JP2008223155A - Deodorizing antibacterial sheet and use thereof - Google Patents

Deodorizing antibacterial sheet and use thereof Download PDF

Info

Publication number
JP2008223155A
JP2008223155A JP2007059264A JP2007059264A JP2008223155A JP 2008223155 A JP2008223155 A JP 2008223155A JP 2007059264 A JP2007059264 A JP 2007059264A JP 2007059264 A JP2007059264 A JP 2007059264A JP 2008223155 A JP2008223155 A JP 2008223155A
Authority
JP
Japan
Prior art keywords
antibacterial
sheet
bamboo charcoal
powder
deodorant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2007059264A
Other languages
Japanese (ja)
Inventor
Ritsuko Tanaka
リツ子 田仲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to JP2007059264A priority Critical patent/JP2008223155A/en
Publication of JP2008223155A publication Critical patent/JP2008223155A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a deodorizing antibacterial sheet having high deodorizing power and antibacterial power, giving good feeling and affinity to the skin to give good feeling in use and exhibiting wound heal promoting effect and to provide products produced by using the sheet. <P>SOLUTION: A front nonwoven fabric sheet 1 is formed by entangling short silk fibers by needle punching or hydroentanglement and pressing the product. An intermediate sheet 2 is produced by applying Cu-Ni alloy plating to the surface of iron powder, uniformly mixing the obtained antibacterial metal powder into a blended fiber of rayon and acetate fiber and placing bamboo charcoal powder under the fiber sheet to a thickness of about 1 mm. The intermediate sheet 2 is sandwiched between two front sheets 1 and the obtained three-layered laminate is hot-pressed to integrally bond the layers. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、防臭と抗菌力がある抗菌性金属粉と絹素材の表シートと竹炭層を有する防臭抗菌シート、及び同シートを使用した防臭抗菌機能を有するマスク・シャツ・靴中敷・壁布・肌着の利用技術に関する。   The present invention relates to an antibacterial metal powder having a deodorizing and antibacterial activity, a surface sheet of silk material, a deodorizing antibacterial sheet having a bamboo charcoal layer, and a mask / shirt / shoe insole / wall cloth having a deodorizing and antibacterial function using the sheet・ It relates to the use technology of underwear.

防臭抗菌性を有するシートとして、木炭パウダーを含んだ綿繊維又は不織布が実用新案登録第３１１７７５３号公報で知られている。同公報では、木炭パウダーを含んだ同シートに更に二酸化チタン粉を含んだバインダー層を形成して防臭・抗菌力を高めたマスクとした利用技術が開示されている。
しかしながら、このシート・マスクで使用される木炭パウダーでは、その脱臭力・抗菌力が弱く、又木炭パウダーを含んだ綿・不織布では人の肌との感触が悪く使用感がよくないものであった。又抗菌力・吸水性も充分に期待できにくいものであった。
又、生体・肌とのなじみがよい絹繊維をガーゼ生地に用いる技術が再表９７／００７２７３の再公表特許公報で知られている。しかしながら、この素材のみでは抗菌力及び防臭性に欠くものであった。
更に、金属粉の表面にＣｕ−Ｎｉ合金のメッキを施すことで高い抗菌力を有する抗菌性金属粉が特開２００３−１３８３８６号公報で知られている。しかしながら、この抗菌力を有する金属粉は、抗菌力・防かび性が強力で医療用に使用されているが、強力な抗菌性を有するため、人体・肌に直接長い間接触する使用には刺激が強すぎて実用的ではなかった。又防臭・消臭機能が低いものであった。
実用新案登録第３１１７７５３号公報 再表９７／００７２７３の再公表特許公報 特開２００３−１３８３８６号公報 As a sheet having deodorizing and antibacterial properties, a cotton fiber or non-woven fabric containing charcoal powder is known from Utility Model Registration No. 3117754. This publication discloses a technique for using a mask in which a binder layer containing titanium dioxide powder is further formed on the same sheet containing charcoal powder to enhance deodorization and antibacterial activity.
However, the charcoal powder used in this sheet / mask is weak in deodorizing and antibacterial power, and the cotton / nonwoven fabric containing charcoal powder has poor touch with human skin and is not good to use. . In addition, antibacterial activity and water absorption were not sufficiently expected.
In addition, a technique of using silk fibers that are well-adapted to living body / skin for gauze fabric is known from the republished patent publication of Table 97/007273. However, this material alone lacks antibacterial activity and deodorization.
Furthermore, an antibacterial metal powder having a high antibacterial power by plating a surface of the metal powder with a Cu—Ni alloy is known from Japanese Patent Application Laid-Open No. 2003-138386. However, this antibacterial metal powder has strong antibacterial and antifungal properties and is used for medical purposes. However, because it has strong antibacterial properties, it is irritating to direct contact with the human body and skin for a long time. Was too strong to be practical. The deodorizing / deodorizing function was low.
Utility Model Registration No. 3111753 Republished Patent Gazette of Table 97/007273 JP 2003-138386 A

本発明が解決しようとする課題は、従来のこれらの問題点を解消し、防臭力・抗菌力が高く、肌触り・肌とのなじみがよく使用感がよく、しかも創傷治癒促進効果がある防臭抗菌シート及び上記特徴を有するそのシート利用製品のマスク・シャツ・靴中敷・壁布・肌着を提供することにある。   The problems to be solved by the present invention are to solve these conventional problems, have a high deodorizing ability and antibacterial ability, have a good feel and familiarity with the skin, have a good feeling of use, and have an effect of promoting wound healing. An object of the present invention is to provide a mask, a shirt, a shoe insole, a wall cloth, and an undergarment for the sheet and the sheet-use product having the above characteristics.

かかる課題を解決した本発明の構成は、
１） 微紛状の金属粒の表面にＣｕ−Ｎｉ合金メッキを施した抗菌性金属粉を混入させた織布又は不織布の布シートの一部又は全部のシート表面又はシート内に、竹炭粉を薄く付着させた竹炭層を形成した防臭抗菌シート
２） 布シートが短い絹繊維を絡合させた後加圧してシート状にし、更にこれに細孔を多数穿孔した通気性の高い絹シートである、前記１）記載の防臭抗菌シート
３） 前記１）又は２）記載の防臭抗菌シートを用いてマスク面を形成し、竹炭粉がマスク面の下方に形成された防臭抗菌マスク
４） 前記１）又は２）記載の防臭抗菌シートを靴中敷の上層に設けたことを特徴とする、防臭抗菌靴中敷
５） 前記１）又は２）記載の防臭抗菌シートを壁布地とした、防臭抗菌壁布
６） 前記１）又は２）記載の防臭抗菌シートを生地として作製された、防臭抗菌肌着
７） 前記１）又は２）記載の防臭抗菌シートをシャツ生地として作製された、防臭抗菌シャツ
にある。 The configuration of the present invention that solves this problem is as follows.
1) Bamboo charcoal powder is applied on the surface or in a part or all of a woven or non-woven cloth sheet in which antibacterial metal powder plated with Cu-Ni alloy is mixed on the surface of fine metal particles. Anti-bacterial and antibacterial sheet with thinly attached bamboo charcoal layer 2) A cloth sheet is a highly breathable silk sheet in which short silk fibers are intertwined and then pressed to form a sheet, and a large number of pores are perforated. 1) Deodorant antibacterial sheet 3) described above 1) A mask surface is formed using the deodorized antibacterial sheet 1) or 2), and bamboo charcoal powder is formed below the mask surface 4) 1) Or the deodorant antibacterial sheet | seat insole characterized by providing the deodorant antibacterial sheet of 2) in the upper layer of a shoe insole 5) The deodorant antibacterial wall which used the deodorant antibacterial sheet of said 1) or 2) as a wall fabric Cloth 6) The deodorant antibacterial sheet described in 1) or 2) above is used as a fabric. Produced by, deodorizing antibacterial underwear 7) wherein 1) or 2) produced a deodorizing antibacterial sheet according as shirt fabric in deodorant antimicrobial shirt.

本発明によれば、布シートにＣｕ−Ｎｉ合金メッキされた抗菌性金属粉を付着させたことにより、金属粉のもつ高い抗菌力・防かび力が発現できる。しかも竹炭粉層をシートの表面又は内部の一部又は全面に形成したことにより、竹炭粉が有する有害物質の吸着、消臭及び防菌・除菌力が働いて高い防臭力を有し、又遠赤外線を放出し、更に適度の保湿力を有する。綿又は絹等の布シートに、金属粉は分散されて入れられることで、肌・人体との直接の接触が少なくなり、刺激性がなく、使用感に優れている。特に布シートが絹素材の絡合加圧シートであれば、肌とのなじみ・肌触りがよく、傷の治癒効果を有する。   According to the present invention, the antibacterial and antifungal power of the metal powder can be exhibited by attaching the antibacterial metal powder plated with Cu-Ni alloy to the cloth sheet. Moreover, because the bamboo charcoal powder layer is formed on the surface or part of the inside or the entire surface of the sheet, the bamboo charcoal powder adsorbs harmful substances, deodorizes, and has a high deodorizing power due to its antibacterial / sterilizing power. It emits far-infrared rays and has a moderate moisturizing power. Since the metal powder is dispersed and put in a cloth sheet such as cotton or silk, direct contact with the skin / human body is reduced, there is no irritation, and the feeling of use is excellent. In particular, if the cloth sheet is an intertwined pressure sheet made of silk, it has a good familiarity and feel with the skin and has a wound healing effect.

本発明の布シートの織布・不織布としては、綿繊維，絹繊維，紙を使用したものがあるが、肌とのなじみがよい絹繊維を使用することが好ましい。特に抗菌性金属粉を入れるために短い絹繊維を絡合して加圧して作製する絹布がよい。抗菌性金属粉を入れる方法として、絹繊維中に抗菌性金属粉を散布して固定する方法もあるが、好ましくは上下一対の短い絹繊維のシート間に、熱溶解性のレーヨン・アセテート又はその混同繊維を入れ、これに抗菌性金属粉を混入し、又は竹炭粉を混入又は配置し、これらの積層物を加熱加圧してレーヨン・アセテートを溶かして接着剤にしてシートを互に連結して一体化し、内部に金属粉，竹炭粉を封止する方法が好ましい。抗菌性金属粉としては、鉄粉の表面にＣｕ−Ｎｉ合金メッキを施すことで抗菌性を得るケニファイン粉（商標名：株式会社神戸製鋼所）が代表例であり、ケニファイン粉が好ましい。   As the woven / nonwoven fabric of the cloth sheet of the present invention, there are those using cotton fibers, silk fibers, and paper, but it is preferable to use silk fibers that are well-familiar with the skin. In particular, a silk cloth produced by entanglement and pressurization of short silk fibers in order to put antibacterial metal powder is preferable. As a method of putting the antibacterial metal powder, there is a method of spraying and fixing the antibacterial metal powder in the silk fiber. Preferably, the heat-dissolved rayon acetate or its Put mixed fiber, mix antibacterial metal powder, or mix or place bamboo charcoal powder, heat and press these laminates to dissolve rayon acetate and make adhesives to connect sheets together The method of integrating and sealing metal powder and bamboo charcoal powder inside is preferable. A representative example of the antibacterial metal powder is Kenifine powder (trade name: Kobe Steel, Ltd.), which obtains antibacterial properties by plating the surface of the iron powder with Cu—Ni alloy, and Kenifine powder is preferred.

以下、本発明の実施例の防臭抗菌シート及びその利用の防臭抗菌マスクを説明する。
本実施例１は、シートの素材として短い絹繊維をニードルパンチ法又は水流絡合法で絡合し、これを加圧して不織布の長尺の表シートにする。次に、この絹素材の表シートの２枚間に、鉄粉表面にＣｕ−Ｎｉ合金のメッキを施した抗菌性金属粉（商標名：ケニファイン粉末：株式会社神戸製鋼所）をレーヨン・アセテート又はそれらの混合繊維シートの全体に均一に、しかも下部に竹炭粉を帯状に１ｍｍ程厚みで挟持した長尺の中間シートを配置して、上下２枚の表シートと中間シートを積層して外側から加熱加圧して混合繊維を溶融して一体的に連結して布シートとした防臭抗菌シートを作製する。 Hereinafter, the deodorization antibacterial sheet of the Example of this invention and the deodorization antibacterial mask of the utilization are demonstrated.
In Example 1, a short silk fiber is entangled by a needle punch method or a water entanglement method as a raw material of the sheet, and this is pressurized to form a long nonwoven fabric front sheet. Next, an antibacterial metal powder (trade name: Kenifine Powder: Kobe Steel Co., Ltd.) in which the surface of the iron powder is plated with a Cu—Ni alloy is placed between the two surface sheets of the silk material with rayon acetate or A long intermediate sheet with a thickness of about 1 mm sandwiched between bamboo charcoal powders in a strip shape is arranged uniformly on the entire mixed fiber sheet, and two upper and lower front sheets and intermediate sheets are laminated from the outside. A deodorized and antibacterial sheet is produced by heating and pressing to melt the mixed fibers and integrally connecting them to form a cloth sheet.

次に、作製した防臭抗菌シートを１８ｃｍ×１１ｃｍ程の長方形状のマスク面の大きさに切断し、切断した周縁を折り返して且つ耳掛けの左右のマスクゴム紐端を上下端で固定する。   Next, the produced deodorant antibacterial sheet is cut into a rectangular mask surface of about 18 cm × 11 cm, the cut periphery is folded back, and the left and right mask rubber string ends of the ear hook are fixed at the upper and lower ends.

図１は、実施例１の防臭抗菌シートを示す分解斜視図である。
図２は、実施例１の防臭抗菌シートを示す一部切欠斜視図である。
図３は、実施例１の防臭抗菌シートの拡大縦断面図である。
図４は、実施例１の防臭抗菌マスクを示す一部切欠斜視図である。 FIG. 1 is an exploded perspective view showing the deodorized antibacterial sheet of Example 1. FIG.
FIG. 2 is a partially cutaway perspective view showing the deodorized antibacterial sheet of Example 1. FIG.
FIG. 3 is an enlarged longitudinal sectional view of the deodorizing antibacterial sheet of Example 1.
4 is a partially cutaway perspective view showing the deodorizing and antibacterial mask of Example 1. FIG.

図中、Ａは実施例１の絹素材の布シートの防臭抗菌シートである。符号１〜４は同防臭抗菌シートＡの構成部分で、１は５〜７ｃｍ程の短い絹繊維をニードルパンチ法でもって絡合させて加圧した２０ｃｍ巾の長尺の不織布の表シート、２はレーヨン・アセテートの混合繊維２−ａ中に鉄粉表面にＣｕ−Ｎｉ合金メッキを施した抗菌性金属粉３のケニファイン粉（商標名：株式会社神戸製綱所販売）を均一に散布して混入し、又下部の３ｃｍ程の巾領域に竹炭粉を１ｍｍ程の厚みとなるように１３ｃｍの長さにわたって配置して竹炭層４を形成し、同竹炭層を４ｃｍの間隔をあけて間欠的に長手方向に設けた長尺の中間シート、３は抗菌性金属粉、４は竹炭層、５は１ｍｍ程の径の穴である。実施例１の防臭抗菌シートＡは、上下一対の表シート１間に上記中間シート２を挿入するように積層し、積層したものを上下から加圧しながら加熱させて、中間シート２の混合繊維２−ａを溶かして上下の表シート１と中間シート２の３層のシートを接着して一体化し、それを１ｍｍ径の針で多数の穴５を形成したものである。Ｂは実施例１の防臭抗菌シートＡを用いて作製されるマスク、１０〜１２は同マスクの構成部分で、１０は防臭抗菌シートＡを１７ｃｍ巾で切り出したマスク本体、１１はマスク本体１０の周縁を折り返して加圧接着した折り返し部、１２は同折り返しに一端を挟んで固定したマスクゴム紐である。   In the figure, A is a deodorizing and antibacterial sheet of the silk cloth sheet of Example 1. Reference numerals 1 to 4 are constituent parts of the deodorant antibacterial sheet A, and 1 is a front sheet of a long nonwoven fabric of 20 cm width that is pressed by entanglement with a short silk fiber of about 5 to 7 cm by a needle punch method. Spread uniformly the antibacterial metal powder 3 Keni fine powder (trade name: sold by Kobe Steel Corporation) in the rayon / acetate mixed fiber 2-a with the Cu-Ni alloy plating on the iron powder surface. In addition, the bamboo charcoal powder is disposed over a width of about 3 cm in the lower part of the width region to form a bamboo charcoal layer 4 having a thickness of about 1 mm to form a bamboo charcoal layer 4, and the bamboo charcoal layer is intermittently spaced at an interval of 4 cm. 3 is an antibacterial metal powder, 4 is a bamboo charcoal layer, and 5 is a hole having a diameter of about 1 mm. The deodorized antibacterial sheet A of Example 1 was laminated so that the intermediate sheet 2 was inserted between a pair of upper and lower front sheets 1, and the laminated sheet was heated while being pressed from above and below to mix the fibers 2 of the intermediate sheet 2 -A is melted and the upper and lower front sheets 1 and intermediate sheets 2 are bonded and integrated to form a large number of holes 5 with 1 mm diameter needles. B is a mask produced using the deodorant antibacterial sheet A of Example 1, 10 to 12 are constituent parts of the mask, 10 is a mask body cut out of the deodorant antibacterial sheet A with a width of 17 cm, and 11 is a mask body 10. Reference numeral 12 denotes a folded portion which is folded around the periphery and is pressure-bonded, and a mask rubber string 12 which is fixed by sandwiching one end of the folded portion.

この実施例１のマスクＢのマスク本体１０は、絹繊維の表シート１であるので、肌にソフトに接触し、しかも人体・肌の汗，血等を吸収でき、傷の治癒効果を有する。
表シート１の細孔の穴５によってマスク本体１０の通気性は確保されている。
しかも、大気からの菌・カビ又は人体側からの息・呼吸に含まれる菌・カビは、マスク本体１０の表シート１内に封止されたケニファイン粉の抗菌性金属粉と接触し、その表面のＣｕ−Ｎｉメッキ層の着水膜に溶けたイオンの働きによる抗菌作用により、強力に減菌・抑菌させる。
更に、竹炭層４は、有害ガス吸着作用・消臭作用・保湿作用があり、遠赤外線の放出効果がある。特に息の中の悪臭を消臭し、長い時間使用し易くすることができる。 Since the mask body 10 of the mask B of Example 1 is the front sheet 1 of silk fiber, it can come into soft contact with the skin and absorb human body / skin sweat, blood, etc., and has a wound healing effect.
The air permeability of the mask body 10 is ensured by the holes 5 in the pores of the front sheet 1.
In addition, the bacteria and mold contained in the atmosphere and the bacteria and mold contained in the breath and respiration from the human body come into contact with the antibacterial metal powder of the Kenifine powder sealed in the front sheet 1 of the mask body 10, and the surface The bacteria are strongly sterilized and suppressed by the antibacterial action due to the action of ions dissolved in the water landing film of the Cu-Ni plating layer.
Furthermore, the bamboo charcoal layer 4 has a harmful gas adsorbing action, a deodorizing action and a moisturizing action, and has an effect of emitting far infrared rays. In particular, it can deodorize bad odors in the breath and can be used for a long time.

本発明の他の利用の靴中敷の実施例について説明する。図５に示す実施例は、靴中敷Ｃの例であり、実施例１の防臭抗菌シートＡと同じ構造で、縦寸法を長くした防臭抗菌シートを靴型に切り出し、竹炭層４が足指側になるようにし、更に切り出した周縁に緑布２０を取り付けた例である。
この例は、絹の表シート１が吸汗し、又抗菌性金属粉３が抗菌し、足の裏・指の間の雑菌の増殖を抑える。又竹炭層４が強く吸汗し、消臭と抗菌と保温を行う。 Another embodiment of the shoe insole of the present invention will be described. The embodiment shown in FIG. 5 is an example of a shoe insole C. The deodorized antibacterial sheet A having the same structure as that of the first embodiment and having a longer vertical dimension is cut into a shoe shape, and the bamboo charcoal layer 4 has a toe. This is an example in which a green cloth 20 is attached to the cut out periphery.
In this example, the silk front sheet 1 absorbs sweat, and the antibacterial metal powder 3 is antibacterial, and suppresses the growth of bacteria between the soles and fingers. Moreover, the bamboo charcoal layer 4 absorbs sweat strongly and performs deodorization, antibacterial action and heat insulation.

本発明の他の利用のパンツの実施例について説明する。図６にその例の一部切欠斜視図を示す実施例１の防臭抗菌シートＡと同じ構造の広いシートをパンツ生地とし、又竹炭層４は股間・下腹部に当る個所に広く形成させた例である。
このパンツＤでは、股間・下腹部の竹炭層４が吸汗・吸尿し、又消臭するとともに、絹素材の表シート１も吸汗し、又傷の治癒効果もあり、肌との接触がよく、なじみもよい。又抗菌性も高いものとなる。 Another embodiment of the pants according to the present invention will be described. An example in which a wide sheet having the same structure as that of the deodorizing and antibacterial sheet A of Example 1 is shown in FIG. 6 as a partially cut perspective view, and the bamboo charcoal layer 4 is formed widely at a position corresponding to the crotch / lower abdomen. It is.
In this pant D, the bamboo charcoal layer 4 in the crotch and lower abdomen absorbs and urinates and deodorizes, and the front sheet 1 made of silk also absorbs sweat, has a healing effect on the wound, and has good contact with the skin. Also familiar. In addition, the antibacterial property is high.

本発明の他の利用としては、竹炭層４を表シート１に均一に薄く形成することで、壁布・シーツとしても使える。この壁布は、絹素材の表シート１が表面にあるため、人体と接触しても柔らかでなめらかな肌触りであり、しかも吸汗作用・抗菌作用・消臭作用がある製品とすることができる。   As another use of the present invention, the bamboo charcoal layer 4 is formed uniformly and thinly on the front sheet 1 so that it can be used as a wall cloth / sheet. This wall cloth has a surface sheet 1 made of silk on the surface, so that it can be made into a product that has a soft and smooth touch even when it comes into contact with the human body, and has a sweat-absorbing action, an antibacterial action, and a deodorizing action.

本発明の防臭抗菌シートは、パンツ以外の肌着・シャツの衣服生地として使え、カーテン生地，布団表生地，包帯，帽子裏生地，ハンカチ等にも利用できる。   The deodorant antibacterial sheet of the present invention can be used as an underwear / shirt clothes fabric other than pants, and can also be used as a curtain fabric, a futon surface fabric, a bandage, a hat back fabric, a handkerchief and the like.

実施例１の防臭抗菌シートを示す分解斜視図である。It is a disassembled perspective view which shows the deodorizing antibacterial sheet of Example 1. FIG. 実施例１の防臭抗菌シートを示す一部切欠斜視図である。1 is a partially cutaway perspective view showing a deodorizing antibacterial sheet of Example 1. FIG. 実施例１の防臭抗菌シートの拡大縦断面図である。2 is an enlarged longitudinal sectional view of a deodorizing antibacterial sheet of Example 1. FIG. 実施例１の防臭抗菌マスクを示す一部切欠斜視図である。It is a partially cutaway perspective view showing the deodorant antibacterial mask of Example 1. 本発明の靴中敷の利用を示す一部切欠斜視図である。It is a partially notched perspective view which shows utilization of the shoe insole of this invention. 本発明のパンツの利用を示す一部切欠斜視図である。It is a partially notched perspective view which shows utilization of the underpants of this invention.

符号の説明Explanation of symbols

Ａ 防臭抗菌シート
Ｂ マスク
Ｃ 靴中敷
Ｄ パンツ
１ 表シート
２ 中間シート
２−ａ 混合繊維
３ 抗菌性金属粉
４ 竹炭層
５ 穴
１０ マスク本体
１１ 折り返し部
１２ マスクゴム紐
２０ 緑布 A Deodorant antibacterial sheet B Mask C Shoe insole D Pants 1 Table sheet 2 Intermediate sheet 2-a Mixed fiber 3 Antibacterial metal powder 4 Bamboo charcoal layer 5 Hole 10 Mask body 11 Folded part 12 Mask rubber string 20 Green cloth

Claims (7)

微紛状の金属粒の表面にＣｕ−Ｎｉ合金メッキを施した抗菌性金属粉を混入させた織布又は不織布の布シートの一部又は全部のシート表面又はシート内に、竹炭粉を薄く付着させた竹炭層を形成した防臭抗菌シート。   Bamboo charcoal powder is thinly attached to a part or all of the surface of a woven fabric or non-woven fabric sheet in which antibacterial metal powder plated with Cu-Ni alloy is mixed on the surface of fine metal particles. Deodorized antibacterial sheet with a bamboo charcoal layer formed. 布シートが短い絹繊維を絡合させた後加圧してシート状にし、更にこれに細孔を多数穿孔した通気性の高い絹シートである、請求項１記載の防臭抗菌シート。   The anti-odor and antibacterial sheet according to claim 1, wherein the fabric sheet is a highly breathable silk sheet in which short silk fibers are entangled and then pressed to form a sheet, and a plurality of pores are perforated in the sheet. 請求項１又は２記載の防臭抗菌シートを用いてマスク面を形成し、竹炭粉がマスク面の下方に形成された防臭抗菌マスク。   A deodorant antibacterial mask in which a mask surface is formed using the deodorant antibacterial sheet according to claim 1 and bamboo charcoal powder is formed below the mask surface. 請求項１又は２記載の防臭抗菌シートを靴中敷の上層に設けたことを特徴とする、防臭抗菌靴中敷。   An anti-odor antibacterial insole, comprising the anti-odor antibacterial sheet according to claim 1 or 2 in an upper layer of a shoe insole. 請求項１又は２記載の防臭抗菌シートを壁布地とした、防臭抗菌壁布。   A deodorized and antibacterial wall cloth using the deodorized antibacterial sheet according to claim 1 or 2 as a wall cloth. 請求項１又は２記載の防臭抗菌シートを生地として作製された、防臭抗菌肌着。   A deodorant and antibacterial undergarment produced using the deodorant and antibacterial sheet according to claim 1 as a fabric. 請求項１又は２記載の防臭抗菌シートをシャツ生地として作製された、防臭抗菌シャツ。   An anti-odor antibacterial shirt produced by using the anti-odor antibacterial sheet according to claim 1 as a shirt fabric.
JP2007059264A 2007-03-08 2007-03-08 Deodorizing antibacterial sheet and use thereof Pending JP2008223155A (en)