JP2006089369A - Optical glass - Google Patents
Optical glass Download PDFInfo
- Publication number
- JP2006089369A JP2006089369A JP2005243873A JP2005243873A JP2006089369A JP 2006089369 A JP2006089369 A JP 2006089369A JP 2005243873 A JP2005243873 A JP 2005243873A JP 2005243873 A JP2005243873 A JP 2005243873A JP 2006089369 A JP2006089369 A JP 2006089369A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- component
- optical glass
- mol
- optical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、高屈折率低分散性を有し、さらに低い転移温度(Tg)を有し、精密プレス成形に使用するガラスプリフォーム材、及び精密プレス成形に適した光学ガラスに関する。 The present invention relates to a glass preform material having high refractive index and low dispersibility, and having a low transition temperature (Tg), and used for precision press molding, and optical glass suitable for precision press molding.
近年、光学機器の小型軽量化が著しく進行している中で、光学機器の光学系を構成するレンズの枚数を減少させる目的でガラス製の非球面レンズが多く用いられるようになってきている。ガラス製の非球面レンズは、加熱軟化したガラスプリフォーム材を、高精度な成形面をもつ金型でプレス成形し、金型の高精度な成形面の形状をガラスプリフォーム材に転写して得る方法、すなわち、精密プレス成形によって製造されることが主流となっている。 In recent years, as optical devices are remarkably reduced in size and weight, glass aspherical lenses are often used for the purpose of reducing the number of lenses constituting the optical system of optical devices. An aspherical lens made of glass is produced by press-molding a heat-softened glass preform with a mold having a high-precision molding surface, and transferring the shape of the high-precision molding surface of the mold to the glass preform. The mainstream method is to obtain it, that is, manufactured by precision press molding.
精密プレス成形によって、ガラス成形品を得るにあたっては、加熱軟化させたガラスプリフォーム材を高温環境下でプレス成形することが必要であるので、この際使用する金型も高温に曝され、金型の成形面が酸化、侵食されたり、金型成形面の表面に設けられている離型膜が損傷したりして金型の高精度な成形面が維持できなくなることが多く、また、金型自体も損傷し易い。そのようになると、金型の交換、メンテナンスの回数が増加して、低コスト、大量生産を実現できなくなる。そこで、精密プレス成形に使用するガラス及び精密プレス成形に使用するガラスプリフォーム材のガラスは、上記損傷を抑制し、金型の高精度な成形面を長く維持し、かつ低い温度での精密プレス成形を可能にするという観点から、できるだけ低い転移温度(Tg)を有することが望まれている。現在、精密プレス成形に使用するガラスプリフォーム材のガラスの転移温度(Tg)が630℃を超えると精密プレス成形が困難となるため、転移温度(Tg)が630℃以下である高屈折率低分散性ガラスが求められている。また、失透が生じたガラスプリフォーム材を精密プレス成形しても失透は消失せず、失透を含むガラス成形品は、レンズ等の光学素子として使用することができないため、精密プレス成形に使用するガラスプリフォーム材のガラスは、耐失透性が優れたガラスであることが必要とされる。 In order to obtain a glass molded product by precision press molding, it is necessary to press-mold a glass preform material that has been heat-softened in a high-temperature environment. In many cases, the molding surface of the mold is oxidized or eroded, or the mold release film provided on the surface of the mold molding surface is damaged, so that it is impossible to maintain a high-precision molding surface of the mold. It is easy to damage itself. In such a case, the number of times of mold replacement and maintenance increases, and low cost and mass production cannot be realized. Therefore, the glass used for precision press molding and the glass preform material glass used for precision press molding suppress the above-mentioned damage, maintain a high-precision molding surface of the mold for a long time, and perform precision press at a low temperature. From the viewpoint of enabling molding, it is desired to have a transition temperature (Tg) as low as possible. At present, when the glass transition temperature (Tg) of the glass preform material used for precision press molding exceeds 630 ° C., precision press molding becomes difficult, so the transition temperature (Tg) is 630 ° C. or less and the high refractive index is low. There is a need for dispersible glass. In addition, even when precision preformed glass preform material that has been devitrified, devitrification does not disappear, and glass molded products containing devitrification cannot be used as optical elements such as lenses. The glass of the glass preform material used for is required to have excellent devitrification resistance.
非球面レンズに用いられる光学ガラスは、種々の光学定数(屈折率(nd)及びアッベ数(νd))を有するものが求められているが、なかでも、近年、光学系の焦点距離の短縮、小型化の為、高屈折率低分散性を有するものが求められている。特に光学設計上、屈折率(nd)が1.9以上、アッベ数(νd)が25以上を有する高屈折率低分散性光学ガラスが強く求められている。 Optical glasses used for aspherical lenses are required to have various optical constants (refractive index (nd) and Abbe number (νd)). In particular, recently, the focal length of optical systems has been shortened. In order to reduce the size, a material having high refractive index and low dispersion is required. In particular, from the viewpoint of optical design, there is a strong demand for a high-refractive index, low-dispersion optical glass having a refractive index (nd) of 1.9 or higher and an Abbe number (νd) of 25 or higher.
そのため、従来から高屈折率低分散ガラスを得る為に種々の提案がされている。例えば、特開平9−278480(特許文献1)にはB2O3−GeO2−La2O3−Nb2O5−ZrO2−TiO2系の光学ガラス、特開昭52−155614(特許文献2)には、B2O3−La2O3−Gd2O5−WO3−ZrO2系の光学ガラスが、特開昭53−4023(特許文献3)には、B2O3−La2O3−HfO2系の光学ガラスが開示されているが、これらの公報に具体的に開示されているガラスは、転移温度を下げ、また、ガラスの溶融性を良くするアルカリ成分の含有量が0.5%までと少ないため、転移温度(Tg)が高くなり、精密プレス成形が困難になり、また、ガラスの溶融性が悪くなる。 Therefore, various proposals have heretofore been made in order to obtain a high refractive index and low dispersion glass. For example, Japanese Patent Application Laid-Open No. 9-278480 (Patent Document 1) discloses an optical glass based on B 2 O 3 —GeO 2 —La 2 O 3 —Nb 2 O 5 —ZrO 2 —TiO 2 , Japanese Patent Application Laid-Open No. 52-155614 (Patent Document). the literature 2), B 2 O 3 -La 2 O 3 -Gd 2 O 5 -WO 3 -ZrO 2 system of the optical glass, the JP 53-4023 (Patent Document 3), B 2 O 3 -la 2 is O 3 -HfO 2 system of the optical glass is disclosed, the glass that is specifically disclosed in these publications, lowering the transition temperature, also the alkaline component to improve the melting property of the glass Since the content is as low as 0.5%, the transition temperature (Tg) becomes high, precision press molding becomes difficult, and the meltability of the glass becomes poor.
特開2002−362939(特許文献4)には、B2O3−CaO−La2O3−Nb2O3−TiO2−ZrO2系の光学ガラスが開示されているが、この公報に具体的に開示されているガラスは、低屈折率成分であるB2O3とSiO2の合計含有量が19〜28%と多く、上記所望の光学定数を満たしていない。 JP-A-2002-362939 (Patent Document 4) discloses B 2 O 3 —CaO—La 2 O 3 —Nb 2 O 3 —TiO 2 —ZrO 2 -based optical glass. The glass disclosed here has a high total content of B 2 O 3 and SiO 2 as low refractive index components of 19 to 28%, and does not satisfy the desired optical constant.
特開2000−128570(特許文献5)には、SiO2−B2O3−CaO−La2O3−TiO2系の光学ガラスが、特開2000−159537(特許文献6)には、SiO2−B2O3−ZrO2−La2O3−TiO2系開示されている。これらの公報に記載の光学ガラスは屈折率を上げるためにTiO2を多量に含有させている。しかしTiO2は多量に含有させると透過率を著しく悪化させ、ガラスを着色させるという不利益がある。 JP-A-2000-128570 (Patent Document 5), the optical glass of SiO 2 -B 2 O 3 -CaO- La 2 O 3 -TiO2 system, Japanese 2000-159537 (Patent Document 6), SiO 2 -B 2 O 3 -ZrO 2 -La 2 O 3 is -TiO 2 system disclosed. The optical glasses described in these publications contain a large amount of TiO 2 in order to increase the refractive index. However, when TiO 2 is contained in a large amount, the transmittance is remarkably deteriorated and the glass is colored.
特開昭52−63211(特許文献7)には、B2O3−La2O3−Y2O3−TiO2系の光学ガラスが開示されているが、転移温度を下げ、また、ガラスの溶融性を良くする成分である、アルカリ成分を含有しておらず、転移温度(Tg)が高くなり、精密プレス成形が困難になる。 Japanese Patent Application Laid-Open No. 52-63221 (Patent Document 7) discloses a B 2 O 3 —La 2 O 3 —Y 2 O 3 —TiO 2 type optical glass. It does not contain an alkali component, which is a component that improves the meltability of the resin, and the transition temperature (Tg) becomes high, making precision press molding difficult.
特開昭54−103411(特許文献8)には、B2O3−La2O3−Ta2O5系の光学ガラスが開示されているが、転移温度を下げ、また、ガラスの溶融性を良くする成分であるアルカリ成分を含有しておらず、転移温度(Tg)が高くなり、精密プレス成形が困難になる。 Japanese Patent Application Laid-Open No. 54-103411 (Patent Document 8) discloses a B 2 O 3 —La 2 O 3 —Ta 2 O 5 optical glass. However, the transition temperature is lowered, and the melting property of the glass is also disclosed. It does not contain an alkali component that improves the viscosity, and the transition temperature (Tg) increases, making precision press molding difficult.
特開2004−175632(特許文献9)にはSiO2−B2O3−BaO−La2O3−TiO2系の光学ガラスが開示されているが、この公報に具体的に開示されているガラスは、TiO2を多量に含有しているが、TiO2は多量に含有させると透過率を著しく悪化させ、ガラスを着色させるという不利益がある。
従来の低分散性光学ガラスでは、転移温度(Tg)が高いか又は転移温度(Tg)は低くても、近年強く求められている前記特定範囲の光学定数を有することはできない。また、Tgを下げ得る成分、例えばLi2O等を増加させると耐失透性の低下等を生じ、光学ガラスの安定性を損なうこととなる。一方、従来の技術においては、高屈折率を追い求めるためにTiO2を多量に含有させる傾向がある、しかしその結果光学ガラスの着色性が悪化し、実用性にかけるものとなってしまっていた。本発明は、前記従来の技術に記載した光学ガラスの諸欠点を総合的に解消し、TiO2を多量に含有させること無く前記特定範囲の光学定数を有し、かつ、転移温度(Tg)が低く、精密プレス成形に使用できるガラスプリフォーム材及び精密プレス成形に適し、安定性に優れた光学ガラスを提供することにある。 Conventional low-dispersion optical glasses cannot have optical constants in the specific range that have been strongly demanded in recent years, even if the transition temperature (Tg) is high or the transition temperature (Tg) is low. Also, components that may lower the Tg, for example, increasing the Li 2 O or the like cause devitrification resistance decreases and the like, and thus compromising the stability of optical glass. On the other hand, in the prior art, there is a tendency to contain a large amount of TiO 2 in order to pursue a high refractive index. However, as a result, the colorability of the optical glass is deteriorated, which has been put to practical use. The present invention comprehensively eliminates the disadvantages of the optical glass described in the prior art, has an optical constant in the specific range without containing a large amount of TiO 2 , and has a transition temperature (Tg) of An object of the present invention is to provide a glass preform material that is low and can be used for precision press molding and an optical glass that is suitable for precision press molding and excellent in stability.
本発明者は、上記課題を解決するために、鋭意試験研究を重ねた結果、ガラス組成物においてSiO2、B2O3及びGeO2からなる群より選択される1種又は2種以上、並びにLa2O3、Nb2O5、Ta2O5、Li2O及びZnOを含有させることにより、さらにZnO及びLi2Oの比、及び/又はZnO及びLi2O含有量とLa2O3含有量との比を所定の範囲に規定することにより、前記特定範囲の光学定数を有しかつ精密プレス成形が可能な低い転移温度(Tg)を有し、かつ安定性に優れた精密プレス成形に使用するガラスプリフォーム材、及び精密プレス成形に適した光学ガラスが得られることを見出した。 In order to solve the above-mentioned problems, the present inventor has conducted intensive test studies, and as a result, one or more selected from the group consisting of SiO 2 , B 2 O 3 and GeO 2 in the glass composition, and By including La 2 O 3 , Nb 2 O 5 , Ta 2 O 5 , Li 2 O and ZnO, the ratio of ZnO and Li 2 O and / or the ZnO and Li 2 O content and La 2 O 3 are further increased. By regulating the ratio to the content within a predetermined range, precision press molding having an optical constant in the specific range, a low transition temperature (Tg) capable of precision press molding, and excellent stability. The present inventors have found that an optical glass suitable for glass preform material and precision press molding can be obtained.
本発明の第1の構成は、屈折率(nd)が1.9以上、アッベ数(νd)が25以上を有し、SiO2、B2O3及びGeO2からなる群より選択される1種又は2種以上、並びにLa2O3、Nb2O5、Ta2O5、Li2O及びZnOを含有する光学ガラスである。 The first configuration of the present invention has a refractive index (nd) of 1.9 or more, an Abbe number (νd) of 25 or more, and is selected from the group consisting of SiO 2 , B 2 O 3 and GeO 2. It is an optical glass containing seeds or two or more kinds, and La 2 O 3 , Nb 2 O 5 , Ta 2 O 5 , Li 2 O and ZnO.
本発明の第2の構成は、液相温度が1150℃以下である前記構成1の光学ガラスである。 The second configuration of the present invention is the optical glass of the above configuration 1 having a liquidus temperature of 1150 ° C. or lower.
本発明の第3の構成は、液相温度における粘度(dPa・s)の対数logηが0.3以上である前記構成1及び2の光学ガラスである。 The third constitution of the present invention is the optical glass of the constitutions 1 and 2, wherein the logarithm log η of the viscosity (dPa · s) at the liquidus temperature is 0.3 or more.
本発明の第4の構成は、ガラス転移温度(Tg)が630℃以下である前記構成1〜3の光学ガラスである。 The 4th structure of this invention is the optical glass of the said structures 1-3 whose glass transition temperature (Tg) is 630 degrees C or less.
本発明の第5の構成は、質量%で表したB2O3、La2O3、Nb2O5、Ta2O5、GeO2及びLi2Oの各成分の合計量が、76%以上である前記構成1〜4の光学ガラスである。 In the fifth configuration of the present invention, the total amount of each component of B 2 O 3 , La 2 O 3 , Nb 2 O 5 , Ta 2 O 5 , GeO 2 and Li 2 O expressed by mass% is 76%. It is the optical glass of the said structures 1-4 which is the above.
本発明の第6の構成は、質量%で表したLi2O含有量に対するZnO含有量が1.5〜7.5である前記構成1〜5の光学ガラスである。 The sixth structure of the present invention, ZnO content with respect to the content of Li 2 O, expressed in mass% is the configuration 1-5 of the optical glass is 1.5 to 7.5.
本発明の第7の構成は、質量%で表したLa2O3含有量に対するZnO及びLi2O含有量の和の値が0.1〜0.5の範囲である前記構成1〜6の光学ガラスである。 In a seventh configuration of the present invention, the value of the sum of ZnO and Li 2 O content with respect to La 2 O 3 content expressed by mass% is in the range of 0.1 to 0.5. Optical glass.
本発明の第8の構成は、質量%で
B2O3 5〜15%
La2O3 20〜29%
Nb2O5 22〜30%
Ta2O5 4〜15%
Li2O 0.5%を超え6%まで、
GeO2 1〜20%、及び
ZnO 2〜10%
並びに
SiO2 0〜5.5%、及び/又は
Gd2O3 0〜8%、及び/又は
Y2O3 0〜8%、及び/又は
Yb2O3 0〜8%、及び/又は
TiO2 0〜5%未満、及び/又は
ZrO2 0〜10%、及び/又は
WO3 0〜7%、及び/又は
Bi2O3 0〜3%、及び/又は
RO 0〜15%
ただし、ROは、CaO、SrO及びBaOから選ばれる1種又は2種以上、及び/又は
Sb2O3 0〜1%
の酸化物換算組成の各成分を含有し、かつ上記酸化物の一部又は全部をフッ化物置換したFの合計量が、上記酸化物換算組成100質量部に対して0〜5質量部の範囲となる各成分を含有する前記構成1〜7の光学ガラスである。
Eighth aspect of the present invention, B 2 O 3 5~15% by mass%
La 2 O 3 20-29%
Nb 2 O 5 22-30%
Ta 2 O 5 4-15%
Li 2 O 0.5% to 6%,
GeO 2 1-20% and ZnO 2-10%
And SiO 2 0-5.5% and / or Gd 2 O 3 0-8% and / or Y 2 O 3 0-8% and / or Yb 2 O 3 0-8% and / or TiO 20 to less than 5% and / or ZrO 2 0 to 10% and / or WO 3 0 to 7% and / or Bi 2 O 3 0 to 3% and / or RO 0 to 15%
However, RO is, CaO, 1 kind or more selected from SrO and BaO, and / or Sb 2 O 3 0 to 1%
The total amount of F containing each component of the oxide equivalent composition and fluoride-substituted part or all of the oxide is in the range of 0 to 5 parts by mass with respect to 100 parts by mass of the oxide equivalent composition. It is the optical glass of the said structures 1-7 containing each component used as.
本発明の第9の構成は、mol%で
B2O3 10〜35%
La2O3 5〜20%
Nb2O5 8〜22%
Ta2O5 1〜10%
Li2O 1〜20%
GeO2 1〜34%
ZnO 3〜20%
及び
SiO2 0〜15%及び/又は
Gd2O3 0〜5%及び/又は
Y2O3 0〜5%及び/又は
Yb2O3 0〜5%及び/又は
TiO2 0〜10%及び/又は
ZrO2 0〜15%及び/又は
WO3 0〜5%及び/又は
RO 0〜30%
ただし、ROは、CaO、SrO及びBaOから選ばれる1種又は2種以上、及び/又はSb2O3 0〜1%
の酸化物換算組成の各成分を含有し、かつ酸化物換算組成の総モル数に対する上記酸化物の一部又は全部をフッ化物置換したFのモル数の比が0〜0.25となるように各成分を含有する光学ガラスである。
In the ninth aspect of the invention, B 2 O 3 10~35% by mol%
La 2 O 3 5-20%
Nb 2 O 5 8-22%
Ta 2 O 5 1-10%
Li 2 O 1-20%
GeO 2 1~34%
ZnO 3-20%
And SiO 2 0-15% and / or Gd 2 O 3 0-5% and / or Y 2 O 3 0-5% and / or Yb 2 O 3 0-5% and / or TiO 2 0-10% and / Or ZrO 2 0-15% and / or WO 3 0-5% and / or RO 0-30%
However, RO is, CaO, 1 kind or more selected from SrO and BaO, and / or Sb 2 O 3 0 to 1%
The ratio of the number of moles of F containing each component of the oxide conversion composition and fluoride-substituting a part or all of the oxide with respect to the total number of moles of the oxide conversion composition is 0 to 0.25. Is an optical glass containing each component.
本発明の第10の構成は、SiO2とB2O3の合計含有量が、質量%で5%以上かつ17%未満である前記構成1〜9の光学ガラスである。 Tenth aspect of the invention, the total content of SiO 2 and B 2 O 3 is the above configuration 1-9 of the optical glass is less than 5% or more and 17% by mass%.
本発明の第11の構成は、前記構成1〜10の光学ガラスからなる精密プレス成形用プリフォームである。 The eleventh configuration of the present invention is a precision press-molding preform made of the optical glass of the above configurations 1-10.
本発明の第12の構成は、前記構成11の精密プレス成形用プリフォームを精密プレス成形してなる光学製品である。 The twelfth configuration of the present invention is an optical product obtained by precision press-molding the precision press-molding preform of the above-described configuration 11.
本発明によれば、屈折率(nd)が1.9以上、アッベ数(νd)が25以上であり、かつ精密プレス成形が可能な低い630℃以下の転移温度(Tg)を有し、かつ安定性に優れた精密プレス成形に使用するガラスプリフォーム材、及び精密プレス成形に適した光学ガラスが得られる。 According to the present invention, the refractive index (nd) is 1.9 or more, the Abbe number (νd) is 25 or more, and has a low transition temperature (Tg) of 630 ° C. or less capable of precision press molding, and A glass preform material used for precision press molding excellent in stability and optical glass suitable for precision press molding can be obtained.
以下、本発明について詳細に説明する。 Hereinafter, the present invention will be described in detail.
本発明の光学ガラスに含有できる成分について説明する。以下、特に断らない限り各成分の含有率は質量%で表すものとする。 The components that can be contained in the optical glass of the present invention will be described. Hereinafter, unless otherwise specified, the content of each component is expressed in mass%.
上記組成のガラスにおいてSiO2成分は、本発明の光学ガラスにおいて、ガラスの粘度を高め、耐失透性を向上させるのに有効な成分であるが、その量が多すぎると転移温度(Tg)が高くなり、未熔解物が発生しやすくなる。また、低屈折率成分である為、所望の光学定数を満たすことができなくなる。 In the glass having the above composition, the SiO 2 component is an effective component for increasing the viscosity of the glass and improving the devitrification resistance in the optical glass of the present invention. If the amount is too large, the transition temperature (Tg) Becomes higher and undissolved material is likely to be generated. Moreover, since it is a low refractive index component, it becomes impossible to satisfy a desired optical constant.
従って、耐失透性を維持し、低い転移温度(Tg)を得やすくするためには、好ましくは5.5%、より好ましくは5%、最も好ましくは4%を上限として含有できる。 Therefore, in order to maintain devitrification resistance and easily obtain a low transition temperature (Tg), it is preferably 5.5%, more preferably 5%, and most preferably 4%.
SiO2成分は、原料として例えばSiO2等を使用してガラス組成物中に導入できる。 The SiO 2 component can be introduced into the glass composition using, for example, SiO 2 as a raw material.
B2O3成分は、本発明の光学ガラスにおいて、ガラス形成酸化物成分として欠かすことのできない成分である。しかし、その量が少なすぎると耐失透性が不十分となり、多すぎると化学的耐久性が悪くなる。従って、良好な化学的安定性を維持しやすくする為には、好ましくは5%、より好ましくは6%、最も好ましくは7%を下限とし、好ましくは15%、より好ましくは14.5%、最も好ましくは14%を上限として含有できる。 The B 2 O 3 component is an indispensable component as a glass-forming oxide component in the optical glass of the present invention. However, when the amount is too small, the devitrification resistance is insufficient, and when the amount is too large, the chemical durability is deteriorated. Therefore, in order to easily maintain good chemical stability, the lower limit is preferably 5%, more preferably 6%, most preferably 7%, preferably 15%, more preferably 14.5%, Most preferably, it can contain up to 14%.
B2O3成分は、原料として例えばH3BO3等を使用してガラス組成物中に導入できる。 The B 2 O 3 component can be introduced into the glass composition using, for example, H 3 BO 3 as a raw material.
本発明の光学ガラスにおいてはSiO2とB2O3の含有量の和が所定の範囲内であることが好ましい。この値が大きすぎると未熔解物を発生しやすく、また所望の光学定数の値を維持し難くなる。また小さすぎるとガラスの対失透性が不十分となるといった不利益を生じてしまう。従って、当該値は各成分の含有量を質量%で表した場合に、好ましくは5%、より好ましくは5.5%、最も好ましくは6%を下限とし、好ましくは17%未満、より好ましくは16.5%、最も好ましくは16%を上限とする。 In the optical glass of the present invention, the sum of the contents of SiO 2 and B 2 O 3 is preferably within a predetermined range. If this value is too large, undissolved products are likely to be generated, and it becomes difficult to maintain a desired optical constant value. On the other hand, if it is too small, there is a disadvantage that the anti-devitrification property of the glass becomes insufficient. Therefore, the value is preferably 5%, more preferably 5.5%, and most preferably 6% when the content of each component is expressed in mass%, preferably less than 17%, more preferably The upper limit is 16.5%, most preferably 16%.
La2O3成分は、ガラスの屈折率を高め、低分散化させるのに有効であり低分散性を有する本発明のガラスに欠かすことのできない成分である。しかし、その量が少なすぎるとガラスの光学定数の値を前記特定範囲内に維持し難く、多すぎると耐失透性が悪くなる。 The La 2 O 3 component is an essential component for the glass of the present invention, which is effective for increasing the refractive index of the glass and reducing the dispersion, and has low dispersibility. However, when the amount is too small, it is difficult to maintain the value of the optical constant of the glass within the specific range, and when it is too large, the devitrification resistance is deteriorated.
従って、上記効果を奏するために、好ましくは20%、より好ましくは21%、最も好ましくは22%を下限とし、好ましくは29%、より好ましくは28%、最も好ましくは27%を上限として含有することができる。La2O3成分は、原料として例えばLa2O3、La(NO3)3・xH2O、LaF3等を使用してガラス組成物中に導入できる。 Therefore, in order to achieve the above effect, it is preferably 20%, more preferably 21%, most preferably 22% as the lower limit, preferably 29%, more preferably 28%, most preferably 27% as the upper limit. be able to. La 2 O 3 component can be introduced for example as a material La 2 O 3, La (NO 3) 3 · xH 2 O, using LaF 3, etc. in the glass composition.
Nb2O5成分は、ガラスの屈折率を高め、本発明のガラスに欠かすことのできない成分である。しかし、その量が少なすぎるとガラスの光学定数の値を前記特定範囲内に維持し難く、多すぎるとガラスが着色し、透過率を悪化させる。 The Nb 2 O 5 component is a component that increases the refractive index of glass and is indispensable for the glass of the present invention. However, if the amount is too small, it is difficult to maintain the value of the optical constant of the glass within the specific range, and if it is too large, the glass is colored and the transmittance is deteriorated.
従って、本発明の光学ガラスにおける所望の光学定数を維持しつつ良好な透過率を維持しやすくするためには、22%を下限とし、好ましくは30%、より好ましくは29%、最も好ましくは28%を上限として含有することができる。 Therefore, in order to easily maintain good transmittance while maintaining the desired optical constant in the optical glass of the present invention, the lower limit is 22%, preferably 30%, more preferably 29%, and most preferably 28. % Can be contained as the upper limit.
Nb2O5成分は、原料として例えばNb2O5等を使用してガラス組成物中に導入きる。 The Nb 2 O 5 component can be introduced into the glass composition using, for example, Nb 2 O 5 as a raw material.
Ta2O5成分は、ガラスの屈折率を高め、対失透性を向上させるのに有効な成分である。しかし、その量が少なすぎるとガラスの光学定数の値を前記特定範囲内に維持し難く、その量が多すぎると、対失透性を悪化させ、未熔解物が発生しやすくなる。 The Ta 2 O 5 component is an effective component for increasing the refractive index of glass and improving anti-devitrification properties. However, if the amount is too small, it is difficult to maintain the value of the optical constant of the glass within the specific range. If the amount is too large, the anti-devitrification property is deteriorated and undissolved products are easily generated.
従って、上記効果を奏するために、好ましくは4%、より好ましくは5%、最も好ましくは6%を下限とし、好ましくは15%、より好ましくは14%、最も好ましくは13%を上限として含有することができる。Ta2O5成分は、原料として例えばTa2O5等を使用してガラス組成物中に導入できる。 Therefore, in order to achieve the above effect, the lower limit is preferably 4%, more preferably 5%, most preferably 6%, preferably 15%, more preferably 14%, and most preferably 13%. be able to. The Ta 2 O 5 component can be introduced into the glass composition using, for example, Ta 2 O 5 as a raw material.
GeO2成分は、ガラスの屈折率を高め、対失透性を向上させる効果があるが、その量が少なすぎるとガラスの光学定数の値を前記特定範囲内に維持し難く、その量が多すぎると、非常に原料が高価であり、コストが高くなってしまう。 The GeO 2 component has the effect of increasing the refractive index of the glass and improving anti-devitrification, but if the amount is too small, it is difficult to maintain the value of the optical constant of the glass within the specific range, and the amount is large. If it is too high, the raw material is very expensive and the cost becomes high.
従って、上記効果を奏するために、好ましくは1%、より好ましくは3%、最も好ましくは6%を下限とし、好ましくは20%、より好ましくは19%、最も好ましくは18%を上限として含有することができる。GeO2成分は、原料として例えばGeO2等を使用してガラス組成物中に導入できる。 Therefore, in order to achieve the above effect, the lower limit is preferably 1%, more preferably 3%, most preferably 6%, preferably 20%, more preferably 19%, and most preferably 18%. be able to. The GeO 2 component can be introduced into the glass composition using, for example, GeO 2 as a raw material.
Li2O成分は、転移温度(Tg)を大幅に下げ、かつ、混合したガラス原料の溶融を促進する効果を奏する。しかしその量が少なすぎるとこれらの効果が不十分であり、多すぎると耐失透性が急激に悪化する。 The Li 2 O component has the effect of significantly lowering the transition temperature (Tg) and promoting the melting of the mixed glass raw material. However, if the amount is too small, these effects are insufficient, and if the amount is too large, the devitrification resistance deteriorates rapidly.
従って、上記効果を奏するために、好ましくは0.5%以上を超えることを下限とし、好ましくは6%、より好ましくは5%、最も好ましくは4%を上限として含有することができる。 Therefore, in order to exhibit the above-mentioned effect, it is preferable that the upper limit is preferably over 0.5%, preferably 6%, more preferably 5%, and most preferably 4%.
Li2O成分は、原料として例えばLi2CO3、LiF、LiNO3、LiOH、等を使用してガラス組成物中に導入できる。 Li 2 O component, the raw material as, for example, Li 2 CO 3, LiF, LiNO 3, LiOH, etc. can be introduced into the glass composition using.
ZnO成分は、転移温度(Tg)を低める効果が大きい成分であるが、高分散成分である為、過剰に添加すると上記特定範囲内の光学定数を有することが難しくなり、耐失透性も悪くなる。 The ZnO component is a component having a large effect of lowering the transition temperature (Tg). However, since it is a highly dispersed component, it becomes difficult to have an optical constant within the specific range when added in excess, and the devitrification resistance is poor. Become.
従って、良好な耐失透性を維持しつつ転移温度(Tg)を低くするためには、好ましくは10%以下、より好ましくは9%以下、最も好ましくは8%以下の量で含有し、好ましくは2%、より好ましくは3%、最も好ましくは4%を下限として含有することができる。 Therefore, in order to lower the transition temperature (Tg) while maintaining good devitrification resistance, the content is preferably 10% or less, more preferably 9% or less, and most preferably 8% or less. Can be contained at a lower limit of 2%, more preferably 3%, and most preferably 4%.
ZnO成分は、原料として例えばZnO、ZnF2等を使用してガラス組成物中に導入できる。 The ZnO component can be introduced into the glass composition using, for example, ZnO, ZnF 2 or the like as a raw material.
本発明の光学ガラスにおいてはLi2O含有量に対するZnO含有量の比が所定の範囲内であることが好ましい。この値が大きすぎると耐失透性が悪くなり、小さすぎると化学的耐久性が悪くなるといった不利益を生じてしまう。従って、当該値は各成分の含有量を質量%で表した場合に、好ましくは1.5、より好ましくは1.6、最も好ましくは1.7を下限とし、好ましくは7.5、より好ましくは7.4、最も好ましくは7.3を上限とする。 In the optical glass of the present invention, the ratio of ZnO content to Li 2 O content is preferably within a predetermined range. When this value is too large, the devitrification resistance is deteriorated, and when it is too small, the chemical durability is deteriorated. Therefore, the value is preferably 1.5, more preferably 1.6, and most preferably 1.7 as the lower limit, and preferably 7.5, more preferably when the content of each component is expressed in mass%. Is 7.4, most preferably 7.3.
さらに本発明においてはLa2O3含有量に対するZnO及びLi2O含有量の和の値、すなわち(ZnO+Li2O)/La2O3の値が所定の範囲内の値となることが好ましい。この値が大きすぎると粘度(logη)が低くなりプレス時の作業性が悪くなる上、所望の光学定数も維持し難くなる。他方、小さすぎると転移温度(Tg)が高くなり、対失透性が悪くなる。従って、当該値は各成分の含有量を質量%で表した場合に、好ましくは0.1、より好ましくは0.15、最も好ましくは0.2を下限とし、好ましくは0.5、より好ましくは0.45、最も好ましくは0.4を上限とする。 Furthermore, in the present invention, it is preferable that the value of the sum of ZnO and Li 2 O content with respect to La 2 O 3 content, that is, the value of (ZnO + Li 2 O) / La 2 O 3 is a value within a predetermined range. If this value is too large, the viscosity (log η) will be low, the workability during pressing will be poor, and the desired optical constant will be difficult to maintain. On the other hand, when too small, transition temperature (Tg) will become high and anti-devitrification property will worsen. Therefore, the value is preferably 0.1, more preferably 0.15, and most preferably 0.2 as the lower limit, preferably 0.5, more preferably when the content of each component is expressed in mass%. 0.45, most preferably 0.4.
Gd2O3成分は、ガラスの屈折率を高め、低分散化させるのに有効である。しかし、その量が多すぎると耐失透性が悪くなる。 The Gd 2 O 3 component is effective for increasing the refractive index of the glass and reducing the dispersion. However, if the amount is too large, the devitrification resistance deteriorates.
従って、本発明における所望の光学定数を維持しつつ良好な耐失透性を維持しやすくするために、好ましくは8%以下、より好ましくは6%以下、最も好ましくは4%以下で含有することができる。 Therefore, in order to easily maintain good devitrification resistance while maintaining the desired optical constant in the present invention, it is preferably 8% or less, more preferably 6% or less, and most preferably 4% or less. Can do.
Gd2O3成分は、原料として例えばGd2O3、GdF3等を使用してガラス組成物中に導入できる。 The Gd 2 O 3 component can be introduced into the glass composition using, for example, Gd 2 O 3 , GdF 3 or the like as a raw material.
Y2O3成分は、ガラスの屈折率を高め、低分散化させるのに有効である。しかし、その量が多すぎると耐失透性が悪くなる。 The Y 2 O 3 component is effective in increasing the refractive index of the glass and reducing the dispersion. However, if the amount is too large, the devitrification resistance deteriorates.
従って、本発明における所望の光学定数を維持しつつ良好な耐失透性を維持しやすくするために、好ましくは8%以下、より好ましくは6%以下、最も好ましくは4%以下で含有することができる。 Therefore, in order to easily maintain good devitrification resistance while maintaining the desired optical constant in the present invention, it is preferably 8% or less, more preferably 6% or less, and most preferably 4% or less. Can do.
Y2O3成分は、原料として例えばY2O3、YF3等を使用してガラス組成物中に導入できる。 The Y 2 O 3 component can be introduced into the glass composition using, for example, Y 2 O 3 , YF 3 or the like as a raw material.
Yb2O3成分は、ガラスの屈折率を高め、低分散化させるのに有効である。しかし、過剰に添加するとガラスの耐失透性を悪化させる。 The Yb 2 O 3 component is effective for increasing the refractive index of the glass and lowering the dispersion. However, when added excessively, the devitrification resistance of the glass is deteriorated.
従って、本発明における所望の光学定数を維持しつつ良好な耐失透性を維持しやすくするために、好ましくは8%以下、より好ましくは6%以下、最も好ましくは4%以下で含有することができる。 Therefore, in order to easily maintain good devitrification resistance while maintaining the desired optical constant in the present invention, it is preferably 8% or less, more preferably 6% or less, and most preferably 4% or less. Can do.
Yb2O3成分は、原料として例えばYb2O3、YbF3等を使用してガラス組成物中に導入できる。 The Yb 2 O 3 component can be introduced into the glass composition using, for example, Yb 2 O 3 , YbF 3 or the like as a raw material.
TiO2成分は光線透過率を悪化させることと、ガラスを高分散化させるが、ガラスのソーラリゼーション防止のため任意に添加することもできる。本発明の光学定数を維持するためには、その量は好ましくは5%未満、より好ましくは4.5%以下、最も好ましくは4%以下で含有することができる。 The TiO 2 component deteriorates the light transmittance and makes the glass highly dispersed, but can be optionally added to prevent glass solarization. In order to maintain the optical constant of the present invention, the amount is preferably less than 5%, more preferably 4.5% or less, and most preferably 4% or less.
TiO2成分は、原料として例えばTiO2等を使用してガラス組成物中に導入できる。 TiO 2 component as a raw material by using, eg, TiO 2 or the like can be incorporated in the glass composition.
ZrO3成分は、光学定数を調整し、耐失透性を改善し、化学的耐久性を向上させる効果があるが、しかし、過剰に添加すると逆に耐失透性が悪くなる。 The ZrO 3 component has the effect of adjusting the optical constant, improving the devitrification resistance, and improving the chemical durability. However, if added excessively, the devitrification resistance is worsened.
従って、良好な化学的耐久性、耐失透性を維持しやすくする為には、好ましくは10%以下、より好ましくは9%以下、最も好ましくは8%以下で含有させることができる。 Therefore, in order to make it easy to maintain good chemical durability and resistance to devitrification, the content can be preferably 10% or less, more preferably 9% or less, and most preferably 8% or less.
ZrO2成分は、原料として例えばZrO2、ZrF4等を使用してガラス組成物中に導入できる。 The ZrO 2 component can be introduced into the glass composition using, for example, ZrO 2 , ZrF 4 or the like as a raw material.
CaO、SrO及びBaO成分から選ばれる1種又は2種以上の成分であるRO成分は光学定数の調整に有効である。しかし、CaO、SrO及びBaO成分の合計量が多すぎると耐失透性が悪くなる。 The RO component which is one or more components selected from CaO, SrO and BaO components is effective for adjusting the optical constant. However, when the total amount of the CaO, SrO and BaO components is too large, the devitrification resistance is deteriorated.
従って、特に良好な耐失透性を維持しやすくする為には、好ましくは15%以下、より好ましくは13%以下、最も好ましくは10%以下で含有させることができる。 Therefore, in order to easily maintain particularly good devitrification resistance, it can be contained preferably at 15% or less, more preferably 13% or less, and most preferably 10% or less.
CaO成分は、原料として例えばCaCO3、CaF2、Ca(OH)2、等を使用してガラス組成物中に導入できる。 The CaO component can be introduced into the glass composition using, for example, CaCO 3 , CaF 2 , Ca (OH) 2 , or the like as a raw material.
SrO成分は、原料として例えばSr(NO3)2、SrF2、Sr(OH)2等を使用してガラス組成物中に導入できる。 The SrO component can be introduced into the glass composition using, for example, Sr (NO 3 ) 2 , SrF 2 , Sr (OH) 2 or the like as a raw material.
BaO成分は、原料として例えばBaCO3、Ba(NO3)2、BaF2、Ba(OH)2等を使用してガラス組成物中に導入できる。 The BaO component can be introduced into the glass composition using, for example, BaCO 3 , Ba (NO 3 ) 2 , BaF 2 , Ba (OH) 2 or the like as a raw material.
WO3成分は、光学定数を調整し、対失透性を改善する効果があるが、その量が多いと逆に耐失透性や、可視域の短波長域の光線透過率が悪くなる。 The WO 3 component has an effect of adjusting the optical constant and improving the anti-devitrification property. However, when the amount is large, the devitrification resistance and the light transmittance in the short wavelength region of the visible region are deteriorated.
従って、良好な対失透性を保ち、可視域の短波長域の光線透過率が優れたガラスを得やすくする為には、好ましくは7%以下、より好ましくは6%以下、最も好ましくは5%以下で含有させることができる。 Therefore, in order to maintain good anti-devitrification property and to easily obtain a glass having excellent light transmittance in the short wavelength region in the visible region, it is preferably 7% or less, more preferably 6% or less, and most preferably 5 % Or less.
WO3成分は、原料として例えばWO3等を使用してガラス組成物中に導入できる。 The WO 3 component can be introduced into the glass composition using, for example, WO 3 as a raw material.
Bi2O3成分は、ガラスの屈折率を高め、点移転(Tg)を下げる効果があるが、環境に有害な影響を与え、環境負荷の大きい成分であるため、好ましくは4%、より好ましくは2%を上限とし、最も好ましくは含有しない。 The Bi 2 O 3 component has an effect of increasing the refractive index of the glass and lowering the point transfer (Tg). However, since it is a component that has a harmful effect on the environment and has a large environmental load, it is preferably 4%, more preferably Has an upper limit of 2%, most preferably not contained.
Sb2O3成分は、ガラス溶融時の脱泡剤として添加しうるが、その量は1%までで十分である。 The Sb2O3 component can be added as a defoaming agent at the time of melting the glass, but up to 1% is sufficient.
F成分は、ガラスの分散を低くしつつ、転移温度(Tg)を低下させ、耐失透性を向上させるために有効であり、特にF成分をLa2O3成分と共存させることにより、前記特定範囲内の光学定数を有し、かつ、精密プレス成形が可能な低い転移温度(Tg)を有する低分散性の光学ガラスを得ることができる。 The F component is effective for lowering the transition temperature (Tg) and improving the devitrification resistance while lowering the dispersion of the glass. In particular, the F component is allowed to coexist with the La 2 O 3 component. A low-dispersion optical glass having an optical constant within a specific range and a low transition temperature (Tg) capable of precision press molding can be obtained.
なお、本発明の光学ガラス中においては、F成分は各珪素や他の金属元素の1種又は2種以上の酸化物一部又は全部と置換したフッ化物の形態で存在するものと考えられる。当該酸化物の一部又は全部と置換したフッ化物のFとしての合計量が多すぎると、フッ素成分の揮発量が多くなり、均質なガラスを得にくくなる。 In the optical glass of the present invention, it is considered that the F component exists in the form of fluoride substituted with one or more oxides of one or more kinds of silicon and other metal elements. If the total amount of the fluoride substituted with part or all of the oxide is too large, the volatilization amount of the fluorine component increases and it becomes difficult to obtain a homogeneous glass.
従って、酸化物換算組成のガラス組成物100質量部に対して、好ましくは5質量部以下、より好ましくは4質量部以下、最も好ましくは3%質量部以下の量を含有する。なお、本明細書中において「酸化物換算組成」とは、本発明のガラス構成成分として使用される弗化物等がガラス溶融時に全て分解され酸化物へ変化すると仮定した場合の生成酸化物の総重量を100質量%として各成分を表記した組成である。 Therefore, the amount is preferably 5 parts by mass or less, more preferably 4 parts by mass or less, and most preferably 3% by mass or less with respect to 100 parts by mass of the glass composition having an oxide equivalent composition. In the present specification, the “oxide equivalent composition” means the total amount of oxides generated when it is assumed that the fluoride used as the glass component of the present invention is all decomposed and changed into an oxide when the glass is melted. It is a composition in which each component is expressed with a weight of 100% by mass.
次に本発明の光学ガラスにおいて含有させるべきでない成分について説明する。
鉛化合物は、精密プレス成形時に金型と融着しやすい成分であるという問題並びにガラスの製造のみならず、研磨等のガラスの冷間加工及びガラスの廃棄に至るまで、環境対策上の措置が必要となり、環境負荷が大きい成分であるという問題があるため、本発明の光学ガラスに含有させるべきではない。
Next, components that should not be contained in the optical glass of the present invention will be described.
Lead compounds are components that are easy to fuse with molds during precision press molding and glass manufacturing, as well as glass processing such as polishing and environmental measures such as glass processing and glass disposal. The optical glass of the present invention should not be contained because it is necessary and has a problem that it is a component with a large environmental load.
As2O3、カドミウム及びトリウムは、共に、環境に有害な影響を与え、環境負荷の非常に大きい成分であるため、本発明の光学ガラスに含有させるべきではない。 As 2 O 3 , cadmium and thorium both have harmful effects on the environment and are extremely heavy components of the environment, and therefore should not be contained in the optical glass of the present invention.
P2O5は、本発明の光学ガラスに含有させると、耐失透性を悪化させやすいのでP2O5を含有させることは好ましくない。 When P 2 O 5 is contained in the optical glass of the present invention, devitrification resistance is likely to be deteriorated, so it is not preferable to contain P 2 O 5 .
TeO2は、白金製の坩堝や、溶融ガラスと接する部分が白金で形成されている溶融槽でガラス原料を溶融する際、テルルと白金が合金化し、合金となった箇所は耐熱性が悪くなるため、その箇所に穴が開き溶融ガラス流出する事故がおこる危険性が憂慮されるため、本発明の光学ガラスに含有させるべきではない。 When TeO 2 melts a glass raw material in a crucible made of platinum or a melting tank in which a portion in contact with molten glass is formed of platinum, tellurium and platinum are alloyed, and the alloyed portion has poor heat resistance. Therefore, since there is concern about the danger of an accident that a hole is opened at that location and the molten glass flows out, it should not be included in the optical glass of the present invention.
さらに本発明の光学ガラスにおいては、V、Cr、Mn、Fe、Co、Ni、Cu、Mo、Eu、Nd、Sm、Tb、Dy、Er等の着色成分は含有しないことが好ましい。ただし、ここでいう「含有しない」とは、不純物として混入される場合を除き、人為的に含有させないことを意味する。 Further, the optical glass of the present invention preferably contains no coloring components such as V, Cr, Mn, Fe, Co, Ni, Cu, Mo, Eu, Nd, Sm, Tb, Dy, and Er. However, “not contained” here means that it is not contained artificially unless it is mixed as an impurity.
本発明のガラス組成物は、その組成が質量%で表されているため直接的にmol%の記載に表せるものではないが、本発明において要求される諸特性を満たすガラス組成物中に存在する各成分のmol%表示による組成は、酸化物換算組成で概ね以下の値をとる。 The glass composition of the present invention cannot be expressed directly in the description of mol% because the composition is expressed by mass%, but exists in the glass composition satisfying various properties required in the present invention. The composition of each component in terms of mol% takes the following values in terms of oxide equivalent composition.
B2O3 10〜35%
La2O3 5〜20%
Nb2O5 8〜22%
Ta2O5 1〜10%
Li2O 1〜20%
GeO2 1〜34%
ZnO 3〜20%及び/又は
及び
SiO2 0〜15%及び/又は
Gd2O3 0〜5%及び/又は
Y2O3 0〜5%及び/又は
Yb2O3 0〜5%及び/又は
TiO2 0〜10%及び/又は
ZrO2 0〜15%及び/又は
WO3 0〜5%及び/又は
RO 0〜30%
ただし、ROは、CaO、SrO及びBaOから選ばれる1種又は2種以上、及び/又はSb2O3 0〜1%
の酸化物換算組成の各成分を含有し、かつ酸化物換算組成の総モル数に対する上記酸化物の一部又は全部をフッ化物置換したFのモル数の比が0〜0.25となる。
B 2 O 3 10~35%
La 2 O 3 5-20%
Nb 2 O 5 8-22%
Ta 2 O 5 1-10%
Li 2 O 1-20%
GeO 2 1~34%
3 to 20% ZnO and / or and SiO 2 0 to 15% and / or Gd 2 O 3 0~5% and / or Y 2 O 3 0~5% and / or Yb 2 O 3 0~5% and / Or TiO 2 0-10% and / or ZrO 2 0-15% and / or WO 3 0-5% and / or RO 0-30%
However, RO is, CaO, 1 kind or more selected from SrO and BaO, and / or Sb 2 O 3 0 to 1%
The ratio of the number of moles of F containing each component of the oxide-converted composition and fluoride-substituting a part or all of the oxide with respect to the total number of moles of the oxide-converted composition is 0 to 0.25.
本発明のガラス組成物におけるSiO2成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね15mol%、より好ましくは概ね13mol%、最も好ましくは概ね11mol%を上限として含有できる。 The effect of the SiO 2 component in the glass composition of the present invention is as described above. In order to achieve the effect, it is preferably about 15 mol%, more preferably about 13 mol%, and most preferably about 11 mol% as the upper limit. it can.
本発明のガラス組成物におけるB2O3成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね10mol%、より好ましくは概ね12mol%、最も好ましくは概ね13mol%を下限とし、好ましくは概ね35mol%、より好ましくは概ね33mol%、最も好ましくは概ね32mol%を上限として含有できる。 The effect of the B 2 O 3 component in the glass composition of the present invention is as described above. In order to achieve the effect, the lower limit is preferably about 10 mol%, more preferably about 12 mol%, and most preferably about 13 mol%. And preferably about 35 mol%, more preferably about 33 mol%, and most preferably about 32 mol% as the upper limit.
本発明のガラス組成物におけるLa2O3成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね5mol%、より好ましくは概ね7mol%、最も好ましくは概ね8mol%を下限とし、好ましくは概ね20mol%、より好ましくは概ね18mol%、最も好ましくは概ね17mol%を上限として含有できる。 The effect of the La 2 O 3 component in the glass composition of the present invention is as described above. In order to achieve the effect, the lower limit is preferably about 5 mol%, more preferably about 7 mol%, and most preferably about 8 mol%. And preferably about 20 mol%, more preferably about 18 mol%, and most preferably about 17 mol%.
本発明のガラス組成物におけるNb2O5成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね8mol%、より好ましくは概ね9mol%、最も好ましくは概ね10mol%を下限とし、好ましくは概ね22mol%、より好ましくは概ね21mol%、最も好ましくは概ね20mol%を上限として含有できる。 The effect of the Nb 2 O 5 component in the glass composition of the present invention is as described above, but in order to achieve the effect, the lower limit is preferably about 8 mol%, more preferably about 9 mol%, and most preferably about 10 mol%. And preferably about 22 mol%, more preferably about 21 mol%, and most preferably about 20 mol%.
本発明のガラス組成物におけるTa2O5成分の効果は上述のとおりであるが、当該効果を奏するために、1mol%を下限とし、好ましくは概ね10mol%、より好ましくは概ね8mol%、最も好ましくは概ね6mol%を上限として含有できる。 The effect of the Ta 2 O 5 component in the glass composition of the present invention is as described above, but in order to achieve the effect, 1 mol% is the lower limit, preferably approximately 10 mol%, more preferably approximately 8 mol%, most preferably Can generally contain up to 6 mol%.
本発明のガラス組成物におけるGeO2成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね1mol%、より好ましくは概ね4mol%、最も好ましくは概ね7mol%を下限とし、好ましくは概ね34mol%、より好ましくは概ね33mol%、最も好ましくは概ね32mol%を上限として含有できる。 The effect of the GeO 2 component in the glass composition of the present invention is as described above. However, in order to achieve the effect, the lower limit is preferably about 1 mol%, more preferably about 4 mol%, most preferably about 7 mol%, Preferably, the upper limit can be about 34 mol%, more preferably about 33 mol%, and most preferably about 32 mol%.
本発明のガラス組成物におけるLi2O成分の効果は上述のとおりであるが、当該効果を奏するために、1mol%を下限とし、好ましくは概ね20mol%、より好ましくは概ね18mol%、最も好ましくは概ね17mol%を上限として含有できる。 The effect of the Li 2 O component in the glass composition of the present invention is as described above, but in order to achieve the effect, 1 mol% is the lower limit, preferably approximately 20 mol%, more preferably approximately 18 mol%, most preferably Approximately 17 mol% can be contained as the upper limit.
本発明のガラス組成物におけるGd2O3成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね5mol%、より好ましくは概ね4mol%、最も好ましくは概ね3mol%を上限として含有できる。 The effect of the Gd 2 O 3 component in the glass composition of the present invention is as described above. In order to achieve the effect, the upper limit is preferably about 5 mol%, more preferably about 4 mol%, and most preferably about 3 mol%. Can be included.
本発明のガラス組成物におけるY2O3成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね5mol%、より好ましくは概ね4mol%、最も好ましくは概ね3mol%を上限として含有できる。 The effect of the Y 2 O 3 component in the glass composition of the present invention is as described above. In order to achieve the effect, the upper limit is preferably about 5 mol%, more preferably about 4 mol%, and most preferably about 3 mol%. Can be included.
本発明のガラス組成物におけるYb2O3成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね5mol%、より好ましくは概ね4mol%、最も好ましくは概ね3mol%を上限として含有できる。 The effect of the Yb 2 O 3 component in the glass composition of the present invention is as described above. In order to achieve the effect, the upper limit is preferably about 5 mol%, more preferably about 4 mol%, and most preferably about 3 mol%. Can be included.
本発明のガラス組成物におけるTiO2成分の効果は上述のとおりである。本発明のガラス中においては好ましくは概ね10mol%、より好ましくは概ね9mol%、最も好ましくは概ね8mol%を上限として含有できる。 The effect of the TiO 2 component in the glass composition of the present invention is as described above. In the glass of the present invention, the upper limit can be preferably about 10 mol%, more preferably about 9 mol%, and most preferably about 8 mol%.
本発明のガラス組成物におけるZrO2成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね15mol%、より好ましくは概ね14mol%、最も好ましくは概ね12mol%を上限として含有できる。 The effect of the ZrO 2 component in the glass composition of the present invention is as described above. In order to achieve the effect, it is preferably about 15 mol%, more preferably about 14 mol%, and most preferably about 12 mol% as the upper limit. it can.
本発明のガラス組成物におけるZnO成分の効果は上述のとおりである。本発明のガラス中においては好ましくは概ね20mol%未満、より好ましくは概ね18mol%、最も好ましくは16mol%を上限とし、3mol%、好ましくは4mol%、最も好ましくは5mol%を下限として含有することができる。 The effect of the ZnO component in the glass composition of the present invention is as described above. The glass of the present invention preferably contains less than about 20 mol%, more preferably about 18 mol%, most preferably 16 mol%, and 3 mol%, preferably 4 mol%, most preferably 5 mol% as the lower limit. it can.
本発明のガラス組成物におけるRO成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね30mol%、より好ましくは概ね28mol%、最も好ましくは概ね26mol%を上限として含有できる。 The effect of the RO component in the glass composition of the present invention is as described above, but in order to achieve the effect, it can preferably contain approximately 30 mol%, more preferably approximately 28 mol%, and most preferably approximately 26 mol% as the upper limit. .
本発明のガラス組成物におけるWO3成分の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね5mol%、より好ましくは概ね4.5mol%、最も好ましくは概ね4mol%を上限として含有できる。 The effect of the WO 3 component in the glass composition of the present invention is as described above. In order to achieve the effect, the upper limit is preferably about 5 mol%, more preferably about 4.5 mol%, and most preferably about 4 mol%. Can be included.
本発明のガラス組成物におけるSiO2、B2O3成分の合計含有量の効果は上述のとおりであるが、当該効果を奏するために、好ましくは概ね10mol%、より好ましくは概ね12mol%、最も好ましくは概ね14mol%を下限とし、好ましくは概ね42mol%、より好ましくは概ね41mol%、最も好ましくは概ね40mol%を上限として含有できる。 The effect of the total content of SiO 2 and B 2 O 3 components in the glass composition of the present invention is as described above, but in order to achieve the effect, preferably about 10 mol%, more preferably about 12 mol%, most preferably Preferably, the lower limit is about 14 mol%, preferably about 42 mol%, more preferably about 41 mol%, and most preferably about 40 mol%.
本発明のガラス組成物におけるSb2O3成分の効果は上述のとおりであるが、当該効果を奏するために、概ね1mol%以下で十分である。 Although the effect of the Sb 2 O 3 component in the glass composition of the present invention is as described above, approximately 1 mol% or less is sufficient to achieve the effect.
本発明のガラス組成物におけるF成分は上述のとおりであるが、当該効果を奏するために、酸化物換算組成の総モル数に対する上記酸化物の一部又は全部をフッ化物置換したFのモル数の比が好ましくは概ね0.25以下、より好ましくは0.24以下、最も好ましくは0.23以下となるように含有される。 Although the F component in the glass composition of the present invention is as described above, the number of moles of F in which part or all of the oxide is fluoride-substituted with respect to the total number of moles of the oxide-converted composition in order to achieve the effect. The ratio is preferably about 0.25 or less, more preferably 0.24 or less, and most preferably 0.23 or less.
次に本発明の光学ガラスの物性について説明する。 Next, the physical properties of the optical glass of the present invention will be described.
本発明の光学ガラスは、主に加熱軟化させて精密プレス成形によってガラス成形品を得るためのガラスプリフォーム材として使用される。従ってこの際使用する金型の損傷を抑制し、金型の高精度な成形面を長く維持し、かつ、低い温度での精密プレス成形を可能にするために、できるだけ低い転移温度(Tg)を有することが望まれている。そのため、上記特定範囲の組成を用いることにより、所望のガラス転移温度(Tg)を実現させたものである。 The optical glass of the present invention is mainly used as a glass preform material for softening by heating and obtaining a glass molded product by precision press molding. Therefore, in order to suppress damage to the mold used at this time, maintain a high-precision molding surface of the mold for a long time, and enable precision press molding at a low temperature, a transition temperature (Tg) as low as possible is set. It is desirable to have. Therefore, a desired glass transition temperature (Tg) is realized by using the composition in the specific range.
ここでTgが低すぎると化学的耐久性が悪化し同時に耐失透性が低下し安定した生産を行うことが困難になる。また、Tgが高くなりすぎるとモールドプレス性が悪化するだけでなく溶融性が低下し溶け残り等が発生しやすい。しかし溶け残り防止のために溶融温度を高くすると溶融容器からの白金溶け込み量が増し光線透過性が悪化してしまう傾向にある。従って、本発明の光学ガラスのTgは好ましくは570℃、より好ましくは575℃、最も好ましくは580℃を下限とし、好ましくは630℃、より好ましくは625℃、最も好ましくは620℃を上限とする。 Here, if Tg is too low, chemical durability is deteriorated, and at the same time, devitrification resistance is lowered, making it difficult to perform stable production. On the other hand, if Tg is too high, not only mold pressability is deteriorated, but meltability is lowered and undissolved parts are easily generated. However, if the melting temperature is increased to prevent undissolved residue, the amount of platinum dissolved from the melting container increases and the light transmittance tends to deteriorate. Accordingly, the Tg of the optical glass of the present invention is preferably 570 ° C., more preferably 575 ° C., most preferably 580 ° C., preferably 630 ° C., more preferably 625 ° C., most preferably 620 ° C. .
本発明の光学ガラスでは、下記製造方法により、安定した生産を実現するため、液相温度を1150℃以下とすることが重要である。特に好ましくは1135℃以下とすることで、安定生産可能な温度範囲が広くなり、また、ガラス熔解温度を下げることができるため、消費されるエネルギーを抑えることができる。 In the optical glass of the present invention, it is important to set the liquidus temperature to 1150 ° C. or lower in order to realize stable production by the following manufacturing method. Particularly preferably, by setting the temperature to 1135 ° C. or lower, the temperature range in which stable production can be performed is widened, and the glass melting temperature can be lowered, so that the consumed energy can be suppressed.
本明細書中において、「液相温度」とは一般の溶解炉を使用し、50ccのガラス試料を白金製のルツボにて溶融させ、その後、任意の温度で2時間保持した後取り出し、ガラスの結晶の有無を目視にて観察し、結晶が認められない一番低い温度を表す。 In the present specification, the “liquid phase temperature” means that a general melting furnace is used, a 50 cc glass sample is melted with a platinum crucible, held at an arbitrary temperature for 2 hours, then taken out, and the glass The lowest temperature at which no crystal is observed is shown by visual observation of the presence or absence of crystals.
前述のとおり本発明の光学ガラスはプレス成形用のプリフォーム材として使用することができ、或いは溶融ガラスをダイレクトプレスすることも可能である。プリフォーム材として使用する場合、その製造方法及び熱間成形方法は特に限定されるものではなく、公知の製造方法及び成形方法を使用することができる。プリフォーム材の製造方法としては、例えば特開平8−319124に記載のガラスゴブの成形方法や特開平8−73229に記載の光学ガラスの製造方法及び製造装置のような溶融ガラスから直接プリフォーム材を製造することもでき、また板状に成形した材料を冷間加工して製造しても良い。 As described above, the optical glass of the present invention can be used as a preform material for press molding, or the molten glass can be directly pressed. When used as a preform material, the production method and hot forming method are not particularly limited, and known production methods and forming methods can be used. As a method for producing a preform material, for example, a glass gob forming method described in JP-A-8-319124, an optical glass manufacturing method described in JP-A-8-73229, and a preform material directly from molten glass such as a manufacturing apparatus are used. It can also be manufactured, or it may be manufactured by cold working a plate-shaped material.
なお、本発明の光学ガラスを用いて溶融ガラスを白金或いは強化白金から滴下させてプリフォームを製造する場合、溶融ガラスの粘度は、低すぎるとガラスプリフォームに脈理が入りやすくなり、高すぎると、自重と表面張力によるガラスの切断が困難になる。 In addition, when manufacturing the preform by dripping molten glass from platinum or reinforced platinum using the optical glass of the present invention, if the viscosity of the molten glass is too low, the glass preform is likely to be striae and too high. Then, it becomes difficult to cut the glass due to its own weight and surface tension.
従って、高品質かつ安定した生産のためには、液相温度における粘度(dPa・s)の対数logηの値が好ましくは0.3以上であり、好ましくは2.0、より好ましくは1.8、最も好ましくは1.5を上限とする。 Therefore, for high-quality and stable production, the logarithmic log η value of the viscosity (dPa · s) at the liquidus temperature is preferably 0.3 or more, preferably 2.0, more preferably 1.8. Most preferably, the upper limit is 1.5.
なお、プリフォームの熱間成形方法を特に限定するものではないが、例えば特公昭62−41180に記載の光学素子の成形方法のような方法を使用することができる。 The method for hot forming the preform is not particularly limited. For example, a method such as the method for molding an optical element described in JP-B-62-41180 can be used.
以下、本発明の実施例について述べるが、本発明はこれら実施例に限定されるものではない。なお下表1〜6に規定する各成分の含有量は全て質量%で表すものとする。
表1〜表5に示した本発明のガラスの実施例(No.1〜No.25)は、酸化物、水酸化物、炭酸塩、硝酸塩、フッ化物等の通常の光学ガラス用原料を、各実施例の組成の割合となるように秤量し、混合し、白金坩堝に投入し、組成による溶融性に応じて、1000〜1300℃で、3〜5時間溶融、清澄、撹拌して均質化した後、金型等に鋳込み徐冷することにより得ることができた。 Examples (No. 1 to No. 25) of the glasses of the present invention shown in Tables 1 to 5 are ordinary optical glass materials such as oxides, hydroxides, carbonates, nitrates, fluorides, Weigh and mix so as to have the composition ratio of each example, put into a platinum crucible, and melt, clarify, and stir for 3 to 5 hours at 1000 to 1300 ° C. according to the meltability by composition. Then, it could be obtained by casting into a mold or the like and gradually cooling.
屈折率(nd)及び、アッベ数(νd)は徐冷降温速度を−25℃/hにして得られた光学ガラスについて測定した。 The refractive index (nd) and the Abbe number (νd) were measured on the optical glass obtained at a slow cooling rate of -25 ° C / h.
ガラス転移温度(Tg)は日本光学硝子工業会規格JOGIS08−2003(光学ガラスの熱膨張の測定方法)に記載された方法により測定した。ただし、試料片として長さ50mm、直径4mmの試料を使用した。 The glass transition temperature (Tg) was measured by the method described in Japan Optical Glass Industry Association Standard JOGIS08-2003 (Measurement Method of Thermal Expansion of Optical Glass). However, a sample having a length of 50 mm and a diameter of 4 mm was used as a sample piece.
液相温度の測定は、一般の溶解炉を使用し、50ccのガラス試料を白金製のルツボにて溶融させ、その後、任意の温度で2時間保持した後取り出し、ガラスの結晶の有無を目視にて観察し、結晶が認められない一番低い温度を求めた。 The liquid phase temperature is measured by using a general melting furnace, melting a 50 cc glass sample with a platinum crucible, holding it at an arbitrary temperature for 2 hours, and then taking it out to visually check for glass crystals. The lowest temperature at which no crystals were observed was determined.
液相温度における粘度η(dPa・s)は、球引上げ式粘度計(有限会社オプト企業製:型番BVM−13LH)を使用し、液相温度での粘度を測定した。なお、表1〜6中において粘度を表す場合は粘度ηの常用対数で表した。 Viscosity η (dPa · s) at the liquidus temperature was measured by using a ball pulling viscometer (manufactured by Opto Corporation, model number: BVM-13LH) and measuring the viscosity at the liquidus temperature. In addition, in Tables 1-6, when expressing a viscosity, it represented with the common logarithm of viscosity (eta).
表1〜表5に見られるとおり、本発明の実施例の光学ガラス(No.1〜No.25)はすべて、上記特定範囲内の光学定数(屈折率(nd)及びアッベ数(νd)、)を有し、転移温度(Tg)が630℃以下の範囲にあり、かつ液相温度における粘度の対数(logη)が0.3〜2の範囲内であることから、精密プレス成形に使用するガラスプリフォーム材及び精密プレス成形に適していた。 As seen in Tables 1 to 5, all of the optical glasses (No. 1 to No. 25) of the examples of the present invention have optical constants (refractive index (nd) and Abbe number (νd), ), The transition temperature (Tg) is in the range of 630 ° C. or less, and the logarithm (log η) of the viscosity at the liquidus temperature is in the range of 0.3 to 2, so that it is used for precision press molding. Suitable for glass preform materials and precision press molding.
これに対し、表6には比較例を示すが、比較例No.1(特開2000−128570号公報の実施例No.5)、比較例 No.2(特開2000−128570号公報の実施例No.10)のガラスは、金型に鋳込む際に激しく失透し、ガラス化しなかった。 In contrast, Table 6 shows a comparative example. 1 (Example No. 5 of JP 2000-128570 A), Comparative Example No. 1 2 (Example No. 10 of JP 2000-128570 A) was vigorously devitrified when cast into a mold and did not vitrify.
比較例No.3(特開平9−278480号公報の実施例No.3)のガラスは、所望する光学定数は満たしているものの、転移温度(Tg)が高く、精密プレス成形による安定した生産が困難であり、上述した近年の光学設計上の要求を満たしていない。 Comparative Example No. 3 (Example No. 3 of Japanese Patent Laid-Open No. 9-278480) satisfies the desired optical constant, but has a high transition temperature (Tg) and is difficult to stably produce by precision press molding. The above-mentioned recent optical design requirements are not satisfied.
本発明の光学ガラスは屈折率(nd)が1.9以上、アッベ数(νd)が25以上を有し、ガラス転移温度(Tg)が630℃以下であり、精密プレス成形に使用するガラスプリフォーム材、及び精密プレス成形に適している。 The optical glass of the present invention has a refractive index (nd) of 1.9 or more, an Abbe number (νd) of 25 or more, a glass transition temperature (Tg) of 630 ° C. or less, and is used for precision press molding. Suitable for remodeling materials and precision press molding.
Claims (12)
〜5のいずれかに記載の光学ガラス。 The ZnO content with respect to the Li 2 O content expressed in mass% is 1.5 to 7.5.
Optical glass in any one of -5.
B2O3 5〜15%
La2O3 20〜29%
Nb2O5 22〜30%
Ta2O5 4〜15%
Li2O 0.5%を超え6%まで、
GeO2 1〜20%、及び
ZnO 2〜10%
並びに
SiO2 0〜5.5%、及び/又は
Gd2O3 0〜8%、及び/又は
Y2O3 0〜8%、及び/又は
Yb2O3 0〜8%、及び/又は
TiO2 0〜5%未満、及び/又は
ZrO2 0〜10%、及び/又は
WO3 0〜7%、及び/又は
Bi2O3 0〜3%、及び/又は
RO 0〜15%
ただし、ROは、CaO、SrO及びBaOから選ばれる1種又は2種以上、及び/又は
Sb2O3 0〜1%
の酸化物換算組成の各成分を含有し、かつ上記酸化物の一部又は全部をフッ化物置換したFの合計量が、上記酸化物換算組成100質量部に対して0〜5質量部の範囲となる各成分を含有する請求請1〜7のいずれか1項に記載の光学ガラス。 % By mass B 2 O 3 5 to 15%
La 2 O 3 20-29%
Nb 2 O 5 22-30%
Ta 2 O 5 4-15%
Li 2 O 0.5% to 6%,
GeO 2 1-20% and ZnO 2-10%
And SiO 2 0-5.5% and / or Gd 2 O 3 0-8% and / or Y 2 O 3 0-8% and / or Yb 2 O 3 0-8% and / or TiO 20 to less than 5% and / or ZrO 2 0 to 10% and / or WO 3 0 to 7% and / or Bi 2 O 3 0 to 3% and / or RO 0 to 15%
However, RO is, CaO, 1 kind or more selected from SrO and BaO, and / or Sb 2 O 3 0 to 1%
The total amount of F containing each component of the oxide equivalent composition and fluoride-substituted part or all of the oxide is in the range of 0 to 5 parts by mass with respect to 100 parts by mass of the oxide equivalent composition. Optical glass given in any 1 paragraph of Claims 1-7 containing each ingredient used as above.
B2O3 10〜35%
La2O3 5〜20%
Nb2O5 8〜22%
Ta2O5 1〜10%
Li2O 1〜20%
GeO2 1〜34%
ZnO 3〜20%
及び
SiO2 0〜15%及び/又は
Gd2O3 0〜5%及び/又は
Y2O3 0〜5%及び/又は
Yb2O3 0〜5%及び/又は
TiO2 0〜10%及び/又は
ZrO2 0〜15%及び/又は
WO3 0〜5%及び/又は
RO 0〜30%
ただし、ROは、CaO、SrO及びBaOから選ばれる1種又は2種以上、及び/又は
Sb2O3 0〜1%
の酸化物換算組成の各成分を含有し、かつ酸化物換算組成の総モル数に対する上記酸化物の一部又は全部をフッ化物置換したFのモル数の比が0〜0.25となるように各成分を含有する光学ガラス。 mol% with B 2 O 3 10~35%
La 2 O 3 5-20%
Nb 2 O 5 8-22%
Ta 2 O 5 1-10%
Li 2 O 1-20%
GeO 2 1~34%
ZnO 3-20%
And SiO 2 0-15% and / or Gd 2 O 3 0-5% and / or Y 2 O 3 0-5% and / or Yb 2 O 3 0-5% and / or TiO 2 0-10% and / Or ZrO 2 0-15% and / or WO 3 0-5% and / or RO 0-30%
However, RO is, CaO, 1 kind or more selected from SrO and BaO, and / or Sb 2 O 3 0 to 1%
The ratio of the number of moles of F containing each component of the oxide conversion composition and fluoride-substituting a part or all of the oxide with respect to the total number of moles of the oxide conversion composition is 0 to 0.25. An optical glass containing each component.