JP2007320479A - Pneumatic tire - Google Patents
Pneumatic tire Download PDFInfo
- Publication number
- JP2007320479A JP2007320479A JP2006154738A JP2006154738A JP2007320479A JP 2007320479 A JP2007320479 A JP 2007320479A JP 2006154738 A JP2006154738 A JP 2006154738A JP 2006154738 A JP2006154738 A JP 2006154738A JP 2007320479 A JP2007320479 A JP 2007320479A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- pneumatic tire
- rubber
- tire according
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、薄ゲージ化が可能なインナーライナー層として単層又は多層熱可塑性フイルムを使用するタイヤであって、前記熱可塑性フイルム層とゴム弾性層とを接着剤組成物を含む接着剤層を介して接合一体化させ、加熱・加硫後における接着剤に由来する製造上の不具合点を解消した空気入りタイヤに関するものである。 The present invention relates to a tire using a single layer or multilayer thermoplastic film as an inner liner layer capable of reducing gauge, and comprising an adhesive layer containing an adhesive composition comprising the thermoplastic film layer and a rubber elastic layer. The present invention relates to a pneumatic tire that has been joined and integrated to eliminate manufacturing defects caused by the adhesive after heating and vulcanization.
従来、空気入タイヤの内面には、空気漏れを防止しタイヤ空気圧を一定に保つために、ブチルゴム、ハロゲン化ブチルゴムなどの低気体透過性ブチル系ゴムを主成分とするインナーライナー層が設けられている。しかし、これらのブチル系ゴムの含有量を多くすれば、未加硫ゴムの強度が低下し、ゴム切れやシート穴空きなどを生じ易く、特にインナーライナーを薄ゲージ化する場合には、タイヤ製造時に内面のコードが露出し易いという問題を生じる。
したがって、前記のブチル系ゴムの配合量は自ら制限され、該ブチル系ゴムを配合したゴム組成物を用いる場合、空気バリア性の点からインナーライナー層の厚さは、１ｍｍ前後が必要であった。そのため、タイヤに占めるインナーライナー層の重量は約５％程度となり、タイヤの重量を低減し、自動車燃費を向上するための障害となっていた。
そこで、近年の省エネルギーの社会的な要請に伴い、自動車タイヤの軽量化を目的として、インナーライナー層を薄ゲージ化するための手法が提案されている。例えば、ナイロンフイルム層や塩化ビニリデン層をインナーライナー層として従来のブチル系ゴムの代わりに用いる手法が開示されている（例えば、特許文献１及び特許文献２参照）。また、ポリアミド系樹脂、ポリエステル系樹脂などの熱可塑性樹脂とエラストマーとのブレンドからなる組成物のフイルムをインナーライナー層に用いることが開示されている（例えば、特許文献３参照）。
Conventionally, an inner liner layer mainly composed of a low gas permeable butyl rubber such as butyl rubber or halogenated butyl rubber has been provided on the inner surface of a pneumatic tire in order to prevent air leakage and keep the tire air pressure constant. Yes. However, if the content of these butyl rubbers is increased, the strength of the unvulcanized rubber will decrease, and it will easily cause rubber breakage and sheet holes. Sometimes the inner cord tends to be exposed.
Therefore, the blending amount of the butyl rubber is limited by itself, and when using a rubber composition blended with the butyl rubber, the thickness of the inner liner layer needs to be around 1 mm from the viewpoint of air barrier properties. . Therefore, the weight of the inner liner layer in the tire is about 5%, which has been an obstacle for reducing the weight of the tire and improving the fuel efficiency of the automobile.
Therefore, in accordance with social demands for energy saving in recent years, a method for reducing the thickness of the inner liner layer has been proposed for the purpose of reducing the weight of automobile tires. For example, a method of using a nylon film layer or a vinylidene chloride layer as an inner liner layer instead of a conventional butyl rubber is disclosed (for example, see Patent Document 1 and Patent Document 2). In addition, it is disclosed that a film of a composition comprising a blend of a thermoplastic resin such as a polyamide-based resin or a polyester-based resin and an elastomer is used for the inner liner layer (see, for example, Patent Document 3).
しかしながら、これらのフイルムを用いる方法は、タイヤ軽量化はある程度可能であるとしても、マトリックス剤が結晶性の樹脂材料であるために、特に５℃以下の低温での使用時における耐クラック性や耐屈曲疲労性が通常用いられるブチル系ゴム配合組成物層の場合より劣るという欠点があり、また、タイヤ製造も複雑となる。
一方、エチレン−ビニルアルコール共重合体（以下、ＥＶＯＨと略記することがある。）はガスバリア性に優れていることが知られている。ＥＶＯＨは、空気透過量がブチル系ゴムを配合したインナーライナーゴム組成物の１００分の１以下であるため、５０μｍ以下の厚さでも、内圧保持性を大幅に向上することができる上、タイヤを重量低減することが可能である。したがって、空気入りタイヤの空気透過性を改良するために、ＥＶＯＨをタイヤインナーライナーに用いることは有効であると言える。例えばＥＶＯＨからなるタイヤインナーライナーを有する空気入りタイヤが開示されている（例えば、特許文献４参照）。
However, the methods using these films, even if the weight of the tire can be reduced to some extent, since the matrix agent is a crystalline resin material, crack resistance and resistance particularly when used at a low temperature of 5 ° C. or less. There is a drawback that bending fatigue is inferior to that of a butyl rubber compounded composition layer that is usually used, and tire manufacture is also complicated.
On the other hand, an ethylene-vinyl alcohol copolymer (hereinafter sometimes abbreviated as EVOH) is known to have excellent gas barrier properties. EVOH has an air permeation amount of 1/100 or less of the inner liner rubber composition containing butyl rubber, so that the internal pressure retention can be greatly improved even with a thickness of 50 μm or less. It is possible to reduce the weight. Therefore, it can be said that it is effective to use EVOH for the tire inner liner in order to improve the air permeability of the pneumatic tire. For example, a pneumatic tire having a tire inner liner made of EVOH is disclosed (see, for example, Patent Document 4).
しかしながら、このＥＶＯＨをインナーライナーとして用いた場合は、内圧保持性改良効果は大きいが、弾性率が通常タイヤに用いられているゴムに比べ大幅に高いため、屈曲時の変形で破断、あるいはクラックが生じることがあった。このため、ＥＶＯＨからなるインナーライナーを用いる場合、タイヤ使用前の内圧保持性は大きく向上するものの、タイヤ転動時の屈曲変形を受けた使用後のタイヤでは、内圧保持性が使用前に比べて低下することがあるなどの問題を有していた。
この問題を解決するためには、例えばエチレン含有量２０〜７０モル％、ケン化度８５％以上のエチレン−ビニルアルコール共重合体６０〜９９重量％及び疎水性可塑剤１〜４０重量％からなる樹脂組成物を用いてなるタイヤ内面用インナーライナーが開示されているが（例えば、特許分献５参照）、耐屈曲性については、必ずしも十分に満足し得るものではない。
したがって、ガスバリア性を保持したまま、高度の耐屈曲性を有し、薄ゲージ化が可能なインナーライナーの開発が望まれていた。
このようなインナーライナーとしては、例えば耐屈曲性に優れるゴム状弾性体フイルム又はシートとガスバリア性の良好な樹脂フイルムとが接着剤層を介して接合、一体化してなる積層体が考えられる。この場合、該積層体の製造工程における作業性がよく、タイヤ加硫後の接着剤に由来する気泡等の発生による不具合点がなく、かつ剥離抗力に優れることが要求される。
However, when this EVOH is used as an inner liner, the effect of improving the internal pressure retention is great, but because the elastic modulus is significantly higher than that of rubber used in normal tires, it will break or crack due to deformation during bending. It sometimes occurred. For this reason, when an inner liner made of EVOH is used, the internal pressure retention before use of the tire is greatly improved, but the internal pressure retention of the tire after use subjected to bending deformation during rolling of the tire is higher than that before use. There was a problem that it may decrease.
In order to solve this problem, for example, it comprises 60 to 99% by weight of an ethylene-vinyl alcohol copolymer having an ethylene content of 20 to 70 mol%, a saponification degree of 85% or more, and 1 to 40% by weight of a hydrophobic plasticizer. Although an inner liner for a tire inner surface using a resin composition is disclosed (see, for example, Patent Document 5), the bending resistance is not always satisfactory.
Accordingly, there has been a demand for the development of an inner liner that has a high degree of bending resistance and can be made thinner while maintaining gas barrier properties.
As such an inner liner, for example, a laminated body in which a rubber-like elastic film or sheet having excellent bending resistance and a resin film having good gas barrier properties are joined and integrated via an adhesive layer can be considered. In this case, workability in the production process of the laminate is required, there is no problem due to the generation of bubbles or the like derived from the adhesive after vulcanization of the tire, and excellent peeling resistance is required.
本発明は、このような状況下で、薄ゲージ化が可能なインナーライナー層として単層又は多層熱可塑性フイルムを使用するタイヤを製造する際に、前記熱可塑性フイルム層とゴム弾性層とを接着剤組成物を含む接着剤層を介して接合一体化させた積層体とし、加熱・加硫後における該接着剤に由来する製造上の気泡発生等の不具合点が無く、かつ剥離抗力の優れた前記積層体を用いた空気入りタイヤを提供することを目的とするものである。 Under such circumstances, the present invention bonds the thermoplastic film layer and the rubber elastic layer when manufacturing a tire using a single-layer or multilayer thermoplastic film as an inner liner layer that can be made thinner. It is a laminate that is joined and integrated through an adhesive layer containing an adhesive composition, has no defects such as production of bubbles derived from the adhesive after heating and vulcanization, and has excellent peeling resistance An object of the present invention is to provide a pneumatic tire using the laminate.
本発明者らは、前記目的を達成するために鋭意研究を重ねた結果、熱可塑性樹脂フイルム層及び／又はゴム状弾性体層に特定の接着剤組成物を含む接着剤を塗布・乾燥して得られた接着剤層を含む熱可塑性樹脂フイルム層及び／又は接着剤層を含むゴム状弾性体からなる積層体をさらに、特定の温度及び時間で処理し、発生する揮発成分の値が特定の値以下になるような乾燥条件で乾燥させた接着剤層を介して熱可塑性樹脂フイルム層とゴム状弾性体層とを接合、一体化し加熱・加硫することにより、その目的を達成し得ることを見出した。本発明は、かかる知見に基づいて完成したものである。
すなわち、本発明は、
（１） インナーライナー層として（Ａ）単層又は多層熱可塑性樹脂フイルム層を使用するタイヤであって、接着剤組成物を含む塗工液を前記（Ａ）層及び／又は（Ｂ）ゴム弾性層に塗布・乾燥し（Ｃ）接着剤層を形成した後、（Ａ）層と前記（Ｂ）層とを（Ｃ）接着剤層を介して接着するにあたり、（Ｃ）接着剤層を含む（Ａ）層及び／又は（Ｂ）層からなる積層体をさらに、１２０℃で２時間処理した際の揮発成分が、１０質量％以下であることを特徴とする空気入りタイヤ、
（２） （Ｃ）接着剤層を構成する接着剤組成物が、（ａ）ゴム成分と、その１００質量部当たり、（ｂ）架橋剤及び架橋助剤としてポリ−ｐ−ジニトロソベンゼン、１，４−フェニレンジマレイミドのうち少なくとも一種を０．１質量部以上含む上記（１）の空気入りタイヤ、
（３） 接着剤組成物が、（ａ）ゴム成分として、クロロスルホン化ポリエチレン１０質量％以上を含む上記（１）又は（２）の空気入りタイヤ、
（４） 接着剤組成物がさらに、（ｃ）充填剤２〜５０質量部含む上記（１）〜（３）いずれかの空気入りタイヤ、
（５） 接着剤組成物が、（ｃ）充填剤としてカーボンブラックを含む上記（４）の空気入りタイヤ、
（６） 接着剤組成物において、（ａ）ゴム成分が、ブチルゴム及び／又はハロゲン化ブチルゴム５０質量部％以上を含む上記（１）〜（５）いずれかの空気入りタイヤ、
（７） 接着剤組成物がさらに、（ｄ）ゴム用加硫促進剤０．１質量部以上含む上記（１）〜（６）いずれかの空気入りタイヤ、
（８） 前記（ｄ）ゴム用加硫促進剤が、チウラム系及び／又は置換ジチオカルバミン酸塩系加硫促進剤である上記（７）の空気入りタイヤ、
（９） 接着剤組成物がさらに、（ｅ）樹脂、低分子量ポリマーのうち少なくとも1種を０．１重量部以上含む上記（１）〜（８）いずれかの空気入りタイヤ、
（１０） （ｅ）成分における樹脂が、Ｃ５系樹脂、フェノール系樹脂、テルペン系樹脂、変性テルペン系樹脂、水添テルペン系樹脂及びロジン系樹脂の中から選ばれる少なくとも一種である上記（９）の空気入りタイヤ、
（１１） 前記樹脂が、フェノール系樹脂である上記（９）の空気入りタイヤ、
（１２） （ｅ）成分における低分子量重合体の重量平均分子量が、ポリスチレン換算で１，０００〜１００，０００である上記（９）の空気入りタイヤ、
（１３） （ｅ）成分における低分子量重合体の重量平均分子量が、ポリスチレン換算で１，０００〜５０，０００である上記（９）の空気入りタイヤ、
（１４） （ｅ）成分における低分子量重合体が、分子内に二重結合を有する重合体である上記（９）〜（１３）いずれかの空気入りタイヤ、
（１５） （ｅ）成分における低分子量重合体が、スチレン単位を含む重合体である上記（９）〜（１４）いずれかの空気入りタイヤ、
（１６） （ｅ）成分における低分子量重合体が、スチレン−ブタジエン共重合体である上記（１５）の空気入りタイヤ、
（１７） 前記（Ａ）単層又は多層熱可塑性樹脂フイルム層が、エチレン含有量２５〜５０モル％のエチレン−ビニルアルコール共重合体１００質量部に対して、エポキシ化合物１〜５０重量部を反応させて得られる変性エチレン−ビニルアルコール共重合体からなる層を含む上記（１）〜（１６）いずれかの空気入りタイヤ、
（１８） （Ａ）単層又は多層熱可塑性樹脂フイルム層の表面層として熱可塑性ウレタン系エラストマーを用いる上記（１）〜（１７）いずれかの空気入りタイヤ、
（１９） （Ａ）単層又は多層熱可塑性樹脂フイルム層の表面と隣接する（Ｂ）ゴム状弾性体層にブチルゴムまたはハロゲン化ブチルゴムを用いた上記（１）〜（１８）いずれかの空気入りタイヤ、
（２０） （Ａ）単層又は多層熱可塑性樹脂フイルムの表面層と隣接する（Ｂ）ゴム状弾性体層にジエン系エラストマーを用いた上記（１）〜（１８）いずれかの空気入りタイヤ、
（２１） 有機溶媒を含む接着剤組成物からなる塗工液を、ゴム状弾性体フイルム又はシート表面に塗工・乾燥したのち、その上に樹脂フイルムを貼合し、加熱・加硫処理する上記（１）〜（２０）いずれかの空気入りタイヤ、及び
（２２） 加熱・加硫処理温度が１００℃以上である上記（２１）の空気入りタイヤ、
を提供するものである。
As a result of intensive studies to achieve the above object, the present inventors applied and dried an adhesive containing a specific adhesive composition on the thermoplastic resin film layer and / or the rubber-like elastic layer. The resulting laminate comprising a thermoplastic resin film layer containing an adhesive layer and / or a rubber-like elastic body containing an adhesive layer is further treated at a specific temperature and time, and the value of the generated volatile component is a specific value. The purpose can be achieved by joining, integrating, heating and vulcanizing the thermoplastic resin film layer and the rubber-like elastic body layer via the adhesive layer dried under the drying conditions that are below the specified value. I found. The present invention has been completed based on such findings.
That is, the present invention
(1) A tire using (A) a single layer or multilayer thermoplastic resin film layer as an inner liner layer, wherein the coating liquid containing an adhesive composition is used as the layer (A) and / or (B) rubber elasticity. (C) Adhesive layer is included in adhering (A) layer and said (B) layer through (C) adhesive layer, after apply | coating and drying to a layer and forming (C) adhesive layer A pneumatic tire, wherein a laminate comprising (A) layer and / or (B) layer is further treated with a volatile component at 120 ° C. for 2 hours, of 10% by mass or less,
(2) (C) The adhesive composition constituting the adhesive layer comprises (a) a rubber component and 100 parts by mass thereof, (b) poly-p-dinitrosobenzene as a crosslinking agent and a crosslinking aid, The pneumatic tire according to (1) above containing at least 0.1 part by mass of 1,4-phenylene dimaleimide,
(3) The pneumatic tire according to the above (1) or (2), wherein the adhesive composition comprises (a) 10% by mass or more of chlorosulfonated polyethylene as a rubber component,
(4) The pneumatic tire according to any one of (1) to (3), wherein the adhesive composition further includes (c) 2 to 50 parts by mass of a filler,
(5) The pneumatic tire according to (4), wherein the adhesive composition includes (c) carbon black as a filler,
(6) In the adhesive composition, (a) the rubber component includes 50 parts by mass or more of butyl rubber and / or halogenated butyl rubber, the pneumatic tire according to any one of (1) to (5) above,
(7) The pneumatic tire according to any one of (1) to (6), wherein the adhesive composition further includes (d) 0.1 part by mass or more of a rubber vulcanization accelerator,
(8) The pneumatic tire according to (7), wherein (d) the rubber vulcanization accelerator is a thiuram-based and / or substituted dithiocarbamate-based vulcanization accelerator,
(9) The pneumatic tire according to any one of (1) to (8), wherein the adhesive composition further includes (e) 0.1 part by weight or more of at least one of a resin and a low molecular weight polymer,
(10) The above (9), wherein the resin in component (e) is at least one selected from C5 resins, phenol resins, terpene resins, modified terpene resins, hydrogenated terpene resins, and rosin resins. Pneumatic tires,
(11) The pneumatic tire according to (9), wherein the resin is a phenolic resin,
(12) The pneumatic tire according to (9), wherein the weight average molecular weight of the low molecular weight polymer in component (e) is 1,000 to 100,000 in terms of polystyrene,
(13) The pneumatic tire according to (9), wherein the weight average molecular weight of the low molecular weight polymer in component (e) is 1,000 to 50,000 in terms of polystyrene,
(14) The pneumatic tire according to any one of (9) to (13), wherein the low molecular weight polymer in the component (e) is a polymer having a double bond in the molecule.
(15) The pneumatic tire according to any one of (9) to (14), wherein the low molecular weight polymer in the component (e) is a polymer containing a styrene unit.
(16) The pneumatic tire according to (15), wherein the low molecular weight polymer in component (e) is a styrene-butadiene copolymer,
(17) The (A) single layer or multilayer thermoplastic resin film layer reacts with 1 to 50 parts by weight of an epoxy compound with respect to 100 parts by weight of an ethylene-vinyl alcohol copolymer having an ethylene content of 25 to 50 mol%. A pneumatic tire according to any one of the above (1) to (16), comprising a layer comprising a modified ethylene-vinyl alcohol copolymer obtained by
(18) (A) The pneumatic tire according to any one of (1) to (17) above, wherein a thermoplastic urethane elastomer is used as a surface layer of a single layer or multilayer thermoplastic resin film layer,
(19) (A) A pneumatic structure according to any one of (1) to (18) above, wherein butyl rubber or halogenated butyl rubber is used for the rubber-like elastic layer adjacent to the surface of the single layer or multilayer thermoplastic resin film layer. tire,
(20) (A) The pneumatic tire according to any one of (1) to (18), wherein a diene elastomer is used for the rubber-like elastic layer adjacent to the surface layer of the single-layer or multilayer thermoplastic resin film,
(21) After coating and drying a coating liquid comprising an adhesive composition containing an organic solvent on a rubber-like elastic film or sheet surface, a resin film is pasted thereon, followed by heating and vulcanization treatment. The pneumatic tire according to any one of (1) to (20), and (22) the pneumatic tire according to (21), wherein the heating / vulcanizing temperature is 100 ° C. or higher.
Is to provide.
本発明によれば、薄ゲージ化が可能なインナーライナー層として単層又は多層熱可塑性フイルム層を使用するタイヤであって、前記熱可塑性樹脂フイルム層とゴム弾性体層とを接着剤組成物を含む接着剤層を介して接合一体化させた積層体とし、加熱・加硫後における該接着剤に由来する製造上の気泡発生等の不具合点が無く、かつ剥離抗力の優れた前記積層体を用いた空気入りタイヤを提供することができる。 According to the present invention, a tire using a single-layer or multilayer thermoplastic film layer as an inner liner layer capable of reducing the thickness, wherein the thermoplastic resin film layer and the rubber elastic body layer are combined with an adhesive composition. The laminated body joined and integrated through the adhesive layer including the above laminated body having no defects such as production of bubbles derived from the adhesive after heating and vulcanization and having excellent peeling resistance. The used pneumatic tire can be provided.
本発明の空気入りタイヤは、インナーライナー層として（Ａ）単層又は多層熱可塑性樹脂フイルム層を使用するタイヤであって、接着剤組成物を含む塗工液を前記（Ａ）層及び／又は（Ｂ）ゴム弾性層に塗布・乾燥し（Ｃ）接着剤層を形成した後、（Ａ）層と前記（Ｂ）層とを（Ｃ）接着剤層を介して接着するにあたり、（Ｃ）接着剤層を含む（Ａ）層及び／又は（Ｂ）層からなる積層体をさらに、１２０℃で２時間処理した際の揮発成分が、１０質量％以下であることを特徴とする。 The pneumatic tire of the present invention is a tire that uses a single-layer or multilayer thermoplastic resin film layer as an inner liner layer, and the coating liquid containing an adhesive composition is used as the layer (A) and / or (B) After applying and drying on the rubber elastic layer to form the (C) adhesive layer, the (A) layer and the (B) layer are bonded via the (C) adhesive layer. The laminate comprising the (A) layer and / or the (B) layer including the adhesive layer is further characterized in that the volatile component when treated at 120 ° C. for 2 hours is 10% by mass or less.
通常、インナーライナー層として（Ａ）単層又は多層熱可塑性フイルムを用いる場合、単層又は多層熱可塑性フイルムの表面層と隣接する（Ｂ）ゴム状弾性体層とを直接接合させた場合、両者間の接着力は低く、タイヤの要求特性を確保するために、接着剤層を介して接合一体化することが必要となる。
本発明に係わる接着剤は、有機溶媒等の揮発成分を含む接着剤組成物からなる塗工液として用いられ、該塗工液を（Ａ）層及び／又は（Ｂ）表面に塗工・乾燥した後の（Ｃ）接着剤層を含む（Ａ）層及び／又は（Ｂ）層からなる積層体をさらに、１２０℃で２時間処理した際に発生する揮発成分が１０質量％以下であることが必要である。より好ましくは５質量％以下である。乾燥工程を経た（Ｃ）接着剤層をさらに１２０℃２時間処理することによって、接着剤層に残存している主に溶剤に由来する揮発成分は除去され、揮発成分の量を確認することができる。
１０質量％を超える揮発成分が含まれた（Ｃ）接着剤層をそのまま用いて（Ｃ）層を介して（Ａ）層と（Ｂ）層とを接合一体化した未加硫タイヤを加熱・加硫処理を行った場合、（Ｃ）層に残存する揮発成分がタイヤ製造時に揮発し、タイヤ内で局所に気泡として溜まることによってタイヤに性能上の不具合を発生することことがある。このような現象はインナーライナー層として熱可塑性樹脂フイルム層からなる（Ａ）層を用いた場合、特に起こりやすい現象であり従来のブチルゴム系のインナーライナーを用いたものに比較して不具合を発生する可能性が高い。
（Ｃ）層に残存している揮発成分が１０質量％以下の場合には、上記不具合のない、かつ、インナーライナー積層体として剥離抗力の高いタイヤを得ることができる。
Usually, when (A) a single layer or multilayer thermoplastic film is used as the inner liner layer, both the surface layer of the single layer or multilayer thermoplastic film and the adjacent (B) rubber-like elastic layer are directly bonded, The adhesive strength between them is low, and in order to ensure the required characteristics of the tire, it is necessary to integrate them through an adhesive layer.
The adhesive according to the present invention is used as a coating liquid composed of an adhesive composition containing a volatile component such as an organic solvent, and the coating liquid is applied and dried on the (A) layer and / or (B) surface. The volatile component generated when the laminate comprising the (A) layer and / or the (B) layer including the (C) adhesive layer is further treated at 120 ° C. for 2 hours is 10% by mass or less. is required. More preferably, it is 5 mass% or less. (C) The adhesive layer that has undergone the drying process is further treated at 120 ° C. for 2 hours to remove volatile components mainly derived from the solvent remaining in the adhesive layer, and confirm the amount of volatile components. it can.
An unvulcanized tire in which the (A) layer and the (B) layer are joined and integrated through the (C) layer using the (C) adhesive layer containing volatile components exceeding 10% by mass as it is. When the vulcanization treatment is performed, the volatile component remaining in the layer (C) volatilizes during the manufacture of the tire and may accumulate as bubbles locally in the tire, which may cause a malfunction in the tire. Such a phenomenon is particularly likely to occur when the (A) layer composed of a thermoplastic resin film layer is used as the inner liner layer, and causes problems as compared with the conventional one using a butyl rubber-based inner liner. Probability is high.
When the volatile component remaining in the (C) layer is 10% by mass or less, a tire having the above-described problems and having a high peel resistance can be obtained as the inner liner laminate.
本発明の空気入りタイヤにおける（Ａ）層を構成する熱可塑性フイルムとしては、ガスバリア性が良好で、適度の機械的強度を有するものであればよく、特に制限されずに、様々な樹脂フイルムを用いることができる。このような樹脂フイルムの素材としては、例えばポリアミド系樹脂、ポリ塩化ビニリデン系樹脂、ポリエステル系樹脂、エチレン-ビニルアルコール共重合体系樹脂、さらには熱可塑性ウレタン系エラストマーなどを挙げることができる。これらは一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。また、これらの素材を用いて作製された樹脂フイルムは、単層フイルムであっても良く、二層以上の多層フイルムであっても良い。
前記素材の中で、エチレン−ビニルアルコール共重合体系樹脂は、空気透過量が極めて低く、ガスバリア性に優れており、好ましい素材である。また、熱可塑性ウレタン系エラストマーは、耐水性とゴムに対する接着性に優れており、特に多層フイルムにおいて、外層部分に配置して使用することが好ましい。
The thermoplastic film constituting the layer (A) in the pneumatic tire of the present invention is not particularly limited as long as it has good gas barrier properties and appropriate mechanical strength, and various resin films can be used. Can be used. Examples of such a resin film material include polyamide resins, polyvinylidene chloride resins, polyester resins, ethylene-vinyl alcohol copolymer resins, and thermoplastic urethane elastomers. These may be used individually by 1 type, and may be used in combination of 2 or more types. The resin film produced using these materials may be a single layer film or a multilayer film having two or more layers.
Among the materials, ethylene-vinyl alcohol copolymer-based resin is a preferable material because it has an extremely low air permeation amount and excellent gas barrier properties. The thermoplastic urethane-based elastomer is excellent in water resistance and adhesiveness to rubber, and is preferably used by being disposed in the outer layer portion in a multilayer film.
また、前記エチレン−ビニルアルコール共重合体系樹脂としては、特にエチレン−ビニルアルコール共重合体にエポキシ化合物を反応させて得られた変性エチレン−ビニルアルコール共重合体が好ましい。このように変性することにより、未変性のエチレン−ビニルアルコール共重合体の弾性率を大幅に下げることができ、屈曲時の破断性、クラックの発生度合いを改良することができる。
この変性処理に用いられるエチレン−ビニルアルコール共重合体においては、エチレン単位含有量は２５〜５０モル％であることが好ましい。良好な耐屈曲性及び耐疲労性を得る観点からは、エチレン単位含有量は、より好適には３０モル％以上であり、さらに好適には３５モル％以上である。また、ガスバリア性の観点からは、エチレン単位含有量は、より好適には４８モル％以下であり、さらに好適には４５モル％以下である。エチレン単位含有量が２５モル％未満の場合は耐屈曲性及び耐疲労性が悪化するおそれがある上、溶融成形性が悪化するおそれがある。また、５０モル％を超えるとガスバリア性が不足する場合がある。
さらに、前記エチレン−ビニルアルコール共重合体のケン化度は好ましくは９０モル％以上であり、より好ましくは９５モル％以上であり、さらに好ましくは９８モル％以上であり、最適には９９モル％以上である。ケン化度が９０モル％未満では、ガスバリア性及び積層体作製時の熱安定性が不充分となるおそれがある。
The ethylene-vinyl alcohol copolymer-based resin is preferably a modified ethylene-vinyl alcohol copolymer obtained by reacting an epoxy compound with an ethylene-vinyl alcohol copolymer. By modifying in this way, the elastic modulus of the unmodified ethylene-vinyl alcohol copolymer can be greatly reduced, and the breakability during bending and the degree of occurrence of cracks can be improved.
In the ethylene-vinyl alcohol copolymer used for this modification treatment, the ethylene unit content is preferably 25 to 50 mol%. From the viewpoint of obtaining good flex resistance and fatigue resistance, the ethylene unit content is more preferably 30 mol% or more, and even more preferably 35 mol% or more. From the viewpoint of gas barrier properties, the ethylene unit content is more preferably 48 mol% or less, and even more preferably 45 mol% or less. When the ethylene unit content is less than 25 mol%, flex resistance and fatigue resistance may be deteriorated, and melt moldability may be deteriorated. Moreover, when it exceeds 50 mol%, gas barrier property may be insufficient.
Further, the saponification degree of the ethylene-vinyl alcohol copolymer is preferably 90 mol% or more, more preferably 95 mol% or more, further preferably 98 mol% or more, and optimally 99 mol%. That's it. If the degree of saponification is less than 90 mol%, the gas barrier properties and the thermal stability during production of the laminate may be insufficient.
変性処理に用いられるエチレン−ビニルアルコール共重合体の好適なメルトフローレート（ＭＦＲ）（１９０℃、２１．１８Ｎ荷重下）は０．１〜３０ｇ／１０分であり、より好適には０．３〜２５ｇ／１０分である。但し、エチレン−ビニルアルコール共重合体の融点が１９０℃付近あるいは１９０℃を超えるものは２１．１８Ｎ荷重下、融点以上の複数の温度で測定し、片対数グラフで絶対温度の逆数を横軸、ＭＦＲの対数を縦軸にプロットし、１９０℃に外挿した値で表す。
変性処理は、前記の未変性エチレン−ビニルアルコール共重合体１００質量部に対して、エポキシ化合物を、好ましくは１〜５０質量部、より好ましくは２〜４０質量部、さらに好ましくは５〜３５質量部を反応させることにより行うことができる。この際、適当な溶媒を用いて、溶液中で反応させるのが有利である。
The preferred melt flow rate (MFR) (under 190 ° C. and 21.18 N load) of the ethylene-vinyl alcohol copolymer used in the modification treatment is 0.1 to 30 g / 10 minutes, and more preferably 0.3. ~ 25 g / 10 min. However, when the melting point of the ethylene-vinyl alcohol copolymer is around 190 ° C. or exceeds 190 ° C., it is measured under a load of 21.18 N at a plurality of temperatures equal to or higher than the melting point. The logarithm of MFR is plotted on the vertical axis and expressed as a value extrapolated to 190 ° C.
In the modification treatment, the epoxy compound is preferably 1 to 50 parts by mass, more preferably 2 to 40 parts by mass, and further preferably 5 to 35 parts by mass with respect to 100 parts by mass of the unmodified ethylene-vinyl alcohol copolymer. It can be carried out by reacting parts. In this case, it is advantageous to carry out the reaction in a solution using a suitable solvent.
溶液反応による変性処理法では、エチレン−ビニルアルコール共重合体の溶液に酸触媒あるいはアルカリ触媒存在下でエポキシ化合物を反応させることによって変性エチレン−ビニルアルコール共重合体が得られる。反応溶媒としては、ジメチルスルホキシド、ジメチルホルムアミド、ジメチルアセトアミド及びＮ−メチルピロリドン等のエチレン−ビニルアルコール共重合体の良溶媒である極性非プロトン性溶媒が好ましい。反応触媒としては、ｐ−トルエンスルホン酸、メタンスルホン酸、トリフルオロメタンスルホン酸、硫酸及び三弗化ホウ素等の酸触媒や水酸化ナトリウム、水酸化カリウム、水酸化リチウム、ナトリウムメトキサイド等のアルカリ触媒が挙げられる。これらの内、酸触媒を用いることが好ましい。触媒量としては、エチレン−ビニルアルコール共重合体１００質量部に対し、０．０００１〜１０質量部程度が適当である。また、エチレン−ビニルアルコール共重合体及びエポキシ化合物を反応溶媒に溶解させ、加熱処理を行うことによっても変性エチレン−ビニルアルコール共重合体を製造することができる。 In the modification treatment method by solution reaction, a modified ethylene-vinyl alcohol copolymer is obtained by reacting an epoxy compound with an ethylene-vinyl alcohol copolymer solution in the presence of an acid catalyst or an alkali catalyst. The reaction solvent is preferably a polar aprotic solvent which is a good solvent for an ethylene-vinyl alcohol copolymer such as dimethyl sulfoxide, dimethylformamide, dimethylacetamide and N-methylpyrrolidone. Reaction catalysts include acid catalysts such as p-toluenesulfonic acid, methanesulfonic acid, trifluoromethanesulfonic acid, sulfuric acid and boron trifluoride, and alkali catalysts such as sodium hydroxide, potassium hydroxide, lithium hydroxide and sodium methoxide. Is mentioned. Of these, it is preferable to use an acid catalyst. As a catalyst amount, about 0.0001-10 mass parts is suitable with respect to 100 mass parts of ethylene-vinyl alcohol copolymers. The modified ethylene-vinyl alcohol copolymer can also be produced by dissolving an ethylene-vinyl alcohol copolymer and an epoxy compound in a reaction solvent and performing a heat treatment.
変性処理に用いられるエポキシ化合物は特に制限はされないが、一価のエポキシ化合物であることが好ましい。二価以上のエポキシ化合物である場合、エチレン−ビニルアルコール共重合体との架橋反応が生じゲル、ブツ等の発生により積層体の品質が低下するおそれがある。変性エチレン−ビニルアルコール共重合体の製造の容易性、ガスバリア性、耐屈曲性及び耐疲労性の観点から、好ましい一価エポキシ化合物としてグリシドール及びエポキシプロパンが挙げられる。
本発明に用いられる変性エチレン−ビニルアルコール共重合体のメルトフローレート（ＭＦＲ）（１９０℃、２１．１８Ｎ荷重下）は特に制限はされないが、良好なガスバリア性、耐屈曲性及び耐疲労性を得る観点からは、０．１〜３０ｇ／１０分であることが好ましく、０．３〜２５ｇ／１０分であることがより好ましく、０．５〜２０ｇ／１０分であることがさらに好ましい。但し、変性ＥＶＯＨの融点が１９０℃付近あるいは１９０℃を超えるものは２１．１８Ｎ荷重下、融点以上の複数の温度で測定し、片対数グラフで絶対温度の逆数を横軸、ＭＦＲの対数を縦軸にプロットし、１９０℃に外挿した値で表す。
The epoxy compound used for the modification treatment is not particularly limited, but is preferably a monovalent epoxy compound. When the epoxy compound is divalent or higher, a cross-linking reaction with the ethylene-vinyl alcohol copolymer may occur, and the quality of the laminate may be deteriorated due to the generation of gels and blisters. From the viewpoint of ease of production of the modified ethylene-vinyl alcohol copolymer, gas barrier properties, flex resistance, and fatigue resistance, preferred monovalent epoxy compounds include glycidol and epoxy propane.
The melt flow rate (MFR) (under 190 ° C. and 21.18 N load) of the modified ethylene-vinyl alcohol copolymer used in the present invention is not particularly limited, but has good gas barrier properties, flex resistance and fatigue resistance. From the viewpoint of obtaining, it is preferably 0.1 to 30 g / 10 minutes, more preferably 0.3 to 25 g / 10 minutes, and further preferably 0.5 to 20 g / 10 minutes. However, when the melting point of the modified EVOH is around 190 ° C or exceeds 190 ° C, it is measured at multiple temperatures above the melting point under a load of 21.18N, and the inverse of absolute temperature is plotted on the horizontal axis and the logarithm of MFR is plotted on the vertical axis. Plotted on the axis and expressed as a value extrapolated to 190 ° C.
この変性エチレン−ビニルアルコール共重合体を素材とするフイルム層の２０℃、６５ＲＨ％における酸素透過量は、3×１０-15ｃｍ3・ｃｍ／ｃｍ2・ｓｅｃ・Ｐａ以下であることが好ましく、７×１０-16ｃｍ3・ｃｍ／ｃｍ2・ｓｅｃ・Ｐａ以下であることがより好ましく、３×１０-16ｃｍ3・ｃｍ／ｃｍ2・ｓｅｃ・Ｐａ以下であることがさらに好ましい。 The oxygen permeation amount at 20 ° C. and 65 RH% of the film layer made of the modified ethylene-vinyl alcohol copolymer is preferably 3 × 10 −15 cm 3 · cm 2 · sec · Pa or less, It is more preferably 7 × 10 −16 cm 3 · cm 2 · sec · Pa or less, and further preferably 3 × 10 −16 cm 3 · cm 2 · sec · Pa or less.
また、本発明の空気入りタイヤにおける（Ａ）層を構成する熱可塑性フイルムの前記熱可塑性ウレタン系エラストマー（以下、ＴＰＵと略記することがある。）は、分子中にウレタン基（−ＮＨ−ＣＯＯ−）をもつエラストマーであり、（１）ポリオール（長鎖ジオール）、（２）ジイソシアネート、（３）短鎖ジオールの三成分の分子間反応によって生成する。ポリオールと短鎖ジオールは、ジイソシアネートと付加反応をして線状ポリウレタンを生成する。この中でポリオールはエラストマーの柔軟な部分（ソフトセグメント）になり、ジイソシアネートと短鎖ジオールは硬い部分（ハードセグメント）になる。ＴＰＵの性質は、原料の性状、重合条件、配合比によって左右され、この中でポリオールのタイプがＴＰＵの性質に大きく影響する。基本的特性の多くは長鎖ジオールの種類で決定されるが、硬さはハードセグメントの割合で調整される。
種類としては、（イ）カプロラクトン型（カプロラクトンを開環して得られるポリラクトンエステルポリオール）、（ロ）アジピン酸型（＝アジペート型）＜アジピン酸とグリコールとのアジピン酸エステルポリオール＞、（ハ）ＰＴＭＧ（ポリテトラメチレングリコール）型（＝エーテル型）＜テトラヒドロフランの開環重合で得られたポリテトラメチレングリコール＞などがある。
In the pneumatic tire of the present invention, the thermoplastic urethane elastomer (hereinafter sometimes abbreviated as TPU) of the thermoplastic film constituting the layer (A) is a urethane group (—NH—COO) in the molecule. -) Is an elastomer having (1) polyol (long-chain diol), (2) diisocyanate, and (3) short-chain diol. The polyol and the short chain diol undergo an addition reaction with diisocyanate to produce a linear polyurethane. Among these, the polyol becomes a flexible portion (soft segment) of the elastomer, and the diisocyanate and the short-chain diol become a hard portion (hard segment). The properties of TPU depend on the properties of raw materials, polymerization conditions, and blending ratio, and among these, the type of polyol greatly affects the properties of TPU. Many of the basic properties are determined by the type of long chain diol, but the hardness is adjusted by the proportion of hard segments.
The types are (i) caprolactone type (polylactone ester polyol obtained by ring-opening caprolactone), (b) adipic acid type (= adipate type) <adipic acid ester polyol of adipic acid and glycol>, (ha ) PTMG (polytetramethylene glycol) type (= ether type) <polytetramethylene glycol obtained by ring-opening polymerization of tetrahydrofuran>.
本発明において、（Ａ）層を構成する樹脂フイルムの成形方法に特に制限はなく、単層フイルムの場合、従来公知の方法、例えば溶液流延法、溶融押出法、カレンダー法などを採用することができるが、これらの方法の中で、Ｔダイ法やインフレーションなどの溶融押出法が好適である。また、多層フイルムの場合は、共押出しによるラミネート法が好ましく用いられる。
本発明における（Ａ）樹脂フイルム層の厚さは、熱可塑性樹脂フイルムの積層体をインナーライナーとして用いる場合の薄ゲージ化の観点から、２００μｍ以下が好ましい。また、薄すぎると（Ａ）層を（Ｂ）層に接合した効果が十分に発揮されないおそれが生じる。したがって、（Ａ）層の厚さの下限は１μｍ程度であり、より好ましい厚さは１０〜１５０μｍ、さらに好ましい厚さは２０〜１００μｍの範囲である。
本発明においては、（Ａ）樹脂フイルム層として、熱可塑性ウレタン系エラストマー層を含むものが好ましく、特に熱可塑性ウレタン系エラストマー層を含むと共に、前記変性エチレン−ビニルアルコール共重合体層を一層以上含む多層フイルムからなる層が好ましい。
In the present invention, the method for molding the resin film constituting the layer (A) is not particularly limited, and in the case of a single layer film, a conventionally known method, for example, a solution casting method, a melt extrusion method, a calendering method, or the like is adopted. Among these methods, a melt extrusion method such as a T-die method or inflation is preferable. In the case of a multilayer film, a laminating method by coextrusion is preferably used.
The thickness of the (A) resin film layer in the present invention is preferably 200 μm or less from the viewpoint of reducing the gauge when using a laminate of thermoplastic resin films as an inner liner. Moreover, when too thin, there exists a possibility that the effect which joined the (A) layer to the (B) layer may not fully be exhibited. Therefore, the lower limit of the thickness of the layer (A) is about 1 μm, a more preferable thickness is 10 to 150 μm, and a further preferable thickness is 20 to 100 μm.
In the present invention, the (A) resin film layer preferably includes a thermoplastic urethane-based elastomer layer, particularly includes a thermoplastic urethane-based elastomer layer, and further includes one or more of the modified ethylene-vinyl alcohol copolymer layer. A layer made of a multilayer film is preferred.
このような多層フイルムの具体例としては、前記の変性エチレン−ビニルアルコール共重合体フイルムの両面に、それぞれ熱可塑性ウレタン系エラストマーフイルムが積層された三層構造の多層フイルムを挙げることができる。
この（Ａ）層を構成する樹脂フイルムは、その上に設けられる接着剤層との密着性を向上させるために、所望により、少なくとも接着剤層側の面に、酸化法や凹凸化法などにより表面処理を施すことができる。上記酸化法としては、例えばコロナ放電処理、プラズマ放電処理、クロム酸処理（湿式）、火炎処理、熱風処理、オゾン・紫外線照射処理などが挙げられ、また凹凸化法としては、例えばサンドブラスト法、溶剤処理法などが挙げられる。これらの表面処理法は基材フイルムの種類に応じて適宜選ばれるが、一般にはコロナ放電処理法が効果及び操作性などの面から、好ましく用いられる。
As a specific example of such a multilayer film, a multilayer film having a three-layer structure in which a thermoplastic urethane-based elastomer film is laminated on both sides of the modified ethylene-vinyl alcohol copolymer film can be exemplified.
In order to improve the adhesiveness with the adhesive layer provided on the (A) layer, the resin film constituting the layer (A) is optionally formed on at least the surface of the adhesive layer by an oxidation method or an unevenness method. Surface treatment can be applied. Examples of the oxidation method include corona discharge treatment, plasma discharge treatment, chromic acid treatment (wet), flame treatment, hot air treatment, ozone / ultraviolet irradiation treatment, and the like. Treatment methods and the like. These surface treatment methods are appropriately selected depending on the type of the base film, but generally, the corona discharge treatment method is preferably used from the viewpoints of effects and operability.
本発明の空気入りタイヤにおいて、（Ｂ）層を構成するゴム状弾性体としては、ブチルゴム、ジエン系ゴム等が好適なものとして例示される。前記ジエン系ゴムとしては、例えば天然ゴム、イソプレン合成ゴム（ＩＲ）、シス１，４−ポリブタジエン（ＢＲ）、シンジオタクチック−１，２−ポリブタジエン（１，２ＢＲ）、スチレン−ブタジエンゴム（ＳＢＲ）、アクリロニトリル−ブタジエンゴム（ＮＢＲ）、クロロプレンゴム（ＣＲ）などが挙げられる。中でも天然ゴム、ブタジエンゴムなどが好適である。
ガスバリア性の観点からは、ゴム状弾性体としてブチルゴムを用いることが好ましい。前記ブチル系ゴムとしては、ブチルゴム及び／又はハロゲン化ブチルゴムを挙げることができるが、ブチル系ゴムの中では、加硫速度が速く、耐熱性、接着性、他の不飽和ゴムとの相溶性に優れる点から、ハロゲン化ブチルゴムが好ましい。前記ハロゲン化ブチルゴムとしては、塩素化ブチルゴム、臭素化ブチルゴム、その変性ゴムなどが含まれる。例えば塩素化ブチルゴムとしては「Ｅｎｊａｙ Ｂｕｔｙｌ ＨＴ１０−６６」（エンジェイケミカル社製、商標）があり、臭素化ブチルゴムとしては「ブロモブチル２２５５」（エクソン社製、商標）がある。また、変性ゴムとしてイソモノオレフィンとパラメチルスチレンとの共重合体の塩素化又は臭素化変性共重合体を用いることができ、例えば「Ｅｘｐｒｏ５０」（エクソン社製、商標）などとして入手可能である。
In the pneumatic tire of the present invention, preferred examples of the rubber-like elastic body constituting the layer (B) include butyl rubber and diene rubber. Examples of the diene rubber include natural rubber, isoprene synthetic rubber (IR), cis 1,4-polybutadiene (BR), syndiotactic-1,2-polybutadiene (1,2BR), and styrene-butadiene rubber (SBR). , Acrylonitrile-butadiene rubber (NBR), chloroprene rubber (CR) and the like. Of these, natural rubber and butadiene rubber are preferred.
From the viewpoint of gas barrier properties, it is preferable to use butyl rubber as the rubber-like elastic body. Examples of the butyl rubber include butyl rubber and / or halogenated butyl rubber. Among the butyl rubbers, the vulcanization speed is fast, heat resistance, adhesiveness, and compatibility with other unsaturated rubbers. Halogenated butyl rubber is preferred from the standpoint of superiority. Examples of the halogenated butyl rubber include chlorinated butyl rubber, brominated butyl rubber, and modified rubber thereof. For example, there is “Enjay Butyl HT10-66” (trademark, manufactured by Enjay Chemical Co., Ltd.) as a chlorinated butyl rubber, and “bromobutyl 2255” (trademark, manufactured by Exxon Corp.) as a brominated butyl rubber. Further, a chlorinated or brominated modified copolymer of a copolymer of isomonoolefin and paramethylstyrene can be used as the modified rubber, and is available as, for example, “Expro 50” (trademark, manufactured by Exxon). .
また、ゴム状弾性体層にクラックが発生した後の、前記クラックの伸展を抑制する観点からは、ゴム状弾性体として、ブチルゴム及びジエン系ゴムを含む組成物を用いることが好ましい。当該ゴム状弾性体におけるゴム成分中のブチル系ゴムの好ましい含有量は、耐空気透過性の点から７０〜１００質量％であり、該ゴム成分中には、０〜５０質量％、好ましくは０〜３０質量％の割合で、ジエン系ゴムを含有させることができる。ゴム状弾性体としてかかる組成物を用いることにより、ゴム状弾性体層に微小なクラックが発生した場合においても酸素透過を良好に抑制することができる。 In addition, from the viewpoint of suppressing the extension of the crack after the occurrence of cracks in the rubber-like elastic layer, it is preferable to use a composition containing butyl rubber and diene rubber as the rubber-like elastic body. A preferable content of the butyl rubber in the rubber component in the rubber-like elastic body is 70 to 100% by mass from the viewpoint of air permeation resistance, and 0 to 50% by mass, preferably 0 in the rubber component. The diene rubber can be contained at a ratio of ˜30 mass%. By using such a composition as a rubber-like elastic body, oxygen permeation can be satisfactorily suppressed even when minute cracks are generated in the rubber-like elastic body layer.
当該ゴム状弾性体には、耐空気透過性、耐低温クラック性及び耐屈曲疲労性などを向上させるために、前記ゴム成分以外に、無機充填剤を含有させることができる。無機充填剤としては、層状又は板状のものが好ましく、このようなものとしては、例えばカオリン、クレー、マイカ、長石、シリカ及びアルミナの含水複合体などが挙げられる。この無機充填剤の含有量は、前記ゴム成分１００質量部当たり、通常１０〜１８０質量部程度、好ましくは２０〜１２０質量部の範囲である。
また、未加硫ゴムの強度を向上させるなどの目的で、前記ゴム成分１００質量部当たり、さらにカーボンブラック０〜５０質量部、好ましくは１０〜５０質量部を含有させることができる。
上記カーボンブラックの種類は特に制限はなく、従来ゴムの補強用充填剤として慣用されているものの中から任意のものを適宜選択して用いることができ、例えばＦＥＦ、ＳＲＦ、ＨＡＦ、ＩＳＡＦ、ＳＡＦ、ＧＰＦなどが挙げられる。
本発明においては、前記無機充填剤とカーボンブラックとの合計含有量は、耐空気透過性、耐屈曲疲労性、耐低温クラック性及び加工性などのバランスの面から、ゴム成分１００質量部当たり、３０〜２００質量部の範囲が好ましく、特に５０〜１４０質量部の範囲が好適である。
The rubber-like elastic body can contain an inorganic filler in addition to the rubber component in order to improve air permeation resistance, low-temperature crack resistance, bending fatigue resistance, and the like. As the inorganic filler, a layered or plate-like one is preferable, and examples thereof include a hydrous composite of kaolin, clay, mica, feldspar, silica and alumina. The content of the inorganic filler is usually about 10 to 180 parts by mass, preferably 20 to 120 parts by mass per 100 parts by mass of the rubber component.
Further, for the purpose of improving the strength of the unvulcanized rubber, 0 to 50 parts by mass, preferably 10 to 50 parts by mass of carbon black can be further contained per 100 parts by mass of the rubber component.
The type of the carbon black is not particularly limited, and any one of those conventionally used as a reinforcing filler for rubber can be appropriately selected and used. For example, FEF, SRF, HAF, ISAF, SAF, GPF etc. are mentioned.
In the present invention, the total content of the inorganic filler and carbon black is from the balance of air permeation resistance, flex fatigue resistance, low temperature crack resistance, workability, and the like per 100 parts by mass of the rubber component. A range of 30 to 200 parts by mass is preferable, and a range of 50 to 140 parts by mass is particularly preferable.
当該ゴム状弾性体には、ゴム成分中への無機充填剤やカーボンブラックの分散性を良くし、所望の物性を向上させる目的で、ゴム成分１００質量部当たり、さらに分散改良剤０〜５質量部を含有させることができる。この分散改良剤としては、例えばシランカップリング剤、ジメチルステアリルアミン、トリエタノールアミンなどが挙げられる。これらは一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。
さらに、当該ゴム状弾性体においては、前記のカーボンブラックを配合した場合には、ナフテン系オイル又はパラフィン系オイルを、ゴム成分１００質量部当たり、１質量部以上、特に３〜２０質量部の割合で含有させることが好ましい。ここで、ナフテン系オイルは環分析による％ＣNが３０以上のものが好ましく、パラフィン系オイルは％ＣPが６０以上のものが好適である。
In the rubbery elastic body, in order to improve the dispersibility of the inorganic filler and carbon black in the rubber component and to improve the desired physical properties, the dispersion improver is further added in an amount of 0 to 5 mass per 100 parts by mass of the rubber component. Part can be contained. Examples of the dispersion improver include a silane coupling agent, dimethyl stearylamine, and triethanolamine. These may be used individually by 1 type, and may be used in combination of 2 or more types.
Further, in the rubber-like elastic body, when the carbon black is blended, the ratio of naphthenic oil or paraffinic oil is 1 part by mass or more, particularly 3 to 20 parts by mass, per 100 parts by mass of the rubber component. It is preferable to contain. Here, naphthenic oil preferably has% C N by ring analysis of 30 or more, paraffinic oil% C P is preferably of 60 or more.
また、当該ゴム状弾性体には、所望により、有機短繊維を含有させることができる。この有機短繊維を含有させることにより、本発明に係わる積層体をインナーライナーとして用いる場合、インナーライナーを薄ゲージ化してタイヤを製造する際に生じる内面コード露出を抑制することができる。この有機短繊維は、平均径１〜１００μｍで、平均長が０．１〜０．５ｍｍ程度であるものが好ましい。この有機短繊維は、ＦＲＲ（短繊維と未加硫ゴムとの複合体）として配合してもよい。
このような有機短繊維の含有量は、ゴム成分１００質量部当たり、０．３〜１５質量部が好ましい。有機短繊維の材質には特に制限はなく、例えばナイロン６、ナイ６６などのポリアミド、シンジオタクチック−１，２−ポリブタジエン、アイソタクチックポリプロピレン、ポリエチレンなどを挙げることができるが、これらの中では、ポリアミドが好ましい。
The rubbery elastic body can contain organic short fibers as desired. By including this organic short fiber, when the laminate according to the present invention is used as an inner liner, it is possible to suppress the inner surface cord exposure that occurs when the inner liner is thinned to produce a tire. The organic short fibers preferably have an average diameter of 1 to 100 μm and an average length of about 0.1 to 0.5 mm. This organic short fiber may be blended as FRR (complex of short fiber and unvulcanized rubber).
The content of such organic short fibers is preferably 0.3 to 15 parts by mass per 100 parts by mass of the rubber component. The material of the organic short fiber is not particularly limited, and examples thereof include polyamides such as
また、有機短繊維配合ゴムのモデュラスを増大させるためにはヘキサメチレンテトラミンやレゾルシンなどのゴムと繊維との接着向上剤をさらに配合することができる。
当該ゴム状弾性体には、本発明の目的が損なわれない範囲で、前記の配合剤以外に、通常ゴム工業界で用いられる各種薬品、例えば加硫剤、加硫促進剤、老化防止剤、スコーチ防止剤、亜鉛華、ステアリン酸などを配合させることができる。
本発明において、（Ｂ）層を構成するゴム状弾性体は、前記の各成分を含むゴム組成物を、従来公知の方法により、未加硫の段階でフイルム状又はシート状に押出し加工することにより得ることができる。
本発明における（Ｂ）層のゴム状弾性体層の厚さは、通常２００μｍ以上である。その上限は、インナーライナーとして用いる場合の薄ゲージ化を考慮するとタイヤサイズにより適宜決められる。
Further, in order to increase the modulus of the organic short fiber compound rubber, an adhesion improver between rubber and fiber such as hexamethylenetetramine and resorcin can be further compounded.
In the rubbery elastic body, in addition to the above compounding agents, various chemicals usually used in the rubber industry, such as vulcanizing agents, vulcanization accelerators, anti-aging agents, as long as the object of the present invention is not impaired. A scorch inhibitor, zinc white, stearic acid, etc. can be blended.
In the present invention, the rubber-like elastic body constituting the layer (B) is obtained by extruding a rubber composition containing each of the above components into a film or a sheet at an unvulcanized stage by a conventionally known method. Can be obtained.
The thickness of the rubber-like elastic layer (B) in the present invention is usually 200 μm or more. The upper limit is appropriately determined depending on the tire size in consideration of the reduction in gauge when used as an inner liner.
（Ｂ）ゴム状弾性体層を設けた、本発明に係わる積層体を、タイヤのインナーライナーに適用した場合、上記（Ａ）樹脂フイルム層が、２００μｍ以下の薄ゲージで使用されるため耐屈曲性、耐疲労性が向上し、タイヤの転動時の屈曲変形で破断及びクラックが生じにくくなる。また、たとえ破断しても（Ａ）樹脂フイルム層が、後に詳術する（Ｃ）接着剤層を介して（Ｂ）ゴム状弾性体層との接着性が非常に良好で剥離しにくく、亀裂が伸展しにくいため大きな破断及びクラックが生じない。また、生じた場合においても（Ａ）樹脂フイルム層に生じた破断及びクラック部分のガスバリア性を（Ｂ）ゴム弾性層が補うため、タイヤ使用後においても良好な内圧保持が可能となる。 (B) When the laminate according to the present invention provided with a rubber-like elastic layer is applied to an inner liner of a tire, the above-mentioned (A) resin film layer is used with a thin gauge of 200 μm or less, so that it is resistant to bending. And fatigue resistance are improved, and breakage and cracks are less likely to occur due to bending deformation during rolling of the tire. Even if it breaks, the (A) resin film layer has a very good adhesion to the (B) rubber-like elastic layer through the adhesive layer (C), which will be described later, and is difficult to peel off. Since it is difficult to extend, large breakage and cracks do not occur. Even when it occurs, (B) the rubber elastic layer supplements the gas barrier properties of the fracture and cracks generated in the (A) resin film layer, so that good internal pressure can be maintained even after use of the tire.
本発明に係わる積層体において、（Ｃ）接着剤層を構成する接着剤組成物としては、（ａ）ゴム成分と、その１００質量部当たり、（ｂ）架橋剤及び架橋助剤としてポリ−ｐ−ジニトロソベンゼン、１，４−フェニレンジマレイミドのうち少なくとも一種を０．１質量部以上含む組成のものが用いられる。
当該接着剤組成物においては、（ａ）ゴム成分については特に制限はなく、（Ａ）樹脂フイルム層と（Ｂ）ゴム状弾性体層の種類とその組み合わせによってそれぞれに優れたタック性及び剥離抗力を確保するために適宜決定されるが、通常、５０質量％以上のブチルゴム及び／又はハロゲン化ブチルゴムやジエン系ゴムを用いることが好ましい。
前記ブチルゴム及び／又はハロゲン化ブチルゴムやジエン系ゴムは、前述の（Ｂ）層を構成するゴム状弾性体の説明において例示した通りである。
該（ａ）成分としては、接着剤層の作業性及び剥離抗力などの点から、ハロゲン化ブチルゴム７０〜１００質量％を含むものが好ましい。
In the laminate according to the present invention, (C) the adhesive composition constituting the adhesive layer includes (a) a rubber component and 100 parts by mass of (b) a poly-p as a crosslinking agent and a crosslinking aid. -The thing of the composition containing 0.1 mass part or more of at least 1 type is used among dinitrosobenzene and 1, 4- phenylene dimaleimide.
In the adhesive composition, (a) the rubber component is not particularly limited, and (A) a resin film layer and (B) a rubber-like elastic body layer, and a combination thereof and excellent tackiness and peeling resistance, respectively. In general, it is preferable to use 50% by mass or more of butyl rubber and / or halogenated butyl rubber or diene rubber.
The butyl rubber and / or halogenated butyl rubber and diene rubber are as illustrated in the description of the rubber-like elastic body constituting the layer (B).
The component (a) preferably contains 70 to 100% by mass of a halogenated butyl rubber from the viewpoints of workability of the adhesive layer and peeling resistance.
さらに、（ａ）成分として、所望によりクロロスルホン化ポリエチレン１０質量％以上含むことが好ましい。該クロロスルホン化ポリエチレン（以下ＣＳＭと略記することがある）は、塩素と亜硫酸ガスを用いてポリエチレンを塩素化ならびにクロロスルホン化して製造される二重結合を含まない飽和構造を有する合成ゴムであり耐侯性、耐オゾン性、耐熱性などの安定性に優れている。ＣＳＭは商品名「ハイパロン」としてデュポン社より市販されている。接着剤層の剥離抗力の向上、耐熱性等の点から、ＣＳＭを１０〜４０質量％含むものが好ましい。
本発明においては、剥離抗力の点から、特にハロゲン化ブチルゴム７０質量％以上、クロロスルホン化ポリエチレン１０質量％以上及び天然ゴム及び／又はイソプレンゴム５質量％以上を含むことが好ましい。
Furthermore, it is preferable to contain 10% by mass or more of chlorosulfonated polyethylene as desired as the component (a). The chlorosulfonated polyethylene (hereinafter sometimes abbreviated as CSM) is a synthetic rubber having a saturated structure containing no double bond, which is produced by chlorinating and chlorosulfonated polyethylene using chlorine and sulfurous acid gas. Excellent stability such as weather resistance, ozone resistance and heat resistance. CSM is commercially available from DuPont under the trade name “Hypalon”. From the viewpoints of improving the peel resistance of the adhesive layer, heat resistance, etc., those containing 10 to 40% by mass of CSM are preferable.
In the present invention, from the viewpoint of peeling resistance, it is particularly preferable to contain 70% by mass or more of halogenated butyl rubber, 10% by mass or more of chlorosulfonated polyethylene and 5% by mass or more of natural rubber and / or isoprene rubber.
当該接着剤組成物においては、加熱処理後の剥離抗力を改良するために、（ｂ）架橋剤及び架橋助剤として、ポリ−ｐ−ジニトロソベンゼン、１,４−フェニレンジマレイミドのうち少なくとも一種を０．１質量部以上配合することが好ましい。
ポリ−ｐ−ジニトロソベンゼンは、ハロゲン化ブチルゴムのような二重結合の少ないゴムに対して、有効な架橋剤であり、ポリ−ｐ−ジニトロソベンゼンを加えて熱処理することにより未加硫配合物のコールドフローを防止し、押し出し特性、加硫物の物理特性を改良するし、また可塑度を調節することができる。
また、１,４−フェニレンジマレイミドを用いた加硫は炭素−炭素の共有結合が生成し、耐熱性、耐老化性を向上させる。特にクロロスルホン化ポリエチレンゴムに対しても有効な架橋剤である。
これら（ｂ）成分の接着剤組成物に対する配合量は、該接着剤組成物のゴム成分１００質量部に対して０．１質量部配合することが好ましい。
In the adhesive composition, in order to improve the peel resistance after heat treatment, (b) at least one of poly-p-dinitrosobenzene and 1,4-phenylene dimaleimide is used as a crosslinking agent and a crosslinking aid. Is preferably blended in an amount of 0.1 parts by mass or more.
Poly-p-dinitrosobenzene is an effective cross-linking agent for rubbers with few double bonds such as halogenated butyl rubber. Unvulcanized compound by adding poly-p-dinitrosobenzene and heat treatment It can prevent cold flow of products, improve extrusion properties, physical properties of vulcanizates, and adjust plasticity.
In addition, vulcanization using 1,4-phenylene dimaleimide produces a carbon-carbon covalent bond and improves heat resistance and aging resistance. In particular, it is an effective crosslinking agent for chlorosulfonated polyethylene rubber.
The blending amount of the component (b) with respect to the adhesive composition is preferably 0.1 parts by mass with respect to 100 parts by mass of the rubber component of the adhesive composition.
当該接着剤組成物における（ｃ）成分の充填剤としては、無機フィラー及び／又はカーボンブラックを用いることができる。無機フィラーとしては、例えば湿式法によるシリカ（以下、湿式シリカと称する。）、水酸化アルミニウム、酸化アルミニウム、酸化マグネシウム、モンモリロナイト、マイカ、スメクタイト、有機化モンモリロナイト、有機化マイカ及び有機化スメクタイトなどを挙げることができる。これらは一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。
一方、カーボンブラックについては、前述の（Ｂ）層を構成するゴム状弾性体の説明において例示したとおりである。
当該接着剤組成物においては、この（ｃ）成分である充填剤の含有量は、前記（ａ）成分であるゴム成分１００質量部当たり、タック性及び剥離抗力などの点から、２〜５０質量部、好ましくは５〜３５質量部の範囲で選定される。
As the filler of component (c) in the adhesive composition, an inorganic filler and / or carbon black can be used. Examples of the inorganic filler include silica by a wet method (hereinafter referred to as wet silica), aluminum hydroxide, aluminum oxide, magnesium oxide, montmorillonite, mica, smectite, organic montmorillonite, organic mica, and organic smectite. be able to. These may be used individually by 1 type, and may be used in combination of 2 or more types.
On the other hand, about carbon black, it is as having illustrated in description of the rubber-like elastic body which comprises the above-mentioned (B) layer.
In the adhesive composition, the content of the filler that is the component (c) is 2 to 50 masses per 100 parts by mass of the rubber component that is the component (a) in terms of tackiness and peeling resistance. Parts, preferably in the range of 5 to 35 parts by weight.
また、当該接着剤組成物に含まれる（ａ）ゴム成分のクロロスルホン化ポリエチレン、（ｂ）成分の架橋剤及び架橋助剤、（ｃ）成分の充填剤を含む市販接着剤組成物として、例えばケムロック６２５０（ロードコーポレーション社製）が挙げられる。このケムロック６２５０を接着剤組成物の（ａ）、（ｂ）、（ｃ）成分混合物として使用することも可能である。 Further, as a commercially available adhesive composition containing (a) a chlorosulfonated polyethylene as a rubber component, (b) a crosslinking agent and a crosslinking aid, and (c) a filler as a component contained in the adhesive composition, for example, Chemlock 6250 (manufactured by Road Corporation) may be mentioned. It is also possible to use this Chemlock 6250 as a mixture of components (a), (b) and (c) of the adhesive composition.
当該接着剤組成物においては、（ｄ）成分として、ゴム成分１００質量部当たり、加硫促進剤を０．１質量部以上含むことにより、得られる積層体は所望の剥離抗力を発揮することができる。加硫促進剤としては特に制限はなく、例えば、チウラム系、置換ジチオカルバミン酸塩系、グアニジン系、チアゾール系、スルフェンアミド系、チオ尿素系、キサンテート系などの中から選ばれる少なくとも一種を挙げることができる。中でもチウラム系及び／又は置換ジチオカルバミン酸塩系加硫促進剤が好ましい。前記加硫促進剤の含有量の上限については特に制限はないが、通常５質量部程度である。前記加硫促進剤の好ましい含有量は０．３〜３質量部の範囲である。 In the adhesive composition, as a component (d), by including 0.1 part by mass or more of a vulcanization accelerator per 100 parts by mass of the rubber component, the obtained laminate can exhibit a desired peeling resistance. it can. There are no particular restrictions on the vulcanization accelerator, and examples include at least one selected from thiuram, substituted dithiocarbamate, guanidine, thiazole, sulfenamide, thiourea, xanthate, and the like. Can do. Of these, thiuram-based and / or substituted dithiocarbamate-based vulcanization accelerators are preferred. Although there is no restriction | limiting in particular about the upper limit of content of the said vulcanization accelerator, Usually, it is about 5 mass parts. The preferable content of the vulcanization accelerator is in the range of 0.3 to 3 parts by mass.
チウラム系及び／又は置換ジチオカルバミン酸塩系加硫促進剤を０．１質量部以上含むことにより、得られる積層体は所望の剥離抗力を発揮することができる。前記加硫促進剤の含有量の上限については特に制限はないが、通常５質量部程度である。前記加硫促進剤の好ましい含有量は０．３〜３質量部の範囲である。
チウラム系加硫促進剤としては、例えばテトラメチルチウラムモノスルフィド、テトラメチルチウラムジスルフィド、活性化テトラメチルチウラムジスルフィド、テトラエチルチウラムジスルフィド、テトラブチルチウラムモノスルフィド、テトラブチルチウラムジスルフィド、ジペンタメチレンチウラムテトラスルフィド、ジペンタメチレンチウラムヘキサスルフィド、テトラベンジルチウラムジスルフィド、テトラキス（２−エチルヘキシル）チウラムジスルフィドなどが挙げられる。
By including 0.1 part by mass or more of a thiuram-based and / or substituted dithiocarbamate-based vulcanization accelerator, the obtained laminate can exhibit a desired peeling resistance. Although there is no restriction | limiting in particular about the upper limit of content of the said vulcanization accelerator, Usually, it is about 5 mass parts. The preferable content of the vulcanization accelerator is in the range of 0.3 to 3 parts by mass.
Examples of the thiuram vulcanization accelerator include tetramethylthiuram monosulfide, tetramethylthiuram disulfide, activated tetramethylthiuram disulfide, tetraethylthiuram disulfide, tetrabutylthiuram monosulfide, tetrabutylthiuram disulfide, dipentamethylenethiuram tetrasulfide, Examples include dipentamethylene thiuram hexasulfide, tetrabenzyl thiuram disulfide, and tetrakis (2-ethylhexyl) thiuram disulfide.
一方、置換ジチオカルバミン酸塩系加硫促進剤としては、例えばジメチルジチオカルバミン酸ナトリウム、ジエチルジチオカルバミン酸ナトリウム、ジ−ｎ−ブチルジチオカルバミン酸ナトリウム、ジメチルジチオカルバミン酸カリウム、エチルフェニルジチオカルバミン酸鉛、ジメチルジチオカルバミン酸亜鉛、ジエチルジチオカルバミン酸亜鉛、ジ−ｎ−ブチルジチオカルバミン酸亜鉛、ジベンジルジチオカルバミン酸亜鉛、Ｎ−ペンタメチレンジチオカルバミン酸亜鉛、エチルフェニルジチオカルバミン酸亜鉛、ジエチルジチオカルバミン酸テルル、ジメチルジチオカルバミン酸銅、ペンタメチレンジチオカルバミン酸ピペリジンなどが挙げられる。
本発明においては、前記のチウラム系加硫促進剤及び置換ジチオカルバミン酸塩系加硫促進剤の中から選ばれる少なくとも一種が用いられるが、これらの中で、置換ジチオカルバミン酸塩系加硫促進剤が好ましく、特にジベンジルジチオカルバミン酸亜鉛が好適である。
On the other hand, as the substituted dithiocarbamate vulcanization accelerator, for example, sodium dimethyldithiocarbamate, sodium diethyldithiocarbamate, sodium di-n-butyldithiocarbamate, potassium dimethyldithiocarbamate, lead ethylphenyldithiocarbamate, zinc dimethyldithiocarbamate, Zinc diethyldithiocarbamate, zinc di-n-butyldithiocarbamate, zinc dibenzyldithiocarbamate, zinc N-pentamethylenedithiocarbamate, zinc ethylphenyldithiocarbamate, tellurium diethyldithiocarbamate, copper dimethyldithiocarbamate, pentamethylenedithiocarbamate piperidine, etc. Is mentioned.
In the present invention, at least one selected from the thiuram vulcanization accelerator and the substituted dithiocarbamate vulcanization accelerator is used. Among these, the substituted dithiocarbamate vulcanization accelerator is used. Particularly preferred is zinc dibenzyldithiocarbamate.
当該接着剤組成物においては、（ｅ）成分として樹脂及び／又は低分子重合体が、特に貼り付け作業性（接着剤組成物の粘着性向上）のために用いられる。
（ｅ）成分の樹脂としては、例えば、フェノール系樹脂、変性テルペン系樹脂、テルペン系樹脂、水添テルペン系樹脂、ロジン系樹脂，Ｃ5、Ｃ9石油樹脂、キシレン樹脂、クマロンインデン樹脂、ジシクロペンタジエン樹脂、スチレン樹脂などが挙げられるが、これらの中で、Ｃ5留分樹脂、フェノール系樹脂、テルペン系樹脂、変性テルペン系樹脂、水添テルペン系樹脂及びロジン系樹脂が好適である。
Ｃ5留分樹脂としては、ナフサの熱分解によって得られる、通常１−ペンテン、２−ペンテン、２−メチル−１−ブテン、２−メチル−２−ブテン、３−メチル−１−ブテン等のオレフィン系炭化水素、２−メチル−１，３−ブタジエン、１，２−ペンタジエン、１，３−ペンタジエン、３−メチル−１，２−ブタジエンなどのジオレフィン系炭化水素等を重合又は共重合した石油樹脂が挙げられる。
フェノール系樹脂としては、例えばｐ-ｔ-ブチルフェノールとアセチレンを触媒の存在下で縮合させた樹脂、アルキルフェノールとホルムアルデヒドとの縮合物などを挙げることができる。
In the adhesive composition, as the component (e), a resin and / or a low molecular weight polymer is used particularly for sticking workability (adhesion improvement of the adhesive composition).
Examples of the component (e) resin include phenolic resins, modified terpene resins, terpene resins, hydrogenated terpene resins, rosin resins, C 5 and C 9 petroleum resins, xylene resins, coumarone indene resins, dicyclopentadiene resins and styrene resins, among these, C 5 fraction resins, phenol resins, terpene resins, modified terpene resins, hydrogenated terpene resins and rosin-based resin is preferable .
The C 5 fraction resins, obtained by the thermal cracking of naphtha, usually 1-pentene, 2-pentene, 2-methyl-1-butene, 2-methyl-2-butene, 3-methyl-1-butene Polymerized or copolymerized diolefinic hydrocarbons such as olefinic hydrocarbons, 2-methyl-1,3-butadiene, 1,2-pentadiene, 1,3-pentadiene, 3-methyl-1,2-butadiene, etc. Petroleum resin is mentioned.
Examples of the phenolic resin include a resin obtained by condensing pt-butylphenol and acetylene in the presence of a catalyst, and a condensate of alkylphenol and formaldehyde.
また、テルペン系樹脂、変性テルペン系樹脂、水添テルペン系樹脂としては、例えばβ−ピネン樹脂や、α−ピネン樹脂などのテルペン系樹脂、これらを水素添加してなる水添テルペン系樹脂、テルペンとフェノールをフリーデルクラフト型触媒で反応させたり、あるいはホルムアルデヒドと縮合させた変性テルペン系樹脂を挙げることができる。
ロジン系樹脂としては、例えば天然樹脂ロジン、それを水素添加、不均化、二量化、エステル化、ライム化などで変性したロジン誘導体を挙げることができる。これらの樹脂は一種を単独で用いてもよいが、これらの中で、特にフェノール系樹脂が好ましい。
Examples of the terpene resin, modified terpene resin, and hydrogenated terpene resin include, for example, terpene resins such as β-pinene resin and α-pinene resin, hydrogenated terpene resins obtained by hydrogenating these resins, and terpenes. And a modified terpene resin in which phenol and phenol are reacted with a Friedel-Craft type catalyst or condensed with formaldehyde.
Examples of the rosin resin include a natural resin rosin and a rosin derivative modified by hydrogenation, disproportionation, dimerization, esterification, limeization or the like. These resins may be used alone, but among these, phenolic resins are particularly preferable.
一方、低分子量重合体としては、重量平均分子量が、ポリスチレン換算で１，０００から１００，０００の範囲にあるものが好ましく、より好ましくは１，０００〜５０，０００である。また、分子内に二重結合を有するものが好ましく、さらにスチレン単位を有するものが好ましい。このような低分子量重合体としては、スチレン−ブタジエン共重合体を挙げることができる。
この低分子量スチレン−ブタジエン共重合体は、例えばシクロヘキサンなどの炭化水素溶媒中において、有機リチウム化合物開始剤をエーテル又は第３級アミンの存在下で用いて、ブタジエンとスチレンとを、５０〜９０℃程度で共重合させることにより製造することができる。得られた共重合体の分子量は、有機リチウム化合物の量で、ミクロ構造はエーテル又は第３級アミンの量によって制御することができる。
本発明においては、（ｅ）成分として、前記低分子量重合体を一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。あるいは前述の樹脂一種以と前記低分子量重合体一種以上を組み合わせて用いてもよい。
本発明においては、この（ｅ）成分は、前記（ａ）成分のゴム成分１００質量部に対し、５質量部以上用いることが好ましく、より好ましくは５〜４０質量部特に好ましくは１０〜３０質量部の割合で用いられる。
特に該（ｅ）成分としてフェノール系樹脂を用いる場合得られる接着剤組成物は、優れたタック性を示すことから好ましい。
On the other hand, the low molecular weight polymer preferably has a weight average molecular weight in the range of 1,000 to 100,000 in terms of polystyrene, more preferably 1,000 to 50,000. Moreover, what has a double bond in a molecule | numerator is preferable, and what has a styrene unit further is preferable. An example of such a low molecular weight polymer is a styrene-butadiene copolymer.
This low molecular weight styrene-butadiene copolymer is obtained by using butadiene and styrene in a hydrocarbon solvent such as cyclohexane in the presence of an ether or a tertiary amine to produce butadiene and styrene at 50 to 90 ° C. It can be produced by copolymerizing at a degree. The molecular weight of the obtained copolymer can be controlled by the amount of the organic lithium compound, and the microstructure can be controlled by the amount of ether or tertiary amine.
In the present invention, as the component (e), the low molecular weight polymer may be used alone or in combination of two or more. Alternatively, one or more of the above resins and one or more of the low molecular weight polymers may be used in combination.
In the present invention, the component (e) is preferably used in an amount of 5 parts by mass or more, more preferably 5 to 40 parts by mass, particularly preferably 10 to 30 parts by mass with respect to 100 parts by mass of the rubber component of the component (a). Used in parts ratio.
In particular, an adhesive composition obtained when a phenol resin is used as the component (e) is preferable because it exhibits excellent tackiness.
当該接着剤組成部においては、本発明の目的が損なわれない範囲で、所望により、加硫剤、ステアリン酸、酸化亜鉛、老化防止剤などを含有させることができる。 In the adhesive composition part, a vulcanizing agent, stearic acid, zinc oxide, an anti-aging agent and the like can be contained as desired within a range that does not impair the object of the present invention.
次に本発明に用いられる積層体の製造方法について説明する。
まず、有機溶媒に、前記接着剤組成物を構成する各成分を加え、溶解又は分散させて、有機溶媒を含む接着剤組成物からなる塗工液を調製する。
この際、有機溶媒として、（ａ）ゴム成分の良溶媒であるヒルデブランド（Hildebrand）溶解度パラメーターδ値が１４〜２０ＭＰａ1/2の有機溶剤が好ましく用いられる。このような有機溶剤としては、例えば、トルエン、キシレン、ｎ−ヘキサン、シクロヘキサン、クロロホルム、メチルエチルケトンなどを挙げることができる。これらは一種を単独で用いてもよく、二種以上を混合して用いてもよい。
このようにして調製された塗工液の固形分濃度は、塗工性や取り扱い性などを考慮して適宜選定されるが、通常５〜５０質量％、好ましくは１０〜３０質量％の範囲である。
次に、前記塗工液を、（Ａ）層を構成する樹脂フイルム表面に塗工・乾燥したのち、その上に、（Ｂ）層を構成するゴム状弾性体フイルム又はシートを貼合し、加熱・加硫処理することにより、本発明に用いられる積層体が得られる。
Next, the manufacturing method of the laminated body used for this invention is demonstrated.
First, each component which comprises the said adhesive composition is added to an organic solvent, and it melt | dissolves or disperses and prepares the coating liquid which consists of an adhesive composition containing an organic solvent.
In this case, as the organic solvent, (a) an organic solvent having a Hildebrand solubility parameter δ value of 14 to 20 MPa 1/2 which is a good solvent for the rubber component is preferably used. Examples of such an organic solvent include toluene, xylene, n-hexane, cyclohexane, chloroform, methyl ethyl ketone, and the like. These may be used individually by 1 type, and 2 or more types may be mixed and used for them.
The solid content concentration of the coating solution thus prepared is appropriately selected in consideration of coating properties and handleability, but is usually in the range of 5 to 50% by mass, preferably 10 to 30% by mass. is there.
Next, after coating and drying the coating liquid on the surface of the resin film constituting the layer (A), the rubber-like elastic film or sheet constituting the layer (B) is bonded thereon, A laminate used in the present invention is obtained by heating and vulcanization treatment.
あるいは、前記塗工液を、（Ｂ）層を構成するゴム状弾性体のフイルム又はシートの表面に塗工・乾燥したのち、その上に、（Ａ）層を構成する樹脂フイルムを貼合し、加熱・加硫処理することにより、本発明に用いられる積層体が得られる。
この２つの方法の中では、通常前者の方法が用いられる。
上記のように例えば、（Ａ）層を構成する樹脂フイルム表面に前記塗工液を塗工し（Ｂ）層と貼合する前に（Ｃ）接着剤層を乾燥する必要があるが、その乾燥条件としては、乾燥後の（Ｃ）接着剤層を１２０℃２時間で処理した際の（Ｃ）接着剤層に残存する揮発分が１０質量％以下であることが必要である。より好ましくは５質量％以下である。
Alternatively, after coating and drying the coating liquid on the surface of the rubbery elastic film or sheet constituting the layer (B), the resin film constituting the layer (A) is bonded thereon. By heating and vulcanizing, the laminate used in the present invention is obtained.
Of these two methods, the former method is usually used.
As described above, for example, it is necessary to dry the adhesive layer (C) before applying the coating liquid on the surface of the resin film constituting the layer (A) and laminating with the layer (B). As drying conditions, it is necessary that the volatile content remaining in the (C) adhesive layer when the dried (C) adhesive layer is treated at 120 ° C. for 2 hours is 10% by mass or less. More preferably, it is 5 mass% or less.
上記の乾燥条件としては、６０℃〜１５０℃が好ましく、８０℃〜１２０℃がより好ましい。乾燥条件を上記範囲にすることによって生産性の低下及び接着剤の硬化による剥離抗力の低下を抑えることができる。
乾燥時間については、接着剤組成物、溶媒の量によって適宜決定することができるが、接着剤層に残存する揮発成分の量が１０質量％以下であればよい。
１０質量％を超える多くの揮発成分が含まれた（Ｃ）層を介して（Ａ）層及び（Ｂ）層を貼合し、インナーライナー相としてタイヤを加熱・加硫処理を行った場合、その揮発成分がタイヤ製造時に揮発し、タイヤ内で局所に気泡として溜まることによってタイヤに性能上の不具合を発生することがある。
したがって、（Ｃ）接着剤層に残存する揮発分の量を１０質量％以下にすることが重要であり、タック性が良好で、作業性よく作製し得る上、剥離抗力に優れるなどの特徴を有するインナーライナーを有する空気入りタイヤを得ることができる。
As said drying conditions, 60 to 150 degreeC is preferable and 80 to 120 degreeC is more preferable. By setting the drying conditions within the above range, it is possible to suppress a decrease in productivity and a decrease in peeling resistance due to the curing of the adhesive.
The drying time can be appropriately determined depending on the amount of the adhesive composition and the solvent, but the amount of the volatile component remaining in the adhesive layer may be 10% by mass or less.
When the (A) layer and the (B) layer are bonded via the (C) layer containing many volatile components exceeding 10% by mass, and the tire is heated and vulcanized as an inner liner phase, The volatile component volatilizes during the manufacture of the tire and accumulates as bubbles locally in the tire, which may cause performance problems in the tire.
Therefore, it is important that the amount of the volatile component remaining in the adhesive layer (C) is 10% by mass or less, the tackiness is good, the workability is good, and the peel resistance is excellent. A pneumatic tire having an inner liner can be obtained.
前記方法において、（Ａ）層を構成する樹脂フイルムが、変性エチレン−ビニルアルコール共重合体層を有する場合、この樹脂フイルムとゴム状弾性体フイルム又はシートを、接着剤組成物層を介して貼合する前に、該樹脂フイルムに、予めエネルギー線を照射して、該変性エチレン−ビニルアルコール共重合体層を架橋しておくことが好ましい。この架橋操作を行わないと、後で行われる加熱・加硫工程において、変性エチレン−ビニルアルコール共重合体層が著しく変形し、均一な層を保持することができなくなり、得られる積層体がタイヤ用インナーライナーとして所定の機能を発揮しなくなるおそれがある。
エネルギー線としては、紫外線、電子線、Ｘ線、α線、γ線等の電離放射線が挙げられ、好ましくは電子線が挙げられる。
電子線の照射方法に関しては、樹脂フイルムを電子線照射装置に導入し、電子線を照射する方法が挙げられる。電子線の線量に関しては特に限定されないが、好ましくは１０〜６０Ｍｒａｄの範囲内である。照射する電子線量が１０Ｍｒａｄより低いと、架橋が進み難くなる。一方、照射する電子線量が６０Ｍｒａｄを超えると樹脂フイルムの劣化が進行しやすくなる。より好適には電子線量の範囲は２０〜５０Ｍｒａｄである。
In the above method, when the resin film constituting the layer (A) has a modified ethylene-vinyl alcohol copolymer layer, the resin film and the rubber-like elastic film or sheet are pasted via the adhesive composition layer. Before combining, the modified ethylene-vinyl alcohol copolymer layer is preferably crosslinked by irradiating the resin film with energy rays in advance. If this cross-linking operation is not performed, the modified ethylene-vinyl alcohol copolymer layer is remarkably deformed in the subsequent heating / vulcanizing step, and a uniform layer cannot be maintained, and the resulting laminate is a tire. There is a possibility that a predetermined function as an inner liner for a product may not be exhibited.
Examples of the energy rays include ionizing radiation such as ultraviolet rays, electron beams, X-rays, α rays, and γ rays, and electron beams are preferable.
As for the electron beam irradiation method, a method of introducing a resin film into an electron beam irradiation apparatus and irradiating the electron beam can be mentioned. Although it does not specifically limit regarding the dose of an electron beam, Preferably it exists in the range of 10-60 Mrad. When the electron dose to irradiate is lower than 10 Mrad, it becomes difficult to crosslink. On the other hand, when the electron dose to be irradiated exceeds 60 Mrad, the deterioration of the resin film easily proceeds. More preferably, the electron dose range is 20 to 50 Mrad.
前記加熱・加硫処理は、通常１００℃以上、好ましくは１２５〜２００℃、より好ましくは１３０〜１８０℃の温度で実施される。なお、本発明の空気入りタイヤの場合、前記加熱・加硫処理は、通常タイヤ加硫時に行われる。
本発明の空気入りタイヤに用いられるインナーライナー層は、特定組成の接着剤組成物を用いることにより、タック性が良好で、作業性よく作製し得る上、剥離抗力に優れるなどの特徴を有している。
図１は、本発明の係わるインナーライナー層を用いてなる空気入りタイヤの一例を示す部分断面図であって、該タイヤはビードコア１の周りに巻回されてコード方向がラジアル方向に向くカーカスプライを含むカーカス層２と、カーカス層のタイヤ半径方向内側に配設された本発明に係わる積層体からなるインナーライナー層３と、該カーカス層のクラウン部のタイヤ半径方向外側に配設された２枚のベルト層４を有するベルト部と、ベルト部の上部に配設されたトレッド部５と、トレッド部の左右に配置されたサイドウォール部６から構成されている。
図２は、前記空気入りタイヤにおける本発明に係わるインナーライナー層の一例の断面詳細図であって、インナーライナー層３は、変性エチレン−ビニルアルコール共重合体層１１の両面に、それぞれ熱可塑性ウレタン系エラストマー層１２ａ及び１２ｂがラミネートされてなる樹脂フイルム層１３と、ゴム状弾性体層１５が、接着剤層１４を介して接合され、一体化してなる構造を有している。なお、ゴム状弾性体層１５は、接着剤層１４とは反対側の面が、図１におけるカーカス層２と接合されている。
The heating / vulcanizing treatment is usually performed at a temperature of 100 ° C. or higher, preferably 125 to 200 ° C., more preferably 130 to 180 ° C. In the case of the pneumatic tire of the present invention, the heating / vulcanizing treatment is usually performed at the time of tire vulcanization.
The inner liner layer used in the pneumatic tire of the present invention has characteristics such as good tackiness, good workability, and excellent peeling resistance by using an adhesive composition having a specific composition. ing.
FIG. 1 is a partial sectional view showing an example of a pneumatic tire using an inner liner layer according to the present invention, in which the tire is wound around a bead core 1 and a carcass ply in which a cord direction is directed in a radial direction. A carcass layer 2, an inner liner layer 3 made of a laminate according to the present invention disposed on the inner side in the tire radial direction of the carcass layer, and 2 disposed on the outer side in the tire radial direction of the crown portion of the carcass layer. The belt portion includes a belt portion 4, a
FIG. 2 is a detailed cross-sectional view of an example of the inner liner layer according to the present invention in the pneumatic tire. The inner liner layer 3 is formed on both surfaces of the modified ethylene-vinyl
次に、本発明を実施例により、さらに詳細に説明するが、本発明は、これらの例によってなんら限定されるものではない。
製造例１ 変性エチレン−ビニルアルコール共重合体の製造
加圧反応槽に、エチレン含量４４モル％、ケン化度９９．９モル％のエチレン−ビニルアルコール共重合体（ＭＦＲ：５．５ｇ／１０分（１９０℃、２１．１８Ｎ荷重下）２質量部及びＮ−メチル−２−ピロリドン８質量部を仕込み、１２０℃で、２時間加熱攪拌することにより、エチレン−ビニルアルコール共重合体を完全に溶解させた。これにエポキシ化合物としてエポキシプロパン０．４質量部を添加後、１６０℃で４時間加熱した。加熱終了後、蒸留水１００質量部に析出させ、多量の蒸留水で充分にＮ−メチル−２−ピロリドン及び未反応のエポキシプロパンを洗浄し、変性エチレン−ビニルアルコール共重合体を得た。さらに、得られた変性エチレン−ビニルアルコール共重合体を粉砕機で粒子径２ｍｍ程度に細かくした後、再度多量の蒸留水で十分に洗浄した。洗浄後の粒子を８時間室温で真空乾燥した後、２軸押出機を用いて２００℃で溶融し、ペレット化した。
EXAMPLES Next, although an Example demonstrates this invention further in detail, this invention is not limited at all by these examples.
Production Example 1 Production of Modified Ethylene-Vinyl Alcohol Copolymer An ethylene-vinyl alcohol copolymer having an ethylene content of 44 mol% and a saponification degree of 99.9 mol% (MFR: 5.5 g / 10 min) was placed in a pressure reaction vessel. 2 parts by weight (under 190 ° C. and 21.18 N load) and 8 parts by weight of N-methyl-2-pyrrolidone were charged and stirred at 120 ° C. for 2 hours to completely dissolve the ethylene-vinyl alcohol copolymer. After adding 0.4 parts by weight of epoxy propane as an epoxy compound to this, it was heated for 4 hours at 160 ° C. After the heating, it was precipitated in 100 parts by weight of distilled water, and a sufficient amount of distilled water was sufficient for N-methyl. -2-pyrrolidone and unreacted epoxypropane were washed to obtain a modified ethylene-vinyl alcohol copolymer. The copolymer was fined to a particle size of about 2 mm with a pulverizer, and then thoroughly washed with a large amount of distilled water again.The washed particles were vacuum-dried at room temperature for 8 hours, and then 200 ° C. using a twin screw extruder. And then pelletized.
なお、上記エチレンービニルアルコール共重合体のエチレン含有量及びケン化度は、重水素化ジメチルスルホォキシドを溶媒とした1Ｈ−ＮＭＲ測定[日本電子社製［ＪＩＭ−ＧＸ−５００型]を使用]で得られたスペクトルから算出した値である。また、上記エチレンービニルアルコール共重合体のメルトフローレート（ＭＦＲ)は、メルトインデクサーＬ２２４[宝工業株式会社製]の内径９．５５ｍｍ、長さ１６２ｍｍのシリンダーにサンプルを充填し１９０℃で溶融した後、重さ２１６０ｇ、直径９．４８ｍｍのプランジャーを使用して均等に荷重をかけ、シリンダー中央に設けた径２．１ｍｍのオリフィスにより単位時間あたりに押し出される樹脂量（ｇ／１０分）から求めた。但しエチレン−ビニルアルコール共重合体の融点が１９０℃付近あるいは１９０℃を越える場合は、２１６０ｇの荷重下、融点以上の複数の温度で測定し、片対数グラフで絶対温度の逆数を横軸、ＭＦＲの対数を縦軸にプロットし１９０℃に外挿して算出した値をメルトフローレート（ＭＦＲ）とした。 The ethylene content and the degree of saponification of the ethylene-vinyl alcohol copolymer were measured by 1 H-NMR measurement using deuterated dimethyl sulfoxide as a solvent [JIM-GX-500 type manufactured by JEOL Ltd.]. It is a value calculated from the spectrum obtained in [Use]. Also, the melt flow rate (MFR) of the ethylene-vinyl alcohol copolymer was melted at 190 ° C. by filling a sample into a cylinder with an inner diameter of 9.55 mm and a length of 162 mm of a melt indexer L224 (manufactured by Takara Kogyo Co., Ltd.). After that, using a plunger with a weight of 2160 g and a diameter of 9.48 mm, load was evenly applied, and the amount of resin extruded per unit time by an orifice with a diameter of 2.1 mm provided in the center of the cylinder (g / 10 min) I asked for it. However, when the melting point of the ethylene-vinyl alcohol copolymer is around 190 ° C. or exceeds 190 ° C., it is measured at a plurality of temperatures higher than the melting point under a load of 2160 g. The melt flow rate (MFR) was calculated by plotting the logarithm of γ on the vertical axis and extrapolating to 190 ° C.
製造例２ ３層フイルムの作製
製造例１で得られた変性ＥＶＯＨと、エラストマーとして熱可塑性ポリウレタン（（株）クラレ製、クラミロン３１９０）とを使用し、２種３層共押出装置を用いて、下記共押出成形条件で３層フイルム（熱可塑性ポリウレタン層／変性ＥＶＯＨ層／熱可塑性ポリウレタン層）を作製した。各層の厚みは、変性ＥＶＯＨ層、熱可塑性ポリウレタン層ともに２０μｍである。
共押出成形条件は以下のとおりである。
層構成：
熱可塑性ポリウレタン／変性ＥＶＯＨ／熱可塑性ポリウレタン
（厚み２０／２０／２０、単位はμｍ）
各樹脂の押出温度：
Ｃ１／Ｃ２／Ｃ３／ダイ＝１７０／１７０／２２０／２２０℃
各樹脂の押出機仕様：
熱可塑性ポリウレタン：
２５ｍｍφ押出機 Ｐ２５−１８ＡＣ（大阪精機工作株式会社製）
変性ＥＶＯＨ：
２０ｍｍφ押出機 ラボ機ＭＥ型ＣＯ−ＥＸＴ（株式会社東洋精機製）
Ｔダイ仕様：
５００ｍｍ幅２種３層用 （株式会社プラスチック工学研究所製）
冷却ロールの温度：５０℃
引き取り速度：４ｍ／分
Production Example 2 Production of 3-layer film Using the modified EVOH obtained in Production Example 1 and a thermoplastic polyurethane (Kuraray Co., Ltd., Kuramiron 3190) as an elastomer, using a two-kind three-layer coextrusion apparatus, A three-layer film (thermoplastic polyurethane layer / modified EVOH layer / thermoplastic polyurethane layer) was produced under the following coextrusion molding conditions. The thickness of each layer is 20 μm for both the modified EVOH layer and the thermoplastic polyurethane layer.
The coextrusion molding conditions are as follows.
Layer structure:
Thermoplastic polyurethane / modified EVOH / thermoplastic polyurethane (thickness 20/20/20, unit is μm)
Extrusion temperature of each resin:
C1 / C2 / C3 / die = 170/170/220/220 ° C.
Extruder specifications for each resin:
Thermoplastic polyurethane:
25mmφ extruder P25-18AC (manufactured by Osaka Seiki Co., Ltd.)
Modified EVOH:
20mmφ Extruder Lab Machine ME Type CO-EXT (Toyo Seiki Co., Ltd.)
T-die specification:
500mm width for 2 types and 3 layers (Plastic Engineering Laboratory Co., Ltd.)
Cooling roll temperature: 50 ° C
Pickup speed: 4m / min
製造例３ 未加硫ゴム状弾性体シートの作製
下記の配合のゴム組成物を調製し、厚さ５００μｍの未加硫ゴム状弾性体シートを作製した。
ゴム組成物（配合単位：質量部）
＊天然ゴム ３０
＊Ｂｒ-ＩＩＲ：(ＪＳＲ(株)製 Ｂｒｏｍｏｂｕｔｙｌ ２２４４) ７０
＊ＧＰＦカーボンブラック：(旭カーボン社製＃５５) ６０
＊ＳＵＮＰＡＲ２２８０(日本サン石油社製) ７
＊ステアリン酸：(旭電化工業社製) １
＊加硫促進剤：(大内新興化学工業社製 ノクセラー ＤＭ) １．３
＊酸化亜鉛：(白水化学工業社製) ３
＊硫黄：(軽井沢精錬所製) ０．５
Production Example 3 Production of Unvulcanized Rubber-like Elastic Sheet A rubber composition having the following composition was prepared, and an unvulcanized rubber-like elastic sheet having a thickness of 500 μm was produced.
Rubber composition (compounding unit: parts by mass)
* Natural rubber 30
* Br-IIR: (Bromobutyl 2244 manufactured by JSR Corporation) 70
* GPF carbon black: (Asahi Carbon Corporation # 55) 60
* SUNPAR 2280 (Nihon Sun Oil Co., Ltd.) 7
* Stearic acid: (Asahi Denka Kogyo Co., Ltd.) 1
* Vulcanization accelerator: (Noxeller DM manufactured by Ouchi Shinsei Chemical Co., Ltd.) 1.3
* Zinc oxide: (Shiramizu Chemical Co., Ltd.) 3
* Sulfur: (Karuizawa Smelter) 0.5
製造例４ 接着剤組成物及び塗工液の調製
接着剤組成物（配合単位：質量部）
＊Ｂｒ-ＩＩＲ：(ＪＳＲ社製 Ｂｒｏｍｏｂｕｔｙｌ ２２４４) ９０
＊クロロスルホン化ポリエチレン：（Ｄｕｐｎｔ・Ｄｏｗ ＥｌａｓｔｏｍｅｒｓＬＬＣ社製 ハイパロン） １０
＊カーボンブラック：（東海カーボン社製 シーストＮＢ） １０
＊フェノール樹脂：（住友ベークライト社製 ＰＲ-ＳＣ-４００） ２０
＊ステアリン酸：（新日本理化社製 ５０Ｓ ） １
＊酸化亜鉛：(白水化学工業社製 ハクスイテック) ３
＊Ｐ-ジニトロソベンゼン：（大内新興化学工業社製バルノックＤＮＢ） ３
＊１，４フェニレンジマレイミド：（大内新興化学工業社製バルノックＰＭ） ３
＊加硫促進剤：（大内新興化学工業社製 ノクセラーＺＴＣ） １
＊加硫促進剤：（大内新興化学工業社製 ノクセラーＤＭ） ０．５
＊加硫促進剤：（大内新興化学工業社製 ノクセラーＤ） １
＊硫黄：（鶴見化学社製 金華印微粉硫黄） １．５
上記配合組成に従って常法により混練りした後、該接着剤組成物を、有機溶剤としてトルエン（δ値：１８．２ＭＰａ1/2）１０００質量部に加え、溶解又は分散して各接着剤塗工液を調製した。
Production Example 4 Preparation of Adhesive Composition and Coating Solution Adhesive Composition (Formulation Unit: Mass Part)
* Br-IIR: (Bromobutyl 2244 made by JSR) 90
* Chlorosulfonated polyethylene: (Hypalon manufactured by Dupnt Dow Elastomers LLC) 10
* Carbon black: (Toast Carbon Co., Ltd. Seast NB) 10
* Phenolic resin: (PR-SC-400, manufactured by Sumitomo Bakelite) 20
* Stearic acid: (New Nippon Rika Co., Ltd. 50S) 1
* Zinc oxide: (Hakusuitec manufactured by Hakusui Chemical Co., Ltd.) 3
* P-dinitrosobenzene: (Valnock DNB manufactured by Ouchi Shinsei Chemical Co., Ltd.) 3
* 1,4 phenylene dimaleimide: (Valnock PM manufactured by Ouchi Shinsei Chemical Co., Ltd.) 3
* Vulcanization accelerator: (Ouchi Shinsei Chemical Co., Ltd. Noxeller ZTC) 1
* Vulcanization accelerator: (Noxeller DM manufactured by Ouchi Shinsei Chemical Co., Ltd.) 0.5
* Vulcanization accelerator: (Noxeller D manufactured by Ouchi Shinsei Chemical Co., Ltd.) 1
* Sulfur: (Tsurumi Chemical Co., Ltd. Jinhua seal fine powder sulfur) 1.5
After kneading by a conventional method according to the above composition, the adhesive composition is added to 1000 parts by mass of toluene (δ value: 18.2 MPa 1/2 ) as an organic solvent, and dissolved or dispersed to apply each adhesive. A liquid was prepared.
実施例１
日新ハイボルテージ株式会社製電子線照射装置「生産用キュアトロンＥＢＣ２００-１００」を使用して、製造例２で得られた三層フイルム（熱可塑性ポリウレタン／変性ＥＶＯＨ／熱可塑性ポリウレタン）に、加速電圧２００ｋＶ、照射エネルギー３０Ｍｒａｄの条件にて電子線照射し架橋処理を施し、多層熱可塑性樹脂フイルムとして使用した。
製造例４で得られた接着剤組成物１００質量部に、有機溶剤としてトルエン１０００質量部に加え、溶解又は分散して接着剤塗工液を調製した。その塗工液を、上記架橋した多層熱可塑性樹脂フイルムの片面に塗布し、１００℃２分間乾燥処理した後、接着剤層を有する多層熱可塑製樹脂フイルムを２０cm四方の正方形に切りとりさらに１００℃で２分間処理して残存揮発分を測定し、平行して製造例３で得られた厚み５００μｍの未加硫ゴム状弾性シートと貼り合せることにより、インナーライナーを作製した。得られたインナーライナーを用い、常法により加硫工程を経て乗用車用空気入りタイヤ（１９５／６５Ｒ１５）を作製した。
試作タイヤのインナーライナーの外観評価、接着剤層中に残存する揮発分の測定結果について第１表に示す。
Example 1
Using the Nisshin High Voltage Co., Ltd. electron beam irradiation device "Curetron EBC200-100 for production", the three-layer film (thermoplastic polyurethane / modified EVOH / thermoplastic polyurethane) obtained in Production Example 2 was accelerated. The film was irradiated with an electron beam under the conditions of a voltage of 200 kV and an irradiation energy of 30 Mrad, subjected to crosslinking treatment, and used as a multilayer thermoplastic resin film.
To 100 parts by mass of the adhesive composition obtained in Production Example 4, 1000 parts by mass of toluene as an organic solvent was dissolved or dispersed to prepare an adhesive coating solution. The coating solution was applied to one side of the crosslinked multilayer thermoplastic resin film, dried at 100 ° C. for 2 minutes, and then the multilayer thermoplastic resin film having an adhesive layer was cut into a 20 cm square and further 100 ° C. The remaining volatile matter was measured by treating for 2 minutes, and the inner liner was prepared by laminating it in parallel with the unvulcanized rubber-like elastic sheet having a thickness of 500 μm obtained in Production Example 3. Using the obtained inner liner, a pneumatic tire for passenger cars (195 / 65R15) was produced through a vulcanization step by a conventional method.
Table 1 shows the appearance evaluation of the inner liner of the prototype tire and the measurement results of the volatile matter remaining in the adhesive layer.
尚、残存揮発分の測定及び試作タイヤのタイヤ内面確認及び使用可否判断については以下の方法に基づいて行った。
（１）残存揮発成分量測定
接着剤を塗布して乾燥処理した架橋フイルム（ａ）と、接着剤を塗布していない架橋フイルム（ｂ）をそれぞれ２０ｃｍ四方の正方形に切り、それぞれの質量を測定したものを質量１、質量２とし、その後にそれらを１２０℃の恒温槽中に２時間入れた後に再度それぞれの質量を測定し、それぞれの質量を測定したものを質量１'、質量２'として、以下の計算を行い揮発成分量とした。
揮発成分量（質量%）＝１００-（質量１'-質量２'）/（質量１-質量２）×１００
（２）試作タイヤ内面確認及び使用可否判断
加硫工程を経て製造されたタイヤの内面を確認した。内面性状について発泡の有無を確認し、性状問題なく製品として使用可能なタイヤを可、外観上タイヤ性能に問題あると考えられ使用不可能なタイヤを否とした。
In addition, the measurement of residual volatile matter, the tire inner surface confirmation of the prototype tire, and the determination of availability were performed based on the following methods.
(1) Measurement of the amount of residual volatile components Cross-linked film (a) coated with an adhesive and dried and cross-linked film (b) coated with no adhesive are cut into 20 cm squares, and the respective masses are measured. The resulting mass was set to mass 1 and mass 2, and then they were placed in a constant temperature bath at 120 ° C. for 2 hours, and then the respective masses were measured again. The masses measured were designated as mass 1 ′ and mass 2 ′. The following calculation was performed to determine the amount of volatile components.
Volatile component amount (mass%) = 100− (mass 1′−mass 2 ′) / (mass 1−mass 2) × 100
(2) Prototype tire inner surface confirmation and use availability determination The inner surface of the tire manufactured through the vulcanization process was confirmed. The inner surface property was checked for foaming, and a tire that could be used as a product without any property problem was acceptable.
実施例２
実施例1において、乾燥条件が、１００℃で１分間乾燥する処理をしたこと以外は実施例１と同様にして評価を行った。試作タイヤのインナーライナーの外観評価、接着剤層中に残存する揮発分の測定結果について第１表に示す。
Example 2
In Example 1, the evaluation was performed in the same manner as in Example 1 except that the drying condition was a process of drying at 100 ° C. for 1 minute. Table 1 shows the appearance evaluation of the inner liner of the prototype tire and the measurement results of the volatile matter remaining in the adhesive layer.
比較例１
実施例1において、乾燥条件が、室温放置で２分間乾燥する処理をしたこと以外は実施例１と同様にして評価を行った。試作タイヤのインナーライナーの外観評価、接着剤層中に残存する揮発分の測定結果について第１表に示す。
Comparative Example 1
In Example 1, the evaluation was performed in the same manner as in Example 1 except that the drying condition was a treatment for 2 minutes at room temperature. Table 1 shows the appearance evaluation of the inner liner of the prototype tire and the measurement results of the volatile matter remaining in the adhesive layer.
比較例２
実施例1において、乾燥条件が、１００℃で１０秒間乾燥する処理をしたこと以外は実施例１と同様にして評価を行った。試作タイヤのインナーライナーの外観評価、接着剤層中に残存する揮発分の測定結果について第１表に示す。
Comparative Example 2
In Example 1, the evaluation was performed in the same manner as in Example 1 except that the drying was performed at 100 ° C. for 10 seconds. Table 1 shows the appearance evaluation of the inner liner of the prototype tire and the measurement results of the volatile matter remaining in the adhesive layer.
本発明の空気入りタイヤは、薄ゲージ化が可能なインナーライナー層として単層又は多層熱可塑性フイルム層を使用するタイヤを製造する際に、前記熱可塑性樹脂フイルム層とゴム弾性層とを接着剤組成物を含む接着剤を用いて接合一体化させた積層体とし、加熱・加硫後における該接着剤に由来する製造上の気泡発生等の不具合点が無く、かつ剥離抗力の優れた前記積層体を用いた空気入りタイヤを提供することができる。 The pneumatic tire of the present invention has an adhesive agent for bonding the thermoplastic resin film layer and the rubber elastic layer when manufacturing a tire using a single layer or multilayer thermoplastic film layer as an inner liner layer that can be made thinner. A laminated body joined and integrated using an adhesive containing the composition, the laminated body having no problems such as production of bubbles derived from the adhesive after heating and vulcanization, and having excellent peeling resistance A pneumatic tire using the body can be provided.
１：ビートコア
２：カーカス層
３：インナーライナー層
４：ベルト部
５：トレッド部
６：サイドウォール部
７：ビードフィラー
１１：変性エチレン−ビニルアルコール共重合体層
１２ａ、１２ｂ：熱可塑性ウレタン系エラストマー層
１３：樹脂フイルム層
１４：接着剤層
１５：ゴム状弾性体層
1: Beat core 2: Carcass layer 3: Inner liner layer 4: Belt portion 5: Tread portion 6: Side wall portion 7: Bead filler 11: Modified ethylene-vinyl
Claims (22)