JP2007245551A - Oriented laminated film - Google Patents
Oriented laminated film Download PDFInfo
- Publication number
- JP2007245551A JP2007245551A JP2006072546A JP2006072546A JP2007245551A JP 2007245551 A JP2007245551 A JP 2007245551A JP 2006072546 A JP2006072546 A JP 2006072546A JP 2006072546 A JP2006072546 A JP 2006072546A JP 2007245551 A JP2007245551 A JP 2007245551A
- Authority
- JP
- Japan
- Prior art keywords
- laminated film
- film
- layer
- stretched laminated
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
液晶表示装置には、液晶セルの複屈折による位相差を補償するために位相差フィルムが広く用いられている。これまで、様々な構成の位相差フィルムが提案されてきたが、透明樹脂を延伸により配向させて得られる延伸フィルムが広く用いられてきた。該延伸フィルムとしては、耐熱性等に優れるポリカーボネート樹脂からなるフィルムが挙げられるが、特に、耐熱性に優れ、吸湿性が低く、光弾性定数が小さい脂環式ポリオレフィン樹脂からなるフィルムが近年注目を浴びている。 In a liquid crystal display device, a retardation film is widely used to compensate for a retardation due to birefringence of a liquid crystal cell. Various retardation films have been proposed so far, and stretched films obtained by orienting transparent resins by stretching have been widely used. Examples of the stretched film include a film made of a polycarbonate resin having excellent heat resistance and the like, and in particular, a film made of an alicyclic polyolefin resin having excellent heat resistance, low hygroscopicity, and a small photoelastic constant has recently attracted attention. I'm bathing.
しかしながら、脂環式ポリオレフィン樹脂からなる延伸フィルムは従来の材料に対し接着性に劣るという欠点があった。特に偏光板の保護フィルムと位相差フィルムを兼ねる用途においては偏光子のPVAとの接着強度が劣ることは大きな問題であった(特許文献1参照)。 However, a stretched film made of an alicyclic polyolefin resin has a drawback that it has poor adhesion to conventional materials. In particular, in applications where both a protective film for a polarizing plate and a retardation film are used, it is a big problem that the adhesive strength between the polarizer and PVA is inferior (see Patent Document 1).
かかる問題に対し、脂環式ポリオレフィンフィルムの表面に対してコロナ処理を行ったり接着剤を改良したりすることにより解決が試みられてきたが(特許文献2参照)、未だ接着強度の改善は不十分である。 To solve this problem, attempts have been made to solve the problem by subjecting the surface of the alicyclic polyolefin film to corona treatment or improving the adhesive (see Patent Document 2). It is enough.
本発明は、上述した従来技術の問題点に鑑みてなされたものであり、接着性が改善され、偏光板や液晶表示装置の材料として有用なフィルムを提供することを目的とする。 The present invention has been made in view of the above-described problems of the prior art, and an object thereof is to provide a film having improved adhesiveness and useful as a material for a polarizing plate or a liquid crystal display device.
本発明者は上記課題を改善するために鋭意研究を重ねた結果、特定のガラス転移温度、及び配向度を持つ樹脂層を積層してなり、かつ、厚みの調整された延伸積層フィルムを見出し、本発明に到達した。
すなわち、本発明によれば下記のものが提供される。
〔1〕 熱可塑性樹脂からなるA層と、脂環式ポリオレフィン樹脂からなるB層とを、少なくとも1枚ずつ積層してなる延伸積層フィルムであって、
熱可塑性樹脂のガラス転移温度をTgA(℃)、脂環式ポリオレフィン樹脂のガラス転移温度TgB(℃)を、延伸積層フィルムの平均厚みをT(μm)、A層の全平均厚みをTS(μm)、A層の面配向係数をPとしたとき、
a)TgA+10(℃)≦TgB(℃)であり、
b)0.03×T<TS<0.1×Tであり、
c)P≦1.0×10-3である、
ことを特徴とする延伸積層フィルム。
〔2〕 前記TgAが、100〜125(℃)であることを特徴とする〔1〕に記載の延伸積層フィルム。
〔3〕 前記TgBが、130(℃)以上であることを特徴とする〔1〕または〔2〕に記載の延伸積層フィルム。
〔4〕 前記脂環式ポリオレフィン樹脂が、主鎖に脂環構造を有するポリオレフィン樹脂であることを特徴とする〔1〕〜〔3〕のいずれかに記載の延伸積層フィルム。
〔5〕 前記熱可塑性樹脂が、脂環構造を有するポリオレフィン樹脂であることを特徴とする〔1〕〜〔4〕のいずれかに記載の延伸積層フィルム。
〔6〕 A層−B層−A層の順番に積層してなることを特徴とする〔1〕〜〔5〕のいずれかに記載の延伸積層フィルム。
〔7〕 〔1〕〜〔6〕のいずれかに記載の延伸積層フィルムと、偏光膜とを積層してなる偏光板。
〔8〕 〔1〕〜〔6〕のいずれかに記載の延伸積層フィルムを備えてなる液晶表示装置。
As a result of intensive studies to improve the above problems, the present inventor has laminated a resin layer having a specific glass transition temperature and an orientation degree, and has found a stretched laminated film whose thickness is adjusted, The present invention has been reached.
That is, according to the present invention, the following is provided.
[1] A stretched laminated film obtained by laminating at least one A layer composed of a thermoplastic resin and B layer composed of an alicyclic polyolefin resin,
The glass transition temperature of the thermoplastic resin is Tg A (° C.), the glass transition temperature Tg B (° C.) of the alicyclic polyolefin resin, the average thickness of the stretched laminated film is T (μm), and the total average thickness of the A layer is T S (μm), when the plane orientation coefficient of the A layer is P,
a) Tg A +10 (° C.) ≦ Tg B (° C.)
b) 0.03 × T <T S <0.1 × T,
c) P ≦ 1.0 × 10 −3 .
A stretched laminated film characterized by that.
[2] The stretched laminated film according to [1], wherein the Tg A is 100 to 125 (° C.).
[3] The stretched laminated film according to [1] or [2], wherein the Tg B is 130 (° C.) or more.
[4] The stretched laminated film according to any one of [1] to [3], wherein the alicyclic polyolefin resin is a polyolefin resin having an alicyclic structure in the main chain.
[5] The stretched laminated film according to any one of [1] to [4], wherein the thermoplastic resin is a polyolefin resin having an alicyclic structure.
[6] The stretched laminated film according to any one of [1] to [5], which is laminated in the order of A layer-B layer-A layer.
[7] A polarizing plate formed by laminating the stretched laminated film according to any one of [1] to [6] and a polarizing film.
[8] A liquid crystal display device comprising the stretched laminated film according to any one of [1] to [6].
本発明によれば、厚みムラが小さく長尺で巻取り可能であり、接着性が顕著に改善された延伸積層フィルムが提供される。係る本発明の延伸積層フィルムは、偏光板、液晶表示装置のほか、各種光学材料として利用することができる。 According to the present invention, it is possible to provide a stretched laminated film having a small thickness unevenness and capable of being wound up in a long length and having significantly improved adhesiveness. The stretched laminated film of the present invention can be used as various optical materials in addition to polarizing plates and liquid crystal display devices.
本発明の延伸積層フィルムは、熱可塑性樹脂からなるA層と、脂環式ポリオレフィン樹脂からなるB層とを積層してなるフィルムである。ここで脂環式ポリオレフィン樹脂とは、その繰り返し構造中に脂環構造を含有するポリオレフィン樹脂である。脂環構造はポリオレフィンの主鎖、側鎖のいずれに存在していても良いが、その中でも、機械強度、耐熱性などの観点から、主鎖に脂環構造を含有するポリオレフィン樹脂が好ましい。 The stretched laminated film of the present invention is a film formed by laminating an A layer made of a thermoplastic resin and a B layer made of an alicyclic polyolefin resin. Here, the alicyclic polyolefin resin is a polyolefin resin containing an alicyclic structure in its repeating structure. The alicyclic structure may be present in either the main chain or the side chain of the polyolefin, and among them, a polyolefin resin containing an alicyclic structure in the main chain is preferable from the viewpoint of mechanical strength, heat resistance and the like.
上記の脂環構造を含有するポリオレフィン樹脂の脂環構造としては、飽和脂環炭化水素(シクロアルカン)構造、不飽和脂環炭化水素(シクロアルケン)構造などが挙げられるが、機械強度、耐熱性などの観点から、シクロアルカン構造やシクロアルケン構造が好ましく、中でもシクロアルカン構造が最も好ましい。脂環構造を構成する炭素原子数には、格別な制限はないが、通常4〜30個、好ましくは5〜20個、より好ましくは5〜15個の範囲であるときに、機械強度、耐熱性、及びフィルムの成形性の特性が高度にバランスされ、好適である。本発明に使用される脂環式ポリオレフィン樹脂中の脂環構造を含有してなる繰り返し単位の割合は、使用目的に応じて適宜選択すればよいが、好ましくは55重量%以上、さらに好ましくは70重量%以上、特に好ましくは90重量%以上である。脂環式ポリオレフィン樹脂中の脂環構造を有する繰り返し単位の割合がこの範囲にあると、本発明の延伸積層フィルムの透明性および耐熱性が向上する。 Examples of the alicyclic structure of the polyolefin resin containing the alicyclic structure include a saturated alicyclic hydrocarbon (cycloalkane) structure and an unsaturated alicyclic hydrocarbon (cycloalkene) structure, but mechanical strength and heat resistance. From these viewpoints, a cycloalkane structure or a cycloalkene structure is preferable, and a cycloalkane structure is most preferable. The number of carbon atoms constituting the alicyclic structure is not particularly limited, but is usually 4 to 30, preferably 5 to 20, and more preferably 5 to 15 in the range of mechanical strength and heat resistance. Properties and film formability are highly balanced and suitable. The proportion of the repeating unit containing an alicyclic structure in the alicyclic polyolefin resin used in the present invention may be appropriately selected according to the purpose of use, but is preferably 55% by weight or more, more preferably 70%. % By weight or more, particularly preferably 90% by weight or more. When the ratio of the repeating unit having an alicyclic structure in the alicyclic polyolefin resin is within this range, the transparency and heat resistance of the stretched laminated film of the present invention are improved.
脂環式ポリオレフィン樹脂としては、ノルボルネン系樹脂、単環の環状オレフィン系樹脂、環状共役ジエン系樹脂、ビニル脂環式炭化水素系樹脂、及び、これらの水素化物等を挙げることができる。これらの中で、ノルボルネン系樹脂は、透明性と成形性が良好なため、好適に用いることができる。脂環式ポリオレフィン樹脂は、熱可塑性樹脂であることが好ましい。 Examples of the alicyclic polyolefin resin include a norbornene resin, a monocyclic olefin resin, a cyclic conjugated diene resin, a vinyl alicyclic hydrocarbon resin, and hydrides thereof. Among these, norbornene-based resins can be suitably used because of their good transparency and moldability. The alicyclic polyolefin resin is preferably a thermoplastic resin.
ノルボルネン系樹脂としては、例えば、ノルボルネン構造を有する単量体の開環重合体若しくはノルボルネン構造を有する単量体と他の単量体との開環共重合体又はそれらの水素化物、ノルボルネン構造を有する単量体の付加重合体若しくはノルボルネン構造を有する単量体と他の単量体との付加共重合体又はそれらの水素化物等を挙げることができる。これらの中で、ノルボルネン構造を有する単量体の開環(共)重合体水素化物(水素添加物)は、透明性、成形性、耐熱性、低吸湿性、寸法安定性、軽量性などの観点から、特に好適に用いることができる。 Examples of the norbornene-based resin include a ring-opening polymer of a monomer having a norbornene structure, a ring-opening copolymer of a monomer having a norbornene structure and another monomer, a hydride thereof, and a norbornene structure. An addition polymer of a monomer having a monomer, an addition copolymer of a monomer having a norbornene structure and another monomer, or a hydride thereof. Among these, ring-opening (co) polymer hydrides (hydrogenated products) of monomers having a norbornene structure have transparency, moldability, heat resistance, low hygroscopicity, dimensional stability, light weight, etc. From the viewpoint, it can be particularly preferably used.
ノルボルネン構造を有する単量体としては、ビシクロ〔2.2.1〕ヘプト−2−エン(慣用名:ノルボルネン)、トリシクロ〔4.3.0.12,5〕デカ−3,7−ジエン(慣用名:ジシクロペンタジエン)、7,8−ベンゾトリシクロ〔4.3.0.12,5〕デカ−3−エン(慣用名:メタノテトラヒドロフルオレン)、テトラシクロ〔4.4.0.12,5.17,10〕ドデカ−3−エン(慣用名:テトラシクロドデセン)、およびこれらの化合物の誘導体(例えば、環に置換基を有するもの)などを挙げることができる。ここで、置換基としては、例えばアルキル基、アルキレン基、極性基などを挙げることができる。また、これらの置換基は、同一または相異なって複数個が環に結合していてもよい。ノルボルネン構造を有する単量体は1種単独で、あるいは2種以上を組み合わせて用いることができる。 Examples of monomers having a norbornene structure include bicyclo [2.2.1] hept-2-ene (common name: norbornene), tricyclo [4.3.0.1 2,5 ] deca-3,7-diene. (Common name: dicyclopentadiene), 7,8-benzotricyclo [4.3.0.1 2,5 ] dec-3-ene (common name: methanotetrahydrofluorene), tetracyclo [4.4.0. 1 2,5 . 1 7,10 ] dodec-3-ene (common name: tetracyclododecene), and derivatives of these compounds (for example, those having a substituent in the ring). Here, examples of the substituent include an alkyl group, an alkylene group, and a polar group. Moreover, these substituents may be the same or different and a plurality may be bonded to the ring. Monomers having a norbornene structure can be used singly or in combination of two or more.
極性基の種類としては、ヘテロ原子、またはヘテロ原子を有する原子団などが挙げられる。ヘテロ原子としては、例えば、酸素原子、窒素原子、硫黄原子、ケイ素原子、ハロゲン原子などが挙げられる。極性基の具体例としては、カルボキシル基、カルボニルオキシカルボニル基、エポキシ基、ヒドロキシル基、オキシ基、エステル基、シラノール基、シリル基、アミノ基、ニトリル基、スルホン基などが挙げられる。 Examples of the polar group include a hetero atom or an atomic group having a hetero atom. Examples of the hetero atom include an oxygen atom, a nitrogen atom, a sulfur atom, a silicon atom, and a halogen atom. Specific examples of the polar group include a carboxyl group, a carbonyloxycarbonyl group, an epoxy group, a hydroxyl group, an oxy group, an ester group, a silanol group, a silyl group, an amino group, a nitrile group, and a sulfone group.
ノルボルネン構造を有する単量体と開環共重合可能な他の単量体としては、シクロヘキセン、シクロヘプテン、シクロオクテンなどのモノ環状オレフィン類およびその誘導体;シクロヘキサジエン、シクロヘプタジエンなどの環状共役ジエンおよびその誘導体;などが挙げられる。 Other monomers capable of ring-opening copolymerization with a monomer having a norbornene structure include monocyclic olefins such as cyclohexene, cycloheptene, and cyclooctene and derivatives thereof; cyclic conjugated dienes such as cyclohexadiene and cycloheptadiene; Derivatives thereof; and the like.
ノルボルネン構造を有する単量体の開環重合体およびノルボルネン構造を有する単量体と共重合可能な他の単量体との開環共重合体は、単量体を公知の開環重合触媒の存在下に(共)重合することにより得ることができる。 A ring-opening polymer of a monomer having a norbornene structure and a ring-opening copolymer of a monomer having a norbornene structure and another monomer copolymerizable with the monomer have a known ring-opening polymerization catalyst. It can be obtained by (co) polymerization in the presence.
ノルボルネン構造を有する単量体と付加共重合可能な他の単量体としては、例えば、エチレン、プロピレン、1−ブテンなどの炭素数2〜20のα−オレフィンおよびこれらの誘導体;シクロブテン、シクロペンテン、シクロヘキセンなどのシクロオレフィンおよびこれらの誘導体;1,4−ヘキサジエン、4−メチル−1,4−ヘキサジエン、5−メチル−1,4−ヘキサジエンなどの非共役ジエンなどが挙げられる。これらの単量体は1種単独で、あるいは2種以上を組み合わせて用いることができる。これらの中でも、α−オレフィンが好ましく、エチレンがより好ましい。 Examples of other monomers that can be addition copolymerized with a monomer having a norbornene structure include α-olefins having 2 to 20 carbon atoms such as ethylene, propylene, and 1-butene, and derivatives thereof; cyclobutene, cyclopentene, And cycloolefins such as cyclohexene and derivatives thereof; non-conjugated dienes such as 1,4-hexadiene, 4-methyl-1,4-hexadiene, 5-methyl-1,4-hexadiene, and the like. These monomers can be used alone or in combination of two or more. Among these, α-olefin is preferable and ethylene is more preferable.
ノルボルネン構造を有する単量体の付加重合体およびノルボルネン構造を有する単量体と共重合可能な他の単量体との付加共重合体は、単量体を公知の付加重合触媒の存在下に重合することにより得ることができる。 An addition polymer of a monomer having a norbornene structure and an addition copolymer of a monomer having a norbornene structure with another monomer copolymerizable with a monomer having a norbornene structure are prepared in the presence of a known addition polymerization catalyst. It can be obtained by polymerization.
ノルボルネン構造を有する単量体の開環重合体の水素添加物、ノルボルネン構造を有する単量体とこれと開環共重合可能なその他の単量体との開環共重合体の水素添加物、ノルボルネン構造を有する単量体の付加重合体の水素添加物、およびノルボルネン構造を有する単量体とこれと共重合可能なその他の単量体との付加重合体の水素添加物は、これらの重合体の溶液に、ニッケル、パラジウムなどの遷移金属を含む公知の水素添加触媒を添加し、炭素−炭素不飽和結合を好ましくは90%以上水素添加することによって得ることができる。 A hydrogenated product of a ring-opening polymer of a monomer having a norbornene structure, a hydrogenated product of a ring-opening copolymer of a monomer having a norbornene structure and another monomer capable of ring-opening copolymerization thereof, Hydrogenated products of addition polymers of monomers having a norbornene structure and hydrogenated products of addition polymers of monomers having a norbornene structure and other monomers copolymerizable therewith are not A known hydrogenation catalyst containing a transition metal such as nickel or palladium is added to the combined solution, and the carbon-carbon unsaturated bond is preferably hydrogenated by 90% or more.
ノルボルネン系樹脂の中でも、繰り返し単位として、X:ビシクロ〔3.3.0〕オクタン−2,4−ジイル−エチレン構造と、Y:トリシクロ〔4.3.0.12,5〕デカン−7,9−ジイル−エチレン構造とを有し、これらの繰り返し単位の含有量が、ノルボルネン系樹脂の繰り返し単位全体に対して90重量%以上であり、かつ、Xの含有割合とYの含有割合との比が、X:Yの重量比で100:0〜40:60であるものが好ましい。このような樹脂を用いることにより、本発明の延伸積層フィルムを長期的に寸法変化がなく、光学特性の安定性に優れるものとすることができる。 Among norbornene-based resins, X: bicyclo [3.3.0] octane-2,4-diyl-ethylene structure and Y: tricyclo [4.3.0.1 2,5 ] decane-7 are used as repeating units. , 9-diyl-ethylene structure, the content of these repeating units is 90% by weight or more based on the entire repeating units of the norbornene-based resin, and the content ratio of X and the content ratio of Y Is preferably 100: 0 to 40:60 by weight ratio of X: Y. By using such a resin, it is possible to make the stretched laminated film of the present invention have no dimensional change over a long period of time and have excellent optical property stability.
本発明に用いる脂環式ポリオレフィン樹脂の分子量は使用目的に応じて適宜選定されるが、溶媒としてシクロヘキサン(樹脂が溶解しない場合はトルエン)を用いるゲル・パーミエーション・クロマトグラフィーで測定したポリイソプレン(溶媒がトルエンのときはポリスチレン換算)の重量平均分子量(Mw)で、通常10,000〜100,000、好ましくは15,000〜80,000、より好ましくは20,000〜50,000である。重量平均分子量がこのような範囲にあるときに、フィルムの機械的強度および成型加工性が高度にバランスされ好適である。 The molecular weight of the alicyclic polyolefin resin used in the present invention is appropriately selected according to the purpose of use, but polyisoprene measured by gel permeation chromatography using cyclohexane (toluene when the resin is not dissolved) as a solvent ( When the solvent is toluene, the weight average molecular weight (Mw) in terms of polystyrene is usually 10,000 to 100,000, preferably 15,000 to 80,000, more preferably 20,000 to 50,000. When the weight average molecular weight is in such a range, the mechanical strength and molding processability of the film are highly balanced and suitable.
脂環式ポリオレフィン樹脂の分子量分布(重量平均分子量(Mw)/数平均分子量(Mn))は特に制限されないが、通常1.0〜10.0、好ましくは1.1〜4.0、より好ましくは1.2〜3.5の範囲である。 The molecular weight distribution (weight average molecular weight (Mw) / number average molecular weight (Mn)) of the alicyclic polyolefin resin is not particularly limited, but is usually 1.0 to 10.0, preferably 1.1 to 4.0, more preferably. Is in the range of 1.2 to 3.5.
本発明に用いる脂環式ポリオレフィン樹脂は、光弾性係数の絶対値が10×10-12Pa-1以下であることが好ましく、7×10-12Pa-1以下であることがより好ましく、4×10-12Pa-1以下であることが特に好ましい。光弾性係数Cは、複屈折をΔn、応力をσとしたとき、
C=Δn/σ
で表される値である。脂環式ポリオレフィン樹脂の光弾性係数が10×10-12Pa-1を超えると、本発明の延伸積層フィルムの面内レターデーションのバラツキが大きくなるおそれがある。
Alicyclic polyolefin resin used in the present invention preferably has an absolute value of the photoelastic coefficient is 10 × 10 -12 Pa -1 or less, more preferably 7 × 10 -12 Pa -1 or less, 4 It is particularly preferable that it is 10 × 10 −12 Pa −1 or less. The photoelastic coefficient C is expressed as follows: birefringence is Δn and stress is σ.
C = Δn / σ
It is a value represented by If the photoelastic coefficient of the alicyclic polyolefin resin exceeds 10 × 10 −12 Pa −1 , the in-plane retardation of the stretched laminated film of the present invention may increase.
本発明の延伸積層フィルムにおいては、上述の脂環式ポリオレフィン樹脂からなるB層に加え、熱可塑性樹脂からなるA層が含まれる。ここで熱可塑性樹脂としては、各種の熱可塑性樹脂を挙げることができ、例えば、脂環式ポリオレフィン樹脂、ポリエチレンやポリプロピレン等の鎖状オレフィン系重合体、トリアセチルセルロース、ポリビニルアルコール、ポリイミド、ポリアリレート、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエステル、ポリカーボネート、ポリスルホン、ポリエーテルスルホン、ポリアクリレート、ポリエステルサルホン、変性アクリルポリマー等が挙げられる。これらの中でも、透明性、低吸湿性、寸法安定性、軽量性の観点から脂環構造を有するポリオレフィン樹脂が好ましく、中でも、主鎖に脂環構造を有するポリオレフィン樹脂が特に好ましい。なお、A層に好ましく用いる脂環構造を有するポリオレフィン樹脂の具体例としては、上述の脂環構造を有するポリオレフィン樹脂(B層に用いる樹脂として例示したもの)(但し、下述のように、TgA+10(℃)≦TgB(℃)を満たすもの)を挙げることができる。 The stretched laminated film of the present invention includes an A layer made of a thermoplastic resin in addition to the B layer made of the alicyclic polyolefin resin. Here, examples of the thermoplastic resin include various thermoplastic resins, such as alicyclic polyolefin resins, chain olefin polymers such as polyethylene and polypropylene, triacetyl cellulose, polyvinyl alcohol, polyimide, polyarylate. Polyethylene terephthalate, polybutylene terephthalate, polyester, polycarbonate, polysulfone, polyethersulfone, polyacrylate, polyester sulfone, modified acrylic polymer, and the like. Among these, a polyolefin resin having an alicyclic structure is preferable from the viewpoint of transparency, low hygroscopicity, dimensional stability, and lightness, and among them, a polyolefin resin having an alicyclic structure in the main chain is particularly preferable. In addition, as a specific example of the polyolefin resin having an alicyclic structure preferably used for the A layer, the above-described polyolefin resin having an alicyclic structure (exemplified as a resin used for the B layer) (however, as described below, Tg A + 10 (° C.) ≦ Tg B (° C.)).
本発明の延伸積層フィルムにおいて、熱可塑性樹脂のガラス転移温度をTgA(℃)、脂環式ポリオレフィン樹脂のガラス転移温度をTgB(℃)としたときに、TgAとTgBの差が10℃以上あることが必要であり、中でも15℃以上であると良い。すなわち、TgA+10(℃)≦TgB(℃)であり、特にTgA+15(℃)≦TgB(℃)であることが好ましい。ガラス転移温度の差が10℃未満では得られる延伸積層フィルムの接着性が不十分となる。また、TgAは100〜125℃であることが好ましい。100℃未満では耐熱性が不足する可能性があり、125℃を超えると得られる延伸積層フィルムの接着性が不十分となるおそれがある。さらに、TgBは130℃以上であることが好ましく、130〜160℃の範囲にあることが特に好ましい。130℃未満では耐熱性の不足を招く可能性があり、160℃を超えると加工が困難になるおそれがある。 In the stretched laminated film of the present invention, when the glass transition temperature of the thermoplastic resin is Tg A (° C.) and the glass transition temperature of the alicyclic polyolefin resin is Tg B (° C.), the difference between Tg A and Tg B is It is necessary that the temperature is 10 ° C. or higher, and it is preferable that the temperature is 15 ° C. or higher. That is, Tg A +10 (° C.) ≦ Tg B (° C.), and particularly preferably Tg A +15 (° C.) ≦ Tg B (° C.). If the difference in glass transition temperature is less than 10 ° C., the resulting stretched laminated film has insufficient adhesion. Further, Tg A is preferably 100-125 ° C.. If it is less than 100 degreeC, heat resistance may be insufficient, and when it exceeds 125 degreeC, there exists a possibility that the adhesiveness of the stretched laminated film obtained may become inadequate. Furthermore, Tg B is preferably 130 ° C. or higher, and particularly preferably in the range of 130 to 160 ° C. If it is less than 130 ° C., heat resistance may be insufficient, and if it exceeds 160 ° C., processing may be difficult.
本発明における延伸積層フィルムの面内の平均レターデーション(Re)及び厚み方向の平均レターデーション(Rth)は、一般的には、Reで50〜200nm程度であり、Rthで100〜300nm程度であるが、用いられる表示装置の設計によってこの範囲内での最適値が選択される。 In-plane average retardation (Re) and thickness direction average retardation (Rth) of the stretched laminated film in the present invention are generally about 50 to 200 nm in Re and about 100 to 300 nm in Rth. However, the optimum value within this range is selected depending on the design of the display device used.
本発明における延伸積層フィルムの平均厚み(T(μm))は、機械的強度などの観点から、好ましくは30〜90μm、さらに好ましくは40〜80μmである。
また、巾方向の厚みムラは巻取りの可否に影響を与えるため、好ましくはレンジで3nm以下、より好ましくは2nm以下とすることができる。
The average thickness (T (μm)) of the stretched laminated film in the present invention is preferably 30 to 90 μm, more preferably 40 to 80 μm, from the viewpoint of mechanical strength and the like.
In addition, since the thickness unevenness in the width direction affects the availability of winding, the range is preferably 3 nm or less, more preferably 2 nm or less.
本発明の延伸積層フィルム中の残留揮発性成分の含有量は特に制約されないが、好ましくは0.1重量%以下、より好ましくは0.05重量%以下、さらに好ましくは0.02重量%以下である。残留揮発性成分の含有量が0.1重量%を超えると、経時的にフィルムの光学特性が変化するおそれがある。揮発性成分の含有量を上記範囲にすることにより、寸法安定性が向上し、ReやRthの経時変化を小さくすることができ、さらには本発明の延伸積層フィルムを有する偏光板や液晶表示装置の劣化を抑制でき、長期的にディスプレイの表示を安定で良好に保つことができる。 The content of the residual volatile component in the stretched laminated film of the present invention is not particularly limited, but is preferably 0.1% by weight or less, more preferably 0.05% by weight or less, and further preferably 0.02% by weight or less. is there. If the content of residual volatile components exceeds 0.1% by weight, the optical properties of the film may change over time. By setting the content of the volatile component in the above range, the dimensional stability can be improved, the change with time of Re and Rth can be reduced, and further, the polarizing plate and the liquid crystal display device having the stretched laminated film of the present invention. Deterioration can be suppressed, and the display on the display can be kept stable and good in the long term.
揮発性成分は、フィルム中に微量含まれる分子量200以下の物質であり、例えば、残留単量体や溶媒などが挙げられる。揮発性成分の含有量は、フィルム中に含まれる分子量200以下の物質の合計として、フィルムをガスクロマトグラフィーにより分析することにより定量することができる。 The volatile component is a substance having a molecular weight of 200 or less contained in a trace amount in the film, and examples thereof include a residual monomer and a solvent. The content of volatile components can be quantified by analyzing the film by gas chromatography as the sum of the substances having a molecular weight of 200 or less contained in the film.
本発明の延伸積層フィルムの飽和吸水率は好ましくは0.03重量%以下、さらに好ましくは0.02重量%以下、特に好ましくは0.01重量%以下である。飽和吸水率が上記範囲であると、ReやRthの経時変化を小さくすることができ、さらには本発明の延伸積層フィルムを有する偏光板や液晶表示装置の劣化を抑制でき、長期的にディスプレイの表示を安定で良好に保つことができる。 The saturated water absorption of the stretched laminated film of the present invention is preferably 0.03% by weight or less, more preferably 0.02% by weight or less, and particularly preferably 0.01% by weight or less. When the saturated water absorption is in the above range, the change with time of Re and Rth can be reduced, and further, deterioration of the polarizing plate and the liquid crystal display device having the stretched laminated film of the present invention can be suppressed, and the display can be used for a long time. The display can be kept stable and good.
飽和吸水率は、フィルムの試験片を一定温度の水中に一定時間、浸漬し、増加した質量の浸漬前の試験片質量に対する百分率で表される値である。通常は、23℃の水中に24時間、浸漬して測定される。
本発明の延伸積層フィルムにおける飽和吸水率は、例えば前記熱可塑性樹脂及び/又は前記脂環式ポリオレフィン樹脂中の極性基の量を減少させることにより、前記値に調節することができるが、好ましくは、極性基を持たない樹脂であることが望まれる。
Saturated water absorption is a value expressed as a percentage of the mass of the test piece before immersion, after the test piece of the film is immersed in water at a constant temperature for a fixed time. Usually, it is measured by immersing in 23 ° C. water for 24 hours.
The saturated water absorption in the stretched laminated film of the present invention can be adjusted to the above value, for example, by reducing the amount of polar groups in the thermoplastic resin and / or the alicyclic polyolefin resin, preferably It is desirable that the resin does not have a polar group.
本発明における延伸積層フィルムは、上述の熱可塑性樹脂からなるA層と脂環式ポリオレフィン樹脂からなるB層とを、少なくとも1枚ずつ積層するものであれば良い。2層構造の積層フィルムに限定されず、3層またはそれ以上の層構成からなる積層フィルムであってもよい。中でも、A層を最表層とする層構成が好ましく、特に、A層−B層(芯層)−A層の順番に積層してなるものが好ましい。A層とB層とは、接着層を介して接しているものであってもよいが、直接に触れて接しているものであることが好ましい。
本発明において、A層の全平均厚みTsはフィルムの平均厚みをTとした時に0.03×T<Ts<0.1×Tの関係を満たす事が必要である。Ts≧0.1×Tでは延伸の際にフィルムの幅方向厚み斑が悪化し好ましくない。またTs≧0.03Tでは接着強度の顕著な上昇が見られないので好ましくない。
The stretched laminated film in the present invention may be any film as long as at least one A layer made of the thermoplastic resin and B layer made of an alicyclic polyolefin resin are laminated. The laminated film is not limited to a laminated film having a two-layer structure, and may be a laminated film composed of three or more layers. Especially, the layer structure which makes A layer the outermost layer is preferable, and what laminates | stacks in order of A layer-B layer (core layer) -A layer in particular is preferable. The A layer and the B layer may be in contact with each other through an adhesive layer, but are preferably in direct contact with each other.
In the present invention, the total average thickness Ts of the A layer needs to satisfy the relationship of 0.03 × T <Ts <0.1 × T, where T is the average thickness of the film. Ts ≧ 0.1 × T is not preferable because the thickness unevenness in the width direction of the film deteriorates during stretching. Also, Ts ≧ 0.03T is not preferable because no significant increase in adhesive strength is observed.
本発明の延伸積層フィルムにおいて、A層は、その面配向係数Pが、1.0×10-3以下であることが好ましく、0.5×10-3以下であることがより好ましい。ここで、面配向係数とは、フィルム内の分子鎖の配向状態を示す指標であり、A層の屈折率、すなわち、面内最大屈折率nx、nxに直行する方向の屈折率ny、及び厚み方向の屈折率nzから、以下の式に従って算出される数値である。
P=(nx+ny)/2−nz
本発明において、Pが1.0×10-3を超える場合には、A層の配向が過度となり、得られる延伸積層フィルムの接着性が低下するので好ましくない。
In the stretched laminated film of the present invention, the layer A has a plane orientation coefficient P of preferably 1.0 × 10 −3 or less, and more preferably 0.5 × 10 −3 or less. Here, the plane orientation coefficient is an index indicating the orientation of the molecular chains within the film, the refractive index of the layer A, i.e., in-plane maximum refractive index n x, the refractive index in the direction perpendicular to the n x n y And a numerical value calculated according to the following formula from the refractive index nz in the thickness direction.
P = ( nx + ny ) / 2- nz
In the present invention, when P exceeds 1.0 × 10 −3 , the orientation of the A layer becomes excessive, and the adhesiveness of the obtained stretched laminated film is unfavorable.
本発明の延伸積層フィルムは、Reのバラツキが10nm以内、好ましくは5nm以内、さらに好ましくは2nm以内である。Reのバラツキを、上記範囲にすることにより、液晶表示装置用の位相差フィルムとして用いた場合に表示品質を良好なものにすることが可能になる。ここで、Reのバラツキは、光入射角0°(入射光線と本発明の延伸積層フィルム表面が直交する状態)の時のReを積層体の幅方向に測定したときの、そのReの最大値と最小値との差である。 The stretched laminated film of the present invention has a Re variation within 10 nm, preferably within 5 nm, and more preferably within 2 nm. By setting the Re variation within the above range, it is possible to improve the display quality when used as a retardation film for a liquid crystal display device. Here, the variation in Re is the maximum value of Re when the Re is measured in the width direction of the laminate at a light incident angle of 0 ° (incident light beam and the surface of the stretched laminated film of the present invention are orthogonal). And the minimum value.
本発明の延伸積層フィルムは長尺状であることが好ましい。長尺状とは、フィルムの幅方向に対し少なくとも5倍程度以上の長さを有するものを言い、好ましくは10倍もしくはそれ以上の長さを有し、具体的にはロール状に巻回されて保管または運搬される程度の長さを有するものを言う。 The stretched laminated film of the present invention is preferably long. The long shape means one having a length of at least about 5 times the width direction of the film, preferably 10 times or more, and specifically wound in a roll shape. It has a length that can be stored or transported.
本発明の延伸積層フィルムは、前記熱可塑性樹脂からなる層と前記脂環式ポリオレフィン樹脂からなる層とを積層してなる未延伸積層フィルムを延伸して得られたものであることが好ましい。 The stretched laminated film of the present invention is preferably obtained by stretching an unstretched laminated film formed by laminating the layer made of the thermoplastic resin and the layer made of the alicyclic polyolefin resin.
前記未延伸フィルムを成形する方法は、特に制限されないが、共押出成形方法、ドライラミネーション等のフィルムラミネーション成形方法、及びコーティング成形方法などの公知の方法が適宜利用され得る。中でも、共押出成形方法が好ましい。
共押出成形法には、フラットなダイを用いたフラットダイ共押出成形法や、円筒形のダイを用いた共インフレーション成形法などなどがあるが、フラットダイ共押出成形法が好ましい。フラットダイ共押出成形法は、樹脂を押出機で加熱溶融後、フラットダイから共押し出しし、連続的にフィルム形状の成形品を得る方法である。フラットダイとしては、樹脂の分配流路の構造別に、Tダイ、コートハンガーダイ、フィッシュテールダイなどが挙げられる。押出機は樹脂を加熱混練して、一定押出量でダイよりフィルム形状で溶融体を押し出す。通常押出機とダイとの間にスクリーンやフィルタを入れて、ゲルや異物を除去することが好ましい。また使用される樹脂は、押出機に投入する前に乾燥し、水や揮発性溶剤の含有量を減らしておくことがフィッシュアイや気泡の発生を防止する上で好ましい。
The method for molding the unstretched film is not particularly limited, and known methods such as a coextrusion molding method, a film lamination molding method such as dry lamination, and a coating molding method can be appropriately used. Among these, the coextrusion molding method is preferable.
The coextrusion molding method includes a flat die coextrusion molding method using a flat die, a coinflation molding method using a cylindrical die, and the like, and the flat die coextrusion molding method is preferable. The flat die co-extrusion molding method is a method in which a resin is heated and melted with an extruder and then co-extruded from a flat die to continuously obtain a film-shaped molded product. Examples of the flat die include a T die, a coat hanger die, and a fish tail die according to the structure of the resin distribution flow path. The extruder heats and kneads the resin and extrudes the melt in the form of a film from the die with a constant extrusion amount. Usually, it is preferable to remove a gel or a foreign substance by inserting a screen or a filter between the extruder and the die. The resin used is preferably dried before being introduced into the extruder, and the content of water and volatile solvents is reduced in order to prevent the generation of fish eyes and bubbles.
本発明の延伸積層フィルムを製造する際の延伸方法としては、特に制限はなく、従来公知の方法を適用し得る。具体的には、ロール間の周速の差を利用して縦方向に一軸延伸する方法、テンターを用いて横方向に一軸延伸する方法等の一軸延伸法;固定するクリップの間隔が開かれて縦方向の延伸と同時にガイドレールの広がり角度により横方向に延伸する同時二軸延伸法や、ロール間の周速の差を利用して縦方向に延伸した後にその両端部がクリップ把持してテンターを用いて横方向に延伸する逐次二軸延伸法などの二軸延伸法;が挙げられる。 There is no restriction | limiting in particular as a extending | stretching method at the time of manufacturing the extending | stretching laminated | multilayer film of this invention, A conventionally well-known method can be applied. Specifically, a uniaxial stretching method such as a method of uniaxially stretching in the longitudinal direction using a difference in peripheral speed between rolls, a method of uniaxially stretching in the lateral direction using a tenter; Simultaneously biaxial stretching method that stretches in the transverse direction according to the spread angle of the guide rail at the same time as stretching in the longitudinal direction, or after stretching in the longitudinal direction by utilizing the difference in peripheral speed between the rolls, both ends thereof are clipped and tenter And a biaxial stretching method such as a sequential biaxial stretching method in which stretching is performed in the transverse direction.
縦方向に延伸する方法としては、ロール間でのIR加熱方式、フロート方式等が上げられるが、本発明のフィルムの用途に求められる光学的な均一性を得るためには後者が好適である。延伸条件に特に制限はないが、延伸温度としてはTgB〜TgB+20℃の範囲で、延伸倍率としては1.1〜3.0倍の範囲にて所望の光学特性を得るために調整すればよい。 Examples of the method of stretching in the machine direction include an IR heating method and a float method between rolls, and the latter is preferable for obtaining optical uniformity required for the use of the film of the present invention. There is no particular limitation on stretching conditions, in the range of Tg B ~Tg B + 20 ℃ as stretching temperature, the stretching ratio is adjusted to obtain the desired optical properties in the range of 1.1 to 3.0 times That's fine.
横方向に延伸する方法としては、テンター法が挙げられる。この場合も延伸条件に特に制限はないが、延伸温度としてはTgB〜TgB+20℃の範囲で、延伸倍率としては1.3〜5.0倍、好ましくは1.5〜4.0倍の範囲にて所望の光学特性を得るために調整すればよい。5.0以上の倍率は設備に過大な負荷がかかり現実的な値ではない。また1.3倍以下の倍率での延伸は幅方向厚みムラの悪化を招き好ましくない。 An example of a method of stretching in the transverse direction is a tenter method. In this case as well, the stretching conditions are not particularly limited, but the stretching temperature is in the range of Tg B to Tg B + 20 ° C., and the stretching ratio is 1.3 to 5.0 times, preferably 1.5 to 4.0 times. In order to obtain the desired optical characteristics within the above range, it may be adjusted. A scale factor of 5.0 or more is an unrealistic value because the equipment is overloaded. In addition, stretching at a magnification of 1.3 times or less is not preferable because it causes deterioration of thickness unevenness in the width direction.
本発明の延伸積層フィルムにおける製膜では巾方向厚みムラの制御のため延伸ゾーンにおいて巾方向に温度差がつくような製膜をすることも可能である。延伸ゾーンにおいて巾方向の温度差をつけるにはノズルの開度を巾方向で調整したり、IRヒーターを巾方向に並べて加熱制御したりするなど公知の手法を用いることができ、これと上述のレールパターン組み合わせにより、より厚みムラの制御された延伸積層フィルムを得ることが可能となる。 In film formation in the stretched laminated film of the present invention, it is also possible to form a film that has a temperature difference in the width direction in the stretching zone in order to control the thickness unevenness in the width direction. In order to provide a temperature difference in the width direction in the stretching zone, a known method such as adjusting the opening of the nozzle in the width direction or controlling the heating by arranging IR heaters in the width direction can be used. By combining the rail patterns, it becomes possible to obtain a stretched laminated film in which thickness unevenness is further controlled.
本発明の偏光板は、偏光膜の少なくとも片面に本発明の延伸積層フィルムを積層させてなる。偏光膜には、ポリピニルアルコールや部分ホルマール化ポリビニルアルコール等の従来に準じた適宜なビニルアルコール系ポリマーよりなるフィルムに、ヨウ素や二色性染料等よりなる二色性物質による染色処理、延伸処理、架橋処理等の適宜な処理を適宜な順序や方式で施したもので、自然光を入射させると直線偏光を透過する適宜なものを用いることができる。特に、光透過率や偏光度に優れるものが好ましい。偏光膜の厚さは、5〜80μmが一般的であるが、これに限定されない。 The polarizing plate of the present invention is formed by laminating the stretched laminated film of the present invention on at least one surface of a polarizing film. For the polarizing film, a film made of a suitable vinyl alcohol polymer such as polypinyl alcohol or partially formalized polyvinyl alcohol, etc., dyeing treatment with a dichroic substance such as iodine or dichroic dye, stretching Appropriate treatments such as treatment and cross-linking treatment can be performed in an appropriate order and manner, and appropriate materials that transmit linearly polarized light when natural light is incident can be used. In particular, those excellent in light transmittance and degree of polarization are preferable. The thickness of the polarizing film is generally 5 to 80 μm, but is not limited thereto.
積層形態としては、本発明の延伸積層フィルムを偏光膜の両面に積層させても片面に積層させてもよく、また積層数にも特に限定はなく、2枚以上積層させてもよい。また、積層手法としては、必須手法ではないが、接着剤を用いて積層させることができる。延伸積層フィルムと偏光膜との間に本発明の特性を損なわない範囲で他の部材を介在させることもできる。 As a lamination | stacking form, the extending | stretching laminated | multilayer film of this invention may be laminated | stacked on both surfaces of a polarizing film, may be laminated | stacked on one side, and there is no limitation in particular in the number of lamination | stacking, You may laminate | stack two or more. Moreover, as a lamination | stacking method, although it is not an essential method, it can laminate | stack using an adhesive agent. Another member can be interposed between the stretched laminated film and the polarizing film as long as the characteristics of the present invention are not impaired.
偏光膜の片側又は両側には、偏光膜の保護を目的として、適宜の接着層を介して保護フィルムが接着されていてもよい。保護フィルムとしては、適宜な透明フィルムを用いることができる。中でも、透明性や機械的強度、熱安定性や水分遮蔽性等に優れる樹脂を有するフィルム等が好ましく用いられる。その樹脂の例としては、トリアセチルセルロースの如きアセテート重合体、脂環構造を有する重合体、ポリオレフィン重合体、ポリカーボネート重合体、ポリエチレンテレフタレートの如きポリエステル重合体、ポリ塩化ビニル重合体、ポリスチレン重合体、ポリアクリロニトリル重合体、ポリスルホン重合体、ポリエーテルスルホン重合体、ポリアミド重合体、ポリイミド重合体、アクリル重合体等があげられる。 For the purpose of protecting the polarizing film, a protective film may be bonded to one side or both sides of the polarizing film via an appropriate adhesive layer. An appropriate transparent film can be used as the protective film. Among them, a film having a resin excellent in transparency, mechanical strength, thermal stability, moisture shielding property, etc. is preferably used. Examples of the resin include an acetate polymer such as triacetyl cellulose, a polymer having an alicyclic structure, a polyolefin polymer, a polycarbonate polymer, a polyester polymer such as polyethylene terephthalate, a polyvinyl chloride polymer, a polystyrene polymer, Examples thereof include a polyacrylonitrile polymer, a polysulfone polymer, a polyether sulfone polymer, a polyamide polymer, a polyimide polymer, and an acrylic polymer.
本発明の延伸積層フィルムと偏光膜が接する構成の場合は、延伸積層フィルムを偏光膜の保護フィルムとして兼用することができる。延伸積層フィルムを偏光膜の保護フィルムとして兼用することにより、保護フィルム一層を省いて液晶表示装置を薄型化するとともに、偏光膜の耐久性を向上することができる。 In the case where the stretched laminated film of the present invention is in contact with the polarizing film, the stretched laminated film can also be used as a protective film for the polarizing film. By using the stretched laminated film as a protective film for the polarizing film, the thickness of the liquid crystal display device can be reduced by omitting one protective film, and the durability of the polarizing film can be improved.
本発明の延伸積層フィルムは、容易に製造が可能で、複屈折の高度な補償が可能なので、それ単独あるいは他の部材と組み合わせて、位相差板や視野角補償フィルムとして、液晶表示装置、有機EL表示装置、プラズマ表示装置、FED(電界放出)表示装置、SED(表面電界)表示装置などに広く応用が可能である。液晶表示装置としては、例えば、インプレーンスイッチング(IPS)モード、バーチカルアラインメント(VA)モード、マルチドメインバーチカルアラインメント(MVA)モード、コンティニュアスピンホイールアラインメント(CPA)モード、ハイブリッドアラインメントネマチック(HAN)モード、ツイステッドネマチック(TN)モード、スーパーツイステッドネマチック(STN)モード、オプチカルコンペンセイテッドベンド(OCB)モードなどを挙げることができる。 Since the stretched laminated film of the present invention can be easily manufactured and can highly compensate birefringence, it can be used alone or in combination with other members as a retardation plate or a viewing angle compensation film as a liquid crystal display device, organic The present invention can be widely applied to EL display devices, plasma display devices, FED (field emission) display devices, SED (surface electric field) display devices, and the like. As the liquid crystal display device, for example, in-plane switching (IPS) mode, vertical alignment (VA) mode, multi-domain vertical alignment (MVA) mode, continuous spin wheel alignment (CPA) mode, hybrid alignment nematic (HAN) mode, Examples include a twisted nematic (TN) mode, a super twisted nematic (STN) mode, and an optically compensated bend (OCB) mode.
本発明の液晶表示装置において、液晶表示装置の形成に際しては、例えばプリズムアレイシート、レンズアレイシート、光拡散板、バックライトや輝度向上フィルム等の適宜な部品を適宜な位置に1層又は2層以上配置することができる。バックライトとしては、冷陰極管、水銀平面ランプ、発光ダイオード、ELなどが挙げられる。 In the liquid crystal display device of the present invention, when forming the liquid crystal display device, for example, a prism array sheet, a lens array sheet, a light diffusing plate, a backlight, a brightness enhancement film, etc. The above can be arranged. Examples of the backlight include a cold cathode tube, a mercury flat lamp, a light emitting diode, and an EL.
本発明を、実施例及び比較例を示しながら、さらに詳細に説明するが、本発明は以下の実施例のみに限定されるものではない。
本実施例における評価は、以下の方法によって行う。
The present invention will be described in more detail with reference to examples and comparative examples, but the present invention is not limited to the following examples.
Evaluation in this example is performed by the following method.
(1)樹脂のガラス転移温度
セイコーインスツルメンツ製DSC6220を用いて樹脂ペレットのガラス転移温度を測定した。条件はサンプル重量10mg、昇温速度20℃/minとした。
(1) Glass transition temperature of resin The glass transition temperature of the resin pellet was measured using DSC6220 by Seiko Instruments. The conditions were a sample weight of 10 mg and a heating rate of 20 ° C./min.
(2)各層の厚み
エポキシ樹脂に包埋したフィルムを大和光機(株)製ミクロトームRV−240を用いて30μm厚みにスライスしオリンパス製偏光顕微鏡BX51を用いて観察し各層の厚みを決定した。
(2) Thickness of each layer A film embedded in an epoxy resin was sliced to a thickness of 30 μm using a microtome RV-240 manufactured by Daiwa Koki Co., Ltd., and observed using an Olympus polarizing microscope BX51 to determine the thickness of each layer.
(3)厚みムラ
(株)ミツトヨ製スナップゲージID547−301を用いて巾方向に5cm間隔で厚みを測定し平均値を求める。次に最大値−最小値の値を厚みムラとした。
(3) Thickness nonuniformity Thickness is measured at intervals of 5 cm in the width direction using Mitutoyo Corporation snap gauge ID547-301, and an average value is calculated | required. Next, the maximum value-minimum value was defined as thickness unevenness.
(4)配向係数P
メトリコン社製プリズムカプラ屈折率計Model2010を用いて波長590nmでの屈折率nx、ny、nzを測定し以下式に従って面配向係数を算出した。
P=(nx+ny)/2−nz
ここでnxは面内最大屈折率、nyはnxに直行する方向の屈折率、nzは厚み方向の屈折率を表している。
(4) Orientation coefficient P
Refractive indices n x at a wavelength 590nm using a Metricon Corporation prism coupler refractometer Model 2010, n y, to calculate the plane orientation coefficient according to the equation below by measuring the n z.
P = ( nx + ny ) / 2- nz
Where n x is the in-plane maximum refractive index, n y is a refractive index in the direction perpendicular to the n x, n z represents the refractive index in the thickness direction.
(5)剥離強度
得られた延伸フィルムを偏光フィルム(偏光膜)と常法によって貼りあわせ、25mmの幅に裁断して90度剥離試験を実施し以下の基準で延伸フィルムと偏光フィルムとの間の剥離強度を評価した。
◎・・・材破壊が先に発生して試験不能
○・・・剥離強度3.0N以上
×・・・剥離強度3.0N未満
(5) Peel strength The obtained stretched film is bonded to a polarizing film (polarizing film) by a conventional method, cut to a width of 25 mm, a 90-degree peel test is performed, and between the stretched film and the polarizing film according to the following criteria: The peel strength was evaluated.
◎ ・ ・ ・ Material failure occurs first and cannot be tested ○ ・ ・ ・ Peel strength 3.0N or more × ・ ・ ・ Peel strength less than 3.0N
(実施例1〜3)
芯層用樹脂(B層)としてノルボルネン系樹脂であるZEONOR1420(ガラス転移温度137℃)、最表層用樹脂(A層)としてZEONOR1020(ガラス転移温度104℃)(共に日本ゼオン(株)製)のペレットを100℃で5時間乾燥した後、それぞれ別々の押出し機に供給した。樹脂は押出し機内で溶融された後、ポリマーパイプ及びポリマーフィルターを経てフィードブロック内で合流しTダイからキャスティングドラム上にシート状に押出されて冷却され厚み140μmの未延伸フィルム(1)を得た。(1)はそのまま連続してフローティング方式の縦延伸装置に供給され表に示す条件で縦延伸を行った後、さらに連続してテンターに供給された。テンター内は表に示す温度、延伸倍率で進行方向に対し直角方向に延伸を施され最終的に表に示す2軸延伸フィルム(2)を1300mmの巾で得た。得られたフィルムは上記の巾で均一なものであった。
(Examples 1-3)
ZEONOR1420 (glass transition temperature 137 ° C.) which is a norbornene resin as the core layer resin (B layer), and ZEONOR1020 (glass transition temperature 104 ° C.) (both manufactured by Nippon Zeon Co., Ltd.) as the outermost layer resin (A layer). The pellets were dried at 100 ° C. for 5 hours and then fed to separate extruders. After the resin was melted in an extruder, it joined in a feed block through a polymer pipe and a polymer filter, extruded from a T-die onto a casting drum in a sheet form, and cooled to obtain an unstretched film (1) having a thickness of 140 μm. . (1) was continuously supplied to a floating-type longitudinal stretching apparatus as it was and subjected to longitudinal stretching under the conditions shown in the table, and then continuously fed to a tenter. In the tenter, the biaxially stretched film (2) shown in the table was finally obtained with a width of 1300 mm by stretching in the direction perpendicular to the traveling direction at the temperature and stretch ratio shown in the table. The obtained film was uniform with the above width.
得られた2軸延伸フィルムは特開2005−70140号公報の実施例1にしたがって偏光フィルムと貼り合せ反対面にはトリアセチルセルロースを貼合して偏光板(3)を得た。偏光板(3)の剥離試験結果は良好であった。 The obtained biaxially stretched film was bonded to the polarizing film according to Example 1 of JP-A-2005-70140, and triacetyl cellulose was bonded to the opposite surface to obtain a polarizing plate (3). The peeling test result of the polarizing plate (3) was good.
(比較例1)
未延伸フィルムとしてZEONOR1420(日本ゼオン(株)製)単層品を用いたところ剥離強度が低下した。
(Comparative Example 1)
When a ZEONOR 1420 (manufactured by Nippon Zeon Co., Ltd.) single layer product was used as an unstretched film, the peel strength was reduced.
(比較例2)
実施例1に対し表層厚みをアップさせたものは厚みムラが悪化し、ロール巻取りに支障を生じた。
(Comparative Example 2)
When the surface layer thickness was increased with respect to Example 1, the thickness unevenness deteriorated, and the roll winding was hindered.
(比較例3)
実施例1に対し表層厚みをダウンさせたものは剥離強度が不足していた。
(Comparative Example 3)
What peeled down surface layer thickness from Example 1 had insufficient peel strength.
(比較例4)
表層樹脂としてZEONEX330R(日本ゼオン(株)製:ガラス転移温度124℃)を用い表層の面配向係数Pを1.1×10-3とした所、剥離強度が低下した。
(Comparative Example 4)
When ZEONEX 330R (manufactured by Nippon Zeon Co., Ltd .: glass transition temperature 124 ° C.) was used as the surface layer resin and the surface orientation coefficient P of the surface layer was set to 1.1 × 10 −3 , the peel strength decreased.
(比較例5)
表層樹脂としてZEONEX480R(日本ゼオン(株)製:ガラス転移温度135℃)を用いたところ表層の面配向係数Pが1.4×10-3となり、剥離強度が低下した。
(Comparative Example 5)
When ZEONEX480R (manufactured by Nippon Zeon Co., Ltd .: glass transition temperature 135 ° C.) was used as the surface layer resin, the surface orientation coefficient P of the surface layer was 1.4 × 10 −3 and the peel strength was reduced.
Claims (8)
熱可塑性樹脂のガラス転移温度をTgA(℃)、脂環式ポリオレフィン樹脂のガラス転移温度TgB(℃)を、延伸積層フィルムの平均厚みをT(μm)、A層の全平均厚みをTS(μm)、A層の面配向係数をPとしたとき、
a)TgA+10(℃)≦TgB(℃)であり、
b)0.03×T<TS<0.1×Tであり、
c)P≦1.0×10-3である、
ことを特徴とする延伸積層フィルム。 A stretched laminated film in which an A layer made of a thermoplastic resin and a B layer made of an alicyclic polyolefin resin are laminated one by one,
The glass transition temperature of the thermoplastic resin is Tg A (° C.), the glass transition temperature Tg B (° C.) of the alicyclic polyolefin resin, the average thickness of the stretched laminated film is T (μm), and the total average thickness of the A layer is T S (μm), when the plane orientation coefficient of the A layer is P,
a) Tg A +10 (° C.) ≦ Tg B (° C.)
b) 0.03 × T <T S <0.1 × T,
c) P ≦ 1.0 × 10 −3 .
A stretched laminated film characterized by that.