JP2006072134A - Dye-containing negative curable composition, and color filter, and method for producing color filter - Google Patents

Dye-containing negative curable composition, and color filter, and method for producing color filter Download PDF

Info

Publication number
JP2006072134A
JP2006072134A JP2004257480A JP2004257480A JP2006072134A JP 2006072134 A JP2006072134 A JP 2006072134A JP 2004257480 A JP2004257480 A JP 2004257480A JP 2004257480 A JP2004257480 A JP 2004257480A JP 2006072134 A JP2006072134 A JP 2006072134A
Authority
JP
Japan
Prior art keywords
dye
acid
curable composition
containing negative
negative curable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2004257480A
Other languages
Japanese (ja)
Inventor
Toru Fujimori
亨 藤森
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujifilm Holdings Corp
Original Assignee
Fuji Photo Film Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuji Photo Film Co Ltd filed Critical Fuji Photo Film Co Ltd
Priority to JP2004257480A priority Critical patent/JP2006072134A/en
Publication of JP2006072134A publication Critical patent/JP2006072134A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a dye-containing negative curable composition having high sensitivity, capable of forming a rectangular pattern and ensuring less residue in an unexposed portion, and provide a color filter using the curable composition, and a method for producing the color filter. <P>SOLUTION: The dye-containing negative curable composition comprises at least (A) an alkali-soluble binder, (B) an organic-solvent-soluble dye, (C) a photopolymerization initiator, (D) a radical polymerizable monomer, and (E) an organic solvent, wherein the alkali-soluble binder (A) is a resin having an unsaturated double bond in a side chain. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

本発明は、液晶表示素子（ＬＣＤ）や固体撮像素子（ＣＣＤ、ＣＭＯＳなど）等に用いられるカラーフィルタを構成する着色画像の形成に好適な染料含有ネガ型硬化性組成物、並びに該染料含有ネガ型硬化性組成物を用いたカラーフィルタおよびその製造方法に関する。   The present invention relates to a dye-containing negative curable composition suitable for forming a colored image constituting a color filter used in a liquid crystal display device (LCD), a solid-state image pickup device (CCD, CMOS, etc.), and the dye-containing negative. The present invention relates to a color filter using a mold curable composition and a method for producing the same.

液晶表示素子や固体撮像素子に用いられるカラーフィルタを作製する方法としては、染色法、印刷法、電着法および顔料分散法が知られている。   As a method for producing a color filter used for a liquid crystal display device or a solid-state imaging device, a dyeing method, a printing method, an electrodeposition method, and a pigment dispersion method are known.

このうち、顔料分散法は、顔料を種々の感光性組成物に分散させた着色感放射線性組成物を用いてフォトリソ法によってカラーフィルタを作製する方法であり、顔料を使用しているために光や熱等に安定であるという利点を有している。また、フォトリソ法によってパターニングするため、位置精度が高く、大画面、高精細カラーディスプレイ用カラーフィルタを作製するのに好適な方法として広く利用されてきた。   Among these, the pigment dispersion method is a method for producing a color filter by a photolithography method using a colored radiation-sensitive composition in which a pigment is dispersed in various photosensitive compositions. It has the advantage of being stable to heat and the like. Further, since patterning is performed by a photolithography method, it has been widely used as a suitable method for manufacturing a color filter for a large-screen, high-definition color display with high positional accuracy.

顔料分散法によりカラーフィルタを作製する場合、ガラス基板上に感放射線性組成物をスピンコーターやロールコーター等により塗布し乾燥させて塗膜を形成し、該塗膜をパターン露光・現像することによって着色された画素が形成され、この操作を各色ごとに繰り返し行なうことでカラーフィルタを得ることができる。   When producing a color filter by a pigment dispersion method, a radiation sensitive composition is applied on a glass substrate by a spin coater or a roll coater and dried to form a coating film, and the coating film is subjected to pattern exposure and development. Colored pixels are formed, and a color filter can be obtained by repeating this operation for each color.

前記の顔料分散法としては、アルカリ可溶性樹脂に光重合性モノマーと光重合開始剤とを併用したネガ型感光性組成物が記載されたものがある（例えば、特許文献１〜４参照。）。   Examples of the pigment dispersion method include a negative photosensitive composition in which a photopolymerizable monomer and a photopolymerization initiator are used in combination with an alkali-soluble resin (see, for example, Patent Documents 1 to 4).

また、近年固体撮像素子用のカラーフィルタにおいては更なる高精細化が望まれている。しかしながら、従来の顔料分散系では解像度を更に向上させることは困難であり、顔料の粗大粒子により色ムラが発生する等の問題がある。このため、固体撮像素子のように微細パターンが要求される用途には適さなかった。   In recent years, there has been a demand for higher definition in color filters for solid-state imaging devices. However, it is difficult to further improve the resolution in the conventional pigment dispersion system, and there is a problem that color unevenness occurs due to the coarse particles of the pigment. For this reason, it was not suitable for uses requiring a fine pattern such as a solid-state imaging device.

かかる問題を解決すべく、従来から顔料に代えて染料を使用する技術が提案されている（例えば、特許文献５参照。）。しかしながら、一般的に染料を含有する硬化性組成物は、例えば、耐光性、耐熱性、溶解性、塗布均一性など様々な性能につき、顔料を用いた硬化性組成物に比べて劣るという問題があった。特に固体撮像素子用カラーフィルタ作製用途の場合には１．５μｍ以下の膜厚が要求されるため、硬化性組成物中に多量の色素を添加しなければならず、これにより基板との密着が不充分となったり、十分な硬化が得られなかったり、露光部でも染料が抜けてしまうなど、パターン形成性が著しく困難であるといった問題も生じていた。   In order to solve such a problem, a technique of using a dye instead of a pigment has been conventionally proposed (for example, see Patent Document 5). However, in general, a curable composition containing a dye is inferior to a curable composition using a pigment in terms of various properties such as light resistance, heat resistance, solubility, and coating uniformity. there were. In particular, in the case of a color filter manufacturing application for a solid-state image sensor, a film thickness of 1.5 μm or less is required, so that a large amount of dye must be added to the curable composition, and thereby adhesion to the substrate can be improved. There have also been problems that pattern formation is extremely difficult, such as insufficientness, insufficient curing, and loss of dye even in exposed areas.

特開平２−１８１７０４号公報JP-A-2-181704 特開平２−１９９４０３号公報JP-A-2-199403 特開平５−２７３４１１号公報Japanese Patent Laid-Open No. 5-273411 特開平７−１４０６５４号公報JP-A-7-140654 特開平６−７５３７５号公報JP-A-6-75375

したがって、本発明の目的は、染料を使用するのに好適な染料含有ネガ型硬化性組成物を提供することであり、具体的には、高感度で未露光部分に残渣がなく、矩形な微細パターン形成が可能な染料含有ネガ型硬化性組成物を提供することにある。また、同時に優れたカラーフィルタを製造し得、コストパフォーマンスの高いカラーフィルタ、特には固体撮像素子用のカラーフィルタの製造方法を提供することを目的とする。   Accordingly, an object of the present invention is to provide a dye-containing negative curable composition suitable for using a dye. Specifically, the dye-containing negative curable composition has high sensitivity, no residue in an unexposed portion, and a rectangular fine pattern. It is an object of the present invention to provide a dye-containing negative curable composition capable of forming a pattern. It is another object of the present invention to provide a method for producing a color filter with high cost performance, particularly a color filter for a solid-state imaging device, which can simultaneously produce an excellent color filter.

前記課題を解決するための具体的手段は以下の通りである。
＜１＞ （Ａ）アルカリ可溶性バインダーと、（Ｂ）有機溶剤可溶性染料と、（Ｃ）光重合開始剤と、（Ｄ）ラジカル重合性モノマーと、（Ｅ）有機溶剤と、を少なくとも含む染料含有ネガ型硬化性組成物であって、前記（Ａ）アルカリ可溶性バインダーが、側鎖に不飽和二重結合を有する樹脂であることを特徴とする染料含有ネガ型硬化性組成物である。 Specific means for solving the above problems are as follows.
<1> A dye containing at least: (A) an alkali-soluble binder, (B) an organic solvent-soluble dye, (C) a photopolymerization initiator, (D) a radical polymerizable monomer, and (E) an organic solvent. It is a negative curable composition, wherein the (A) alkali-soluble binder is a resin having an unsaturated double bond in the side chain.

＜２＞ 前記（Ｂ）有機溶剤可溶性染料が、少なくとも吸収特性の異なる２種の染料の混合物からなることを特徴とする上記＜１＞の染料含有ネガ型硬化性組成物である。   <2> The dye-containing negative curable composition according to <1>, wherein the organic solvent-soluble dye (B) comprises a mixture of at least two kinds of dyes having different absorption characteristics.

＜３＞ 前記（Ｃ）光重合開始剤がオキシム系化合物であることを特徴とする上記＜１＞または＜２＞の染料含有ネガ型硬化性組成物である。   <3> The dye-containing negative curable composition according to <1> or <2>, wherein the (C) photopolymerization initiator is an oxime compound.

＜４＞ 前記（Ｅ）有機溶剤が環状ケトン溶剤であることを特徴とする上記＜１＞〜＜３＞の染料含有ネガ型硬化性組成物である。   <4> The dye-containing negative curable composition according to <1> to <3>, wherein the organic solvent (E) is a cyclic ketone solvent.

＜５＞ 前記（Ｅ）有機溶剤が、環状ケトン溶剤とさらに別の１種の有機溶剤とを含む少なくとも２種の混合溶剤であることを特徴とする上記＜１＞〜＜３＞の染料含有ネガ型硬化性組成物である。   <5> The above-mentioned <1> to <3> containing a dye, wherein the organic solvent (E) is at least two mixed solvents including a cyclic ketone solvent and another organic solvent. It is a negative curable composition.

＜６＞ 上記＜１＞〜＜５＞の染料含有ネガ型硬化性組成物を用いてなることを特徴とするカラーフィルタである。   <6> A color filter comprising the dye-containing negative curable composition according to <1> to <5> above.

＜７＞ 上記＜１＞〜＜５＞の染料含有ネガ型硬化性組成物を、支持体上に塗布後、マスクを通して露光し、現像してパターンを形成する工程を含むことを特徴とするカラーフィルタの製造方法である。   <7> A color comprising the steps of applying the dye-containing negative curable composition of the above <1> to <5> onto a support, exposing through a mask, and developing to form a pattern. It is a manufacturing method of a filter.

本発明によれば、高感度で、矩形なパターン形成が可能（特にステッパー露光によりパターン形成した時）であり、且つ、未露光部分に残渣のない染料含有ネガ型硬化性組成物を提供することができる。また、本発明によれば、パターン形成性に優れ、コストパフォーマンスの高いカラーフィルタおよびその製造方法を提供することができる。   According to the present invention, there is provided a dye-containing negative curable composition having a high sensitivity and capable of forming a rectangular pattern (particularly when a pattern is formed by stepper exposure) and having no residue in an unexposed portion. Can do. Further, according to the present invention, it is possible to provide a color filter excellent in pattern formability and high cost performance, and a manufacturing method thereof.

以下、本発明の染料含有ネガ型硬化性組成物、並びに該染料含有ネガ型硬化性組成物を用いて構成されるカラーフィルタおよびその製造方法について詳述する。   Hereinafter, the dye-containing negative curable composition of the present invention, a color filter constituted using the dye-containing negative curable composition, and a method for producing the same will be described in detail.

《染料含有ネガ型硬化性組成物》
本発明の染料含有ネガ型硬化性組成物は、（Ａ）アルカリ可溶性バインダーと、（Ｂ）有機溶剤可溶性染料と、（Ｃ）光重合開始剤と、（Ｄ）ラジカル重合性モノマーと、（Ｅ）有機溶剤と、を少なくとも含み、上記（Ａ）アルカリ可溶性バインダーが側鎖に不飽和二重結合を有する樹脂であることを特徴とする。本発明の染料含有ネガ型硬化性組成物は、側鎖に不飽和二重結合を有する樹脂をアルカリ可溶性バインダーとして含むことで、高感度で、未露光部分に残渣がなく、且つ、これを用いて形成されるパターンの矩形性を向上させることができる。 << Dye-containing negative curable composition >>
The dye-containing negative curable composition of the present invention comprises (A) an alkali-soluble binder, (B) an organic solvent-soluble dye, (C) a photopolymerization initiator, (D) a radical polymerizable monomer, (E And (A) the alkali-soluble binder is a resin having an unsaturated double bond in the side chain. The dye-containing negative curable composition of the present invention contains a resin having an unsaturated double bond in the side chain as an alkali-soluble binder, so that it has high sensitivity and no residue in an unexposed portion. The rectangularity of the pattern formed can be improved.

本発明の染料含有ネガ型硬化性組成物は、プロキシミティ方式、ミラープロジェクション方式、およびステッパー方式のいずれの方式で露光をおこなってもよいが、特に、ステッパー方式（縮小投影露光機を用いた縮小投影露光方式）で露光をおこなうのが好ましい。係るステッパー方式は、露光量を段階的に変動しながら露光をおこなうことによってパターンを形成するものであり、かかるステッパー露光を行った際に特に本発明の効果の一つであるパターンの矩形性を良好にすることができる。
また、上記ステッパー露光に用いる露光装置としては、例えば、ｉ線ステッパー（商品名：ＦＰＡ−３０００ｉ５＋、キャノン（株）製）等を用いることができる。 The dye-containing negative curable composition of the present invention may be exposed by any of a proximity method, a mirror projection method, and a stepper method, and in particular, a stepper method (reduction using a reduction projection exposure machine). It is preferable to perform exposure by a projection exposure method. Such a stepper method forms a pattern by performing exposure while varying the exposure amount stepwise, and the rectangularity of the pattern, which is one of the effects of the present invention, particularly when performing such stepper exposure. Can be good.
As an exposure apparatus used for the stepper exposure, for example, an i-line stepper (trade name: FPA-3000i5 +, manufactured by Canon Inc.) can be used.

−（Ａ）アルカリ可溶性バインダー−
まず、本発明におけるアルカリ可溶性バインダーについて説明する。本発明におけるアルカリ可溶性バインダーは、側鎖に不飽和二重結合を有する樹脂である。本発明におけるアルカリ可溶性バインダーとしては、アルカリ可溶性であり、且つ、側鎖に不飽和二重結合を有する樹脂であれば特に限定はないが、耐熱性、現像性、入手性等の観点から選ばれることが好ましい。 -(A) Alkali-soluble binder-
First, the alkali-soluble binder in the present invention will be described. The alkali-soluble binder in the present invention is a resin having an unsaturated double bond in the side chain. The alkali-soluble binder in the present invention is not particularly limited as long as it is an alkali-soluble resin having an unsaturated double bond in the side chain, but is selected from the viewpoints of heat resistance, developability, availability, and the like. It is preferable.

前記アルカリ可溶性バインダーとしては、線状有機高分子重合体で、有機溶剤に可溶で、弱アルカリ水溶液で現像できるものが好ましい。このような線状有機高分子重合体としては、側鎖にカルボン酸を有するポリマー、例えば特開昭５９−４４６１５号、特公昭５４−３４３２７号、特公昭５８−１２５７７号、特公昭５４−２５９５７号、特開昭５９−５３８３６号、特開昭５９−７１０４８号の各公報に記載されているような、メタクリル酸共重合体、アクリル酸共重合体、イタコン酸共重合体、クロトン酸共重合体、マレイン酸共重合体、部分エステル化マレイン酸共重合体等が挙げられ、また同様に側鎖にカルボン酸を有する酸性セルロース誘導体が有用である。   The alkali-soluble binder is preferably a linear organic polymer, soluble in an organic solvent, and developable with a weak alkaline aqueous solution. Examples of such linear organic high molecular polymers include polymers having a carboxylic acid in the side chain, such as JP-A-59-44615, JP-B-54-34327, JP-B-58-12777, and JP-B-54-25957. Methacrylic acid copolymer, acrylic acid copolymer, itaconic acid copolymer, crotonic acid copolymer, as described in JP-A-59-53836 and JP-A-59-71048. Examples thereof include polymers, maleic acid copolymers, partially esterified maleic acid copolymers, and acidic cellulose derivatives having a carboxylic acid in the side chain are also useful.

但し、本発明にアルカリ可溶性樹脂は側鎖に不飽和二重結合を有することが必要であることから、上記に示したようなユニットを有する樹脂に不飽和二重結合を有するユニットを共重合した樹脂であることが必要である。本発明におけるアルカリ可溶性樹脂の側鎖に結合される不飽和二重結合としては、例えば、アリル基、（メタ）アクリル基、ビニル基などが挙げられ、アリル基、（メタ）アクリル基が好ましい。これら不飽和二重結合は、該不飽和二重結合を有するユニットを共重合して導入してもよいし、後からポリマー反応で導入してもよい。本発明におけるアルカリ可溶性バインダーとしては、例えば、ＫＳレジストー１０６（大阪有機化学工業（株）製）、サイクロマーＰシリーズ（ダイセル化学工業（株）製）等が好適に用いられる。   However, since the alkali-soluble resin in the present invention needs to have an unsaturated double bond in the side chain, a unit having an unsaturated double bond was copolymerized with a resin having a unit as shown above. It must be a resin. As an unsaturated double bond couple | bonded with the side chain of alkali-soluble resin in this invention, an allyl group, a (meth) acryl group, a vinyl group etc. are mentioned, for example, An allyl group and a (meth) acryl group are preferable. These unsaturated double bonds may be introduced by copolymerizing the unit having the unsaturated double bond or may be introduced later by a polymer reaction. As the alkali-soluble binder in the present invention, for example, KS resist 106 (manufactured by Osaka Organic Chemical Industry Co., Ltd.), cyclomer P series (manufactured by Daicel Chemical Industries, Ltd.) and the like are preferably used.

上記アルカリ可溶性バインダーとしては、現像性、液粘度等の観点から重量平均分子量（ＧＰＣ法で測定されたポリスチレン換算値）が１０００〜２×１０5の重合体が好ましく、２０００〜１×１０5の重合体がより好ましく、５０００〜５×１０4の重合体が特に好ましい。 Examples of the alkali-soluble binder, developability, the weight-average molecular weight from the viewpoint of liquid viscosity polymer (measured in terms of polystyrene by GPC method) of 1,000-2 × 10 5 is preferable, a 2,000-1 × 10 5 A polymer is more preferable, and a 5000 to 5 × 10 4 polymer is particularly preferable.

上記アルカリ可溶性バインダーの含有量は、現像性等の観点から、組成物中の全固形分に対して１０〜９０質量％が好ましく、２０〜８０質量％がさらに好ましく、３０〜７０質量％が特に好ましい。
また、本発明の染料含有ネガ型硬化性組成物は、本発明におけるアルカリ可溶性バインダーと、他の公知のアルカリ可溶性バインダーを併用することができる。上記他の公知のアルカリ可溶性バインダーとしては、上述の線状有機高分子重合体として例示したものであって側鎖に不飽和二重結合を有さないものを用いることができる。本発明におけるアルカリ可溶性バインダーと他の公知のアルカリ可溶性バインダーとを併用する場合、全アルカリ可溶性バインダーの総量に占める本発明におけるアルカリ可溶性バインダーの含有量は、２０質量％以上であることが好ましく、３０質量％以上であることが更に好ましい。 The content of the alkali-soluble binder is preferably 10 to 90% by mass, more preferably 20 to 80% by mass, and particularly preferably 30 to 70% by mass with respect to the total solid content in the composition from the viewpoint of developability and the like. preferable.
Moreover, the dye-containing negative curable composition of the present invention can be used in combination with the alkali-soluble binder of the present invention and other known alkali-soluble binders. As said other well-known alkali-soluble binder, what was illustrated as the above-mentioned linear organic high molecular polymer, and does not have an unsaturated double bond in a side chain can be used. When using together the alkali-soluble binder in this invention and another well-known alkali-soluble binder, it is preferable that content of the alkali-soluble binder in this invention which occupies the total amount of all the alkali-soluble binders is 20 mass% or more, 30 More preferably, it is at least mass%.

−（Ｂ）有機溶剤可溶性染料−
本発明における有機溶剤可溶性染料は、特に制限なく使用することができ、例えば、従来カラーフィルタ用として公知の染料などが挙げられる。上記公知の染料としては、例えば、特開昭６４−９０４０３号公報、特開昭６４−９１１０２号公報、特開平１−９４３０１号公報、特開平６−１１６１４号公報、特登２５９２２０７号、米国特許第４，８０８，５０１号明細書、米国特許第５，６６７，９２０号明細書、米国特許第５，０５９，５００号明細書、特開平５−３３３２０７号公報、特開平６−３５１８３号公報、特開平６−５１１１５号公報、特開平６−１９４８２８号公報等に記載の色素が挙げられる。本発明における有機溶剤可溶性染料として用いることのできる染料の化学構造としては、トリフェニルメタン系、アントラキノン系、ベンジリデン系、オキソノール系、シアニン系、フェノチアジン系、ピロロピラゾールアゾメチン系、キサンテン系、フタロシアニン系、ベンゾピラン系、インジゴ系、等が挙げられる。本発明における有機溶剤可溶性染料として特に好ましくは、ピラゾールアゾ系、アニリノアゾ系、ピラゾロトリアゾールアゾ系、ピリドンアゾ系、アントラキノン系、アンスラピリドン系の染料である。 -(B) Organic solvent soluble dye-
The organic solvent-soluble dye in the present invention can be used without particular limitation, and examples thereof include conventionally known dyes for color filters. Examples of the known dye include, for example, JP-A 64-90403, JP-A 64-91102, JP-A-1-94301, JP-A-6-11614, Tokuho 2592207, US Patent No. 4,808,501, U.S. Pat.No. 5,667,920, U.S. Pat.No. 5,059,500, JP-A-5-333207, JP-A-6-35183, Examples thereof include dyes described in JP-A-6-51115 and JP-A-6-194828. The chemical structure of the dye that can be used as the organic solvent-soluble dye in the present invention includes triphenylmethane, anthraquinone, benzylidene, oxonol, cyanine, phenothiazine, pyrrolopyrazole azomethine, xanthene, phthalocyanine, A benzopyran type, an indigo type, etc. are mentioned. Particularly preferred as the organic solvent-soluble dye in the present invention are pyrazole azo dyes, anilinoazo dyes, pyrazolotriazole azo dyes, pyridone azo dyes, anthraquinone dyes, and anthrapyridone dyes.

また、水またはアルカリ現像を行うレジスト系の場合には現像によりバインダーおよび／または染料を完全に除去するという観点から、本発明における有機溶剤可溶性染料として酸性染料および／またはその誘導体が好適に使用できることがある。そのほか、本発明における有機溶剤可溶性染料としては、直接染料、塩基性染料、媒染染料、酸性媒染染料、アゾイック染料、分散染料、油溶染料、食品染料、および／またはこれらの誘導体等も好適に使用することができる。   In the case of a resist system that performs water or alkali development, an acid dye and / or a derivative thereof can be preferably used as the organic solvent-soluble dye in the present invention from the viewpoint of completely removing the binder and / or dye by development. There is. In addition, as the organic solvent-soluble dye in the present invention, direct dyes, basic dyes, mordant dyes, acid mordant dyes, azoic dyes, disperse dyes, oil-soluble dyes, food dyes, and / or derivatives thereof are also preferably used. can do.

（酸性染料）
上記酸性染料について説明する。酸性染料は、スルホン酸やカルボン酸やフェノール性水酸基等の酸性基を有する色素であれば特に限定されないが、有機溶剤や現像液に対する溶解性、塩基性化合物との塩形成性、吸光度、硬化性組成物中の他の成分との相互作用、耐光性、耐熱性等の必要とされる性能の全てを考慮して選択される。 (Acid dyes)
The acid dye will be described. The acidic dye is not particularly limited as long as it is a dye having an acidic group such as sulfonic acid, carboxylic acid, phenolic hydroxyl group, etc., but is soluble in an organic solvent or a developer, salt-forming with a basic compound, absorbance, curability. It is selected in consideration of all required performance such as interaction with other components in the composition, light resistance, heat resistance and the like.

以下、上記酸性染料の具体例を挙げる。但し、本発明においてはこれらに限定されるものではない。例えば、
ａｃｉｄ ａｌｉｚａｒｉｎ ｖｉｏｌｅｔ Ｎ；
ａｃｉｄ ｂｌａｃｋ １，２，２４，４８；
ａｃｉｄ ｂｌｕｅ １，７，９，１５，１８，２３，２５，２７，２９，４０，４２，４５，５１，６２，７０，７４，８０，８３，８６，８７，９０，９２，９６，１０３，１１２，１１３，１２０，１２９，１３８，１４７，１５０，１５８，１７１，１８２，１９２，２１０，２４２，２４３，２５６，２５９，２６７，２７８，２８０，２８５，２９０，２９６，３１５，３２４：１，３３５，３４０；
ａｃｉｄ ｃｈｒｏｍｅ ｖｉｏｌｅｔ Ｋ；
ａｃｉｄ Ｆｕｃｈｓｉｎ；
ａｃｉｄ ｇｒｅｅｎ １，３，５，９，１６，２５，２７，５０，５８，６３，６５，８０，１０４，１０５，１０６，１０９；
ａｃｉｄ ｏｒａｎｇｅ ６，７，８，１０，１２，２６，５０，５１，５２，５６，６２、６３，６４、７４，７５、９４、９５，１０７，１０８，１６９，１７３； Hereinafter, specific examples of the acid dye will be given. However, the present invention is not limited to these. For example,
acid alizarin violet N;
acid black 1, 2, 24, 48;
acid blue 1,7,9,15,18,23,25,27,29,40,42,45,51,62,70,74,80,83,86,87,90,92,96,103, 112, 113, 120, 129, 138, 147, 150, 158, 171, 182, 192, 210, 242, 243, 256, 259, 267, 278, 280, 285, 290, 296, 315, 324: 1, 335, 340;
acid chroma violet K;
acid Fuchsin;
acid green 1,3,5,9,16,25,27,50,58,63,65,80,104,105,106,109;
acid orange 6, 7, 8, 10, 12, 26, 50, 51, 52, 56, 62, 63, 64, 74, 75, 94, 95, 107, 108, 169, 173;

ａｃｉｄ ｒｅｄ １，４，８，１４，１７，１８，２６，２７，２９，３１，３４，３５，３７，４２，４４，５０，５１，５２，５７，６６，７３，８０，８７，８８，９１，９２，９４，９７，１０３，１１１，１１４，１２９，１３３，１３４，１３８，１４３，１４５，１５０，１５１，１５８，１７６，１８２，１８３，１９８，２０６，２１１，２１５，２１６，２１７，２２７，２２８，２４９，２５２，２５７，２５８，２６０，２６１，２６６，２６８，２７０，２７４，２７７，２８０，２８１，１９５，３０８，３１２，３１５，３１６，３３９，３４１，３４５，３４６，３４９，３８２，３８３，３９４，４０１，４１２，４１７，４１８，４２２，４２６；
ａｃｉｄ ｖｉｏｌｅｔ ６Ｂ，７，９，１７，１９；
ａｃｉｄ ｙｅｌｌｏｗ １，３，７，９，１１，１７，２３，２５，２９，３４，３６，３８，４０、４２，５４，６５，７２，７３，７６，７９，９８，９９，１１１，１１２，１１３，１１４，１１６，１１９，１２３，１２８，１３４，１３５，１３８，１３９，１４０，１４４，１５０、１５５，１５７，１６０，１６１，１６３，１６８，１６９，１７２，１７７，１７８，１７９，１８４，１９０，１９３，１９６，１９７，１９９，２０２，２０３，２０４，２０５，２０７，２１２，２１４，２２０，２２１，２２８，２３０，２３２，２３５，２３８，２４０，２４２，２４３，２５１； acid red 1,4,8,14,17,18,26,27,29,31,34,35,37,42,44,50,51,52,57,66,73,80,87,88, 91, 92, 94, 97, 103, 111, 114, 129, 133, 134, 138, 143, 145, 150, 151, 158, 176, 182, 183, 198, 206, 211, 215, 216, 217, 227,228,249,252,257,258,260,261,266,268,270,274,277,280,281,195,308,312,315,316,339,341,345,346,349, 382, 383, 394, 401, 412, 417, 418, 422, 426;
acid violet 6B, 7, 9, 17, 19;
acid yellow 1,3,7,9,11,17,23,25,29,34,36,38,40,42,54,65,72,73,76,79,98,99,111,112, 113, 114, 116, 119, 123, 128, 134, 135, 138, 139, 140, 144, 150, 155, 157, 160, 161, 163, 168, 169, 172, 177, 178, 179, 184 190,193,196,197,199,202,203,204,205,207,212,214,220,221,228,230,232,235,238,240,242,243,251;

Ｄｉｒｅｃｔ Ｙｅｌｌｏｗ ２，３３，３４，３５，３８，３９，４３，４７，５０，５４，５８，６８，６９，７０，７１，８６，９３，９４，９５，９８，１０２，１０８，１０９，１２９，１３６，１３８，１４１；
Ｄｉｒｅｃｔ Ｏｒａｎｇｅ ３４，３９，４１，４６，５０，５２，５６，５７，６１，６４，６５，６８，７０，９６，９７，１０６，１０７；
Ｄｉｒｅｃｔ Ｒｅｄ ７９，８２，８３，８４，９１，９２，９６，９７，９８，９９，１０５，１０６，１０７，１７２，１７３，１７６，１７７，１７９，１８１，１８２，１８４，２０４，２０７，２１１，２１３，２１８，２２０，２２１，２２２，２３２，２３３，２３４，２４１，２４３，２４６，２５０；
Ｄｉｒｅｃｔ Ｖｉｏｌｅｔ ４７，５２，５４，５９，６０，６５，６６，７９，８０，８１，８２，８４，８９，９０，９３，９５，９６，１０３，１０４； Direct Yellow 2,33,34,35,38,39,43,47,50,54,58,68,69,70,71,86,93,94,95,98,102,108,109,129, 136, 138, 141;
Direct Orange 34, 39, 41, 46, 50, 52, 56, 57, 61, 64, 65, 68, 70, 96, 97, 106, 107;
Direct Red 79, 82, 83, 84, 91, 92, 96, 97, 98, 99, 105, 106, 107, 172, 173, 176, 177, 179, 181, 182, 184, 204, 207, 211, 213, 218, 220, 221, 222, 232, 233, 234, 241, 243, 246, 250;
Direct Violet 47, 52, 54, 59, 60, 65, 66, 79, 80, 81, 82, 84, 89, 90, 93, 95, 96, 103, 104;

Ｄｉｒｅｃｔ Ｂｌｕｅ ５７，７７，８０，８１，８４，８５，８６，９０，９３，９４，９５，９７，９８，９９，１００，１０１，１０６，１０７，１０８，１０９，１１３，１１４，１１５，１１７，１１９，１３７，１４９，１５０，１５３，１５５，１５６，１５８，１５９，１６０，１６１，１６２，１６３，１６４，１６６，１６７，１７０，１７１，１７２，１７３，１８８，１８９，１９０，１９２，１９３，１９４，１９６，１９８，１９９，２００，２０７，２０９，２１０，２１２，２１３，２１４，２２２，２２８，２２９，２３７，２３８，２４２，２４３，２４４，２４５，２４７，２４８，２５０，２５１，２５２，２５６，２５７，２５９，２６０，２６８，２７４，２７５，２９３；
Ｄｉｒｅｃｔ Ｇｒｅｅｎ ２５，２７，３１，３２，３４，３７，６３，６５，６６，６７，６８，６９，７２，７７，７９，８２；
Ｍｏｒｄａｎｔ Ｙｅｌｌｏｗ ５，８，１０，１６，２０，２６，３０，３１，３３，４２，４３，４５，５６，５０，６１，６２，６５；
Ｍｏｒｄａｎｔ Ｏｒａｎｇｅ ３，４，５，８，１２，１３，１４，２０，２１，２３，２４，２８，２９，３２，３４，３５，３６，３７，４２，４３，４７，４８； Direct Blue 57, 77, 80, 81, 84, 85, 86, 90, 93, 94, 95, 97, 98, 99, 100, 101, 106, 107, 108, 109, 113, 114, 115, 117, 119, 137, 149, 150, 153, 155, 156, 158, 159, 160, 161, 162, 163, 164, 166, 167, 170, 171, 172, 173, 188, 189, 190, 192, 193 194,196,198,199,200,207,209,210,212,213,214,222,228,229,237,238,242,243,244,245,247,248,250,251,252, 256, 257, 259, 260, 268, 274, 275, 293;
Direct Green 25, 27, 31, 32, 34, 37, 63, 65, 66, 67, 68, 69, 72, 77, 79, 82;
Modern Yellow 5, 8, 10, 16, 20, 26, 30, 31, 33, 42, 43, 45, 56, 50, 61, 62, 65;
Modern Orange 3, 4, 5, 8, 12, 13, 14, 20, 21, 23, 24, 28, 29, 32, 34, 35, 36, 37, 42, 43, 47, 48;

Ｍｏｒｄａｎｔ Ｒｅｄ １，２，３，４，９，１１，１２，１４，１７，１８，１９，２２，２３，２４，２５，２６，３０，３２，３３，３６，３７，３８，３９，４１，４３，４５，４６，４８，５３，５６，６３，７１，７４，８５，８６，８８，９０，９４，９５；
Ｍｏｒｄａｎｔ Ｖｉｏｌｅｔ ２，４，５，７，１４，２２，２４，３０，３１，３２，３７，４０，４１，４４，４５，４７，４８，５３，５８；
Ｍｏｒｄａｎｔ Ｂｌｕｅ ２，３，７，８，９，１２，１３，１５，１６，１９，２０，２１，２２，２３，２４，２６，３０，３１，３２，３９，４０，４１，４３，４４，４８，４９，５３，６１，７４，７７，８３，８４；
Ｍｏｒｄａｎｔ Ｇｒｅｅｎ １，３，４，５，１０，１５，１９，２６，２９，３３，３４，３５，４１，４３，５３；
Ｆｏｏｄ Ｙｅｌｌｏｗ ３；
およびこれらの染料の誘導体が挙げられる。 Modern Red 1, 2, 3, 4, 9, 11, 12, 14, 17, 18, 19, 22, 23, 24, 25, 26, 30, 32, 33, 36, 37, 38, 39, 41, 43, 45, 46, 48, 53, 56, 63, 71, 74, 85, 86, 88, 90, 94, 95;
Modern Violet 2, 4, 5, 7, 14, 22, 24, 30, 31, 32, 37, 40, 41, 44, 45, 47, 48, 53, 58;
Modern Blue 2, 3, 7, 8, 9, 12, 13, 15, 16, 19, 20, 21, 22, 23, 24, 26, 30, 31, 32, 39, 40, 41, 43, 44, 48, 49, 53, 61, 74, 77, 83, 84;
Modern Green 1, 3, 4, 5, 10, 15, 19, 26, 29, 33, 34, 35, 41, 43, 53;
Food Yellow 3;
And derivatives of these dyes.

上記の酸性染料の中でも、
ａｃｉｄ ｂｌａｃｋ ２４；
ａｃｉｄ ｂｌｕｅ ２３，２５，２９，６２，８０，８６，８７，９２，１３８，１５８，１８２，２４３，３２４：１；
ａｃｉｄ ｏｒａｎｇｅ ８，５１，５６，７４，６３，７４；
ａｃｉｄ ｒｅｄ １，４，８，３４，３７，４２，５２，５７，８０，９７，１１４，１４３，１４５，１５１，１８３，２１７，２４９；
ａｃｉｄ ｖｉｏｌｅｔ ７；
ａｃｉｄ ｙｅｌｌｏｗ １７，２５，２９，３４，４２，７２，７６，９９，１１１，１１２，１１４，１１６，１３４，１５５，１６９，１７２，１８４，２２０，２２８，２３０，２３２，２４３；
ａｃｉｄ Ｇｒｅｅｎ ２５；
などの染料およびこれらの染料の誘導体が好ましい。 Among the above acid dyes,
acid black 24;
acid blue 23, 25, 29, 62, 80, 86, 87, 92, 138, 158, 182, 243, 324: 1;
acid orange 8, 51, 56, 74, 63, 74;
acid red 1,4,8,34,37,42,52,57,80,97,114,143,145,151,183,217,249;
acid violet 7;
acid yellow 17, 25, 29, 34, 42, 72, 76, 99, 111, 112, 114, 116, 134, 155, 169, 172, 184, 220, 228, 230, 232, 243;
acid Green 25;
And the like and derivatives of these dyes are preferred.

また、上記以外の、アゾ系、キサンテン系、フタロシアニン系の酸性染料も好ましく、Ｃ．Ｉ．Ｓｏｌｖｅｎｔ Ｂｌｕｅ ４４，３８；Ｃ．Ｉ．Ｓｏｌｖｅｎｔ Ｏｒａｎｇｅ４５；Ｒｈｏｄａｍｉｎｅ Ｂ； Ｒｈｏｄａｍｉｎｅ １１０；２，７−Ｎａｐｈｔｈａｌｅｎｅｄｉｓｕｌｆｏｎｉｃ ａｃｉｄ；３−［（５−ｃｈｌｏｒｏ−２−ｐｈｅｎｏｘｙｐｈｅｎｙｌ）ｈｙｄｒａｚｏｎｏ］−３，４−ｄｉｈｙｄｒｏ−４−ｏｘｏ−５−［（ｐｈｅｎｙｌｓｕｌｆｏｎｙｌ）ａｍｉｎｏ］−，等の酸性染料およびこれらの染料の誘導体も好適に使用することができる。   Other than the above, azo, xanthene and phthalocyanine acid dyes are also preferred. I. Solvent Blue 44, 38; I. Solvent Orange 45; Rhodamine B; Rhodamine 110; 2,7-Naphthalendisulfonic acid; 3-[(5-chloro-2-phenoxyphenyl) hydrazono] -3,4-dihydro-4-oxo-5- [minyl]-[ulphonyl] , Etc. and derivatives of these dyes can also be suitably used.

上記酸性染料の誘導体としては、スルホン酸やカルボン酸等の酸性基を有する酸性染料の無機塩、酸性染料と含窒素化合物との塩、酸性染料のスルホンアミド体等が使用でき、硬化性組成物溶液として溶解させることができるものであれば特に限定されないが、有機溶剤や現像液に対する溶解性、吸光度、硬化性組成物中の他の成分との相互作用、耐光性、耐熱性等の必要とする性能の全てを考慮して選択される。   Examples of the derivative of the acid dye include inorganic salts of acid dyes having an acid group such as sulfonic acid and carboxylic acid, salts of acid dyes and nitrogen-containing compounds, sulfonamides of acid dyes, and the like, and curable compositions. It is not particularly limited as long as it can be dissolved as a solution, but it needs solubility, absorbance, interaction with other components in the curable composition, light resistance, heat resistance, etc. in an organic solvent or developer. It is selected in consideration of all the performance to be performed.

上記酸性染料と含窒素化合物との塩について説明する。酸性染料と含窒素化合物との塩を形成する方法は、酸性染料の溶解性改良（有機溶剤への溶解性付与）や、耐熱性および耐光性改良に効果的な場合がある。   The salt of the said acid dye and a nitrogen-containing compound is demonstrated. The method of forming a salt of an acid dye and a nitrogen-containing compound may be effective for improving the solubility of the acid dye (providing solubility in an organic solvent) and improving heat resistance and light resistance.

酸性染料と塩を形成する含窒素化合物、および酸性染料とアミド結合を形成する含窒素化合物について説明する。
含窒素化合物は、塩またはアミド化合物の有機溶剤や現像液に対する溶解性、塩形成性、染料の吸光度・色価、硬化性組成物中の他の成分との相互作用、着色剤としての耐熱性および耐光性等の全てを勘案して選択される。吸光度・色価の観点のみで選択する場合には、上記含窒素化合物としてはできるだけ分子量の低いものが好ましく、中でも分子量３００以下のものが好ましく、分子量２８０以下のものがより好ましく、分子量２５０以下のものが特に好ましい。 The nitrogen-containing compound that forms a salt with the acid dye and the nitrogen-containing compound that forms an amide bond with the acid dye will be described.
Nitrogen-containing compounds are the solubility of salts or amide compounds in organic solvents and developers, salt-forming properties, dye absorbance / color value, interaction with other components in the curable composition, and heat resistance as a colorant. In addition, it is selected in consideration of all of light resistance and the like. When selecting only from the viewpoint of absorbance and color value, the nitrogen-containing compound is preferably as low as possible in molecular weight, more preferably having a molecular weight of 300 or less, more preferably having a molecular weight of 280 or less, and a molecular weight of 250 or less. Those are particularly preferred.

酸性染料と含窒素化合物との塩における、含窒素化合物／酸性染料のモル比（以下、「ｎ」という。）について説明する。上記ｎは、酸性染料分子と対イオンであるアミン化合物とのモル比率を決定する値であり、酸性染料−アミン化合物の塩形成条件によって自由に選択することができる。具体的には、酸性染料中の酸の官能基数の０＜ｎ≦５の間の数値が実用上多く用いられ、有機溶剤や現像液に対する溶解性、塩形成性、吸光度、硬化性組成物中の他の成分との相互作用、耐光性、耐熱性等、必要とする性能の全てを考慮して選択される。吸光度のみの観点で選択する場合には、上記ｎは０＜ｎ≦４．５の間の数値をとることが好ましく、０＜ｎ≦４の間の数値をとることがさらに好ましく、０＜ｎ≦３．５の間の数値をとることが特に好ましい。   The molar ratio (hereinafter referred to as “n”) of the nitrogen-containing compound / acid dye in the salt of the acid dye and the nitrogen-containing compound will be described. The above n is a value that determines the molar ratio between the acid dye molecule and the amine compound that is a counter ion, and can be freely selected according to the salt forming conditions of the acid dye-amine compound. Specifically, a number between 0 <n ≦ 5 of the number of functional groups of the acid in the acid dye is practically used, and the solubility in organic solvents and developers, salt formation, absorbance, and curable composition It is selected in consideration of all necessary performance such as interaction with other components, light resistance, heat resistance and the like. When selecting from the standpoint of absorbance only, n is preferably a value between 0 <n ≦ 4.5, more preferably a value between 0 <n ≦ 4, and 0 <n. It is particularly preferable to take a numerical value between ≦ 3.5.

上記に示した酸性染料はその構造上酸性基を導入したことにより、酸性染料としてなりたっていることから、その置換基を変更することにより、非酸性染料とすることができる。
酸性染料は、アルカリ現像の際に好適に作用する場合もあるが、一方で過現像となってしまうこともあり、非酸性染料を好適に使用する場合もある。該非酸性染料としては、上記において例示した酸性染料の酸性基を有さない染料などが好適に使用される。 Since the acidic dye shown above has become an acidic dye by introducing an acidic group in its structure, it can be made a non-acidic dye by changing its substituent.
In some cases, the acid dye works favorably during alkali development, but on the other hand, it may become over-developed, and a non-acid dye may be preferably used. As the non-acidic dye, dyes having no acidic group of the acidic dyes exemplified above are preferably used.

これら染料は、補色系であるイエロー、マゼンタ、シアンを構成する場合は、それぞれ単色の染料を用いるが、原色系であるレッド、グリーン、ブルーを構成する場合には、二種類以上の染料を組合わせを用いることが好ましい。上記有機溶剤可溶性染料としては、二種類以上の染料を組合わせて原色系を組上げることが好ましい。   These dyes use single-color dyes when constituting complementary colors such as yellow, magenta, and cyan, respectively, but when constituting primary colors such as red, green, and blue, two or more kinds of dyes are combined. It is preferable to use a combination. As the organic solvent-soluble dye, it is preferable to assemble a primary color system by combining two or more kinds of dyes.

上記有機溶剤可溶性染料を二種類以上組み合わせる場合、その組合わせとしては少なくとも吸収特性の異なる２種の染料の混合物として用いることが好ましい。上記吸収特性としては、例えば、最大吸収波長が挙げられる。この場合、例えば、最大吸収波長が５０ｎｍ〜２５０ｎｍ異なる染料の組み合わせが好ましく、５０ｎｍ〜２００ｎｍ異なる染料の組み合わせが更に好ましい。
このような好ましい有機溶剤可溶性染料の組合わせとしては、例えば、Ｖａｌｉｆａｓｔ Ｙｅｌｌｏｗ １１０１とＡｃｉｄ Ｒｅｄ ５７との組み合わせ（質量比２：３）、Ｄｉｒｅｃｔ Ｙｅｌｌｏｗ ３３とＤｉｒｅｃｔ Ｇｒｅｅｎ ２７との組み合わせ（質量比２：３）、Ｍｏｒｄａｎｔ Ｖｉｏｌｅｔ ４０とＤｉｒｅｃｔ Ｇｒｅｅｎ ６９との組み合わせ（質量比１：２）、等が挙げられる。 When two or more organic solvent-soluble dyes are combined, the combination is preferably used as a mixture of at least two dyes having different absorption characteristics. As said absorption characteristic, the maximum absorption wavelength is mentioned, for example. In this case, for example, a combination of dyes having different maximum absorption wavelengths by 50 nm to 250 nm is preferable, and a combination of dyes having different 50 nm to 200 nm is more preferable.
Examples of combinations of such preferable organic solvent-soluble dyes include a combination of Varifast Yellow 1101 and Acid Red 57 (mass ratio 2: 3), and a combination of Direct Yellow 33 and Direct Green 27 (mass ratio 2: 3). ), A combination of Modern Violet 40 and Direct Green 69 (mass ratio 1: 2), and the like.

上記有機溶剤可溶性染料の含有量は、染料により異なるが、硬化性、現像性、パターン形状、および混色等の観点から、組成物中の全固形分に対して、０．５〜８０質量％が好ましく、１０〜６０質量％がより好ましく、３０質量％以上であることが特に好ましい。また、２種以上の染料を混合して調色する場合は、最も添加量の少ない染料の含有量が染料の総量に対して、少なくとも１０％以上であることが好ましい。   The content of the organic solvent-soluble dye varies depending on the dye, but from the viewpoint of curability, developability, pattern shape, color mixing, etc., the content is 0.5 to 80% by mass with respect to the total solid content in the composition. Preferably, 10-60 mass% is more preferable, and it is especially preferable that it is 30 mass% or more. In the case of mixing two or more dyes to adjust the color, the content of the dye with the smallest addition amount is preferably at least 10% or more based on the total amount of the dye.

−（Ｃ）光重合開始剤−
次に、光重合開始剤について説明する。光重合開始剤は、本発明の染料含有ネガ型硬化性組成物に後述のラジカル重合性モノマーと共に含有される。本発明における光重合開始剤としては、上記ラジカル重合性モノマーを重合させ得るものであれば、特に限定されないが、特性、開始効率、吸収波長、入手性、コスト等の観点で選ばれるのが好ましい。 -(C) Photopolymerization initiator-
Next, the photopolymerization initiator will be described. A photoinitiator is contained with the below-mentioned radically polymerizable monomer in the dye-containing negative curable composition of the present invention. The photopolymerization initiator in the present invention is not particularly limited as long as it can polymerize the radical polymerizable monomer, but is preferably selected from the viewpoints of characteristics, starting efficiency, absorption wavelength, availability, cost, and the like. .

上記光重合開始剤としては、例えば、ハロメチルオキサジアゾール化合物およびハロメチル−ｓ−トリアジン化合物から選択される少なくとも一つの活性ハロゲン化合物、３−アリール置換クマリン化合物、ロフィン２量体、ベンゾフェノン化合物、アセトフェノン化合物およびその誘導体、シクロペンタジエン−ベンゼン−鉄錯体およびその塩、オキシム系化合物、等が挙げられる。   Examples of the photopolymerization initiator include at least one active halogen compound selected from a halomethyloxadiazole compound and a halomethyl-s-triazine compound, a 3-aryl-substituted coumarin compound, a lophine dimer, a benzophenone compound, and an acetophenone. Examples thereof include compounds and derivatives thereof, cyclopentadiene-benzene-iron complexes and salts thereof, and oxime compounds.

上記ハロメチルオキサジアゾール化合物である活性ハロゲン化合物としては、特公昭５７−６０９６号公報に記載の２−ハロメチル−５−ビニル−１，３，４−オキサジアゾール化合物等や、２−トリクロロメチル−５−スチリル−１，３，４−オキサジアゾール、２−トリクロロメチル−５−（ｐ−シアノスチリル）−１，３，４−オキサジアゾール、２−トリクロロメチル−５−（ｐ−メトキシスチリル）−１，３，４−オキサジアゾール、等が挙げられる。   Examples of the active halogen compound that is the halomethyloxadiazole compound include 2-halomethyl-5-vinyl-1,3,4-oxadiazole compounds described in JP-B-57-6096, 2-trichloromethyl, and the like. -5-styryl-1,3,4-oxadiazole, 2-trichloromethyl-5- (p-cyanostyryl) -1,3,4-oxadiazole, 2-trichloromethyl-5- (p-methoxy) Styryl) -1,3,4-oxadiazole, and the like.

ハロメチル−ｓ−トリアジン系化合物である活性ハロゲン化合物としては、特公昭５９−１２８１号公報に記載のビニル−ハロメチル−ｓ−トリアジン化合物、特開昭５３−１３３４２８号公報に記載の２−（ナフト−１−イル）−４，６−ビス−ハロメチル−ｓ−トリアジン化合物および４−（ｐ−アミノフェニル）−２，６−ジ−ハロメチル−ｓ−トリアジン化合物、等が挙げられる。   Examples of the active halogen compound which is a halomethyl-s-triazine compound include vinyl-halomethyl-s-triazine compounds described in JP-B-59-1281 and 2- (naphtho-) described in JP-A-53-133428. 1-yl) -4,6-bis-halomethyl-s-triazine compound and 4- (p-aminophenyl) -2,6-di-halomethyl-s-triazine compound.

上記ハロメチル−ｓ−トリアジン系化合物として、具体的には、２，４−ビス（トリクロロメチル）−６−ｐ−メトキシスチリル−ｓ−トリアジン、２，６−ビス（トリクロロメチル）−４−（３，４−メチレンジオキシフェニル）−１，３，５−トリアジン、２，６−ビス（トリクロロメチル）−４−（４−メトキシフェニル）−１，３，５−トリアジン、２，４−ビス（トリクロロメチル）−６−（１−ｐ−ジメチルアミノフェニル−１，３−ブタジエニル）−ｓ−トリアジン、２−トリクロロメチル−４−アミノ−６−ｐ−メトキシスチリル−ｓ−トリアジン、２−（ナフト−１−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（４−メトキシ−ナフト−１−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（４−エトキシ−ナフト−１−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（４−ブトキシ−ナフト−１−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−〔４−（２−メトキシエチル）−ナフト−１−イル〕−４，６−ビス−トリクロロメチル−ｓ−トリアジン、   Specific examples of the halomethyl-s-triazine compound include 2,4-bis (trichloromethyl) -6-p-methoxystyryl-s-triazine, 2,6-bis (trichloromethyl) -4- (3 , 4-methylenedioxyphenyl) -1,3,5-triazine, 2,6-bis (trichloromethyl) -4- (4-methoxyphenyl) -1,3,5-triazine, 2,4-bis ( Trichloromethyl) -6- (1-p-dimethylaminophenyl-1,3-butadienyl) -s-triazine, 2-trichloromethyl-4-amino-6-p-methoxystyryl-s-triazine, 2- (naphtho) -1-yl) -4,6-bis-trichloromethyl-s-triazine, 2- (4-methoxy-naphth-1-yl) -4,6-bis-trichloromethyl-s-tria 2- (4-Ethoxy-naphth-1-yl) -4,6-bis-trichloromethyl-s-triazine, 2- (4-butoxy-naphth-1-yl) -4,6-bis-trichloro Methyl-s-triazine, 2- [4- (2-methoxyethyl) -naphth-1-yl] -4,6-bis-trichloromethyl-s-triazine,

２−〔４−（２−エトキシエチル）−ナフト−１−イル〕−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−〔４−（２−ブトキシエチル）−ナフト−１−イル〕−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（２−メトキシ−ナフト−１−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（６−メトキシ−５−メチル−ナフト−２−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（６−メトキシ−ナフト−２−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（５−メトキシ−ナフト−１−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（４，７−ジメトキシ−ナフト−１−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（６−エトキシ−ナフト−２−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、２−（４，５−ジメトキシ−ナフト−１−イル）−４，６−ビス−トリクロロメチル−ｓ−トリアジン、 2- [4- (2-Ethoxyethyl) -naphth-1-yl] -4,6-bis-trichloromethyl-s-triazine, 2- [4- (2-butoxyethyl) -naphth-1-yl] -4,6-bis-trichloromethyl-s-triazine, 2- (2-methoxy-naphth-1-yl) -4,6-bis-trichloromethyl-s-triazine, 2- (6-methoxy-5- Methyl-naphth-2-yl) -4,6-bis-trichloromethyl-s-triazine, 2- (6-methoxy-naphth-2-yl) -4,6-bis-trichloromethyl-s-triazine, 2 -(5-Methoxy-naphth-1-yl) -4,6-bis-trichloromethyl-s-triazine, 2- (4,7-dimethoxy-naphth-1-yl) -4,6-bis-trichloromethyl -S-triazine, 2- 6-Ethoxy-naphth-2-yl) -4,6-bis-trichloromethyl-s-triazine, 2- (4,5-dimethoxy-naphth-1-yl) -4,6-bis-trichloromethyl-s -Triazine,

４−〔ｐ−Ｎ，Ｎ−ジ（エトキシカルボニルメチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｏ−メチル−ｐ−Ｎ，Ｎ−ジ（エトキシカルボニルメチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｐ−Ｎ，Ｎ−ジ（クロロエチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｏ−メチル−ｐ−Ｎ，Ｎ−ジ（クロロエチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｐ−Ｎ−クロロエチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｐ−Ｎ−エトキシカルボニルメチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｐ−Ｎ，Ｎ−ジ（フェニル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｐ−Ｎ−クロロエチルカルボニルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、 4- [pN, N-di (ethoxycarbonylmethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [o-methyl-pN, N-di (ethoxycarbonyl) Methyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [pN, N-di (chloroethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine 4- [o-methyl-pN, N-di (chloroethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- (pN-chloroethylaminophenyl) -2 , 6-Di (trichloromethyl) -s-triazine, 4- (p-N-ethoxycarbonylmethylaminophenyl) -2,6-di (trichloromethyl) -s-triazine, 4- [p-N, -Di (phenyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- (pN-chloroethylcarbonylaminophenyl) -2,6-di (trichloromethyl) -s-triazine ,

４−〔ｐ−Ｎ−（ｐ−メトキシフェニル）カルボニルアミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｍ−Ｎ，Ｎ−ジ（エトキシカルボニルメチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｍ−ブロモ−ｐ−Ｎ，Ｎ−ジ（エトキシカルボニルメチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｍ−クロロ−ｐ−Ｎ，Ｎ−ジ（エトキシカルボニルメチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｍ−フロロ−ｐ−Ｎ，Ｎ−ジ（エトキシカルボニルメチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｏ−ブロモ−ｐ−Ｎ，Ｎ−ジ（エトキシカルボニルメチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｏ−クロロ−ｐ−Ｎ，Ｎ−ジ（エトキシカルボニルメチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、 4- [pN- (p-methoxyphenyl) carbonylaminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [mN, N-di (ethoxycarbonylmethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [m-bromo-pN, N-di (ethoxycarbonylmethyl) aminophenyl] -2,6-di (trichloromethyl) -s- Triazine, 4- [m-chloro-pN, N-di (ethoxycarbonylmethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [m-fluoro-pN, N-di (ethoxycarbonylmethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [o-bromo-pN, N-di (ethoxycarbonylmethyl) Minophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [o-chloro-pN, N-di (ethoxycarbonylmethyl) aminophenyl] -2,6-di (trichloromethyl)- s-triazine,

４−〔ｏ−フロロ−ｐ−Ｎ，Ｎ−ジ（エトキシカルボニルメチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｏ−ブロモ−ｐ−Ｎ，Ｎ−ジ（クロロエチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｏ−クロロ−ｐ−Ｎ，Ｎ−ジ（クロロエチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｏ−フロロ−ｐ−Ｎ，Ｎ−ジ（クロロエチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｍ−ブロモ−ｐ−Ｎ，Ｎ−ジ（クロロエチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−〔ｍ−クロロ−ｐ−Ｎ，Ｎ−ジ（クロロエチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、 4- [o-fluoro-pN, N-di (ethoxycarbonylmethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [o-bromo-pN, N- Di (chloroethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [o-chloro-pN, N-di (chloroethyl) aminophenyl] -2,6-di (trichloro Methyl) -s-triazine, 4- [o-fluoro-p-N, N-di (chloroethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [m-bromo-p -N, N-di (chloroethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- [m-chloro-pN, N-di (chloroethyl) aminophenyl] -2, 6-di (trick Romechiru) -s- triazine,

４−〔ｍ−フロロ−ｐ−Ｎ，Ｎ−ジ（クロロエチル）アミノフェニル〕−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｍ−ブロモ−ｐ−Ｎ−エトキシカルボニルメチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｍ−クロロ−ｐ−Ｎ−エトキシカルボニルメチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｍ−フロロ−ｐ−Ｎ−エトキシカルボニルメチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｏ−ブロモ−ｐ−Ｎ−エトキシカルボニルメチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｏ−クロロ−ｐ−Ｎ−エトキシカルボニルメチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、 4- [m-Fluoro-pN, N-di (chloroethyl) aminophenyl] -2,6-di (trichloromethyl) -s-triazine, 4- (m-bromo-pN-ethoxycarbonylmethylamino) Phenyl) -2,6-di (trichloromethyl) -s-triazine, 4- (m-chloro-pN-ethoxycarbonylmethylaminophenyl) -2,6-di (trichloromethyl) -s-triazine, 4 -(M-Fluoro-pN-ethoxycarbonylmethylaminophenyl) -2,6-di (trichloromethyl) -s-triazine, 4- (o-bromo-pN-ethoxycarbonylmethylaminophenyl) -2 , 6-Di (trichloromethyl) -s-triazine, 4- (o-chloro-pN-ethoxycarbonylmethylaminophenyl) -2,6-di (trichloro) Methyl) -s-triazine,

４−（ｏ−フロロ−ｐ−Ｎ−エトキシカルボニルメチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｍ−ブロモ−ｐ−Ｎ−クロロエチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｍ−クロロ−ｐ−Ｎ−クロロエチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｍ−フロロ−ｐ−Ｎ−クロロエチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｏ−ブロモ−ｐ−Ｎ−クロロエチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｏ−クロロ−ｐ−Ｎ−クロロエチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン、４−（ｏ−フロロ−ｐ−Ｎ−クロロエチルアミノフェニル）−２，６−ジ（トリクロロメチル）−ｓ−トリアジン等が挙げられる。 4- (o-Fluoro-pN-ethoxycarbonylmethylaminophenyl) -2,6-di (trichloromethyl) -s-triazine, 4- (m-bromo-pN-chloroethylaminophenyl) -2 , 6-Di (trichloromethyl) -s-triazine, 4- (m-chloro-pN-chloroethylaminophenyl) -2,6-di (trichloromethyl) -s-triazine, 4- (m-fluoro -PN-chloroethylaminophenyl) -2,6-di (trichloromethyl) -s-triazine, 4- (o-bromo-pN-chloroethylaminophenyl) -2,6-di (trichloromethyl) ) -S-triazine, 4- (o-chloro-pN-chloroethylaminophenyl) -2,6-di (trichloromethyl) -s-triazine, 4- (o-fluoro-pN-chloro) Ethylamino) -2,6-di (trichloromethyl) -s-triazine.

その他、上記光重合開始剤としては、みどり化学（株）製のＴＡＺシリーズ（例えば、ＴＡＺ−１０７、ＴＡＺ−１１０、ＴＡＺ−１０４、ＴＡＺ−１０９、ＴＡＺ−１４０、ＴＡＺ−２０４、ＴＡＺ−１１３、ＴＡＺ−１２３）、ＰＡＮＣＨＩＭ社製のＴシリーズ（例えば、Ｔ−ＯＭＳ、Ｔ−ＢＭＰ、Ｔ−Ｒ、Ｔ−Ｂ）、チバ・スペシャルティ・ケミカルズ社製のイルガキュアシリーズ（例えば、イルガキュア６５１、イルガキュア１８４、イルガキュア５００、イルガキュア１０００、イルガキュア１４９、イルガキュア８１９、イルガキュア２６１）、ダロキュアシリーズ（例えばダロキュア１１７３）、４，４'−ビス（ジエチルアミノ）−ベンゾフェノン、２−（Ｏ−ベンゾイルオキシム）−１−［４−（フェニルチオ）フェニル］−１，２−オクタンジオン、２−ベンジル−２−ジメチルアミノ−４−モルホリノブチロフェノン、２，２−ジメトキシ−２−フェニルアセトフェノン、   In addition, as the photopolymerization initiator, TAZ series (for example, TAZ-107, TAZ-110, TAZ-104, TAZ-109, TAZ-140, TAZ-204, TAZ-113, manufactured by Midori Chemical Co., Ltd.) TAZ-123), T series (for example, T-OMS, T-BMP, TR, TB) manufactured by PANCHIM, Irgacure series (for example, Irgacure 651, Irgacure 184) manufactured by Ciba Specialty Chemicals , Irgacure 500, Irgacure 1000, Irgacure 149, Irgacure 819, Irgacure 261), Darocur series (eg Darocur 1173), 4,4′-bis (diethylamino) -benzophenone, 2- (O-benzoyloxime) -1- [ 4- (Phenylthio) phenyl] -1,2-octanedione, 2-benzyl-2-dimethylamino-4-morpholinobutyrophenone, 2,2-dimethoxy-2-phenylacetophenone,

２−（ｏ−クロルフェニル）−４，５−ジフェニルイミダゾリル二量体、２−（ｏ−フルオロフェニル）−４，５−ジフェニルイミダゾリル二量体、２−（ｏ−メトキシフェニル）−４，５−ジフェニルイミダゾリル二量体、２−（ｐ−メトキシフェニル）−４，５−ジフェニルイミダゾリル二量体、２−（ｐ−ジメトキシフェニル）−４，５−ジフェニルイミダゾリル二量体、２−（２，４−ジメトキシフェニル）−４，５−ジフェニルイミダゾリル二量体、２−（ｐ−メチルメルカプトフェニル）−４，５−ジフェニルイミダゾリル二量体、ベンゾインイソプロピルエーテル、等も有用に用いられる。 2- (o-chlorophenyl) -4,5-diphenylimidazolyl dimer, 2- (o-fluorophenyl) -4,5-diphenylimidazolyl dimer, 2- (o-methoxyphenyl) -4,5 -Diphenylimidazolyl dimer, 2- (p-methoxyphenyl) -4,5-diphenylimidazolyl dimer, 2- (p-dimethoxyphenyl) -4,5-diphenylimidazolyl dimer, 2- (2, 4-Dimethoxyphenyl) -4,5-diphenylimidazolyl dimer, 2- (p-methylmercaptophenyl) -4,5-diphenylimidazolyl dimer, benzoin isopropyl ether, and the like are also useful.

これら光重合開始剤の中でも、オキシム系化合物が好ましく、例えば、２−（Ｏ−ベンゾイルオキシム）−１−［４−（フェニルチオ）フェニル］−１，２−オクタンジオン、および、１−（Ｏ−アセチルオキシム）−１−［９−エチル−６−（２−メチルベンゾイル）−９Ｈ−カルバゾール−３−イル］エタノンが特に好ましい。   Among these photopolymerization initiators, oxime compounds are preferable. For example, 2- (O-benzoyloxime) -1- [4- (phenylthio) phenyl] -1,2-octanedione and 1- (O— Acetyloxime) -1- [9-ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl] ethanone is particularly preferred.

また、これら光重合開始剤には、増感剤や光安定剤を併用することができる。
その具体例としては、ベンゾイン、ベンゾインメチルエーテル、ベンゾイン、９−フルオレノン、２−クロロ−９−フルオレノン、２−メチル−９−フルオレノン、９−アントロン、２−ブロモ−９−アントロン、２−エチル−９−アントロン、９，１０−アントラキノン、２−エチル−９，１０−アントラキノン、２−ｔ−ブチル−９，１０−アントラキノン、２，６−ジクロロ−９，１０−アントラキノン、キサントン、２−メチルキサントン、２−メトキシキサントン、２−メトキシキサントン、チオキサントン、２，４−ジエチルチオキサントン、アクリドン、１０−ブチル−２−クロロアクリドン、ベンジル、ジベンジルアセトン、ｐ−（ジメチルアミノ）フェニルスチリルケトン、ｐ−（ジメチルアミノ）フェニル−ｐ−メチルスチリルケトン、ベンゾフェノン、ｐ−（ジメチルアミノ）ベンゾフェノン（またはミヒラーケトン）、ｐ−（ジエチルアミノ）ベンゾフェノン、ベンゾアントロン等や特公昭５１−４８５１６号公報記載のベンゾチアゾール系化合物等や、チヌビン１１３０、同４００等が挙げられる。 These photopolymerization initiators can be used in combination with a sensitizer and a light stabilizer.
Specific examples thereof include benzoin, benzoin methyl ether, benzoin, 9-fluorenone, 2-chloro-9-fluorenone, 2-methyl-9-fluorenone, 9-anthrone, 2-bromo-9-anthrone, 2-ethyl- 9-anthrone, 9,10-anthraquinone, 2-ethyl-9,10-anthraquinone, 2-t-butyl-9,10-anthraquinone, 2,6-dichloro-9,10-anthraquinone, xanthone, 2-methylxanthone 2-methoxyxanthone, 2-methoxyxanthone, thioxanthone, 2,4-diethylthioxanthone, acridone, 10-butyl-2-chloroacridone, benzyl, dibenzylacetone, p- (dimethylamino) phenylstyryl ketone, p- (Dimethylamino) phenyl-p-methyl Examples include tyryl ketone, benzophenone, p- (dimethylamino) benzophenone (or Michler's ketone), p- (diethylamino) benzophenone, benzoanthrone, benzothiazole compounds described in Japanese Patent Publication No. 51-48516, and tinuvin 1130, 400. Can be mentioned.

本発明の染料含有ネガ型硬化性組成物には、上述の光重合開始剤のほかに他の公知の光重合開始剤を使用することができる。
具体的には、米国特許第２，３６７，６６０号明細書に開示されているビシナールポリケトルアルドニル化合物、米国特許第２，３６７，６６１号および第２，３６７，６７０号明細書に開示されているα−カルボニル化合物、米国特許第２，４４８，８２８号明細書に開示されているアシロインエーテル、米国特許第２，７２２，５１２号明細書に開示されているα−炭化水素で置換された芳香族アシロイン化合物、米国特許第３，０４６，１２７号および第２，９５１，７５８号明細書に開示されている多核キノン化合物、米国特許第３，５４９，３６７号明細書に開示されているトリアリールイミダゾールダイマー／ｐ−アミノフェニルケトンの組合せ、特公昭５１−４８５１６号公報に開示されているベンゾチアゾール系化合物／トリハロメチール−ｓ−トリアジン系化合物、等を挙げることができる。 In addition to the above-mentioned photopolymerization initiator, other known photopolymerization initiators can be used in the dye-containing negative curable composition of the present invention.
Specifically, the vicinal polykettle aldonyl compound disclosed in US Pat. No. 2,367,660, disclosed in US Pat. Nos. 2,367,661 and 2,367,670. Substituted α-carbonyl compounds, acyloin ethers disclosed in US Pat. No. 2,448,828, α-hydrocarbons disclosed in US Pat. No. 2,722,512 Aromatic acyloin compounds, polynuclear quinone compounds disclosed in US Pat. Nos. 3,046,127 and 2,951,758, disclosed in US Pat. No. 3,549,367. Triarylimidazole dimer / p-aminophenylketone combination, benzothiazole compound disclosed in Japanese Patent Publication No. 51-48516 / tri And halomethyl-s-triazine compounds.

上記光重合開始剤の総含有量としては、上記ラジカル重合性モノマー固形分（質量）に対して、０．０１質量％〜５０質量％が好ましく、１質量％〜３０質量％がより好ましく、１質量％〜２０質量％が特に好ましい。上記光重合開始剤の含有量が０．０１〜５０質量％の範囲内にあると、重合が進み易く、膜強度を十分向上させることができる。   As total content of the said photoinitiator, 0.01 mass%-50 mass% are preferable with respect to the said radical polymerizable monomer solid content (mass), 1 mass%-30 mass% are more preferable, 1 A mass% to 20 mass% is particularly preferred. When the content of the photopolymerization initiator is in the range of 0.01 to 50% by mass, the polymerization is easy to proceed, and the film strength can be sufficiently improved.

−（Ｄ）ラジカル重合性モノマー−
次に、上記ラジカル重合性モノマーについて説明する。本発明において用いられるラジカル重合性モノマーとしては、少なくとも１つの付加重合可能なエチレン性二重結合を有し、且つ、常圧下で１００℃以上の沸点を持つ化合物が好ましい。上述の光重合開始剤等と共に含有することにより、本発明の組成物をネガ型に構成することができる。 -(D) Radical polymerizable monomer-
Next, the radical polymerizable monomer will be described. As the radical polymerizable monomer used in the present invention, a compound having at least one addition-polymerizable ethylenic double bond and having a boiling point of 100 ° C. or higher under normal pressure is preferable. By containing with the above-mentioned photoinitiator etc., the composition of this invention can be comprised in a negative type.

上記ラジカル重合性モノマーの例としては、ポリエチレングリコールモノ（メタ）アクリレート、ポリプロピレングリコールモノ（メタ）アクリレート、フェノキシエチル（メタ）アクリレート、等の単官能のアクリレートやメタアクリレート；ポリエチレングリコールジ（メタ）アクリレート、トリメチロールエタントリ（メタ）アクリレート、ネオペンチルグリコールジ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールペンタ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、ヘキサンジオール（メタ）アクリレート、   Examples of the radical polymerizable monomer include monofunctional acrylates and methacrylates such as polyethylene glycol mono (meth) acrylate, polypropylene glycol mono (meth) acrylate, and phenoxyethyl (meth) acrylate; polyethylene glycol di (meth) acrylate , Trimethylolethane tri (meth) acrylate, neopentyl glycol di (meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) ) Acrylate, hexanediol (meth) acrylate,

トリメチロールプロパントリ（アクリロイルオキシプロピル）エーテル、トリ（アクリロイロキシエチル）イソシアヌレート、グリセリンやトリメチロールエタン等の多官能アルコールにエチレンオキサイドやプロピレンオキサイドを付加させた後（メタ）アクリレート化したもの；特公昭４８−４１７０８号、特公昭５０−６０３４号、特開昭５１−３７１９３号の各公報に記載されているようなウレタンアクリレート類；特開昭４８−６４１８３号、特公昭４９−４３１９１号、特公昭５２−３０４９０号各公報に記載されているポリエステルアクリレート類；エポキシ樹脂と（メタ）アクリル酸との反応生成物であるエポキシアクリレート類等の多官能のアクリレートやメタアクリレートおよびこれらの混合物；を挙げることができる。更に、日本接着協会誌Ｖol．２０、Ｎo.７、３００〜３０８頁に光硬化性モノマーおよびオリゴマーとして紹介されているものも挙げることができる。本発明におけるラジカル重合性モノマーとしては、多官能（メタ）アクリル化合物であることが好ましい。
上記ラジカル重合性モノマーの含有量としては、組成物中の全固形分に対して、１〜６０質量％であることが好ましく、１０〜５０質量％であることが更に好ましい。上記ラジカル重合性モノマーの含有量が１〜６０質量％の範囲内にあると、露光部の硬化性が十分であり、未露光部の溶出性を向上させることができる。 Trimethylolpropane tri (acryloyloxypropyl) ether, tri (acryloyloxyethyl) isocyanurate, polyfunctional alcohols such as glycerin and trimethylolethane and then (meth) acrylated after addition of ethylene oxide or propylene oxide; Urethane acrylates as described in JP-B-48-41708, JP-B-50-6034, JP-A-51-37193; JP-A-48-64183, JP-B-49-43191, Polyester acrylates described in JP-B Nos. 52-30490; polyfunctional acrylates and methacrylates such as epoxy acrylates which are reaction products of epoxy resin and (meth) acrylic acid, and mixtures thereof; Can be mentioned Furthermore, the Japan Adhesion Association Vol. 20, No. 7, pages 300 to 308, which are introduced as photocurable monomers and oligomers. The radical polymerizable monomer in the present invention is preferably a polyfunctional (meth) acrylic compound.
As content of the said radically polymerizable monomer, it is preferable that it is 1-60 mass% with respect to the total solid in a composition, and it is still more preferable that it is 10-50 mass%. When the content of the radical polymerizable monomer is in the range of 1 to 60% by mass, the curability of the exposed part is sufficient, and the elution property of the unexposed part can be improved.

−架橋剤−
本発明においては、補足的に架橋剤を用いて更に高度に硬化させた膜を得ることも可能である。以下、架橋剤について説明する。
本発明に使用可能な架橋剤としては、架橋反応により膜硬化を行えるものであれば特に限定はなく、例えば、（ａ）エポキシ樹脂、（ｂ）メチロール基、アルコキシメチル基、およびアシロキシメチル基から選ばれる少なくとも一つの置換基で置換された、メラミン化合物、グアナミン化合物、グリコールウリル化合物またはウレア化合物、（ｃ）メチロール基、アルコキシメチル基、およびアシロキシメチル基から選ばれる少なくとも一つの置換基で置換された、フェノール化合物、ナフトール化合物またはヒドロキシアントラセン化合物、が挙げられる。中でも、多官能エポキシ樹脂が好ましい。 -Crosslinking agent-
In the present invention, it is also possible to obtain a film that has been further cured by using a crosslinking agent. Hereinafter, the crosslinking agent will be described.
The crosslinking agent usable in the present invention is not particularly limited as long as the film can be cured by a crosslinking reaction. For example, (a) an epoxy resin, (b) a methylol group, an alkoxymethyl group, and an acyloxymethyl group. At least one substituent selected from a melamine compound, a guanamine compound, a glycoluril compound or a urea compound, (c) a methylol group, an alkoxymethyl group, and an acyloxymethyl group, which is substituted with at least one substituent selected from Substituted phenolic compounds, naphthol compounds or hydroxyanthracene compounds. Of these, polyfunctional epoxy resins are preferred.

上記（ａ）エポキシ樹脂としては、エポキシ基を有し、かつ架橋性を有するものであればいずれであってもよく、例えば、ビスフェノールＡジグリシジルエーテル、エチレングリコールジグリシジルエーテル、ブタンジオールジグリシジルエーテル、へキサンジオールジグリシジルエーテル、ジヒドロキシビフェニルジグリシジルエーテル、フタル酸ジグリシジルエステル、Ｎ，Ｎ−ジグリシジルアニリン等の２価のグリシジル基含有低分子化合物、同様に、トリメチロールプロパントリグリシジルエーテル、トリメチロールフェノールトリグリシジルエーテル、ＴｒｉｓＰ−ＰＡトリグリシジルエーテル等に代表される３価のグリシジル基含有低分子化合物、同様に、ペンタエリスリトールテトラグリシジルエーテル、テトラメチロールビスフェノールＡテトラグリシジルエーテル等に代表される４価のグリシジル基含有低分子化合物、同様に、ジペンタエリスリトールペンタグリシジルエーテル、ジペンタエリスリトールヘキサグリシジルエーテル等の多価グリシジル基含有低分子化合物、ポリグリシジル（メタ）アクリレート、２，２−ビス（ヒドロキシメチル）−１−ブタノールの１，２−エポキシ−４−（２−オキシラニル）シクロヘキサン付加物等に代表されるグリシジル基含有高分子化合物、等が挙げられる。   The (a) epoxy resin may be any epoxy resin as long as it has an epoxy group and has crosslinkability, for example, bisphenol A diglycidyl ether, ethylene glycol diglycidyl ether, butanediol diglycidyl ether. , Hexanediol diglycidyl ether, dihydroxybiphenyl diglycidyl ether, diphthalic acid diglycidyl ester, N, N-diglycidyl aniline and other divalent glycidyl group-containing low molecular weight compounds, as well as trimethylolpropane triglycidyl ether, Trivalent glycidyl group-containing low molecular weight compounds represented by methylolphenol triglycidyl ether, TrisP-PA triglycidyl ether, etc., as well as pentaerythritol tetraglycidyl ether, tetramethylol vinyl Tetravalent glycidyl group-containing low molecular weight compounds typified by phenol A tetraglycidyl ether, polyvalent glycidyl group-containing low molecular weight compounds such as dipentaerythritol pentaglycidyl ether, dipentaerythritol hexaglycidyl ether, polyglycidyl ( And glycidyl group-containing polymer compounds represented by 1,2-epoxy-4- (2-oxiranyl) cyclohexane adduct of 2,2-bis (hydroxymethyl) -1-butanol and the like. .

上記架橋剤（ｂ）に含まれるメチロール基、アルコキシメチル基、アシロキシメチル基が置換している数としては、メラミン化合物の場合２〜６、グリコールウリル化合物、グアナミン化合物、ウレア化合物の場合は２〜４であるが、好ましくはメラミン化合物の場合５〜６、グリコールウリル化合物、グアナミン化合物、ウレア化合物の場合は３〜４である。
以下、上記（ｂ）のメラミン化合物、グアナミン化合物、グリコールウリル化合物およびウレア化合物を総じて、（ｂ）に係る（メチロール基、アルコキシメチル基またはアシロキシメチル基含有）化合物という。 The number of methylol groups, alkoxymethyl groups, and acyloxymethyl groups substituted in the crosslinking agent (b) is 2 to 6 for melamine compounds, 2 for glycoluril compounds, guanamine compounds, and urea compounds. Although it is -4, Preferably it is 5-6 in the case of a melamine compound, and is 3-4 in the case of a glycoluril compound, a guanamine compound, and a urea compound.
Hereinafter, the melamine compound, guanamine compound, glycoluril compound and urea compound of (b) are collectively referred to as a compound (containing a methylol group, an alkoxymethyl group or an acyloxymethyl group) according to (b).

上記（ｂ）に係るメチロール基含有化合物は、（ｂ）に係るアルコキシメチル基含有化合物をアルコール中で塩酸、硫酸、硝酸、メタンスルホン酸等の酸触媒存在下、加熱することにより得られる。上記（ｂ）に係るアシロキシメチル基含有化合物は、（ｂ）に係るメチロール基含有化合物を塩基性触媒存在下、アシルクロリドと混合攪拌することにより得られる。   The methylol group-containing compound according to (b) can be obtained by heating the alkoxymethyl group-containing compound according to (b) in the presence of an acid catalyst such as hydrochloric acid, sulfuric acid, nitric acid, methanesulfonic acid, etc. in alcohol. The acyloxymethyl group-containing compound according to (b) above can be obtained by mixing and stirring the methylol group-containing compound according to (b) with acyl chloride in the presence of a basic catalyst.

以下、上記置換基を有する（ｂ）に係る化合物の具体例を挙げる。
上記メラミン化合物として、例えば、ヘキサメチロールメラミン、ヘキサメトキシメチルメラミン、ヘキサメチロールメラミンのメチロール基の１〜５個がメトキシメチル化した化合物またはその混合物、ヘキサメトキシエチルメラミン、ヘキサアシロキシメチルメラミン、ヘキサメチロールメラミンのメチロール基の１〜５個がアシロキシメチル化した化合物またはその混合物、などが挙げられる。 Hereinafter, specific examples of the compound according to (b) having the above-described substituent are given.
Examples of the melamine compound include hexamethylol melamine, hexamethoxymethyl melamine, a compound in which 1 to 5 methylol groups of hexamethylol melamine are methoxymethylated or a mixture thereof, hexamethoxyethyl melamine, hexaacyloxymethyl melamine, hexamethylol. Examples thereof include compounds in which 1 to 5 methylol groups of melamine are acyloxymethylated, or mixtures thereof.

上記グアナミン化合物として、例えば、テトラメチロールグアナミン、テトラメトキシメチルグアナミン、テトラメチロールグアナミンの１〜３個のメチロール基をメトキシメチル化した化合物またはその混合物、テトラメトキシエチルグアナミン、テトラアシロキシメチルグアナミン、テトラメチロールグアナミンの１〜３個のメチロール基をアシロキシメチル化した化合物またはその混合物などが挙げられる。   Examples of the guanamine compound include, for example, tetramethylolguanamine, tetramethoxymethylguanamine, a compound obtained by methoxymethylating 1 to 3 methylol groups of tetramethylolguanamine, or a mixture thereof, tetramethoxyethylguanamine, tetraacyloxymethylguanamine, tetramethylol. Examples thereof include compounds in which 1 to 3 methylol groups of guanamine are acyloxymethylated or a mixture thereof.

上記グリコールウリル化合物としては、例えば、テトラメチロールグリコールウリル、テトラメトキシメチルグリコールウリル、テトラメチロールグリコールウリルのメチロール基の１〜３個をメトキシメチル化した化合物またはその混合物、テトラメチロールグリコールウリルのメチロール基の１〜３個をアシロキシメチル化した化合物またはその混合物、などが挙げられる。   Examples of the glycoluril compound include tetramethylol glycoluril, tetramethoxymethyl glycoluril, a compound obtained by methoxymethylating 1 to 3 methylol groups of tetramethylol glycoluril, or a mixture thereof, or a methylol group of tetramethylol glycoluril. Examples thereof include compounds obtained by acylating 1 to 3 or a mixture thereof.

上記ウレア化合物として、例えば、テトラメチロールウレア、テトラメトキシメチルウレア、テトラメチロールウレアの１〜３個のメチロール基をメトキシメチル化した化合物またはその混合物、テトラメトキシエチルウレア、などが挙げられる。
これら（ｂ）に係る化合物は、単独で使用してもよく、組み合わせて使用してもよい。 Examples of the urea compound include tetramethylol urea, tetramethoxymethyl urea, a compound obtained by methoxymethylating 1 to 3 methylol groups of tetramethylol urea, a mixture thereof, and tetramethoxyethyl urea.
These compounds according to (b) may be used alone or in combination.

上記（ｃ）の架橋剤、即ち、メチロール基、アルコキシメチル基、およびアシロキシメチル基から選ばれる少なくとも一つの基で置換された、フェノール化合物、ナフトール化合物またはヒドロキシアントラセン化合物は、上記架橋剤（ｂ）の場合と同様、熱架橋により上塗りフォトレジストとのインターミキシングを抑制すると共に、膜強度を更に高めるものである。以下、これら化合物を総じて、（ｃ）に係る（メチロール基、アルコキシメチル基またはアシロキシメチル基含有）化合物ということがある。   The crosslinking agent (c), that is, a phenol compound, a naphthol compound, or a hydroxyanthracene compound substituted with at least one group selected from a methylol group, an alkoxymethyl group, and an acyloxymethyl group is the crosslinking agent (b As in the case of), intermixing with the overcoated photoresist is suppressed by thermal crosslinking, and the film strength is further increased. Hereinafter, these compounds may be collectively referred to as a compound according to (c) (containing a methylol group, an alkoxymethyl group or an acyloxymethyl group).

上記架橋剤（ｃ）に含まれるメチロール基、アシロキシメチル基またはアルコキシメチル基の数としては、一分子当り最低２個必要であり、熱架橋性および保存安定性の観点から、骨格となるフェノール化合物の２位，４位が全て置換されている化合物が好ましい。また、骨格となるナフトール化合物、ヒドロキシアントラセン化合物も、ＯＨ基のオルト位、パラ位が全て置換されている化合物が好ましい。上記フェノール化合物の３位または５位は、未置換であっても置換基を有していてもよい。
上記ナフトール化合物においても、ＯＨ基のオルト位以外は、未置換であっても置換基を有していてもよい。 The number of methylol groups, acyloxymethyl groups or alkoxymethyl groups contained in the crosslinking agent (c) is at least 2 per molecule, and from the viewpoint of thermal crosslinkability and storage stability, phenol as a skeleton Compounds in which the 2nd and 4th positions of the compound are all substituted are preferred. In addition, the naphthol compound and hydroxyanthracene compound as the skeleton are preferably compounds in which all of the ortho-position and para-position of the OH group are substituted. The 3-position or 5-position of the phenol compound may be unsubstituted or may have a substituent.
Also in the said naphthol compound, except the ortho position of OH group, it may be unsubstituted or may have a substituent.

上記（ｃ）に係るメチロール基含有化合物は、フェノール性ＯＨ基の２位または４位が水素原子である化合物を原料に用い、これを水酸化ナトリウム、水酸化カリウム、アンモニア、テトラアルキルアンモニウムヒドロキシド等の、塩基性触媒の存在下でホルマリンと反応させることにより得られる。
上記（ｃ）に係るアルコキシメチル基含有化合物は、（ｃ）に係るメチロール基含有化合物をアルコール中で塩酸、硫酸、硝酸、メタンスルホン酸等の酸触媒の存在下で加熱することにより得られる。
上記（ｃ）に係るアシロキシメチル基含有化合物は、（ｃ）に係るメチロール基含有化合物を塩基性触媒の存在下アシルクロリドと反応させることにより得られる。 The methylol group-containing compound according to the above (c) uses a compound in which the phenolic OH group is a hydrogen atom at the 2nd or 4th position as a raw material, and this is used as sodium hydroxide, potassium hydroxide, ammonia, tetraalkylammonium hydroxide. It can be obtained by reacting with formalin in the presence of a basic catalyst.
The alkoxymethyl group-containing compound according to (c) is obtained by heating the methylol group-containing compound according to (c) in an alcohol in the presence of an acid catalyst such as hydrochloric acid, sulfuric acid, nitric acid or methanesulfonic acid.
The acyloxymethyl group-containing compound according to (c) is obtained by reacting the methylol group-containing compound according to (c) with an acyl chloride in the presence of a basic catalyst.

架橋剤（ｃ）における骨格化合物としては、フェノール性ＯＨ基のオルト位またはパラ位が未置換の、フェノール化合物、ナフトール、ヒドロキシアントラセン化合物等が挙げられ、例えば、フェノール、クレゾールの各異性体、２，３−キシレノ−ル、２，５−キシレノ−ル、３，４−キシレノール、３，５−キシレノール、ビスフェノールＡなどのビスフェノール類、４，４'−ビスヒドロキシビフェニル、ＴｒｉｓＰ−ＰＡ（本州化学工業（株）製）、ナフトール、ジヒドロキシナフタレン、２，７−ジヒドロキシアントラセン、等が使用される。   Examples of the skeletal compound in the crosslinking agent (c) include phenolic compounds, naphthols, hydroxyanthracene compounds in which the ortho-position or para-position of the phenolic OH group is unsubstituted, and examples thereof include phenol and cresol isomers, 2 , 3-xylenol, 2,5-xylenol, 3,4-xylenol, 3,5-xylenol, bisphenols such as bisphenol A, 4,4'-bishydroxybiphenyl, TrisP-PA (Honshu Chemical Industry) Naphthol, dihydroxynaphthalene, 2,7-dihydroxyanthracene, etc. are used.

上記架橋剤（ｃ）の具体例としては、フェノール化合物として、例えば、トリメチロールフェノール、トリ（メトキシメチル）フェノール、トリメチロールフェノールの１〜２個のメチロール基をメトキシメチル化した化合物、トリメチロール−３−クレゾール、トリ（メトキシメチル）−３−クレゾール、トリメチロール−３−クレゾールの１〜２個のメチロール基をメトキシメチル化した化合物、２，６−ジメチロール−４−クレゾール等のジメチロールクレゾール、テトラメチロールビスフェノールＡ、テトラメトキシメチルビスフェノールＡ、テトラメチロールビスフェノールＡの１〜３個のメチロール基をメトキシメチル化した化合物、テトラメチロール−４，４'−ビスヒドロキシビフェニル、テトラメトキシメチル−４，４'−ビスヒドロキシビフェニル、ＴｒｉｓＰ−ＰＡのヘキサメチロール体、ＴｒｉｓＰ−ＰＡのヘキサメトキシメチル体、ＴｒｉｓＰ−ＰＡのヘキサメチロール体の１〜５個のメチロール基をメトキシメチル化した化合物、ビスヒドロキシメチルナフタレンジオール、等が挙げられる。   Specific examples of the crosslinking agent (c) include, for example, trimethylolphenol, tri (methoxymethyl) phenol, a compound obtained by methoxymethylating one or two methylol groups of trimethylolphenol, trimethylol- Compounds obtained by methoxymethylating one or two methylol groups of 3-cresol, tri (methoxymethyl) -3-cresol, trimethylol-3-cresol, dimethylol cresol such as 2,6-dimethylol-4-cresol, Compounds obtained by methoxymethylating 1 to 3 methylol groups of tetramethylol bisphenol A, tetramethoxymethyl bisphenol A, tetramethylol bisphenol A, tetramethylol-4,4′-bishydroxybiphenyl, tetramethoxymethyl-4,4 ′ − Suhydroxybiphenyl, TrisP-PA hexamethylol, TrisP-PA hexamethoxymethyl, TrisP-PA hexamethylol compound methoxymethylated from 1 to 5 methylol groups, Bishydroxymethylnaphthalenediol, etc. Is mentioned.

また、ヒドロキシアントラセン化合物として、例えば、１，６−ジヒドロキシメチル−２，７−ジヒドロキシアントラセン等が挙げられ、アシロキシメチル基含有化合物として、例えば、上記メチロール基含有化合物のメチロール基を、一部または全部アシロキシメチル化した化合物等が挙げられる。   Examples of the hydroxyanthracene compound include 1,6-dihydroxymethyl-2,7-dihydroxyanthracene, and examples of the acyloxymethyl group-containing compound include, for example, a part of the methylol group of the methylol group-containing compound or Examples include compounds that are all acyloxymethylated.

これらの化合物の中で好ましいものとしては、トリメチロールフェノール、ビスヒドロキシメチル−ｐ−クレゾール、テトラメチロールビスフェノールＡ、ＴｒｉｓＰ−ＰＡ（本州化学工業（株）製）のヘキサメチロール体またはそれらのメチロール基がアルコキシメチル基およびメチロール基とアルコキシメチル基との両方で置換されたフェノール化合物が挙げられる。
これら（ｃ）に係る化合物は、単独で使用してもよく、組み合わせて使用してもよい。 Among these compounds, trimethylolphenol, bishydroxymethyl-p-cresol, tetramethylolbisphenol A, trisP-PA (manufactured by Honshu Chemical Industry Co., Ltd.) or a methylol group thereof is preferable. Examples thereof include an alkoxymethyl group and a phenol compound substituted with both a methylol group and an alkoxymethyl group.
These compounds according to (c) may be used alone or in combination.

上記架橋剤の染料含有ネガ型硬化性組成物における総含有量としては、素材により異なるが、硬化性を向上させるの観点から、該硬化性組成物の固形分（質量）に対して、１〜７０質量％が好ましく、５〜５０質量％がより好ましく、７〜３０質量％が特に好ましい。   The total content of the above-mentioned crosslinking agent in the dye-containing negative curable composition varies depending on the material, but from the viewpoint of improving curability, the solid content (mass) of the curable composition is 1 to 70 mass% is preferable, 5-50 mass% is more preferable, and 7-30 mass% is especially preferable.

−熱重合防止剤−
本発明の染料含有ネガ型硬化性組成物には、以上のほか、更に熱重合防止剤を加えておくことが好ましい。例えば、ハイドロキノン、ｐ−メトキシフェノール、ジ−ｔ−ブチル−ｐ−クレゾール、ピロガロール、ｔ−ブチルカテコール、ベンゾキノン、４，４'−チオビス（３−メチル−６−ｔ−ブチルフェノール）、２，２'−メチレンビス（４−メチル−６−ｔ−ブチルフェノール）、２−メルカプトベンゾイミダゾール等が有用である。 -Thermal polymerization inhibitor-
In addition to the above, it is preferable to add a thermal polymerization inhibitor to the dye-containing negative curable composition of the present invention. For example, hydroquinone, p-methoxyphenol, di-t-butyl-p-cresol, pyrogallol, t-butylcatechol, benzoquinone, 4,4'-thiobis (3-methyl-6-t-butylphenol), 2,2 ' -Methylenebis (4-methyl-6-tert-butylphenol), 2-mercaptobenzimidazole, etc. are useful.

−（Ｅ）有機溶剤−
本発明に用いることのできる有機溶剤は、各成分の溶解性や染料含有ネガ型硬化性組成物の塗布性を満足すれば基本的に特に限定されないが、特に染料、バインダーの溶解性、塗布性、安全性を考慮して選ばれることが好ましく、例えば、環状ケトン溶剤が好ましい。また、本発明の染料含有ネガ型硬化性組成物を調製する際には、少なくとも２種類の有機溶剤を含む混合溶剤を用いることが好ましい。 -(E) Organic solvent-
The organic solvent that can be used in the present invention is not particularly limited as long as the solubility of each component and the coating property of the dye-containing negative curable composition are satisfied, but in particular, the solubility and coating property of the dye and binder. In view of safety, it is preferably selected, for example, a cyclic ketone solvent is preferable. Moreover, when preparing the dye-containing negative curable composition of this invention, it is preferable to use the mixed solvent containing at least 2 type of organic solvent.

また、２種類以上の有機溶剤を混合した混合溶剤を用いる場合、該混合溶剤ととしては、環状ケトン溶剤とさらに別の１種の有機溶剤との混合溶剤であることが好ましい。上記環状ケトン溶剤としては、例えば、シクロペンタノン、シクロヘキサノン、シクトヘプタノンなどが挙げられ、シクロヘキサノンが特に好ましい。   Moreover, when using the mixed solvent which mixed 2 or more types of organic solvents, it is preferable that this mixed solvent is a mixed solvent of cyclic ketone solvent and another 1 type of organic solvent. Examples of the cyclic ketone solvent include cyclopentanone, cyclohexanone, and octoheptanone, and cyclohexanone is particularly preferable.

前記環状ケトン以外の溶剤としては、エステル類、例えば、酢酸エチル、酢酸−ｎ−ブチル、酢酸イソブチル、ギ酸アミル、酢酸イソアミル、酢酸イソブチル、プロピオン酸ブチル、酪酸イソプロピル、酪酸エチル、酪酸ブチル、アルキルエステル類、乳酸メチル、乳酸エチル、オキシ酢酸メチル、オキシ酢酸エチル、オキシ酢酸ブチル、メトキシ酢酸メチル、メトキシ酢酸エチル、メトキシ酢酸ブチル、エトキシ酢酸メチル、エトキシ酢酸エチル、等；   Examples of the solvent other than the cyclic ketone include esters such as ethyl acetate, n-butyl acetate, isobutyl acetate, amyl formate, isoamyl acetate, isobutyl acetate, butyl propionate, isopropyl butyrate, ethyl butyrate, butyl butyrate, and alkyl esters. , Methyl lactate, ethyl lactate, methyl oxyacetate, ethyl oxyacetate, butyl oxyacetate, methyl methoxyacetate, ethyl methoxyacetate, butyl methoxyacetate, methyl ethoxyacetate, ethyl ethoxyacetate, etc .;

３−オキシプロピオン酸メチル、３−オキシプロピオン酸エチル等の３−オキシプロピオン酸アルキルエステル類、例えば、３−メトキシプロピオン酸メチル、３−メトキシプロピオン酸エチル、３−エトキシプロピオン酸メチル、３−エトキシプロピオン酸エチル、等；２−オキシプロピオン酸メチル、２−オキシプロピオン酸エチル、２−オキシプロピオン酸プロピル等の２−オキシプロピオン酸アルキルエステル類、例えば、２−メトキシプロピオン酸メチル、２−メトキシプロピオン酸エチル、２−メトキシプロピオン酸プロピル、２−エトキシプロピオン酸メチル、２−エトキシプロピオン酸エチル、２−オキシ−２−メチルプロピオン酸メチル、２−オキシ−２−メチルプロピオン酸エチル、２−メトキシ−２−メチルプロピオン酸メチル、２−エトキシ−２−メチルプロピオン酸エチル、等；ピルビン酸メチル、ピルビン酸エチル、ピルビン酸プロピル、アセト酢酸メチル、アセト酢酸エチル、２−オキソブタン酸メチル、２−オキソブタン酸エチル、等； 3-oxypropionic acid alkyl esters such as methyl 3-oxypropionate and ethyl 3-oxypropionate, such as methyl 3-methoxypropionate, ethyl 3-methoxypropionate, methyl 3-ethoxypropionate, 3-ethoxy Ethyl propionate, etc .; 2-oxypropionic acid alkyl esters such as methyl 2-oxypropionate, ethyl 2-oxypropionate, propyl 2-oxypropionate, such as methyl 2-methoxypropionate, 2-methoxypropion Acid ethyl, propyl 2-methoxypropionate, methyl 2-ethoxypropionate, ethyl 2-ethoxypropionate, methyl 2-oxy-2-methylpropionate, ethyl 2-oxy-2-methylpropionate, 2-methoxy- 2-methylpropio Methyl acid, 2-ethoxy-2-methylpropionic acid ethyl, etc; methyl pyruvate, ethyl pyruvate, propyl pyruvate, methyl acetoacetate, ethyl acetoacetate, methyl 2-oxobutanoate, ethyl 2-oxobutanoate, etc .;

エーテル類、例えば、ジエチレングリコールジメチルエーテル、テトラヒドロフラン、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、メチルセロソルブアセテート、エチルセロソルブアセテート、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテート、等；芳香族炭化水素類、例えば、トルエン、キシレン、等が好ましい。 Ethers such as diethylene glycol dimethyl ether, tetrahydrofuran, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, methyl cellosolve acetate, ethyl cellosolve acetate, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monomethyl Ether acetate, propylene glycol monoethyl ether acetate, propylene glycol monopropyl ether acetate and the like; aromatic hydrocarbons such as toluene and xylene are preferred.

これらの中でも上記環状ケトン溶剤と併用する他の有機溶剤としては、乳酸エチル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテートが好ましく、乳酸エチル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、が特に好ましい。   Among these, as the other organic solvent used in combination with the cyclic ketone solvent, ethyl lactate, propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, propylene glycol monoethyl ether acetate, propylene glycol monopropyl ether acetate are preferable, ethyl lactate, Propylene glycol monomethyl ether and propylene glycol monomethyl ether acetate are particularly preferred.

上記環状ケトン溶剤と他の有機溶剤とを混合した場合、混合溶媒の総量に占める上記環状ケトン溶剤の含有量は、４０質量％以上であることが好ましく、６０質量％以上であることが更に好ましい。   When the cyclic ketone solvent and another organic solvent are mixed, the content of the cyclic ketone solvent in the total amount of the mixed solvent is preferably 40% by mass or more, and more preferably 60% by mass or more. .

本発明における有機溶剤の使用量は、塗布性の観点から、本発明の染料含有ネガ型硬化性組成物の全固形分濃度が５〜８０質量％になる量とすることが好ましく、５〜６０質量％が更に好ましく、１０〜５０質量％が特に好ましい。   The amount of the organic solvent used in the present invention is preferably such that the total solid concentration of the dye-containing negative curable composition of the present invention is 5 to 80% by mass from the viewpoint of coatability, and 5 to 60. More preferably, it is more preferably 10 to 50% by weight.

＜各種添加物＞
本発明の染料含有ネガ型硬化性組成物には、必要に応じて、各種添加物、例えば充填剤、上記以外の高分子化合物、界面活性剤、密着促進剤、酸化防止剤、紫外線吸収剤、凝集防止剤等を配合することができる。 <Various additives>
In the dye-containing negative curable composition of the present invention, various additives such as a filler, a polymer compound other than the above, a surfactant, an adhesion promoter, an antioxidant, an ultraviolet absorber, An anti-aggregation agent or the like can be blended.

上記各種添加物の具体例としては、ガラス、アルミナ等の充填剤；ポリビニルアルコール、ポリアクリル酸、ポリエチレングリコールモノアルキルエーテル、ポリフロロアルキルアクリレート等の結着樹脂以外の高分子化合物；ノニオン系、カチオン系、アニオン系等の界面活性剤；ビニルトリメトキシシラン、ビニルトリエトキシシラン、ビニルトリス（２−メトキシエトキシ）シラン、Ｎ−（２−アミノエチル）−３−アミノプロピルメチルジメトキシシラン、Ｎ−（２−アミノエチル）−３−アミノプロピルトリメトキシシラン、３−アミノプロピルトリエトキシシラン、３−グリシドキシプロピルトリメトキシシラン、３−グリシドキシプロピルメチルジメトキシシラン、２−（３，４−エポキシシクロヘキシル）エチルトリメトキシシラン、３−クロロプロピルメチルジメトキシシラン、３−クロロプロピルトリメトキシシラン、３−メタクリロキシプロピルトリメトキシシラン、３−メルカプトプロピルトリメトキシシラン等の密着促進剤；２，２−チオビス（４−メチル−６−ｔ−ブチルフェノール）、２，６−ジ−ｔ−ブチルフェノール等の酸化防止剤；２−（３−ｔ−ブチル−５−メチル−２−ヒドロキシフェニル）−５−クロロベンゾトリアゾール、アルコキシベンゾフェノン等の紫外線吸収剤；およびポリアクリル酸ナトリウム等の凝集防止剤を挙げることができる。   Specific examples of the various additives include fillers such as glass and alumina; polymer compounds other than binder resins such as polyvinyl alcohol, polyacrylic acid, polyethylene glycol monoalkyl ether, and polyfluoroalkyl acrylate; nonionic, cationic And anionic surfactants: vinyltrimethoxysilane, vinyltriethoxysilane, vinyltris (2-methoxyethoxy) silane, N- (2-aminoethyl) -3-aminopropylmethyldimethoxysilane, N- (2 -Aminoethyl) -3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 2- (3,4-epoxycyclohexyl) ) Ethyltrimetoki Adhesion promoters such as silane, 3-chloropropylmethyldimethoxysilane, 3-chloropropyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane; 2,2-thiobis (4-methyl- 6-t-butylphenol), 2,6-di-t-butylphenol and other antioxidants; 2- (3-t-butyl-5-methyl-2-hydroxyphenyl) -5-chlorobenzotriazole, alkoxybenzophenone, etc. And an anti-aggregation agent such as sodium polyacrylate.

また、非画像部のアルカリ溶解性を促進し、本発明の染料含有ネガ型硬化性組成物の現像性の更なる向上を図る場合には、該組成物に有機カルボン酸、好ましくは分子量１０００以下の低分子量有機カルボン酸の添加を行うことができる。
具体的には、例えば、ギ酸、酢酸、プロピオン酸、酪酸、吉草酸、ピバル酸、カプロン酸、ジエチル酢酸、エナント酸、カプリル酸等の脂肪族モノカルボン酸；シュウ酸、マロン酸、コハク酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、ブラシル酸、メチルマロン酸、エチルマロン酸、ジメチルマロン酸、メチルコハク酸、テトラメチルコハク酸、シトラコン酸等の脂肪族ジカルボン酸；トリカルバリル酸、アコニット酸、カンホロン酸等の脂肪族トリカルボン酸；安息香酸、トルイル酸、クミン酸、ヘメリト酸、メシチレン酸等の芳香族モノカルボン酸；フタル酸、イソフタル酸、テレフタル酸、トリメリト酸、トリメシン酸、メロファン酸、ピロメリト酸等の芳香族ポリカルボン酸；フェニル酢酸、ヒドロアトロパ酸、ヒドロケイ皮酸、マンデル酸、フェニルコハク酸、アトロパ酸、ケイ皮酸、ケイ皮酸メチル、ケイ皮酸ベンジル、シンナミリデン酢酸、クマル酸、ウンベル酸等のその他のカルボン酸が挙げられる。 Further, when the alkali solubility of the non-image area is promoted and the developability of the dye-containing negative curable composition of the present invention is further improved, the composition has an organic carboxylic acid, preferably a molecular weight of 1000 or less. Of low molecular weight organic carboxylic acids can be added.
Specifically, for example, aliphatic monocarboxylic acids such as formic acid, acetic acid, propionic acid, butyric acid, valeric acid, pivalic acid, caproic acid, diethyl acetic acid, enanthic acid, caprylic acid; oxalic acid, malonic acid, succinic acid, Aliphatic dicarboxylic acids such as glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, brassic acid, methylmalonic acid, ethylmalonic acid, dimethylmalonic acid, methylsuccinic acid, tetramethylsuccinic acid, citraconic acid; Aliphatic tricarboxylic acids such as tricarballylic acid, aconitic acid, and camphoric acid; aromatic monocarboxylic acids such as benzoic acid, toluic acid, cumic acid, hemelitic acid, and mesitylene acid; phthalic acid, isophthalic acid, terephthalic acid, trimellitic acid, Aromatic polycarboxylic acids such as trimesic acid, melophanoic acid, pyromellitic acid; phenylacetic acid Hydratropic acid, hydrocinnamic acid, mandelic acid, phenyl succinic acid, atropic acid, cinnamic acid, methyl cinnamate, benzyl cinnamate, cinnamylidene acetic acid, coumaric acid, other carboxylic acids such as umbellic acid.

《カラーフィルタおよびその製造方法》
次に、本発明のカラーフィルタについて、その製造方法を通じて詳述する。
本発明のカラーフィルタの製造方法においては、既述の本発明の染料含有ネガ型硬化性組成物が用いられる。
本発明の染料含有ネガ型硬化性組成物を支持体上に回転塗布、流延塗布、ロール塗布等の塗布方法により塗布して感放射線性組成物層を形成し、該層を所定のマスクパターンを介して露光し、現像液で現像することによって、ネガ型の着色パターンを形成する（画像形成工程）。また、必要により、形成された着色パターンを加熱および／または露光により硬化する硬化工程を含んでいてもよい。
本発明においては、上記露光の際、上述のステッパー露光によって露光を行うことが好ましい。 << Color filter and manufacturing method thereof >>
Next, the color filter of the present invention will be described in detail through its manufacturing method.
In the method for producing a color filter of the present invention, the above-described dye-containing negative curable composition of the present invention is used.
The dye-containing negative curable composition of the present invention is coated on a support by a coating method such as spin coating, cast coating, roll coating, etc. to form a radiation-sensitive composition layer, and the layer is formed into a predetermined mask pattern. And a negative coloring pattern is formed by developing with a developer (image forming step). Moreover, the hardening process which hardens | cures the formed coloring pattern by heating and / or exposure as needed may be included.
In the present invention, the exposure is preferably performed by the above-described stepper exposure at the time of the exposure.

カラーフィルタの作製においては、上記画像形成工程（および必要により硬化工程）を所望の色相数だけ繰り返すことにより、所望の色相よりなるカラーフィルタを作製することができる。この際に使用される光若しくは放射線としては、特にｇ線、ｈ線、ｉ線等の紫外線が好ましく用いられる。   In the production of a color filter, a color filter having a desired hue can be produced by repeating the image forming step (and curing step if necessary) for the desired number of hues. As light or radiation used at this time, ultraviolet rays such as g-line, h-line and i-line are particularly preferably used.

上記支持体としては、例えば、液晶表示素子等に用いられるソーダガラス、パイレックス（登録商標）ガラス、石英ガラスおよびこれらに透明導電膜を付着させたものや、撮像素子等に用いられる光電変換素子基板、例えばシリコン基板等や、相補性金属酸化膜半導体（ＣＭＯＳ）等が挙げられる。これらの基板は、各画素を隔離するブラックストライプが形成されている場合もある。
また、これらの支持体上には、必要により、上部の層との密着改良、物質の拡散防止あるいは基板表面の平坦化のために下塗り層を設けてもよい。 Examples of the support include soda glass, Pyrex (registered trademark) glass, and quartz glass used for liquid crystal display elements and the like, and those obtained by attaching a transparent conductive film thereto, and photoelectric conversion element substrates used for imaging elements and the like. Examples thereof include a silicon substrate and a complementary metal oxide semiconductor (CMOS). These substrates may have black stripes that separate pixels.
Further, an undercoat layer may be provided on these supports, if necessary, in order to improve adhesion with the upper layer, prevent diffusion of substances, or flatten the substrate surface.

上記現像液としては、本発明の染料含有ネガ型硬化性組成物の未硬化部を溶解する一方、照射部は溶解しない組成よりなるものであればいかなるものも用いることができる。具体的には、種々の有機溶剤の組み合わせやアルカリ性の水溶液を用いることができる。上記有機溶剤としては、本発明の染料含有ネガ型硬化性組成物を調製する際に使用される前述の有機溶剤が挙げられる。   Any developer can be used as long as it has a composition that dissolves the uncured part of the dye-containing negative curable composition of the present invention but does not dissolve the irradiated part. Specifically, a combination of various organic solvents or an alkaline aqueous solution can be used. As said organic solvent, the above-mentioned organic solvent used when preparing the dye-containing negative curable composition of this invention is mentioned.

上記アルカリ性の水溶液としては、例えば、水酸化ナトリウム、水酸化カリウム、炭酸ナトリウム，硅酸ナトリウム、メタ硅酸ナトリウム、アンモニア水、エチルアミン、ジエチルアミン、ジメチルエタノールアミン、テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシド、コリン、ピロール、ピペリジン、１，８−ジアザビシクロ−〔５．４．０〕−７−ウンデセン等のアルカリ性化合物を、濃度が０．００１〜１０質量％、好ましくは０．０１〜１質量％となるように溶解してなるアルカリ性水溶液が好適である。尚、このようなアルカリ性水溶液からなる現像液を使用した場合は、一般に、現像後水で洗浄する。   Examples of the alkaline aqueous solution include sodium hydroxide, potassium hydroxide, sodium carbonate, sodium oxalate, sodium metasuccinate, aqueous ammonia, ethylamine, diethylamine, dimethylethanolamine, tetramethylammonium hydroxide, tetraethylammonium hydroxide. , Choline, pyrrole, piperidine, alkaline compounds such as 1,8-diazabicyclo- [5.4.0] -7-undecene, the concentration is 0.001 to 10% by mass, preferably 0.01 to 1% by mass. An alkaline aqueous solution obtained by dissolution is preferable. When a developer composed of such an alkaline aqueous solution is used, it is generally washed with water after development.

本発明のカラーフィルタは、液晶表示素子やＣＣＤ等の固体撮像素子に用いることができ、特に１００万画素を超えるような高解像度のＣＣＤ素子やＣＭＯＳ等に好適である。本発明のカラーフィルタは、例えば、ＣＣＤを構成する各画素の受光部と集光するためのマイクロレンズとの間に配置されるカラーフィルタとして用いることができる。   The color filter of the present invention can be used for a solid-state imaging device such as a liquid crystal display device or a CCD, and is particularly suitable for a high-resolution CCD device or a CMOS that exceeds 1 million pixels. The color filter of the present invention can be used as, for example, a color filter disposed between a light receiving portion of each pixel constituting a CCD and a microlens for condensing light.

以下、本発明を実施例により更に具体的に説明するが、本発明はその主旨を越えない限り、以下の実施例に限定されるものではない。尚、特に断りのない限り、「部」は質量基準である。   EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not limited to the following examples unless it exceeds the gist thereof. Unless otherwise specified, “part” is based on mass.

１）染料含有ネガ型硬化性組成物の調製
以下に示す組成で各化合物を混合して溶解し、本発明の染料含有ネガ型硬化性組成物を調製した。
〔組成〕
・シクロヘキサノン（有機溶剤） ２６ｇ
・樹脂Ａ ２．４ｇ
（商品名：ＡＣＡ２５０、ダイセル化学（株）製）
・モノマーＡ ３．６ｇ
（ラジカル重合性モノマー：ジペンタエリスリトールヘキサアクリレート、日本化薬（株）製）
・光重合開始剤 ０．５ｇ
（２−（Ｏ−ベンゾイルオキシム）−１−［４−（フェニルチオ）フェニル］−１，２−オクタンジオン、チバ・スペシャルティ・ケミカル（株）製）
）
・有機溶剤可溶性染料 ３．０ｇ
（Ｖａｌｉｆａｓｔ ｙｅｌｌｏｗ １１０１） 1) Preparation of dye-containing negative curable composition Each compound was mixed and dissolved in the composition shown below to prepare the dye-containing negative curable composition of the present invention.
〔composition〕
・ Cyclohexanone (organic solvent) 26g
・ Resin A 2.4 g
(Product name: ACA250, manufactured by Daicel Chemical Industries, Ltd.)
・ Monomer A 3.6g
(Radically polymerizable monomer: Dipentaerythritol hexaacrylate, manufactured by Nippon Kayaku Co., Ltd.)
・ Photopolymerization initiator 0.5g
(2- (O-benzoyloxime) -1- [4- (phenylthio) phenyl] -1,2-octanedione, manufactured by Ciba Specialty Chemicals)
)
・ Organic solvent soluble dye 3.0g
(Valifast yellow 1101)

２）下塗り層付ガラス基板の作製
ガラス基板（商品名：コーニング１７３７、コーニング社製）を１％ＮａＯＨ水で超音波洗浄した後、水洗、脱水ベーク（２００℃／３０分）を行なった。次いで、レジスト溶液（商品名：ＣＴ−２０００Ｌ、富士フイルムアーチ（株）製）を、洗浄後のガラス基板上に膜厚２μｍになるようにスピンコーターを用いて塗布し、２２０℃で１時間加熱乾燥し、硬化膜（下塗り層）を形成した。 2) Production of glass substrate with undercoat layer A glass substrate (trade name: Corning 1737, manufactured by Corning) was ultrasonically washed with 1% NaOH water, followed by washing with water and dehydration baking (200 ° C./30 minutes). Next, a resist solution (trade name: CT-2000L, manufactured by Fuji Film Arch Co., Ltd.) is applied on the glass substrate after cleaning to a thickness of 2 μm using a spin coater and heated at 220 ° C. for 1 hour. It dried and formed the cured film (undercoat layer).

３）染料含有ネガ型硬化性組成物の露光・現像（画像形成工程）
上記１）で得られた染料含有ネガ型硬化性組成物を、上記２）で得られた下塗り層付ガラス基板の下塗り層の上に膜厚が１μｍになるようにスピンコーターを用いて塗布し、１００℃で１２０秒間プリベークし、基板上にレジスト層が形成されたサンプルを作製した。 3) Exposure and development of dye-containing negative curable composition (image forming process)
The dye-containing negative curable composition obtained in 1) above was applied on the undercoat layer of the glass substrate with an undercoat layer obtained in 2) above using a spin coater so that the film thickness was 1 μm. The sample was pre-baked at 100 ° C. for 120 seconds to prepare a sample in which a resist layer was formed on the substrate.

［実施例２〜１３］
実施例１において、染料含有ネガ型硬化性組成物に含まれる各組成を下記表１に示す組成にそれぞれ変更した以外は実施例１と同様にして、染料含有ネガ型硬化性組成物を調製し、サンプルを形成した。 [Examples 2 to 13]
In Example 1, a dye-containing negative curable composition was prepared in the same manner as in Example 1 except that each composition contained in the dye-containing negative curable composition was changed to the composition shown in Table 1 below. A sample was formed.

［比較例１］
実施例１において、染料含有ネガ型硬化性組成物に含まれる各組成を下記表１に示す組成にそれぞれ変更した以外は実施例１と同様にして、比較用の染料含有ネガ型硬化性組成物を調製し、サンプルを形成した。 [Comparative Example 1]
In Example 1, a dye-containing negative curable composition for comparison was used in the same manner as in Example 1 except that each composition contained in the dye-containing negative curable composition was changed to the composition shown in Table 1 below. Was prepared to form a sample.

４）評価
（１）感度
各実施例および比較例において形成したサンプルについて、ｉ線縮小投影露光装置を使用して、塗布膜に３６５ｎｍの波長で縦２μｍ×横２μｍのマスクを通して露光量をふって照射した。照射後、現像液（商品名：ＣＤ−２０００、６０％、富士フイルムアーチ（株）製）を使用して、２３℃で６０秒間現像した。次いで、流水で２０秒間リンスした後、スプレー乾燥して、パターン画像を得た。画像形成は、光学顕微鏡およびＳＥＭ写真観察により通常の方法で確認した。
この際、縦２μｍ×横２μｍの画素パターンと、該画素パターン間のスペースと、の幅が１：１になる露光量を適正露光量とし、その露光量を感度とした。数字が小さい方が高感度となり好ましい。結果を下記表１に示す。 4) Evaluation (1) Sensitivity For the samples formed in each of the examples and comparative examples, using an i-line reduction projection exposure apparatus, the exposure amount was passed through a coating film at a wavelength of 365 nm through a 2 μm vertical × 2 μm horizontal mask. Irradiated. After irradiation, development was performed at 23 ° C. for 60 seconds using a developer (trade name: CD-2000, 60%, manufactured by Fuji Film Arch Co., Ltd.). Subsequently, after rinsing with running water for 20 seconds, spray drying was performed to obtain a pattern image. The image formation was confirmed by an ordinary method using an optical microscope and SEM photograph observation.
At this time, the exposure amount at which the width of the pixel pattern of 2 μm in length × 2 μm in width and the space between the pixel patterns is 1: 1 is set as an appropriate exposure amount, and the exposure amount is set as sensitivity. Smaller numbers are preferable because of higher sensitivity. The results are shown in Table 1 below.

（２）プロファイル
上記（１）において、適正露光量時に形成された画素パターンについて、ＳＥＭ画像にてパターン断面を観察した。この際、良好な矩形なプロファイルであるものを「〇」と評価し、ややラウンドトップ（頭が丸い）形状であるものを「△」と評価し、完全にラウンドトップ形状のものを「×」と評価した。結果を下記表１に示す。 (2) Profile In (1) above, the pattern cross section of the pixel pattern formed at the appropriate exposure amount was observed on the SEM image. At this time, a good rectangular profile is evaluated as “◯”, a slightly round top (round head) shape is evaluated as “△”, and a completely round top shape is evaluated as “×”. It was evaluated. The results are shown in Table 1 below.

（３）未露光部残渣
上記（１）において、適正露光量時に形成された画素パターンについて、ＳＥＭ画像にてパターン断面を観察した。この際、未露光部に残査が残査が全く認められないものを「〇」と評価し、未露光部に残査が残査がやや認められるものの実用上問題はないものを「△」と評価し、未露光部に残渣が明らかに認められるものを「×」と評価した。結果を下記表１に示す。 (3) Unexposed portion residue In (1) above, the pattern cross section of the pixel pattern formed at the appropriate exposure amount was observed with an SEM image. At this time, the case where no residue was found at all in the unexposed area was evaluated as “◯”, and the case where the residue was slightly recognized in the unexposed area but there was no practical problem was “△”. The case where the residue was clearly recognized in the unexposed part was evaluated as “x”. The results are shown in Table 1 below.



Figure 2006072134
※アルカリ可溶性樹脂
・樹脂Ａ：商品名 ＡＣＡ２５０、ダイセル化学（株）製
（化合物名：メタクリル酸−４−アクリロイルオキシメチル−２−ヒドロキシシクロヘキシルエステル／メタクリル酸アルキル共重合体）
・樹脂Ｂ：商品名 ＡＣＡ３００、ダイセル化学（株）製
（化合物名：メタクリル酸−４−アクリロイルオキシメチル−２−ヒドロキシシクロヘキシルエステル／メタクリル酸アルキル共重合体）
・樹脂Ｃ：ベンジルメタクリレート／メタクリル酸共重合体（＝６０／４０〔モル比〕）
※ラジカル重合性モノマー
・モノマーＡ：日本化薬（株）製、ＤＰＨＡ（主成分：ジペンタエリスリトールヘキサアクリレート）
※光重合開始剤
・「ＴＡＺ−１０７」：みどり化学（株）製
・オキシムＡ：２−（Ｏ−ベンゾイルオキシム）−１−［４−（フェニルチオ）フェニル］−１，２−オクタンジオン、チバ・スペシャルティ・ケミカル（株）製
オキシムＢ：１−（Ｏ−アセチルオキシム）−１−［９−エチル−６−（２−メチルベンゾイル）−９Ｈ−カルバゾール−３−イル］エタノン
※有機溶剤
ＰＧＭＥＡ：プロピレングリコールモノメチルエーテルアセテート
ＰＧＭＥ：プロピレングリコールモノメチルエーテル
ＭＦＤＧ：ジプロピレングリコールモノメチルエーテル

Figure 2006072134
 * Alkali-soluble resin / resin A: Trade name ACA250, manufactured by Daicel Chemical Industries, Ltd.
(Compound name: Methacrylic acid-4-acryloyloxymethyl-2-hydroxycyclohexyl ester / alkyl methacrylate copolymer)
-Resin B: Product name ACA300, manufactured by Daicel Chemical Industries, Ltd.
(Compound name: Methacrylic acid-4-acryloyloxymethyl-2-hydroxycyclohexyl ester / alkyl methacrylate copolymer)
Resin C: benzyl methacrylate / methacrylic acid copolymer (= 60/40 [molar ratio])
* Radically polymerizable monomer / Monomer A: Nippon Kayaku Co., Ltd., DPHA (main component: dipentaerythritol hexaacrylate)
* Photopolymerization initiator “TAZ-107” manufactured by Midori Chemical Co., Ltd. • Oxime A: 2- (O-benzoyloxime) -1- [4- (phenylthio) phenyl] -1,2-octanedione, Ciba Oxime B manufactured by Specialty Chemicals Co., Ltd .: 1- (O-acetyloxime) -1- [9-ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl] ethanone * Organic solvent PGMEA: Propylene glycol monomethyl ether acetate PGME: Propylene glycol monomethyl ether MFDG: Dipropylene glycol monomethyl ether

上記表１から、本発明におけるアルカリ可溶性バインダーを用いた実施例においては、感度に優れ、パターンの矩形性も良好であり、未露光部に残渣も確認されなかった。これに対し、側鎖に不飽和二重結合を有さないアルカリ可溶性バインダーを用いた比較例においては、感度およびパターンの矩形性が共に悪く、更に、未露光部に残渣が認められた。   From the said Table 1, in the Example using the alkali-soluble binder in this invention, it was excellent in the sensitivity, the rectangularity of the pattern was also favorable, and the residue was not confirmed in the unexposed part. On the other hand, in the comparative example using the alkali-soluble binder having no unsaturated double bond in the side chain, both the sensitivity and the rectangularity of the pattern were poor, and a residue was observed in the unexposed area.

Claims (7)

（Ａ）アルカリ可溶性バインダーと、（Ｂ）有機溶剤可溶性染料と、（Ｃ）光重合開始剤と、（Ｄ）ラジカル重合性モノマーと、（Ｅ）有機溶剤と、を少なくとも含む染料含有ネガ型硬化性組成物であって、前記（Ａ）アルカリ可溶性バインダーが、側鎖に不飽和二重結合を有する樹脂であることを特徴とする染料含有ネガ型硬化性組成物。   Dye-containing negative curing comprising at least: (A) an alkali-soluble binder, (B) an organic solvent-soluble dye, (C) a photopolymerization initiator, (D) a radical polymerizable monomer, and (E) an organic solvent. A dye-containing negative curable composition, wherein the (A) alkali-soluble binder is a resin having an unsaturated double bond in a side chain. 前記（Ｂ）有機溶剤可溶性染料が、少なくとも吸収特性の異なる２種の染料の混合物からなることを特徴とする請求項１に記載の染料含有ネガ型硬化性組成物。   The dye-containing negative curable composition according to claim 1, wherein the organic solvent-soluble dye (B) comprises a mixture of at least two kinds of dyes having different absorption characteristics. 前記（Ｃ）光重合開始剤がオキシム系化合物であることを特徴とする請求項１または２に記載の染料含有ネガ型硬化性組成物。   The dye-containing negative curable composition according to claim 1 or 2, wherein the (C) photopolymerization initiator is an oxime compound. 前記（Ｅ）有機溶剤が環状ケトン溶剤であることを特徴とする請求項１〜３のいずれか１項に記載の染料含有ネガ型硬化性組成物。   The dye-containing negative curable composition according to any one of claims 1 to 3, wherein the organic solvent (E) is a cyclic ketone solvent. 前記（Ｅ）有機溶剤が、環状ケトン溶剤とさらに別の１種の有機溶剤とを含む少なくとも２種の混合溶剤であることを特徴とする請求項１〜３のいずれか１項に記載の染料含有ネガ型硬化性組成物。   The dye according to any one of claims 1 to 3, wherein the organic solvent (E) is at least two mixed solvents including a cyclic ketone solvent and another organic solvent. Containing negative curable composition. 請求項１〜５のいずれか１項に記載の染料含有ネガ型硬化性組成物を用いてなることを特徴とするカラーフィルタ。   A color filter comprising the dye-containing negative curable composition according to any one of claims 1 to 5. 請求項１〜５のいずれか１項に記載の染料含有ネガ型硬化性組成物を、支持体上に塗布後、マスクを通して露光し、現像してパターンを形成する工程を含むことを特徴とするカラーフィルタの製造方法。   It includes a step of applying the dye-containing negative curable composition according to any one of claims 1 to 5 on a support, exposing through a mask, and developing to form a pattern. A method for producing a color filter.
JP2004257480A 2004-09-03 2004-09-03 Dye-containing negative curable composition, and color filter, and method for producing color filter Pending JP2006072134A (en)