JP2007078947A - Intermediate transfer belt - Google Patents
Intermediate transfer belt Download PDFInfo
- Publication number
- JP2007078947A JP2007078947A JP2005264982A JP2005264982A JP2007078947A JP 2007078947 A JP2007078947 A JP 2007078947A JP 2005264982 A JP2005264982 A JP 2005264982A JP 2005264982 A JP2005264982 A JP 2005264982A JP 2007078947 A JP2007078947 A JP 2007078947A
- Authority
- JP
- Japan
- Prior art keywords
- intermediate transfer
- transfer belt
- image
- belt
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、電子写真方式の画像形成装置に用いられる中間転写ベルトに関し、画像欠陥のない良好なトナー画像を記録媒体上に形成することが可能な中間転写ベルトに関する。 The present invention relates to an intermediate transfer belt used in an electrophotographic image forming apparatus, and more particularly to an intermediate transfer belt capable of forming a good toner image without image defects on a recording medium.
電子写真方式の画像形成装置は、オフィス向けの複写機、プリンタに加えて、最近では、軽印刷と呼ばれる印刷分野にまで普及し、版をおこさずに数千枚レベルのプリントを短時間で行えるというメリットから注目されるようになってきた。 In addition to copiers and printers for office use, electrophotographic image forming apparatuses have recently become widespread in the printing field called light printing, and can print thousands of pages in a short time without printing. It has come to attract attention from the merit.
電子写真方式の画像形成方法の１つに、感光体上に形成されたトナー画像を転写中間体上に転写し、転写中間体より記録媒体上に２次転写する工程を経て画像形成を行うものがある。そして、中間転写体の実施形態の１つに、樹脂製の無端ベルトを用いた中間転写ベルトがあり、良好な転写性能を発現させるために、中間転写ベルトの改良がこれまでも進められてきた。 One of the electrophotographic image forming methods is a method in which a toner image formed on a photoconductor is transferred onto a transfer intermediate, and the image is formed through a secondary transfer from the transfer intermediate onto a recording medium. There is. One embodiment of the intermediate transfer member is an intermediate transfer belt using an endless belt made of resin, and the improvement of the intermediate transfer belt has been promoted so far in order to develop good transfer performance. .
例えば、高い撥水性を付与し、かつ、トナーと逆極性の摩擦帯電性を発現する材料を中間転写ベルトの表面に用いることにより、虫食い版画と呼ばれる局所的な転写不良の発生をなくして安定した転写を行える技術がある（例えば、特許文献１参照）。 For example, by using a material that imparts high water repellency and that exhibits a triboelectric charge property of reverse polarity to that of the toner on the surface of the intermediate transfer belt, it is stable without the occurrence of local transfer defects called worm-eating prints. There is a technique capable of performing transfer (for example, see Patent Document 1).
また、導電性フィラーを含有する層とシリコーン樹脂を含有する表面層を設けることにより、長期にわたりトナーの離型性を維持させるとともに、引張強度を向上させた技術がある（例えば、特許文献２参照）。 In addition, there is a technique in which a release layer of a toner is maintained over a long period of time and a tensile strength is improved by providing a layer containing a conductive filler and a surface layer containing a silicone resin (see, for example, Patent Document 2). ).
また、最近では、デジタル化の進展に対応して高精細なトナー画像を精度よく転写できるように、中間転写ベルト表面領域の性能を向上させる技術が検討されている。具体的には、表面層に導電剤を含有させた中間転写ベルト（例えば、特許文献３参照）や電子受容性あるいは電子供与性の原子団を有するカップリング剤を表面層に含有する中間転写ベルト（例えば、特許文献４参照）などが挙げられる。 Recently, a technique for improving the performance of the surface area of the intermediate transfer belt has been studied so that a high-definition toner image can be accurately transferred in accordance with the progress of digitization. Specifically, an intermediate transfer belt having a surface layer containing a conductive agent (see, for example, Patent Document 3) or an intermediate transfer belt containing a coupling agent having an electron-accepting or electron-donating atomic group in the surface layer. (For example, refer to Patent Document 4).
ところで、中間転写ベルト上のトナー像を記録部材に転写した後、記録部材を中間転写ベルトから剥離するときに剥離放電と呼ばれる現象が発生することがある。これは、中間転写ベルト側と紙側のギャップ間に電位差が生じて両者間に電界が形成されて放電を起こすもので、トナー画像上に白抜けと呼ばれる数ミリレベルの大きさの画像欠陥を発生させる。 By the way, when the toner image on the intermediate transfer belt is transferred to the recording member and then the recording member is peeled from the intermediate transfer belt, a phenomenon called peeling discharge may occur. This is because a potential difference occurs between the gap on the intermediate transfer belt side and the paper side, and an electric field is formed between the two, causing discharge, and an image defect of several millimeter level called white spot is formed on the toner image. generate.
すなわち、中間転写ベルトより記録紙を剥離するとき、残存電荷とトナー電荷が共存することにより、中間転写ベルトと記録紙間の空隙に電界が形成される。一方、空隙における耐電圧値はＰａｓｃｈｅｎの法則により規定されるが、空隙に耐電圧値以上の電界が形成されると、電荷がリークして耐電圧値以下になろうとする。この電荷のリークが放電となってあらわれる結果、トナー画像に乱れを発生させることになる。放電が発生した個所では適正なトナーの転写が行えず、白抜けの画像欠陥を発生させることになる。 That is, when the recording paper is peeled from the intermediate transfer belt, the residual charge and the toner charge coexist, whereby an electric field is formed in the gap between the intermediate transfer belt and the recording paper. On the other hand, the withstand voltage value in the air gap is defined by Paschen's law, but when an electric field higher than the withstand voltage value is formed in the air gap, the electric charge leaks and tends to be below the withstand voltage value. As a result of this electric charge leak appearing as a discharge, the toner image is disturbed. Proper toner transfer cannot be performed at the location where the discharge has occurred, and a white-out image defect occurs.
この様な画像欠陥を防止する方法の１つとして、前述の特許文献３の様に、中間転写ベルト表面層にカーボンブラック等の導電性微粒子を添加して、転写電圧による抵抗低下をなくすことで画像欠陥の発生を抑制する方法が検討されていた。 One method for preventing such image defects is to add conductive fine particles such as carbon black to the surface layer of the intermediate transfer belt so as to eliminate the resistance drop due to the transfer voltage as described in Patent Document 3 above. A method for suppressing the occurrence of image defects has been studied.
しかしながら、前述した軽印刷分野のように、数千枚レベルのプリント作成を短時間で行うケースでは、２次転写を連続的に行うために剥離放電の発生を十分に抑えることができなかった。また、中間転写ベルトと記録媒体との間に密着性が付与されることでトナー画像の転写性が向上するが、連続かつ高速でのプリント作成を円滑に行えるようにする密着性を付与することはなかなか難しく、画像欠陥の発生を十分に抑えられなかった。 However, in the case of producing prints on the order of several thousand sheets in a short time as in the light printing field described above, the occurrence of peeling discharge cannot be sufficiently suppressed because secondary transfer is continuously performed. In addition, the adhesion between the intermediate transfer belt and the recording medium improves the transferability of the toner image. However, it provides the adhesion to enable continuous and high-speed print creation smoothly. It was very difficult and the occurrence of image defects could not be suppressed sufficiently.
この様に、大量のプリント作成を連続で行うような画像形成条件下で、画像欠陥を発生せずに画像形成を行える中間転写ベルトが求められていた。
本発明は、２次転写を行った後、剥離放電を起こさずにトナー画像を転写した記録媒体を中間転写ベルトから剥離できるようにして、白抜けによる画像欠陥を発生させない中間転写ベルトを提供することを目的とする。 The present invention provides an intermediate transfer belt that does not cause image defects due to white spots by allowing a recording medium on which a toner image has been transferred without secondary discharge to be peeled off from the intermediate transfer belt after secondary transfer. For the purpose.
特に、連続で５０００枚以上のプリント作成を行う場合など、大量の画像形成を行ったときに剥離放電を起こさず、画像欠陥のないトナー画像が得られる中間転写ベルトを提供することを目的とする。 In particular, an object of the present invention is to provide an intermediate transfer belt that does not cause peeling discharge when a large amount of image formation is performed and can obtain a toner image free from image defects, such as when continuously creating 5000 or more sheets. .
本発明の課題は、以下に記載の構成により達成されることを見出した。すなわち、
（１）
基材上に少なくとも表面層を有する中間転写ベルトであって、
該表面層に導電性物質と、下記一般式（１）で表される化合物を用いて形成されるものとを含有し、
表面硬度が８５〜１３０Ｎ／ｍｍ2であることを特徴とする中間転写ベルト。
It has been found that the object of the present invention can be achieved by the constitution described below. That is,
(1)
An intermediate transfer belt having at least a surface layer on a substrate,
The surface layer contains a conductive substance and one formed using a compound represented by the following general formula (1),
An intermediate transfer belt having a surface hardness of 85 to 130 N / mm 2 .
一般式（１） Ｍ（Ｏ−ＣnＨ2n+1）m
（式中、Ｍはケイ素、アルミニウム、ジルコニウムまたはチタンを表す。ｍはＭの価数となる。）
（２）
前記一般式（１）で表される化合物が、下記一般式（２）で表されるものであることを特徴とする請求項１に記載の中間転写ベルト。
Formula (1) M (O-C n H 2n + 1) m
(In the formula, M represents silicon, aluminum, zirconium or titanium. M represents the valence of M.)
(2)
The intermediate transfer belt according to claim 1, wherein the compound represented by the general formula (1) is represented by the following general formula (2).
一般式（２） Ｓｉ（Ｏ−ＣnＨ2n+1）4
（３）
前記表面層における表面抵抗値が１×１０10〜１×１０12Ω／□であることを特徴とする前記（１）または（２）に記載の中間転写ベルト。
General formula (2) Si (O—C n H 2n + 1 ) 4
(3)
The intermediate transfer belt according to (1) or (2), wherein a surface resistance value in the surface layer is 1 × 10 10 to 1 × 10 12 Ω / □.
本発明では、特定構造の化合物と導電性物質とを中間転写ベルト表面層に含有させることにより、中間転写ベルト表面に放電可能な領域が形成されるためと推測されるが、中間転写ベルトと紙との間での集中放電を抑制できるようにした。その結果、中間転写ベルトより記録紙上に転写されたトナー画像上に白抜けが発生しなくなり、画像欠陥のない良好なトナー画像を安定して形成できるようになった。 In the present invention, it is presumed that a dischargeable region is formed on the surface of the intermediate transfer belt by containing a compound having a specific structure and a conductive material in the surface layer of the intermediate transfer belt. It was made possible to suppress the concentrated discharge between the two. As a result, white spots are not generated on the toner image transferred onto the recording paper from the intermediate transfer belt, and a good toner image without image defects can be stably formed.
とりわけ、本発明では、連続で５０００枚以上のプリント作成を行う様な場合でも、２次転写による局所的な剥離放電を起こさないので、画像欠陥のない良好な画像形成を長期にわたり安定して行えるようになった。その結果、数千枚レベルのプリント作成を短時間で行う軽印刷分野で良好な品質のプリント物を安定して提供できるようになった。 In particular, in the present invention, even in the case where 5000 or more prints are continuously produced, local peeling discharge due to secondary transfer does not occur, so that good image formation without image defects can be stably performed over a long period of time. It became so. As a result, it has become possible to stably provide prints of good quality in the light printing field in which prints on the order of several thousand sheets are made in a short time.
また、本発明では上記構成に加えて中間転写ベルトの表面物性を特定することにより、中間転写ベルト上に形成されたトナー画像と記録媒体との間に適正な密着力が発現されることを見出し、２次転写性能の向上を可能にした。 Further, in the present invention, in addition to the above-described configuration, it is found that an appropriate adhesion force is developed between the toner image formed on the intermediate transfer belt and the recording medium by specifying the surface physical properties of the intermediate transfer belt. The secondary transfer performance can be improved.
本発明では、中間転写ベルトの表面層に特定構造を有する化合物と導電性物質を含有させることにより、剥離放電の発生を抑えられることを見出した。これはおそらく、これらを含有させることで放電可能な個所が形成され、中間転写ベルト表面の帯電性が改良されて中間転写ベルトと紙との間で局所的な放電が発生しなくなったものと推測される。 In the present invention, it has been found that the occurrence of peeling discharge can be suppressed by including a compound having a specific structure and a conductive substance in the surface layer of the intermediate transfer belt. It is presumed that, by including these, dischargeable portions were formed, the chargeability of the surface of the intermediate transfer belt was improved, and local discharge was not generated between the intermediate transfer belt and the paper. Is done.
最初に、本発明に係る中間転写ベルトについて説明する。 First, the intermediate transfer belt according to the present invention will be described.
本発明に係る中間転写ベルトは、基材上に表面層を有するいわゆる多層構造のもので、表面層に前述した特定構造を有する化合物と導電性物質とを含有するものである。また、本発明では、中間転写ベルトを多層構造とすることにより、単一の材料構成では得られない、可撓性と剛性とをバランスよく発現することも可能である。なお、本発明では前述の基材のことを基材層ともいう。 The intermediate transfer belt according to the present invention has a so-called multilayer structure having a surface layer on a substrate, and the surface layer contains the compound having the specific structure described above and a conductive material. In the present invention, the intermediate transfer belt can have a multilayer structure, so that flexibility and rigidity, which cannot be obtained with a single material structure, can be expressed in a balanced manner. In the present invention, the aforementioned base material is also referred to as a base material layer.
本発明に係る中間転写ベルト２の一例を図１に示す。図１（ａ）は、表面層２１と基材層２３とからなる２層構造の中間転写ベルト２で、図１（ｂ）は、基材層２３上に中間層２４を有し、中間層２４上に表面層２１を有する３層構造の中間転写ベルト２である。また、図１（ｃ）は基材層２３の外側に２つの中間層２４、２５を有し、中間層２５の外側に表面層２１を有する４層構造の中間転写ベルト２である。
An example of the
次に、表面層に含有される特定構造の化合物と導電性物質について説明する。 Next, the compound having a specific structure and the conductive material contained in the surface layer will be described.
本発明に係る中間転写ベルト２の表面層２１には、下記一般式（１）の化合物を用いて形成されるものが含有される。
The
一般式（１） Ｍ（Ｏ−ＣnＨ2n+1）m
式中、Ｍはケイ素、アルミニウム、ジルコニウムまたはチタンのいずれかであり、ｍはＭの価数となる。一般式（１）で表される化合物は、ケイ素、アルミニウム、ジルコニウム、チタンの金属アルコキシド化合物であるが、この中でもＭがケイ素である下記に示す一般式（２）のテトラアルコキシシラン化合物が好ましく用いられる。
Formula (1) M (O-C n H 2n + 1) m
In the formula, M is any one of silicon, aluminum, zirconium or titanium, and m is the valence of M. The compound represented by the general formula (1) is a metal alkoxide compound of silicon, aluminum, zirconium, or titanium. Among them, a tetraalkoxysilane compound of the following general formula (2) in which M is silicon is preferably used. It is done.
一般式（２） Ｓｉ（Ｏ−ＣnＨ2n+1）4
上記テトラアルコキシシラン化合物では、式中のアルコキシ基は炭素数が１〜８、好ましくは１〜４のアルコキシ基である。本発明に好ましく用いられるテトラアルコキシシラン化合物の具体例としては、テトラメトキシシラン、テトラエトキシシラン、テトラブトキシシラン等が挙げられる。
General formula (2) Si (O—C n H 2n + 1 ) 4
In the tetraalkoxysilane compound, the alkoxy group in the formula is an alkoxy group having 1 to 8, preferably 1 to 4 carbon atoms. Specific examples of the tetraalkoxysilane compound preferably used in the present invention include tetramethoxysilane, tetraethoxysilane, and tetrabutoxysilane.
前述した本発明で発現された効果に対し、テトラアルコキシシラン化合物などの化合物を用いて形成されるものを表面層に含有させたことにより画像欠陥を回避できる理由は明らかではないが以下のようなことが推測される。おそらく、表面層に含有される導電性物質が結着樹脂に強固に結合する結果、表面層における導電性が向上して２次転写時の局所的な剥離放電の発生をなくして、画像欠陥の発生を回避できるようになったものと推測される。 The reason why image defects can be avoided by including in the surface layer what is formed using a compound such as a tetraalkoxysilane compound in contrast to the effects manifested in the present invention is not clear, but is as follows. I guess that. Probably, as a result of the conductive substance contained in the surface layer being firmly bonded to the binder resin, the conductivity in the surface layer is improved and the occurrence of local peeling discharge at the time of secondary transfer is eliminated. It is presumed that the occurrence can be avoided.
また、これらの化合物が表面層の結着樹脂を構成する高分子鎖との間でカップリング反応を起こすことにより、表面層に適度な硬度が付与されることも推測される。 In addition, it is presumed that moderate hardness is imparted to the surface layer by causing a coupling reaction between these compounds and the polymer chains constituting the binder resin of the surface layer.
上記以外の使用可能な金属アルコキシドの具体例として、アルコキシシラン化合物は、テトラ−ｎ−プロポキシシラン、テトラ−ｉ−プロポキシシラン、テトラ−ｎ−ブトキシシラン、テトラフェノキシシランなどが挙げられる。また、アルコキシチタン化合物は、テトラメトキシチタン、テトラエトキシチタン、テトライソプロポキシチタンなどが、アルコキシアルミニウム化合物は、トリメトキシアルミニウム、トリエトキシアルミニウム、トリイソプロポキシアルミニウム、トリブトキシアルミニウムなどが挙げられる。 Specific examples of usable metal alkoxides other than the above include tetra-n-propoxysilane, tetra-i-propoxysilane, tetra-n-butoxysilane, and tetraphenoxysilane. Examples of the alkoxytitanium compound include tetramethoxytitanium, tetraethoxytitanium, and tetraisopropoxytitanium. Examples of the alkoxyaluminum compound include trimethoxyaluminum, triethoxyaluminum, triisopropoxyaluminum, and tributoxyaluminum.
さらに、アルコキシジルコニウム化合物は、テトラエトキシジルコニウム、テトライソプロポキシジルコニウム、テトラ−ｎ−ブトキシジルコニウムなどが挙げられる。 Furthermore, examples of the alkoxyzirconium compound include tetraethoxyzirconium, tetraisopropoxyzirconium, and tetra-n-butoxyzirconium.
なお、本発明に係る中間転写ベルトには、上述した一般式（１）、（２）で表される化合物を用いて形成されるものが含有されるが、ここで、一般式（１）、（２）で表される化合物を用いて形成されるものとは、上記化合物が単体で含有されている場合や、これらの化合物と結着樹脂とがカップリング反応などにより結合したものを含有する場合を意味するものである。 The intermediate transfer belt according to the present invention includes those formed by using the compounds represented by the general formulas (1) and (2) described above. What is formed using the compound represented by (2) includes a case where the above compound is contained alone or a combination of these compounds and a binder resin by a coupling reaction or the like. Means the case.
次に、中間転写ベルトの表面層に含有される導電性物質について説明する。本発明に係る中間転写ベルトの表面層に含有される導電性物質としては、電子伝導性を与するもの（以下、「電子伝導性導電性物質」ともいう。）やイオン伝導性を付与するもの（以下、「イオン伝導性導電性物質」ともいう。）が挙げられる。 Next, the conductive material contained in the surface layer of the intermediate transfer belt will be described. The conductive material contained in the surface layer of the intermediate transfer belt according to the present invention is one that imparts electron conductivity (hereinafter also referred to as “electron conductive material”) or one that imparts ion conductivity. (Hereinafter, also referred to as “ion-conductive conductive material”).
電子伝導性導電性物質としては、例えば、カーボンブラック、グラファイト、アルミニウム、ニッケル、銅合金等の金属又は合金、酸化錫、酸化亜鉛、チタン酸カリウム、酸化錫−酸化インジウムまたは酸化錫−酸化アンチモン複合酸化物等の金属酸化物等が挙げられる。この中でもファーネスブラック、ケッチェンブラック、チャンネルブラック等のカーボンブラックが代表的なものである。具体的には、電気化学（株）製粒状アセチレンブラック、旭カーボン（株）製ＨＳ−５００、アサヒサーマルＦＴ、アサヒサーマルＭＴ、ライオンアグゾ（株）製ケッチェンブラック、キャボット（株）製バルカンＸＣ−７２、Ｄｅｇｕｓｓａ社製ＳＰＥＣＩＡＬ ＢＬＡＣＫ４等が挙げられる。これらのカーボンブラックは１種単独で使用する他に、２種以上を併用してもよい。 Examples of the electron conductive conductive material include metals or alloys such as carbon black, graphite, aluminum, nickel, and copper alloys, tin oxide, zinc oxide, potassium titanate, tin oxide-indium oxide, or tin oxide-antimony oxide composite. Examples thereof include metal oxides such as oxides. Among these, carbon black such as furnace black, ketjen black, and channel black are representative. Specifically, granular acetylene black manufactured by Electrochemical Co., Ltd., HS-500 manufactured by Asahi Carbon Co., Ltd., Asahi Thermal FT, Asahi Thermal MT, Ketjen Black manufactured by Lion Azo Co., Ltd., Vulcan XC- manufactured by Cabot Co., Ltd. 72, SPECIAL BLACK4 manufactured by Degussa, and the like. These carbon blacks may be used alone or in combination of two or more.
電子伝導性導電性物質の含有量は、前記表面層中の結着樹脂１００質量部に対して、４〜２０質量部が好ましく、５〜１５質量部がより好ましい。電子伝導性導電性物質の含有量を上記範囲とすることにより、表面層に適度な電子伝導性が付与される。 4-20 mass parts is preferable with respect to 100 mass parts of binder resins in the said surface layer, and, as for content of an electron conductive electroconductive substance, 5-15 mass parts is more preferable. By setting the content of the electron-conductive conductive material in the above range, moderate electron conductivity is imparted to the surface layer.
イオン伝導性導電性物質としては、例えば、カルボキシル基に４級アンモニウム塩基を結合する（メタ）アクリレートとの各種（例えばスチレン）共重合体、４級アンモニウム塩基と結合するマレイミドとメタアクリレートとの共重合体等の４級アンモニウム塩基を結合するポリマー、ポリスルホン酸ナトリウム等に見られるスルホン酸のアルカリ金属塩を結合するポリマー、分鎖中に少なくともアルキルオキシドの親水性ユニットを結合するポリマー、例えば、ポリエチレンオキシド、ポリエチレングリコール系−ポリアミド共重合体、ポリエチレン−エピクロルヒドリン共重合体、ポリエーテルアミドイミド、ポリエーテルをセグメントとするブロック型のポリマー等の各種の界面活性剤が挙げられる。これらは、１種単独で使用してもよく、２種以上併用してもよい。 Examples of the ion conductive conductive material include various (for example, styrene) copolymers with (meth) acrylates that bind a quaternary ammonium base to a carboxyl group, and copolymers of maleimide and methacrylate that bind to a quaternary ammonium base. Polymers that bind quaternary ammonium bases such as polymers, polymers that bind alkali metal salts of sulfonic acids found in sodium polysulfonates, polymers that bind at least alkyl oxide hydrophilic units in the chain, such as poly Examples include various surfactants such as ethylene oxide, polyethylene glycol-polyamide copolymer, polyethylene-epichlorohydrin copolymer, polyether amide imide, and block polymer having a polyether segment. These may be used alone or in combination of two or more.
また、イオン伝導性導電性物質と前述の電子伝導性導電性物質とを組み合わせてもよく、安定した電気抵抗値が得られる。 Further, an ion conductive material and the above-described electron conductive material may be combined, and a stable electric resistance value can be obtained.
イオン伝導性導電性物質の含有量は、表面層中の結着樹脂１００質量部に対して、０．５〜３０質量部が好ましく、１〜２０質量部がより好ましい。 0.5-30 mass parts is preferable with respect to 100 mass parts of binder resin in a surface layer, and, as for content of an ion conductive electroconductive substance, 1-20 mass parts is more preferable.
この様に、中間転写ベルト２を構成する表面層２１には、前述した化合物と導電性物質が含有されている。また、表面層２１には表面エネルギーの低い結着樹脂が好ましく用いられ、中間転写ベルト２の表面エネルギーを低くすることによりベルトからのトナー画像の離れを促進させている。その結果、２次転写時に中間転写ベルトから記録媒体へのトナー画像の転写性が促進されて、記録媒体上には高画質のトナー画像が得られる。低表面エネルギーを有する材料としては、例えば、フッ素系材料、シリコン系材料、あるいはこれらを主成分とする材料、フッ素樹脂粉末、シリコーン樹脂、シリコンオイル成分を分散してなる材料等が挙げられる。
In this way, the
この中でも、シリコーン樹脂を用いて形成した表面層２１が好ましい。表面層２１の形成に使用されるシリコーン樹脂は、特に限定されるものではないが、通常、作業効率から液状のシリコーン樹脂が好ましく、ｎ−ヘキサン等の有機溶剤を含有したものや有機溶媒を使用しない反応型のものが挙げられる。また、特にハードタイプの一液または二液の硬化型のシリコーン樹脂が好ましい。なかでも、加熱硬化型シリコーン樹脂（メチル系）や室温硬化型シリコーン樹脂が好適である。
Among these, the
以下に、本発明に係る中間転写ベルト２の表面層２１に使用可能な硬化型シリコーン樹脂の硬化反応の例を下記に示す。
Below, the example of hardening reaction of the curable silicone resin which can be used for the
中間転写体２を構成する基材層２３について説明する。基材層２３は、クリーニングブレードのあたりをはじめとする中間転写ベルト２に加わる負荷によりベルトが変形することを回避し、転写部への影響を低減させる剛性を有するものである。基材層２３は、ヤング率が２００ＭＰａ（２００ｋｇ／ｍｍ2）以上となる材料を用いて形成することが好ましく、３００ＭＰａ（３００ｋｇ／ｍｍ2）以上の材料がより好ましい。
The
ベルト材料（ベルト状の基材に用いられる材料）のヤング率とベルト駆動時の外乱（負荷変動）によるベルトの変位量との関係は、下記式（１）で表すことができる。 The relationship between the Young's modulus of the belt material (the material used for the belt-shaped base material) and the amount of displacement of the belt due to disturbance (load fluctuation) when the belt is driven can be expressed by the following equation (1).
式（１） ΔＬ＝Ｐ・Ｌ・α／（ｔ・ｗ・Ｅ）
ここで、ΔＬ：ベルトの変位量（μｍ）
Ｐ：負荷 （Ｎ）
Ｌ：２本のテンションロール間のベルトの長さ（ｍｍ）
α：係数
ｔ：ベルト厚み（ｍｍ）
ｗ：ベルト幅（ｍｍ）
Ｅ：ベルト材料のヤング率（Ｎ／ｍｍ2）を表す。
Formula (1) (DELTA) L = P * L * (alpha) / (t * w * E)
Where ΔL: belt displacement (μm)
P: Load (N)
L: Belt length between two tension rolls (mm)
α: Coefficient
t: Belt thickness (mm)
w: Belt width (mm)
E: represents the Young's modulus (N / mm 2 ) of the belt material.
ベルト駆動時の外乱（負荷変動）によるベルトの伸び・縮み（変位量）は、ベルト材料のヤング率と厚みに逆比例する。すなわち、高ヤング率のベルト材料を用いると、ベルト駆動時の外乱（負荷変動）によるベルトの変位量が少なくなり、駆動時の応力に対するベルト変形が小さくなり、良好な画質が安定して得られる。この様な性能を発現する材料として、例えば、ポリカーボネート、ＰＶＤＦ（ポリフッ化ビニリデン）、ポリイミド、ＰＥＥＫ（ポリエーテル・エ−テルケトン）等の樹脂材料が挙げられる。これらの樹脂材料ではヤング率が２００ＭＰａを超えるものであり、厚み１００〜１５０μｍで、ベルト基材としての機械特性を満足する。 The expansion / contraction (displacement amount) of the belt due to disturbance (load fluctuation) during driving of the belt is inversely proportional to the Young's modulus and thickness of the belt material. That is, when a belt material having a high Young's modulus is used, the amount of displacement of the belt due to disturbance (load fluctuation) at the time of driving the belt is reduced, and the belt deformation with respect to the stress at the time of driving is reduced. . Examples of materials that exhibit such performance include resin materials such as polycarbonate, PVDF (polyvinylidene fluoride), polyimide, and PEEK (polyether ether ketone). These resin materials have a Young's modulus exceeding 200 MPa, have a thickness of 100 to 150 μm, and satisfy the mechanical properties as a belt base material.
また、基材層２３に使用される材料は、例えば、ポリイミド、ポリエステル、ポリエーテルエーテルケトン、ポリアミド、ポリカーボネート、ポリフッ化ビニリデン（ＰＶＤＦ）、ポリフロロエチレン−エチレン共重合体（ＥＴＦＥ）等の樹脂材料及びこれらを主原料としてなる樹脂材料が挙げられる。更に、前述の脂材料と弾性材料とをブレンドした材料を使用することも可能である。前記弾性材料としては、例えば、ポリウレタン、塩素化ポリイソプレン、ＮＢＲ、クロロピレンゴム、ＥＰＤＭ、水素添加ポリブタジエン、ブチルゴム、シリコーンゴム等が挙げられる。これらは１種単独で使用してもよく、２種以上を併用してもよい。
The material used for the
この中でも、ポリイミド樹脂を含有することが好ましい。ポリイミド樹脂は、ポリイミド樹脂の前駆体であるポリアミック酸の加熱により形成される。また、ポリアミック酸は、テトラカルボン酸二無水物や、その誘導体とジアミンのほぼ等モル混合物を有機極性溶媒に溶解させ、溶液状態で反応させることにより得られる。 Among these, it is preferable to contain a polyimide resin. The polyimide resin is formed by heating polyamic acid that is a precursor of the polyimide resin. The polyamic acid can be obtained by dissolving tetracarboxylic dianhydride or an approximately equimolar mixture of its derivative and diamine in an organic polar solvent and reacting in a solution state.
ポリアミック酸の調液に使用される芳香族テトラカルボン酸二無水物としては、ピロメリット酸、ナフタレン−１，４，５，８−テトラカルボン酸、ナフタレン−２，３，６，７−テトラカルボン酸、２，３，５，６−ビフェニルテトラカルボン酸、２，２’，３，３’−ビフェニルテトラカルボン酸、３，３’，４，４’−ビフェニルテトラカルボン酸、３，３’，４，４’−ジフェニルエーテルテトラカルボン酸、３，３’，４，４’−ベンゾフェノンテトラカルボン酸、３，３’，４，４’−ジフェニルスルホンテトラカルボン酸、３，３’，４，４’−アゾベンゼンテトラカルボン酸、ビス（２，３−ジカルボキシフェニル）メタン、ビス（３，４−ジカルボキシフェニル）メタン、β，β−ビス（３，４−ジカルボキシフェニル）プロパン、β，β−ビス（３，４−ジカルボキシフェニル）ヘキサフルオロプロパン等が挙げられる。 Examples of aromatic tetracarboxylic dianhydrides used for preparing polyamic acid include pyromellitic acid, naphthalene-1,4,5,8-tetracarboxylic acid, naphthalene-2,3,6,7-tetracarboxylic acid. Acid, 2,3,5,6-biphenyltetracarboxylic acid, 2,2 ′, 3,3′-biphenyltetracarboxylic acid, 3,3 ′, 4,4′-biphenyltetracarboxylic acid, 3,3 ′, 4,4′-diphenyl ether tetracarboxylic acid, 3,3 ′, 4,4′-benzophenone tetracarboxylic acid, 3,3 ′, 4,4′-diphenylsulfone tetracarboxylic acid, 3,3 ′, 4,4 ′ -Azobenzenetetracarboxylic acid, bis (2,3-dicarboxyphenyl) methane, bis (3,4-dicarboxyphenyl) methane, β, β-bis (3,4-dicarboxyphenyl) propyl Lopan, β, β-bis (3,4-dicarboxyphenyl) hexafluoropropane, and the like.
また、芳香族ジアミン成分としては、ｍ−フェニルジアミン、ｐ−フェニルジアミン、２，４−ジアミノトルエン、２，６−ジアミノトルエン、２，４−ジアミノクロロベンゼン、ｍ−キシリレンジアミン、ｐ−キシリレンジアミン、１，４−ジアミノナフタレン、１，５−ジアミノナフタレン、２，６−ジアミノナフタレン、２，４’−ジアミノナフタレビフェニル、ベンジジン、３，３−ジメチルベンジジン、３，３’−ジメトキシベンジジン、３，４’−ジアミノジフェニルエ−テル、４，４’−ジアミノジフェニルエーテル（オキシ−ｐ，ｐ’−ジアニリン；ＯＤＡ）、４，４’−ジアミノジフェニルスルフィド、３，３’−ジアミノベンゾフェノン、４，４’−ジアミノフェニルスルホン、４，４’−ジアミノアゾベンゼン、４，４’−ジアミノジフェニルメタン、β，β−ビス（４−アミンフェニル）プロパン等が挙げられる。 Moreover, as an aromatic diamine component, m-phenyldiamine, p-phenyldiamine, 2,4-diaminotoluene, 2,6-diaminotoluene, 2,4-diaminochlorobenzene, m-xylylenediamine, p-xylylenediamine Amine, 1,4-diaminonaphthalene, 1,5-diaminonaphthalene, 2,6-diaminonaphthalene, 2,4′-diaminonaphthalenediphenyl, benzidine, 3,3-dimethylbenzidine, 3,3′-dimethoxybenzidine, 3,4′-diaminodiphenyl ether, 4,4′-diaminodiphenyl ether (oxy-p, p′-dianiline; ODA), 4,4′-diaminodiphenyl sulfide, 3,3′-diaminobenzophenone, 4, 4′-diaminophenylsulfone, 4,4′-diaminoazobenzene, 4, '- diaminodiphenylmethane, beta, beta-bis (4-amine phenyl) propane.
さらに、ポリアミック酸の調液に使用される有機極性溶媒としては、例えば、Ｎ−メチル−２−ピロリドン、Ｎ，Ｎ−ジメチルアセトアミド、ジメチルスルホキシド、ヘキサメチルホスホルトリアミド等が挙げられる。これらの有機極性溶媒には、必要に応じて、クレゾ−ル、フェノ−ル、キシレノール等のフェノール類、ヘキサン、ベンゼン、トルエン等の炭化水素類を混合することができる。これらの有機極性溶媒を１種単独、あるいは２種類以上の混合物として使用することも可能である。 Furthermore, as an organic polar solvent used for the preparation of polyamic acid, for example, N-methyl-2-pyrrolidone, N, N-dimethylacetamide, dimethyl sulfoxide, hexamethyl phosphortriamide and the like can be mentioned. These organic polar solvents can be mixed with phenols such as cresol, phenol and xylenol, and hydrocarbons such as hexane, benzene and toluene, if necessary. These organic polar solvents can be used alone or as a mixture of two or more.
このようなポリアミック酸の中でも、特に、芳香族テトラカルボン酸二無水物と芳香族ジアミンとを反応して得られるポリアミック酸が好ましい。具体的には、ポリイミド樹脂材料として、ＤｕＰｏｎｔ（株）のカプトンＨＡ等のポリピロメリット酸イミド系のイミド樹脂材料、宇部興産（株）のユーピレックスＳ等のポリビフェニルテトラカルボン酸イミド系樹脂材料、宇部興産（株）のユーピレックスＲ、三井東圧化学工業（株）のＬＡＲＣ−ＴＰＩ（熱可塑性ポリイミド樹脂）等のポリベンゾフェノンテトラカルボン酸イミド酸系樹脂材料等が挙げられ、いずれも、ヤング率が３００ＭＰａ（３００ｋｇ／ｍｍ2）以上であり、厚み７０〜１５０μｍで、ベルト基材としての機械特性を満足させることができる。 Among such polyamic acids, a polyamic acid obtained by reacting an aromatic tetracarboxylic dianhydride and an aromatic diamine is particularly preferable. Specifically, as a polyimide resin material, a polypyromellitic acid imide resin material such as DuPont Kapton HA, a polybiphenyltetracarboxylic acid imide resin material such as Ube Industries, Upilex S, Ube Industries, Ltd. Upilex R, Mitsui Toatsu Chemical Industries, Ltd. LARC-TPI (thermoplastic polyimide resin) and other polybenzophenone tetracarboxylic acid imide acid resin materials, etc., all of which have Young's modulus It is 300 MPa (300 kg / mm 2 ) or more, and a thickness of 70 to 150 μm can satisfy the mechanical properties as a belt base material.
また、本発明の中間転写体の基材に、例えば、宇部興産（株）のユーピレックスＳ等のポリビフェニルテトラカルボン酸イミド系樹脂材料にカーボンブラックを分散した材料を用いると、該材料のヤング率は、２００ＭＰａ（２００ｋｇ／ｍｍ2）以上であり、ベルトの厚み７０〜１００μｍで、ベルト基材としての機械特性を満足させることができる。 Further, when a material obtained by dispersing carbon black in a polybiphenyltetracarboxylic imide resin material such as Upilex S of Ube Industries, Ltd. is used as the base material of the intermediate transfer member of the present invention, the Young's modulus of the material is used. Is 200 MPa (200 kg / mm 2 ) or more, and a belt thickness of 70 to 100 μm can satisfy the mechanical properties as a belt substrate.
なお、本発明では、基材層にポリイミド系樹脂を使用する場合、基材層におけるポリイミド系樹脂の含有率が５１％以上であることが好ましい。 In addition, in this invention, when using a polyimide-type resin for a base material layer, it is preferable that the content rate of the polyimide-type resin in a base material layer is 51% or more.
本発明に係る中間転写ベルトは、図１の（ｂ）や（ｃ）に示すように、基材層２３と表面層２１との間に中間層を設けることも可能である。中間層２４に使用可能な材料としては、ポリアミド樹脂が挙げられ、具体的なポリアミド樹脂の例としては、Ｎ−メトキシメチル化ナイロン（以下「ナイロン８」と略す）、ナイロン１２、共重合ナイロン等が挙げられる。本発明では、基材層２３と表面層２１との密着強度を向上させ、しかも、これらの層が相溶しないようにするために、中間層２４を設けることは好ましい。
The intermediate transfer belt according to the present invention can also be provided with an intermediate layer between the
ポリアミド樹脂の溶剤としては、メタノール、エタノール等の単独溶剤またはそれら単独溶剤に水、トルエン等を混合させた混合溶剤、１−プロパノール、２−プロパノール等が用いられる。なかでも、ナイロン８とメタノール／水混合溶剤（メタノール／水＝３／１）との組合わせが好適である。
As the solvent for the polyamide resin, a single solvent such as methanol or ethanol, or a mixed solvent obtained by mixing water, toluene or the like with these single solvents, 1-propanol, 2-propanol or the like is used. Among these, a combination of
また、図１（ｃ）のベルトのように２つの中間層を設けることも可能で、前述のポリアミド樹脂の中間層２４に隣接させて第２の中間層２５を設け、多層化により中間転写ベルトの強度がより増大する。第２の中間層２５に使用可能な樹脂材料としては、前述したポリイミド樹脂やポリアミド樹脂の他に、フッ化ビニリデン−四フッ化エチレン共重合体、エチレン−四フッ化エチレン共重合体、ポリクロロトリフルオロエチレン、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体、テトラフルオロエチレン−パーフルオロアルキルビニルエーテル共重合体等のフッ素樹脂が挙げられる。
It is also possible to provide two intermediate layers as in the belt of FIG. 1 (c). A second
本発明に係る中間転写ベルトは、各層に導電性フィラーと呼ばれる導電性もしくは半導電性の微粉末を含有させることも可能である。使用可能な導電性フィラーとしては、例えば、カーボンブラック等の導電性粉末、アルミニウム粉末、ニッケル粉末、ステンレス粉末等の金属粉末、ｃ−ＺｎＯ、ｃ−ＴｉＯ2、ｃ−ＺｎＯ4、ｃ−ＳｎＯ2等の導電性金属酸化物、グラファイト、４級アンモニウム塩、リン酸エステル、スルホン酸塩、脂肪族多価アルコール、脂肪族アルコールサルフェート塩等のイオン性導電材等が挙げられる。これら導電性フィラーのなかでも、良好な分散安定性が得られるケッチェンブラック、アセチレンブラック等のカーボンブラックやｃ−ＴｉＯ2、ｃ−ＳｎＯ2が好ましい。なお、上記「ｃ−」は、導電性を有するという意味である。これらの導電性フィラーは、単独でもしくは２種以上を併せて用いられる。 The intermediate transfer belt according to the present invention can also contain conductive or semiconductive fine powder called conductive filler in each layer. Usable conductive fillers include, for example, conductive powder such as carbon black, metal powder such as aluminum powder, nickel powder, stainless steel powder, c-ZnO, c-TiO 2 , c-ZnO 4 , c-SnO 2. And conductive metal oxides such as graphite, quaternary ammonium salts, phosphate esters, sulfonates, aliphatic polyhydric alcohols, aliphatic alcohol sulfate salts, and the like. Among these conductive fillers, carbon black such as ketjen black and acetylene black, c-TiO 2 , and c-SnO 2 that can provide good dispersion stability are preferable. In addition, the above “c−” means having conductivity. These conductive fillers may be used alone or in combination of two or more.
本発明では中間転写ベルトに導電性フィラーを含有させることにより、中間転写ベルトにおける抵抗率の調整や抵抗バラツキの抑制、さらには、表面層に含有させた導電性樹脂微粒子を補助して、転写電圧による電界集中の発生の抑制をより効果的に行えるようにすることが期待される。 In the present invention, by containing a conductive filler in the intermediate transfer belt, adjustment of resistivity and resistance variation in the intermediate transfer belt are suppressed, and further, the conductive resin fine particles contained in the surface layer are assisted to transfer voltage. It is expected to be able to more effectively suppress the occurrence of electric field concentration due to.
本発明に係る中間転写ベルトの製造方法は、特に限定されるものではないが、例えば、各層の形成材料およびその溶剤をそれぞれ適宜に配合し、ボールミル等で混練、攪拌して各コーティング液を調製する。このようにして調製したコーティング液の濃度は、層の厚みに応じて適宜に設定される。ついで、各コーティング液をそれぞれ槽に収容し、その一方でアルミニウム、ステンレス等の金属製の軸体を準備して、この軸体を基材層用のコーティング液が収容されている槽中に垂直に立てた状態で入れて浸漬させる。この時、浸漬を数回繰り返して所定の厚さの塗膜を形成させた後、コーティング液中から軸体を引き上げる。ついで、各層のコーティング液を用いて同様の操作を繰り返し、多層構造を形成する。次に、乾燥し溶剤を除去した後、加熱処理（例えば６０〜１８０℃×６０分間）を行い、軸体を抜き取って図１に示す無端状の中間転写ベルトを作製する。 The method for producing the intermediate transfer belt according to the present invention is not particularly limited. For example, each layer forming material and the solvent thereof are appropriately blended, and each coating solution is prepared by kneading and stirring with a ball mill or the like. To do. The concentration of the coating solution thus prepared is appropriately set according to the layer thickness. Next, each coating solution is accommodated in a tank, and on the other hand, a shaft made of metal such as aluminum or stainless steel is prepared, and this shaft is vertically placed in a tank in which the coating liquid for the base material layer is accommodated. Put in a standing condition and immerse. At this time, the immersion is repeated several times to form a coating film having a predetermined thickness, and then the shaft is pulled up from the coating solution. Subsequently, the same operation is repeated using the coating liquid of each layer to form a multilayer structure. Next, after drying and removing the solvent, heat treatment (for example, 60 to 180 ° C. × 60 minutes) is performed, and the shaft body is extracted to produce the endless intermediate transfer belt shown in FIG.
この浸漬法による製法以外にも、押出成形法、スプレーコーティング法、インフレーション法、ブロー成形法等の方法により、中間転写ベルトを作製することが可能である。 In addition to this dipping method, an intermediate transfer belt can be produced by methods such as extrusion molding, spray coating, inflation, and blow molding.
また、特に、基材層にポリイミド樹脂を使用する場合は、例えば、全芳香族骨格を有するテトラカルボン酸二無水物とジアミン成分とを重合反応して得たポリアミド酸溶液を適宜な方式で展開し、その展開層を乾燥製膜してフィルム状に成形し、その成形物を加熱処理してポリアミド酸をイミドに転化する方法により基材層が得られる。そして、基材層上に他層を構成するコーティング液を順次浸漬、あるいは、スプレーコーティングして中間転写ベルトを作製する。 In particular, when a polyimide resin is used for the base material layer, for example, a polyamic acid solution obtained by polymerizing a tetracarboxylic dianhydride having a wholly aromatic skeleton and a diamine component is developed in an appropriate manner. Then, the development layer is dried and formed into a film, and the base material layer is obtained by a method of heat-treating the molded product to convert the polyamic acid into an imide. Then, an intermediate transfer belt is produced by sequentially dipping or spray-coating a coating solution constituting another layer on the base material layer.
シームレスの中間転写ベルトを形成する場合、例えば、ポリアミド酸溶液を円筒状金型の外周面に浸漬する方式や、内周面に塗布する方式や更に遠心する方式、或いは注形型に充填する方式などの適宜な方式でリング状に展開し、その展開層を乾燥製膜してベル卜形に成形し、その成形物を加熱処理してポリアミド酸をイミドに転化して型より回収する方法などの従来に準じた適宜な方法により行うことができる（特開昭６１−９５３６１号公報、特開昭６４−２２５１４号公報、特開平３−１８０３０９号公報等）。シームレスベルトの形成に際しては、型の離型処理や脱泡処理などの適宜な処理を施すことができる。 When forming a seamless intermediate transfer belt, for example, a method in which a polyamic acid solution is immersed in the outer peripheral surface of a cylindrical mold, a method in which it is applied to the inner peripheral surface, a method in which centrifugation is further performed, or a method in which a casting mold is filled Such as a method of expanding into a ring shape by an appropriate method such as, drying the formed layer into a bell-shaped shape, heat-treating the molded product to convert the polyamic acid into an imide, and recovering from the mold Can be carried out by an appropriate method according to the conventional method (JP-A 61-95361, JP-A 64-22514, JP-A 3-180309, etc.). In forming the seamless belt, an appropriate treatment such as mold release treatment or defoaming treatment can be performed.
本発明に係る中間転写ベルトは、ベルト表面の表面抵抗率が１×１０10〜１×１０12Ω／□であることが好ましい。表面抵抗率を上記範囲内にすることで、前述した導電性微粒子の作用によるポストニップ部（２次転写部で記録媒体と中間転写ベルトとが剥離する個所）での局所的な剥離放電の抑制を補助しているものと推測される。また、プレニップ部（２次転写部の記録媒体と中間転写体とが接触開始する個所）でも電界強度の均一化を補助しているものと推測され、従来技術でプレニップ部でのギャップ放電による影響として懸念されていた画質の粒状性に対する影響も改善されている。 The intermediate transfer belt according to the present invention preferably has a surface resistivity of 1 × 10 10 to 1 × 10 12 Ω / □ on the belt surface. By controlling the surface resistivity within the above range, suppression of local peeling discharge at the post nip portion (where the recording medium and the intermediate transfer belt peel at the secondary transfer portion) due to the action of the conductive fine particles described above is suppressed. Presumed to be assisting. In addition, it is presumed that the pre-nip portion (where the recording medium of the secondary transfer portion and the intermediate transfer body start to contact) also assists in uniformizing the electric field strength, and the effect of gap discharge at the pre-nip portion in the prior art. The influence on the graininess of the image quality that has been a concern is also improved.
本発明に係る中間転写ベルト表面における表面抵抗率は、円形電極（例えば、三菱油化（株）製ハイレスターＩＰの「ＨＲプローブ」）を用い、ＪＩＳ Ｋ６９９１に基づいて測定することができる。本発明に係る中間転写ベルトの表面抵抗率の測定方法は、例えば、特開２００１−２４２７２５号公報の段落００４７や図７の記載を参照することができる。 The surface resistivity on the surface of the intermediate transfer belt according to the present invention can be measured based on JIS K6991 using a circular electrode (for example, “HR probe” of High Lester IP manufactured by Mitsubishi Oil Chemical Co., Ltd.). For the method of measuring the surface resistivity of the intermediate transfer belt according to the present invention, reference can be made to, for example, the description in paragraph 0047 and FIG. 7 of JP-A-2001-242725.
また、本発明に係る中間転写ベルトの体積抵抗率は、１×１０9〜１×１０11Ω・ｃｍであることが好ましい。体積抵抗率を上記範囲内にすることで、中間転写体より記録媒体に転写された未定着トナー像の電荷を適度に保持する様に作用する静電的な力により、トナー同士の静電的反発力や画像エッジ付近のフリンジ電界の影響が抑制されるものと推測される。その結果、記録媒体上に転写されたトナー画像は飛散せずに、静電的反発力などによるノイズの影響を受けることなく安定した画像形成が期待される。この様に、本発明に係る中間転写ベルトは、画像欠陥の発生防止に加えてトナー飛散の発生を懸念する必要がない。 The volume resistivity of the intermediate transfer belt according to the present invention is preferably 1 × 10 9 to 1 × 10 11 Ω · cm. By setting the volume resistivity within the above range, the electrostatic force between the toners is increased by an electrostatic force that acts to appropriately hold the charge of the unfixed toner image transferred from the intermediate transfer member to the recording medium. It is estimated that the influence of the repulsive force and the fringe electric field near the image edge is suppressed. As a result, the toner image transferred onto the recording medium does not scatter, and stable image formation is expected without being affected by noise due to electrostatic repulsion. In this way, the intermediate transfer belt according to the present invention does not need to worry about the occurrence of toner scattering in addition to preventing the occurrence of image defects.
体積抵抗率の測定は、前述の表面抵抗率と同様に円形電極（例えば、三菱油化（株）製ハイレスターＩＰのＨＲプローブ）を用い、ＪＩＳ Ｋ６９９１に基づいて測定することが可能である。体積抵抗率の具体的な測定方法は、例えば、特開２００１−２４２７２５号公報の段落００４８や図８の記載を参照することができる。 The volume resistivity can be measured based on JIS K6991 using a circular electrode (for example, HR probe of Hirester IP manufactured by Mitsubishi Yuka Co., Ltd.) in the same manner as the surface resistivity described above. For a specific method of measuring the volume resistivity, reference can be made to, for example, paragraph 0048 of JP-A-2001-242725 and the description of FIG.
本発明に係る中間転写体ベルトの表面硬度は８５〜１３０Ｎ／ｍｍ2である。ここで、表面硬度は金属材料の硬さ測定等に広く用いられているビッカース圧子により、圧子が試料にどれだけ侵入したかを測定する方法によって求めることができる。試験荷重Ｐ（ｍＮ）、圧子の試料への侵入量（押し込み深さ）Ｄ（μｍ）とした時、表面硬度ＤＨは下記式（３）で定義される。 The surface hardness of the intermediate transfer belt according to the present invention is 85 to 130 N / mm 2 . Here, the surface hardness can be obtained by a method of measuring how much the indenter has entered the sample with a Vickers indenter widely used for measuring the hardness of a metal material. When the test load P (mN) and the amount of penetration of the indenter into the sample (indentation depth) D (μm), the surface hardness DH is defined by the following formula (3).
式（３）
ＤＨ≡αＰ／Ｄ2
ここで、αは圧子形状による定数で、α＝３．８５８４（使用圧子：ビッカース圧子の場合）である。
Formula (3)
DH≡αP / D 2
Here, α is a constant depending on the shape of the indenter, and α = 3.8854 (used indenter: in the case of a Vickers indenter).
この表面硬度は、圧子を押し込んで行く過程の過重と押し込み深さから得られる硬さで、試料の塑性変形だけでなく、弾性変形をも含んだ状態での材料の強度特性を表すものである。なおかつ、その計測面積は微小であり、トナー粒径に近い範囲でより正確な硬度の測定が可能になる。本発明者らは、ここで得られたダイナミックス硬度と、ホロキャラクターの発生レベルには極めて正確な相関があることを発見した。即ち、中間転写体の転写面の表面硬度が好ましくは１０以下、より好ましくは５以下の場合には、上述した２次転写部において、バイアスローラの押圧力によって中間転写体の転写面の変形が起こり、これにより中間転写体上のトナーに集中していた押圧力は分散される。このためトナーは凝集せず、ライン画像が中抜けするホロキャラクター等の画質欠陥は発生しない。 This surface hardness is the hardness obtained from the excessive weight and indentation depth in the process of indenting the indenter, and represents the strength characteristics of the material in a state including not only plastic deformation of the sample but also elastic deformation. . In addition, the measurement area is very small, and more accurate hardness measurement is possible within a range close to the toner particle diameter. The present inventors have found that there is a very accurate correlation between the dynamics hardness obtained here and the generation level of the holocharacter. That is, when the surface hardness of the transfer surface of the intermediate transfer member is preferably 10 or less, more preferably 5 or less, the transfer surface of the intermediate transfer member is deformed by the pressing force of the bias roller in the secondary transfer portion described above. As a result, the pressing force concentrated on the toner on the intermediate transfer member is dispersed. For this reason, the toner does not aggregate, and image quality defects such as holocharacters in which the line image is lost do not occur.
なお、中間転写体の転写面における微小表面硬度は、ＤＩＮ５０ ３５９に準拠するユニバーサル硬度により測定される。具体的には、微小硬度計Ｈ１００（フィッシャーインスツルメンツ社製）にて測定し、プログラムＷＩＮ−ＨＣＵによって解析した。
測定条件は、以下の通りである。
The micro surface hardness on the transfer surface of the intermediate transfer member is measured by universal hardness in accordance with
The measurement conditions are as follows.
測定環境：２３℃、５５％ＲＨ
使用圧子：ビッカース圧子
負荷速度：１０ｍＮ／２０ｓｅｃ
最大押込み深さ：０．５μｍ
次に、本発明に係る中間転写ベルトが使用可能な画像形成装置について説明する。
Measurement environment: 23 ° C, 55% RH
Working indenter: Vickers indenter Load speed: 10 mN / 20 sec
Maximum indentation depth: 0.5 μm
Next, an image forming apparatus in which the intermediate transfer belt according to the present invention can be used will be described.
本発明に係る中間転写ベルトの使用が可能な画像形成装置としては、例えば、複写機やレーザプリンタ等が挙げられるが、特に、５０００枚以上の連続プリントを行うような画像形成装置が含まれる。この様な画像形成では、中間転写ベルトと記録紙との間での電界発生が頻繁に行われるが、本発明に係る中間転写ベルトを使用することにより画像欠陥を発生させることのない安定した２次転写を実現している。 Examples of the image forming apparatus that can use the intermediate transfer belt according to the present invention include a copying machine and a laser printer. In particular, an image forming apparatus that performs continuous printing of 5000 sheets or more is included. In such image formation, an electric field is frequently generated between the intermediate transfer belt and the recording paper. However, by using the intermediate transfer belt according to the present invention, a stable 2 which does not cause an image defect is generated. The next transfer is realized.
本発明に使用可能な画像形成装置は、画像情報に応じた静電潜像を形成する像担持体、像担持体に形成した静電潜像をトナーを用いて可視化する現像装置、像担持体に担持されたトナー像を本発明に係る中間転写ベルトに転写する１次転写手段、中間転写ベルト上のトナー像を紙やＯＨＰシートといった記録媒体上に転写する２次転写手段とを有する。そして、本発明に係る中間転写ベルトを中間転写体として備えることにより、剥離放電による画像欠陥を発生させることのない安定した画像形成が行える。 An image forming apparatus usable in the present invention includes an image carrier that forms an electrostatic latent image according to image information, a developing device that visualizes the electrostatic latent image formed on the image carrier using toner, and an image carrier. Primary transfer means for transferring the toner image carried on the intermediate transfer belt to the intermediate transfer belt according to the present invention, and secondary transfer means for transferring the toner image on the intermediate transfer belt onto a recording medium such as paper or an OHP sheet. By providing the intermediate transfer belt according to the present invention as an intermediate transfer member, stable image formation without causing image defects due to peeling discharge can be performed.
本発明に使用可能な中間転写方式の画像形成装置は、特に限定されるものではなく、例えば、単色のトナーのみにより画像形成を行うモノクロの画像形成装置や、感光体ドラム等の像担持体上に担持されたトナー像の中間転写体への１次転写を順次繰り返してカラー画像を形成する装置や、各色毎の現像器を備えた複数の像担持体を中間転写体上に直列に配置したタンデム型カラー画像形成装置と呼ばれるものが挙げられる。 The intermediate transfer type image forming apparatus that can be used in the present invention is not particularly limited. For example, a monochrome image forming apparatus that forms an image using only a single color toner or an image carrier such as a photosensitive drum. An apparatus for forming a color image by sequentially repeating the primary transfer of the toner image carried on the intermediate transfer member, and a plurality of image carriers having developing units for respective colors are arranged in series on the intermediate transfer member. A so-called tandem type color image forming apparatus is exemplified.
図２は、本発明の画像形成装置の実施の形態としてのカラー画像形成装置を示す断面構成図である。 FIG. 2 is a cross-sectional configuration diagram showing a color image forming apparatus as an embodiment of the image forming apparatus of the present invention.
このカラー画像形成装置は、タンデム型カラー画像形成装置と称せられるもので、複数組の画像形成部１０Ｙ、１０Ｍ、１０Ｃ、１０Ｋと、転写部としての無端ベルト状中間転写体ユニット７と、転写材Ｐを搬送する無端ベルト状の給紙搬送手段２１及び定着手段としてのベルト式定着装置２４とを有する。画像形成装置の本体Ａの上部には、原稿画像読み取り装置ＳＣが配置されている。
This color image forming apparatus is called a tandem color image forming apparatus, and includes a plurality of sets of
各感光体に形成される異なる色のトナー像の１つとして、イエロー色の画像を形成する画像形成部１０Ｙは、第１の像担持体としてのドラム状の感光体１Ｙ、該感光体１Ｙの周囲に配置された帯電手段２Ｙ、露光手段３Ｙ、現像手段４Ｙ、１次転写手段としての１次転写ローラ５Ｙ、クリーニング手段６Ｙを有する。また、別の異なる色のトナー像の１つとして、マゼンタ色の画像を形成する画像形成部１０Ｍは、第１の像担持体としてのドラム状の感光体１Ｍ、該感光体１Ｍの周囲に配置された帯電手段２Ｍ、露光手段３Ｍ、現像手段４Ｍ、１次転写手段としての１次転写ローラ５Ｍ、クリーニング手段６Ｍを有する。また、更に別の異なる色のトナー像の１つとして、シアン色の画像を形成する画像形成部１０Ｃは、第１の像担持体としてのドラム状の感光体１Ｃ、該感光体１Ｃの周囲に配置された帯電手段２Ｃ、露光手段３Ｃ、現像手段４Ｃ、１次転写手段としての１次転写ローラ５Ｃ、クリーニング手段６Ｃを有する。また、更に他の異なる色のトナー像の１つとして、黒色画像を形成する画像形成部１０Ｋは、第１の像担持体としてのドラム状の感光体１Ｋ、該感光体１Ｋの周囲に配置された帯電手段２Ｋ、露光手段３Ｋ、現像手段４Ｋ、１次転写手段としての１次転写ローラ５Ｋ、クリーニング手段６Ｋを有する。
As one of the different color toner images formed on each photoconductor, an
無端ベルト状中間転写ベルトユニット７は、複数のローラにより巻回され、回動可能に支持された半導電性エンドレスベルト状の第２の像担持体としての無端ベルト状中間転写体７０を有する。
The endless belt-shaped intermediate
画像形成部１０Ｙ、１０Ｍ、１０Ｃ、１０Ｋより形成された各色の画像は、１次転写ローラ５Ｙ、５Ｍ、５Ｃ、５Ｋにより、回動する無端ベルト状中間転写ベルト７０上に逐次転写されて、合成されたカラー画像が形成される。給紙カセット２０内に収容された記録媒体として用紙等の記録部材Ｐは、給紙搬送手段２１により給紙され、複数の中間ローラ２２Ａ、２２Ｂ、２２Ｃ、２２Ｄ、レジストローラ２３を経て、２次転写手段としての２次転写ローラ５Ａに搬送され、記録部材Ｐ上にカラー画像が一括転写される。カラー画像が転写された記録部材Ｐは、ベルト式定着装置２４により定着処理され、排紙ローラ２５に挟持されて機外の排紙トレイ２６上に載置される。
The respective color images formed by the
一方、２次転写ローラ５Ａにより記録部材Ｐにカラー画像を転写した後、記録部材Ｐを曲率分離した無端ベルト状中間転写ベルト７０は、クリーニング手段６Ａにより残留トナーが除去される。
On the other hand, after the color image is transferred to the recording member P by the
画像形成処理中、１次転写ローラ５Ｋは常時、感光体１Ｋに圧接している。他の１次転写ローラ５Ｙ、５Ｍ、５Ｃはカラー画像形成時にのみ、それぞれ対応する感光体１Ｙ、１Ｍ、１Ｃに圧接する。
During the image forming process, the primary transfer roller 5K is always in pressure contact with the
２次転写ローラ５Ａは、ここを記録部材Ｐが通過して２次転写が行われる時にのみ、無端ベルト状中間転写ベルト７０に圧接する。
The
また、装置本体Ａから筐体８を支持レール８２Ｌ、８２Ｒを介して引き出し可能にしてある。
Further, the
筐体８は、画像形成部１０Ｙ、１０Ｍ、１０Ｃ、１０Ｋと、無端ベルト状中間転写ベルトユニット７とを有する。
The
画像形成部１０Ｙ、１０Ｍ、１０Ｃ、１０Ｋは、垂直方向に縦列配置されている。感光体１Ｙ、１Ｍ、１Ｃ、１Ｋの図示左側方には無端ベルト状中間転写ベルトユニット７が配置されている。無端ベルト状中間転写ベルトユニット７は、ローラ７１、７２、７３、７４、７６を巻回して回動可能な無端ベルト状中間転写ベルト７０、１次転写ローラ５Ｙ、５Ｍ、５Ｃ、５Ｋ及びクリーニング手段６Ａとからなる。
The
筐体８の引き出し操作により、画像形成部１０Ｙ、１０Ｍ、１０Ｃ、１０Ｋと、無端ベルト状中間転写ベルトユニット７とは、一体となって、本体Ａから引き出される。
The
このように感光体１Ｙ、１Ｍ、１Ｃ、１Ｋ上に帯電、露光、現像によりトナー像を形成し、無端ベルト状中間転写ベルト７０上で各色のトナー像を重ね合わせ、一括して記録部材Ｐに転写し、ベルト式定着装置２４で加圧及び加熱により固定して定着する。トナー像を記録部材Ｐに転移させた後の感光体１Ｙ、１Ｍ、１Ｃ、１Ｋは、クリーニング装置６Ａで転写時に感光体に残されたトナーを清掃した後、上記の帯電、露光、現像のサイクルに入り、次の像形成が行われる。
In this way, toner images are formed on the
本発明に使用される記録部材Ｐは、トナー画像を保持する支持体で、通常画像支持体、転写材あるいは転写紙と呼ばれるものである。具体的には、薄紙から厚紙までの普通紙、アート紙やコート紙等の塗工された印刷用紙、市販されている和紙やはがき用紙、ＯＨＰ用のプラスチックフィルム、布等の各種記録部材が挙げられる。 The recording member P used in the present invention is a support for holding a toner image, and is usually called an image support, a transfer material, or transfer paper. Specific examples include various recording members such as plain paper from thin paper to thick paper, coated printing paper such as art paper and coated paper, commercially available Japanese paper and postcard paper, plastic film for OHP, and cloth. It is done.
以下、本発明の実施例を説明するが、本発明は本実施例に限定されるものではない。
１．中間転写ベルトの作製
（１）基材層の作製
３，３’，４，４’−ビフェニルテトラカルボン酸二無水物（ＢＰＤＡ）とｐ−フェニレンジアミン（ＰＤＡ）とからなるポリアミド酸のＮ−メチル−２−ピロリドン（ＮＭＰ）溶液（宇部興産製ユーワニスＳ（固形分１８質量％））に、乾燥した酸化処理カーボンブラック（ＳＰＥＣＩＡＬ ＢＬＡＣＫ４（Ｄｅｇｕｓｓａ社製、ｐＨ３．０、揮発分：１４．０％））をポリイミド系樹脂固形分１００質量部に対して、２３質量部になるよう添加して、衝突型分散機（シーナス製ＧｅａｎｕｓＰＹ）を用い、圧力２００ＭＰａで、最小面積が１．４ｍｍ2で２分割後衝突させ、再度２分割する経路を５回通過させて、混合して、基材層用のカーボンブラック入りポリアミド酸溶液を得た。
Examples of the present invention will be described below, but the present invention is not limited to these examples.
1. Preparation of intermediate transfer belt (1) Preparation of substrate layer N-methyl polyamic acid composed of 3,3 ′, 4,4′-biphenyltetracarboxylic dianhydride (BPDA) and p-phenylenediamine (PDA) -2-pyrrolidone (NMP) solution (Ube Industries' Euvanis S (solid content: 18% by mass)) and dried oxidized carbon black (SPECIAL BLACK4 (Degussa, pH 3.0, volatile content: 14.0%) ) With respect to 100 parts by mass of the polyimide resin solids, and is divided into two parts at a pressure of 200 MPa and a minimum area of 1.4 mm 2 using a collision type disperser (GeanusPY manufactured by Seanas). It was made to collide afterward, and the path | route which divides | segments into 2 again was passed 5 times, it mixed, and the polyamic-acid solution containing the carbon black for base material layers was obtained.
基材層用のカーボンブラック入りポリアミド酸溶液を円筒状金型内面に、ディスペンサーを介して０．５ｍｍに塗布し、１５００ｒｐｍで１５分間回転させて均一な厚みを有する展開層とした後、２５０ｒｐｍで回転させながら、金型の外側より６０℃の熱風を３０分間あてた後、１５０℃で６０分間加熱した。その後、３６０℃まで２℃／分の昇温速度で昇温し、さらに３６０℃で３０分加熱して溶媒の除去、脱水閉環水の除去、及びイミド転化反応の完結を行った。その後室温に戻し、金型から剥離し、目的とする無端ベルト状の基材層を得た。この基材層の総厚みは０．１ｍｍであった。
（２）中間層の形成
塩化ビニル８０％、酢酸ビニル１５％、マレイン酸５％の組成比よりなる共重合体樹脂１００質量部をシクロヘキサノン４００質量部に溶解させた。この溶液に酸化処理カーボンブラック（ＳＰＥＣＩＡＬ ＢＬＡＣＫ４（Ｄｅｇｕｓｓａ社製、ｐＨ３．０、揮発分：１４．０％））を前述の共重合体樹脂１００質量部に対して１０質量部になるよう添加した。添加後、衝突型分散機（シーナス製ＧｅａｎｕｓＰＹ）で、圧力２００ＭＰａ、最小面積が１．４ｍｍ2で２分割後衝突させ、再度２分割する経路を５回通過させて、混合して、基材層用のカーボンブラック入り共重合体樹脂溶液を得た。
After applying the polyamic acid solution containing carbon black for the base material layer to the inner surface of the cylindrical mold to 0.5 mm via a dispenser and rotating it at 1500 rpm for 15 minutes to form a development layer having a uniform thickness, at 250 rpm While rotating, hot air at 60 ° C. was applied for 30 minutes from the outside of the mold, and then heated at 150 ° C. for 60 minutes. Thereafter, the temperature was raised to 360 ° C. at a rate of 2 ° C./min, and further heated at 360 ° C. for 30 minutes to remove the solvent, remove dehydrated ring-closing water, and complete the imide conversion reaction. Thereafter, the temperature was returned to room temperature, and it was peeled off from the mold to obtain a target endless belt-like base material layer. The total thickness of this base material layer was 0.1 mm.
(2) Formation of intermediate layer 100 parts by mass of a copolymer resin having a composition ratio of 80% vinyl chloride, 15% vinyl acetate, and 5% maleic acid was dissolved in 400 parts by mass of cyclohexanone. To this solution, oxidation-treated carbon black (SPECIAL BLACK4 (manufactured by Degussa, pH 3.0, volatile content: 14.0%)) was added so as to be 10 parts by mass with respect to 100 parts by mass of the copolymer resin. After the addition, with a collision type disperser (GeanusPY made by Seanas), the pressure is 200 MPa, the minimum area is 1.4 mm 2 , the two parts are made to collide, and the path is further divided into five parts, mixed, and mixed. A carbon black-containing copolymer resin solution was obtained.
この溶液を前述の基材層上に厚さ１０μｍとなるようにスプレー塗布を行って中間層を形成した。
（３）表面層の形成
一般式（１）に示される化合物と導電性物質とを表１に示すように組み合わせ、両者を混練、撹拌した後、ｎ−ヘキサン１００質量部を添加して調製液を作製した。次に、シリコーン樹脂Ｘ−４０−２２６９（信越化学社製）１００質量部をｎ−ヘキサン４００質量部に溶解させ、得られた液に前述の調製液を添加し、ボールミルで混練、撹拌を行って１０ｃｐｓの表面層形成用コーティング液１〜１５を作製した。なお、使用した導電性物質のうち、カーボンブラックはＳＰＥＣＩＡＬ ＢＬＡＣＫ４（Ｄｅｇｕｓｓａ社製、ｐＨ３．０、揮発分：１４．０％）を、ポリオキシエチレンノニルフェニルエーテルはノニオンＨＳ−２４０（日本油脂化学社製）を使用した。
This solution was spray-coated on the base material layer so as to have a thickness of 10 μm to form an intermediate layer.
(3) Formation of surface layer A compound represented by the general formula (1) and a conductive material are combined as shown in Table 1, and after kneading and stirring both, 100 parts by mass of n-hexane is added to prepare a solution. Was made. Next, 100 parts by mass of silicone resin X-40-2269 (manufactured by Shin-Etsu Chemical Co., Ltd.) is dissolved in 400 parts by mass of n-hexane, and the prepared liquid is added to the obtained liquid, followed by kneading and stirring with a ball mill. 10 cps of surface layer forming coating solutions 1 to 15 were prepared. Of the conductive materials used, carbon black is SPECIAL BLACK4 (Degussa, pH 3.0, volatile content: 14.0%), polyoxyethylene nonylphenyl ether is Nonion HS-240 (Nippon Yushi Chemical Co., Ltd.) Made).
作製した各コーティング液を前述の中間層を形成した試料ベルト上に厚さ１０μｍとなるようにスプレー塗布を行った。その後、オーブンで１７０℃に加熱した後１時間乾燥させて、各中間転写ベルト１〜１５を作製した。作製した中間転写ベルトの表面硬度、表面抵抗値、体積抵抗値の測定結果を表１に示す。なお、測定は前述した条件、及び、測定装置を用いて行った。 Each of the prepared coating solutions was spray-coated on the sample belt on which the intermediate layer was formed so as to have a thickness of 10 μm. Then, after heating to 170 degreeC in oven, it was made to dry for 1 hour, and each intermediate transfer belt 1-15 was produced. Table 1 shows the measurement results of the surface hardness, surface resistance value, and volume resistance value of the produced intermediate transfer belt. In addition, the measurement was performed using the conditions described above and a measuring apparatus.
２．評価実験
作製した「中間転写ベルト１〜１５」を図２の画像形成装置に搭載して、それぞれ連続１万枚のプリントを行った。なお、画像形成には体積基準によるメディアン径（Ｄ５０）が６．０μｍのトナーを含有する２成分現像剤を使用した。
2. Evaluation Experiment The produced “intermediate transfer belts 1 to 15” were mounted on the image forming apparatus shown in FIG. For image formation, a two-component developer containing toner having a volume-based median diameter (D50) of 6.0 μm was used.
画像形成は低温低湿（１０℃、２０％ＲＨ）と高温高湿（３３℃、８０％ＲＨ）でそれぞれ行い、記録用紙はＡ４判の上質紙（６４ｇ／ｍ2）を用いた。画像形成に使用した原稿は、画素率が７％の文字画像（３ポイント、５ポイント）、カラー人物顔画像（ハーフトーンを含むドット画像）、べた白画像、べた画像がそれぞれ１／４等分に掲載されたオリジナル画像（Ａ４判）を用いた。 Image formation was performed at low temperature and low humidity (10 ° C., 20% RH) and high temperature and high humidity (33 ° C., 80% RH), respectively, and the recording paper was A4 size high quality paper (64 g / m 2 ). The original used for image formation is a character image (3 points, 5 points) with a pixel rate of 7%, a color human face image (dot image including halftone), a solid white image, and a solid image divided into quarters. The original image (A4 size) published in is used.
連続プリント実施中の１０００枚、５０００枚、１００００枚の時に下記評価用のサンプルを５枚ずつ作成した。 Five samples for evaluation were prepared for 1000 sheets, 5000 sheets, and 10,000 sheets during continuous printing.
評価は、２次転写で発生する画像欠陥（べた画像部の白抜け、文字画像部の中抜け、文字部のトナー散り、転写率）で行った。なお、評価において、◎、○は合格、×は不合格とした。 The evaluation was performed based on image defects (white areas in the solid image area, voids in the text image area, toner scattering in the text area, and transfer rate) generated in the secondary transfer. In the evaluation, ◎ and ○ are acceptable and × is unacceptable.
〈べた画像部の白抜け〉
白抜けの評価は、高温高湿でプリントしたべた画像部で、長径が０．４ｍｍ以上の白抜けがＡ４用紙上に何個あるかで判定した。なお、白抜け長径はビデオプリンタ付き顕微鏡で測定した。
<White area in solid image area>
The evaluation of white spots was determined by the number of white spots having a major axis of 0.4 mm or more on A4 paper in a solid image portion printed at high temperature and high humidity. In addition, the hollow long diameter was measured with a microscope with a video printer.
◎：０．４ｍｍ以上の白抜け頻度：全てのプリント画像で３個以下となり良好
○：０．４ｍｍ以上の白抜け頻度：４個以上、１９個以下が１枚以上発生
×：０．４ｍｍ以上の白抜け頻度：２０個以上が１枚以上発生し、実用上問題あり。
◎: White spot frequency of 0.4 mm or more: Good with 3 or less in all printed images ○: White spot frequency of 0.4 mm or more: 1 or more sheets of 4 or more, 19 or less ×: 0.4 mm or more White spot frequency: One or more of 20 or more occurs, which is a practical problem.
〈文字画像の中抜け〉
高温高湿でプリントした文字画像をルーペで拡大観察して、文字画像上の中抜け発生を評価した。
<Cut out of text image>
The character image printed at high temperature and high humidity was magnified and observed with a magnifying glass to evaluate the occurrence of voids on the character image.
◎：１００００枚目まで中抜けの発生なし
○：５０００枚目のプリントまで中抜けの発生なし
×：１０００枚目のプリントで中抜けの発生あり
〈文字部のトナー散り〉
低温低湿でプリントした文字画像をルーペで拡大観察し、文字部周辺のトナー散りの状態を目視で評価した。
A: No void occurred up to the 10,000th sheet. ○: No void occurred until the 5000th print. X: A void occurred in the 1000th print.
A character image printed at low temperature and low humidity was magnified and observed with a magnifying glass, and the state of toner scattering around the character portion was visually evaluated.
◎：１００００枚目のプリントまで見られないか、または、ルーペでやっと見られる程度
○：５０００枚目のプリントまで見られないか、または、ルーペでやっと見られる程度
×：１０００枚目未満でルーペなしでトナー散りが確認され、実用上問題あり。
◎: not seen up to 10000th print or finally seen with loupe ○: not seen up to 5000th print or finally seen with loupe ×: less than 1000th loupe No toner scattering was confirmed without any problem.
〈転写率〉
低温低湿での１万枚目のプリント終了後、画素濃度が１．３０のソリッド画像（２０ｍｍ×５０ｍｍ）を形成し、下記式により転写率を求めて評価した。
<Transfer rate>
After the completion of printing on the 10,000th sheet at low temperature and low humidity, a solid image (20 mm × 50 mm) with a pixel density of 1.30 was formed, and the transfer rate was determined by the following formula and evaluated.
転写率（％）＝（記録部材上に転写されたトナーの質量／中間転写ベルト上に供給されるトナーの質量）×１００
◎：転写率が９０％以上で良好
○：転写率が８０％以上で実用上問題なし
×：転写率が８０％未満で実用上問題あり。
Transfer rate (%) = (mass of toner transferred onto recording member / mass of toner supplied onto intermediate transfer belt) × 100
A: Good when the transfer rate is 90% or more B: No problem for practical use when the transfer rate is 80% or more X: There is a practical problem when the transfer rate is less than 80%.
結果を表２に示す。 The results are shown in Table 2.
表２の結果から明らかなように、本発明に係る中間転写ベルトを用いた場合は、連続で５０００枚以上のプリント作成を行ってもべた画像部の白抜けや文字画像の中抜け、文字部のトナー散りといった画像欠陥の発生が見られず、転写率も良好であった。一方、比較例では１０００枚あたりから画像欠陥の発生が見られ、本発明に係る中間転写ベルトとは明らかに異なる結果となった。 As is apparent from the results in Table 2, when the intermediate transfer belt according to the present invention is used, white areas in the image portion, character images in the middle portion, character portions in the image portion even when the prints of 5000 sheets or more are continuously formed are displayed. No image defects such as toner scattering were observed, and the transfer rate was good. On the other hand, in the comparative example, the occurrence of image defects was observed from around 1000 sheets, and the result was clearly different from the intermediate transfer belt according to the present invention.
このように、本実施例により本発明に係る中間転写ベルトが大量のプリントを行ったときに良好な２次転写性能を持続することが確認された。 As described above, it was confirmed that the intermediate transfer belt according to the present invention maintained good secondary transfer performance when a large amount of printing was performed.
１ 感光体ドラム
２ 中間転写ベルト
２１ 表面層
２２ 導電性微粒子
２３ 基材層
２４、２５ 中間層
DESCRIPTION OF SYMBOLS 1
Claims (3)
該表面層に導電性物質と、下記一般式（１）で表される化合物を用いて形成されるものとを含有し、
表面硬度が８５〜１３０Ｎ／ｍｍ2であることを特徴とする中間転写ベルト。
一般式（１） Ｍ（Ｏ−ＣnＨ2n+1）m
（式中、Ｍはケイ素、アルミニウム、ジルコニウムまたはチタンを表す。ｍはＭの価数となる。） An intermediate transfer belt having at least a surface layer on a substrate,
The surface layer contains a conductive substance and one formed using a compound represented by the following general formula (1),
An intermediate transfer belt having a surface hardness of 85 to 130 N / mm 2 .
Formula (1) M (O-C n H 2n + 1) m
(In the formula, M represents silicon, aluminum, zirconium or titanium. M represents the valence of M.)
一般式（２） Ｓｉ（Ｏ−ＣnＨ2n+1）4 The intermediate transfer belt according to claim 1, wherein the compound represented by the general formula (1) is represented by the following general formula (2).
General formula (2) Si (O—C n H 2n + 1 ) 4