JP2007083681A - Inkjet recording paper - Google Patents

Inkjet recording paper Download PDF

Info

Publication number
JP2007083681A
JP2007083681A JP2005278523A JP2005278523A JP2007083681A JP 2007083681 A JP2007083681 A JP 2007083681A JP 2005278523 A JP2005278523 A JP 2005278523A JP 2005278523 A JP2005278523 A JP 2005278523A JP 2007083681 A JP2007083681 A JP 2007083681A
Authority
JP
Japan
Prior art keywords
paper
recording paper
ink
printer
ink jet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2005278523A
Other languages
Japanese (ja)
Inventor
Norifumi Tanaka
憲文 田中
Yuji Sawa
裕治 澤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Paper Industries Co Ltd
Jujo Paper Co Ltd
Original Assignee
Nippon Paper Industries Co Ltd
Jujo Paper Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Paper Industries Co Ltd, Jujo Paper Co Ltd filed Critical Nippon Paper Industries Co Ltd
Priority to JP2005278523A priority Critical patent/JP2007083681A/en
Publication of JP2007083681A publication Critical patent/JP2007083681A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To obtain double-sided inkjet recording paper which has good printing quality when printing is done by a high-speed inkjet printer equipped with a line head, and which is excellent in printer conveyability in a wide range of environment. <P>SOLUTION: In the double-side-coated inkjet recording paper for the high-speed sheet-fed inkjet printer with the line head, ink absorbing layers are provided on both the sides of a substrate, respectively; contained moisture is in the range of 4.0-5.5%; stiffness is 30 or more in a CD-direction and 130 or less in an MD-direction; and basic weight is 100 g/m<SP>2</SP>or less. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、インクジェット記録用紙に関するものであり、特にラインヘッドを有する高速枚葉インクジェットプリンターで使用する際に、広範囲の環境下でプリンター搬送性に優れるインクジェット記録用紙に関する。   The present invention relates to an ink jet recording paper, and more particularly to an ink jet recording paper excellent in printer transportability in a wide range of environments when used in a high-speed sheet-fed ink jet printer having a line head.

インクジェット記録方式は、フルカラー化が容易なことや印字騒音が少ないことなどから近年急速に普及してきた。この方式はノズルから記録媒体に向けてインクの微小液滴を高速で飛翔、付着させて画像や文字などの記録を行うものである。このため、多色、高精細化が容易であり、特に近年の高解像度フルカラープリンターでは、カラー印刷や銀塩写真と比べてもほとんど遜色のない画像も印字可能になった。そこで、現在一般家庭にも数多くのインクジェットプリンターが導入され、主にデジタルカメラからの画像をインクジェット記録により印字して、ダイレクトメール用カードや年賀葉書等を作成するといった用途で使用されている。   The ink jet recording system has been rapidly spread in recent years because it is easy to make full color and the printing noise is low. In this method, fine droplets of ink are ejected at high speed from a nozzle toward a recording medium, and images and characters are recorded. For this reason, it is easy to achieve multicolor and high definition, and in particular, high-resolution full-color printers in recent years can print images that are almost inferior to color printing or silver halide photography. Therefore, a large number of ink jet printers have been introduced into ordinary households, and are used mainly for printing images from digital cameras by ink jet recording to create direct mail cards, new year postcards, and the like.

しかし、商業的な面では、家庭用インクジェットプリンターの印刷速度では、印刷機による印刷と比べて処理時間が長すぎて、商売としては成立しにくい。そこで、主に商業用途用に印刷時間を大幅に短縮した、すなわち高速印刷が可能なラインヘッド搭載型プリンターが登場した(例えば、特許文献1参照)。ラインヘッド搭載型プリンターは、インクヘッドが移動して印刷を行う従来のインクジェットプリンターとは異なり、ライン状のインクヘッドが装備されており、その下をインクジェット記録用紙がベルトに乗って高速で搬送される。そのため、1枚当たりの印字時間は数秒又は1秒以下であり、家庭用インクジェットプリンターと比べて圧倒的な高速印字が可能となる。また、プリンター機内で記録用紙を反転させる機構を有しており、両面印字も可能となっている。しかしながら、高速・両面印字が可能となった一方で、インクジェット記録用紙に僅かなカールや波打ちがあってもプリンターの用紙入口で引っかかったり、或いはインクヘッドに擦ったりするというトラブルが発生しやすくなった。なお、プリンターヘッドと記録用紙との擦れは、画像品質を損なうと共に、記録用紙から紙の繊維やコート層の粉体などがプリンターヘッドへ付着し、印字不良の原因となる恐れがあるため好ましくない。   However, on the commercial side, at the printing speed of a home inkjet printer, the processing time is too long compared to printing by a printing press, making it difficult to establish a business. Therefore, a line head-mounted printer that has greatly reduced printing time for commercial use, that is, capable of high-speed printing has appeared (for example, see Patent Document 1). Unlike conventional inkjet printers that print by moving the ink head, the line head mounted printer is equipped with a line-shaped ink head, under which the inkjet recording paper is carried on a belt at high speed. The Therefore, the printing time per sheet is several seconds or 1 second or less, and overwhelming high-speed printing is possible as compared with home inkjet printers. In addition, the printer has a mechanism for reversing the recording paper in the printer, and double-sided printing is also possible. However, while high-speed and double-sided printing has become possible, problems such as being caught at the paper inlet of the printer or rubbing against the ink head are more likely to occur even if the ink-jet recording paper is slightly curled or wavy. . In addition, rubbing between the printer head and the recording paper is not preferable because image quality is deteriorated and paper fibers or coating layer powder adheres to the printer head from the recording paper and may cause a printing defect. .

通常のインクジェット記録用紙は、インクジェットプリンターでの搬送トラブル、例えば給紙不良や多重搬送、給紙の際に発生する用紙の角折れ、さらには印字の際のインクヘッドと記録媒体との擦れ等の問題を防ぐため、カールはインク受理層面側に凸状となるよう調整してある(例えば、特許文献2参照)が、両面で印字を行う両面インクジェット記録用紙の場合、どちらかにカールを凸状とするわけにはいかない。   Ordinary inkjet recording paper has problems such as conveyance troubles in inkjet printers, such as poor feeding and multiple conveyance, corner breakage of paper that occurs during paper feeding, and rubbing between the ink head and recording medium during printing. In order to prevent problems, the curl is adjusted to be convex toward the ink receiving layer surface (see, for example, Patent Document 2), but in the case of double-sided inkjet recording paper that performs printing on both sides, the curl is convex on either side. It cannot be said that.

さらに、商業用途で使用されるためには、広範囲な環境下で問題無く使用できる必要がある。従って、広範囲の環境下で、カール及び波打ちをよりフラットな状態に保つことができる両面インクジェット記録用紙が必要になるが、現在この様な記録用紙は得られていない。   Furthermore, in order to be used in commercial applications, it must be usable without problems in a wide range of environments. Therefore, a double-sided ink jet recording paper that can keep curls and undulations flat in a wide range of environments is required, but such a recording paper has not been obtained at present.

特開2004−276486号公報JP 2004-276486 A 特開2002−86896号公報JP 2002-86896 A

そこで、本発明は、ラインヘッドを搭載した高速インクジェットプリンターで印字を行った際に、良好な印字品質を有し、かつ広範囲の環境下でプリンター搬送性に優れる両面インクジェット記録用紙を得ることを目的とする。   Therefore, the present invention has an object to obtain a double-sided ink jet recording paper having good print quality and excellent printer transportability in a wide range of environments when printing is performed with a high-speed ink jet printer equipped with a line head. And

本発明の発明者らは、上記課題を解決するために鋭意検討した結果、以下の構成を用いることにより、本発明の目的を達成することを可能にした。   The inventors of the present invention have made extensive studies in order to solve the above problems, and as a result, have made it possible to achieve the object of the present invention by using the following configuration.

すなわち、本発明は支持体の両面にインク受理層を設けた、ラインヘッドを有する高速枚葉インクジェットプリンター用の両面塗工インクジェット記録用紙であって、含有水分が4.0〜5.5%であり、かつ剛度がCD方向で30以上、MD方向で130以下であり、かつ坪量が100g/m以下であることを特徴とする両面塗工インクジェット記録用紙であり、さらにその透気抵抗度が30秒以上であることが好ましい。 That is, the present invention is a double-side coated inkjet recording paper for a high-speed sheet-fed inkjet printer having an ink receiving layer on both sides of a support, and having a moisture content of 4.0 to 5.5%. A double-sided coated inkjet recording paper characterized by having a stiffness of 30 or more in the CD direction, 130 or less in the MD direction, and a basis weight of 100 g / m 2 or less; Is preferably 30 seconds or longer.

本発明においては、ラインヘッドを搭載した高速インクジェットプリンターで印字を行った際に、良好な印字品質を有し、かつ広範囲の環境下でプリンター搬送性に優れる両面インクジェット記録用紙を得ることができる。   In the present invention, when printing is performed with a high-speed inkjet printer equipped with a line head, it is possible to obtain a double-sided inkjet recording paper having good print quality and excellent printer transportability in a wide range of environments.

本発明におけるインクジェット記録用紙は、好ましくはシート状を有する支持体とその両面上に形成されたインク受理層からなる。本発明のインクジェット記録用紙の支持体は特に制限されるものではなく、木材繊維(パルプ)主体の紙、またはポリエチレンなどのプラスチック類、もしくは木材繊維や合成繊維を主体とした不織布のごときシート状物質使用することができる。また前述した異なる種類のシート状物質を貼り合わせたものを支持体として用いることもできる。本発明においては、特にインク吸収性に優れるという点で、紙を支持体として使用することが望ましい。   The ink jet recording paper in the present invention preferably comprises a support having a sheet shape and an ink receiving layer formed on both sides thereof. The support of the inkjet recording paper of the present invention is not particularly limited, and is a sheet-like substance such as paper mainly made of wood fiber (pulp), plastics such as polyethylene, or non-woven fabric mainly made of wood fiber or synthetic fiber. Can be used. Moreover, what bonded together the different kind of sheet-like substance mentioned above can also be used as a support body. In the present invention, it is desirable to use paper as a support, particularly in terms of excellent ink absorbability.

紙支持体を構成する木材パルプとしてはLBKP、NBKP等の化学パルプ、GP、PGW、RMP、TMP、CTMP、CMP、CGP等の機械パルプ、DIP等の古紙パルプ等のパルプを単独あるいは併用して用いることが可能である。紙支持体は上記木材パルプには必要に応じて従来公知の填料やバインダー及びサイズ剤や定着剤、歩留まり向上剤、紙力増強剤等の各種添加剤を混合し、長網抄紙機、円網抄紙機、ツインワイヤー抄紙機等の各種抄紙機にて紙匹を形成した後に、乾燥させて得ることができる。なお、紙支持体においては内添サイズ剤の添加の有無、内添填料の有無、サイズプレスの有無等は何等制限しない。   Wood pulp that constitutes the paper support, chemical pulps such as LBKP and NBKP, mechanical pulps such as GP, PGW, RMP, TMP, CTMP, CMP, and CGP, and pulps such as waste paper pulp such as DIP are used alone or in combination. It is possible to use. The paper support is mixed with various additives such as fillers, binders, sizing agents, fixing agents, yield improvers, paper strength enhancers, etc., which are conventionally known, in the above wood pulp. It can be obtained by drying after forming a web with various paper machines such as a paper machine and a twin wire paper machine. In the paper support, the presence or absence of an internal sizing agent, the presence or absence of an internal filler, and the presence or absence of a size press are not limited.

本発明のインク受理層に用いられる顔料としては、従来公知の白色顔料を使用することが出来る。例えば、軽質炭酸カルシウム、重質炭酸カルシウム、カオリン、タルク、硫酸カルシウム、硫酸バリウム、二酸化チタン、酸化亜鉛、硫化亜鉛、炭酸亜鉛、サチンホワイト、珪酸アルミニウム、ケイソウ土、珪酸カルシウム、珪酸マグネシウム、合成非晶質シリカ、コロイダルシリカ、コロイダルアルミナ、ベーマイト、擬ベーマイト、水酸化アルミニウム、アルミナ、リトポン、ゼオライト、加水ハロイサイト、炭酸マグネシウム、水酸化マグネシウムなどの無機顔料、スチレン系プラスチックピグメント、アクリル系プラスチックピグメント、ポリエチレン、マイクロカプセル、尿素樹脂、メラミン樹脂など有機顔料を用いることができる。この中でも、JIS K5101に順じた測定法による吸油量が150ml/100g〜300ml/100gである合成非晶質シリカ、又はアルミナを使用することが好ましく、印字品質が良好なインクジェット記録用紙を得ることができる。   A conventionally known white pigment can be used as the pigment used in the ink receiving layer of the present invention. For example, light calcium carbonate, heavy calcium carbonate, kaolin, talc, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide, zinc sulfide, zinc carbonate, satin white, aluminum silicate, diatomaceous earth, calcium silicate, magnesium silicate, synthetic non Amorphous silica, colloidal silica, colloidal alumina, boehmite, pseudoboehmite, aluminum hydroxide, alumina, lithopone, zeolite, hydrous halloysite, magnesium carbonate, magnesium hydroxide, inorganic pigments, styrene plastic pigment, acrylic plastic pigment, polyethylene Organic pigments such as microcapsules, urea resins, and melamine resins can be used. Among these, it is preferable to use synthetic amorphous silica or alumina having an oil absorption amount of 150 ml / 100 g to 300 ml / 100 g according to a measurement method in accordance with JIS K5101, and to obtain an ink jet recording paper having good print quality. Can do.

本発明のインク受理層には、塗膜としての特性を維持するために親水性結着剤を含有する。親水性結着剤とは、例えばポリビニルアルコール及びその変性物、酸化デンプン、エーテル化デンプン、カゼイン、ゼラチン、大豆蛋白、カルボキシメチルセルロース、SBラテックス、NBラテックス、アクリルラテックス、酢酸ビニル重合体ラテックス、エチレン酢酸ビニル系ラテックス、ポリウレタン、不飽和ポリエステル樹脂等が使用できる。   The ink receiving layer of the present invention contains a hydrophilic binder in order to maintain the properties as a coating film. Examples of the hydrophilic binder include polyvinyl alcohol and modified products thereof, oxidized starch, etherified starch, casein, gelatin, soy protein, carboxymethyl cellulose, SB latex, NB latex, acrylic latex, vinyl acetate polymer latex, ethylene acetate Vinyl latex, polyurethane, unsaturated polyester resin, etc. can be used.

本発明においては、これらの親水性結着剤の少なくとも1種を使用することができるが、その配合部数は、前記した顔料100重量部に対し、10〜80重量部であることが好ましい。結着剤の配合部数が少ないと表面強度が不十分となり、多すぎるとインク吸収性が不十分となる。   In the present invention, at least one of these hydrophilic binders can be used, and the number of blended parts is preferably 10 to 80 parts by weight with respect to 100 parts by weight of the pigment. When the number of blended parts of the binder is small, the surface strength is insufficient, and when it is too large, the ink absorbability is insufficient.

本発明ではインク受理層にカチオン性水溶性樹脂を含有することも好ましい。本発明で使用されるカチオン性水溶性樹脂としては、二級アミン、三級アミン、及び四級アンモニウム塩としてポリエチレンイミン塩、ジメチルアミンエピハロヒドリン縮合体、ポリビニルアミン塩、ポリアリルアミン塩、ポリジメチルアミノエチルメタクリレート四級塩、ポリジアリルジメチルアンモニウム塩、ジアリルアミンアクリルアミド共重合体塩、ポリスチレンの四級アンモニウム塩等が挙げられる。またこれらカチオン性樹脂の2種類以上を配合使用することも可能である。
これらカチオン性水溶性樹脂は、顔料インク中の色材である顔料が分散剤によって溶媒中に分散され、その表面が負に帯電していることより、これらを捕捉する作用がある。よって、顔料インクはインク受理層表面付近に残るようになり発色性が改善される。
In the present invention, the ink receiving layer preferably contains a cationic water-soluble resin. Examples of the cationic water-soluble resin used in the present invention include secondary amines, tertiary amines, and quaternary ammonium salts such as polyethyleneimine salts, dimethylamine epihalohydrin condensates, polyvinylamine salts, polyallylamine salts, and polydimethylaminoethyl. Examples thereof include methacrylate quaternary salts, polydiallyldimethylammonium salts, diallylamine acrylamide copolymer salts, and quaternary ammonium salts of polystyrene. Two or more of these cationic resins can be used in combination.
These cationic water-soluble resins have an action of capturing the pigment, which is a color material in the pigment ink, by dispersing it in a solvent with a dispersant and charging the surface negatively. Therefore, the pigment ink remains in the vicinity of the surface of the ink receiving layer, and the color developability is improved.

また、支持体あるいはインク受理層に、サイズ剤、顔料分散剤、増粘剤、流動性改良剤、界面活性剤、消泡剤、抑泡剤、離型剤、発泡剤、浸透剤、着色染料、蛍光増白剤、紫外線吸収剤、酸化防止剤、防腐剤、防バイ剤、耐水化剤、湿潤紙力増強剤、乾燥紙力増強剤、保水剤などを必要に応じ適宜含有させることもできる。   In addition, sizing agent, pigment dispersant, thickener, fluidity improver, surfactant, antifoaming agent, antifoaming agent, mold release agent, foaming agent, penetrating agent, coloring dye on support or ink receiving layer , Fluorescent whitening agents, ultraviolet absorbers, antioxidants, antiseptics, antibacterial agents, water resistance agents, wet paper strength enhancers, dry paper strength enhancers, water retention agents, and the like can be appropriately contained as necessary. .

本発明において、支持体上に設けられるインク受理層及びインク受理層以外の塗工層の総数及び構成については特に限定されるものではないが、インク受理層の塗工量(乾燥塗工量)は片面当たり3〜15g/mとなることが好ましい。さらに好ましくは4〜10g/mである。インク受理層の塗工量が3g/mに満たないと、インク吸収性が低下したり、ベタ斑が発生するため、インクジェット印字性能に悪影響が生じる。また15g/mを超えると薄手のインクジェット記録用紙の場合、原紙部分の割合が小さくなりすぎ、必要な用紙剛度が得られなくなる。 In the present invention, the total number and configuration of the ink receiving layer and the coating layer other than the ink receiving layer provided on the support are not particularly limited, but the coating amount of the ink receiving layer (dry coating amount). Is preferably 3 to 15 g / m 2 per side. More preferably, it is 4-10 g / m < 2 >. When the coating amount of the ink receiving layer is less than 3 g / m 2 , the ink absorbability is reduced or solid spots are generated, which adversely affects the ink jet printing performance. On the other hand, if it exceeds 15 g / m 2 , in the case of thin inkjet recording paper, the ratio of the base paper portion becomes too small, and the required paper rigidity cannot be obtained.

インク受理層を基紙表面に設けるために、本発明においては、一般的な塗工装置である各種ブレードコーター、ロールコーター、エアーナイフコーター、バーコーター、ゲートロールコーター、カーテンコーター、ショートドゥエルコーター、グラビアコーター、フレキソグラビアコーター、サイズプレス等の各種装置をオンマシン又はオフマシンで使用することができる。また、インク受理層を塗工した後にインク受理層をマシンカレンダー、スーパーカレンダー、ソフトカレンダー等のカレンダー装置で表面処理することも可能であるし、また、インク受理層をキャストコーター等を用いて塗工し、光沢性を付与することも可能である。   In order to provide the ink receiving layer on the surface of the base paper, in the present invention, various blade coaters, roll coaters, air knife coaters, bar coaters, gate roll coaters, curtain coaters, short dwell coaters, which are general coating devices, Various apparatuses such as a gravure coater, a flexographic gravure coater, and a size press can be used on-machine or off-machine. In addition, after the ink receiving layer is applied, the ink receiving layer can be surface-treated with a calendar device such as a machine calendar, a super calendar, or a soft calendar, and the ink receiving layer can be applied using a cast coater or the like. It is possible to work and give glossiness.

また、インク受理層を両面に塗工した後には、必要に応じて水分を供給したり、蒸気による加湿をする等の処理を、オンラインまたはオフラインで実施して、カールをよりフラットにコントロールすることができる。尚、カール形状は、水分を供給したり、蒸気による加湿を行った面側が凹状となる方向に変化し、この変化は加湿量を増やしていくことで増大する。従って、凸となっている面側に適量の水分を供給したり、蒸気による加湿を行うことで、記録用紙のカールをフラットに調整することができる。尚、この水分供給装置又は加湿処理装置は、特に限定されるものではなく、どのような装置を用いても良い。   In addition, after coating the ink receiving layer on both sides, the curl can be controlled more flatly by performing online or offline processing such as supplying moisture or humidifying with steam as needed. Can do. Note that the curl shape changes in a direction in which the surface on which moisture is supplied or humidified with steam becomes concave, and this change increases as the amount of humidification is increased. Therefore, the curl of the recording paper can be adjusted to be flat by supplying an appropriate amount of moisture to the convex surface side or by humidifying with steam. The moisture supply device or the humidification processing device is not particularly limited, and any device may be used.

本発明において、ラインヘッドを搭載した高速インクジェットプリンターで印字を行った際に、良好な印字品質を有し、かつ広範囲の環境下でプリンター搬送性に優れる両面インクジェット記録用紙を得ることができる理由については、以下のように説明される。広範囲の環境下で、記録用紙の変形を小さく留めるために注意すべき点は、記録用紙を低湿環境下に放置した際の脱湿カール、及び高湿環境下に放置した際の吸湿波打ちを抑制する点である。   In the present invention, when printing is performed with a high-speed inkjet printer equipped with a line head, it is possible to obtain a double-sided inkjet recording paper having good print quality and excellent printer transportability in a wide range of environments. Is described as follows. In order to keep the deformation of the recording paper small in a wide range of environments, it should be noted that dehumidification curl when the recording paper is left in a low humidity environment and moisture absorption undulation when left in a high humidity environment are suppressed. It is a point to do.

記録用紙が低湿環境に放置されると、徐々に用紙の水分がぬけていく(脱湿)。用紙を重ねていた場合、この脱湿は、低湿環境に接している用紙の端面、及び上面から生じることになる。水分の抜けた用紙部分の繊維は収縮するため、用紙の周囲、及び上側に収縮する作用が生まれ、結果として用紙は上側にカール(下向きに凸状)することになる。従って、片面の記録用紙であるならば、あらかじめ非記録面側にカール(記録面側に凸状)させておくなどの緩和処置が取れるが、本願のような両面記録用紙では、脱湿カールの発生自体を抑制する必要が生じる。そこで、本願では、記録用紙の水分を4.0〜5.5%と低い範囲に保つことで、用紙から水分がぬけることを防止し、脱湿カールを抑制した。水分が5.5%を超えると、脱湿カールが大きくなり、一方水分が4.0%未満であると、脱湿カールは生じないが、今度は高湿時の吸湿波打ちが悪化するので好ましくない。   When the recording paper is left in a low humidity environment, the moisture of the paper gradually drains (dehumidification). When the sheets are stacked, this dehumidification occurs from the end surface and the upper surface of the sheet that is in contact with the low humidity environment. Since the fibers in the paper portion from which moisture has been removed contract, an effect of contracting around and above the paper is produced, and as a result, the paper curls upward (convex downward). Therefore, if it is a single-sided recording paper, it is possible to take mitigation measures such as curling on the non-recording surface side in advance (convex shape on the recording surface side). It is necessary to suppress the occurrence itself. Therefore, in the present application, the moisture of the recording paper is kept in a low range of 4.0 to 5.5%, thereby preventing moisture from being removed from the paper and suppressing dehumidification curl. If the moisture content exceeds 5.5%, dehumidification curl becomes large. On the other hand, if the moisture content is less than 4.0%, dehumidification curl does not occur, but this time is preferable because the moisture absorption wave at high humidity deteriorates. Absent.

次に、記録用紙が高湿環境に放置された場合は、吸湿して用紙が伸びる。用紙を重ねていた場合、この吸湿は、用紙の周囲、及び最上面で生じる。吸湿した部分で伸びが生じるので、用紙の周囲は中央部に比べ長くなり、その結果用紙の周囲で波打ちが生じる。従って、吸湿波打ちを防ぐには、用紙の水分を高くして高湿環境でも吸湿しないようにすれば良いのだが、本願では、脱湿カール抑制のため低水分であることが前提となっている。このため水分以外の方法で、吸湿波打ちを抑制する必要があった。そこで鋭意検討した結果、用紙剛度を一定範囲に制御することで、波打ちを抑制し良好なプリンター搬送性が得られることを見出した。   Next, when the recording paper is left in a high humidity environment, the recording paper is absorbed and stretched. When sheets are stacked, this moisture absorption occurs around the sheet and on the top surface. Since elongation occurs in the moisture-absorbed portion, the periphery of the sheet becomes longer than the central portion, and as a result, undulation occurs around the sheet. Therefore, in order to prevent moisture absorption undulations, it is only necessary to increase the moisture of the paper so that it does not absorb moisture even in a high humidity environment. However, in the present application, it is assumed that the moisture is low in order to suppress dehumidification curl. . For this reason, it was necessary to suppress the moisture absorption wave by a method other than moisture. As a result of intensive studies, it was found that by controlling the paper stiffness within a certain range, it is possible to suppress undulations and obtain good printer transportability.

即ちCD方向(抄紙方向に対して直交する方向)の剛度が30以上であり、MD方向(抄紙方向)の剛度が130以下であることが重要である。CD剛度が30未満であると、波打ちという変形に対する用紙の抵抗力が小さくなり、非常に多くの波打ちが発生することになる。波打ちの個数が多いと、プリンター搬送時に行われる吸引効果が損なわれ、用紙が十分に矯正されなくなるため、インクヘッドに擦れてしまう現象が生じる。CD剛度が30以上であれば、用紙の抵抗力が十分となって波打ちの個数が減少し、プリンターの吸引効果が十分発揮され、ヘッド擦れが生じない。波打ちに関しては、剛度は高い方が良いので、特に上限はないが、剛度が高すぎると用紙が曲がり難くなるため、両面印刷を行う際の搬送時にプリンターの中で用紙が詰まってしまう現象が発生する。この現象を回避するために、MD剛度で130以下であることが必要となる。   That is, it is important that the stiffness in the CD direction (direction perpendicular to the paper making direction) is 30 or more and the stiffness in the MD direction (paper making direction) is 130 or less. If the CD stiffness is less than 30, the resistance of the sheet to the deformation called undulation is reduced, and a great number of undulations are generated. If the number of undulations is large, the suction effect that is performed when the printer is transported is impaired, and the paper is not sufficiently corrected, resulting in a phenomenon that the ink head is rubbed. If the CD stiffness is 30 or more, the resistance of the paper is sufficient, the number of undulations is reduced, the suction effect of the printer is sufficiently exhibited, and head rubbing does not occur. There is no particular upper limit for undulations, so there is no upper limit. However, if the stiffness is too high, the paper will be difficult to bend, causing the paper to jam in the printer during transport when performing duplex printing. To do. In order to avoid this phenomenon, the MD stiffness needs to be 130 or less.

また、プリンター搬送性には剛度に加えて、透気抵抗度の影響も見られる。多少の波打ちであるならば、プリンターの吸引によって矯正されるが、用紙の透気抵抗度が低すぎると、吸引による矯正効果が発揮されなくなる。そのため、透気抵抗度が30秒以上であると好ましい。   In addition to rigidity, the printer transportability is affected by the air resistance. If it is somewhat wavy, it is corrected by suction of the printer, but if the air resistance of the paper is too low, the correction effect by suction cannot be exhibited. Therefore, it is preferable that the air resistance is 30 seconds or more.

上記したインクジェット記録用紙は、主として溶剤と分散剤と顔料とからなる非水系イ
ンクを用いたインクジェット記録に最も適する。水系インクを用いたインクジェット記録に用いることも可能であるが、水系インクでは、印字後のコックリング(インク吸収による波打ち)の影響もあるので、ヘッド擦れに関しては非水系顔料インクを用いたインクジェット記録と比較するとやや劣るものとなる。
The above-described ink jet recording paper is most suitable for ink jet recording using a non-aqueous ink mainly composed of a solvent, a dispersant, and a pigment. It can also be used for ink jet recording using water-based ink, but water-based ink also has the effect of cockling after printing (waving due to ink absorption), so ink scrubbing with non-aqueous pigment ink is used for head rubbing. It is a little inferior compared with.

以下に実施例を挙げて本発明をより具体的に説明するが、本発明はこれらによって限定されるものではない。また、実施例において示す「部」及び「%」は、特に明示しない限り質量部及び質量%を示す。
<実施例1>
基紙
広葉樹漂白クラフトパルプを叩解して濾水度を350mlに調整したパルプ100部に対し、タルク30部、カチオン化デンプン2部、硫酸バンド1部、及びアルキルケテンダイマー乳化物0.2部を添加してスラリーを調製した。次いでスラリーから長網抄紙機で抄紙した。その後、この原紙の両面に、燐酸エステル化デンプン5%とポリビニルアルコール0.5%の液をサイズプレスを用いて乾燥重量が両面で3g/mとなるように塗布し、乾燥後マシンカレンダー処理して坪量70g/mの基紙を製造した。
インク受理層
非晶質シリカ(ミズカシルP−50 水澤化学工業製:平均二次粒子径10μm、吸油量170ml/100g)100部
ポリビニルアルコール(PVA−117 クラレ製)30部
エチレン酢酸ビニルエマルジョン(リカボンドBE−7000 中央理化工業製)15部
スチレンアクリル樹脂(ポリマロン360 荒川化学製)3部
ポリジアリルジメチルアンモニウムクロライド(PAS−H−10L 日東紡績製)5部
消泡剤(SNデフォーマー480 サンノプコ製)0.5部
及び希釈水等を適宜添加した、固形分が18%の塗工液を、エアーナイフコーターを用いてその乾燥塗工量が片面当たり7g/mとなるように基紙の両面に塗工した。塗工後、水分が4.8%になるように、またカールがフラットになるように、乾燥及びカール修正を行い、さらに表裏にカレンダー処理を行ってインクジェット記録用紙を得た。
Hereinafter, the present invention will be described more specifically with reference to examples, but the present invention is not limited thereto. Further, “parts” and “%” shown in the examples indicate parts by mass and mass% unless otherwise specified.
<Example 1>
Base paper 30 parts of talc, 2 parts of cationized starch, 1 part of sulfuric acid band, and alkyl ketene dimer emulsion 0 per 100 parts of pulp obtained by beating bleached hardwood bleached kraft pulp and adjusting the freeness to 350 ml A slurry was prepared by adding 2 parts. Next, paper was made from the slurry by a long paper machine. Thereafter, a solution of 5% phosphoric esterified starch and 0.5% polyvinyl alcohol was applied to both sides of this base paper using a size press so that the dry weight was 3 g / m 2 on both sides, and machine calendar treatment after drying Thus, a base paper having a basis weight of 70 g / m 2 was produced.
Ink-receiving layer Amorphous silica (Mizukasil P-50, manufactured by Mizusawa Chemical Co., Ltd .: average secondary particle size 10 μm, oil absorption 170 ml / 100 g) 100 parts polyvinyl alcohol (PVA-117 Kuraray) 30 parts ethylene vinyl acetate Emulsion (Rikabond BE-7000, manufactured by Chuo Rika Kogyo Co., Ltd.) 15 parts styrene acrylic resin (Polymaron 360, manufactured by Arakawa Chemical Co., Ltd.) 3 parts Polydiallyldimethylammonium chloride (PAS-H-10L, manufactured by Nittobo Co., Ltd.) 5 parts Antifoaming agent (SN Deformer 480 Sannopco) (Manufactured) Base paper so that the dry coating amount is 7 g / m 2 per side by using an air knife coater with a coating liquid having a solid content of 18% to which 0.5 part and dilution water are appropriately added. Coated on both sides. After coating, drying and curl correction were carried out so that the water content was 4.8% and the curl was flat, and further, calendar treatment was performed on the front and back to obtain an ink jet recording paper.

<実施例2>
水分を4.2%に変更したこと以外は、実施例1と全く同様にしてインクジェット記録用紙を得た。
<実施例3>
水分を5.4%に変更したこと以外は、実施例1と全く同様にしてインクジェット記録用紙を得た。
<実施例4>
基紙の坪量を80g/mに変更したこと以外は、実施例1と全く同様にしてインクジェット記録用紙を得た。
<実施例5>
インク受理層の塗布量を片面当たり5g/mに変更したこと以外は、実施例1と全く同様にしてインクジェット記録用紙を得た。
<Example 2>
An ink jet recording paper was obtained in the same manner as in Example 1 except that the water content was changed to 4.2%.
<Example 3>
An ink jet recording paper was obtained in the same manner as in Example 1 except that the water content was changed to 5.4%.
<Example 4>
An inkjet recording paper was obtained in exactly the same manner as in Example 1 except that the basis weight of the base paper was changed to 80 g / m 2 .
<Example 5>
An ink jet recording sheet was obtained in exactly the same manner as in Example 1 except that the coating amount of the ink receiving layer was changed to 5 g / m 2 per side.

<比較例1>
記録用紙の水分を6.0%に調整したこと以外は、実施例1と全く同様にしてインクジェット記録用紙を得た。
<比較例2>
記録用紙の水分を3.5%に調整したこと以外は、実施例1と全く同様にしてインクジェット記録用紙を得た。
<比較例3>
基紙において、燐酸エステル化デンプン5%とポリビニルアルコール0.5%の液をサイズプレスを用いて乾燥重量が両面で1.5g/mとなるように塗布したこと以外は、実施例1と全く同様にしてインクジェット記録用紙を得た。
<比較例4>
基紙において、燐酸エステル化デンプン5%とポリビニルアルコール0.5%の液をサイズプレスを用いて乾燥重量が両面で6g/mとなるように塗布したこと以外は、実施例4と全く同様にしてインクジェット記録用紙を得た。
<Comparative Example 1>
An ink jet recording paper was obtained in the same manner as in Example 1 except that the moisture of the recording paper was adjusted to 6.0%.
<Comparative example 2>
An ink jet recording paper was obtained in the same manner as in Example 1 except that the moisture of the recording paper was adjusted to 3.5%.
<Comparative Example 3>
In Example 1, except that a solution of 5% phosphoric esterified starch and 0.5% polyvinyl alcohol was applied using a size press so that the dry weight was 1.5 g / m 2 on both sides. Inkjet recording paper was obtained in exactly the same manner.
<Comparative example 4>
Except that a solution of 5% phosphoric esterified starch and 0.5% polyvinyl alcohol was applied to the base paper using a size press so that the dry weight was 6 g / m 2 on both sides. Inkjet recording paper was obtained.

実施例1〜5、比較例1〜4で得られたインクジェット記録用紙について、以下の評価を行い、得られた結果を表1に示す。
評価方法
実施例及び比較例における各々の記録用紙の評価を、以下に示す方法により行った。印字は全てORPHIS HC 5000(理想化学工業社製、ラインヘッド搭載高速枚葉インクジェットプリンター)にて行い、印字モードは写真優先/HC専用紙マット(高品位紙)モードを使用した。各項目において、△以上の評価であれば問題なく使用できる。
The ink jet recording paper obtained in Examples 1 to 5 and Comparative Examples 1 to 4 was evaluated as follows, and the obtained results are shown in Table 1.
Evaluation method Each recording paper in the examples and comparative examples was evaluated by the following method. All printing was performed with ORPHIS HC 5000 (Riso Kagaku Kogyo Co., Ltd., line head-mounted high-speed sheet-fed inkjet printer), and the printing mode was photographic priority / HC dedicated paper mat (high quality paper) mode. In each item, if the evaluation is Δ or more, it can be used without any problem.

評価項目
<用紙物性>
用紙物性値は、各々下記手順に従い測定した。
坪量 :JIS P 8124
紙厚 :JIS P 8118
水分 :JIS P 8127
こわさ(剛度):JIS P 8143
透気抵抗度:JIS P 8117
<発色性>
シアン、マゼンタ、イエロー、ブラックについて各ベタ画像を印字し、23℃、50%RH環境下で24時間放置した後に、各画像部の印字濃度を反射濃度計(MACBEATH RD194I)で測定した。
Evaluation item <paper physical properties>
The paper physical properties were measured according to the following procedures.
Basis weight: JIS P 8124
Paper thickness: JIS P 8118
Moisture: JIS P 8127
Stiffness (rigidity): JIS P 8143
Air permeability resistance: JIS P 8117
<Color development>
Each solid image was printed for cyan, magenta, yellow, and black, and allowed to stand for 24 hours in an environment of 23 ° C. and 50% RH, and then the print density of each image area was measured with a reflection densitometer (MACBEATH RD194I).

○…4色合計値が4.2以上
△…4色合計値が4以上4.2未満
×…4色合計値が4未満
○… The total value of four colors is 4.2 or more Δ: The total value of four colors is 4 or more and less than 4.2 ×… The total value of four colors is less than 4

<インク吸収性>
レッド、グリーンの各ベタ画像を両面に5枚連続印字した後、印字物の白紙部分に汚れや裏移りの発生の有無を調べた。
○…インクの吸収性が速いため、汚れや裏移りが全く発生しない。
△…汚れや裏移りが若干発生するが、ほとんど目立たない程度である。
×…インクの吸収性が遅いため、汚れや裏移りが発生し程度も酷い。
<脱湿カール>
台上にA4サイズの用紙を50枚重ねて、低温低湿環境(10℃、30%RH)に2時間放置した後に四隅のカール高さをを測定した。カール高さは一番下の用紙が台上から浮いた高さを測定し、四隅の平均値を測定値とした。
<Ink absorbability>
After five red and green solid images were continuously printed on both sides, the white paper portion of the printed matter was examined for the presence of smudges and set-off.
○: The ink absorbency is fast, so that no stain or set-off occurs.
Δ: Slight dirt or set-off occurs but is almost inconspicuous.
X: Since the ink absorbency is slow, dirt and set-off occur and the degree is severe.
<Dehumidification curl>
Fifty sheets of A4 size paper were stacked on the table and left in a low temperature and low humidity environment (10 ° C., 30% RH) for 2 hours, and then the curl heights at the four corners were measured. The curl height was measured by measuring the height at which the bottom sheet floated from the top, and the average value at the four corners was taken as the measured value.

○…平均のカール高さが5mm未満
△…平均のカール高さが5mm以上、10mm未満
×…平均のカール高さが10mm以上
○: Average curl height is less than 5 mm Δ: Average curl height is 5 mm or more and less than 10 mm ×… Average curl height is 10 mm or more

<吸湿波打ち>
台上にA4サイズの用紙を50枚重ねて、高温高湿環境(30℃、70%RH)で2時間放置して、CD方向に現れた用紙の波打ちの個数を観察した。なお、波打ちが用紙端部で途切れている場合0.5個として数えた。
○…波打ちの個数が3.0個以下
△…波打ちの個数が3.5個〜4.5個
×…波打ちの個数が5.0個以上
<プリンター搬送性>
低温低湿環境(10℃、30%RH)、及び高温高湿環境(30℃、70%RH)で用紙を各100枚両面印字して、プリンター搬送性を評価した。用紙は各環境で2時間放置した用紙を使用した。
○…搬送不良、ヘッド擦れが全く生じず、合計200枚の印字を行うことができた。
△…カールによる搬送不良は生じなかったが、波打ちによる軽度のヘッド擦れが散見された。
×…カールによる搬送不良や波打ちによるヘッド擦れが多発した。
<Hygroscopic wave>
Fifty sheets of A4 size paper were stacked on the table and left in a high temperature and high humidity environment (30 ° C., 70% RH) for 2 hours, and the number of paper undulations appearing in the CD direction was observed. In addition, when the waving was interrupted at the edge of the paper, it was counted as 0.5.
○: The number of undulations is 3.0 or less △: The number of undulations is 3.5 to 4.5 ×: The number of undulations is 5.0 or more <Printer transportability>
100 sheets of paper were printed on both sides in a low temperature and low humidity environment (10 ° C., 30% RH) and a high temperature and high humidity environment (30 ° C., 70% RH), and the printer transportability was evaluated. The paper used was left for 2 hours in each environment.
○: No conveyance failure or head rubbing occurred, and a total of 200 sheets could be printed.
Δ: No conveyance failure due to curling occurred, but slight head rubbing due to waviness was observed.
X: Conveyance failure due to curling and head rubbing due to undulation frequently occurred.

Figure 2007083681
Figure 2007083681

Figure 2007083681
Figure 2007083681

表1から、実施例1〜5で製造したインクジェット記録用紙は、ラインヘッドを有する高速インクジェットプリンターで印字した際に、発色性、インク吸収性が良好で、かつ、プリンター搬送性に優れることが分かる。
これに対し、記録用紙の水分が高い比較例1は、低湿環境で使用した際の脱湿カールが大きくなり、プリンターの給紙口で引っかかるため搬送性不良となる。一方記録用紙の水分が低い比較例2及びCD剛度の低い比較例3は、高湿環境下で使用した際の吸湿波打ちが悪化し、インクヘッドに擦れるため搬送性不良となる。また、MD剛度の高い比較例4は、低湿環境での脱湿カール及び高湿環境下での吸湿波打ちに関しては問題ないが、用紙が曲がり難いことが原因により搬送性不良となる。
From Table 1, it can be seen that the ink jet recording paper produced in Examples 1 to 5 has good color developability and ink absorbability when printed with a high speed ink jet printer having a line head and excellent printer transportability. .
On the other hand, in Comparative Example 1 in which the moisture of the recording paper is high, the dehumidification curl becomes large when used in a low humidity environment, and it is caught at the paper feed port of the printer, resulting in poor transportability. On the other hand, in Comparative Example 2 where the moisture content of the recording paper is low and Comparative Example 3 where the CD stiffness is low, the moisture absorption wave when used in a high humidity environment deteriorates and rubs against the ink head, resulting in poor transportability. In Comparative Example 4 having a high MD stiffness, there is no problem with dehumidification curl in a low-humidity environment and moisture absorption undulation in a high-humidity environment, but the transportability is poor because the paper is difficult to bend.

Claims (2)

支持体の両面にインク受理層を設けた、ラインヘッドを有する高速枚葉インクジェットプリンター用の両面塗工インクジェット記録用紙であって、含有水分が4.0〜5.5%であり、かつ剛度がCD方向で30以上、MD方向で130以下であり、かつ坪量が100g/m以下であることを特徴とする両面塗工インクジェット記録用紙。 A double-sided coated ink jet recording sheet for a high-speed sheet-fed ink jet printer having a line head provided with an ink receiving layer on both sides of a support, having a moisture content of 4.0 to 5.5% and a rigidity of A double-sided coated ink jet recording paper having a CD direction of 30 or more, an MD direction of 130 or less, and a basis weight of 100 g / m 2 or less. 透気抵抗度が30秒以上であることを特徴とする請求項1に記載の両面塗工インクジェット記録用紙。



2. The double-sided coated ink jet recording paper according to claim 1, wherein the air permeability resistance is 30 seconds or more.



JP2005278523A 2005-09-26 2005-09-26 Inkjet recording paper Pending JP2007083681A (en)