JP2006088118A - Ceramic siding and coating method therefor - Google Patents

Ceramic siding and coating method therefor Download PDF

Info

Publication number
JP2006088118A
JP2006088118A JP2004280325A JP2004280325A JP2006088118A JP 2006088118 A JP2006088118 A JP 2006088118A JP 2004280325 A JP2004280325 A JP 2004280325A JP 2004280325 A JP2004280325 A JP 2004280325A JP 2006088118 A JP2006088118 A JP 2006088118A
Authority
JP
Japan
Prior art keywords
color
coating
ceramic siding
paint
siding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2004280325A
Other languages
Japanese (ja)
Inventor
Yasushi Ogawa
泰史 小川
Yutaro Yamada
雄太郎 山田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KMEW Co Ltd
Original Assignee
Kubota Matsushitadenko Exterior Works Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kubota Matsushitadenko Exterior Works Ltd filed Critical Kubota Matsushitadenko Exterior Works Ltd
Priority to JP2004280325A priority Critical patent/JP2006088118A/en
Publication of JP2006088118A publication Critical patent/JP2006088118A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a coating method for ceramic siding by which coating stability is guaranteed, the coating cost is saved, and the appearance of two color coating is improved. <P>SOLUTION: The coating method can separately coat a portion of a joint-like groove 2 formed in the ceramic siding 1 by grooving and the remaining portion with two colors. The entire surface of the ceramic siding 1 is coated with a first color coating material 7 and then only the portion of the joint-like groove 2 is coated by spraying a second color coating material 6 by a spray 3. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

本発明は、主として建築物の外装に用いられる窯業系サイディングであって、この屋外側の面に凹設された目地状溝の部分とこれ以外の部分とを２色に塗り分けて塗装する方法及びこのように塗装された窯業系サイディングに関するものである。   The present invention is a ceramic siding mainly used for an exterior of a building, and a method of coating the joint groove portion recessed in the outdoor side surface and the other portion in two colors. And ceramics siding painted in this way.

従来、建築用などに使用される窯業系サイディング１にあっては、その表面に目地状溝２が凹設され、この目地状溝２の部分とこれ以外の部分（平坦部分）とを２色に塗り分けて塗装（ツートン塗装）することが行われている。図３はその一例を示すものであり、この方法は、窯業系サイディング１の表面全体にベース色の塗料６を塗布した後、ベース色とは異なる色の塗料７をスポンジロール等のロール８で塗布するものである（例えば、特許文献１参照。）。そして、ロール８は目地状溝２の奥深くには入り込まないので、目地状溝２の部分にはベース色が着色されたまま残り、その他の部分にはベース色とは異なる色が着色されるものである。
特開２００３−３１１２０６号公報 Conventionally, in ceramic siding 1 used for construction, etc., a joint groove 2 is formed on the surface, and the joint groove 2 portion and the other portion (flat portion) are in two colors. It is done to paint separately (two-tone painting). FIG. 3 shows an example. In this method, after the base color paint 6 is applied to the entire surface of the ceramic siding 1, the paint 7 having a color different from the base color is applied with a roll 8 such as a sponge roll. It is applied (for example, refer to Patent Document 1). And since the roll 8 does not enter deeply into the joint groove 2, the base color remains in the joint groove 2 portion and the other portion is colored with a color different from the base color. It is.
Japanese Patent Laid-Open No. 2003-311206

しかしながら、上記のようなロール８を用いた従来の２色塗り分けの塗装方法にあっては、次のような問題がある。すなわち、目地状溝２以外の部分では２色の塗料が塗り重ねられることとなるが、ロール８による塗装で形成された外側の塗膜９の厚さは約３〜５μｍ程度と非常に薄いため、窯業系サイディング１の表面状態（表面の凹凸）や板厚によっては、内側の塗膜１０が部分的に外側に露出して塗り残しが生じ、隠蔽性が悪く、塗装安定性の確保が困難である。また、上記のように目地状溝２以外の部分では２色の塗料が塗り重ねられることとなるが、外部から見えるのは外側の塗膜９だけであるので、そもそもこの塗膜９で隠蔽される内側の塗膜１０は不要であり、この分だけ塗装コストが増加する。また、ロール８による塗装では、図４に示すように、外側に塗布した塗料７が目地状溝２の内側面２ｂに垂れてくるなどして、塗装後の窯業系サイディング１を正面から見た場合に、目地状溝２の部分とこれ以外の部分との境界が直線状にならないことが多い。この場合、使用する塗料６，７が２色とも同系統の色であれば上記の境界はあまり目立たないが、２色の塗料６，７が全く異なる系統の色であれば上記の境界は目立つので、直線性が十分に出ていないと外観が悪くなるものである。   However, the conventional two-color painting method using the roll 8 as described above has the following problems. That is, two colors of paint are applied over the portions other than the joint grooves 2, but the thickness of the outer coating film 9 formed by painting with the roll 8 is very thin, about 3 to 5 μm. Depending on the surface state (surface irregularities) and plate thickness of the ceramic siding 1, the inner coating 10 is partially exposed to the outside, leaving unpainted, poor concealment, and difficult to ensure coating stability. It is. Also, as described above, two colors of paint are applied over the portion other than the joint groove 2, but since only the outer coating film 9 is visible from the outside, it is concealed by this coating film 9 in the first place. The inner coating film 10 is unnecessary, and the coating cost increases accordingly. Moreover, in the painting by the roll 8, as shown in FIG. 4, the coating 7 applied to the outside is dripped onto the inner side surface 2b of the joint groove 2, so that the ceramic siding 1 after painting is viewed from the front. In many cases, the boundary between the joint groove 2 and the other portion is not linear. In this case, if the two paints 6 and 7 are in the same color, the above boundary is not so noticeable. If the two colors of paint 6 and 7 are in completely different colors, the above boundary is noticeable. Therefore, if the linearity is not sufficient, the appearance is deteriorated.

本発明は上記の点に鑑みてなされたものであり、塗装安定性を確保し、塗装コストを削減することができると共に、２色塗り分けの外観を良くすることができる窯業系サイディングの塗装方法及び２色塗り分けの外観に優れた窯業系サイディングを提供することを目的とするものである。   The present invention has been made in view of the above points, and it is possible to ensure the coating stability, reduce the coating cost, and improve the appearance of two-color coating, and improve the appearance of the ceramic siding. The object of the present invention is to provide ceramic siding excellent in the appearance of two colors.

本発明の請求項１に係る窯業系サイディングの塗装方法は、窯業系サイディング１に凹設された目地状溝２の部分とこれ以外の部分とを２色に塗り分けて塗装するにあたって、窯業系サイディングの表面全体に１色目の塗料７を塗布した後、目地状溝２の部分のみに２色目の塗料６をスプレー３で吹き付けて塗布することを特徴とするものである。   The ceramic siding coating method according to claim 1 of the present invention is the ceramic industry siding in which the portion of the joint groove 2 formed in the ceramic siding 1 and the other portion are separately applied in two colors. The first color paint 7 is applied to the entire surface of the siding, and then the second color paint 6 is sprayed and applied only to the joint grooves 2.

本発明の請求項２に係る窯業系サイディングは、目地状溝２を凹設して形成されると共に、目地状溝２の部分とこれ以外の部分とが２色に塗り分けられて塗装された窯業系サイディング１において、窯業系サイディング１の表面全体に１色目の塗料７が塗布されて第１塗膜４が形成されていると共に、目地状溝２の部分のみに２色目の塗料６が塗布されて第２塗膜５が形成されていることを特徴とするものである。   The ceramic siding according to claim 2 of the present invention is formed by forming the joint groove 2 in a recessed manner, and the joint groove 2 portion and the other portion are separately applied in two colors and painted. In the ceramic siding 1, the first color paint 7 is applied to the entire surface of the ceramic siding 1 to form the first coating film 4, and the second color paint 6 is applied only to the joint grooves 2. Thus, the second coating film 5 is formed.

本発明の請求項１に係る窯業系サイディングの塗装方法によれば、塗装安定性を確保し、塗装コストを削減することができると共に、２色塗り分けの外観を良くすることができるものである。   According to the ceramic siding coating method according to claim 1 of the present invention, the coating stability can be secured, the coating cost can be reduced, and the appearance of two-color coating can be improved. .

本発明の請求項２に係る窯業系サイディングによれば、２色塗り分けの外観に優れているものである。   According to the ceramics siding according to claim 2 of the present invention, the appearance of two-color coating is excellent.

以下、本発明の実施の形態を説明する。   Embodiments of the present invention will be described below.

本発明において窯業系サイディング１としては、特に限定されるものではなく、主原料としてセメント質原料及び繊維質原料を用いて板状に成形し、養生・硬化させたものを用いることができる。窯業系サイディング１の大きさは、例えば、縦（長手方向）：１．８２〜３．０３ｍ×横（短手方向）：０．４５５ｍであり、板厚：１２〜２５ｍｍである。ただし、このような窯業系サイディング１は、屋外側の面に目地状溝２（例えば、幅：３〜２０ｍｍ、深さ：２〜１０ｍｍ）が１つ又は２つ以上凹設されて形成されている。   In the present invention, the ceramic siding 1 is not particularly limited, and a ceramic material siding 1 formed into a plate shape using a cementitious material and a fiber material as main materials, and cured and cured can be used. The size of the ceramic siding 1 is, for example, length (longitudinal direction): 1.82 to 3.03 m × width (short direction): 0.455 m, and plate thickness: 12 to 25 mm. However, the ceramic siding 1 is formed by forming one or two or more joint grooves 2 (for example, width: 3 to 20 mm, depth: 2 to 10 mm) on the outdoor side surface. Yes.

そして、窯業系サイディング１に凹設された目地状溝２の部分とこれ以外の部分（平坦部分）とを２色に塗り分けて塗装するにあたっては、次のようにして行うことができる。   Then, when coating the joint groove 2 recessed in the ceramic siding 1 and the other portion (flat portion) separately in two colors, it can be performed as follows.

まず、図１（ａ）に示すように、窯業系サイディング１の表面全体（目地状溝２の内面を含む）に１色目の塗料７を塗布する。ここで、１色目の塗料７とは、従来ロール８で塗布していた塗料と同様のものであって、ベース色とは異なる色の塗料をいい、市販されているものを任意に用いることができる。つまり、本発明では、従来の方法とは逆に、ベース色の塗料６を塗布する前に、これとは異なる色の塗料７を窯業系サイディング１に塗布するものである。この場合の塗布方法としては、特に限定されるものではないが、例えば、スプレーコーターやフローコーターによる方法を使用することができる。そして、窯業系サイディング１の表面全体に塗布された１色目の塗料７が乾燥することによって、厚さ：２０〜５０μｍの第１塗膜４が形成される。   First, as shown in FIG. 1A, the first color paint 7 is applied to the entire surface of the ceramic siding 1 (including the inner surface of the joint groove 2). Here, the first color paint 7 is the same as the paint applied with the roll 8 in the past, and is a paint having a color different from the base color, and a commercially available one can be used arbitrarily. it can. That is, in the present invention, contrary to the conventional method, before the base color paint 6 is applied, the paint 7 having a different color is applied to the ceramic siding 1. A coating method in this case is not particularly limited, and for example, a method using a spray coater or a flow coater can be used. And the 1st coating film 4 of thickness: 20-50 micrometers is formed when the coating material 7 of the 1st color apply | coated to the whole surface of the ceramic siding 1 is dried.

その後、図１（ｂ）に示すように、目地状溝２の部分のみに２色目の塗料６をスプレー３で吹き付けて塗布する。ここで、２色目の塗料６とは、従来ベース色の塗料として使用されていたものをいい、市販されているものを任意に用いることができる。上述したように、本発明では、従来の方法とは逆に、ベース色とは異なる色の塗料７を塗布した後に、ベース色の塗料６を窯業系サイディング１に塗布するものである。この場合、ベース色の塗料である２色目の塗料６は目地状溝２の部分のみに塗布するため、上記のようにスプレー３を用いるようにしている。このスプレー３としては、特に限定されるものではないが、例えば、ノードソン（株）製「Ｘカットノズル」を備えた同社製「モデルＡ７Ａ型エアレス自動ガン」等を用いることができる。そして、目地状溝２の部分のみに塗布された２色目の塗料６が乾燥することによって、厚さ：４０〜１６０μｍの第２塗膜５が第１塗膜４の上に形成される。   Thereafter, as shown in FIG. 1B, the second color paint 6 is sprayed and applied only to the joint grooves 2. Here, the paint 6 of the second color refers to what has been conventionally used as a base color paint, and a commercially available one can be arbitrarily used. As described above, in the present invention, the base color paint 6 is applied to the ceramic siding 1 after the paint 7 having a color different from the base color is applied, contrary to the conventional method. In this case, since the second color paint 6 which is the base color paint is applied only to the joint groove 2, the spray 3 is used as described above. Although it does not specifically limit as this spray 3, For example, the company "model A7A type airless automatic gun" provided with "X cut nozzle" by Nordson Co., Ltd., etc. can be used. And the 2nd coating material 6 of thickness: 40-160 micrometers is formed on the 1st coating film 4 by drying the coating material 6 of the 2nd color apply | coated only to the part of the joint groove | channel 2.

上記のような２色塗り分けの塗装方法にあっては、目地状溝２以外の部分では、第１塗膜４のみが存在し、２色の塗料６，７が塗り重ねられることはないので、内側の塗膜４が外側に露出するなどという現象は起こり得ない。そして、第１塗膜４の形成は、スプレーコーターやフローコーターによる方法を使用して行うことができるので、塗り残しが生じることはなく、窯業系サイディング１の表面状態や板厚の影響を受けずに安定した塗装が可能となるものである。   In the two-color coating method as described above, only the first coating film 4 is present in portions other than the joint grooves 2, and the two-color paints 6 and 7 are not repeatedly applied. The phenomenon that the inner coating film 4 is exposed to the outside cannot occur. And since formation of the 1st coating film 4 can be performed using the method by a spray coater or a flow coater, an unpainted part does not arise and is influenced by the surface state and plate | board thickness of the ceramics-type siding 1. Stable painting is possible.

また、上記のように目地状溝２以外の部分では、２色の塗料６，７を塗り重ねる必要はなく、第１塗膜４のみを形成すればよいので、従来よりも塗装コストを削減することができるものである。特に、２色目の塗料６（ベース色の塗料）で着色される面積の少ない商品を製造する場合には、２色目の塗料６の使用量が減少することによって、大幅な塗装コストの削減を図ることができる。   Further, as described above, in the portions other than the joint grooves 2, it is not necessary to apply the two-color paints 6, 7, and only the first coating film 4 needs to be formed. It is something that can be done. In particular, when a product with a small area colored with the second color paint 6 (base color paint) is manufactured, the amount of use of the second color paint 6 is reduced, thereby greatly reducing the coating cost. be able to.

また、上記のような２色塗り分けの塗装方法にあっては、目地状溝２の部分では第１塗膜４を形成した後に第２塗膜５を形成するので、２色の塗料６，７が全く異なる系統の色であっても、目地状溝２の部分とこれ以外の部分との境界を容易に直線状とすることができ、２色塗り分けの外観を良くすることができるものである。特に、目地状溝２の内面全体に第２塗膜５を形成するのではなく、図２に示すように、目地状溝２の底面２ａにおいて目地状溝２の内側面２ｂから若干離して第２塗膜５を形成するのが好ましい。具体的には、目地状溝２の底面２ａの幅が８ｍｍである場合には、目地状溝２の両側の内側面２ｂから１ｍｍずつ離して、幅６ｍｍの第２塗膜５を形成するのが好ましい。このようにすることで、目地状溝２の部分とこれ以外の部分との境界の直線性をさらに十分に出すことができ、２色塗り分けの外観をより優れたものとすることができるものである。   In the two-color coating method as described above, since the second coating film 5 is formed after the first coating film 4 is formed in the joint grooves 2, the two-color paint 6, Even if 7 is a completely different system color, the boundary between the joint groove 2 and the other part can be easily made linear, and the appearance of two colors can be improved. It is. In particular, the second coating film 5 is not formed on the entire inner surface of the joint groove 2, but the second bottom surface 2 a of the joint groove 2 is slightly separated from the inner surface 2 b of the joint groove 2 as shown in FIG. It is preferable to form two coating films 5. Specifically, when the width of the bottom surface 2a of the joint groove 2 is 8 mm, the second coating film 5 having a width of 6 mm is formed by separating the inner surface 2b on both sides of the joint groove 2 by 1 mm. Is preferred. By doing in this way, the linearity of the boundary between the portion of the joint groove 2 and the other portion can be more sufficiently obtained, and the appearance of two-color coating can be further improved. It is.

以下、本発明を実施例によって具体的に説明する。   Hereinafter, the present invention will be specifically described by way of examples.

窯業系サイディング１としては、主原料としてセメントを用いて板状に成形し、養生・硬化させたものを用いた。また、窯業系サイディング１の大きさは、縦：３．０３ｍ×横：０．４５５ｍであり、板厚：１３ｍｍである。また、窯業系サイディング１の屋外側の面には目地状溝２（幅：８ｍｍ、深さ：４ｍｍ）を３列凹設した。   As the ceramic siding 1, a material formed into a plate using cement as a main raw material and cured and cured was used. Moreover, the magnitude | size of the ceramics system siding 1 is length: 3.03m x width: 0.455m, and plate | board thickness: 13mm. In addition, joint-like grooves 2 (width: 8 mm, depth: 4 mm) were recessed in three rows on the outdoor side surface of the ceramic siding 1.

まず、図１（ａ）に示すように、窯業系サイディング１の表面全体（目地状溝２の内面を含む）に１色目の塗料７として、アクリルエマルジョン系塗料を塗布した。この場合の塗布方法としては、スプレーによる方法を使用した。そして、窯業系サイディング１の表面全体に塗布した１色目の塗料７を乾燥させることによって、第１塗膜４を形成した。   First, as shown in FIG. 1A, an acrylic emulsion paint was applied as the first color paint 7 to the entire surface of the ceramic siding 1 (including the inner surface of the joint groove 2). As a coating method in this case, a spray method was used. And the 1st coating film 4 was formed by drying the coating material 7 of the 1st color apply | coated to the whole surface of the ceramics system siding 1. FIG.

その後、第１塗膜４が形成された窯業系サイディング１をベルトコンベア（図示省略）で搬送しながら、図１（ｂ）に示すように、目地状溝２の部分のみに２色目の塗料６（ベース色の塗料）をスプレー３で吹き付けて塗布した。ここで、２色目の塗料６としては、「大日本塗料（株）製アクリルエマルジョンエナメル塗料ホワイト系色」を用いた。また、スプレー３として、ノードソン（株）製「Ｘカットノズル」を備えた同社製「モデルＡ７Ａ型エアレス自動ガン」を用いた。スプレー３と窯業系サイディング１との距離は約１０ｍｍに設定した。そして、目地状溝２の部分のみに塗布した２色目の塗料６を乾燥させることによって、第２塗膜５を第１塗膜４の上に形成した。   Then, while conveying the ceramic siding 1 on which the first coating film 4 is formed by a belt conveyor (not shown), as shown in FIG. (Base color paint) was applied by spraying with spray 3. Here, as the paint 6 of the second color, “Dai Nippon Paint Co., Ltd. acrylic emulsion enamel paint white color” was used. As the spray 3, a “model A7A type airless automatic gun” manufactured by Nordson Co., Ltd. equipped with an “X cut nozzle” was used. The distance between the spray 3 and the ceramics siding 1 was set to about 10 mm. And the 2nd coating film 5 was formed on the 1st coating film 4 by drying the coating material 6 of the 2nd color apply | coated only to the part of the joint groove 2.

下記［表１］に示すようにコンベア速度、ノズル、液圧、吐出量の条件を変更して、上述した一連の作業を実施例１〜５として行った。   As shown in [Table 1] below, the conditions of the conveyor speed, nozzle, hydraulic pressure, and discharge amount were changed, and the series of operations described above were performed as Examples 1-5.

Figure 2006088118
Figure 2006088118

実施例１〜５の仕上がりはいずれも良好であったが、実施例４の仕上がりは、図２に示すようなものとなり、特に良好であった。   The finishes of Examples 1 to 5 were all good, but the finish of Example 4 was as shown in FIG.

本発明の実施の形態の一例を示すものであり、（ａ）（ｂ）は概略断面図である。An example of embodiment of this invention is shown, (a) (b) is a schematic sectional drawing. 同上の一部を拡大して示す断面図である。It is sectional drawing which expands and shows a part of the same as the above. 従来の技術の一例を示すものであり、（ａ）（ｂ）は概略断面図である。An example of the prior art is shown and (a) and (b) are schematic sectional views. 同上の一部を拡大して示す断面図である。It is sectional drawing which expands and shows a part of the same as the above.

符号の説明Explanation of symbols

１ 窯業系サイディング
２ 目地状溝
３ スプレー
４ 第１塗膜
５ 第２塗膜
６ ２色目の塗料
７ １色目の塗料 DESCRIPTION OF SYMBOLS 1 Ceramics system siding 2 Joint groove 3 Spray 4 1st coating film 5 2nd coating film 6 2nd color paint 7 1st color paint

Claims (2)

窯業系サイディングに凹設された目地状溝の部分とこれ以外の部分とを２色に塗り分けて塗装するにあたって、窯業系サイディングの表面全体に１色目の塗料を塗布した後、目地状溝の部分のみに２色目の塗料をスプレーで吹き付けて塗布することを特徴とする窯業系サイディングの塗装方法。   When coating the jointed groove part recessed in the ceramic siding and the other part separately in two colors, after applying the first color paint to the entire surface of the ceramic siding, A method for painting ceramic siding, characterized in that the second color paint is sprayed on only the part and applied. 目地状溝を凹設して形成されると共に、目地状溝の部分とこれ以外の部分とが２色に塗り分けられて塗装された窯業系サイディングにおいて、窯業系サイディングの表面全体に１色目の塗料が塗布されて第１塗膜が形成されていると共に、目地状溝の部分のみに２色目の塗料が塗布されて第２塗膜が形成されていることを特徴とする窯業系サイディング。
In the ceramic siding that is formed by recessing the joint groove and the joint groove portion and the other portion are separately painted in two colors, the first color is applied to the entire surface of the ceramic siding. A ceramic siding characterized in that a first paint film is formed by applying a paint, and a second paint film is formed by applying a second color paint only to the joint grooves.
JP2004280325A 2004-09-27 2004-09-27 Ceramic siding and coating method therefor Pending JP2006088118A (en)