JP2008229964A - Synthetic resin molding, its manufacturing method and electronic instrument - Google Patents
Synthetic resin molding, its manufacturing method and electronic instrument Download PDFInfo
- Publication number
- JP2008229964A JP2008229964A JP2007070907A JP2007070907A JP2008229964A JP 2008229964 A JP2008229964 A JP 2008229964A JP 2007070907 A JP2007070907 A JP 2007070907A JP 2007070907 A JP2007070907 A JP 2007070907A JP 2008229964 A JP2008229964 A JP 2008229964A
- Authority
- JP
- Japan
- Prior art keywords
- synthetic resin
- molded product
- resin material
- molded
- molding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、合成樹脂成形品とその製造方法及び電子機器に関するものである。 The present invention relates to a synthetic resin molded article, a manufacturing method thereof, and an electronic device.
従来、プリンタ等の事務機器(電子機器)においては、外装ケース等のハウジングをプラスチック等の合成樹脂で成形していることが多い。この種のハウジングは、人目に触れる、いわゆる外観部品であるため、プラスチック成形終了後に、意匠面もしくは反意匠面(透明樹脂の場合)に塗装を施し(例えば特許文献1参照)、外観の見栄えを向上させている。
しかしながら、上述したような従来技術には、以下のような問題が存在する。
塗装工程が増加することにより塗装費が高価になる傾向があり、コストアップを招くとともに、塵埃、毛羽等の影響で歩留まりが悪くなるという問題が生じてしまう。
また、近年では塗装工程を設けない製品が増えているが、意匠面の品位が低く見栄えが悪いという問題があった。
さらに、塗装工程では有機溶剤が使用されるため、地球環境に悪影響を及ぼす可能性がある。
However, the following problems exist in the conventional technology as described above.
An increase in the number of painting steps tends to increase the cost of painting, leading to an increase in cost and a problem that yield decreases due to the influence of dust, fluff and the like.
In recent years, products that do not have a painting process are increasing, but there is a problem that the quality of the design surface is low and the appearance is poor.
Furthermore, since an organic solvent is used in the painting process, there is a possibility of adversely affecting the global environment.
本発明は、以上のような点を考慮してなされたもので、塗装工程を設けることなく、意匠面の品位が向上する合成樹脂成形品とその製造方法及びこの合成樹脂成形品を備えた電子機器を提供することを目的とする。 The present invention has been made in consideration of the above points, and a synthetic resin molded product that improves the quality of a design surface without providing a painting process, a method for manufacturing the same, and an electronic device including the synthetic resin molded product The purpose is to provide equipment.
上記の目的を達成するために本発明は、以下の構成を採用している。
本発明の合成樹脂成形品は、第1合成樹脂材で成形された第1成形部と、透明または半透明の第2合成樹脂材で前記第1成形部を覆って一体的に成形された第2成形部とを有し、前記第1成形部には、前記第2成形部との界面に所定の規則性を有するパターンが形成されていることを特徴とするものである。
従って、本発明の合成樹脂成形品では、第2成形部を透過した光が第1成形部のパターンで乱反射することで、光の屈折が変わり、CD(コンパクトディスク)等で多く見受けられる虹色に輝く光輝性が生じる。そのため、本発明では、第2成形部を介して第1成形部(パターン)を見る角度によって色が変わり、意匠面の品位を向上させることができる。また、このパターンは、第1成形部を覆う第2成形部で保護され、また透明または半透明の樹脂で覆うことで深みのある意匠面を得ることができる。
このように、本発明では、塗装工程を設けることなく意匠面の品位が上がるため、コストアップ、歩留まりの悪化、地球環境への悪影響を回避することが可能になる。
In order to achieve the above object, the present invention employs the following configuration.
The synthetic resin molded product according to the present invention includes a first molded part molded with a first synthetic resin material and a first molded part integrally formed by covering the first molded part with a transparent or translucent second synthetic resin material. And a pattern having a predetermined regularity is formed on the interface with the second molded part.
Therefore, in the synthetic resin molded product of the present invention, the light transmitted through the second molding part is irregularly reflected by the pattern of the first molding part, so that the light refraction changes, and the iridescent color often seen in CDs (compact discs) and the like. Shining shine is generated. Therefore, in this invention, a color changes with the angle which looks at a 1st shaping | molding part (pattern) via a 2nd shaping | molding part, and the quality of a design surface can be improved. Moreover, this pattern is protected by the 2nd shaping | molding part which covers a 1st shaping | molding part, and a deep design surface can be obtained by covering with transparent or translucent resin.
As described above, in the present invention, since the quality of the design surface is improved without providing a painting process, it is possible to avoid the cost increase, the yield deterioration, and the adverse influence on the global environment.
前記パターンとしては、所定ピッチで交互に形成された凹凸パターンとする構成を好適に採用できる。
これにより、本発明では隣り合う凸部や、凸部と凹部で反射した光が干渉しあって、容易に光輝性を生じさせることができる。
As said pattern, the structure used as the uneven | corrugated pattern alternately formed by the predetermined pitch can be employ | adopted suitably.
Thereby, in this invention, the light reflected by the adjacent convex part or a convex part and a recessed part interferes, and it can produce glitter easily.
一方、本発明の合成樹脂成形品は、第1合成樹脂材で成形された第1成形部と、透明または半透明の第2合成樹脂材で前記第1成形部を覆って一体的に成形された第2成形部とを有し、前記第1合成樹脂材は、前記第2成形部を介して入射した光を反射する反射材を含むことを特徴とするものである。
従って、本発明の合成樹脂成形品では、第2成形部を透過した光が第1成形部の反射材で乱反射することで、光の屈折が変わり光輝性が生じる。そのため、本発明では、第2成形部を介して第1成形部(パターン)を見る角度によって、反射される光が変化することで色が変わり、意匠面の品位を向上させることができる。また、第1成形部の表面は、第1成形部を覆う第2成形部で保護され、また透明または半透明の樹脂で覆うことで深みのある意匠面を得ることができる。
このように、本発明では、塗装工程を設けることなく意匠面の品位が上がるため、コストアップ、歩留まりの悪化、地球環境への悪影響を回避することが可能になる。
On the other hand, the synthetic resin molded product of the present invention is integrally molded by covering the first molded part molded with the first synthetic resin material and the first molded part with the transparent or translucent second synthetic resin material. The first synthetic resin material includes a reflective material that reflects light incident through the second molded portion.
Therefore, in the synthetic resin molded product of the present invention, the light transmitted through the second molded portion is irregularly reflected by the reflective material of the first molded portion, so that the light refraction is changed and glitter is generated. Therefore, in this invention, a color changes by the light reflected by the angle which looks at a 1st shaping | molding part (pattern) through a 2nd shaping | molding part, and the quality of a design surface can be improved. Moreover, the surface of the 1st shaping | molding part is protected by the 2nd shaping | molding part which covers a 1st shaping | molding part, and a deep design surface can be obtained by covering with transparent or translucent resin.
As described above, in the present invention, since the quality of the design surface is improved without providing a painting process, it is possible to avoid the cost increase, the yield deterioration, and the adverse influence on the global environment.
前記反射材としては、金属材、鉱物、気体の少なくとも一つとする構成を好適に採用できる。
これにより、本発明では、第1成形部に入射した光を容易に反射または乱反射させることが可能になる。
As the reflection material, a configuration in which at least one of a metal material, a mineral, and a gas can be suitably employed.
Thereby, in this invention, it becomes possible to reflect or diffusely reflect the light which injected into the 1st shaping | molding part easily.
また、前記第1成形部としては、前記第2成形部との界面における算術表面粗さが10μm以下である構成を好適に採用できる。
第1成形部の表面粗さが10μmを超える場合には、反射した光の干渉が少なく、人の目では単なる凹凸にしか見えなくなり、品位向上を達成できないが、表面粗さを10μm以下とすることにより、光輝性を生じさせて品位を向上させることが可能になる。
Moreover, as said 1st shaping | molding part, the structure whose arithmetic surface roughness in an interface with the said 2nd shaping | molding part is 10 micrometers or less can be employ | adopted suitably.
When the surface roughness of the first molded part exceeds 10 μm, there is little interference of reflected light, and it can be seen only as concavo-convex by human eyes, and improvement in quality cannot be achieved, but the surface roughness should be 10 μm or less. As a result, it is possible to improve the quality by producing glitter.
また、前記第1合成樹脂材と前記第2合成樹脂材としては、同一材料またはベースレジンが同一の共重合体樹脂材である構成を好適に採用できる。
これにより、本発明では、第1成形部と第2成形部との密着性が向上するため、剥離等が生じづらい高品質の合成樹脂成形品を得ることができる。
In addition, as the first synthetic resin material and the second synthetic resin material, a configuration in which the same material or the base resin is the same copolymer resin material can be suitably employed.
Thereby, in this invention, since the adhesiveness of a 1st shaping | molding part and a 2nd shaping | molding part improves, a high quality synthetic resin molded product which cannot produce peeling etc. easily can be obtained.
そして、本発明の電子機器は、先に記載の合成樹脂成形品を備えることを特徴とするものである。
従って、本発明の電子機器では、意匠面の品位が向上し、コストアップ、歩留まりの悪化、地球環境への悪影響が回避された高品質の電子機器を得ることができる。
And the electronic device of this invention is equipped with the synthetic resin molded product as described above, It is characterized by the above-mentioned.
Therefore, in the electronic device of the present invention, it is possible to obtain a high-quality electronic device in which the quality of the design surface is improved and the cost increase, the yield deterioration, and the adverse effect on the global environment are avoided.
一方、本発明の合成樹脂成形品の製造方法は、第1合成樹脂材で第1成形部を成形する第1工程と、透明または半透明の第2合成樹脂材で前記第1成形部を覆う第2成形部を一体的に成形する第2工程とを有し、前記第1工程では、前記第1成形部の前記第2成形部との界面に所定の規則性を有するパターンを形成することを特徴とするものである。
従って、本発明の合成樹脂成形品の製造方法では、第2成形部を透過した光が第1成形部のパターンで乱反射することで、光の屈折が変わり、CD(コンパクトディスク)等で多く見受けられる虹色に輝く光輝性が生じる。そのため、本発明では、第2成形部を介して第1成形部(パターン)を見る角度によって色が変わり、意匠面の品位を向上させることができる。また、このパターンは、第1成形部を覆う第2成形部で保護され、また透明または半透明の樹脂で覆うことで深みのある意匠面を得ることができる。
このように、本発明では、塗装工程を設けることなく意匠面の品位が上がるため、コストアップ、歩留まりの悪化、地球環境への悪影響を回避することが可能になる。
On the other hand, in the method for producing a synthetic resin molded article of the present invention, the first step of forming the first molded part with the first synthetic resin material, and the first molded part with the transparent or translucent second synthetic resin material are covered. And forming a pattern having a predetermined regularity at the interface between the first molded part and the second molded part. It is characterized by.
Therefore, in the method for producing a synthetic resin molded product according to the present invention, the light transmitted through the second molded part is irregularly reflected by the pattern of the first molded part, so that the light refraction changes, and is often seen on a CD (compact disc) or the like. The rainbow-colored glitter is generated. Therefore, in this invention, a color changes with the angle which looks at a 1st shaping | molding part (pattern) via a 2nd shaping | molding part, and the quality of a design surface can be improved. Moreover, this pattern is protected by the 2nd shaping | molding part which covers a 1st shaping | molding part, and a deep design surface can be obtained by covering with transparent or translucent resin.
As described above, in the present invention, since the quality of the design surface is improved without providing a painting process, it is possible to avoid the cost increase, the yield deterioration, and the adverse influence on the global environment.
前記パターンとしては、所定ピッチで交互に形成された凹凸パターンである
これにより、本発明では隣り合う凸部や、凸部と凹部で反射した光が干渉しあって、容易に光輝性を生じさせることができる。
The pattern is a concavo-convex pattern formed alternately at a predetermined pitch. With this, in the present invention, light reflected by adjacent convex portions or convex portions and concave portions interfere with each other, and easily generate glitter. be able to.
さらに、本発明の合成樹脂成形品の製造方法は、第1合成樹脂材で第1成形部を成形する第1工程と、透明または半透明の第2合成樹脂材で前記第1成形部を覆う第2成形部を一体的に成形する第2工程とを有し、前記第1合成樹脂材は、前記第2成形部を介して入射した光を反射する反射材を含むことを特徴とするものである。
従って、本発明の合成樹脂成形品の製造方法では、第2成形部を透過した光が第1成形部の反射材で乱反射することで光輝性が生じる。そのため、本発明では、第2成形部を介して第1成形部(パターン)を見る角度によって、反射される光が変化することで色が変わり、意匠面の品位を向上させることができる。また、第1成形部の表面は、第1成形部を覆う第2成形部で保護され、また透明または半透明の樹脂で覆うことで深みのある意匠面を得ることができる。
このように、本発明では、塗装工程を設けることなく意匠面の品位が上がるため、コストアップ、歩留まりの悪化、地球環境への悪影響を回避することが可能になる。
Furthermore, in the method for producing a synthetic resin molded article of the present invention, a first step of molding the first molded part with the first synthetic resin material, and the first molded part is covered with a transparent or translucent second synthetic resin material. And a second step of integrally molding the second molded portion, wherein the first synthetic resin material includes a reflective material that reflects light incident through the second molded portion. It is.
Therefore, in the method for producing a synthetic resin molded product according to the present invention, the light transmitted through the second molded part is diffusely reflected by the reflective material of the first molded part, thereby producing glitter. Therefore, in this invention, a color changes by the light reflected by the angle which looks at a 1st shaping | molding part (pattern) through a 2nd shaping | molding part, and the quality of a design surface can be improved. Moreover, the surface of the 1st shaping | molding part is protected by the 2nd shaping | molding part which covers a 1st shaping | molding part, and a deep design surface can be obtained by covering with transparent or translucent resin.
As described above, in the present invention, since the quality of the design surface is improved without providing a painting process, it is possible to avoid the cost increase, the yield deterioration, and the adverse influence on the global environment.
前記反射材としては、金属材、鉱物、気体の少なくとも一つとする構成を好適に採用できる。
これにより、本発明では、第1成形部に入射した光を容易に反射または乱反射させることが可能になる。
As the reflection material, a configuration in which at least one of a metal material, a mineral, and a gas can be suitably employed.
Thereby, in this invention, it becomes possible to reflect or diffusely reflect the light which injected into the 1st shaping | molding part easily.
前記第1合成樹脂材と前記第2合成樹脂材としては、同一材料またはベースレジンが同一の共重合体樹脂材である構成を好適に採用できる。
これにより、本発明では、第1成形部と第2成形部との密着性が向上するため、剥離等が生じづらい高品質の合成樹脂成形品を得ることができる。
As said 1st synthetic resin material and said 2nd synthetic resin material, the structure which the same material or base resin is the same copolymer resin material can be employ | adopted suitably.
Thereby, in this invention, since the adhesiveness of a 1st shaping | molding part and a 2nd shaping | molding part improves, a high quality synthetic resin molded product which cannot produce peeling etc. easily can be obtained.
以下、本発明の合成樹脂成形品とその製造方法及び電子機器の実施の形態を、図1ないし図9を参照して説明する。
なお、以下の説明に用いる各図面では、各部材を認識可能な大きさとするため、各部材の縮尺を適宜変更している。
DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments of a synthetic resin molded product, a manufacturing method thereof, and an electronic device according to the present invention will be described below with reference to FIGS.
In each drawing used for the following description, the scale of each member is appropriately changed to make each member a recognizable size.
(第1実施形態)
ここでは、まず、本発明に係る合成樹脂成形品を備えた第1実施形態の電子機器としてのインクジェット式記録装置(液体噴射装置、液滴吐出装置)1の概略構成について説明する。
図1は、インクジェット式記録装置1を示す斜視図であり、図2は、インクジェット式記録装置1からスキャナユニットを外した装置本体3の斜視図であり、図3は、同じくインクジェット式記録装置1からスキャナユニットを外した装置本体3の異なる角度の斜視図であり、図4は、インクジェット式記録装置1の要部側面図である。
(First embodiment)
Here, a schematic configuration of an ink jet recording apparatus (liquid ejecting apparatus, liquid droplet ejecting apparatus) 1 as an electronic apparatus according to the first embodiment provided with the synthetic resin molded product according to the present invention will be described first.
FIG. 1 is a perspective view showing an ink
図1に示す如くインクジェット式記録装置1は、プリンタ機能に加えてスキャナ機能を備えるタイプであり、装置本体3と、装置本体3の上面側に位置するスキャナユニット5と、スキャナユニット5の後方側に設けられる給送部7とを備えている。装置本体3は、主としてインクジェット式プリンタの機能、すなわち給送部7から給送された「被噴射材」としての記録紙Pに記録を行う「液体噴射ヘッド」としての記録ヘッド38、記録ヘッド38を支持しながら主走査方向Xに往復移動可能なキャリッジ37を備えている。符号9で示す部材は記録紙Pの排出受け部9を示し、この排出受け部9は、プリンタ機能の使用時に手前側にほぼ90°回動した状態で記録後の記録紙Pを受けるようにして使用する。装置本体3の上面左側には操作パネル11が設けられており、スキャナユニット5を使用したスキャニング機能、装置本体3での記録機能及びスキャニングした画像を記録する機能などがこの操作パネル11で操作可能となっている。
As shown in FIG. 1, the ink
スキャナユニット5は回動軸13を中心に上方へ回動することにより開閉可能な蓋体15を備え、蓋体15の下側にはスキャニングを行う際に対象となる印刷物等を載置するガラス載置面(図示せず)が形成されている。更にガラス載置面の下側にはスキャニング装置(図示せず)が設けられている。スキャナユニット5は、それ自体が全体として回動軸17を中心に上方へ回動することで装置本体3の上部が開放し、キャリッジ37等のメンテナンスができるようになっている。
The
図1に示すように給送部7は、不使用時には蓋体19によって閉鎖されており、蓋体19を図1に示すように後方側へ回動させることにより給送部7が開放状態となり、また一定角度位置で固定することで記録紙サポート23として機能するようになる。記録紙サポート23には、記録紙Pの幅寸法に合わせてスライド可能にエッジガイド25が設けられている。蓋体19が開放状態にある時、給送部7には給送口27が形成され、記録紙サポート23に積重された記録紙Pが図示しない給送機構により一枚ずつ給送口27から記録ヘッド38による記録実行領域へ給送されるようになっている。
As shown in FIG. 1, the
給送部7から給送された記録紙Pは、下側の搬送駆動ローラ21と上側の搬送従動ローラ22とに挟持された状態で、副走査方向Yへの精密な搬送動作を受けながら、記録紙Pの搬送方向(副走査方向Y)の下流側に位置する記録ヘッド38側へ搬送される。記録ヘッド38は、キャリッジ37に支持されており、キャリッジ37は記録紙Pの搬送方向(副走査方向Y)に直交する主走査方向Xへ往復運動可能に配設されている。キャリッジ37には、記録ヘッド38から噴射されるインクが充填されたインクカートリッジ(図示せず)が装着される。
While the recording paper P fed from the
記録ヘッド38と対向する位置には、案内前部材26に一体に形成されたプラテン24が設けられており、プラテン24は、記録ヘッド38によって記録紙Pに記録を行う際に、記録紙Pを下側から支持する作用を担う。記録ヘッド38とプラテン24の上面との距離PGは、記録紙Pの厚さに応じて適宜調節できる。距離PGが適正に調整されている状態で、記録紙Pは、プラテン24上を滑らかに通過しながら、高品質の記録が行なわれるようになっており、記録ヘッド38で記録された記録紙Pは、排出駆動ローラ91と排出フレーム93に設けられた排出ギザローラ92とに挟持された状態で、排出駆動ローラ91の回転駆動により引き出されて排出される。また排出フレーム93の先端側(搬送方向上流側)であって、記録ヘッド38と排出ギザローラ92との間には、記録紙Pの後端の浮き上がりを規制する押さえローラ28が設けられている。
A
図3に示すように、キャリッジ37の背面側にはキャリッジ支持部(図示せず)が形成されており、キャリッジ支持部は、スライド軸31に対して滑らかに摺動できるように支持されている。装置本体3には、キャリッジ37を往復可動範囲の任意の位置へ移動させるべく駆動力源としてのキャリッジ駆動用モータ32が配設されている。また、キャリッジ駆動用モータ32の駆動力をキャリッジ37へ伝達する駆動力伝達手段として、キャリッジ駆動用モータ32の出力軸に設けられる駆動プーリ(歯車)331と、反対側に設けられる従動プーリ(歯車)332との間に歯付き無端ベルト33が巻回されている。歯付き無端ベルト33は、図3に示すように、キャリッジ支持部においてキャリッジ37に接続されており、キャリッジ駆動用モータ32の正回転(CW回転)又は逆回転(CCW回転)に伴い、歯付き無端ベルト33が時計回り又は反時計回りに周回運動をすることにより、キャリッジ37が主走査方向Xに往復運動する。
As shown in FIG. 3, a carriage support portion (not shown) is formed on the back side of the
図3に示すように、キャリッジ37の往復可動範囲の一端側(右側)近傍の所定位置には、キャリッジ37の移動制御位置の基点となるホームポジションHPが設定されている。ホームポジションHPの近傍には、ホームポジションHP近傍にキャリッジ37が待機停止している状態でキャリッジ37の他端側(左側)への移動を任意にロック可能なキャリッジロック部材39及び記録ヘッド38のヘッド面を封止するキャッピング装置4(図2参照)が設けられている。キャリッジロック部材39は、記録紙Pを給送する駆動系の輪列を介して回転駆動する回動軸41に対して摩擦抵抗を有した状態で回動可能に軸支されている。また、キャリッジ37の往復可動範囲の他端側(左側)には、キャリッジ37が突き当たった状態で往復可動範囲の他端側(左側)におけるキャリッジ37の移動限界位置を規定する突き当て部2が装置本体3のフレームの一部により形成されている。
As shown in FIG. 3, a home position HP serving as a base point of the movement control position of the
本実施形態では、例えば外装ケース(筺体)としての装置本体3や、蓋体15、19、排出受け部9、記録紙サポート23、エッジガイド25等の合成樹脂成形品が外部に露出しており、これらの合成樹脂成形品は、入射した光を反射(乱反射)する反射層と、この反射層を覆って一体的に成型された保護層とから構成されている。
以下、詳細に説明する。
In the present embodiment, for example, the apparatus
Details will be described below.
図5に、これら合成樹脂成形品の部分断面図を代表的に示す。
この合成樹脂成形品PLは、反射層(第1成形部)PRと、外部に露出される意匠面側の反射層PRの表面を覆う保護層(第2成形部)PHとが2色成形により一体的に構成されている。反射層PRの保護層PHとの界面には、所定ピッチで交互に形成された凹凸パターン(パターン)Paが形成されている。この凹凸パターンPaは、例えば高さH及び幅Wが0.5〜5μm程度の凸部60が0.01〜0.5mm程度のピッチPtの規則性をもって複数配列された構成となっている。なお、反射層PRの材質としては、特に限定はされないが、成形性に優れた第1合成樹脂材として、例えばABS材、PS材、PC材、PP材等のプラスチック材が用いられる。また、本実施形態では、凹凸パターンPaを含む反射層PRの表面は、算術表面粗さが10μm以下に形成されている。
FIG. 5 representatively shows a partial cross-sectional view of these synthetic resin molded products.
In this synthetic resin molded product PL, the reflective layer (first molded portion) PR and the protective layer (second molded portion) PH covering the surface of the reflective layer PR on the design surface exposed to the outside are formed by two-color molding. It is constructed integrally. At the interface between the reflective layer PR and the protective layer PH, concavo-convex patterns (patterns) Pa formed alternately at a predetermined pitch are formed. The concavo-convex pattern Pa has a configuration in which, for example, a plurality of
保護層PHは、例えばPC材、PS材、ABS材、アクリル材等の透明または半透明の第2合成樹脂材により、反射層PR(の凹凸パターンPa)を覆うように形成されている。本実施形態では、反射層PRと保護層PHとを同一材料またはベースレジンが同一の共重合体樹脂材としている。この場合、反射層PRの凹凸パターンPaにおける光の反射性を向上させるために、透明または半透明の上記樹脂に対して着色剤を添加してもよい。 The protective layer PH is formed so as to cover the reflective layer PR (the uneven pattern Pa) with a transparent or translucent second synthetic resin material such as a PC material, a PS material, an ABS material, or an acrylic material. In the present embodiment, the reflective layer PR and the protective layer PH are made of the same material or a copolymer resin material having the same base resin. In this case, a colorant may be added to the transparent or translucent resin in order to improve the light reflectivity in the uneven pattern Pa of the reflective layer PR.
上記の合成樹脂成形品PLを成形する際には、まず、第1工程で反射層PRに対応するキャビティを有する金型及び第1合成樹脂材を用いて反射層PRを成形した後に、第2工程で、例えば固定型のみを保護層PHに応じた金型に交換(変更)し、反射層PRが未排出(未突き出し)状態の移動型との間で第2合成樹脂材を用いた2色成形を行うことにより、反射層PRと保護層PHとが一体的に成形された合成樹脂成形品PLが製造される。 When molding the above synthetic resin molded product PL, first, after forming the reflective layer PR using the mold having the cavity corresponding to the reflective layer PR and the first synthetic resin material in the first step, In the process, for example, only the fixed mold is replaced (changed) with a mold corresponding to the protective layer PH, and the second synthetic resin material is used with the movable mold in which the reflective layer PR is not discharged (not projected). By performing color molding, a synthetic resin molded product PL in which the reflective layer PR and the protective layer PH are integrally molded is manufactured.
本実施形態の合成樹脂成形品PLでは、保護層PHを透過した光が反射層PRの凹凸パターンPaで乱反射することで、隣り合う凸部や、凸部と凹部で反射した光が干渉しあって光の屈折が変わり、CD(コンパクトディスク)等で多く見受けられる虹色に輝く光輝性を容易に生じさせることができる。そのため、本実施形態では、保護層PHを介して反射層PRの凹凸パターンPaを見る角度によって微妙に色合いが変わり、意匠面としての品位を向上させることが可能になる。また、この凹凸パターンPaは、保護層PHで保護されるため、傷等により光輝性が失われることなく、また透明または半透明の樹脂で覆うことで深みのある意匠面を得ることができる。特に、本実施形態では、反射層PRの保護層PHとの界面における表面粗さを10μm以下としているため、表面粗さが10μmを超える場合のように、反射した光の干渉が少なく、人の目では単なる凹凸にしか見えなくなるといった事態を回避して、効果的に光輝性を生じさせて品位を向上させることが可能になる。
このように、本実施形態では、塗装工程を設けることなく意匠面の品位が上がるため、コストアップ、歩留まりの悪化、および地球環境への悪影響を回避することが可能になる。
In the synthetic resin molded product PL of the present embodiment, the light that has passed through the protective layer PH is irregularly reflected by the concavo-convex pattern Pa of the reflective layer PR, so that the light reflected by the adjacent convex portions or the convex portions and the concave portions interferes. Therefore, the refraction of light is changed, and the brilliant brilliancy that is often found on CDs (compact discs) can be easily generated. Therefore, in the present embodiment, the hue slightly changes depending on the angle at which the concave / convex pattern Pa of the reflective layer PR is viewed through the protective layer PH, and the quality as a design surface can be improved. Moreover, since this uneven | corrugated pattern Pa is protected by the protective layer PH, a deep design surface can be obtained by covering with a transparent or translucent resin without losing the glitter due to scratches or the like. In particular, in this embodiment, since the surface roughness at the interface between the reflective layer PR and the protective layer PH is 10 μm or less, there is little interference of reflected light as in the case where the surface roughness exceeds 10 μm. It is possible to improve the quality by avoiding a situation in which the eye can see only a concavo-convex shape, and effectively producing a glitter.
Thus, in this embodiment, since the quality of the design surface is improved without providing a painting process, it is possible to avoid an increase in cost, a decrease in yield, and an adverse effect on the global environment.
(第2実施形態)
続いて、合成樹脂成形品の第2実施形態について、図6を参照して説明する。
上記第1実施形態では、反射層PRが光を乱反射させる凹凸パターンPaを有する構成としたが、本実施形態では反射層PRを構成する材料が光を反射する反射材を含む構成となっている。
なお、この図において、図1乃至図5に示す第1実施形態の構成要素と同一の要素については同一符号を付し、その説明を省略する。
(Second Embodiment)
Next, a second embodiment of the synthetic resin molded product will be described with reference to FIG.
In the first embodiment, the reflective layer PR has a concavo-convex pattern Pa for irregularly reflecting light. However, in the present embodiment, the material constituting the reflective layer PR includes a reflective material that reflects light. .
In this figure, the same components as those of the first embodiment shown in FIGS. 1 to 5 are denoted by the same reference numerals, and the description thereof is omitted.
図6に示すように、本実施形態における反射層PRは、保護層PHと同一の透明または半透明の合成樹脂材に対して、入射した光を反射する反射材Rが添加して混錬されている。この反射材Rとしては、金属、鉱石(鉱物)、ガラス、樹脂等で構成された球状粉末、フレーク粉末、針状粉末、異屈折率粉末等を選択することができる。 As shown in FIG. 6, the reflective layer PR in the present embodiment is kneaded by adding a reflective material R that reflects incident light to the same transparent or translucent synthetic resin material as the protective layer PH. ing. As the reflecting material R, spherical powder, flake powder, acicular powder, different refractive index powder, or the like made of metal, ore (mineral), glass, resin, or the like can be selected.
具体的には、天然雲母の表面を45〜58重量%の酸化チタンで被覆(コーティング)し、被覆層の光学的厚さが245〜415nmで、粒度が5〜60μmのメタリック色金属光沢顔料を反射材Rとして添加・混錬された場合には金色に輝く光輝性を付与することができる。また、平均粒子径0.01〜50μmのアルミニウム箔状物が添加・混錬された場合には、銀色に輝く光輝性を付与することができる。 Specifically, a metallic metallic luster pigment in which the surface of natural mica is coated (coated) with 45 to 58% by weight of titanium oxide, the optical thickness of the coating layer is 245 to 415 nm, and the particle size is 5 to 60 μm. When it is added and kneaded as the reflector R, it is possible to impart a glittering gold color. In addition, when an aluminum foil having an average particle diameter of 0.01 to 50 μm is added and kneaded, it can impart a glittering silvery glitter.
上記の合成樹脂成形品PLにおいては、保護層PHを透過して反射層PRに入射した光は、反射材Rで乱反射することで光輝性が生じる。そのため、本発明では、保護層PHを介して反射層PRを見る角度によって、反射される光が変化することで色が変わり、意匠面の品位を向上させることができる。
従って、本実施形態でも、上記第1実施形態と同様の作用・効果が得られることに加えて、保護層PHと反射層PRとのベースレジンが同一であることから、用いる合成樹脂材の種類を削減することが可能となり、生産性の一層の向上及び生産コストの低下に寄与できる。
In the synthetic resin molded product PL described above, the light that has passed through the protective layer PH and entered the reflective layer PR is diffusely reflected by the reflective material R, resulting in glitter. Therefore, in the present invention, the color is changed by changing the reflected light depending on the angle at which the reflective layer PR is viewed through the protective layer PH, and the quality of the design surface can be improved.
Therefore, in this embodiment, in addition to obtaining the same operation and effect as in the first embodiment, the base resin of the protective layer PH and the reflective layer PR is the same, so the type of synthetic resin material to be used This can contribute to further improvement of productivity and reduction of production cost.
(第3実施形態)
続いて、合成樹脂成形品の第3実施形態について、図7を参照して説明する。
上記第2実施形態では、反射材Rとして金属や鉱物を添加・混錬させる構成としたが、本実施形態では、図7に示すように、反射層PRに点在する気泡(気体)Kを反射材としている。本実施形態では、ベースレジンに対して発泡剤を含有させて成形する発泡成形や、ベースレジンとなる合成樹脂材を金型内で溶融させた状態でエアを注入するガスインジェクション成形等により、気泡Kを有する反射層PRを形成することができる。
(Third embodiment)
Next, a third embodiment of the synthetic resin molded product will be described with reference to FIG.
In the said 2nd Embodiment, it was set as the structure which adds and knead | mixes a metal and a mineral as the reflecting material R, but in this embodiment, as shown in FIG. 7, the bubble (gas) K scattered in the reflection layer PR is shown. Reflective material. In this embodiment, bubbles are formed by foam molding in which a foaming agent is contained in the base resin, or by gas injection molding in which air is injected in a state where the synthetic resin material to be the base resin is melted in the mold. A reflective layer PR having K can be formed.
本実施形態においても、保護層PHを透過して反射層PRに入射した光は、反射材である気泡Kで乱反射することで光輝性が生じる。そのため、本発明でも、保護層PHを介して反射層PRを見る角度によって、反射される光が変化することで色が変わり、意匠面の品位を向上させることができ、上記第2実施形態と同様の効果を得ることができる。 Also in the present embodiment, the light that has passed through the protective layer PH and entered the reflective layer PR is diffusely reflected by the bubbles K that are the reflective material, thereby producing glitter. Therefore, also in the present invention, the color can be changed by changing the reflected light depending on the angle at which the reflective layer PR is viewed through the protective layer PH, and the quality of the design surface can be improved. Similar effects can be obtained.
(第4実施形態)
続いて、第4実施形態として電子機器の別形態について、図8及び図9を参照して説明する。
上記実施形態では、プリンタ機能に加えてスキャナ機能を備えるインクジェット式記録装置を例に用いて説明したが、本実施形態では比較的サイズの小さいハガキ、L判サイズ等の記録用紙への記録に適するように、且つ、運搬の容易性を考慮して小型サイズに構成された記録装置としてのインクジェットプリンタ(以下「プリンタ」と略称する)について説明する。ここで、図8はプリンタ100の外観斜視図、図9はプリンタ100の用紙搬送経路の側断面図である。
(Fourth embodiment)
Next, another embodiment of the electronic device will be described as a fourth embodiment with reference to FIGS.
In the above embodiment, an ink jet recording apparatus having a scanner function in addition to a printer function has been described as an example. However, the present embodiment is suitable for recording on recording paper having a relatively small postcard, L size, or the like. An inkjet printer (hereinafter abbreviated as “printer”) as a recording apparatus configured in a small size in consideration of ease of transport will be described. Here, FIG. 8 is an external perspective view of the
このプリンタ100は、プリンタ本体の後部に、積重された複数枚の記録用紙を傾斜姿勢に支持する給送装置101を備え、プリンタ本体の前部には、記録の行われた記録用紙をスタックするスタッカ150が、図8に示す様に略垂直に立設された収納状態と、プリンタ前方側に開いて記録用紙をスタック可能な使用状態(図示せず)とを切り換え可能に設けられている。
The
プリンタ100の上面中央には、電源ボタン、印刷設定ボタン等によって構成された操作部131と、印刷設定内容や現在の動作ステータス等を表示する表示部130が配置され、プリンタ本体の前部右側には、画像データ等が記憶された半導体メモリ媒体を装着可能なカードスロット(図示せず)を覆う開閉自在なカバー161が設けられている。即ち、プリンタ100は、外部のホスト・コンピュータと接続して印刷データを受信するのみならず、画像データを記憶した半導体メモリから直接画像データを読み込み、そして印刷用のデータを生成して自ら印刷実行可能に構成された所謂スタンドアロンプリンタである。
In the center of the upper surface of the
プリンタ100の外観を構成するハウジングは、複数の部材によって構成され、図8にはその中で上部パネル151と、ハウジング左153と、ハウジング右155と、サイドパネル右159と、が示されている。そして、ハウジング左153とハウジング右155とには、把持部137と、把持部137の両端からプリンタ本体に向かってL字状に延びる腕部141とを備えて構成された手提げ用ハンドル(以下「ハンドル」と略称する)135が、プリンタ本体を側視して回動自在に取り付けられていて、これによってプリンタ100を持ち運ぶ際にハンドル135を把持すれば、プリンタ100を容易に運搬することができるようになっている。
The housing constituting the external appearance of the
尚、プリンタ100のハウジング構造は、上下に分割された装置本体をハウジング左153とハウジング右155とでキャップするようになっており、従ってハンドル155によってプリンタ100を持ち運ぶ場合でも、装置本体が上下に分離する様なこともなく、運搬の際の安全性(即ちハウジングの機械的強度)が向上している。
The housing structure of the
続いて、プリンタ100の内部構成について説明する。プリンタ100には、記録用紙Pに記録を行う記録手段の主たる構成要素として、主走査方向(図9の紙面表裏方向)に往復可能にキャリッジガイド軸112によって軸支されたキャリッジ110が設けられている。そして、該キャリッジ110には記録用紙Pにインクを吐出して記録を行なう記録ヘッド113が搭載されている。
Next, the internal configuration of the
記録ヘッド113の下方には、記録ヘッド113と対向して記録ヘッド113のヘッド面と記録用紙Pとの間のギャップを規定するプラテン128が設けられている。そしてキャリッジ110とプラテン128との間に記録用紙Pを主走査方向と直交する副走査方向(図9の左右方向)に所定の搬送量で搬送する動作と、記録ヘッド113を主走査方向に一往復させる間に記録ヘッド113から記録用紙Pにインクを噴射する動作とを交互に繰り返すことによって記録用紙Pに記録が行われる。
A platen 128 that defines the gap between the head surface of the recording head 113 and the recording paper P is provided below the recording head 113 so as to face the recording head 113. Then, the recording paper P is transported between the
次に、記録用紙Pの搬送経路に従ってプリンタ100の構成を更に詳しく説明する。先ず最も搬送方向上流側に記録用紙Pを積重する支持部材としてのホッパ116が、給送装置101の基体を構成するフレーム105に揺動可能に設けられている。ホッパ116上の記録用紙Pは給送用ローラ114の回転軸117の回転に伴って、ホッパ116が所定のタイミングで上昇し、給送用ローラ114に向けて押し上げられる。
これら給送用ローラ114、ホッパ116等を含む給送装置101は、給送用ローラ114の回転に伴って最上位に位置する記録用紙Pから順番に、給送用ローラ114近傍に設けられる分離パッド107によって次位以降の記録用紙Pから分離しつつ、1枚ずつピックアップし、されて搬送方向下流に向かって給送する。
Next, the configuration of the
The
ここで、給送装置101は、図9の仮想線と実線との関係で示す様にホッパ116を含む、フレーム105を基体とする装置(ユニット)そのものが回動自在に設けられ、実線で示す使用状態では後方に張り出す様な傾斜姿勢となる。一方、仮想線で示す収納状態においては、記録用紙Pを挿入する為の開口165が塞がれて塵埃等の進入を防止可能となっている。そして当該収納状態では、給送装置101は後方に張り出さず、プリンタ100のコンパクト化及び外観の向上が図られる様になっている。
Here, as shown in the relationship between the phantom line and the solid line in FIG. 9, the
給送用ローラ114の下流には、記録用紙Pの通過を検出する被記録媒体検出手段(図示せず)が設けられており、その下流には搬送用駆動ローラ119aと搬送用従動ローラ119bとによって構成される搬送用ローラ119が設けられている。このうち搬送用従動ローラ119bは、搬送用従動ローラ用のローラホルダ118の下流側において軸支され、当該ローラホルダ118は、図示しない回転軸を中心に回動可能に設けられ、かつ図示しないねじりコイルばねによって搬送用従動ローラ119bが常に搬送用駆動ローラ119aに圧接したニップ状態になるように回動付勢されている。
A recording medium detection means (not shown) for detecting the passage of the recording paper P is provided downstream of the feeding
搬送用ローラ119によって挟圧された状態で搬送される記録用紙Pは記録ヘッド113の下方の記録ポジション126に導かれ、上述のキャリッジ110及び搬送用ローラ119の動作によって記録用紙Pに所望の記録が実行される。記録ヘッド113とその下方において、これと対向して設けられるプラテン128とのギャップは高精度の記録を実行する上で極めて重要な要素となっており、記録用紙Pの厚さの変化に応じて適宜調節されるようになっている。
The recording sheet P conveyed in a state of being pinched by the conveying
記録ヘッド113の下流には排出用駆動ローラ120aと、排出用歯付きローラ120bとによって構成される排出用ローラ120が設けられ、この排出用ローラ120によって排出された記録用紙Pは更に下流に位置する排出用スタッカ150上に排出されるようになっている。尚、排出用歯付きローラ120bは、その外周に複数の歯を有する歯付きローラであり、排出用歯付きローラ用の図示しないローラホルダによって自由回転可能に軸支されている。排出用歯付きローラ120bの上流には補助歯付きローラ122が設けられ、当該補助歯付きローラ122によって記録用紙Pのプラテン128からの浮き上がりが防止され、適切な記録品質が維持されるようになっている。
A
そして、上記のプリンタ100においては、カバー161、上部パネル151、ハウジング左153、ハウジング右155、サイドパネル右159、ハンドル135等を、上述した意匠面を有する合成樹脂成形品PLと同様の構成とすることができる。
また、上記のプリンタ100においては、給送用ローラ114の回転軸117、搬送用駆動ローラ119aと搬送用従動ローラ119b、排出用駆動ローラ120a、排出用歯付きローラ120b、補助歯付きローラ122等に回転駆動を伝達するための歯車(ピニオン)等を、上述した合成樹脂成形品PLと同様の構成とすることができる。この場合には、例えば外装ケースが透過性を有して、これら内部の機能部品が外部から視認できる際には、スケルトン風のプリンタ100を提供することが可能になり、さらに、スキャナ等においては、走査光等も外部から視認可能となり、意匠面の品位のみならず、趣のある電子機器を提供することが可能になる。
In the
Further, in the
以上、添付図面を参照しながら本発明に係る好適な実施形態について説明したが、本発明は係る例に限定されないことは言うまでもない。上述した例において示した各構成部材の諸形状や組み合わせ等は一例であって、本発明の主旨から逸脱しない範囲において設計要求等に基づき種々変更可能である。 As described above, the preferred embodiments according to the present invention have been described with reference to the accompanying drawings, but the present invention is not limited to the examples. Various shapes, combinations, and the like of the constituent members shown in the above-described examples are examples, and various modifications can be made based on design requirements and the like without departing from the gist of the present invention.
例えば、上記第1実施形態で示した凹凸パターンPaは一例であり、所定の規則性を有するものであれば、他のパターン(波状等)であってもよい。
また、上記実施形態では、第1合成樹脂材と第2合成樹脂材とが同一材料として説明したが、これに限定されるものではなく、例えばベースレジンが同一の共重合体樹脂材であったり、別の材料であってもよい。また、反射層PRに含まれる反射材も金属、鉱石(鉱物)、ガラス、樹脂、気体のいずれか一つに限られるものではなく、複数が含まれる構成としてもよい。
For example, the concavo-convex pattern Pa shown in the first embodiment is an example, and may be another pattern (such as a wave shape) as long as it has a predetermined regularity.
Moreover, in the said embodiment, although the 1st synthetic resin material and the 2nd synthetic resin material were demonstrated as the same material, it is not limited to this, For example, a base resin is the same copolymer resin material. Another material may be used. Also, the reflective material included in the reflective layer PR is not limited to any one of metal, ore (mineral), glass, resin, and gas, and may include a plurality.
また、上記実施形態では、本発明に係る合成樹脂成形品がプリンタ等の記録装置に配されるものとして説明したが、これ以外にも、種々の電子機器に適用することができる。例えば、液晶プロジェクタ、マルチメディア対応のパーソナルコンピュータ(PC)及びエンジニアリング・ワークステーション(EWS)、ページャ、ワードプロセッサ、テレビ、ビューファインダ型又はモニタ直視型のビデオテープレコーダ、電子手帳、電子卓上計算機、カーナビゲーション装置、POS端末、タッチパネルを備えた装置などの電子機器、さらに自動車のコンソールのハウジング面等の意匠面に適用することが可能である。 In the above-described embodiment, the synthetic resin molded product according to the present invention has been described as being disposed in a recording apparatus such as a printer. However, the present invention can be applied to various electronic devices. For example, LCD projectors, multimedia-compatible personal computers (PCs) and engineering workstations (EWS), pagers, word processors, televisions, viewfinder type or monitor direct view type video tape recorders, electronic notebooks, electronic desk calculators, car navigation systems The present invention can be applied to an electronic device such as a device, a POS terminal, a device including a touch panel, and a design surface such as a housing surface of an automobile console.
K…気泡(気体、反射材)、 Pa…凹凸パターン(パターン)、 PH…保護層(第2成形部)、 PL…合成樹脂成形品、 PR…反射層(第1成形部)、 R…反射材、 1…インクジェット式記録装置(液体噴射装置、液滴吐出装置) K: Air bubbles (gas, reflective material), Pa: Uneven pattern (pattern), PH: Protective layer (second molded part), PL: Synthetic resin molded product, PR: Reflective layer (first molded part), R: Reflected 1. Inkjet recording apparatus (liquid ejecting apparatus, droplet ejecting apparatus)
Claims (12)
透明または半透明の第2合成樹脂材で前記第1成形部を覆って一体的に成形された第2成形部とを有し、
前記第1成形部には、前記第2成形部との界面に所定の規則性を有するパターンが形成されていることを特徴とする合成樹脂成形品。 A first molded part molded of a first synthetic resin material;
A second molded part integrally formed by covering the first molded part with a transparent or translucent second synthetic resin material;
A synthetic resin molded product, wherein a pattern having a predetermined regularity is formed on the interface with the second molded part in the first molded part.
前記パターンは、所定ピッチで交互に形成された凹凸パターンであることを特徴とする合成樹脂成形品。 In the synthetic resin molded product according to claim 1,
The synthetic resin molded product, wherein the pattern is an uneven pattern formed alternately at a predetermined pitch.
透明または半透明の第2合成樹脂材で前記第1成形部を覆って一体的に成形された第2成形部とを有し、
前記第1合成樹脂材は、前記第2成形部を介して入射した光を反射する反射材を含むことを特徴とする合成樹脂成形品。 A first molded part molded of a first synthetic resin material;
A second molded part integrally formed by covering the first molded part with a transparent or translucent second synthetic resin material;
Said 1st synthetic resin material contains the reflecting material which reflects the light which injected through the said 2nd shaping | molding part, The synthetic resin molded product characterized by the above-mentioned.
前記反射材は、金属材、鉱物、気体の少なくとも一つであることを特徴とする合成樹脂成形品。 In the synthetic resin molded product according to claim 3,
The synthetic resin molded product, wherein the reflective material is at least one of a metal material, a mineral, and a gas.
前記第1成形部は、前記第2成形部との界面における算術表面粗さが10μm以下であることを特徴とする合成樹脂成形品。 In the synthetic resin molded product according to any one of claims 1 to 4,
The synthetic resin molded product, wherein the first molded part has an arithmetic surface roughness of 10 μm or less at an interface with the second molded part.
前記第1合成樹脂材と前記第2合成樹脂材とは、同一材料またはベースレジンが同一の共重合体樹脂材であることを特徴とする合成樹脂成形品。 In the synthetic resin molded product according to any one of claims 1 to 5,
The first synthetic resin material and the second synthetic resin material are the same material or a copolymer resin material having the same base resin.
透明または半透明の第2合成樹脂材で前記第1成形部を覆う第2成形部を一体的に成形する第2工程とを有し、
前記第1工程では、前記第1成形部の前記第2成形部との界面に所定の規則性を有するパターンを形成することを特徴とする合成樹脂成形品の製造方法。 A first step of molding the first molding part with the first synthetic resin material;
A second step of integrally molding a second molded part that covers the first molded part with a transparent or translucent second synthetic resin material,
In the first step, a pattern having a predetermined regularity is formed at an interface between the first molding part and the second molding part.
前記パターンは、所定ピッチで交互に形成された凹凸パターンであることを特徴とする合成樹脂成形品の製造方法。 In the manufacturing method of the synthetic resin molded product of Claim 8,
The method for producing a synthetic resin molded product, wherein the pattern is a concavo-convex pattern formed alternately at a predetermined pitch.
透明または半透明の第2合成樹脂材で前記第1成形部を覆う第2成形部を一体的に成形する第2工程とを有し、
前記第1合成樹脂材は、前記第2成形部を介して入射した光を反射する反射材を含むことを特徴とする合成樹脂成形品の製造方法。 A first step of molding the first molding part with the first synthetic resin material;
A second step of integrally molding a second molded part that covers the first molded part with a transparent or translucent second synthetic resin material,
The method of manufacturing a synthetic resin molded product, wherein the first synthetic resin material includes a reflective material that reflects light incident through the second molded portion.
前記反射材は、金属材、鉱物、気体の少なくとも一つであることを特徴とする合成樹脂成形品の製造方法。 In the manufacturing method of the synthetic resin molded product according to claim 10,
The method for producing a synthetic resin molded product, wherein the reflective material is at least one of a metal material, a mineral, and a gas.
前記第1合成樹脂材と前記第2合成樹脂材とは、同一材料またはベースレジンが同一の共重合体樹脂材であることを特徴とする合成樹脂成形品の製造方法。 In the manufacturing method of the synthetic resin molded product according to any one of claims 8 to 11,
The method for producing a synthetic resin molded product, wherein the first synthetic resin material and the second synthetic resin material are the same material or a copolymer resin material having the same base resin.