JP2007096133A - Manufacturing method of white led, manufacturing method of back light using same white led, and manufacturing method of liquid crystal display - Google Patents
Manufacturing method of white led, manufacturing method of back light using same white led, and manufacturing method of liquid crystal display Download PDFInfo
- Publication number
- JP2007096133A JP2007096133A JP2005285624A JP2005285624A JP2007096133A JP 2007096133 A JP2007096133 A JP 2007096133A JP 2005285624 A JP2005285624 A JP 2005285624A JP 2005285624 A JP2005285624 A JP 2005285624A JP 2007096133 A JP2007096133 A JP 2007096133A
- Authority
- JP
- Japan
- Prior art keywords
- phosphor
- white led
- manufacturing
- light emitting
- green
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、液晶表示装置のバックライトに好適な白色LED(発光ダイオード)の製造方法およびそれを用いたバックライトの製造方法並びに液晶表示装置の製造方法に関する。 The present invention relates to a manufacturing method of a white LED (light emitting diode) suitable for a backlight of a liquid crystal display device, a manufacturing method of a backlight using the same, and a manufacturing method of a liquid crystal display device.
発光ダイオード(LED:Light Emitting Diode)は光を放射する半導体ダイオードであり、電気エネルギーを紫外光または可視光に変換するものである。特に可視光を利用するためにGaP、GaAsP、GaAlAs、GaN、InGaAlPなどの発光材料で形成した発光チップを透明樹脂で封止したLEDとして広く使用されている。また、発光材料をプリント基板や金属リードの上面に固定し、数字や文字を形どった樹脂ケースで封止したディスプレィ型のLEDも多用されている。
また、発光チップの前表面あるいは前部樹脂中に各種の蛍光体粉末を含有させることにより、放射光の色を適正に調整することも可能である。すなわちLEDの発光色は、青色から赤色まで使用用途に応じた可視光領域の発光を再現することが出来る。また、発光ダイオードは半導体素子であるため、長寿命、高信頼性で、光源として用いた場合には、その交換頻度も低減されることから、携帯通信機器、パーソナルコンピュータ周辺機器、OA機器、家庭用電気機器、オーディオ機器、各種スイッチ、バックライト用光源表示板等の各種表示装置の構成部品として広く使用されている。
A light emitting diode (LED: Light Emitting Diode) is a semiconductor diode that emits light, and converts electrical energy into ultraviolet light or visible light. In particular, in order to use visible light, it is widely used as an LED in which a light-emitting chip formed of a light-emitting material such as GaP, GaAsP, GaAlAs, GaN, or InGaAlP is sealed with a transparent resin. In addition, a display type LED in which a light emitting material is fixed to the upper surface of a printed board or a metal lead and sealed with a resin case in which numbers and letters are formed is also frequently used.
In addition, it is possible to appropriately adjust the color of the emitted light by including various phosphor powders in the front surface or front resin of the light emitting chip. That is, the emission color of the LED can reproduce the light emission in the visible light region depending on the usage from blue to red. In addition, since a light emitting diode is a semiconductor element, it has a long life, high reliability, and when used as a light source, its replacement frequency is also reduced. Therefore, a portable communication device, a personal computer peripheral device, an OA device, a home It is widely used as a component of various display devices such as electrical equipment, audio equipment, various switches, and backlight light source display panels.
しかしながら、最近では上記各種表示装置の利用者の色彩感覚が向上し、各種表示装置においても、微妙な色合いをより高精細に再現できる機能や、LEDの均一な外観が要求要求されるようになってきた。特に白色発光のLEDは携帯電話のバックライトや車載用ランプにおいてその拡大は著しく、将来的には、蛍光灯の代替として大きく伸長していくことが期待されるところから、その白色光の高演色性や均一な外観をもとめ種々の改善が試みられている。
現在、普及し、あるいは試行されている白色発光LEDには青色発光ダイオードと黄色発光蛍光体(YAG)場合によっては更に赤色蛍光体を組み合わせたタイプ(タイプ1と呼称)、紫外線あるいは紫光発光ダイオードと青色、黄色、赤色蛍光体を組み合わせたタイプ(タイプ2と呼称)がある。現時点で、タイプ1はタイプ2より高輝度で最も普及しているが、見る方向によっては黄色っぽく見えたり、白色面に投影したとき黄色や青色のムラが現れたりする。そのためタイプ1は擬似白色と呼ばれることもある。白色光の質を表す平均演色指数においてもタイプ1の白色発光LEDでは70〜75(70以上75以下)の範囲に留まっている。一方、後者(タイプ2)は輝度において前者に劣るものの、発光ならびに投影光のムラが少なく、将来的には照明、あるいはバックライト用途の本命として展開が期待され開発が進められている。
However, recently, the color sensation of users of the above various display devices has been improved, and various display devices are required to have a function capable of reproducing subtle hues with higher definition and a uniform appearance of LEDs. I came. In particular, white light-emitting LEDs have been greatly expanded in the backlights of mobile phones and in-vehicle lamps. In the future, they are expected to grow greatly as an alternative to fluorescent lamps. Various attempts have been made to improve performance and uniform appearance.
Currently, white light-emitting LEDs that are widely used or tried include blue light-emitting diodes and yellow light-emitting phosphors (YAG), in some cases a combination of red phosphors (referred to as type 1), ultraviolet or purple light-emitting diodes, and so on. There is a type combining blue, yellow and red phosphors (referred to as type 2). At present, Type 1 is the most popular because of higher brightness than Type 2, but it may appear yellowish depending on the viewing direction, or yellow or blue unevenness may appear when projected onto a white surface. Therefore, Type 1 is sometimes called pseudo white. The average color rendering index representing the quality of white light remains in the range of 70 to 75 (70 or more and 75 or less) in the type 1 white light emitting LED. On the other hand, although the latter (type 2) is inferior to the former in luminance, there is little unevenness of light emission and projection light, and in the future, it is expected to be developed as a favorite for illumination or backlight use, and development is being promoted.
この方向での改善としては、例えば三菱電線工業時報(2002年7月第99号:非特許文献1)には紫外LEDとユーロピウム付活ハロ燐酸塩蛍光体またはユーロピウム付活アルミン酸塩蛍光体、緑色発光蛍光体として銅、アルミニウム付活硫化亜鉛蛍光体またはユーロピウム、マンガン付活アルミン酸塩蛍光体、赤色発光蛍光体としてユーロピウム付活酸硫化イットリウム蛍光体を組合せた白色LEDが報告されている。また特開2000−73052号公報(特許文献1)には紫外LEDとユーロピウム付活ハロ燐酸塩蛍光体またはユーロピウム付活アルミン酸塩蛍光体、緑色発光蛍光体としてユーロピウム、マンガン付活アルミン酸塩蛍光体、赤色発光成分としてユーロピウム付活酸硫化ランタン蛍光体を組合せた白色LEDが報告されている。これらはいずれもタイプ2型の特徴である高い演色性をそなえているものの、輝度の点では未だ不十分であり更なる改善が必要である。
タイプ2型の白色発光LEDで高演色、高輝度を達成するには白色光のスペクトルにおいて、人間の色感度のピークがある450nm近辺,560nm近辺,620nm近辺の光がバランス良く含まれていること、青色、緑色、赤色発光成分の蛍光体の効率がいずれも良くバランスのとれていることが必要である。また、発光色が異なる複数の蛍光体を組み合わせて使用していること等に起因した、発光色度におけるばらつきが発生することも分かってきた。
As an improvement in this direction, for example, Mitsubishi Cable Industrial Time Report (July 2002, No. 99: Non-Patent Document 1) describes an ultraviolet LED and a europium activated halophosphate phosphor or a europium activated aluminate phosphor, A white LED in which copper, aluminum-activated zinc sulfide phosphor or europium, manganese-activated aluminate phosphor, and europium-activated yttrium oxysulfide phosphor are combined as a green light-emitting phosphor has been reported. Japanese Patent Application Laid-Open No. 2000-73052 (Patent Document 1) discloses an ultraviolet LED and europium activated halophosphate phosphor or europium activated aluminate phosphor, europium as a green light emitting phosphor, manganese activated aluminate fluorescence. A white LED in which a europium-activated lanthanum oxysulfide phosphor is combined as a red light emitting component has been reported. All of these have the high color rendering properties that are characteristic of the type 2 type, but are still insufficient in terms of luminance, and further improvement is necessary.
In order to achieve high color rendering and high brightness with a type 2 type white light emitting LED, the white light spectrum must include light in the vicinity of 450 nm, 560 nm, and 620 nm with human color sensitivity peaks in a well-balanced manner. The efficiency of the phosphors of blue, green and red light emitting components must be well balanced. It has also been found that variations in emission chromaticity occur due to a combination of a plurality of phosphors having different emission colors.
タイプ2型の白色LEDの実用化が種々試みられるなか照明用途とバックライト用途ではその開発方向に違いのあることが分かってきた。照明用途の白色LEDは輝度と白色光の質を規定する平均演色指数(Ra)が高いことが重要であるのに対し、バックライト用途では輝度が高く、かつ色再現域が広いことが求められる。照明およびバックライトで輝度が高いことは両者で要求される共通の特性であるが、高平均演色指数、広色再現域はそれぞれのデバイスで要求されるもので必ずしも両立するものではない。
一方、発光色が異なる複数の蛍光体を組み合わせて使用していること等に起因して、発光色度にばらつきが発生することがわかり、このような色度のばらつきは白色LEDを製造する過程において、歩留まりを低下させ、白色LEDを使用したバックライトの色再現性能を低下させることから、色度のばらつきを抑制することが強く求められている。
特に近年成長が著しい液晶テレビ用の白色LEDにおいては従来の冷陰極管で問題となっていた水銀使用の環境問題がなく、かつ色再現域を広げられる可能性のあるところから、その技術開発への期待は大きいものがある。
このような状況下本発明者らは、紫外線あるいは紫色発光ダイオードと、可視光発光蛍光体を3種類以上を組み合わせたタイプ(タイプ2)の開発を進めていくなかで、液晶バックライト用白色LEDランプとして望ましい発光スペクトルおよびそれを実現する蛍光体の組合せ、およびその形態を見出し本発明に至った。
As various types of type 2 white LEDs have been put to practical use, it has been found that there is a difference in the direction of development between illumination use and backlight use. White LEDs for lighting use are required to have a high average color rendering index (Ra) that regulates brightness and quality of white light, whereas backlight applications require high brightness and a wide color reproduction range. . High brightness in illumination and backlight is a common characteristic required by both, but a high average color rendering index and a wide color reproduction range are required by each device and are not necessarily compatible.
On the other hand, it can be seen that there is a variation in emission chromaticity due to a combination of a plurality of phosphors having different emission colors, and this variation in chromaticity is a process of manufacturing a white LED. Therefore, it is strongly desired to suppress variations in chromaticity because the yield is lowered and the color reproduction performance of a backlight using a white LED is lowered.
In particular, white LEDs for LCD TVs, which have been growing rapidly in recent years, are free from the environmental problems associated with the use of mercury, which has been a problem with conventional cold cathode fluorescent lamps. There are great expectations.
Under such circumstances, the present inventors have developed a type (type 2) in which three or more types of ultraviolet or violet light-emitting diodes and visible light-emitting phosphors are combined. The present inventors have found an emission spectrum desirable for a lamp, a combination of phosphors that realize the emission spectrum, and forms thereof, and have reached the present invention.
本発明は上記のような課題を解決するためのものであり、紫外線発光または紫色発光ダイオードと、3種類以上の可視光発光蛍光体を具備する白色LEDの製造方法において、その発光スペクトルが440nm以上460nm以下の青色部、510nm以上530nm以下の緑色部、620nm以上640nm以下の赤色部にピーク値を有し、かつ前記3種類以上の可視光蛍光体を予め結合剤で結合する工程を具備することを特徴とする白色LEDの製造方法である。 The present invention is for solving the above-mentioned problems, and in a method for producing a white LED comprising an ultraviolet light emitting or violet light emitting diode and three or more kinds of visible light emitting phosphors, the emission spectrum thereof is 440 nm or more. Having a peak value in a blue part of 460 nm or less, a green part of 510 nm or more and 530 nm or less, and a red part of 620 nm or more and 640 nm or less, and combining the three or more kinds of visible light phosphors with a binder in advance. This is a method for producing a white LED.
また、青色部、緑色部および赤色部のピークの半値幅が50nm以下であることが好ましい。
また、青色発光蛍光体として
一般式1:(Sr1-x-yBaxCayEuz)10(PO4)6・Cl2
(式中x、y、zはx<0.2、y<0.1、0.005<z<0.1)で表されるユーロピウム付活ハロ燐酸塩蛍光体であることが好ましい。
また、緑色発光蛍光体として
一般式2:(Ba1−x−y−zSrxCayEuz)(Mg1−uMnu)Al10O17
(式中x、y、z、uはx<0.5、y<0.1、0.15<z<0.4、0.3<u<0.6)で表されるユーロピウム、マンガン付活アルミン酸塩蛍光体であることが好ましい。
また、赤色発光蛍光体として
一般式3:(La1−x−yEuxMy)2O2S
(式中Mは元素Sb,Snの少なくとも1種、x及びyは0.01<x<0.15,y<0.03)で表わされるユーロピウム付活酸硫化ランタン蛍光体であることが好ましい。
Moreover, it is preferable that the half value width of the peak of a blue part, a green part, and a red part is 50 nm or less.
In general formula 1 as a blue-emitting phosphor: (Sr 1-xy Ba x Ca y Eu z) 10 (PO 4) 6 · Cl 2
(Wherein x, y, and z are preferably x <0.2, y <0.1, 0.005 <z <0.1) and are europium activated halophosphate phosphors.
In general formula 2 as a green-emitting phosphor: (Ba 1-x-y -z Sr x Ca y Eu z) (Mg 1-u Mn u) Al 10 O 17
(Wherein x, y, z and u are preferably europium and manganese activated aluminate phosphors represented by x <0.5, y <0.1, 0.15 <z <0.4, 0.3 <u <0.6). .
In general formula 3 as the red-emitting phosphor: (La 1-x-y Eu x M y) 2 O 2 S
(Wherein M is at least one of elements Sb and Sn, and x and y are 0.01 <x <0.15, y <0.03), and is preferably a europium activated lanthanum oxysulfide phosphor. .
また、紫外線発光または紫色発光ダイオードの発光波長がそのピーク値において370〜410nmの値を有することが好ましい。
また、本発明の白色LEDの製造方法はバックライトの製造方法およびそれを用いた液晶表示装置の製造方法に好適である。
Moreover, it is preferable that the light emission wavelength of an ultraviolet light emission or a violet light emitting diode has the value of 370-410 nm in the peak value.
The white LED manufacturing method of the present invention is suitable for a backlight manufacturing method and a liquid crystal display manufacturing method using the same.
本発明の白色LEDの製造方法は高輝度を具備し、かつ色再現性も優れ、また発光色度のばらつきを低減する。そのため本発明により製造された白色LEDを用いたバックライトの製造方法並びに本発明により製造されたバックライトを用いた液晶表示装置の製造方法によれば、いずれも高輝度を具備し、色再現性が優れ、かつ発光色度のばらつきが低減されたバックライト並びに液晶表示装置が提供できる。
また、従来の冷陰極管(CCFL)のように水銀を使用する必要もないので環境問題が生じない。
The method for producing a white LED of the present invention has high luminance, excellent color reproducibility, and reduces variations in emission chromaticity. Therefore, according to the manufacturing method of the backlight using the white LED manufactured by the present invention and the manufacturing method of the liquid crystal display device using the backlight manufactured by the present invention, both have high brightness and color reproducibility. In addition, a backlight and a liquid crystal display device in which variation in emission chromaticity is reduced can be provided.
Further, since it is not necessary to use mercury unlike the conventional cold cathode fluorescent lamp (CCFL), there is no environmental problem.
図1に本発明の白色LEDの一例を示す断面図を示した。図1aは発光ダイオード、bは樹脂に埋め込まれた蛍光体層を、cは発光ダイオード及び蛍光体の発光を外部へ導く反射層を、dは発光部を支える樹脂枠を示している。LEDランプに印加された電気エネルギーは発光ダイオードにより紫外光あるいは紫色光に変換され、それらの光が発光ダイオード上部の蛍光体層によりより長波長の光に変換され、総計として白色光がLEDランプ外へ放出される仕組みになっている。
紫外線発光ダイオードまたは紫色発光ダイオードはInGaN系、GaN系、AlGaN系のダイオードなど様々なものが適用可能である。特に発光波長のピーク値が360〜420nmの発光ダイオードであると、後述の蛍光体との組合せにより、高輝度かつ色再現性のより優れた白色LEDを為し得ることができる。
FIG. 1 is a sectional view showing an example of the white LED of the present invention. 1a shows a light emitting diode, b shows a phosphor layer embedded in a resin, c shows a reflection layer that guides the light emission of the light emitting diode and the phosphor to the outside, and d shows a resin frame that supports the light emitting part. Electric energy applied to the LED lamp is converted into ultraviolet light or violet light by the light emitting diode, and the light is converted into longer wavelength light by the phosphor layer on the top of the light emitting diode. It has a mechanism to be released.
Various ultraviolet light emitting diodes or violet light emitting diodes such as InGaN-based, GaN-based, and AlGaN-based diodes can be applied. In particular, when the light emitting diode has a peak value of emission wavelength of 360 to 420 nm, a white LED having higher luminance and better color reproducibility can be obtained by combination with a phosphor described later.
蛍光体層bに用いる蛍光体としては可視光発光蛍光体を3種以上用い、予め結合剤で結合されていることが重要である。具体的には、その発光スペクトルが440nm以上460nm以下の青色部、510nm以上530nm以下の緑色部、620nm以上640nm以下の赤色部にそれぞれピーク値を有する蛍光体を用い、結合剤で結合する。つまり、ピーク波長440nm以上460nm以下の青色蛍光体、ピーク波長510nm以上530nm以下の緑色蛍光体、ピーク波長620nm以上640nm以下の赤色蛍光体をそれぞれ用いることにより可視光発光蛍光体が3種となり、これらを結合剤で結合する。また、同じ色の蛍光体を2種以上用いれば、可視光発光蛍光体が3種以上となる。
例えば図1のような白色LEDの場合、発光ダイオードaに印加された電気エネルギーは発光ダイオードにより紫外光(あるいは紫色光)に変換され、それらの光が発光ダイオード上部の蛍光体層によりより長波長の光に変換され、総計として白色光がLED外へ放出される仕組みになっている。
なお、本発明では発光ダイオードaに用いられる紫外線発光ダイオードまたは紫色発光ダイオードは発光ダイオードと表記し、完成した白色発光ダイオードに関しては白色LEDと表記する。
As the phosphor used for the phosphor layer b, it is important that three or more kinds of visible light emitting phosphors are used and bonded in advance with a binder. Specifically, phosphors whose emission spectra have peak values in a blue part of 440 nm to 460 nm, a green part of 510 nm to 530 nm, and a red part of 620 nm to 640 nm, respectively, are bonded with a binder. That is, by using a blue phosphor having a peak wavelength of 440 nm to 460 nm, a green phosphor having a peak wavelength of 510 nm to 530 nm, and a red phosphor having a peak wavelength of 620 nm to 640 nm, there are three types of visible light emitting phosphors. Are bound with a binder. If two or more phosphors of the same color are used, the number of visible light emitting phosphors is three or more.
For example, in the case of a white LED as shown in FIG. 1, the electrical energy applied to the light emitting diode a is converted into ultraviolet light (or violet light) by the light emitting diode, and the light has a longer wavelength due to the phosphor layer above the light emitting diode. The total amount of white light is emitted to the outside of the LED.
In the present invention, an ultraviolet light emitting diode or a purple light emitting diode used for the light emitting diode a is referred to as a light emitting diode, and a completed white light emitting diode is referred to as a white LED.
図2に、図1のような構成の本発明の白色LEDの発光スペクトルの一例を示した。電流値20mAでピーク値400nm紫外線発光ダイオードを発光させ蛍光体により色度(0.253,0.238)の白色光に変換した時のものである。447nmの青色部、518nmの緑色部、623nmの赤色部にピーク値を有し、さらに各ピークの半値幅がそれぞれ50nm以下であることを特徴としている。
図3には本発明の白色LEDの発光を液晶ディスプレイ(液晶表示装置)で使われる一般的な青色、緑色、赤色のカラーフィルターを通しその発光色をCIE色度図にプロットしたものである。その色度図において青色、緑色、赤色の発光点を結んで得られる三角形の内部の色度の光をその液晶ディスプレイは表現できることを意味している。
三角形の面積が広いほうが多くの色度の光を表現でき、その液晶ディスプレイは色再現域が広い(色再現性が良い)ことになる。図3には従来の冷陰極管を用いた液晶ディスプレイの色再現域も示されているが、明らかに本発明の色再現域の方が広く優れたものであることが分かる。
FIG. 2 shows an example of the emission spectrum of the white LED of the present invention having the configuration as shown in FIG. This is a case where an ultraviolet light emitting diode having a current value of 20 mA and a peak value of 400 nm is made to emit light and converted into white light of chromaticity (0.253, 0.238) by a phosphor. It has a peak value in a blue part of 447 nm, a green part of 518 nm, and a red part of 623 nm, and the half width of each peak is 50 nm or less.
FIG. 3 is a graph in which the emitted light of the white LED of the present invention is passed through common blue, green and red color filters used in a liquid crystal display (liquid crystal display device), and the emitted color is plotted in a CIE chromaticity diagram. In the chromaticity diagram, this means that the liquid crystal display can express light having chromaticity inside a triangle obtained by connecting light emitting points of blue, green, and red.
The wider the triangular area, the more chromaticity light can be expressed, and the liquid crystal display has a wide color reproduction range (good color reproducibility). FIG. 3 also shows the color gamut of a liquid crystal display using a conventional cold cathode tube, but it can be clearly seen that the color gamut of the present invention is broader and better.
図3には同時に理想的な色再現域を示す国際標準(NTSC)も示した。色再現域の広さはこのNTSCの三角形の面積を100としたときの相対値で示され、本発明の液晶ディスプレイの色再現域は98であるのに対し従来の冷陰極管液晶ディスプレイのそれは65であった。
上記のように青色部、緑色部、赤色部のピーク値の半値幅が50nm以下であることが好ましい。例えば、図4に、本発明の蛍光体を組合せて得られる白色LEDにおいて、青色・緑色・赤色のピーク値の半値幅が50nm以下のもの(製品1)と一部の半値幅が50nmを超えたもの(製品2)を用意し、その発光スペクトルを比較した。また、製品1および製品2を用いた液晶ディスプレイの色再現域を図5に示した。これらの色再現域は対NTSCで製品1が98であり、製品2が87であった。
製品2の色再現域は冷陰極管のそれよりは優れているものの、製品1の色再現域よりは劣っている。その理由は製品2のスペクトルが本発明と同様447nmの青色部、518nmの緑色部、623nmの赤色部にピーク値を有しているものの、青色ピークの半値幅が60nmと広く青色成分の純度が悪いためである。なお、各ピークの半値幅はすべてが50nm以下であることが最も好ましいが、半値幅の最大値は80nm以下であれば実用に値する。特に青色・緑色・赤色のうち1種のみが半値幅80nmで、残り2種が50nm以下であれば色再現域は対NTSCで80以上とすることができる。従って、各ピーク値の半値幅は、好ましくは80nm以下、さらに好ましくは50nm以下となる。
上記のように、440nm以上460nm以下の青色部、510nm以上530nm以下の緑色部、620nm以上640nm以下の赤色部の各ピーク値を具備し、その半値幅が70nm以下、さらには50nm以下の特性を具備する蛍光体を用いることにより、高輝度を具備し、かつ色再現性の優れた白色LEDを為し得ることができる。
FIG. 3 also shows an international standard (NTSC) showing an ideal color gamut. The width of the color gamut is shown as a relative value when the area of the NTSC triangle is 100, and the color gamut of the liquid crystal display of the present invention is 98, whereas that of the conventional cold cathode tube liquid crystal display is 65.
As described above, the full width at half maximum of the peak value of the blue portion, the green portion, and the red portion is preferably 50 nm or less. For example, in the white LED obtained by combining the phosphor of the present invention in FIG. 4, the half-value width of the blue, green, and red peak values is 50 nm or less (product 1) and some of the half-value widths exceed 50 nm. The product (Product 2) was prepared and the emission spectra were compared. FIG. 5 shows the color gamut of the liquid crystal display using the products 1 and 2. These color gamuts were 98 for product 1 and 87 for product 2 versus NTSC.
Although the color gamut of product 2 is superior to that of the cold cathode tube, it is inferior to that of product 1. The reason for this is that although the spectrum of product 2 has peak values in the blue part of 447 nm, the green part of 518 nm, and the red part of 623 nm as in the present invention, the half-value width of the blue peak is wide as 60 nm and the purity of the blue component is high. This is because it is bad. In addition, it is most preferable that the full width at half maximum of each peak is 50 nm or less, but if the maximum value of the full width at half maximum is 80 nm or less, it is practical. In particular, if only one of blue, green, and red has a half-value width of 80 nm and the remaining two types are 50 nm or less, the color reproduction range can be 80 or more for NTSC. Accordingly, the half width of each peak value is preferably 80 nm or less, more preferably 50 nm or less.
As described above, it has peak values of a blue portion of 440 nm to 460 nm, a green portion of 510 nm to 530 nm, and a red portion of 620 nm to 640 nm, and the half-value width is 70 nm or less, and further has a characteristic of 50 nm or less. By using the phosphor provided, a white LED having high luminance and excellent color reproducibility can be obtained.
次に、蛍光体について説明する。蛍光体の組成については、上記特性を具備するものであれば特に限定されるものではないが、好ましい一例として次のものが挙げられる。
青色発光蛍光体としては
一般式1:(Sr1-x-yBaxCayEuz)10(PO4)6・Cl2
(式中x、y、zはx<0.2、y<0.1、0.005<z<0.1)で表されるユーロピウム付活ハロ燐酸塩蛍光体が挙げられる。一般式1においてx値およびy値は0(ゼロ)を含むものとする。
また、緑色発光蛍光体としては
一般式2:(Ba1−x−y−zSrxCayEuz)(Mg1−uMnu)Al10O17
(式中x、y、z、uはx<0.5、y<0.1、0.15<z<0.4、0.3<u<0.6)で表されるユーロピウム、マンガン付活アルミン酸塩蛍光体が挙げられる。なお、一般式2においてx値およびy値は0(ゼロ)を含むものとする。
また、赤色発光蛍光体として一般式3:(La1−x−yEuxMy)2O2S
(式中Mは元素Sb,Snの少なくとも1種、x及びyは0.01<x<0.15,y<0.03)で表わされるユーロピウム付活酸硫化ランタン蛍光体が挙げられる。なお、一般式3においてy値は0(ゼロ)を含むものとする。
Next, the phosphor will be described. Although it will not specifically limit if it has the said characteristic about the composition of a fluorescent substance, The following are mentioned as a preferable example.
General formula as a blue-emitting phosphor 1: (Sr 1-xy Ba x Ca y Eu z) 10 (PO 4) 6 · Cl 2
(Wherein, x, y, and z are x <0.2, y <0.1, 0.005 <z <0.1) and europium activated halophosphate phosphors. In the general formula 1, the x value and the y value include 0 (zero).
Also, as the green-emitting phosphor general formula 2: (Ba 1-x- y-z Sr x Ca y Eu z) (Mg 1-u Mn u) Al 10 O 17
(Wherein x, y, z and u are x <0.5, y <0.1, 0.15 <z <0.4, 0.3 <u <0.6) and europium and manganese activated aluminate phosphors. In the general formula 2, the x value and the y value include 0 (zero).
In general formula 3 as the red-emitting phosphor: (La 1-x-y Eu x M y) 2 O 2 S
(Wherein M is at least one of the elements Sb and Sn, and x and y are 0.01 <x <0.15, y <0.03), and a europium activated lanthanum oxysulfide phosphor. In the
蛍光体の平均粒径は特に限定されるものではないが平均粒径3μm以上が好ましい。平均粒径が3μm以上、つまりは粒径が大きい方が高輝度を得やすい。平均粒径の上限については特に限定は無く、白色LEDの構造に合わせて適宜決めるものとするが、あまり大きすぎると均一に混ざり難いことから上限は平均粒径50μm以下が好ましい。また、各蛍光体の混合比率については目的とする色度になるような比率であれば任意であるが、白色LEDを得るためには青色蛍光体を15〜25wt%、緑色蛍光体を15〜25wt%、赤色蛍光体が残部(青色蛍光体、緑色蛍光体、赤色蛍光体の合計が100wt%)が好ましい。 The average particle diameter of the phosphor is not particularly limited, but an average particle diameter of 3 μm or more is preferable. Higher brightness is easily obtained when the average particle size is 3 μm or more, that is, the larger the particle size. The upper limit of the average particle diameter is not particularly limited and is appropriately determined according to the structure of the white LED. However, the upper limit is preferably 50 μm or less because it is difficult to mix uniformly if it is too large. The mixing ratio of the phosphors is arbitrary as long as the target chromaticity is achieved, but in order to obtain a white LED, 15 to 25 wt% of the blue phosphor and 15 to 25% of the green phosphor. The remaining amount is preferably 25 wt% and the red phosphor (the total of the blue phosphor, the green phosphor and the red phosphor is 100 wt%).
これらの可視光発光蛍光体を予め結合剤で結合してから樹脂と混ぜ合わせて混合蛍光体を作製し、出来上がった混合蛍光体を、発光ダイオード上に塗布し、樹脂を固めることにより、白色LEDを形成することができる。予め蛍光体を結合してから用いることで、色度のばらつきを低減することができる。例えば、白色LEDランプを構成する青色、緑色、および赤色発光蛍光体のうち、赤色発光蛍光体が青色および緑色発光蛍光体に比べて比重が大きい場合、これら3色の蛍光体を単に混合しただけでは、樹脂の硬化処理前に赤色発光蛍光体だけが早く沈降してしまう。このような沈降速度の差に起因する蛍光体の分散状態の不均一性が、発光色度のばらつきを生じさせていたものと考えられる。そこで、青色、緑色、赤色の各色発光蛍光体を予め一体化した状態で、透明樹脂に分散させることによって、各蛍光体の透明樹脂中での分散状態を均一化させることができる。
上述した青色、緑色、赤色の各色発光蛍光体を予め結合した蛍光体は、例えば以下のようにして得ることができる。まず、青色、緑色、赤色の各色発光蛍光体を水に投入して懸濁液とする。この懸濁液を撹拌しながら、無機結合剤として微粉化したアルカリ土類ホウ酸塩等を加え、この状態で一定時間撹拌する。無機結合剤は青色、緑色、赤色の各色発光蛍光体の合計量に対して0.01〜0.3質量%の割合で添加することが好ましい。この後、撹拌を停止して蛍光体を沈降させ、ろ過、乾燥、さらに300℃以上の温度で数時間ベーキングしたものに篩分け等の処理を施すことによって、複数の蛍光体を結合した蛍光体を得ることができる。また、青色、緑色、赤色の各色発光蛍光体にアクリル樹脂等の有機結合剤を各色発光蛍光体の合計量に対して、例えば0.01〜0.3質量%の割合で添加、混合し、乾燥後篩分け等の処理を施すことによっても得ることができる。
なお、白色LEDに用いる基板や金属枠等の構成は任意である。
以上のような本発明の白色LEDの製造方法は高輝度を維持しつつ色再現性も優れており、発光色度のばらつきを低減することから、携帯電話やモバイル等の携帯通信機器、パーソナルコンピュータ周辺機器、OA機器、家庭用電気機器、オーディオ機器、各種スイッチ、バックライト用光源表示板等の各種表示装置に用いられる液晶表示装置のバックライトの製造方法に有効であり、それを用いた液晶表示装置の製造方法は高輝度かつ色再現性が優れ、発光色度のばらつきを低減した、高品質な製品が提供できる。特に、色度ばらつきが小さいことから白色LEDランプを複数個用いるバックライトの製造方法に用いたとしても均一な白色を有する面光源を得ることができる。従って、それを用いた液晶表示装置の特性も向上する。また、本発明のバックライトの製造方法は、サイドライト方式、直下型方式どちらでも適用できる。
These visible-light-emitting phosphors are combined with a binder in advance and mixed with a resin to produce a mixed phosphor. The resulting mixed phosphor is applied onto a light-emitting diode, and the resin is solidified to obtain a white LED. Can be formed. Variation in chromaticity can be reduced by using the phosphor after being combined in advance. For example, among the blue, green, and red light emitting phosphors that make up a white LED lamp, when the specific gravity of the red light emitting phosphor is larger than that of the blue and green light emitting phosphors, these three color phosphors are simply mixed. Then, only the red light-emitting phosphor settles quickly before the resin curing treatment. It is considered that the non-uniformity of the dispersed state of the phosphor due to such a difference in the sedimentation speed caused variations in emission chromaticity. Therefore, the dispersion state of each phosphor in the transparent resin can be made uniform by dispersing the blue, green, and red light emitting phosphors in a transparent resin in a previously integrated state.
A phosphor in which the above-described blue, green, and red light emitting phosphors are combined in advance can be obtained, for example, as follows. First, blue, green and red light emitting phosphors are put into water to form a suspension. While this suspension is being stirred, finely ground alkaline earth borate or the like is added as an inorganic binder, and this state is stirred for a certain time. The inorganic binder is preferably added at a ratio of 0.01 to 0.3% by mass with respect to the total amount of the blue, green and red light emitting phosphors. Thereafter, the stirring is stopped, the phosphor is settled, filtered, dried, and further subjected to treatment such as sieving after baking at a temperature of 300 ° C. or higher for several hours, thereby combining a plurality of phosphors. Can be obtained. In addition, an organic binder such as an acrylic resin is added to each color light-emitting phosphor of blue, green, and red with respect to the total amount of each color light-emitting phosphor, for example, in a ratio of 0.01 to 0.3 mass%, mixed, and sieved after drying. It can also be obtained by performing such a process.
In addition, the structure of the board | substrate used for white LED, a metal frame, etc. is arbitrary.
The white LED manufacturing method of the present invention as described above is excellent in color reproducibility while maintaining high luminance, and reduces variations in emission chromaticity. Therefore, mobile communication devices such as mobile phones and mobiles, personal computers, and the like. It is effective in a method for manufacturing a backlight of a liquid crystal display device used in various display devices such as peripheral devices, OA devices, household electric devices, audio devices, various switches, and backlight light source display plates, and liquid crystal using the same. The manufacturing method of the display device can provide a high-quality product with high luminance, excellent color reproducibility, and reduced variation in emission chromaticity. In particular, since the chromaticity variation is small, a surface light source having a uniform white color can be obtained even when used in a backlight manufacturing method using a plurality of white LED lamps. Therefore, the characteristics of the liquid crystal display device using the same are also improved. In addition, the backlight manufacturing method of the present invention can be applied to either a sidelight system or a direct type.
次に実施例について説明する。
本実施例の白色LEDの評価は、横断面が図1のような構造を採用した。発光ダイオードはサイズ300μm四方のチップを配し、60mAの電流値にて発光させ、液晶ディスプレイで一般に使われる青色、緑色、赤色のカラーフィルターを通した。その光を積分球に導き青色、緑色、赤色の発光色を評価し、ディスプレイにしたときの色再現域(色再現性)を評価した。色再現性については前述の通り対NTSCとの面積比で示した。また白色LEDの輝度はフィルターを通さずに評価した。
色再現性評価はInstrument Systems社製CAS 140 COMPACT ARRAY SPECTROMETER、白色LEDの輝度は大塚電子社製MCPD装置を使い行った。
Next, examples will be described.
For the evaluation of the white LED of this example, the structure as shown in FIG. The light emitting diodes were arranged in a 300 μm square chip, emitted light at a current value of 60 mA, and passed through blue, green and red color filters generally used in liquid crystal displays. The light was guided to an integrating sphere, and the blue, green, and red emission colors were evaluated, and the color reproduction range (color reproducibility) when the display was made was evaluated. As described above, the color reproducibility is shown by the area ratio with respect to NTSC. The brightness of the white LED was evaluated without passing through a filter.
The color reproducibility evaluation was performed using CAS 140 COMPACT ARRAY SPECTROMETER manufactured by Instrument Systems, and the brightness of white LED using an MCPD apparatus manufactured by Otsuka Electronics.
<LEDランプの作製方法>
3種類以上の蛍光体は、LEDランプの色度がx=0.250−0.255,y=0.235−0.240の範囲に入るように調合され、予め結合する。この結合された蛍光体をシリコーン樹脂と30質量%、または40質量%の比率で混合し、スラリーを作製した。得られたスラリーの一部を抜取り、図1のように配置されたLEDに滴下し、100〜150℃の温度で熱処理、シリコーン樹脂を硬化し白色LEDランプを得た。
なお、実施例、比較例においては発光ダイオードの発光波長のピーク値が399nmにある発光ダイオードを使用した。
<Production method of LED lamp>
Three or more kinds of phosphors are prepared so that the chromaticity of the LED lamp is in the range of x = 0.250−0.255 and y = 0.235−0.240, and are combined in advance. This bonded phosphor was mixed with a silicone resin at a ratio of 30% by mass or 40% by mass to prepare a slurry. A part of the obtained slurry was extracted and dropped onto the LED arranged as shown in FIG. 1, and heat treatment was performed at a temperature of 100 to 150 ° C. to cure the silicone resin, thereby obtaining a white LED lamp.
In Examples and Comparative Examples, a light emitting diode having a light emitting diode peak value of 399 nm was used.
(実施例1)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.99Eu0.01)10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.726Eu0.274)(Mg0.55Mn0.45)Al10O17、赤色蛍光体ユーロピウム付活酸硫化ランタン(La0.883Sb0.002Eu0.115)2O2Sを20.1%、19.5%、60.4%の割合で予め結合し、シリコーン樹脂と40質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。ここで、結合した3色混合蛍光体は以下の工程により得た。まず、各色発光蛍光体を水に投入して懸濁液とし、この懸濁液を撹拌しながらホウ酸バリウム・カルシウム(3(Ba,Ca)O・B2O3)を各色発光蛍光体の合計量に対して0.1重量%の割合で添加した。撹拌を30分間継続した後に停止し、蛍光体を沈降させた。次いで、これをろ過してベーキングした後に200メッシュのナイロン篩にかけて、結合された3色混合蛍光体を得た。
Example 1
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.99 Eu 0.01 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.726 Eu 0.274 ) (Mg 0.55 Mn 0.45 ) Al 10 O 17 , red phosphor europium activated lanthanum oxysulfide (La 0.883 Sb 0.002 Eu 0.115 ) 2 O 2 S was previously bonded in the ratio of 20.1%, 19.5%, 60.4%. A slurry was prepared by mixing with a silicone resin at a concentration of 40% by mass. This slurry was applied onto a light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example. Here, the combined three-color mixed phosphor was obtained by the following steps. First, each color light emitting phosphor is put into water to form a suspension, and while stirring this suspension, barium calcium borate (3 (Ba, Ca) O.B 2 O 3 ) is added to each color light emitting phosphor. It added in the ratio of 0.1 weight% with respect to the total amount. Stirring was continued for 30 minutes and then stopped to allow the phosphor to settle. Next, this was filtered and baked and then passed through a 200 mesh nylon sieve to obtain a combined three-color mixed phosphor.
(実施例2)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.97Ca0.02Eu10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.726Eu0.274)(Mg0.50Mn0.50)Al10O17、赤色蛍光体ユーロピウム付活酸硫化ランタン(La0.884Sb0.001Eu0.115)2O2Sを18.8%、19.4%、61.8%の割合で予め結合し、シリコーン樹脂と40質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。ここで、結合した3色混合蛍光体は以下の工程により得た。まず各色発光蛍光体にアクリル樹脂エマルジョンを各色発光蛍光体の合計量に対して固形分で0.1質量%の割合で添加し、これらを混合した。次いで、この混合物を120℃で乾燥させた後、ナイロンメッシュにかけて結合された3色混合蛍光体を得た。
(Example 2)
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.97 Ca 0.02 Eu 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.726 Eu 0.274 ) (Mg 0.50 Mn 0.50 ) Al 10 O 17 , red phosphor europium activated lanthanum oxysulfide (La 0.884 Sb 0.001 Eu 0.115 ) 2 O 2 S was previously bonded at a ratio of 18.8%, 19.4%, 61.8%. The slurry was mixed with a silicone resin at a concentration of 40% by mass to apply a slurry onto the light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example. The three-color mixed phosphor was obtained by the following steps: First, an acrylic resin emulsion was added to each color light-emitting phosphor at a solid content of 0.1% by mass with respect to the total amount of each color light-emitting phosphor. The mixture was then dried at 120 ° C., and a three-color mixed phosphor bonded to a nylon mesh was obtained.
(実施例3)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.99Eu0.01)10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.25Sr0.475Eu0.275)(Mg0.55Mn0.45)Al10O17、赤色蛍光体ユーロピウム付活酸硫化ランタン(La0.883Sn0.002Eu0.115)2O2Sを18.7%、19.5%、61.8%の割合で実施例1による結合工程により予め結合し、シリコーン樹脂と40質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。
(Example 3)
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.99 Eu 0.01 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.25 Sr 0.475 Eu 0.275 ) ( Mg 0.55 Mn 0.45 ) Al 10 O 17 , red phosphor europium activated lanthanum oxysulfide (La 0.883 Sn 0.002 Eu 0.115 ) 2 O 2 S at a rate of 18.7%, 19.5%, 61.8% The slurry was preliminarily bonded by the bonding step according to Example 1 and mixed with a silicone resin at a concentration of 40% by mass to prepare a slurry. This slurry was applied onto a light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example.
(実施例4)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.75Ba0.23Ca0.01Eu0.01)10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.756Eu0.274)(Mg0.55Mn0.45)Al10O17、赤色蛍光体としてユーロピウム付活酸硫化ランタン(La0.883Sn0.002Eu0.115)2O2Sを18.9%、19.5%、61.6%の割合で実施例1による結合工程により、予め結合し、シリコーン樹脂と40質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。
Example 4
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.75 Ba 0.23 Ca 0.01 Eu 0.01 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.756 Eu 0.274 ) (Mg 0.55 Mn 0.45 ) Al 10 O 17 , europium activated lanthanum oxysulfide (La 0.883 Sn 0.002 Eu 0.115 ) 2 O 2 S as red phosphor, 18.9%, 19.5%, 61.6% By the bonding step according to Example 1 in proportion, it was previously bonded and mixed with a silicone resin at a concentration of 40% by mass to prepare a slurry. This slurry was applied onto a light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example.
(実施例5)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.98Eu0.02)10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.756Eu0.274)(Mg0.60Mn0.40)Al10O17、赤色蛍光体ユーロピウム付活酸硫化ランタン(La0.883Sb0.002Eu0.115)2O2Sを18.8%、19.4%、61.8%の割合で実施例1による結合工程により予め結合し、シリコーン樹脂と40質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。
(Example 5)
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.98 Eu 0.02 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.756 Eu 0.274 ) (Mg 0.60 Mn 0.40 ) Al 10 O 17 , red phosphor europium activated lanthanum oxysulfide (La 0.883 Sb 0.002 Eu 0.115 ) 2 O 2 S in the proportions of 18.8%, 19.4%, 61.8% Example 1 The slurry was preliminarily bonded by the bonding step by and mixed with the silicone resin at a concentration of 40% by mass to prepare a slurry. This slurry was applied onto a light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example.
(実施例6)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.97Ca0.02Eu0.01)10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.35Sr0.375Eu0.275)(Mg0.55Mn0.45)Al10O17、赤色蛍光体ユーロピウム付活酸硫化ランタン(La0.884Sb0.001Eu0.115)2O2Sを18.5%、19.2%、62.3%の割合で実施例1による結合工程により予め結合し、シリコーン樹脂と40質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。
(Example 6)
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.97 Ca 0.02 Eu 0.01 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.35 Sr 0.375 Eu 0.275 ) (Mg 0.55 Mn 0.45 ) Al 10 O 17 , red phosphor europium activated lanthanum oxysulfide (La 0.884 Sb 0.001 Eu 0.115 ) 2 O 2 S 18.5%, 19.2%, 62.3% Then, they were previously bonded by the bonding step according to Example 1 and mixed with a silicone resin at a concentration of 40% by mass to prepare a slurry. This slurry was applied onto a light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example.
(実施例7)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.99Eu0.01)10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.75Eu0.25)(Mg0.55Mn0.45)Al10O17、赤色蛍光体ユーロピウム付活酸硫化ランタン(La0.883Sb0.002Eu0.115)2O2Sを18.8%、19.5%、61.7%の割合で実施例1による結合工程により予め結合し、シリコーン樹脂と40質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。
(Example 7)
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.99 Eu 0.01 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.75 Eu 0.25 ) (Mg 0.55 Example 1 Mn 0.45 ) Al 10 O 17 , red phosphor europium activated lanthanum oxysulfide (La 0.883 Sb 0.002 Eu 0.115 ) 2 O 2 S in proportions of 18.8%, 19.5%, 61.7% The slurry was preliminarily bonded by the bonding step by and mixed with the silicone resin at a concentration of 40% by mass to prepare a slurry. This slurry was applied onto a light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example.
(実施例8)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.99Eu0.01)10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.726Eu0.274)(Mg0.55Mn0.45)Al10O17、赤色蛍光体ユーロピウム付活酸硫化ランタン(La0.883Sb0.002Eu0.115)2O2Sを18.7%、19.6%、61.7%の割合で実施例1による結合工程により予め結合し、シリコーン樹脂と30質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。
(Example 8)
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.99 Eu 0.01 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.726 Eu 0.274 ) (Mg 0.55 Example 1 Mn 0.45 ) Al 10 O 17 , red phosphor europium activated lanthanum oxysulfide (La 0.883 Sb 0.002 Eu 0.115 ) 2 O 2 S in proportions of 18.7%, 19.6%, 61.7% The slurry was preliminarily bonded by the bonding step of and mixed with a silicone resin at a concentration of 30% by mass to prepare a slurry. This slurry was applied onto a light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example.
(実施例9)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.97Eu0.03)10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.75Eu0.25)(Mg0.55Mn0.45)Al10O17、赤色蛍光体ユーロピウム付活酸硫化ランタン(La0.883Sn0.002Eu0.115)2O2Sを18.9%、19.5%、61.6%の割合で実施例1による結合工程により予め結合し、シリコーン樹脂と40質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。
Example 9
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.97 Eu 0.03 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.75 Eu 0.25 ) (Mg 0.55 Example 1 Mn 0.45 ) Al 10 O 17 , red phosphor europium activated lanthanum oxysulfide (La 0.883 Sn 0.002 Eu 0.115 ) 2 O 2 S in proportions of 18.9%, 19.5%, 61.6% The slurry was preliminarily bonded by the bonding step by and mixed with the silicone resin at a concentration of 40% by mass to prepare a slurry. This slurry was applied onto a light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example.
(実施例10)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.99Eu0.01)10(PO4)6・Cl2、緑色蛍光体ユーロピウム、マンガン付活アルミン酸塩蛍光体(Ba0.726Eu0.274)(Mg0.55Mn0.45)Al10O17、赤色蛍光体ユーロピウム付活酸硫化ランタン(La0.882Sb0.003Eu0.115)2O2Sを18.8%、19.4%、61.8%の割合で実施例1による結合工程により予め結合し、シリコーン樹脂と30質量%の濃度で混合しスラリーを作製した。このスラリーを発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、本実施例の白色LEDを得た。
(Example 10)
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.99 Eu 0.01 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor europium, manganese activated aluminate phosphor (Ba 0.726 Eu 0.274 ) (Mg 0.55 Example 1 Mn 0.45 ) Al 10 O 17 , red phosphor europium activated lanthanum oxysulfide (La 0.882 Sb 0.003 Eu 0.115 ) 2 O 2 S in proportions of 18.8%, 19.4% and 61.8% The slurry was preliminarily bonded by the bonding step of and mixed with a silicone resin at a concentration of 30% by mass to prepare a slurry. This slurry was applied onto a light emitting diode, and the resin was cured by a heat treatment at 140 ° C. to obtain a white LED of this example.
(比較例1)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.59Ba0.39Ca0.01Eu0.01)10(PO4)6・Cl2、緑色蛍光体銅、アルミニウム付活硫化亜鉛蛍光体ZnS:Cu,Al、赤色蛍光体としてユーロピウム付活酸硫化イットリウム(Y0.94Eu0.06)2O2Sをそれぞれシリコーン樹脂と30質量%の濃度で混合した。次にこれらのスラリーを18,8%、19.4%、61.8%の割合で混ぜた後、発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化、比較例1の白色LEDを得た。なお、比較例1では蛍光体の結合工程は行わなかった。
(比較例2)
青色蛍光体ユーロピウム付活アルカリ土類クロロリン酸塩(Sr0.59Ba0.39Ca0.01Eu0.01)10(PO4)6・Cl2、緑色発光蛍光体としてユーロピウム、マンガン付活アルミン酸塩蛍光体緑色蛍光体(Ba0.864Eu0.136)(Mg0.74Mn0.26)Al10O17赤色蛍光体としてユーロピウム付活酸硫化イットリウム(Y0.94Eu0.06)2O2Sをそれぞれシリコーン樹脂と30質量%の濃度で混合した。次にこれらのスラリーを18.7%、19,5%、61.8%の割合で混ぜた後、発光ダイオード上に塗布し、140℃の熱処理で樹脂を硬化し、比較例2の白色LEDを得た。なお、比較例2では蛍光体の結合工程は行わなかった。
(Comparative Example 1)
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.59 Ba 0.39 Ca 0.01 Eu 0.01 ) 10 (PO 4 ) 6 · Cl 2 , green phosphor copper, aluminum activated zinc sulfide phosphor ZnS: Cu, Al, Europium activated yttrium oxysulfide (Y 0.94 Eu 0.06 ) 2 O 2 S was mixed as a red phosphor with a silicone resin at a concentration of 30% by mass. Next, these slurries were mixed at a ratio of 18.8%, 19.4%, and 61.8%, and then applied onto the light emitting diode, and the resin was cured by heat treatment at 140 ° C., and the white LED of Comparative Example 1 was obtained. Obtained. In Comparative Example 1, the phosphor bonding step was not performed.
(Comparative Example 2)
Blue phosphor europium activated alkaline earth chlorophosphate (Sr 0.59 Ba 0.39 Ca 0.01 Eu 0.01 ) 10 (PO 4 ) 6 · Cl 2 , europium as a green emitting phosphor, manganese activated aluminate phosphor green phosphor Europium-activated yttrium oxysulfide (Y 0.94 Eu 0.06 ) 2 O 2 S was mixed with a silicone resin at a concentration of 30% by mass as (Ba 0.864 Eu 0.136 ) (Mg 0.74 Mn 0.26 ) Al 10 O 17 red phosphor. Next, these slurries were mixed at a ratio of 18.7%, 19.5%, and 61.8%, and then applied onto the light emitting diode, and the resin was cured by heat treatment at 140 ° C. Got. In Comparative Example 2, the phosphor binding step was not performed.
表1には、得られた白色LEDおよびそれをバックライトに用いた液晶ディスプレイ(液晶表示装置)に40mAの電流を流し点灯させ、その発光の色再現域および輝度を測定した。さらに従来例(比較例3)として冷陰極管をバックライトに用いた場合の色再現域および輝度を同時に示した。
なお、各白色LEDの発光スペクトルを測定したところ、本実施例に係る白色LEDはいずれも440nm以上460nm以下の青色部、510nm以上530nm以下の緑色部、620nm以上640nm以下の赤色部にピーク値を具備し、各色のピーク波長の半値幅は50nm以下であった。
それに対し、比較例1のものは緑色部および赤色部の波長ピークが本発明の範囲外であり、比較例2は赤色部の波長ピークのみが本発明の範囲外であった。
In Table 1, the obtained white LED and a liquid crystal display (liquid crystal display device) using the white LED as a backlight were turned on by passing a current of 40 mA, and the color reproduction range and luminance of the emitted light were measured. Further, as a conventional example (Comparative Example 3), the color gamut and luminance in the case where a cold cathode tube is used for the backlight are shown simultaneously.
In addition, when the emission spectrum of each white LED was measured, all of the white LEDs according to this example had peak values in a blue portion of 440 nm to 460 nm, a green portion of 510 nm to 530 nm, and a red portion of 620 nm to 640 nm. And the full width at half maximum of the peak wavelength of each color was 50 nm or less.
In contrast, in Comparative Example 1, the wavelength peaks of the green part and the red part were outside the scope of the present invention, and in Comparative Example 2, only the wavelength peak of the red part was outside the scope of the present invention.
表から分かる通り、本実施例に係る白色LEDおよびそれをバックライトに用いた液晶表示装置は、色再現性が90以上、輝度390mcd以上の優れた特性を示すことが分かった。
(実施例11〜14)
次に、発光ダイオードの発光波長を表2のように変えた以外は実施例1と同様の白色LEDを作製し、同様の測定を行った。但し青色、緑色、赤色蛍光体の配合比率は色度がx=0.250−0.255,y=0.235−0.240の範囲に入るよう調整した。
As can be seen from the table, it was found that the white LED according to this example and the liquid crystal display device using the white LED as a backlight showed excellent characteristics of color reproducibility of 90 or more and luminance of 390 mcd or more.
(Examples 11-14)
Next, a white LED similar to that of Example 1 was prepared and the same measurement was performed except that the emission wavelength of the light emitting diode was changed as shown in Table 2. However, the mixing ratio of the blue, green and red phosphors was adjusted so that the chromaticity was in the range of x = 0.250-0.255 and y = 0.235-0.240.
表から分かる通り、発光ダイオードの発光波長は370nm以上410nm以下が好ましいことが分かった。 As can be seen from the table, the light emission wavelength of the light emitting diode is preferably 370 nm or more and 410 nm or less.
次に、実施例1〜10の白色発光LEDランプの色度ばらつきを測定した。色度は各実施例にかかる白色LEDを各20個用意し、各LEDの真上で色度(CIE色度座標)を測定し、x座標、y座標の最大値と最小値の差(Δx、Δy)を測定した。なお、参考例として結合工程を行わない以外は実施例1と同様のものを用意した。その結果を表3に示す。 Next, chromaticity variation of the white light emitting LED lamps of Examples 1 to 10 was measured. As for chromaticity, 20 white LEDs according to each example are prepared, chromaticity (CIE chromaticity coordinates) is measured directly above each LED, and the difference between the maximum and minimum values of the x-coordinate and y-coordinate (Δx , Δy). In addition, the thing similar to Example 1 was prepared except not performing a coupling | bonding process as a reference example. The results are shown in Table 3.
特に、色度ばらつきが小さいことから白色LEDランプを複数個用いるバックライトに用いたとしても均一な白色を有する面光源を得ることができる。従って、それを用いた液晶表示装置の特性も向上する。
In particular, since the chromaticity variation is small, a surface light source having a uniform white color can be obtained even when used for a backlight using a plurality of white LED lamps. Therefore, the characteristics of the liquid crystal display device using the same are also improved.
a…発光ダイオード
b…蛍光体層
c…反射層
d…樹脂枠
a ... light emitting diode b ... phosphor layer c ... reflective layer d ... resin frame
Claims (8)
青色発光蛍光体として一般式1:(Sr1-x-yBaxCayEuz)10(PO4)6・Cl2
(式中x、y、zはx<0.2、y<0.1、0.005<z<0.1)で表されるユーロピウム付活ハロ燐酸塩蛍光体。 2. The method of manufacturing a white LED lamp according to claim 1, wherein the visible light emitting phosphor satisfies the following general formula.
General formula 1: (Sr 1-xy Ba x Ca y Eu z ) 10 (PO 4 ) 6 · Cl 2
(Wherein x, y, z are x <0.2, y <0.1, 0.005 <z <0.1), a europium activated halophosphate phosphor.
緑色発光蛍光体として一般式2:(Ba1−x−y−zSrxCayEuz)(Mg1−uMnu)Al10O17
(式中x、y、z、uはx<0.5、y<0.1、0.15<z<0.4、0.3<u<0.6)で表されるユーロピウム、マンガン付活アルミン酸塩蛍光体。 2. The method of manufacturing a white LED lamp according to claim 1, wherein the visible light emitting phosphor satisfies the following general formula.
Formula as a green emitting phosphor 2: (Ba 1-x- y-z Sr x Ca y Eu z) (Mg 1-u Mn u) Al 10 O 17
(Wherein x, y, z, u are x <0.5, y <0.1, 0.15 <z <0.4, 0.3 <u <0.6) Europium-manganese activated aluminate phosphor.
赤色発光蛍光体として一般式3:(La1−x−yEuxMy)2O2S
(式中Mは元素Sb,Snの少なくとも1種、x及びyは0.01<x<0.15,y<0.03)で表わされるユーロピウム付活酸硫化ランタン蛍光体。 2. The method of manufacturing a white LED lamp according to claim 1, wherein the visible light emitting phosphor satisfies the following general formula.
Formula as a red-emitting phosphor 3: (La 1-x- y Eu x M y) 2 O 2 S
(Wherein M is at least one of the elements Sb and Sn, and x and y are 0.01 <x <0.15, y <0.03), a europium activated lanthanum oxysulfide phosphor.