JP2008023409A - Coating film - Google Patents
Coating film Download PDFInfo
- Publication number
- JP2008023409A JP2008023409A JP2006195427A JP2006195427A JP2008023409A JP 2008023409 A JP2008023409 A JP 2008023409A JP 2006195427 A JP2006195427 A JP 2006195427A JP 2006195427 A JP2006195427 A JP 2006195427A JP 2008023409 A JP2008023409 A JP 2008023409A
- Authority
- JP
- Japan
- Prior art keywords
- coating film
- transparent
- paint
- material layer
- glitter material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、塗膜に係り、更に詳細には、光輝材と構造発色繊維から成る透明光輝材とを含有し、緻密感を向上させ得る塗膜に関する。 The present invention relates to a coating film, and more particularly to a coating film that contains a glittering material and a transparent glittering material composed of structural coloring fibers, and can improve a dense feeling.
従来から、光輝材を含有する塗料を塗装する場合には、塗装条件や塗装環境の影響により、光輝材の配向性を確保することが非常に困難であった。
そこで、光輝材の配向性を向上させるために、セルロースアセテートブチレートなどの繊維素樹脂や高分子のアクリル樹脂などを適用することが提案されている（特許文献１参照。）。
Therefore, in order to improve the orientation of the glittering material, it has been proposed to apply a fiber resin such as cellulose acetate butyrate or a polymer acrylic resin (see Patent Document 1).
しかしながら、上記特許文献１に記載の塗料を用いた塗膜では、十分な緻密感を有する塗膜が作製できないという問題点があった。 However, the coating film using the paint described in Patent Document 1 has a problem in that a coating film having a sufficiently dense feeling cannot be produced.
本発明は、このような従来技術の有する課題に鑑みてなされたものであり、その目的とするところは、緻密感を向上させ得る塗膜を提供することにある。 This invention is made | formed in view of the subject which such a prior art has, and the place made into the objective is to provide the coating film which can improve a dense feeling.
本発明者らは、上記目的を達成すべく鋭意検討を重ねたところ、構造発色繊維から成る透明光輝材を塗膜に含有させることなどにより、上記目的が達成できることを見出し、本発明を完成するに至った。 The inventors of the present invention have made extensive studies in order to achieve the above object, and as a result, found that the above object can be achieved by including a transparent glittering material composed of a structural coloring fiber in the coating film, thereby completing the present invention. It came to.
即ち、本発明の塗膜は、光輝材と、構造発色繊維から成る透明光輝材と、を含有して成り、当該塗膜が淡彩色であることを特徴とする。 That is, the coating film of the present invention comprises a glittering material and a transparent glittering material composed of structural coloring fibers, and the coating film is lightly colored.
また、本発明の塗膜の好適形態は、光輝材を含有して成り、淡彩色である光輝材層と、該光輝材層より表面側に配設され、構造発色繊維から成る透明光輝材を含有して成る透明光輝材層と、を少なくとも備えることを特徴とする。 Further, the preferred form of the coating film of the present invention comprises a glittering material, comprising a glittering material layer that is lightly colored, and a transparent glittering material that is disposed on the surface side of the glittering material layer and is composed of structural coloring fibers. And a transparent glittering material layer containing it.
本発明によれば、構造発色繊維から成る透明光輝材を塗膜に含有させることなどとしたため、緻密感を向上させ得る塗膜を提供することができる。 According to the present invention, since a transparent glittering material composed of structural coloring fibers is included in the coating film, it is possible to provide a coating film that can improve the denseness.
以下、本発明の塗膜について詳細に説明する。なお、本明細書及び特許請求の範囲において、濃度及び含有量などについての「％」は、特記しない限り質量百分率を表わすものとする。
上述の如く、本発明の塗膜は、光輝材と、構造発色繊維から成る透明光輝材とを含有して成り、当該塗膜が淡彩色であるものである。
このような構成とすることにより、光輝材の表面の乱反射に起因する黒味を構造発色繊維から成る透明光輝材の発色によって低減することができ、緻密感が優れたもの、換言すればメタリック感やパール感が優れたものとなる。
なお、一般的に、「淡彩色」とはＬａｂ測色系において明度を示すＬ値が３０以上であり且つ彩度を示すｃ（＝（ａ２＋ｂ２）１／２）値が５以上である色をいう。
Hereinafter, the coating film of the present invention will be described in detail. In the present specification and claims, “%” for concentration, content, and the like represents a mass percentage unless otherwise specified.
As described above, the coating film of the present invention contains a glittering material and a transparent glittering material composed of structural coloring fibers, and the coating film is lightly colored.
By adopting such a configuration, the blackness caused by the irregular reflection on the surface of the glittering material can be reduced by the color development of the transparent glittering material made of structural coloring fibers, in other words, it has excellent denseness, in other words, metallic feeling. And pearly feeling is excellent.
In general, “light color” means that an L value indicating brightness is 30 or more and a c (= (a 2 + b 2 ) 1/2 ) value indicating saturation is 5 or more in the Lab colorimetry system. A certain color.
また、本発明においては、例えば光輝材を含有して成り、淡彩色である光輝材層と、その光輝材層より表面側に配設され、構造発色繊維から透明光輝材を含有して成る透明光輝材層とを少なくとも備える塗膜とすることができる。
このような構成とすることにより、光輝材の表面の乱反射に起因する黒味を構造発色繊維から成る透明光輝材の発色によって、より低減することができ、より緻密感が優れたものとなる。
なお、例えば、上述したような光輝材層と透明光輝材層とから成る積層構造であってもよく、光輝材層と透明光輝材層との間に例えばクリヤー層や淡い色の層を配設して成る積層構造であってもよい。また、これらの積層構造の上にクリヤー層を配設していてもよく、これらの積層構造の下に下地塗膜を有していてもよく、被塗装物があってもよい。
Further, in the present invention, for example, a bright material layer containing a bright material, a light-colored bright material layer, disposed on the surface side of the bright material layer, and transparent transparent material containing a transparent bright material from a structural coloring fiber. It can be set as the coating film provided with a luster material layer at least.
By setting it as such a structure, the blackness resulting from the irregular reflection of the surface of a luminescent material can be reduced more by the coloring of the transparent luminescent material which consists of a structural coloring fiber, and a more dense feeling is excellent.
In addition, for example, a laminated structure composed of the above-mentioned glitter material layer and transparent glitter material layer may be used, and for example, a clear layer or a light color layer is disposed between the glitter material layer and the transparent glitter material layer. It may be a laminated structure. In addition, a clear layer may be disposed on these laminated structures, a base coating film may be provided under these laminated structures, and an object to be coated may be present.
更に、本発明においては、例えば上述したような光輝材層が、透明光輝材を更に含有していてもよい。なお、透明光輝材層は、本発明の効果を奏し得る範囲において光輝材を含有していてもよい。この場合には、例えば透明光輝材層の表面側において、光輝材の濃度を低くすることがよい。 Further, in the present invention, for example, the above-described glittering material layer may further contain a transparent glittering material. The transparent glittering material layer may contain a glittering material as long as the effects of the present invention can be achieved. In this case, for example, the concentration of the glittering material is preferably lowered on the surface side of the transparent glittering material layer.
また、本発明に用いる透明光輝材は、屈折率の異なる少なくとも２種類のポリマーを交互に積層した構造を有し、その積層構造によって得られる光の反射干渉作用による干渉光と干渉光以外の透過光とを制御するものであり、且つ少なくとも入射光源スペクトルが透明光輝材により反射干渉して発色する干渉色と、透明光輝材を透過した光源スペクトルが上述した光輝材層と作用して発色する物体色と、入射光源スペクトルが直接的に上述した光輝材層と作用して発色する物体色とが混在することにより色相変化をもたらす発色機構を備えているものであることが望ましい。
このような透明光輝材を用いると、光輝材の表面の乱反射に起因する黒味を構造発色繊維から成る透明光輝材の発色によって、更に低減することができ、更に緻密感が優れたものとなる。
Further, the transparent glitter material used in the present invention has a structure in which at least two types of polymers having different refractive indexes are alternately laminated, and interference light caused by reflection interference action of light obtained by the laminated structure and transmission other than the interference light. An object that controls light and at least an incident light source spectrum is reflected and interfered by a transparent glittering material, and an colored object that is colored by the light source spectrum transmitted through the transparent glittering material acts on the aforementioned glittering material layer It is desirable to have a coloring mechanism that causes a hue change by mixing a color and an object color that is colored by the incident light source spectrum directly acting on the above-described glittering material layer.
When such a transparent glittering material is used, the blackness caused by the irregular reflection on the surface of the glittering material can be further reduced by the color development of the transparent glittering material composed of the structural coloring fiber, and the fineness is further improved. .
更に、上述した透明光輝材としては、例えば略矩形断面を有し、その断面における積層面に垂直な辺の長さを１とするとき、積層面に平行な辺の長さが０．８〜２５であると共に、その透明光輝材の長さが０．８〜２５０であるものを適用することが好ましい。
積層面に平行な辺の長さが０．８未満の場合には発色効果が低下し、２５超の場合には透明光輝材が塗膜表面より突き出ることにより外観性が低下することがある。また、透明光輝材の長さが０．８未満の場合には発色効果低下し、２５０超の場合には透明光輝材が塗膜表面より突き出ることにより外観性が低下することがある。
例えば、透明光輝材の積層面に平行な辺の長さが５０〜６０μｍであり、透明光輝材の長さが７５μｍのものを好適に用いることができる。
Furthermore, as the above-mentioned transparent glittering material, for example, it has a substantially rectangular cross section, and when the length of the side perpendicular to the laminated surface in the cross section is 1, the length of the side parallel to the laminated surface is 0.8 to In addition, it is preferable to apply the transparent glittering material having a length of 0.8 to 250.
When the length of the side parallel to the laminated surface is less than 0.8, the coloring effect is lowered, and when it is more than 25, the transparent glittering material protrudes from the surface of the coating film and the appearance may be lowered. Further, when the length of the transparent glitter material is less than 0.8, the coloring effect is lowered, and when it is more than 250, the appearance of the transparent glitter material may be lowered due to protrusion of the transparent glitter material.
For example, the length of the side parallel to the laminated surface of the transparent glitter material is 50 to 60 μm, and the length of the transparent glitter material is 75 μm can be suitably used.
上述した構造発色繊維を構成するポリマーとしては、例えばポリエステル、ポリアクリロニトリル、ポリスチレン、ナイロン、ポリプロピレン、ポリビニルアルコール、ポリカーボネート、ポリエチレンナフタレート、ポリエチレンテレフタレート、ポリメタクリル酸メチル、ポリエーテルエーテルケトン、ポリパラフェニレンテレフタルアミド、ポリフェニレンサルファイドなどの単体樹脂、又はこれらの共重合体樹脂、更には各種液晶ポリマー樹脂などを用いることができ、これらの中から屈折率の異なる２種類のポリマーを適宜選択して使用することになる。構造発色繊維におけるポリマーの交互積層数としては、特に限定されるものではないが、例えば反射・干渉効果及び製造上の観点から、５層以上、とりわけ１０〜１５０層の範囲が好ましい。なお、３種類以上のポリマーを用いる場合には、これら３種類以上のポリマーの順序を変えることなく所定の順序に繰り返し積層することが必要となる。 Examples of the polymer constituting the structural coloring fiber include polyester, polyacrylonitrile, polystyrene, nylon, polypropylene, polyvinyl alcohol, polycarbonate, polyethylene naphthalate, polyethylene terephthalate, polymethyl methacrylate, polyether ether ketone, and polyparaphenylene terephthalate. A single resin such as amide or polyphenylene sulfide, or a copolymer resin thereof, or various liquid crystal polymer resins can be used, and two types of polymers having different refractive indexes are appropriately selected and used. become. The number of alternating layers of the polymer in the structural color fiber is not particularly limited, but for example, from the viewpoint of reflection / interference effect and production, a range of 5 layers or more, particularly 10 to 150 layers is preferable. When three or more kinds of polymers are used, it is necessary to repeatedly laminate them in a predetermined order without changing the order of these three or more kinds of polymers.
また、上述した構造発色繊維を製造する方法としては、公知の各種薄膜形成法が適用可能であり、例えば真空蒸着や電子ビーム蒸着、イオンプレーティング、分子線エピタキシアルなどの物理蒸着法、キャスティングやスピンコート、プラズマ重合、ラングミュア・ブロジェットなどの方法、又は溶融、湿式、乾式などの各種紡糸法などを用いることができる。これら各種薄膜形成法の中でも特に溶融複合法は紡糸交互積層構造を形成するための特殊な口金を備えた溶融複合紡糸装置を用いることにより、連続して安定且つ生産性良く構造発色繊維を得ることができ、例えば必要に応じて延伸処理を施すことによって、所望の断面寸法とし、所定の長さに切断粉砕して、透明光輝材として使用することができる。 In addition, as a method for producing the above-described structural coloring fiber, various known thin film forming methods can be applied. For example, physical vapor deposition such as vacuum vapor deposition, electron beam vapor deposition, ion plating, molecular beam epitaxy, casting, Methods such as spin coating, plasma polymerization, Langmuir / Blodget, or various spinning methods such as melting, wet, and dry methods can be used. Among these various thin film forming methods, in particular, the melt composite method uses a composite melt spinning apparatus equipped with a special die for forming a spun alternating laminated structure to obtain a structural colored fiber continuously and stably with high productivity. For example, it can be used as a transparent glittering material by subjecting it to a desired cross-sectional dimension by subjecting it to stretching treatment as necessary, cutting and pulverizing it to a predetermined length.
また、本発明においては、例えば上述した透明光輝材層が、透明光輝材を０．１〜３０％含有していることが好ましく、０．１〜１０％含有していることがより好ましく、０．１〜５％含有していることが更に好ましい。
含有量が０．１％未満の場合には、発色効果が十分に発揮されないことがあり、３０％を超える場合には、透明光輝材が塗膜表面より突き出ることにより外観性が低下することがある。
なお、例えば上述した光輝材層が透明光輝材を含有している場合にも、その含有量が０．１〜３０％であることが好ましく、０．１〜１０％であることがより好ましく、０．１〜５％であることが更に好ましい。この場合には、例えば光輝材層の表面側において、透明光輝材の濃度を高くすることがよい。
Moreover, in this invention, it is preferable that the transparent glitter material layer mentioned above contains 0.1-30% of transparent glitter materials, it is more preferable to contain 0.1-10%, for example. More preferably, the content is 1 to 5%.
When the content is less than 0.1%, the coloring effect may not be sufficiently exhibited. When the content exceeds 30%, the appearance may deteriorate due to the transparent glittering material protruding from the coating surface. is there.
In addition, for example, when the above-described glittering material layer contains a transparent glittering material, the content is preferably 0.1 to 30%, more preferably 0.1 to 10%, More preferably, it is 0.1 to 5%. In this case, for example, the concentration of the transparent glitter material is preferably increased on the surface side of the glitter material layer.
更に、本発明に用いる光輝材としては、例えばアルミニウム顔料及びパール顔料を単独で又は組合わせて用いることができる。
なお、上述したパール顔料として着色したパール顔料を用いることもできる。また、上述したアルミニウム顔料として着色したアルミニウム顔料を用いることもできる。但し、意匠性を考慮すると、できる限り淡彩色のものを用いることが好ましい。
Furthermore, as the bright material used in the present invention, for example, an aluminum pigment and a pearl pigment can be used alone or in combination.
In addition, the colored pearl pigment can also be used as the pearl pigment mentioned above. Moreover, the colored aluminum pigment can also be used as the aluminum pigment mentioned above. However, in consideration of design properties, it is preferable to use a pale color as much as possible.
そして、本発明においては、淡彩色の塗膜のＬ値が５０以上であることが好ましく、６０以上であることがより好ましく、８０以上であることが更に好ましい。５０未満の場合には、透明光輝材の発色により、意匠が変化することがある。 In the present invention, the L value of the light-colored coating film is preferably 50 or more, more preferably 60 or more, and still more preferably 80 or more. If it is less than 50, the design may change due to the color of the transparent glitter material.
更に、本発明においては、塗膜を形成する際に用いる塗料として、塗料の形態について特に限定されるものではなく、溶剤系塗料、水系塗料及び粉体塗料のいずれを用いてもよい。
更にまた、本発明においては、塗膜を形成する際に用いる塗料として、塗料のタイプについて特に限定されるものではなく、メラミン硬化型塗料、ウレタン塗料、酸・エポキシ硬化型塗料、アクリル樹脂塗料、塩化ビニル酢酸ビニル共重合体樹脂塗料及びポリエステル樹脂塗料などのいずれを用いてもよい。
そして、光輝材や透明光輝材を含有する層を形成する場合には、塗装に用いる塗料の希釈率を高くすることが望ましい。希釈率を高くして塗装した場合には、光輝材や透明光輝材の配向性が良くなり易く、外観性がより向上する。
Furthermore, in the present invention, the form of the paint is not particularly limited as the paint used when forming the coating film, and any of solvent-based paint, water-based paint, and powder paint may be used.
Furthermore, in the present invention, the paint used for forming the coating film is not particularly limited with respect to the type of paint, and melamine curable paint, urethane paint, acid / epoxy curable paint, acrylic resin paint, Any of vinyl chloride vinyl acetate copolymer resin paint and polyester resin paint may be used.
And when forming the layer containing a luster material or a transparent luster material, it is desirable to make the dilution rate of the coating material used for coating high. When the coating is performed at a high dilution rate, the orientation of the glittering material or the transparent glittering material tends to be improved, and the appearance is further improved.
ここで、本発明の塗膜を図面に基づいて説明する。
図１は、本発明の塗膜の一実施形態を示す構成図である。同図に示すように、被塗装物の一例である鋼板５０に積層形成された電着塗膜２０と、中塗塗膜３０と、本実施形態の塗膜１０と、クリヤー塗膜４０とが配設されている。そして、本実施形態の塗膜１０は、淡彩色の光輝材層１２と透明光輝材層１４とを備えている。
このような構成とすることにより、光輝材の表面の乱反射に起因する黒味を構造発色繊維から成る透明光輝材の発色によって低減することができ、緻密感が特に優れたものとなる。
なお、図示しないが、他の実施形態として、淡彩色の光輝材と透明光輝材とが混在して含まれる塗膜であっても、緻密感に優れたものとなる。
上記のような塗膜構成は、自動車用のメタリック塗膜やパール塗膜として好適に用いることができる。
Here, the coating film of this invention is demonstrated based on drawing.
FIG. 1 is a block diagram showing an embodiment of the coating film of the present invention. As shown in the figure, an
By setting it as such a structure, the blackness resulting from the irregular reflection of the surface of a luminescent material can be reduced by the color development of the transparent luminescent material which consists of a structural coloring fiber, and a dense feeling becomes especially excellent.
In addition, although not shown in figure, as another embodiment, even if it is a coating film containing the light-colored luster material and the transparent luster material mixedly, it will be excellent in a dense feeling.
The coating composition as described above can be suitably used as a metallic coating film or a pearl coating film for automobiles.
以下、本発明を実施例及び比較例により、更に詳細に説明するが本発明はこれら実施例に限定されるものではない。
具体的には、以下の各例に記載したような操作を行い、塗膜を作製し、評価した。
EXAMPLES Hereinafter, although an Example and a comparative example demonstrate this invention further in detail, this invention is not limited to these Examples.
Specifically, an operation as described in each of the following examples was performed to prepare and evaluate a coating film.
（実施例１）
まず、リン酸亜鉛処理した厚み０．８ｍｍ、７０ｍｍ×１５０ｍｍのダル鋼板に、カチオン電着塗料（日本ペイント社製カチオン型電着塗料、商品名「パワートップＵ６００Ｍ」）を、乾燥膜厚が２０μｍとなるように電着塗装した後、１６０℃で３０分間焼き付けた。
次に、白色の中塗塗料（ＢＡＳＦコーティングス株式会社製、商品名「ハイエピコＮｏ．５００」）を、３０μｍ塗装し、１４０℃で３０分間焼き付けた。
次に、着色塗料（ＢＡＳＦコーティングス株式会社製、ベルコートＮｏ６０１０ホワイト）を、１０μｍ塗装し、ウェットオンウェットで、光輝材含有塗料（ＢＡＳＦコーティングス株式会社製、ベルコートＮｏ６０１０パール）とＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製、ＭＯＲＰＨＯＴＥＸ（幅：８０μｍ））を表１に示すような含有量となるように添加したものを混合し、これを８μｍ塗装し、ウェットオンウェットでクリヤー塗料（ＢＡＳＦコーティングス株式会社製、ベルコートＮｏ６２００）を、３５μｍ塗装し、１４０℃で３０分間焼き付けて、本例の塗膜を得た。
得られた塗膜の明度を示すＬ値は８５であった（以下の実施例及び比較例において同じである。）。
(Example 1)
First, a cation electrodeposition paint (cation type electrodeposition paint manufactured by Nippon Paint Co., Ltd., trade name “Power Top U600M”) is applied to a dull steel sheet having a thickness of 0.8 mm and 70 mm × 150 mm treated with zinc phosphate, and a dry film thickness is 20 μm. After electrodeposition coating so as to be, it was baked at 160 ° C. for 30 minutes.
Next, a white intermediate coating (BASF Coatings, trade name “High Epico No. 500”) was applied by 30 μm and baked at 140 ° C. for 30 minutes.
Next, a colored paint (BASF Coatings Co., Ltd., Bell Coat No 6010 White) was applied at 10 μm, wet-on-wet, and a glittering material-containing paint (BASF Coatings Co., Ltd., Bell Coat No 6010 Pearl) and BASF Coatings. A transparent base of Bell Coat No. 6010 manufactured by Co., Ltd., with a transparent glittering material (Made by Teijin Ltd., MORPHOTEX (width: 80 μm)) added so as to have a content as shown in Table 1 This was mixed, applied with 8 μm, wet-on-wet with a clear paint (BASF Coatings, Bell Coat No 6200) was applied with 35 μm, and baked at 140 ° C. for 30 minutes to obtain a coating film of this example.
L value which shows the brightness of the obtained coating film was 85 (it is the same in a following example and a comparative example).
（実施例２）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を、表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 2)
Except for using a transparent base of Bell Coat No. 6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (made by Teijin Limited) as shown in Table 1 added so as to have a content as shown in Table 1. Repeated the same operation as Example 1, and obtained the coating film of this example.
（実施例３）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 3)
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例４）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
Example 4
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例５）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 5)
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例６）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 6)
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例７）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 7)
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例８）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 8)
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例９）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
Example 9
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例１０）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 10)
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例１１）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 11)
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例１２）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
Example 12
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例１３）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 13)
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（実施例１４）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに表１に示すような透明光輝材（帝人株式会社製）を表１に示すような含有量となるように添加したものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
(Example 14)
Except for using a transparent base of Bell Coat No6010 manufactured by BASF Coatings Co., Ltd. with a transparent glittering material (manufactured by Teijin Ltd.) as shown in Table 1 added to a content as shown in Table 1. The same operation as in Example 1 was repeated to obtain a coating film of this example.
（比較例１）
ＢＡＳＦコーティングス株式会社製のベルコートＮｏ６０１０の透明ベースに透明光輝材を添加しなかったものを用いた以外は、実施例１と同様の操作を繰り返し、本例の塗膜を得た。
上記各例の仕様を表１に示す。なお、長さについては、透明光輝材の断面における積層面に垂直な辺の長さを１としたときの比である。
(Comparative Example 1)
A coating film of this example was obtained by repeating the same operation as in Example 1 except that the transparent base of Bell Coat No 6010 manufactured by BASF Coatings Co., Ltd. was used.
Table 1 shows the specifications of the above examples. In addition, about length, it is a ratio when the length of the side perpendicular | vertical to the lamination surface in the cross section of a transparent luster material is set to 1.
［性能評価］
（緻密感向上効果試験）
緻密感の評価を、粒子感を目視判定することにより評価した。得られた結果を表１に併記する。なお、表１中「◎」は粒子感が全くないこと、「○」は粒子感が殆どないこと、「△」は粒子感が少しあること、「×」は粒子感がかなりあること、を示す。
[Performance evaluation]
(Density improvement test)
The evaluation of denseness was evaluated by visually judging the particle feeling. The obtained results are also shown in Table 1. In Table 1, “◎” indicates that there is no particle feeling, “◯” indicates that there is almost no particle feeling, “Δ” indicates that there is a little particle feeling, and “×” indicates that there is a considerable particle feeling. Show.
表１より、本発明の範囲に属する実施例１〜１４の塗膜は、本発明外の比較例１の塗膜と比較して、優れた緻密感、具体的には優れたパール感を有することが分かる。 From Table 1, the coating films of Examples 1 to 14 belonging to the scope of the present invention have an excellent dense feeling, specifically an excellent pearl feeling, as compared with the coating film of Comparative Example 1 outside the present invention. I understand that.
以上、本発明を若干の実施形態及び実施例によって、説明したが本発明はこれらに限定されるものではなく、本発明の要旨の範囲内で種々の変形が可能である。
例えば、上記の実施形態では、被塗装物として、塗装被膜を有する鋼板を用いたが、これに限定されるものではなく、樹脂材料や金属材料、セラミック材料などに適用することもできる。
As mentioned above, although this invention was demonstrated with some embodiment and an Example, this invention is not limited to these, A various deformation | transformation is possible within the range of the summary of this invention.
For example, in the above embodiment, a steel plate having a coating film is used as an object to be coated. However, the present invention is not limited to this, and can be applied to a resin material, a metal material, a ceramic material, or the like.
１０ 塗膜
１２ 淡彩色の光輝材層
１４ 透明光輝材層
２０ 電着塗膜
３０ 中塗塗膜
４０ クリヤー塗膜
５０ 鋼板
DESCRIPTION OF
Claims (10)
上記塗膜が淡彩色であることを特徴とする塗膜。 A coating film comprising a glittering material and a transparent glittering material composed of structural coloring fibers,
A coating film, wherein the coating film is lightly colored.
上記光輝材層より表面側に配設され、上記構造発色繊維から成る透明光輝材を含有して成る透明光輝材層と、
を少なくとも備えることを特徴とする請求項１に記載の塗膜。 A glitter material layer comprising the glitter material and having a light color;
A transparent glitter material layer disposed on the surface side of the glitter material layer and containing a transparent glitter material composed of the structural coloring fibers;
The coating film according to claim 1, further comprising:
且つ少なくとも入射光源スペクトルが上記透明光輝材により反射干渉して発色する干渉色と、上記透明光輝材を透過した光源スペクトルが上記光輝材層と作用して発色する物体色と、入射光源スペクトルが直接的に上記光輝材層と作用して発色する物体色とが混在することにより色相変化をもたらす発色機構を備えているものである、ことを特徴とする請求項２又は３に記載の塗膜。 The transparent glittering material has a structure in which at least two kinds of polymers having different refractive indexes are alternately laminated, and controls interference light due to reflection interference action of light obtained by the laminated structure and transmitted light other than the interference light. Is,
And an interference color in which at least an incident light source spectrum is colored by reflection interference by the transparent glitter material, an object color in which a light source spectrum transmitted through the transparent glitter material acts on the glitter material layer, and an incident light source spectrum is directly The coating film according to claim 2 or 3, further comprising a coloring mechanism that brings about a hue change by mixing with the glitter material layer and an object color that develops color.