JP2007220644A - 鉛蓄電池用極板の製造方法 - Google Patents
鉛蓄電池用極板の製造方法 Download PDFInfo
- Publication number
- JP2007220644A JP2007220644A JP2006163858A JP2006163858A JP2007220644A JP 2007220644 A JP2007220644 A JP 2007220644A JP 2006163858 A JP2006163858 A JP 2006163858A JP 2006163858 A JP2006163858 A JP 2006163858A JP 2007220644 A JP2007220644 A JP 2007220644A
- Authority
- JP
- Japan
- Prior art keywords
- paste
- active material
- electrode plate
- aging
- lead
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】鉛を主成分とする鉛合金の基板にペースト状活物質を充填し、その両面にペースト紙を貼り付けて作製される鉛蓄電池用極板の製造方法において、熟成初期段階またはペースト練り工程時に、ペースト状活物質中に四塩基性硫酸鉛(4BS)を生成させ、熟成終了後に4BS生成量を50wt%以上とする。
【選択図】図1
Description
熟成初期段階で炉内温度が80℃、相対湿度が95%に到達するまでの時間を1.5時間とした以外は本発明1と同様にして含水率測定用極板3と極板3を作製した(比較例1)。
熟成初期段階で炉内温度が80℃、相対湿度が95%に到達するまでの時間を3時間とし、ボイラーおよびヒータの所望の容量(実施例1記載のボイラーおよびヒータの1/3の容量)とした以外は本発明1と同様にして含水率測定用極板4と極板4を作製した(従来例1)。
酸錬り時の冷却停止時間とペースト平均温度を本発明規定値外とした以外は、実施例と同じ方法により極板を作製した(比較例活物質2〜3)。
Claims (4)
- 鉛を主成分とする鉛合金の基板にペースト状活物質を充填し、その両面にペースト紙を貼り付けて作製される鉛蓄電池用極板の製造方法において、熟成初期段階で活物質に四塩基性硫酸鉛を生成させ、熟成終了後に4塩基性硫酸鉛生成量を50質量%以上とすることを特徴とする鉛蓄電池用極板の製造方法。
- 極板を熟成する炉内の雰囲気温度と相対湿度を1時間以内で所定の熟成条件にすることを特徴とする請求項1に記載の鉛蓄電池用極板の製造方法。
- 熟成開始1時間後の極板の含水率が6%以上とすることを特徴とする請求項1又は2に記載の鉛蓄電池用極板の製造方法。
- 鉛を主成分とする鉛合金の基板にペースト状活物質を充填し、その両面にペースト紙を貼り付けて作製される鉛蓄電池用極板の製造方法において、該ペースト状活物質のペースト練り工程終了時のペースト状活物質中に5〜20質量%の4塩基性硫酸鉛を生成させ、熟成終了後に4塩基性硫酸鉛の生成量を50質量%以上とすることを特徴とする鉛蓄電池用極板の製造方法。