JP2007231298A - Method for producing vulcanizable fluorine-containing elastomer - Google Patents

Method for producing vulcanizable fluorine-containing elastomer Download PDF

Info

Publication number
JP2007231298A
JP2007231298A JP2007164016A JP2007164016A JP2007231298A JP 2007231298 A JP2007231298 A JP 2007231298A JP 2007164016 A JP2007164016 A JP 2007164016A JP 2007164016 A JP2007164016 A JP 2007164016A JP 2007231298 A JP2007231298 A JP 2007231298A
Authority
JP
Japan
Prior art keywords
polymerization
fluorine
containing elastomer
weight
vulcanization
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2007164016A
Other languages
Japanese (ja)
Inventor
Yosuke Nishimura
洋介 西村
Masaki Irie
正樹 入江
Sadashige Irie
貞成 入江
Manabu Fujisawa
学 藤澤
Satoshi Tokuno
敏 徳野
Mitsuru Kishine
充 岸根
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Daikin Industries Ltd
Original Assignee
Daikin Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2003278545A external-priority patent/JP2005104992A/en
Application filed by Daikin Industries Ltd filed Critical Daikin Industries Ltd
Priority to JP2007164016A priority Critical patent/JP2007231298A/en
Publication of JP2007231298A publication Critical patent/JP2007231298A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a fluorine-containing elastomer being reduced in the content of branches and having a high terminal iodine content, and a fluorine-containing molded article having good balance between compression set and elongation at break, which is obtained by vulcanizing the elastomer. <P>SOLUTION: A peroxide vulcanizable fluorine-containing elastomer comprises 20 to 90% by mole of vinylidene fluoride repeating units and 10 to 80% by mole of hexafluoropropylene repeating units; (a) which contains 0.01 to 10% by weight of an iodine atom in the elastomer, (b) which has a number average molecular weight of from 1,000 to 300,000, and (c) which has a VdF branch ratio of at most 200 ppm, the ratio being calculated from the formula (1), in which an acetone solution having a polymer concentration of about 20% is subjected to the measurement by high-resolution<SP>19</SP>F-NMR. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、高圧下でヨウ素移動重合による含フッ素エラストマーの製造方法に関する。さらに、この方法によって製造したエラストマー分岐が少なく、かつ末端ヨウ素含有率が高い含フッ素エラストマーと、エラストマーを加硫することにより得られる圧縮永久歪みと引張破断伸びのバランスに優れた含フッ素成形品に関する。   The present invention relates to a method for producing a fluorine-containing elastomer by iodine transfer polymerization under high pressure. Further, the present invention relates to a fluorine-containing elastomer having a small elastomer branch and high terminal iodine content produced by this method, and a fluorine-containing molded article having an excellent balance between compression set and tensile elongation at break obtained by vulcanizing the elastomer. .

ビニリデンフルオライド−ヘキサフルオロプロピレン（ＶｄＦ−ＨＦＰ）系やテトラフルオロエチレン（ＴＦＥ）−パーフルオロビニルエーテル系の含フッ素エラストマーは、それらの卓抜した耐薬品性、耐溶剤性、耐熱性を示すことから、過酷な環境下で使用されるＯ−リング、ガスケット、ホース、ステムシール、シャフトシール、ダイヤフラムなどとして自動車工業、半導体工業、化学工業などの分野において広く用いられている。   Since vinylidene fluoride-hexafluoropropylene (VdF-HFP) -based and tetrafluoroethylene (TFE) -perfluorovinyl ether-based fluorine-containing elastomers exhibit their outstanding chemical resistance, solvent resistance, and heat resistance, O-rings, gaskets, hoses, stem seals, shaft seals, diaphragms and the like used in harsh environments are widely used in fields such as the automobile industry, semiconductor industry, and chemical industry.

こうした用途に用いられるフッ素エラストマーとしては、分子末端に高活性のヨウ素原子を有するヨウ素含有フッ素エラストマーがある。このヨウ素含有含フッ素エラストマーは、分子末端のヨウ素原子により良好な架橋効率が可能で、加硫性に優れている。また、金属成分をもつ化学物質を添加する必要がないことから、パーオキサイド加硫成形品としても広く用いられている。   Fluoroelastomers used for such applications include iodine-containing fluoroelastomers having highly active iodine atoms at the molecular ends. This iodine-containing fluorine-containing elastomer can have good crosslinking efficiency due to iodine atoms at the molecular terminals, and has excellent vulcanizability. Further, since it is not necessary to add a chemical substance having a metal component, it is widely used as a peroxide vulcanized product.

パーオキサイド加硫系（たとえば、特許文献１参照）は、耐薬品性、および耐スチーム（熱水）性に優れているが、耐圧縮永久歪みは、ポリオール加硫系と比べて劣っていたため、シール材用途として適切ではなかった。この問題は、エラストマー主鎖中に、加硫サイトを導入することで解決されている（たとえば、特許文献２参照）。しかし、加硫密度が上昇するため、引張破断伸びが犠牲となっていた。よって、耐圧縮永久歪みおよび引張破断伸びの両者を兼ね備えることは、非常に困難であった。   The peroxide vulcanization system (see, for example, Patent Document 1) is excellent in chemical resistance and steam (hot water) resistance, but the compression set resistance is inferior to that of the polyol vulcanization system. It was not suitable as a sealing material. This problem is solved by introducing a vulcanization site into the elastomer main chain (see, for example, Patent Document 2). However, since the vulcanization density increased, the tensile elongation at break was sacrificed. Therefore, it was very difficult to combine both compression set and tensile elongation at break.

また、高圧重合による含フッ素エラストマー製造法としては、モノマーの少なくとも一種が超臨界の状態での重合法（たとえば、特許文献３参照）や、ポリマー粒子中のモノマー濃度が基準値以上での乳化重合法（たとえば、特許文献４参照）がある。しかし、いずれの特許文献においても本発明で述べるＲf 1・Ｉx存在下での重合が可能との記述はあるものの、具体的な実施例はなく、本発明で開示する効果についても一切触れられていない。 In addition, as a method for producing a fluorine-containing elastomer by high-pressure polymerization, a polymerization method in which at least one monomer is in a supercritical state (for example, refer to Patent Document 3), or an emulsification weight in which the monomer concentration in the polymer particles exceeds a reference value. There is a law (for example, see Patent Document 4). However, although there is a description in any patent document that the polymerization in the presence of R f 1 · I x described in the present invention is possible, there is no specific example, and the effects disclosed in the present invention are not mentioned at all. It is not done.

ヨウ素含有含フッ素エラストマーは、いわゆるヨウ素移動重合法などの乳化重合法により製造（たとえば、特許文献５参照）されているが、高い末端ヨウ素化率を達成するためには重合開始剤の使用量を抑える必要があり（たとえば、非特許文献１参照）、その分、生産性を上げることができない。重合開始剤の使用量の制約がない重合系では開始剤量を増やすことで容易に重合速度を大きくすることが可能であるが、ヨウ素移動重合系では開始剤末端濃度が最終製品の物性に大きな影響を与えるため開始剤使用量の増大は望めない。   The iodine-containing fluorine-containing elastomer is produced by an emulsion polymerization method such as a so-called iodine transfer polymerization method (see, for example, Patent Document 5), but in order to achieve a high terminal iodination rate, the amount of polymerization initiator used must be reduced. It is necessary to suppress (see, for example, Non-Patent Document 1), and productivity cannot be increased accordingly. In polymerization systems where there is no restriction on the amount of polymerization initiator used, it is possible to easily increase the polymerization rate by increasing the amount of initiator, but in iodine transfer polymerization systems, the initiator end concentration is large in the physical properties of the final product. It is not possible to increase the amount of initiator used due to the influence.

生産性を向上させるために種々の提案がなされている。たとえば、乳化重合を連続して行なうことにより、生産性を向上させる方法（たとえば、特許文献６、７参照）が提案されているが、ヨウ素含有含フッ素エラストマーの特性である良好な引張強度や圧縮永久ひずみ性が得られない。   Various proposals have been made to improve productivity. For example, a method for improving productivity by continuously performing emulsion polymerization (see, for example, Patent Documents 6 and 7) has been proposed, but good tensile strength and compression that are characteristics of an iodine-containing fluorine-containing elastomer are proposed. Permanent strain cannot be obtained.

また、１．７ＭＰａ以上（ゲージ圧。以下同様）の高圧で重合する方法（たとえば、特許文献８参照）が提案されているが、２．６〜２．７ＭＰａの範囲の圧力が好適とされており、実施例においてもその範囲内での開示にとどまっている。また、重合時間も１５時間をこえるものである。さらに、マイクロエマルション重合法（たとえば、特許文献９参照）が提案されているが、初期にマイクロエマルションを形成させるためにフッ素オイルなどの使用が必要であり、このフッ素オイルなどが製品に残留し汚染源となるので洗浄除去が必要となる。   Further, a method of polymerizing at a high pressure of 1.7 MPa or more (gauge pressure; the same applies hereinafter) (for example, see Patent Document 8) has been proposed, but a pressure in the range of 2.6 to 2.7 MPa is considered suitable. In the embodiments, the disclosure is limited to that range. Further, the polymerization time exceeds 15 hours. Furthermore, a microemulsion polymerization method (see, for example, Patent Document 9) has been proposed, but it is necessary to use fluorine oil or the like in order to form a microemulsion in the initial stage. Therefore, cleaning removal is required.

単に重合系を安定させ、あるいは重合速度を上げるためには乳化剤の使用量を多くすればよいが、乳化剤自身が加硫阻害を起すため、これまた洗浄除去が必要となる上に、コスト面および環境面でも好ましくない。   In order to simply stabilize the polymerization system or increase the polymerization rate, the amount of emulsifier used may be increased. However, since the emulsifier itself causes vulcanization inhibition, this also requires washing and removal, as well as cost and It is not preferable in terms of the environment.

これらを解決するために、ヨウ素移動重合を二段階の乳化重合法で行うことが提案されている（たとえば、特許文献１０参照）。２段階の乳化重合とは、一段目の重合で比較的多量の乳化剤を使用して多数のポリマー粒子を合成し、ついで得られた乳濁液を希釈してポリマー粒子濃度および乳化剤濃度を下げ、この希釈乳濁液を用いて二段目の重合を行なう方法である。この方法では、今までの乳化重合用の設備を大きく変えることなく、均一な粒径でかつ本来の特性を維持したまま、重合速度を２倍以上短縮可能にしたが、依然としてヨウ素化合物を使用しない重合法と比較して生産性は劣っている。また、この重合法で得られたエラストマーに関しては従来のヨウ素移動重合法と比較して特に改良された部分はなく、上述のシール性においての課題は残されていた。   In order to solve these problems, it has been proposed to perform iodine transfer polymerization by a two-stage emulsion polymerization method (see, for example, Patent Document 10). In the two-stage emulsion polymerization, a large amount of emulsifier is used in the first stage polymerization to synthesize a large number of polymer particles, and then the obtained emulsion is diluted to lower the polymer particle concentration and the emulsifier concentration. This is a method of performing the second stage polymerization using this diluted emulsion. In this method, the polymerization rate can be shortened more than twice while maintaining the original characteristics with a uniform particle size without greatly changing the equipment for emulsion polymerization so far, but no iodine compound is used yet. Productivity is inferior compared with the polymerization method. In addition, the elastomer obtained by this polymerization method does not have a particularly improved portion as compared with the conventional iodine transfer polymerization method, and the above-described problem in sealing performance remains.

このようにヨウ素含有含フッ素エラストマーの生産性と特性の維持を両立させる製造法はない。   Thus, there is no production method that achieves both productivity and maintenance of characteristics of the iodine-containing fluorine-containing elastomer.

特開昭５３−１２５４９１号公報JP-A-53-125491 特開昭６２−１２７３４号公報JP 62-12734 A 国際公開第００／４７６４１号パンフレットInternational Publication No. 00/47641 Pamphlet 国際公開第０１／３４６６６号パンフレットInternational Publication No. 01/34666 Pamphlet 特公昭６３−４１９２８号公報Japanese Examined Patent Publication No. 63-41928 特開平３−３３１０８号公報JP-A-3-33108 特開平３−２２１５１０号公報JP-A-3-221510 特開平５−２２２１３０号公報JP-A-5-222130 特開昭６３−８４０６号公報Japanese Unexamined Patent Publication No. 63-8406 国際公開第００／０１７４１号パンフレットInternational Publication No. 00/01741 Pamphlet 建元 正祥 Ｐ１９、８６／６ ミクロシンポジウム、ラジカル重合におけるポリマーの構造規制、高分子学会（１９８６）Masayoshi Jianmoto P19, 86/6 Microsymposium, Structural regulation of polymers in radical polymerization, Society of Polymer Science (1986)

本発明は、高圧下でヨウ素移動重合を行うことにより、非ヨウ素移動重合法に匹敵する生産性の高い含フッ素エラストマーの製造方法を提供する。さらに、この方法によって製造した、ポリマー分岐が少なく、かつ末端ヨウ素含有率が高い含フッ素エラストマーと、エラストマーを加硫することにより得られる圧縮永久歪みと引張破断伸びのバランスに優れた含フッ素成形品を提供する。   The present invention provides a method for producing a fluorine-containing elastomer having high productivity comparable to the non-iodine transfer polymerization method by performing iodine transfer polymerization under high pressure. Furthermore, a fluorine-containing molded article having an excellent balance between compression set and elongation at break obtained by vulcanizing the elastomer, and a fluorine-containing elastomer having a low polymer branching and a high terminal iodine content, produced by this method. I will provide a.

すなわち、本発明は、含フッ素エラストマーが、ビニリデンフルオライド繰り返し単位２０〜９０モル％、ヘキサフルオロプロピレン繰り返し単位１０〜８０モル％を含み、
（ａ）エラストマー中に０．０１〜１０重量％のヨウ素原子を含有し、
（ｂ）ポリマー数平均分子量が１,０００〜３００,０００であり、
（ｃ）ポリマー濃度約２０％のアセトン溶液を高分解能19Ｆ−ＮＭＲで測定し、下記式

Figure 2007231298
により求められる「ＶｄＦ分岐率」が２００ｐｐｍ以下であり、
パーオキサイド加硫が可能である含フッ素エラストマーに関する。 That is, in the present invention, the fluorine-containing elastomer contains 20 to 90 mol% of vinylidene fluoride repeating units, 10 to 80 mol% of hexafluoropropylene repeating units,
(A) containing 0.01 to 10% by weight of iodine atoms in the elastomer;
(B) The polymer number average molecular weight is 1,000 to 300,000,
(C) An acetone solution having a polymer concentration of about 20% was measured by high resolution 19 F-NMR, and the following formula
Figure 2007231298
 "VdF branching rate" calculated by the following is 200 ppm or less,
The present invention relates to a fluorine-containing elastomer capable of peroxide vulcanization.

加硫して得られる成形体の引張破断伸びＥｂが２００％以上、５５０％以下であり、かつ２００℃、７２時間での圧縮永久歪みＣＳが５％以上、３０％以下であることが好ましい。   The molded article obtained by vulcanization preferably has a tensile elongation at break Eb of 200% or more and 550% or less, and a compression set CS at 200 ° C. for 72 hours of 5% or more and 30% or less.

含フッ素エラストマーおよび加硫剤からなる含フッ素エラストマー硬化用組成物。   A fluorine-containing elastomer curing composition comprising a fluorine-containing elastomer and a vulcanizing agent.

本発明は、高圧下でヨウ素移動重合を行うことにより、重合開始剤が少ないにもかかわらず重合速度が大幅に増大し、非ヨウ素移動重合法に匹敵する生産性の高い含フッ素エラストマーの製造方法を提供する。さらに、この方法によって製造したエラストマーは、分岐が少なく、末端ヨウ素原子含有率が高く、また、含フッ素エラストマーと圧縮永久歪みと引張破断伸びのバランスが優れた含フッ素成形品を提供する。   The present invention is a method for producing a fluorine-containing elastomer having a high productivity comparable to the non-iodine transfer polymerization method by performing iodine transfer polymerization under a high pressure, thereby greatly increasing the polymerization rate despite a small amount of polymerization initiator. I will provide a. Furthermore, the elastomer produced by this method provides a fluorine-containing molded article having few branches, high terminal iodine atom content, and excellent balance between the fluorine-containing elastomer, compression set and tensile elongation at break.

本発明の含フッ素エラストマーの製造方法は、反応槽内の気相部分における各モノマーの臨界温度、臨界圧力、およびそれぞれの組成比からＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式を用いて算出した臨界定数の換算温度が０．９５以上、換算圧力が０．８０以上の条件下で行なわれる、バッチ式共重合法による含フッ素エラストマーの製造方法であって、
一般式：Ｒf 1・Ｉx
（ただし、式中、Ｒf 1は炭素数１〜１６の飽和もしくは不飽和のフルオロ炭化水素基またはクロロフルオロ炭化水素基であり、ｘはＲf 1の結合手の数であって、１以上４以下の整数である）の存在下に、少なくとも１種のフルオロオレフィンを含むエチレン性不飽和化合物を共重合させる含フッ素エラストマーの製造方法に関する。 In the method for producing a fluorine-containing elastomer of the present invention, the conversion temperature of the critical constant calculated using the Peng-Robinson equation from the critical temperature, critical pressure, and composition ratio of each monomer in the gas phase portion in the reaction vessel is 0. A method for producing a fluorine-containing elastomer by a batch copolymerization method, which is performed under a condition of 0.95 or more and a converted pressure of 0.80 or more,
The general formula: R f 1 · I x
(In the formula, R f 1 is a saturated or unsaturated fluorohydrocarbon group or chlorofluorohydrocarbon group having 1 to 16 carbon atoms, and x is the number of bonds of R f 1 and is 1 or more. And an ethylenically unsaturated compound containing at least one fluoroolefin in the presence of an integer of 4 or less.

本発明は、高圧下でヨウ素移動重合を行うことにより、重合開始剤が少ないにもかかわらず重合速度が大幅に増大し、非ヨウ素移動重合法に匹敵する生産性の高い含フッ素エラストマーの製造方法に関する。さらに、この方法によって製造したエラストマーは、分岐が少なく、末端ヨウ素含有率が高く、また、圧縮永久歪みが小さく、引張破断伸びが良い、優れた含フッ素成形品を提供することができるものである。   The present invention is a method for producing a fluorine-containing elastomer having a high productivity comparable to the non-iodine transfer polymerization method by performing iodine transfer polymerization under a high pressure, thereby greatly increasing the polymerization rate despite a small amount of polymerization initiator. About. Furthermore, the elastomer produced by this method can provide an excellent fluorine-containing molded article with few branches, high terminal iodine content, low compression set, good tensile elongation at break. .

本発明の製造方法の特徴は、ヨウ素移動重合法を高圧下で行なうところにある。ヨウ素移動重合法に特に規定はないが、重合終了時の含フッ素ポリマー粒子数を多くすることが生産性の点で好ましく、その手段として、国際公開第００／０１７４１号パンフレットに記載されているシード重合法が好ましい。   The production method of the present invention is characterized in that the iodine transfer polymerization method is performed under high pressure. The iodine transfer polymerization method is not particularly defined, but it is preferable from the viewpoint of productivity to increase the number of fluorine-containing polymer particles at the end of the polymerization. As a means for that, the seed described in International Publication No. 00/01741 pamphlet is used. A polymerization method is preferred.

本発明に使用する反応槽は、加圧下に重合を行なうので、耐圧容器を使用する。この反応槽内に乳化重合用の目的とするポリマーと同じ組成のポリマー粒子を含む水性媒体（通常は純水）を入れ、液相部分とする。   Since the reaction vessel used in the present invention performs polymerization under pressure, a pressure vessel is used. An aqueous medium (usually pure water) containing polymer particles having the same composition as that of the target polymer for emulsion polymerization is placed in this reaction tank to form a liquid phase portion.

反応槽はこの液相部分と気相部分とから構成されており、気相部分を窒素などで置換したのち重合性モノマーを導入する。ついで反応槽内、とくに液相部分を攪拌して重合性モノマーを気相部分から液相部分に供給する。液相部分に供給されたモノマーはポリマー粒子中に浸透し、ポリマー粒子内の重合性モノマー濃度を上げる。気相部分にモノマーを供給しつづけることにより、ポリマー粒子中のモノマー濃度が飽和状態となる（液相部分へのモノマー供給速度が平衡状態になるとも言える）ので、重合開始剤とヨウ素化合物を投入して重合を開始する。   The reaction tank is composed of a liquid phase portion and a gas phase portion. After the gas phase portion is replaced with nitrogen or the like, a polymerizable monomer is introduced. Next, the polymerizable monomer is supplied from the gas phase portion to the liquid phase portion by stirring the inside of the reaction vessel, particularly the liquid phase portion. The monomer supplied to the liquid phase part penetrates into the polymer particles and raises the concentration of the polymerizable monomer in the polymer particles. By continuously supplying the monomer to the gas phase part, the monomer concentration in the polymer particles becomes saturated (it can be said that the monomer supply rate to the liquid phase part is in an equilibrium state), so the polymerization initiator and iodine compound are added. To start the polymerization.

重合を継続していくとモノマーが消費され、生成ポリマー粒子中のモノマー濃度が低下していくため、ポリマー粒子中に常にモノマー（追加モノマー）を供給し続ける。   As the polymerization is continued, the monomer is consumed and the monomer concentration in the produced polymer particles decreases, so the monomer (additional monomer) is always supplied into the polymer particles.

追加モノマーの比率は、追加されるモノマーおよび目的とするポリマーの組成によるが、重合初期の反応槽内モノマー組成を一定に保つ比率であることが好ましい。   The ratio of the additional monomer depends on the composition of the added monomer and the target polymer, but is preferably a ratio that keeps the monomer composition in the reaction vessel at the initial stage of polymerization constant.

また、重合終了時に含フッ素ポリマー粒子数が水１ｇあたり５×１０13個以上になることが好ましく、粒子数が水１ｇあたり１．０×１０14個以上であることがより好ましい。粒子数が、５×１０13個未満であると、反応速度が低下するだけでなく、粒径が大きく不安定となり、重合槽へのポリマー付着が増加する傾向がある。 Further, the number of fluoropolymer particles is preferably 5 × 10 13 or more per 1 g of water at the end of the polymerization, and more preferably 1.0 × 10 14 or more per 1 g of water. When the number of particles is less than 5 × 10 13 , not only the reaction rate decreases, but also the particle size becomes large and unstable, and the polymer adhesion to the polymerization tank tends to increase.

重合終了時の粒子数を多くする重合方法としては、シード重合法の他に、特公昭６３−８４０６号公報、特公昭６２−２８８６０９号公報に記載されているマイクロエマルション法や、一般的な方法として乳化剤の増量などがあげられる。これらのうち、マイクロエマルション法では、初期にマイクロエマルションを形成させるために、フッ素オイルなどの使用が必要であるため、製品にオイルが残留し、汚染源となるので洗浄除去が必要である。また、乳化剤増量についても、単に重合系を安定にさせ、あるいは重合速度を上げるためには効果的であるが、重合前後に泡立ち現象が発生しやすく、得られたエラストマーに残留した乳化剤が加硫阻害をおこしやすい。また、コストおよび環境の面からも好ましくない方法である。一方、シード重合法は上記の問題がなく、ヨウ素移動系で抜群の効果を示す。   As a polymerization method for increasing the number of particles at the end of the polymerization, in addition to the seed polymerization method, a microemulsion method described in JP-B 63-8406, JP-B 62-288609, or a general method As an example, the amount of emulsifier can be increased. Of these, the microemulsion method requires the use of fluorine oil or the like in order to form a microemulsion in the initial stage, so that the oil remains in the product and becomes a source of contamination, which requires cleaning and removal. In addition, an increase in emulsifier is effective for simply stabilizing the polymerization system or increasing the polymerization rate, but foaming is likely to occur before and after polymerization, and the emulsifier remaining in the resulting elastomer is vulcanized. Easy to block. In addition, this method is not preferable in terms of cost and environment. On the other hand, the seed polymerization method does not have the above-described problem, and exhibits an excellent effect in an iodine transfer system.

本発明の製造方法においては、各モノマー単独の臨界温度、臨界圧力および初期モノマー組成比からＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式によって導いた気相モノマー混合物の臨界温度・臨界圧力から、若干の誤差を補正するための換算温度０．９５以上、好ましくは、０．９７以上、換算圧力０．８０以上、好ましくは、０．８５以上の条件でのバッチ式重合をおこなう。気相部の混合モノマーが換算温度、換算圧力ともに上回ることにより、高いモノマー密度のもとでの重合が可能になり、重合速度が速くなることに加え、主鎖の分岐やイオン末端が少ないポリマーが得られるため、圧縮永久歪みが大幅に改善される。ここで、換算温度とは、
換算温度 ＴR＝Ｔ／Ｔc
（式中、Ｔは重合時の実際の温度であり、ＴcはＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式を用いて算出した臨界温度である）
により決定されるものであり、同様に換算圧力とは、
換算圧力 ＰR＝Ｐ／Ｐc
（式中、Ｐは重合時の実際の圧力であり、ＰcはＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式を用いて算出した臨界圧力である）
により決定されるものである。 In the production method of the present invention, a slight error is corrected from the critical temperature and critical pressure of the gas phase monomer mixture derived from the critical temperature, critical pressure and initial monomer composition ratio of each monomer by the Peng-Robinson equation. Batch polymerization is carried out under the conditions of a conversion temperature of 0.95 or more, preferably 0.97 or more, a conversion pressure of 0.80 or more, preferably 0.85 or more. When the mixed monomer in the gas phase exceeds both the converted temperature and the converted pressure, it is possible to polymerize at a high monomer density, and the polymerization rate is increased. In addition, the polymer has few main chain branches and ion ends. Therefore, compression set is greatly improved. Here, the converted temperature is
Conversion temperature T R = T / T c
(Where T is the actual temperature during polymerization and T c is the critical temperature calculated using the Peng-Robinson equation)
Similarly, the equivalent pressure is
Conversion pressure P R = P / P c
(Where P is the actual pressure during polymerization and P c is the critical pressure calculated using the Peng-Robinson equation)
Is determined by

ここで、臨界温度および臨界圧力を決定するＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式について説明する。一般に、重合槽内の初期モノマー密度が高いほど得られるポリマーに組成分布が生じやすいこと、および、特に初期モノマーが臨界点付近からモノマー密度が急激に上昇することが知られている。ところが２成分以上のモノマーを共重合する場合、気相モノマー混合物の臨界点はモノマーの種類と組成比によって変動する。これを各モノマー単独の臨界温度、臨界圧力および初期モノマー組成比から混合モノマーの臨界点を算出する方法としてＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式を採用した。同式の原理はＤ．Ｙ．Ｐｅｎｇ ａｎｄ Ｄ．Ｂ．Ｒｏｂｉｎｓｏｎ，”Ａ Ｎｅｗ Ｔｗｏ−Ｃｏｎｓｔａｎｔ Ｅｑｕａｔｉｏｎ ｏｆ ｓｔａｔｅ”，Ｉｎｄ．Ｅｎｇ．Ｃｈｅｍ．Ｆｕｎｄ．，Ｖｏｌ．１５，（１９７６），p.５９−６４で述べられている。概要としては下記の式を原理としており、実際の計算にはＡｓｐｅｎ Ｐｌｕｓ（Ａｓｐｅｎ Ｔｅｃｈ社製）などのプロセスシュミレーターが使用できる。   Here, the Peng-Robinson equation for determining the critical temperature and the critical pressure will be described. In general, it is known that the higher the initial monomer density in the polymerization tank, the easier the composition distribution occurs in the polymer obtained, and that the monomer density increases rapidly from the critical point of the initial monomer. However, when copolymerizing two or more monomers, the critical point of the gas phase monomer mixture varies depending on the type and composition ratio of the monomers. The Peng-Robinson equation was employed as a method for calculating the critical point of the mixed monomer from the critical temperature, critical pressure and initial monomer composition ratio of each monomer alone. The principle of this equation is Y. Peng and D.C. B. Robinson, “A New Two-Constant Equation of state”, Ind. Eng. Chem. Fund. , Vol. 15, (1976), p.59-64. The outline is based on the following formula, and a process simulator such as Aspen Plus (manufactured by Aspen Tech) can be used for actual calculation.

Ｐｅｎｇ−Ｒｏｂｉｎｓｏｎ式の概略は下記の通りである。   The outline of the Peng-Robinson formula is as follows.

Figure 2007231298
ここで、上記式中のａi、ｂiは、それぞれ以下のように定義する。
ａi＝αi０．４５７２４Ｒ2Ｔci 2／Ｐci
αi（Ｔ）＝［１＋ｍi（１−Ｔci 0.5）］2
ｍi＝０．３７４６４＋１．５４２２６ωi−０．２６９９２ωi 2
ｂi＝０．０７７８ＲＴci／Ｐci
Figure 2007231298
 Here, a i and b i in the above formula are respectively defined as follows.
a i = α i 0.45724R 2 T ci 2 / P ci
α i (T) = [1 + m i (1−T ci 0.5 )] 2
m i = 0.37464 + 1.54226ω i −0.26992ω i 2
b i = 0.0778RT ci / P ci

また、各パラメータは下記のことを表す。
Ｐ ：圧力
Ｔ ：温度
Ｖm ：体積
Ｒ ：気体定数
Ｘi ：モノマー成分ｉの組成比
Ｔci：モノマー成分ｉの臨界温度
Ｐci：モノマー成分ｉの臨界圧力
ωi ：モノマー成分ｉの偏心因子 Each parameter represents the following.
P: Pressure T: Temperature V m: volume R: gas constant X i: composition ratio of the monomer component i T ci: critical temperature P ci of the monomer component i: critical pressure of the monomer component i omega i: eccentricity factor of monomer component i

具体的な計算例として、重合槽内組成がＶｄＦ／ＨＦＰ＝３６／６４（モル％）であるときのＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式による臨界温度、臨界圧力計算をＡｓｐｅｎ Ｐｌｕｓ Ｖｅｒ．１１．１を用いて行なったところ、Ｔc＝８７．７℃、Ｐc＝３．０５ＭＰａであった。前記換算温度０．９５、換算圧力０．８０による変換を行なうと、この場合の重合条件は、Ｔ＝６９．７℃以上、Ｐ＝２．４４ＭＰａ以上である。 As a specific calculation example, the critical temperature and critical pressure calculation according to the Peng-Robinson equation when the composition in the polymerization tank is VdF / HFP = 36/64 (mol%) is calculated using Aspen Plus Ver. As a result of using 11.1, T c = 87.7 ° C. and P c = 3.05 MPa. When conversion is performed at a conversion temperature of 0.95 and a conversion pressure of 0.80, the polymerization conditions in this case are T = 69.7 ° C. or higher and P = 2.44 MPa or higher.

換算温度が、０．９５未満または換算圧力が、０．８０未満であると、ポリマー粒子中のモノマー濃度が飽和に達せず、重合速度が低下するだけでなく、目的のポリマーが得られにくい傾向がある。また、前記式から算出される条件式を満たす温度および圧力の中でもさらに好ましい重合温度は、１０〜１２０℃であり、特に好ましくは３０〜１００℃であり、好ましい重合圧力は、３ＭＰａ以上であり、より好ましくは３．５ＭＰａ以上であり、さらに好ましくは４ＭＰａ以上である。また、圧力の上限値は、特に限定はないが、モノマーの取扱いや、反応設備コストなどを考慮すると１５ＭＰａ以下が好ましく、１２ＭＰａ以下であることがより好ましい。   When the conversion temperature is less than 0.95 or the conversion pressure is less than 0.80, the monomer concentration in the polymer particles does not reach saturation, the polymerization rate is decreased, and the target polymer tends not to be obtained. There is. Further, among the temperature and pressure satisfying the conditional expression calculated from the above formula, a more preferable polymerization temperature is 10 to 120 ° C, particularly preferably 30 to 100 ° C, and a preferable polymerization pressure is 3 MPa or more, More preferably, it is 3.5 MPa or more, More preferably, it is 4 MPa or more. The upper limit value of the pressure is not particularly limited, but is preferably 15 MPa or less, more preferably 12 MPa or less in consideration of handling of the monomer, reaction equipment cost, and the like.

さらに、攪拌することが好ましい。攪拌することによって、ポリマー粒子中のモノマー濃度を、重合を通して高く維持できるためである。   Furthermore, it is preferable to stir. This is because the monomer concentration in the polymer particles can be kept high throughout the polymerization by stirring.

攪拌の手段としては、たとえばアンカー翼、タービン翼、傾斜翼なども使用できるが、モノマーの拡散とポリマーの分散安定性が良好な点からフルゾーンやマックスブレンドと呼ばれる大型翼による攪拌が好ましい。   As a means for stirring, for example, an anchor blade, a turbine blade, an inclined blade, or the like can be used. From the viewpoint of good monomer diffusion and polymer dispersion stability, stirring with a large blade called full zone or max blend is preferable.

攪拌装置としては、横型攪拌装置でも縦型攪拌装置でもよい。   The stirring device may be a horizontal stirring device or a vertical stirring device.

反応系は、実質的にモノマー相部分を有する。ここで、実質的にモノマー相を有するとは、重合容器の体積に対して、水などの媒体が占める体積が９０％以下の状態で重合を行うことを示し、好ましくは８０％以下である。体積が９０％を超えると、モノマーが媒体に供給されにくく、重合速度が低下する、あるいはポリマー物性が悪化する傾向がある。   The reaction system has a monomer phase portion substantially. Here, having substantially a monomer phase means that the polymerization is performed in a state where the volume occupied by a medium such as water is 90% or less, preferably 80% or less, with respect to the volume of the polymerization vessel. When the volume exceeds 90%, it is difficult for the monomer to be supplied to the medium, the polymerization rate tends to decrease, or the polymer physical properties tend to deteriorate.

本発明で用いられる一般式：Ｒf 1・Ｉxで示されるヨウ素化合物のＲf 1は、炭素数１〜１６の飽和もしくは不飽和のフルオロ炭化水素基またはクロロフルオロ炭化水素基であり、炭素数４〜８のパーフルオロアルキル基であることが好ましい。炭素数が１６をこえると、反応性が低下する傾向がある。 Formula used in the present invention: R f 1 iodine compound represented by R f 1 · I x is fluoro hydrocarbon group or chlorofluoro hydrocarbon group having a saturated or unsaturated 1 to 16 carbon atoms, carbon A perfluoroalkyl group of several 4 to 8 is preferable. When the carbon number exceeds 16, the reactivity tends to decrease.

一般式：Ｒf 1・Ｉxで示されるヨウ素化合物のｘは、Ｒf 1の結合手の数であって、１以上４以下の整数であり、２以上３以下であることが好ましい。ｘが４をこえても使用可能であるが、合成コストの点では好ましくない。ポリマー分岐が少ない点で、ｘは２が最も好ましい。 In the iodine compound represented by the general formula: R f 1 · I x , x is the number of bonds of R f 1 and is an integer of 1 or more and 4 or less, preferably 2 or more and 3 or less. Although it can be used even if x exceeds 4, it is not preferable in terms of synthesis cost. X is most preferably 2 in terms of few polymer branches.

このヨウ素化合物の炭素−ヨウ素結合は、比較的弱い結合であって、ラジカル発生源の存在下にラジカルとして開裂する。生じたラジカルの反応性が高いために、モノマーが付加成長反応を起こし、しかる後にヨウ素化合物からヨウ素を引き抜くことにより反応を停止する。このようにして得られた分子末端の炭素にヨウ素が結合している含フッ素エラストマーは、末端ヨウ素が有効な加硫点となり効率的に加硫できる。   The carbon-iodine bond of this iodine compound is a relatively weak bond and is cleaved as a radical in the presence of a radical source. Due to the high reactivity of the radicals generated, the monomer undergoes an additional growth reaction, and then the reaction is stopped by extracting iodine from the iodine compound. The fluorine-containing elastomer in which iodine is bonded to the carbon at the molecular terminal thus obtained can be efficiently vulcanized with the terminal iodine as an effective vulcanization point.

一般式：Ｒf 1・Ｉxで示されるヨウ素化合物としては、モノヨードパーフルオロメタン、モノヨードパーフルオロエタン、モノヨードパーフルオロプロパン、モノヨードパーフルオロブタン〔たとえば、２−ヨードパーフルオロブタン、１−ヨードパーフルオロ（１，１−ジメチルエタン）〕、モノヨードパーフルオロペンタン〔たとえば１−ヨードパールフオロ（４−メチルブタン）〕、１−ヨードパーフルオロ−ｎ−オクタン、モノヨードパーフルオロシクロブタン、２−ヨードパーフルオロ（１−シクロブチルエタン）シクロヘキサン、モノヨードパーフルオロシクロヘキサン、モノヨードトリフルオロシクロブタン、モノヨードジフルオロメタン、モノヨードモノフルオロメタン、２−ヨード−１−ハイドロパーフルオロエタン、３−ヨード−１−ハイドロパーフルオロプロパン、モノヨードモノクロロジフルオロメタン、モノヨードジクロロモノフルオロメタン、２−ヨード−１，２−ジクロロ−１，１，２−トリフルオロエタン、４−ヨード−１，２−ジクロロパーフルオロブタン、６−ヨード−１，２−ジクロロパーフルオロヘキサン、４−ヨード−１，２，４−トリクロロパーフルオロブタン、１−ヨード−２，２−ジハイドロパーフルオロプロパン、１−ヨード−２−ハイドロパーフルオロプロパン、モノヨードトリフルオロエチレン、３−ヨードパフルオロプロペン−１、４−ヨードパーフルオロペンテン−１、４−ヨード−５−クロロパーフルオロペンテン−１、２−ヨードパーフルオロ（１−シクロブテニルエタン）、１，３−ジヨードパフルオロプロパン、１，４−ジヨードパーフルオロ−ｎ−ブタン、１，３−ジヨード−２−クロロパーフルオロプロパン、１，５−ジヨード−２，４−ジクロロパーフルオロ−ｎ−ペンタン、１，７−ジヨードパーフルオロ−ｎ−オクタン、１，２−ジ（ヨードジフルオロメチル）パーフルオロシクロブタン、２−ヨード−１，１，１−トリフルオロエタン、１−ヨード−１−ハイドロパーフルオロ（２−メチルエタン）、２−ヨード−２，２−ジクロロ−１，１，１−トリフルオロエタン、２−ヨード−２−クロロ−１，１，１−トリフルオロエタンなどがあげられる。さらに、Ｒf 1の炭化水素基には、エーテル結合性酸素原子、チオエーテル結合性硫黄原子、カルボキシル基などの官能基を含んでいてもよく、２−ヨードパーフルオロエチルパーフルオロビニルエーテル、２−ヨードパーフルオロエチルパーフルオロイソプロピルエーテル、３−ヨード−２−クロロパーフルオロブチルパーフルオロメチルチオエーテル、３−ヨード−４−クロロパーフルオロ酪酸などをあげることができる。 Examples of the iodine compound represented by the general formula: R f 1 · I x include monoiodoperfluoromethane, monoiodoperfluoroethane, monoiodoperfluoropropane, monoiodoperfluorobutane [for example, 2-iodoperfluorobutane, 1-iodoperfluoro (1,1-dimethylethane)], monoiodoperfluoropentane [for example, 1-iodoperfluoro (4-methylbutane)], 1-iodoperfluoro-n-octane, monoiodoperfluorocyclobutane, 2-iodoperfluoro (1-cyclobutylethane) cyclohexane, monoiodoperfluorocyclohexane, monoiodotrifluorocyclobutane, monoiododifluoromethane, monoiodomonofluoromethane, 2-iodo-1-hydroperfluoroethane, 3 Iodo-1-hydroperfluoropropane, monoiodomonochlorodifluoromethane, monoiododichloromonofluoromethane, 2-iodo-1,2-dichloro-1,1,2-trifluoroethane, 4-iodo-1,2- Dichloroperfluorobutane, 6-iodo-1,2-dichloroperfluorohexane, 4-iodo-1,2,4-trichloroperfluorobutane, 1-iodo-2,2-dihydroperfluoropropane, 1-iodo 2-hydroperfluoropropane, monoiodotrifluoroethylene, 3-iodopafluoropropene-1, 4-iodoperfluoropentene-1, 4-iodo-5-chloroperfluoropentene-1, 2-iodoperfluoro (1-cyclobutenylethane), 1,3-diiodopafluoropropa 1,4-diiodoperfluoro-n-butane, 1,3-diiodo-2-chloroperfluoropropane, 1,5-diiodo-2,4-dichloroperfluoro-n-pentane, 1,7-di Iodoperfluoro-n-octane, 1,2-di (iododifluoromethyl) perfluorocyclobutane, 2-iodo-1,1,1-trifluoroethane, 1-iodo-1-hydroperfluoro (2-methylethane) 2-iodo-2,2-dichloro-1,1,1-trifluoroethane, 2-iodo-2-chloro-1,1,1-trifluoroethane, and the like. Further, the hydrocarbon group of R f 1 may contain a functional group such as an ether-bonded oxygen atom, a thioether-bonded sulfur atom, a carboxyl group, 2-iodoperfluoroethyl perfluorovinyl ether, 2-iodo Examples thereof include perfluoroethyl perfluoroisopropyl ether, 3-iodo-2-chloroperfluorobutyl perfluoromethylthioether, and 3-iodo-4-chloroperfluorobutyric acid.

これらの中でも、合成の容易さ、反応性、経済性、安定性の点で、１，４−ジヨードパーフルオロ−ｎ−ブタンが好ましい。   Among these, 1,4-diiodoperfluoro-n-butane is preferable from the viewpoint of ease of synthesis, reactivity, economy, and stability.

これらのヨウ素化合物は、適宜公知の方法により製造することができる。たとえば、２−ヨードパーフルオロプロパンは、フッ化カリウムの存在下にヘキサフルオロプロペンをヨウ素と反応させることにより、また１，５−ジヨード−２，４−ジクロロパーフルオロ−ｎ−ペンタンは、３，５−ジクロロパーフルオロ−１，７−へプタン二酸の銀塩をヨウ素と反応させることにより、さらにまた４−ヨード−５−クロロパーフルオロ−１−ペンテンは、パーフルオロ−１，４−ペンタジエンに塩化ヨウ素を反応させることにより製造することができる。   These iodine compounds can be appropriately produced by known methods. For example, 2-iodoperfluoropropane is obtained by reacting hexafluoropropene with iodine in the presence of potassium fluoride, and 1,5-diiodo-2,4-dichloroperfluoro-n-pentane is By reacting the silver salt of 5-dichloroperfluoro-1,7-heptanedioic acid with iodine, 4-iodo-5-chloroperfluoro-1-pentene can also be converted to perfluoro-1,4-pentadiene. It can be produced by reacting with iodine chloride.

ヨウ素化合物の添加量は、含フッ素エラストマーに対して、０．０５〜２．０重量％であることが好ましい。添加量が、０．０５重量％未満であると、加硫が不充分となり、圧縮永久歪み（ＣＳ）が悪化する傾向があり、２．０重量％をこえると、架橋密度が上がり過ぎるために、伸びなどのゴムとしての性能を損なう傾向がある。   The addition amount of the iodine compound is preferably 0.05 to 2.0% by weight with respect to the fluorine-containing elastomer. If the addition amount is less than 0.05% by weight, the vulcanization will be insufficient and the compression set (CS) tends to deteriorate, and if it exceeds 2.0% by weight, the crosslinking density will increase too much. , Tend to impair the performance as rubber, such as elongation.

上記ヨウ素化合物と含フッ素エラストマーを形成するモノマーとしては、少なくとも１種以上のフルオロオレフィンを含み、その共重合モノマーとして、フルオロオレフィン以外のエチレン性不飽和化合物を含んでいてもよい。   The monomer that forms the fluorine-containing elastomer with the iodine compound may contain at least one fluoroolefin, and the copolymerization monomer may contain an ethylenically unsaturated compound other than the fluoroolefin.

この組成が、含フッ素エラストマーを形成する目的には、好ましい。   This composition is preferable for the purpose of forming a fluorine-containing elastomer.

本発明で用いられるフルオロオレフィンとしては、ＣＸ1Ｘ2＝ＣＸ3Ｘ4で示されるものが好ましい。式中のＸ1〜Ｘ3は、水素原子またはハロゲン原子、Ｘ4は、水素原子、ハロゲン原子、カルボキシル基、炭素数１〜９で、水素原子の一部または全部がフッ素原子で置換されたアルキル基、または炭素数１〜９で、水素原子の一部または全部がフッ素原子で置換されたアルコキシ基であり、該オレフィンは少なくとも１つのフッ素原子を含む。 The fluoroolefin used in the present invention, those represented by CX 1 X 2 = CX 3 X 4 are preferred. In the formula, X 1 to X 3 are a hydrogen atom or a halogen atom, X 4 is a hydrogen atom, a halogen atom, a carboxyl group, 1 to 9 carbon atoms, and part or all of the hydrogen atoms are substituted with fluorine atoms The olefin contains at least one fluorine atom, which is an alkyl group or an alkoxy group having 1 to 9 carbon atoms, in which part or all of the hydrogen atoms are substituted with fluorine atoms.

ＣＸ1Ｘ2＝ＣＸ3Ｘ4で示されるフルオロオレフィンとしては、ヘキサフルオロプロピレン（ＨＦＰ）、ビニリデンフルオライド（ＶｄＦ）、テトラフルオロエチレン（ＴＦＥ）、トリフルオロエチレン、ペンタフルオロプロピレン、ビニルフルオライド、ヘキサフルオロイソブテン、クロロトリフルオロエチレン（ＣＴＦＥ）、トリフルオロプロピレン、ペンタフルオロプロピレン、テトラフルオロプロピレン、ヘキサフルオロイソブテン、パーフルオロ（アルキルビニルエーテル）（ＰＡＶＥ）などがあげられるが、エラストマー組成が得られやすい点から、ビニリデンフルオライド（ＶｄＦ）、ヘキサフルオロプロピレン（ＨＦＰ）、テトラフルオロエチレン（ＴＦＥ）、パーフルオロ（アルキルビニルエーテル）（ＰＡＶＥ）が好ましい。 Examples of the fluoroolefin represented by CX 1 X 2 = CX 3 X 4 include hexafluoropropylene (HFP), vinylidene fluoride (VdF), tetrafluoroethylene (TFE), trifluoroethylene, pentafluoropropylene, vinyl fluoride, Hexafluoroisobutene, chlorotrifluoroethylene (CTFE), trifluoropropylene, pentafluoropropylene, tetrafluoropropylene, hexafluoroisobutene, perfluoro (alkyl vinyl ether) (PAVE) and the like, but an elastomer composition is easily obtained To vinylidene fluoride (VdF), hexafluoropropylene (HFP), tetrafluoroethylene (TFE), and perfluoro (alkyl vinyl ether) (PAVE). Arbitrariness.

また、パーフルオロ（アルキルビニルエーテル）類は、耐寒性、耐薬品性の点でも好ましい。   Perfluoro (alkyl vinyl ethers) are also preferable in terms of cold resistance and chemical resistance.

パーフルオロ（アルキルビニルエーテル）としては、パーフルオロ（メチルビニルエーテル）（ＰＭＶＥ）、パーフルオロ（エチルビニルエーテル）（ＰＥＶＥ）、パーフルオロ（プロピルビニルエーテル）（ＰＰＶＥ）などがあげられる。   Examples of perfluoro (alkyl vinyl ether) include perfluoro (methyl vinyl ether) (PMVE), perfluoro (ethyl vinyl ether) (PEVE), perfluoro (propyl vinyl ether) (PPVE), and the like.

また、ＣＸ1Ｘ2＝ＣＸ3Ｘ4以外のフルオロオレフィンとしては、 Moreover, as fluoroolefins other than CX 1 X 2 = CX 3 X 4 ,

Figure 2007231298
で示されるフルオロオレフィンや、
Figure 2007231298
 Fluoroolefins represented by

Figure 2007231298
（式中Ｙは、−ＣＨ2Ｉ、−ＯＨ、−ＣＯＯＨ、−ＳＯ2Ｆ、−ＳＯ3Ｍ(Ｍは水素、ＮＨ4基またはアルカリ金属)、カルボン酸塩、カルボキシエステル基、エポキシ基、ニトリル基、ヨウ素原子、Ｘ5およびＸ6は同じかまたは異なりいずれも水素原子またはフッ素原子、Ｒf 2は炭素数０〜４０の２価の含フッ素アルキレン基であり、エーテル結合性酸素原子を含んでいてもよい）で示される官能基含有フルオロオレフィンやポリフルオロジエン類などがあげられる。
Figure 2007231298
 (Wherein Y is, -CH 2 I, -OH, -COOH , -SO 2 F, -SO 3 M (M is hydrogen, NH 4 group or an alkali metal), carboxylate, carboxylic ester group, an epoxy group, A nitrile group, an iodine atom, X 5 and X 6 are the same or different and each is a hydrogen atom or a fluorine atom, R f 2 is a divalent fluorine-containing alkylene group having 0 to 40 carbon atoms, and an ether-bonded oxygen atom Functional group-containing fluoroolefins and polyfluorodienes which may be included).

官能基含有フルオロオレフィンは、表面改質、架橋密度アップなどの機能性モノマーとして好ましく、ポリフルオロジエン類は、架橋効率の点で好ましい。   Functional group-containing fluoroolefins are preferred as functional monomers for surface modification and crosslinking density increase, and polyfluorodienes are preferred from the viewpoint of crosslinking efficiency.

官能基含有フルオロオレフィンとしては、   As the functional group-containing fluoroolefin,

Figure 2007231298
Figure 2007231298
 などがあげられる。
Figure 2007231298
Figure 2007231298
 Etc.

また、官能基含有フルオロオレフィンとして、特許文献２で開示されているモノマー
ＣＦ2＝ＣＦＯＣＦ2ＣＦ2ＣＨ2Ｉ
は、架橋密度を上昇させる目的において好ましい。 Further, as a functional group-containing fluoroolefin, the monomer CF 2 ═CFOCF 2 CF 2 CH 2 I disclosed in Patent Document 2 is used.
Is preferable for the purpose of increasing the crosslinking density.

ポリフルオロジエン類としては、ＣＦ2＝ＣＦＣＦ＝ＣＦ2、ＣＦ2＝ＣＦＣＦ2ＯＣＦ＝ＣＦ2などがあげられる。 Examples of polyfluorodienes include CF 2 ═CFCF═CF 2 , CF 2 ═CFCF 2 OCF═CF 2, and the like.

フルオロオレフィン以外のエチレン性不飽和化合物としては、特に限定されないが、エチレン（ＥＴ）、プロピレン、ブテン、ペンテンなどの炭素数２〜１０のα−オレフィンモノマー、メチルビニルエーテル、エチルビニルエーテル、プロピルビニルエーテル、シクロヘキシルビニルエーテル、ヒドロキシブチルビニルエーテル、ブチルビニルエーテルなどの炭素数１〜２０のアルキル基を有するアルキルビニルエーテルなどがあげられる。   Although it does not specifically limit as ethylenically unsaturated compounds other than a fluoro olefin, C2-C10 alpha olefin monomers, such as ethylene (ET), propylene, butene, pentene, methyl vinyl ether, ethyl vinyl ether, propyl vinyl ether, cyclohexyl Examples thereof include alkyl vinyl ethers having an alkyl group having 1 to 20 carbon atoms such as vinyl ether, hydroxybutyl vinyl ether and butyl vinyl ether.

これらは、低コスト、耐アミン性の点で好ましい。   These are preferable in terms of low cost and amine resistance.

本発明の含フッ素エラストマーを形成するモノマーの組み合わせとしては、上記ＣＸ1Ｘ2＝ＣＸ3Ｘ4で示されるフルオロオレフィンを１種以上、ＣＸ1Ｘ2＝ＣＸ3Ｘ4以外のフルオロオレフィンを１種以上、ＣＸ1Ｘ2＝ＣＸ3Ｘ4で示されるフルオロオレフィンを１種以上とＣＸ1Ｘ2＝ＣＸ3Ｘ4以外のフルオロオレフィンを１種以上含む組合わせがあり、かつそれぞれの組み合わせの共重合モノマーとして、フルオロオレフィン以外のエチレン性不飽和化合物を含んでいてもよい。 Examples of the combination of monomers forming the fluoroelastomer of the present invention, the CX 1 X 2 = CX 3 X 4 in fluoroolefins represented one or more, the fluoroolefin other than CX 1 X 2 = CX 3 X 4 1 seed above, there is CX 1 X 2 = CX 3 X 4 in fluoroolefins one or more indicated and CX 1 X 2 = CX 3 X 4 other than the fluoroolefin combination comprising at least one, and where each of the combinations As the copolymerization monomer, an ethylenically unsaturated compound other than the fluoroolefin may be contained.

上記フルオロオレフィン、およびフルオロオレフィン以外のエチレン性不飽和化合物の中でも、低コストで良好な加硫性を有する含フッ素エラストマーを形成する目的では、ビニリデンフルオライド（ＶｄＦ）と共重合可能なエチレン性不飽和化合物からなることが好ましい。   Among the above-mentioned fluoroolefins and ethylenically unsaturated compounds other than fluoroolefins, an ethylenically unsaturated copolymerizable with vinylidene fluoride (VdF) is used for the purpose of forming a fluorine-containing elastomer having good vulcanizability at low cost. It is preferable to consist of a saturated compound.

本発明の製造方法により製造された含フッ素エラストマーの１００℃におけるムーニー粘度は、好ましくは３０以上、より好ましくは３５以上であり、パーオキサイド加硫を行なうことにより、同粘度の従来品と比較して、伸びが大きく、圧縮永久歪み（ＣＳ）やロール加工性に優れている。高粘度領域になるほど圧縮永久歪み（ＣＳ）に関しては、従来品との差が大きくなる。   The Mooney viscosity at 100 ° C. of the fluorine-containing elastomer produced by the production method of the present invention is preferably 30 or more, more preferably 35 or more. Compared with a conventional product having the same viscosity by performing peroxide vulcanization. Elongation is large, and compression set (CS) and roll processability are excellent. The higher the viscosity range, the greater the difference from the conventional product in terms of compression set (CS).

ムーニー粘度が、３０未満では、従来品においても同粘度では、架橋効率が上がるため、従来品との差が小さくなる傾向があるが、従来品より悪化することはない。   When the Mooney viscosity is less than 30, even in the conventional product, the crosslinking efficiency is increased at the same viscosity, so that the difference from the conventional product tends to be small, but it is not worse than the conventional product.

次に、本発明の新規含フッ素エラストマーは、ビニリデンフルオライド繰り返し単位２０〜９０モル％、ヘキサフルオロプロピレン繰り返し単位１０〜８０モル％を含み、
（ａ）エラストマー中に０．０１〜１０重量％のヨウ素原子を含有し、
（ｂ）ポリマー数平均分子量が１,０００〜３００,０００であり、
（ｃ）ポリマー濃度約２０％のアセトン溶液を高分解能19Ｆ−ＮＭＲで測定し、下記式 Next, the novel fluorine-containing elastomer of the present invention contains 20 to 90 mol% of vinylidene fluoride repeating units, 10 to 80 mol% of hexafluoropropylene repeating units,
(A) containing 0.01 to 10% by weight of iodine atoms in the elastomer;
(B) The polymer number average molecular weight is 1,000 to 300,000,
(C) An acetone solution having a polymer concentration of about 20% was measured by high resolution 19 F-NMR, and the following formula

Figure 2007231298
により求められる「ＶｄＦ分岐率」が２００ｐｐｍ以下であり、
パーオキサイド加硫が可能である含フッ素エラストマーである。
Figure 2007231298
 "VdF branching rate" calculated by the following is 200 ppm or less,
It is a fluorine-containing elastomer that can be peroxide vulcanized.

本発明の含フッ素エラストマーは、上記の方法によって製造することができる。   The fluorine-containing elastomer of the present invention can be produced by the above method.

本発明の含フッ素エラストマーは、ビニリデンフルオライド（ＶｄＦ）繰り返し単位を２０〜９０モル％含むことが好ましく、より好ましくは４０〜８５モル％、ビニリデンフルオライド（ＶｄＦ）とヘキサフルオロプロピレン（ＨＦＰ）繰り返し単位１０〜８０モル％を含むことが好ましく、１５〜６０モル％がより好ましい。   The fluorine-containing elastomer of the present invention preferably contains 20 to 90 mol% of vinylidene fluoride (VdF) repeating units, more preferably 40 to 85 mol%, and vinylidene fluoride (VdF) and hexafluoropropylene (HFP) repeating units. It is preferable that 10-80 mol% of units are included, and 15-60 mol% is more preferable.

ＶｄＦとＨＦＰの２元共重合体からなる含フッ素エラストマーは、下記に限定するＶｄＦ分岐率が２００ｐｐｍ以下であることが好ましく、１５０ｐｐｍ以下であることがより好ましい。ＶｄＦ分岐率が、２００ｐｐｍをこえると、特にヨウ素を含有するパーオキサイド加硫用エラストマーにおいて、ヨウ素末端が減少するため、加硫効率が低下し、圧縮永久歪み（ＣＳ）などの諸物性が悪化する傾向がある。   The fluorine-containing elastomer composed of a binary copolymer of VdF and HFP preferably has a VdF branching ratio limited to 200 ppm or less, more preferably 150 ppm or less. When the VdF branching ratio exceeds 200 ppm, particularly in the peroxide vulcanization elastomer containing iodine, the end of iodine is reduced, so that the vulcanization efficiency is lowered and various physical properties such as compression set (CS) are deteriorated. Tend.

前記ＶｄＦ分岐率が、２００ｐｐｍ以下であるＶｄＦ／ＨＦＰからなる含フッ素エラストマーに対し、その特性を損なわない範囲で、他の単量体を共重合させることも可能である。他の共重合体としては、例えばテトラフルオロエチレンが例示でき、共重合体組成としては、ビニリデンフルオライド（ＶｄＦ）繰り返し単位を３０〜８９モル％、ヘキサフルオロプロピレン（ＨＦＰ）繰り返し単位を１０〜５０モル％、テトラフルオロエチレン（ＴＦＥ）繰り返し単位を０．１〜４０モル％の範囲があげられる。   It is also possible to copolymerize other monomers to the fluorine-containing elastomer composed of VdF / HFP having a VdF branching ratio of 200 ppm or less within a range that does not impair the characteristics. Examples of the other copolymer include tetrafluoroethylene, and the copolymer composition includes 30 to 89 mol% of vinylidene fluoride (VdF) repeating units and 10 to 50 hexafluoropropylene (HFP) repeating units. A range of 0.1 to 40 mol% of the mol%, tetrafluoroethylene (TFE) repeating unit is given.

記
測定ポリマーのアセトン溶液（濃度約２０％）を高分解能19Ｆ−ＮＭＲで測定し、次の計算式で「ＶｄＦ分岐率」を求める。 The acetone solution (concentration of about 20%) of the measurement polymer is measured by high resolution 19 F-NMR, and “VdF branching ratio” is obtained by the following calculation formula.

Figure 2007231298
Figure 2007231298

上記で規定した分岐とは、   The branch specified above is

Figure 2007231298
主に上記のような構造単位で分岐ＣＨ基に隣接するＣＦ2基の面積を表し、これがδＦ−９６．５〜−９９．５ｐｐｍ間に現れる。このピークの面積が、δＦ−８８．０〜−１２４．０ｐｐｍに現れる全体のＣＦ2基合計面積に対して、占める割合が分岐率である。ところが、一本のＣＦ2連鎖に対して、３個の分岐隣接ＣＦ2基が存在するため、単位ＶｄＦに対する分岐率は、この測定値の１／３と計算される。
Figure 2007231298
 It mainly represents the area of the CF 2 group adjacent to the branched CH group in the structural unit as described above, and this appears between δF-96.5 to -99.5 ppm. The ratio of the peak area to the total area of CF 2 groups appearing at δF-88.0 to -124.0 ppm is the branching rate. However, since there are three branched adjacent CF 2 groups for one CF 2 chain, the branching rate for the unit VdF is calculated as 1/3 of this measured value.

ここで高分解能とは、５００ＭＨｚ以上のスペクトロメータによる測定をさす。   Here, high resolution refers to measurement with a spectrometer of 500 MHz or higher.

また、含フッ素エラストマーは、エラストマー中に０．０１〜１０重量％のヨウ素原子を含むことが好ましく、０．０５〜２．０重量％がより好ましい。ヨウ素原子含有量が、０．０５重量％未満であると加硫が不充分となり、圧縮永久歪みが悪化する傾向があり、２．０重量％をこえると架橋密度が高すぎ、伸びが小さすぎるなど、ゴムとしての性能が悪化する傾向がある。   Moreover, it is preferable that a fluorine-containing elastomer contains 0.01-10 weight% iodine atom in an elastomer, and 0.05-2.0 weight% is more preferable. When the iodine atom content is less than 0.05% by weight, the vulcanization becomes insufficient and the compression set tends to deteriorate, and when it exceeds 2.0% by weight, the crosslinking density is too high and the elongation is too small. As a result, the rubber performance tends to deteriorate.

さらに、エラストマーの数平均分子量が１，０００〜３００，０００であることが好ましい。分子量が、１，０００未満であると、粘度が低すぎて取り扱い性が悪化する傾向があり、３００，０００をこえると同様に粘度が上昇しすぎて取り扱い性が悪化する傾向がある。   Further, the number average molecular weight of the elastomer is preferably 1,000 to 300,000. If the molecular weight is less than 1,000, the viscosity tends to be too low and the handleability tends to deteriorate, and if it exceeds 300,000, the viscosity tends to increase and the handleability tends to deteriorate.

分子量分布（重量平均分子量Ｍｗ／数平均分子量Ｍｎ）は、１．５以上であることが好ましく、１．８以上であることがより好ましい。分子量分布が、１．５未満であると、物性面で問題はないものの、ロール加工性が悪化する傾向がある。   The molecular weight distribution (weight average molecular weight Mw / number average molecular weight Mn) is preferably 1.5 or more, and more preferably 1.8 or more. When the molecular weight distribution is less than 1.5, there is no problem in terms of physical properties, but roll processability tends to deteriorate.

また、得られた含フッ素エラストマーに、さらに結晶性セグメントを逐次重合して得られるセグメント化エラストマーは、熱可塑性プラスチックなどに好適に用いられる。   Moreover, the segmented elastomer obtained by sequentially polymerizing the crystalline segment to the obtained fluorine-containing elastomer is suitably used for thermoplastics and the like.

結晶性セグメントとしては、特に限定されないが、テトラフルオロエチレン、パーフルオロ（プロピル）ビニルエーテル、ヘキサフルオロプロピレン、エチレン（ＥＴ）、プロピレン、ブテンなどがあげられる。   The crystalline segment is not particularly limited, and examples thereof include tetrafluoroethylene, perfluoro (propyl) vinyl ether, hexafluoropropylene, ethylene (ET), propylene, and butene.

本発明の製造方法において、重合開始剤として油溶性ラジカル重合開始剤、または水溶性ラジカル開始剤を使用できる。   In the production method of the present invention, an oil-soluble radical polymerization initiator or a water-soluble radical initiator can be used as the polymerization initiator.

本発明で用いる油溶性ラジカル重合開始剤としては、通常周知の油溶性の過酸化物が用いられ、たとえばジイソプロピルパーオキシジカーボネート、ジｓｅｃ−ブチルパーオキシジカーボネートなどのジアルキルパーオキシカーボネート類、ｔ−ブチルパーオキシイソブチレート、ｔ−ブチルパーオキシピバレートなどのパーオキシエステル類、ジｔ−ブチルパーオキサイドなどのジアルキルパーオキサイド類などが、また、ジ（ω−ハイドロ−ドデカフルオロヘプタノイル）パーオキサイド、ジ（ω−ハイドロ−テトラデカフルオロヘプタノイル）パーオキサイド、ジ（ω−ハイドロ−ヘキサデカフルオロノナノイル）パーオキサイド、ジ（パーフルオロブチリル）パーオキサイド、ジ（パーフルパレリル）パーオキサイド、ジ（パーフルオロヘキサノイル）パーオキサイド、ジ（パーフルオロヘプタノイル）パーオキサイド、ジ（パーフルオロオクタノイル）パーオキサイド、ジ（パーフルオロノナノイル）パーオキサイド、ジ（ω−クロロ−ヘキサフルオロブチリル）パーオキサイド、ジ（ω−クロロ−デカフルオロヘキサノイル）パーオキサイド、ジ（ω−クロロ−テトラデカフルオロオクタノイル）パーオキサイド、ω−ハイドロ−ドデカフルオロヘプタノイル−ω−ハイドロヘキサデカフルオロノナノイル−パーオキサイド、ω−クロロ−ヘキサフルオロブチリル−ω−クロ−デカフルオロヘキサノイル−パーオキサイド、ω−ハイドロドデカフルオロヘプタノイル−パーフルオロブチリル−パーオキサイド、ジ（ジクロロペンタフルオロブタノイル）パーオキサイド、ジ（トリクロロオクタフルオロヘキサノイル）パーオキサイド、ジ（テトラクロロウンデカフルオロオクタノイル）パーオキサイド、ジ（ペンタクロロテトラデカフルオロデカノイル）パーオキサイド、ジ（ウンデカクロロドトリアコンタフルオロドコサノイル）パーオキサイドのジ［パーフロロ（またはフルオロクロロ）アシル］パーオキサイド類などが代表的なものとしてあげられる。   As the oil-soluble radical polymerization initiator used in the present invention, generally known oil-soluble peroxides are used. For example, dialkyl peroxycarbonates such as diisopropyl peroxydicarbonate and disec-butylperoxydicarbonate, t Peroxyesters such as butyl peroxyisobutyrate and t-butyl peroxypivalate, dialkyl peroxides such as di-t-butyl peroxide, and di (ω-hydro-dodecafluoroheptanoyl) Peroxide, di (ω-hydro-tetradecafluoroheptanoyl) peroxide, di (ω-hydro-hexadecafluorononanoyl) peroxide, di (perfluorobutyryl) peroxide, di (perfluarparyl) peroxide, The (perfluo Hexanoyl) peroxide, di (perfluoroheptanoyl) peroxide, di (perfluorooctanoyl) peroxide, di (perfluorononanoyl) peroxide, di (ω-chloro-hexafluorobutyryl) peroxide, di (Ω-chloro-decafluorohexanoyl) peroxide, di (ω-chloro-tetradecafluorooctanoyl) peroxide, ω-hydro-dodecafluoroheptanoyl-ω-hydrohexadecafluorononanoyl peroxide, ω -Chloro-hexafluorobutyryl-ω-chloro-decafluorohexanoyl-peroxide, ω-hydrododecafluoroheptanoyl-perfluorobutyryl-peroxide, di (dichloropentafluorobutanoyl) peroxide, di (to Chlorooctafluorohexanoyl) peroxide, di (tetrachloroundecafluorooctanoyl) peroxide, di (pentachlorotetradecafluorodecanoyl) peroxide, di (undecachlorodotriacontafluorodocosanoyl) peroxide Typical examples include di [perfluoro (or fluorochloro) acyl] peroxides.

しかし、代表的な油溶性開始剤である、ジ−イソプロピルパーオキシカーボネイト（ＩＰＰ）やジ−ｎ−プロピルパーオキシカーボネイト（ＮＰＰ）などのパーオキシカーボネイト類は爆発の危険性がある上、高価であり、しかも重合反応中に重合槽の壁面などのスケールの付着が生じやすいという問題があるので、水溶性ラジカル重合開始剤を使用することが好ましい。   However, typical oil-soluble initiators such as di-isopropyl peroxycarbonate (IPP) and di-n-propyl peroxycarbonate (NPP) are explosive and expensive. In addition, since there is a problem that scales such as the wall of the polymerization tank are easily deposited during the polymerization reaction, it is preferable to use a water-soluble radical polymerization initiator.

水溶性ラジカル重合性開始剤としては、通常周知の水溶性の過酸化物が用いられ、たとえば、過硫酸、過ホウ酸、過塩素酸、過リン酸、過炭酸などのアンモニウム塩、カリウム塩、ナトリウム塩、ｔ−ブチルパーマレエート、ｔ−ブチルハイドロパーオキサイドなどがあげられる。   As the water-soluble radical polymerizable initiator, generally known water-soluble peroxides are used. For example, ammonium salts such as persulfuric acid, perboric acid, perchloric acid, perphosphoric acid, percarbonate, potassium salts, Examples thereof include sodium salt, t-butyl permaleate, t-butyl hydroperoxide and the like.

水溶性ラジカル開始剤の添加量は、特に限定はないが、重合速度が著しく低下しない程度の量（たとえば、数ｐｐｍ対水濃度）以上を重合の初期に一括して、または逐次的に、または連続して添加すればよい。上限は、装置面から重合反応熱を除熱出来る範囲である。   The addition amount of the water-soluble radical initiator is not particularly limited, but an amount that does not significantly reduce the polymerization rate (for example, several ppm with respect to water concentration) or more in the initial stage of polymerization, or sequentially, or What is necessary is just to add continuously. The upper limit is a range in which the heat of polymerization reaction can be removed from the surface of the apparatus.

本発明の製造法において、さらに乳化剤、分子量調整剤、ｐＨ調整剤などを添加してもよい。分子量調整剤は、初期に一括して添加してもよいし、連続的または分割して添加してもよい。   In the production method of the present invention, an emulsifier, a molecular weight adjusting agent, a pH adjusting agent and the like may be further added. The molecular weight modifier may be added all at once in the initial stage, or may be added continuously or dividedly.

乳化剤としては、非イオン性界面活性剤、アニオン性界面活性剤、カチオン性界面活性剤などが使用でき、とくにたとえばパーフルオロオクタン酸アンモニウムなどのフッ素系のアニオン性界面活性剤が好ましい。添加量（対重合水）は、好ましくは５０〜５０００ｐｐｍである。   As the emulsifier, a nonionic surfactant, an anionic surfactant, a cationic surfactant, and the like can be used, and a fluorine-based anionic surfactant such as ammonium perfluorooctanoate is particularly preferable. The addition amount (with respect to polymerization water) is preferably 50 to 5000 ppm.

分子量調整剤としては、たとえばマロン酸ジメチル、マロン酸ジエチル、酢酸メチル、酢酸エチル、酢酸ブチル、コハク酸ジメチルなどのエステル類のほか、イソペンタン、イソプロパノール、アセトン、各種メルカプタン、四塩化炭素、シクロヘキサン、モノヨードメタン、１−ヨードメタン、１−ヨード−ｎ−プロパン、ヨウ化イソプロピル、ジヨードメタン、１，２−ジヨードメタン、１，３−ジヨード−ｎ−プロパンなどがあげられる。   Examples of the molecular weight regulator include esters such as dimethyl malonate, diethyl malonate, methyl acetate, ethyl acetate, butyl acetate, dimethyl succinate, isopentane, isopropanol, acetone, various mercaptans, carbon tetrachloride, cyclohexane, mono Examples include iodomethane, 1-iodomethane, 1-iodo-n-propane, isopropyl iodide, diiodomethane, 1,2-diiodomethane, 1,3-diiodo-n-propane.

そのほか緩衝剤などを適宜添加してもよいが、その量は本発明の効果を損なわない範囲とする。   In addition, a buffering agent or the like may be added as appropriate, but the amount is within a range that does not impair the effects of the present invention.

本発明の含フッ素エラストマー組成物は、こうした含フッ素エラストマーおよび加硫剤からなり、加硫助剤を含んでもよい。   The fluorine-containing elastomer composition of the present invention comprises such a fluorine-containing elastomer and a vulcanizing agent, and may contain a vulcanization aid.

本発明で使用可能な加硫剤としては、採用する加硫系によって適宜選定すればよい。加硫系としてはポリアミン加硫系、ポリオール加硫系、パーオキサイド加硫系のいずれも採用できるが、とくにパーオキサイド加硫系で加硫したときに本発明の効果が顕著に発揮できる。   What is necessary is just to select suitably as a vulcanizing agent which can be used by this invention by the vulcanization system to employ | adopt. As the vulcanization system, any of a polyamine vulcanization system, a polyol vulcanization system, and a peroxide vulcanization system can be adopted, but the effect of the present invention can be remarkably exhibited especially when vulcanized in a peroxide vulcanization system.

加硫剤としては、ポリオール加硫系ではたとえば、ビスフェノールＡＦ、ヒドロキノン、ビスフェノールＡ、ジアミノビスフェノールＡＦなどのポリヒドロキシ化合物が、パーオキサイド加硫系ではたとえばα，α′−ビス（ｔ−ブチルパーオキシ）ジイソプロピルベンゼン、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキサン、ジクミルパーオキサイドなどの有機過酸化物が、ポリアミン加硫系ではたとえばヘキサメチレンジアミンカーバメート、Ｎ，Ｎ′−ジシンナミリデン−１，６−ヘキサメチレンジアミンなどのポリアミン化合物があげられる。しかしこれらに限られるものではない。   Examples of the vulcanizing agent include polyhydroxy compounds such as bisphenol AF, hydroquinone, bisphenol A, and diaminobisphenol AF in the polyol vulcanizing system, and α, α'-bis (t-butylperoxy) in the peroxide vulcanizing system. ) Organic peroxides such as diisopropylbenzene, 2,5-dimethyl-2,5-di (t-butylperoxy) hexane, dicumyl peroxide are polymethylene vulcanization systems such as hexamethylenediamine carbamate, N, N And polyamine compounds such as' -dicinnamylidene-1,6-hexamethylenediamine. However, it is not limited to these.

これらの中でも、加硫性、取り扱い性の点から、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキサンが好ましい。   Among these, 2,5-dimethyl-2,5-di (t-butylperoxy) hexane is preferable from the viewpoints of vulcanizability and handleability.

加硫剤の配合量はエラストマー１００重量部に対して０．０１〜１０重量部であり、好ましくは０．１〜５重量部である。加硫剤が、０．０１重量部より少ないと、加硫度が不足するため、含フッ素成形品の性能が損なわれる傾向があり、１０重量部をこえると、加硫密度が高くなりすぎるため加硫時間が長くなることに加え、経済的にも好ましくない傾向がある。   The compounding quantity of a vulcanizing agent is 0.01-10 weight part with respect to 100 weight part of elastomers, Preferably it is 0.1-5 weight part. If the vulcanizing agent is less than 0.01 parts by weight, the degree of vulcanization is insufficient, so the performance of the fluorine-containing molded product tends to be impaired. If the amount exceeds 10 parts by weight, the vulcanization density becomes too high. In addition to a long vulcanization time, there is a tendency to be economically undesirable.

ポリオール加硫系の加硫助剤としては、各種の４級アンモニウム塩、４級ホスホニウム塩、環状アミン、１官能性アミン化合物など、通常エラストマーの加硫に使用される有機塩基が使用できる。具体例としては、たとえばテトラブチルアンモニウムブロミド、テトラブチルアンモニウムクロリド、ベンジルトリブチルアンモニウムクロリド、ベンジルトリエチルアンモニウムクロリド、テトラブチルアンモニウム硫酸水素塩、テトラブチルアンモニウムヒドロキシドなどの４級アンモニウム塩；ベンジルトリフェニルホスホニウムクロライド、トリブチルアリルホスホニウムクロリド、トリブチル−２−メトキシプロピルホスホニウムクロリド、ベンジルフェニル（ジメチルアミノ）ホスホニウムクロリドなどの４級ホスホニウム塩；ベンジルメチルアミン、ベンジルエタノールアミンなどの一官能性アミン；１，８−ジアザビシクロ［５．４．０］−ウンデク−７−エンなどの環状アミンなどがあげられる。   As the vulcanization aid for the polyol vulcanization system, organic bases usually used for vulcanization of elastomers such as various quaternary ammonium salts, quaternary phosphonium salts, cyclic amines and monofunctional amine compounds can be used. Specific examples include quaternary ammonium salts such as tetrabutylammonium bromide, tetrabutylammonium chloride, benzyltributylammonium chloride, benzyltriethylammonium chloride, tetrabutylammonium hydrogensulfate and tetrabutylammonium hydroxide; benzyltriphenylphosphonium chloride , Quaternary phosphonium salts such as tributylallylphosphonium chloride, tributyl-2-methoxypropylphosphonium chloride, benzylphenyl (dimethylamino) phosphonium chloride; monofunctional amines such as benzylmethylamine and benzylethanolamine; 1,8-diazabicyclo [ And cyclic amines such as 5.4.0] -undec-7-ene.

パーオキサイド加硫系の加硫助剤としては、トリアリルシアヌレート、トリアリルイソシアヌレート（ＴＡＩＣ）、トリス（ジアリルアミン−ｓ−トリアジン）、トリアリルホスファイト、Ｎ，Ｎ−ジアリルアクリルアミド、ヘキサアリルホスホルアミド、Ｎ，Ｎ，Ｎ′，Ｎ′−テトラアリルテトラフタラミド、Ｎ，Ｎ，Ｎ′，Ｎ′−テトラアリルマロンアミド、トリビニルイソシアヌレート、２,４,６−トリビニルメチルトリシロキサン、トリ（５−ノルボルネン−２−メチレン）シアヌレートなどがあげられる。これらの中でも、加硫性、加硫物の物性の点から、トリアリルイソシアヌレート（ＴＡＩＣ）が好ましい。   Peroxide vulcanization aids include triallyl cyanurate, triallyl isocyanurate (TAIC), tris (diallylamine-s-triazine), triallyl phosphite, N, N-diallylacrylamide, hexaallylphospho. Luamide, N, N, N ′, N′-tetraallyltetraphthalamide, N, N, N ′, N′-tetraallylmalonamide, trivinyl isocyanurate, 2,4,6-trivinylmethyltrisiloxane , Tri (5-norbornene-2-methylene) cyanurate and the like. Among these, triallyl isocyanurate (TAIC) is preferable from the viewpoint of vulcanizability and physical properties of the vulcanizate.

加硫助剤の配合量は、エラストマー１００重量部に対して０．０１〜１０重量部であり、好ましくは０．１〜５．０重量部である。加硫助剤が、０．０１重量部より少ないと、加硫時間が実用に耐えないほど長くなる傾向があり、１０重量部をこえると、加硫時間が速くなり過ぎることに加え、成形品の圧縮永久歪も低下する傾向がある。   The compounding quantity of a vulcanization auxiliary is 0.01-10 weight part with respect to 100 weight part of elastomers, Preferably it is 0.1-5.0 weight part. If the vulcanization aid is less than 0.01 parts by weight, the vulcanization time tends to be unpractical, and if it exceeds 10 parts by weight, the vulcanization time becomes too fast, and the molded product There is also a tendency for the compression set to decrease.

さらに通常の添加剤である充填材、加工助剤、カーボンブラック、無機充填剤や、酸化マグネシウムのような金属酸化物、水酸化カルシウムのような金属水酸化物などを本発明の目的を損なわない限り使用してもよい。   Furthermore, usual additives such as fillers, processing aids, carbon black, inorganic fillers, metal oxides such as magnesium oxide, metal hydroxides such as calcium hydroxide, etc. do not impair the object of the present invention. As long as you use.

本発明の組成物の調製法および加硫法はとくに制限はなく、たとえば、圧縮成形、押出し成形、トランスファー成形、射出成形など、従来公知の方法が採用できる。   The preparation method and vulcanization method of the composition of the present invention are not particularly limited, and conventionally known methods such as compression molding, extrusion molding, transfer molding and injection molding can be employed.

加硫剤を用いて、含フッ素エラストマーを加硫した成形品の引張破断伸び（Ｅｂ）が２００〜５５０％であることが好ましい。引張破断伸びが２００％未満であると、いわゆる「ゴムらしさ」がなくなり、シール材として適さない傾向があり、５５０％をこえると、架橋密度が下がり過ぎ、圧縮永久歪み（ＣＳ）が悪化する傾向がある。   It is preferable that the tensile elongation at break (Eb) of the molded product obtained by vulcanizing the fluorine-containing elastomer using a vulcanizing agent is 200 to 550%. If the tensile elongation at break is less than 200%, the so-called “rubberiness” tends to be lost, and it tends to be unsuitable as a sealing material. If it exceeds 550%, the crosslinking density is too low, and compression set (CS) tends to deteriorate. There is.

また、成形品の２００℃、７２時間での圧縮永久歪み（ＣＳ）は、５〜３０％が好ましく、７〜２５％がより好ましい。圧縮永久歪みが、５％未満であると、シール性は良好であるが、一般に伸びが小さすぎる傾向があり、３０％をこえると、シール材としての性能が悪化する傾向がある。   Moreover, 5-30% is preferable and, as for the compression set (CS) in 200 degreeC and 72 hours of a molded article, 7-25% is more preferable. If the compression set is less than 5%, the sealing property is good, but generally the elongation tends to be too small, and if it exceeds 30%, the performance as a sealing material tends to deteriorate.

ここで、本発明における加硫とは、下記に示す標準配合、標準加硫条件により加硫することをいう。   Here, vulcanization in the present invention refers to vulcanization according to the following standard composition and standard vulcanization conditions.

（標準配合）
含フッ素エラストマー １００重量部
トリアリルイソシアヌレート（ＴＡＩＣ） ４重量部
パーヘキサ２５Ｂ １．５重量部
カーボンブラックＭＴ−Ｃ ２０重量部 (Standard formulation)
Fluorine-containing elastomer 100 parts by weight Triallyl isocyanurate (TAIC) 4 parts by weight Perhexa 25B 1.5 parts by weight Carbon black MT-C 20 parts by weight

（標準加硫条件）
混練方法 ：ロール練り
プレス加硫 ：１６０℃で１０分
オーブン加硫：１８０℃で４時間 (Standard vulcanization conditions)
Kneading method: Roll kneading press vulcanization: 10 minutes at 160 ° C Oven vulcanization: 4 hours at 180 ° C

本発明の製造方法では、従来の低圧でのヨウ素移動重合反応と比較して、重合時間が大幅に短縮され、さらに、得られた含フッ素エラストマーのロール加工性が向上した。このため、低圧ヨウ素移動重合により得られた含フッ素エラストマーと本発明品で、同等のムーニ粘度品を比較した場合に、低圧品では練り中に加硫剤（ＴＡＩＣ）が析出し、ゴムが切れやすくなる傾向があったが、本発明品では、そのような現象はみられなくなった。   In the production method of the present invention, compared with the conventional iodine transfer polymerization reaction at a low pressure, the polymerization time was significantly shortened, and the roll processability of the obtained fluorine-containing elastomer was improved. For this reason, when the same Mooney viscosity product is compared between the fluorine-containing elastomer obtained by low-pressure iodine transfer polymerization and the product of the present invention, the vulcanizing agent (TAIC) is precipitated during kneading in the low-pressure product and the rubber is cut. Although there was a tendency to become easier, such a phenomenon was not observed in the product of the present invention.

本発明により得られた含フッ素エラストマーと加硫剤からなる組成物は、コーティング剤、金属、セラミック等の無機材料を含む基材にディスペンサー成形してなる基材一体型ガスケット、パッキン類、金属、セラミック等の無機材料を含む基材にコーティングしてなる複層品、磁気記録装置用ガスケット、燃料電池用シール材、クリーン設備用シール材として好適に用いられる。   A composition comprising a fluorine-containing elastomer and a vulcanizing agent obtained by the present invention comprises a base material-integrated gasket formed by dispenser molding on a base material containing an inorganic material such as a coating agent, metal, ceramic, packing, metal, It is suitably used as a multilayer product formed by coating a substrate containing an inorganic material such as ceramic, a gasket for a magnetic recording device, a sealing material for a fuel cell, and a sealing material for a clean facility.

評価法
＜重量平均分子量（Ｍｗ）および数平均分子量（Ｍｎ）＞
装置：ＨＬＣ−８０００（東ソー（株）製）
昭和カラム：ＧＰＣ ＫＦ−８０６Ｍ ２本
ＧＰＣ ＫＦ−８０１ １本
ＧＰＣ ＫＦ−８０１ ２本
検出器：示差屈折率計
展開溶媒：テトラヒドロフラン
温度：３５℃
試料濃度：０．１重量％
標準試料：単分散ポリスチレン各種（（Ｍｗ／Ｍｎ）＝１．１４（Ｍａｘ））、ＴＳＫ ｓｔａｎｄａｒｄ ＰＯＬＹＳＴＹＲＥＮＥ（東ソー（株）製） Evaluation Method <Weight Average Molecular Weight (Mw) and Number Average Molecular Weight (Mn)>
Apparatus: HLC-8000 (manufactured by Tosoh Corporation)
Showa Column: 2 GPC KF-806M
1 GPC KF-801
GPC KF-801 2 detectors: differential refractometer developing solvent: tetrahydrofuran temperature: 35 ° C
Sample concentration: 0.1% by weight
Standard samples: Various monodisperse polystyrene ((Mw / Mn) = 1.14 (Max)), TSK standard POLYSTYRENE (manufactured by Tosoh Corporation)

＜ムーニー粘度＞
ＡＳＴＭ−Ｄ１６４６およびＪＩＳ Ｋ６３００に準拠して測定する。
測定機器：ＡＬＰＨＡ ＴＥＣＨＮＯＬＯＧＩＥＳ社製 ＭＶ２０００Ｅ型
ローター回転数：２ｒｐｍ
測定温度：１００℃ <Mooney viscosity>
Measured according to ASTM-D1646 and JIS K6300.
Measuring equipment: ALPHA TECHNOLOGIES MV2000E type rotor rotation speed: 2rpm
Measurement temperature: 100 ° C

＜圧縮永久歪み（ＣＳ）＞
下記標準配合物を下記標準加硫条件で１次プレス加硫および２次オーブン加硫して０−リング（Ｐ−２４）を作製し、ＪＩＳ−Ｋ６３０１に準じて、１次プレス加硫後の圧縮永久歪みおよび２次オーブン加硫後の圧縮永久歪み（ＣＳ）を測定する（２５％加圧圧縮下に２００℃で７２時間保持したのち２５℃の恒温室内に３０分間放置した試料を測定）。 <Compression set (CS)>
The following standard composition is subjected to primary press vulcanization and secondary oven vulcanization under the following standard vulcanization conditions to produce a 0-ring (P-24), and after the primary press vulcanization according to JIS-K6301. Measure compression set and compression set (CS) after secondary oven vulcanization (measurement of sample held in 25 ° C constant temperature chamber for 30 minutes after holding for 72 hours at 200 ° C under 25% pressure compression) .

（標準配合）
含フッ素エラストマー １００重量部
トリアリルイソシアヌレート（ＴＡＩＣ） ４重量部
パーヘキサ２５Ｂ １．５重量部
カーボンブラックＭＴ−Ｃ ２０重量部 (Standard formulation)
Fluorine-containing elastomer 100 parts by weight Triallyl isocyanurate (TAIC) 4 parts by weight Perhexa 25B 1.5 parts by weight Carbon black MT-C 20 parts by weight

（標準加硫条件）
混練方法 ：ロール練り
プレス加硫 ：１６０℃で１０分
オーブン加硫：１８０℃で４時間 (Standard vulcanization conditions)
Kneading method: Roll kneading press vulcanization: 10 minutes at 160 ° C Oven vulcanization: 4 hours at 180 ° C

＜１００％モジュラス（Ｍ１００）＞
標準配合物を標準加硫条件で１次プレス加硫および２次オーブン加硫して厚さ２ｍｍのシートとし、ＪＩＳ−Ｋ６２５１に準じて測定する。 <100% modulus (M100)>
The standard blend is subjected to primary press vulcanization and secondary oven vulcanization under standard vulcanization conditions to obtain a sheet having a thickness of 2 mm, and measurement is performed according to JIS-K6251.

＜引張破断強度（Ｔｂ）および引張破断伸び（Ｅｂ）＞
標準配合物を標準加硫条件で１次プレス加硫および２次オーブン加硫して厚さ２ｍｍのシートとし、ＪＩＳ−Ｋ６２５１に準じて測定する。 <Tensile breaking strength (Tb) and tensile breaking elongation (Eb)>
The standard blend is subjected to primary press vulcanization and secondary oven vulcanization under standard vulcanization conditions to obtain a sheet having a thickness of 2 mm, and measurement is performed according to JIS-K6251.

＜硬度（Ｈｓ）＞
標準配合物を標準加硫条件で１次プレス加硫および２次オーブン加硫して厚さ２ｍｍのシートとし、ＪＩＳ−Ｋ６２５３に準じて測定する。 <Hardness (Hs)>
The standard blend is subjected to primary press vulcanization and secondary oven vulcanization under standard vulcanization conditions to obtain a sheet having a thickness of 2 mm, and the measurement is performed according to JIS-K6253.

＜加硫特性＞
１次プレス加硫時にＪＳＲ型キュラストメータＩＩ型、およびＶ型を用いて１７０℃における加硫曲線を求め、最低粘度（ＭＬ）、加硫度（ＭＨ）、誘導時間（Ｔ10）および最適加硫時間（Ｔ90）を求める。 <Vulcanization characteristics>
At the time of primary press vulcanization, the vulcanization curve at 170 ° C. is obtained using JSR type curlastometer type II and V type, minimum viscosity (ML), vulcanization degree (MH), induction time (T 10 ) and optimum Determine the vulcanization time (T 90 ).

＜ポリマーの平均粒子径測定＞
マイクロトラック９３４０ＵＰＡ（ＨＯＮＥＹＷＥＬＬ社製）にて粒子径を測定した。 <Measurement of average particle size of polymer>
The particle size was measured with a Microtrac 9340UPA (manufactured by HONEYWELL).

＜粒子数計算＞
上記ポリマーの平均粒子径の測定結果を用いて、下記式より粒子数を算出する。 <Particle number calculation>
Using the measurement result of the average particle diameter of the polymer, the number of particles is calculated from the following formula.

Figure 2007231298
Figure 2007231298

＜ＶｄＦ分岐率測定＞
測定サンプルをアセトンに溶解し、その濃度を約２０％とした。これを19Ｆ−ＮＭＲ（Ｂｒｕｋｅｒ社製ＡＭＸ５００型）により測定し、処理ソフトにＭｅｓｔＲｅ−Ｃ２．３ａ（ＭｅｓｔＲｅ−Ｃ Ｔｅｃｈｎｏｌｏｇｉｅｓ社製）を用いて、分岐ピーク面積、および全ＣＦ2ピーク面積を算出し、得られた結果より分岐率を求める。 <VdF branching rate measurement>
The measurement sample was dissolved in acetone, and the concentration was about 20%. This was measured by 19 F-NMR (Bruker Co. AMX500 type), processing software to using MestRe-C2.3a (MestRe-C Technologies, Inc.), calculated branch peak area and the total CF 2 peak area The branching rate is obtained from the obtained result.

＜組成分析＞
19Ｆ−ＮＭＲ（Ｂｒｕｋｅｒ社製ＡＣ３００Ｐ型）を用いて測定した。ただし、含ＴＦＥポリマーは、19Ｆ−ＮＭＲ（日本電子（株）製ＦＸ１００型）を用いて測定をした。 <Composition analysis>
19 F-NMR (Bruker AC300P type) was used for measurement. However, the TFE-containing polymer was measured using 19 F-NMR (FX100 type manufactured by JEOL Ltd.).

＜元素分析＞
横河フューレットパッカード社Ｇ２３５０Ａ型を用いて測定した。 <Elemental analysis>
It measured using Yokogawa Hewlett Packard G2350A type.

＜Ｐｅｎｇ−Ｒｏｂｉｎｓｏｎ式計算＞
Ａｓｐｅｎ Ｐｌｕｓ Ｖｅｒ．１１．１（Ａｓｐｅｎ Ｔｅｃｈ社製）を使用した。各モノマーの臨界温度、臨界圧力、偏心因子は全てソフトに内蔵の値を使用した。
Ｔc ： ＶｄＦ ２９．６５℃、
ＴＦＥ ３３．３ ℃、
ＨＦＰ ８５．０ ℃
Ｐc ： ＶｄＦ ４．４６ ＭＰａ／ＳＱＣＭ、
ＴＦＥ ３．９４ ＭＰａ／ＳＱＣＭ、
ＨＦＰ ３．２１ ＭＰａ／ＳＱＣＭ
ω ： ＶｄＦ ０．１３６、
ＴＦＥ ０．２２６、
ＨＦＰ ０．３８２ <Peng-Robinson formula calculation>
Aspen Plus Ver. 11.1 (Aspen Tech) was used. The values built into the software were used for the critical temperature, critical pressure, and eccentricity factor of each monomer.
T c : VdF 29.65 ° C.
TFE 33.3 ° C,
HFP 85.0 ℃
P c : VdF 4.46 MPa / SQCM,
TFE 3.94 MPa / SQCM,
HFP 3.21 MPa / SQCM
ω: VdF 0.136,
TFE 0.226,
HFP 0.382

参考例１
（シードポリマー粒子の重合）
攪拌装置として、電磁誘導攪拌装置を有する内容積１．８リットルの重合槽に、純水７２０ｇ、１０重量％のパーフルオロオクタン酸アンモニウム水溶液２９０ｇ、およびマロン酸ジエチル０．６ｇを仕込み、系内を窒素ガスで充分置換したのち減圧にした。この操作を３回繰り返し、減圧状態でＶｄＦ２０ｇとＨＦＰ５１ｇを仕込み、攪拌下に８０℃まで昇温した。ついで、純水０．６ｇに溶解した過硫酸アンモニウム塩（ＡＰＳ）０．０２ｇを窒素ガスにて圧入して重合を開始した。重合圧力を２ＭＰａとし、重合時の圧力低下を補うため、ＶｄＦ／ＨＦＰ混合モノマー（７８／２２（モル％））の連続的に供給し、攪拌下に重合を行った。重合終了までに、２１５ｇのモノマーを槽内に供給した。 Reference example 1
(Polymerization of seed polymer particles)
As a stirrer, a polymerization tank having an internal volume of 1.8 liters having an electromagnetic induction stirrer was charged with 720 g of pure water, 290 g of a 10 wt% ammonium perfluorooctanoate aqueous solution, and 0.6 g of diethyl malonate. After fully replacing with nitrogen gas, the pressure was reduced. This operation was repeated three times, and 20 g of VdF and 51 g of HFP were charged under reduced pressure, and the temperature was raised to 80 ° C. with stirring. Subsequently, 0.02 g of ammonium persulfate (APS) dissolved in 0.6 g of pure water was injected with nitrogen gas to initiate polymerization. The polymerization pressure was set to 2 MPa, and in order to compensate for the pressure drop during the polymerization, a VdF / HFP mixed monomer (78/22 (mol%)) was continuously supplied, and polymerization was performed with stirring. By the end of the polymerization, 215 g of monomer was fed into the tank.

得られた乳濁液の重量は１２３３ｇ、ポリマー濃度が１８．１重量％であり、ポリマー粒子の数は、１．２×１０16個／水１ｇの乳化液を得た。３０分後に攪拌を止め、モノマーを放出して重合を停止した。 The weight of the obtained emulsion was 1233 g, the polymer concentration was 18.1 wt%, and the number of polymer particles was 1.2 × 10 16 particles / water 1 g. After 30 minutes, the stirring was stopped and the monomer was released to stop the polymerization.

参考例２
（シードポリマー粒子の重合）
攪拌装置として、電磁誘導攪拌装置を有する内容積１．８リットルの重合槽に、純水８０９ｇ、１０重量％のパーフルオロオクタン酸アンモニウム水溶液２００ｇを仕込み、系内を窒素ガスで充分置換したのち減圧にした。この操作を３回繰り返し、減圧状態でイソペンタン０．５ｍＬ仕込み、８０℃での相内組成がＶｄＦ／ＴＦＥ／ＨＦＰ＝２９．０／１３．０／５８．０モル％、槽内圧を１．４ＭＰａになるように各モノマーを仕込んだ。昇温終了後、純水２０ｇに溶解した過硫酸アンモニウム塩（ＡＰＳ）０．６７ｇを窒素ガスにて圧入して重合を開始した。重合圧力を１．４ＭＰａとし、重合時の圧力低下を補うため、ＶｄＦ／ＴＦＥ／ＨＦＰ混合モノマー（５０／２０／３０（モル％））を連続的に供給し、攪拌下に重合を行なった。重合終了までに、３２０ｇのモノマーを槽内に供給した。 Reference example 2
(Polymerization of seed polymer particles)
As a stirrer, a polymerization tank having an internal volume of 1.8 liters having an electromagnetic induction stirrer was charged with 809 g of pure water and 200 g of a 10 wt% ammonium perfluorooctanoate aqueous solution. I made it. This operation was repeated three times, 0.5 mL of isopentane was charged in a reduced pressure state, the composition in the phase at 80 ° C. was VdF / TFE / HFP = 29.0 / 13.0 / 58.0 mol%, and the internal pressure of the tank was 1.4 MPa. Each monomer was charged so that After completion of the temperature increase, 0.67 g of ammonium persulfate (APS) dissolved in 20 g of pure water was injected with nitrogen gas to initiate polymerization. The polymerization pressure was set to 1.4 MPa, and in order to compensate for the pressure drop during the polymerization, a VdF / TFE / HFP mixed monomer (50/20/30 (mol%)) was continuously supplied to carry out the polymerization with stirring. By the end of the polymerization, 320 g of monomer was fed into the tank.

得られた乳濁液の重量は１２８５ｇ、ポリマー濃度が２４．８重量％であり、ポリマー粒子の数は、１．０×１０15個／水１ｇの乳化液を得た。３６０分後に攪拌を止め、モノマーを放出して重合を停止した。 The weight of the obtained emulsion was 1285 g, the polymer concentration was 24.8% by weight, and an emulsion of 1.0 × 10 15 particles / water 1 g was obtained. After 360 minutes, the stirring was stopped and the monomer was released to stop the polymerization.

実施例１
参考例１同様の電磁誘導攪拌装置を有する内容積２．５リットルの重合槽に、純水１３２４ｇと参考例１で製造したポリマー粒子の水性分散液３３．５ｇと１０重量％のパーフルオロオクタン酸アンモニウム水溶液１９．１ｇを仕込み、系内を窒素ガスで充分置換したのち減圧にした。この操作を３回繰り返し、減圧状態で、ＶｄＦ１７１ｇとＨＦＰ７２９ｇを仕込み、攪拌下に８０℃まで昇温した。ついでオクタフルオロ−１，４−ジヨードブタン２．９８ｇと純水１５ｇに溶解したＡＰＳ０．０６８ｇを窒素ガスにて圧入して重合を開始し、（ａ）、（ｂ）および（ｃ）の条件で重合を継続し、４．３時間後に攪拌を止め、モノマーを放出して重合を停止した。 Example 1
In a polymerization tank having an internal volume of 2.5 liters having the same electromagnetic induction stirrer as in Reference Example 1, 1324 g of pure water, 33.5 g of an aqueous dispersion of polymer particles prepared in Reference Example 1, and 10% by weight of perfluorooctanoic acid An aqueous ammonium solution (19.1 g) was charged, the inside of the system was sufficiently replaced with nitrogen gas, and then the pressure was reduced. This operation was repeated three times. Under reduced pressure, 171 g of VdF and 729 g of HFP were charged, and the temperature was raised to 80 ° C. with stirring. Next, 0.068 g of APS dissolved in 2.98 g of octafluoro-1,4-diiodobutane and 15 g of pure water was injected with nitrogen gas to start polymerization, and polymerization was performed under the conditions of (a), (b) and (c). The stirring was stopped after 4.3 hours, and the monomer was released to stop the polymerization.

（ａ）重合槽内組成ＶｄＦ／ＨＦＰ＝３６／６４（モル％）に対するＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式による臨界温度・臨界圧力計算をＡｓｐｅｎ Ｐｌｕｓ Ｖｅｒ．１１．１を用いて行ったところ、Ｔc＝８７．７℃、Ｐc＝３．０５ＭＰａであった。さらに換算温度ＴR０．９５、換算圧力ＰR０．８０による変換を行なうと、Ｔ＝６９．７℃、Ｐ＝２．４４ＭＰａとなり、本実施例の重合条件は、換算温度以上かつ換算圧力以上である。
（ｂ）ＶｄＦ／ＨＦＰ（９５／５（モル％））モノマー混合物を連続的に供給し、気相部分の圧力を６ＭＰａに維持した。また、重合終了までに、３０２ｇのモノマーを槽内に供給した。
（ｃ）攪拌速度を５６０ｒｐｍで維持した。
（ｄ）重合時間が３時間を過ぎた時点で、純水１５ｇに溶解したＡＰＳ０．０３４ｇを仕込んだ。 (A) Calculation of critical temperature and critical pressure by the Peng-Robinson equation for the composition VdF / HFP = 36/64 (mol%) in the polymerization tank was performed using Aspen Plus Ver. As a result of using 11.1, T c = 87.7 ° C. and P c = 3.05 MPa. Further, when conversion is performed at a conversion temperature T R 0.95 and a conversion pressure P R 0.80, T = 69.7 ° C. and P = 2.44 MPa, and the polymerization conditions in this example are equal to or higher than the conversion temperature and the conversion pressure. That's it.
(B) VdF / HFP (95/5 (mol%)) monomer mixture was continuously supplied, and the pressure in the gas phase portion was maintained at 6 MPa. In addition, 302 g of monomer was supplied into the tank until the polymerization was completed.
(C) The stirring speed was maintained at 560 rpm.
(D) When the polymerization time exceeded 3 hours, 0.034 g of APS dissolved in 15 g of pure water was charged.

得られた乳濁液の重量は１８７９ｇ、ポリマー濃度が２９．６重量％であり、ポリマー粒子の数は、２．７×１０14個/水１ｇであった。また、含フッ素エラストマーとしては５６６ｇであり、ＧＰＣで測定した重量平均分子量Ｍｗは２３．６万、数平均分子量Ｍｎは１１．３万、Ｍｗ／Ｍｎは２．１であった。また、19Ｆ−ＮＭＲで測定した重合体の組成はＶｄＦ／ＨＦＰ＝７７／２３（モル％）であった。 The weight of the obtained emulsion was 1879 g, the polymer concentration was 29.6 wt%, and the number of polymer particles was 2.7 × 10 14 particles / water 1 g. Moreover, it was 566g as a fluorine-containing elastomer, the weight average molecular weight Mw measured by GPC was 236,000, the number average molecular weight Mn was 113,000, and Mw / Mn was 2.1. Further, the composition of the polymer measured by 19 F-NMR was VdF / HFP = 77/23 (mol%).

実施例２
ＡＰＳを０．１７ｇとしたこと以外は、実施例１と同様に含フッ素エラストマーを重合した。 Example 2
The fluorine-containing elastomer was polymerized in the same manner as in Example 1 except that APS was changed to 0.17 g.

重合時間は１．５時間、得られた乳濁液の重量は１９０９ｇ、ポリマー濃度が３０．１重量％であり、ポリマー粒子の数は、２．９×１０14個／水１ｇであった。また、含フッ素エラストマー５７５ｇであり、ＧＰＣで測定した重量平均分子量Ｍｗは２７．７万、数平均分子量Ｍｎは１０．３万、Ｍｗ／Ｍｎは２．７であった。また、19Ｆ−ＮＭＲで測定した重合体の組成はＶｄＦ／ＨＦＰ＝７６／２４（モル％）であった。 The polymerization time was 1.5 hours, the weight of the obtained emulsion was 1909 g, the polymer concentration was 30.1 wt%, and the number of polymer particles was 2.9 × 10 14 particles / water 1 g. The weight average molecular weight Mw measured by GPC was 277,000, the number average molecular weight Mn was 103,000, and Mw / Mn was 2.7. Further, the composition of the polymer measured by 19 F-NMR was VdF / HFP = 76/24 (mol%).

実施例３
オクタフルオロ−１，４−ジヨードブタンを５．９６ｇとしたこと以外は、実施例１と同様にして含フッ素エラストマーを重合した。 Example 3
The fluorine-containing elastomer was polymerized in the same manner as in Example 1 except that 5.96 g of octafluoro-1,4-diiodobutane was used.

重合時間は３．４時間、得られた乳濁液の重量は１８９９ｇ、ポリマー濃度が２８．６重量％であり、ポリマー粒子の数は、２．６×１０14個／水１ｇであった。また、含フッ素エラストマーは５４３ｇであり、ＧＰＣで測定した重量平均分子量Ｍｗは１０．５万、数平均分子量Ｍｎは５．６３万、Ｍｗ／Ｍｎは１．９であった。また、19Ｆ−ＮＭＲで測定した重合体の組成はＶｄＦ／ＨＦＰ＝７７／２３（モル％）であった。 The polymerization time was 3.4 hours, the weight of the obtained emulsion was 1899 g, the polymer concentration was 28.6% by weight, and the number of polymer particles was 2.6 × 10 14 particles / g water. Moreover, the fluorine-containing elastomer was 543g, the weight average molecular weight Mw measured by GPC was 105,000, the number average molecular weight Mn was 563,000, and Mw / Mn was 1.9. Further, the composition of the polymer measured by 19 F-NMR was VdF / HFP = 77/23 (mol%).

比較例１
参考例１同様の電磁誘導攪拌装置を有する内容積２．５リットルの重合槽に、純水１３２４ｇと参考例１で製造したポリマー粒子の水性分散液３３．５ｇと１０重量％のパーフルオロオクタン酸アンモニウム水溶液１９．１ｇを仕込み、系内を窒素ガスで充分置換したのち減圧にした。この操作を３回繰り返し、減圧状態で、ＶｄＦ２０ｇとＨＦＰ５７ｇを仕込み、攪拌下に８０℃まで昇温した。ついでオクタフルオロ−１，４−ジヨード-ブタン２．９８ｇと純水１５ｇに溶解したＡＰＳ０．０６８ｇを窒素ガスにて圧入して重合を開始し、（ａ）、（ｂ）、（ｃ）および（ｄ）の条件で重合を継続し、１６．５時間後に攪拌を止め、モノマーを放出して重合を停止した。 Comparative Example 1
In a polymerization tank having an internal volume of 2.5 liters having the same electromagnetic induction stirrer as in Reference Example 1, 1324 g of pure water, 33.5 g of an aqueous dispersion of polymer particles prepared in Reference Example 1, and 10% by weight of perfluorooctanoic acid An aqueous ammonium solution (19.1 g) was charged, the inside of the system was sufficiently replaced with nitrogen gas, and then the pressure was reduced. This operation was repeated three times. Under reduced pressure, 20 g of VdF and 57 g of HFP were charged, and the temperature was raised to 80 ° C. with stirring. Next, 0.068 g of APS dissolved in 2.98 g of octafluoro-1,4-diiodo-butane and 15 g of pure water was injected with nitrogen gas to initiate polymerization, and (a), (b), (c) and ( Polymerization was continued under the conditions of d). After 16.5 hours, the stirring was stopped, the monomer was released, and the polymerization was stopped.

（ａ）重合槽内組成ＶｄＦ／ＨＦＰ＝５０／５０（モル％）に対するＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式による臨界温度・臨界圧力計算をＡｓｐｅｎ Ｐｌｕｓ Ｖｅｒ．１１．１を用いて行ったところ、Ｔc＝５７．３℃、Ｐc＝３．８３ＭＰａであった。さらに換算温度ＴR０．９５、換算圧力ＰR０．８０による変換を行なうと、Ｔ＝４０．８℃、Ｐ＝３．０６ＭＰａとなり、本比較例の重合条件は、換算温度以上かつ換算圧力以下である。
（ｂ）ＶｄＦ／ＨＦＰ（７８／２２（モル％））モノマー混合物を連続的に供給し、気相部分の圧力を１．５ＭＰａに維持した。また、重合終了までに、５７０ｇのモノマーを槽内に供給した。
（ｃ）攪拌速度を５６０ｒｐｍで維持した。
（ｄ）重合時間が３時間を過ぎる毎に、純水１５ｇに溶解したＡＰＳ０．０３４ｇを仕込んだ。 (A) Calculation of critical temperature and critical pressure by the Peng-Robinson equation for the composition VdF / HFP = 50/50 (mol%) in the polymerization tank was performed using Aspen Plus Ver. As a result of using 11.1, T c = 57.3 ° C. and P c = 3.83 MPa. Further reduced temperature T R 0.95, when performing conversion by reduced pressure P R 0.80, T = 40.8 ℃ , P = 3.06MPa , and the polymerization conditions of this comparative example, in terms of temperature or higher and the reduced pressure It is as follows.
(B) VdF / HFP (78/22 (mol%)) monomer mixture was continuously supplied, and the pressure in the gas phase portion was maintained at 1.5 MPa. In addition, 570 g of monomer was supplied into the tank until the end of the polymerization.
(C) The stirring speed was maintained at 560 rpm.
(D) Every time the polymerization time passed 3 hours, 0.034 g of APS dissolved in 15 g of pure water was charged.

得られた乳濁液の重量は２０８７ｇ、ポリマー濃度が２７．７重量％であり、ポリマー粒子の数は、１．４×１０14個／水１ｇであった。また、含フッ素エラストマーは５７８ｇであり、ＧＰＣで測定した重量平均分子量Ｍｗは１８．３万、数平均分子量Ｍｎは１３．３万、Ｍｗ／Ｍｎは１．４であった。また、19Ｆ−ＮＭＲで測定した重合体の組成はＶｄＦ／ＨＦＰ＝７７．３／２２．７（モル％）であった。 The weight of the obtained emulsion was 2087 g, the polymer concentration was 27.7 wt%, and the number of polymer particles was 1.4 × 10 14 particles / water 1 g. Moreover, the fluorine-containing elastomer was 578 g, the weight average molecular weight Mw measured by GPC was 183,000, the number average molecular weight Mn was 133,000, and Mw / Mn was 1.4. Further, the composition of the polymer measured by 19 F-NMR was VdF / HFP = 77.3 / 22.7 (mol%).

実施例４〜６および比較例２
実施例１〜３および比較例１で得られた含フッ素エラストマーを用い、下記の配合、加硫条件にしたがって、含フッ素成形品を得た。評価結果を表１に示す。 Examples 4 to 6 and Comparative Example 2
Using the fluorine-containing elastomers obtained in Examples 1 to 3 and Comparative Example 1, fluorine-containing molded products were obtained according to the following blending and vulcanization conditions. The evaluation results are shown in Table 1.

（標準配合）
含フッ素エラストマー １００重量部
トリアリルイソシアヌレート（ＴＡＩＣ） ４重量部
パーヘキサ２５Ｂ １．５重量部
カーボンブラックＭＴ−Ｃ ２０重量部 (Standard formulation)
Fluorine-containing elastomer 100 parts by weight Triallyl isocyanurate (TAIC) 4 parts by weight Perhexa 25B 1.5 parts by weight Carbon black MT-C 20 parts by weight

（標準加硫条件）
混練方法 ：ロール練り
プレス加硫 ：１６０℃で１０分
オーブン加硫：１８０℃で４時間 (Standard vulcanization conditions)
Kneading method: Roll kneading press vulcanization: 10 minutes at 160 ° C Oven vulcanization: 4 hours at 180 ° C

Figure 2007231298
Figure 2007231298

実施例７
参考例１同様の電磁誘導攪拌装置を有する内容積１．８リットルの重合槽に、純水９７０ｇと参考例２で製造したポリマー粒子の水性分散液２７ｇを仕込み、系内を充分に窒素置換したのち減圧にした。この操作を３回繰返し、減圧状態でＶｄＦ１８ｇ、ＴＦＥ２２ｇ、ＨＦＰ５３７ｇを仕込み、攪拌下に８０℃まで昇温した。ついで、オクタフルオロ−１，４−ジヨードブタン２．８ｇと純水１５ｇに溶解したＡＰＳ０．０５ｇを窒素ガスにて圧入して重合を開始し、（ａ）、（ｂ）、（ｃ）の条件で重合を継続し、３．６時間後に攪拌を止め、モノマーを放出して重合を停止した。 Example 7
In a polymerization tank having an internal volume of 1.8 liters having the same electromagnetic induction stirrer as in Reference Example 1, 970 g of pure water and 27 g of an aqueous dispersion of polymer particles produced in Reference Example 2 were charged, and the system was sufficiently purged with nitrogen. After that, the pressure was reduced. This operation was repeated three times. Under reduced pressure, 18 g of VdF, 22 g of TFE, and 537 g of HFP were charged, and the temperature was raised to 80 ° C. with stirring. Subsequently, 0.05 g of APS dissolved in 2.8 g of octafluoro-1,4-diiodobutane and 15 g of pure water was injected with nitrogen gas to start polymerization, and the conditions (a), (b) and (c) were satisfied. The polymerization was continued, and stirring was stopped after 3.6 hours, and the monomer was released to terminate the polymerization.

（ａ）重合槽内組成ＶｄＦ／ＴＦＥ／ＨＦＰ＝６．５／５．０／８８．５（モル％）に対するＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式による臨界温度・臨界圧力計算をＡｓｐｅｎ Ｐｌｕｓ Ｖｅｒ．１１．１を用いて行ったところ、Ｔc＝８７．７℃、Ｐc＝３．０５ＭＰａであった。さらに換算温度ＴR０．９５、換算圧力ＰR０．８０による変換を行なうと、Ｔ＝６９．７℃、Ｐ＝２．４４ＭＰａとなり、本実施例の重合条件は、換算温度以上かつ換算圧力以上である。
（ｂ）ＶｄＦ／ＴＦＥ／ＨＦＰ（６８．０／２３．８／８．２（モル％））モノマー混合物を連続的に供給し、気相部分の圧力を３．５ＭＰａに維持した。また、重合終了までに、２４７ｇのモノマーを槽内に供給した。
（ｃ）攪拌速度を５６０ｒｐｍで維持した。 (A) Calculation of critical temperature and critical pressure according to the Peng-Robinson equation for the composition VdF / TFE / HFP = 6.5 / 5.0 / 88.5 (mol%) in the polymerization vessel was carried out by Aspen Plus Ver. As a result of using 11.1, T c = 87.7 ° C. and P c = 3.05 MPa. Further, when conversion is performed at a conversion temperature T R 0.95 and a conversion pressure P R 0.80, T = 69.7 ° C. and P = 2.44 MPa, and the polymerization conditions in this example are equal to or higher than the conversion temperature and the conversion pressure. That's it.
(B) VdF / TFE / HFP (68.0 / 23.8 / 8.2 (mol%)) monomer mixture was continuously fed, and the pressure in the gas phase portion was maintained at 3.5 MPa. In addition, 247 g of monomer was supplied into the tank until the polymerization was completed.
(C) The stirring speed was maintained at 560 rpm.

得られた乳濁液の重量は１３６８ｇ、ポリマー濃度が２６．８重量％であり、ポリマー粒子の数は、９．５×１０14個／水１ｇであった。また、含フッ素エラストマーとしては３６９ｇであり、ＧＰＣで測定した重量平均分子量Ｍｗは６．７万、数平均分子量Ｍｎは４．８万、Ｍｗ／Ｍｎは１．４であった。また、19Ｆ−ＮＭＲで測定した重合体の組成はＶｄＦ／ＴＦＥ／ＨＦＰ＝５０．７／１９．５／２９．８（モル％）であった。 The weight of the obtained emulsion was 1368 g, the polymer concentration was 26.8 wt%, and the number of polymer particles was 9.5 × 10 14 particles / water 1 g. The fluorine-containing elastomer was 369 g, the weight average molecular weight Mw measured by GPC was 67,000, the number average molecular weight Mn was 48,000, and Mw / Mn was 1.4. The composition of the polymer measured by 19 F-NMR was VdF / TFE / HFP = 50.7 / 19.5 / 29.8 (mol%).

実施例８
オクタフルオロ−１，４−ジヨードブタンを２．４ｇとしたこと以外は、実施例７と同様にして含フッ素エラストマーを重合した。 Example 8
The fluorine-containing elastomer was polymerized in the same manner as in Example 7 except that 2.4 g of octafluoro-1,4-diiodobutane was used.

重合時間は４．２時間、得られた乳濁液の重量は１４０１g、ポリマー濃度が２８．６重量％であり、ポリマー粒子の数は、３．５×１０14個/水１ｇであった。また、含フッ素エラストマーは３９６gであり、ＧＰＣで測定した重量平均分子量Ｍｗは８．７万、数平均分子量Ｍｎは５．７万、Ｍｗ／Ｍｎは１．５であった。また、19Ｆ−ＮＭＲで測定した重合体の組成はＶｄＦ／ＴＦＥ／ＨＦＰ＝５１．０／１９．８／２９．２（モル％）であった。 The polymerization time was 4.2 hours, the weight of the obtained emulsion was 1401 g, the polymer concentration was 28.6% by weight, and the number of polymer particles was 3.5 × 10 14 particles / water 1 g. The fluorine-containing elastomer was 396 g, the weight average molecular weight Mw measured by GPC was 87,000, the number average molecular weight Mn was 57,000, and Mw / Mn was 1.5. Further, the composition of the polymer measured by 19 F-NMR was VdF / TFE / HFP = 51.0 / 19.8 / 29.2 (mol%).

実施例９
（ａ）オクタフルオロ−１，４−ジヨードブタンを２．４ｇ、
（ｂ）仕込みモノマー量の５０％時にＣＦ2＝ＣＦＯＣＦ2ＣＦ2ＣＨ2Ｉを３．９６ｇ、
（ｃ）重合時間が３時間を過ぎる毎に、純水１５ｇに溶解したＡＰＳ０．０２５ｇを仕込む、
としたこと以外は、実施例７と同様にして含フッ素エラストマーを重合した。 Example 9
(A) 2.4 g of octafluoro-1,4-diiodobutane,
(B) 3.96 g of CF 2 = CFOCF 2 CF 2 CH 2 I at 50% of the charged monomer amount,
(C) Every time the polymerization time exceeds 3 hours, 0.025 g of APS dissolved in 15 g of pure water is charged.
Except for the above, the fluorine-containing elastomer was polymerized in the same manner as in Example 7.

重合時間は３．８時間、得られた乳濁液の重量は１３９１g、ポリマー濃度が２７．３重量％であり、ポリマー粒子の数は、８．３×１０14個/水１ｇであった。また、含フッ素エラストマーは３８４ｇであり、ＧＰＣで測定した重量平均分子量Ｍｗは９．２万、数平均分子量Ｍｎは５．９万、Ｍｗ／Ｍｎは１．６であった。また、19Ｆ−ＮＭＲで測定した重合体の組成はＶｄＦ／ＴＦＥ／ＨＦＰ＝５２．０／２０．７／２７．３（モル％）であった。 The polymerization time was 3.8 hours, the weight of the obtained emulsion was 1391 g, the polymer concentration was 27.3% by weight, and the number of polymer particles was 8.3 × 10 14 particles / g water. Moreover, the fluorine-containing elastomer was 384 g, the weight average molecular weight Mw measured by GPC was 92,000, the number average molecular weight Mn was 59,000, and Mw / Mn was 1.6. Further, the composition of the polymer measured by 19 F-NMR was VdF / TFE / HFP = 52.0 / 20.7 / 27.3 (mol%).

比較例３
参考例７同様の電磁誘導攪拌装置を有する内容積１．８３リットルの重合槽に、純水９７０ｇと参考例２で製造したポリマー粒子の水性分散液２７ｇを仕込み、系内を充分窒素置換したのち減圧にした。この操作を３回繰り返し、８０℃での槽内組成がＶｄＦ／ＴＦＥ／ＨＦＰ＝１１．０／１９．０／７０．０（モル％）、槽内圧を１．５ＭＰａになるように各モノマーを仕込んだ。ついでオクタフルオロ−１，４−ジヨードブタン１．７ｇと純水１５ｇに溶解したＡＰＳ０．０５ｇを窒素ガスにて圧入して重合を開始し、（ａ）〜（ｄ）の条件で重合を継続し、１５．３時間後に攪拌を止め、モノマーを放出して重合を停止した。 Comparative Example 3
In a polymerization tank having an internal volume of 1.83 liters having the same electromagnetic induction stirrer as in Reference Example 7, 970 g of pure water and 27 g of an aqueous dispersion of polymer particles produced in Reference Example 2 were charged, and the system was sufficiently purged with nitrogen. Reduced pressure. This operation was repeated three times, and each monomer was adjusted so that the composition in the tank at 80 ° C. was VdF / TFE / HFP = 11.0 / 19.0 / 70.0 (mol%) and the tank internal pressure was 1.5 MPa. Prepared. Then, 0.05 g of APS dissolved in 1.7 g of octafluoro-1,4-diiodobutane and 15 g of pure water was injected with nitrogen gas to start the polymerization, and the polymerization was continued under the conditions (a) to (d). After 15.3 hours, the stirring was stopped, the monomer was released, and the polymerization was stopped.

（ａ）重合槽内組成ＶｄＦ／ＴＦＥ／ＨＦＰ＝１１／１９／７０（モル％）に対するＰｅｎｇ−Ｒｏｂｉｎｓｏｎ式による臨界温度・臨界圧力計算をＡｓｐｅｎ Ｐｌｕｓ Ｖｅｒ．１１．１を用いて行ったところ、Ｔc＝６９．０℃、Ｐc＝３．４８ＭＰａであった。さらに換算温度ＴR０．９５、換算圧力ＰR０．８０による変換を行なうと、Ｔ＝５１．９℃、Ｐ＝２．７８ＭＰａとなり、本実施例の重合条件は、換算温度以上かつ換算圧力以下である。
（ｂ）ＶｄＦ／ＴＦＥ／ＨＦＰ（５０．０／２０．０／３０．０（モル％））モノマー混合物を連続的に供給し、気相部分の圧力を１．５ＭＰａに維持した。また、重合終了までに、３７０ｇのモノマーを槽内に供給した。
（ｃ）攪拌速度を５６０ｒｐｍで維持した。
（ｄ）重合時間が３時間を過ぎる毎に、純水１５ｇに溶解したＡＰＳ０．０２５ｇを仕込んだ。 (A) Calculation of critical temperature and critical pressure according to the Peng-Robinson equation for the composition VdF / TFE / HFP = 11/19/70 (mol%) in the polymerization tank was performed by Aspen Plus Ver. As a result of using 11.1, T c = 69.0 ° C. and P c = 3.48 MPa. Further, when conversion is performed at a conversion temperature T R 0.95 and a conversion pressure P R 0.80, T = 51.9 ° C. and P = 2.78 MPa, and the polymerization conditions in this example are equal to or higher than the conversion temperature and the conversion pressure. It is as follows.
(B) VdF / TFE / HFP (50.0 / 20.0 / 30.0 (mol%)) monomer mixture was continuously supplied, and the pressure in the gas phase portion was maintained at 1.5 MPa. In addition, 370 g of monomer was supplied into the tank until the end of the polymerization.
(C) The stirring speed was maintained at 560 rpm.
(D) Every time the polymerization time exceeded 3 hours, 0.025 g of APS dissolved in 15 g of pure water was charged.

得られた乳濁液の重量は１４１０ｇ、ポリマー濃度が２６．２重量％であり、ポリマー粒子の数は、３．９×１０14個／水１ｇであった。また、含フッ素エラストマーは３７０ｇであり、ＧＰＣで測定した重量平均分子量Ｍｗは８．５万、数平均分子量Ｍｎは６．１万、Ｍｗ／Ｍｎは１．４であった。また、19Ｆ−ＮＭＲで測定した重合体の組成はＶｄＦ／ＴＦＥ／ＨＦＰ＝５０．２／１９．８／３０．０（モル％）であった。 The weight of the obtained emulsion was 1410 g, the polymer concentration was 26.2 wt%, and the number of polymer particles was 3.9 × 10 14 particles / g water. Moreover, the fluorine-containing elastomer was 370 g, the weight average molecular weight Mw measured by GPC was 85,000, the number average molecular weight Mn was 61,000, and Mw / Mn was 1.4. Further, the composition of the polymer measured by 19 F-NMR was VdF / TFE / HFP = 50.2 / 19.8 / 30.0 (mol%).

実施例１０〜１２および比較例４
実施例７〜９および比較例３で得られた含フッ素エラストマーを用い、下記の配合、加硫条件にしたがって、含フッ素成形品を得た。評価結果を表２に示す。 Examples 10-12 and Comparative Example 4
Using the fluorine-containing elastomers obtained in Examples 7 to 9 and Comparative Example 3, fluorine-containing molded articles were obtained according to the following blending and vulcanization conditions. The evaluation results are shown in Table 2.

（標準配合）
含フッ素エラストマー １００重量部
トリアリルイソシアヌレート（ＴＡＩＣ） ４重量部
パーヘキサ２５Ｂ １．５重量部
カーボンブラックＭＴ−Ｃ ２０重量部 (Standard formulation)
Fluorine-containing elastomer 100 parts by weight Triallyl isocyanurate (TAIC) 4 parts by weight Perhexa 25B 1.5 parts by weight Carbon black MT-C 20 parts by weight

（標準加硫条件）
混練方法 ：ロール練り
プレス加硫 ：１６０℃で１０分
オーブン加硫：１８０℃で４時間 (Standard vulcanization conditions)
Kneading method: Roll kneading press vulcanization: 10 minutes at 160 ° C Oven vulcanization: 4 hours at 180 ° C

Figure 2007231298
Figure 2007231298

Claims (3)

含フッ素エラストマーが、ビニリデンフルオライド繰り返し単位２０〜９０モル％、ヘキサフルオロプロピレン繰り返し単位１０〜８０モル％を含み、
（ａ）エラストマー中に０．０１〜１０重量％のヨウ素原子を含有し、
（ｂ）ポリマー数平均分子量が１,０００〜３００,０００であり、
（ｃ）ポリマー濃度約２０％のアセトン溶液を高分解能19Ｆ−ＮＭＲで測定し、下記式
Figure 2007231298
 により求められる「ＶｄＦ分岐率」が２００ｐｐｍ以下であり、
パーオキサイド加硫が可能である含フッ素エラストマー。 The fluorine-containing elastomer contains 20 to 90 mol% of vinylidene fluoride repeating units, 10 to 80 mol% of hexafluoropropylene repeating units,
(A) containing 0.01 to 10% by weight of iodine atoms in the elastomer;
(B) The polymer number average molecular weight is 1,000 to 300,000,
(C) An acetone solution having a polymer concentration of about 20% was measured by high resolution 19 F-NMR, and the following formula
Figure 2007231298
 "VdF branching rate" calculated by the following is 200 ppm or less,
Fluorine-containing elastomer that can be peroxide vulcanized. 加硫して得られる成形体の引張破断伸びＥｂが２００％以上、５５０％以下であり、かつ２００℃、７２時間での圧縮永久歪みＣＳが５％以上、３０％以下である請求項１記載の含フッ素エラストマー。 The tensile breaking elongation Eb of the molded product obtained by vulcanization is 200% or more and 550% or less, and the compression set CS at 200 ° C for 72 hours is 5% or more and 30% or less. Fluorine-containing elastomer. 請求項１または２記載の含フッ素エラストマーおよび加硫剤からなる含フッ素エラストマー硬化用組成物。 A composition for curing a fluorine-containing elastomer, comprising the fluorine-containing elastomer according to claim 1 or 2 and a vulcanizing agent.
JP2007164016A 2003-01-24 2007-06-21 Method for producing vulcanizable fluorine-containing elastomer Pending JP2007231298A (en)