JP2006282237A - Wrapping material and flexible container - Google Patents

Wrapping material and flexible container Download PDF

Info

Publication number
JP2006282237A
JP2006282237A JP2005105266A JP2005105266A JP2006282237A JP 2006282237 A JP2006282237 A JP 2006282237A JP 2005105266 A JP2005105266 A JP 2005105266A JP 2005105266 A JP2005105266 A JP 2005105266A JP 2006282237 A JP2006282237 A JP 2006282237A
Authority
JP
Japan
Prior art keywords
layer
flexible container
heat
gas barrier
packaging material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2005105266A
Other languages
Japanese (ja)
Inventor
Mitsuru Nozue
満 野末
Akikazu Yamamoto
明和 山本
Yoshimasa Nakano
吉雅 中野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kurita Water Industries Ltd
Original Assignee
Kurita Water Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kurita Water Industries Ltd filed Critical Kurita Water Industries Ltd
Priority to JP2005105266A priority Critical patent/JP2006282237A/en
Publication of JP2006282237A publication Critical patent/JP2006282237A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a wrapping material showing no transfer of smell into itself but having a superior tearing characteristic and provide a flexible container using this wrapping material. <P>SOLUTION: There is provided a wrapping material showing a tearing characteristic (a flexible raw material 1). This material includes a laminated member comprising a heat fusion layer 2 showing a heat fusion characteristic, a gas shielding layer 3 having a gas shielding characteristic and a protection layer 4 having a mechanical strength, wherein the heat fusion layer 2 is exposed at the surface of the laminated member. As this gas shielding layer 3, an alumina oxide coating polyethylene terephthalate (CPET) film is used. In addition, as the heat fusion layer 2, a polyethylene (PE) film or the like can be used and as the protection layer 4, a nylon (NY) film or the like can be used. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、飲料水、純水等の液体の商品化、運搬又は保管等に用いられ引き裂いて開封可能な柔軟性素材を用いた包装材料、及びこれを用いた柔軟性容器に関する。   The present invention relates to a packaging material using a flexible material that can be teared and opened and used for commercialization, transportation or storage of liquids such as drinking water and pure water, and a flexible container using the packaging material.

一般に、ミネラル水等の飲料水、その他の液体の商品化、その運搬及び保管等には、ペットボトルと称される合成樹脂容器が多用されている。この合成樹脂容器としては、例えば、特開平８−１９８２３１号公報に記載の非常用飲料水容器が挙げられる（特許文献１参照）。この種の合成樹脂容器は、軽量で安全性が高いが、剛性が高く、内容物の多寡に関係なく一定形状を呈しているために嵩張り、扱い難いという指摘がある。このような容器に対し、合成樹脂フィルムで袋状に形成された柔軟性容器が普及している。この柔軟性容器は、その内容物の流動性によって外観形状が変化し、箱等への収容性効率が高く、使用済の柔軟性容器のみであれば、その体積が小さく、しかも、任意に折り曲げたり、重ねたりできるため、ペットボトルのように嵩張らず、その取扱いが容易である。   Generally, synthetic resin containers called PET bottles are frequently used for the commercialization, transport and storage of drinking water such as mineral water and other liquids. Examples of the synthetic resin container include an emergency drinking water container described in JP-A-8-198231 (see Patent Document 1). Although this type of synthetic resin container is lightweight and highly safe, it is pointed out that it is bulky and difficult to handle because it has high rigidity and has a fixed shape regardless of the content. In contrast to such containers, flexible containers formed in a bag shape with a synthetic resin film are in widespread use. This flexible container changes its appearance shape depending on the fluidity of its contents, has high efficiency in storing in a box, etc., and if it is only a used flexible container, its volume is small and it can be bent arbitrarily. Since they can be stacked or stacked, they are not bulky like PET bottles and are easy to handle.

従来、積層フィルムを包装材料に用いた例として、例えば、特開平１０−１３９０７４号公報に記載の長期保存飲料水用包装袋およびその製造方法（特許文献２参照）、特開２０００−１４３７４号公報に記載の液状加工食品（特許文献３参照）等がある。特開平１０−１３９０７４号公報に係る長期保存飲料水用包装袋は、ポリエチレンフィルムとナイロンフィルムとの積層体からなる基材の表面に抗菌層を形成したものである。また、特開２０００−１４３７４号公報に係る液状加工食品は、複数層の樹脂フィルムの積層体による包装例であるが、これは、液状食品中及びヘッドスペース中の酸素ガスを急速に吸収することによって香気成分の変質・消失がなく、耐久性に優れた長期保存可能な液状加工食品を提供するものである。   Conventionally, as an example of using a laminated film as a packaging material, for example, a packaging bag for long-term storage of drinking water described in JP-A-10-139974 and a method for producing the same (see Patent Document 2), JP-A 2000-14374 Liquid processed foods described in (see Patent Document 3) and the like. The packaging bag for long-term storage drinking water according to JP-A-10-139074 is obtained by forming an antibacterial layer on the surface of a base material composed of a laminate of a polyethylene film and a nylon film. Moreover, although the liquid processed food based on Unexamined-Japanese-Patent No. 2000-14374 is a packaging example by the laminated body of the resin film of several layers, this absorbs oxygen gas in liquid food and a head space rapidly. Therefore, it is possible to provide a liquid processed food that is excellent in durability and can be stored for a long period of time without deterioration or disappearance of aroma components.

ところで、液体等の商品化、その搬送、保管等に用いられる柔軟性容器には、解決すべき課題として次のような指摘がある。
第１に、柔軟性容器を用いて液体等の内容物を商品化し、その商品を搬送し及び保管するには、素材に臭気がないことが不可欠である。特に、液体等の無味無臭であることが品質を決定する商品、臭気付着で品質が劣化する商品では柔軟性容器の素材自体の無臭化が要請される。また、柔軟性容器は、その搬送容器にダンボール箱等を用いて複数個を搬送することができるが、搬送途上や保管上、そのダンボール箱等と柔軟性容器とを接触させると、ダンボール箱等が持つ臭気が柔軟性容器内部に侵入し、液体等の内容物に付着するというおそれがあった。液体等のように無味無臭が不可欠である内容物は、付着した臭いが味覚として錯覚されてしまう等、その商品価値が損なわれるおそれがある。 By the way, the following points are pointed out as problems to be solved for flexible containers used for commercialization of liquids, transportation, storage and the like.
First, in order to commercialize contents such as liquid using a flexible container, and to transport and store the product, it is essential that the material has no odor. In particular, products that determine the quality of being tasteless and odorless, such as liquids, and products that deteriorate in quality due to odor adherence, require that the material of the flexible container itself be free of bromide. In addition, a plurality of flexible containers can be transported using a cardboard box or the like to the transport container. However, if the cardboard box or the like is brought into contact with the flexible container during transport or storage, the cardboard box or the like There is a risk that the odor of the liquid enters the inside of the flexible container and adheres to contents such as liquid. There is a risk that the value of a product such as a liquid that is indispensable for tasteless odor will be damaged in its commercial value, for example, the attached odor is illusioned as a taste.

第２に、柔軟性容器によって商品化された液体は、トラック輸送によって配送されるが、ダンボール箱等を搬送容器として用いても、搬送途上や配達途上で振動や落下等の衝撃や加圧を受けて柔軟性容器が損傷すると、液漏れ等、内容物の漏洩を生じるおそれがある。   Secondly, liquids commercialized by flexible containers are delivered by truck transport, but even if cardboard boxes or the like are used as transport containers, shocks and pressures such as vibrations and drops are applied during transport and delivery. If the flexible container is damaged, the contents may leak, such as liquid leakage.

第３に、柔軟性容器の損傷による内容物の流出を阻止するには、柔軟性容器の強度を高めることが必要であるが、その強化が引裂性を阻害すると、柔軟性容器の利点である開封性を損なうおそれがある。   Third, in order to prevent the contents from flowing out due to damage to the flexible container, it is necessary to increase the strength of the flexible container. However, if the strengthening hinders tearability, it is an advantage of the flexible container. There is a risk of unsealing.

また、第４に、柔軟性容器は、廃棄処分が容易であるが、環境ホルモンや塩素が含まれる材質で形成されていると、廃棄時に環境ホルモンの流出、焼却時にダイオキシンの発生等、環境悪化の原因になる。   Fourth, flexible containers are easy to dispose of, but if they are made of a material that contains environmental hormones or chlorine, environmental hormones such as outflow of environmental hormones during disposal and generation of dioxins during incineration, etc. Cause.

そこで、本発明者らは、ナイロン（ＮＹ）、エチレンビニルアルコール樹脂（ＥＶＯＨ）、ポリエチレン（ＰＥ）の三層構造を有する包装材料、及びこれを用いた柔軟性容器を先に開発した。
特開平８−１９８２３１号公報 特開平１０−１３９０７４号公報 特開２０００−１４３７４号公報 Therefore, the present inventors have previously developed a packaging material having a three-layer structure of nylon (NY), ethylene vinyl alcohol resin (EVOH), and polyethylene (PE), and a flexible container using the packaging material.
JP-A-8-198231 Japanese Patent Laid-Open No. 10-139074 JP 2000-14374 A

しかしながら、この三層構造を有する包装材料からなる柔軟性容器は、中間層にガス遮断性を持つエチレンビニルアルコール樹脂（ＥＶＯＨ）層を配置しているにもかかわらず、内容物に臭いが移ってしまうことがあった。そこで、本発明者らが種々検討した結果、柔軟性容器の表面側のナイロン層が濡れると、ＥＶＯＨ層に水分が浸透し、このＥＶＯＨ層が濡れるとガス遮断性が低下して内容物に臭いが移ってしまうことがわかった。また内容物に臭いが移ってしまうほか、ナイロンが加水分解されてカプロラクタムが発生し、このカプロラクタムがＥＶＯＨ層を透過して内容物に溶解し、内容物の風味を悪くすることが分かった。さらに、ＥＶＯＨはポリエチレンとの相性が悪く引裂性が必ずしも良くないという問題点もあった。   However, the flexible container made of the packaging material having this three-layer structure has an odor transferred to the contents despite the fact that an ethylene vinyl alcohol resin (EVOH) layer having gas barrier properties is arranged in the intermediate layer. There was a case. Therefore, as a result of various studies by the present inventors, when the nylon layer on the surface side of the flexible container gets wet, moisture penetrates into the EVOH layer, and when this EVOH layer gets wet, the gas barrier property is lowered and the contents are smelled. Knew that would move. In addition to the smell moving to the contents, it was found that nylon was hydrolyzed to generate caprolactam, and this caprolactam permeated the EVOH layer and dissolved in the contents, thereby deteriorating the flavor of the contents. Furthermore, EVOH has a problem that compatibility with polyethylene is poor and tearability is not always good.

本発明は上記課題に鑑みてなされたものであり、内容物への臭い移りがなく、引裂性の良好な包装材料及びこれを用いた柔軟性容器を提供することを目的とする。   The present invention has been made in view of the above problems, and an object of the present invention is to provide a packaging material having good tearability and no odor transfer to the contents, and a flexible container using the same.

本発明は、加熱融着性を持つ加熱融着層と、ガス遮断性を持つガス遮断層と、機械的強度を持つ保護層とからなる積層体を含み、前記積層体の表面に前記加熱融着層を露出してなる、引裂性を備える包装材料であって、前記ガス遮断層が、ポリエチレンテレフタレートに酸化アルミナをコーティングした酸化アルミナコーティングポリエチレンテレフタレートからなることを特徴とする包装材料を提供する（請求項１）。酸化アルミナコーティングポリエチレンテレフタレートは、保護層が濡れて水分に侵されたとしてもガス遮断性を維持するので、ガス遮断層として酸化アルミナコーティングポリエチレンテレフタレートを用いることで、加熱融着層にまで臭気ガスが到達することがない。また、引裂性にも優れている。   The present invention includes a laminate comprising a heat-fusible layer having heat-fusibility, a gas barrier layer having gas barrier properties, and a protective layer having mechanical strength, and the heat-fused layer is provided on the surface of the laminate. Provided is a packaging material having a tearing property, wherein the gas barrier layer is made of an oxide-coated polyethylene terephthalate obtained by coating polyethylene terephthalate with alumina oxide. Claim 1). Alumina oxide-coated polyethylene terephthalate maintains gas barrier properties even when the protective layer gets wet and is invaded by moisture, so by using alumina oxide-coated polyethylene terephthalate as the gas barrier layer, odorous gas can reach the heat fusion layer. Never reach. It is also excellent in tearability.

特に前記加熱融着層は、ポリエチレン又はその他の加熱融着性を持つ樹脂であることが好ましく（請求項２）、また、前記保護層は、ナイロン、ポリエチレンテレフタレート及び二軸延伸ポリプロピレンからなる群より選ばれる１種以上であることが好ましい（請求項３）。保護層であるナイロン面が濡れてナイロンがカプロラクタムに加水分解されたとしても、酸化アルミナコーティングポリエチレンテレフタレートがカプロラクタムの透過を遮断するので、本発明の包装材料を用いて飲料等を包装しても飲料等の風味が悪くなることはなく、飲料等からカプロラクタムが検出されることもない。   In particular, the heat-sealing layer is preferably polyethylene or other heat-fusible resin (Claim 2), and the protective layer is made of nylon, polyethylene terephthalate and biaxially oriented polypropylene. It is preferable that it is 1 or more types selected (Claim 3). Even if the nylon surface, which is the protective layer, gets wet and the nylon is hydrolyzed to caprolactam, the alumina oxide-coated polyethylene terephthalate blocks the permeation of caprolactam. The caprolactam is not detected from beverages or the like.

また、本発明の柔軟性容器は、請求項１から３のいずれか１項に記載の包装材料を用い、前記加熱融着層を内面側としたことを特徴とする（請求項４）。酸化アルミナコーティングポリエチレンテレフタレートは、保護層が濡れて水分に侵されたとしてもガス遮断性を維持するので、内容物に臭いが移ることはなく、また、引裂性にも優れているため柔軟性容器を容易に開封することができる。   Moreover, the flexible container of this invention uses the packaging material of any one of Claim 1 to 3, and made the said heat-fusion layer into the inner surface side (Claim 4). Alumina oxide-coated polyethylene terephthalate maintains gas barrier properties even when the protective layer gets wet and is invaded by moisture, so the smell does not transfer to the contents, and it is also excellent in tearability. Can be opened easily.

この包装材料は、前記保護層の内面側表面若しくは前記ガス遮断層又は双方を印刷等の表示面に設定してもよい（請求項５）。   In this packaging material, the inner surface of the protective layer or the gas barrier layer or both may be set on a display surface such as printing.

本発明の包装材料は、ガス遮断層を酸化アルミナコーティングポリエチレンテレフタレートとしているので、エチレンビニルアルコール樹脂などを用いた場合と比べて、内容物に移り香がなく、また、内容物からの臭気を抑制でき、臭気ガスによる内容物の劣化を防止できるとともに、引裂きによって容易に開封でき、機械的強度及び環境性に優れたものとなっている。   The packaging material of the present invention has a gas barrier layer made of alumina oxide-coated polyethylene terephthalate, so there is no scent in the contents compared to the case of using ethylene vinyl alcohol resin, and the odor from the contents can be suppressed. In addition to preventing deterioration of the contents due to odor gas, it can be easily opened by tearing, and has excellent mechanical strength and environmental properties.

そして、このような包装材料を用いた柔軟性容器は、水、その他の液体等を封入して商品化でき、その運搬及び保管を容易に行うことができる。しかも、内容物である水、その他の液体等に移り香がなく、また、内容物からの臭気を抑制でき、臭気による内容物の劣化を防止できるとともに、引裂きによって容易に開封でき、機械的強度及び環境性に優れた安価な柔軟性容器となっている。   And the flexible container using such a packaging material can enclose water, other liquids, etc., can be commercialized, and can carry and store it easily. Moreover, there is no fragrance in the water, other liquids, etc., and the odor from the contents can be suppressed, the deterioration of the contents due to the odor can be prevented, and it can be easily opened by tearing, and the mechanical strength and It is an inexpensive flexible container with excellent environmental properties.

本発明の包装材料は、水等の液体を収容する柔軟性容器等に用いられ、例えば、図１に示す柔軟性素材１が用いられる。
この柔軟性素材１は、複数層からなる積層フィルムであって、本実施形態においては、加熱融着性を持つ基材としての加熱融着層２と、表裏双方向からの臭気ガス等の透過を遮断可能なガス遮断性を持つガス遮断層３と、内容物の漏洩等を阻止できる適当な機械的強度を持つ保護層４とからなる積層体である。この柔軟性素材１を構成する積層体は、加熱融着層２とガス遮断層３との間及びガス遮断層３と保護層４との間に接着剤及び接着樹脂を介在させて、加熱・加圧等のドライラミネート処理で加熱融着層２とガス遮断層３と保護層４とを貼り合わせたものである。 The packaging material of this invention is used for the flexible container etc. which hold liquids, such as water, for example, the flexible material 1 shown in FIG. 1 is used.
This flexible material 1 is a laminated film composed of a plurality of layers. In this embodiment, the heat-fusible layer 2 as a base material having heat-fusibility and permeation of odor gas or the like from both the front and back sides. It is a laminate composed of a gas barrier layer 3 having a gas barrier property capable of blocking water and a protective layer 4 having an appropriate mechanical strength capable of preventing leakage of contents. The laminate constituting the flexible material 1 is formed by interposing an adhesive and an adhesive resin between the heat fusion layer 2 and the gas barrier layer 3 and between the gas barrier layer 3 and the protective layer 4. The heat-fused layer 2, the gas barrier layer 3, and the protective layer 4 are bonded together by a dry laminating process such as pressurization.

加熱融着層２としては、例えば、ポリエチレン（ＰＥ）又はその他の加熱融着性を持つ樹脂を用いることができる。その他の加熱融着性を持つ樹脂としては、例えば、ポリプロピレン（ＰＰ）、エチレンビニルアルコール（ＥＶＡ）、直鎖状低密度ポリエチレン（ＬＬＰＥ）等が挙げられる。また、保護層４としては、例えば、ナイロン（ＮＹ）、ポリエチレンテレフタレート（ＰＥＴ）、二軸延伸ポリプロピレン（ＯＰＰ）等を用いることができ、保護層４に印刷するのであれば、ナイロン又はポリエチレンテレフタレートを用いるのが好ましい。そして、本実施形態においては、ガス遮断層３として、ポリエチレンテレフタレートに酸化アルミナをコーティングした酸化アルミナコーティングポリエチレンテレフタレート（以下「ＣＰＥＴ」という場合がある。）を用いる。   As the heat fusion layer 2, for example, polyethylene (PE) or other resin having heat fusion property can be used. Examples of the other heat-fusible resin include polypropylene (PP), ethylene vinyl alcohol (EVA), and linear low density polyethylene (LLPE). Further, as the protective layer 4, for example, nylon (NY), polyethylene terephthalate (PET), biaxially oriented polypropylene (OPP), or the like can be used. If printing on the protective layer 4, nylon or polyethylene terephthalate is used. It is preferable to use it. In this embodiment, the gas barrier layer 3 is made of alumina oxide-coated polyethylene terephthalate (hereinafter sometimes referred to as “CPET”) obtained by coating polyethylene terephthalate with alumina oxide.

これらの樹脂を選択した柔軟性素材１として、例えば、「ＮＹ＃１５／ＣＰＥＴ＃１２／ＰＥ＃４０」等からなる積層体を構成できる。ここで、「ＮＹ＃１５／ＣＰＥＴ＃１２／ＰＥ＃４０」は、厚さ１５μｍのナイロン（ＮＹ）、厚さ１２μｍの酸化アルミナコーティングポリエチレンテレフタレート（ＣＰＥＴ）及び厚さ４０μｍのポリエチレン（ＰＥ）の積層体である。   For example, a laminate made of “NY # 15 / CPET # 12 / PE # 40” or the like can be configured as the flexible material 1 selected from these resins. Here, “NY # 15 / CPET # 12 / PE # 40” is a laminate of 15 μm thick nylon (NY), 12 μm thick alumina oxide coated polyethylene terephthalate (CPET) and 40 μm thick polyethylene (PE). Is the body.

このような柔軟性素材１は、図２に示すように、表面層に設置された保護層４及び加熱融着層２でガス遮断層３を挟み込んだサンドイッチ構造であって、保護層４の内面側が印刷面に設定されて内容物の表示５が施されている。このように、保護層４の内面側に表示５を施せば、保護層４によって表示５が防護されるとともに、保護層４に透明材料を使用すれば、その表示５の機能を損なうことはない。なお、本実施形態では、保護層４の内面側を印刷面に設定し、保護層４の内面側に「ミネラル水」と表示されているが、ガス遮断層３の保護層４側を印刷面に設定してもよい。   As shown in FIG. 2, the flexible material 1 has a sandwich structure in which the gas barrier layer 3 is sandwiched between the protective layer 4 and the heat fusion layer 2 installed on the surface layer, and the inner surface of the protective layer 4. The side is set as the printing surface and the content display 5 is provided. In this way, if the display 5 is provided on the inner surface side of the protective layer 4, the display 5 is protected by the protective layer 4, and if a transparent material is used for the protective layer 4, the function of the display 5 is not impaired. . In the present embodiment, the inner surface side of the protective layer 4 is set as a printing surface, and “mineral water” is displayed on the inner surface side of the protective layer 4, but the protective layer 4 side of the gas barrier layer 3 is printed on the printing surface. May be set.

このような柔軟性素材１は、三層構造によって加熱融着性、ガス遮断性及び耐磨耗性を有するとともに、引裂性及び無臭性を備えている。ここで、加熱融着性とは、加熱融着層４側を互いに接合させて加熱することで融着する性質をいう。また、ガス遮断性とは、臭気ガス等のガスの透過を遮断し得る性質をいい、ガス遮断性を持つ柔軟性素材１から形成された柔軟性容器であれば、その柔軟性容器の内容物に移り香を生じさせることはなく、また、内容物から発生する臭気を遮断することができる。さらに、引裂性とは、例えば、柔軟性容器に切り口を形成した場合、その切り口から容易に引き裂いて開封可能な性質をいい、無臭性とは、加熱融着層４又は柔軟性素材１から臭気が生じない性質をいう。   Such a flexible material 1 has a heat fusion property, a gas barrier property, and an abrasion resistance by a three-layer structure, and also has a tear property and an odorless property. Here, the heat-fusible property refers to a property of fusing by heating the heat-fusible layer 4 side to each other. Further, the gas barrier property means a property capable of blocking the permeation of gas such as odor gas. If the flexible container is formed from the flexible material 1 having the gas barrier property, the contents of the flexible container are included. No odor is produced and the odor generated from the contents can be blocked. Furthermore, tearability means a property that, when a cut is formed in a flexible container, for example, can be easily torn and opened from the cut, and odorless means odor from the heat-sealing layer 4 or the flexible material 1. The property that does not occur.

基材である加熱融着層２に純粋なポリエチレン（ＰＥ）のフィルムを使用すれば、このポリエチレン（ＰＥ）に内容物である水等が接触しても、その水等にプラスチック臭等が移ることはなく、内容物の無臭化を図ることができるとともに、臭気による内容物の劣化を防止できる。また、加熱融着層２側を密着させて保護層４側から加熱することで、加熱融着層２を容易に融着させることができ、水等を遮断できる程度の封止状態が得られる。   If a pure polyethylene (PE) film is used for the heat-fusible layer 2 that is a base material, even if water or the like that comes in contact with the polyethylene (PE), a plastic odor or the like is transferred to the water or the like. In addition, the content can be made non-brominated and the content can be prevented from deteriorating due to odor. Moreover, the heat-sealing layer 2 side is adhered and heated from the protective layer 4 side, whereby the heat-sealing layer 2 can be easily fused, and a sealed state that can block water or the like is obtained. .

しかも、ガス遮断層３に酸化アルミナコーティングポリエチレンテレフタレート（ＣＰＥＴ）を使用しているので、保護層４側から侵入した外部からの臭気ガスをガス遮断層３で遮断することができる。したがって、その臭気ガスが加熱融着層２に到達することはなく、内容物である水等が臭気ガスで汚染されることはない。ＣＰＥＴフィルムは、その表面層にガスを遮断する強化層として酸化アルミナ層がコーティングによって形成されており、この酸化アルミナ層はあらかじめＰＥＴフィルム上にコーティング処理が施される。   Moreover, since the oxide barrier-coated polyethylene terephthalate (CPET) is used for the gas barrier layer 3, the gas barrier layer 3 can block external odor gas that has entered from the protective layer 4 side. Therefore, the odor gas does not reach the heat-fusible layer 2, and the water or the like as the contents is not contaminated with the odor gas. In the CPET film, an alumina oxide layer is formed by coating on the surface layer as a reinforcing layer that blocks gas, and this alumina oxide layer is previously coated on the PET film.

また、保護層４にナイロン（ＮＹ）を使用すれば、機械的強度を高めることができ、基材である加熱融着層２及びガス遮断層３への穿孔等を確実に防止できる。保護層４にナイロン（ＮＹ）を使用した場合、ナイロン（ＮＹ）が水に濡れると、ナイロンの加水分解によりカプロラクタムが生成され、生成されたカプロラクタムを吸収した水分がガス遮断層３に到達する場合があるが、ガス遮断層３にＣＰＥＴを使用することで内容物にカプロラクタムが混入することはない。   Further, if nylon (NY) is used for the protective layer 4, the mechanical strength can be increased, and perforation or the like in the heat fusion layer 2 and the gas barrier layer 3 as the base material can be reliably prevented. When nylon (NY) is used for the protective layer 4, when nylon (NY) gets wet with water, caprolactam is generated by hydrolysis of nylon, and moisture that has absorbed the generated caprolactam reaches the gas barrier layer 3 However, caprolactam is not mixed into the contents by using CPET for the gas barrier layer 3.

そして、純粋なナイロン、ポリエチレンテレフタレート、ポリエチレン等の樹脂を保護層４、ガス遮断層３、加熱融着層２として使用すれば、これらの樹脂には環境ホルモンや塩素が含まれていないので、柔軟性素材１を廃棄しても環境ホルモンが流出することはなく、また、焼却処分をしてもダイオキシンが発生することもなく、環境悪化を来すことはない。   If a resin such as pure nylon, polyethylene terephthalate, or polyethylene is used as the protective layer 4, the gas barrier layer 3, and the heat fusion layer 2, these resins do not contain environmental hormones or chlorine, so that they are flexible. Even if the sex material 1 is discarded, environmental hormones do not flow out, and even if disposed of by incineration, no dioxins are generated, and the environment is not deteriorated.

次に、本発明の包装材料としての柔軟性素材を用いた柔軟性容器について説明する。
本実施形態の柔軟性容器１１は、図３に示すように、前述した柔軟性素材１を加熱融着層２が内側となるように巻装して両端を重ねてシールし、このシール部が中心となるように折り畳んで稜線１４，１５を形成するとともに、センターシール部１２を形成し、上端を封止してトップシール部１３を形成する。 Next, a flexible container using a flexible material as the packaging material of the present invention will be described.
As shown in FIG. 3, the flexible container 11 of the present embodiment is wound with the flexible material 1 described above so that the heat-fusible layer 2 is inside, and the both ends are stacked and sealed. The ridge lines 14 and 15 are formed by being folded so as to be the center, the center seal portion 12 is formed, and the upper end is sealed to form the top seal portion 13.

そして、トップシール部１３の角部側には表示５に対応して開封位置を示すとともに、開封を容易にするため、引裂部として切り口１６，１７を形成する。   Then, on the corner portion side of the top seal portion 13, an opening position is shown corresponding to the display 5, and incisions 16 and 17 are formed as tearing portions for easy opening.

このようにセンターシール部１２とトップシール部１３との二箇所で閉じられた収容部Ａは、ボトムシール部１８の未形成によって開口された状態で柔軟性容器１１を構成している。そこで、この柔軟性容器１１の開口部１９側を上方に向けて図示しない水装填手段により水を装填するとともに収容部Ａから気体を抜き、トップシール部１３と同様にボトムシール部１８を封止し、液体封入及びその封緘処理を完了する。   Thus, the accommodating part A closed by two places, the center seal part 12 and the top seal part 13, comprises the flexible container 11 in the state opened by the bottom seal part 18 not being formed. Therefore, with the opening 19 side of the flexible container 11 facing upward, water is loaded by water loading means (not shown), and the gas is discharged from the housing portion A, and the bottom seal portion 18 is sealed in the same manner as the top seal portion 13. Then, the liquid filling and the sealing process are completed.

以下、実施例により本発明をさらに詳細に説明するが、本発明は下記の実施例に何ら限定されるものではない。   EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, this invention is not limited to the following Example at all.

〔実施例１〕
厚さ１５μｍのＮＹフィルムと、厚さ１２μｍのＣＰＥＴフィルムと、厚さ４０μｍのＰＥフィルムとからなるＮＹ＃１５／ＣＰＥＴ＃１２／ＰＥ＃４０フィルムを用いて図３に示す柔軟性容器１１を形成し、その収容部Ａに無味無臭のミネラル水を装填した後、ボトムシール部１８を封止した。 [Example 1]
The flexible container 11 shown in FIG. 3 is formed using a NY # 15 / CPET # 12 / PE # 40 film composed of a 15 μm thick NY film, a 12 μm thick CPET film, and a 40 μm thick PE film. Then, after the tasteless and odorless mineral water was loaded into the housing part A, the bottom seal part 18 was sealed.

〔比較例１〕
厚さ２５μｍのＮＹフィルムと、厚さ１２μｍのＥＶＯＨフィルムと、厚さ４０μｍのＰＥフィルムとからなるＮＹ＃２５／ＥＶＯＨ＃１２／ＰＥ＃４０フィルムを用いて図３に示す柔軟性容器１１を形成し、その収容部Ａに無味無臭のミネラル水を装填した後、ボトムシール部１８を封止した。 [Comparative Example 1]
The flexible container 11 shown in FIG. 3 is formed using a NY # 25 / EVOH # 12 / PE # 40 film composed of a 25 μm thick NY film, a 12 μm thick EVOH film, and a 40 μm thick PE film. Then, after the tasteless and odorless mineral water was loaded into the housing part A, the bottom seal part 18 was sealed.

これら実施例１及び比較例１について、液体の商品化、品質保持、運搬性及び保管性等の観点から、性能比較（強度試験、移り香試験、引裂性試験）を行った。   About these Example 1 and Comparative Example 1, performance comparison (a strength test, a fragrance test, a tearability test) was performed from the viewpoints of liquid commercialization, quality maintenance, transportability, storage property, and the like.

（１）強度試験
強度試験では、ミネラル水を装填して封止した柔軟性容器１１を段ボールケースに収納し、当該段ボールケースを高さ３０ｃｍからコンクリート床上に４０回落下させて、柔軟性容器１１から水漏れするか否かについて試験した。当該試験結果を表１に示す。 (1) Strength test In the strength test, the flexible container 11 filled with mineral water and sealed is stored in a cardboard case, and the cardboard case is dropped 40 times from a height of 30 cm onto the concrete floor, and the flexible container 11 It was tested whether or not water leaked from. The test results are shown in Table 1.

Figure 2006282237
Figure 2006282237

表１に示すように、実施例１に係る柔軟性容器１１は水漏れしなかったが、比較例１に係る柔軟性容器１１は２０個中２個の容器で水漏れが生じた。このことから、実施例１に係る柔軟性容器１１は、比較例１に係る柔軟性容器１１に比して強度が高いことが確認された。   As shown in Table 1, the flexible container 11 according to Example 1 did not leak, but the flexible container 11 according to Comparative Example 1 leaked water in two out of twenty containers. From this, it was confirmed that the flexible container 11 according to Example 1 has higher strength than the flexible container 11 according to Comparative Example 1.

（２）移り香試験
移り香試験では、柔軟性容器１１の製造時フィルム臭を感じないこと、即ち、無臭であること、及び段ボールケースの材料である段ボール紙を湿らせ、この段ボール紙とともに柔軟性容器１１をラップで包み込み、３５℃の恒温槽で２週間保存し、柔軟性容器１１内のミネラル水に移り香がないことを確認する試験を行った。当該試験においては、柔軟性容器１１内のミネラル水の匂いを嗅いで、「ブランクと同じ匂いで良好である（Ｅ：Excellent）」、「ブランクとは異なる匂いがするが良好である（Ｇ：Good）」、「移り香があるが飲むことはできる（Ｆ：Fair）」及び「移り香があり飲むことができない（ＮＧ：No Good）」の４段階により主観的に評価した。結果を表２に示す。 (2) Transfer incense test In the transfer incense test, the flexible container 11 does not feel the film odor during manufacture, that is, it is odorless, and the corrugated cardboard paper that is the material of the corrugated cardboard case is moistened. 11 was wrapped with a wrap, stored in a thermostatic bath at 35 ° C. for 2 weeks, and a test was conducted to confirm that there was no scent in the mineral water in the flexible container 11. In the test, the odor of mineral water in the flexible container 11 is smelled, and “smells with the same scent as the blank (E: Excellent)” and “smells different from the blank, but good (G: “Good” ”,“ There is a moving incense but can be drunk (F: Fair) ”and“ No migrant incense and cannot be drunk (NG: No Good) ”. The results are shown in Table 2.

Figure 2006282237
Figure 2006282237

表２に示すように、比較例１の柔軟性容器１１では内容物であるミネラル水に移り香が生じたが、実施例１の柔軟性容器１１では移り香はなく、装填時のミネラル水の品質を保持し、共に味覚上、良好な結果が得られた。なお、Ｅは、最高ランクを示している。   As shown in Table 2, in the flexible container 11 of Comparative Example 1, fragrance was generated in the mineral water as the contents, but in the flexible container 11 of Example 1, there was no fragrance and the quality of the mineral water at the time of loading was improved. Both were retained and good taste was obtained. E indicates the highest rank.

（３）引裂性試験
引裂性試験は、柔軟性容器１１に形成されている切り口１７を用いて開封した際に、その難易度を検査した。この場合、検査員６名が３点満点で評価をし、その合計点を評点とした。具体的には、良好である場合は３点、多少引っかかるがきれいに切れる場合は２点、開封に力が必要等、嫌な気分を伴う場合は１点、うまく切れない場合は０点とし、主観的評価により採点した。試験結果を表３に示す。 (3) Tearability test The tearability test examined the difficulty when opening using the cut 17 formed in the flexible container 11. In this case, 6 inspectors gave a rating with a maximum of 3 points, and the total score was taken as the score. Specifically, the score is 3 points if it is good, 2 points if it gets stuck slightly but it cuts cleanly, 1 point if it is unpleasant, such as the need for opening, and 0 point if it does not cut well. A scoring system was used for scoring. The test results are shown in Table 3.

Figure 2006282237
Figure 2006282237

表３に示すように、実施例１に係る柔軟性容器１１は、比較例１に係る柔軟性容器１１に比して引裂性が高く、切り口１７からカットするのが容易であることが確認された。   As shown in Table 3, it was confirmed that the flexible container 11 according to Example 1 has higher tearability than the flexible container 11 according to Comparative Example 1 and can be easily cut from the cut end 17. It was.

本発明の包装材料の一実施形態である柔軟性素材の一部を切り欠いて示した斜視図である。It is the perspective view which notched and showed a part of flexible material which is one Embodiment of the packaging material of this invention. 図１のII−II線断面を示す拡大断面図である。It is an expanded sectional view which shows the II-II line cross section of FIG. 本発明の一実施形態に係る柔軟性容器を示す平面図である。It is a top view which shows the flexible container which concerns on one Embodiment of this invention.

符号の説明Explanation of symbols

１ 柔軟性素材（包装材料）
２ 加熱融着層
３ ガス遮断層（ＣＰＥＴ）
４ 保護層
５ 表示
１１ 柔軟性容器
1 Flexible material (packaging material)
2 Heat-fusion layer 3 Gas barrier layer (CPET)
4 Protective layer 5 Display 11 Flexible container

Claims (5)

加熱融着性を持つ加熱融着層と、ガス遮断性を持つガス遮断層と、機械的強度を持つ保護層とからなる積層体を含み、前記積層体の表面に前記加熱融着層を露出してなる、引裂性を備えた包装材料であって、
前記ガス遮断層は、ポリエチレンテレフタレートに酸化アルミナをコーティングした酸化アルミナコーティングポリエチレンテレフタレートからなることを特徴とする包装材料。 A laminate comprising a heat-fusible layer having heat-fusibility, a gas-barrier layer having gas barrier properties, and a protective layer having mechanical strength, and the heat-fused layer is exposed on the surface of the laminate. A packaging material having tearability,
The packaging material according to claim 1, wherein the gas barrier layer is made of an alumina-coated polyethylene terephthalate in which polyethylene terephthalate is coated with alumina oxide. 前記加熱融着層は、ポリエチレン又はその他の加熱融着性を持つ樹脂であることを特徴とする請求項１記載の包装材料。   The packaging material according to claim 1, wherein the heat-fusible layer is polyethylene or other resin having heat-fusible properties. 前記保護層は、ナイロン、ポリエチレンテレフタレート及び二軸延伸ポリプロピレンからなる群より選ばれる１種以上であることを特徴とする請求項１又は２記載の包装材料。   The packaging material according to claim 1 or 2, wherein the protective layer is at least one selected from the group consisting of nylon, polyethylene terephthalate, and biaxially oriented polypropylene. 請求項１から３のいずれか１項に記載の包装材料を用い、前記加熱融着層を内面側としたことを特徴とする柔軟性容器。   A flexible container using the packaging material according to claim 1, wherein the heat-fusible layer is on the inner surface side. 前記包装材料は、前記保護層の内面側表面若しくは前記ガス遮断層又は双方を印刷等の表示面に設定したことを特徴とする請求項４記載の柔軟性容器。
The flexible container according to claim 4, wherein the packaging material is configured such that a surface on the inner surface side of the protective layer or the gas barrier layer or both are set on a display surface such as printing.
JP2005105266A 2005-03-31 2005-03-31 Wrapping material and flexible container Pending JP2006282237A (en)