JP2006063475A - Method for producing artificial leather - Google Patents
Method for producing artificial leather Download PDFInfo
- Publication number
- JP2006063475A JP2006063475A JP2004246430A JP2004246430A JP2006063475A JP 2006063475 A JP2006063475 A JP 2006063475A JP 2004246430 A JP2004246430 A JP 2004246430A JP 2004246430 A JP2004246430 A JP 2004246430A JP 2006063475 A JP2006063475 A JP 2006063475A
- Authority
- JP
- Japan
- Prior art keywords
- flame retardant
- artificial leather
- fiber
- elastic body
- phosphorus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、人工皮革の製造方法に関し、さらに詳しくは高度な難燃性が付与された人工皮革の製造方法に関する。 The present invention relates to a method for manufacturing artificial leather, and more particularly to a method for manufacturing artificial leather imparted with high flame retardancy.
繊維集合体と高分子弾性体からなる人工皮革が、軽さ、イージーケアー、低価格などの特徴から、天然皮革代替物として靴、ボール、鞄、家具・車輌、衣料用、一般資材およびスポーツ分野などに幅広く利用されている。 Artificial leather made of fiber aggregate and polymer elastic body is light, easy care, low price, etc., as a substitute for natural leather, shoes, balls, bags, furniture / vehicles, clothing, general materials and sports It is widely used for such as.
さらに最近、特に家具・車両用とにおいて顕著であるが、人工皮革に難燃性を付与して幅広く使用されるようになってきた。難燃性付与の方法としては、完成した人工皮革製品に難燃剤処理液を浸漬処理する方法が一般的だが、市場から要求される難燃性のレベルが向上し、その要求に応えるためには多量の難燃剤を使用しなければならず、経済的にもコスト高となるという問題があった。 More recently, particularly for furniture and vehicles, it has become widely used by imparting flame retardancy to artificial leather. As a method of imparting flame retardancy, a method of immersing a flame retardant treatment solution in a finished artificial leather product is common, but to improve the level of flame retardancy required by the market and meet that demand A large amount of a flame retardant has to be used, and there is a problem that the cost is increased economically.
特に質感向上のために、使用される繊維が極細繊維となってきたのに伴い、その困難性は増してきている。例えば繊維に難燃剤を含有した場合、0.5dtex未満のような極細繊維においては、繊維強度が低下し人工皮革としての実用強度を保つことが出来ないという問題があった。また、後処理にて難燃剤を処理した場合にも、このような極細繊維は、極細繊維が束となった形状をとる場合が多く、その繊維束の周囲には付着するものの、繊維束の内部には難燃剤が浸透できないという問題があった。このような場合、極細繊維の周囲には空間があり、空気が存在するために、難燃効果が大きく低下していた。 In particular, the difficulty has increased as the fibers used have become ultrafine fibers in order to improve the texture. For example, when a flame retardant is contained in the fiber, there is a problem that the fiber strength is lowered in an ultrafine fiber of less than 0.5 dtex, and the practical strength as an artificial leather cannot be maintained. In addition, even when the flame retardant is treated in the post-treatment, such an ultrafine fiber often takes a shape in which the ultrafine fiber is bundled, and although it adheres around the fiber bundle, There was a problem that the flame retardant could not penetrate inside. In such a case, there is a space around the ultrafine fibers, and air is present, so that the flame-retardant effect is greatly reduced.
そこで、このような極細繊維使いの人工皮革の難燃性を向上させるために例えば特許文献1には、極細繊維に有機リン成分共重合ポリエステルを用い、さらに極細繊維からなる不織布内の高分子弾性体に難燃剤としての水酸化アルミニウムを添加した人工皮革が開示されている。しかし共重合されたポリエステルは強度において共重合成分を有しないポリエステルに劣り、特に耐久性を要求される家具・車両分野においては問題であった。また溶剤系のポリウレタンに水酸化アルミニウムを添加した樹脂は脆くなり人工皮革の強度が低下するばかりか、例えば表面の銀付層に用いられないという問題があった。
本発明は上記従来技術の有する問題点を鑑みなされたもので、その目的は、有機溶剤を使用しない環境に優しい水性タイプの含浸基材を用いて、高度な難燃性を有しながら物性に優れた人工皮革を提供することにある。 The present invention has been made in view of the above-mentioned problems of the prior art, and its purpose is to use an environmentally friendly aqueous type impregnated base material that does not use an organic solvent, to achieve physical properties while having high flame retardancy. It is to provide excellent artificial leather.
本発明の人工皮革の製造方法は、極細繊維からなる繊維集合体にリン系難燃剤及び界面活性剤を含む水系の処理液を付与し、乾燥し、次いで高分子弾性体とリン系難燃剤とを含む水系の含浸液を付与し、その後に片側表面の造面処理を行うことを特徴とする。 In the method for producing artificial leather of the present invention, an aqueous treatment liquid containing a phosphorus-based flame retardant and a surfactant is applied to a fiber assembly composed of ultrafine fibers, dried, and then a polymer elastic body and a phosphorus-based flame retardant are used. A water-based impregnating solution containing selenium is applied, and then one side surface is subjected to surface preparation treatment.
また造面処理が高分子弾性体とリン系難燃剤からなる銀面を形成するものであること、リン系難燃剤が脂肪族環式ホスホン酸エステルであること、界面活性剤がノニオン系であることが好ましい。 Further, the surface-forming treatment is to form a silver surface composed of a polymer elastic body and a phosphorus flame retardant, the phosphorus flame retardant is an aliphatic cyclic phosphonic acid ester, and the surfactant is a nonionic surfactant. It is preferable.
本発明の製造方法によれば、環境に優しい水性タイプの含浸基材を使用したのにもかかわらず、高度な難燃性を有しながら物性に優れた人工皮革の製造方法を提供する。 According to the production method of the present invention, there is provided a method for producing artificial leather having excellent physical properties while having high flame retardancy despite using an environmentally friendly aqueous type impregnated base material.
以下、本発明を詳細に説明する。
本発明の製造方法は、極細繊維からなる繊維集合体に水系の処理液を付与し、乾燥し、次いで高分子弾性体とリン系難燃剤とを含む水系の含浸液を付与し、その後に片側表面の造面処理を行う人工皮革の製造方法である。
Hereinafter, the present invention will be described in detail.
In the production method of the present invention, an aqueous treatment liquid is applied to a fiber assembly composed of ultrafine fibers, dried, and then an aqueous impregnation liquid containing a polymer elastic body and a phosphorus flame retardant is applied, and then one side It is a manufacturing method of artificial leather which performs surface forming treatment.
本発明で用いられる繊維集合体を構成する極細繊維としては、例えばポリエステル、ポリアミド、ポリアクリル、ポリオレフィンなどの従来公知の繊維形成可能な合成樹脂の一種、あるいは二種以上の樹脂からなる極細繊維が使用出来る。中でも、ポリエステル繊維、ポリアミド繊維またはポリエステル/ポリアミド混合繊維を用いることが好ましい。繊維となるポリエステル系樹脂としては、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリプロピレンテレフタレートなどがあげられ、ポリアミド系樹脂としては、ナイロン−6、ナイロン−66、ナイロン−12などがあげられる。中でもポリエチレンテレフタレート、ナイロン−6などが、工程安定性やコスト面から最も好ましい。また、繊維の繊度は0.001〜0.4dtexであることが好ましく、さらには0.05〜0.3dtexであることが好ましい。また海島型の混合紡糸繊維、複合紡糸繊維、あるいは剥離分割型複合繊維等で、該繊維分割後に極細繊維となることが好ましい。また少量ならば極細以外の繊維を用いることも可能であり、風合いなどの面から天然繊維を混合することも好ましい。 Examples of the ultrafine fibers constituting the fiber assembly used in the present invention include, for example, one of conventionally known fiber-forming synthetic resins such as polyester, polyamide, polyacryl, and polyolefin, or ultrafine fibers made of two or more resins. Can be used. Among these, it is preferable to use polyester fiber, polyamide fiber or polyester / polyamide mixed fiber. Examples of the polyester-based resin used as the fiber include polyethylene terephthalate, polybutylene terephthalate, and polypropylene terephthalate. Examples of the polyamide-based resin include nylon-6, nylon-66, and nylon-12. Among these, polyethylene terephthalate, nylon-6 and the like are most preferable from the viewpoint of process stability and cost. The fineness of the fiber is preferably 0.001 to 0.4 dtex, and more preferably 0.05 to 0.3 dtex. In addition, it is preferable to use an ultra-fine fiber after dividing the fiber, such as a sea-island type mixed spun fiber, a composite spun fiber, or a peeled split composite fiber. If the amount is small, it is possible to use fibers other than ultrafine fibers, and it is also preferable to mix natural fibers in terms of texture and the like.
本発明で用いられる繊維集合体は、上述の繊維からなる不織布、織編物であるが、本発明で得られる人工皮革用基材が、より天然皮革らしい風合いを得るためには、不織布であることが好ましい。これらの繊維を不織布に形成する方法としては、短繊維からのカーディング、交絡処理による方法、あるいは長繊維のダイレクトシート化、交絡処理による方法などの従来から公知の方法が採用できる。さらに緻密でかつ均質な不織布を得るためには、極細繊維化される前の剥離分割型複合繊維を用い、高圧水流により分割、絡合させた繊維集合体であることが好ましい。 The fiber assembly used in the present invention is a nonwoven fabric or a woven or knitted fabric made of the above-mentioned fibers. However, in order to obtain a natural leather-like texture, the artificial leather base material obtained in the present invention is a nonwoven fabric. Is preferred. As a method for forming these fibers into a nonwoven fabric, conventionally known methods such as carding from short fibers and a method of entanglement, or a method of forming a direct sheet of long fibers and a method of entanglement can be employed. Further, in order to obtain a dense and homogeneous nonwoven fabric, it is preferable that the fiber assembly is a fiber assembly that is split and entangled by a high-pressure water stream using a peeled split type composite fiber before being made into ultrafine fibers.
また繊維集合体は、例えば構成繊維の一部が熱収縮性繊維である繊維集合体を収縮処理することにより、収縮緻密化、高密度化し、得られる繊維集合体の見かけ密度を0.3〜0.6g/cm3とすることが好ましい。熱収縮性繊維としては、高温多湿雰囲気中で収縮する合成繊維であることが好ましく、特に好ましくは収縮応力が大きい高収縮ポリエステル系繊維であることである。例えばポリエチレンテレフタレートを主成分とする繊維形成性ポリマーを紡糸した後、温水中にて低倍率で延伸して得られる熱収縮性繊維などであることが好ましい。さらに、該熱収縮性繊維は延伸条件などの制御により50℃以上100℃以下で収縮特性を発現するものが好ましい。収縮により高密度化する場合には、50℃より低い温度で特性を発現するものは品質のバラツキの要因になり、100℃より高い温度で特性を発現するものは、多くの熱量を必要し生産性が悪くなる傾向にある。 In addition, the fiber aggregate is contracted, densified and densified by, for example, contracting a fiber aggregate in which some of the constituent fibers are heat-shrinkable fibers, and the apparent density of the resulting fiber aggregate is 0.3 to 0.3. It is preferable to set it as 0.6 g / cm 3 . The heat-shrinkable fiber is preferably a synthetic fiber that shrinks in a high-temperature and high-humidity atmosphere, and particularly preferably a high-shrinkage polyester fiber having a large shrinkage stress. For example, it is preferably a heat-shrinkable fiber obtained by spinning a fiber-forming polymer mainly composed of polyethylene terephthalate and then stretching it at a low magnification in warm water. Furthermore, the heat-shrinkable fiber is preferably one that exhibits shrinkage characteristics at 50 ° C. or higher and 100 ° C. or lower by controlling stretching conditions and the like. When densifying by shrinkage, those that exhibit characteristics at temperatures lower than 50 ° C cause quality variations, and those that exhibit characteristics at temperatures higher than 100 ° C require a large amount of heat and are produced. It tends to get worse.
また、繊維集合体の繊維を熱収縮する場合の好ましい面積収縮率は、10%以上60%以下であり、より好ましくは20%以上50%以下である。面積収縮率が10%未満であると緻密かつ均質な構造の繊維集合体となりにくい傾向にある。一方、面積収縮率が60%を超えると繊維間の空隙が小さくなり繊維の自由度が低下する傾向にあり、繊維複合シートとしたときのドレープ性等が低下する傾向にある。 Moreover, the preferable area shrinkage rate when heat shrinking the fibers of the fiber assembly is 10% or more and 60% or less, and more preferably 20% or more and 50% or less. If the area shrinkage is less than 10%, it tends to be difficult to form a fiber assembly having a dense and homogeneous structure. On the other hand, when the area shrinkage rate exceeds 60%, the gap between the fibers tends to be small and the degree of freedom of the fibers tends to decrease, and the drapability and the like when the fiber composite sheet is formed tend to decrease.
本発明の製造方法ではまず上記の繊維集合体にリン系難燃剤及び界面活性剤を含む水系の処理液を付与し、乾燥することが必要である。さらにはリン系難燃剤が脂肪族環式ホスホン酸エステルであることが好ましく、界面活性剤はノニオン系であることが好ましい。このように、水系の含浸液を含浸する前の繊維集合体にリン系難燃剤を付与することによって極細繊維間の細かい空隙に難燃剤を付与することが出来、難燃性が大きく向上するとともに、リン系の剤を用いているため環境への影響の少ない人工皮革を得ることが出来る。また、難燃剤に水によく溶解する脂肪族環式ホスホン酸エステルを用いることや、ノニオン系の界面活性剤を用いることによって、難燃剤の極細繊維間への浸透性をさらに高め、難燃効果をさらに高めることが可能である。 In the production method of the present invention, first, it is necessary to apply an aqueous treatment liquid containing a phosphorus-based flame retardant and a surfactant to the fiber assembly and dry it. Furthermore, the phosphorus flame retardant is preferably an aliphatic cyclic phosphonic acid ester, and the surfactant is preferably a nonionic surfactant. In this way, by adding a phosphorus-based flame retardant to the fiber assembly before impregnating with the water-based impregnating liquid, a flame retardant can be applied to the fine gaps between the ultrafine fibers, and the flame retardancy is greatly improved. Since a phosphorus-based agent is used, it is possible to obtain an artificial leather with little influence on the environment. In addition, by using an aliphatic cyclic phosphonic acid ester that dissolves well in water as a flame retardant, or by using a nonionic surfactant, the permeability of the flame retardant between ultrafine fibers can be further increased, and the flame retardant effect Can be further increased.
処理液を付与する方法には、たとえば難燃剤の水溶液または水分散液に繊維集合体を浸漬する方法が採用される。その付着量としては繊維重量に対し乾燥重量で0.5〜10重量%であることが好ましい。少なすぎると難燃効果が減少し、多すぎると製品の触感を損ねる傾向にある。また、後に処理する高分子弾性体中の難燃剤の添加量が多い場合にはその分、この段階での処理量を減少させることが好ましい。 As a method for applying the treatment liquid, for example, a method of immersing the fiber assembly in an aqueous solution or an aqueous dispersion of a flame retardant is employed. The adhesion amount is preferably 0.5 to 10% by dry weight with respect to the fiber weight. If the amount is too small, the flame retardant effect is reduced. If the amount is too large, the feel of the product tends to be impaired. Moreover, when there is much addition amount of the flame retardant in the polymeric elastic body processed later, it is preferable to reduce the processing amount in this step by that much.
本発明では、次いで乾燥した繊維集合体に対し、高分子弾性体とリン系難燃剤とを含む水系の含浸液を付与することが必要である。ここでもリン系難燃剤としては、水によく溶解する脂肪族環式ホスホン酸エステルであることが好ましい。高分子弾性体としては、例えばポリエステル系エラストマー、ポリウレタン、NBR、SBR、アクリル等の高分子からなる樹脂があげられる。中でもポリウレタン樹脂が柔軟性、強度、耐候性、耐摩耗性などの点から好ましい。これらの本発明で用いられる高分子弾性体は、曇点を有する非イオン性界面活性剤にて分散、あるいは溶解された感熱凝固性を有する分散液、あるいは溶液であることが好ましい。高分子弾性体が感熱凝固性を有する場合、その凝固特性が発現する温度は30℃以上90℃以下が好ましく、さらには60℃以上80℃以下で凝固特性を発現するものが好ましい。高分子弾性体の凝固特性が発現する温度とは、含浸液を攪拌しながら昇温した時に、含浸液が流動性を失い凝固する温度であり、例えば曇点を下げる添加剤などを加えることで凝固温度を調節することが可能である。 In the present invention, it is necessary to apply an aqueous impregnating solution containing a polymer elastic body and a phosphorus-based flame retardant to the dried fiber assembly. Again, the phosphorus-based flame retardant is preferably an aliphatic cyclic phosphonic acid ester that dissolves well in water. Examples of the polymer elastic body include resins made of a polymer such as polyester elastomer, polyurethane, NBR, SBR, and acrylic. Among these, polyurethane resins are preferable from the viewpoints of flexibility, strength, weather resistance, wear resistance, and the like. These polymer elastic bodies used in the present invention are preferably dispersions or solutions having heat-sensitive coagulation properties dispersed or dissolved in a nonionic surfactant having a cloud point. When the polymer elastic body has a heat-sensitive coagulation property, the temperature at which the coagulation characteristics are exhibited is preferably 30 ° C. or more and 90 ° C. or less, and more preferably those that exhibit the coagulation properties at 60 ° C. or more and 80 ° C. or less. The temperature at which the solidification characteristics of the polymer elastic body are manifested is the temperature at which the impregnating liquid loses fluidity and solidifies when the impregnating liquid is heated while stirring. For example, an additive that lowers the cloud point is added. It is possible to adjust the solidification temperature.
本発明では、高分子弾性体とリン系難燃剤とを含む水系の含浸液が水分散液、あるいは水溶液として繊維集合体に含浸される。リン系難燃剤の添加量は、高分子弾性体の固形分重量に対して0.5〜10重量%の範囲であることが好ましい。 In the present invention, the fiber assembly is impregnated with an aqueous impregnating liquid containing a polymer elastic body and a phosphorus flame retardant as an aqueous dispersion or an aqueous solution. The addition amount of the phosphorus-based flame retardant is preferably in the range of 0.5 to 10% by weight with respect to the solid content weight of the polymer elastic body.
またこの含浸液には、高分子弾性体の耐光性、耐熱性、耐水性、耐溶剤性等の各種耐久性を改善する目的で酸化防止剤、紫外線吸収剤、加水分解防止剤等の安定剤や、エポキシ樹脂、メラミン樹脂、イソシアネート化合物、アジリジン化合物、ポリカルボジイミド化合物等の架橋剤を配合して使用することもできる。さらに、着色を目的として各種無機、有機顔料を配合することができる。また、シリコン系、フッ素系などの各種撥水剤や、ポリエチレングリコールなどの親水性の剤を加えることで、繊維と高分子弾性体との非接合構造を調整し、繊維複合シートのドレープ性を向上させることも好ましい。 In addition, this impregnating liquid contains stabilizers such as antioxidants, ultraviolet absorbers and hydrolysis inhibitors for the purpose of improving various durability such as light resistance, heat resistance, water resistance and solvent resistance of the polymer elastic body. Alternatively, a crosslinking agent such as an epoxy resin, a melamine resin, an isocyanate compound, an aziridine compound, or a polycarbodiimide compound can be blended and used. Furthermore, various inorganic and organic pigments can be blended for the purpose of coloring. In addition, by adding various water repellents such as silicon and fluorine, and hydrophilic agents such as polyethylene glycol, the non-bonding structure between the fiber and the polymer elastic body is adjusted, and the drapeability of the fiber composite sheet is improved. It is also preferable to improve.
本発明に用いられる繊維複合体を得るための高分子弾性体の繊維集合体への含浸方法は、通常行われる方法であればいずれでも良く、例えばマングルによる含浸法、コーティング法、スプレー法等が挙げられる。高分子弾性体の付着量(固形分)は、目的に応じて任意の値が採用されるが、好ましくは、繊維集合体100重量部に対し3〜150重量部である。さらには10〜50重量部であることが好ましい。高分子弾性体付着量(固形分)が3重量部未満では得られるシートの充実感が低下する傾向がある。一方150重量部を越えると、得られる繊維複合体は硬くなり、皮革様の風合いが低下する傾向がある。 The method for impregnating the fiber assembly of the polymer elastic body to obtain the fiber composite used in the present invention may be any method that is usually performed, such as a mangle impregnation method, a coating method, and a spray method. Can be mentioned. Although the arbitrary amount is employ | adopted for the adhesion amount (solid content) of a polymeric elastic body according to the objective, Preferably, it is 3-150 weight part with respect to 100 weight part of fiber assemblies. Furthermore, it is preferable that it is 10-50 weight part. If the amount of attached polymer elastic body (solid content) is less than 3 parts by weight, the sense of fullness of the resulting sheet tends to be reduced. On the other hand, if it exceeds 150 parts by weight, the resulting fiber composite becomes hard and the leather-like texture tends to be lowered.
高分子弾性体等を含浸した後の繊維集合体は、例えば感熱凝固ゾーンで高分子弾性体を凝固させることが好ましい。感熱凝固法としては、加熱スチームによる凝固、熱水への浸漬による凝固、高周波誘電加熱による凝固などの手法を採ることが出来る。感熱凝固を行う場合には処理温度は50℃以上80℃以下が好ましいが、より安定的に生産を行うためには感熱ゲル化温度の10℃以上とするのがさらに好ましい。凝固後の高分子弾性体と繊維からなる繊維複合体はマングル絞り、減圧脱水などにより過剰の水分を除去した後、熱風乾燥機にて乾燥することが好ましい。 The fiber assembly after impregnating the polymer elastic body or the like is preferably solidified in the heat sensitive coagulation zone, for example. As the heat-sensitive coagulation method, methods such as coagulation by heating steam, coagulation by immersion in hot water, and coagulation by high-frequency dielectric heating can be employed. When heat-sensitive coagulation is performed, the treatment temperature is preferably 50 ° C. or more and 80 ° C. or less, but more preferably a heat-sensitive gelling temperature of 10 ° C. or more for more stable production. It is preferable that the fiber composite composed of the polymer elastic body and the fiber after the coagulation is dried with a hot air dryer after excess water is removed by mangle drawing, vacuum dehydration or the like.
本発明の製造方法では、このようにして得られた繊維複合体の片側表面に造面処理を行う。この造面処理としては、高分子弾性体とリン系難燃剤からなる銀面を形成するものであることが好ましい。高分子弾性体とリン系難燃剤からなる膜の厚さは、繊維複合体の厚さとのバランスで風合いに適した厚さに決定すべきであるが、10〜70μmであることが好ましい。厚さが薄すぎる場合には、人工皮革の耐黄変色性、耐加水分解性、接着性等の性能が低下する傾向にある。また、厚過ぎる場合には、表面が硬くなり、シート状物の風合いが低下する傾向にある。 In the production method of the present invention, a surface forming treatment is performed on one side surface of the fiber composite obtained in this way. As this surface-forming treatment, it is preferable to form a silver surface comprising a polymer elastic body and a phosphorus flame retardant. The thickness of the film composed of the polymer elastic body and the phosphorus-based flame retardant should be determined to a thickness suitable for the texture in balance with the thickness of the fiber composite, but is preferably 10 to 70 μm. When the thickness is too thin, the artificial leather tends to deteriorate in performance such as yellowing resistance, hydrolysis resistance and adhesion. If it is too thick, the surface becomes hard and the texture of the sheet tends to be lowered.
造面処理に用いる高分子弾性体としては、先に繊維集合体の含浸用に挙げたSBR、NBR、ポリウレタン、ポリエステルエラストマー、アクリル酸エステル等が挙げられるが、中でも人工皮革としての高い表面物性を得るためにはポリウレタンが好ましく、特には無黄変タイプのポリウレタンエラストマーであることが好ましい。リン系難燃剤としては、水によく溶解する脂肪族環式ホスホン酸エステルであることが好ましい。リン系難燃剤の添加量は造面に用いられる高分子弾性体の固形分重量に対して0.5〜10重量%であることが好ましい。 Examples of the polymer elastic body used for the surface forming treatment include SBR, NBR, polyurethane, polyester elastomer, acrylate ester and the like mentioned above for impregnation of the fiber assembly. In order to obtain it, a polyurethane is preferable, and a non-yellowing type polyurethane elastomer is particularly preferable. The phosphorus-based flame retardant is preferably an aliphatic cyclic phosphonic acid ester that dissolves well in water. The addition amount of the phosphorus-based flame retardant is preferably 0.5 to 10% by weight based on the solid content weight of the polymer elastic body used for the surface preparation.
造面処理は通常のコート法も採用できるが、離型紙上に高分子弾性体を主とする膜を形成し、接着剤にて繊維複合体の表面に接着させた後、離型紙を剥離するいわゆるラミネート法を採用することが風合いと難燃性のバランスから最も好ましい。ラミネート法によって造面する場合、膜を形成するには例えば高分子弾性体を溶剤に溶解させた溶液、あるいは高分子弾性体を分散媒に分散させた分散液を離型上にコーティングし、溶剤あるいは分散媒を蒸発させる方法が採用される。中でも高分子弾性体の水分散液を用いる方法が作業環境等の面で好ましい。さらには膜である弾性体フィルムは、繊維複合体上の表面に水系接着剤を介して接着することが好ましい。たとえば、離型紙上に形成された高分子弾性体フィルム上に接着剤を塗布し張り合わせることで接着する。このとき接着剤として、水分散型、あるいは水溶型の接着剤を用いた場合、得られる接着層も水に対して膨潤、あるいは溶解し易い傾向に有り、これを解決するためには該接着剤は架橋反応タイプ、いわゆる2液タイプの接着剤であることが好ましい。接着剤としては、ウレタン系、オレフィン系等があるが耐磨耗性、柔軟性の面からウレタン系が好ましい。架橋剤としては、メラミン系、ポリイソシアネート系、エポキシ系等があげられるが、中でも作業環境面、柔軟性等の面でポリイソシアネート系が好ましい。このような接着剤の塗布量は溶液目付けで50〜250g/m2であることが好ましい。 A normal coating method can be used for the surface forming treatment, but a film mainly composed of a polymer elastic body is formed on the release paper, and the release paper is peeled off after being adhered to the surface of the fiber composite with an adhesive. The so-called laminating method is most preferable from the balance of texture and flame retardancy. When forming a surface by the laminating method, for example, a film is formed by coating a mold with a solution in which a polymer elastic body is dissolved in a solvent or a dispersion liquid in which a polymer elastic body is dispersed in a dispersion medium. Or the method of evaporating a dispersion medium is employ | adopted. Among these, a method using an aqueous dispersion of a polymer elastic body is preferable in terms of working environment and the like. Furthermore, it is preferable that the elastic film as a film is bonded to the surface on the fiber composite via a water-based adhesive. For example, the adhesive is applied by applying and bonding an adhesive on a polymer elastic film formed on a release paper. At this time, when a water-dispersed or water-soluble adhesive is used as the adhesive, the resulting adhesive layer also tends to swell or dissolve in water, and in order to solve this, the adhesive Is preferably a cross-linking reaction type, so-called two-component adhesive. Adhesives include urethanes and olefins, but urethanes are preferred in terms of wear resistance and flexibility. Examples of the crosslinking agent include melamine-based, polyisocyanate-based, epoxy-based, etc. Among them, polyisocyanate-based is preferable in terms of work environment and flexibility. The application amount of such an adhesive is preferably 50 to 250 g / m 2 in terms of solution weight.
そしてラミネート法を採用する場合には、弾性体フィルムおよび/又は接着剤の両方またはいずれか一方にリン系の難燃剤を添加する。また、接着剤液の中に熱膨張マイクロカプセル粒子を添加混合することも好ましく、これにより接着剤層が多孔化され、人工皮革となった場合の表面のソフト性、厚さ増加による耐磨耗性が増すことができる。 When employing the laminating method, a phosphorus-based flame retardant is added to either or both of the elastic film and / or the adhesive. In addition, it is also preferable to add and mix thermally expanded microcapsule particles in the adhesive liquid, which makes the adhesive layer porous and softens the surface when it becomes artificial leather, wear resistance due to increased thickness Can be increased.
さらには、離型紙上に高分子弾性体フィルムを形成し、その上に水系の水分散型、あるいは水溶型の接着剤を塗布、次いで任意の乾燥後、あらかじめ高分子弾性体の処理液が表面に浸透された繊維質基材を重ねて任意の圧力の下で接着させる方法とすることが好ましい。さらには温度100〜130℃の金属加熱シリンダーで熱接着を行うことが好ましい。その後、十分に接着剤の反応させた後、離型紙から繊維質基材を剥ぎ取ることにより、人工皮革が得られる。 Furthermore, a polymer elastic film is formed on the release paper, and a water-based water-dispersed or water-soluble adhesive is applied on the release paper. It is preferable to use a method in which the fibrous base material infiltrated into the layer is stacked and bonded under an arbitrary pressure. Furthermore, it is preferable to perform thermal bonding with a metal heating cylinder having a temperature of 100 to 130 ° C. Thereafter, after sufficiently reacting the adhesive, the fibrous base material is peeled off from the release paper to obtain an artificial leather.
本発明の人工皮革の製造方法において、各段階でのリン系難燃剤の添加量は、繊維集合体への付着量:含浸用高分子弾性体への添加量:造面用高分子弾性体への添加量の固形分重量の比率は、2〜4:2〜4:6〜2の範囲であることが好ましい。このように人工皮革の表面から、内部の極細繊維表面のリン系難燃剤の付着バランスを調整することによって、難燃性と風合いその他の物性との高いバランスを保つことが出来る。また最終的な人工皮革全体の重量に対する、全リン系難燃剤の固形分重量としては0.5〜30重量%であることが好ましい。 In the method for producing artificial leather of the present invention, the amount of the phosphorus-based flame retardant added at each stage is as follows: the amount attached to the fiber assembly: the amount added to the polymer elastomer for impregnation: the polymer elastomer for surface preparation The ratio of the solid content weight of the added amount is preferably in the range of 2-4: 2-4: 6-2. Thus, by adjusting the adhesion balance of the phosphorus-based flame retardant on the surface of the inner ultrafine fiber from the surface of the artificial leather, a high balance between flame retardancy and texture and other physical properties can be maintained. Moreover, it is preferable that it is 0.5-30 weight% as solid content weight of all the phosphorus flame retardants with respect to the weight of the final whole artificial leather.
このような本発明の製造方法により得られた銀付調の人工皮革は、有機溶剤を使用しない環境に優しい水性タイプの含浸基材を用いたにもかかわらず、高度な難燃性を有しながら物性に優れた人工皮革となる。 Such artificial leather with a silver tone obtained by the production method of the present invention has high flame retardancy despite using an environmentally friendly water-based impregnated base material that does not use an organic solvent. It is an artificial leather with excellent physical properties.
得られた人工皮革は、スポーツシューズ、婦人・紳士靴などの靴用途、競技用各種ボール用途、手帳・ノート等の装丁用途、衣料用途に用いることができ、特に難燃性と風合いの高いバランスが要求される家具・車輌、内装材、インテリア材などの産業資材用途に好ましく用いることができる。 The resulting artificial leather can be used for sports shoes, shoes for women's and men's shoes, various ball applications for competitions, binding for notebooks and notebooks, and clothing, especially with a high balance of flame resistance and texture. Can be preferably used for industrial materials such as furniture / vehicles, interior materials and interior materials.
以下、実施例により、本発明を更に具体的に説明する。
なお、実施例における各項目は次の方法で測定した。
(1)収縮率
収縮前の面積をS1とする。収縮後の面積をS2とする。収縮率は次の計算で求める。
収縮率(%)=(S1−S2)×100/S1
(2)難燃性
英国防炎規格(布張家具用防炎試験)BS5862に準じた方法で実施し、バーナーとしてはブンゼンバーナーを、ガスは都市ガスを使用し、炎長3.5cm、バーナーを45度に傾け20秒間接炎した後の燃焼長さで表す。
Hereinafter, the present invention will be described more specifically with reference to examples.
In addition, each item in an Example was measured with the following method.
(1) the area before shrinkage shrinkage and S 1. Area after shrinkage is referred to as S 2. The shrinkage rate is obtained by the following calculation.
Shrinkage rate (%) = (S 1 −S 2 ) × 100 / S 1
(2) Flame retardance The flame retardant standard (flameproof test for upholstered furniture) is conducted in accordance with BS 5862. Bunsen burner is used as the burner, city gas is used as the gas, flame length is 3.5 cm, burner Is represented by the combustion length after inclining at 45 degrees and indirect flame for 20 seconds.
[実施例1]
第1成分として収縮特性を有するポリエチレンテレフタレート、第2成分をナイロン−6とする16分割歯車型の断面を有する親糸繊度4.4dtexの剥離分割型複合繊維を、ニードルパンチと高圧水流交絡処理により、繊維の絡合と分割処理を行い厚さ1.15mm、目付け265g/m2の不織布とし、次いでこの分割処理後の繊維集合体を75℃の温水槽中に20秒間浸漬し、第1成分のポリエチレンテレフタレート繊維を収縮させ、面積収縮率を24%とし、次いで乾燥して繊維集合体(不織布)を得た。
[Example 1]
A peeled split type composite fiber having a cross section of a 16 split gear type with polyethylene terephthalate having shrinkage characteristics as the first component and nylon-6 as the second component and having a main yarn fineness of 4.4 dtex is obtained by needle punching and high-pressure hydroentanglement treatment. The fiber is entangled and divided into a non-woven fabric having a thickness of 1.15 mm and a basis weight of 265 g / m 2 , and then the fiber assembly after the division treatment is immersed in a 75 ° C. hot water tank for 20 seconds to obtain a first component. The polyethylene terephthalate fiber was shrunk to an area shrinkage rate of 24% and then dried to obtain a fiber assembly (nonwoven fabric).
次いで得られた繊維集合体をリン系難燃剤(脂肪族環式ホスホン酸エステル、明成化学工業株式会社製K−19A)の水溶液に浸漬し、マングルで絞りリン系難燃剤の固形分付着量が繊維重量に対し4重量%付着するように調整し、乾燥した。
得られた繊維集合体は、目付け367g/m2、厚さ1.0mm、見掛け密度0.367g/m3と高密度で充実感のあるものであった。
Next, the obtained fiber assembly is immersed in an aqueous solution of a phosphorus-based flame retardant (aliphatic cyclic phosphonic acid ester, K-19A manufactured by Meisei Chemical Industry Co., Ltd.), and the solid content of the phosphorus-based flame retardant is reduced by mangle. It adjusted so that 4 weight% might adhere with respect to fiber weight, and dried.
The obtained fiber assembly had a high density with a basis weight of 367 g / m 2 , a thickness of 1.0 mm, and an apparent density of 0.367 g / m 3 .
次いで得られた繊維集合体(不織布)に、感熱凝固型水系ポリウレタンの9%分散液(感熱凝固温度60℃)100部にリン系難燃剤(明成化学工業株式会社製K−19A)0.5部を混合し調整した含浸液を含浸させ、表面の余分な分散液を掻き落として、下部に設置された水槽中の沸騰水によって上部の雰囲気温度を92℃、相対湿度を99%の凝固ボックスに1分間曝してポリウレタンの感熱凝固を行い、次いで97℃の熱水槽中で1分間処理した。その後、冷却してからマングルロールで絞り、110℃の熱風乾燥機で乾燥させて厚さ1.0mm、見掛け密度0.44g/cm3の繊維複合体(基材)を得た。得られた繊維複合体の繊維:ポリウレタンの比率は重量で100:30であった。ポリウレタン中のリン系難燃剤の固形分付着量がポリウレタン重量に対し12重量%であった。また電子顕微鏡により断面を観察したところポリウレタンは繊維複合体の厚さ方向に均一に分布されたものであった。 Next, the obtained fiber assembly (nonwoven fabric) was mixed with 100 parts of a 9% dispersion of a heat-sensitive coagulation-type aqueous polyurethane (heat-sensitive coagulation temperature 60 ° C.), and a phosphorus flame retardant (K-19A manufactured by Meisei Chemical Co., Ltd.) 0.5 The impregnating liquid was mixed and the impregnated liquid was impregnated, the excess dispersion liquid on the surface was scraped off, and the upper atmosphere temperature was 92 ° C. and the relative humidity was 99% by boiling water in the water tank installed at the lower part. Was subjected to thermal coagulation of the polyurethane for 1 minute, and then treated in a 97 ° C. hot water bath for 1 minute. Then, after cooling, it was squeezed with a mangle roll and dried with a hot air dryer at 110 ° C. to obtain a fiber composite (base material) having a thickness of 1.0 mm and an apparent density of 0.44 g / cm 3 . The fiber composite had a fiber: polyurethane ratio of 100: 30 by weight. The solid content adhesion amount of the phosphorus-based flame retardant in the polyurethane was 12% by weight with respect to the polyurethane weight. When the cross section was observed with an electron microscope, the polyurethane was uniformly distributed in the thickness direction of the fiber composite.
一方、離型紙(リンテック社製R53)上に、ポリウレタンの33%水分散液100部に増粘剤、および着色剤5部を攪拌しながら添加し粘度を8000mPa・sに調整した調合液を目付け100g/m2でコートし、温度70℃で2分間、110℃で2分間乾燥した。さらにその表面に、水分散型ポリウレタン系接着剤(45%濃度)100部にリン系難燃剤(明成化学工業株式会社製K−19A)1.5部、着色剤(大日本インキ化学工業株製ダイラックブラックHS9530)5部、および増粘剤(大日本インキ化学工業株製ハイドランアシスターT1)を混合して粘度を5000mPa・sに調整した調合液を目付け150g/m2でコートした。次いで、温度90℃で2分乾燥後、先に得られた繊維複合体を重ね合わせ、温度110℃の加熱シリンダー表面上で0.6mmの間隙のロールに通過させ圧着した。その後、温度60℃の雰囲気下で2日間放置した後、離型紙を剥ぎ取り人工皮革を得た。得られた人工皮革は、厚さ1.1mm、目付け530g/m2、難燃剤の含有量が4.4重量%、剥離強力は18N/cmであり、風合い、物性に優れているにもかかわらず、炎に曝しても燃焼せず燃焼テストでは難燃性0mmであった。 On the other hand, on a release paper (R53 manufactured by Lintec Corporation), a thickening agent and 5 parts of a coloring agent were added to 100 parts of a 33% aqueous dispersion of polyurethane while stirring, and the mixture was adjusted to a viscosity of 8000 mPa · s. The film was coated at 100 g / m 2 and dried at a temperature of 70 ° C. for 2 minutes and at 110 ° C. for 2 minutes. Furthermore, 100 parts of a water-dispersible polyurethane adhesive (45% concentration) on the surface, 1.5 parts of a phosphorus-based flame retardant (K-19A manufactured by Meisei Chemical Co., Ltd.), and a colorant (manufactured by Dainippon Ink & Chemicals, Inc.) A mixture prepared by mixing 5 parts of Dirac Black HS9530) and a thickener (Hydran Assister T1 manufactured by Dainippon Ink & Chemicals, Inc.) and adjusting the viscosity to 5000 mPa · s was coated at a weight of 150 g / m 2 . Next, after drying for 2 minutes at a temperature of 90 ° C., the previously obtained fiber composite was superposed and passed through a roll with a gap of 0.6 mm on the surface of a heated cylinder having a temperature of 110 ° C. and pressure bonded. Then, after leaving it for 2 days in the atmosphere of 60 degreeC temperature, the release paper was peeled off and the artificial leather was obtained. The obtained artificial leather has a thickness of 1.1 mm, a basis weight of 530 g / m 2 , a flame retardant content of 4.4% by weight, and a peel strength of 18 N / cm, although it has excellent texture and physical properties. In addition, it did not burn even when exposed to flames, and the flame test showed flame resistance of 0 mm.
[比較例1]
リン系難燃剤を使用しない以外は、実施例1と同様に人工皮革を作成した。得えられた人工皮革をリン系難燃剤(脂肪族環式ホスホン酸エステル、明成化学工業株式会社製K−19A)の3%水溶液に浸漬しマングルロールで絞り含水率を150%として乾燥した。得られた人工皮革は難燃剤の含有量が4.5重量%、剥離強力は13N/cmであり、表面平滑性が悪く、アラビが目立ち、しかも炎に曝した後に炎を離しても燃焼し続け、燃焼テストでは難燃性∞mmのものであった。
[Comparative Example 1]
An artificial leather was produced in the same manner as in Example 1 except that no phosphorus flame retardant was used. The obtained artificial leather was dipped in a 3% aqueous solution of a phosphorus flame retardant (aliphatic cyclic phosphonate ester, K-19A manufactured by Meisei Chemical Industry Co., Ltd.) and squeezed with mangle roll to dry the moisture content to 150%. The resulting artificial leather has a flame retardant content of 4.5% by weight, peel strength of 13 N / cm, poor surface smoothness, noticeable arabi, and burns even after the flame is released. Subsequently, in the combustion test, the flame resistance was ∞ mm.
[比較例2]
リン系難燃剤を使用しない以外は、実施例1と同様に人工皮革を作成した。得えられた人工皮革をリン系難燃剤(脂肪族環式ホスホン酸エステル、明成化学工業株式会社製K−19A)の10%水溶液に浸漬しマングルロールで絞り含水率を150%として乾燥した。得られた人工皮革は難燃剤の含有量が15.0重量%、剥離強力は12N/cmであり、燃焼テストでは難燃性0mであったが、人工皮革の表面および裏面から難燃剤がしみ出て粘着性を有するばかりか接触するものに付着し、実用に耐えないものであった。
[Comparative Example 2]
An artificial leather was produced in the same manner as in Example 1 except that no phosphorus flame retardant was used. The obtained artificial leather was dipped in a 10% aqueous solution of a phosphorus-based flame retardant (aliphatic cyclic phosphonic acid ester, K-19A manufactured by Meisei Chemical Industry Co., Ltd.) and squeezed with mangle roll and dried at a moisture content of 150%. The obtained artificial leather had a flame retardant content of 15.0% by weight, a peel strength of 12 N / cm, and the flame test showed flame resistance of 0 m. It was sticky to the thing that came out and adhered to it, and it was unbearable for practical use.
[比較例3]
繊維集合体に難燃剤を処理しない以外は、含浸用およびラミネート用の水系ポリウレタンには実施例1と同じリン系難燃剤(脂肪族環式ホスホン酸エステル、明成化学工業株式会社製K−19A)を含有した水系ポリウレタンを使用し、実施例1と同様に人工皮革を作成した。
[Comparative Example 3]
The same phosphorus-based flame retardant as in Example 1 (aliphatic cyclic phosphonic acid ester, K-19A manufactured by Meisei Chemical Co., Ltd.) is used for the water-based polyurethane for impregnation and lamination except that the fiber assembly is not treated with a flame retardant. An artificial leather was prepared in the same manner as in Example 1 using water-based polyurethane containing.
得えられた人工皮革をリン系難燃剤(明成化学工業株式会社製K−19A)の3%水溶液に浸漬しマングルロールで絞り含水率を150%として乾燥した。得られた人工皮革は難燃剤の含有量が6.3重量%、剥離強力は15N/cmであり、触感が悪く、難燃剤のベタつきがあり、又面平滑性が悪いものであり、炎に曝した後に炎を離しても燃焼し続け、燃焼テストでは難燃性∞mmであった。 The obtained artificial leather was dipped in a 3% aqueous solution of a phosphorus flame retardant (K-19A, manufactured by Meisei Chemical Industry Co., Ltd.) and dried with a mangle roll with a water content of 150%. The obtained artificial leather has a flame retardant content of 6.3% by weight, a peel strength of 15 N / cm, poor tactile sensation, flame retardant stickiness, and poor surface smoothness. Even after releasing the flame after exposure, it continued to burn, and in the combustion test, it was flame retardant ∞ mm.
Claims (7)