JP2007146892A - Marine hose

Info

Publication number: JP2007146892A
Application number: JP2005338738A
Authority: JP
Inventors: Satoru Shimanoe; 哲島ノ江; Tadashi Wakabayashi; 若林　　正
Original assignee: Yokohama Rubber Co Ltd
Current assignee: Yokohama Rubber Co Ltd
Priority date: 2005-11-24
Filing date: 2005-11-24
Publication date: 2007-06-14

Abstract

<P>PROBLEM TO BE SOLVED: To provide a novel marine hose capable of effectively reinforcing the hose to cope with a peculiar problem such as rubbing between marine hoses or between the marine hose and a reel caused during its use as a marine hose line. <P>SOLUTION: In this marine hose having a cover rubber layer at at least the outermost periphery and a reinforcing cord layer and an inner face rubber layer on its inner layer side, a cover rubber reinforcing layer composed of a reinforcing fiber body made of at least one kind of fiber selected from glass fiber, aramid fiber, carbon fiber, and metallic fiber is buried in the inside of the cover rubber layer. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、たとえば、陸上の原油基地等から海上に停泊する大型タンカー等を結ぶように海上もしくは海中に設置されて、原油等の流体を原油基地等から大型タンカーに移送して荷役する際、または逆に大型タンカーから陸上の原油基地などに移送する際、あるいは原油を、海底の油井から海上の浮体構造構造物・船舶などに移送する際などに用いられるマリンホースに関する。 The present invention is, for example, installed on the sea or in the sea so as to connect a large tanker or the like anchored on the sea from an onshore crude oil base or the like, and when transferring a fluid such as crude oil from a crude oil base or the like to a large tanker for cargo handling, Conversely, the present invention relates to a marine hose used when transferring a large tanker to an onshore crude oil base or the like, or when transferring crude oil from an oil well on the seabed to a floating structure or ship on the sea.

一般に、マリンホースは、その使用目的・使用環境などに応じて、浮沈方式、パーマネントフローティング方式、サブマリン方式などと称される三方式に分けることができる。 In general, marine hoses can be divided into three types called a floating / sink type, a permanent floating type, a submarine type, etc., depending on the purpose and environment of use.

例えば、陸上の施設と沖合のタンカーなどを結ぶものとして使用されるとき（一般に、パーマネントフローティング方式が多い）には、複数のマリンホースが長さ数百メートルにも及ぶように連結されて構成されたマリンホースの複数本のラインが、隣接して使用されることも多い。このような場合、海上での風、波浪が激しいときには近接したホースラインのホースどうしが激しく擦れ合い、表面のカバーゴム層が損傷を受けることや、さらにはその内部の浮力材層までが損傷を受けて、マリンホースとしての性能が損なわれることがあった。 For example, when used as a connection between an onshore facility and an offshore tanker (generally, there are many permanent floating systems), a plurality of marine hoses are connected to reach a length of several hundred meters. Often, multiple lines of marine hoses are used adjacent to each other. In such a case, when the wind and waves at the sea are severe, the hoses in the adjacent hose lines rub against each other violently, and the cover rubber layer on the surface is damaged, and even the buoyant material layer inside is damaged. In response, the performance as a marine hose may be impaired.

また、海底と海上を結ぶものとして使用されるとき（一般に、サブマリン方式が多い）には、リールにホースラインが巻き付けられて扱われることなども多いが、リールにホースが巻かれる際に、リールとホースあるいはホースどうしが擦れ合い、表面のカバーゴム層に損傷が生じマリンホースとしての性能が損なわれることがあった。 In addition, when used as a connection between the sea floor and the sea (generally, the submarine method is often used), the hose line is often wound around the reel, but when the hose is wound around the reel, the reel The hose or the hoses rub against each other, and the cover rubber layer on the surface may be damaged, and the marine hose performance may be impaired.

一方、マリンホースラインの保全は、ホースライン全体の交換を行うことによりなされるのが一般的であり、一部に損傷が生じたとしてもホースライン全体の交換作業を要することとなり、損傷がたとえ一部でも生ずることは、マリンホースライン全体のコストの点や、保全・交換作業による操業の一時停止などの不都合を招くことも多い。 On the other hand, marine hose lines are generally maintained by exchanging the entire hose line. Even if part of the hose line is damaged, the entire hose line must be replaced. The occurrence of even a part often leads to inconveniences such as the cost of the entire marine hose line and temporary suspension of operations due to maintenance and replacement work.

こうした点から、強化されたマリンホースを実現した従来のマリンホースの基本的な構造例は、ホース内周側に内面ゴム層、外周側にカバーゴム層を配し、それらの間に、中間ゴム層、補強繊維コード層や必要であればさらにワイヤコード層等からなる補強コード層を配した積層構造のものであり、更に、海上に浮上させて使用するタイプのものであれば浮力材層を形成したもの、海中（海面下）で用いられるものであれば耐圧性を付与する観点からワイヤの線径を太くしたり複数のワイヤ補強層を設けたものなどがあり、各種の提案がされている（特許文献１、特許文献２、特許文献３等）。 From these points, the basic structure example of a conventional marine hose that realizes a reinforced marine hose has an inner rubber layer on the inner peripheral side of the hose and a cover rubber layer on the outer peripheral side, and an intermediate rubber between them. Layer, a reinforcing fiber cord layer and, if necessary, a laminated structure in which a reinforcing cord layer made of a wire cord layer is arranged. If it is formed or used in the sea (under the sea), there are various proposals, such as increasing the wire diameter or providing multiple wire reinforcement layers from the viewpoint of providing pressure resistance. (Patent Document 1, Patent Document 2, Patent Document 3, etc.).

また、このような内周側に内面ゴム層、外周側に外面ゴム層、それらの間に補強繊維層を設けるというホースの基本的積層構造は、土砂や粉体、液体、生コンクリートなどの分野で移送に用いられるようなホースでも同様であり、該基本構造で、特に耐摩耗性の向上のためにポリエチレンシートを最外面・最内面に配置したという耐摩耗性ホースなどが知られている（特許文献４）。 In addition, the basic laminated structure of the hose in which an inner rubber layer is provided on the inner peripheral side, an outer rubber layer is provided on the outer peripheral side, and a reinforcing fiber layer is provided therebetween, is a field of earth and sand, powder, liquid, ready-mixed concrete, etc. The same applies to a hose used for transfer in the same manner, and a wear-resistant hose in which a polyethylene sheet is arranged on the outermost surface / innermost surface in order to improve the wear resistance is known. Patent Document 4).

また、特に、一般の高圧用のゴムホースを補強するポリエステル繊維あるいはアラミド繊維についての提案、さらに該繊維を用いた一般の高圧用ゴムホースの提案がされている（特許文献５−７）。 In particular, there have been proposals for polyester fibers or aramid fibers that reinforce general high-pressure rubber hoses, and general high-pressure rubber hoses using such fibers (Patent Documents 5-7).

しかしながら、特許文献１〜４に記載の提案においては、特にホースどうしあるいはホースとリール間の擦れ等の固有の問題に対して有効な補強がされているわけでなく、また、特許文献５〜７に記載の提案においては、特に、マリンホースの補強についての具体的構造について、ましてや上述の固有の問題に対しての有効な提案がされているわけではなかった。
特開２０００−９２６７号公報特開２００４−１２５１２５号公報特開平１−１７６８８６号公報特開平８−７２１７７号公報特開２００１−３２６７号公報特開平１０−１１０３９０号公報特開平９−３１８５４号公報 However, the proposals described in Patent Documents 1 to 4 do not provide effective reinforcement particularly for inherent problems such as rubbing between hoses or between a hose and a reel. In the proposal described in (1), an effective proposal for the above specific problem has not been made, in particular, with respect to the specific structure for reinforcing the marine hose.
JP 2000-9267 A JP 2004-125125 A JP-A-1-176886 JP-A-8-72177 JP 2001-3267 A Japanese Patent Laid-Open No. 10-110390 JP 9-31854 A

上述したような点に鑑み、本発明の目的は、特に、マリンホースラインとして使用中に生ずるマリンホースどうしあるいはマリンホースとリール間の擦れ等の固有の問題に対して有効な補強をなし得た新規なマリンホースを提供することにある。 In view of the above-described points, the object of the present invention was able to achieve effective reinforcement especially for inherent problems such as rubbing between marine hoses or marine hoses and reels that occur during use as marine hose lines. It is to provide a new marine hose.

上述した目的を達成する本発明のマリンホースは、下記(1) の構成からなる。
（１）少なくとも最外周にカバーゴム層、その内層側に補強コード層、内面ゴム層とを有するマリンホースにおいて、前記カバーゴム層の内部に、ガラス繊維、アラミド繊維、炭素繊維、金属繊維から選択された少なくとも一種からなる補強繊維体からなるカバーゴム補強層を埋設してなることを特徴とするマリンホース。 The marine hose of the present invention that achieves the above object has the following configuration (1).
(1) In a marine hose having a cover rubber layer at least on the outermost periphery, a reinforcing cord layer on the inner layer side, and an inner rubber layer, selected from glass fiber, aramid fiber, carbon fiber, and metal fiber inside the cover rubber layer A marine hose characterized by burying a cover rubber reinforcing layer made of at least one type of reinforcing fiber body.

また、かかる本発明のマリンホースにおいて、好ましくは、下記(2) の具体的構成からなるものである。
（２）カバーゴム層と内面ゴム層の間にあるいずれかの層間において、少なくとも浮力材層が配されていることを特徴とする上記(1) 記載のマリンホース。 The marine hose of the present invention preferably has the following specific configuration (2).
(2) The marine hose as described in (1) above, wherein at least a buoyant material layer is disposed between any of the layers between the cover rubber layer and the inner rubber layer.

請求項１ないし２にかかる本発明によれば、マリンホースラインとして使用中に生ずるマリンホースどうしあるいはマリンホースとリール間の擦れ等の固有の問題に対して有効な補強をなし得た新規なマリンホースが提供されるものである。 According to the present invention according to claim 1 or 2, a novel marine that can effectively reinforce marine hoses generated during use as marine hose lines or inherent problems such as rubbing between marine hoses and reels. A hose is provided.

特に、請求項２にかかる発明によれば、上述の効果を有するパーマネントフローティング方式の新規なマリンホースが提供されるものである。 In particular, the invention according to claim 2 provides a novel marine hose of the permanent floating type having the above-described effects.

以下、図面等を参照しながら、更に詳しく本発明のマリンホースについて説明する。
図１は、本発明にかかるマリンホース構造の代表的な１実施態様例を示したマリンホース本体の一部概略断面図である。 Hereinafter, the marine hose of the present invention will be described in more detail with reference to the drawings.
FIG. 1 is a partial schematic cross-sectional view of a marine hose body showing a typical embodiment of a marine hose structure according to the present invention.

本発明のマリンホース１は、少なくとも最外周にカバーゴム層３、その内層側に補強コード層４、内面ゴム層２とを必須の構成層として有するマリンホースにおいて、カバーゴム層３の内部にガラス繊維、アラミド繊維、炭素繊維、金属繊維から選択された少なくとも一種からなる補強繊維体からなるカバーゴム補強層８を埋設してなるものである。 A marine hose 1 according to the present invention is a marine hose having a cover rubber layer 3 at least on the outermost periphery, a reinforcing cord layer 4 on the inner layer side, and an inner rubber layer 2 as essential constituent layers. A cover rubber reinforcing layer 8 made of a reinforcing fiber body made of at least one selected from fibers, aramid fibers, carbon fibers and metal fibers is embedded.

図１において、５はワイヤーコード層、６は中間ゴム層、７は浮力材層、９はホース内孔である。ワイヤーコード層５と浮力材層７は、そのマリンホースの使用目的や態様に応じて、構造要素として適宜に採用されればよいものであり、必須のものではない。 In FIG. 1, 5 is a wire cord layer, 6 is an intermediate rubber layer, 7 is a buoyancy material layer, and 9 is a hose inner hole. The wire cord layer 5 and the buoyancy material layer 7 may be appropriately adopted as structural elements according to the purpose and mode of use of the marine hose, and are not essential.

本発明のマリンホースにおいては、上述したガラス繊維、アラミド繊維、炭素繊維、金属繊維から選択された少なくとも一種からなる補強繊維体からなるカバーゴム補強層８がカバーゴム層３中に埋設されていることから、マリンホースどうしやマリンホースとリールなどが激しく擦れ合ったとしても該カバーゴム層が損傷を受けることを効果的に防止することができる。 In the marine hose of the present invention, a cover rubber reinforcing layer 8 made of a reinforcing fiber body made of at least one selected from the glass fiber, aramid fiber, carbon fiber, and metal fiber described above is embedded in the cover rubber layer 3. Therefore, even if marine hoses or marine hoses and reels rub against each other violently, the cover rubber layer can be effectively prevented from being damaged.

該ガラス繊維、アラミド繊維、炭素繊維、金属繊維のそれぞれは、ＪＩＳＬ１０１３に準拠して測定される引張強度が１８０ｍＮ／ｄｔｅｘ以上のものを用いることが、本発明の上述した損傷防止効果をより効果的に得る上で好ましい。 Each of the glass fiber, the aramid fiber, the carbon fiber, and the metal fiber has a tensile strength measured in accordance with JIS L1013 of 180 mN / dtex or more, so that the above-described damage prevention effect of the present invention is more effective. It is preferable for obtaining it.

上述したガラス繊維、アラミド繊維、炭素繊維あるいは金属繊維は、補強繊維体としてカバーゴム補強層を構成するに際して、その繊維の使用方法は、繊維布状として使用してもよいし、あるいは、繊維を糸状物にして、それを単に引き揃えた状態で使用してもよいし、あるいは繊維を糸状物にして使用してもよく、あるいは更にその糸状物を複数本撚り合わせた繊維糸コード状のものとして使用してもよい。 The glass fiber, the aramid fiber, the carbon fiber, or the metal fiber described above may be used as a fiber cloth when the cover rubber reinforcing layer is formed as the reinforcing fiber body, or the fiber may be used. It may be used in the form of a thread-like product that is simply aligned, or may be used as a fiber-like product, or a fiber-yarn cord-like product obtained by twisting a plurality of the filaments. May be used as

繊維布状のものとして使用する場合は、織布状あるいは編布状、不織布状あるいは網状でもよく、また、繊維状の場合は引き揃えられたフィラメント繊維状、あるいはカット繊維とされた短繊維状などでもよい。 When used as a fiber cloth, it may be a woven or knitted cloth, a non-woven cloth or a net, and in the case of a fiber, it is an aligned filament fiber or a short fiber which is a cut fiber. Etc.

カバーゴム補強層の中で、上述したガラス繊維、アラミド繊維、炭素繊維あるいは金属繊維は、その繊維長さ方向が、マリンホース長さ方向と径方向に存在しているのが好ましく、その点からは、補強繊維体の形態は、織布状やスダレ織状のものなどが好ましい。
あるいはまた、繊維糸状もしくはコード状のものがらせん状に配列されて補強繊維体を構成してもよいものである。 Among the cover rubber reinforcing layers, the glass fiber, aramid fiber, carbon fiber or metal fiber described above preferably has a fiber length direction in the marine hose length direction and a radial direction. The shape of the reinforcing fiber body is preferably a woven fabric or a woven fabric.
Alternatively, fiber yarns or cords may be arranged in a spiral to constitute the reinforcing fiber body.

また、フローティングマリンホースとして本発明のマリンホースを構成する場合、カバーゴム層と内面ゴム層の間に、浮力材層が配されていることが好ましい。具体的には、カバーゴム層と内面ゴム層の間にあるいずれかの層間において、例えば、発泡樹脂あるいは発泡ゴムなどの適宜の構成材料からなる浮力材層を、いずれかの層間に配することが好ましいものである。 Further, when the marine hose of the present invention is configured as a floating marine hose, it is preferable that a buoyancy material layer is disposed between the cover rubber layer and the inner rubber layer. Specifically, a buoyancy material layer made of an appropriate constituent material such as foamed resin or foamed rubber is disposed between any of the layers between the cover rubber layer and the inner rubber layer. Is preferred.

本発明のマリンホースは、その製造方法については、特に限定されるものではないが、例えば、マンドレルに本発明のマリンホースの構成材料を順次に巻いていき、そのままの状態で加硫を行い、さらにマンドレルを引き抜くことにより製造することができる。 The manufacturing method of the marine hose of the present invention is not particularly limited.For example, the constituent materials of the marine hose of the present invention are sequentially wound around a mandrel, and vulcanized as it is. Furthermore, it can manufacture by pulling out a mandrel.

図１は、本発明にかかるマリンホース構造の代表的な１実施態様例を示したマリンホース本体の一部概略断面図である。FIG. 1 is a partial schematic cross-sectional view of a marine hose body showing a typical embodiment of a marine hose structure according to the present invention.

符号の説明Explanation of symbols

１：マリンホース
２：内面ゴム層
３：カバーゴム層
４：補強コード層
５：ワイヤーコード層
６：中間ゴム層
７：浮力材層
８：カバーゴム補強層
９：ホース内孔 1: Marine hose 2: Internal rubber layer 3: Cover rubber layer 4: Reinforcement cord layer 5: Wire cord layer 6: Intermediate rubber layer 7: Buoyancy material layer 8: Cover rubber reinforcement layer 9: Hose bore

Claims

少なくとも最外周にカバーゴム層、その内層側に補強コード層、内面ゴム層とを有するマリンホースにおいて、前記カバーゴム層の内部に、ガラス繊維、アラミド繊維、炭素繊維、金属繊維から選択された少なくとも一種からなる補強繊維体からなるカバーゴム補強層を埋設してなることを特徴とするマリンホース。 In a marine hose having at least a cover rubber layer on the outermost periphery, a reinforcing cord layer on the inner layer side, and an inner rubber layer, at least selected from glass fiber, aramid fiber, carbon fiber, and metal fiber inside the cover rubber layer A marine hose comprising a cover rubber reinforcing layer made of a kind of reinforcing fiber body.

カバーゴム層と内面ゴム層の間にあるいずれかの層間において、少なくとも浮力材層が配されていることを特徴とする請求項１記載のマリンホース。 2. The marine hose according to claim 1, wherein at least a buoyancy material layer is disposed between any of the layers between the cover rubber layer and the inner rubber layer.