Abstract

<P>PROBLEM TO BE SOLVED: To provide a reflective screen that is inexpensive, requires no large space and less time and effort for carrying in to install, can be easily stuck and peeled and used for a long period of time. <P>SOLUTION: The reflective screen to display a reflected image comprises an image display layer, a fibrous material base layer containing at least one kind of synthetic resin fiber, a concealing layer and an adhesive layer comprising starch glue and a water-based acrylic adhesive, in this order from the display side, wherein the fibrous material base layer comprises synthetic fiber by 30 wt.% or more. The screen is free from elongation in a wet state and from shrinkage in a dry state and shows dimensional stability. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、反射映像を表示するための反射型スクリーンに関し、特には安価で取扱が容易な反射型スクリーンに関する。 The present invention relates to a reflective screen for displaying a reflected image, and more particularly to a reflective screen that is inexpensive and easy to handle.

反射型スクリーンとしては、巻き上げ装置を天井近傍に吊るして使用時に引き下げるものが知られている。最近では天井内部に巻き上げ装置を設置し、壁面の操作盤で引き下げ、巻き上げができるように設計されたものもある。また壁が扉状に開いてその壁面内部に設置されたものも知られている。より安価な例では、組立可能な設置装置の上部に前記巻き上げ装置を設置するものがあり、さらには、大型で移動可能な台車がついたものなどもある。巻き上げるタイプのものは省スペースではあるが、表示面が平面に安定せず、また巻き上げ引き下げの装置機構が別途必要であり複雑な構造となっている。壁面内部や移動できる大型なものなどで映像表示部が固定されたものは光学特性に優れたものが多いが、その分高価なものとなっていた。また搬入や設置にも手間と費用が発生するものであった。 As a reflection type screen, one that hangs a hoisting device near the ceiling and pulls it down during use is known. Recently, a hoisting device has been installed inside the ceiling, and some have been designed so that they can be pulled down and rolled up with a wall operation panel. In addition, there is also known that the wall is opened in a door shape and installed inside the wall surface. In a cheaper example, there is one in which the hoisting device is installed on the upper part of an assembling installation device, and there is also a device having a large and movable carriage. Although the type of hoisting type is space-saving, the display surface is not stable on a flat surface, and an apparatus mechanism for hoisting and lowering is required separately, resulting in a complicated structure. Many of the interiors of the wall surface and large movable objects with the image display unit fixed have excellent optical characteristics, but they are expensive. In addition, it takes time and money to carry in and install.

そこで、任意の平面に剥離自在に貼着できる反射型スクリーンが考えられた。（特許文献１）しかしながら、粘着性の強い粘着剤を用いると、貼る際の位置付けが困難であった。逆に粘着性の弱い粘着剤では、剥がれやすいものとなる。また、長期間貼りつづけることにより、温度や湿度に伴う寸法変化の影響で割れやシワや膨れが発生しやすかった。割れやシワや膨れが発生すると、映像が歪んでしまい、問題となる。
特開２００４−０５４０６７号 Therefore, a reflection type screen that can be detachably attached to an arbitrary plane has been considered. (Patent Document 1) However, when an adhesive with strong adhesiveness is used, positioning at the time of application is difficult. On the contrary, an adhesive with weak adhesiveness is easily peeled off. In addition, by sticking for a long time, cracks, wrinkles, and blisters were likely to occur due to dimensional changes associated with temperature and humidity. When cracks, wrinkles, and blisters occur, the image is distorted, which is a problem.
JP 2004-054067 A

本発明はこのような問題点を解決するためになされたものであり、その課題とするところは、安価でスペースを要せず設置で搬入の手間も少なく、容易に貼着と剥離が可能で共期間の使用も可能な反射型スクリーンを提供することにある。 The present invention has been made in order to solve such problems, and the problem is that it is inexpensive, does not require space, requires less labor for installation, and can be easily attached and peeled off. It is an object of the present invention to provide a reflective screen that can be used for a period of time.

本発明はこのような課題を解決するためのものであり、請求項１記載の発明は、反射映像を表示するための反射型スクリーンであって、表示側より、映像表示層、少なくとも１種類の合成樹脂繊維を含む繊維質基材層、隠蔽層、でんぶん糊と水性アクリル系接着剤とからなる粘着剤層とをこの順に有することを特徴とする反射型スクリーンである。 The present invention is for solving such problems, and the invention according to claim 1 is a reflective screen for displaying a reflected image, wherein the image display layer includes at least one kind of image display layer from the display side. A reflective screen comprising a fibrous base material layer containing synthetic resin fibers, a concealing layer, and a pressure-sensitive adhesive layer made of starch paste and a water-based acrylic adhesive in this order.

また、請求項２記載の発明は、前記繊維質基材層の３０重量％以上が合成樹脂繊維からなることを特徴とする請求項１記載の反射型スクリーンである。 The invention according to claim 2 is the reflective screen according to claim 1, wherein 30% by weight or more of the fibrous base material layer is made of synthetic resin fibers.

本発明はその請求項１記載の発明により、でんぷん糊により貼る際の位置決めが容易となり、水性アクリル系接着剤により既存の壁紙の上などにも貼り合わせることが可能となる。また、合成樹脂繊維を含む繊維質基材層とすることで、湿潤時の伸び、乾燥時の縮みを避け、寸法安定性が得られるものとなる。 According to the invention of the first aspect, the present invention facilitates positioning when pasting with starch paste, and can be pasted onto an existing wallpaper or the like with a water-based acrylic adhesive. Moreover, by using a fibrous base material layer containing synthetic resin fibers, dimensional stability can be obtained while avoiding elongation when wet and shrinkage when drying.

以下、本発明を図面に基づき詳細に説明する。図１に本発明の反射型スクリーンの一実施例の断面の構造を示す。適宜設ける剥離層１の上に、でんぷん糊と水性アクリル系接着剤からなる粘着剤層２、背面の色を隠蔽するための黒や灰色に着色した隠蔽層３、少なくとも１種類の合成樹脂繊維を含む繊維質基材層４、酸化チタンなどを含有して白色とした樹脂などによる映像表示層５からなる。 Hereinafter, the present invention will be described in detail with reference to the drawings. FIG. 1 shows a cross-sectional structure of an embodiment of a reflective screen according to the present invention. An adhesive layer 2 made of starch paste and a water-based acrylic adhesive, a concealing layer 3 colored in black or gray for concealing the color of the back, and at least one synthetic resin fiber on the release layer 1 provided as appropriate. It includes a fibrous base material layer 4 and a video display layer 5 made of a white resin containing titanium oxide.

適宜設ける剥離層１は、接着時に水分を含有して貼り付けることを目的とした後述する粘着剤層を長期間保護するために設けるものであって、防湿性及び酸素バリア性を有するものであれば市販のものを使用可能である。具体的には２軸延伸ポリプロピレンフィルムまたはポリエチレンテレフタレートフィルムなどで背面に桝目やロゴ、注意書きなどの印刷があっても良い。
また、本発明の反射型スクリーンを一次的にはがすときに、巻き上げる場合、粘着剤が映像表示層に付着するのを防止するために、映像表示層表面に重ねてから巻き上げるのに使用したりすることもできる。
また本発明の反射型スクリーンを、蒸着フィルムやアルミ箔からなり防湿性及び酸素バリア性に優れた包材で包装し、脱酸素剤を同封することで長期間の保存が可能である。 The release layer 1 provided as appropriate is provided for the purpose of protecting a pressure-sensitive adhesive layer described later for the purpose of containing and adhering moisture at the time of adhesion, and has moisture resistance and oxygen barrier properties. Commercially available products can be used. Specifically, a biaxially stretched polypropylene film or a polyethylene terephthalate film may be printed on the back such as a grid, a logo, or a warning.
In addition, when the reflective screen of the present invention is temporarily peeled off, it is used to roll up after overlapping the image display layer surface in order to prevent the adhesive from adhering to the image display layer. You can also
Further, the reflective screen of the present invention can be stored for a long period of time by packaging it with a packaging material made of a vapor-deposited film or aluminum foil and having excellent moisture resistance and oxygen barrier properties and enclosing an oxygen scavenger.

本発明における粘着剤層２は、でんぶん糊と水性アクリル系接着剤とからなるものであり、その配合の詳細や塗布量は後述する繊維質基材層に合わせて適宜調整すればよいが、特には、配合としては５０対５０、塗布量は１００〜２００ｇ／ｍ^２程度が好ましい。製法としては、ロールコーター等によるコートで設けることができる。
粘着剤層２は乾燥した状態で保持され、再湿により粘着性を復元するものとなる。 The pressure-sensitive adhesive layer 2 in the present invention is composed of starch paste and a water-based acrylic adhesive, and the details and application amount of the blend may be appropriately adjusted according to the fibrous base material layer described later. In particular, the composition is preferably 50 to 50 and the coating amount is about 100 to 200 g / m ² . As a manufacturing method, it can provide by the coat | court by a roll coater etc.
The pressure-sensitive adhesive layer 2 is held in a dry state, and the pressure-sensitive adhesive layer 2 is restored by rewetting.

本発明における隠蔽層３は、背面の色を隠蔽するための黒色や灰色に着色したものであればよいが、特にはカーボンブラック、硝化綿などが好ましい。製法としては、グラビア印刷又はロールコーター等によるコートで設けることができる。黒色や灰色にすることで光吸収層を兼ねることができ、下地の色を隠すだけでなく、反射特性にも寄与するものとなる。 The concealing layer 3 in the present invention is not particularly limited as long as it is colored black or gray for concealing the color of the back surface, and carbon black, nitrified cotton and the like are particularly preferable. As a manufacturing method, it can provide by the coat | court by gravure printing or a roll coater. By making it black or gray, it can also serve as a light absorbing layer, which not only hides the underlying color but also contributes to reflection characteristics.

本発明における繊維質基材層４は、少なくとも１種類の合成樹脂繊維を含むものであり、合成樹脂繊維混抄紙や不織布などであって、合成樹脂繊維としてはポリエチレン繊維、ポリエチレンテレフタレート繊維などが使用可能である。
これにより、粘着時に水分を含有することで粘着性を発現する粘着剤を利用しても、反射型スクリーンの寸法が安定したものとなる。
合成樹脂繊維だけのフィルムではでんぷん糊との接着性に難がある。紙だけの基材では湿潤時に伸び、また乾燥時には縮んでしまう。紙または不織布に合成樹脂繊維を、特には３０重量％以上含むことで、粘着剤との粘着性と寸法安定性の両方を得ることが可能となる。坪量は５０〜１５０ｇ／ｍ^２が好ましい。 The fibrous base material layer 4 in the present invention contains at least one kind of synthetic resin fiber, and is a synthetic resin fiber mixed paper or non-woven fabric. As the synthetic resin fiber, polyethylene fiber, polyethylene terephthalate fiber or the like is used. Is possible.
Thereby, even if it uses the adhesive which expresses adhesiveness by containing a water | moisture content at the time of adhesion | attachment, the dimension of a reflective screen will be stabilized.
A film made only of synthetic resin fibers has difficulty in adhesion to starch paste. A paper-only substrate stretches when wet and shrinks when dried. By including synthetic resin fibers in paper or non-woven fabric, particularly 30% by weight or more, it becomes possible to obtain both adhesiveness with the adhesive and dimensional stability. The basis weight is preferably 50 to 150 g / m ² .

本発明における映像表示層５は、酸化チタンなどを含有して白色とした樹脂などによるものであれば良い。樹脂はエチレンビニルアルコールなどが適用可能であり、酸化チタンの他には炭酸カルシウムなどでも良い。製法としてはエマルジョンのコーティングまたはカレンダーで製膜すればよい。また表面はコーティングで平滑に仕上げるＫとができるのであれば平滑なままでも良いが、微細なエンボス加工を施すことで、外光によるコントラストへの悪影響を軽減することが可能となる。厚みとしては、スクリーンの施工やハンドリング上、４０〜２００μｍの範囲であることが好ましい。これより薄いとコシが無く、シワになりやすい。またこれより厚いと剛性がありすぎて、運搬時にロール状にした際に折れシワが入ったりする可能性が有る。 The image display layer 5 in the present invention may be made of a white resin containing titanium oxide or the like. As the resin, ethylene vinyl alcohol or the like is applicable, and calcium carbonate or the like may be used in addition to titanium oxide. As a production method, a film may be formed by emulsion coating or calendering. Further, the surface may be kept smooth as long as it can be smoothed with a coating. However, by performing fine embossing, it is possible to reduce adverse effects on contrast due to external light. As thickness, it is preferable that it is the range of 40-200 micrometers on construction and handling of a screen. If it is thinner than this, there is no stiffness and wrinkles easily. On the other hand, if it is thicker than this, there is too much rigidity, and there is a possibility that wrinkles will occur when it is rolled during transportation.

剥離層１として、厚さ１２μｍの２軸延伸ポリプロピレンフィルムを用いた。接着剤層２として、澱粉糊５０重量部と水性アクリル系接着剤５０重量部とを水で希釈したものを乾燥後塗布量１５０ｇ／ｍ^２となるように塗布した。隠蔽層３として、顔料カーボンブラックとビヒクル硝化綿を乾燥後塗布量１ｇ／ｍ^２となるように塗布した。混抄紙層４として、パルプ３０重量％にポリエチレンテレフタレート繊維３５重量％、ポリエチレン繊維１０重量％、麻２５重量％からなり、坪量８５ｇ／ｍ^２のものを用いた。表面樹脂層５として、エチレン酢酸ビニル共重合樹脂４７．５重量％と炭酸カルシウム４７．５重量％と酸化チタン５重量％を厚み１００μｍとなるようにカレンダー装置で製膜し、表面には微細なエンボス加工を施した。以上のようにして反射型スクリーンを得た。得られた反射型スクリーンを壁に貼る施工は位置の特定も容易で状態も良好で平滑な仕上がりとなり、市販のプロジェクターで映写したが問題はなかった。 As the release layer 1, a biaxially stretched polypropylene film having a thickness of 12 μm was used. As the adhesive layer 2, a solution obtained by diluting 50 parts by weight of starch paste and 50 parts by weight of an aqueous acrylic adhesive with water was applied so that the coating amount after drying was 150 g / m ² . As the concealing layer 3, pigment carbon black and vehicle nitrified cotton were applied at a coating amount of 1 g / m ² after drying. As the mixed paper layer 4, 30% by weight of pulp, 35% by weight of polyethylene terephthalate fiber, 10% by weight of polyethylene fiber, 25% by weight of hemp, and a basis weight of 85 g / m ² were used. As the surface resin layer 5, 47.5% by weight of ethylene vinyl acetate copolymer resin, 47.5% by weight of calcium carbonate, and 5% by weight of titanium oxide were formed by a calender device so as to have a thickness of 100 μm. Embossed. A reflective screen was obtained as described above. The application of the obtained reflective screen to the wall was easy to specify the position and in good condition with a smooth finish. Although it was projected with a commercially available projector, there was no problem.

＜比較例１＞
混抄紙層４として、パルプ３０重量％、麻７０重量％とした以外は実施例１と同様にして反射型スクリーンを得た。得られた反射型スクリーンは貼った後に全体が収縮し、継ぎ目が開いたものとなった。 <Comparative Example 1>
A reflective screen was obtained in the same manner as in Example 1 except that the mixed paper layer 4 was 30% by weight of pulp and 70% by weight of hemp. The obtained reflection type screen was entirely shrunk after being applied, and the seam was opened.

＜比較例２＞
接着剤層２として、強い粘着性を持つアクリル系粘着剤を厚さ５０μｍで設けたものとした以外は実施例１と同様にして反射型スクリーンを得た。得られた反射型スクリーンを貼る際に位置決めが難しく、少しずれて貼ったところを直そうとした際に紙層で剥離を起こしてしまった。 <Comparative example 2>
A reflective screen was obtained in the same manner as in Example 1 except that the adhesive layer 2 was provided with an acrylic pressure-sensitive adhesive having a strong tackiness with a thickness of 50 μm. When applying the obtained reflective screen, positioning was difficult, and peeling occurred at the paper layer when trying to fix the place where the reflection screen was slightly shifted.

＜比較例３＞
接着剤層２として、弱い粘着性を持つアクリル系粘着剤を厚さ５０μｍで設けたものとした以外は実施例１と同様にして反射型スクリーンを得た。得られた反射型スクリーンは貼った後に膨れが生じた。 <Comparative Example 3>
A reflective screen was obtained in the same manner as in Example 1 except that the adhesive layer 2 was provided with a weak adhesive acrylic adhesive having a thickness of 50 μm. The obtained reflective screen was swollen after being applied.

本発明の反射型スクリーンは、小さいクリーンを連続して貼る事で容易に大型のスクリーンとしても利用可能である。このように用いても本願発明の反射型スクリーンは寸法安定性を有することから、継ぎ目が開いたりすることもない。また、壁面の大きさに併せて任意のサイズのスクリーンとすることもに可能である。 The reflective screen of the present invention can be easily used as a large screen by applying a small clean continuously. Even when used in this manner, the reflective screen of the present invention has dimensional stability, so that the seam does not open. Moreover, it is also possible to set it as the screen of arbitrary sizes according to the magnitude | size of a wall surface.

本発明の反射型スクリーンの一実施例の断面の構造を示す説明図である。It is explanatory drawing which shows the structure of the cross section of one Example of the reflection type screen of this invention.

符号の説明Explanation of symbols

１…剥離層
２…粘着剤層
３…隠蔽層
４…繊維質基材層
５…映像表示層 DESCRIPTION OF SYMBOLS 1 ... Release layer 2 ... Adhesive layer 3 ... Concealment layer 4 ... Fiber base material layer 5 ... Video display layer

Claims

反射映像を表示するための反射型スクリーンであって、表示側より、映像表示層、少なくとも１種類の合成樹脂繊維を含む繊維質基材層、隠蔽層、でんぶんを含む粘着剤層をこの順に有することを特徴とする反射型スクリーン。 A reflective screen for displaying a reflected image, from the display side, an image display layer, a fibrous base material layer containing at least one synthetic resin fiber, a concealing layer, and a pressure-sensitive adhesive layer containing starch. A reflection type screen comprising:

前記繊維質基材層の３０重量％以上が合成樹脂繊維からなることを特徴とする請求項１記載の反射型スクリーン。

The reflective screen according to claim 1, wherein 30% by weight or more of the fibrous base material layer is made of synthetic resin fibers.