JP2006274268A - Ink composition for erasable marking pen - Google Patents
Ink composition for erasable marking pen Download PDFInfo
- Publication number
- JP2006274268A JP2006274268A JP2006133362A JP2006133362A JP2006274268A JP 2006274268 A JP2006274268 A JP 2006274268A JP 2006133362 A JP2006133362 A JP 2006133362A JP 2006133362 A JP2006133362 A JP 2006133362A JP 2006274268 A JP2006274268 A JP 2006274268A
- Authority
- JP
- Japan
- Prior art keywords
- water
- dye
- soluble resin
- ink composition
- type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、墨汁、絵具、マーキングペン用インキ等として用いることができ、布、不織布などの繊維集合体に付着した場合に水洗などにより簡単に消去できる水溶性の消去性着色剤組成物に関する。 The present invention relates to a water-soluble erasable colorant composition that can be used as ink for ink, paints, marking pens, etc., and can be easily erased by washing with water when adhering to a fiber assembly such as cloth or nonwoven fabric.
従来、例えば墨汁や絵具は、誤って衣服などの布、不織布などの繊維集合体に付着し定着した場合、洗っても簡単にはとれないという問題があった。 Conventionally, for example, ink ink or paint has a problem that it cannot be easily removed even if it is washed and attached to a fiber assembly such as cloth or non-woven fabric by mistake.
一方、墨汁と絵具だけでなく、マーキングペン用インキ等を被服等の繊維集合体に積極的に描いて、簡単に消去できれば、新たな着色剤としての利用に供することもできる。 On the other hand, if inks for marking pens and the like can be actively drawn on a fiber assembly such as clothing and easily erased in addition to ink and paint, it can be used as a new colorant.
従来、特許文献１では、染料を水不溶性の樹脂等と反応させて水不溶性の複合物とし、繊維集合体に染着しないようにして消去性を付与するか、又は水不溶性樹脂で染料を覆い水不溶性の複合物の粒子径を大きくさせ、染料の繊維の目に引っかかるのを防止して消去性を付与している。 Conventionally, in Patent Document 1, a dye is reacted with a water-insoluble resin or the like to form a water-insoluble composite and imparts erasability so as not to be dyed on a fiber assembly, or the dye is covered with a water-insoluble resin. The particle diameter of the water-insoluble composite is increased to prevent the dye fibers from getting caught in the eyes, thereby imparting erasability.
しかしながら、前者の技術は、染料をわざわざ水不溶性の樹脂等と反応させる必要が生じる。また、後者の技術では、筆記面との定着が悪くなるため、これを防止するためにインキ成分に別途定着剤を添加する必要があった。 However, in the former technique, it is necessary to react the dye with a water-insoluble resin or the like. Further, in the latter technique, fixing with the writing surface is deteriorated, so that a fixing agent needs to be added to the ink component in order to prevent this.
本発明の課題は、染料を水不溶性樹脂との複合物で消去性を実現することなく、衣服などに誤って着色剤が付着しても染色されることなく、水洗又は洗剤使用で洗濯等により簡単に消去できる消去性着色剤組成物を提供する点にある。 The object of the present invention is to achieve the erasability with a composite of a dye and a water-insoluble resin, without staining even if a coloring agent is accidentally attached to clothes, etc. The object is to provide an erasable colorant composition that can be easily erased.
本発明者らは上記の問題を解決すべく鋭意検討した結果、直染性が低い染料と水溶性樹脂を溶解させた着色剤組成物が消去性を有することを見いだした。特に、水溶性樹脂を少なくとも１０％含有する消去性着色剤組成物が消去性を実現する上で好ましいことを見出した。本発明は、直染性の低い染料と水溶性樹脂を含有することを特徴とする消去性着色剤組成物である。また本発明は、直染性の低い染料に水溶性樹脂を少なくとも１０％含有することを特徴とする消去性着色剤組成物である。 As a result of intensive studies to solve the above problems, the present inventors have found that a colorant composition in which a dye having low direct dyeability and a water-soluble resin are dissolved has erasability. In particular, it has been found that an erasable colorant composition containing at least 10% of a water-soluble resin is preferable for achieving erasability. The present invention is an erasable colorant composition comprising a dye having low direct dyeability and a water-soluble resin. The present invention also provides an erasable colorant composition characterized by containing a water-soluble resin at least 10% in a dye having low direct dyeability.
染料に添加する水溶性樹脂は、水溶性樹脂であれば特に限定されないが、中でも、水溶性樹脂がＯＨ基、ＣＯＯＨ基、ＳＯ3Ｈ基及び塩から選ばれる官能基を１又はそれ以上持つ水溶性樹脂が好ましい。すなわち、合成多価アルコール系、カルボン酸（塩）系、スルホン酸（塩）系の水溶性樹脂が好ましい。具体的には、ポリエチレングリコール、ポリアルキレンオキシ化合物、ポリビニールアルコール、変性ポリビニールアルコール、ポリアクリル酸、ポリアクリル酸共重合物、ポリスルフォン酸、ポリスルフォン酸共重合物が好ましく、中でもポリエチレングリコールが最適である。 The water-soluble resin added to the dye is not particularly limited as long as it is a water-soluble resin. Among them, the water-soluble resin has one or more functional groups selected from OH groups, COOH groups, SO3H groups and salts. Is preferred. That is, a synthetic polyhydric alcohol-based, carboxylic acid (salt) -based, or sulfonic acid (salt) -based water-soluble resin is preferable. Specifically, polyethylene glycol, polyalkyleneoxy compound, polyvinyl alcohol, modified polyvinyl alcohol, polyacrylic acid, polyacrylic acid copolymer, polysulfonic acid, and polysulfonic acid copolymer are preferable. Among them, polyethylene glycol is preferable. Is optimal.
水溶性樹脂、特にポリエチレングリコールの含有量を検討した結果、既述の通り、少なくとも１０重量パーセントで効果が顕著となることが判明した。水溶性樹脂の割合が１０重量パーセントより低い場合は、水溶性樹脂が染料を取り込むことができす、染料の一部が繊維に入り込んでしまうため消去性が悪くなる。従って、水溶性樹脂の添加量は少なくとも１０重量パーセントが好ましい。 As a result of examining the content of the water-soluble resin, particularly polyethylene glycol, it has been found that the effect becomes remarkable at least 10 weight percent as described above. When the proportion of the water-soluble resin is lower than 10 percent by weight, the water-soluble resin can take in the dye, and a part of the dye gets into the fiber, resulting in poor erasability. Therefore, the amount of water-soluble resin added is preferably at least 10 weight percent.
着色剤に加える水溶性樹脂の平均分子量が低い場合は着色剤がにじみやすくなり、また染料を取り込む樹脂の分子の長さも短いため、樹脂に取り込まれた染料の見かけ上の分子の長さも短く、繊維中に入り込みやすくなることが考えられ、消去性に悪影響を及ぼす。また分子量が大きくなるとその水溶液は粘性が高くなり、取り扱い面から考慮して好ましくない。ポリエチレングリコールの分子量は少なくとも４００、好ましくは６００〜７５００である。なお、本発明でいう平均分子量は重量平均分子量を示す。 When the average molecular weight of the water-soluble resin added to the colorant is low, the colorant tends to bleed, and since the length of the resin molecule that incorporates the dye is short, the apparent molecular length of the dye incorporated into the resin is also short, It may be easy to penetrate into the fiber, which adversely affects erasability. Further, when the molecular weight is increased, the aqueous solution becomes highly viscous, which is not preferable from the viewpoint of handling. The molecular weight of polyethylene glycol is at least 400, preferably 600-7500. In addition, the average molecular weight as used in the field of this invention shows a weight average molecular weight.
本発明でいう直染性が低い染料とは、水溶性樹脂を含有する消去性着色剤組成物の系において、繊維中への染料の拡散及び染料と繊維の相互作用が低い染料をすべていうが、具体的には反応性染料、酸性染料が好ましいことを見出した。直染性の低い染料は反応性染料、酸性染料のいずれかである。 In the present invention, the dye having a low direct dyeability refers to all dyes in which the dye diffuses into the fiber and the dye-fiber interaction is low in the system of the erasable colorant composition containing the water-soluble resin. Specifically, it has been found that reactive dyes and acid dyes are preferable. The dye having low direct dyeability is either a reactive dye or an acid dye.
直接染料についても検討したが、水溶性樹脂、特にポリエチレングリコールを添加することにより逆に消去性が悪くなる傾向にあることを見出した。直接染料は直接セルロース繊維に染着するアニオン性の染料であって直接性と呼ばれる性質を有する。木綿に対する染着機構はファン・デル・ワールス力による結合や、染料分子中のアミノ基、水酸基、π電子系がセルロースの水酸基との間で行なう水素結合が考えられている。そして、ポリエチレングリコールを添加することにより、染料溶液の表面張力が下がり、繊維への拡散がかえって促進されるため、繊維に対する汚染力が増大するためと考えられる。また、塩基性染料では、目立った消去性の向上は見られない。これに対し、酸性染料では、反応性染料と同程度の消去性の向上がみられた。これは、反応性染料の染料部は酸性染料であることから消去性向上の要因も反応性染料と同様の要因だと考えられる。 Although direct dyes were also examined, it was found that erasability tends to be worsened by adding a water-soluble resin, particularly polyethylene glycol. The direct dye is an anionic dye which is directly dyed on cellulose fibers and has a property called directness. The dyeing mechanism for cotton is considered to be a bond by van der Waals force, or a hydrogen bond formed between an amino group, a hydroxyl group, and a π-electron system in the dye molecule with a hydroxyl group of cellulose. By adding polyethylene glycol, the surface tension of the dye solution is lowered, and the diffusion to the fiber is promoted. Therefore, it is considered that the staining power to the fiber increases. In addition, with a basic dye, there is no noticeable improvement in erasability. In contrast, the acid dye exhibited the same level of erasability improvement as the reactive dye. This is because the dye part of the reactive dye is an acid dye, so the erasability improvement factor is considered to be the same factor as the reactive dye.
本発明の着色剤組成物が消去性を持つ理由は、定かではないが、１つは直染性が低い染料、好ましくは酸性染料又は反応性染料の場合、混合物ではあるとはいうものの、その染料部が水溶性樹脂に包接されるような形で包み込まれるため、染料の見かけの大きさが大きくなり、繊維集合体の繊維の表面を通って繊維内に入り込むことができないためと考えられる。また、水溶性樹脂に直染性が低い染料が取り込まれているため染料の反応基が繊維と反応することを阻害しており、更に、水溶性樹脂が洗浄液と繊維に付着した染料のあいだの表面張力を下げ、湿潤、浸透作用により染料が繊維の表面から引き離されるのを助け、消去性を向上させる作用を有するためであると考えられる。 The reason why the colorant composition of the present invention has erasability is not clear, but one is a dye having low direct dyeability, preferably an acid dye or a reactive dye, although it is a mixture, It is thought that because the dye part is wrapped in a form that is included in the water-soluble resin, the apparent size of the dye increases, and it cannot enter the fiber through the fiber surface of the fiber assembly. . In addition, since the dye having low direct dyeability is incorporated into the water-soluble resin, the reactive group of the dye is prevented from reacting with the fiber, and the water-soluble resin is between the washing liquid and the dye attached to the fiber. It is considered that this is because the surface tension is lowered, and the dye is separated from the surface of the fiber by the wetting and penetrating action, thereby improving the erasability.
直染性が低い染料として特に有効なものは、既述の通り、酸性染料又は反応性染料であるが、その中でも、特に有効なものを検討した結果、ジクロルトリアジン型、モノクロルトリアジン型、ビニールスルホン型、クロルピリミジン型、ジクロルキノキサジン型、モノクロルトリアジンとビニールスルホンの二官能基型が好ましいことが判明した。また中でも、モノクロルトリアジン型、ビニールスルホン型、特にモノクロルトリアジン型の反応性染料が最適である。直染性の低い染料は、ジクロルトリアジン型、モノクロルトリアジン型、ビニールスルホン型、クロルピリミジン型、ジクロルキノキサジン型、モノクロルトリアジンとビニールスルホンの二官能基型のいずれかの反応性染料であることが好ましい。直染性の低い染料が、モノクロルトリアジン型、ビニールスルホン型のいずれかの反応性染料であることが好ましい。直染性の低い染料がモノクロルトリアジン型の反応性染料であることが好ましい。 As described above, acid dyes or reactive dyes are particularly effective as dyes having low direct dyeing properties. Among them, as a result of studying particularly effective dyes, dichlorotriazine type, monochlorotriazine type, vinyl It has been found that a sulfone type, a chloropyrimidine type, a dichloroquinoxazine type, and a bifunctional type of monochlorotriazine and vinyl sulfone are preferable. Among them, monochlorotriazine type, vinyl sulfone type, particularly monochlorotriazine type reactive dyes are most suitable. The dye having low direct dyeability is a reactive dye of dichlorotriazine type, monochlorotriazine type, vinylsulfone type, chloropyrimidine type, dichloroquinoxazine type, or bifunctional type of monochlorotriazine and vinylsulfone. It is preferable. The dye having low direct dyeability is preferably a reactive dye of either monochlorotriazine type or vinylsulfone type. The dye having low direct dyeability is preferably a monochlorotriazine type reactive dye.
本発明は従来のように水不溶性樹脂と染料とのあいだで反応を起こさせる必要がなく、染料に水溶性樹脂を混合することのみにより達成される。また染料を取り込む樹脂に水溶性のものを用いることにより、繊維との定着が確保されやすく、水不溶性樹脂を用いた場合の様に定着剤の添加の必要がないが、必要に応じて定着剤を添加することもできる。
すなわち、染料を包含した水溶性樹脂はその水酸基などを有することにより繊維、特に綿などの水酸基などを多く有する繊維の表面のみと水素結合、もしくはファンデアワールス力などにより結合し、定着性においても好ましい効果を有する。さらにこのような水素結合などは結合が比較的弱く、水などで洗浄することにより、簡単に繊維との結合を切断させることができるため、消去性においても有効である。
The present invention does not require a reaction between the water-insoluble resin and the dye as in the prior art, and is achieved only by mixing the water-soluble resin with the dye. In addition, by using a water-soluble resin that takes in the dye, it is easy to ensure fixation with the fiber, and it is not necessary to add a fixing agent as in the case of using a water-insoluble resin. Can also be added.
In other words, the water-soluble resin containing the dye is bonded to only the surface of the fiber, particularly the fiber having many hydroxyl groups such as cotton, by the hydrogen bond or van der Waals force by having the hydroxyl group. It has a favorable effect. Further, such a hydrogen bond is relatively weak and can be easily cut off with a fiber or the like so that the bond with the fiber can be easily cut.
本発明の消去性着色剤は、従来のように、染料を水不溶性樹脂との複合物で消去性を実現することなく、直染性の低い染料と水溶性樹脂を混合して含有するだけで、衣服などに誤って着色剤が付着しても染色されることなく、水洗又は洗剤使用で洗濯等により簡単に消去できる。
従って、簡単な組成で、洗濯で消去できる墨汁、絵具、マーキングペン用インキ等として利用することができ、当該分野に資するところが大きい。
The erasable colorant of the present invention can be obtained by mixing a dye having a low direct dyeability with a water-soluble resin without realizing the erasability with a composite of a water-insoluble resin as in the prior art. Even if a colorant accidentally adheres to clothes, it can be easily erased by washing or the like by washing with water or using a detergent.
Therefore, it can be used as ink, paint, marking pen ink, etc. that can be erased by washing with a simple composition, which greatly contributes to this field.
直染性が低い染料としては、限定されるものではないが、例えば、商品名 Cibacron Black P-SG（チバガイギー社製）、Cibacron
Black P-2PD（チバガイギー社製）、Cibacron Black F-2B（チバガイギー社製）、Cibacron GrayG-R-01（チバガイギー社製）、Cibacron Blue
P-B （チバガイギー社製）、Cibacron Navy GR-E-01（チバガイギー社製）、Cibacron Blue F-R（チバガイギー社製）、Cibacron Red P-B（チバガイギー社製）、Cibacron Red 4G-E-N（チバガイギー社製）、Cibacron Red
F-B（チバガイギー社製）、Cibacron Yellow P-6GS（チバガイギー社製）、Cibacron Yellow 2G-E（チバガイギー社製）、Cibacron
Yellow F-3R（チバガイギー社製）等のモノクロルトリアジン型反応性染料、商品名 Cibacron
Black C-N（チバガイギー社製）、Cibacron Blue C-R（チバガイギー社製）、Cibacron Red C-R（チバガイギー社製）、Cibacron Yellow
C-R-1（チバガイギー社製）等のモノクロルトリアジン−ビニルスルホン二官能基型反応性染料、Remazol
Black DEN Hi-Gran（ダイスター社製）、Remazol Blue RU-N（ダイスター社製）、Remazol Red RU-N（ダイスター社製）、Remazol Yellow
RU-N（ダイスター社製）等のビニルスルホン型反応性染料、商品名 Levafix Navy Blue
E-BNA GRAN（ダイスター社製）、Levafix BR.Red E-RN（ダイスター社製）、Levafix G Yellow E-G（ダイスター社製）等のジクロルキノキサジン型反応性染料を用いることができる。また、C.I.番号 A.Bk.2（商品名
Water Black R-455）、C.I.番号
A.Bk.119（商品名 Opal Black new conc 保土谷社製）、C.I.番号 A.R.87（商品名 エオシン）、C.I.番号 A.B.9（商品名
Water Blue #9）等の酸性染料を用いることができる。
Examples of the dye having low direct dyeing property include, but are not limited to, for example, trade name Cibacron Black P-SG (Ciba Geigy), Cibacron
Black P-2PD (Ciba Geigy), Cibacron Black F-2B (Ciba Geigy), Cibacron GrayG-R-01 (Ciba Geigy), Cibacron Blue
PB (Ciba Geigy), Cibacron Navy GR-E-01 (Ciba Geigy), Cibacron Blue FR (Ciba Geigy), Cibacron Red PB (Ciba Geigy), Cibacron Red 4G-EN (Ciba Geigy), Cibacron Red
FB (Ciba Geigy), Cibacron Yellow P-6GS (Ciba Geigy), Cibacron Yellow 2G-E (Ciba Geigy), Cibacron
Monochlorotriazine type reactive dye such as Yellow F-3R (Ciba Geigy), trade name Cibacron
Black CN (Ciba Geigy), Cibacron Blue CR (Ciba Geigy), Cibacron Red CR (Ciba Geigy), Cibacron Yellow
Monochlorotriazine-vinylsulfone bifunctional reactive dye such as CR-1 (Ciba Geigy), Remazol
Black DEN Hi-Gran (Dystar), Remazol Blue RU-N (Dystar), Remazol Red RU-N (Dystar), Remazol Yellow
Vinylsulfone reactive dyes such as RU-N (Dystar), trade name Levafix Navy Blue
Dichloroquinoxazine type reactive dyes such as E-BNA GRAN (Dystar), Levafix BR.Red E-RN (Dystar), Levafix G Yellow EG (Dystar) can be used. Also, CI number A.Bk.2 (product name
Water Black R-455), CI number
A.Bk.119 (Brand name Opal Black new conc Hodogaya), CI number AR87 (Brand name Eosin), CI number AB9 (Brand name)
Acid dyes such as Water Blue # 9) can be used.
直染性が低い染料の添加量は特に限定されない。但し、２〜４０重量パーセント程度が好ましく、４０重量パーセントを超えて添加すると水溶性樹脂に包括しきれなくなり消去性に悪影響を及ぼす。一方、２重量パーセントより少ないと、着色が薄く好ましくない。 The addition amount of the dye having low direct dyeability is not particularly limited. However, about 2 to 40 percent by weight is preferable, and if it exceeds 40 percent by weight, it cannot be included in the water-soluble resin and adversely affects erasability. On the other hand, if it is less than 2 weight percent, the coloration is thin and undesirable.
水溶性樹脂は、着色剤の消去性を向上させるために添加するものであり、ポリエチレングリコール、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンオレイン酸エステル、ポリオキシエチレンノニルフェニルエーテル、カルボン酸変性ポリビニルアルコール、ポリアクリル酸、ポリスチレンスルフォン酸ソーダのほか、ポリビニルアルコール、ポリオキシエチレンポリオキシプロピレンブロックポリマー、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレン脂肪酸エステル、ポリグリセリン脂肪酸エステル、ポリオキシエチレンソルビタンモノオレエート、ポリオキシエチレンソルビタンモノラウレート、ポリオキシエチレンソルビタンモノステアレート、ポリオキシエチレンソルビタンモノパルミテート、プルラン、ポリアクリル酸イタコン酸共重合体などのうち１種または２種以上混合して使用できるが、消去性、価格、取り扱いなどを考慮するとポリエチレングリコールが最適である。 The water-soluble resin is added to improve the erasability of the colorant, and includes polyethylene glycol, polyoxyethylene lauryl ether, polyoxyethylene oleate, polyoxyethylene nonylphenyl ether, carboxylic acid-modified polyvinyl alcohol, In addition to polyacrylic acid and polystyrene sulfonate soda, polyvinyl alcohol, polyoxyethylene polyoxypropylene block polymer, polyoxyethylene alkyl ether, polyoxyethylene nonylphenyl ether, polyoxyethylene fatty acid ester, polyglycerin fatty acid ester, polyoxyethylene Sorbitan monooleate, polyoxyethylene sorbitan monolaurate, polyoxyethylene sorbitan monostearate, polyoxyethylene Sorbitan monopalmitate, pullulan, can be used alone or in combination of two or more of polyacrylic acid itaconic acid copolymers, erasability, price, consider polyethylene glycol and handling is optimal.
着色剤に加える水溶性樹脂の割合が低い場合は樹脂が前記染料を取り込むことができす、染料の一部が繊維に入り込んでしまうため消去性が悪くなる。従って、既述の通り、水溶性樹脂の含有量は少なくとも１０重量パーセントであることが好ましい。 When the ratio of the water-soluble resin added to the colorant is low, the resin can take in the dye, and a part of the dye gets into the fiber, resulting in poor erasability. Therefore, as described above, the content of the water-soluble resin is preferably at least 10 weight percent.
着色剤組成物には、定着剤、増量剤、防腐剤、防黴剤、香料、界面活性剤、ｐＨ調整剤、粘度調整剤、分散剤、保水剤、湿潤剤、消泡剤、レベリング剤、粘弾性調整剤、にじみ防止剤、水、アルコールなど一般に墨汁、絵具、マーキングペンに含まれるものを含めることができる。 Colorant compositions include fixing agents, extenders, preservatives, antifungal agents, perfumes, surfactants, pH adjusters, viscosity adjusters, dispersants, water retention agents, wetting agents, antifoaming agents, leveling agents, Viscoelasticity adjusting agents, anti-bleeding agents, water, alcohol, and the like that are generally contained in ink, paints, and marking pens can be included.
本発明の消去性着色剤組成物は、例えば必須成分として直染性の低い染料及び水溶性樹脂を含有し、これらを水と混合、攪拌により溶解させることによって得られる。 The erasable colorant composition of the present invention contains, for example, a dye having low direct dyeability and a water-soluble resin as essential components, and these are mixed with water and dissolved by stirring.
本発明の着色剤は、墨汁、絵具、インキなどとして使用可能であり、これらが誤って衣服などに付いた場合でも繊維の表面を通して繊維内に入り込むことがないため、水洗または洗濯により簡単に消去することができる。 The colorant of the present invention can be used as ink, paint, ink, etc., and even if it is accidentally attached to clothes, it does not enter the fiber through the surface of the fiber, so it can be easily erased by washing or washing. can do.
本発明の消去性着色剤組成物は、繊維であれば特に限定されずに使用できるが、特に、綿、羊毛、ナイロン、ビニロン、アセテート、ウール、レーヨン、アクリル、絹、ポリエステルなどの繊維に対して有効に作用する。特に、反応性染料の場合、当該染料のみでは、綿、レーヨンといったセルロース骨格、ビニロンといったＰＶＡ骨格の様にＯＨ基を持つ繊維や、ウール、絹といったアミンを持つ繊維で染る傾向があり、染料とＯＨ基やアミンの間に何らかの相互作用（結合）が生じると考えられるが、水溶性樹脂、特にポリエチレングリコールを添加することにより洗濯での消去性がほぼ全ての繊維において向上する。 The erasable colorant composition of the present invention can be used without particular limitation as long as it is a fiber, but in particular, for fibers such as cotton, wool, nylon, vinylon, acetate, wool, rayon, acrylic, silk, polyester, etc. Works effectively. In particular, in the case of reactive dyes, the dye alone has a tendency to be dyed with fibers having an OH group, such as cellulose skeletons such as cotton and rayon, and PVA skeletons such as vinylon, and fibers having amines such as wool and silk. It is believed that some interaction (bonding) occurs between OH groups and amines, but by adding a water-soluble resin, particularly polyethylene glycol, the erasability in washing is improved in almost all fibers.
以下、本発明を実施例に基づいて詳細に説明する。 Hereinafter, the present invention will be described in detail based on examples.
（実施例１）
イオン交換水５０ｍｌにポリエチレングリコール（平均分子量３０００）を２０ｇを溶解し、室温で攪拌しながら、商品名 Cibacron Black P-SG（チバガイギー社製）の反応性染料２．０ｇを添加して十分攪拌し、完全に溶解させて黒色の着色剤組成物を得た。
Example 1
Dissolve 20 g of polyethylene glycol (average molecular weight 3000) in 50 ml of ion-exchanged water, add 2.0 g of the reactive dye under the trade name Cibacron Black P-SG (manufactured by Ciba Geigy) and stir well while stirring at room temperature. And completely dissolved to obtain a black colorant composition.
（実施例２）
イオン交換水５０ｍｌにポリエチレングリコール（平均分子量３０００）を２０ｇを溶解し、室温で攪拌しながら、商品名 Cibacron Blue P-B（チバガイギー社製）の反応性染料２．０ｇを添加して十分攪拌し、完全に溶解させて青色の着色剤組成物を得た。
(Example 2)
Dissolve 20 g of polyethylene glycol (average molecular weight 3000) in 50 ml of ion-exchanged water, add 2.0 g of the reactive dye under the trade name Cibacron Blue PB (Ciba Geigy) while stirring at room temperature, and stir thoroughly. To obtain a blue colorant composition.
（実施例３）
イオン交換水５０ｍｌにポリエチレングリコール（平均分子量３０００）を２０ｇを溶解し、室温で攪拌しながら、商品名 Cibacron Yellow P-6GS（チバガイギー社製）の反応性染料２．０ｇを添加して十分攪拌し、完全に溶解させて黄色着色剤組成物を得た。
(Example 3)
Dissolve 20 g of polyethylene glycol (average molecular weight 3000) in 50 ml of ion-exchanged water, add 2.0 g of a reactive dye under the trade name Cibacron Yellow P-6GS (Ciba Geigy) and stir well while stirring at room temperature. And completely dissolved to obtain a yellow colorant composition.
（実施例４）
イオン交換水５０ｍｌにポリエチレングリコール（平均分子量３０００）を２０ｇを溶解し、室温で攪拌しながら、商品名 Cibacron Red P-B （チバガイギー社製）の反応性染料２．０ｇを添加して十分攪拌し、完全に溶解させて赤色着色剤組成物を得た。
Example 4
Dissolve 20 g of polyethylene glycol (average molecular weight 3000) in 50 ml of ion-exchanged water, add 2.0 g of the reactive dye of the trade name Cibacron Red PB (manufactured by Ciba Geigy) while stirring at room temperature, and stir thoroughly. To obtain a red colorant composition.
（比較例１）
実施例１においてポリエチレングリコール（平均分子量３０００）を除いて黒色着色剤組成物を得た。
(Comparative Example 1)
In Example 1, a black colorant composition was obtained by removing polyethylene glycol (average molecular weight 3000).
（比較例２）
実施例２においてポリエチレングリコール（平均分子量３０００）を除いて青色着色剤組成物を得た。
(Comparative Example 2)
In Example 2, a blue colorant composition was obtained by removing polyethylene glycol (average molecular weight 3000).
（比較例３）
実施例３においてポリエチレングリコール（平均分子量３０００）を除いて黄色着色剤組成物を得た。
(Comparative Example 3)
In Example 3, a yellow colorant composition was obtained by removing polyethylene glycol (average molecular weight 3000).
（比較例４）
実施例４においてポリエチレングリコール（平均分子量３０００）を除いて赤色着色剤組成物を得た。
(Comparative Example 4)
In Example 4, a red colorant composition was obtained by removing polyethylene glycol (average molecular weight 3000).
（消去性試験）
次に、綿ブロードの試験布に、水の含まない画筆（平筆４号）を用いて、上記実施例１〜４及び比較例１〜４の着色剤組成物を塗布し、室温で指触乾燥するまで放置した。乾燥後、洗濯機で合成洗剤を使用して（０．２％になる様に調整）２５℃で１５分間洗濯を行ない、１５分間水洗した。
乾燥後、下記の基準で目視評価した。４以上を消去性着色剤組成物として合格とした。
５．．．完全に消去。
４．．．ほぼ消去。（光に透かして見るとかすかに残っている。）
３．．．洗濯前に比べ薄くはなっており効果はあるが、塗布跡がわかる。
２．．．洗濯前に比べ薄くはなっているが、あまり洗濯の効果なし。
１．．．洗濯前と変わらず。
(Eraseability test)
Next, the colorant composition of Examples 1 to 4 and Comparative Examples 1 to 4 was applied to a cotton broad test cloth using a paint brush (flat brush No. 4) containing no water, and touched at room temperature. Left to dry. After drying, using a synthetic detergent in a washing machine (adjusted so as to be 0.2%), washing was performed at 25 ° C. for 15 minutes, followed by washing with water for 15 minutes.
After drying, visual evaluation was performed according to the following criteria. Four or more were considered acceptable as erasable colorant compositions.
5. . . Completely erased.
4). . . Almost erased. (It remains faint when viewed through the light.)
3. . . Although it is thinner than before washing, there is an effect, but the application mark can be seen.
2. . . Although it is thinner than before washing, there is not much washing effect.
1. . . Same as before washing.
表１より、直染性の低い染料を用いた実施例１〜４の着色剤組成物は、いずれも洗濯によって完全又はほぼ消去されている。また、ポリエチレングリコールを混合することで、消去性が増大することが認められる。また、いずれの着色剤組成物も室温で指触乾燥するまで放置した後の筆跡は、綿ブロードの試験布に充分定着していた。 From Table 1, all of the colorant compositions of Examples 1 to 4 using a dye having low direct dyeability are completely or almost erased by washing. Moreover, it is recognized that erasability increases by mixing polyethylene glycol. In addition, the handwriting after leaving any colorant composition to dry to the touch at room temperature was sufficiently fixed on a cotton broad test cloth.
（実施例５、実施例６及び比較例５）
次に、ポリエチレングリコール（平均分子量３０００）の含有量を除き、実施例１と同条件で、黒色の着色剤組成物を得た。すなわち、イオン交換水５０ｍｌにポリエチレングリコール（平均分子量３０００）をそれぞれ２．０ｇ、５．０ｇ、１５ｇを溶解したものを、各々室温で攪拌しながら、商品名 Cibacron Black P-SG（チバガイギー社製）の反応性染料２．０ｇをそれぞれ添加して十分攪拌し、完全に溶解させて、それぞれ比較例５、実施例５及び実施例６の黒色の着色剤組成物を得た。
(Example 5, Example 6 and Comparative Example 5)
Next, a black colorant composition was obtained under the same conditions as in Example 1 except for the content of polyethylene glycol (average molecular weight 3000). That is, the product name Cibacron Black P-SG (manufactured by Ciba Geigy Co., Ltd.) was prepared by dissolving 2.0 g, 5.0 g, and 15 g of polyethylene glycol (average molecular weight 3000) in 50 ml of ion exchange water, respectively, while stirring at room temperature. Each of the reactive dyes (2.0 g) was added, stirred sufficiently, and completely dissolved to obtain black colorant compositions of Comparative Example 5, Example 5, and Example 6, respectively.
これらの着色剤組成物について、前記消去性試験をした結果、比較例５は評価点は３であったのに対して、実施例５及び実施例６はいずれも評価点は４であり、前記の実施例１の結果と考え合わせると、水溶性樹脂であるポリエチレングリコールはかなり多量含有させることが重要な点であり、その含有量は少なくとも１０重量％は必要であることが認められた。 As a result of the erasability test on these colorant compositions, Comparative Example 5 had an evaluation score of 3, whereas Examples 5 and 6 both had an evaluation score of 4. In combination with the results of Example 1, it was important that polyethylene glycol, which is a water-soluble resin, was contained in a considerably large amount, and the content was required to be at least 10% by weight.
（実施例７〜１１）
次に、ポリエチレングリコール（平均分子量３０００）を代えた以外は実施例１と同条件下で、各種の水溶性樹脂を用いて黒色の着色剤組成物を得た。すなわち、イオン交換水５０ｍｌに、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンノニルフェニルエーテル、カルボン酸変性ポリビニルアルコール、ポリアクリル酸、ポリスチレンスルフォン酸ソーダをそれぞれ２０ｇを溶解したものを、各々室温で攪拌しながら、商品名 Cibacron Black P-SG（チバガイギー社製）の反応性染料２．０ｇをそれぞれ添加して十分攪拌し、完全に溶解させて、それぞれ実施例７〜１１の黒色の着色剤組成物を得た。
(Examples 7 to 11)
Next, a black colorant composition was obtained using various water-soluble resins under the same conditions as in Example 1 except that polyethylene glycol (average molecular weight 3000) was changed. That is, 20 g each of polyoxyethylene lauryl ether, polyoxyethylene nonylphenyl ether, carboxylic acid-modified polyvinyl alcohol, polyacrylic acid, and sodium polystyrene sulfonate dissolved in 50 ml of ion-exchanged water was stirred at room temperature. , 2.0 g of a reactive dye of trade name Cibacron Black P-SG (manufactured by Ciba Geigy Co., Ltd.) was added and stirred sufficiently to dissolve completely to obtain black colorant compositions of Examples 7 to 11, respectively. It was.
これらの着色剤組成物について、前記消去性試験をした結果、実施例７〜１１はいずれも評価点が４であった。従って、実施例１のポリエチレングリコールとともに、各種の水溶性樹脂について同様の消去性向上の傾向が認められた。因みに、水溶性樹脂を添加しない以外同条件の染料水溶液について、同様の消去性試験をした結果、評価点はいずれも３点であった。また、その他の水溶性樹脂としてカチオン化デンプン、ポリアリルアミンを含む着色剤組成物についても同様に消去性試験をした結果、評価点は３〜４の間であり、消去性はやや低い傾向を示した。その結果、水溶性樹脂の中でも、特に、合成多価アルコール系、カルボン酸（塩）系、スルホン酸（塩）系水溶性樹脂が最適であることを見出した。 As a result of the erasability test on these colorant compositions, Examples 7 to 11 all had an evaluation score of 4. Accordingly, the same tendency to improve erasability was observed for various water-soluble resins together with the polyethylene glycol of Example 1. Incidentally, as a result of the same erasability test on the dye aqueous solution under the same conditions except that no water-soluble resin was added, the evaluation score was 3 points. In addition, as a result of the same erasability test for colorant compositions containing cationized starch and polyallylamine as other water-soluble resins, the evaluation score is between 3 and 4, and the erasability tends to be slightly low. It was. As a result, it has been found that, among water-soluble resins, synthetic polyhydric alcohol, carboxylic acid (salt), and sulfonic acid (salt) water-soluble resins are most suitable.
（実施例１２〜１５）
次に、染料以外は実施例１と同条件下で黒色の着色剤組成物を得た。すなわち、イオン交換水５０ｍｌにポリエチレングリコール（平均分子量３０００）を２０ｇを溶解し、室温で攪拌しながら、商品名 C.I.番号 A.Bk.2（商品名
Water Black R-455）、C.I.番号
A.Bk.119（商品名 OpalBlack new conc 保土谷社製）、C.I.番号 A.R.87（商品名 エオシン）、C.I.番号 A.B.9（商品名
WaterBlue #9）の各酸性染料を２．０ｇを添加して十分攪拌し、完全に溶解させて実施例１２〜１５の黒色の着色剤組成物を得た。
(Examples 12 to 15)
Next, a black colorant composition was obtained under the same conditions as in Example 1 except for the dye. That is, 20 g of polyethylene glycol (average molecular weight 3000) is dissolved in 50 ml of ion-exchanged water and stirred at room temperature with the trade name CI number A.Bk.2 (trade name)
Water Black R-455), CI number
A.Bk.119 (trade name OpalBlack new conc made by Hodogaya), CI number AR87 (trade name Eosin), CI number AB9 (trade name)
2.0 g of each acid dye of WaterBlue # 9) was added and sufficiently stirred and completely dissolved to obtain black colorant compositions of Examples 12 to 15.
これらの着色剤組成物について、前記消去性試験をした結果、実施例１２〜１５はいずれも評価点が４であった。特に実施例１２は評価点が５であった。一方、C.I.番号 D.Bk.19（商品名
Kayarus Black G conc、日本化薬社製）、C.I.番号 D.R.225（商品名 Kayarus Light Red F5G、日本化薬社製）の直接染料はいずれも評価点が１であり、評価点が２である同染料水溶液よりも更に消去性は低下した。また、C.I.番号 B.R.1（商品名 ローダミン６ＧＣＰ）、C.I.番号 B.B.116（商品名
Kayaacryl Blue BGL）の塩基性染料も評価点が３であった。
As a result of the erasability test on these colorant compositions, Examples 12 to 15 all had an evaluation score of 4. Particularly, in Example 12, the evaluation score was 5. CI number D.Bk.19 (product name
Kayarus Black G conc (manufactured by Nippon Kayaku Co., Ltd.) and CI number DR225 (trade name Kayarus Light Red F5G, manufactured by Nippon Kayaku Co., Ltd.) both have a scoring score of 1 and a scoring score of 2. The erasability declined further than the aqueous solution. Also, CI number BR1 (product name Rhodamine 6GCP), CI number BB116 (product name
The basic dye of Kayaacryl Blue BGL) also had a score of 3.
これらの結果から、直接染料では、水溶性樹脂を添加することにより逆に消去性が悪くなる傾向にある。これは直接染料は直接セルロース繊維に染着するアニオン性の染料であって直接性と呼ばれる性質を有することに起因すると考えられる。すなわち、木綿に対する染着機構はファン・デル・ワールス力による結合や、染料分子中のアミノ基、水酸基、π電子系がセルロースの水酸基との間で行なう水素結合が考えられている。そして、ポリエチレングリコールを添加することにより、染料溶液の表面張力が下がり、繊維への拡散が促進させるため、会合などの現象がなければ、繊維に対する汚染力が増大するためだと考えられる。塩基性染料では、目立った消去性の向上は見られない。これに対して、酸性染料では、反応性染料と同程度の消去性の向上がみられた。これは、反応性染料の染料部は酸性染料であることから消去性向上の要因も反応性染料と同様の要因だと思われる。 From these results, direct dyes tend to deteriorate erasability by adding a water-soluble resin. This is considered to be due to the fact that the direct dye is an anionic dye that is directly dyed on cellulose fibers and has a property called directity. In other words, the dyeing mechanism for cotton is considered to be a bond by van der Waals force, or a hydrogen bond formed between an amino group, a hydroxyl group, and a π-electron system in the dye molecule with a hydroxyl group of cellulose. The addition of polyethylene glycol lowers the surface tension of the dye solution and promotes diffusion into the fiber. This is thought to be due to an increase in the staining power to the fiber if there is no association phenomenon. With basic dyes, there is no noticeable improvement in erasability. In contrast, the acid dye exhibited the same level of erasability improvement as the reactive dye. This seems to be because the dye part of the reactive dye is an acid dye, so that the erasability improvement factor is also the same factor as the reactive dye.
（実施例１６〜１９及び比較例６）
ポリエチレングリコールの平均分子量をそれぞれ４００、６００、５０００、７５００とした以外は、それぞれ実施例１、２、３、４と同条件で実施例１６〜１９の着色剤組成物を得た。また比較のため、ポリエチレングリコールの平均分子量をそれぞれ３００、８０００とした以外は実施例１と同条件で比較例６、７の着色剤組成物を得た。
(Examples 16 to 19 and Comparative Example 6)
The colorant compositions of Examples 16 to 19 were obtained under the same conditions as in Examples 1, 2, 3, and 4 except that the average molecular weights of polyethylene glycol were 400, 600, 5000, and 7500, respectively. For comparison, colorant compositions of Comparative Examples 6 and 7 were obtained under the same conditions as in Example 1 except that the average molecular weights of polyethylene glycol were 300 and 8000, respectively.
これらの着色剤組成物について、実施例１と同条件下で消去性試験を行った。その結果、ポリエチレングリコールの平均分子量３００とした場合は、消去性試験の評価点が３、ポリエチレングリコールの平均分子量８０００とした場合は、その水溶液の粘性が高くなり、取り扱い面で好ましくなかった。ポリエチレングリコールの平均分子量を４００とした場合は、消去性試験の評価点は４となり、特に平均分子量を６００、５０００、７５００とした場合は、いずれも評価点は５となって良好であった。なお、ポリエチレングリコールの平均分子量を３００とした場合に消去性が低下したのは、３００以下の場合、水溶性樹脂の平均分子量が低いため、着色剤がにじみやすくなり、また染料を取り込む樹脂の分子の長さも短いため、樹脂に取り込まれた染料の見かけ上の分子の長さも短く、繊維中に入り込みやすくなり、消去性に悪影響を及ぼすと考えられる。これらの結果、望ましいポリエチレングリコールの平均分子量は、少なくとも４００、好ましくは６００〜７５００が最適である。 These colorant compositions were subjected to an erasability test under the same conditions as in Example 1. As a result, when the average molecular weight of polyethylene glycol was 300, the evaluation score of the erasability test was 3, and when the average molecular weight of polyethylene glycol was 8000, the viscosity of the aqueous solution was high, which was not preferable in terms of handling. When the average molecular weight of polyethylene glycol was 400, the evaluation score of the erasability test was 4, and particularly when the average molecular weight was 600, 5000, and 7500, the evaluation score was 5 and all were good. In addition, when the average molecular weight of polyethylene glycol is 300, the erasability is lowered when the average molecular weight is 300 or less, since the average molecular weight of the water-soluble resin is low, the colorant is likely to bleed, and the molecule of the resin that takes in the dye. Therefore, the apparent molecular length of the dye incorporated in the resin is also short, and it is easy to enter the fiber, which is considered to adversely affect the erasability. As a result, the average molecular weight of the desired polyethylene glycol is optimally at least 400, preferably 600-7500.
（各種繊維に対する消去性試験）
次に、ＪＩＳ交織布（綿、ナイロン、ビニロン、アセテート、ウール、レーヨン、アクリル、絹、ポリエステル）を、１０分間、実施例１、２、３、４、１１、１２、１３、１４の着色剤組成物に浸漬し、当該着色剤組成物を吸収させた。これを室温で指触乾燥するまで放置した。乾燥後、洗濯機で合成洗剤を使用（０．２％になるように調節）して２５度で１５分間洗濯を行い、１５分間水洗いした。乾燥後、目視にてその残りを前記試験と同様に５段階で評価した。また洗濯時にＪＩＳ交織布を同時に洗濯し、洗濯中の他布への汚染も評価した。
以上の試験によって評価した結果、絹及び一部のレーヨンを除いて評価点は４〜５であり、消去性は良好であった。また、実施例１、２、３、４、１１、１２、１３、１４の着色剤組成物において水溶性樹脂を含まない染料水溶液についても比較のため試験した結果、繊維によっては差異があるが、１〜３の評価点になった。このことから、上記染料に水溶性樹脂を加えることにより、洗濯により消去性が実現することが認められた。また、汚染も絹の一部を除いて汚染されなかった。
(Erasability test for various fibers)
Next, JIS union cloth (cotton, nylon, vinylon, acetate, wool, rayon, acrylic, silk, polyester) is used for 10 minutes for the coloring agents of Examples 1, 2, 3, 4, 11, 12, 13, and 14. The colorant composition was absorbed by being immersed in the composition. This was left to dry to the touch at room temperature. After drying, a synthetic detergent was used in a washing machine (adjusted so as to be 0.2%), and washing was performed at 25 degrees for 15 minutes, followed by washing with water for 15 minutes. After drying, the remainder was visually evaluated in five stages in the same manner as in the above test. In addition, JIS union cloth was washed at the same time as washing, and the contamination of other cloths during washing was also evaluated.
As a result of evaluation by the above test, the evaluation score was 4 to 5 except silk and some rayons, and the erasability was good. Moreover, as a result of testing for comparison with dye aqueous solutions not containing a water-soluble resin in the colorant compositions of Examples 1, 2, 3, 4, 11, 12, 13, and 14, there are differences depending on the fibers. The evaluation score was 1-3. From this, it was confirmed that erasability was realized by washing by adding a water-soluble resin to the dye. Also, the contamination was not contaminated except for some silk.
墨汁、絵具、マーキングペン用インキ等として用いることができ、布、不織布などの繊維集合体に付着した場合に水洗などにより簡単に消去できる。
It can be used as ink for ink, paints, marking pens, etc., and can be easily erased by washing with water when adhering to a fiber assembly such as cloth or nonwoven fabric.
Claims (10)
前記直染性の低い染料が、反応性染料又は酸性染料であり、
前記水溶性樹脂が、合成多価アルコール系、カルボン酸又はその塩、及びスルホン酸又はその塩)から選ばれる水溶性樹脂であることを特徴とする消去性マーキングペン用インキ組成物。 Contains dyes with low direct dyeability, water-soluble resins and water,
The dye having low direct dyeability is a reactive dye or an acid dye,
An ink composition for an erasable marking pen, wherein the water-soluble resin is a water-soluble resin selected from a synthetic polyhydric alcohol, a carboxylic acid or a salt thereof, and a sulfonic acid or a salt thereof.
The low direct dye is a reactive dye of dichlorotriazine type, monochlorotriazine type, vinylsulfone type, chloropyrimidine type, dichloroquinoxazine type, bifunctional group type of monochlorotriazine and vinylsulfone. The ink composition for erasable marking pens according to any one of claims 1 to 7.