim 7, since it is the rubber composition for belts in any one of Claims 1-6 which mix | blended the rubber resin with the phenol resin, adhesion | attachment of a rubber composition and a core wire This has the effect of improving the performance.
請求項８に記載の発明によると、前記ベルト用ゴム組成物が歯付ベルトの歯ゴムに使用される請求項１から７のいずれかに記載のベルト用ゴム組成物であることから、強度の大きさが要求される歯付ベルトの歯ゴムへの使用用途としては最適となる。 According to the invention of claim 8, since the rubber composition for belts is a rubber composition for belts according to any one of claims 1 to 7, which is used for tooth rubber of a toothed belt, It is most suitable for use as a toothed rubber of a toothed belt that requires a size.
請求項９に記載の発明によると、前記水素化ニトリルゴムのアクリロニトリル含有量が分布の中心値で水素化ニトリルゴム１００質量部のうち４０〜５０質量部含まれる請求項１から８のいずれかに記載のベルト用ゴム組成物であることから、耐油性のあるアクリロニトリル含有量を増加させることにより、耐油性を増加させ、油中で使用してもベルトが膨潤しないという効果がある。 According to the invention described in claim 9, the acrylonitrile content of the hydrogenated nitrile rubber is 40 to 50 parts by mass of 100 parts by mass of the hydrogenated nitrile rubber at the center value of the distribution. Since it is the rubber composition for belts described above, increasing the oil-resistant acrylonitrile content has the effect of increasing oil resistance and preventing the belt from swelling even when used in oil.
請求項１０に記載の発明によると、不飽和カルボン酸金属塩を含有した水素化ニトリルゴムをマトリックスゴムとし、該マトリックスゴム１００質量部に対してシリカを１０〜６０質量部添加し、さらに耐熱性短繊維を含み、有機過酸化物により架橋したゴムからなるゴムベルトにあることから、心線との接着性、耐屈曲性に優れるという効果がある。 According to the invention described in claim 10, hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt is used as a matrix rubber, 10 to 60 parts by mass of silica is added to 100 parts by mass of the matrix rubber, and heat resistance is further increased. Since it is in a rubber belt made of rubber containing short fibers and crosslinked with an organic peroxide, it has an effect of being excellent in adhesion to a core wire and bending resistance.
請求項１１に記載の発明は、前記耐熱性短繊維が、アクリル酸化繊維、アラミド繊維、フェノール繊維、フッ素系繊維、ＰＰＳ繊維、ＰＢＩ繊維の中から、少なくとも一つ選ばれてなる請求項１０に記載のゴムベルトであることから高温雰囲気下での走行においても耐久性が優れるという効果がある。 According to an eleventh aspect of the present invention, in the tenth aspect, the heat-resistant short fibers are selected from at least one selected from acrylic oxidized fibers, aramid fibers, phenol fibers, fluorine-based fibers, PPS fibers, and PBI fibers. Since the rubber belt is described, there is an effect that the durability is excellent even in running in a high temperature atmosphere.
請求項１２に記載の発明は、前記アラミド繊維がメタ系アラミド繊維である請求項１１に記載のゴムベルトであることから耐摩耗性に優れるという効果がある。 The invention according to claim 12 has an effect of being excellent in wear resistance since the aramid fiber is a meta-aramid fiber and is the rubber belt according to claim 11.
請求項１３に記載の発明は、前記耐熱性短繊維１．０質量部〜１０質量部添加する請求項１０から１２のいずれかに記載のゴムベルトであることから、耐屈曲性を損なうことなく、高硬度のベルトが得られるという効果がある。 Since the invention according to claim 13 is the rubber belt according to any one of claims 10 to 12 to which 1.0 part by mass to 10 parts by mass of the heat-resistant short fiber is added, without impairing the flex resistance, There is an effect that a high hardness belt can be obtained.
請求項１４に記載の発明は、マトリックスゴムは不飽和カルボン酸金属塩を含有した水素化ニトリゴムと水素化ニトリルゴムとを７：３〜１：９の割合で混合したものである請求項１０から１３のいずれかに記載のゴムベルトであることから、必要に応じて不飽和カルボン酸金属塩を含有した水素化ニトリルゴムと不飽和カルボン酸金属塩を含んでいない水素化ニトリルゴムをブレンドして用いることが可能となる効果がある。 In the invention described in claim 14, the matrix rubber is a mixture of hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt and hydrogenated nitrile rubber in a ratio of 7: 3 to 1: 9. Since the rubber belt according to any one of 13 is used, a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt and a hydrogenated nitrile rubber not containing an unsaturated carboxylic acid metal salt are blended as necessary. There is an effect that becomes possible.
請求項１５に記載の発明は、シリカの添加量が３０〜６０質量部である請求項１０から１４のいずれかに記載のゴムベルトであることから、シリカの配合量をより多い範囲に限定することによって、より高硬度のベルトを得ることができる。 The invention according to claim 15 is the rubber belt according to any one of claims 10 to 14, wherein the addition amount of silica is 30 to 60 parts by mass, so that the compounding amount of silica is limited to a larger range. Thus, a belt with higher hardness can be obtained.
請求項１６に記載の発明は、前記マトリックスゴムにフェノール樹脂を添加した請求項１０から１５のいずれかに記載のゴムベルトであることから、ゴム組成物と心線との接着性が向上するという効果がある。 Since the invention according to claim 16 is the rubber belt according to any one of claims 10 to 15 in which a phenol resin is added to the matrix rubber, an effect of improving the adhesion between the rubber composition and the core wire. There is.
請求項１７に記載の発明は、前記ゴムベルトが歯付ベルトである請求項１０から１６のいずれかに記載のゴムベルトであることから、強度の大きさが要求される歯付ベルトの歯ゴムへの使用用途としては最適となる。 The invention according to claim 17 is the rubber belt according to any one of claims 10 to 16, wherein the rubber belt is a toothed belt. It is optimal for usage.
請求項１８に記載の発明は、前記水素化ニトリルゴムのアクリロニトリル含有量が分布の中心値で水素化ニトリルゴム１００質量部のうち４０〜５０質量部含まれる請求項１０から１７に記載のゴムベルトであることから、耐油性のあるアクリロニトリル含有量を増加させることにより、耐油性を増加させ、油中で使用してもベルトが膨潤しないという効果がある。 The invention according to claim 18 is the rubber belt according to any one of claims 10 to 17, wherein the acrylonitrile content of the hydrogenated nitrile rubber is 40 to 50 parts by mass of 100 parts by mass of the hydrogenated nitrile rubber at the center value of the distribution. Therefore, by increasing the oil-resistant acrylonitrile content, the oil resistance is increased, and the belt does not swell even when used in oil.
請求項１９に記載の発明は、ベルト長手方向に沿って所定間隔で配置された複数の歯部と、心線が埋設された背部と、前記歯部と前記背部との間に設けられた接着層と、前記複数の歯部を被覆する歯布と、を備え、少なくとも前記歯部が不飽和カルボン酸金属塩を含有した水素化ニトリルゴムをマトリックスゴムとし、該マトリックスゴム１００質量部に対して補強材としてシリカを３０〜６０質量部、着色材としてのカーボンブラックを０〜５質量部添加したゴム組成物からなる自動二輪車駆動用歯付ベルトであることから、自動二輪車駆動用歯付ベルトとして、歯部のゴムが強化されるとともに、補強材としてシリカを使用することでカーボンブラックの使用を着色剤としてのみの使用にとどめることができ、歯付ベルトの成形加工性が改良されるという効果がある。 According to the nineteenth aspect of the present invention, there are provided a plurality of tooth portions arranged at predetermined intervals along the belt longitudinal direction, a back portion in which a core wire is embedded, and an adhesive provided between the tooth portion and the back portion. A layer and a tooth cloth covering the plurality of teeth, wherein at least the teeth include a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt as a matrix rubber, and 100 parts by mass of the matrix rubber Since it is a toothed belt for motorcycle driving comprising a rubber composition in which 30 to 60 parts by mass of silica as a reinforcing material and 0 to 5 parts by mass of carbon black as a coloring material are added, as a toothed belt for motorcycle driving In addition to strengthening the rubber of the tooth part, the use of silica as a reinforcing material allows the use of carbon black to be used only as a colorant, and the processability of toothed belts is improved. There is an effect that good is.
請求項２０に記載の発明は、前記ゴム組成物にさらに有機過酸化物を０．２〜１０質量部、耐熱性短繊維を１．０質量部〜１０質量部添加する請求項１９に記載の自動二輪車駆動用歯付ベルトであることから、請求項１９の効果に加えてさらに歯部の強度が上がり、より自動二輪車駆動用歯付ベルトとしての機能を備える効果がある。 The invention according to claim 20 is according to claim 19, wherein 0.2 to 10 parts by mass of organic peroxide and 1.0 to 10 parts by mass of heat-resistant short fibers are further added to the rubber composition. Since it is a toothed belt for driving a motorcycle, in addition to the effect of claim 19, the strength of the tooth portion is further increased, and there is an effect of providing a function as a toothed belt for driving a motorcycle.
請求項２１に記載の発明は、前記耐熱性短繊維がメタ系アラミド繊維である請求項２０に記載の自動二輪車駆動用歯付ベルトであることから、少なくとも歯部のゴムが耐摩耗性に優れるという効果がある。
The invention according to
請求項２２に記載の発明は、前記マトリックスゴムは不飽和カルボン酸金属塩を含有した水素化ニトリルゴムと水素化ニトリルゴムを７：３〜１：９の割合で混合したものである請求項１９から２１のいずれかに記載の自動二輪車駆動用歯付ベルトであることから、必要に応じて不飽和カルボン酸金属塩を含有した水素化ニトリルゴムと不飽和カルボン酸金属塩を含んでいない水素化ニトリルゴムをブレンドして用いることが可能となる効果がある。 According to a twenty-second aspect of the present invention, the matrix rubber is a mixture of a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt and a hydrogenated nitrile rubber in a ratio of 7: 3 to 1: 9. 21. A hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt and a hydrogenation containing no unsaturated carboxylic acid metal salt as necessary, because it is a toothed belt for motorcycle driving according to any one of 1 to 21. There is an effect that nitrile rubber can be blended and used.
請求項２３に記載の発明は、ベルト長手方向に沿って所定間隔で配置された複数の歯部と、心線が埋設された背部と、前記複数の歯部を被覆する歯布と、を備え、少なくとも前記歯部を構成するゴムが、１ｍｍせん断変形させるのに２０ｍｍ幅当たり５００Ｎから１０００Ｎの力が必要である自動二輪車駆動用歯付ベルトであることから、ゴムのせん断変形力を限定することによって、高負荷が掛かる自動二輪車を駆動させた場合に、ベルト歯がせん断変形せずに長寿命とすることができる。
The invention described in
請求項２４に記載の発明は、前記心線と前記接着層との接着力が１５０Ｎ／２５ｍｍ〜 Ｎ／２５ｍｍである請求項２３に記載の自動二輪車駆動用歯付ベルトであることから、請求項２３の効果に加えて、心線と接着層との接着力が大きくなり、心線と接着層との剥離が発生せず自動二輪車駆動用歯付ベルトを長寿命とすることができる。
The invention according to
図１は本発明のベルトの一例を示す歯付ベルトの一例であり、本発明歯付ベルト１はベルト長手方向に沿ってガラス繊維コード又はアラミドコードなど、低伸度、高強力のロープからなる心線４を埋設した接着ゴム３の下部に歯布５を外表面に積層した歯ゴム６を配置すると共に、接着ゴム３の上部に背ゴム２を配層することによって構成されている。
FIG. 1 is an example of a toothed belt showing an example of the belt of the present invention. The toothed belt 1 of the present invention is made of a low elongation and high strength rope such as a glass fiber cord or an aramid cord along the belt longitudinal direction. A
ここで、上記の歯付ベルト１は接着ゴム層３、歯ゴム層６及び背ゴム層２の原料ゴムとして少なくとも歯ゴムについては、不飽和カルボン酸金属塩を含有した水素化ニトリルゴムをマトリックスゴムとし、該マトリックスゴム１００質量部に対してシリカを２０〜８０質量部、より好ましくは３０〜６０質量部添加し、有機過酸化物を０.２〜１０質量部添加し、さらに耐熱性短繊維を配合したゴムの架橋物からなっている。
Here, the toothed belt 1 is a matrix rubber made of hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt as at least the tooth rubber as the raw rubber of the
又、歯付ベルト１が自動二輪車駆動用に使用される場合は、少なくとも歯ゴムとして前記マトリックスゴム１００質量部に対してシリカを３０〜６０質量部、着色剤としてカーボンブラックを０〜５質量部添加するのが好ましい。 Further, when the toothed belt 1 is used for driving a motorcycle, at least 30 to 60 parts by mass of silica and at least 0 to 5 parts by mass of carbon black as a colorant with respect to 100 parts by mass of the matrix rubber as a tooth rubber. It is preferable to add.
この原料ゴムに用いられる水素化ニトリルゴムは特に限定されるものではないが水素添加率が８０％以上であり、特に耐熱性、耐オゾン性の特性を発揮するためには９０％以上が好ましい。水素添加率８０％未満の水素化ニトリルゴムは耐熱性、耐オゾン性が極度に低下するので好ましくなく、耐熱性を考慮すればヨウ素価は５〜３５であることが好ましい。更に耐油性の観点から、結合アクリロニトリル量は分布の中心値で４０〜５０％の範囲が好ましい。又、ムーニー粘度（ＭＬ１＋４（１００°Ｃ））が７０〜８５のものであることが機械的強度や側圧剛性を良好にすること、また、屈曲性や加工性を良好にする上で好ましい。 The hydrogenated nitrile rubber used for the raw rubber is not particularly limited, but the hydrogenation rate is 80% or more, and particularly 90% or more is preferable in order to exhibit heat resistance and ozone resistance characteristics. Hydrogenated nitrile rubber having a hydrogenation rate of less than 80% is not preferable because the heat resistance and ozone resistance are extremely lowered. In view of heat resistance, the iodine value is preferably 5 to 35. Further, from the viewpoint of oil resistance, the amount of bound acrylonitrile is preferably in the range of 40 to 50% in the central value of the distribution. Further, it is preferable that the Mooney viscosity (ML1 + 4 (100 ° C.)) is 70 to 85 in order to improve the mechanical strength and lateral pressure rigidity, and to improve the flexibility and workability.
不飽和カルボン酸金属塩はカルボキシル基を有する不飽和カルボン酸と金属とがイオン結合したものであり、不飽和カルボン酸としてはアクリル酸、メタクリル酸等のモノカルボン酸、マレイン酸、フマル酸、イタコン酸等のジカルボン酸が好ましく、金属としては、ベリリウム、マグネシウム、カルシウム、ストロンチウム、バリウム、チタン、クロム、モリブデン、マンガン、鉄、コバルト、ニッケル、銅、銀、亜鉛、カドミウム、アルミニウム、錫、鉛、アンチモン等を用いることができる。 The unsaturated carboxylic acid metal salt is an ionic bond of an unsaturated carboxylic acid having a carboxyl group and a metal. Examples of the unsaturated carboxylic acid include monocarboxylic acids such as acrylic acid and methacrylic acid, maleic acid, fumaric acid, and itacone. Dicarboxylic acids such as acids are preferred, and the metals include beryllium, magnesium, calcium, strontium, barium, titanium, chromium, molybdenum, manganese, iron, cobalt, nickel, copper, silver, zinc, cadmium, aluminum, tin, lead, Antimony or the like can be used.
そして水素化ニトリルゴムと不飽和カルボン酸金属塩との組成比は９８：２〜５５：４５とする。水素化ニトリルゴムが９８より大きい割合になると耐摩耗性が不足することになり、５５より小さい割合になると耐摩耗性は良いが、ベルトの屈曲性が悪くなるので好ましくない。又、この組成比を調整する為に不飽和カルボン酸金属塩を含有した水素化ニトリルゴムと通常の水素化ニトリルゴムとをブレンドしてマトリックスゴムとすることも可能である。 And the composition ratio of hydrogenated nitrile rubber and unsaturated carboxylic acid metal salt shall be 98: 2-55: 45. If the proportion of hydrogenated nitrile rubber is greater than 98, the wear resistance will be insufficient, and if it is less than 55, the wear resistance will be good, but the flexibility of the belt will be poor, which is not preferable. In order to adjust the composition ratio, a hydrogenated nitrile rubber containing an unsaturated carboxylic acid metal salt and a normal hydrogenated nitrile rubber can be blended to form a matrix rubber.
有機過酸化物は架橋剤として用いられるものであって、ジ−ｔ−ブチルパオキサイド、ジクミルパーオキサイド、ｔ−ブチルクミルパーオキサイド、１，１−ｔ−ブチルぺロキシ−３，３，５−トリメチルシクロヘキサン、２，５−ジ−メチル−２，５−ジ（ベンゾイルぺロキシ）へキサン、ｔ−ブチルぺロキシベンゾアート、ｔ−ブチルぺロキシ−２−エチル−ヘキシルカーボネートなどを挙げることができる。その配合量としてはマトリックスゴム１００質量部に対して０.２〜１０質量部とする。０.２質量部未満であると架橋が十分に行われず、１０質量部を超えると十分な弾性が得られなくなる。 The organic peroxide is used as a cross-linking agent and is di-t-butyl peroxide, dicumyl peroxide, t-butyl cumyl peroxide, 1,1-t-butylperoxy-3, 3, 5 -Trimethylcyclohexane, 2,5-di-methyl-2,5-di (benzoylperoxy) hexane, t-butylperoxybenzoate, t-butylperoxy-2-ethyl-hexyl carbonate, etc. it can. The blending amount is 0.2 to 10 parts by mass with respect to 100 parts by mass of the matrix rubber. If the amount is less than 0.2 parts by mass, crosslinking is not sufficiently performed, and if it exceeds 10 parts by mass, sufficient elasticity cannot be obtained.
シリカはマトリックスゴム１００質量部に対して２０〜８０質量部、より好ましく、特に自動二輪車駆動用に使用される歯付ベルトの場合は、３０〜６０質量部の範囲で配合するものとする。１０質量部未満であるとゴムと心線との間の接着力が乏しくなって心線の剥離による飛び出しなどの故障につながり、６０質量部を超えると未加硫での粘度が大きくなりベルトが成形できなくなるので好ましくない。又、３０質量部以上であることがより高硬度なベルトを得ることができることから好ましい。 Silica is added in an amount of 20 to 80 parts by mass with respect to 100 parts by mass of the matrix rubber, and particularly in the case of a toothed belt used for driving a motorcycle, it is blended in the range of 30 to 60 parts by mass. If the amount is less than 10 parts by mass, the adhesive force between the rubber and the core wire becomes poor, leading to a failure such as popping out due to peeling of the core wire. If the amount exceeds 60 parts by mass, the unvulcanized viscosity increases and the belt becomes Since it becomes impossible to mold, it is not preferable. Moreover, it is preferable that it is 30 mass parts or more from the viewpoint that a belt with higher hardness can be obtained.
耐熱性短繊維としては、アクリル酸化繊維、アラミド繊維、フェノール繊維、フッ素系繊維、ＰＰＳ繊維、ＰＢＩ繊維等が使用できる。好ましくはアラミド繊維、その中でもメタ系アラミド繊維であることが好ましい。短繊維の添加量は該マトリックスゴム１００質量部に対して１．０質量部〜１０質量部であることが好ましい。１．０質量部未満の場合は、短繊維の補強効果が不十分で、当該ゴムを使用してベルトを作製した際、高負荷での使用に耐えられない可能性が有り、１０質量部を越えると短繊維の列理方向の伸びが低下し、当該ゴムを使用してベルトを作製した際、屈曲性が低下し、早期にクラックが発生する可能性がある。 As the heat-resistant short fibers, acrylic oxide fibers, aramid fibers, phenol fibers, fluorine fibers, PPS fibers, PBI fibers, and the like can be used. Aramid fibers are preferable, and meta-aramid fibers are particularly preferable. It is preferable that the addition amount of a short fiber is 1.0 mass part-10 mass parts with respect to 100 mass parts of this matrix rubber. When the amount is less than 1.0 part by mass, the reinforcing effect of the short fibers is insufficient, and when a belt is produced using the rubber, there is a possibility that it cannot be used under a high load. If it exceeds, the elongation of the short fibers in the row direction decreases, and when a belt is produced using the rubber, the flexibility is lowered and cracks may occur at an early stage.
又、前記ゴム組成物にフェノール樹脂を配合すると、心線との接着力が向上し好ましい。より好ましくは熱硬化性フェノール樹脂を配合すると良い。 Moreover, it is preferable to add a phenol resin to the rubber composition because the adhesive strength with the core wire is improved. More preferably, a thermosetting phenol resin is added.
又、上記以外にも通常ゴムに配合されるカーボンブラック、炭酸カルシウム、タルクなどの耐摩耗性を向上させる充填財、架橋補助剤、可塑剤、安定剤、加工補助剤、老化防止剤、着色剤などの添加剤を使用目的に応じて配合することは可能である。これらの配合剤を混合する方法も通常用いられる手段、例えばバンバリーミキサやニーダー等を用いて混練する方法が挙げられる。 Besides the above, fillers such as carbon black, calcium carbonate, talc, etc., which are usually blended in rubber, improve wear resistance, crosslinking aids, plasticizers, stabilizers, processing aids, anti-aging agents, coloring agents. It is possible to add additives such as according to the purpose of use. The method of mixing these compounding agents also includes a method of kneading using a commonly used means such as a Banbury mixer or a kneader.
又、シリカを３０〜６０質量部配合することによって、前記カーボンブラックは補強剤として配合しなくても十分にシリカが補強剤として機能するので、カーボンブラックは着色剤としてのみ配合することができる。添加量をゴムマトリックス１００質量部に対して０〜５質量部添加することで、ベルトを着色でき、さらに、ベルトの加工性も損なわない。 Further, by blending 30 to 60 parts by mass of silica, the carbon black can be blended only as a colorant since the silica functions sufficiently as a reinforcing agent even if the carbon black is not blended as a reinforcing agent. By adding 0 to 5 parts by mass of the addition amount to 100 parts by mass of the rubber matrix, the belt can be colored and the workability of the belt is not impaired.
心線４としては、低伸度高強力のロープが用いられ、アラミド繊維、ポリアミド繊維、ポリエチレンテレフタレート繊維、エチレン−２，６−ナフタレートを主たる構成単位とするポリエステル繊維などの有機繊維や、ガラス繊維などの無機繊維や金属繊維からなる撚成したロープが挙げられる。この心線４は一般にレゾルシン−ホルマリン−ラテックス処理した表面に更にゴム糊などをコーティングしたものも用いられる。
As the
このような接着処理としては繊維をレゾルシン−ホルマリン−ラテックス（ＲＦＬ液）に浸漬後、加熱乾燥して表面に均一に接着層を形成するのが一般的である。しかし、これに限ることなくエポキシ又はイソシアネート化合物で前処理を行った後に、ＲＦＬ液で処理する方法等もある。 As such an adhesion treatment, it is common to immerse the fiber in resorcin-formalin-latex (RFL solution) and then heat-dry to form a uniform adhesion layer on the surface. However, the present invention is not limited to this, and there is a method of performing a pretreatment with an epoxy or isocyanate compound and then treating with an RFL solution.
ＲＦＬ液はレゾルシンとホルマリンとの初期縮合体をラテックスに混合したものであり、ここで使用するラテックスとしてはクロロプレン、スチレン・ブタジエン・ビニルピリジン三元共重合体、水素化ニトリル、ＮＢＲ等が挙げられるが、接着ゴム層、背ゴム層の構成原料より水素化ニトリルゴムが好適である。 The RFL liquid is obtained by mixing an initial condensate of resorcin and formalin into a latex. Examples of the latex used here include chloroprene, styrene / butadiene / vinylpyridine terpolymer, hydrogenated nitrile, NBR, and the like. However, hydrogenated nitrile rubber is preferred from the constituent raw materials of the adhesive rubber layer and the back rubber layer.
歯布５は、綿、ポリアミド、ポリエチレンテレフタレート、アラミド繊維からなるフィラメント状又は紡績糸を用いて、平織、綾織、朱子織等に製織又は製編みした布を使用する。これらはその後、ＲＦＬ処理にて接着処理して厚みを硬くし、スピニング工程での筒状のベルト帆布のしわの発生を阻止する。ＲＦＬ処理はＲＦＬ液に０.１〜２０秒間浸漬した後、１００〜２００°Ｃで３０〜６００秒にて乾燥させる。
As the
このＲＦＬ処理で使用するＲＦＬ液は、前記心線のそれと同じくレゾルシンとホルマリンの初期縮合物とゴムラテックスとを混合したものであるが、この場合レゾルシンとホルマリンのモル比は１：０.５〜３にすることが接着力を高める上で好適である。また、レゾルシンとホルマリンの初期縮合物は、これをラテックスのゴム分１００質量部に対してその樹脂分が１０〜１００質量部になるようにラテックスと混合した上、全固形物濃度が５〜４０％になるように調節される。 The RFL solution used in this RFL treatment is a mixture of resorcin and formalin initial condensate and rubber latex, similar to that of the core wire. In this case, the molar ratio of resorcin to formalin is 1: 0.5. It is suitable to increase the adhesive strength to 3. The initial condensate of resorcin and formalin is mixed with latex so that the resin content is 10 to 100 parts by mass with respect to 100 parts by mass of latex rubber, and the total solid concentration is 5 to 40. % Adjusted.
尚、ＲＦＬ液には適宜カーボンブラック液を混合して処理反を黒染めする場合もある。綿織物の場合には、ＲＦＬ液に公知の界面活性剤を０.１〜１３.０質量％加えると良い。 In some cases, the RFL solution is mixed with a carbon black solution as appropriate to black the process. In the case of cotton fabric, 0.1 to 13.0% by mass of a known surfactant may be added to the RFL solution.
上記ラテックスはスチレン−ブタジエン−ビニルピリジン三元共重合体、クロロスルフォン化ポリエチレン、水素化ニトリルゴム、エビクロルヒドリン、天然ゴム、ＳＢＲ、クロロプレンゴム、オレフィン−ビニルエステル共重合体等のラテックスであり、先と同じく接着ゴム層、背ゴム層の構成原料との関係で水素化ニトリルゴムが好適である。 The latex is a latex of styrene-butadiene-vinylpyridine terpolymer, chlorosulfonated polyethylene, hydrogenated nitrile rubber, shrimp chlorohydrin, natural rubber, SBR, chloroprene rubber, olefin-vinyl ester copolymer, etc. Like the above, hydrogenated nitrile rubber is preferable in relation to the constituent raw materials of the adhesive rubber layer and the back rubber layer.
又、二輪車駆動用歯付ベルトとしては、図４に示すように前記歯部と背部との間に接着層３を設ける。前記接着層３と心線との接着力としては、１５０Ｎ／２５ｍｍ〜４００Ｎ／２５ｍｍが好ましい。
接着力が１５０Ｎ／２５ｍｍより小さければ高負荷が掛かる二輪車を駆動した場合に心線と接着層とが剥離し、ベルトが早期に破損する。一方、接着力が４００Ｎ／２５ｍｍより小さくなると、ゴムの硬度が高くなり、屈曲性が低下するという問題がある。
Further, as a toothed belt for driving a motorcycle, an
If the adhesive force is smaller than 150 N / 25 mm, the core wire and the adhesive layer are peeled off when a two-wheeled vehicle with a high load is driven, and the belt is damaged early. On the other hand, when the adhesive force is less than 400 N / 25 mm, there is a problem that the hardness of the rubber is increased and the flexibility is lowered.
接着ゴム層３のゴム組成物については、耐熱性と耐油性を備えた水素化ニトリルゴムや、クロロプレンゴム、ＣＳＭ、不飽和カルボン酸金属塩を含有した水素化ニトリルゴム等を使用することができる。この場合、上記の心線との接着力を満たすゴム配合が選択される。
For the rubber composition of the
又、二輪車駆動用歯付ベルトとして使用する歯布５は、前記繊維織物として、少なくとも２種類の緯糸と１種類の経糸とが織成された多重織（２重織）構造のものを採用することもできる。この場合、経糸をナイロン繊維とし、緯糸にはフッ素系繊維、ナイロン繊維、及びウレタン弾性糸を使用することが好ましい。又、緯糸のうちの、少なくとも歯布５の表面側（歯付プーリとのかみ合い側）に位置する（露出する）緯糸としては、歯布５と歯付プーリとの間の摩擦を低減するために、摩擦係数が低いフッ素系繊維（例えばＰＴＦＥ繊維）を使用することが好ましい。一方、歯布５の歯部６との接着側に位置する緯糸には、フッ素系繊維以外の繊維（ナイロン繊維やウレタン弾性糸）を使用することで、歯布５と歯部６を構成するゴムの接着力を高めることが可能となる。
The
この歯布５は、以下のような工程を含む一連の接着処理を経て、歯部６を構成するゴムに接着される。
The
（１)歯布５を構成する繊維織物を、レゾルシン−ホルマリン−ゴムラテックス処理液（以下、ＲＦＬ処理液という）に含浸し、乾燥させる。
(1) The fiber fabric constituting the
ここで、前記ＲＦＬ処理液には、硫黄化合物の水分散物、キノンオキシム系化合物、メタアクリレート系化合物、マレイミド系化合物、のうち少なくとも一つの加硫助剤も又は、これらの加硫助剤を水に分散させたものを添加することが好ましい。 Here, in the RFL treatment liquid, at least one vulcanization aid of an aqueous dispersion of a sulfur compound, a quinone oxime compound, a methacrylate compound, or a maleimide compound, or these vulcanization aids are added. What is dispersed in water is preferably added.
硫黄化合物の水分散物としては、例えば、硫黄の水分散物やテトラメチルチウラムジスルフィドなどが採用され得る。キノンオキシム系化合物としては、例えば、ｐ−キノンジオキシムなどが採用され得る。メタアクリレート系化合物としては、例えば、エチレングリコールジメタクリレートやトリメチロールプロパントリメタクリレートなどが採用され得る。マレイミド系化合物としては、例えばＮ，Ｎ´−ｍ−フェニレンビスマレイミドやＮ，Ｎ´−（４，４´−ジフェニルメタンビスマレイミド）などが採用され得る。 As an aqueous dispersion of a sulfur compound, for example, an aqueous dispersion of sulfur or tetramethylthiuram disulfide can be employed. As the quinone oxime compound, for example, p-quinone dioxime may be employed. As the methacrylate compound, for example, ethylene glycol dimethacrylate, trimethylolpropane trimethacrylate, or the like may be employed. As the maleimide compound, for example, N, N′-m-phenylene bismaleimide, N, N ′-(4,4′-diphenylmethane bismaleimide) or the like can be employed.
尚、上述した「当該加硫助剤を水に分散させたもの」における「水」は、例えばアルコールなどのメタノールを若干程度含むものであってもよい。これによれば、「当該加硫助剤が水に対して不溶性の場合であっても、「当該加硫助剤」の水に対する親和性が向上して「当該加硫助剤」が分散し易くなる。 In addition, “water” in “the vulcanization aid dispersed in water” described above may contain, for example, a slight amount of methanol such as alcohol. According to this, even when the vulcanization aid is insoluble in water, the affinity of the vulcanization aid for water is improved and the vulcanization aid is dispersed. It becomes easy.
このように、ＲＦＬ処理液に加硫助剤を添加することで以下の効果が期待される。即ち、ＲＦＬ処理液中に含まれるゴムラテックス成分と外層ゴム（後記（２）のゴム糊処理や（３）のＣｏａｔ処理で形成されるゴム糊又は圧延ゴムを意味する。Ｃｏａｔ処理が省略される場合は歯部２を構成するゴムを意味する。）との層間の化学的結合力が強化されることで、接着性が向上し、歯布５の剥離が抑制される。更に期待される効果として、ＲＦＬ処理液中に含まれるゴムラテックス成分自身の化学的結合力（架橋の力）が強化され、その結果、接着層の凝集破壊による剥離（即ち、層間剥離）よりも、接着対象である上記外層ゴムの破壊による剥離が先行すると考えられる。
Thus, the following effects are expected by adding the vulcanization aid to the RFL treatment liquid. That is, the rubber latex component and the outer layer rubber contained in the RFL treatment liquid (meaning the rubber paste or the rolled rubber formed by the rubber paste treatment (2) and the coat treatment (3) described later). In the case, it means a rubber constituting the tooth portion 2), and the adhesive strength is improved and peeling of the
又、ＲＦＬ処理液に加硫助剤を添加することで以下の効果が期待される。即ち、ＲＦＬ処理液中に含まれるゴムラテックス成分と外層ゴム（後記(２)のゴム糊処理や（３）のＣｏａｔ処理で形成されるゴム糊又は圧延ゴムを意味する。Ｃｏａｔ処理が省略される場合は歯部６を構成するゴムを意味する。）との層間の化学的結合力が強化されることで、接着性が向上し、歯布５の剥離が抑制される。更に期待される効果として、ＲＦＬ処理液中に含まれるゴムラテックス成分自身の化学的結合力（架橋の力）が強化され、その結果、接着層の凝集破壊による剥離(即ち、層間剥離)よりも、接着対象である上記外層ゴムの破壊による剥離が先行すると考えられる。
Moreover, the following effects are expected by adding a vulcanization aid to the RFL treatment liquid. That is, the rubber latex component and the outer layer rubber contained in the RFL treatment liquid (meaning rubber paste or rolled rubber formed by the rubber paste process (2) and the coat process (3) described later. The Coat process is omitted. In the case, it means a rubber constituting the tooth portion 6), and the adhesive strength is improved and peeling of the
又、ＲＦＬ処理液に加硫助剤を添加する場合、繊維織物の含浸処理を２回に分けて実行してもよい。この場合、まず、１回目のＲＦＬ含浸処理においては、ＲＦＬ処理液には、前述した何れの加硫助剤も添加しないこととする。これは、１回目の処理工程においては、ゴムラテックス成分の架橋よりもＲＦの熱硬化を優先するためである。 Moreover, when adding a vulcanization | cure adjuvant to a RFL process liquid, you may perform the impregnation process of a textile fabric in 2 steps. In this case, first, in the first RFL impregnation treatment, none of the vulcanization aids described above is added to the RFL treatment liquid. This is because, in the first treatment step, priority is given to RF thermal curing over crosslinking of the rubber latex component.
一方、２回目のＲＦＬ含浸処理においては、１回目のＲＦＬ処理液と比較してゴムラテックス成分を多く含み、硫黄化合物の水分散物、キノンオキシム系化合物、メタアクリレート系化合物、マレイミド系化合物、のうち少なくとも一つの加硫助剤、又は、加硫助剤を水に分散させたものを添加したＲＦＬ処理液を使用する。尚、１回目の含浸処理と２回目の含浸処理とで、ＲＦＬ処理液のゴムラテックス成分の割合に差を設けるのは、親和性の異なる繊維とゴムの両方に対する、ＲＦＬ層の接着性を高める為である。 On the other hand, the second RFL impregnation treatment contains more rubber latex components than the first RFL treatment solution, and includes an aqueous dispersion of a sulfur compound, a quinone oxime compound, a methacrylate compound, and a maleimide compound. Of these, at least one vulcanization aid or an RFL treatment solution to which a vulcanization aid is dispersed in water is used. Note that the difference in the ratio of the rubber latex component of the RFL treatment liquid between the first impregnation treatment and the second impregnation treatment improves the adhesion of the RFL layer to both fibers and rubber having different affinity. Because of that.
（２）繊維織物に、ゴム組成物を溶剤に溶かしたゴム糊からなる接着処理剤を付着させた後にベーキング処理する、２種類のゴム糊処理（Ｐ１処理、Ｓ１処理）を行う。 (2) Two types of rubber paste treatments (P1 treatment and S1 treatment) are performed in which an adhesive treatment agent made of a rubber paste obtained by dissolving a rubber composition in a solvent is attached to a fiber fabric, followed by baking.
(３)繊維織物の表面に、ゴム糊と圧延ゴムとをこの順にコーティングする。本工程は、Ｃｏａｔ処理とも称される。「この順に」とあるのは、詳細には「繊維織物から歯部６へ向かって、この順に」を意味する。ここで、ＲＦＬ処理液に加硫助剤を添加した場合には、このＣｏａｔ処理で使用するゴム糊と圧延ゴムにも、ＲＦＬ処理液に添加した加硫助剤と同一の加硫助剤を添加することが好ましい。これにより、（ａ）ＲＦＬ処理液で処理された繊維織物とゴム糊の間の接着力、（ｂ）ＲＦＬ処理液で処理された繊維織物と圧延ゴムの間の接着力、（ｃ）ＲＦＬ処理液で処理された繊維織物と圧延ゴムの間の接着力、（ｃ）ＲＦＬ処理液で処理された繊維織物とゴム糊と圧延ゴムの間の接着力、の著しい改善が期待される。
(3) The surface of the fiber fabric is coated with rubber paste and rolled rubber in this order. This step is also referred to as “Coat processing”. The phrase “in this order” means “in this order from the fiber fabric toward the
尚、上記（１）〜（３）の処理は、全てを行う必要は無く、必要に応じて、いずれか一つ、或いは、２以上の複数を組み合わせて行う。例えば、（１）の処理においてＲＦＬ処理液に加硫助剤を添加する場合には、この処理のみで繊維織物とゴム間の接着力がかなり高められることから、（２）のゴム糊処理を省略しても良い。 Note that the processes (1) to (3) need not be performed all, and are performed as needed, or any one or a combination of two or more. For example, when a vulcanization aid is added to the RFL processing solution in the process (1), the adhesive force between the fiber fabric and the rubber is considerably increased only by this process. May be omitted.
以上の説明では歯付ベルトに本発明を適用した例を説明したが、ベルトの種類は歯付ベルトに限られるものではなく図２に示すような心線２３を埋設した接着ゴム層２４と圧縮ゴム２６とから構成され、更に上記接着ゴム層２４及び圧縮ゴム層２６の各表面層にゴム付帆布２２を積層したカットエッジタイプのＶベルト２１や図示はしないがＶリブドベルト等のベルト、又ベルトの用途についても動力伝動用、搬送用と様々なベルトに適用することができるものである。もちろん強度の大きさが要求される歯付ベルトの歯ゴムに使用することがより好ましい。
In the above description, an example in which the present invention is applied to a toothed belt has been described. However, the type of belt is not limited to a toothed belt, and an
次に表１に示す配合でゴムを混練りして各ゴムシートを作成し、その物性を測定した。その結果を表２に示す。 Next, rubber was kneaded with the formulation shown in Table 1 to prepare each rubber sheet, and its physical properties were measured. The results are shown in Table 2.
次に、自動二輪車用ベルトの配合として表３に示す配合でゴムを混練りして各ゴムシートを作成し、その物性を作成した。その結果を表４に示す。 Next, rubber was kneaded with the composition shown in Table 3 as a composition for a motorcycle belt to prepare each rubber sheet, and its physical properties were prepared. The results are shown in Table 4.
又、歯数１３２歯、歯ピッチ１３ｍｍ、ベルト幅２０ｍｍの歯付ベルトを作成し、図３に示すようなレイアウトにて第一走行試験を行った。第一走行試験の結果を表４に示す。
さらに、ＪＩＳＫ６２５８に従って、実施例１から３のベルト、及び実施例１０〜１３のベルト、比較例２のベルトを１００°ＣのＩＲＭ＃９０３浸漬液に７日間浸漬し、体積変化率を測定した。その結果を表３に示す。さらに浸漬後のこれらのベルトを図３に示すレイアウトによって、雰囲気温度２３°Ｃにて、ベルト幅１ｍｍ幅当たり１５ｋｇｆという高負荷での第二走行試験を実施した。その結果を表３に示す。
Further, a toothed belt having 132 teeth, a tooth pitch of 13 mm, and a belt width of 20 mm was prepared, and a first running test was performed with a layout as shown in FIG. Table 4 shows the results of the first running test.
Furthermore, according to JISK6258, the belts of Examples 1 to 3, the belts of Examples 10 to 13, and the belt of Comparative Example 2 were immersed in an IRM # 903 immersion liquid at 100 ° C. for 7 days, and the volume change rate was measured. The results are shown in Table 3. Further, a second running test was conducted on these belts after immersion at a high load of 15 kgf per 1 mm belt width at an ambient temperature of 23 ° C. according to the layout shown in FIG. The results are shown in Table 3.
表２の結果からわかるように、実施例は比較例と比べて引裂き強さは大きくなっている。又、熱可塑性フェノール樹脂を配合した実施例２、実施例４、及び実施例６は比較例と比べてアラミド心線との接着力が大きく向上している。又、表３から、実施例１、実施例３、及び実施例４と比較例を比べると長寿命であることがわかる。とりわけ実施例１及び実施例４は５００時間走行可能となった。
さらに、アクリロニトリル含有量が水素化ニトリルゴム１００質量部に対して４０質量部以上である実施例１０、１１、１３は、アクリロニトリル含有量が４０未満のベルトに比べて、油中での膨潤後に第二走行試験をすると、長時間の寿命を維持していた。
As can be seen from the results in Table 2, the tear strength of the example is larger than that of the comparative example. Moreover, Example 2, Example 4, and Example 6 which mix | blended the thermoplastic phenol resin have improved the adhesive force with an aramid core wire significantly compared with the comparative example. Moreover, it can be seen from Table 3 that the lifespan is longer when Examples 1, 3 and 4 are compared with Comparative Example. In particular, Example 1 and Example 4 were able to run for 500 hours.
Furthermore, Examples 10, 11, and 13 in which the acrylonitrile content is 40 parts by mass or more with respect to 100 parts by mass of the hydrogenated nitrile rubber are compared with the belt having an acrylonitrile content of less than 40 after the swelling in oil. Two running tests maintained a long life.
次に、自動二輪車用ベルトの配合として表４に示す配合でゴムを混練りしてＨ１４Ｍ１３０歯２０ｍｍ幅の歯付ベルトを作製し、歯ゴムの物性を測定した。その結果を表５に示す。
又、歯ゴムのせん断変形を変形が１ｍｍのときの応力を調べた。測定方法は、ＪＡＳＯＥ１１０：２０００に準じた。そのときの結果は、表７に示す。
Next, rubber was kneaded with the composition shown in Table 4 as a composition for a motorcycle belt to produce a toothed belt having a width of H14M130 teeth of 20 mm, and the physical properties of the tooth rubber were measured. The results are shown in Table 5.
Further, the shear deformation of the tooth rubber was examined for the stress when the deformation was 1 mm. The measuring method was based on JASOE110: 2000. The results at that time are shown in Table 7.
次に、自動二輪車駆動用エンジンに対応した第三走行試験を行った。歯付ベルトは、ベルト歯がＨ１４Ｍの丸歯タイプの歯で、ベルト歯数１３０歯、ベルト幅２０ｍｍのベルトを使用した。このとき、歯部及び背部は、表４に示すベルト内で同じゴム配合を用い、接着層としては表６に示す配合のゴムを使用した。ベルト走行試験を行った雰囲気温度は室温で、図５に示すようなレイアウトにて走行試験を行った。その結果を表７に示す。又、図５の駆動側プーリから従動側プーリへ３０ｃｍ離れ、駆動側プーリから軸方向へ３０ｃｍ離れた位置で音圧の測定を行った。その結果も表７に示す。 Next, a third running test corresponding to a motorcycle driving engine was performed. As the toothed belt, a round tooth type tooth having a belt tooth of H14M, a belt having 130 teeth and a belt width of 20 mm was used. At this time, the tooth part and the back part used the same rubber | gum compounding in the belt shown in Table 4, and used the rubber | gum of the compounding shown in Table 6 as an adhesive layer. The ambient temperature at which the belt running test was performed was room temperature, and the running test was performed with a layout as shown in FIG. The results are shown in Table 7. Further, the sound pressure was measured at a position 30 cm away from the driving pulley to the driven pulley in FIG. 5 and 30 cm away from the driving pulley in the axial direction. The results are also shown in Table 7.
実施例１４から２６は、第三走行試験では全て５００時間走行可能となった。実施例２７及び２８は実施例１４〜２６と比べてやや寿命が短くなったが、４８０時間は走行した。
一方、比較例２、４、５のベルトは２４時間で歯欠けが発生し、短寿命となった。
Examples 14 to 26 were all capable of running for 500 hours in the third running test. Examples 27 and 28 were slightly shorter in life than Examples 14 to 26, but ran for 480 hours.
On the other hand, in the belts of Comparative Examples 2, 4, and 5, tooth chipping occurred in 24 hours and the life was shortened.
本発明は、Ｖベルト、Ｖリブドベルト、歯付ベルト等の伝達力向上及び伝達力を向上させたときの加工性の維持等に利用可能である。 INDUSTRIAL APPLICABILITY The present invention can be used to improve the transmission force of a V-belt, a V-ribbed belt, a toothed belt, etc. and maintain workability when the transmission force is improved.
１ 歯付ベルト
２ 背ゴム
３ 接着ゴム
４ 心線
５ 歯布
６ 歯ゴム
２１ Ｖベルト
３１ ベルト
３２ 駆動側プーリ（Ｄｒプーリ）
３３ 従動側プーリ（Ｄｎプーリ）
DESCRIPTION OF SYMBOLS 1
33 Driven pulley (Dn pulley)
Claims (24)