JP2007177166A - Water-soluble temper rolling liquid composition - Google Patents
Water-soluble temper rolling liquid composition Download PDFInfo
- Publication number
- JP2007177166A JP2007177166A JP2005379848A JP2005379848A JP2007177166A JP 2007177166 A JP2007177166 A JP 2007177166A JP 2005379848 A JP2005379848 A JP 2005379848A JP 2005379848 A JP2005379848 A JP 2005379848A JP 2007177166 A JP2007177166 A JP 2007177166A
- Authority
- JP
- Japan
- Prior art keywords
- water
- acid
- soluble
- carboxylic acid
- liquid composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は調質圧延液組成物に関し、より詳しくは耐ガムアップ性、防錆性などに優れた水溶性調質圧延液組成物に関する。 The present invention relates to a tempered rolling fluid composition, and more particularly to a water-soluble tempered rolling fluid composition excellent in gum-up resistance, rust resistance, and the like.
調質圧延は冷間圧延後、微少の圧下率で圧延するもので、冷延鋼板の形状を制御し、機械特性を付与し(降伏点伸びの消去)、光沢を調整することなどを目的に行われている。この調質圧延された冷延鋼板は、それぞれの用途に応じて加工使用されるまでにかなりの期間があるために、通常防錆油で処理される。しかしながら、調質圧延工程で用いられた水溶性調質圧延剤中の成分と防錆油中の成分とが化学反応を起こし、いわゆる「ガムアップ」と呼ばれる粘着物が生成する。その粘着物は鉄粉やカーボン等の異物を抱き込んで搬送ロールに堆積し、それが鋼板に転写されて表面品位を著しく損なわせ、また、その後のプレス加工等において、「滑り」を生じさせるなどの問題を引き起こすことがある。そのため、ガムアップの発生を防止できる、耐ガムアップ性調質圧延剤であることが要求される。 Temper rolling is performed at a small reduction after cold rolling, for the purpose of controlling the shape of the cold-rolled steel sheet, imparting mechanical properties (erasing the yield point elongation), adjusting gloss, etc. Has been done. The temper-rolled cold-rolled steel sheet is usually treated with a rust-preventing oil because there is a considerable period until it is processed and used in accordance with each application. However, the component in the water-soluble temper rolling agent used in the temper rolling step and the component in the rust preventive oil cause a chemical reaction, thereby producing a so-called “gum-up” adhesive. The sticking material embeds foreign matter such as iron powder and carbon and accumulates on the transport roll, which is transferred to the steel plate and remarkably impairs the surface quality, and also causes "slip" in subsequent press processing. May cause problems. Therefore, it is required to be a gum-up-resistant temper rolling agent that can prevent the occurrence of gum-up.
また、調質圧延後、冷延鋼板は調質圧延液のみが付着した状態で、長期にわたり保管されることがあるため、それ自身が防錆性に優れることが必要である。さらに調質圧延液には、脱脂性が良好であること、良好な圧延性(具体的には、例えば、濡れ性が良好で、適正な摩擦係数を有する)を有することなども要求される。
さらに、水溶性調質圧延液には、通常その調質圧延液を水で10〜50倍程度に希釈して使用するが、その希釈水の水質が問題となることもある。すなわち希釈水として工業用水など、硬度が高い水を用いて水溶性調質圧延剤を調合すると、調質圧延剤中の配合物の溶解又は分散状態が変化し、カルシウムやナトリウムが脂肪酸と石けんを生成し、スカムが発生することがある。このようなスカムの発生は、外観が好ましくはないばかりでなく、調質圧延剤としての安定した性能を維持する上でも問題となる恐れがある。
Further, after temper rolling, the cold-rolled steel sheet may be stored for a long time in a state where only the temper rolling solution is adhered, so that itself must be excellent in rust prevention. Furthermore, the tempered rolling liquid is required to have good degreasing properties and good rolling properties (specifically, for example, good wettability and an appropriate friction coefficient).
Furthermore, the water-soluble tempered rolling fluid is usually used after diluting the tempered rolling fluid with water about 10 to 50 times. However, the quality of the diluted water may be a problem. In other words, when water-soluble temper rolling agent is prepared using water with high hardness such as industrial water as dilution water, the dissolved or dispersed state of the compound in the temper rolling agent changes, and calcium and sodium replace fatty acid and soap. And scum may occur. The occurrence of such scum not only has an unfavorable appearance, but also may cause a problem in maintaining stable performance as a temper rolling agent.
従来この種の水溶性調質圧延剤としては、通常、二塩基酸や芳香族カルボン酸のアルカノールアミンの塩を主体とするものが用いられており、具体的には例えば、(a)二塩基酸等と第1級アルカノールアミン及び無機アルカリとの塩を主体とする水溶性調質圧延油剤(特許文献1参照)、(b)スピクリスポール酸及びp‐ニトロ安息香酸などとアルカノールアミンとの塩を含有する水溶性調質圧延油剤(特許文献2参照)、(c)脂肪族二塩基酸と飽和脂肪酸、及びモノエンカルボン酸などとアルカノールアミンを主体として含有する水溶性調質圧延油剤(特許文献3参照)、(d)ベンゾチアゾリルチオアルキレンカルボン酸及び脂肪族ジカルボン酸、芳香族ジカルボン酸などのアルカノールアミンの塩を主体として含有する水溶性調質圧延油剤(特許文献4参照)、などが挙げられる。
しかしながら、これらの油剤はいずれも耐ガムアップ性が不十分であり、また防錆性についても必ずしも充分とはいえなかった。そのため、いずれの性能についても充分な性能を具備した調質圧延鋼板を得られないのが実情である。そこで、調質圧延業界においては、これらの耐ガムアップ性、防錆性のいずれの性能についても優れた性能を有する油剤の開発が望まれている。
また、上記のとおり、油剤の希釈水として硬度が高い工業用水を用いてもスカムを発生しない油剤の出現が要望されている。
Conventionally, as this type of water-soluble temper rolling agent, those mainly composed of alkanolamine salts of dibasic acids and aromatic carboxylic acids have been used. Specifically, for example, (a) dibasic A water-soluble tempered rolling oil mainly composed of a salt of an acid and the like with a primary alkanolamine and an inorganic alkali (see Patent Document 1), (b) a salt of spikrispolic acid, p-nitrobenzoic acid and the like with an alkanolamine Water-soluble tempered rolling oil containing water (see Patent Document 2), (c) Water-soluble tempered rolling oil mainly containing an aliphatic dibasic acid and a saturated fatty acid, a monoenecarboxylic acid, and an alkanolamine (Patent Document) 3), (d) a water-soluble preparation mainly containing a salt of alkanolamine such as benzothiazolylthioalkylenecarboxylic acid and aliphatic dicarboxylic acid or aromatic dicarboxylic acid. Rolling oil (see Patent Document 4), and the like.
However, all of these oil agents have insufficient gum-up resistance and are not necessarily sufficient in terms of rust prevention. Therefore, the actual situation is that it is not possible to obtain a temper rolled steel sheet having sufficient performance for any performance. Therefore, in the temper rolling industry, it is desired to develop an oil agent that has excellent performance in both the gum-up resistance and the rust resistance.
In addition, as described above, there is a demand for the appearance of an oil agent that does not generate scum even when industrial water having high hardness is used as dilution water for the oil agent.
本発明は、このような状況下において、耐ガムアップ性、防錆性のいずれの性能にも優れた水溶性調質圧延液組成物を提供することを第一の目的とする。さらに本発明は、耐ガムアップ性、防錆性のいずれの性能にも優れると共に、希釈水として硬度が高い工業用水を使用してもスカムを発生せず、良好な性能を発揮できる水溶性調質圧延液組成物を提供することを第二の目的とするものである。 Under such circumstances, the first object of the present invention is to provide a water-soluble tempered rolling liquid composition that is excellent in both the gum-up resistance and the rust-proof performance. Furthermore, the present invention is excellent in both the anti-gum resistance and anti-rust properties, and does not generate scum even when industrial water with high hardness is used as the dilution water, and is a water-soluble compound that can exhibit good performance. A second object is to provide a quality rolling liquid composition.
本発明者らは、特定の芳香族カルボン酸、特定の脂肪族カルボン酸及び塩基性化合物とを含有する水溶性調質圧延液で、各カルボン酸の配合比率を特定の範囲に調整することによって、その目的を達成できることを見出した。本発明はかかる知見に基づいて完成したものである。 The present inventors are a water-soluble tempered rolling liquid containing a specific aromatic carboxylic acid, a specific aliphatic carboxylic acid and a basic compound, and by adjusting the mixing ratio of each carboxylic acid to a specific range. And found that the purpose can be achieved. The present invention has been completed based on such findings.
すなわち、本発明は、
1.水に、組成物基準で、(A)下記の一般式(1)
(X)m−Ar−(COOH)n ・・・(1)
〔式中、Xは、NO2-,RO‐,又はR‐(但し、Rは、炭素数1〜10の炭化水素基)、Arは2〜4の結合手を有する芳香族炭化水素基、m及びnは1又は2の整数を示し、mが2の場合、Xは同一でも異なっていてもよい。〕
で表される芳香族カルボン酸を0.5〜20質量%、(B)炭素数8〜24の脂肪族カルボン酸を0.5〜40質量%、及び(C)アルカリ金属の水酸化物及びアルカノールアミンから選ばれる少なくとも1種の塩基性化合物を含有する水溶性調質圧延液組成物であって、前記(B)の脂肪族カルボン酸と(A)の芳香族カルボン酸との含有比、B/A(モル比)が1.0〜10であることを特徴とする水溶性調質圧延液組成物、
2.(B)の脂肪族カルボン酸の70モル%以上が脂肪族モノカルボン酸である請求項1に記載の水溶性調質圧延液組成物、
3.(B)の脂肪族モノカルボン酸の80モル%以上が、分岐鎖を有する脂肪族モノカルボン酸である請求項2に記載の水溶性調質圧延液組成物。
4.(C)の塩基性化合物の含有量が、(A)及び(B)成分の中和当量以上である請求項1〜3のいずれかに記載の水溶性調質圧延液組成物、
5.(A)の芳香族カルボン酸が、ニトロ安息香酸及び又は炭素数1〜5のアルコキシ安息香酸である請求項1〜4のいずれかに記載の水溶性調質圧延液組成物、
6.前記1〜5のいずれかに記載の水溶性調質圧延液組成物を希釈水で10〜50倍に希釈した水溶性調質圧延液組成物、
を提供するものである。
That is, the present invention
1. In water, on a composition basis, (A) the following general formula (1)
(X) m -Ar- (COOH) n (1)
[Wherein, X is NO 2 —, RO—, or R— (wherein R is a hydrocarbon group having 1 to 10 carbon atoms), Ar is an aromatic hydrocarbon group having 2 to 4 bonds, m and n each represent an integer of 1 or 2, and when m is 2, X may be the same or different. ]
0.5 to 20% by mass of an aromatic carboxylic acid represented by formula (B) 0.5 to 40% by mass of an aliphatic carboxylic acid having 8 to 24 carbon atoms, and (C) an alkali metal hydroxide and A water-soluble tempered rolling fluid composition containing at least one basic compound selected from alkanolamines, the content ratio of the aliphatic carboxylic acid (B) and the aromatic carboxylic acid (A), B / A (molar ratio) is 1.0 to 10 in water-soluble tempered rolling fluid composition,
2. The water-soluble tempered rolling liquid composition according to claim 1, wherein 70 mol% or more of the aliphatic carboxylic acid of (B) is an aliphatic monocarboxylic acid,
3. The water-soluble tempered rolling liquid composition according to claim 2, wherein 80 mol% or more of the aliphatic monocarboxylic acid (B) is an aliphatic monocarboxylic acid having a branched chain.
4). Content of the basic compound of (C) is more than the neutralization equivalent of (A) and (B) component, The water-soluble tempered rolling liquid composition in any one of Claims 1-3,
5. The water-soluble tempered rolling fluid composition according to any one of claims 1 to 4, wherein the aromatic carboxylic acid of (A) is nitrobenzoic acid and / or an alkoxybenzoic acid having 1 to 5 carbon atoms.
6). A water-soluble tempered rolling fluid composition obtained by diluting the water-soluble tempered rolling fluid composition according to any one of 1 to 5 with diluted water 10 to 50 times;
Is to provide.
本発明の第一の発明における水溶性調質圧延液組成物は、耐ガムアップ性、防錆性のいずれの性能にも優れる。また、本発明の第二の発明の水溶性調質圧延液組成物は、耐ガムアップ性、防錆性のいずれの性能にも優れると共に、希釈水として硬度が高い水を用いた場合でも、スカムの発生を抑制できる。 The water-soluble tempered rolling liquid composition in the first invention of the present invention is excellent in both performances of gum-up resistance and rust resistance. In addition, the water-soluble tempered rolling liquid composition of the second invention of the present invention is excellent in both performance of gum-up resistance and rust prevention, and even when water with high hardness is used as dilution water, Scum generation can be suppressed.
本発明における第一の発明は、以下の条件を満たすものである。すなわち、水に、組成物基準で、(A)下記の一般式(1)
(X)m−Ar−(COOH)n ・・・(1)
〔式中、Xは、NO2-,RO‐,又はR‐(但し、Rは、炭素数1〜10の炭化水素基)、Arは、2〜4の結合手を有する芳香族炭化水素基、m及びnは1又は2の整数を示し、mが2の場合、Xは同一でも異なっていてもよい。〕
で表される芳香族カルボン酸を0.5〜20質量%、(B)炭素数8〜24の脂肪族カルボン酸を0.5〜40質量%、及び(C)アルカリ金属の水酸化物及びアルカノールアミンから選ばれる少なくとも1種の塩基性化合物を含有する水溶性調質圧延液組成物であって、前記(B)の脂肪族カルボン酸と(A)の芳香族カルボン酸との配合比、B/A(モル比)が1.0〜10であることを特徴とする水溶性調質圧延液組成物である。
The first invention in the present invention satisfies the following conditions. That is, in water, on a composition basis, (A) the following general formula (1)
(X) m -Ar- (COOH) n (1)
[Wherein, X is NO 2- , RO-, or R- (where R is a hydrocarbon group having 1 to 10 carbon atoms), Ar is an aromatic hydrocarbon group having 2 to 4 bonds. , M and n represent an integer of 1 or 2, and when m is 2, X may be the same or different. ]
0.5 to 20% by mass of an aromatic carboxylic acid represented by formula (B) 0.5 to 40% by mass of an aliphatic carboxylic acid having 8 to 24 carbon atoms, and (C) an alkali metal hydroxide and A water-soluble tempered rolling fluid composition containing at least one basic compound selected from alkanolamines, the blending ratio of the aliphatic carboxylic acid (B) and the aromatic carboxylic acid (A), B / A (molar ratio) is a water-soluble tempered rolling fluid composition characterized by 1.0 to 10.
前記(A)成分の一般式(1)において、Rで示される炭素数1〜10の炭化水素基としては、直鎖若しくは分岐鎖を有するアルキル基又はアルケニル基が好ましい。好ましいRの具体例としては、メチル基、エチル基、n−プロピル基、iso−プロピル基,各種(n‐,sec‐,tert‐,及びiso‐)ブチル基、各種ペンチル基、各種ヘキシル基、各種ヘプチル基、各種オクチル基、各種ノニル基、各種デシル基及びこれらのアルキル基(メチル基を除く)に対応するアルケニル基などを挙げることができる。Rは炭素数1〜8、さらには炭素数1〜6、特に炭素数1〜4のアルキル基が好ましい。 In the general formula (1) of the component (A), the hydrocarbon group having 1 to 10 carbon atoms represented by R is preferably a linear or branched alkyl group or alkenyl group. Specific examples of preferable R include a methyl group, an ethyl group, an n-propyl group, an iso-propyl group, various (n-, sec-, tert-, and iso-) butyl groups, various pentyl groups, various hexyl groups, Examples thereof include various heptyl groups, various octyl groups, various nonyl groups, various decyl groups, and alkenyl groups corresponding to these alkyl groups (excluding methyl groups). R is preferably an alkyl group having 1 to 8 carbon atoms, more preferably 1 to 6 carbon atoms, particularly 1 to 4 carbon atoms.
Arの2〜4の結合手を有する芳香族炭化水素基としては、いずれも芳香環に1又は2の結合手を有する安息香酸残基、フタル酸残基、イソフタル酸残基、テレフタル酸残基などの芳香族のモノカルボン酸残基やジカルボン酸残基が好ましく、入手が容易である点で、安息香酸残基やフタル酸残基が特に好ましい。 As the aromatic hydrocarbon group having 2 to 4 bonds of Ar, any of benzoic acid residue, phthalic acid residue, isophthalic acid residue, terephthalic acid residue having 1 or 2 bonds in the aromatic ring Aromatic monocarboxylic acid residues and dicarboxylic acid residues such as benzoic acid residues and phthalic acid residues are particularly preferable because they are easily available.
前記一般式(1)で表される芳香族カルボン酸の好適な例としては、安息香酸又はフタル酸の、(ジ)ニトロ化物(ニトロ化物又はジニトロ化物の意味である。)、(ジ)アルコキシ(アルキル基の炭素数1〜4)化物、(ジ)アルキル(アルキル基の炭素数1〜4)化物、アルキル(アルキル基の炭素数1〜4)ニトロ化物、アルコキシ(アルキル基の炭素数1〜4)ニトロ化物、アルコキシ(アルキル基の炭素数1〜4)アルキル(アルキル基の炭素数1〜4)化物が好ましく、具体的には、p‐ニトロ安息香酸、p‐メトキシ安息香酸、p‐エトキシ安息香酸、p‐nプロポキシ安息香酸、p‐isoプロポキシ安息香酸、p‐nブトキシ安息香酸、p‐secブトキシ安息香酸、p‐tertブトキシ安息香酸、p‐isoブトキシ安息香酸、p‐メチル安息香酸、p‐エチル安息香酸、p‐nプロピル安息香酸、p‐isoプロピル安息香酸、p‐nブチル安息香酸、p‐secブチル安息香酸、p‐tertブチル安息香酸、p‐isoブチル安息香酸、4−メチル3−ニトロ安息香酸、3−ニトロフタル酸などが挙げられる。 Preferable examples of the aromatic carboxylic acid represented by the general formula (1) include (di) nitrated products (meaning nitrated products or dinitrated products) and (di) alkoxy acids of benzoic acid or phthalic acid. (Alkyl group having 1 to 4 carbon atoms), (di) alkyl (alkyl group having 1 to 4 carbon atoms), alkyl (alkyl group having 1 to 4 carbon atoms) nitrate, alkoxy (alkyl group having 1 carbon atom) -4) nitrated compounds, alkoxy (alkyl group having 1 to 4 carbon atoms) alkyl (alkyl group having 1 to 4 carbon atoms) compound are preferable, specifically, p-nitrobenzoic acid, p-methoxybenzoic acid, p -Ethoxybenzoic acid, pn propoxybenzoic acid, p-isopropoxybenzoic acid, pn butoxybenzoic acid, p-sec butoxybenzoic acid, p-tertbutoxybenzoic acid, p-isobutoxy Benzoic acid, p-methylbenzoic acid, p-ethylbenzoic acid, pnpropylbenzoic acid, p-isopropylbenzoic acid, pnbutylbenzoic acid, p-secbutylbenzoic acid, p-tertbutylbenzoic acid P-isobutylbenzoic acid, 4-methyl 3-nitrobenzoic acid, 3-nitrophthalic acid, and the like.
本発明においては、これら芳香族カルボン酸を1種単独で、又は2種以上を混合して用いる。その配合量は組成物全量基準で0.5〜20質量%であり、好ましくは1〜15質量%である。芳香族カルボン酸の配合量が0.5〜20質量%であれば、それが(C)成分の塩基性化合物と塩を形成し、組成物の防錆性を高める効果があり、耐ガムアップ性も良好に保つことができる。 In this invention, these aromatic carboxylic acids are used individually by 1 type or in mixture of 2 or more types. The blending amount is 0.5 to 20% by mass, preferably 1 to 15% by mass based on the total amount of the composition. If the blending amount of the aromatic carboxylic acid is 0.5 to 20% by mass, it forms a salt with the basic compound (C) and has the effect of increasing the rust resistance of the composition, and is anti-gum-proof. Property can also be kept good.
本発明の水溶性調質圧延液組成物においては、(B)成分として炭素数8〜24、好ましくは炭素数12〜20の脂肪族カルボン酸を配合する。この炭素数8〜24の脂肪族カルボン酸としては、直鎖若しくは分岐鎖を有する飽和又は不飽和の脂肪族モノカルボン酸及び脂肪族ジカルボン酸が含まれる。 In the water-soluble tempered rolling liquid composition of the present invention, an aliphatic carboxylic acid having 8 to 24 carbon atoms, preferably 12 to 20 carbon atoms, is blended as the component (B). Examples of the aliphatic carboxylic acid having 8 to 24 carbon atoms include saturated or unsaturated aliphatic monocarboxylic acid and aliphatic dicarboxylic acid having a linear or branched chain.
前記炭素数8〜24の脂肪族カルボン酸の具体例としては、各種オクタン酸、各種ノナン酸、各種デカン酸、各種ウンデカン酸、各種ドデカン酸、各種テトラデカン酸、各種ヘキサデカン酸、各種オクタデカン酸、各種エイコサン酸、各種ドコサン酸などの脂肪族モノカルボン酸、オクタン二酸(スベリン酸)、ノナン二酸(アゼライン酸)、デカン二酸(セバシン酸)、ドデカン二酸、テトラデカン二酸、ヘキサデカン二酸、オクタデカン二酸などの脂肪族ジカルボン酸が挙げられる。 Specific examples of the aliphatic carboxylic acid having 8 to 24 carbon atoms include various octanoic acids, various nonanoic acids, various decanoic acids, various undecanoic acids, various dodecanoic acids, various tetradecanoic acids, various hexadecanoic acids, various octadecanoic acids, various Eicosanoic acid, aliphatic monocarboxylic acids such as various docosanoic acids, octanedioic acid (suberic acid), nonanedioic acid (azeleic acid), decanedioic acid (sebacic acid), dodecanedioic acid, tetradecanedioic acid, hexadecanedioic acid, Aliphatic dicarboxylic acids such as octadecanedioic acid.
前記(B)の脂肪族カルボン酸については、その70モル%以上が脂肪族モノカルボン酸であることが好ましい。脂肪族カルボン酸の70モル%以上が脂肪族モノカルボン酸であれば、水溶性調質圧延液組成物の耐ガムアップ性を良好に保つと共に、防錆性を高める効果がある。脂肪族カルボン酸中の脂肪族モノカルボン酸の割合は、80モル%以上、更には90モル%以上であることがより好ましい。 As for the aliphatic carboxylic acid (B), 70 mol% or more is preferably an aliphatic monocarboxylic acid. If 70 mol% or more of the aliphatic carboxylic acid is an aliphatic monocarboxylic acid, the water-soluble tempered rolling liquid composition has the effect of improving the anti-rust property while maintaining good gum-up resistance. The proportion of the aliphatic monocarboxylic acid in the aliphatic carboxylic acid is more preferably 80 mol% or more, and even more preferably 90 mol% or more.
本発明においては、これら脂肪族カルボン酸は1種を単独で、又は2種以上を混合して用いる。その配合量は組成物全量基準で1〜30質量%であり、好ましくは5〜15質量%である。(B)成分の脂肪族カルボン酸の含有量が1質量%以上であれば、錆止め性が認められ、30質量%以下であれば、耐ガムアップ性などを低下させることもない。 In the present invention, these aliphatic carboxylic acids are used singly or in combination of two or more. The blending amount is 1 to 30% by mass, preferably 5 to 15% by mass, based on the total amount of the composition. When the content of the aliphatic carboxylic acid as the component (B) is 1% by mass or more, rust preventive properties are recognized, and when it is 30% by mass or less, the gum-up resistance and the like are not deteriorated.
本発明の水溶性調質圧延液組成物においては、前記(B)の脂肪族カルボン酸と前記(A)の芳香族カルボン酸との配合比、B/A(モル比)が1.0〜10であることを要し、好ましくは1.0〜8、特に好ましくは2.0〜5.0である。B/A(モル比)が1.0未満では、ガムアップ性が不充分であり、一方B/A(モル比)が10を越えると、錆止め性能が低下する場合がある。 In the water-soluble tempered rolling liquid composition of the present invention, the blending ratio of the aliphatic carboxylic acid (B) and the aromatic carboxylic acid (A), B / A (molar ratio) is 1.0 to 1.0. 10 and preferably 1.0 to 8, particularly preferably 2.0 to 5.0. If the B / A (molar ratio) is less than 1.0, the gum-up property is insufficient. On the other hand, if the B / A (molar ratio) exceeds 10, the rust prevention performance may be lowered.
本発明においては、(C)成分としてアルカリ金属の水酸化物、及びアルカノールアミンから選ばれる少なくとも1種の塩基性化合物を配合する。
前記アルカリ金属水酸化物としては、水酸化ナトリウム、水酸化カリウム、水酸化リチウムを例示することができる。また、アルカノールアミンとしては、モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、モノn−プロパノールアミン、ジ(n−プロパノール)アミン、トリ(n−プロパノール)アミン、モノイソプロパノールアミン、ジイソプロパノールアミン、トリイソプロパノールアミン、メチルイソプロパノールアミンなどが挙げられる。これらのアルカノールアミンの中でも、総炭素数2〜4の一級又は二級のアルカノールアミンが好ましい。
In the present invention, as the component (C), at least one basic compound selected from alkali metal hydroxides and alkanolamines is blended.
Examples of the alkali metal hydroxide include sodium hydroxide, potassium hydroxide, and lithium hydroxide. In addition, as alkanolamine, monoethanolamine, diethanolamine, triethanolamine, mono n-propanolamine, di (n-propanol) amine, tri (n-propanol) amine, monoisopropanolamine, diisopropanolamine, triisopropanolamine And methyl isopropanolamine. Among these alkanolamines, primary or secondary alkanolamines having 2 to 4 carbon atoms are preferable.
本発明においては、(C)成分のアルカリ金属の水酸化物、及びアルカノールアミンから選ばれる少なくとも1種の塩基性化合物を含有することを要する。この(C)成分の含有量は、前記(A)及び(B)成分の中和当量以上含有することが好ましい。(C)成分のアルカリ金属の水酸化物及びアルカノールアミンから選ばれる少なくとも1種の塩基性化合物の含有量が、前記(A)及び(B)成分の中和当量以上であれば、(A)及び(B)の各カルボン酸が(C)成分と良好な塩を形成し、優れた防錆性を発現する。この(C)成分の配合量は前記(A)及び(B)成分の1.0〜1.2当量であることがより好ましい。 In the present invention, it is necessary to contain at least one basic compound selected from the alkali metal hydroxide of component (C) and alkanolamine. The content of the component (C) is preferably at least the neutralization equivalent of the components (A) and (B). (C) If the content of at least one basic compound selected from the alkali metal hydroxides and alkanolamines of the component is not less than the neutralization equivalent of the components (A) and (B), (A) And each carboxylic acid of (B) forms a favorable salt with (C) component, and expresses the outstanding rust prevention property. The amount of component (C) is more preferably 1.0 to 1.2 equivalents of components (A) and (B).
本発明の(C)成分には、上記アルカリ金属水酸化物、アルカノールアミンからなる群から選ばれる1種もしくは2種以上の塩基性化合物が任意に使用可能であるが、アルカリ金属水酸化物の1種以上とアルカノールアミンの1種以上とを混合して配合することがより好ましい。その場合の混合割合は任意であるが、耐ガムアップ性の観点か、アルカノールアミンがアルカリ金属水酸化物より過剰当量であることが好ましく、例えば、アルカノールアミンがアルカリ金属水酸化物1当量に付き1〜8当量、さらに1.5〜5当量であることがより好ましい。 As the component (C) of the present invention, one or more basic compounds selected from the group consisting of the above alkali metal hydroxides and alkanolamines can be arbitrarily used. It is more preferable to mix one or more types with one or more types of alkanolamines. In this case, the mixing ratio is arbitrary, but from the viewpoint of gum-up resistance, it is preferable that the alkanolamine is in excess equivalent to the alkali metal hydroxide. For example, the alkanolamine is attached to 1 equivalent of the alkali metal hydroxide. It is more preferable that it is 1-8 equivalent, and also 1.5-5 equivalent.
本発明の水溶性調質圧延液組成は、水に、上記(A)、(B)及び(C)の各成分を配合した水溶性調質圧延液組成物である。ここで用いる水については、特に制限はなく、例えば脱イオン水、純水、水道水、工業用水などが使用できるが、脱イオン水、及び純水が好ましい。また、その含有量は、水溶性調質圧延液組成物基準で通常30〜90質量%である。 The water-soluble tempered rolling fluid composition of the present invention is a water-soluble tempered rolling fluid composition in which the components (A), (B), and (C) are blended with water. There is no restriction | limiting in particular about the water used here, For example, deionized water, a pure water, a tap water, industrial water etc. can be used, A deionized water and a pure water are preferable. Moreover, the content is 30-90 mass% normally on the basis of a water-soluble temper rolling liquid composition.
本発明の水溶性調質圧延液組成物は、上記の組成を有するものであるが、さらに必要に応じて公知の添加剤を配合することができる。そのような添加剤としては、例えば、ポリエチレングリコール、ポリプロピレングリコールなどのポリアルキレングリコール類、ポリアルキレングリコールのエチレンオキサイド(EO)、プロピレンオキサイド(PO)等のアルキレンオキサイド付加物、メチルセルロース類などの水溶性ポリマーがある。このような水溶性ポリマーは、調質圧延の圧延ロールに残る粘着性の不揮発分の発生を抑制する効果(耐ビルドアップ性)があり、通常水溶性調質圧延液組成物を基準にして、およそ0.5〜15質量%配合する。 The water-soluble tempered rolling liquid composition of the present invention has the above-described composition, but may further contain known additives as necessary. Examples of such additives include polyalkylene glycols such as polyethylene glycol and polypropylene glycol, alkylene oxide adducts such as ethylene oxide (EO) and propylene oxide (PO) of polyalkylene glycol, and water solubility such as methylcellulose. There is a polymer. Such a water-soluble polymer has an effect of suppressing the generation of sticky non-volatile content remaining on the roll of temper rolling (build-up resistance), and is usually based on a water-soluble temper rolling composition, About 0.5 to 15% by mass is blended.
また、ほう酸、タングステン酸、モリブデン酸、リン酸、炭酸、硫酸、珪酸、硝酸、亜硝酸等の無機酸のナトリウム塩、及びカリウム塩;ベンゾトリアゾール、メチルベンゾトリアゾール、トリルトリアゾール、ヒドロカルビルトリアゾール等のトリアゾール類及びその塩;メルカプトベンゾチアゾール等のチアゾール類およびその塩;脂肪酸アルカノールアミド類;イミダゾリン類;オキサゾリン類など水溶性金属腐食防止剤は、水溶性調質圧延液組成物の錆止め作用を向上させる効果がある。その他、硫酸およびスルホン酸エステルなどのアニオン系界面活性剤;ポリオキシエチレン化合物などのノニオン系界面活性剤などを例示できる。これら水溶性金属腐食防止剤など添加剤の配合量は水溶性調質圧延液組成物基準で、通常10質量%以下の範囲で配合する。 In addition, sodium salts and potassium salts of inorganic acids such as boric acid, tungstic acid, molybdic acid, phosphoric acid, carbonic acid, sulfuric acid, silicic acid, nitric acid, and nitrous acid; triazoles such as benzotriazole, methylbenzotriazole, tolyltriazole, and hydrocarbyltriazole And salts thereof; thiazoles such as mercaptobenzothiazole and salts thereof; fatty acid alkanolamides; imidazolines; oxazolines, and the like, water-soluble metal corrosion inhibitors such as rust-preventing action of a water-soluble tempered rolling liquid composition There is. Other examples include anionic surfactants such as sulfuric acid and sulfonic acid esters; nonionic surfactants such as polyoxyethylene compounds. The amount of additives such as these water-soluble metal corrosion inhibitors is usually in the range of 10% by mass or less based on the water-soluble tempered rolling fluid composition.
本発明の水溶性調質圧延液組成物は、以上のような構成を有するが、その組成物のpHが7〜10であることが好ましく、8〜9であることがより好ましい。pHが7〜10であれば、防錆性や濡れ性を良好に保つ効果がある。
また、本発明の水溶性調質圧延液組成物は、摩擦係数が一定値より低いことが好ましく、例えば、曾田式摩擦試験機で摩擦係数が0.3以下であることが好ましく、0.2以下であるものがより好ましい。摩擦係数が0.3以下であれば、調質圧延において、圧延荷重の変動幅が小さく、安定したロール表面の転写を行うことができる効果がある。
Although the water-soluble tempered rolling liquid composition of the present invention has the above-described configuration, the pH of the composition is preferably 7 to 10, and more preferably 8 to 9. If pH is 7-10, there exists an effect which keeps rust prevention property and wettability favorable.
Further, the water-soluble tempered rolling fluid composition of the present invention preferably has a friction coefficient lower than a certain value, for example, the friction coefficient is preferably 0.3 or less with a Kamata type friction tester, 0.2 The following are more preferable. If the friction coefficient is 0.3 or less, the temper rolling has a small fluctuation range of the rolling load, and has an effect of performing stable transfer of the roll surface.
上記本発明の水溶性調質圧延液組成物は、いわゆる水溶性調質圧延液の原液であり、通常これを希釈水で10〜50倍に希釈して実際の調質圧延に使用される。その場合の希釈水としては、脱イオン水、純水、水道水などが使用できる。 The water-soluble tempered rolling fluid composition of the present invention is a stock solution of a so-called water-soluble tempered rolling fluid, and is usually diluted 10 to 50 times with dilution water and used for actual temper rolling. In this case, deionized water, pure water, tap water, or the like can be used as dilution water.
本発明における第二の発明は、以下の構成を有する。上記第一の発明において、(B)の脂肪族モノカルボン酸の80モル%以上、好ましくは90モル%以上が、さらに好ましくは95モル%以上が分岐鎖を有する脂肪族モノカルボン酸である水溶性調質圧延液組成物である。
このような組成であることによって、第一の発明が有する性能を具備する上に、希釈水として硬度が高い工業用水を用いた場合であっても、スカムの発生を抑制でき、かつ性能が低下することもない。従って、希釈水は硬水であるか軟水であるかを問わず、水道水、工業用水、イオン交換水、蒸留水などを任意に使用することができる。
The second invention in the present invention has the following configuration. In the first aspect of the invention, the water-soluble water in which 80 mol% or more, preferably 90 mol% or more, more preferably 95 mol% or more of the aliphatic monocarboxylic acid (B) is an aliphatic monocarboxylic acid having a branched chain. It is a tempered rolling liquid composition.
By having such a composition, in addition to having the performance of the first invention, even when industrial water with high hardness is used as dilution water, the occurrence of scum can be suppressed and the performance is reduced. I don't have to. Therefore, regardless of whether the dilution water is hard water or soft water, tap water, industrial water, ion exchange water, distilled water, and the like can be arbitrarily used.
次に実施例により本発明を詳しく説明するが、本発明はこれらの例によって何ら制限されるものではない。なお、水溶性調質圧延液組成物の性能は次の方法に従って評価した。
(1)耐ガムアップ性
300mlの容器に各水溶性調質圧延液組成物の試料10gと市販の防錆油(「ダフニーオイルコートZ−3」出光興産株式会社製)70gとを採取し、70℃で16時間、1000rpmで攪拌した。その後、ヘキサン溶剤で容器を洗浄し、洗浄後の付着物をガム量として秤量した。
EXAMPLES Next, although an Example demonstrates this invention in detail, this invention is not restrict | limited at all by these examples. The performance of the water-soluble tempered rolling liquid composition was evaluated according to the following method.
(1) Gum-up resistance 10 g of each water-soluble tempered rolling liquid composition sample and 70 g of commercially available rust preventive oil ("Dafney Oil Coat Z-3" manufactured by Idemitsu Kosan Co., Ltd.) are collected in a 300 ml container, It stirred at 1000 rpm for 16 hours at 70 degreeC. Thereafter, the container was washed with a hexane solvent, and the adhered matter after washing was weighed as a gum amount.
(2)防錆試験
JIS G 3141に規定する鋼板(60×80×1mm)を脱脂後、各水溶性調質圧延液組成物の試料に浸漬し、乾燥後、その試験片屋内暴露試験及びスタック試験を行った。
屋内暴露試験は10日後に、さび、ステインの有無と程度を観察した。また、スタック試験は、温度50℃×湿度95%RHの条件で10日経過後に、さび、ステインの有無と程度を観察した。
(3)摩擦係数
曾田振り子式摩擦試験機を用いて測定した。
(2) Rust prevention test A steel plate (60 × 80 × 1 mm) specified in JIS G 3141 is degreased, immersed in a sample of each water-soluble tempered rolling liquid composition, dried, and then the test piece indoor exposure test and stack A test was conducted.
In the indoor exposure test, the presence and degree of rust and stain were observed after 10 days. In the stack test, the presence or absence and degree of rust and stain were observed after 10 days at a temperature of 50 ° C. and a humidity of 95% RH.
(3) Friction coefficient It measured using the Kamata pendulum type friction tester.
(4)調質圧延実験
4段式小型圧延機を用いて下記の条件で圧延し、圧延時の圧延荷重変動幅を測定した。
・圧延条件
ロール径 135mm
圧延材 SPCC−SB(200m×50mm×0.05mm)
圧延荷重 3.8kN(3.9tf)
圧下率 3%
圧延速度 50m/min.
(4) Conditioning rolling experiment Rolling was performed under the following conditions using a four-stage small rolling mill, and the rolling load fluctuation range during rolling was measured.
・ Rolling conditions Roll diameter 135mm
Rolled material SPCC-SB (200m x 50mm x 0.05mm)
Rolling load 3.8kN (3.9tf)
Rolling rate 3%
Rolling speed 50 m / min.
実施例1〜5及び比較例1〜3
第1表に示す成分を用いて水溶性調質圧延液組成物を調整した。それら調整
した組成物及び市販の水溶性調質圧延油剤について、各種性能を評価した。その結果を第1表に示した。第1表中、その他の成分とは、水溶性ポリマー(エチレングリコールEO,PO付加物)、グリコーエーテル、ノニオン系界面活性剤及びベンゾトリアゾールの混合物である。
Examples 1-5 and Comparative Examples 1-3
A water-soluble tempered rolling liquid composition was prepared using the components shown in Table 1. Various performances were evaluated for these prepared compositions and commercially available water-soluble tempered rolling oils. The results are shown in Table 1. In Table 1, the other components are a mixture of a water-soluble polymer (ethylene glycol EO, PO adduct), glycoether, nonionic surfactant and benzotriazole.
第1表によれば、B/A(モル比)が1.0以上の実施例1〜5の水溶性調質圧延液組成物は、「ガム生成無し」又は「ガム生成少量」であり、耐ガムアップ性が優れていることが分る。これに対してB/A(モル比)が0.3である比較例1は、「ガム生成多量」であり、一方、B/A(モル比)が∞、すなわちA成分を含有しなく、しかもB中のモノカルボン酸が70モル%である比較例2では、ガムは生成しないが、防錆試験では錆を発生することが分る。
また、B中の(分岐鎖を有するモノカルボン酸)/(モノカルボン酸)(モル%)
が100%である実施例2〜5の水溶性調質圧延液組成物は、工業用水で希釈してもスカムを発生しないが、その値が72%である実施例1の場合はスカムを発生することが分る。
また、第1表によれば、実施例1〜3及び5の摩擦係数はいずれも3以下であるが、比較例1及び4では摩擦係数が高く、3以上である。また、実施例2及び3では、調質圧延における荷重変動幅が2.5kN以下で小さいのに対し、比較例3は3.9kNであって、調質圧延における荷重変動幅が大きいことが分る。
According to Table 1, the water-soluble tempered rolling liquid composition of Examples 1 to 5 having a B / A (molar ratio) of 1.0 or more is “no gum production” or “a small amount of gum production”. It can be seen that the gum-up resistance is excellent. On the other hand, Comparative Example 1 in which B / A (molar ratio) is 0.3 is “a large amount of gum generation”, while B / A (molar ratio) is ∞, that is, it does not contain an A component. Moreover, in Comparative Example 2 in which the monocarboxylic acid in B is 70 mol%, no gum is produced, but it is found that rust is generated in the rust prevention test.
In addition, (monocarboxylic acid having a branched chain) / (monocarboxylic acid) (mol%) in B
The water-soluble tempered rolling fluid compositions of Examples 2 to 5 with 100% do not generate scum even when diluted with industrial water, but in the case of Example 1 whose value is 72%, scum is generated. I know what to do.
Further, according to Table 1, the friction coefficients of Examples 1 to 3 and 5 are all 3 or less, but in Comparative Examples 1 and 4, the friction coefficient is high and 3 or more. Further, in Examples 2 and 3, the load fluctuation width in the temper rolling is small at 2.5 kN or less, whereas Comparative Example 3 is 3.9 kN, and the load fluctuation width in the temper rolling is large. The
本発明の水溶性調質圧延液組成物は、耐ガムアップ性、防錆性のいずれの性能にも優れる水溶性調質圧延液組成物である。また、本発明の水溶性調質圧延液組成物は、耐ガムアップ性、防錆性のいずれの性能にも優れると共に、希釈水として硬度が高い水を用いた場合でも、スカムの発生を抑制できる水溶性調質圧延液組成物として有用である。 The water-soluble tempered rolling liquid composition of the present invention is a water-soluble tempered rolling liquid composition that is excellent in both performances of gum-up resistance and rust resistance. In addition, the water-soluble tempered rolling liquid composition of the present invention is excellent in both the anti-gum resistance and rust-proof performance, and suppresses the occurrence of scum even when water with high hardness is used as dilution water. It is useful as a water-soluble tempered rolling liquid composition.
Claims (6)
(X)m−Ar−(COOH)n ・・・(1)
〔式中、Xは、NO2-,RO‐,又はR‐(但し、Rは、炭素数1〜10の炭化水素基)、Arは2〜4の結合手を有する芳香族炭化水素基、m及びnは1又は2の整数を示し、mが2の場合、Xは同一でも異なっていてもよい。〕
で表される芳香族カルボン酸を0.5〜20質量%、(B)炭素数8〜24の脂肪族カルボン酸を0.5〜40質量%、及び(C)アルカリ金属の水酸化物及びアルカノールアミンから選ばれる少なくとも1種の塩基性化合物を含有する水溶性調質圧延液組成物であって、前記(B)の脂肪族カルボン酸と(A)の芳香族カルボン酸との含有比、B/A(モル比)が1.0〜10であることを特徴とする水溶性調質圧延液組成物。 In water, on a composition basis, (A) the following general formula (1)
(X) m -Ar- (COOH) n (1)
[Wherein, X is NO 2 —, RO—, or R— (wherein R is a hydrocarbon group having 1 to 10 carbon atoms), Ar is an aromatic hydrocarbon group having 2 to 4 bonds, m and n each represent an integer of 1 or 2, and when m is 2, X may be the same or different. ]
0.5 to 20% by mass of an aromatic carboxylic acid represented by formula (B) 0.5 to 40% by mass of an aliphatic carboxylic acid having 8 to 24 carbon atoms, and (C) an alkali metal hydroxide and A water-soluble tempered rolling fluid composition containing at least one basic compound selected from alkanolamines, the content ratio of the aliphatic carboxylic acid (B) and the aromatic carboxylic acid (A), B / A (molar ratio) is 1.0-10, The water-soluble refining rolling liquid composition characterized by the above-mentioned.