JP2006249041A - Antifungal and antibacterial composition, coating of the same and film of the same - Google Patents
Antifungal and antibacterial composition, coating of the same and film of the same Download PDFInfo
- Publication number
- JP2006249041A JP2006249041A JP2005071174A JP2005071174A JP2006249041A JP 2006249041 A JP2006249041 A JP 2006249041A JP 2005071174 A JP2005071174 A JP 2005071174A JP 2005071174 A JP2005071174 A JP 2005071174A JP 2006249041 A JP2006249041 A JP 2006249041A
- Authority
- JP
- Japan
- Prior art keywords
- antifungal
- antibacterial
- same
- inorganic
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
この発明は、無機系材粉末と無機銅粉末(純銅粉末)を混合し、銅イオンにより防カビ、殺菌を目的とした防カビ及び抗菌組成物及び防カビ抗菌塗料並びに防カビ、抗菌皮膜に関する。 The present invention relates to an antifungal and antibacterial composition, an antibacterial antibacterial coating, an antifungal antibacterial coating, an antibacterial coating and an antibacterial coating, which are prepared by mixing inorganic material powder and inorganic copper powder (pure copper powder).
従来防カビ、抗菌塗料としては、溶剤系、アクリル系などの樹脂に殺菌作用のある薬剤及び殺虫剤を混ぜた物を塗布していた。 Conventionally, as antifungal and antibacterial paints, a mixture of a solvent-based resin, an acrylic resin, or the like with a sterilizing agent and an insecticide is applied.
また無機系の塗膜形成組成物と、銀、銅、亜鉛等の抗菌性金属及び/又はその化合物を含有した無機物とを含有する無機系コーティング剤が提案され、プールの表面に塗布されていた。
従来使用されている殺菌塗料は、溶剤系、アクリル系などの樹脂に殺菌作用の薬剤及び殺虫剤を混ぜ、問題箇所に塗る方法が採用されていた。然し乍ら、この方法では薬剤効果が短期間で無くなり、また溶剤及び薬剤の臭いがして、食品工場などでは使用できない問題点があった。 Conventionally used sterilizing paints employ a method in which a solvent-based resin, an acrylic-based resin, and the like are mixed with a sterilizing agent and an insecticide and applied to a problem area. However, this method has a problem that the drug effect disappears in a short period of time, and the solvent and the drug smell and cannot be used in food factories.
前記公知発明においても、エポキシ、アクリル、ポリエステルなどが塗膜形成組成物として使用され、前記従来の問題点を完全に是正することはできないものと推定される。 Also in the known invention, it is presumed that epoxy, acrylic, polyester and the like are used as a film-forming composition, and the conventional problems cannot be completely corrected.
前記のように、無臭で、塗膜強度良好で、人体に悪影響なく、しかも長期に亘り有効な防カビ、抗菌組成物塗料はなく、その開発が望まれていた。 As described above, there is no anti-mold and anti-bacterial composition paint that is odorless, has good coating strength, does not adversely affect the human body, and is effective for a long period of time.
然るにこの発明は、塗膜性のよい無機系材粉末と、無機銅粉末とを混合することにより、無臭、塗膜性良好で、しかも防カビ、抗菌良好な組成物を得て、前記従来の問題点を解決したのである。 However, according to the present invention, an inorganic material powder having a good coating property and an inorganic copper powder are mixed to obtain a odorless, good coating property, antifungal and antibacterial composition. It solved the problem.
即ちこの発明は、無機系材粉末80%〜97%(質量)と、無機銅粉末20%〜3%(質量)を混合したことを特徴とする防カビ及び抗菌組成物であり、無機系材粉末をポルトランドセメントを主材とし、これに親和性のある無機材粉末を混合したものであり、無機銅を、高純度銅としたものである。 That is, this invention is an antifungal and antibacterial composition characterized in that inorganic material powder 80% to 97% (mass) and inorganic copper powder 20% to 3% (mass) are mixed. The powder is made of Portland cement as a main material and mixed with an inorganic material powder having affinity for this, and the inorganic copper is made of high purity copper.
次に他の発明は、請求項1記載の組成物75%〜50%(質量)に、水25%〜50%(質量)を混合したことを特徴とする防カビ及び抗菌塗料である。また他の発明は、請求項2記載の塗料を、0.2kg/m2〜1.5kg/m2の薄層にしたことを特徴とする防カビ、抗菌皮膜である。 Next, another invention is an antifungal and antibacterial paint characterized in that 25% to 50% (mass) of water is mixed with 75% to 50% (mass) of the composition of claim 1. Another invention is an antifungal and antibacterial film characterized in that the paint according to claim 2 is made into a thin layer of 0.2 kg / m 2 to 1.5 kg / m 2 .
前記発明において、無機銅粉末は、純銅(例えば不純物0.001以下)3%以下では、効果の低下が認められ、20%以上添加しても効果の向上は認められないので、添加量を3%〜20%(質量)とした。 In the above invention, the inorganic copper powder has a decrease in effect when it is 3% or less of pure copper (for example, impurities of 0.001 or less). % To 20% (mass).
前記発明において、使用量を0.2kg/m2以下にすると、塗着面への付着強度の低下又は防カビ、抗菌能の低下のおそれがあり、1.5kg/m2で十分の効力を奏し、これ以上使用の必要性がない。 In the invention, when the amount below 0.2 kg / m 2, reduction or antifungal adhesion strength to the coating surface, there is a risk of decrease in antimicrobial capacity, sufficient efficacy at 1.5 kg / m 2 There is no need for further use.
前記において、0.2kg/m2であっても、無機銅の混合量が多い場合には、防カビ、抗菌効果はあるが、塗膜強度の低下の関係で下限を0.2kg/m2を低限とした。例えば、防カビ、抗菌効果は、1m2当り6gの無機銅が散在しておれば、目的を達成するものと認められた。 In the above, even if it is 0.2 kg / m 2 , when the amount of inorganic copper mixed is large, there are antifungal and antibacterial effects, but the lower limit is 0.2 kg / m 2 due to the decrease in coating film strength. Was made the lowest limit. For example, antifungal, antibacterial effect, inorganic copper 1 m 2 per 6g is if I scattered, was recognized as to achieve the object.
この発明における無機系材粉末としては、セメントを主材とし、これに炭酸カルシウムその他無機粉末を混合して得たもので、無害、無臭であって、造膜性の強い材料であれば使用することができる。例えばセメントは、通常ポルトランドセメントを使用する。 The inorganic material powder in the present invention is obtained by mixing a cement as a main material with calcium carbonate or other inorganic powder, and it is harmless, odorless, and has a strong film forming property. be able to. For example, Portland cement is usually used as the cement.
前記ポルトランドセメントの成分は、SiO220〜25%、Al2O34〜6%、Fe2O32〜4%、CaO62〜66%、MgO1〜2%、SO31.5〜3.5%とされている。 Component of the Portland cement, SiO 2 20~25%, Al 2 O 3 4~6%, Fe 2 O 3 2~4%, CaO62~66%, MgO1~2%, SO 3 1.5~3. 5%.
製造に際しては、石灰石、粘土、珪石、酸化鉄を微粉砕混合し、ロータリーキルンなどで最高1450℃に焼成し、1200℃まで徐冷した後、急冷してクリンカーを作り、これに石膏3〜4%を加えて微粉砕すれば、前記ポルトランドセメント製品ができる。 In production, limestone, clay, silica, and iron oxide are finely pulverized and mixed, calcined to a maximum of 1450 ° C in a rotary kiln, etc., gradually cooled to 1200 ° C, then rapidly cooled to make a clinker, and gypsum 3-4% The above-mentioned Portland cement product can be obtained by adding and pulverizing.
従って前記発明においては、セメント成分中の無機物割合を増加し、又は割合を多少変化を与える為に、前記成分中の1つ又は複数を少量添加(無機粉末として)することになる。 Therefore, in the said invention, in order to increase the ratio of the inorganic substance in a cement component, or to give a some change in a ratio, one or more in the said component is added a small amount (as inorganic powder).
例えば、石灰石、珪石、石膏などの粉末を添加することにより、使途に最適の組成物を得ることができる。 For example, by adding powders such as limestone, silica stone, and gypsum, an optimal composition for use can be obtained.
この発明によれば、銅イオンの作用により、防カビ、殺菌を行うことができると共に、無機系材料の混合により臭いが全く無くなり、食品工場を始めとし、貯水槽内部など、今まで臭いの為に採用されなかった場所の防カビ、抗菌に使用し得る効果がある。 According to this invention, it is possible to prevent mold and sterilization by the action of copper ions, and the odor is completely eliminated by mixing inorganic materials. It has an effect that can be used for antifungal and antibacterial in places not adopted.
また造膜性に優れている為に、薄く塗布できて十分の効果を奏すると共に、耐久性に富み、効力も持続するなどの諸効果がある。 Moreover, since it is excellent in film-forming property, it can be applied thinly and has a sufficient effect, and has various effects such as high durability and long-lasting efficacy.
この発明はポルトランドセメントに、石灰石粉末、珪石粉末及び純銅粉末夫々の適量を混合機に入れて均一に混合して、この発明の組成物を得る。これを定量宛(例えば50kg)包装して製品にする。 In the present invention, Portland cement is mixed with appropriate amounts of limestone powder, silica powder and pure copper powder in a mixer to obtain the composition of the present invention. This is packed into a fixed quantity (for example, 50 kg) and made into a product.
次に前記製品に対し、適量の水を加入して混練すれば、この発明の塗料ができる。そこでこの塗料を例えば水槽の内面へ塗布すれば、防カビ、殺菌水槽ができる。 Next, if a suitable amount of water is added to the product and kneaded, the paint of the present invention can be obtained. Therefore, if this paint is applied to the inner surface of the water tank, for example, a mold prevention and sterilization water tank can be formed.
この発明の組成物の実施例について説明すると、ポルトランドセメント90%に、石灰石粉末3%と、珪石粉末3%及び純銅粉末(異物0.001%以下)4%を混入し、均一に撹拌すれば、この発明の組成物ができる。従ってこれを定量(例えば30kg)宛包装すれば、製品となる。 An example of the composition of the present invention will be described. When 90% of Portland cement is mixed with 3% limestone powder, 3% silica powder and 4% pure copper powder (foreign matter 0.001% or less), and stirred uniformly. The composition of this invention is made. Therefore, if this is packaged for a fixed amount (for example, 30 kg), it becomes a product.
前記実施例1で得た製品10kgに、水1.5リットル〜4.5リットルを加えて混練すれば、この発明の塗料ができる。 The paint of the present invention can be obtained by adding 1.5 liters to 4.5 liters of water to 10 kg of the product obtained in Example 1 and kneading.
前記実施例において、使用水分量に幅があるのは、環境条件(例えば温度、湿度、日照条件など)に合った水分量とする為である。また使用場所により粘度を変える場合もあるので、使用時の条件に合致した水分量を用いるからである。 In the said Example, there exists a width | variety in the amount of used water | moisture contents in order to set it as the amount of water | moisture contents suitable for environmental conditions (for example, temperature, humidity, sunlight conditions, etc.). Moreover, since the viscosity may be changed depending on the place of use, the amount of water that matches the conditions during use is used.
前記塗料を水槽の防カビ及び殺菌に使用する場合には、前記水槽の内壁へ、1kg/m2の割合に塗布すれば、防カビ、殺菌機能を有する水槽ができる。前記水槽には、防カビ、殺菌作用があるので、安心して使用することができる。 When the paint is used for mold prevention and sterilization of the water tank, if it is applied to the inner wall of the water tank at a rate of 1 kg / m 2 , a water tank having fungicide and sterilization functions can be obtained. Since the water tank has fungicidal and bactericidal action, it can be used with peace of mind.
また水槽がコンクリート製の場合には、前記塗料と、壁面とが緊密に一体化し、剥落などのおそれはない。また銅が露出して防カビ、殺菌作用を奏するので、長年継続して使用することができる。 When the water tank is made of concrete, the paint and the wall surface are tightly integrated, and there is no fear of peeling off. Moreover, since copper exposes and has an antifungal and bactericidal action, it can be used continuously for many years.
またこの発明の塗料は、無害かつ無臭であるから、食品関係に用いる水槽であっても、安心して使用することができる。 Moreover, since the coating material of this invention is harmless and odorless, even if it is a water tank used for foodstuffs, it can be used safely.
Claims (5)