JP2007323092A

JP2007323092A - Protection panel for electronic equipment display window and manufacturing method for protection panel

Info

Publication number: JP2007323092A
Application number: JP2007217398A
Authority: JP
Inventors: Koji Kusuda; 康次楠田; Takao Hashimoto; 孝夫橋本; Jun Shimizu; 潤清水; Shinya Yamada; 真也山田
Original assignee: Nissha Printing Co Ltd
Current assignee: Nissha Printing Co Ltd
Priority date: 2004-02-20
Filing date: 2007-08-23
Publication date: 2007-12-13
Anticipated expiration: 2025-02-17
Also published as: JP4279890B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a low reflectance protection panel with decoration for a display window of electronic equipment, superior in productivity. <P>SOLUTION: A decorating film is laminated on a surface of a transparent protective plate; the decorating film forms at least a window forming layer having a transparent window part on the surface of a hard coating film at the transparent protective plate side and is formed with a low reflectance processed layer on the opposite surface thereof; and a low reflectance processed layer is formed on the rear surface of the transparent protective plate. A decorating film is alternatively laminated on a surface of an optical isotropic transparent protective plate being interposed by a polarizing plate, the decorating film forms at least a window forming layer having a transparent window part on the surface of the hard coating film at the transparent protective plate side. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、電子機器のケーシングの表示窓用開口に嵌め込まれ、前記ケーシングの表示窓用開口の近傍に設けられたディスプレイ装置の表面を保護する電子機器表示窓の保護パネル及び保護パネルの製造方法に関する。 The present invention relates to a protection panel for an electronic device display window that is fitted in a display window opening of a casing of an electronic device and protects the surface of a display device provided in the vicinity of the display window opening of the casing, and a method for manufacturing the protective panel About.

携帯電話機、スマートフォン等の電子機器におけるケーシングは、合成樹脂製の前面ケーシングと背面ケーシングを組み合わせて構成された扁平なものが一般的である。具体的には、前面ケーシングには液晶ディスプレイ装置などを配置する表示窓用開口が設けられており、表示窓の下側に設けられるディスプレイ装置の表面を保護するために保護パネルが融着等により固定されている。 As for the casing in electronic devices, such as a mobile phone and a smart phone, the flat thing comprised combining the front casing and back casing made from a synthetic resin is common. Specifically, the front casing is provided with an opening for a display window in which a liquid crystal display device or the like is arranged, and a protective panel is fused or the like to protect the surface of the display device provided below the display window. It is fixed.

そして、この保護パネルには、従来より様々な工夫が提案されている。例えば、特開２００２−７２２１４号公報には、反射によって明るい室内あるいは屋外では液晶表示が極めて見にくくなるという問題を解決するためにλ／４板と偏光板と透明保護板との組み合わせで保護パネルを構成することが開示されている。また、上記透明保護板をタッチパネルとしたり、ハードコートフィルムや低反射フィルムを貼合するなどして保護パネルの最表面に付加機能を付与したりすることも開示されている。 Various ideas have been proposed for this protective panel. For example, Japanese Patent Laid-Open No. 2002-72214 discloses a protection panel with a combination of a λ / 4 plate, a polarizing plate, and a transparent protective plate in order to solve the problem that the liquid crystal display becomes extremely difficult to see in a bright room or outdoors due to reflection. Configuration is disclosed. It is also disclosed that the transparent protective plate is used as a touch panel or a hard coat film or a low reflection film is bonded to give an additional function to the outermost surface of the protective panel.

また、最近では、電子機器のファッション化に伴い、特開２００１−３１８６１２号公報に開示されているように、印刷にて縁取り等の加飾が上記保護パネルに施されるようになってきている。
特開２００２−７２２１４号公報特開２００１−３１８６１２号公報 Recently, with the trend toward fashion of electronic devices, as described in Japanese Patent Application Laid-Open No. 2001-318612, decorations such as fringing have been applied to the protective panel by printing. .
JP 2002-72214 A JP 2001-318612 A

しかしながら、上記印刷による保護パネルへの加飾は、保護パネルを成形し、成形された保護パネルごとに印刷を行なわなければならないため、生産性の面で不利であるという問題があった。 However, the decoration on the protective panel by the above printing has a problem in that it is disadvantageous in terms of productivity because the protective panel must be molded and printing must be performed for each molded protective panel.

そこで、本発明の目的は、上記の問題点を解決し、生産性に優れた電子機器表示窓の保護パネル及び保護パネルの製造方法を提供することである。 SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to solve the above problems and provide a protective panel for an electronic device display window and a method for manufacturing the protective panel that are excellent in productivity.

上記目的を達成するために、本発明の第１態様によれば、電子機器のケーシングの表示窓用開口部分に設けられたディスプレイ装置の前記表示窓用開口からの露出部分を保護する前記表示窓用開口に嵌め込まれる電子機器表示窓の保護パネルであって、
前記ディスプレイ装置の前記露出部分表面に対向して設けられる透明保護板と、
透明なハードコートフィルムと前記ハードコートフィルムの一方の表面の一部に薄膜状に形成された加飾部を有し前記加飾部が形成されていない部分が前記ディスプレイ装置の前記表示窓用開口からの露出部分を視認可能に構成された透明窓部として形成された窓形成層を備えた加飾フィルムと、
前記窓形成層が透明保護板の表面側に位置するように、前記加飾フィルムを前記透明保護板の前記ディスプレイ装置に対向しない側の表面に積層状態に貼着する透明な貼着層を有する、電子機器表示窓の保護パネルを提供する。 In order to achieve the above object, according to the first aspect of the present invention, the display window for protecting an exposed portion from the display window opening of the display device provided in the display window opening portion of the casing of the electronic device. A protection panel for an electronic device display window fitted in the opening for use,
A transparent protective plate provided opposite to the exposed portion surface of the display device;
The display window opening of the display device has a transparent hard coat film and a decorative portion formed in a thin film on a part of one surface of the hard coat film, and the decorative portion is not formed. A decorative film provided with a window forming layer formed as a transparent window portion configured such that an exposed portion can be visually recognized;
A transparent adhesive layer for adhering the decorative film to the surface of the transparent protective plate on the side not facing the display device so that the window forming layer is located on the surface side of the transparent protective plate; Provide protection panel for electronic device display window.

本発明の第２態様によれば、前記加飾部は、前記加飾フィルムの周縁に印刷層として設けられ、前記透明窓部は前記加飾フィルムの中央部分に形成される、第１態様の電子機器表示窓の保護パネルを提供する。 According to the 2nd aspect of this invention, the said decorating part is provided as a printing layer in the periphery of the said decorating film, and the said transparent window part is formed in the center part of the said decorating film. A protection panel for an electronic device display window is provided.

本発明の第３態様によれば、前記加飾フィルムは、さらに、第１の低反射処理層が設けられている第１態様の電子機器表示窓の保護パネルを提供する。 According to the third aspect of the present invention, the decorative film further provides a protective panel for an electronic device display window according to the first aspect, wherein the first low-reflection treatment layer is provided.

本発明の第４態様によれば、前記第１の低反射処理層は、前記ハードコートフィルムの他方の表面全体に設けられている、第３態様の電子機器表示窓の保護パネルを提供する。 According to a fourth aspect of the present invention, there is provided the electronic device display window protection panel according to the third aspect, wherein the first low reflection treatment layer is provided on the entire other surface of the hard coat film.

本発明の第５態様によれば、前記透明保護板は、光学等方性であり、いずれかの表面に偏光板が設けられている、第１態様の電子機器表示窓の保護パネルを提供する。 According to a fifth aspect of the present invention, there is provided the electronic device display window protective panel according to the first aspect, wherein the transparent protective plate is optically isotropic and a polarizing plate is provided on any surface. .

本発明の第６態様によれば、前記偏光板は、前記透明保護板の前記ディスプレイ装置に対向しない側の表面に設けられている、第５態様の電子機器表示窓の保護パネルを提供する。 According to a sixth aspect of the present invention, there is provided the protective panel for an electronic device display window according to the fifth aspect, wherein the polarizing plate is provided on a surface of the transparent protective plate that is not opposed to the display device.

本発明の第７態様によれば、前記透明保護板は、前記ディスプレイ装置に対向する側の表面に第２の低反射処理層が設けられている第５態様の電子機器表示窓の保護パネルを提供する。 According to a seventh aspect of the present invention, the transparent protective plate is the electronic device display window protective panel according to the fifth aspect in which a second low-reflection treatment layer is provided on the surface facing the display device. provide.

本発明の第８態様によれば、前記第２の低反射処理層は、λ／４板で構成されている、第７態様の電子機器表示窓の保護パネルを提供する。 According to an eighth aspect of the present invention, there is provided the electronic device display window protection panel according to the seventh aspect, wherein the second low reflection treatment layer is composed of a λ / 4 plate.

本発明の第９態様によれば、透明保護板は、前記加飾フィルムと積層された可動電極フィルムと、前記可動電極フィルムとの間に空気層を形成するように周縁部において前記可動電極フィルムと接着された固定電極板と、を備えるタッチパネルで構成されている、第１から第８態様のいずれか１つの電子機器表示窓の保護パネルを提供する。 According to a ninth aspect of the present invention, the transparent protective plate has the movable electrode film at a peripheral portion so as to form an air layer between the movable electrode film laminated with the decorative film and the movable electrode film. A protective panel for an electronic device display window according to any one of the first to eighth aspects, comprising a touch panel provided with a fixed electrode plate bonded to the electronic device.

本発明の第１０態様によれば、電子機器のケーシング表示窓用開口部分に設けられたディスプレイ装置の前記表示窓用開口からの露出部分を保護する前記表示窓用開口に嵌め込まれる電子機器表示窓の保護パネルの製造方法であって、
ハードコートフィルムの一方の表面の一部に薄膜状に形成された加飾部を有する窓形成層を備え、前記加飾部が設けられていない部分が前記ディスプレイ装置の前記表示窓用開口からの露出部分を視認可能に透過させる透明窓部として形成される加飾領域を複数形成して、大判加飾フィルムを作成し、
前記加飾領域よりも大きい面積を有する大判透明保護板に、前記大判加飾フィルムを、前記加飾部が大判透明保護板の表面と対向する方向となるように貼り合わせ、
前記透明窓部の外側位置かつ加飾領域の内側位置において、前記貼り合わされた大判加飾フィルムと前記大判透明保護板を一体的に切断して保護パネルを得る、電子機器表示窓の保護パネルの製造方法を提供する。 According to the tenth aspect of the present invention, the electronic device display window fitted in the display window opening that protects the exposed portion from the display window opening of the display device provided in the casing display window opening portion of the electronic device. A method for manufacturing a protective panel of
A portion of one surface of the hard coat film is provided with a window forming layer having a decorative portion formed in a thin film shape, and a portion where the decorative portion is not provided is from the display window opening of the display device Form a plurality of decorative areas formed as transparent windows that allow the exposed part to be seen through, creating a large decorative film,
The large format decorative protective film having an area larger than the decorative region is bonded to the large format decorative film so that the decorative portion is in a direction facing the surface of the large format transparent protective plate,
A protective panel for an electronic device display window, wherein the laminated large-sized decorative film and the large-sized transparent protective plate are integrally cut to obtain a protective panel at an outer position of the transparent window and an inner position of the decorative region. A manufacturing method is provided.

本発明の電子機器表示窓の保護パネルは、以上のような構成からなるので、次の効果を奏する。 Since the protection panel for an electronic device display window according to the present invention is configured as described above, the following effects can be obtained.

すなわち、本発明の電子機器表示窓の保護パネルは、透明保護板表面に、透明窓部を有する窓形成層がハードコートフィルム裏面にあらかじめ形成されてなる加飾フィルムを積層状態に貼着するものであるから、保護パネル毎に印刷を行なう必要がない。しかも、このように構成すれば、窓形成層の形成対象であるハードコートフィルムに印刷を行なう際に、このフィルムをロール状にして多数個分の柄を連続印刷することが可能となるので、製造時には、これらの大判の加飾フィルムと大判の透明保護板を貼り合わせ、一体的に切断することによって保護パネルの生産性を高めることができる。また、窓形成層はハードコートフィルムと透明保護板の間に配置され、外側に露出していないため経時的使用による加飾部の塗装落ちがない。さらに、加飾部は薄膜として設けられているため、加飾フィルムの表面に凹凸が形成されることがなく、透明保護板に貼着される場合に間に気泡が形成されるなどの問題が生じることがない。 That is, the protection panel for an electronic device display window of the present invention is such that a decorative film in which a window forming layer having a transparent window portion is formed in advance on the back surface of a hard coat film is laminated on the surface of a transparent protective plate. Therefore, it is not necessary to perform printing for each protection panel. Moreover, when configured in this way, when printing on the hard coat film that is the object of forming the window forming layer, it becomes possible to continuously print a large number of patterns in the form of a roll, At the time of manufacture, productivity of a protection panel can be improved by bonding these large decorative films and large transparent protective plates together and cutting them integrally. Moreover, since the window forming layer is disposed between the hard coat film and the transparent protective plate and is not exposed to the outside, there is no paint drop off of the decorative portion due to use over time. Furthermore, since the decorating part is provided as a thin film, there is no problem that irregularities are formed on the surface of the decorative film, and bubbles are formed in the case of being stuck to the transparent protective plate. It does not occur.

本発明の記述を続ける前に、添付図面において同じ部品については同じ参照符号を付している。以下、図面も参照しながら、本発明についてさらに詳細に説明する。 Before continuing the description of the present invention, the same parts are denoted by the same reference numerals in the accompanying drawings. Hereinafter, the present invention will be described in more detail with reference to the drawings.

本発明の電子機器表示窓の保護パネルは、図６に示すように、薄い樹脂製のパネルであり、図７に示すように、電子機器のケーシングの表示窓用開口を被覆するものである。すなわち、前面ケーシング２１には液晶ディスプレイ装置１５などを配置する表示窓用開口２２が設けられており、表示窓用開口２２の下側に設けられるディスプレイ装置１５の表面を保護するために保護パネルが融着等により固定される。 The protective panel for an electronic device display window of the present invention is a thin resin panel as shown in FIG. 6, and covers the display window opening of the casing of the electronic device as shown in FIG. That is, the front casing 21 is provided with a display window opening 22 for arranging the liquid crystal display device 15 and the like, and a protective panel is provided to protect the surface of the display device 15 provided below the display window opening 22. It is fixed by fusion or the like.

電子機器表示窓の保護パネル１は、加飾部分２及び透明窓部分３とが設けられている。保護パネルが電子機器表示窓に配置された場合には、透明窓部分３から保護パネル１の下方に設けられる液晶パネル１５を視認することができる。加飾部分２は、後述するように、保護パネルの周囲に設けられた加飾部を有する窓形成層６を備えた加飾フィルム７によって形成され、加飾部が形成されていない部分が透明窓部分３として形成される。したがって、加飾フィルム７は、保護パネルの全面にわたって設けられていてもよく、保護パネルを形成する透明保護板の表面に窓形成層を有する加飾フィルム７を貼り合わせ、その後透明保護板４と加飾フィルム７とを一体的に切断することにより、作成することができる。 A protective panel 1 for an electronic device display window is provided with a decorative portion 2 and a transparent window portion 3. When the protective panel is disposed in the electronic device display window, the liquid crystal panel 15 provided below the protective panel 1 can be viewed from the transparent window portion 3. As will be described later, the decorative portion 2 is formed by a decorative film 7 including a window forming layer 6 having a decorative portion provided around the protective panel, and a portion where the decorative portion is not formed is transparent. Formed as window portion 3. Therefore, the decorative film 7 may be provided over the entire surface of the protective panel, and the decorative film 7 having a window forming layer is bonded to the surface of the transparent protective plate forming the protective panel, and then the transparent protective plate 4 and It can create by cut | disconnecting the decorating film 7 integrally.

例えば、図８に示すように、加飾部２が設けられている加飾領域２６を複数形成したロール状の加飾フィルム２３を、透明両面テープ２５を用いて大判の透明保護板２４に貼り合わせ、その後、貼り合わされた透明保護板と加飾フィルムとを一体的に切断することにより、作成することができる。貼り合わされた大判の透明保護板２４とロール状の加飾フィルム２３とを一体的に切断する位置は、透明窓部３の外側であって、加飾領域２６の内側であることが好ましい。このように構成することにより、周縁部分まで加飾層２が形成された保護パネルを作成することができる。 For example, as shown in FIG. 8, a roll-shaped decorative film 23 formed with a plurality of decorative regions 26 provided with the decorative portion 2 is attached to a large transparent protective plate 24 using a transparent double-sided tape 25. After that, the transparent protective plate and the decorative film bonded together can be integrally cut and then created. The position at which the large transparent protective plate 24 and the roll-shaped decorative film 23 are integrally cut is preferably outside the transparent window 3 and inside the decorating region 26. By comprising in this way, the protection panel in which the decoration layer 2 was formed to the peripheral part can be created.

図６に示す保護パネルは、透明保護板４と加飾フィルム７の積層構造であり、具体的には、例えば、図１に示すような断面構造を有する。 The protective panel shown in FIG. 6 is a laminated structure of the transparent protective plate 4 and the decorative film 7, and specifically has, for example, a cross-sectional structure as shown in FIG.

図１に示す保護パネル１ａは、透明保護板４の表面に加飾フィルム７が貼着層１０によって積層状態に貼着され、透明保護板４の裏面に第２の低反射処理層１１が形成されている。また、加飾フィルム７は、ハードコートフィルム５の透明保護板４側の面に加飾部２を有する窓形成層６を形成し且つ反対面に第１の低反射処理層１２を形成してなるものである。 In the protective panel 1 a shown in FIG. 1, a decorative film 7 is stuck in a laminated state on the surface of the transparent protective plate 4 by a sticking layer 10, and a second low reflection treatment layer 11 is formed on the back surface of the transparent protective plate 4. Has been. Moreover, the decoration film 7 forms the window formation layer 6 which has the decoration part 2 in the surface at the side of the transparent protective board 4 of the hard coat film 5, and forms the 1st low reflection process layer 12 in the opposite surface. It will be.

なお、第１及び第２の低反射処理層１２，１１は、それぞれ、透明窓部分を通して視認される液晶パネル１５の表示を見やすくするために、光学的に何らかの反射を軽減するものであれば、特にその構成は問わない。 The first and second low-reflection treatment layers 12 and 11 may each be capable of optically reducing some reflection in order to make the display of the liquid crystal panel 15 viewed through the transparent window portion easy to see. The configuration is not particularly limited.

上記透明保護板４としては、透視性に優れ、液晶パネル１５を破損から保護できる材料を用いる。例えば、ポリスチレン系樹脂、ポリオレフィン系樹脂、ＡＢＳ樹脂、ＡＳ樹脂、アクリル系樹脂、ＡＮ樹脂などの汎用樹脂を挙げることができる。また、ポリスチレン系樹脂、ポリカーボネート系樹脂、ポリアセタール系樹脂、ポリカーボネート変性ポリフェニレンエーテル樹脂、ポリブチレンテレフタレート樹脂、超高分子量ポリエチレン樹脂などの汎用エンジニアリング樹脂や、ポリスルホン樹脂、ポリフェニレンサルファイド系樹脂、ポリフェニレンオキシド系樹脂、ポリアリレート樹脂、ポリエーテルイミド樹脂、ポリイミド樹脂、液晶ポリエステル樹脂、ポリアリル系耐熱樹脂などのスーパーエンジニアリング樹脂を用いる。 As the transparent protective plate 4, a material that has excellent transparency and can protect the liquid crystal panel 15 from breakage is used. For example, general-purpose resins such as polystyrene resin, polyolefin resin, ABS resin, AS resin, acrylic resin, and AN resin can be used. In addition, general-purpose engineering resins such as polystyrene resins, polycarbonate resins, polyacetal resins, polycarbonate-modified polyphenylene ether resins, polybutylene terephthalate resins, ultrahigh molecular weight polyethylene resins, polysulfone resins, polyphenylene sulfide resins, polyphenylene oxide resins, Super engineering resins such as polyarylate resin, polyetherimide resin, polyimide resin, liquid crystal polyester resin, and polyallyl heat-resistant resin are used.

透明保護板４裏面に設けられる第２の低反射処理層１１の形成には、次のような低反射処理方法を用いることができる。例えば、フッ素樹脂やシリコン樹脂などの低屈折率樹脂を用いた低反射材料を塗布したり、金属の多層膜を蒸着等により形成したり、低反射フィルムを貼り付けたり、サンドブラスト加工やエンボス加工、マットコーティング加工、エッチング加工等により表面を梨地状に処理したりする等である。 For the formation of the second low reflection treatment layer 11 provided on the back surface of the transparent protective plate 4, the following low reflection treatment method can be used. For example, a low-reflective material using a low refractive index resin such as a fluororesin or a silicon resin is applied, a metal multilayer film is formed by vapor deposition, a low-reflective film is attached, sandblasting or embossing, For example, the surface may be processed into a satin finish by mat coating or etching.

上記加飾フィルム７のハードコートフィルム５としては、ポリカーボネート系、ポリアミド系、ポリエーテルケトン系等のエンジニアリングプラスチック、アクリル系、ポリエチレンテレフタレート系、ポリブチレンテレフタレート系などの透明樹脂フィルムの片面又は両面にアクリル樹脂、シリコン樹脂、ＵＶ硬化樹脂などによるハードコート処理層を形成したものを用いる。なお、片面にハードコート処理層を形成する場合は、ハードコート処理層の形成されていない面を透明保護板４側とする。 The hard coat film 5 of the decorative film 7 is made of acrylic on one or both sides of a transparent resin film such as engineering plastic such as polycarbonate, polyamide or polyether ketone, acrylic, polyethylene terephthalate or polybutylene terephthalate. What formed the hard-coat process layer by resin, silicon resin, UV curable resin, etc. is used. In addition, when forming a hard-coat process layer on one side, let the surface in which the hard-coat process layer is not formed be the transparent protection board 4 side.

上記加飾フィルム７の第１の低反射処理層１２の形成には、前記透明保護板４裏面の第２の低反射処理層１１と同様に、フッ素樹脂やシリコン樹脂などの低屈折率樹脂を用いた低反射材料を塗布したり、金属の多層膜を蒸着等により形成したり、低反射フィルムを貼り付けたり、サンドブラスト加工やエンボス加工、マットコーティング加工、エッチング加工等により表面を梨地状に処理したりする等である。なお、この第１の低反射処理層１２を形成するタイミングは、ハードコートフィルム５に窓形成層６を形成する前又は後のいずれでもよい。 For the formation of the first low reflection treatment layer 12 of the decorative film 7, a low refractive index resin such as a fluororesin or a silicon resin is used similarly to the second low reflection treatment layer 11 on the back surface of the transparent protective plate 4. Apply the low-reflective material used, form a multilayer metal film by vapor deposition, paste a low-reflective film, sandblasting, embossing, mat coating, etching, etc. And so on. The timing for forming the first low reflection treatment layer 12 may be before or after the window forming layer 6 is formed on the hard coat film 5.

上記加飾フィルム７は透明窓部と加飾部を有し、該加飾フィルム７が前記透明保護板４の表面に積層されて得られる保護パネル１は、加飾される部分が加飾部分２となり、加飾部２が設けられていない部分が透明窓部３となる。加飾部分２は、加飾フィルムの周囲にのみ設けられ、中央部分に透明窓部３が形成されるように形成することにより、例えば、液晶パネル１５の周囲に設けられている電極部分の隠蔽部としても用いることができる。 The decorative film 7 has a transparent window part and a decorative part. The protective panel 1 obtained by laminating the decorative film 7 on the surface of the transparent protective plate 4 has a decorative part. 2 and the part where the decoration part 2 is not provided becomes the transparent window part 3. The decorative portion 2 is provided only around the decorative film, and is formed so that the transparent window portion 3 is formed at the central portion, for example, concealing the electrode portion provided around the liquid crystal panel 15 It can also be used as a part.

窓形成層６の加飾部の材質としては、ポリ塩化ビニル系樹脂、ポリアミド系樹脂、ポリエステル系樹脂、ポリアクリル系樹脂、ポリウレタン系樹脂、ポリビニルアセタール系樹脂、ポリエステルウレタン系樹脂、セルロースエステル系樹脂、アルキド樹脂などの樹脂をバインダーとし、適切な色の顔料または染料を着色剤として含有する着色インキを用いるとよい。加飾部の形成方法としては、グラビア印刷法やスクリーン印刷法などを用いるとよい。窓形成層に加飾部を印刷法により薄膜状に形成することにより、加飾フィルム表面に形成される凹凸が少なくなり、透明保護板に貼着する場合に透明保護板４と加飾フィルム７の間に気泡が形成されるなどが起こりにくくなる。 As a material of the decoration part of the window forming layer 6, polyvinyl chloride resin, polyamide resin, polyester resin, polyacryl resin, polyurethane resin, polyvinyl acetal resin, polyester urethane resin, cellulose ester resin A colored ink containing a resin such as an alkyd resin as a binder and an appropriate color pigment or dye as a colorant may be used. As a method for forming the decoration portion, a gravure printing method, a screen printing method, or the like may be used. By forming the decorative portion in the window forming layer in a thin film by a printing method, the unevenness formed on the surface of the decorative film is reduced, and the transparent protective plate 4 and the decorative film 7 are applied when pasting on the transparent protective plate. Bubbles are less likely to occur between the two.

また、窓形成層６は、金属薄膜層からなるもの、あるいは印刷層と金属薄膜層との組み合わせからなるものでもよい。金属薄膜層は、窓形成層６として金属光沢を表現するためのものであり、真空蒸着法、スパッタリング法、イオンプレーティング法、鍍金法などで形成する。この場合、表現したい金属光沢色に応じて、アルミニウム、ニッケル、金、白金、クロム、鉄、銅、スズ、インジウム、銀、チタニウム、鉛、亜鉛などの金属、これらの合金又は化合物を使用する。金属薄膜層は、通常は、部分的に形成する。また、金属薄膜層を設ける際に、他の層との密着性を向上させるために、前アンカー層や後アンカー層を設けてもよい。 Further, the window forming layer 6 may be composed of a metal thin film layer or a combination of a printed layer and a metal thin film layer. The metal thin film layer is used to express metallic luster as the window forming layer 6 and is formed by a vacuum deposition method, a sputtering method, an ion plating method, a plating method, or the like. In this case, a metal such as aluminum, nickel, gold, platinum, chromium, iron, copper, tin, indium, silver, titanium, lead, or zinc, or an alloy or compound thereof is used depending on the metallic luster color to be expressed. The metal thin film layer is usually formed partially. Moreover, when providing a metal thin film layer, in order to improve adhesiveness with another layer, you may provide a front anchor layer and a rear anchor layer.

貼着層１０は、透明両面テープが好適に使用できるが、透明接着剤を使用してもよい。貼着層は加飾フィルム７の表面全面に設けられていてもよいし、透明窓部の視認性を高めるために窓形成層の加飾部が設けられている部分のみに設けられていてもよい。 A transparent double-sided tape can be suitably used for the adhesive layer 10, but a transparent adhesive may be used. The adhesive layer may be provided on the entire surface of the decorative film 7 or may be provided only on a portion where the decorative portion of the window forming layer is provided in order to improve the visibility of the transparent window portion. Good.

以上のように構成することにより、この保護パネルは、生産性に優れたものとなる。つまり、透明保護板４表面に、加飾部と透明窓部を有する窓形成層６がハードコートフィルム５裏面にあらかじめ形成されてなる加飾フィルム７を積層するものであるから、保護パネル毎に印刷を行なう必要がない。しかも、窓形成層６の形成対象であるハードコートフィルム５又は透明樹脂フィルム１２に加飾部を設ける際にこれらのフィルムをロール状にして多数個分の柄を連続印刷することが可能となるので、保護パネルの生産性を向上させることができる。 By configuring as described above, this protective panel is excellent in productivity. That is, since the decorative film 7 in which the window forming layer 6 having the decorative portion and the transparent window portion is formed in advance on the back surface of the hard coat film 5 is laminated on the surface of the transparent protective plate 4. There is no need to print. In addition, when the decorative portion is provided on the hard coat film 5 or the transparent resin film 12 to be formed with the window forming layer 6, it becomes possible to continuously print a large number of patterns by making these films into a roll shape. Therefore, the productivity of the protection panel can be improved.

なお、本発明の実施形態にかかる電子機器表示窓の保護パネルは、上記した構成に限定されるものではない。例えば、図２に示す保護パネル１ｂは、光学等方性の透明保護板４の表面に偏光板８を介して加飾フィルム７を積層して構成されている（図２参照）。なお、この場合、ハードコートフィルム５の透明保護板４側の面に加飾部と透明窓部を有する窓形成層６を少なくとも形成してなるものである。このように偏光板８を配置することで液晶パネル１５側からの反射光を低減することができる。また、保護パネルを電子機器配置した場合において、窓形成層６が偏光板４よりも前面に位置するように構成されているため、窓形成層６の視認性がよい。これに対して、窓形成層６が偏光板４よりも背面側に位置すると、偏光板４を通して窓形成層６を見ることとなるため、窓形成層の視認性が悪くなる。偏光板８は、液晶表示分野で通常用いられているものであることができ、例えば、ポリビニルアルコール系樹脂にヨウ素や二色性染料のような二色性物質が吸着配向された一軸延伸フィルムなどが好適であり、通常はかかる二色性物質が吸着配向された一軸延伸フィルムの両面に保護フィルムが積層された状態で用いられる。また、この保護パネルを用いる場合は、液晶パネル１５に設けられる偏光板を省略することもできる。 In addition, the protection panel of the electronic device display window according to the embodiment of the present invention is not limited to the above-described configuration. For example, the protective panel 1b shown in FIG. 2 is configured by laminating a decorative film 7 on the surface of an optically isotropic transparent protective plate 4 via a polarizing plate 8 (see FIG. 2). In this case, at least the window forming layer 6 having a decorative portion and a transparent window portion is formed on the surface of the hard coat film 5 on the transparent protective plate 4 side. By disposing the polarizing plate 8 in this way, the reflected light from the liquid crystal panel 15 side can be reduced. In addition, when the protective panel is arranged in an electronic device, the window forming layer 6 is configured to be positioned in front of the polarizing plate 4, and thus the visibility of the window forming layer 6 is good. On the other hand, when the window forming layer 6 is positioned on the back side of the polarizing plate 4, the window forming layer 6 is seen through the polarizing plate 4, so that the visibility of the window forming layer is deteriorated. The polarizing plate 8 can be one normally used in the field of liquid crystal display, for example, a uniaxially stretched film in which a dichroic substance such as iodine or a dichroic dye is adsorbed and oriented on a polyvinyl alcohol resin. In general, the protective film is used in a state where protective films are laminated on both surfaces of a uniaxially stretched film on which such a dichroic substance is adsorbed and oriented. When this protective panel is used, the polarizing plate provided on the liquid crystal panel 15 can be omitted.

ところで、電子機器表示窓の保護パネルに加飾を施す方法として特開２００１−３１８６１２号公報には転写インモールド法やインサート法が記載されている。これらの方法でも透明保護板４のみへの加飾なら可能ではあるが、上記した偏光板８を備えた構成の場合には用いることができない。なぜなら、印刷済みシートを金型内挿入し溶融樹脂を射出すると、熱により偏光板８が変質してしまうからである。偏光板８を設けた透明保護板４に加飾フィルム７を積層すれば、偏光板８が変質することはない。 By the way, as a method for decorating a protective panel of an electronic device display window, JP-A-2001-318612 describes a transfer in-mold method and an insert method. Although these methods can be used only for decoration on the transparent protective plate 4, they cannot be used in the case of the configuration including the polarizing plate 8 described above. This is because when the printed sheet is inserted into the mold and the molten resin is injected, the polarizing plate 8 is altered by heat. If the decorative film 7 is laminated on the transparent protective plate 4 on which the polarizing plate 8 is provided, the polarizing plate 8 will not be altered.

また、本発明の他の実施形態にかかる電子機器表示窓の保護パネル１ｃは、上記偏光板８を備えた構成においてさらに透明保護板４裏面にλ／４板９を積層してもよい（図３参照）。λ／４板９は、入射光線に１／４波長の位相差を生じさせる機能を持った波長板である。また、このλ／４板９は偏光板８と透明保護板４との間に配置してもよい（図５参照）。λ／４板９と偏光板８は、それぞれの光学軸が相対的に約４５゜の角度をなすように組み合わされ、円偏光板を形成している。この円偏光板は、外部からの入射光による内部反射を効率よく吸収する反射防止フィルターとして機能し、視認性を向上させることができる。 Further, in the protective panel 1c for an electronic device display window according to another embodiment of the present invention, a λ / 4 plate 9 may be further laminated on the back surface of the transparent protective plate 4 in the configuration including the polarizing plate 8 (see FIG. 3). The λ / 4 plate 9 is a wave plate having a function of causing a quarter-wave phase difference in incident light. The λ / 4 plate 9 may be disposed between the polarizing plate 8 and the transparent protective plate 4 (see FIG. 5). The λ / 4 plate 9 and the polarizing plate 8 are combined so that their optical axes are relatively at an angle of about 45 ° to form a circularly polarizing plate. This circularly polarizing plate functions as an antireflection filter that efficiently absorbs internal reflection due to incident light from the outside, and can improve visibility.

λ／４板９は、液晶表示分野で一般に採用されている各種高分子物質の一軸延伸フィルムであることができ、その素材としては、例えば、ポリビニルアルコール、ノルボルネン系樹脂、セルロース系樹脂、ポリカーボネートなどが挙げられるが、これらに限定されるものではない。 The λ / 4 plate 9 can be a uniaxially stretched film of various polymer materials generally employed in the liquid crystal display field. Examples of the material include polyvinyl alcohol, norbornene resin, cellulose resin, and polycarbonate. However, it is not limited to these.

また、上記偏光板８を配置した各構成において、透明保護板４をタッチパネル１４で構成してもよい（図４参照）。タッチパネルとしては、従来より広く用いられているものを用いることができ、加飾フィルム７と積層された可動電極フィルムと、間に空気層を形成するように周縁部において前記可動電極フィルムと接着された固定電極板とを備えるものがあげられる。 Moreover, in each structure which has arrange | positioned the said polarizing plate 8, you may comprise the transparent protective plate 4 with the touch panel 14 (refer FIG. 4). As the touch panel, those that have been widely used can be used, and the movable electrode film laminated with the decorative film 7 is bonded to the movable electrode film at the peripheral portion so as to form an air layer therebetween. And a fixed electrode plate.

また、本発明の電子機器表示窓保護パネル１は、上記加飾フィルム７を、ハードコートフィルム５の透明保護板４側の面に透明樹脂フィルムを介して窓形成層６を形成したものでとしてもよい。この場合、ハードコートフィルム５に透明樹脂フィルムを貼り合わせた後に窓形成層６を形成してもよいし、窓形成層６を透明保護板４側の面に形成した透明樹脂フィルムをハードコートフィルム５に貼り合わせてもよい。また、本発明では、加飾フィルム７として、窓形成層６をハードコートフィルム５側の面に形成した透明樹脂フィルムをハードコートフィルム５の透明保護板４側の面に貼り合わせたものを用いてもよい。 Moreover, as for the electronic device display window protection panel 1 of the present invention, the decorative film 7 is formed by forming a window forming layer 6 on the surface of the hard coat film 5 on the transparent protective plate 4 side through a transparent resin film. Also good. In this case, the window forming layer 6 may be formed after the transparent resin film is bonded to the hard coat film 5, or the transparent resin film having the window forming layer 6 formed on the surface of the transparent protective plate 4 is used as the hard coat film. 5 may be pasted together. In the present invention, as the decorative film 7, a transparent resin film in which the window forming layer 6 is formed on the surface of the hard coat film 5 is bonded to the surface of the hard coat film 5 on the transparent protective plate 4 side. May be.

（実施例１）
厚み０．０７５ｍｍのＰＥＴ基材の片面ハードコートフィルム（低反射処理付き）を用い、そのハードコート面とは反対面に透明窓部を有する窓形成層をグラビア印刷法にて形成して加飾フィルムとした。次に、厚み１．０ｍｍのアクリル板からなるが光学等方性の透明保護板の表面に、上記加飾フィルムを窓形成層側が裏面となるように透明両面テープで貼り合わせる一方、透明保護板の裏面に低反射フィルム（日本油脂製）を貼り合わせることにより低反射処理層を形成した。 Example 1
Using a PET base single-sided hard coat film (with low reflection treatment) with a thickness of 0.075 mm, a window forming layer having a transparent window on the opposite side of the hard coat surface is formed by a gravure printing method and decorated. A film was obtained. Next, the decorative film is bonded to the surface of an optically isotropic transparent protective plate made of an acrylic plate having a thickness of 1.0 mm with a transparent double-sided tape so that the window forming layer side is the back surface, while the transparent protective plate A low-reflective treatment layer was formed by pasting a low-reflective film (manufactured by NOF Corporation) on the back of the film.

この保護パネルは、透明保護板表面に、透明窓部を有する窓形成層がハードコートフィルム裏面にあらかじめ形成されてなる加飾フィルムを積層するものであるので、生産性に優れていた。 This protective panel was excellent in productivity because a decorative film in which a window forming layer having a transparent window portion was previously formed on the back surface of the hard coat film was laminated on the transparent protective plate surface.

（実施例２）
厚み０．０７５ｍｍのＰＥＴ基材の片面ハードコートフィルムを用い、そのハードコート面とは反対面に透明窓部を有する窓形成層をグラビア印刷法にて形成して加飾フィルムとした。次に、厚み１．０ｍｍのアクリル板からなるが光学等方性の透明保護板の表面に、厚み０．２ｍｍのポリビニルアルコール系樹脂にヨウ素が吸着配向された偏光板（日東電工（株）製HEG1425DU）を貼り合わせ、さらに偏光板の表面に上記加飾フィルムを窓形成層側が裏面となるように透明両面テープで貼り合わせる一方、透明保護板の裏面に厚み．４０μｍのポリカーボネート樹脂からなるλ／４板（住友化学工業（株）製SEF340138B）を貼り合わせて電子機器表示窓の保護パネルを得た。なお、λ／４板の配向軸及び偏光板の吸収軸は、横方向を０°とし、反時計回りに角度が進むように表わした場合において、λ／４板は配向軸を９０°とし、偏光板２は吸収軸を４５゜とした。また、各貼り合わせは、厚み２５μｍの基材レス透明粘着剤を用い全面的に行なう。 (Example 2)
Using a PET base single-sided hard coat film having a thickness of 0.075 mm, a window forming layer having a transparent window on the opposite side of the hard coat surface was formed by a gravure printing method to obtain a decorative film. Next, a polarizing plate (made by Nitto Denko Co., Ltd.) made of an acrylic plate having a thickness of 1.0 mm and having an iodine is adsorbed and oriented on a polyvinyl alcohol resin having a thickness of 0.2 mm on the surface of an optically isotropic transparent protective plate. HEG1425DU) is pasted, and the decorative film is pasted on the surface of the polarizing plate with a transparent double-sided tape so that the window forming layer side is on the back side, while the thickness on the back side of the transparent protective plate. A protective panel for an electronic device display window was obtained by laminating a λ / 4 plate (SEF340138B manufactured by Sumitomo Chemical Co., Ltd.) made of 40 μm polycarbonate resin. In addition, when the orientation axis of the λ / 4 plate and the absorption axis of the polarizing plate are expressed such that the transverse direction is 0 ° and the angle advances counterclockwise, the λ / 4 plate has the orientation axis of 90 °, The polarizing plate 2 has an absorption axis of 45 °. In addition, each bonding is performed entirely using a substrate-less transparent adhesive having a thickness of 25 μm.

（実施例３）
透明保護板を下記タッチパネルとしたこと以外は、実施例２と同様とした。すなわち、厚み０．１ｍｍのポリカーボネートフィルムの一面に厚み２０ｎｍのＩＴＯ膜をスパッタリングにて全面形成し、ＩＴＯ膜の周縁部分を除去して幅広の四角形状をした透明電極とした。また、透明電極の横方向に対向する二辺に配置されるバスバーと該バスバーから各々外部に出力するための引き回し回路とからなる回路を、銀ペーストをスクリーン印刷して形成した。また、縦横が上記ＰＥＴフィルムと同寸法で厚み０．７ｍｍのアクリル板を、上記ポリカーボネートフィルムの透明電極を形成した面とは反対面に厚み２５μｍの基材レス透明粘着剤で貼り合わせ、下側電極板を得た。また、縦横が下側電極板と同寸法で厚み１２５μｍのポリカーボネートフィルムフィルムを用い、その一面に厚み２０ｎｍのＩＴＯ膜をスパッタリングにて全面形成し、ＩＴＯ膜の周縁部分を除去して幅広の四角形状をした透明電極とした。また、透明電極の縦方向に対向する二辺に配置されるバスバーと該バスバーから各々外部に出力するための引き回し回路とからなる回路を、銀ペーストをスクリーン印刷して上側電極板を得た。上記上側電極板と上記下側電極板とを電極間を隔てるように対向配置させ、フィルムコネクタの挿入部分を除く周縁で粘着糊により貼り合わせ、タッチパネルとした。 (Example 3)
The same procedure as in Example 2 was performed except that the transparent protective plate was the following touch panel. That is, an ITO film having a thickness of 20 nm was formed on the entire surface of a polycarbonate film having a thickness of 0.1 mm by sputtering, and the peripheral portion of the ITO film was removed to obtain a transparent electrode having a wide rectangular shape. Further, a circuit composed of a bus bar disposed on two sides facing the transparent electrode in the lateral direction and a routing circuit for outputting to the outside from the bus bar was formed by screen printing silver paste. Also, an acrylic plate having the same height and width as the PET film and a thickness of 0.7 mm is bonded to the surface opposite to the surface on which the transparent electrode of the polycarbonate film is formed with a baseless transparent adhesive having a thickness of 25 μm. An electrode plate was obtained. In addition, using a polycarbonate film film whose length and width are the same as those of the lower electrode plate and having a thickness of 125 μm, an ITO film having a thickness of 20 nm is formed on the entire surface by sputtering, and the peripheral portion of the ITO film is removed to form a wide rectangular shape. A transparent electrode was formed. Moreover, the upper electrode plate was obtained by screen-printing a silver paste on a circuit composed of a bus bar arranged on two sides facing the vertical direction of the transparent electrode and a routing circuit for outputting to the outside from the bus bar. The upper electrode plate and the lower electrode plate were arranged to face each other so that the electrodes were separated from each other, and bonded together with adhesive paste at the periphery except for the insertion portion of the film connector to obtain a touch panel.

なお、上記様々な実施形態のうちの任意の実施形態を適宜組み合わせることにより、それぞれの有する効果を奏するようにすることができる。 It is to be noted that, by appropriately combining arbitrary embodiments of the various embodiments described above, the effects possessed by them can be produced.

本発明は、添付図面を参照しながら好ましい実施形態に関連して充分に記載されているが、この技術の熟練した人々にとっては種々の変形や修正は明白である。そのような変形や修正は、添付した請求の範囲による本発明の範囲から外れない限りにおいて、その中に含まれると理解されるべきである。 Although the present invention has been fully described in connection with preferred embodiments with reference to the accompanying drawings, various variations and modifications will be apparent to those skilled in the art. Such changes and modifications are to be understood as being included therein, so long as they do not depart from the scope of the present invention according to the appended claims.

本発明の一実施例に係る電子機器表示窓の保護パネルの断面図であり、図６のＩ−Ｉ線断面図である。It is sectional drawing of the protection panel of the electronic device display window which concerns on one Example of this invention, and is the II sectional view taken on the line of FIG. 本発明の他の実施形態に係る電子機器表示窓の保護パネルの断面図である。It is sectional drawing of the protection panel of the electronic device display window which concerns on other embodiment of this invention. 本発明のさらに他の実施例に係る電子機器表示窓の保護パネルの断面図である。It is sectional drawing of the protection panel of the electronic device display window which concerns on the further another Example of this invention. 本発明のさらに他の実施例に係る電子機器表示窓の保護パネルの断面図である。It is sectional drawing of the protection panel of the electronic device display window which concerns on the further another Example of this invention. 本発明のさらに他の実施例に係る電子機器表示窓の保護パネルの断面図である。It is sectional drawing of the protection panel of the electronic device display window which concerns on the further another Example of this invention. 本発明の実施形態にかかる電子機器表示窓の保護パネルの外観構成を示す図である。It is a figure which shows the external appearance structure of the protection panel of the electronic device display window concerning embodiment of this invention. 本発明の実施形態にかかる電子機器表示窓の保護パネルの使用例を示す図である。It is a figure which shows the usage example of the protection panel of the electronic device display window concerning embodiment of this invention. 本発明の実施形態にかかる電子機器表示窓の保護パネルの製造工程を示す図である。It is a figure which shows the manufacturing process of the protection panel of the electronic device display window concerning embodiment of this invention.

符号の説明Explanation of symbols

１，１ａ，１ｂ保護パネル
２加飾部分
３透明窓部分
４透明保護板
５ハードコートフィルム
６窓形成層
７加飾フィルム
８偏光板
９ λ／４板
１０貼着層
１１第２の低反射処理層
１２第１の低反射処理層
１５液晶ディスプレイ装置
２１前面ケーシング
２２表示窓用開口
２３加飾フィルム
２５透明両面テープ
２４大判の透明保護板
２６加飾領域 1, 1a, 1b Protective panel 2 Decorated part 3 Transparent window part 4 Transparent protective plate 5 Hard coat film 6 Window forming layer 7 Decorated film 8 Polarizing plate 9 λ / 4 plate 10 Adhering layer 11 Second low reflection treatment Layer 12 First low-reflection treatment layer 15 Liquid crystal display device 21 Front casing 22 Display window opening 23 Decorative film 25 Transparent double-sided tape 24 Large transparent protective plate 26 Decorative region

Claims

電子機器のケーシングの表示窓用開口部分に設けられたディスプレイ装置の前記表示窓用開口からの露出部分を保護する前記表示窓用開口に嵌め込まれる電子機器表示窓の保護パネルであって、
前記ディスプレイ装置の前記露出部分表面に対向して設けられる透明保護板と、
透明なハードコートフィルムと前記ハードコートフィルムの一方の表面の一部に薄膜状に形成された加飾部を有し前記加飾部が形成されていない部分が前記ディスプレイ装置の前記表示窓用開口からの露出部分を視認可能に構成された透明窓部として形成された窓形成層を備えた加飾フィルムと、
前記窓形成層が透明保護板の表面側に位置するように、前記加飾フィルムを前記透明保護板の前記ディスプレイ装置に対向しない側の表面に積層状態に貼着する透明な貼着層を有する、電子機器表示窓の保護パネル。 A protection panel for an electronic device display window fitted in the display window opening for protecting an exposed portion from the display window opening of a display device provided in the display window opening portion of a casing of the electronic device,
A transparent protective plate provided opposite to the exposed portion surface of the display device;
The display window opening of the display device has a transparent hard coat film and a decorative portion formed in a thin film on a part of one surface of the hard coat film, and the decorative portion is not formed. A decorative film provided with a window forming layer formed as a transparent window portion configured such that an exposed portion can be visually recognized;
A transparent adhesive layer for adhering the decorative film to the surface of the transparent protective plate on the side not facing the display device so that the window forming layer is located on the surface side of the transparent protective plate; , Protection panel for electronic device display window.

前記加飾部は、前記加飾フィルムの周縁に印刷層として設けられ、前記透明窓部は前記加飾フィルムの中央部分に形成される、請求項１に記載の電子機器表示窓の保護パネル。 The said decoration part is provided in the peripheral edge of the said decoration film as a printing layer, The said transparent window part is a protection panel of the electronic device display window of Claim 1 formed in the center part of the said decoration film.

前記加飾フィルムは、さらに、第１の低反射処理層が設けられている請求項１に記載の電子機器表示窓の保護パネル。 The protection panel for an electronic device display window according to claim 1, wherein the decorative film is further provided with a first low reflection treatment layer.

前記第１の低反射処理層は、前記ハードコートフィルムの他方の表面全体に設けられている、請求項３に記載の電子機器表示窓の保護パネル。 The electronic device display window protection panel according to claim 3, wherein the first low reflection treatment layer is provided on the entire other surface of the hard coat film.

前記透明保護板は、光学等方性であり、いずれかの表面に偏光板が設けられている、請求項１に記載の電子機器表示窓の保護パネル。 The said transparent protective board is an optical isotropy, The protection panel of the electronic device display window of Claim 1 by which the polarizing plate is provided in any surface.

前記偏光板は、前記透明保護板の前記ディスプレイ装置に対向しない側の表面に設けられている、請求項５に記載の電子機器表示窓の保護パネル。 The said polarizing plate is a protection panel of the electronic device display window of Claim 5 provided in the surface of the side which does not oppose the said display apparatus of the said transparent protective plate.

前記透明保護板は、前記ディスプレイ装置に対向する側の表面に第２の低反射処理層が設けられている請求項５記載の電子機器表示窓の保護パネル。 The electronic device display window protective panel according to claim 5, wherein the transparent protective plate is provided with a second low-reflection treatment layer on a surface facing the display device.

前記第２の低反射処理層は、λ／４板で構成されている、請求項７記載の電子機器表示窓の保護パネル。 The electronic device display window protection panel according to claim 7, wherein the second low reflection treatment layer is formed of a λ / 4 plate.

透明保護板は、前記加飾フィルムと積層された可動電極フィルムと、前記可動電極フィルムとの間に空気層を形成するように周縁部において前記可動電極フィルムと接着された固定電極板と、を備えるタッチパネルで構成されている、請求項１から８のいずれか１つに記載の電子機器表示窓の保護パネル。 The transparent protective plate includes a movable electrode film laminated with the decorative film, and a fixed electrode plate bonded to the movable electrode film at a peripheral edge so as to form an air layer between the movable electrode film and The protection panel for an electronic device display window according to any one of claims 1 to 8, comprising a touch panel.

電子機器のケーシング表示窓用開口部分に設けられたディスプレイ装置の前記表示窓用開口からの露出部分を保護する前記表示窓用開口に嵌め込まれる電子機器表示窓の保護パネルの製造方法であって、
ハードコートフィルムの一方の表面の一部に薄膜状に形成された加飾部を有する窓形成層を備え、前記加飾部が設けられていない部分が前記ディスプレイ装置の前記表示窓用開口からの露出部分を視認可能に透過させる透明窓部として形成される加飾領域を複数形成して、大判加飾フィルムを作成し、
前記加飾領域よりも大きい面積を有する大判透明保護板に、前記大判加飾フィルムを、前記加飾部が大判透明保護板の表面と対向する方向となるように貼り合わせ、
前記透明窓部の外側位置かつ加飾領域の内側位置において、前記貼り合わされた大判加飾フィルムと前記大判透明保護板を一体的に切断して保護パネルを得る、電子機器表示窓の保護パネルの製造方法。 A method of manufacturing a protective panel for an electronic device display window fitted in the display window opening for protecting an exposed portion from the display window opening of a display device provided in an opening portion for a casing display window of an electronic device,
A portion of one surface of the hard coat film is provided with a window forming layer having a decorative portion formed in a thin film shape, and a portion where the decorative portion is not provided is from the display window opening of the display device Form a plurality of decorative areas formed as transparent windows that allow the exposed part to be seen through, creating a large decorative film,
The large format decorative protective film having an area larger than the decorative region is bonded to the large format decorative film so that the decorative portion is in a direction facing the surface of the large format transparent protective plate,
A protective panel for an electronic device display window, wherein the laminated large-sized decorative film and the large-sized transparent protective plate are integrally cut to obtain a protective panel at an outer position of the transparent window and an inner position of the decorative region. Production method.