JP2008056958A - Continuous partially-plating method and apparatus

Info

Publication number: JP2008056958A
Application number: JP2006233085A
Authority: JP
Inventors: Takeshi Suzuki; 鈴木　　剛; Tadashi Shimizu; 正清水
Original assignee: HIRAI SEIMITSU KK
Current assignee: HIRAI SEIMITSU KK
Priority date: 2006-08-30
Filing date: 2006-08-30
Publication date: 2008-03-13
Anticipated expiration: 2026-08-30
Also published as: JP4974614B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a continuous partially-plating method by which a material to be plated is continuously partially plated while securing stable quality of partially plating without using a short material as the material to be plated, a continuous partially plating apparatus for carrying out the method and a rotary belt for partially plating. <P>SOLUTION: The endless rotary belt 10 (10a) for partially plating is formed by sticking a masking magnetic body sheet 15 having a soft elastomer coating film layer 14 formed on a magnetic sheet 13 formed by dispersing and orienting magnetic powder using a synthetic resin as a binder on a base tape 17. A part of a metal sheet 5 which is not covered with the rotary belt 10 is continuously partially plated while carrying the metal sheet 5 held between the rotary belts 10 by magnetic force. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は連続部分めっき方法および、連続部分めっき装置に関し、より詳しくは、耐めっき特性ならびに高磁力吸引特性を持つ部分めっき用回転ベルトの間に、金属薄板条を挟んだ状態を維持したまま連続的に走行させながら、当該金属薄板条表面のうち前記部分めっき用回転ベルトで覆われていない部分に対して部分めっきするものであり、作業性の向上による短納期化、低コスト化が図れる連続部分めっき方法、連続部分めっき装置、および、連続部分めっき装置を構成する連続部分めっき用の回転ベルトに関するものである。 The present invention relates to a continuous partial plating method and a continuous partial plating apparatus. More specifically, the present invention is continuous while maintaining a state in which a thin metal strip is sandwiched between rotating belts for partial plating having anti-plating characteristics and high magnetic attraction characteristics. The part of the surface of the metal sheet strip that is not covered with the rotating belt for partial plating is partially plated while continuously running, and it is possible to reduce the delivery time and cost by improving workability. The present invention relates to a partial plating method, a continuous partial plating apparatus, and a rotating belt for continuous partial plating constituting the continuous partial plating apparatus.

金めっき等の高価な材料を用いた表面処理を行う場合、コスト低減のために被めっき物の必要最小限の部分だけに部分めっきを施すことが行われる。従来の連続部分めっき方法としては、被めっき物（金属薄板条）のめっき面側を、マスキング治具で覆い、被めっき物のめっき面側でない面側を、弾力性のある循環走行する回転ベルトにより押しつけて、被めっき物をマスキング治具と回転ベルトの間に挟持し、マスキング治具と回転ベルトベルトとともに金属薄板条を搬送しながら、金属薄板条のめっき面側のマスキング治具の開口部から露出した部分にめっき液を吹きつけ、被めっき物とアノード間に所定電圧を負荷して、被めっき物を連続的に部分めっきする方法が開示されている。 When surface treatment using an expensive material such as gold plating is performed, partial plating is performed only on the minimum necessary portion of an object to be plated for cost reduction. As a conventional continuous partial plating method, the plating surface side of the object to be plated (metal thin strip) is covered with a masking jig, and the surface that is not the plating surface side of the object to be plated is elastically circulated. The object to be plated is clamped between the masking jig and the rotating belt, and the metal sheet strip is conveyed together with the masking jig and the rotating belt belt. A method is disclosed in which a plating solution is sprayed onto a portion exposed from the substrate, a predetermined voltage is applied between the object to be plated and the anode, and the object to be plated is continuously partially plated.

この場合、マスキング治具側に金属薄板条を押圧し、マスキング治具とを密着させる方式としては、つぎの１）乃至４）の方法が提案されている。 In this case, the following methods 1) to 4) have been proposed as a method of pressing the metal sheet strip on the masking jig side and bringing it into close contact with the masking jig.

１）（回転ドラム方式）回転ドラムの上側周面または下側周面にマスキングベルトを押しつけ、この回転ドラムの下側部分をめっき槽内に浸漬し、被めっき材とアノード間に所定電圧を負荷して、前記マスキングベルトの隙間に位置する被めっき物に部分めっきする方法（特許文献１）、さらに、マスキングベルトの回転ドラム側の面に凸部を設け、回転ドラム側の周面に設けられた凹部に嵌合してマスキングベルトの蛇行（位置変動）を抑制させる方式（特許文献２）。 1) (Rotating drum method) A masking belt is pressed against the upper or lower peripheral surface of the rotating drum, the lower portion of the rotating drum is immersed in the plating tank, and a predetermined voltage is applied between the material to be plated and the anode. Then, a method of partially plating an object to be plated located in the gap of the masking belt (Patent Document 1), and further, a convex portion is provided on the surface of the masking belt on the rotating drum side, and provided on the peripheral surface of the rotating drum side. A method of suppressing the meandering (position fluctuation) of the masking belt by fitting in the concave portion (Patent Document 2).

２）（レインボ−セル方式）：連続循環移動するマスキングベルトに、循環移動する回転ベルトを組み合わせ、被めっき物（金属薄板条）を両ベルト間に対応位置決めして挟み、マスキングベルト側をかまぼこ形状のスパジャー表面上に、バックテンションを付加して両ベルトを圧接挟持した状態で連続的に走行させ、その際に、ノズルから噴射されためっき液をマスキングベルト側に吹きかけ、被めっき材とアノード間に所定電圧を負荷して、前記被めっき物に連続的に部分めっきする方式を採用した、商品名を「レインボーセル−ＲＢＣＭ／７５０」とする連続部分めっき装置が上市されている。 2) (Rainbow-cell system): A masking belt that continuously circulates and a rotating belt that circulates and moves, and the object to be plated (thin metal strip) is positioned and sandwiched between the two belts. On the surface of the spudger, the belt is continuously run with the back tension applied and the belts are pressed and clamped. At that time, the plating solution sprayed from the nozzle is sprayed to the masking belt side, between the material to be plated and the anode. A continuous partial plating apparatus having a product name of “Rainbow Cell-RBCM / 750”, which employs a system in which a predetermined voltage is applied to the object to be plated and is continuously plated, is marketed.

３）めっき領域を特定する開口を形成したマスク体を、めっき液通孔を形成した多数のブロックを連結して全体的にキャタビラ状に形成された回転ベルトに組み合わせ、回転ベルトの前後回転部間に配置してあるスパージャの上方へ同期的に循環移動自在なプレスベルトを対応位置決めして配し、そして順次送り込まれる短冊状めっき物をマスク体の上面へ載置してはプレスベルトと回転ベルト都で狭持しつつスパージャの上部を通過させ、その際にスパージャよりめっき液を噴射して部分めっきする方法（特許文献３）。 3) A mask body having an opening for specifying a plating area is combined with a rotating belt formed in a generally caterpillar shape by connecting a large number of blocks with plating solution passage holes between the front and rear rotating parts of the rotating belt. A press belt which can be circulated and moved synchronously above the sparger arranged in the corresponding position is arranged and arranged, and a strip-like plated product to be sequentially fed is placed on the upper surface of the mask body, and the press belt and the rotating belt A method of performing partial plating by passing the upper part of a sparger while holding it in the capital and spraying a plating solution from the sparger (Patent Document 3).

４）被めっき物（金属薄板条）をマスキングしてマスキングするマスク部分を個々のマスクプレートとしこれを連結して対抗するエンドレスコンベアとし、被めっき物（金属薄板条）を挟み、めっきゾーン全長にわたる支持構造体で係合、保持し、前記エンドレスコンベアの上下に具備した搬送用コンベアとの摩擦力で搬送し、ノズルから噴射されためっき液を吹きかけ、被めっき物（金属薄板条）とアノード間に所定電圧を負荷して、当該被めっき物（金属薄板条）に部分めっきすることを繰り返す方式（特許文献４）。 4) Masking parts to be plated (thin metal strips) and masking each mask plate as an individual endless conveyor, connecting them against each other, sandwiching the objects to be plated (thin metal strips) and covering the entire plating zone Engaged and held by a support structure, conveyed by frictional force with the conveying conveyor provided above and below the endless conveyor, sprayed with the plating solution sprayed from the nozzle, and between the object to be plated (metal thin strip) and the anode A method of repeatedly applying a predetermined voltage to the object to be plated (metal thin strip) and repeating partial plating (Patent Document 4).

米国特許第４１３２６１７号公報U.S. Pat. No. 4,132,617 特開平１１−１３１２８４号公報JP-A-11-131284 特公平３−１３９３号公報Japanese Patent Publication No.3-1393 特表平９−５０４５７６号公報Japanese National Patent Publication No. 9-504576

しかしながら、上記１）及び２）記載のめっき方法は、回転ドラムの上側周面もしくは下側周面またはスパジャー表面上にバックテンションを付加した状態で押し圧、金属薄板条を圧接した状態で狭持して部分めっき層を形成するので、金属薄板条の板厚に制限を受けるとか、引っ張り搬送やバックテンションの付加などによって生じる伸びの変化に追従することができず、めっき層の形成領域の位置にバラツキが生じるとか、めっき層形成領域外にフラッシュ（にじみ）が発生するという問題があり、また、めっき層の形成位置が、回転ドラムの上側周面もしくは下側周面またはスパジャー表面上での圧接移動距離相当しかないため、めっきできる長さ（めっき有効長）に制限があり、めっき形成効率が悪いという問題があった。 However, in the plating methods described in 1) and 2) above, the pressing force is applied with the back tension applied to the upper peripheral surface or the lower peripheral surface of the rotating drum or the surface of the spudger, and the thin metal strip is held in a pressed state. Since the partial plating layer is formed, the thickness of the thin metal strip is limited, and it is not possible to follow the change in elongation caused by pulling and adding back tension. There is a problem in that there is variation in the surface of the plating layer, or flashing (bleeding) occurs outside the plating layer formation region, and the formation position of the plating layer is on the upper peripheral surface or lower peripheral surface of the rotating drum or on the surface of the spudger. Since there is only a pressure moving distance, there is a limit to the length that can be plated (effective plating length), and there is a problem that plating formation efficiency is poor.

上記３）記載の方法は、押しつけ治具でマスキングベルト側に向けて押し圧、単位マスク部に金属薄板条を圧接した状態のまま所定長さ移動させて、めっき層の部分形成を行うので、金属薄板条の板厚に自由度があるものの、めっき層の形成領域の位置にバラツキが生じ易いとか、また、押しつけ治具の押圧付加などによってマスキング強度に強弱ができるためにめっき層形成領域外にフラッシュ（にじみ）が発生するなど、めっき品質が不安定になり、また、めっき形成効率が悪いという問題があった。 In the method described in 3), the pressing pressure is applied toward the masking belt with the pressing jig, and the metal thin plate is moved to a predetermined length while being pressed into the unit mask portion, so that the plating layer is partially formed. Although there is a degree of freedom in the thickness of the thin metal strip, there is a tendency for variations in the position of the plating layer formation area, and because the masking strength can be increased or decreased by applying a pressing jig, etc., it is outside the plating layer formation area. There is a problem that the plating quality becomes unstable and the plating formation efficiency is poor.

上記４）記載の方法は、互いに対峙する複数対の押圧ローラによって、マスキングベルトと回転ベルト間に被めっき物（金属薄板条）を圧接、密着するように構成されているため、マスキング強度に強弱ができ、めっき品質が不安定になる等の問題があった。 In the method described in 4) above, since the object to be plated (metal thin strip) is pressed and adhered between the masking belt and the rotating belt by a plurality of pairs of pressing rollers facing each other, the strength of the masking is strong. There is a problem that the plating quality becomes unstable.

本発明は上記の実情に鑑みなされたもので、その目的とするところは、被めっき物を短尺品とせず、安定した部分めっき品質を確保でき、高速で連続的に部分めっきできる連続部分めっき方法、および、本方法を実施する連続部分めっき装置を提供することにある。 The present invention has been made in view of the above circumstances, and its object is to make a continuous partial plating method capable of ensuring stable partial plating quality without making the object to be plated a short product, and continuously performing partial plating at a high speed. And it is providing the continuous partial plating apparatus which enforces this method.

本発明の他の目的とするところは、前記連続部分めっき装置の要部を構成する部分めっき用の回転ベルトを提供することにある。 Another object of the present invention is to provide a rotating belt for partial plating which constitutes a main part of the continuous partial plating apparatus.

本発明に係る連続部分めっき方法は以下の発明を包含する。
（１）合成樹脂をバインダーに用いて磁気粉末を配向分散して形成されたマグネットシートに軟質エラストマー被膜層を備えてなるマスキング用磁性体シートを、ベーステープ上に接着してエンドレスの部分めっき用回転ベルトを構成し、所定のマイナス電位が付加された金属薄板条を前記部分めっき用回転ベルトの磁力によって当該部分めっき用回転ベルト間に挟んだ状態を維持したまま搬送させながら、当該金属薄板条表面のうち前記部分めっき用回転ベルトで覆われていない部分に対して部分めっきを施すところに特徴がある。
（２）上記（１）記載に連続部分めっき方法において、前記部分めっき用回転ベルトの一方が、前記軟質エラストマー被膜層の磁着面側に所望する所定形状の凹凸形状が形成された平ベルト、孔付加工された平ベルト、または、前記軟質エラストマー被膜層の磁着面側に所望する所定形状の凹凸形状が形成されかつ孔付加工された平ベルトのうちのいずれかであるところに特徴がある。
（３）上記（１）または（２）に記載の連続部分めっき方法において、前記部分めっき用回転ベルトの一方が、エラストマー被膜層を備えた磁性金属薄板ベルト、または、エラストマー被膜層を備え磁着面側に所望する所定形状の凹凸形状が形成された磁性金属薄板ベルトであるところに特徴がある。 The continuous partial plating method according to the present invention includes the following inventions.
(1) Endless partial plating by adhering a magnetic sheet for masking comprising a soft elastomer coating layer to a magnetic sheet formed by orienting and dispersing magnetic powder using a synthetic resin as a binder on a base tape While forming a rotating belt and transporting the thin metal strip to which a predetermined negative potential is applied while maintaining the state sandwiched between the partial plating rotary belts by the magnetic force of the partial plating rotary belt, It is characterized in that partial plating is performed on a portion of the surface that is not covered with the partial plating rotary belt.
(2) In the continuous partial plating method described in the above (1), one of the partial plating rotary belts is a flat belt in which a desired uneven shape is formed on the magnetic adhesion surface side of the soft elastomer coating layer, It is characterized in that it is either a flat belt that has been processed with holes, or a flat belt that has a desired irregular shape formed on the magnetic adhesion surface side of the soft elastomer coating layer and has been processed with holes. is there.
(3) In the continuous partial plating method according to the above (1) or (2), one of the partial plating rotary belts is a magnetic metal thin plate belt provided with an elastomer coating layer, or an elastomer coating layer is magnetically attached. It is characterized in that it is a magnetic metal sheet belt in which a desired irregular shape is formed on the surface side.

本発明に係る連続部分めっき装置は以下の発明を包含する。
（４）合成樹脂をバインダーに用いて磁気粉末を配向分散して形成されたマグネットシートに軟質エラストマー被膜層を備えてなるマスキング用磁性体シートを、ベーステープ上に接着してエンドレスに形成された部分めっき用回転ベルトと、該部分めっき用回転ベルトを連続的に走行させる駆動手段とを有し、前記部分めっき用回転ベルトの間に、所定のマイナス電位が付加された金属薄板条を前記部分めっき用回転ベルトの磁力によって当該部分めっき用回転ベルト間に挟んだ状態を維持したままめっき槽またはスパジャに搬送、通過させながら、当該金属薄板条表面のうち前記部分めっき用回転ベルトで覆われていない部分に対して連続部分めっきを施す連続部分めっき装置であって、
前記部分めっき用回転ベルトが、平ベルト同士の対、平ベルトと孔付加工された平ベルトとの組、孔付加工された平ベルト同士の対、または、平ベルトもしくは孔付加工された平ベルトとエラストマー被膜層を備えた磁性金属薄板ベルトとの組のうちのいずれかであるところに特徴がある。
（５）上記（４）記載の連続部分めっき装置において、前記部分めっき用回転ベルトの一方が、エラストマー被膜層を備えた磁性金属薄板ベルト、または、エラストマー被膜層を備え磁着面側に所望する所定形状の凹凸形状が形成された磁性金属薄板ベルトであるところに特徴がある。 The continuous partial plating apparatus according to the present invention includes the following inventions.
(4) A magnetic sheet for masking comprising a soft elastomer coating layer on a magnetic sheet formed by orienting and dispersing magnetic powder using a synthetic resin as a binder was bonded endlessly on a base tape and formed endlessly. A rotating belt for partial plating, and a driving means for continuously running the rotating belt for partial plating, and a metal sheet with a predetermined negative potential applied between the rotating belts for partial plating. It is covered with the partial plating rotary belt on the surface of the metal sheet strip while being transported and passed to the plating tank or spudger while maintaining the state sandwiched between the partial plating rotary belts by the magnetic force of the plating rotary belt. A continuous partial plating apparatus for performing continuous partial plating on a non-part,
The rotating belt for partial plating is a pair of flat belts, a pair of flat belts and flat belts with holes, a pair of flat belts with holes, or a flat belt or flat holes with holes. It is characterized in that it is one of a set of a belt and a magnetic metal sheet belt provided with an elastomer coating layer.
(5) In the continuous partial plating apparatus according to the above (4), one of the partial plating rotary belts is desired on the magnetic adhesion surface side including a magnetic metal thin plate belt provided with an elastomer coating layer or an elastomer coating layer. It is characterized in that it is a magnetic metal thin plate belt having a predetermined uneven shape.

本発明に係る部分めっき用の回転ベルトは下記の構成よりなる。
（６）合成樹脂をバインダーに用いて磁気粉末を配向分散して形成されたマグネットシート上に軟質エラストマー被膜層を備えたマスキング用磁性体シートと、該マスキング用磁性体シートの複数をシームレスに接着するとともに全体をエンドレスに形成するためのベーステープとを具備しており、前記軟質エラストマー被膜層の磁着面側に所望する所定形状の凹凸形状が形成された平ベルト、孔付加工された平ベルト、または、前記軟質エラストマー被膜層の磁着面側に所望する所定形状の凹凸形状が形成されかつ孔付加工された平ベルトのうちのいずれかであるところに特徴がある。 The rotating belt for partial plating according to the present invention has the following configuration.
(6) Seamlessly bonding a masking magnetic sheet having a soft elastomer coating layer on a magnetic sheet formed by orientation-dispersing magnetic powder using a synthetic resin as a binder and a plurality of the masking magnetic sheets A flat belt having a desired irregular shape formed on the magnetic adhesion surface side of the soft elastomer coating layer, and a flat plate with holes. It is characterized in that it is either a belt or a flat belt in which a desired irregular shape is formed on the magnetic adhesion surface side of the soft elastomer coating layer and is processed with holes.

本発明の連続部分めっき装置は、被めっき物（金属薄板条）を長尺のまま部分めっき用の回転ベルトの間にマグネットの磁力によって密着、挟持させた状態で搬送するようになっているから、回転ベルトに対して金属薄板条（被めっき物）を均一に面当接できめっき液の浸み込みがないため、めっき境界部分にフラッシュやにじみの発生がなく高精度と高品質の安定した部分めっきができ、さらに、金属薄板条の長さに制限を受けることなくめっき有効長を所望する所定長さに自在に設定できる。 In the continuous partial plating apparatus of the present invention, the object to be plated (metal thin strip) is transported in a state of being adhered and sandwiched between the rotating belts for partial plating by the magnetic force of the magnet while being long. Since the metal strip (plating object) can be evenly abutted against the rotating belt and the plating solution does not penetrate, there is no flashing or bleeding at the plating boundary, and high accuracy and high quality are stable. Partial plating can be performed, and further, the plating effective length can be freely set to a desired predetermined length without being limited by the length of the thin metal strip.

また、回転ベルトと金属薄板条との密着性を確保するため、従来の係る装置構成に必須であった例えばめっきするための加圧装置機構や、めっきをするための領域に配設されている機械的加圧装置機構などの障害物（例えばめっき領域に配設されている複数個の押圧ローラなど）が不要となり、めっき装置の全体構造を簡略化できるため装置全体を小型化でき、さらに、金属薄板条片面の部分めっきのみならず両面に対して同時的かつ高速めっきできる連続部分めっき装置の設計自由度が高く、マスキングベルトの低コスト化などと互いに相まって、生産効率が高く、短納期、低コスト化を図った連続部分めっき装置として提供できる。 Moreover, in order to ensure the adhesiveness of a rotating belt and a metal thin strip, it is arrange | positioned in the area | region for performing the pressurization apparatus mechanism for plating, etc. which were essential to the apparatus structure which concerns conventionally, for example. Obstacles such as a mechanical pressure device mechanism (for example, a plurality of pressing rollers disposed in the plating area) are not required, and the overall structure of the plating device can be simplified, so that the entire device can be downsized. High degree of design freedom of continuous partial plating equipment that can simultaneously and high-speed plating on both sides as well as partial plating on one side of metal sheet strip, coupled with cost reduction of masking belt, etc., high production efficiency, short delivery time, It can be provided as a continuous partial plating apparatus for cost reduction.

また、めっき液の製品外への飛散量や付着量がともに少ないため、めっき液の管理、廃液処理などが容易となる。 In addition, since the amount of the plating solution scattered and adhered to the outside of the product is small, the management of the plating solution and the treatment of the waste solution are facilitated.

本発明の実施の形態を実施例によって説明するが、これらはその代表例に過ぎず、様々に設計変更して実施できるものとする。 Embodiments of the present invention will be described by way of examples. However, these are merely representative examples, and can be implemented with various design changes.

図１は、本発明の一実施例となる連続部分めっき装置１を説明するために概略的に示す平面図である。図２（ａ））は、回転ベルトの代表的な一使用状態を模式的に示す斜視図であり、図２（ｂ）は、図２（ａ）のＡ−Ａ線に沿った断面図である。なお、図面中、塗りつぶした部分が部分めっきされる領域であり、また、各部材の厚さなどは、理解を容易にするため誇張して図示されている。以下、同様である。 FIG. 1 is a plan view schematically showing a continuous partial plating apparatus 1 according to an embodiment of the present invention. FIG. 2 (a)) is a perspective view schematically showing a typical use state of the rotating belt, and FIG. 2 (b) is a cross-sectional view taken along the line AA of FIG. 2 (a). is there. In the drawings, the painted portion is a region to be partially plated, and the thickness of each member is exaggerated for easy understanding. The same applies hereinafter.

図１において、この連続部分めっき装置１は、めっき槽において長尺の被めっき物（金属薄板条）５に対して連続部分めっきを施すもので、回転ベルト１０ａと，前記被めっき物（金属薄板条）５のめっき域を特定するための開口１１が形成された回転ベルト１０ｂとからなる１対の回転ベルト１０の間に、前記被めっき物（金属薄板条）５を磁力によって密着させて挟み込んだ状態のまま１方向に搬送させ、前記回転ベルト１０の開口１１から露出する前記被めっき物（金属薄板条）５の所定のめっき部分に向けてめっき液を吹き付けて、前記被めっき物（金属薄板条）の所定のめっき部分のみに電気めっきを施す装置であり、被めっき物表面は図示しない給電ローラを介してカソード（陰極）となるように構成されており、被めっき物５のめっき領域にめっき液が供給されると、陰極との間に電流が流れ連続的に部分めっきを施すようになっている。 In FIG. 1, a continuous partial plating apparatus 1 performs continuous partial plating on a long object to be plated (metal thin strip) 5 in a plating tank, and includes a rotating belt 10a and the object to be plated (metal thin plate). The object to be plated (thin metal strip) 5 is put in close contact with a magnetic force between a pair of rotating belts 10 including a rotating belt 10b in which an opening 11 for specifying the plating area 5) is formed. In this state, the plate is conveyed in one direction, and a plating solution is sprayed toward a predetermined plating portion of the object to be plated (thin metal strip) 5 exposed from the opening 11 of the rotating belt 10, so that the object to be plated (metal) This is an apparatus for performing electroplating only on a predetermined plating portion of the thin strip), and the surface of the object to be plated is configured to be a cathode (cathode) via a power supply roller (not shown). When the plating liquid is supplied to the plating zone, so that applying a continuous partial plating current flows between the cathode.

上記部分めっき用の回転ベルト１０ａは、合成樹脂をバインダーに用いて磁気粉末を配向分散してマグネットシート１３を形成し、該マグネットシート１３の磁着面側に軟質エラストマー被膜層１４を被覆することによってマスキング用磁性体シート１５を形成し、さらに、該マスキング用磁性体シート１５複数の磁着面と反対側に、軟質のベーステープ１７（例えば接着剤つきポリエステルフィルム）上にシームレスに接着してエンドレスループ状に形成されており、前記回転ベルト１０ｂは、前記回転ベルト１０ａに、前記被めっき物（金属薄板条）５の所定のめっき部分に向けてめっき液を吹き付けするための開口１１を設けたものであり、各回転ベルトのテンション調整機能を兼ねる駆動ローラ３（駆動手段）によって循環走行させることにより、反復して部分めっき処理に使用されるようになっている。 The rotating belt 10a for partial plating uses a synthetic resin as a binder to orient and disperse magnetic powder to form a magnet sheet 13 and coat the soft elastomer coating layer 14 on the magnetized surface side of the magnet sheet 13. Then, the masking magnetic sheet 15 is formed on the soft base tape 17 (for example, a polyester film with an adhesive) on the side opposite to the plurality of magnetic attachment surfaces. The rotating belt 10b is provided with an opening 11 for spraying a plating solution toward a predetermined plating portion of the object (metal thin strip) 5 on the rotating belt 10a. It is circulated by a driving roller 3 (driving means) that also functions as a tension adjustment for each rotating belt. By, and is used to iteratively partial plating process.

なお、部分めっき用の回転ベルト１０は、軟質エラストマー被膜層１４の磁着面側に必要に応じて所望する所定形状の凹凸形状が形成された平ベルト形状、めっき域を特定するための孔付加工（開口１１）が施された平ベルト形状、所望する所定形状の凹凸形状を形成されかつめっき域を特定用の孔付加工（開口１１）が施された平ベルト形状などとして形成されている。なお、部分めっき用の回転ベルトの一方にマスキング用磁性体シートが備えられている場合、これと対をなす部分めっき用の回転ベルトとして、マグネットシートを有しておらずかつ軟質エラストマー被膜層で被覆された磁性金属薄板ベルトを使用しても、マスキング用磁性体シートを有する回転ベルトと磁性金属薄板ベルト間に、金属薄板条（被めっき物）を密着して挟持させることができるので、本明細書においては、マグネットシートを有していない前記磁性金属薄板ベルトもまた部分めっき用の回転ベルトとみなすものとする。 The rotating belt 10 for partial plating has a flat belt shape in which an uneven shape of a desired shape is formed on the magnetic adhesion surface side of the soft elastomer coating layer 14 as necessary, and has a hole for specifying a plating area. A flat belt shape that has been subjected to processing (opening 11), a flat belt shape that has a predetermined uneven shape and a plating area that has been subjected to specific hole processing (opening 11), and the like. . In addition, when a magnetic sheet for masking is provided on one of the rotating belts for partial plating, the rotating belt for partial plating that forms a pair with this does not have a magnet sheet and is a soft elastomer coating layer. Even if a coated magnetic metal sheet belt is used, a metal sheet strip (to-be-plated object) can be tightly held between the rotating belt having the masking magnetic sheet and the magnetic metal sheet belt. In the specification, the magnetic metal sheet belt not having a magnet sheet is also regarded as a rotating belt for partial plating.

また、ベーステープ１７としてアイランド用マスク（メッシュのベースシート）１７ａを備えた回転ベルトを使用してスポットめっきをする場合には、部分めっき用回転ベルトの長さを、製品１個の長さの整数倍にすることが好ましく、また、高精度のスポットめっきをする場合には、マスキング用磁性体シートを、最終製品１個１個となるセグメント方式を採用するとともに回転ベルトのベーステープに、孔付またはメッシュ構造の例えばポリエステルテープなど使用することが好ましい。 Further, when spot plating is performed using a rotating belt provided with an island mask (mesh base sheet) 17a as the base tape 17, the length of the rotating belt for partial plating is set to the length of one product. It is preferable to use an integral multiple, and when high-precision spot plating is used, the magnetic sheet for masking adopts a segment system that is one by one for the final product, and holes are formed in the base tape of the rotating belt. It is preferable to use an attached or mesh structure such as polyester tape.

また、めっきの品質を考慮した場合、部分めっき用回転ベルトに、図示しない位置決め手段を備えて金属薄板条の位置合わせを行い、回転ベルト間に金属薄板条（被めっき物）を磁力吸着によって挾みこみ密着させてめっきを施す方法が採用されると、めっき位置精度や、めっき厚の均一性などに優れるから、高精度かつ高品質の部分めっきができる。 In consideration of the quality of plating, the rotating belt for partial plating is provided with positioning means (not shown) to align the thin metal strips, and the thin metal strips (to-be-plated objects) are separated by magnetic adsorption between the rotating belts. If a method of plating by intimate contact is adopted, the plating position accuracy and the uniformity of the plating thickness are excellent, so that high-precision and high-quality partial plating can be performed.

なお、以上説明した連続部分めっき用の回転ベルトは、後述するように、部分めっき領域の限定や特殊性に鑑み、適宜選択して対に組合せて、使い分けされる。 In addition, the rotation belt for continuous partial plating described above is appropriately selected and used in combination as appropriate in consideration of the limitation and speciality of the partial plating region, as will be described later.

つぎに、上記マグネットシート１３は、例えばシリコーンゴムをバインダーとして用い例えばNdFeB（ネオジウム・鉄・ボロン）系磁性粉末を配向、分散させ、所要の厚さ、長さおよび幅に形成されたものである。ただし、前記磁性粉末をNdFeB（ネオジウム・鉄・ボロン）系磁性粉末に限定するものではなく、磁束密度が高く高磁力のマグネットシートを形成し得るものであれば何ででも良く、また、バインダーを前記シリコーンゴムに限定するものではなく、耐薬品性、耐クラック性、および、シート厚の均一精度に優れ、駆動中の寸法変化が少なく、そして、磁束密度を低下させないゴム体であれば、前記シリコーンゴムに代えてこれを使用できるものとする。 Next, the magnet sheet 13 is formed to have a required thickness, length, and width by, for example, aligning and dispersing, for example, NdFeB (neodymium / iron / boron) based magnetic powder using silicone rubber as a binder. . However, the magnetic powder is not limited to NdFeB (neodymium / iron / boron) based magnetic powder, and may be anything as long as it can form a magnetic sheet having a high magnetic flux density and a high magnetic force. The silicone rubber is not limited to the silicone rubber, and any silicone body can be used as long as it is excellent in chemical resistance, crack resistance and sheet thickness uniformity accuracy, has little dimensional change during driving, and does not reduce magnetic flux density. This can be used instead of rubber.

上記マスキング用磁性体シート１５は、マグネットシート１３の全面に、軟質エラストマー（硬度；５〜１０°）をコーティングして、軟質エラストマー被膜層１４を形成したものである。ただし、コーティング剤を限定するものではないが、加工性、耐薬品性、耐クラック性、および、シート厚の均一精度などに優れ、駆動中の寸法変化が少なく、そして、磁束密度を低下させ難いものであることが好ましい。 The masking magnetic sheet 15 is obtained by coating the entire surface of the magnet sheet 13 with a soft elastomer (hardness: 5 to 10 °) to form a soft elastomer coating layer 14. However, although the coating agent is not limited, it is excellent in workability, chemical resistance, crack resistance, and uniform sheet thickness accuracy, has little dimensional change during driving, and is difficult to lower the magnetic flux density. It is preferable.

上記軟質のベーステープ１７は、マスキング用磁性体シート１５を裏から支え、マスキング用磁性体シート１５をエンドレス平ベルト状に構成するためのものであり、孔付加工した平ベルトを形成する際には、ベーステープ１７として軟質のアイランド用マスク（メッシュのベースシート）１７ａを使用することが好ましい。なお、ベーステープ１７の材質を上記のようにポリエステルフィルムのみに限定するものではないが、耐薬品性を有し、温度による変化が小さく、引張応力に強く伸びも小さく、そして、マスキング用磁性体シート１５の吸引力による変形に追従して自在変形可能な柔軟性を保有していることが好ましく、ベーステープ１７の裏面の接着材が剥離紙等で被覆されていると、使い勝手に優れるためさらに好ましい。 The soft base tape 17 is for supporting the masking magnetic sheet 15 from the back and forming the masking magnetic sheet 15 in an endless flat belt shape. When forming a flat belt with holes, It is preferable to use a soft island mask (mesh base sheet) 17 a as the base tape 17. Although the material of the base tape 17 is not limited to the polyester film as described above, it has chemical resistance, changes with temperature are small, it is strong against tensile stress and has little elongation, and a magnetic material for masking It is preferable that the sheet 15 has flexibility so as to be freely deformable following the deformation caused by the suction force. If the adhesive on the back surface of the base tape 17 is covered with a release paper or the like, it is easy to use. preferable.

本連続部分めっき装置１によると、被めっき物である金属薄板条５は、駆動手段によって連続走行する部分めっき用回転ベルト１０，１０の間に、当該部分めっき用回転ベルト１０，１０の面にほぼ密着した状態に挟持されて入口からめっき槽内に送り込まれ、金属薄板条５を挟んだ状態を維持したまま連続搬送させながらめっき液を噴射し、開口１１により特定されためっき領域のみに部分めっきが施され、ついで、出口から送り出され、回転ベルト１０，１０の転回位置で回転ベルト１０，１０が互いに引き離される時、これに伴って、部分めっき済み金属薄板条として分離される。 According to this continuous partial plating apparatus 1, the metal thin strip 5 that is an object to be plated is placed on the surface of the partial plating rotary belts 10, 10 between the partial plating rotary belts 10, 10 continuously running by the driving means. It is sandwiched in an almost intimate state and fed into the plating tank from the entrance, and the plating solution is sprayed while being continuously conveyed while maintaining the state in which the thin metal strip 5 is sandwiched, and only in the plating region specified by the opening 11 Plating is performed, and then, when the rotating belts 10 and 10 are separated from each other at the rotation position of the rotating belts 10 and 10, they are separated as partially plated thin metal strips.

つぎに、本発明に係る連続部分めっき方法について説明する。
駆動手段によって循環走行する部分めっき用の回転ベルト１０，１０の間に、金属薄板条（被めっき物）５を、当該回転ベルト１０，１０に備えられたマグネット磁力によってほぼ密着、挟持した状態を維持したまま入口からめっき槽内に送り込み、めっき液が噴射される。この時、回転ベルトには開口（孔付き加工）１１が施されており、必要に応じて、部分めっき用回転ベルトの金属薄板条側表面に凸部（堤防）が形成されておりこの凸部（堤防）で囲まれた領域に開口が連通するように形成するので、回転ベルト１０でマスクされていないめっき域にのみにめっき液を噴射供給することになるから、めっき領域を特定して部分めっきすることができる。 Next, the continuous partial plating method according to the present invention will be described.
Between the rotating belts 10 and 10 for partial plating that circulates by the drive means, a state in which the thin metal strip (to-be-plated object) 5 is substantially adhered and sandwiched by the magnet magnetic force provided in the rotating belts 10 and 10. While maintaining, it is fed into the plating tank from the inlet, and the plating solution is sprayed. At this time, the rotating belt is provided with an opening (processing with a hole) 11, and if necessary, a convex portion (embankment) is formed on the surface of the rotating belt for partial plating on the metal sheet strip side. Since the opening is formed so as to communicate with the region surrounded by (the dike), the plating solution is sprayed and supplied only to the plating region that is not masked by the rotating belt 10, so that the plating region is specified and partially Can be plated.

部分めっき用回転ベルト１０の走行方向は水平方向であっても垂直方向であっても構わないが、被めっき物５の両面に対して部分めっきを行う場合には、回転ベルト１０を垂直方向に走行させると両面を均一にめっきできる。また、金属薄板条５の板厚が極めて薄い場合、回転ベルト１０を水平方向に走行させると、安定した製品を得ることができるから好ましい。 The traveling direction of the rotating belt 10 for partial plating may be a horizontal direction or a vertical direction. However, when performing partial plating on both surfaces of the object 5 to be plated, the rotating belt 10 is set in the vertical direction. When run, both sides can be plated uniformly. Moreover, when the plate | board thickness of the metal thin strip 5 is very thin, since the stable product can be obtained when the rotating belt 10 is made to drive in a horizontal direction, it is preferable.

なお、上記部分めっき用の回転ベルト１０は、部分めっきの種類によって、つぎの（ア）乃至（ウ）のように組み合わせて使用すると好適であるので、以下、この点について説明する。。
（ア）エッジめっきの場合は、上記平ベルト同士の組合せ、
（イ）ストライブめっきの場合は、上記平ベルトと上記磁性金属薄板ベルトとの組合せ、
（ウ）スポットめっきの場合は、上記孔付加工した平ベルト同士の組合せ。 The rotating belt 10 for partial plating is preferably used in combination as shown in the following (a) to (c) depending on the type of partial plating. This will be described below. .
(A) In the case of edge plating, a combination of the above flat belts,
(B) In the case of stripe plating, a combination of the flat belt and the magnetic metal sheet belt,
(C) In the case of spot plating, a combination of flat belts with holes.

上記（ア）に係る一対の回転ベルト１０ａはともに、軟質のベーステープ１７上に、マスキング用磁性体シート１５が裏から支えられ、エンドレスの平ベルト状に構成されたものであり、これら対の回転ベルト１０ａ，１０ａの間に、エッジめっきする金属薄板条５の上端部もしくは下端部の一方またはその両方が、回転ベルト１０ａ，１０ａによってマスクされていない状態に密着、狭持され、そのままの状態で搬送され、めっき部分に向けてめっき液が吹き付けられ、前記被めっき物（金属薄板条）５の上端部もしくは下端部の一方またはその両方に電気めっきを施すめっきを施すようになっている（図３参照）。 Each of the pair of rotating belts 10a according to (a) above is configured in the shape of an endless flat belt on which a magnetic base sheet 15 for masking is supported from the back on a soft base tape 17. Between the rotating belts 10a and 10a, one or both of the upper end portion and the lower end portion of the thin metal strip 5 to be edge-plated are in close contact with each other and are not masked by the rotating belts 10a and 10a. The plating solution is sprayed toward the plating portion, and plating for applying electroplating to one or both of the upper end portion and the lower end portion of the object (metal thin strip) 5 is performed ( (See FIG. 3).

つぎに、上記（イ）記載のストライブめっき法をより具体的に説明する。図４は、好適なストライブめっきをする時の状態を説明するため、模式的に示す要部斜視図である。 Next, the strip plating method described in (a) above will be described more specifically. FIG. 4 is a perspective view schematically showing a main part for explaining a state when suitable stripe plating is performed.

上記（イ）に係る回転ベルト１０の一方は、軟質のベーステープ上にマスキング用磁性体シートの複数が裏から支えられエンドレスの平ベルト状に構成された回転ベルト１０ａでおり、他方の回転ベルトは、被めっき物（金属薄板条）の長手方向に、軟質エラストマー被膜層を備えたエンドレス磁性金属薄板ｃ’の複数を、所望するめっきストライブ幅で離間させることによって磁性金属薄板ベルト１０ｃとして形成されたものである。すなわち、、平ベルト状に構成されたエンドレス回転ベルトの磁力によって被めっき物（金属薄板条）５の磁着面側（非めっき面側）を密着させ、被めっき物（金属薄板条）５のめっき面側に、上記磁性金属薄板条１０ｃ’の複数を所望するめっきストライブ幅で離間させた状態に磁着させ、両者間に被めっき物（金属薄板条）５を密着、挟持した状態のまま搬送して、上記と同様に部分めっき処理するようになっている。すなわち、磁性金属薄板条１０ｃ’間の離間させた位置に、所望するめっき幅をもったストライブめっき（部分めっき）を施すｒことができる。なお、この場合、めっき装置のめっき槽出入口近傍に、図１に仮想線で示すマグネットリング内蔵ローラ３’を配し、磁性金属薄板条１０ｃ’の配設位置および離間幅を正確かつ精密に管理できるように構成されるので、フラッシュ（にじみ）のない繊細な部分ストライブめっきをすることができるのである。 One of the rotating belts 10 according to the above (a) is a rotating belt 10a that is configured as an endless flat belt supported by a plurality of masking magnetic sheets on a soft base tape, and the other rotating belt. Is formed as a magnetic metal sheet belt 10c by separating a plurality of endless magnetic metal sheets c 'having a soft elastomer coating layer in a longitudinal direction of an object to be plated (metal sheet strip) with a desired plating stripe width. It has been done. That is, the magnetized surface side (non-plated surface side) of the object to be plated (metal thin sheet strip) 5 is brought into close contact by the magnetic force of the endless rotating belt configured in a flat belt shape, and the object to be plated (metal thin sheet strip) 5 A plurality of the magnetic metal thin strips 10c ′ are magnetically attached to the plating surface side so as to be separated by a desired plating stripe width, and an object to be plated (metal thin strip) 5 is in close contact and sandwiched therebetween. It is conveyed as it is, and the partial plating treatment is performed in the same manner as described above. That is, stripe plating (partial plating) having a desired plating width can be performed at a position spaced apart between the magnetic metal thin strips 10c '. In this case, a magnet ring built-in roller 3 ′ shown by a phantom line in FIG. 1 is disposed in the vicinity of the plating tank entrance / exit of the plating apparatus, and the arrangement position and separation width of the magnetic metal sheet strip 10c ′ are managed accurately and precisely. Since it is configured so that it can be performed, it is possible to perform delicate partial stripe plating without flash.

つぎに、上記（ウ）記載のスポットめっき法について、非めっき部分としてアイランドを有する部分めっきを具体例として説明する。図５（ａ）は、部分めっきする時の様子を説明するために模式的に示す要部分解斜視図であり、図５（ｂ）は、図５（ａ）のＡ−Ａ線に沿った断面図である。 Next, the spot plating method described in the above (c) will be described by taking a partial plating having an island as a non-plating portion as a specific example. FIG. 5A is an exploded perspective view schematically showing an essential part for explaining a state when partial plating is performed, and FIG. 5B is taken along line AA in FIG. It is sectional drawing.

回転ベルトの一方は、軟質のベーステープ上にマスキング用磁性体シート複数の裏側を支えるエンドレスの平ベルト状に形成された回転ベルト１０ａであり、他方の回転ベルトは、マスキング用磁性体シート１５とベーステープ１７間に、被めっき部分を形成する孔（開口１１）よりも大経のアイランド用マスク（メッシュのベーステープ）１８を介在させアイランドを形成するマスキング用磁性体部分１５’を備えた平ベルト状のエンドレス回転ベルト１０ｄであり（図５（ｂ）参照）、両回転ベルト１０ａ，１０ｄの間に被めっき物５を磁力によって密着、狭持した状態のまま搬送して、上記と同様に部分めっき処理するようになっている。 One of the rotating belts is an endless flat belt 10a formed on a soft base tape that supports a plurality of masking magnetic sheets, and the other rotating belt includes a masking magnetic sheet 15 and a rotating belt 10a. A flat plate having a masking magnetic part 15 'for forming islands with a mask (mesh base tape) 18 that is larger than a hole (opening 11) for forming a portion to be plated interposed between the base tapes 17. It is a belt-like endless rotating belt 10d (see FIG. 5 (b)), and the object to be plated 5 is conveyed between the rotating belts 10a and 10d while being in close contact with each other by magnetic force. Partial plating is applied.

すなわち、アイランドを形成するマスキング用磁性体部分１５’がアイランド用マスク（メッシュのベーステープ）上に固定されているため、この部分のみがアイランド状の被めっき部分となるのである。 That is, since the masking magnetic part 15 ′ for forming the island is fixed on the island mask (mesh base tape), only this part becomes an island-like plated part.

つぎに、所定形状の繰り返し形状に加工された被めっき物（略金属薄板条）に対して、部分めっきを施す他のめっき方法について、図６を参照しながら説明する。
図６（ａ）は、このめっき方法を実施するための回転ベルト１０ａ，１０ｄなどを模式的に示す要部分解斜視図であり、図６（ｂ）は、図６（ａ）のＡ−Ａ線に沿った断面図である。 Next, another plating method for performing partial plating on an object to be plated (substantially thin metal strip) processed into a predetermined repeated shape will be described with reference to FIG.
FIG. 6A is an exploded perspective view schematically showing main parts of the rotating belts 10a, 10d and the like for carrying out this plating method, and FIG. 6B is an AA view of FIG. 6A. It is sectional drawing along a line.

この方法は、所定形状の繰り返し形状に加工された被めっき物５の一部分に対して部分めっきを施すものであり、回転ベルトの一方は、ベーステープ上にマスキング用磁性体シートの複数の裏側を支えるエンドレス平ベルト状に形成された回転ベルト１０ａであり、他方は、マスキング用磁性体シート１３のエラストマー被膜層１４に、前記被めっき物５の繰り返し形状に対応する凹部１４’が形成されており、凹部１４’にめっき領域に対応する孔加工（開口１１）が施されている回転ベルトｅであり、必要に応じて図示しない位置決め部を介して位置決めして凹部１４’内に嵌合させ，両回転ベルト１０ａ，１０ｅ間に磁力によつて密着、挟持した状態のまま搬送して、上記と同様に部分めっき処理するようになっているものである。 In this method, partial plating is performed on a part of an object to be plated 5 that has been processed into a repetitive shape of a predetermined shape, and one of the rotating belts has a plurality of back sides of the masking magnetic sheet on the base tape. The rotating belt 10a is formed in the shape of a supporting endless flat belt, and the other is formed with a recess 14 'corresponding to the repeated shape of the object 5 to be plated on the elastomer coating layer 14 of the masking magnetic sheet 13. , The rotating belt e in which the hole 14 (opening 11) corresponding to the plating region is provided in the concave portion 14 ′, is positioned via a positioning portion (not shown) as necessary, and is fitted in the concave portion 14 ′. The two belts 10a and 10e are conveyed while being in close contact and sandwiched by magnetic force, and are subjected to partial plating in the same manner as described above.

すなわち、所定形状の繰り返し形状に加工された部分のうち、開口を介してめっき液を噴射供給できる部分にのみ連続的に部分めっきを施すことができるのである。なお、この場合にも、上述したアイランド形成用の回転ベルトと同様に構成できることは無論である。 That is, partial plating can be continuously performed only on a portion where the plating solution can be sprayed and supplied through the opening among the portions processed into a predetermined shape. In this case, it is needless to say that the configuration can be the same as the above-described island forming rotary belt.

以上、本発明に係る連続部分めっき装置、本発明に係る連続部分めっき方法、および、本発明に係る連続部分めっき用回転ベルトについて説明したが、これらはその一例として説明されているに過ぎず、とりわけ連続部分めっき用の回転ベルトを自在設計することができ、そして、当該回転ベルトの組合せもまた自在設計できるため、本発明に係る連続部分めっき方法および連続部分めっき装置もまた自在に設計できるなど、本発明要旨の範囲内において様々に設計変更することができるものとする。 As described above, the continuous partial plating apparatus according to the present invention, the continuous partial plating method according to the present invention, and the continuous partial plating rotary belt according to the present invention have been described, but these are only described as an example, In particular, a rotating belt for continuous partial plating can be freely designed, and the combination of the rotating belts can also be freely designed. Therefore, the continuous partial plating method and continuous partial plating apparatus according to the present invention can also be designed freely. Various design changes can be made within the scope of the present invention.

図１は、本発明の一実施例となる連続部分めっき装置を説明するために概略的に示す平面図である。なお、図中に仮想線で図示したローラはマグネットリング内蔵ローラである。FIG. 1 is a plan view schematically showing a continuous partial plating apparatus according to an embodiment of the present invention. In addition, the roller shown with the phantom line in the figure is a magnet ring built-in roller. 図２（ａ）は、回転ベルトの代表的な一使用状態を模式的に示す斜視図であり、図２（ｂ）は、図２（ａ）のＡ−Ａ線に沿った断面図である。なお、図面中、塗りつぶした部分が部分めっきされる領域であり、また、各部材の厚さなどは、理解を容易にするため誇張して図示されている。以下の図面も同様である。FIG. 2A is a perspective view schematically showing a typical use state of the rotating belt, and FIG. 2B is a cross-sectional view taken along the line AA in FIG. . In the drawings, the painted portion is a region to be partially plated, and the thickness of each member is exaggerated for easy understanding. The same applies to the following drawings. 図３は、金属薄板条の上端部のみを部分めっきする時の状態を説明するために模式的に示す要部斜視図である。FIG. 3 is a main part perspective view schematically illustrating a state when only the upper end portion of the thin metal strip is partially plated. 図４（ａ）は、ストライブめっきする時の一状態を説明するために模式的に示す要部斜視図である。なお、このストライブめっき法を実施する際には、図１に仮想線で図示したマグネットリング内蔵ローラを有する連続部分めっき装置が使用される。FIG. 4A is a main part perspective view schematically illustrating one state when stripe plating is performed. In carrying out this stripe plating method, a continuous partial plating apparatus having a magnet ring built-in roller shown in phantom lines in FIG. 1 is used. 図５（ａ）は、部分めっきする時の様子を説明するために模式的に示す要部分解斜視図であり、図５（ｂ）は、図５（ａ）のＡ−Ａ線に沿った断面図である。FIG. 5A is an exploded perspective view schematically showing an essential part for explaining a state when partial plating is performed, and FIG. 5B is taken along line AA in FIG. It is sectional drawing. 図６（ａ）は、他の部分めっき方法を実施するために使用する回転ベルトを模式的に示す要部分解斜視図であり、図６（ｂ）は図６（ａ）のＡ−Ａ断面に沿った断面図である。FIG. 6A is an exploded perspective view schematically showing a main part of a rotating belt used for carrying out another partial plating method, and FIG. 6B is a cross-sectional view taken along line AA in FIG. FIG.

符号の説明Explanation of symbols

１ … 連続部分めっき装置
３ … 駆動ローラ（駆動手段）
３’… マグネットリング内蔵ローラ
５ … 被めっき物（金属薄板条）
１０ … 回転ベルト
１０ａ… 回転ベルト
１０ｂ… 回転ベルト
１０ｃ… 磁性金属薄板ベルト
１０ｃ’… 磁性金属薄板条
１０ｄ… 回転ベルト
１０ｅ… 回転ベルト
１１ … 開口
１３ … マグネットシート
１４ … 軟質エラストマー被膜層
１４’… 凹部
１５ … マスキング用磁性体シート
１５’… マスキング用磁性体シート
１７ … 軟質のベーステープ
１７ａ… アイランド用マスク（メッシュのベーステープ
１８ … アイランド用マスク（メッシュのベーステープ） DESCRIPTION OF SYMBOLS 1 ... Continuous partial plating apparatus 3 ... Drive roller (drive means)
3 '... Roller with built-in magnet ring 5 ... Material to be plated (metal thin strip)
DESCRIPTION OF SYMBOLS 10 ... Rotating belt 10a ... Rotating belt 10b ... Rotating belt 10c ... Magnetic metal thin plate belt 10c '... Magnetic metal thin plate strip 10d ... Rotating belt 10e ... Rotating belt 11 ... Opening 13 ... Magnet sheet 14 ... Soft elastomer coating layer 14' ... Concave DESCRIPTION OF SYMBOLS 15 ... Masking magnetic sheet 15 '... Masking magnetic sheet 17 ... Soft base tape 17a ... Island mask (mesh base tape 18 ... Island mask (mesh base tape)

Claims

合成樹脂をバインダーに用いて磁気粉末を配向分散して形成されたマグネットシートに軟質エラストマー被膜層を備えてなるマスキング用磁性体シートを、ベーステープ上に接着してエンドレスの部分めっき用回転ベルトを構成し、所定のマイナス電位が付加された金属薄板条を前記部分めっき用回転ベルトの磁力によって当該部分めっき用回転ベルト間に挟んだ状態を維持したまま搬送させながら、当該金属薄板条表面のうち前記部分めっき用回転ベルトで覆われていない部分に対して部分めっきを施すことを特徴とする連続部分めっき方法。 A magnetic sheet for masking comprising a soft elastomer coating layer is bonded to a magnetic sheet formed by orienting and dispersing magnetic powder using a synthetic resin as a binder, and a rotating belt for endless partial plating is bonded to the base tape. The sheet metal strips to which a predetermined negative potential is applied are conveyed while maintaining the state sandwiched between the partial plating rotary belts by the magnetic force of the partial plating rotary belts. A continuous partial plating method, wherein partial plating is performed on a portion that is not covered with the partial plating rotary belt.

前記部分めっき用回転ベルトが、前記軟質エラストマー被膜層の磁着面側に所望する所定形状の凹凸形状が形成された平ベルト、孔付加工された平ベルト、または、前記軟質エラストマー被膜層の磁着面側に所望する所定形状の凹凸形状が形成されかつ孔付加工された平ベルトのうちのいずれかであることを特徴とする請求項１に記載の連続部分めっき方法。 The rotating belt for partial plating is a flat belt having an irregular shape of a predetermined shape formed on the magnetic adhesion surface side of the soft elastomer coating layer, a flat belt with holes, or a magnetic belt of the soft elastomer coating layer. 2. The continuous partial plating method according to claim 1, wherein the continuous partial plating method is any one of flat belts in which a desired uneven shape is formed on the wearing surface side and is processed with holes.

前記部分めっき用回転ベルトの一方が、エラストマー被膜層を備えた磁性金属薄板ベルト、または、エラストマー被膜層を備え磁着面側に所望する所定形状の凹凸形状が形成された磁性金属薄板ベルトであることを特徴とする請求項１または２記載の連続部分めっき方法。 One of the rotating belts for partial plating is a magnetic metal thin plate belt provided with an elastomer coating layer, or a magnetic metal thin plate belt provided with an elastomer coating layer and having a desired irregular shape formed on the side of the magnetized surface. The continuous partial plating method according to claim 1, wherein the method is a continuous partial plating method.

合成樹脂をバインダーに用いて磁気粉末を配向分散して形成されたマグネットシートに軟質エラストマー被膜層を備えてなるマスキング用磁性体シートを、ベーステープ上に接着してエンドレスに形成された部分めっき用回転ベルトと、該部分めっき用回転ベルトを連続的に走行させる駆動手段とを有し、前記部分めっき用回転ベルトの間に、所定のマイナス電位が付加された金属薄板条を前記部分めっき用回転ベルトの磁力によって当該部分めっき用回転ベルト間に挟んだ状態を維持したままめっき槽またはスパジャに搬送、通過させながら、当該金属薄板条表面のうち前記部分めっき用回転ベルトで覆われていない部分に対して連続部分めっきを施す連続部分めっき装置であって、
前記部分めっき用回転ベルトが、平ベルト同士の対、平ベルトと孔付加工された平ベルトとの組、孔付加工された平ベルト同士の対、または、平ベルトもしくは孔付加工された平ベルトとエラストマー被膜層を備えた磁性金属薄板ベルトとの組のうちのいずれかであることを特徴とする連続部分めっき装置。 For partial plating that is formed endlessly by adhering a magnetic sheet for masking comprising a soft elastomer coating layer to a magnetic sheet formed by orienting and dispersing magnetic powder using a synthetic resin as a binder, on a base tape A rotating belt and a driving means for continuously driving the rotating belt for partial plating, and rotating a thin metal strip to which a predetermined negative potential is applied between the rotating belts for partial plating. While being transported and passed to the plating tank or spudger while maintaining the state sandwiched between the partial plating rotary belts by the magnetic force of the belt, on the portion of the surface of the thin metal strip not covered with the partial plating rotary belt A continuous partial plating apparatus that applies continuous partial plating to
The rotating belt for partial plating is a pair of flat belts, a pair of flat belts and flat belts with holes, a pair of flat belts with holes, or a flat belt or flat holes with holes. A continuous partial plating apparatus which is one of a set of a belt and a magnetic metal thin plate belt provided with an elastomer coating layer.

前記部分めっき用回転ベルトの一方が、エラストマー被膜層を備えた磁性金属薄板ベルト、または、エラストマー被膜層を備え磁着面側に所望する所定形状の凹凸形状が形成された磁性金属薄板ベルトであることを特徴とする請求項４記載の連続部分めっき装置。 One of the rotating belts for partial plating is a magnetic metal thin plate belt provided with an elastomer coating layer, or a magnetic metal thin plate belt provided with an elastomer coating layer and having a desired irregular shape formed on the side of the magnetized surface. The continuous partial plating apparatus according to claim 4.

合成樹脂をバインダーに用いて磁気粉末を配向分散して形成されたマグネットシート上に軟質エラストマー被膜層を備えたマスキング用磁性体シートと、該マスキング用磁性体シートの複数をシームレスに接着するとともに全体をエンドレスに形成するためのベーステープとを具備しており、
前記軟質エラストマー被膜層の磁着面側に所望する所定形状の凹凸形状が形成された平ベルト、孔付加工された平ベルト、または、前記軟質エラストマー被膜層の磁着面側に所望する所定形状の凹凸形状が形成されかつ孔付加工された平ベルトのうちのいずれかに形成されていることを特徴とする部分めっき用回転ベルト。 A masking magnetic sheet provided with a soft elastomer coating layer on a magnetic sheet formed by orienting and dispersing magnetic powder using a synthetic resin as a binder, and a plurality of the masking magnetic sheets are seamlessly bonded together. And a base tape for forming the endlessly,
A flat belt having a desired irregular shape formed on the magnetized surface side of the soft elastomer coating layer, a flat belt that has been perforated, or a desired shape desired on the magnetized surface side of the soft elastomer coating layer A rotating belt for partial plating, characterized in that it is formed on any one of flat belts having a concavo-convex shape and having holes.