JP2008189712A - 耐久性に優れた塗料組成物とその塗装物品 - Google Patents
耐久性に優れた塗料組成物とその塗装物品 Download PDFInfo
- Publication number
- JP2008189712A JP2008189712A JP2007022817A JP2007022817A JP2008189712A JP 2008189712 A JP2008189712 A JP 2008189712A JP 2007022817 A JP2007022817 A JP 2007022817A JP 2007022817 A JP2007022817 A JP 2007022817A JP 2008189712 A JP2008189712 A JP 2008189712A
- Authority
- JP
- Japan
- Prior art keywords
- parts
- coating composition
- weight
- epoxy group
- vinyl monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(1)脂環式エポキシ基を含有するビニル単量体(A)、側鎖にポリエステルを含有するビニル単量体(B)とを共重合して得られるエポキシ基含有ポリエステル変性ビニル重合体(D)100重量部に対して、(2)有機金属化合物0.01〜10重量部、(3)シラノール基を有するケイ素化合物0.1〜10重量部、を含むことを特徴とする。
【選択図】なし
Description
(1) 2コートにする方法
(2) 膜を厚くする方法
の2つの方法が採用されている。
(1)脂環式エポキシ基を含有するビニル単量体(A)、側鎖にポリエステルを含有するビニル単量体(B)とを共重合して得られるエポキシ基含有ポリエステル変性ビニル重合体(D)100重量部に対して、
(2)有機金属化合物0.01〜10重量部、
(3)シラノール基を有するケイ素化合物0.1〜10重量部、
を含むことを特徴とする。
前記「脂環式エポキシ基含有ビニル単量体」(A)は、脂環式エポキシ基が、後述の(2)シラノール基と有機金属化合物の作用により開環し、架橋反応を生じうる架橋点を提供し、架橋反応可能な単量体として添加されるものであり、この種の塗料組成物として広く使用されている。
「(メタ)アクリル酸エステル」、「カルボキシル基またはアルコキシカルボニル基含有ビニル単量体」、「酸無水物基含有ビニル単量体」、「非脂環式エポキシ基含有ビニル単量体」、「芳香族ビニル単量体」、「水酸基含有ビニル単量体」等を挙げることができる。
本発明において使用される有機金属化合物は、後述のシラノール基含有ケイ素化合物とともに、前記ビニル単量体(A)を架橋可能なものであれば、いかなるものでもよい。このような「有機金属化合物」としては、β−ジケトン、β−ケトエスチル、サリチルアルデヒド誘導体等を配位子とするG、a、Sn、Zr、Zn、Cu、Fe、Co、Ni、Mn、Cr、V、Pt、Mo、Pd等の錯体が挙げられる。
前述のようにシラノール基を含むケイ素化合物は、前記有機金属化合物とともにエポキシ基に作用して、開環させ、前記ビニル単量体(A)を架橋可能なものであればいかなるものでもよい。
本発明においては、任意に加水分解性シリル基を有する化合物を添加することができる。このような加水分解性シリル基を有する化合物はワックスリムーバー性を改良するために添加される。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部(重量部;以下、「部」は「重量部」を示す)、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、脂環式エポキシ基含有ビニル単量体として、3,4−エポキシシクロヘキシルメチルアクリレート(サイクロマーA200:商標名:ダイセル化学株式会社製)を45部、側鎖にポリエステルを含有するビニル単量体として2−ヒドロキシエチルアクリレートのε−カプロラクトン10モル付加物(プラクセルFA−10:商標名:ダイセル化学株式会社製)を55部、AIBN(重合開始剤;アゾビスイソブチロニトリル)7部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成してから、さらにAIBN1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が7000であるエポキシ基含有ポリエステル変性ビニル重合体溶液#Aを得た。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部(重量部;以下、「部」は「重量部」を示す)、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、脂環式エポキシ基含有ビニル単量体として、3,4−エポキシシクロヘキシルメチルアクリレート(サイクロマーA200:商標名:ダイセル化学株式会社製)を40部、側鎖にポリエステルを含有するビニル単量体として2−ヒドロキシエチルメタクリレートのε−カプロラクトン5モル付加物(プラクセルFM−5:商標名:ダイセル化学株式会社製)を40部、ブチルメタクリレート10部、ブチルアクリレート10部、AIBN(重合開始剤;アゾビスイソブチロニトリル)7部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成してから、さらにAIBN1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が7000であるエポキシ基含有ポリエステル変性ビニル重合体溶液#Bを得た。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、脂環式エポキシ基含有ビニル単量体としてサイクロマーA200を40部、側鎖にポリエステルを含有するビニル単量体としてプラクセルFA−10(ダイセル化学株式会社製:2−ヒドロキシエチルアクリレートのε−カプロラクトン10モル付加物)を40部、ブチルメタクリレート10部、ブチルアクリレート10部、AIBN7部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成してから、さらにAIBN1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が7000であるエポキシ基含有ポリエステル変性ビニル重合体溶液#Cを得た。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、エポキシ基含有ビニル単量体としてサイクロマーA200を30部、側鎖にポリエステルを含有するビニル単量体としてプラクセルFM−5(ダイセル化学株式会社製:2−ヒドロキシエチルメタクリレートのε−カプロラクトン5モル付加物)を30部、ブチルメタクリレー卜20部、ブチルアクリレート20部、AIBN7部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成し、さらにAIBNの1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が7000であるエポキシ基含有ポリエステル変性ビニル重合体溶液#Dを得た。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、脂環式エポキシ基含有ビニル単量体としてサイクロマーA200を40部、側鎖にポリエステルを含有するビニル単量体としてプラクセルFA−2(ダイセル化学株式会社製:2−ヒドロキシエチルアクリレートのε−カプロラクトン2モル付加物)40部、ブチルメタクリレート10部、ブチルアクリレート10部、AIBN7部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成してから、さらにAIBN1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が7000であるエポキシ基含有ポリエステル変性ビニル重合体溶液#Eを得た。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、脂環式エポキシ基含有ビニル単量体としてサイクロマーA200を40部、ブチルメタクリレート20部、ブチルアクリレート40部、AIBN7部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成してから、さらにAIBN1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が7000であるエポキシ基含有ビニル重合体溶液#Fを得た。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、脂環式エポキシ基含有ビニル単量体としてサイクロマーA200を40部、2−ヒドロキシエチルアクリレートを40部、ブチルアクリレート20部、AIBN7部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成してから、さらにAIBN1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が7000であるエポキシ基含有ビニル重合体溶液#Gを得た。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、脂環式エポキシ基含有ビニル単量体としてサイクロマーA200を40部、側鎖にポリエステルを含有するビニル単量体としてプラクセルFA−10を10部、ブチルメタクリレート30部、ブチルアクリレート20部、AIBN7部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成してから、さらにAIBN1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が7000であるエポキシ基含有ポリエステル変性ビニル重合体溶液#Hを得た。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、脂環式エポキシ基含有ビニル単量体としてサイクロマーA200を30部、側鎖にポリエステルを含有するビニル単量体としてプラクセルFM−5を30部、イソボルニルメタクリレート40部、AIBN7部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成してから、さらにAIBN1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が7000であるエポキシ基含有ポリエステル変性ビニル重合体溶液#Iを得た。
撹拌装置、温度計、還流冷却管、窒素導入管を備えた反応器に、トルエン40部、酢酸イソブチル50部を仕込み、窒素雰囲気中で100℃に昇温し、脂環式エポキシ基含有ビニル量体としてサイクロマーA200を40部、側鎖にポリエステルを含有するビニル単量体としてプラクセルFA−10を40部、ブチルメタクリレート10部、ブチルアクリレート10部、AIBN0.5部からなる混合物を2時間かけて滴下した。滴下終了後も同温度で2時間熟成してから、さらにAIBN1部、トルエン10部からなる混合物を滴下した。その後も、同温度に4時間保持して不揮発分が50%で、かつ数平均分子量が50000であるエポキシ基含有ポリエステル変性ビニル重合体溶液#Jを得た。
以下、実施例および比較例を挙げ、本発明を更に詳しく説明する。なお、実施例および比較例中の部は全て重量部を意味する。
(測定項目)
(1)耐擦傷性:スチールウール#0000を用い傷つき程度を試験した。
荷重は、150g/cm2、摩耗回数は11往復とした。なお、耐擦傷性の評価は、へーズ値(曇り度)で表し、5〜0の6段階で示した。すなわち
合格:密着性:1mm碁盤目セロテープ(登録商標)剥離で剥離無し
外観:異常なし
不合格:密着性:1mm碁盤目セロテープ(登録商標)剥離で剥離有り
外観:クラック、自然剥離などの異常有り
製造例5で得たビニル重合体溶液#E 81部にメチルイソブチルケトン5部、ノルマルブタノール10部、さらに紫外線吸収剤Sanduvor3206(クラリアント株式会社)2部、光安定剤Sanduvor3058(クラリアント株式会社)2部を添加した配合物に、アルミニウムトリスアセチルアセトネート1部、トリフェニルシラノール3部を添加して1液型塗料組成物#E−1を得た。塗料組成物#E−1の100部に実施例1のトリフェニルシラノールを含む硬化剤10部を添加した後、同様の条件の試験片を作製し、試験片について同様の評価を実施した。
製造例6で得たビニル重合体溶液#F 81部にメチルイソブチルケトン5部、ノルマルブタノール10部、さらに紫外線吸収剤Sanduvor3206(クラリアント株式会社)2部、光安定剤Sanduvor3058(クラリアント株式会社)2部を添加した配合物に、アルミニウムトリスアセチルアセトネート1部を添加して塗料組成物#F−1を得た。塗料組成物#F−1の100部に実施例1のトリフェニルシラノールを含む硬化剤10部を添加した後、同様の条件の試験片を作製し、試験片について同様の評価を実施した。
製造例7で得たビニル重合体溶液#G 81部にメチルイソブチルケトン5部、ノルマルブタノール10部、さらに紫外線吸収剤Sanduvor3206(クラリアント株式会社)2部、光安定剤Sanduvor3058(クラリアント株式会社)2部を添加した配合物に、アルミニウムトリスアセチルアセトネート1部を添加して塗料組成物#G−1を得た。塗料組成物#G−1の100部に実施例1のトリフェニルシラノールを含む硬化剤10部を添加した後、同様の条件の試験片を作製し、試験片について同様の評価を実施した。
製造例8で得たビニル重合体溶液#H 81部にメチルイソブチルケトン5部、ノルマルブタノール10部、さらに紫外線吸収剤Sanduvor3206(クラリアント株式会社)2部、光安定剤「Sanduvor3058(クラリアント株式会社)2部を添加した配合物に、アルミニウムトリスアセチルアセトネート1部を添加して塗料組成物#H−1を得た。塗料組成物#H−1の10O部に実施例1のトリフェニルシラノールを含む硬化剤10部を添加した後、同様の条件の試験片を作製し、試験片について同様の評価を実施した。
製造例9で得たビニル重合体溶液#I 81部にメチルイソブチルケトン5部、ノルマルブタノール10部、さらに紫外線吸収剤Sanduvor3206(クラリアント株式会社)2部、光安定剤Sanduvor3058(クラリアント株式会社)2部を添加した配合物にアルミニウムトリスアセチルアセトネート1部を添加して塗料組成物#I−1を得た。塗料組成物#I−1の100部に実施例1のトリフェニルシラノールを含む硬化剤10部を添加した後、同様の条件の試験片を作製し、試験片について同様の評価を実施した。
製造例10で得たビニル重合体溶液#J 81部にメチルイソブチルケトン5部、ノルマルブタノール10部、さらに紫外線吸収剤Sanduvor3206(クラリアント株式会社)2部、光安定剤Sanduvor3058(クラリアント株式会社)2部を添加した配合物に、アルミニウムトリスアセチルアセトネート1部を添加して塗料組成物#J−1を得た。塗料組成物#J−1の100部に実施例1のトリフェニルシラノールを含む硬化剤10部を添加した後、同様の条件の試験片を作製し、試験片について同様の評価を実施した。
製造例2で得たビニル重合体溶液#B 81部にメチルイソブチルケトン5部、ノルマルブタノール10部、さらに紫外線吸収剤Sanduvor3206(クラリアント株式会社)2部、光安定剤Sanduvor3058(クラリアント株式会社)2部を添加した配合物に、アルミニウムトリスアセチルアセトネート1部を添加して塗料組成物#B−3を得た。塗料組成物#B−3の100部にシラノール基含有硬化剤としてSH6018((シラノール基6%含有ポリシロキサン)東レダウコーニング)0.3部を添加した後、同様の条件の試験片を作製し、試験片について同様の評価を実施した。
Claims (11)
- (1)脂環式エポキシ基を含有するビニル単量体(A)、側鎖にポリエステルを含有するビニル単量体(B)とを共重合して得られるエポキシ基含有ポリエステル変性ビニル重合体(D)100重量部に対して、
(2)有機金属化合物0.01〜10重量部、
(3)シラノール基を有するケイ素化合物0.1〜10重量部、
を含むことを特徴とする塗料組成物。 - 前記エポキシ基含有ポリエステル変性ビニル重合体(D)は前記単量体(A)および(B)に重合可能なビニル単量体(C)を前記単量体(A)および(B)とともに共重合させたものであることを特徴とする請求項1記載の塗料組成物。
- 脂環式エポキシ基含有ポリエステル変性ビニル重合体(D)の100重量部に対し、側鎖にポリエステルを含有するビニル単量体(B)は、30〜80重量部である請求項1または2記載の塗料組成物。
- 脂環式エポキシ基含有ポリエステル変性ビニル重合体(D)の100重量部に対し、前記単量体(A)および(B)に重合可能なビニル単量体(C)は0〜50重量部である請求項2または3記載の塗料組成物。
- 前記ビニル単量体(B)のポリエステル側鎖の炭素数は、15〜60であることを特徴とする請求項1から4記載のいずれかの塗料組成物。
- 前記ビニル単量体(B)が、カプロラクトンと水酸基含有アクリル酸エステルとの開環付加反応により得られ、カプロラクトンの平均連鎖モル数が5モル以上からなる側鎖にポリエステルを含有するビニル単量体である請求項5記載の塗料組成物。
- 前記水酸基含有アクリル酸エステルはヒドロキシアルキル(メタ)アクリレートである請求項6記載の塗料組成物。
- 前記アルキルはエチル、ヒドロキシブチル、プロピルである請求項7記載の塗料組成物。
- 脂環式エポキシ基含有ポリエステル変性ビニル重合体(D)のガラス転移点が−60〜20℃、数平均分子量が1000〜40000である請求項1から8記載のいずれかの塗料組成物。
- 請求項1〜9に記載のいずれかの塗料組成物を直接塗布またはべースコートを介して塗布したプラスチックの塗装物品。
- 前記プラスチックはポリカーボネート樹脂、ABS樹脂、アクリル樹脂とこれらを含有する樹脂アロイである請求項10記載の塗装物品。