JP2007171310A - Authenticity determining article and medium with authenticity determining article - Google Patents
Authenticity determining article and medium with authenticity determining article Download PDFInfo
- Publication number
- JP2007171310A JP2007171310A JP2005365594A JP2005365594A JP2007171310A JP 2007171310 A JP2007171310 A JP 2007171310A JP 2005365594 A JP2005365594 A JP 2005365594A JP 2005365594 A JP2005365594 A JP 2005365594A JP 2007171310 A JP2007171310 A JP 2007171310A
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- cholesteric liquid
- layer
- crystal layer
- retardation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、偽造防止性が非常に高く、また見る角度によって色相が異なって見え、また左偏光板もしくは右偏光板のいずれかを介して観察し、反射光の有無を確認することにより、見えるパターンが変化して、真偽判定を確実に行なえる真偽判定体及び真偽判定体付き媒体に関するものである。 The present invention has a very high anti-counterfeit property, and the hue looks different depending on the viewing angle, and it can be seen by observing through either the left polarizing plate or the right polarizing plate and confirming the presence or absence of reflected light. The present invention relates to a true / false determining body and a medium with a true / false determining body capable of reliably performing authenticity determination by changing a pattern.
従来から、経済的に価値の高い高額商品や、ＩＤ（Ｉｄｅｎｔｉｆｉｃａｔｉｏｎ；照合一致）手段として用いると高い価値を生じるクレジットカードや、トラベラーズチェック、または金券類等には、それらの真偽性を判定するのに適したホログラム（ラベル）を付与させて、偽造を防止して、真正物として証明することが行われている。しかし、最近では、目視では本物と区別がつかないようなホログラムの製造が行われて、真正性を証明する新規なものが要求されている。 Conventionally, authenticity is determined for expensive products with high economic value, credit cards, traveler's checks, or vouchers that produce high value when used as ID (Identification) means. A hologram (label) suitable for the above is given to prevent forgery and prove as a genuine product. However, recently, holograms that are indistinguishable from the real thing are manufactured, and new ones that prove authenticity are required.
偽造防止対策として、例えば、特許文献１にあるように、対象物の真正性を識別するべく対象物に設けられる識別媒体として、入射した光のうち、左回り偏光又は右回り偏光のいずれか一方の光のみを反射する光選択反射層として、コレステリック液晶インキにより印刷して、その光選択反射層を形成することが記載されている。
As an anti-counterfeiting measure, for example, as disclosed in
偽造防止の対策として、上記の方法で改善はされたものの、高分子コレステリック液晶の材料を入手すれば、偽造することは不可能ではなく、未だ十分に偽造防止の方法として、満足できるものとは言えないものである。
したがって、上記のような課題を解決するために、本発明は、真偽判定体あるいは真偽判定体が付与された媒体において、偽造防止性が非常に高く、また真偽判定を確実に行なえる真偽判定体及び真偽判定体付き媒体を提供することを目的とする。 Therefore, in order to solve the above-described problems, the present invention has a very high anti-counterfeit property and can reliably perform authenticity determination in a medium provided with authenticity determination body or authenticity determination body. It is an object to provide a true / false determination object and a medium with a true / false determination object.
以上の状況を鑑み、鋭意研究開発を進め、本発明は真偽判定体及び真偽判定体付き媒体において、上記の課題を解決したものである。すなわち、請求項１に記載の発明は、位相差を生じさせる効果を有したフィルム（位相差フィルム）の両面に、コレステリック液晶層が設けられた真偽判定体において、該位相差フィルムの一方の面に設けられたコレステリック液晶層Ａと、該位相差フィルムの他方の面に設けられたコレステリック液晶層Ｂとの形成された形状が、互いに異なっていることを特徴とする真偽判定体である。
In view of the above situation, earnest research and development has been advanced, and the present invention solves the above-described problems in the authenticity determination body and the medium with the authenticity determination body. That is, the invention according to
また、請求項２の発明は、位相差を生じさせる効果を有した層（位相差層）の上下に、コレステリック液晶層が設けられた真偽判定体において、該位相差層の一方の面に設けられたコレステリック液晶層Ａと、該位相差層の他方の面に設けられたコレステリック液晶層Ｂとの形成された形状が、互いに異なっていることを特徴とする真偽判定体である。請求項３の発明は、請求項１または２のコレステリック液晶層Ａ及びＢが、各々の反射波長が異なることを特徴とする真偽判定体である。また、請求項４の発明は、請求項１または２のコレステリック液晶層Ａ及びＢが、各々の反射波長が同等であることを特徴とする真偽判定体である。 Further, the invention of claim 2 is an authenticity determination body in which a cholesteric liquid crystal layer is provided above and below a layer having an effect of causing a retardation (retardation layer), on one surface of the retardation layer. The authenticity determination body is characterized in that the formed cholesteric liquid crystal layer A and the cholesteric liquid crystal layer B provided on the other surface of the retardation layer have different shapes. According to a third aspect of the present invention, there is provided a true / false determining body characterized in that the cholesteric liquid crystal layers A and B of the first or second aspect have different reflection wavelengths. According to a fourth aspect of the present invention, there is provided a true / false determining body characterized in that the cholesteric liquid crystal layers A and B of the first or second aspect have the same reflection wavelength.
請求項５の発明は、請求項１〜４の真偽判定体を粘着剤を介して、媒体に貼着させたもの、該真偽判定体を、媒体に転写またはラミネートして付着させたもの、該真偽判定体を基紙に、スレッド状に抄き込んだものの中のいずれかの一つであることを特徴とする真偽判定体付き媒体である。
The invention of claim 5 is the one in which the authenticity determination body of
本発明の真偽判定体は、位相差フィルムまたは位相差層の上下に、コレステリック液晶層が設けられた真偽判定体において、該位相差フィルムまたは位相差層の一方の面に設けられたコレステリック液晶層Ａと、該位相差フィルムまたは位相差層の他方の面に設けられたコレステリック液晶層Ｂとの形成された形状が、互いに異なっているものである。従来のコレステリック液晶材料をフィルム化させたものでは、偽造防止性（セキュリティ性）をさらに付加させることが困難であったが、本発明の真偽判定体はコレステリック液晶層Ａとコレステリック液晶層Ｂを組み合わせたものである。この本発明の真偽判定体に対して、偏光板を介して見ると、コレステリック液晶層ＡとＢとの見え方が、異なり、一方の液晶層の色が見え、他方の液晶層の色が見えないようにすることができた。これにより、偽造防止性が非常に高く、また真偽判定を確実に行なえるものが得られた。 The authenticity determination body of the present invention is a true / false determination body in which a cholesteric liquid crystal layer is provided above and below a retardation film or retardation layer, and a cholesteric body provided on one surface of the retardation film or retardation layer. The formed shapes of the liquid crystal layer A and the cholesteric liquid crystal layer B provided on the other surface of the retardation film or retardation layer are different from each other. Although it is difficult to further add anti-counterfeiting (security) with a conventional cholesteric liquid crystal material formed into a film, the authenticity determination body of the present invention includes a cholesteric liquid crystal layer A and a cholesteric liquid crystal layer B. It is a combination. With respect to the authenticity determination body of the present invention, when viewed through the polarizing plate, the appearance of the cholesteric liquid crystal layers A and B is different, the color of one liquid crystal layer is visible, and the color of the other liquid crystal layer is I was able to hide it. As a result, an anti-counterfeiting property is very high, and a product that can reliably perform authenticity determination is obtained.
図１は、本発明の真偽判定体１の一つの実施形態を示す概略断面図であり、位相差を生じさせる効果を有したフィルムである位相差フィルム２の一方の面に、コレステリック液晶層Ａ（３）が部分的に、つまりパターン状に設けられ、また該位相差フィルム２の他方の面には、コレステリック液晶層Ｂ（４）が位相差フィルムの片側の全面に設けられたものであり、コレステリック液晶層Ａと、コレステリック液晶層Ｂとの形成された形状が、互いに異なっている。このコレステリック液晶層ＡとＢは、いずれも入射した光のうち、左回り偏光又は右回り偏光のいずれか一方の光のみを反射する機能をもつので、言い換えれば、光選択反射層でもある。
FIG. 1 is a schematic cross-sectional view showing one embodiment of the
また、図２は本発明の真偽判定体１の他の実施形態を示す概略断面図であり、位相差フィルム２の一方の面の全面に、コレステリック液晶層Ａ（３）がベタ状に設けられ、また該位相差フィルム２の他方の面には、コレステリック液晶層Ｂ（４）が部分的に、つまりパターン状に設けられたものであり、コレステリック液晶層Ａと、コレステリック液晶層Ｂとの形成された形状が、互いに異なっている。
FIG. 2 is a schematic cross-sectional view showing another embodiment of the
また、図３は本発明の真偽判定体１の他の実施形態を示す概略断面図であり、基材フィルム５の一方の面の全面に、コレステリック液晶層Ａ（３）がベタ状に設けられ、そのコレステリック液晶層Ａ（３）の上に、位相差層６がベタ状に設けられ、さらにその位相差層６の上に、コレステリック液晶層Ｂ（４）が部分的に、つまりパターン状に設けられたものである。この形態の状態のままで、真偽判定体として利用することが可能であるが、コレステリック液晶層Ａ（３）を含めた積層体（符号では３、６、４で示される３層）が基材フィルムから剥離可能にした転写フィルムとして利用し、被転写体の対象物（媒体）にその積層体を熱、圧力を加えて、転写して付着させることが好ましく行なわれる。この転写フィルムの形態の場合、基材フィルムとコレステリック液晶層との熱離型性が不十分であれば、基材フィルム表面に各種の熱離型性をもたせるための手段として、従来公知の離型層を設けてもよい。さらに、転写フィルムの表面となるコレステリック液晶層の上に、熱転写の際に被転写体との密着性を高めるために、従来公知の接着層を設けることができる。尚、図３のものでも、コレステリック液晶層Ａと、コレステリック液晶層Ｂとの形成された形状が、互いに異なっている。また、図示はしないが、図３に示した真偽判定体において、位相差層６の上に設けられたコレステリック液晶層Ａ（３）とコレステリック液晶層Ｂ（４）において、コレステリック液晶層Ａ（３）を部分的に、パターン状に設け、コレステリック液晶層Ｂ（４）を位相差層６の上の全面に設けても良い。
FIG. 3 is a schematic cross-sectional view showing another embodiment of the
図４は、本発明の真偽判定体１の一つの実施形態のものを、偏光板を介して観察した時に見えるコレステリック液晶層の発色状態を説明する概略図である。図４で示した真偽判定体１は、コレステリック液晶層Ａが位相差フィルムまたは位相差層の片側の全面にベタ状に設けられ、コレステリック液晶層Ｂが、その位相差フィルムまたは位相差層の反対側に、「ＤＮＰ」というパターンを設けたものである。この真偽判定体１を例えば、右円偏光板を介して観察すると、コレステリック液晶層Ａのベタ状の発色の背景が見え、また左円偏光板を介して観察すると、その背景の色は消えて、コレステリック液晶層Ｂの「ＤＮＰ」というパターンの発色が浮き出てくる。また、上記のコレステリック液晶層Ａ、Ｂを構成するコレステリック液晶材料を変更する等により、上記の真偽判定体を左円偏光板を介して観察すると、コレステリック液晶層Ａのベタ状の発色の背景が見え、また右円偏光板を介して観察すると、その背景の色は消えて、コレステリック液晶層Ｂの「ＤＮＰ」というパターンの発色が浮き出てくるようにすることもできる。
FIG. 4 is a schematic diagram for explaining the color development state of the cholesteric liquid crystal layer that can be seen when one of the embodiments of the
図５は、本発明の真偽判定体付き媒体７の一つの実施形態を示す概略平面図であり、真偽判定体がスレッド状（糸状）のもので、媒体として紙を用い、基紙８に、図１〜４に示したような真偽判定体のスレッド９を抄き込んだもので、スレッド９が間欠的に露出する複数の露出部１０と、各露出部間でスレッド９を間欠的に覆う被覆部１１とを備えている。また、その露出部１０のスレッド９には、図４で示したような「ＤＮＰ」というパターンの発色が浮き出てくるようにしたものである。この露出部１０と被覆部１１のパターンに対応した抄き網を使用した抄紙機で、スレッドの搬送を制御する等して、露出部１０に「ＤＮＰ」というパターンが図示したような位置になるようにして、抄造することにより、真偽判定体付き媒体７を得ることができる。図５では、真偽判定体を基紙に、スレッド状に抄き込んだものを示したが、これに限らず、真偽判定体を粘着剤を介して、媒体に貼着させたもの、あるいは真偽判定体を、媒体に転写またはラミネートして付着させたもの等がある。 FIG. 5 is a schematic plan view showing one embodiment of the medium 7 with the authenticity determination body of the present invention, where the authenticity determination body is thread-like (thread-like), paper is used as the medium, and the base paper 8 is used. 1 to 4, a thread 9 having a true / false judgment as shown in FIGS. 1 to 4 is incorporated, and a plurality of exposed portions 10 where the threads 9 are intermittently exposed and the threads 9 intermittently between the exposed portions. And a covering portion 11 for covering. Further, the color of the pattern “DNP” as shown in FIG. 4 appears on the thread 9 of the exposed portion 10. With a paper machine using a papermaking net corresponding to the pattern of the exposed portion 10 and the covering portion 11, the pattern “DNP” is located on the exposed portion 10 as shown in the figure by controlling the conveyance of the thread. Thus, the medium 7 with authenticity determination body can be obtained by papermaking. In FIG. 5, the authenticity determination body is shown on the base paper, which is drawn into a thread shape. However, the present invention is not limited thereto, and the authenticity determination body is attached to the medium via an adhesive. Alternatively, the authenticity determination body is transferred or laminated to a medium and attached.
以下、本発明の真偽判定体及び真偽判定体付き媒体を構成する各層や、構成要素について、詳細に説明する。
（位相差フィルムまたは位相差層）
本発明の真偽判定体における位相差を生じさせる効果を有した位相差フィルム２または位相差層６に関し、位相差フィルムは、延伸したフィルムの形態であり、また位相差層は、その構成成分を含有する塗工液により、塗布して形成される塗膜の形態である。位相差フィルム、位相差層のいずれにおいても、つまり成膜された延伸フィルムであっても、塗工された塗膜であっても、それらの構成する材料としては、位相差を生じる材料であれば、限定するものではない。例えば、ネマチック相を形成し得る液晶材料や延伸フィルムが挙げられる。ネマチック相を形成し得る液晶材料としては、重合性液晶材料と重合性の無い高分子液晶材料とを挙げることができる。重合性液晶材料としては、重合性液晶モノマー、重合性液晶オリゴマー、および重合性液晶高分子のいずれかを用いることが可能である。
Hereinafter, the layers and components constituting the authenticity determination body and the medium with the authenticity determination body of the present invention will be described in detail.
(Retardation film or retardation layer)
Regarding the retardation film 2 or the retardation layer 6 having the effect of causing the retardation in the authenticity determination body of the present invention, the retardation film is in the form of a stretched film, and the retardation layer is a constituent component thereof. It is the form of the coating film formed by application | coating with the coating liquid containing this. Regardless of the retardation film or retardation layer, that is, whether it is a stretched film formed or a coated film, the material constituting them may be a material that causes a retardation. For example, it is not limited. For example, a liquid crystal material or a stretched film that can form a nematic phase can be used. Examples of the liquid crystal material capable of forming a nematic phase include a polymerizable liquid crystal material and a non-polymerizable polymer liquid crystal material. As the polymerizable liquid crystal material, any of a polymerizable liquid crystal monomer, a polymerizable liquid crystal oligomer, and a polymerizable liquid crystal polymer can be used.
上記の延伸フィルムは、延伸工程で作製されたプラスチックフィルムである。延伸とは、プラスチックを融点以下ガラス転移点以上の適当な温度で引き延ばしてフィルムを作製する工法であり、その引き延ばす方向によって、一軸延伸、二軸延伸などがある。本発明では、屈折率異方性が存在すればよいので、一軸延伸、二軸延伸のいずれの工法で作製したフィルムでも使用することができる。具体的には、位相差層は、セロハン，セルロース，ポリエステル，ポリカーボネート（ＰＣ），ポリエチレン（ＰＥ），ポリプロピレン（ＰＰ），ポリビニルアルコール（ＰＶＡ），ポリ塩化ビニル（ＰＶＣ），ポリ塩化ビニリデン（ＰＶＤＣ），ポリメチルメタクリレート（ＰＭＭＡ），ポリスチレン（ＰＳ），ポリエチレンテレフタレート（ＰＥＴ），ナイロン等を材料とする延伸フィルムを用いることができる。 The stretched film is a plastic film produced by a stretching process. Stretching is a method for producing a film by stretching a plastic at an appropriate temperature not higher than the melting point and not lower than the glass transition point, and includes uniaxial stretching and biaxial stretching depending on the stretching direction. In the present invention, since it is sufficient that the refractive index anisotropy exists, a film produced by any method of uniaxial stretching and biaxial stretching can be used. Specifically, the retardation layer is made of cellophane, cellulose, polyester, polycarbonate (PC), polyethylene (PE), polypropylene (PP), polyvinyl alcohol (PVA), polyvinyl chloride (PVC), or polyvinylidene chloride (PVDC). , Stretched films made of polymethyl methacrylate (PMMA), polystyrene (PS), polyethylene terephthalate (PET), nylon or the like can be used.
（基材フィルム）
また、本発明の真偽判定体において、基材フィルム５に対して、コレステリック液晶層Ａ（３）、位相差層６、コレステリック液晶層Ｂ（４）の順に積層した形態が挙げられる。（図３参照）その際の基材フィルムとしては、構成する材料としては特に制限されるものではなく、ポリエチレンテレフタレート（ＰＥＴ）、ポリカーボネート、ポリビニルアルコール、ポリスルホン、ポリエチレン、ポリプロピレン、ポリスチレン、ポリアリレート、トリアセチルセルロール（ＴＡＣ）、ジアセチルセルロール、ポリエチレン−エチルビニルアルコールなどのプラスチックを単独あるいは組み合わせて、単層のものや積層したりして用いることができる。基材フィルムの厚さは、０．００５〜５ｍｍ程度が適当である。
(Base film)
Moreover, the authenticity determination body of this invention WHEREIN: The form laminated | stacked on the base film 5 in order of the cholesteric liquid crystal layer A (3), the phase difference layer 6, and the cholesteric liquid crystal layer B (4) is mentioned. (Refer to FIG. 3) The base film in that case is not particularly limited as a constituent material, but is polyethylene terephthalate (PET), polycarbonate, polyvinyl alcohol, polysulfone, polyethylene, polypropylene, polystyrene, polyarylate, trimethyl. Plastics such as acetyl cellulose (TAC), diacetyl cellulose, and polyethylene-ethyl vinyl alcohol can be used alone or in combination, with a single layer or laminated. An appropriate thickness of the base film is about 0.005 to 5 mm.
（コレステリック液晶層）
本発明の真偽判定体におけるコレステリック液晶層は、位相差フィルムまたは位相差層の上下に、コレステリック液晶層Ａと、コレステリック液晶層Ｂを設ける構成であり、コレステリック液晶層Ａと、コレステリック液晶層Ｂとの形成された形状が、互いに異なっている条件を満足すれば、コレステリック液晶層Ａ及びＢが、各々の反射波長が異なるものであってもよく、また、コレステリック液晶層Ａ及びＢが、各々の反射波長が同等であるものであってもよい。また、コレステリック液晶層Ａ及びＢを構成する液晶材料は、同じものであっても、異なる材料であってもよい。いずれにしても、上記の反射波長の条件を満たせばよい。
(Cholesteric liquid crystal layer)
The cholesteric liquid crystal layer in the authenticity determination body of the present invention has a configuration in which a cholesteric liquid crystal layer A and a cholesteric liquid crystal layer B are provided above and below the retardation film or retardation layer. The cholesteric liquid crystal layer A and the cholesteric liquid crystal layer B And the cholesteric liquid crystal layers A and B may have different reflection wavelengths, and the cholesteric liquid crystal layers A and B may each have a different shape from each other. May have the same reflection wavelength. Further, the liquid crystal materials constituting the cholesteric liquid crystal layers A and B may be the same or different materials. In any case, it suffices if the above reflection wavelength condition is satisfied.
コレステリック液晶層は、上記に挙げた位相差フィルムの上、あるいは上記の基材フィルムの上に、高分子コレステリック液晶をインキ化して、グラビア印刷等の凹版印刷、オフセット方式などの平版印刷、凸版印刷、スクリーン印刷等で形成される。位相差フィルムあるいは基材フィルム上に、コレステリック液晶層を積層する側には、必要に応じて配向膜を設けても良く、配向膜は、ポリビニルアルコール樹脂（ＰＶＡ）、ポリイミド樹脂等の一般に配向膜として使用し得るものであれば、いずれを用いて構成したものでもよい。配向膜は、これらの樹脂の溶剤溶液を、プラスチックフィルム基材の表面に適宜な塗布方法により塗布し、乾燥させた後に、布、ブラシ等を用いて摩擦するラビングを行なって形成することができる。 The cholesteric liquid crystal layer is formed on the above retardation film or the above-mentioned base film by converting a polymer cholesteric liquid crystal into an ink, intaglio printing such as gravure printing, lithographic printing such as offset method, letterpress printing, etc. It is formed by screen printing or the like. An alignment film may be provided on the side where the cholesteric liquid crystal layer is laminated on the retardation film or the base film, and the alignment film is generally an alignment film such as polyvinyl alcohol resin (PVA) or polyimide resin. As long as it can be used, any of them may be used. The alignment film can be formed by applying a solvent solution of these resins to the surface of the plastic film substrate by an appropriate application method and drying, followed by rubbing with a cloth, a brush, or the like. .
このように形成されるコレステリック液晶層の厚さは、１μｍ〜２０μｍ程度が望ましい。単位面積当たりの質量では、乾燥時で約１〜２０ｇ／ｍ2程度である。その厚さが少なすぎると、コレステリック液晶特有の円偏光選択性と選択反射性の２つの特性を充分に発揮できなくなり、また厚すぎると液晶の配向が低下し、基材との密着性が低下したり、さらにコスト的にも不利である。コレステリック液晶層は単層で設けるだけでなく、２層以上を積層することも可能である。尚、上記の高分子コレステリック液晶の材料をインキ化したものは、例えばワッカーケミー社のコレステリック液晶「ＨＥＬＩＣＯＮＥ（登録商標）」等で、市販されているものを使用することができる。 The thickness of the cholesteric liquid crystal layer thus formed is desirably about 1 μm to 20 μm. The mass per unit area is about 1 to 20 g / m 2 when dried. If the thickness is too small, the two characteristics of circularly polarized light and selective reflection that are characteristic of cholesteric liquid crystals cannot be fully exhibited. If the thickness is too thick, the orientation of the liquid crystal decreases and the adhesion to the substrate decreases. It is also disadvantageous in terms of cost. The cholesteric liquid crystal layer can be provided not only as a single layer but also as a laminate of two or more layers. In addition, what made the above-mentioned polymer cholesteric liquid crystal into an ink may be a commercially available cholesteric liquid crystal “HELICONE (registered trademark)” manufactured by Wacker Chemie.
本発明で使用される高分子コレステリック液晶とは、液晶分子の配向構造が膜厚方向に螺旋を描くように規則的なねじれを有している。また、高分子コレステリック液晶は、ピッチＰ（液晶分子が３６０°回転するのに必要な膜厚）と、入射光の波長λとがほぼ等しい場合に、選択反射性と円偏光選択性という２つの光学的性質を示すことが知られている。（参考文献；液晶とディスプレイ応用の基礎、コロナ社等） The polymer cholesteric liquid crystal used in the present invention has a regular twist so that the alignment structure of liquid crystal molecules draws a spiral in the film thickness direction. In addition, polymer cholesteric liquid crystal has two properties, selective reflectivity and circular polarization selectivity, when the pitch P (the film thickness necessary for the liquid crystal molecules to rotate 360 °) and the wavelength λ of incident light are substantially equal. It is known to exhibit optical properties. (Reference: Basics of liquid crystal and display applications, Corona, etc.)
選択反射性とは、入射光のうち特定の波長帯域内にある光を強く反射する性質をいう。この選択反射性は、特定の波長帯域内に限定されて発現するため、高分子コレステリック液晶のピッチＰを適切に選択することで、反射光は色純度の高い有彩色となる。その帯域の中心波長をλS、帯域幅をΔλとすれば、これらは光学媒体のピッチＰ（＝λ／ｎm）と平均屈折率ｎm（＝√（（ｎｅ2＋ｎｏ2）／２））によって、下記式（１）、（２）のように決まる。ここで、Δｎは光学媒体の面内の異常光線屈折率ｎeと、常光線屈折率ｎoの差（Δｎ＝ｎe−ｎo）とする。
λS＝ｎm・Ｐ ・・・（１）
Δλ＝Δｎ・Ｐ／ｎm ・・・（２）
Selective reflectivity refers to the property of strongly reflecting light within a specific wavelength band of incident light. Since the selective reflectivity is limited and expressed within a specific wavelength band, the reflected light becomes a chromatic color with high color purity by appropriately selecting the pitch P of the polymer cholesteric liquid crystal. If the center wavelength of the band lambda S, the bandwidth [Delta] [lambda], these optical media pitch P (= λ / nm) and average refractive index n m (= √ ((ne 2 + no 2) / 2)) Is determined by the following equations (1) and (2). Here, [Delta] n is the extraordinary ray refraction index n e in the plane of the optical medium, the difference between the ordinary refractive index n o (Δn = n e -n o).
λ S = n m · P (1)
Δλ = Δn · P / n m (2)
上記式（１）、（２）に示した中心波長λｓおよび波長帯域幅Δλは、コレステリック液晶層への入射光が垂直入射（０°入射、ｏｎ−ａｘｉｓ入射）の場合において定義されるが、入射光が斜め入射（ｏｆｆ−ａｘｉｓ入射）である場合、ピッチＰが見かけ上、減少することから、中心波長λSは短波長側へ移行し、波長帯域幅Δλは減少する。この現象は、λSが短波長側に移行することから、ブルーシフトと呼ばれ、その移行量は入射角に依存するが、目視で観察しても容易に識別可能である。例えば、垂直（０°入射位置）から観察して赤色に呈色する高分子コレステリック液晶の反射色は、視野角を大きくすることにつれ、オレンジ色、黄色、緑色、青緑色、青色と順次変化するように観察される。このように、コレステリック液晶層は観察する角度によって、色が短波長側にシフトし、カラーコピー等で再現することができない特殊な色を示す（変化する）ために、偽造防止には非常に有効なものである。 The center wavelength λs and the wavelength bandwidth Δλ shown in the above equations (1) and (2) are defined when the incident light to the cholesteric liquid crystal layer is vertically incident (0 ° incidence, on-axis incidence). When the incident light is obliquely incident (off-axis incident), the pitch P apparently decreases, so that the center wavelength λ S shifts to the short wavelength side, and the wavelength bandwidth Δλ decreases. This phenomenon is called blue shift because λ S shifts to the short wavelength side, and the shift amount depends on the incident angle, but can be easily identified by visual observation. For example, the reflected color of a polymer cholesteric liquid crystal that is colored red when viewed from the vertical (0 ° incident position) changes in order of orange, yellow, green, blue-green, and blue as the viewing angle increases. Observe as. In this way, the cholesteric liquid crystal layer shifts to the short wavelength side depending on the viewing angle, and shows (changes) a special color that cannot be reproduced by color copying. It is a thing.
コレステリック液晶層は、特有の反射色を示すことから、その液晶層を用いた真偽判定体に対し、目視でも容易に真偽判定を行うことができ、さらにその円偏光選択性を有しているため、左円偏光か右円偏光のどちらかを選択的に反射する。尚、円偏光選択性とは、特定の回転方向の円偏光だけを透過し、これと回転方向が反対の円偏光を反射する性質をいう。入射光のうち高分子コレステリック液晶の配向構造のねじれ方向と同方向の円偏光成分は反射され、その反射光の回転方向も同一方向となるのに対し、逆方向に回転する円偏光成分は透過する点が高分子コレステリック液晶に特有な特異な性質である。左ねじれ構造を有する高分子コレステリック液晶の場合、左円偏光を反射し、かつ反射光は左円偏光のままであり、右円偏光は透過することになる。また、右ねじれ構造を有する高分子コレステリック液晶の場合、右円偏光を反射し、かつ反射光は右円偏光のままであり、左円偏光は透過することになる。 Since the cholesteric liquid crystal layer exhibits a unique reflection color, it is possible to easily determine the authenticity of the authenticity determination body using the liquid crystal layer by visual inspection, and to have the circular polarization selectivity. Therefore, either left circularly polarized light or right circularly polarized light is selectively reflected. The circularly polarized light selectivity means a property of transmitting only circularly polarized light in a specific rotation direction and reflecting circularly polarized light having the opposite rotation direction. Of the incident light, the circularly polarized light component in the same direction as the twist direction of the alignment structure of the polymer cholesteric liquid crystal is reflected and the rotation direction of the reflected light is also the same direction, while the circularly polarized light component rotating in the opposite direction is transmitted. This is a unique property peculiar to polymer cholesteric liquid crystals. In the case of the polymer cholesteric liquid crystal having the left twisted structure, the left circularly polarized light is reflected, the reflected light remains as the left circularly polarized light, and the right circularly polarized light is transmitted. In the case of a polymer cholesteric liquid crystal having a right-handed twisted structure, right circularly polarized light is reflected, and the reflected light remains right circularly polarized light, and left circularly polarized light is transmitted.
本発明の真偽判定体におけるコレステリック液晶層に使用される液晶材料は、例えば側鎖に液晶形成基を有するポリアクリレート、ポリメタクリレート、ポリシロキサン、ポリマロネート等の側鎖型ポリマー、主鎖に液晶形成基をもつポリエステル、ポリエステルアミド、ポリカーボネート、ポリアミド、ポリイミドなどの主鎖型ポリマーを挙げることができる。 The liquid crystal material used for the cholesteric liquid crystal layer in the authenticity determination body of the present invention is, for example, a side chain type polymer such as polyacrylate, polymethacrylate, polysiloxane, polymalonate having a liquid crystal forming group in the side chain, and liquid crystal formation in the main chain. Mention may be made of main chain polymers such as polyester, polyesteramide, polycarbonate, polyamide and polyimide having groups.
配向状態にあるコレステリック液晶層は、入射した光のうち、左円偏光もしくは右円偏光のいずれか一方のみを反射する性質を有している。また、見る角度により、色相が異なって見える効果も有する。したがって、このコレステリック液晶層は光を選択して反射する層であり、言い換えれば、光選択反射層である。この光選択反射層はコレステリック液晶の溶剤溶液を各種の印刷法によって適用し、乾燥させることにより形成することができ、あるいは、このとき、重合性のコレステリック液晶を用いて紫外線重合性組成物を調製し、得られた紫外線重合性組成物を各種の印刷法によって適用し、乾燥後に、紫外線を照射して重合させて形成することもできる。コレステリック液晶層からなる光選択反射層は、上記の見る角度により、色相が異なって見えることを除けば、透視性を有しており、その意味で透明性を有するものである。 The cholesteric liquid crystal layer in the aligned state has a property of reflecting only one of left circularly polarized light and right circularly polarized light in incident light. Also, it has an effect that the hue looks different depending on the viewing angle. Therefore, the cholesteric liquid crystal layer is a layer that selectively reflects light, in other words, a light selective reflection layer. This light selective reflection layer can be formed by applying a solvent solution of cholesteric liquid crystal by various printing methods and drying, or at this time, preparing an ultraviolet polymerizable composition using polymerizable cholesteric liquid crystal In addition, the obtained ultraviolet polymerizable composition can be applied by various printing methods, dried, and then irradiated with ultraviolet rays to be polymerized. The light selective reflection layer made of a cholesteric liquid crystal layer has transparency, except that the hue looks different depending on the viewing angle, and in that sense, has transparency.
配向状態を実現するには、延伸したプラスチックシートの表面にコレステリック液晶の溶剤溶液もしくは重合性のコレステリック液晶を用いて調製した紫外線重合性組成物を適用するか、もしくは対象物の表面に配向膜を形成してからコレステリック液晶の溶剤溶液もしくは重合性のコレステリック液晶を用いて調製した紫外線重合性組成物を適用すればよい。光選択反射層を二層以上設けるときは、層の厚みや素材のらせんピッチ等を異なるように構成し、より複雑な光学特性を付与することができる。あるいは光選択反射層はパターン状に形成することもできるので、一方を一様な層として形成し、他方をパターン状に形成してもよい。 In order to realize the alignment state, an ultraviolet polymerizable composition prepared using a solvent solution of cholesteric liquid crystal or polymerizable cholesteric liquid crystal is applied to the surface of the stretched plastic sheet, or an alignment film is formed on the surface of the object. After the formation, an ultraviolet polymerizable composition prepared by using a cholesteric liquid crystal solvent solution or a polymerizable cholesteric liquid crystal may be applied. When two or more light selective reflection layers are provided, the thickness of the layers, the helical pitch of the material, and the like can be configured differently to give more complicated optical characteristics. Alternatively, since the light selective reflection layer can be formed in a pattern, one may be formed as a uniform layer and the other may be formed in a pattern.
重合性のコレステリック液晶材料としては、下記の一般式（１）で表される化合物や、式（２）〜式（１０）で示す化合物を例示することができる。これら例示したものはモノマーであるが、オリゴマーやポリマーであってもよい。一般式（１）で表される化合物を２種類以上併用することや、一般式（１）で表される化合物および式（２）〜式（１０）で示す化合物の中から選択して２種類以上併用してもよい。
上記の一般式（１）において、Ｒ１およびＲ２は、それぞれ水素もしくはメチル基を示し、Ｘは塩素もしくはメチル基であることが好ましい。また一般式（１）で表される化合物のスペーサーであるアルキレン基の鎖長を示すａおよびｂは、２〜９の範囲であることが液晶性を発現させる上で好ましい。 In the above general formula (1), R1 and R2 each represent hydrogen or a methyl group, and X is preferably a chlorine or methyl group. Moreover, it is preferable when a and b which show the chain length of the alkylene group which is a spacer of the compound represented by General formula (1) are the range of 2-9 to express liquid crystallinity.
上記の液晶性化合物には、下記式（１１）〜式（１３）で表されるカイラル剤を配合してもよい。
上記の式（１１）において、Ｒ３は、水素もしくはメチル基を示す。上記式（１１）および式（１２）において、Ｙは、下記式（１４）および（１５）で示す式（ｉ）〜式（ｘｘｉｖ）のうちのいずれかである。また、上記式（１１）〜式（１３）において、アルキレン基の鎖長を示すｃ、ｄおよびｅは、２〜９の範囲であることが液晶性を発現させる上で好ましい。
上記のコレステリック液晶材料およびカイラル剤は、必要に応じて紫外線重合開始剤、さらに溶剤や希釈剤と共に、一例として、コレステリック液晶材料：カイラル剤：紫外線重合開始剤＝１００：５：５（質量基準）の配合比で混合し、混合して得られた粉体をトルエン等の溶剤を用いて溶解し、３０質量％程度の濃度の塗布用溶液を調製するとよい。なお、配合比は、使用するコレステリック液晶材料、カイラル剤、もしくは紫外線重合開始剤等の種類、塗布方式もしくは塗布機、または得たい塗布量によって適宜に定めることができる。 The above-mentioned cholesteric liquid crystal material and chiral agent include, as an example, an ultraviolet polymerization initiator, a solvent and a diluent, as an example. It is preferable to prepare a coating solution having a concentration of about 30% by mass by mixing at a blending ratio of 2 and dissolving the powder obtained by mixing using a solvent such as toluene. The blending ratio can be appropriately determined depending on the type of cholesteric liquid crystal material, chiral agent, or ultraviolet polymerization initiator to be used, the coating method or coating machine, or the desired coating amount.
コレステリック液晶層は、左回り偏光または右回り偏光のどちらを反射するタイプでもよく、同方向でも複数の異なる反射色を示す液晶材料を使用してもよい。また、コレステリック液晶層を基材上に、形成する方法としては、上記の液晶材料を、例えば分子配向させ、次に紫外線照射し、架橋させてから、粉砕して顔料化させた液晶顔料をビヒクル中に分散させて、つまり液晶材料をインキ化して、上記に説明したような公知の印刷方式が挙げられる。 The cholesteric liquid crystal layer may be of a type that reflects either left-handed polarized light or right-handed polarized light, and may use a liquid crystal material that exhibits a plurality of different reflected colors in the same direction. Further, as a method of forming a cholesteric liquid crystal layer on a substrate, for example, a liquid crystal pigment obtained by aligning the liquid crystal material described above with, for example, molecular orientation, then irradiating with ultraviolet rays, crosslinking, and then pulverizing and pigmenting the vehicle is used. A known printing method as described above may be used by dispersing in, that is, converting the liquid crystal material into an ink.
また、光選択反射層として、上記のコレステリック液晶層だけでなく、種々の素材を用いて構成することができ、例えば、見る角度によって色が変化する顔料を用いる、蒸着薄膜を用いる、もしくは二色性色素を用いることにより構成することができる。見る角度によって色が変化する顔料としては、高屈折率の酸化ケイ素、酸化チタン、酸化鉄などの層と、低屈折率のマイカ等の層を積層したパール顔料を例示することができ、具体的には、（株）資生堂製の商品名；インフィニットカラーや、メルク社（独国）製の商品名；イリオジン等が入手可能である。蒸着薄膜はアルミニウム等の金属やそのほかの素材を気相法により薄膜として形成したもので、水面に浮かんだ油の薄膜のようないわゆる干渉色を示すものである。二色性色素は、分子軸の方向によって光の吸収性を相違する長鎖色素分子からなり、例えば、色素分子の分子軸の方向に対して法線方向の光成分は吸収性がほぼなく光を透過するのに対して、分子軸の方向に対して平行方向の光成分は吸収性を有し、光を透過しない性質を有するもので、アントラキノン系、アゾ系、もしくはビスアゾ系の色素を例示することができる。上記のうち、見る角度によって色が変化する顔料もしくは二色性色素は適宜なバインダ樹脂中に分散し、溶剤で希釈して塗布用組成物としたものをシルクスクリーン印刷、グラビア印刷、もしくは公知のコーティング法によって対象表面に適用すればよい。 Further, as the light selective reflection layer, not only the above cholesteric liquid crystal layer but also various materials can be used. For example, a pigment whose color changes depending on the viewing angle, a vapor deposition thin film, or two colors are used. It can comprise by using a sex pigment. Examples of pigments whose color changes depending on the viewing angle include pearl pigments in which layers of high refractive index silicon oxide, titanium oxide, iron oxide, and the like, and layers of low refractive index mica, etc. are laminated. Are available from Shiseido Co., Ltd. under the trade name; Infinite Color and Merck (Germany) trade name; Iriodin. The deposited thin film is formed by forming a metal such as aluminum or other material as a thin film by a vapor phase method, and exhibits a so-called interference color like an oil thin film floating on the water surface. A dichroic dye is composed of long-chain dye molecules that have different light absorption depending on the direction of the molecular axis. For example, the light component in the normal direction relative to the direction of the molecular axis of the dye molecule has almost no absorption. The light component in the direction parallel to the direction of the molecular axis has an absorptive property and does not transmit light, and examples include anthraquinone, azo, or bisazo dyes. can do. Among the above, pigments or dichroic dyes that change color depending on the viewing angle are dispersed in an appropriate binder resin, diluted with a solvent to form a coating composition, silk screen printing, gravure printing, or a known one What is necessary is just to apply to a target surface by the coating method.
（ホログラム形成層）
本発明の真偽判定体では、偽造防止性をより高めるために、ホログラム形成層をコレステリック液晶層と組み合わせて使用することができる。位相差フィルムの上、あるいは基材フィルムの上に形成されたコレステリック液晶層の上、または。位相差フィルム、あるいは基材フィルムとコレステリック液晶層との間に、ホログラム形成層を設けることができる。
(Hologram forming layer)
In the authenticity determination body of the present invention, the hologram forming layer can be used in combination with the cholesteric liquid crystal layer in order to further improve the forgery prevention property. On a cholesteric liquid crystal layer formed on a retardation film or a substrate film, or. A hologram forming layer can be provided between the retardation film or the base film and the cholesteric liquid crystal layer.
ホログラム形成層は、下面にホログラムの微細凹凸が形成されたものであるが、層自体は、ホログラムの微細凹凸の形成が可能な種々の素材を用いて構成し得るものである。例えば、ホログラム形成層４は、ポリ塩化ビニル、アクリル樹脂（例、ＰＭＭＡ）、ポリスチレン、ポリカーボネートなどの透明な熱可塑性樹脂で構成することができる。あるいは、不飽和ポリエステル、メラミン、エポキシ、ポリエステル（メタ）アクリレート、ウレタン（メタ）アクリレート、エポキシ（メタ）アクリレート、ポリエーテル（メタ）アクリレート、ポリオール（メタ）アクリレート、メラミン（メタ）アクリレート、トリアジン系アクリレートなどの透明熱硬化性樹脂で構成することができる。さらには、上記の熱可塑性樹脂と上記の熱硬化性樹脂とを混合して使用し、更には、ラジカル重合性不飽和基を有する熱成形性物質、或いは、これらにラジカル重合性不飽和単量体を加え電離放射線硬化性としたものなどを使用して構成することができる。 The hologram forming layer is one in which fine hologram irregularities are formed on the lower surface, but the layer itself can be formed using various materials capable of forming the hologram minute irregularities. For example, the hologram forming layer 4 can be made of a transparent thermoplastic resin such as polyvinyl chloride, acrylic resin (eg, PMMA), polystyrene, or polycarbonate. Or unsaturated polyester, melamine, epoxy, polyester (meth) acrylate, urethane (meth) acrylate, epoxy (meth) acrylate, polyether (meth) acrylate, polyol (meth) acrylate, melamine (meth) acrylate, triazine acrylate Or a transparent thermosetting resin such as Further, the thermoplastic resin and the thermosetting resin are mixed and used, and further, a thermoformable substance having a radical polymerizable unsaturated group, or a radical polymerizable unsaturated monomer thereof. It can be constructed using a material that is ionized radiation curable by adding a body.
ホログラム形成層へのホログラムの微細凹凸の形成は、回折格子やホログラムの干渉縞が凹凸の形で記録された原版をプレス型として用い、基材に上記の樹脂を塗布用組成物として調製したものを、グラビアコート法、ロールコート法、バーコート法などの手段で塗布して、塗膜を形成し、その上に前記原版を重ねて加熱ロールなどの適宜手段により、両者を加熱圧着する等により、行なうことができる。また、フォトポリマーを用いる場合は、基材上に、フォトポリマーを同様に塗布した後、前記原版を重ねてレーザー光を照射することにより複製してもよい。 Formation of fine unevenness of hologram on hologram forming layer was prepared by using the original resin on which diffraction gratings and interference fringes of hologram were recorded in the form of unevenness as a press mold, and preparing the above resin as a coating composition on the substrate Is applied by means such as a gravure coating method, a roll coating method, a bar coating method, etc. to form a coating film, and the original plate is stacked thereon, and the both are heated and pressure-bonded by an appropriate means such as a heating roll. Can be done. In the case of using a photopolymer, the photopolymer may be similarly applied on a base material, and then the original plate may be overlapped to be irradiated with a laser beam for duplication.
またホログラムの微細凹凸の回折効率を高めるために、反射性金属層を設けることができる。その反射性金属層は、Ｃｒ、Ｆｅ、Ｃｏ、Ｎｉ、Ｃｕ、Ａｇ、Ａｕ、Ｇｅ、Ａｌ、Ｍｇ、Ｓｂ、Ｐｂ、Ｃｄ、Ｂｉ、Ｓｎ、Ｓｅ、Ｉｎ、Ｇａ、もしくはＲｂ等の金属を用いて構成することができ、またはこれらの金属の酸化物、もしくはそれらの窒化物を単独で、もしくは組合わせて構成することもできるので、便宜上、金属の酸化物、もしくはそれらの窒化物も金属の範囲として含めるものとする。上記のうちでも、Ａｌ、Ｓｎ、Ｃｒ、Ｎｉ、Ｃｕ、もしくはＡｕ等が特に好ましい。反射性金属層は、真空蒸着法、スパッタリング法、イオンプレーティング法などの薄膜形成法によって形成することが好ましいが、メタリック顔料を含有するメタリックインクを用いて印刷することによって形成してもよい。また、透明タイプのホログラムを形成する薄膜はホログラム効果を発現できる光透過性のものであれば、いかなる材料のものも使用できる。たとえば、ホログラム形成層(光硬化性樹脂層)の樹脂と屈折率の異なる透明材料がある。この場合の屈折率はホログラム形成層の樹脂の屈折率よりも大きくても、小さくても良いが、屈折率の差は０．１以上が望ましく、より好ましくは０．５以上であり、１．０以上が最適である。また、上記以外では２０ｎｍ以下の金属反射層がある。好適に使用される透明タイプ反射層としては酸化チタン（ＴｉＯ2）、硫化亜鉛（ＺｎＳ）、Ｃｕ・Ａｌ複合金属酸化物等が挙げられる。 A reflective metal layer can be provided in order to increase the diffraction efficiency of the fine irregularities of the hologram. The reflective metal layer uses a metal such as Cr, Fe, Co, Ni, Cu, Ag, Au, Ge, Al, Mg, Sb, Pb, Cd, Bi, Sn, Se, In, Ga, or Rb. For convenience, the metal oxides or their nitrides can also be composed of metal oxides or their nitrides alone or in combination. It shall be included as a range. Among the above, Al, Sn, Cr, Ni, Cu, Au, or the like is particularly preferable. The reflective metal layer is preferably formed by a thin film forming method such as a vacuum deposition method, a sputtering method, or an ion plating method, but may be formed by printing using a metallic ink containing a metallic pigment. Moreover, the thin film which forms a transparent type hologram can use what kind of material as long as it is a light-transmitting thing which can express a hologram effect. For example, there is a transparent material having a refractive index different from that of the resin of the hologram forming layer (photocurable resin layer). The refractive index in this case may be larger or smaller than the refractive index of the resin of the hologram forming layer, but the difference in refractive index is desirably 0.1 or more, more preferably 0.5 or more. Zero or more is optimal. In addition to the above, there is a metal reflection layer of 20 nm or less. Examples of the transparent type reflective layer that can be suitably used include titanium oxide (TiO 2 ), zinc sulfide (ZnS), and Cu · Al composite metal oxide.
（真偽判定体を粘着剤を介して、媒体に貼着させる方法）
本発明の真偽判定体は、粘着剤を介して、真偽判定の対象となる種々の物品、すなわち媒体に貼着させることができる。図１、２に示すような真偽判定体では、一方のコレステリック液晶層の上に、つまり表面に粘着剤層を積層させ、さらにその粘着剤層の上に離型シートを積層させることができる。また、図３に示すような真偽判定体では、基材フィルムのコレステリック液晶層の設けられていない表面に、粘着剤層を積層させ、さらにその粘着剤層の上に離型シートを積層させることができる。このような形態は、いわゆるラベルと呼ばれるもので、離型シートを剥がして、粘着剤層により任意の物品に、真偽判定体（ラベル）を貼り付けることができる。粘着剤層は、例えば、アクリル系樹脂、天然ゴム系樹脂、合成ゴム系樹脂、シリコーン系樹脂等からなる水性タイプまたは溶剤系タイプの塗工液を用いて、形成できる。塗工方法はロールコーター法、リバースコーター法、ナイフコーター法、コンマコーター法、グラビアコーター法などの一般的な方法で塗工する。その塗工量として０．１〜５０ｇ／ｍ2（乾燥状態）が好ましい。
(Method of sticking the authenticity judgment body to the medium through the adhesive)
The authenticity determination body of the present invention can be attached to various articles, that is, media that are the targets of authenticity determination, via an adhesive. In the authenticity determination body as shown in FIGS. 1 and 2, a pressure-sensitive adhesive layer can be laminated on one cholesteric liquid crystal layer, that is, a release sheet can be laminated on the pressure-sensitive adhesive layer. . Moreover, in the authenticity determination body as shown in FIG. 3, an adhesive layer is laminated on the surface of the base film on which the cholesteric liquid crystal layer is not provided, and a release sheet is further laminated on the adhesive layer. be able to. Such a form is called a so-called label, and the release sheet can be peeled off, and an authenticity determination body (label) can be attached to an arbitrary article with an adhesive layer. The pressure-sensitive adhesive layer can be formed using, for example, an aqueous type or solvent type coating solution made of an acrylic resin, a natural rubber resin, a synthetic rubber resin, a silicone resin, or the like. Coating is performed by a general method such as a roll coater method, a reverse coater method, a knife coater method, a comma coater method, or a gravure coater method. The coating amount is preferably 0.1 to 50 g / m 2 (dry state).
離型シートは、ラベルを物品に貼り付ける迄の間、粘着剤層を保護する為に積層されるものであり、使用時には引き剥がされる。使用する離型シートは一般的なものが利用でき、特に限定されない。例えば、上質紙、コート紙、キャストコート紙、アルミニウム箔／紙、樹脂含浸紙、合成紙などの紙ベース基材やポリエステル樹脂、ポリプロピレン樹脂、塩化ビニル樹脂、発泡ポリエステル樹脂、発泡ポリプロピレン樹脂などの高分子樹脂フィルムベース基材の一方の面に剥離剤としてシリコーン系樹脂を塗工したもの等が利用できる。紙ベースの場合、紙の坪量は３０〜３００ｇ／ｍ2のもの、フィルムベースの場合は厚みが１０〜３００μｍの範囲のフィルムが使用できる。 The release sheet is laminated to protect the pressure-sensitive adhesive layer until the label is attached to the article, and is peeled off during use. A general release sheet can be used and is not particularly limited. For example, high-quality paper, coated paper, cast coated paper, aluminum foil / paper, resin-impregnated paper, synthetic paper, and other paper base materials, polyester resin, polypropylene resin, vinyl chloride resin, foamed polyester resin, foamed polypropylene resin, etc. A material obtained by coating a silicone resin as a release agent on one surface of the molecular resin film base substrate can be used. In the case of a paper base, a paper having a basis weight of 30 to 300 g / m 2 can be used, and in the case of a film base, a film having a thickness in the range of 10 to 300 μm can be used.
（真偽判定体を、媒体に転写して付着させる方法）
真偽判定の対象となる種々の物品である媒体に対して、真偽判定体を転写して、真偽判定体付き媒体を得る方法を、以下に説明する。基材に真偽判定体を転写する場合、以下の転写方法が挙げられる。
（１）位相差フィルムまたは位相差層の上下に、コレステリック液晶層Ａ、Ｂを設けた本発明の真偽判定体である転写箔を、熱や圧を利用して、転写箔の全体を媒体に転写する。
（２）基材フィルム上にコレステリック液晶層Ａ（３）、位相差層６、コレステリック液晶層Ｂ（４）を順次設けた転写フィルムを用いて、熱や圧力を利用して、媒体にコレステリック液晶層Ａ（３）、位相差層６、コレステリック液晶層Ｂ（４）からなる３層を転写し、転写フィルムの基材フィルムをコレステリック液晶層Ａ（３）から剥がす。
(Method of transferring the authenticity judgment material to the medium and attaching it)
A method for obtaining a medium with authenticity determination body by transferring the authenticity determination body to a medium that is a variety of articles that are subject to authenticity determination will be described below. When the authenticity determination body is transferred to the base material, the following transfer method is exemplified.
(1) The transfer foil which is the authenticity determination body of the present invention in which the cholesteric liquid crystal layers A and B are provided on the upper and lower sides of the retardation film or retardation layer, and the entire transfer foil is used as a medium by utilizing heat and pressure. Transcript to.
(2) Using a transfer film in which a cholesteric liquid crystal layer A (3), a retardation layer 6, and a cholesteric liquid crystal layer B (4) are sequentially provided on a base film, using heat and pressure, a cholesteric liquid crystal is used as a medium. Three layers comprising the layer A (3), the retardation layer 6 and the cholesteric liquid crystal layer B (4) are transferred, and the base film of the transfer film is peeled off from the cholesteric liquid crystal layer A (3).
（真偽判定体を、媒体にラミネートして付着させる方法）
真偽判定の対象となる種々の物品である媒体に対して、真偽判定体をラミネートして、真偽判定体付き媒体を得る方法を、以下に説明する。図１、２に示すような真偽判定体では、一方のコレステリック液晶層と、媒体であるフィルムとが接する向きで、接着剤を介して、重ね合わせて、圧力のみ、あるいは熱及び圧力により、真偽判定体とフィルムの媒体をラミネートする。また、図３に示すような真偽判定体では、基材フィルムのコレステリック液晶層の設けられていない表面と、媒体であるフィルムとが接する向きで、接着剤を介して、重ね合わせて、圧力のみ、あるいは熱及び圧力により、真偽判定体とフィルムの媒体をラミネートする。尚、その接着層を構成する接着剤が、感圧接着剤であれば、圧力のみ、またその接着剤が、感熱接着剤であれば、熱及び圧力をかけて接着させる。
(Method of laminating and attaching the authenticity judgment body to the medium)
A method for obtaining a medium with a true / false determining body by laminating a true / false determining body on a medium, which is a variety of articles that are subject to authenticity determination, will be described below. In the authenticity judgment body as shown in FIGS. 1 and 2, in a direction in which one cholesteric liquid crystal layer and the film as a medium are in contact with each other, they are overlapped with an adhesive, only by pressure, or by heat and pressure. Laminate authenticity and film media. Further, in the authenticity determination body as shown in FIG. 3, the surface of the base film on which the cholesteric liquid crystal layer is not provided and the film as the medium are in contact with each other through an adhesive, and pressure is applied. Laminate the authenticity and the film medium only by heat or pressure. If the adhesive constituting the adhesive layer is a pressure sensitive adhesive, only the pressure is applied. If the adhesive is a heat sensitive adhesive, the adhesive is applied with heat and pressure.
（真偽判定体を基紙に、スレッド状に抄き込む方法）
真偽判定の対象となる紙である媒体に対して、真偽判定体をスレッド状に抄き込む方法を、以下に説明する。
この媒体となる基紙８は、針葉樹晒クラフトパルプ（ＮＢＫＰ）、広葉樹晒クラフトパルプ（ＬＢＫＰ）、針葉樹晒サルファイトパルプ（ＮＢＳＰ）等の木材パルプや麻、綿、藁を原料とした非木材パルプ等を適宜混合して叩解して、主剤を用意し、これに填料、乾燥紙力増強剤、湿潤紙力増強剤、サイズ剤、定着剤、歩留り向上剤、濾水性向上剤、消泡剤、染料、着色顔料、蛍光剤等の助剤などを適宜添加した原料を用いて、長網抄紙機、円網抄紙機等の公知の抄紙機を使用して抄紙される。基紙の厚さは、０．０２〜５ｍｍ程度が適当である。
(Method of embedding the authenticity judgment body into a thread on a base paper)
A method for embedding a true / false determination object in a thread form on a medium that is a paper to be subjected to true / false determination will be described below.
The base paper 8 used as this medium is wood pulp such as softwood bleached kraft pulp (NBKP), hardwood bleached kraft pulp (LBKP), softwood bleached sulfite pulp (NBSP), and non-wood pulp made from hemp, cotton and straw. Etc. are mixed appropriately and beaten to prepare a main agent, and a filler, a dry paper strength enhancer, a wet paper strength enhancer, a sizing agent, a fixing agent, a yield improver, a drainage improver, an antifoaming agent, Paper making is performed using a known paper machine such as a long net paper machine or a circular net paper machine using raw materials to which auxiliary agents such as dyes, coloring pigments, and fluorescent agents are appropriately added. A suitable thickness of the base paper is about 0.02 to 5 mm.
上記の基紙に、本発明の真偽判定体であるスレッドを抄き込む方法の一つの実施形態を、以下に説明する。二槽のシリンダーバットを備えた円網抄紙機の、一槽目の円網シリンダーの同一円周表面上に予め所定サイズの形のテープを一定間隔で貼り付けて網目を塞いでおき、第一紙層として、一定間隔で、所定サイズの穴が空いた紙層（第一紙層）を形成する。二槽目の円網シリンダーには、上記のような細工を施さず、無地の第二紙層を形成する。 One embodiment of a method for embedding a thread, which is the authenticity determination body of the present invention, in the above base paper will be described below. On a circular paper machine equipped with two tank bats, a predetermined size of tape is affixed on the same circumferential surface of the first cylinder cylinder, and the mesh is closed. As a paper layer, a paper layer (first paper layer) having holes of a predetermined size is formed at regular intervals. The second tank circular mesh cylinder is not subjected to the above-described work, and a plain second paper layer is formed.
また、スレッドの巻き出し装置を第一槽目と第二槽目の円網シリンダー間に設置して、スレッドが第一紙層の穴と重なる位置に、挿入されるようにする。この際、第一紙層と第二紙層が積層された状態で、第一紙層の穴の位置にスレッドがコレステリック液晶層が観察できるようにしておく。そして、マシンカレンダー処理や、スーパーカレンダー処理で表面平滑処理を施して、真偽判定体付きラベルを製造できる。この場合は、スレッドが片面で露出部と被覆部が繰り返し形成された図５に示すようなタイプの真偽判定体付き媒体が得られる。尚、上記の一槽目の円網シリンダーの円周表面上に、テープを連続的に貼り付けて網目を塞いでおけば、連続したストライプ形状の露出部を有したスレッドを基紙に抄き込むことも可能である。 Also, a thread unwinding device is installed between the first and second tank cylinders so that the thread is inserted at a position overlapping the hole in the first paper layer. At this time, in a state where the first paper layer and the second paper layer are laminated, a cholesteric liquid crystal layer can be observed with a thread at the position of the hole in the first paper layer. And a label with a true / false judgment object can be manufactured by performing a surface smoothing process by a machine calendar process or a super calendar process. In this case, a medium with authenticity determination body of the type shown in FIG. 5 in which the exposed portion and the covering portion are repeatedly formed on one side of the thread is obtained. In addition, if the tape is continuously stuck on the circumferential surface of the circular mesh cylinder of the first tank and the mesh is closed, a thread having a continuous stripe-shaped exposed portion is made on the base paper. Can be included.
本発明の真偽判定体付き媒体は、真正性を識別する必要性のある種々の物品に貼り付ける等により適用すると価値が高いものである。このような真正性を識別する必要性のある物品としては様々なものがあり、必要とされる真正性および識別性のレベルも一定ではないが、次のようなものを例示することができる。 The medium with authenticity determination body of the present invention is highly valuable when applied to various articles that need to identify authenticity. There are various types of articles that need to identify authenticity, and the level of authenticity and distinguishability required is not constant, but the following can be exemplified.
真正性を識別する必要性のある種々の物品としては、保持者の本人確認（ＩＤ）用であるＩＤ証、金券類、純正品、ブランドが著名な高級ブランド品等がある。ＩＤ証とは、例えば、パスポート、運転免許証、保険証、図書カード（図書館の貸出し用カード）等である。金券とは、例えば、商品券、ギフト券等の有価証券、プリペイドカード等である。純正品とは、種々の機器類に用いるための部品や消耗品等であって、純正である認証の必要なものであり、物品としては、電子機器、電気機器、コンピュータ製品、プリンタ等に用いる消耗品、医薬品、化学薬品等がある。高級ブランド品としては、著名なブランドの高価な商品、例えば、時計、衣類、バッグ、宝飾品、スポーツ用品、化粧品がある。さらに、コンピュータソフト、音楽ソフトもしくは映像ソフトが記憶された媒体類も真正性を識別する必要性のある種々の物品として挙げることができる。 Examples of various articles that need to identify authenticity include ID certificates for identification (ID) of holders, cash vouchers, genuine products, and high-end brand products with prominent brands. The ID card is, for example, a passport, a driver's license, an insurance card, a book card (library lending card), or the like. A cash voucher is, for example, securities such as gift certificates or gift certificates, prepaid cards, and the like. Genuine products are parts, consumables, etc. for use in various devices and require genuine certification. Articles are used for electronic devices, electrical devices, computer products, printers, etc. Consumables, pharmaceuticals, chemicals, etc. High-end brand products include expensive products of famous brands such as watches, clothing, bags, jewelry, sports equipment, and cosmetics. Furthermore, media storing computer software, music software or video software can also be cited as various articles that require authenticity identification.
したがって、本発明の真偽判定体付き媒体は、上記のような物品そのもの、もしくは、それら物品のケースであってもよい。あるいは、上記の物品に荷札として、くくりつける等により適用することもできる。 Therefore, the medium with authenticity determination body of the present invention may be an article itself as described above or a case of these articles. Alternatively, it can be applied as a tag to the above-mentioned article.
次に実施例を挙げて、本発明を更に具体的に説明する。以下、特に断りのない限り、部又は％は質量基準である。 Next, the present invention will be described more specifically with reference to examples. Hereinafter, unless otherwise specified, parts or% is based on mass.
（実施例１）
厚さ１００μｍのポリカーボネート樹脂を一軸延伸配向させてできたフィルムを位相差フィルムとし、該位相差フィルムの一方の面に、右円偏光性をもつコレステリック液晶層インキを用いて、グラビア印刷法により、パターンで印刷し、印刷直後に紫外線を照射して、乾燥時で厚さ１０ｇ／ｍ2のコレステリック液晶層Ａを形成した。また、上記位相差フィルムの他方の面に、上記で使用した右円偏光性をもつコレステリック液晶層インキと同じインキ（反射波長が同じである）を用いて、スクリーン印刷法により、位相差フィルムの全面に、ベタ状に印刷し、印刷直後に紫外線を照射して、乾燥時で厚さ１０ｇ／ｍ2のコレステリック液晶層Ｂを形成し、図１に示すような真偽判定体を作製した。
Example 1
Using a cholesteric liquid crystal layer ink having right circular polarization on one surface of the retardation film as a retardation film, a film formed by uniaxially stretching and orientation of a polycarbonate resin having a thickness of 100 μm, by a gravure printing method, Printing was performed in a pattern, and ultraviolet rays were irradiated immediately after printing to form a cholesteric liquid crystal layer A having a thickness of 10 g / m 2 when dried. Further, on the other surface of the retardation film, using the same ink (the same reflection wavelength) as the cholesteric liquid crystal layer ink having the right circular polarization used in the above, by screen printing, Printed in a solid form on the entire surface, and irradiated with ultraviolet rays immediately after printing to form a cholesteric liquid crystal layer B having a thickness of 10 g / m 2 at the time of drying, to produce a true / false judgment body as shown in FIG.
この得られた真偽判定体の全面ベタ印刷面（コレステリック液晶層Ｂ）から、右円偏光板を通じて観察すると、全面ベタの色が明瞭に見え、左円偏光板を通じて観察すると、全面ベタ印刷の色は見えず、パターン印刷の色が確認できた。 From the entire solid printing surface (cholesteric liquid crystal layer B) of the obtained authenticity determination body, the color of the entire solid surface is clearly seen when observed through the right circular polarizing plate. The color was not visible, and the pattern printing color was confirmed.
（実施例２）
実施例１で作製した真偽判定体のパターン印刷面（コレステリック液晶層Ａ）の上に、アクリル系樹脂からなる強粘着用粘着剤を用いて、乾燥時の厚さ３０ｇ／ｍ2になるように、グラビア印刷により、粘着剤層を形成し、さらに、その粘着剤層の上に、離型シートとして、上質紙ベースでシリコーン樹脂の塗工がされた市販の坪量９０ｇ／ｍ2の剥離紙を貼り合せて、さらに抜き加工を行なって、ラベルを作製した。
(Example 2)
On the pattern printing surface (cholesteric liquid crystal layer A) of the authenticity judgment body prepared in Example 1, a strong adhesive pressure sensitive adhesive made of an acrylic resin is used so that the thickness when dried is 30 g / m 2. In addition, a pressure-sensitive adhesive layer is formed by gravure printing, and on the pressure-sensitive adhesive layer, as a release sheet, a silicone resin is coated on a high-quality paper base with a grammage of 90 g / m 2 on the market. Paper was pasted and further punched to produce a label.
この得られたラベルは、真偽判定の対象となる種々の物品、つまり媒体に、剥離紙を剥がして、粘着剤層により貼着させることができた。また。その真偽判定体（ラベル）付き媒体は、実施例１の真偽判定体と同様に、全面ベタ印刷面（コレステリック液晶層Ｂ）から、右円偏光板を通じて観察すると、全面ベタの色が明瞭に見え、左円偏光板を通じて観察すると、全面ベタ印刷の色は見えず、パターン印刷の色が確認できた。 The obtained label was able to be peeled off and peeled off from various articles, that is, mediums to be subjected to authenticity determination, with an adhesive layer. Also. When the medium with the authenticity determination body (label) is observed through the right circular polarizing plate from the entire solid printing surface (cholesteric liquid crystal layer B), as in the authenticity determination body of Example 1, the color of the entire surface is clear. When observed through the left circularly polarizing plate, the color of the solid printing was not visible, and the color of the pattern printing could be confirmed.
（実施例３）
実施例１で作製した真偽判定体のパターン印刷面（コレステリック液晶層Ａ）の上に、ホログラム形成層を設け、そのホログラム形成層の表面に、微細凹凸の加工を施し、さらに、そのホログラム形成層の上に、透明タイプの反射性金属層を設け、さらにその反射性金属層の上に、アクリル系樹脂からなる強粘着用粘着剤を用いて、乾燥時の厚さ３０ｇ／ｍ2になるように、グラビア印刷により、粘着剤層を形成し、さらに、その粘着剤層の上に、離型シートとして、上質紙ベースでシリコーン樹脂の塗工がされた市販の坪量９０ｇ／ｍ2の剥離紙を貼り合せて、さらに抜き加工を行なって、ラベルを作製した。
(Example 3)
A hologram forming layer is provided on the pattern printing surface (cholesteric liquid crystal layer A) of the authenticity determination body prepared in Example 1, and the surface of the hologram forming layer is processed with fine irregularities, and further, the hologram formation is performed. A transparent type reflective metal layer is provided on the layer, and a strong adhesive pressure sensitive adhesive made of an acrylic resin is used on the reflective metal layer, resulting in a dry thickness of 30 g / m 2 . As described above, an adhesive layer is formed by gravure printing, and a commercially available basis weight of 90 g / m 2 on which a silicone resin is coated on a high-quality paper base as a release sheet on the adhesive layer. A release paper was pasted and further punched to produce a label.
この得られたラベルは、真偽判定の対象となる種々の物品、つまり媒体に、剥離紙を剥がして、粘着剤層により貼着させることができた。また。その真偽判定体（ラベル）付き媒体は、全面ベタ印刷面（コレステリック液晶層Ｂ）から、右円偏光板を通じて観察すると、全面ベタの色が明瞭に見え、左円偏光板を通じて観察すると、全面ベタ印刷の色は見えず、パターン印刷の色が確認できた。さらに、このラベルは、ホログラム形成層におけるホログラム画像を観察することができ、偽造防止性がより高まったものである。 The obtained label was able to be peeled off and peeled off from various articles, that is, mediums to be subjected to authenticity determination, with an adhesive layer. Also. When the medium with the authenticity determination body (label) is observed from the entire solid printing surface (cholesteric liquid crystal layer B) through the right circular polarizing plate, the color of the entire solid surface is clearly seen. The solid printing color was not visible, and the pattern printing color was confirmed. Furthermore, this label can observe the hologram image in a hologram formation layer, and is forgery prevention property improved more.
（実施例４）
厚さ１６μｍの透明ポリエチレンテレフタレートフィルムを基材フィルムとし、該基材フィルムの一方の面に、右円偏光性をもつコレステリック液晶層インキを用いて、グラビア印刷法により、基材フィルムの全面に、ベタ状に印刷し、印刷直後に紫外線を照射して、乾燥時で厚さ１０ｇ／ｍ2のコレステリック液晶層Ａを形成した。また、そのコレステリック液晶層Ａの上に、ネマチック液晶層インキを用いて、グラビア印刷法により、全面のベタ状に印刷し、印刷直後に紫外線を照射して、乾燥時で厚さ１０ｇ／ｍ2の位相差層を形成した。さらに、その位相差層の上に、右円偏光性をもつコレステリック液晶層インキを用いて、スクリーン印刷法により、パターンで印刷し、印刷直後に紫外線を照射して、乾燥時で厚さ１０ｇ／ｍ2のコレステリック液晶層Ｂを形成し、図３に示すような転写フィルムの形態である真偽判定体を作製した。尚、上記の基材フィルムのコレステリック液晶層を設けた側の表面には、予め熱離型性をもたせるための表面処理を施しておいた。
Example 4
A transparent polyethylene terephthalate film having a thickness of 16 μm is used as a base film, and a cholesteric liquid crystal layer ink having a right circular polarization property is applied to one surface of the base film by a gravure printing method. A solid was printed, and ultraviolet rays were irradiated immediately after printing to form a cholesteric liquid crystal layer A having a thickness of 10 g / m 2 at the time of drying. Further, on the cholesteric liquid crystal layer A, a nematic liquid crystal layer ink is used to print the entire surface in a solid state by gravure printing, and irradiated with ultraviolet rays immediately after printing, and a thickness of 10 g / m 2 when dried. The retardation layer was formed. Further, on the retardation layer, a cholesteric liquid crystal layer ink having a right circular polarization property is used to print in a pattern by a screen printing method, irradiated with ultraviolet rays immediately after printing, and a thickness of 10 g / An m 2 cholesteric liquid crystal layer B was formed, and a true / false judgment body in the form of a transfer film as shown in FIG. 3 was produced. The surface of the base film on the side where the cholesteric liquid crystal layer was provided was previously subjected to a surface treatment for imparting heat release properties.
この得られた真偽判定体のパターン印刷面（コレステリック液晶層Ｂ）から、右円偏光板を通じて観察すると、パターン印刷の色が確認でき、左円偏光板を通じて観察すると、パターン印刷の色は見えず、全面ベタの色が確認できた。 From the pattern printing surface (cholesteric liquid crystal layer B) of the obtained authenticity determination body, the color of the pattern printing can be confirmed by observing through the right circular polarizing plate, and the color of the pattern printing can be seen by observing through the left circular polarizing plate. The solid color was confirmed.
（実施例５）
実施例４で作製した真偽判定体の転写フィルムのパターン印刷されたコレステリック液晶層Ｂの上に、黒色ヒートシール剤をグラビア印刷法により、全面ベタ状に印刷して、接着層を乾燥時で厚さ８ｇ／ｍ2で形成した。この転写フィルムの接着層と、被着体（媒体）とが接するように、重ね合わせて、熱及び圧力を加えて、媒体にコレステリック液晶層Ａ（３）、位相差層６、コレステリック液晶層Ｂ（４）からなる３層を転写し、転写フィルムの基材フィルムをコレステリック液晶層Ａ（３）から剥離した。これにより、真偽判定体付き媒体が得られた。この真偽判定体付き媒体は、右円偏光板を通じて観察すると、全面ベタの色が明瞭に見え、左円偏光板を通じて観察すると、全面ベタ印刷の色は見えず、パターン印刷の色が確認できた。
(Example 5)
On the cholesteric liquid crystal layer B on which the authenticity transfer film produced in Example 4 was printed, a black heat sealant was printed in a solid form by a gravure printing method, and the adhesive layer was dried. A thickness of 8 g / m 2 was formed. The transfer film adhesive layer and the adherend (medium) are overlapped so that they are in contact with each other, and heat and pressure are applied to the medium, and the medium is subjected to cholesteric liquid crystal layer A (3), retardation layer 6 and cholesteric liquid crystal layer B. Three layers consisting of (4) were transferred, and the base film of the transfer film was peeled from the cholesteric liquid crystal layer A (3). As a result, a medium with authenticity determination body was obtained. When this medium with authenticity is observed through the right circular polarizing plate, the color of the whole surface is clearly visible, and when observed through the left circular polarizing plate, the color of the whole surface is not visible, and the color of the pattern printing can be confirmed. It was.
（実施例６）
厚さ１６μｍの透明ポリエチレンテレフタレートフィルムを基材フィルムとし、該基材フィルムの一方の面に、右円偏光性をもつコレステリック液晶層インキを用いて、スクリーン印刷法により、パターン印刷し、印刷直後に紫外線を照射して、乾燥時で厚さ１０ｇ／ｍ2のコレステリック液晶層Ａを形成した。また、そのコレステリック液晶層Ａの上に、ネマチック液晶層インキを用いて、スクリーン印刷法により、全面のベタ状に印刷し、印刷直後に紫外線を照射して、乾燥時で厚さ１０ｇ／ｍ2の位相差層を形成した。さらに、その位相差層の上に、右円偏光性をもつコレステリック液晶層インキを用いて、スクリーン印刷法により、全面のベタ状に印刷し、印刷直後に紫外線を照射して、乾燥時で厚さ１０ｇ／ｍ2のコレステリック液晶層Ｂを形成し、真偽判定体を作製した。
(Example 6)
A transparent polyethylene terephthalate film with a thickness of 16 μm is used as a base film, and pattern printing is performed on one surface of the base film by screen printing using a cholesteric liquid crystal layer ink having right circular polarization, immediately after printing. A cholesteric liquid crystal layer A having a thickness of 10 g / m 2 was formed by irradiation with ultraviolet rays. Further, on the cholesteric liquid crystal layer A, nematic liquid crystal layer ink is used and printed on the entire surface by screen printing, irradiated with ultraviolet rays immediately after printing, and dried to a thickness of 10 g / m 2. The retardation layer was formed. Furthermore, on the retardation layer, a cholesteric liquid crystal layer ink having right circular polarization is printed on the entire surface by screen printing and irradiated with ultraviolet rays immediately after printing. A cholesteric liquid crystal layer B having a thickness of 10 g / m 2 was formed to produce a true / false determination body.
この真偽判定体は、全面ベタ印刷面（コレステリック液晶層Ｂ）から、右円偏光板を通じて観察すると、全面ベタの色が明瞭に見え、左円偏光板を通じて観察すると、全面ベタ印刷の色は見えず、パターン印刷の色が確認できた。 This true / false judgment body, when observed through the right circular polarizing plate from the entire solid printing surface (cholesteric liquid crystal layer B), the color of the entire solid surface is clearly visible, and when observed through the left circular polarizing plate, the color of the entire solid printing is It was not visible, and the color of pattern printing was confirmed.
（実施例７）
上記の実施例１及び実施例６で作製した真偽判定体を用いて、各真偽判定体の両面に、ガラス転移温度３０℃のエチレン−酢酸ビニル共重合体の接着剤を用いて、乾燥時で厚さ２ｇ／ｍ2の接着層をそれぞれ形成した。この真偽判定体をスリッター機により、２ｍｍ幅に裁断して、巻芯に巻き取って、ロール状のスレッドとして用意した。
(Example 7)
Using the authenticity determination bodies prepared in Example 1 and Example 6 above, using an adhesive of an ethylene-vinyl acetate copolymer having a glass transition temperature of 30 ° C. on both sides of each authenticity determination object, drying is performed. Occasionally, adhesive layers each having a thickness of 2 g / m 2 were formed. This authenticity determination body was cut into a width of 2 mm by a slitter machine, wound around a winding core, and prepared as a roll-shaped thread.
二槽のシリンダーバットを備えた円網抄紙機の、一槽目の円網シリンダーの同一円周表面上に予め所定サイズの形のテープを一定間隔で貼り付けて網目を塞いでおき、第一紙層として、一定間隔で、所定サイズの穴が空いた紙層（第一紙層）を形成する。二槽目の円網シリンダーには、上記のような細工を施さず、無地の第二紙層を形成する。また、スレッドの巻き出し装置を第一槽目と第二槽目の円網シリンダー間に設置して、スレッドが第一紙層の穴と重なる位置で、さらにスレッドの接着層と第二紙層とが接する向きで、挿入されるようにする。この際、第一紙層と第二紙層が積層された状態で、第一紙層の穴の位置にスレッドのコレステリック液晶層が観察できるようにしておく。 On a circular paper machine equipped with two tank bats, a predetermined size of tape is affixed on the same circumferential surface of the first cylinder cylinder, and the mesh is closed. As a paper layer, a paper layer (first paper layer) having holes of a predetermined size is formed at regular intervals. The second tank circular mesh cylinder is not subjected to the above-described work, and a plain second paper layer is formed. Also, a thread unwinding device is installed between the first and second tank cylinders so that the thread overlaps the hole in the first paper layer. So that it is inserted in the direction in which it touches. At this time, in a state where the first paper layer and the second paper layer are laminated, the cholesteric liquid crystal layer of the thread can be observed at the position of the hole in the first paper layer.
この抄紙機で抄造される紙は、シリンダードライヤー（表面温度約７０〜１００℃）で乾燥後、マシンカレンダー処理される。上記抄紙機により、上記のスレッドを使用して、図５に示すように、スレッドが片面で露出部と被覆部が繰り返し形成された真偽判定体付き媒体を得た。尚、第一紙層は３５ｇ／ｍ2、第二紙層は６９ｇ／ｍ2の厚さで、第一紙層と第二紙層が積層された状態では、９０ｋｇ／四六版の上質紙のものである。 The paper made by this paper machine is dried by a cylinder dryer (surface temperature of about 70 to 100 ° C.) and then machine calendered. As shown in FIG. 5, the above paper machine was used to obtain a medium with a true / false judgment body in which the exposed portion and the covering portion were repeatedly formed on one side as shown in FIG. The first paper layer has a thickness of 35 g / m 2 , the second paper layer has a thickness of 69 g / m 2 , and when the first paper layer and the second paper layer are laminated, the high-quality paper of 90 kg / sixth edition belongs to.
実施例１及び実施例６で作製した真偽判定体がスレッドとして紙に抄き込まれた媒体は、両方とも右円偏光板を通じて観察すると、全面ベタの色が明瞭に見え、左円偏光板を通じて観察すると、全面ベタ印刷の色は見えず、パターン印刷の色が確認できた。 In both the media in which the authenticity determination material produced in Example 1 and Example 6 was incorporated into paper as a thread, the entire solid color was clearly seen when observed through the right circular polarizing plate. Through the observation, the color of the solid printing was not visible, and the color of the pattern printing could be confirmed.
１ 真偽判定体
２ 位相差フィルム
３ コレステリック液晶層Ａ
４ コレステリック液晶層Ｂ
５ 基材フィルム
６ 位相差層
７ 真偽判定体付き媒体
８ 基紙
９ スレッド
１０ 露出部
１１ 被覆部
1 authenticity determination body 2 retardation film 3 cholesteric liquid crystal layer A
4 Cholesteric liquid crystal layer B
DESCRIPTION OF SYMBOLS 5 Base film 6 Retardation layer 7 Medium with authenticity judgment body 8 Base paper 9 Thread 10 Exposed part 11 Covering part
Claims (5)
What attached the authenticity determination body of Claims 1-4 to the medium via the adhesive, What this transcription determination body transferred or laminated to the medium, and attached, This authenticity determination body A medium with a true / false judgment material, characterized in that the medium is one of the papers that are threaded on a base paper.