JP2008106385A - Thread, anti-counterfeit paper using the same, and anti-counterfeit printed matter using the thread - Google Patents

Thread, anti-counterfeit paper using the same, and anti-counterfeit printed matter using the thread Download PDF

Info

Publication number
JP2008106385A
JP2008106385A JP2006288840A JP2006288840A JP2008106385A JP 2008106385 A JP2008106385 A JP 2008106385A JP 2006288840 A JP2006288840 A JP 2006288840A JP 2006288840 A JP2006288840 A JP 2006288840A JP 2008106385 A JP2008106385 A JP 2008106385A
Authority
JP
Japan
Prior art keywords
thread
paper
layer
base film
counterfeit
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2006288840A
Other languages
Japanese (ja)
Inventor
Toru Murakami
徹 村上
Makoto Maehira
誠 前平
Kanako Seki
佳奈子 関
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toppan Inc
Original Assignee
Toppan Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Printing Co Ltd filed Critical Toppan Printing Co Ltd
Priority to JP2006288840A priority Critical patent/JP2008106385A/en
Publication of JP2008106385A publication Critical patent/JP2008106385A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide anti-counterfeit paper so designed that, when a thread with microletters formed on is watermarked into a sheet of paper, the microletters can be seen in the identical way when visually checked through the obverse face or reverse face of the paper even if the position where the thread is watermarked is biased toward the obverse face side or reverse face side. <P>SOLUTION: The thread is watermarked into a sheet of paper so as to be visually check through both the obverse and reverse faces of the paper for the purpose of preventing forging. The thread has a transparent base film (1), an anti-counterfeit layer (2) formed on the transparent base film (1), and light transmission-inhibitory layer (3) formed corresponding to at least the anti-counterfeit layer (2) on one or both sides of the transparent base film (1). <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、偽造防止が要望される分野に好適に用いられるスレッド(ストリップ、フィラメント、糸状物、安全帯片などとも称される)と、そのスレッドを抄き込んだスレッド入り紙でなる偽造防止用紙、およびそれらを利用した有価証券類、紙幣類などの偽造防止印刷物に関する。   The present invention is a forgery prevention comprising a thread (also referred to as a strip, a filament, a thread, a safety band, etc.) suitably used in a field where anti-counterfeiting is desired and a threaded paper in which the thread is formed. The present invention relates to paper, and forgery prevention printed matter such as securities and banknotes using them.

紙層内に、スレッドと呼ばれる糸状物を抄き込んだ「スレッド入り紙」は、偽造防止用紙の一形態としてよく知られている。このスレッドは、周知のように、ベースフィルムの表面に、ホログラム層、金属蒸着層、磁気層、マイクロ文字層、マイクロ画像層、サーモクロミック層、紫外蛍光発色層、干渉色発現層などの偽造防止層を設け、マイクロスリッター加工により製造される。前記スレッド入り紙は製造に極めて高度な技術を必要とするので偽造防止に大きな効果があり、周知のように各国の紙幣などに多用されている。   “Threaded paper” in which a thread-like material called a thread is formed in a paper layer is well known as a form of anti-counterfeit paper. As is well known, this thread prevents forgery such as hologram layer, metal deposition layer, magnetic layer, micro character layer, micro image layer, thermochromic layer, ultraviolet fluorescent color developing layer, interference color developing layer on the surface of the base film. A layer is provided and manufactured by micro slitting. The threaded paper requires a very high level of technology for manufacturing, and thus has a great effect on preventing forgery. As is well known, it is frequently used for banknotes in various countries.

前記スレッド入り紙は大きく2種類に分類される。その一つはスレッドが用紙内部に抄き込まれ、用紙表面に露出しないものである。もう一つはスレッドの一部が用紙表面に間欠的に露出した「窓空きスレッド入り紙」と呼ばれるものである。   The threaded paper is roughly classified into two types. One of them is that the thread is engraved inside the paper and is not exposed on the paper surface. The other is called “paper with open window thread” in which a part of the thread is intermittently exposed on the paper surface.

前者の用紙を製造する方法としては、長網抄紙機のスライス部分における紙料の流れの中にノズルを入れ、ノズルに水を流しながらスレッドを繰り出し、抄紙網に形成される紙匹中にスレッドを抄き込む方法(たとえば特許文献1)、長網抄紙機のフローボックスから流出する紙料へスレッドの挿入装置を設置し、空気流でスレッドと紙料を非接触状態としながらスレッドを抄き込む方法(たとえば特許文献2)、2層以上を有した円網抄紙機を使用し、2層以上の抄き合わせで、内壁に凹凸を設けた送管を使用してスレッドを紙層間に送り出し、紙層間にスレッドを抄き込む方法(たとえば特許文献3)などが提案されている。   In the former method, the nozzle is inserted into the flow of the stock in the slice portion of the long net paper machine, the thread is fed while water is passed through the nozzle, and the thread is formed in the web formed on the paper net. (For example, Patent Document 1), a thread insertion device is installed in the stock flowing out of the flow box of a long paper machine, and the thread is made while the thread and the stock are in a non-contact state by air flow. (For example, Patent Document 2) Using a circular paper machine having two or more layers, the thread is fed between the paper layers by using a feeding pipe having irregularities on the inner wall by making two or more layers. In addition, a method of making a thread between paper layers (for example, Patent Document 3) has been proposed.

後者の「窓空きスレッド入り紙」を製造する方法としては、凹凸状に加工した網を円網抄紙機の上網に使用し、スレッドを網表面の凹凸部に接触させながら挿入して窓空き部分にスレッドを抄き込む方法(たとえば特許文献4)や、円網抄紙機を使用して多層抄き合わせ紙を製造する際に、最外層に窓空き部を形成した紙層が位置するようにし、他の紙層は窓空き部を形成しない紙層が位置するようにして抄き合わせ、抄き合わせる際に窓空き部にスレッドが露出するようにスレッドを抄き込む製造方法(たとえば特許文献5)が代表的な製造方法である。   The latter method of making “paper with window empty thread” is to use a mesh processed into an uneven shape for the upper net of a circular paper machine, and insert the thread while making contact with the uneven portion of the net surface to open the window When manufacturing multi-layered laminated paper using a method of making a thread into a paper (for example, Patent Document 4) or using a circular paper machine, make sure that the paper layer in which the window space is formed is located in the outermost layer. The other paper layers are combined so that a paper layer that does not form a window vacant part is positioned, and a manufacturing method (for example, patent document) in which a thread is formed so that the thread is exposed in the window vacant part when the paper layers are combined. 5) is a typical production method.

以下、スレッドの代表例として、ベースフィルムの表面に偽造防止層としてマイクロ文字を形成したマイクロ文字入りスレッドについて説明する。その理由は、マイクロ文字入りスレッドを用いた偽造防止用紙において本発明の効果が最大限に発揮できるからである。   Hereinafter, as a representative example of the thread, a micro character-containing thread in which micro characters are formed as a forgery prevention layer on the surface of the base film will be described. The reason is that the effect of the present invention can be exhibited to the maximum extent in the forgery prevention paper using the thread with micro characters.

マイクロ文字入りスレッドは、着色インクを用いてプラスチックフィルムにマイクロ文字印刷を施してスレッド化する方法や、プラスチックフィルムにマイクロ文字を直接箔押しする方法や、真空蒸着装置においてマスクまたはテンプレートを使用して選択的に金属化する方法、金属化した後に腐食によりデメタライジング加工する方法が知られている(たとえば特許文献6)。これらのうち、着色インキによりマイクロ文字を形成したスレッドや、「デメタライジング加工」によりマイクロ文字を形成したスレッドは、紙幣用紙、パスポート用紙、商品券用紙などに多用されている。
特開昭51−130309号公報 特開平2−169790号公報 特公平5−40080号公報 米国特許第4462866号公報 特許第2845197号 特公平6−062030号公報
Threads with micro characters are selected by printing micro characters on plastic films using colored inks, threading micro characters directly on plastic films, or using a mask or template in a vacuum evaporation system There are known a method of metallization and a method of demetalizing by corrosion after metallization (for example, Patent Document 6). Of these, threads that form micro characters with colored ink and threads that form micro characters by “demetalizing” are frequently used for banknote paper, passport paper, gift certificate paper, and the like.
Japanese Patent Laid-Open No. 51-130309 JP-A-2-169790 Japanese Patent Publication No. 5-40080 U.S. Pat. No. 4,462,866 Japanese Patent No. 2845197 Japanese Patent Publication No. 6-062030

紙は厚みが薄い場合には光を多く透過するが、厚みが増すに従って光を透過しにくくなる。処方によっても異なるが、たとえば坪量90g/m2のパスポート冊子の本文用紙に使用される偽造防止用紙で、不透明度(JIS P8149に規定)は80〜90%の値を示すことが多い。用紙の不透明度がこの程度であれば、透明なベースフィルム上にマイクロ文字を形成したスレッドを用紙に抄き込んだ場合、用紙の表面および裏面からマイクロ文字を読むことができる。ただし、スレッドが紙の厚み方向に対してほぼ中央に抄き込まれていないと、用紙の表から見た場合と裏から見た場合とで、マイクロ文字の見え方が同一ではなく、かなり異なった見え方になる。しかし、たとえばパスポート冊子の本文用紙のように表裏両面を利用するような用途においては、各頁の表側と裏側でスレッドに形成されたマイクロ文字の見え方が同一でないと不都合を生じる。 When the thickness of the paper is small, it transmits a lot of light, but as the thickness increases, it becomes difficult to transmit the light. Although it depends on the prescription, for example, it is an anti-counterfeit paper used for the body paper of a passport booklet having a basis weight of 90 g / m 2 , and the opacity (specified in JIS P8149) often shows a value of 80 to 90%. If the opacity of the paper is about this level, the micro characters can be read from the front and back surfaces of the paper when a thread in which the micro characters are formed on the transparent base film is formed on the paper. However, if the thread is not roughly centered with respect to the thickness direction of the paper, the appearance of the micro characters is not the same when viewed from the front of the paper and when viewed from the back, and is quite different. It will be visible. However, in applications where both the front and back sides are used, such as the text sheet of a passport booklet, inconvenience arises if the appearance of the micro characters formed on the threads on the front side and the back side of each page is not the same.

また、偽造防止用紙はスレッドの抄き込みのほかに種々の偽造防止技術を採用することが多い。その代表的な技術に「透かし」がある。透かしは周知のように、円網抄紙機の円網シリンダーや、長網抄紙機のダンディーロールの上網に、(1)金属やプラスチック製の型を貼り付けたり、(2)上網の目を部分的に樹脂などで塗りつぶしたり、(3)上網に凹凸加工を施した網を使用して製造されている。   In addition, forgery prevention paper often employs various forgery prevention techniques in addition to threading. A representative technique is “watermark”. As is well known, (1) a metal or plastic mold is attached to the upper net of a circular net paper machine or a dandy roll of a long net paper machine. In particular, it is manufactured using a net that is painted with a resin or the like, and (3) a net having an uneven pattern on the upper net.

上記(1)、(2)の方法では、型の部分の網目が塞がれているので紙料の通過が抑制され、この部分には紙層が形成されないか形成されても薄くなるため、透かしが発現する。(3)の方法では、透かし模様を網の凹凸として打ち出すが、網の目は塞がれていない。透かし模様は網の凹凸の大きさ、網の斜面の角度などにより繊維の堆積に差が生じて透かしが発現する。   In the above methods (1) and (2), since the mesh of the mold part is blocked, the passage of the paper stock is suppressed, and even if a paper layer is not formed or formed in this part, it becomes thin. A watermark appears. In the method (3), the watermark pattern is formed as the unevenness of the mesh, but the mesh is not blocked. The watermark pattern appears as a result of differences in fiber accumulation depending on the size of the unevenness of the mesh and the angle of the slope of the mesh.

透かし入りの用紙は、単層抄きの用紙、多層抄き合せの用紙のいずれにおいても製造されている。多層抄き合せの透かし入り用紙においては、透かしの効果を最大限に発揮させるために必ずしも各層を同じ重量に抄き合わせるとは限らないし、奇数の紙層を抄き合わせる場合もある。たとえば100g/m2の透かし入りの用紙を3層抄き合わせで製造するとして、表面層および裏面層を30g/m2ずつとし、中間層を40g/m2として、中間層に透かしを入れるようなことが行われる。また、透かしを入れなくても、紫外蛍光発色繊維を3層抄き合わせ紙の中間層に抄き込み、この用紙にマイクロ文字入りのスレッドを抄き込む場合もある。このような場合、表面層の紙層と中間層の紙層との間、または裏面層の紙層と中間層の紙層との間のどちらかにスレッドを挿入することになる。 Watermarked paper is manufactured for both single-layer paper and multi-layer paper. In a multi-layered watermarked paper, in order to maximize the effect of the watermark, the layers are not necessarily combined with the same weight, and an odd number of paper layers may be combined. For example, if a paper sheet with a watermark of 100 g / m 2 is manufactured by combining three layers, the front layer and the back layer are each 30 g / m 2 , the intermediate layer is 40 g / m 2 , and the intermediate layer is watermarked. Things are done. Further, there is a case in which ultraviolet fluorescent coloring fiber is formed on the intermediate layer of the three-layered laminated paper without using a watermark, and a thread with micro characters is formed on the paper. In such a case, the thread is inserted either between the paper layer of the front surface layer and the paper layer of the intermediate layer, or between the paper layer of the back surface layer and the paper layer of the intermediate layer.

仮に前者の構成で用紙を製造したとすると、表面からは30g/m2の紙層を通して、裏面からは70g/m2の紙層を通してスレッドに形成されたマイクロ文字を読むことになる。30g/m2の紙層と70g/m2の紙層では、当然のことながら、光の透過率は30g/m2の方が大きいので、表面から見たときの方が裏面から見たときよりマイクロ文字が鮮明に見えることになる。このため、前述したように、パスポート冊子の本文用紙のように表裏両面を利用するような用途においては、表裏両面からマイクロ文字が同一の見え方で見えることが要求されるにもかかわらず、裏面からはマイクロ文字が見えにくいという不都合を生じる。 If the paper is manufactured with the former configuration, the micro characters formed on the thread are read from the front surface through a 30 g / m 2 paper layer and from the back surface through a 70 g / m 2 paper layer. Of course, in the 30 g / m 2 paper layer and the 70 g / m 2 paper layer, the light transmittance is larger in 30 g / m 2 , so when viewed from the front side, it is seen from the back side. The micro letters will appear clearer. For this reason, as described above, in applications where both front and back sides are used, such as the text of a passport booklet, the back side is required even though the micro characters are required to be seen from both sides. Causes the inconvenience that micro characters are difficult to see.

本発明の目的は、マイクロ文字を形成したスレッドを用紙に抄き込んだときに、スレッドの抄き込まれた位置が表面側または裏面側に偏っていても、用紙の表面または裏面から視認した際にマイクロ文字が同一の見え方で見えるようなスレッド、このようなスレッドを用いた偽造防止用紙および偽造防止印刷物を提供することにある。   An object of the present invention is to visually recognize a thread formed with micro characters from the front or back surface of the paper even if the threaded position is biased to the front or back side. It is an object of the present invention to provide a thread in which micro characters can be seen in the same way, and a forgery prevention paper and a forgery prevention print using such a thread.

請求項1の発明は、偽造防止のために用紙の表裏両面から視認できるように用紙に抄き込まれるスレッドであって、透明なベースフィルムと、前記透明なベースフィルム上に形成された偽造防止層と、前記透明なベースフィルムの一面または両面に、少なくとも前記偽造防止層に対応して形成された光透過抑制層とを有することを特徴とするスレッドである。   The invention according to claim 1 is a thread that is formed on a sheet so that the sheet can be seen from both the front and back sides of the sheet for preventing counterfeiting, and includes a transparent base film and a forgery prevention formed on the transparent base film. It is a thread characterized by having a layer and a light transmission suppressing layer formed corresponding to at least the forgery prevention layer on one side or both sides of the transparent base film.

請求項2の発明は、偽造防止のために用紙の表裏両面から視認できるように用紙に抄き込まれるスレッドであって、光の透過を抑制するベースフィルムと、前記光の透過を抑制するベースフィルム上に形成された偽造防止層とを有することを特徴とするスレッドである。   According to a second aspect of the present invention, there is provided a thread that is formed on a sheet so as to be visible from both the front and back sides of the sheet for preventing counterfeiting, and a base film that suppresses transmission of light, and a base that suppresses transmission of light. It is a thread | yarn characterized by having a forgery prevention layer formed on the film.

請求項3の発明は、前記光透過抑制層の光線透過率(JIS B9620−1)が20%〜60%であることを特徴とする請求項1に記載のスレッドである。   The invention according to claim 3 is the thread according to claim 1, wherein the light transmittance of the light transmission suppressing layer (JIS B9620-1) is 20% to 60%.

請求項4の発明は、前記光の透過を抑制するベースフィルムの光線透過率(JIS B9620−1)が20%〜60%であることを特徴とする請求項2に記載のスレッドである。   The invention according to claim 4 is the thread according to claim 2, wherein the light transmittance (JIS B9620-1) of the base film that suppresses the transmission of the light is 20% to 60%.

請求項5の発明は、前記偽造防止層が、所望のパターンを形成していることを特徴とする請求項1乃至4のいずれか1項に記載のスレッドである。   The invention according to claim 5 is the thread according to any one of claims 1 to 4, wherein the anti-counterfeit layer forms a desired pattern.

請求項6の発明は、前記パターンが、有彩色もしくは無彩色のインキで形成されたマイクロ文字、またはデメタライジングにより形成されたマイクロ文字であることを特徴とする請求項1乃至5項のいずれか1項に記載のスレッドである。   The invention of claim 6 is characterized in that the pattern is a micro character formed with chromatic or achromatic ink or a micro character formed by demetalizing. Or a thread according to item 1.

請求項7の発明は、前記光透過抑制層がデメタライジングのための保護層であることを特徴とする請求項6に記載のスレッドである。   The invention according to claim 7 is the thread according to claim 6, wherein the light transmission suppressing layer is a protective layer for demetalizing.

請求項8の発明は、前記マイクロ文字がベースフィルムの一面に形成されていることを特徴とする請求項6に記載のスレッドである。   The invention according to claim 8 is the thread according to claim 6, wherein the micro characters are formed on one surface of a base film.

請求項9の発明は、前記マイクロ文字がベースフィルムの両面に形成されていることを特徴とする請求項6に記載のスレッドである。   The invention according to claim 9 is the thread according to claim 6, wherein the micro characters are formed on both surfaces of the base film.

請求項10の発明は、請求項1乃至9のいずれかに記載のスレッドが抄き込まれた偽造防止用紙であって、それぞれ偽造防止用紙の表面および裏面から前記スレッドの偽造防止層までの厚み方向の距離が互いに異なることを特徴とする偽造防止用紙である。   A tenth aspect of the present invention is an anti-counterfeit paper in which the thread according to any one of the first to ninth aspects is engraved, and the thickness from the front and back surfaces of the anti-counterfeit paper to the anti-counterfeit layer of the thread, respectively. This is a forgery prevention paper characterized in that the distances in the directions are different from each other.

請求項11の発明は、請求項10に記載の偽造防止用紙に、偽造防止印刷物としての印刷部が設けられていることを特徴とする偽造防止印刷物である。   The invention according to claim 11 is the forgery-preventing printed matter, wherein the forgery-preventing paper according to claim 10 is provided with a printing section as a forgery-preventing printed matter.

本発明のスレッドによれば、透明なベースフィルム上に形成された偽造防止層に対応して光透過抑制層を形成するか、または光の透過を抑制するベースフィルム上に偽造防止層を形成したことにより、マイクロ文字を形成したスレッドを用紙の厚み方向において中央からずれた位置に抄き込んだとしても、用紙の表面または裏面から視認した際にマイクロ文字が実質的に同一の見え方で見えるようになる。ここで、マイクロ文字が実質的に同一の見え方で見えるとは、マイクロ文字の色相、濃度、彩度が同一かほぼ同一に見えることを意味する(以下、本明細書では、特に断りのない限り、「同一かほぼ同一」を「ほぼ同一」という)。   According to the thread of the present invention, the light transmission suppression layer is formed corresponding to the anti-counterfeit layer formed on the transparent base film, or the anti-counterfeit layer is formed on the base film that suppresses light transmission. As a result, even if the thread on which the micro characters are formed is drawn at a position shifted from the center in the thickness direction of the paper, the micro characters can be seen with substantially the same appearance when viewed from the front or back surface of the paper. It becomes like this. Here, the fact that the micro characters can be seen in substantially the same way means that the hue, density, and saturation of the micro characters appear to be the same or almost the same (hereinafter, there is no notice in the present specification). As long as “identical or nearly identical” is called “almost identical”).

また、本発明において、光透過抑制層をスレッドの表面の全面に設けたスレッドまたは光の透過を抑制するベースフィルムを使用したスレッドを抄き込んだ偽造防止用紙は、用紙を光に透かすとマイクロ文字が明瞭に見えるのは無論であるが、スレッド自体が光の透過を抑制するのでスレッド部分が暗く見え、スレッドが抄き込まれていることが明らかにわかる。これは、偽造を試みる者にとって偽造を困難にする。すなわち、偽造者は通常、印刷手段を用いて用紙の表面にマイクロ文字を印刷することで偽造を試みる。しかし、こうして偽造された用紙は光に透かしてもただマイクロ文字が見えるだけであり、本発明に係る偽造防止用紙のようにスレッドが抄き込まれているようには視認されないので、容易に偽造を見破ることができる。一方、光に透かしたときにあたかもスレッドが抄き込まれているかのように見えるように偽造する手段として、用紙の表面に二酸化チタンなどを主成分としたインキでスレッドに相当する印刷を施し、その上にマイクロ文字を印刷することが考えられる。しかし、このような用紙は、表面にスレッド状に印刷されたインキが周囲とは全く異なった状態(一般的には光沢に差がある状態)で視認されるので、本発明のようなスレッド抄き込み偽造防止用紙ではなく偽造であることを見破ることができる。   In the present invention, the anti-counterfeit paper in which a thread having a light transmission suppressing layer provided on the entire surface of the thread or a thread using a base film that suppresses the transmission of light is microscopic when the paper is transparent to light. Of course, it is obvious that the letters look clear, but the thread itself appears dark because the thread itself suppresses the transmission of light, and it can be clearly seen that the thread is engraved. This makes counterfeiting difficult for those attempting to counterfeit. That is, the forger usually tries to forge by printing micro characters on the surface of the paper using the printing means. However, since the paper forged in this way can only see micro characters even if it is watermarked in the light, it is not visible as if the thread is engraved like the anti-counterfeit paper according to the present invention. Can see through. On the other hand, as a means to forge the thread as if it was engraved when it was watermarked in the light, the surface of the paper was subjected to printing corresponding to the thread with ink mainly composed of titanium dioxide, It is conceivable to print micro characters thereon. However, such a sheet is visually recognized in a state where the ink printed in a thread form on the surface is completely different from the surroundings (generally, there is a difference in gloss). It can be seen that it is not counterfeit anti-counterfeit paper but counterfeit.

本発明の偽造防止用紙は、このような特長を有するので、特に表裏両面を使用する用途、たとえばパスポート冊子の本文用紙、紙幣、商品券、身分証明用冊子などに好適に使用できる。   Since the anti-counterfeit paper of the present invention has such a feature, it can be suitably used particularly for applications using both front and back surfaces, for example, text paper for passport booklets, banknotes, gift certificates, and identification booklets.

本発明に係るスレッドにおいて、ベースフィルム上に形成される偽造防止層は、何らかの偽造防止効果を有する層であれば、どのような形態のものでも使用できる。たとえば、着色染料や着色顔料と接着剤を主原料とした塗料をベースフィルム上に形成した形態、透明または半透明の着色フィルムそのものをベースフィルムとして使用する形態、磁気粉末と接着剤を主成分とした塗料をベースフィルム上に形成した形態、磁性金属の蒸着層やスパッタリング層をベースフィルム上に形成した形態、ホログラム層をベースフィルム上に形成した形態、マイクロ文字や画像の印刷層をベースフィルム上に形成した形態、デメタライジング加工によるマイクロ文字や画像の層をベースフィルム上に形成した形態、およびこれらの組み合わせなどが挙げられる。   In the thread according to the present invention, the anti-counterfeit layer formed on the base film can be used in any form as long as it has a certain anti-counterfeit effect. For example, a form in which a paint mainly composed of a coloring dye, a coloring pigment and an adhesive is formed on a base film, a form in which a transparent or translucent colored film itself is used as a base film, a magnetic powder and an adhesive as main components A form in which the coated paint is formed on the base film, a form in which a magnetic metal deposition layer or sputtering layer is formed on the base film, a form in which a hologram layer is formed on the base film, and a printed layer of micro characters and images on the base film , A form in which a layer of micro characters and images by demetalizing processing is formed on a base film, a combination thereof, and the like.

特に本発明の効果を最大限に発揮できるスレッドの形態は、本出願人がPCT/JP2006/313855において提案したものであることが好ましい。具体的には、基材の片側の面に所望のパターン状に形成された1以上の金属薄膜層、および該金属薄膜層のそれぞれの上にそれぞれの金属薄膜層と同じパターン状に形成され且つ着色された着色樹脂層を備え、該金属薄膜層が有る領域と、該金属薄膜層が無い領域との光透過性の違いによって、光に翳したときに前者と後者との間でコントラストが生じること、且つ、該基材の該金属薄膜層および着色樹脂層が備わった側から観察すると、該パターン状の着色樹脂層を視認できることを特徴とするスレッドが好ましい。さらに、前記基材の反対側の面に、所望のパターン状に形成された1以上の金属薄膜層、及び、該金属薄膜層のそれぞれの上にそれぞれの金属薄膜層と同じパターン状に形成され且つ着色された着色樹脂層を備えたスレッドも好ましい。   In particular, the thread form capable of maximizing the effects of the present invention is preferably the one proposed by the present applicant in PCT / JP2006 / 313855. Specifically, one or more metal thin film layers formed in a desired pattern on one surface of the substrate, and each metal thin film layer is formed in the same pattern as each metal thin film layer, and A contrast between the former and the latter when exposed to light due to a difference in light transmittance between a region having the metal thin film layer and a region having no metal thin film layer, provided with a colored resin layer In addition, a thread characterized by being able to visually recognize the patterned colored resin layer when observed from the side of the substrate on which the metal thin film layer and the colored resin layer are provided is preferable. Furthermore, one or more metal thin film layers formed in a desired pattern on the opposite surface of the substrate, and the same pattern as each metal thin film layer is formed on each of the metal thin film layers. A thread provided with a colored colored resin layer is also preferable.

以下、図面を参照しながら本発明を詳細に説明するが、偽造防止層としてマイクロ文字を形成したスレッドを代表例として説明する。   Hereinafter, the present invention will be described in detail with reference to the drawings. A thread in which micro characters are formed as a forgery prevention layer will be described as a representative example.

図1はスレッドの斜視図である。図1に示すように、短冊状のベースフィルム1上に偽造防止層としてたとえばマイクロ文字2が形成されている。   FIG. 1 is a perspective view of a thread. As shown in FIG. 1, for example, a micro character 2 is formed on a strip-shaped base film 1 as a forgery prevention layer.

図2は従来のスレッドの断面図である。図2に示すように、このスレッド20は透明なベースフィルム1上に偽造防止層としてマイクロ文字2を形成したものである。図2のように、ベースフィルム1が透明である場合、スレッド20の表面から見た場合でも裏面から見た場合でも、マイクロ文字2の見え方は実質的に同じになる。   FIG. 2 is a cross-sectional view of a conventional thread. As shown in FIG. 2, the thread 20 is formed by forming a micro character 2 on a transparent base film 1 as a forgery prevention layer. As shown in FIG. 2, when the base film 1 is transparent, the appearance of the micro characters 2 is substantially the same whether viewed from the front surface of the thread 20 or the back surface.

図3は図2のスレッド20を3層抄き合わせ紙に抄き込んだ偽造防止用紙の断面図であり、図4は図2のスレッド20を2層抄き合わせ紙に抄き込んだ偽造防止用紙の断面図である。   3 is a cross-sectional view of the anti-counterfeit paper in which the thread 20 of FIG. 2 is formed on a three-layered laminated paper, and FIG. 4 is a forged form in which the thread 20 of FIG. 2 is formed on a two-layered laminated paper. It is sectional drawing of prevention paper.

図3において、3層抄き合わせ紙の紙層11、12、13の抄き合わせ比率は同一で1:1:1であるものとする。この場合、用紙の表面から見たときと裏面から見たときで、マイクロ文字の見え方が異なる。すなわち、表面から見たときには1層の紙層11を通してスレッド20上のマイクロ文字2を見ることになるのでマイクロ文字2の見え方が鮮明であるが、裏面から見たときには2層の紙層13、12を通してスレッド20上のマイクロ文字2を見ることになるので、マイクロ文字2の見え方が不鮮明になる。   In FIG. 3, it is assumed that the combining ratio of the paper layers 11, 12, and 13 of the three-layered laminated paper is the same and 1: 1: 1. In this case, the appearance of the micro characters is different when viewed from the front side and the back side of the paper. That is, the micro character 2 on the thread 20 is seen through the one paper layer 11 when viewed from the front surface, so that the micro character 2 is clearly visible, but when viewed from the back surface, the two paper layers 13 are formed. , 12, the micro character 2 on the thread 20 is seen, so that the appearance of the micro character 2 becomes unclear.

図4において、2層抄き合わせ紙の紙層14、15の抄き合わせ比率は同一で1:1であるものとする。この場合、用紙の表面から見たときと裏面から見たときで、それぞれほぼ同一厚さの紙層14または紙層15を通してスレッド20上のマイクロ文字2を見るので、マイクロ文字2の見え方はほぼ同一になる。   In FIG. 4, it is assumed that the combining ratio of the paper layers 14 and 15 of the two-layered laminated paper is the same and 1: 1. In this case, since the micro character 2 on the thread 20 is viewed through the paper layer 14 or the paper layer 15 having substantially the same thickness when viewed from the front surface and the back surface of the paper, the appearance of the micro character 2 is as follows. Almost identical.

本発明に係るスレッドは、図3に示したようにそれぞれ偽造防止用紙の表面および裏面からスレッドの偽造防止層までの厚み方向の距離が互いに異なっている場合に、用紙の表面から見ても裏面から見てもマイクロ文字の見え方がほぼ同一の見え方になるようにするものである。   As shown in FIG. 3, the thread according to the present invention has a back surface even when viewed from the front surface of the paper when the thickness direction distance from the front surface and the back surface of the anti-counterfeit paper to the anti-counterfeit layer of the thread is different from each other. From the perspective, the appearance of micro characters will be almost the same.

図5は本発明の一実施形態に係るスレッド10の断面図である。図5に示すように、このスレッド10は、透明なベースフィルム1上に偽造防止層としてマイクロ文字2を形成し、ベースフィルム1のマイクロ文字2が形成されている面の全面に光透過抑制層3を形成したものである。   FIG. 5 is a cross-sectional view of the thread 10 according to an embodiment of the present invention. As shown in FIG. 5, the thread 10 has a micro character 2 formed as a forgery prevention layer on a transparent base film 1, and a light transmission suppressing layer on the entire surface of the base film 1 on which the micro character 2 is formed. 3 is formed.

図6は図5のスレッド10を3層抄き合わせ紙に抄き込んだ偽造防止用紙の断面図である。図6に示すように、スレッド10は3層の紙層11、12、13のうち、紙層11と紙層12との間に抄き込んでいる。この場合、表面からは1層の紙層11を通して、裏面からは2層の紙層13、12を通して、それぞれスレッド10上のマイクロ文字2を見ることになるが、表面側ではマイクロ文字2上に形成された光透過抑制層3が光の透過を抑制するので、スレッド10上のマイクロ文字2の見え方は用紙の表面および裏面のいずれからでもほぼ同一になる。   FIG. 6 is a cross-sectional view of the anti-counterfeit paper in which the thread 10 of FIG. 5 is formed on a three-layer laminated paper. As shown in FIG. 6, the thread 10 is engraved between the paper layers 11 and 12 among the three paper layers 11, 12, and 13. In this case, the micro character 2 on the thread 10 is seen through the one paper layer 11 from the front surface and the two paper layers 13 and 12 from the back surface, but on the micro character 2 on the front surface side. Since the formed light transmission suppressing layer 3 suppresses the transmission of light, the appearance of the micro characters 2 on the thread 10 is almost the same from either the front surface or the back surface of the paper.

本発明者らが種々検討した結果、表面からでも裏面からでもマイクロ文字がほぼ同一に見えるためには、表面および裏面のそれぞれで観察される文字部の光線反射率の差が5%以内であることが好ましく、2%以内であることがより好ましいことが判明した。   As a result of various studies by the present inventors, in order for the micro characters to look almost the same from the front surface and the back surface, the difference in the light reflectance of the character portion observed on the front surface and the back surface is within 5%. It was found that it was preferably 2% or less.

光透過抑制層3の光線透過率は、抄き合わせる紙層(11、12、13など)の厚みや不透明度などの特性によって適宜変化させるが、通常はJIS B9620−1に規定される方法で測定した光線透過率が20%〜60%であることが好ましい。   The light transmittance of the light transmission suppressing layer 3 is appropriately changed according to the characteristics such as the thickness and opacity of the paper layers (11, 12, 13, etc.) to be combined, but is usually a method defined in JIS B9620-1. The measured light transmittance is preferably 20% to 60%.

本発明のスレッドは紙に抄き込まれた際に所定の効果を発揮するが、偽造防止用紙として通常想定される坪量50g/m2〜150g/m2の用紙に抄き込んだ際に、光線透過率が60%を超える場合には光の透過を抑制する層としての効果が得られず、逆に光線透過率が20%未満の場合には光を抑制しすぎて目的とする効果が得られなくなる。 Threads of the present invention is to exert a predetermined effect when plowed into paper, when elaborate paper making basis weight 50g / m 2 ~150g / m 2 of the paper that is normally contemplated as anti-falsification paper When the light transmittance exceeds 60%, the effect as a layer for suppressing light transmission cannot be obtained. On the contrary, when the light transmittance is less than 20%, the light is excessively suppressed and the intended effect is obtained. Cannot be obtained.

光透過抑制層3は、二酸化チタン、二酸化ケイ素、ケイ酸カルシウム、カオリン、クレー、硫酸バリウム、酸化亜鉛、酸化マグネシウム、タルク、炭酸カルシウムや、ポリスチレン、ポリメチルメタアクリレート、ポリアクリロニトリルなどのプラスチックピグメントなどの白色顔料の1種類以上と、アクリル樹脂、塩化ビニル樹脂、酢酸ビニル樹脂、ポリエステル樹脂、ニトロセルロースなどの合成樹脂の1種類以上と、必要に応じて分散剤、流動性向上剤などの添加剤とを水若しくは有機溶剤に分散させた塗工液を塗工または印刷することによって得られる。顔料の割合は、通常、1質量%〜20質量%程度であることが好ましい。この塗工液をロールコーター、グラビアコーター、ワイヤバーコーターなどの塗工機やグラビア印刷機などで塗工または印刷することで、通常、厚み2〜20μmの塗工膜を形成する。顔料の割合と塗工厚を適宜変化させることで、光線透過率が20%〜60%である光透過抑制層3を形成することができる。   The light transmission suppressing layer 3 is made of titanium dioxide, silicon dioxide, calcium silicate, kaolin, clay, barium sulfate, zinc oxide, magnesium oxide, talc, calcium carbonate, plastic pigment such as polystyrene, polymethyl methacrylate, polyacrylonitrile, etc. One or more types of white pigments, one or more types of synthetic resins such as acrylic resins, vinyl chloride resins, vinyl acetate resins, polyester resins, nitrocellulose, and additives such as dispersants and flow improvers as necessary Can be obtained by coating or printing a coating liquid in which is dispersed in water or an organic solvent. The ratio of the pigment is preferably about 1% by mass to 20% by mass. A coating film having a thickness of 2 to 20 μm is usually formed by coating or printing this coating solution with a coating machine such as a roll coater, a gravure coater, or a wire bar coater, or a gravure printing machine. The light transmission suppressing layer 3 having a light transmittance of 20% to 60% can be formed by appropriately changing the ratio of the pigment and the coating thickness.

次に、本発明の他の実施形態に係るスレッドについて説明する。
図7のスレッドは、透明なベースフィルム1上に偽造防止層としてマイクロ文字2を形成し、ベースフィルム1のマイクロ文字2が形成されていない面の全面に光透過抑制層3を形成したものである。このスレッドを図6のように紙層11と紙層12との間に抄き込む場合、スレッドの表裏を図6の場合と逆にして(反転させて)抄き込む。
Next, a thread according to another embodiment of the present invention will be described.
The thread shown in FIG. 7 has a micro character 2 formed as a forgery prevention layer on a transparent base film 1 and a light transmission suppression layer 3 formed on the entire surface of the base film 1 where the micro character 2 is not formed. is there. When this thread is imprinted between the paper layer 11 and the paper layer 12 as shown in FIG. 6, the thread is imprinted with the front and back of the thread reversed (inverted) as in FIG.

図8のスレッドは、透明なベースフィルム1上に偽造防止層としてマイクロ文字2を形成し、マイクロ文字2上に光透過抑制層3を形成したものである。この構成のスレッドは、デメタライジング方式のマイクロ文字を形成する際に、レジスト材に前述した白色顔料を併用することで製造することができる。   The thread shown in FIG. 8 is obtained by forming a micro character 2 as a forgery prevention layer on a transparent base film 1 and forming a light transmission suppressing layer 3 on the micro character 2. The thread having this configuration can be manufactured by using the above-described white pigment in combination with a resist material when forming a demetalizing type micro character.

図9のスレッドは、透明なベースフィルム1上に偽造防止層としてマイクロ文字2を形成し、ベースフィルム1のマイクロ文字2が形成されている面の全面に光透過抑制層3aを形成するとともに、ベースフィルム1のマイクロ文字2が形成されていない面の全面に光透過抑制層3bを形成したものであるが、裏面側の光透過抑制層3bは表面側の光透過抑制層3aより薄く形成されている。   The thread of FIG. 9 forms the micro character 2 as a forgery prevention layer on the transparent base film 1, forms the light transmission suppressing layer 3a on the entire surface of the base film 1 where the micro character 2 is formed, and The light transmission suppression layer 3b is formed on the entire surface of the base film 1 where the micro characters 2 are not formed. The light transmission suppression layer 3b on the back side is formed thinner than the light transmission suppression layer 3a on the front side. ing.

図10のスレッドは、光の透過を抑制するベースフィルム5上にマイクロ文字2を形成したものである。   The thread in FIG. 10 is obtained by forming the micro character 2 on the base film 5 that suppresses light transmission.

図11のスレッドは、光の透過を抑制するベースフィルム5上にマイクロ文字2を形成し、マイクロ文字2上に光透過抑制層3を形成したものである。光透過抑制層3は光の透過を抑制するベースフィルム5より薄く形成されている。   In the thread shown in FIG. 11, the micro character 2 is formed on the base film 5 that suppresses light transmission, and the light transmission suppressing layer 3 is formed on the micro character 2. The light transmission suppressing layer 3 is formed thinner than the base film 5 that suppresses light transmission.

図10および図11のように光の透過を抑制するベースフィルム5を用いる場合、光透過抑制層3の場合と同様に、JIS B9620−1に規定される方法で測定したベースフィルム5の光線透過率が20%〜60%であることが好ましい。   When the base film 5 that suppresses the transmission of light as shown in FIGS. 10 and 11 is used, the light transmission of the base film 5 measured by the method defined in JIS B9620-1 as in the case of the light transmission suppression layer 3. The rate is preferably 20% to 60%.

マイクロ文字の形成手段としては、印刷とデメタライジング加工が代表例として知られている。   Printing and demetalizing processes are known as representative examples of micro character forming means.

印刷法によってマイクロ文字を形成する場合に使用するインキは、バインダー樹脂、着色顔料、白色顔料の他に、硬化剤、流動性改良剤、ブロッキング防止剤、静電防止剤、可塑剤、界面活性剤などの各種の助剤を必要に応じて配合することによって調製する。着色顔料としては、周知の有機または無機着色顔料を用いる。有機顔料としてはフタロシアニン系、アゾ系、アンスラキノン系など、無機顔料としてはカーボンブラック系、酸化チタン系、酸化鉄系、水酸化鉄系、酸化クロム系、アルミニウムなどの金属粉末など、白色顔料としては前記顔料を使用することができる。   Ink used for forming micro characters by printing method is not only binder resin, color pigment, white pigment, but also curing agent, fluidity improver, antiblocking agent, antistatic agent, plasticizer, surfactant It prepares by mix | blending various adjuvants, such as these as needed. As the color pigment, a known organic or inorganic color pigment is used. Organic pigments such as phthalocyanine, azo, and anthraquinone, inorganic pigments such as carbon black, titanium oxide, iron oxide, iron hydroxide, chromium oxide, aluminum, and other white powders The above pigments can be used.

デメタライジング加工によるマイクロ文字を形成する場合、公知の方法を用いることができる(特表2005−13585号公報など参照)。たとえば、金属アルミニウムを真空蒸着したベースフィルムに耐アルカリ性や耐酸性を有する樹脂インキでマイクロ文字を印刷して樹脂印刷層を形成した後、アルカリ性水溶液や酸性水溶液で印刷部以外のアルミニウムなどの蒸着層を洗い流す方法が用いられる。また、フォトレジストを蒸着層表面に塗布し、マイクロ文字パターンを露光し、レジストを硬化させた後にエッチング処理する方法も用いられる。これらの処理により印刷部または硬化レジスト部にアルミニウムなどの蒸着層を残し、印刷部以外または硬化レジスト部以外の個所ではベースフィルムを露出させる。デメタライジング加工の種々の変形例としては、本出願人がPCT/JP2006/313855において提案した方法が挙げられる。   In the case of forming micro characters by demetalizing processing, a known method can be used (see Japanese Patent Application Publication No. 2005-13585). For example, after printing micro characters with a resin ink having alkali resistance and acid resistance on a base film vacuum-deposited with metallic aluminum to form a resin print layer, a vapor deposition layer of aluminum other than the printing portion with an alkaline aqueous solution or an acidic aqueous solution The method of washing away is used. Moreover, the method of apply | coating a photoresist to the vapor deposition layer surface, exposing a micro character pattern, hardening the resist, and performing the etching process is also used. By these treatments, a vapor deposition layer such as aluminum is left in the printing portion or the cured resist portion, and the base film is exposed at places other than the printing portion or other than the cured resist portion. Examples of various modifications of the demetalizing process include a method proposed by the present applicant in PCT / JP2006 / 313855.

蒸着層に用いられる金属としては、アルミニウムが代表的であるが、この他にスズ、亜鉛、鉄、ニッケル、クロム、コバルトなどの金属の単体や合金を使用できる。マイクロ文字列の少なくとも一部を、たとえばニッケル−コバルトのような磁性体の蒸着膜にすることで、磁気情報に基づく偽造防止手段とすることができる。金属蒸着層の厚みは通常25〜100nmが適切である。   The metal used for the vapor deposition layer is typically aluminum, but in addition to this, a simple substance or an alloy of metal such as tin, zinc, iron, nickel, chromium and cobalt can be used. By forming at least a part of the micro character string as a deposited film of a magnetic material such as nickel-cobalt, forgery prevention means based on magnetic information can be obtained. The thickness of the metal vapor deposition layer is usually 25 to 100 nm.

図12のスレッドは、透明なベースフィルム1の両面にデメタライジング加工によるマイクロ文字2Bを形成し、ベースフィルム1の一方の面の全面に光透過抑制層3を形成したものである。   The thread in FIG. 12 is obtained by forming micro characters 2B by demetalizing processing on both surfaces of a transparent base film 1 and forming a light transmission suppressing layer 3 on the entire surface of one surface of the base film 1.

以下、本発明に係るスレッドの製造方法をより詳しく説明する。以下の記載において、g/m2、質量%、質量部はいずれも乾燥換算の値を示す。 Hereinafter, the thread manufacturing method according to the present invention will be described in more detail. In the following description, g / m 2 , mass%, and parts by mass all represent dry conversion values.

本発明において、ベースフィルムとしては、セロファン、ポリプロピレン、ポリエステル、ポリブチレンテレフタレート、ポリアセタール、ポリフェニレンエーテル、液晶ポリマー、ポリ塩化ビニル、ポリアミド、ポリカーボネート、ポリメタクリル酸エチル、ポリスチレンなどの半合成または合成樹脂フィルムを単層または積層体の形態で使用できる。ベースフィルムは、抄紙機の乾燥ゾーンで融解または軟化せず、90〜110℃で粘着性を帯びないことが好ましい。ベースフィルムの厚みは、薄すぎると各種の加工が困難となり、厚すぎるとスレッドを紙層間に抄き込んだ場合に部分的に厚みが増して種々の問題点を引き起こすので、通常5μm〜25μmとすることが好ましい。   In the present invention, the base film is a semi-synthetic or synthetic resin film such as cellophane, polypropylene, polyester, polybutylene terephthalate, polyacetal, polyphenylene ether, liquid crystal polymer, polyvinyl chloride, polyamide, polycarbonate, polyethyl methacrylate, or polystyrene. It can be used in the form of a single layer or a laminate. The base film is preferably not melted or softened in the drying zone of the paper machine and is not tacky at 90 to 110 ° C. If the thickness of the base film is too thin, various processing becomes difficult, and if it is too thick, when the thread is formed between the paper layers, the thickness partially increases and causes various problems, and therefore usually 5 μm to 25 μm. It is preferable to do.

ベースフィルムは、スレッドが紙層間に抄き込まれた偽造防止用紙や偽造防止印刷物の状態では、外観からその存在を視認できないことが好ましい。この条件を満たすフィルムとして無彩色のフィルムが挙げられる。ごく淡く着色した有彩色のフィルムでも、上記目的を達成できれば使用することができる。本発明においては、ベースフィルムの代表例として、物理的な強度が大きく、化学的にも安定なポリエステルフィルムが好適に使用できる。   In the state of the anti-counterfeit paper or the anti-counterfeit printed matter in which the thread is engraved between the paper layers, it is preferable that the base film cannot be visually recognized from the appearance. An achromatic film is an example of a film that satisfies this condition. Even a very lightly colored chromatic film can be used as long as the above object can be achieved. In the present invention, as a representative example of the base film, a polyester film having a large physical strength and being chemically stable can be suitably used.

ベースフィルムは、紫外線を吸収する性質をもつことが好ましい。その理由は、接着剤に紫外線の照射によって発光する染料や顔料を併用し、用紙製造中に紫外線をスレッドに照射してスレッドの表裏を判定する方法を用いることが困難になるためである。すなわち、ベースフィルムが紫外線を吸収しないと、マイクロ文字を形成していない部分で紫外線がフィルムを透過するのでスレッドの両面で発光が観察され、スレッドの表裏を判定することが困難になる。ベースフィルムにこのような性質を与えるには、基材製造時に紫外線吸収剤を練り込むか、または基材の表面に紫外線を吸収する塗工層を設けるかのいずれかの周知の手段を採用できる。紫外線吸収剤としては、ベンゾフェノン系、トリアジン系、トリアゾール系、サリチル酸系、ハイドロキノン系、アミン系、酸化亜鉛や酸化チタンなどの超微粒子金属酸化物系などの材料を使用することができる。紫外線吸収剤の添加量は基材に対して通常0.01〜5質量%である。   The base film preferably has a property of absorbing ultraviolet rays. The reason is that it is difficult to use a method in which a dye or a pigment that emits light when irradiated with ultraviolet rays is used in the adhesive, and a thread is irradiated with ultraviolet rays during paper manufacture to determine the front and back of the thread. That is, if the base film does not absorb ultraviolet rays, the ultraviolet rays are transmitted through the film in the portions where the micro characters are not formed, so that light emission is observed on both sides of the thread, making it difficult to determine the front and back of the thread. In order to give such properties to the base film, a well-known means of either kneading an ultraviolet absorber during the production of the substrate or providing a coating layer that absorbs ultraviolet rays on the surface of the substrate can be employed. . As the ultraviolet absorber, materials such as benzophenone-based, triazine-based, triazole-based, salicylic acid-based, hydroquinone-based, amine-based, ultrafine metal oxide-based materials such as zinc oxide and titanium oxide can be used. The addition amount of the ultraviolet absorber is usually 0.01 to 5% by mass with respect to the substrate.

次に、ベースフィルム上に、印刷法やデメタライジング法によってマイクロ文字を形成する。必要に応じてベースフィルムの一面または両面に接着剤を塗工する。接着剤としては、抄紙機のドライヤーで軟化または溶融して、用紙と強固に接着する性能を有するものを使用する。具体的には、ポリ酢酸ビニル樹脂系、ポリ塩化ビニル樹脂系、ポリエステル樹脂系、ポリアクリル酸エステル樹脂系、エチレン−酢酸ビニル共重合体樹脂系、ポリビニルアルコール樹脂系などの接着剤を水系または溶剤系の塗料とし、ロールコーターやグラビアコーターなどの塗工機を用いて基材の表面に塗工することにより形成できる。接着剤の塗工量は、通常0.1〜10g/m2である。接着剤には必要に応じて、ブロッキング防止剤、潤滑剤、着色剤、紫外蛍光発色剤などを添加してもよい。前述したように、スレッドの表裏を判定する場合には、ベースフィルムとして紫外線を吸収するベースフィルムを使用し、接着剤に紫外蛍光発色剤を添加して、一面だけにこの接着剤を塗工したスレッドを製造し、紫外線の照射による発光の有無に基づいてスレッドの表裏を判定する。 Next, micro characters are formed on the base film by a printing method or a demetalizing method. If necessary, apply an adhesive to one or both sides of the base film. As the adhesive, an adhesive that has the ability to soften or melt with a dryer of a paper machine and firmly adhere to the paper is used. Specifically, adhesives such as polyvinyl acetate resin, polyvinyl chloride resin, polyester resin, polyacrylate resin, ethylene-vinyl acetate copolymer resin, and polyvinyl alcohol resin are used as water or solvent. It can be formed by coating on the surface of the substrate using a coating machine such as a roll coater or a gravure coater. The coating amount of the adhesive is usually 0.1 to 10 g / m 2 . If necessary, an anti-blocking agent, a lubricant, a colorant, an ultraviolet fluorescent color former and the like may be added to the adhesive. As described above, when judging the front and back of the thread, a base film that absorbs ultraviolet rays is used as a base film, an ultraviolet fluorescent color former is added to the adhesive, and this adhesive is applied only on one side. A sled is manufactured, and the front and back of the sled are determined based on the presence or absence of light emission by ultraviolet irradiation.

ベースフィルムは、透明なベースフィルム1でも、光の透過を抑制するやや不透明なベースフィルム5でもよい。光の透過を抑制するベースフィルム5は、透明フィルムの表面をサンドブラスト加工したり、透明フィルムに白色顔料を練り込んだりすることによって作製することができる。   The base film may be a transparent base film 1 or a slightly opaque base film 5 that suppresses light transmission. The base film 5 that suppresses light transmission can be produced by sandblasting the surface of the transparent film or kneading a white pigment into the transparent film.

次いで、マイクロスリッター装置を使用して、常法に従い所定の巾でベースフィルムをスリットすることにより本発明のスレッドを製造することができる。スレッドの巾は、通常0.5mm〜10mmである。スレッド上のマイクロ文字は、1列以上の正文字や正模様のパターンが視認できるように形成する。   Subsequently, the thread | sled of this invention can be manufactured by slitting a base film with a predetermined width | variety according to a conventional method using a micro slitter apparatus. The width of the thread is usually 0.5 mm to 10 mm. The micro characters on the thread are formed so that one or more rows of regular characters and regular patterns can be visually recognized.

次に、本発明の偽造防止用紙の製造方法の一例を説明する。
まず、針葉樹晒クラフトパルプ(NBKP)、広葉樹晒クラフトパルプ(LBKP)、針葉樹晒サルファイトパルプ(NBSP)、サーモメカニカルパルプ(TMP)などの製紙用パルプを主体とし、ビーターやディスクリファイナーなどを使用して叩解処理し、これに白土、カオリン、炭酸カルシウム、二酸化チタン、水酸化アルミニウムなどの各種填料、紙力増強剤、サイズ剤、歩留まり向上剤、消泡剤、着色染料、着色顔料、蛍光増白剤、定着剤などを適宜併用し紙料を調製する。
Next, an example of the manufacturing method of the forgery prevention paper of this invention is demonstrated.
First, paper pulp such as softwood bleached kraft pulp (NBKP), hardwood bleached kraft pulp (LBKP), softwood bleached sulfite pulp (NBSP), thermomechanical pulp (TMP), etc., and beaters and disc refiners are used. Beating, and adding to this, various types of fillers such as clay, kaolin, calcium carbonate, titanium dioxide, aluminum hydroxide, paper strength enhancer, sizing agent, yield improver, antifoaming agent, coloring dye, coloring pigment, fluorescent whitening A paper stock is prepared by appropriately using an agent, a fixing agent and the like.

本発明の偽造防止用紙は、従来公知の方法を使用して製造できる。たとえば、長網抄紙機のスライス部分における紙料の流れの中にノズルを入れ、ノズルに水を流しながらスレッドを繰り出し、抄紙網に形成される紙匹中にスレッドを抄き込む方法(特許文献1)、長網抄紙機のフローボックスから流出する紙料へスレッドの挿入装置を設置し、空気流でスレッドと紙料を非接触状態としながらスレッドを抄き込む方法(特許文献2)、2層以上を有した円網抄紙機を使用し、2層以上の抄き合わせで、内壁に凹凸を設けた送管を使用してスレッドを紙層間に送り出し、紙層間にスレッドを抄き込む方法(特許文献3)などを採用できる。本発明の偽造防止用紙は、これら以外の方法を採用して製造してもよい。   The anti-counterfeit paper of the present invention can be manufactured using a conventionally known method. For example, by inserting a nozzle into the flow of the stock in the slice part of a long paper machine, feeding the thread while flowing water through the nozzle, and making the thread into the paper web formed on the paper web (Patent Literature) 1) A method in which a thread insertion device is installed in the stock flowing out from the flow box of the long paper machine, and the thread is made in a non-contact state by air flow (Patent Document 2), 2 Using a circular paper machine with two or more layers, and making two or more layers, using a feed pipe with irregularities on the inner wall, sending the threads between the paper layers, and making the threads between the paper layers (Patent document 3) etc. are employable. The anti-counterfeit paper of the present invention may be manufactured by adopting methods other than these.

また、抄紙中に紙面にポリアクリルアマイド樹脂、澱粉、ポリビニルアルコールなどを塗工してもよい。必要に応じて、マシンカレンダー処理やスーパーカレンダー処理を施し、表面平滑性を向上させることも適宜行われる。用紙の坪量は、通常50〜150g/m2である。 Moreover, you may apply polyacrylamide resin, starch, polyvinyl alcohol, etc. to the paper surface during papermaking. If necessary, a machine calendar process or a super calendar process is performed to improve the surface smoothness as appropriate. The basis weight of the paper is usually 50 to 150 g / m 2 .

以下に、実施例に基づいて本発明をより詳細に説明する。
[実施例1]
[印刷法によるマイクロ文字入りスレッドの製造例]
ベースフィルムとして厚み12μmの透明ポリエステルフィルム(東レ(株)製、ルミラー(商品名))の巻き取りを用意した。このベースフィルムの一面に黒インキを使用してマイクロ文字を印刷した。このマイクロ文字は、「SECURITY」の正文字と逆文字(フィルムを裏返して見た時に「SECURITY」の正文字に見える)との繰り返しパターンになっている。マイクロ文字の大きさは2.5ポイント(ポイント数はアメリカ式ポイント数を意味し、1ポイントは約0.35mm)、文字と文字の間隔は0.3mm、文字列と文字列の間隔は0.8mmとした。ベースフィルムのマイクロ文字が印刷されている面の全面に、二酸化チタン10質量部、ポリアクリル酸エステル系樹脂30質量部、シクロヘキサノン30質量部、芳香族炭化水素30質量部よりなる塗料を10μmの厚みで塗工し、光透過抑制層を形成した。ベースフィルムの透明な個所の透過率(光透過抑制層の透過率に相当する)を、JIS B−9620−1に準拠してマクベス濃度計TD−904で測定したところ、29%であった。
Below, based on an Example, this invention is demonstrated in detail.
[Example 1]
[Example of manufacturing thread with micro characters by printing method]
As a base film, a roll of a transparent polyester film having a thickness of 12 μm (manufactured by Toray Industries, Inc., Lumirror (trade name)) was prepared. Micro characters were printed on one side of the base film using black ink. This micro character has a repeating pattern of a normal character of “SECURITY” and a reverse character (appears as a normal character of “SECURITY” when the film is turned over). The size of a micro character is 2.5 points (the number of points means an American point number, 1 point is about 0.35 mm), the distance between characters is 0.3 mm, and the distance between character strings is 0 8 mm. On the entire surface of the base film on which the micro characters are printed, a 10 μm thick coating composed of 10 parts by mass of titanium dioxide, 30 parts by mass of a polyacrylate resin, 30 parts by mass of cyclohexanone, and 30 parts by mass of aromatic hydrocarbons. Was applied to form a light transmission suppressing layer. The transmittance of the transparent portion of the base film (corresponding to the transmittance of the light transmission suppressing layer) was measured by Macbeth densitometer TD-904 in accordance with JIS B-9620-1, and found to be 29%.

ベースフィルムの裏面に、ベンゾフェノン系紫外線吸収剤を自己架橋型のポリエステルアクリル酸エステル樹脂に混合した紫外線吸収層を2μmの厚みで形成した。さらにこの面に、2.5質量%のオキサゾール系蛍光発色剤を添加したエチレン−酢酸ビニル系の感熱接着剤を2μmの厚みで塗工して接着剤層を形成した。次いで、マイクロスリッターを使用して巾2.4mmのスレッドを製造した。   On the back surface of the base film, an ultraviolet absorbing layer in which a benzophenone ultraviolet absorber was mixed with a self-crosslinking polyester acrylate resin was formed to a thickness of 2 μm. Further, an ethylene-vinyl acetate heat-sensitive adhesive to which 2.5% by mass of an oxazole fluorescent coloring agent was added was applied in a thickness of 2 μm to form an adhesive layer. A 2.4 mm wide thread was then produced using a micro slitter.

[実施例2]
[デメタライジング加工による両面マイクロ文字入りスレッドの製造例]
図13に本実施例の両面マイクロ文字入りスレッドの平面図を示す。ベースフィルムとして厚み12μmの透明ポリエステルフィルム(東レ(株)製、ルミラー(商品名))の巻き取りを用意した。真空蒸着機を使用して常法に従い、このベースフィルムの両面に金属アルミニウムを50nm(ナノメートル)ずつ蒸着した。この両面に、グラビア印刷機を使用し、青色に着色した耐アルカリ性樹脂インキ(デメタライジング加工用アクリル系樹脂100質量部に青色染料オレオゾールブルー(住友化学工業社製)を20質量部配合したもの)で着色した樹脂印刷層(マイクロ文字印刷層)を形成した。このマイクロ文字は、「★ABCD」の正文字と逆文字との繰り返しパターンになっている。マイクロ文字の大きさは2.5ポイント、文字と文字の間隔は0.4mm、文字列と文字列の間隔は0.8mmとした。図13に示すように、文字列はスレッドの長さ方向に対して18度傾斜して印刷されている。常法に従い、水酸化アルミニウム水溶液を使用して、デメタライジング加工を施し、水洗、乾燥してロールに巻き取った。ベースフィルムの表面側に、二酸化チタン10質量部、ポリアクリル酸エステル系樹脂30質量部、シクロヘキサノン30質量部、芳香族炭化水素30質量部よりなる塗料を10μmの厚みで塗工し、光透過抑制層を形成した。ベースフィルムの透明な個所の透過率(光透過抑制層の透過率に相当する)を、JIS B−9620−1に準拠してマクベス濃度計TD−904で測定したところ、29%であった。
[Example 2]
[Example of manufacturing thread with double-sided micro characters by demetalizing]
FIG. 13 shows a plan view of a thread with double-sided micro characters according to this embodiment. As a base film, a roll of a transparent polyester film having a thickness of 12 μm (manufactured by Toray Industries, Inc., Lumirror (trade name)) was prepared. According to a conventional method using a vacuum vapor deposition machine, metal aluminum was deposited on both sides of the base film by 50 nm (nanometers). On both sides, a gravure printing machine was used, and an alkali-resistant resin ink colored in blue (100 parts by mass of acrylic resin for demetalizing processing was blended with 20 parts by mass of blue dye oleosol blue (manufactured by Sumitomo Chemical Co., Ltd.)). The resin printing layer (micro character printing layer) colored with the thing) was formed. This micro character has a repeating pattern of a normal character of “★ ABCD” and a reverse character. The size of the micro character was 2.5 points, the distance between the characters was 0.4 mm, and the distance between the character string and the character string was 0.8 mm. As shown in FIG. 13, the character string is printed with an inclination of 18 degrees with respect to the length direction of the thread. According to a conventional method, an aluminum hydroxide aqueous solution was used to perform a demetalizing process, followed by washing with water, drying and winding up on a roll. On the surface side of the base film, a coating composed of 10 parts by mass of titanium dioxide, 30 parts by mass of a polyacrylate resin, 30 parts by mass of cyclohexanone, and 30 parts by mass of aromatic hydrocarbon is applied to a thickness of 10 μm to suppress light transmission. A layer was formed. The transmittance of the transparent portion of the base film (corresponding to the transmittance of the light transmission suppressing layer) was measured by Macbeth densitometer TD-904 in accordance with JIS B-9620-1, and found to be 29%.

ベースフィルムの裏面側に、ベンゾフェノン系紫外線吸収剤を自己架橋型のポリエステルアクリル酸エステル樹脂に混合した紫外線吸収層を2μmの厚みで形成した。さらにこの面に、2.5質量%のオキサゾール系蛍光発色剤を添加したエチレン−酢酸ビニル系の感熱接着剤を2μmの厚みで塗工して接着剤層を形成した。次いで、マイクロスリッターを使用して巾2.4mmのスレッドを製造した。   On the back side of the base film, an ultraviolet absorbing layer in which a benzophenone ultraviolet absorber was mixed with a self-crosslinking polyester acrylate resin was formed with a thickness of 2 μm. Further, an ethylene-vinyl acetate heat-sensitive adhesive to which 2.5% by mass of an oxazole fluorescent coloring agent was added was applied in a thickness of 2 μm to form an adhesive layer. A 2.4 mm wide thread was then produced using a micro slitter.

[実施例3]
[偽造防止用紙の製造]
NBKP25質量部、LBKP75質量部をフリーネス350mlC.S.F.に叩解し、これに白土10質量部、二酸化チタン5質量部、紙力増強剤(荒川化学工業社製、ポリストロン(商品名))0.4質量部、サイズ剤(荒川化学工業社製、サイズパインE(商品名))1.0質量部、硫酸バンドを適量加え、紙料を調製した。
[Example 3]
[Manufacture of anti-counterfeit paper]
25 parts by mass of NBKP and 75 parts by mass of LBKP were mixed with 350 ml freeness. S. F. In this, 10 parts by mass of white clay, 5 parts by mass of titanium dioxide, 0.4 parts by mass of paper strength enhancer (manufactured by Arakawa Chemical Industries, Polystron (trade name)), sizing agent (manufactured by Arakawa Chemical Industries, Size Pine E (trade name)) 1.0 part by mass and an appropriate amount of a sulfuric acid band were added to prepare a paper stock.

3槽式円網抄紙機の各槽でそれぞれ坪量33.3g/m2の紙匹を抄造し、3層を抄き合わせる際に、紙層間に実施例1で製造したスレッドを抄き込んだ。この際、厚みの薄い(1層の紙層に相当)側にスレッドの光透過抑制層が位置するようにスレッドを抄き込んだ。スレッドを紙層間に抄き込んだ直後に紫外蛍光ランプを照射し、スレッドが紫外蛍光発色するか否かでスレッドの表裏を判定し、スレッドが反転していた場合は正常な面が抄き込まれるようにスレッドを挿入し直した。その後、常法に従い乾燥して偽造防止用紙を製造した。得られた偽造防止用紙を反射光でそれぞれ表面および裏面から観察すると、どちらの面からも黒色のマイクロ文字の見え方がほぼ同一であった。このとき、表面および裏面での文字部の光線反射率の差は2%以内であった。 In each tank of a three-tank type circular paper machine, a sheet of paper having a basis weight of 33.3 g / m 2 was made, and when the three layers were combined, the thread produced in Example 1 was incorporated between the paper layers. It is. At this time, the thread was formed so that the light transmission suppression layer of the thread was positioned on the side of the thin thickness (corresponding to one paper layer). Immediately after the thread is engraved between the paper layers, an ultraviolet fluorescent lamp is irradiated, and the front and back of the thread are judged by whether or not the thread develops ultraviolet fluorescence. If the thread is reversed, the normal surface is engraved. Reinserted the thread so that it is. Thereafter, it was dried according to a conventional method to produce a forgery-preventing paper. When the obtained anti-counterfeit paper was observed with reflected light from the front surface and the back surface, the appearance of the black micro characters was almost the same from both surfaces. At this time, the difference in the light reflectance of the character part between the front surface and the back surface was within 2%.

[実施例4]
〔偽造防止用紙の製造〕
実施例2で得られたスレッドに用いた以外は実施例3と同様にして偽造防止用紙を製造した。スレッドを紙層間に抄き込んだ直後に紫外蛍光ランプを照射し、スレッドが紫外蛍光発色するか否かでスレッドの表裏を判定し、スレッドが反転していた場合は正常な面が抄き込まれるようにスレッドを挿入し直した。得られた偽造防止用紙を反射光でそれぞれ表面および裏面から観察すると、どちらの面からも青色のマイクロ文字の見え方がほぼ同一であった。このとき、表面および裏面での文字部の光線反射率の差は2%以内であった。
[Example 4]
[Manufacture of anti-counterfeit paper]
An anti-counterfeit paper was manufactured in the same manner as in Example 3 except that it was used for the thread obtained in Example 2. Immediately after the thread is engraved between the paper layers, an ultraviolet fluorescent lamp is irradiated, and the front and back of the thread are judged by whether or not the thread develops ultraviolet fluorescence. If the thread is reversed, the normal surface is engraved. Reinserted the thread so that it is. When the obtained anti-counterfeit paper was observed with reflected light from the front surface and the back surface, the appearance of blue micro characters was almost the same from both surfaces. At this time, the difference in the light reflectance of the character part between the front surface and the back surface was within 2%.

[実施例5]
〔偽造防止印刷物の製造〕
図14に示すように、実施例3の偽造防止用紙を使用し、商品券の図柄など印刷部30を印刷して偽造防止印刷物40を製造した。
[Example 5]
[Manufacture of anti-counterfeit printed matter]
As shown in FIG. 14, the forgery prevention printed matter 40 was manufactured by printing the printing unit 30 such as the design of the gift certificate using the forgery prevention paper of Example 3.

この偽造防止印刷物40をそれぞれ表面および裏面から反射光で観察すると、抄き込まれたスレッドのマイクロ文字(「SECURITY」の正文字と逆文字)の見え方がほぼ同一であった。   When the anti-counterfeit printed matter 40 was observed from the front surface and the back surface with reflected light, the appearance of the engraved thread micro characters (the normal character and the reverse character of “SECURITY”) was almost the same.

[実施例6]
〔偽造防止印刷物の製造〕
図14に示すように、実施例4の偽造防止用紙を使用し、商品券の図柄など印刷部30を印刷して偽造防止印刷物40を製造した。
[Example 6]
[Manufacture of anti-counterfeit printed matter]
As shown in FIG. 14, the forgery prevention printed matter 40 was manufactured by printing the printing unit 30 such as the design of the gift certificate using the forgery prevention paper of Example 4.

この偽造防止印刷物40をそれぞれ表面および裏面から反射光で観察すると、抄き込まれたスレッドの青色に着色されたマイクロ文字はいずれも正文字「★ABCD」として視認され、金属蒸着層は左右逆向きの文字としてごく薄く視認された。   When the anti-counterfeit printed matter 40 is observed with reflected light from the front surface and the back surface, the blue characters of the engraved thread are visually recognized as normal characters “★ ABCD”, and the metal deposition layer is reversed left and right. It was very thinly recognized as the direction letter.

スレッドの斜視図。The perspective view of a thread | sled. 従来のスレッドの断面図。Sectional drawing of the conventional thread | sled. 図2のスレッドを3層抄き合わせ紙に抄き込んだ偽造防止用紙の断面図。Sectional drawing of the anti-counterfeit paper which woven the thread | sled of FIG. 2 into the three-layer laminated paper. 図2のスレッドを2層抄き合わせ紙に抄き込んだ偽造防止用紙の断面図。FIG. 3 is a cross-sectional view of a forgery prevention paper in which the thread of FIG. 本発明の一実施形態に係るスレッドの断面図。Sectional drawing of the thread | sled which concerns on one Embodiment of this invention. 図5のスレッドを3層抄き合わせ紙に抄き込んだ偽造防止用紙の断面図。FIG. 6 is a cross-sectional view of a forgery prevention paper in which the thread of FIG. 本発明の他の実施形態に係るスレッドの断面図。Sectional drawing of the thread | sled which concerns on other embodiment of this invention. 本発明の他の実施形態に係るスレッドの断面図。Sectional drawing of the thread | sled which concerns on other embodiment of this invention. 本発明の他の実施形態に係るスレッドの断面図。Sectional drawing of the thread | sled which concerns on other embodiment of this invention. 本発明の他の実施形態に係るスレッドの断面図。Sectional drawing of the thread | sled which concerns on other embodiment of this invention. 本発明の他の実施形態に係るスレッドの断面図。Sectional drawing of the thread | sled which concerns on other embodiment of this invention. 本発明の他の実施形態に係るスレッドの断面図。Sectional drawing of the thread | sled which concerns on other embodiment of this invention. 実施例2における両面マイクロ文字入りスレッドの平面図。The top view of the thread | sled with a double-sided micro character in Example 2. FIG. 実施例5および6における偽造防止印刷物の平面図。The top view of the forgery prevention printed matter in Example 5 and 6. FIG.

符号の説明Explanation of symbols

1…透明なベースフィルム、2、2B…マイクロ文字、3、3a、3b…光透過抑制層、5…光の透過を抑制するベースフィルム、10…スレッド、11、12、13…紙層、20…スレッド、30…印刷部、40…偽造防止用紙。   DESCRIPTION OF SYMBOLS 1 ... Transparent base film, 2, 2B ... Micro character, 3, 3a, 3b ... Light transmission suppression layer, 5 ... Base film which suppresses transmission of light, 10 ... Thread, 11, 12, 13 ... Paper layer, 20 ... Thread, 30 ... Printing section, 40 ... Anti-counterfeit paper.

Claims (11)

偽造防止のために用紙の表裏両面から視認できるように用紙に抄き込まれるスレッドであって、
透明なベースフィルムと、
前記透明なベースフィルム上に形成された偽造防止層と、
前記透明なベースフィルムの一面または両面に、少なくとも前記偽造防止層に対応して形成された光透過抑制層と
を有することを特徴とするスレッド。
A thread that is woven into the paper so that it can be seen from both the front and back sides of the paper to prevent forgery,
A transparent base film,
An anti-counterfeit layer formed on the transparent base film;
A thread comprising: a light transmission suppressing layer formed on at least one surface of the transparent base film corresponding to the anti-counterfeit layer.
偽造防止のために用紙の表裏両面から視認できるように用紙に抄き込まれるスレッドであって、
光の透過を抑制するベースフィルムと、
前記光の透過を抑制するベースフィルム上に形成された偽造防止層と
を有することを特徴とするスレッド。
A thread that is woven into the paper so that it can be seen from both the front and back sides of the paper to prevent forgery,
A base film that suppresses light transmission;
A thread having an anti-counterfeit layer formed on a base film that suppresses transmission of the light.
前記光透過抑制層の光線透過率(JIS B9620−1)が20%〜60%であることを特徴とする請求項1に記載のスレッド。   2. The thread according to claim 1, wherein a light transmittance (JIS B9620-1) of the light transmission suppressing layer is 20% to 60%. 前記光の透過を抑制するベースフィルムの光線透過率(JIS B9620−1)が20%〜60%であることを特徴とする請求項2に記載のスレッド。   The thread according to claim 2, wherein the light transmittance (JIS B9620-1) of the base film that suppresses the light transmission is 20% to 60%. 前記偽造防止層が、所望のパターンを形成していることを特徴とする請求項1乃至4のいずれか1項に記載のスレッド。   The thread according to any one of claims 1 to 4, wherein the anti-counterfeit layer forms a desired pattern. 前記パターンが、有彩色もしくは無彩色のインキで形成されたマイクロ文字、またはデメタライジングにより形成されたマイクロ文字であることを特徴とする請求項1乃至5項のいずれか1項に記載のスレッド。   The thread according to any one of claims 1 to 5, wherein the pattern is a micro character formed with chromatic or achromatic ink or a micro character formed by demetalizing. . 前記光透過抑制層がデメタライジングのための保護層であることを特徴とする請求項6に記載のスレッド。   The thread according to claim 6, wherein the light transmission suppressing layer is a protective layer for demetalizing. 前記マイクロ文字がベースフィルムの一面に形成されていることを特徴とする請求項6に記載のスレッド。   The thread according to claim 6, wherein the micro characters are formed on one surface of a base film. 前記マイクロ文字がベースフィルムの両面に形成されていることを特徴とする請求項6に記載のスレッド。   The thread according to claim 6, wherein the micro characters are formed on both surfaces of a base film. 請求項1乃至9のいずれかに記載のスレッドが抄き込まれた偽造防止用紙であって、それぞれ偽造防止用紙の表面および裏面から前記スレッドの偽造防止層までの厚み方向の距離が互いに異なることを特徴とする偽造防止用紙。   A forgery-preventing paper in which the thread according to any one of claims 1 to 9 is engraved, wherein the distance in the thickness direction from the front and back surfaces of the anti-counterfeit paper to the anti-counterfeit layer of the thread is different from each other. Anti-counterfeit paper characterized by. 請求項10に記載の偽造防止用紙に、偽造防止印刷物としての印刷部が設けられていることを特徴とする偽造防止印刷物。   An anti-counterfeit printed matter, wherein the anti-counterfeit paper according to claim 10 is provided with a printing section as an anti-counterfeit printed matter.
JP2006288840A 2006-10-24 2006-10-24 Thread, anti-counterfeit paper using the same, and anti-counterfeit printed matter using the thread Pending JP2008106385A (en)