JP2008270634A - Electromagnetic-wave shield film, and manufacturing method thereof - Google Patents

Electromagnetic-wave shield film, and manufacturing method thereof Download PDF

Info

Publication number
JP2008270634A
JP2008270634A JP2007113929A JP2007113929A JP2008270634A JP 2008270634 A JP2008270634 A JP 2008270634A JP 2007113929 A JP2007113929 A JP 2007113929A JP 2007113929 A JP2007113929 A JP 2007113929A JP 2008270634 A JP2008270634 A JP 2008270634A
Authority
JP
Japan
Prior art keywords
mesh
shielding film
electromagnetic wave
wave shielding
frame
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2007113929A
Other languages
Japanese (ja)
Inventor
Masaru Iwagaki
賢 岩垣
Toshihiko Iwasaki
利彦 岩崎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Konica Minolta Inc
Original Assignee
Konica Minolta Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Konica Minolta Inc filed Critical Konica Minolta Inc
Priority to JP2007113929A priority Critical patent/JP2008270634A/en
Publication of JP2008270634A publication Critical patent/JP2008270634A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a manufacturing method of an electromagnetic-wave shield film wherein it has an excellent electromagnetic-wave shielding performance and a high transparency, and its mesh pattern has an excellent film-sticking property and reduced generations of winding-habit curls even in the longer continuous roll product thereof, and further, its panel has an excellent grounding property too, and moreover, its development-processing and plating unevennesses generated during its manufacture are improved. <P>SOLUTION: The electromagnetic-wave shield film is the one having continuous conductive mesh portion 1 and picture-frame portion 2 formed on a longer transparent supporting body wherein the conductivity of the picture-frame portion 2 is higher than that of the mesh portion 1, and they are constituted out of a geometric pattern. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

本発明は、携帯電話、電子レンジ、ＣＲＴ、及びフラットパネルディスプレイ等の電子機器から発生する電磁波を遮蔽する電磁波シールドフィルム及びその製造方法に関する。   The present invention relates to an electromagnetic wave shielding film that shields electromagnetic waves generated from electronic devices such as mobile phones, microwave ovens, CRTs, and flat panel displays, and a method for manufacturing the same.

近年、携帯電話やパソコン、ＴＶ等に用いられるディスプレイ装置等に代表されるような電子機器の使用機会が増加しているが、これらの電子機器からは一般に電磁波が放出され、それにより、電子、電気機器の誤動作、障害あるいは人体に対しても害を与える可能性がある等、いわゆる電磁波障害（ＥＭＩ）が生じることが知られている。それに伴い、このようなＥＭＩを低減する必要性が高まっており、欧米を中心に電磁波放出の強さに関する規格または規制が設けられ、最近の電子機器にはこれらの基準を満たすことが求められている。特に、ＣＲＴやフラットパネルディスプレイ、あるいは窓ガラスのように視認性を必要とする機材には電磁波遮蔽性能と、透明性を両立させることが必要である。   In recent years, there have been increasing opportunities to use electronic devices such as display devices used in mobile phones, personal computers, TVs, etc., but electromagnetic waves are generally emitted from these electronic devices, so that It is known that so-called electromagnetic interference (EMI) occurs, such as malfunction of electrical equipment, failure, or the possibility of harming the human body. Along with this, there is an increasing need to reduce such EMI, and standards or regulations regarding the intensity of electromagnetic wave emission are established mainly in Europe and the United States, and recent electronic devices are required to meet these standards. Yes. In particular, equipment that requires visibility such as a CRT, a flat panel display, or a window glass needs to satisfy both electromagnetic wave shielding performance and transparency.

これらは、透明樹脂フィルム上に導電性の金属パターンを設けたものが一般的であり、その生産効率向上のために、長尺ロールの透明樹脂フィルム上に連続する金属メッシュパターンを形成し、必要なサイズに裁断して電磁波シールドパネルに供される（特許文献１〜４参照）。   These are generally provided with a conductive metal pattern on a transparent resin film. In order to improve the production efficiency, a continuous metal mesh pattern is formed on the transparent resin film of a long roll, and is necessary. It cut | judged to an appropriate size and it uses for an electromagnetic wave shield panel (refer patent documents 1-4).

電磁波シールドフィルムの端部には、金属メッシュパターンが電磁波を吸収して発生した電流を有効に接地するための導通部を設けることが好ましく、この導通部を本発明では額縁部という。この額縁部は、細線と開口部からなるメッシュ部に比べて、導通性を高めるために一般に短冊状の枠を形成しており、接地線と接続される。   It is preferable to provide a conduction part for effectively grounding the current generated by the metal mesh pattern absorbing the electromagnetic wave at the end of the electromagnetic shielding film, and this conduction part is referred to as a frame part in the present invention. The frame portion generally has a strip-like frame to improve conductivity as compared with a mesh portion composed of a fine line and an opening, and is connected to a ground wire.

前記長尺ロールによる電磁波シールドフィルムの連続生産においては、前期のメッシュ部と額縁部のパターンの相違によって、額縁部の膜はがれが発生したり、巻き癖カールが発生しやすい等の問題がある。特に、ハロゲン化銀感光材料を露光後、現像処理し、めっき等の補力処理によってメッシュパターンを形成する場合は、従来のスパッタ法や印刷法に比べて安価で生産性が高いが、上記問題に加えて現像処理ムラやめっきムラが発生する問題がある。
国際公開第０１／０５１２７６号パンフレット 特開２００４−２２１５６４号公報 国際公開第０４／００７８１０号パンフレット 国際公開第０６／０８８０５９号パンフレット In the continuous production of the electromagnetic wave shielding film by the long roll, there are problems such as film peeling at the frame part and curling curl easily due to the difference in the pattern of the mesh part and the frame part in the previous period. In particular, when a silver halide photosensitive material is exposed and developed, and a mesh pattern is formed by an intensifying process such as plating, it is cheaper and more productive than conventional sputtering and printing methods. In addition to this, there is a problem that uneven development processing and uneven plating occur.
International Publication No. 01/051276 Pamphlet JP 2004-221564 A International Publication No. 04/007810 Pamphlet International Publication No. 06/088059 Pamphlet

本発明は、上記課題に鑑みなされたものであり、その目的は電磁波遮蔽性能に優れ、かつ高い透明性を有し、さらに長尺連続ロール生産においても、メッシュパターンの膜付きに優れ、巻き癖カールの発生が小さく、パネルの接地性にも優れた電磁波シールドフィルムを提供することにある。さらに、電磁波シールドフィルム製造中に発生する現像処理ムラ、めっきムラを改善した電磁波シールドフィルムの製造方法を提供することにある。   The present invention has been made in view of the above-mentioned problems, and its purpose is excellent in electromagnetic wave shielding performance and high transparency. Further, even in the production of long continuous rolls, it has excellent mesh pattern coating, An object of the present invention is to provide an electromagnetic wave shielding film which is small in curling and excellent in grounding property of a panel. Furthermore, it is providing the manufacturing method of the electromagnetic wave shield film which improved the development process nonuniformity and plating nonuniformity which generate | occur | produce during electromagnetic wave shield film manufacture.

本発明の上記課題は、以下の構成により達成される。   The above object of the present invention is achieved by the following configurations.

１．長尺の透明支持体上に形成された、連続する導電性のメッシュ部と額縁部とを有する電磁波シールドフィルムであって、前記額縁部が前記メッシュ部より導電性が高い幾何学パターンであることを特徴とする電磁波シールドフィルム。   1. An electromagnetic wave shielding film having a continuous conductive mesh portion and a frame portion formed on a long transparent support, wherein the frame portion is a geometric pattern having a higher conductivity than the mesh portion. An electromagnetic shielding film characterized by.

２．前記導電性が高い幾何学パターンが、メッシュ部より開口率が小さい額縁メッシュであることを特徴とする前記１に記載の電磁波シールドフィルム。   2. 2. The electromagnetic wave shielding film as described in 1 above, wherein the geometric pattern having high conductivity is a frame mesh having an aperture ratio smaller than that of the mesh portion.

３．前記開口率が小さい額縁メッシュが、メッシュ部よりピッチが小さい額縁メッシュであることを特徴とする前記２に記載の電磁波シールドフィルム。   3. 3. The electromagnetic wave shielding film as described in 2 above, wherein the frame mesh having a small opening ratio is a frame mesh having a smaller pitch than the mesh portion.

４．前記開口率が小さい額縁メッシュが、メッシュ部より線幅が大きい額縁メッシュであることを特徴とする前記２または３に記載の電磁波シールドフィルム。   4). 4. The electromagnetic wave shielding film as described in 2 or 3 above, wherein the frame mesh having a small opening ratio is a frame mesh having a line width larger than that of the mesh portion.

５．前記導電性が高い幾何学パターンが、メッシュ部より厚さが大きい額縁メッシュであることを特徴とする前記１〜４のいずれか１項に記載の電磁波シールドフィルム。   5. 5. The electromagnetic wave shielding film according to any one of 1 to 4, wherein the geometric pattern having high conductivity is a frame mesh having a thickness larger than that of the mesh portion.

６．長尺の透明支持体上に、少なくとも感光性ハロゲン化銀及びバインダーからなる層を塗布したハロゲン化銀感光材料を、パターン露光後、現像処理及びめっきを行って、連続する導電性のメッシュ部と幾何学パターンの額縁部とを形成する透明電磁波シールドフィルムの製造方法において、前記額縁部を前記メッシュ部より導電性を高くする工程を有することを特徴とする電磁波シールドフィルムの製造方法。   6). A silver halide photosensitive material in which a layer comprising at least a photosensitive silver halide and a binder is coated on a long transparent support, and after pattern exposure, development processing and plating are performed, and a continuous conductive mesh portion and In the manufacturing method of the transparent electromagnetic wave shielding film which forms the frame part of a geometric pattern, The manufacturing method of the electromagnetic wave shielding film characterized by having the process which makes the said frame part highly conductive rather than the said mesh part.

７．前記導電性を高くする工程が、ハロゲン化銀乳剤塗布時に額縁部相当領域を厚く塗布する工程であることを特徴とする前記６の電磁波シールドフィルムの製造方法。   7. 6. The method for producing an electromagnetic wave shielding film as described in 6 above, wherein the step of increasing the conductivity is a step of thickly applying a region corresponding to the frame portion at the time of applying the silver halide emulsion.

８．前記導電性を高くする工程が、額縁部の幾何学パターンのピッチをメッシュ部よりも小さく露光する工程であることを特徴とする前記６に記載の電磁波シールドフィルムの製造方法。   8). 7. The method for producing an electromagnetic wave shielding film as described in 6 above, wherein the step of increasing the conductivity is a step of exposing the pitch of the geometric pattern of the frame portion to be smaller than that of the mesh portion.

９．前記導電性を高くする工程が、額縁部の幾何学パターンの線幅を太く露光する工程であることを特徴とする前記６に記載の電磁波シールドフィルムの製造方法。   9. 7. The method for producing an electromagnetic wave shielding film as described in 6 above, wherein the step of increasing the conductivity is a step of exposing the line width of the geometric pattern of the frame portion to be thick.

１０．前記導電性を高くする工程が、額縁部の現像処理を促進する工程であることを特徴とする前記６に記載の電磁波シールドフィルムの製造方法。   10. 7. The method for producing an electromagnetic wave shielding film as described in 6 above, wherein the step of increasing the conductivity is a step of accelerating development processing of the frame portion.

１１．前記導電性を高くする工程が、額縁部のめっきを促進する工程であることを特徴とする前記６に記載の電磁波シールドフィルムの製造方法。   11. 7. The method for producing an electromagnetic wave shielding film as described in 6 above, wherein the step of increasing the conductivity is a step of accelerating the plating of the frame portion.

１２．前記導電性を高くする工程が、額縁部を金めっきする工程であることを特徴とする前記６に記載の電磁波シールドフィルムの製造方法。   12 7. The method for producing an electromagnetic wave shielding film as described in 6 above, wherein the step of increasing the conductivity is a step of gold-plating the frame portion.

１３．前記導電性を高くする工程が、額縁部を加圧、加熱または加圧後加熱する工程であることを特徴とする前記６に記載の電磁波シールドフィルムの製造方法。   13. 7. The method for producing an electromagnetic wave shielding film as described in 6 above, wherein the step of increasing the conductivity is a step of pressurizing, heating or heating the frame portion after pressurization.

本発明によれば、電磁波遮蔽性能に優れ、かつ高い透明性を有し、さらに長尺連続ロール生産においても、メッシュパターンの膜付きに優れ、巻き癖カールの発生が小さく、パネルの接地性にも優れた電磁波シールドフィルムを提供することができる。さらに、電磁波シールドフィルム製造中に発生する現像処理ムラ、めっきムラを改善した電磁波シールドフィルムの製造方法を提供することができる。   According to the present invention, it has excellent electromagnetic wave shielding performance and high transparency, and even in production of long continuous rolls, it has excellent mesh pattern coating, less curl curl generation, and good panel grounding. Can also provide an excellent electromagnetic shielding film. Furthermore, the manufacturing method of the electromagnetic wave shielding film which improved the development processing nonuniformity generate | occur | produced during electromagnetic wave shielding film manufacture and plating nonuniformity can be provided.

本発明者らは上記課題について検討した結果、金属メッシュパターンの額縁部を改良することによって、優れた電磁波シールドフィルム及びその製造方法が得られることを見い出した。   As a result of studying the above problems, the present inventors have found that an excellent electromagnetic shielding film and a method for producing the same can be obtained by improving the frame portion of the metal mesh pattern.

本発明の電磁波シールドフィルムは、長尺の透明支持体上に形成された、連続する導電性のメッシュ部と額縁部とを有する電磁波シールドフィルムであって、前記額縁部が前記メッシュ部よりも導電性が高い幾何学パターンであることを特徴とする。   The electromagnetic wave shielding film of the present invention is an electromagnetic wave shielding film having a continuous conductive mesh portion and a frame portion formed on a long transparent support, wherein the frame portion is more conductive than the mesh portion. It is characterized by a highly geometric pattern.

（透明支持体）
本発明において長尺の透明支持体（以下、単に支持体ともいう）としては、通常の合成樹脂フィルムを用いることができる。 (Transparent support)
In the present invention, a normal synthetic resin film can be used as a long transparent support (hereinafter also simply referred to as a support).

例えば、セルロースエステル系フィルム、ポリエステル系フィルム、ポリカーボネート系フィルム、ポリアリレート系フィルム、ポリスルホン（ポリエーテルスルホンも含む）系フィルム、ポリエチレンテレフタレート、ポリエチレンナフタレート等のポリエステルフィルム、ポリエチレンフィルム、ポリプロピレンフィルム、セロファン、セルロースジアセテートフィルム、セルロースアセテートブチレートフィルム、ポリ塩化ビニリデンフィルム、ポリビニルアルコールフィルム、エチレンビニルアルコールフィルム、シンジオタクティックポリスチレン系フィルム、ポリカーボネートフィルム、ノルボルネン樹脂系フィルム、ポリメチルペンテンフィルム、ポリエーテルケトンフィルム、ポリエーテルケトンイミドフィルム、ポリアミドフィルム、フッ素樹脂フィルム、ナイロンフィルム、ポリメチルメタクリレートフィルムまたはアクリルフィルム等を用いることができる。また、これらプラスチックフィルム以外に、石英ガラス、ソーダガラス等も用いることが可能である。   For example, cellulose ester film, polyester film, polycarbonate film, polyarylate film, polysulfone (including polyethersulfone) film, polyethylene terephthalate, polyethylene naphthalate polyester film, polyethylene film, polypropylene film, cellophane, Cellulose diacetate film, cellulose acetate butyrate film, polyvinylidene chloride film, polyvinyl alcohol film, ethylene vinyl alcohol film, syndiotactic polystyrene film, polycarbonate film, norbornene resin film, polymethylpentene film, polyether ketone film, Polyetherketoneimide film, polyamid Film, fluororesin film, a nylon film, a polymethyl methacrylate film or an acrylic film or the like. In addition to these plastic films, quartz glass, soda glass, and the like can be used.

中でも、セルローストリアセテートフィルム、ポリカーボネートフィルム、ポリスルホン（ポリエーテルスルホンを含む）、ポリエチレンテレフタレートフィルム、ポリエチレンナフタレートフィルムが好ましく用いられる。本発明においては、透明性、等方性、接着性、耐久性等の観点から、支持体としてはポリエステル系フィルムであるポリエチレンテレフタレートフィルム、ポリエチレンナフタレートフィルムを用いることが特に好ましい。   Of these, cellulose triacetate film, polycarbonate film, polysulfone (including polyethersulfone), polyethylene terephthalate film, and polyethylene naphthalate film are preferably used. In the present invention, it is particularly preferable to use a polyethylene terephthalate film or a polyethylene naphthalate film that is a polyester film as the support from the viewpoints of transparency, isotropic properties, adhesiveness, durability, and the like.

本発明の電磁波シールドフィルムをディスプレイの表示画面に用いる場合には、高い透明性が要求されるため、支持体自体の透明性も高いことが望ましい。この場合における支持体であるプラスチックフィルムまたはガラス板の可視光域の平均透過率は、好ましくは８５〜１００％であり、より好ましくは９０〜１００％である。また、本発明では、色調調節剤として前記プラスチックフィルムまたはガラス板を本発明の目的を妨げない程度に着色したものを用いることもできる。可視光域の平均透過率とは、４００〜７００ｎｍの可視光領域の透過率を、少なくとも５ｎｍ毎に測定して求めた可視光域の各透過率を積算し、その平均値として求めたものと定義する。測定においては、測定アパチャーを、前述のメッシュパターンより十分大きくとっておく必要があり、少なくともメッシュの格子面積より１００倍以上大きな面積で測定して求める。   When the electromagnetic wave shielding film of the present invention is used for a display screen of a display, high transparency is required. Therefore, it is desirable that the support itself has high transparency. The average transmittance in the visible light region of the plastic film or glass plate as the support in this case is preferably 85 to 100%, more preferably 90 to 100%. Moreover, in this invention, what colored the said plastic film or glass plate to the extent which does not interfere with the objective of this invention can also be used as a color tone regulator. The average transmittance in the visible light region is obtained by integrating the transmittances in the visible light region obtained by measuring the transmittance in the visible light region of 400 to 700 nm at least every 5 nm, and obtaining the average value thereof. Define. In measurement, the measurement aperture needs to be sufficiently larger than the mesh pattern described above, and is obtained by measuring at least an area 100 times larger than the mesh area of the mesh.

本発明に用いる支持体は、長尺ロール状として連続搬送しながら生産するために、１００ｍ以上、より好ましくは５００ｍ以上、さらに好ましくは１０００ｍ以上、２０００ｍ以下である。   The support used in the present invention is 100 m or more, more preferably 500 m or more, still more preferably 1000 m or more and 2000 m or less in order to produce the continuous support as a long roll.

本発明に用いる支持体の幅は、より大画面のディスプレイパネル用の要望から１ｍ以上、好ましくは１．５ｍ以上、さらに好ましくは、２ｍ以上、５ｍ以下である。   The width of the support used in the present invention is 1 m or more, preferably 1.5 m or more, and more preferably 2 m or more and 5 m or less because of the demand for a display panel with a larger screen.

本発明に用いる支持体の厚さには特に制限はないが、透過率の維持及び取り扱い性の観点から、５〜２００μｍであることが好ましく、３０〜１５０μｍであることがさらに好ましい。   Although there is no restriction | limiting in particular in the thickness of the support body used for this invention, It is preferable that it is 5-200 micrometers from a viewpoint of the maintenance of a transmittance | permeability, and a handleability, and it is further more preferable that it is 30-150 micrometers.

（メッシュ部）
電磁波を遮蔽するために形成される導電性の金属メッシュ部の線幅は、通常２０μｍ以下であり、メッシュを目立たせなくする観点からは、１８μｍ以下が好ましく、１５μｍ以下がさらに好ましく、３μｍ以上、１０μｍ以下が最も好ましい。３μｍ未満では導電性がやや不足する。 (Mesh part)
The line width of the conductive metal mesh portion formed to shield electromagnetic waves is usually 20 μm or less, preferably 18 μm or less, more preferably 15 μm or less, more preferably 3 μm or more, from the viewpoint of making the mesh inconspicuous. 10 μm or less is most preferable. If it is less than 3 μm, the conductivity is slightly insufficient.

メッシュ部の線間隔は１５０μｍ以上であることが好ましく、１８０μｍ以上がより好ましく、２００μｍ以上が特に好ましい。また、メッシュ細線の厚さは、０．１μｍ以上、２５μｍ以下が好ましく、０．２以上、２０μｍ以下がより好ましく、０．５μｍ以上、１５μｍ以下が特に好ましい。   The line spacing of the mesh part is preferably 150 μm or more, more preferably 180 μm or more, and particularly preferably 200 μm or more. The thickness of the fine mesh wire is preferably 0.1 μm or more and 25 μm or less, more preferably 0.2 or more and 20 μm or less, and particularly preferably 0.5 μm or more and 15 μm or less.

本発明におけるメッシュ部は、可視光透過率の観点から開口率は８０％より大きいことが好ましく、８５％以上がさらに好ましく、９０％以上が最も好ましい。開口率とは、メッシュをなす細線のない部分が全体に占める割合であり、例えば、線幅１０μｍ、ピッチ２００μｍの正方形の格子状メッシュの開口率は９０％である。   In the mesh portion of the present invention, the aperture ratio is preferably larger than 80%, more preferably 85% or more, and most preferably 90% or more from the viewpoint of visible light transmittance. The aperture ratio is the ratio of the portion without fine lines forming the mesh to the whole. For example, the aperture ratio of a square lattice mesh having a line width of 10 μm and a pitch of 200 μm is 90%.

本発明においては、高い透光性と高い電磁波遮蔽性能を付与するために、格子状の細線メッシュパターンを露光により描画し、次いで現像処理等を行うことで、導電性のメッシュパターンを形成し、電磁波シールドフィルムとすることが好ましい。   In the present invention, in order to give high translucency and high electromagnetic wave shielding performance, a lattice-like fine line mesh pattern is drawn by exposure, and then a development process or the like is performed to form a conductive mesh pattern. An electromagnetic wave shielding film is preferred.

（額縁部）
額縁部とは、メッシュ部で電磁波を吸収して発生する電流を接地するための接続部分であり、一般的には導通性を高めるために短冊状の枠を形成している。本発明においては、この額縁部が幾何学パターンであることを特徴とする。 (Frame part)
The frame portion is a connection portion for grounding a current generated by absorbing electromagnetic waves in the mesh portion, and generally forms a strip-shaped frame in order to improve conductivity. In the present invention, the frame portion is a geometric pattern.

幾何学パターンとは、多角形、円、楕円、星形等の基本図形を連続的に配列したものをいう。   A geometric pattern is a pattern in which basic figures such as polygons, circles, ellipses, and stars are continuously arranged.

本発明において、額縁部の導電性がメッシュ部よりも高い幾何学パターンとするためには、メッシュ部よりも開口率を小さくすること、メッシュ部よりもピッチを小さくすること、メッシュ部よりも線幅を大きくすること、メッシュ部よりも細線の厚さを大きくすること、等がある。   In the present invention, in order to obtain a geometric pattern in which the conductivity of the frame portion is higher than that of the mesh portion, the aperture ratio is made smaller than that of the mesh portion, the pitch is made smaller than that of the mesh portion, and the line is made more than the mesh portion. For example, the width is increased, and the thickness of the fine line is increased more than the mesh portion.

本発明において、額縁部の前記導電性が高い幾何学パターンが、メッシュ部よりも開口率が小さい電磁波シールドフィルムが好ましい。前記のように、メッシュ部は開口率が高いことが好ましいが、額縁メッシュ部は、好ましくは１０％以上、８０％以下、より好ましくは１０％以上、７０％以下である。１０％よりも小さいと本発明の効果が小さく、８０％よりも高いと接地性が不充分となる。   In the present invention, an electromagnetic wave shielding film in which the geometric pattern having high conductivity in the frame portion has a smaller aperture ratio than the mesh portion is preferable. As described above, the mesh portion preferably has a high aperture ratio, but the frame mesh portion is preferably 10% or more and 80% or less, more preferably 10% or more and 70% or less. If it is less than 10%, the effect of the present invention is small, and if it is more than 80%, the grounding property is insufficient.

前記開口率が小さい幾何学パターンとするには、中央部よりも額縁メッシュ部の線間隔（ピッチ）を小さくすることによって達成される。額縁メッシュ部のピッチは、１３０μｍ以下であることが好ましく、１００μｍ以下がより好ましく、１０μｍ以上、９０μｍ以下が特に好ましい。   The geometric pattern having a small aperture ratio can be achieved by reducing the line interval (pitch) of the frame mesh portion smaller than the center portion. The pitch of the frame mesh portion is preferably 130 μm or less, more preferably 100 μm or less, and particularly preferably 10 μm or more and 90 μm or less.

前記開口率が小さい幾何学パターンとするには、中央部よりも額縁メッシュ部の線幅を大きくすることによっても達成される。額縁メッシュ部の線幅は、３０μｍ以上が好ましく、５０μｍ以上がより好ましく、７０μｍ以上が特に好ましい。   The geometric pattern having a small aperture ratio can also be achieved by increasing the line width of the frame mesh portion rather than the central portion. The line width of the frame mesh portion is preferably 30 μm or more, more preferably 50 μm or more, and particularly preferably 70 μm or more.

本発明において、額縁部の前記導電性が高い幾何学パターンが、メッシュ部よりも細線の厚さが大きい電磁波シールドフィルムが好ましい。額縁メッシュ部の細線の厚さを大きくして導電性を高める場合は、２５μｍよりも大きいことが好ましく、３０μｍ以上がより好ましく、３５μｍ以上が特に好ましい。   In the present invention, an electromagnetic wave shielding film in which the geometric pattern having high conductivity of the frame portion has a fine line thickness larger than that of the mesh portion is preferable. When increasing the thickness of the fine line of the frame mesh part to increase the conductivity, it is preferably larger than 25 μm, more preferably 30 μm or more, and particularly preferably 35 μm or more.

（メッシュの形成方法）
本発明の電磁波シールドフィルムにおいては、電磁波シールド機能を有する導電性メッシュの形成方法は、公知の方法すなわち、蒸着法、各種印刷法（グラビア印刷、スクリーン印刷、インクジェット印刷等）、エッチング法、フォトリソグラフィック法等を利用できるが、ハロゲン化銀感光材料を露光、現像処理、必要に応じて補力処理等を行って形成する銀塩写真法が好ましい。 (Mesh formation method)
In the electromagnetic wave shielding film of the present invention, a method for forming a conductive mesh having an electromagnetic wave shielding function is a known method, that is, a vapor deposition method, various printing methods (gravure printing, screen printing, ink jet printing, etc.), etching method, photolithographic method. A silver salt photographic method in which a silver halide light-sensitive material is formed by exposure, development processing, and intensification processing as necessary is preferable.

本発明の電磁波シールドフィルムを銀塩写真法を用いて形成する場合は、後述する感光性ハロゲン化銀及びバインダーを含有するハロゲン化銀乳剤層が支持体上に設けられるが、ハロゲン化銀乳剤層は、この他に、硬膜剤、硬調化剤、活性剤等を含有することができる。   When the electromagnetic wave shielding film of the present invention is formed using a silver salt photographic method, a silver halide emulsion layer containing a photosensitive silver halide and a binder described later is provided on the support. In addition to this, a hardening agent, a thickening agent, an activator, etc. can be contained.

（感光性ハロゲン化銀）
本発明において、感光性ハロゲン化銀の含有量は、銀換算で０．０５ｇ／ｍ2以上、３ｇ／ｍ2未満であることが好ましく、特に好ましくは銀換算で０．３ｇ／ｍ2以上、１ｇ／ｍ2未満である。感光性ハロゲン化銀の含有量が０．０５ｇ／ｍ2未満の場合、電磁波遮蔽性能を十分に得ることが困難になりやすい。これは、後述する物理現像または金属めっき処理の触媒となる現像銀核の量が不十分となり、有効な導電性メッシュを形成しにくくなるためと推定される。また、感光性ハロゲン化銀の含有量が３ｇ／ｍ2以上である場合、バインダーに対するハロゲン化銀の量が相対的に多くなるため、被膜が脆弱になりやすく、十分な被膜強度を維持することが困難となる。 (Photosensitive silver halide)
In the present invention, the content of photosensitive silver halide in terms of silver in 0.05 g / m 2 or more, preferably less than 3 g / m 2, particularly preferably in terms of silver 0.3 g / m 2 or more, It is less than 1 g / m 2 . When the photosensitive silver halide content is less than 0.05 g / m 2 , it is difficult to obtain sufficient electromagnetic wave shielding performance. This is presumed to be because the amount of developed silver nuclei serving as a catalyst for physical development or metal plating treatment described later becomes insufficient and it becomes difficult to form an effective conductive mesh. In addition, when the photosensitive silver halide content is 3 g / m 2 or more, the amount of silver halide relative to the binder is relatively large, so that the coating tends to become brittle and maintain sufficient coating strength. It becomes difficult.

被膜物性を維持するためにバインダー量を増やした場合、感光性ハロゲン化銀の粒子間距離が大きくなるため、現像銀ネットワークが形成されにくくなり、有効な導電性メッシュを形成しにくくなるとともに、温度、湿度変化に対する耐久性も不十分となり本発明の効果が得られ難くなる。   When the amount of the binder is increased to maintain the physical properties of the film, the distance between the grains of the photosensitive silver halide increases, so that it becomes difficult to form a developed silver network, it is difficult to form an effective conductive mesh, and the temperature Further, the durability against humidity change becomes insufficient, and the effect of the present invention is hardly obtained.

本発明において、ハロゲン化銀感光材料のバインダー量は１０ｍｇ／ｍ2以上、０．２ｇ／ｍ2以下の場合が、導電性と被膜物性の両立という観点から特に好ましい。バインダー量が１０ｍｇ／ｍ2未満の場合、バインダーに対するハロゲン化銀の量が相対的に多くなるため、被膜が脆弱になりやすく、十分な被膜強度を維持することが困難となる。また、バインダー量が０．１ｇ／ｍ2より多い場合には、感光性ハロゲン化銀粒子の粒子間距離が大きくなるため、現像銀ネットワークが形成されにくくなり、有効な導電性メッシュを形成しにくくなるとともに、温度、湿度変化に対する耐久性も不十分となり本発明の効果が得られなくなる。 In the present invention, the binder amount of the silver halide light-sensitive material is particularly preferably 10 mg / m 2 or more and 0.2 g / m 2 or less from the viewpoint of achieving both conductivity and film properties. When the amount of the binder is less than 10 mg / m 2, the amount of silver halide relative to the binder is relatively large, so that the coating tends to become brittle and it is difficult to maintain sufficient coating strength. In addition, when the amount of the binder is more than 0.1 g / m 2 , the distance between the photosensitive silver halide grains is increased, so that it is difficult to form a developed silver network, and it is difficult to form an effective conductive mesh. In addition, the durability against changes in temperature and humidity becomes insufficient, and the effects of the present invention cannot be obtained.

本発明に用いられるハロゲン化銀粒子の組成は、塩化銀、臭化銀、塩臭化銀、沃臭化銀、塩沃臭化銀、塩沃化銀等、任意のハロゲン組成を有するものであってもよいが、導電性のよい金属銀を得るためには、感度の高い微粒子が好ましく、沃臭化銀粒子が好ましく用いられる。沃素を多く含むようにすると感度も高く微粒子にすることができる。   The composition of the silver halide grains used in the present invention has an arbitrary halogen composition such as silver chloride, silver bromide, silver chlorobromide, silver iodobromide, silver chloroiodobromide and silver chloroiodide. However, in order to obtain metallic silver having good conductivity, fine grains having high sensitivity are preferable, and silver iodobromide grains are preferably used. When a large amount of iodine is contained, the sensitivity is high and the particles can be made fine.

ハロゲン化銀粒子が現像され金属銀粒子になった後の表面比抵抗を下げ、電磁波を効率的に遮蔽するためには、現像銀粒子同士の接触面積ができるだけ大きくなる必要がある。そのためには表面積比を高めるためにハロゲン化銀粒子サイズが小さい程よいが、小さすぎる粒子は凝集して大きな塊状になりやすく、その場合接触面積は逆に少なくなってしまうので最適な粒子径が存在する。本発明において、ハロゲン化銀粒子の平均粒子サイズは、球相当径で０．０１〜０．５μｍが好ましく、より好ましくは０．０３〜０．３μｍである。なお、ハロゲン化銀粒子の球相当径とは、粒子形状が球形の同じ体積を有する粒子の直径を表す。ハロゲン化銀粒子の平均粒子サイズは、ハロゲン化銀粒子の調製時の温度、ｐＡｇ、ｐＨ、銀イオン溶液とハロゲン溶液の添加速度、粒子径コントロール剤（例えば、１−フェニル−５−メルカプトテトラゾール、２−メルカプトベンズイミダゾール、ベンズトリアゾール、テトラザインデン化合物類、核酸誘導体類、チオエーテル化合物類等）を適宜組み合わせて制御することができる。   In order to reduce the surface specific resistance after silver halide grains are developed to become metallic silver grains and effectively shield electromagnetic waves, the contact area between developed silver grains needs to be as large as possible. For this purpose, a smaller silver halide grain size is better to increase the surface area ratio, but too small grains tend to agglomerate into large agglomerates, in which case the contact area will be reduced, so there is an optimum grain size. To do. In the present invention, the average grain size of the silver halide grains is preferably 0.01 to 0.5 μm, more preferably 0.03 to 0.3 μm, in terms of a sphere equivalent diameter. In addition, the sphere equivalent diameter of silver halide grains represents the diameter of grains having the same volume and having a spherical shape. The average grain size of silver halide grains is the temperature at the time of preparation of silver halide grains, pAg, pH, addition rate of silver ion solution and halogen solution, grain size control agent (for example, 1-phenyl-5-mercaptotetrazole, 2-mercaptobenzimidazole, benztriazole, tetrazaindene compounds, nucleic acid derivatives, thioether compounds, etc.) can be appropriately combined and controlled.

本発明においては、塗布銀量（ｇ／ｍ2）を粒径（μｍ）で除した値が６〜２５となることが好ましい。比較的粒径の小さい感光性ハロゲン化銀を多量に用いた場合に、この値が２５より大きくなりやすく、この場合、フィルム断裁時のエッジ部分において、被膜からハロゲン化銀粒子の滑落等が生じやすくなる傾向にある。また、比較的粒径の大きい感光性ハロゲン化銀を少量用いた場合にこの値が６より小さくなりやすく、この場合、単位面積中の感光性ハロゲン化銀の粒子個数が少なくなるため、導電性が低下しやすい傾向となるためである。 In the present invention, the value obtained by dividing the coating silver amount (g / m 2 ) by the particle size (μm) is preferably 6 to 25. When a large amount of photosensitive silver halide having a relatively small particle size is used, this value tends to be larger than 25. In this case, the silver halide grains slip off from the coating at the edge when the film is cut. It tends to be easier. Further, when a small amount of photosensitive silver halide having a relatively large particle diameter is used, this value tends to be smaller than 6, and in this case, the number of photosensitive silver halide grains in a unit area is reduced, so that This is because it tends to decrease.

本発明においては、ハロゲン化銀粒子の形状は特に限定されず、例えば、球状、立方体状、平板状（６角平板状、３角形平板状、４角形平板状等）、８面体状、１４面体状等、さまざまな形状であることができる。感度を高くするためにアスペクト比が２以上や４以上、さらに８〜１６であるような平板粒子も好ましく使用することができる。粒子サイズの分布には特に限定はないが、露光によるパターン形成時に、パターンの輪郭をシャープに再現させ、高い導電性を維持しながら透明性を高めるという観点からは、狭い分布が好ましい。本発明に係るハロゲン化銀感光材料に用いられるハロゲン化銀粒子の粒径分布は、好ましくは変動係数が０．２２以下、さらに好ましくは０．１５以下の単分散ハロゲン化銀粒子である。ここで変動係数は、粒径分布の広さを表す係数であり、次式によって定義される。   In the present invention, the shape of the silver halide grains is not particularly limited, and for example, spherical, cubic, flat plate (hexagonal flat plate, triangular flat plate, tetragonal flat plate, etc.), octahedron, tetrahedron It can be in various shapes such as shapes. In order to increase the sensitivity, tabular grains having an aspect ratio of 2 or more, 4 or more, and further 8 to 16 can be preferably used. The particle size distribution is not particularly limited, but a narrow distribution is preferable from the viewpoint of enhancing the transparency while sharply reproducing the outline of the pattern and maintaining high conductivity during pattern formation by exposure. The particle size distribution of the silver halide grains used in the silver halide photosensitive material according to the present invention is preferably monodispersed silver halide grains having a coefficient of variation of 0.22 or less, more preferably 0.15 or less. Here, the variation coefficient is a coefficient representing the breadth of the particle size distribution, and is defined by the following equation.

変動係数＝Ｓ／Ｒ
（式中、Ｓは粒径分布の標準偏差、Ｒは平均粒径を表す。）
本発明で用いられるハロゲン化銀粒子は、さらに他の元素を含有していてもよい。例えば、写真乳剤において、硬調な乳剤を得るために用いられる金属イオンをドープすることも有用である。特に鉄イオン、ロジウムイオン、ルテニウムイオンやイリジウムイオン等の第８〜１０族金属イオンは、金属銀像の生成の際に露光部と未露光部の差が明確に生じやすくなるため好ましく用いられる。 Coefficient of variation = S / R
(In the formula, S represents the standard deviation of the particle size distribution, and R represents the average particle size.)
The silver halide grains used in the present invention may further contain other elements. For example, in a photographic emulsion, it is also useful to dope metal ions used to obtain a high-contrast emulsion. In particular, Group 8-10 metal ions such as iron ion, rhodium ion, ruthenium ion and iridium ion are preferably used because the difference between the exposed portion and the unexposed portion tends to be clearly generated when the metal silver image is generated.

これらの金属イオンは、塩や錯塩の形でハロゲン化銀乳剤に添加することができる。ロジウムイオン、イリジウムイオンに代表される遷移金属イオンは、各種の配位子を有する化合物であることもできる。そのような配位子としては、例えば、シアン化物イオンやハロゲンイオン、チオシアナートイオン、ニトロシルイオン、水、水酸化物イオン等を挙げることができる。具体的な化合物の例としては、臭化ロジウム酸カリウムやイリジウム酸カリウム等が挙げられる。   These metal ions can be added to the silver halide emulsion in the form of a salt or a complex salt. Transition metal ions represented by rhodium ions and iridium ions can also be compounds having various ligands. Examples of such a ligand include cyanide ions, halogen ions, thiocyanate ions, nitrosyl ions, water, hydroxide ions, and the like. Specific examples of the compound include potassium bromide rhodate and potassium iridate.

本発明において、ハロゲン化銀に含有される前記金属イオン化合物の含有率は、ハロゲン化銀１モル当たり、１０-10〜１０-2モル／モルＡｇであることが好ましく、１０-9〜１０-3モル／モルＡｇであることがさらに好ましい。 In the present invention, the content of the metal ion compound contained in the silver halide is preferably 10 −10 to 10 −2 mol / mol Ag per mol of silver halide, and is preferably 10 −9 to 10 −. More preferably, it is 3 mol / mol Ag.

ハロゲン化銀粒子に上述の金属イオンを含有させるためには、該金属化合物をハロゲン化銀粒子の形成前、ハロゲン化銀粒子の形成中、ハロゲン化銀粒子の形成後等、物理熟成中の各工程における任意の場所で添加すればよい。また、添加においては、重金属化合物の溶液を粒子形成工程の全体あるいは一部にわたって連続的に行うことができる。   In order for silver halide grains to contain the above-described metal ions, the metal compound is subjected to physical ripening before formation of silver halide grains, during formation of silver halide grains, after formation of silver halide grains, etc. What is necessary is just to add in the arbitrary places in a process. Moreover, in addition, the solution of a heavy metal compound can be continuously performed over the whole or a part of particle formation process.

本発明では、さらに感度を向上させるため、写真乳剤で行われる化学増感を施したり、分光増感を施したりすることができる。   In the present invention, in order to further improve the sensitivity, chemical sensitization performed with a photographic emulsion or spectral sensitization can be performed.

（バインダー）
本発明に係るハロゲン化銀感光性層（少なくとも感光性ハロゲン化銀及びバインダーからなる層）において、ハロゲン化銀粒子を均一に分散させ、かつハロゲン化銀粒子を支持体上に担持し、ハロゲン化銀感光性層と他の層、または支持体との接着性を確保する目的でバインダーを用いる。本発明に用いることができるバインダーには、特に制限がなく、非水溶性ポリマー及び水溶性ポリマーのいずれも用いることができるが、現像性向上の観点からは、水溶性ポリマーを用いることが好ましい。 (binder)
In the silver halide light-sensitive layer according to the present invention (a layer comprising at least light-sensitive silver halide and a binder), silver halide grains are uniformly dispersed, and the silver halide grains are supported on a support, and halogenated. A binder is used for the purpose of ensuring the adhesiveness between the silver photosensitive layer and other layers or the support. The binder that can be used in the present invention is not particularly limited, and any of a water-insoluble polymer and a water-soluble polymer can be used. From the viewpoint of improving developability, it is preferable to use a water-soluble polymer.

本発明に係るハロゲン化銀感光材料には、バインダーとしてゼラチンを用いることが有利であるが、必要に応じてゼラチン誘導体、ゼラチンと他の高分子のグラフトポリマー、ゼラチン以外のタンパク質、糖誘導体、セルロース誘導体、単一あるいは共重合体のごとき合成親水性高分子物質等の親水性コロイドも用いることができる。   In the silver halide light-sensitive material according to the present invention, it is advantageous to use gelatin as a binder, but if necessary, gelatin derivatives, graft polymers of gelatin and other polymers, proteins other than gelatin, sugar derivatives, cellulose Hydrophilic colloids such as synthetic hydrophilic polymer materials such as derivatives, mono- or copolymers can also be used.

本発明においては、ハロゲン化銀感光性層の銀／バインダー質量比は０．５〜２０が好ましい。これは前述の、現像銀粒子同士の接触面積を大きくするためであり、より好ましくは１．０〜１０、さらに好ましくは３．０〜８．０である。   In the present invention, the silver / binder mass ratio of the silver halide photosensitive layer is preferably from 0.5 to 20. This is to increase the contact area between the developed silver particles described above, more preferably 1.0 to 10, and even more preferably 3.0 to 8.0.

（ハロゲン化銀感光材料の層構成）
本発明の電磁波シールドフィルムの形成に用いられるハロゲン化銀感光材料の層構成については、基本的には、支持体とハロゲン化銀感光性層からなる。さらに電磁波シールドフィルムとしての高機能化、加工特性、耐久性のみならず、ハロゲン化銀感光材料の製造効率、製造安定性等を考慮して、種々の層を設けることが好ましい。 (Layer structure of silver halide photosensitive material)
The layer structure of the silver halide photosensitive material used for forming the electromagnetic wave shielding film of the present invention basically comprises a support and a silver halide photosensitive layer. Furthermore, it is preferable to provide various layers in consideration of not only high functionality, processing characteristics and durability as an electromagnetic wave shielding film but also the production efficiency and production stability of the silver halide photosensitive material.

例えば、支持体とハロゲン化銀感光性層の間に非感光性中間層を設けたり、透明支持体に対してハロゲン化銀感光性層とは反対側に、バッキング層を設けたり、ハロゲン化銀感光性層の上に保護層を設けたりすることが好ましい。これらの層は複数層から構成されてもよい。   For example, a non-photosensitive intermediate layer is provided between the support and the silver halide photosensitive layer, a backing layer is provided on the opposite side of the transparent support from the silver halide photosensitive layer, or the silver halide is provided. It is preferable to provide a protective layer on the photosensitive layer. These layers may be composed of a plurality of layers.

本発明においては、支持体を挟んだ両側に各々ハロゲン化銀感光性層を設け、それぞれに導電性パターンを形成することも好ましく行われる。この場合、各々の面に塗設されるハロゲン化銀乳剤は、分光増感等により、それぞれ異なる波長に感度を有することが好ましい。表裏面で異なる波長に感度を持たせることにより、各々の面に異なる導電性パターンを作成することが可能となり、例えば表裏面で各々異なる周波数の電磁波に対して選択的に遮蔽効果を有するように導電性パターンを形成することも可能となる。   In the present invention, it is also preferable to provide a silver halide photosensitive layer on both sides of the support and to form a conductive pattern on each. In this case, it is preferable that the silver halide emulsion coated on each surface has sensitivity at different wavelengths by spectral sensitization or the like. By giving sensitivity to different wavelengths on the front and back surfaces, it becomes possible to create different conductive patterns on each surface, for example, to selectively shield against electromagnetic waves of different frequencies on the front and back surfaces. It is also possible to form a conductive pattern.

（電磁波シールドフィルムの製造方法）
本発明の電磁波シールドフィルムの製造方法は、長尺の透明支持体上に、少なくとも感光性ハロゲン化銀及びバインダーからなる層を塗布したハロゲン化銀感光材料を、パターン露光後、現像処理及びめっきを行って、連続する導電性のメッシュ部と、幾何学パターンの額縁部とを形成するものである。 (Method for producing electromagnetic shielding film)
In the method for producing an electromagnetic wave shielding film of the present invention, a silver halide photosensitive material in which a layer comprising at least a photosensitive silver halide and a binder is coated on a long transparent support is subjected to patterning exposure, development and plating. In this way, a continuous conductive mesh portion and a frame portion of the geometric pattern are formed.

従って、基本的には、（１）透明支持体上にハロゲン化銀乳剤を塗布してハロゲン化銀感光材料を形成する工程、（２）ハロゲン化銀感光材料にパターン露光する工程、（３）露光済みハロゲン化銀感光材料を現像処理する工程、（４）現像処理済みのハロゲン化銀感光材料をめっき処理する工程、からなるが、ハロゲン化銀乳剤を塗布する前の透明支持体の前処理や下塗り工程、塗布したハロゲン化銀感光材料を乾燥したりエージングする工程、現像処理済みのハロゲン化銀感光材料をめっき処理する前に物理現像する工程、めっき処理後に加圧加熱等の安定化処理する工程等を設けてもよい。   Therefore, basically, (1) a step of forming a silver halide photosensitive material by coating a silver halide emulsion on a transparent support, (2) a step of pattern exposure on the silver halide photosensitive material, (3) It comprises a step of developing the exposed silver halide photosensitive material, and (4) a step of plating the developed silver halide photosensitive material, but the pretreatment of the transparent support before coating the silver halide emulsion And undercoating process, drying and aging process of the coated silver halide photosensitive material, physical development process before plating the developed silver halide photosensitive material, stabilization process such as pressure heating after plating process You may provide the process to do.

これらの各工程は、それぞれ独立してバッチ処理してもよいが、支持体の繰り出しから、各工程が連続するウェブに対して連動していることが好ましい。最後は、形成された電磁波シールドフィルムが長尺巻として得られてもよいし、必要なサイズに裁断されてシート状にて集積されてもよい。   Each of these steps may be batch-processed independently, but it is preferable that each step is linked to a continuous web from the feeding of the support. Finally, the formed electromagnetic shielding film may be obtained as a long roll, or may be cut into a required size and accumulated in a sheet form.

（塗布工程）
塗布工程は、支持体上に前記構成層を塗布する工程である。塗布方法としては、例えば、ディップコート法、スプレーコート法、エアーナイフコート法、カーテンコート法、ローラーコート法、ワイヤーバーコート法、グラビヤコート法、インクジェットコート法あるいは米国特許第２，６８１，２９４号明細書に記載のホッパーを使用するエクストルージョンコート法等が挙げられる。また、必要に応じて、米国特許第２，７６１，７９１号、同第３，５０８，９４７号、同第２，９４１，８９８号及び同第３，５２６，５２８号明細書、原崎勇次著「コーティング工学」２５３頁（１９７３年朝倉書店発行）等に記載された２層以上の層を同時に塗布する方法も、好ましく用いることができる。 (Coating process)
A coating process is a process of apply | coating the said structural layer on a support body. Examples of the coating method include dip coating, spray coating, air knife coating, curtain coating, roller coating, wire bar coating, gravure coating, inkjet coating, or US Pat. No. 2,681,294. Examples include an extrusion coating method using the hopper described in the specification. If necessary, U.S. Pat. Nos. 2,761,791, 3,508,947, 2,941,898 and 3,526,528, Yuji Harasaki, “ The method of simultaneously applying two or more layers described in “Coating Engineering” on page 253 (published by Asakura Shoten in 1973) can also be preferably used.

なお、本発明においては、額縁部をメッシュ部よりも導電性を高くするために、ハロゲン化銀乳剤塗布時に額縁部相当領域を厚く塗布することによって、厚さが大きい額縁メッシュ部を形成することができる。   In the present invention, in order to make the frame portion more conductive than the mesh portion, a frame mesh portion having a large thickness is formed by thickly applying a region corresponding to the frame portion at the time of silver halide emulsion coating. Can do.

（露光工程）
本発明では、後述する現像処理、物理現像及びめっき処理から選ばれる少なくともいずれかを施して、導電性パターンを形成するために、ハロゲン化銀感光材料の露光を行う。露光に用いられる光源としては、例えば、紫外線、可視光線、赤外線等の光、電子線、Ｘ線等の放射線等が挙げられるが、ハロゲン化銀の特性を活用する点で、可視光線を用いることが好ましい。特に波長分布の狭い光源を利用することによって、電磁波シールドフィルム形成を効率よくコントロールでき、安定に製造できるので好ましい。 (Exposure process)
In the present invention, the silver halide photosensitive material is exposed to form a conductive pattern by performing at least one selected from development processing, physical development, and plating processing described later. Examples of the light source used for exposure include light such as ultraviolet rays, visible rays, and infrared rays, and radiation such as electron beams and X-rays. Visible rays are used in terms of utilizing the characteristics of silver halide. Is preferred. In particular, it is preferable to use a light source having a narrow wavelength distribution because the formation of the electromagnetic shielding film can be efficiently controlled and can be stably produced.

特に本発明では、レーザー光を用いて露光することが好ましい。種々のレーザー光の中でも、ハロゲン化銀の感光特性から、青色レーザーが好ましい。その発光波長が３７０〜４５０ｎｍ、特に４１５〜４４０ｎｍが好ましい。   In the present invention, it is particularly preferable to perform exposure using a laser beam. Among various laser beams, a blue laser is preferable because of the photosensitive characteristics of silver halide. The emission wavelength is preferably 370 to 450 nm, particularly 415 to 440 nm.

具体的には、ヘリウム・カドミウムレーザー（約４４２ｎｍ）、ＩｎＧａＮ系材料を用いた発振波長が４００〜４３０ｎｍの青色半導体レーザー、ＧａＡｌＡｓ系（発振波長８５０ｎｍ）の半導体レーザーを、ＭｇＯ：ＬｉＮｂＯ3のＳＨＧ結晶により波長変換して取り出したレーザー（４２５ｎｍ）等があるが、コンパクト、低消費電力、安定性、長寿命等の観点から、青色半導体レーザーが好ましい。特に、２００１年３月第４８回応用物理学関係連合講演会で日亜化学（株）発表の、青色半導体レーザーが好ましい。 Specifically, a helium-cadmium laser (about 442 nm), a blue semiconductor laser using an InGaN-based material with an oscillation wavelength of 400 to 430 nm, a GaAlAs-based (laser wavelength 850 nm) semiconductor laser, an MgO: LiNbO 3 SHG crystal. However, a blue semiconductor laser is preferable from the viewpoints of compactness, low power consumption, stability, long life, and the like. In particular, a blue semiconductor laser announced by Nichia Chemical Co., Ltd. at the 48th Applied Physics Related Conference in March 2001 is preferred.

なお、本発明においては、額縁部をメッシュ部よりも導電性を高くするために、ハロゲン化銀感光材料の額縁部相当領域の露光に際して、幾何学パターンのピッチをメッシュ部よりも小さく露光したり、幾何学パターンの線幅を太く露光することによって、額縁メッシュ部を形成することができる。   In the present invention, in order to make the frame portion more conductive than the mesh portion, when exposing the region corresponding to the frame portion of the silver halide photosensitive material, the geometric pattern pitch is exposed to be smaller than that of the mesh portion. The frame mesh portion can be formed by exposing the line width of the geometric pattern to be thick.

（現像処理）
本発明では、ハロゲン化銀感光材料を露光した後、現像処理が行われる。現像処理は、発色現像主薬を含有しない、いわゆる黒白現像処理であることが好ましい。 (Development processing)
In the present invention, after the silver halide photosensitive material is exposed, development processing is performed. The development process is preferably a so-called black-and-white development process that does not contain a color developing agent.

現像処理液としては、現像主薬としてハイドロキノン、ハイドロキノンスルホン酸ナトリウム、クロルハイドロキノン等のハイドロキノン類の他に、１−フェニル−３−ピラゾリドン、１−フェニル−４，４−ジメチル−３−ピラゾリドン、１−フェニル−４−メチル−４−ヒドロキシメチル−３−ピラゾリドン、１−フェニル−４−メチル−３−ピラゾリドン等のピラゾリドン類及びＮ−メチルパラアミノフェノール硫酸塩等の超加成性現像主薬と併用することができる。また、ハイドロキノンを使用しないでアスコルビン酸やイソアスコルビン酸等レダクトン類化合物を上記超加成性現像主薬と併用することが好ましい。   As the developing solution, in addition to hydroquinones such as hydroquinone, sodium hydroquinonesulfonate, chlorohydroquinone and the like as developing agents, 1-phenyl-3-pyrazolidone, 1-phenyl-4,4-dimethyl-3-pyrazolidone, 1- Use in combination with pyrazolidones such as phenyl-4-methyl-4-hydroxymethyl-3-pyrazolidone, 1-phenyl-4-methyl-3-pyrazolidone and superadditive developing agents such as N-methylparaaminophenol sulfate. Can do. Further, it is preferable to use a reductone compound such as ascorbic acid or isoascorbic acid in combination with the superadditive developing agent without using hydroquinone.

また、現像処理液には保恒剤として亜硫酸ナトリウム塩や亜硫酸カリウム塩、緩衝剤として炭酸ナトリウム塩や炭酸カリウム塩、現像促進剤としてジエタノールアミン、トリエタノールアミン、ジエチルアミノプロパンジオール等を適宜使用できる。   In addition, sodium sulfite or potassium sulfite as a preservative, sodium carbonate or potassium carbonate as a buffer, diethanolamine, triethanolamine, diethylaminopropanediol or the like as a development accelerator can be appropriately used in the developing solution.

現像処理で用いられる現像処理液は、画質を向上させる目的で、画質向上剤を含有することができる。画質向上剤としては、例えば、１−フェニル−５−メルカプトテトラゾール、５−メチルベンゾトリアゾール等の含窒素へテロ環化合物を挙げることができる。   The development processing solution used in the development processing can contain an image quality improver for the purpose of improving the image quality. Examples of the image quality improver include nitrogen-containing heterocyclic compounds such as 1-phenyl-5-mercaptotetrazole and 5-methylbenzotriazole.

本発明においては、露光後に行われる現像処理が、定着前物理現像を含んでいることが好ましい。ここで言う定着前物理現像とは、後述の定着処理を行う前に、露光により潜像を有するハロゲン化銀粒子の内部以外から銀イオンを供給し、現像銀を補強するプロセスのことを示す。現像処理液から銀イオンを供給するための具体的な方法としては、例えば予め現像処理液中に硝酸銀等を溶解しておき銀イオンを溶かしておく方法、あるいは現像液中に、チオ硫酸ナトリウム、チオシアン酸アンモニウム等のようなハロゲン化銀溶剤を溶解しておき、現像時に未露光部のハロゲン化銀を溶解させ、潜像を有するハロゲン化銀粒子の現像を補力する方法等が挙げられる。   In the present invention, it is preferable that the development processing performed after exposure includes physical development before fixing. The term “physical development before fixing” as used herein refers to a process in which silver ions are supplied from outside the silver halide grains having a latent image by exposure to reinforce developed silver before performing a fixing process described later. As a specific method for supplying silver ions from the developing solution, for example, a method of dissolving silver nitrate or the like in advance in a developing solution and dissolving silver ions, or sodium thiosulfate in the developing solution, Examples include a method in which a silver halide solvent such as ammonium thiocyanate is dissolved, unexposed silver halide is dissolved during development, and development of silver halide grains having a latent image is supplemented.

本発明においては、現像液中に予めハロゲン化銀溶剤を溶解しておく処方を用いた方が、未露光部でのカブリ発生による、フィルムの透過率低下を抑制できるため好ましい。   In the present invention, it is preferable to use a formulation in which a silver halide solvent is preliminarily dissolved in a developer because a reduction in the transmittance of the film due to fogging in unexposed areas can be suppressed.

なお、本発明においては、額縁部をメッシュ部よりも導電性を高くするために、ハロゲン化銀感光材料の現像処理に際して、額縁部相当領域の現像処理反応を促進することができる。具体的には、現像処理液中において、額縁部相当領域付近の液温度を高めたり、額縁部相当領域付近の液攪拌を高めることによって達成される。言うまでもなく、現像処理反応が促進された部分では、銀現像率が高まって現像銀がメッシュ部よりも多く形成され、線幅や厚さの大きい額縁メッシュを形成することができる。   In the present invention, in order to make the frame portion more conductive than the mesh portion, it is possible to accelerate the development processing reaction in the region corresponding to the frame portion during the development processing of the silver halide photosensitive material. Specifically, this is achieved by increasing the liquid temperature in the vicinity of the frame portion equivalent region or increasing the liquid agitation in the vicinity of the frame portion equivalent region in the developing solution. Needless to say, in the portion where the development processing reaction is promoted, the silver development rate is increased and more developed silver is formed than in the mesh portion, and a frame mesh having a large line width and thickness can be formed.

本発明に係る現像処理においては、露光されたハロゲン化銀粒子の現像終了後に、未露光部分のハロゲン化銀粒子を除去して安定化させる目的で行われる定着処理を行う。本発明における定着処理は、ハロゲン化銀粒子を用いた写真フィルムや印画紙等で用いられる定着液処方を用いることができる。定着処理で使用する定着液は、定着剤としてチオ硫酸ナトリウム、チオ硫酸カリウム、チオ硫酸アンモニウム等を使用することができる。定着時の硬膜剤として硫酸アルミウム、硫酸クロミウム等を使用することができる。定着剤の保恒剤としては、現像処理液で述べた亜硫酸ナトリウム、亜硫酸カリウム、アスコルビン酸、エリソルビン酸等を使用することができ、その他にクエン酸、蓚酸等を使用することができる。   In the development processing according to the present invention, after the development of the exposed silver halide grains, fixing processing is performed for the purpose of removing and stabilizing the unexposed silver halide grains. For the fixing treatment in the present invention, a fixer formulation used for photographic films, photographic papers and the like using silver halide grains can be used. The fixing solution used in the fixing process may use sodium thiosulfate, potassium thiosulfate, ammonium thiosulfate, or the like as a fixing agent. Aluminum sulfate, chromium sulfate, or the like can be used as a hardener for fixing. As the fixing agent preservative, sodium sulfite, potassium sulfite, ascorbic acid, erythorbic acid and the like described in the developing solution can be used, and citric acid, oxalic acid, and the like can be used.

本発明に使用する水洗水には、防黴剤としてＮ−メチル−イソチアゾール−３−オン、Ｎ−メチル−イソチアゾール−５−クロロ−３−オン、Ｎ−メチル−イソチアゾール−４，５−ジクロロ−３−オン、２−ニトロ−２−ブロム−３−ヒドロキシプロパノール，２−メチル−４−クロロフェノール、過酸化水素等を使用することができる。   The washing water used in the present invention includes N-methyl-isothiazol-3-one, N-methyl-isothiazol-5-chloro-3-one, and N-methyl-isothiazole-4,5 as antifungal agents. -Dichloro-3-one, 2-nitro-2-bromo-3-hydroxypropanol, 2-methyl-4-chlorophenol, hydrogen peroxide and the like can be used.

（補力処理）
本発明においては、上述の現像処理によって形成された現像銀同士の接触を補助し、導電性を高めるために補力処理を行うことが好ましい。本発明において補力処理とは、現像処理中、あるいは処理後に予めハロゲン化銀感光材料中に含有されていない導電性物質源を外部から供給し、導電性を高める処理のことを指し、具体的な方法としては、例えば、物理現像、あるいはめっき処理等を挙げることができる。 (Reinforcement processing)
In the present invention, in order to assist the contact between the developed silvers formed by the above-described development process and to increase the conductivity, it is preferable to perform a reinforcement process. In the present invention, the intensifying process refers to a process in which a conductive substance source not contained in the silver halide photosensitive material is supplied from the outside during the development process or after the process to increase the conductivity. Examples of such a method include physical development or plating treatment.

（物理現像処理）
物理現像は、潜像を有するハロゲン化銀感光材料を、銀イオンあるいは銀錯イオンと還元剤を含有する処理液に浸漬することで施すことができる。 (Physical development processing)
Physical development can be performed by immersing a silver halide photosensitive material having a latent image in a processing solution containing silver ions or silver complex ions and a reducing agent.

本発明においては、物理現像の現像開始点が潜像核だけでなく、現像銀が物理現像開始点となった場合についても物理現像と定義し、これを好ましく用いることができる。   In the present invention, physical development is defined not only when the development start point of physical development is the latent image nucleus but also when developed silver is the physical development start point, and this can be preferably used.

（めっき処理）
本発明において、めっき処理には従来公知の種々のめっき方法を用いることができ、例えば電解めっき及び無電解めっきを単独、あるいは組み合わせて実施することができる。中でも、めっき金属の選択性、めっき速度の調整、めっき強度に優れた電解めっきを本発明では好ましく用いることができる。無電解めっきの場合は、電流分布ムラによるめっきムラが発生しないという長所を有する。めっきに用いることができる金属としては、例えば、銅、ニッケル、コバルト、すず、銀、金、白金、その他各種合金を用いることができる。めっき処理が比較的容易であり、かつ高い導電性を得やすいという観点から、銅電解めっきを用いることが特に好ましい。 (Plating treatment)
In the present invention, various conventionally known plating methods can be used for the plating treatment. For example, electrolytic plating and electroless plating can be carried out alone or in combination. Among them, electrolytic plating excellent in selectivity of plating metal, adjustment of plating speed, and plating strength can be preferably used in the present invention. In the case of electroless plating, there is an advantage that uneven plating due to uneven current distribution does not occur. As a metal that can be used for plating, for example, copper, nickel, cobalt, tin, silver, gold, platinum, and other various alloys can be used. It is particularly preferable to use copper electrolytic plating from the viewpoint that the plating treatment is relatively easy and high conductivity is easily obtained.

なお、上記処理は現像中、現像後定着前、定着処理後のいずれのタイミングにおいても実施可能であるが、フィルムの透明性を高く維持するという観点から、定着処理後に実施することが好ましい。   The above processing can be performed during development, at any timing after development, before fixing, and after fixing processing. However, from the viewpoint of maintaining high transparency of the film, it is preferably performed after the fixing processing.

本発明において、物理現像または金属めっきにより付与された金属量が、ハロゲン化銀感光材料を露光、現像処理することにより得られた現像銀に対して、質量換算で１０〜１００倍である態様が好ましい。この値は、物理現像または金属めっきを施す前後において、ハロゲン化銀感光材料中に含有される金属を、例えば蛍光Ｘ線分析等で定量することによって求めることができる。物理現像または金属めっきにより付与された金属量が、ハロゲン化銀感光材料を露光、現像処理することにより得られた現像銀に対して、質量換算で１０倍未満である場合、導電性がやや低下する傾向となりやすく、また、１００倍より大きい場合には、導電性メッシュパターン部以外の不要な部分への金属析出による透過率の低下が生じやすい傾向となる。なお、本発明においては物理現像及び金属めっきの両方の処理を施すことが好ましい。   In the present invention, an aspect in which the amount of metal applied by physical development or metal plating is 10 to 100 times in terms of mass relative to developed silver obtained by exposing and developing a silver halide photosensitive material. preferable. This value can be determined by quantifying the metal contained in the silver halide photosensitive material by, for example, fluorescent X-ray analysis before and after physical development or metal plating. When the amount of metal applied by physical development or metal plating is less than 10 times in terms of mass relative to developed silver obtained by exposing and developing a silver halide photosensitive material, the conductivity is slightly reduced. If the ratio is larger than 100 times, the transmittance tends to decrease due to metal deposition on unnecessary portions other than the conductive mesh pattern portion. In the present invention, it is preferable to perform both physical development and metal plating.

なお、本発明においては、額縁部をメッシュ部よりも導電性を高くするために、めっき処理に際して、額縁部相当領域のめっき処理反応を促進することができる。具体的には、めっき処理液中において、額縁部相当領域付近の液温度を高めたり、額縁部相当領域付近の液攪拌を高めたり、額縁部相当領域付近に電極を近づけて電流を増大すること等によって達成される。言うまでもなく、めっき処理反応が促進された部分では、めっき反応率が高まってめっきがメッシュ部よりも多く形成され、線幅や厚さの大きい額縁メッシュを形成することができる。   In the present invention, in order to make the frame portion more conductive than the mesh portion, the plating treatment reaction in the frame portion equivalent region can be promoted during the plating treatment. Specifically, in the plating solution, increase the liquid temperature in the vicinity of the frame portion equivalent area, increase the liquid stirring in the vicinity of the frame portion equivalent area, or increase the current by bringing the electrode closer to the frame equivalent area. Achieved by etc. Needless to say, in the portion where the plating treatment reaction is promoted, the plating reaction rate is increased, so that plating is formed more than the mesh portion, and a frame mesh having a large line width and thickness can be formed.

さらに、本発明においては、額縁部をメッシュ部よりも導電性を高くするために、額縁部相当領域を金めっきすることができる。金めっきは、現像処理の後、または現像処理と物理現像の後の現像銀が形成された後、さらには現像銀の上に銅めっき等を施した後であっても、金めっき液に額縁部だけを浸漬して金めっきすることができる。   Furthermore, in the present invention, the frame portion corresponding region can be gold-plated in order to make the frame portion more conductive than the mesh portion. Gold plating can be applied to the gold plating solution even after the development process, after the development silver after development and physical development is formed, and even after copper plating is applied on the development silver. Only the part can be immersed and gold-plated.

さらに、また本発明においては、額縁部をメッシュ部よりも導電性を高くするために、額縁部相当領域を、加圧、加熱または加圧後加熱することができる。   Furthermore, in the present invention, in order to make the frame portion more conductive than the mesh portion, the frame portion equivalent region can be pressurized, heated, or heated after pressurization.

加圧は、１ｋＰａ〜１００ＭＰａ、好ましくは１０ｋＰａ〜１０ＭＰａの範囲、より好ましくは、５０ｋＰａ〜５ＭＰａである。加圧が１ｋＰより少ないと導電性向上の効果が小さく、１００ＭＰａより大きいと、面を平滑に保つことができにくくヘイズが上昇するので好ましくない。   The pressure is 1 kPa to 100 MPa, preferably 10 kPa to 10 MPa, and more preferably 50 kPa to 5 MPa. If the pressure is less than 1 kP, the effect of improving the conductivity is small, and if it is greater than 100 MPa, it is difficult to keep the surface smooth, and haze increases.

加熱は、４０〜３００℃、好ましくは５０〜２００℃、より好ましくは６０〜２００℃である。４０℃未満では導電性向上の効果が小さく、３００℃より高いと面を平滑に保つことができにくいので好ましくない。   The heating is 40 to 300 ° C, preferably 50 to 200 ° C, more preferably 60 to 200 ° C. If it is less than 40 ° C., the effect of improving conductivity is small, and if it is higher than 300 ° C., it is difficult to keep the surface smooth.

（酸化処理）
本発明においては、現像処理あるいは物理現像またはめっき処理後に酸化処理を行うことが好ましい。酸化処理により、不要な金属成分をイオン化して溶解除去することが可能となり、フィルムの透過率をより高めることが可能となる。 (Oxidation treatment)
In the present invention, it is preferable to carry out an oxidation treatment after the development treatment, physical development or plating treatment. By the oxidation treatment, unnecessary metal components can be ionized and dissolved and removed, and the transmittance of the film can be further increased.

酸化処理に用いる処理液としては、例えばＦｅ（III）イオンを含む水溶液を用いて処理する方法、あるいは過酸化水素、過硫酸塩、過硼酸塩、過燐酸塩、過炭酸塩、過ハロゲン酸塩、次亜ハロゲン酸塩、ハロゲン酸塩、有機過酸化物等の過酸化物を含む水溶液を用いて処理する方法等、従来公知の酸化剤を含有する処理液を用いることができる。酸化処理は、現像処理終了後から、めっき処理前の間に行うことが、短時間処理で効率的に透過率向上を行うことができるため好ましく、物理現像終了後に行うことが特に好ましい。   As the treatment liquid used for the oxidation treatment, for example, a treatment method using an aqueous solution containing Fe (III) ions, or hydrogen peroxide, persulfate, perborate, perphosphate, percarbonate, perhalogenate. A treatment solution containing a conventionally known oxidant such as a method of treating with an aqueous solution containing a peroxide such as a hypohalite, a halogenate, or an organic peroxide can be used. The oxidation treatment is preferably performed after completion of the development treatment and before the plating treatment because the transmittance can be efficiently improved in a short time treatment, and particularly preferably after completion of the physical development.

（黒化処理）
本発明においては、電磁波シールドフィルム表面での外光反射を防止するという観点から、金属メッシュ表面に黒化処理を施すことが好ましい。このような黒化処理を施した透明電磁波シールドフィルムを、例えばＰＤＰ（プラズマディスプレイパネル）等のディスプレイに用いた場合、外光反射によるコントラストの低下を軽減できるとともに、非使用時の画面の色調を黒く高品位に保つことができ好ましい。黒化処理の方法としては、特に制限はなく、既知の手法を適宜、単独あるいは組み合わせて用いることができる。例えば導電性パターンの最表面が金属銅から成る場合には、亜塩素酸ナトリウム、水酸化ナトリウム、リン酸三ナトリウムを含む水溶液に浸漬して酸化処理する方法、あるいはピロリン酸銅、ピロリン酸カリウム、アンモニアを含む水溶液に浸漬し、電解めっきを行うことにより、黒化処理する方法、等を好ましく用いることができる。また、導電性パターンの最表層がニッケル−リン合金被膜から成る場合は、塩化銅（II）または硫酸銅（II）、塩化ニッケルまたは硫酸ニッケル、及び塩酸を含有する酸性黒化処理液中に浸漬する方法を好ましく用いることができる。 (Blackening treatment)
In the present invention, it is preferable to perform blackening treatment on the surface of the metal mesh from the viewpoint of preventing external light reflection on the surface of the electromagnetic wave shielding film. When the transparent electromagnetic wave shielding film subjected to such blackening treatment is used for a display such as a plasma display panel (PDP), for example, it is possible to reduce a decrease in contrast due to reflection of external light and to adjust the color tone of the screen when not in use. It is preferable because it can be kept black and high quality. The blackening treatment method is not particularly limited, and known methods can be used alone or in combination as appropriate. For example, when the outermost surface of the conductive pattern is made of metallic copper, a method of oxidizing by immersing in an aqueous solution containing sodium chlorite, sodium hydroxide, or trisodium phosphate, or copper pyrophosphate, potassium pyrophosphate, A method of blackening by immersion in an aqueous solution containing ammonia and electrolytic plating can be preferably used. If the outermost layer of the conductive pattern is made of a nickel-phosphorus alloy coating, immerse it in an acidic blackening solution containing copper (II) chloride or copper (II) sulfate, nickel chloride or nickel sulfate, and hydrochloric acid. The method to do can be used preferably.

また、上述の方法以外にも、表面を微粗面化する方法によっても黒化処理が可能であるが、高い導電性を維持するという観点からは、表面の微粗面化よりも、酸化による黒化処理の方法が好ましい。   In addition to the above-described method, the blackening treatment can be performed by a method of finely roughening the surface. However, from the viewpoint of maintaining high conductivity, oxidation is more effective than finer roughening of the surface. A blackening treatment method is preferred.

（近赤外線吸収層）
本発明の電磁波シールドフィルムを、例えば、ＰＤＰ用の光学フィルタと組み合わせて使う場合には、ハロゲン化銀感光性層の下に近赤外吸収染料を含む層である近赤外線吸収層を設けることも好ましい。場合によっては近赤外線吸収層を支持体に対して、ハロゲン化銀乳剤層のある側の反対側に設けることもできるし、ハロゲン化銀乳剤層側と反対側の両方に設けてもよい。ハロゲン化銀を含むハロゲン化銀乳剤層と支持体との間に近赤外線吸収層を設けること、あるいは、ハロゲン化銀乳剤層からみて支持体の反対側に近赤外線吸収層を設けることができるが、支持体の一方側にすると同時に塗布ができるので前者の方が好ましい。 (Near-infrared absorbing layer)
When the electromagnetic wave shielding film of the present invention is used in combination with, for example, an optical filter for PDP, a near infrared absorbing layer which is a layer containing a near infrared absorbing dye may be provided under the silver halide photosensitive layer. preferable. In some cases, the near-infrared absorbing layer may be provided on the opposite side of the support to the silver halide emulsion layer side, or may be provided on both the silver halide emulsion layer side and the opposite side. A near infrared absorption layer can be provided between the silver halide emulsion layer containing silver halide and the support, or a near infrared absorption layer can be provided on the opposite side of the support as viewed from the silver halide emulsion layer. The former is preferred because it can be applied simultaneously with one side of the support.

近赤外線吸収染料の具体例としては、ポリメチン系、フタロシアニン系、ナフタロシアニン系、金属錯体系、アミニウム系、イモニウム系、ジイモニウム系、アンスラキノン系、ジチオール金属錯体系、ナフトキノン系、インドールフェノール系、アゾ系、トリアリルメタン系の化合物等が挙げられる。ＰＤＰ用光学フィルタで近赤外線吸収能が要求されるのは、主として熱線吸収や電子機器のノイズ防止である。このためには、最大吸収波長が７５０〜１１００ｎｍである近赤外線吸収能を有する色素が好ましく、金属錯体系、アミニウム系、フタロシアニン系、ナフタロシアニン系、ジイモニウム系、スクワリウム化合物系が特に好ましい。   Specific examples of near-infrared absorbing dyes include polymethine, phthalocyanine, naphthalocyanine, metal complex, aminium, imonium, diimonium, anthraquinone, dithiol metal complex, naphthoquinone, indolephenol, azo And triallylmethane-based compounds. The PDP optical filter is required to have near-infrared absorptivity mainly for absorption of heat rays and noise prevention of electronic devices. For this purpose, a dye having a near-infrared absorbing ability having a maximum absorption wavelength of 750 to 1100 nm is preferable, and a metal complex, aminium, phthalocyanine, naphthalocyanine, diimonium, and squalium compound are particularly preferable.

近赤外線吸収染料としては、ジイモニウム化合物は、ＩＲＧ−０２２、ＩＲＧ−０４０（以上、日本化薬株式会社製）、ニッケルジチオール錯体化合物は、ＳＩＲ−１２８、ＳＩＲ−１３０、ＳＩＲ−１３２、ＳＩＲ−１５９、ＳＩＲ−１５２、ＳＩＲ−１６２（以上、三井化学株式会社製）、フタロシアニン系化合物は、ＩＲ−１０，ＩＲ−１２（以上、日本触媒株式会社）等の市販品を利用することができる。   As the near-infrared absorbing dye, the diimonium compound is IRG-022, IRG-040 (above, manufactured by Nippon Kayaku Co., Ltd.), and the nickel dithiol complex compound is SIR-128, SIR-130, SIR-132, SIR-159. , SIR-152, SIR-162 (manufactured by Mitsui Chemicals, Inc.), and phthalocyanine compounds may be commercially available products such as IR-10, IR-12 (manufactured by Nippon Shokubai Co., Ltd.).

本発明の電磁波シールドフィルムを、例えば、ＰＤＰ用の光学フィルタと組み合わせて使う場合には、ＰＤＰに用いられるネオンガスの輝線発光行による色再現性の低下を防ぐために５９５ｎｍ付近の光を吸収する色素を含有することが好ましい。このような特定波長を吸収する色素としては、具体的には例えば、アゾ系、縮合アゾ系、フタロシアニン系、アンスラキノン系、インジゴ系、ペリノン系、ペリレン系、ジオキサジン系、キナクリドン系、メチン系、イソインドリノン系、キノフタロン系、ピロール系、チオインジゴ系、金属錯体系等の周知の有機顔料及び有機染料、無機顔料が挙げられる。これらの中でも、耐候性が良好であることから、フタロシアニン系、アンスラキノン系色素が特に好ましく用いられる。   When the electromagnetic wave shielding film of the present invention is used in combination with, for example, an optical filter for PDP, a dye that absorbs light near 595 nm is used to prevent a decrease in color reproducibility due to emission lines of neon gas used in PDP. It is preferable to contain. Specific examples of the dye that absorbs such a specific wavelength include, for example, azo, condensed azo, phthalocyanine, anthraquinone, indigo, perinone, perylene, dioxazine, quinacridone, methine, Well-known organic pigments and organic dyes such as isoindolinone-based, quinophthalone-based, pyrrole-based, thioindigo-based, and metal complex-based materials, and inorganic pigments may be mentioned. Among these, phthalocyanine-based and anthraquinone-based dyes are particularly preferably used because of good weather resistance.

（紫外線吸収層）
本発明においては、電磁波シールドフィルムの紫外線による劣化を避けるために、極大吸収波長３５０ｎｍ未満の紫外線吸収剤を使用することが好ましい。 (UV absorbing layer)
In the present invention, in order to avoid deterioration of the electromagnetic wave shielding film due to ultraviolet rays, it is preferable to use an ultraviolet absorber having a maximum absorption wavelength of less than 350 nm.

紫外線吸収剤としては、公知の紫外線吸収剤、例えばサリチル酸系化合物、ベンゾフェノン系化合物、ベンゾトリアゾール系化合物、Ｓ−トリアジン系化合物、環状イミノエステル系化合物等を好ましく使用することができる。これらの中、ベンゾフェノン系化合物、ベンゾトリアゾール系化合物、環状イミノエステル系化合物が好ましい。ポリエステルに配合するものとしては、特に環状イミノエステル系化合物が好ましい。これら紫外線吸収剤の添加層については特に制限はないが、ハロゲン化銀感光性層（メッシュパターン層）に用いられるバインダーの紫外線による劣化を防止するという観点から、ハロゲン化銀感光性層への添加、あるいは該層よりも光源側に設けることが好ましい。   As the ultraviolet absorber, known ultraviolet absorbers such as salicylic acid compounds, benzophenone compounds, benzotriazole compounds, S-triazine compounds, cyclic imino ester compounds and the like can be preferably used. Of these, benzophenone compounds, benzotriazole compounds, and cyclic imino ester compounds are preferred. As what is blended with the polyester, a cyclic imino ester compound is particularly preferable. There are no particular restrictions on the layer added to these ultraviolet absorbers, but from the viewpoint of preventing the binder used in the silver halide photosensitive layer (mesh pattern layer) from being deteriorated by ultraviolet rays, it is added to the silver halide photosensitive layer. Alternatively, it is preferably provided on the light source side of the layer.

好ましい紫外線吸収剤としてはベンゾトリアゾール類が挙げられ、例えば特開平１−２５０９４４号公報記載の一般式［III−３］で示される化合物、特開昭６４−６６６４６号公報記載の一般式［III］で示される化合物、特開昭６３−１８７２４０号公報記載のＵＶ−１Ｌ〜ＵＶ−２７Ｌ、特開平４−１６３３号公報記載の一般式［Ｉ］で示される化合物、特開平５−１６５１４４号公報記載の一般式（Ｉ）、（II）で示される化合物等が好ましく用いられる。   Preferred ultraviolet absorbers include benzotriazoles, for example, compounds represented by general formula [III-3] described in JP-A-1-250944, and general formula [III] described in JP-A 64-66646. A compound represented by general formula [I] described in JP-A No. 63-187240, UV-1L to UV-27L described in JP-A No. 63-187240, JP-A No. 4-1633, and JP-A No. 5-165144 The compounds represented by the general formulas (I) and (II) are preferably used.

これらの紫外線吸収剤は、例えばジオクチルフタレート、ジ−ｉ−デシルフタレート、ジブチルフタレート等のフタル酸エステル類、トリクレジルホスフェート、トリオクチルホスフェート等の燐酸エステル類等に代表される高沸点有機溶媒に分散して添加することが好ましい。また、これらの紫外線吸収剤を支持体中に直接添加することも好ましく用いられ、この場合、例えば特表２００４−５３１６１１号に記載の態様も好ましく用いることができる。   These ultraviolet absorbers are used in, for example, high-boiling organic solvents represented by phthalates such as dioctyl phthalate, di-i-decyl phthalate, and dibutyl phthalate, and phosphate esters such as tricresyl phosphate and trioctyl phosphate. It is preferable to add in a dispersed manner. Moreover, it is also preferably used to add these ultraviolet absorbers directly to the support. In this case, for example, the embodiment described in JP-T-2004-531611 can also be preferably used.

（反射防止層）
本発明の電電磁波シールドフィルムを、ディスプレイ画面の保護等を目的として用いる場合には、反射防止層を設けることが好ましい。 (Antireflection layer)
When the electromagnetic wave shielding film of the present invention is used for the purpose of protecting a display screen or the like, it is preferable to provide an antireflection layer.

反射防止層は、屈折率の異なる複数の光透過性層からなることが好ましく、無機微粒子を含有した高屈折率層、中屈折率層、低屈折率層から構成されることがより好ましい。屈折率の異なる層はそれぞれに含有される無機微粒子の種類、粒径、添加量、樹脂バインダーの種類等によって調整される。高屈折率層の屈折率は１．５５〜２．３０であることが好ましく、１．５７〜２．２０であることがさらに好ましい。中屈折率層の屈折率は、基材フィルムの屈折率と高屈折率層の屈折率との中間の値となるように調整する。中屈折率層の屈折率は１．５５〜１．８０であることが好ましい。低屈折率層の屈折率は１．４６以下が好ましく、特に１．３〜１．４５であることが望ましい。   The antireflection layer is preferably composed of a plurality of light transmissive layers having different refractive indexes, and more preferably composed of a high refractive index layer, a medium refractive index layer, and a low refractive index layer containing inorganic fine particles. The layers having different refractive indexes are adjusted according to the kind of inorganic fine particles contained therein, the particle diameter, the added amount, the kind of resin binder, and the like. The refractive index of the high refractive index layer is preferably 1.55 to 2.30, and more preferably 1.57 to 2.20. The refractive index of the medium refractive index layer is adjusted so as to be an intermediate value between the refractive index of the base film and the refractive index of the high refractive index layer. The refractive index of the middle refractive index layer is preferably 1.55 to 1.80. The refractive index of the low refractive index layer is preferably 1.46 or less, and particularly preferably 1.3 to 1.45.

反射防止層としては、金属酸化物、フッ化物、ケイ化物、ホウ化物、炭化物、窒化物、硫化物等の無機物を、真空蒸着法、スパッタリング法、イオンプレーティング法、イオンビームアシスト法等で単層あるいは多層に薄膜積層させる方法、アクリル樹脂、フッ素樹脂等の屈折率の異なる樹脂を単層あるいは多層に薄膜積層させる方法等を用いることができる。   As the antireflection layer, inorganic materials such as metal oxides, fluorides, silicides, borides, carbides, nitrides, sulfides, etc., can be used by vacuum deposition, sputtering, ion plating, ion beam assist, etc. A method of laminating a thin film in a layer or a multilayer, a method of laminating a resin having a different refractive index such as an acrylic resin or a fluororesin into a single layer or a multilayer can be used.

本発明の透明電磁波シールドフィルムにおいて、導電性パターンを有する層に対して該電磁波シールドフィルムの支持体を挟んだ反対側に反射防止層を形成する場合には、最初に反射防止層を形成した後に、プロテクトフィルムを貼り合わせ、その後導電性パターン層を形成することが好ましい。導電性パターンを先に形成した後に反射防止層を形成する場合、反射防止層と支持体の接着性を向上させるために行うプラズマ処理やコロナ処理の効率が低下しやすい傾向にあるため、反射防止層を最初に形成することが好ましい。また、反射防止層を先に形成した場合、該層が現像及びめっき処理等により劣化することを防止するという観点から、予めプロテクトフィルムを貼り合わせた後、導電性パターン層を形成することが好ましい。   In the transparent electromagnetic wave shielding film of the present invention, when the antireflection layer is formed on the opposite side of the layer having the conductive pattern with the support of the electromagnetic wave shielding film sandwiched, after the antireflection layer is first formed, It is preferable to bond a protective film and then form a conductive pattern layer. When the antireflection layer is formed after the conductive pattern is formed first, the efficiency of the plasma treatment and corona treatment performed to improve the adhesion between the antireflection layer and the support tends to be reduced. It is preferred to form the layer first. In addition, when the antireflection layer is formed first, it is preferable to form a conductive pattern layer after pasting a protective film in advance from the viewpoint of preventing the layer from being deteriorated by development, plating treatment or the like. .

本発明において用いられるプロテクトフィルムは、一般的に市販されているプロテクトフィルムを用いることができるが、導電性パターン形成のための感光性ハロゲン化銀乳剤層を塗工しやすくするという観点から、フィルムの厚さは１０〜１００μｍが好ましく、特に好ましくは２０〜６０μｍである。１０μｍ未満の場合、フィルムの剛性が著しく低下するためプロテクトフィルムの貼合せの作業効率が低下しやすく、また１００μｍより厚い場合、フィルムの巻き取り時に巻き取り皺等の故障が発生しやすくなるためである。   As the protective film used in the present invention, a commercially available protective film can be used. From the viewpoint of facilitating coating of a photosensitive silver halide emulsion layer for forming a conductive pattern, the film is used. Is preferably 10 to 100 μm, particularly preferably 20 to 60 μm. If the thickness is less than 10 μm, the rigidity of the film is remarkably reduced, so that the work efficiency of the protection film is likely to be lowered. If the thickness is more than 100 μm, a failure such as a winding reel tends to occur when the film is wound. is there.

プロテクトフィルムに用いられる粘着剤の種類には特に制限はないが、反射防止フィルムを変質させることなく、また剥離時に反射防止フィルムにダメージを与えないものが好ましく用いられる。このような観点から、アクリル系、またはシリコーン系の粘着剤が好ましく用いられる。また、その粘着力としては、０．０８〜０．６Ｎ／２５ｍｍであるものが好ましく用いられる。   Although there is no restriction | limiting in particular in the kind of adhesive used for a protective film, The thing which does not damage an antireflection film at the time of peeling, without altering an antireflection film is used preferably. From such a viewpoint, an acrylic or silicone adhesive is preferably used. Moreover, as the adhesive force, what is 0.08-0.6N / 25mm is used preferably.

以下、実施例を挙げて本発明を具体的に説明するが、本発明はこれらに限定されない。なお、実施例において「部」あるいは「％」の表示を用いるが、特に断りがない限り「質量部」あるいは「質量％」を表す。   EXAMPLES Hereinafter, although an Example is given and this invention is demonstrated concretely, this invention is not limited to these. In addition, although the display of "part" or "%" is used in an Example, unless otherwise indicated, "part by mass" or "mass%" is represented.

実施例
（ハロゲン化銀乳剤の調製）
硝酸銀水溶液と、臭化カリウム及び塩化ナトリウム水溶液とを、３５℃のゼラチン水溶液中へ制御しながら添加混合して、塩臭化銀乳剤（臭化銀１０モル％、塩化銀９０モル％）を調製した。この乳剤中には臭化ロジウム酸カリウム及び塩化イリジウム酸カリウムを濃度が１．０×１０-7（モル／モル銀）になるように添加し、ＲｈイオンとＩｒイオンをドープした。また、銀／ゼラチン質量比は４／１（銀／ゼラチン体積比は約０．５）とし、ゼラチン種としては平均分子量４万のアルカリ処理型低分子量ゼラチンを用いた。平均粒径は０．０４μｍ、粒径分布の変動係数は０．１３であった。 Examples (Preparation of silver halide emulsion)
A silver chlorobromide emulsion (10 mol% silver bromide, 90 mol% silver chloride) was prepared by adding and mixing an aqueous silver nitrate solution and an aqueous potassium bromide and sodium chloride solution while controlling the solution to an aqueous gelatin solution at 35 ° C. did. In this emulsion, potassium rhodium bromide and potassium chloroiridate were added to a concentration of 1.0 × 10 −7 (mol / mol silver), and Rh ions and Ir ions were doped. The silver / gelatin mass ratio was 4/1 (silver / gelatin volume ratio was about 0.5), and an alkali-treated low molecular weight gelatin having an average molecular weight of 40,000 was used as the gelatin species. The average particle size was 0.04 μm, and the variation coefficient of the particle size distribution was 0.13.

その後、チオ硫酸ナトリウムをハロゲン化銀１モル当たり２．０ｍｇ用い、４０℃にて８０分間化学増感を行い、化学増感終了後に４−ヒドロキシ−６−メチル−１，３，３ａ，７−テトラザインデンをハロゲン化銀１モル当たり５００ｍｇ添加して、さらに、下記増感色素ＳＤ−１をハロゲン化銀１モル当たり５００ｍｇ添加して、感光性ハロゲン化銀乳剤を得た。   Thereafter, 2.0 mg of sodium thiosulfate per mol of silver halide was used for chemical sensitization at 40 ° C. for 80 minutes, and after completion of chemical sensitization, 4-hydroxy-6-methyl-1,3,3a, 7- The photosensitive silver halide emulsion was obtained by adding 500 mg of tetrazaindene per mole of silver halide and further adding 500 mg of the following sensitizing dye SD-1 per mole of silver halide.

Figure 2008270634
Figure 2008270634

（支持体）
両面にプラズマ放電処理を施した、厚さ１２０μｍ、幅６０ｃｍ、長さ１２０ｍの透明ポリエチレンテレフタレートフィルム支持体の一方の側に、ブチルアクリレート：スチレン：グリシジルアクリレート（４０：２０：４０質量％）ラテックスが０．４０ｇ／ｍ2、ヘキサメチレン−１，６−ビス（エチレンウレア）が０．０１ｇ／ｍ2となるように塗布して、下塗り層を設けた。その一方の側に、非感光性中間層として、ゼラチンを０．２０ｇ／ｍ2塗布した。 (Support)
A butyl acrylate: styrene: glycidyl acrylate (40:20:40 mass%) latex is applied to one side of a transparent polyethylene terephthalate film support having a thickness of 120 μm, a width of 60 cm, and a length of 120 m, which has been subjected to plasma discharge treatment on both sides. An undercoat layer was provided by applying 0.40 g / m 2 of hexamethylene-1,6-bis (ethylene urea) to 0.01 g / m 2 . On one side, 0.20 g / m 2 of gelatin was applied as a non-photosensitive intermediate layer.

さらに他方の側に、非感光性中間層として、ゼラチンを０．２０ｇ／ｍ2塗布した。 Further, 0.20 g / m 2 of gelatin was coated on the other side as a non-photosensitive intermediate layer.

（ハロゲン化銀感光性層の塗布）
前記のハロゲン化銀乳剤に、塗布助剤として、界面活性剤（スルホ琥珀酸ジ・２−エチルヘキシル・ナトリウム）を添加して表面張力を調整し、硬膜剤（テトラキス・ビニルスルホニルメチル・メタン）をゼラチン１ｇ当たり５０ｍｇとなるようにして添加し、前記非感光性中間層の上に、銀塗布量０．６０ｇ／ｍ2、及びゼラチン塗布量０．１５ｇ／ｍ2となるように、速度２０ｍ／分で塗布を行って乾燥し、ロール状のハロゲン化銀感光材料を６本作製した。 (Coating of silver halide photosensitive layer)
To the above silver halide emulsion, a surfactant (disulfo oxalate, 2-ethylhexyl, sodium) is added as a coating aid to adjust the surface tension, and a hardener (tetrakis, vinylsulfonylmethyl, methane). Is added at a rate of 20 m so that the silver coating amount is 0.60 g / m 2 and the gelatin coating amount is 0.15 g / m 2. The coating was carried out at a rate of / min and dried to prepare six roll-shaped silver halide photosensitive materials.

（露光）
このようにして得られたハロゲン化銀感光材料に対して、図１〜６に示すパターンの露光を行った。メッシュ部は、線幅が１０μｍ、線間隔が２４０μｍの格子状で、格子線がロールの長手方向に対して４５度の角度をもって形成される。 (exposure)
The silver halide photosensitive material thus obtained was subjected to pattern exposure shown in FIGS. The mesh portion has a lattice shape with a line width of 10 μm and a line interval of 240 μm, and the lattice lines are formed at an angle of 45 degrees with respect to the longitudinal direction of the roll.

図１はメッシュ部のみで額縁部を有していない比較例である。図２は幅手両端部に２ｃｍ幅の短冊状の額縁部を長手方向に連続的に有する比較例である。図３は額縁部のメッシュの線幅を５０μｍに太くした額縁メッシュを有する本発明例である。図４は幅手両端部に矩形の幾何学パターンを付加した本発明例であり、ロールの巻き取りでの曲げ方向に対して幾何学パターンに応力がかかりにくいように配列されている。図５は幅手両端部のメッシュ部の一部を覆って平均開口率を下げた本発明例であり、ロールの巻き取りでの曲げ方向に対して幾何学パターンに応力がかかりにくいように配列されている。図６は幅手両端部のメッシュ部の線間隔を８０μｍに小さくした本発明例である。   FIG. 1 is a comparative example having only a mesh portion and no frame portion. FIG. 2 shows a comparative example in which strip-shaped frame portions having a width of 2 cm are continuously provided in the longitudinal direction at both ends of the width. FIG. 3 shows an example of the present invention having a frame mesh in which the line width of the frame mesh is increased to 50 μm. FIG. 4 shows an example of the present invention in which a rectangular geometric pattern is added to both ends of the width, and the geometric pattern is arranged so that stress is not easily applied to the bending direction in winding the roll. FIG. 5 is an example of the present invention in which the average aperture ratio is lowered by covering a part of the mesh portion at both ends of the width, and is arranged so that stress is not easily applied to the geometric pattern with respect to the bending direction in winding the roll. Has been. FIG. 6 shows an example of the present invention in which the line spacing of the mesh portions at both ends of the width is reduced to 80 μm.

これらの電磁波シールドメッシュパターンを、発振波長４４０ｎｍのレーザー光（日亜化学（株）製の青色半導体レーザーダイオード）を用いて、ハロゲン化銀感光材料を連続搬送しながら露光を行った。   These electromagnetic wave shielding mesh patterns were exposed using a laser beam having an oscillation wavelength of 440 nm (blue semiconductor laser diode manufactured by Nichia Corporation) while continuously conveying the silver halide photosensitive material.

（現像処理）
露光済みの試料について、図７に示すような、幅６０ｃｍのリーダーベルト搬送方式の、自動現像処理・物理現像・めっき統合機を用い、下記現像液を用いて２５℃で６０秒間現像処理を行った後、下記定着液を用いて、２５℃で１２０秒間の定着処理を行い、ついで水洗処理を行った。さらに、下記物理現像液を用いて、２５℃５分間の物理現像を行い、ついで水洗処理を行った後、下記銅めっき液にて、２．５Ａ／ｃｍ2で２５℃５分間の電解めっきを行って、水洗した。最後に６０℃温風にて乾燥し、長尺ロール状の電磁波シールドフィルム試料１０１〜１０６を作製した。 (Development processing)
The exposed sample is developed for 60 seconds at 25 ° C. using the following developer using an automatic development / physical development / plating integrated machine of a leader belt conveyance system with a width of 60 cm as shown in FIG. Thereafter, using the following fixing solution, a fixing treatment was performed at 25 ° C. for 120 seconds, followed by a water washing treatment. Furthermore, after performing physical development at 25 ° C. for 5 minutes using the following physical developer, followed by washing with water, electrolytic plating at 25 ° C. for 5 minutes at 2.5 A / cm 2 with the following copper plating solution. Went and washed with water. Finally, it dried with 60 degreeC warm air, and produced the elongate roll-shaped electromagnetic wave shield film samples 101-106.

（現像液）
純水 ５００ｍｌ
メトール ２ｇ
無水亜硫酸ナトリウム ８０ｇ
ハイドロキノン ４ｇ
ホウ砂 ４ｇ
チオ硫酸ナトリウム １０ｇ
臭化カリウム ０．５ｇ
水を加えて全量を１リットルとする
（定着液）
純水 ７５０ｍｌ
チオ硫酸ナトリウム ２５０ｇ
無水亜硫酸ナトリウム １５ｇ
氷酢酸 １５ｍｌ
カリミョウバン １５ｇ
水を加えて全量を１リットルとする
（物理現像液）
純水 ８００ｍｌ
クエン酸 ５ｇ
ハイドロキノン ７ｇ
硝酸銀 ３ｇ
水を加えて全量を１リットルとする
（銅めっき液）
硫酸銅 １２５ｇ
硫酸 ８５ｇ
ポリエチレングリコール ０．１ｇ
１ｍｏｌ／Ｌ塩酸 ２．０ｍｌ
水を加えて全量を１リットルとする。 (Developer)
500 ml of pure water
Metol 2g
80 g of anhydrous sodium sulfite
Hydroquinone 4g
4g borax
Sodium thiosulfate 10g
Potassium bromide 0.5g
Add water to bring the total volume to 1 liter (fixing solution)
750 ml of pure water
Sodium thiosulfate 250g
Anhydrous sodium sulfite 15g
Glacial acetic acid 15ml
Potash alum 15g
Add water to make 1 liter (physical developer)
800ml of pure water
Citric acid 5g
Hydroquinone 7g
Silver nitrate 3g
Add water to bring the total volume to 1 liter (copper plating solution)
125 g of copper sulfate
85 g of sulfuric acid
Polyethylene glycol 0.1g
1mol / L hydrochloric acid 2.0ml
Add water to bring the total volume to 1 liter.

（評価）
このようにして得られた、導電性の金属メッシュ部を有する電磁波シールドフィルム試料１０１〜１０６に対して、以下の評価を行った。 (Evaluation)
Thus, the following evaluation was performed with respect to the electromagnetic wave shield film samples 101-106 which have the electroconductive metal mesh part obtained.

〈現像処理ムラ〉
定着処理とそれに続く水洗が終了した段階で、搬送中の試料を大気中に露出するようにし、各試料の額縁部とメッシュ部の境界付近のパターンのムラの発生状況を、高精細ＣＣＤカメラで複数箇所をコマ撮影して４０インチモニター画面上に拡大倍率２００倍で表示し、目視観察して、下記基準で評価した。 <Development unevenness>
At the stage where the fixing process and subsequent water washing are completed, the sample being transported is exposed to the atmosphere, and the occurrence of pattern unevenness near the border between the frame and mesh of each sample is detected with a high-definition CCD camera. A plurality of positions were photographed and displayed on a 40-inch monitor screen at an enlargement magnification of 200 times, visually observed, and evaluated according to the following criteria.

○：メッシュの線幅のばらつきは認められない
△：わずかにメッシュの線幅のばらつきが認められる
×：線幅が１／２以下の部分や、断線部分が認められる
〈めっきムラ〉
めっき処理し、乾燥した後の試料の、額縁部とメッシュ部の境界付近のパターンのムラの発生状況を、高精細ＣＣＤカメラで複数箇所をコマ撮影して４０インチモニター画面上に拡大倍率２００倍で表示し、目視観察して、下記基準で評価した。 ○: No variation in mesh line width is observed. Δ: A slight variation in mesh line width is observed. ×: Line width is less than 1/2 or disconnection is observed.
After the plating treatment and drying, the pattern unevenness in the vicinity of the border between the frame part and the mesh part of the sample was photographed at several points with a high-definition CCD camera and magnified 200 times on a 40-inch monitor screen. And visually observed and evaluated according to the following criteria.

○：メッシュの線幅のばらつきは認められない
△：わずかにメッシュの線幅のばらつきが認められる
×：線幅が１／２以下の部分や、断線部分が認められる
〈膜接着性〉
めっき処理後、乾燥した各試料をメッシュ部を内側にして直径１０ｃｍの巻き芯に巻き、２３℃５５％ＲＨ雰囲気下に２４時間放置後、今度はメッシュ部を外側にして同様に巻き直し、さらに２３℃５５％ＲＨ雰囲気下に２４時間放置後、ＪＩＳ−Ｋ５４００のクロスカット密着試験方法に従って膜接着性の評価を行った。 ○: No variation in the line width of the mesh is observed. Δ: A slight variation in the line width of the mesh is observed. ×: A portion where the line width is 1/2 or less or a disconnection portion is observed. <Membrane Adhesiveness>
After the plating treatment, each dried sample is wound around a winding core having a diameter of 10 cm with the mesh portion inside, left in a 23 ° C. and 55% RH atmosphere for 24 hours, and then wound again in the same manner with the mesh portion outside. After being allowed to stand in an atmosphere of 23 ° C. and 55% RH for 24 hours, film adhesion was evaluated according to the cross-cut adhesion test method of JIS-K5400.

各試料についてクロス状のカット線を引き、日東電工（株）製のセロハンテープＮｏ．２９を貼り付けて、テープをはがし、膜のマス目の剥離状態を調べた。膜残存率をＦとし、クロスカットしたマス目の数をｎ１としたとき、Ｆ＝ｎ１／ｎ×１００（％）で評価した。   A cross-shaped cut line was drawn for each sample, and cellophane tape No. 1 manufactured by Nitto Denko Corporation was used. 29 was affixed, the tape was peeled off, and the peeling state of the squares of the film was examined. When the film remaining rate is F and the number of cross-cut cells is n1, F = n1 / n × 100 (%).

〈カール〉
各試料を、メッシュ部形成面を内側にして、直径１０ｃｍの巻芯に張力１９．６Ｎ／ｃｍ2で巻き付け、３５℃湿度５５％雰囲気下に１週間放置した。終了後、各試料の巻芯に近い１ｍを切り出し、試料の末端部であった部分が下になるように吊り下げ、２３℃湿度５５％雰囲気下で１日間放置して、延展長さＬｃ（図８）を測定した。数値が大きく１ｍに近いほど、カールが小さくて優れていることを示す。数値が小さいほどカールが大きくて、後工程での加工に不都合が発生する可能性があることを示している。 <curl>
Each sample was wound around a winding core having a diameter of 10 cm with a tension of 19.6 N / cm 2 with the mesh portion forming surface inside, and left for 1 week in an atmosphere of 35 ° C. and 55% humidity. After completion, 1 m close to the core of each sample was cut out, suspended so that the end portion of the sample was down, and left for 1 day in an atmosphere of 23 ° C. and 55% humidity, and extended length Lc ( Fig. 8) was measured. The larger the value, the closer to 1 m, the smaller the curl and the better. The smaller the numerical value, the larger the curl, which indicates that there is a possibility that inconvenience may occur in processing in the subsequent process.

〈接地性〉
電磁波シールドフィルムの額縁部と、該額縁部と同じ幅の厚さ５０μｍのスズめっき軟銅導体とをヒートシーラーで接着（１６０℃、４０Ｎ／ｃｍ2、３秒間）し、導体の線間抵抗性を、幅１５ｍｍで測定し、下記基準で評価した。 <Grounding>
Adhering the frame part of the electromagnetic shielding film and a tin-plated annealed copper conductor with the same width as the frame part and having a thickness of 50 μm with a heat sealer (160 ° C., 40 N / cm 2 , 3 seconds) , Measured at a width of 15 mm and evaluated according to the following criteria.

○：５Ω以下
△：５Ωより大きく２０Ω以下
×：２０Ωより大きい ○: 5Ω or less △: Greater than 5Ω and 20Ω or less ×: Greater than 20Ω

Figure 2008270634
Figure 2008270634

表１から、長尺連続ロール生産においても、本発明はメッシュパターンの膜付きに優れ、巻き癖カールの発生が小さく、パネルの接地性にも優れた透明電磁波シールドフィルムであることが分かる。さらに本発明の製造方法は、電磁波シールドフィルム製造中に発生する現像処理ムラ、めっきムラを改善した透明電磁波シールドフィルムの製造方法であることが分かる。   From Table 1, it can be seen that even in the production of long continuous rolls, the present invention is a transparent electromagnetic wave shielding film that is excellent in attaching a mesh pattern film, having little curl curl generation, and having excellent panel grounding properties. Furthermore, it turns out that the manufacturing method of this invention is a manufacturing method of the transparent electromagnetic wave shielding film which improved the development processing nonuniformity and plating nonuniformity which generate | occur | produce during electromagnetic wave shielding film manufacture.

比較例の露光パターンを示す図である。It is a figure which shows the exposure pattern of a comparative example. 比較例の露光パターンの他の一例を示す図である。It is a figure which shows another example of the exposure pattern of a comparative example. 本発明の露光パターンを示す図である。It is a figure which shows the exposure pattern of this invention. 本発明の露光パターンの他の一例を示す図である。It is a figure which shows another example of the exposure pattern of this invention. 本発明の露光パターンの他の一例を示す図である。It is a figure which shows another example of the exposure pattern of this invention. 本発明の露光パターンの他の一例を示す図である。It is a figure which shows another example of the exposure pattern of this invention. 本発明に用いる自動現像処理・物理現像・めっき統合機の工程を示す概略図である。It is the schematic which shows the process of the automatic image development processing / physical development / plating integrated machine used for this invention. カール測定の延展長さを示す図である。It is a figure which shows the extension length of a curl measurement.

符号の説明Explanation of symbols

１ メッシュ部
２ 額縁部
１１ 現像
１２ 定着
１３ 水洗
１４ 物理現像
１５ めっき
１６ 乾燥
Ｌｃ 延展長さ DESCRIPTION OF SYMBOLS 1 Mesh part 2 Frame part 11 Development 12 Fixing 13 Washing with water 14 Physical development 15 Plating 16 Drying Lc Extension length

Claims (13)

長尺の透明支持体上に形成された、連続する導電性のメッシュ部と額縁部とを有する電磁波シールドフィルムであって、前記額縁部が前記メッシュ部より導電性が高い幾何学パターンであることを特徴とする電磁波シールドフィルム。 An electromagnetic wave shielding film having a continuous conductive mesh portion and a frame portion formed on a long transparent support, wherein the frame portion is a geometric pattern having a higher conductivity than the mesh portion. An electromagnetic shielding film characterized by. 前記導電性が高い幾何学パターンが、メッシュ部より開口率が小さい額縁メッシュであることを特徴とする請求項１に記載の電磁波シールドフィルム。 The electromagnetic wave shielding film according to claim 1, wherein the geometric pattern having high conductivity is a frame mesh having an aperture ratio smaller than that of the mesh portion. 前記開口率が小さい額縁メッシュが、メッシュ部よりピッチが小さい額縁メッシュであることを特徴とする請求項２に記載の電磁波シールドフィルム。 The electromagnetic wave shielding film according to claim 2, wherein the frame mesh having a small opening ratio is a frame mesh having a pitch smaller than that of the mesh portion. 前記開口率が小さい額縁メッシュが、メッシュ部より線幅が大きい額縁メッシュであることを特徴とする請求項２または３に記載の電磁波シールドフィルム。 The electromagnetic wave shielding film according to claim 2 or 3, wherein the frame mesh having a small opening ratio is a frame mesh having a line width larger than that of the mesh portion. 前記導電性が高い幾何学パターンが、メッシュ部より厚さが大きい額縁メッシュであることを特徴とする請求項１〜４のいずれか１項に記載の電磁波シールドフィルム。 The electromagnetic shielding film according to claim 1, wherein the geometric pattern having high conductivity is a frame mesh having a thickness larger than that of the mesh portion. 長尺の透明支持体上に、少なくとも感光性ハロゲン化銀及びバインダーからなる層を塗布したハロゲン化銀感光材料を、パターン露光後、現像処理及びめっきを行って、連続する導電性のメッシュ部と幾何学パターンの額縁部とを形成する透明電磁波シールドフィルムの製造方法において、前記額縁部を前記メッシュ部より導電性を高くする工程を有することを特徴とする電磁波シールドフィルムの製造方法。 A silver halide photosensitive material in which a layer comprising at least a photosensitive silver halide and a binder is coated on a long transparent support, and after pattern exposure, development processing and plating are performed, and a continuous conductive mesh portion and In the manufacturing method of the transparent electromagnetic wave shielding film which forms the frame part of a geometric pattern, The manufacturing method of the electromagnetic wave shielding film characterized by having the process which makes the said frame part highly conductive rather than the said mesh part. 前記導電性を高くする工程が、ハロゲン化銀乳剤塗布時に額縁部相当領域を厚く塗布する工程であることを特徴とする請求項６の電磁波シールドフィルムの製造方法。 7. The method for producing an electromagnetic wave shielding film according to claim 6, wherein the step of increasing the conductivity is a step of thickly applying a region corresponding to the frame portion at the time of applying the silver halide emulsion. 前記導電性を高くする工程が、額縁部の幾何学パターンのピッチをメッシュ部よりも小さく露光する工程であることを特徴とする請求項６に記載の電磁波シールドフィルムの製造方法。 The method for producing an electromagnetic wave shielding film according to claim 6, wherein the step of increasing the conductivity is a step of exposing the geometric pattern pitch of the frame portion to be smaller than that of the mesh portion. 前記導電性を高くする工程が、額縁部の幾何学パターンの線幅を太く露光する工程であることを特徴とする請求項６に記載の電磁波シールドフィルムの製造方法。 The method for producing an electromagnetic wave shielding film according to claim 6, wherein the step of increasing the conductivity is a step of exposing the line width of the geometric pattern of the frame portion to be thick. 前記導電性を高くする工程が、額縁部の現像処理を促進する工程であることを特徴とする請求項６に記載の電磁波シールドフィルムの製造方法。 The method for producing an electromagnetic wave shielding film according to claim 6, wherein the step of increasing the conductivity is a step of accelerating a developing process of the frame portion. 前記導電性を高くする工程が、額縁部のめっきを促進する工程であることを特徴とする請求項６に記載の電磁波シールドフィルムの製造方法。 The method for producing an electromagnetic wave shielding film according to claim 6, wherein the step of increasing the conductivity is a step of promoting plating of a frame portion. 前記導電性を高くする工程が、額縁部を金めっきする工程であることを特徴とする請求項６に記載の電磁波シールドフィルムの製造方法。 The method for producing an electromagnetic wave shielding film according to claim 6, wherein the step of increasing the conductivity is a step of gold-plating a frame portion. 前記導電性を高くする工程が、額縁部を加圧、加熱または加圧後加熱する工程であることを特徴とする請求項６に記載の電磁波シールドフィルムの製造方法。 The method for producing an electromagnetic wave shielding film according to claim 6, wherein the step of increasing the conductivity is a step of pressurizing, heating, or heating the frame portion after pressurization.
JP2007113929A 2007-04-24 2007-04-24 Electromagnetic-wave shield film, and manufacturing method thereof Pending JP2008270634A (en)