JP2006030458A - Polarizing plate and liquid crystal display device - Google Patents
Polarizing plate and liquid crystal display device Download PDFInfo
- Publication number
- JP2006030458A JP2006030458A JP2004207204A JP2004207204A JP2006030458A JP 2006030458 A JP2006030458 A JP 2006030458A JP 2004207204 A JP2004207204 A JP 2004207204A JP 2004207204 A JP2004207204 A JP 2004207204A JP 2006030458 A JP2006030458 A JP 2006030458A
- Authority
- JP
- Japan
- Prior art keywords
- group
- film
- polarizing plate
- carbon atoms
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、吸収軸方向と透過軸方向の弾性率の差異を小さくした偏光板、及び該偏光板を使用した液晶表示装置に関する。 The present invention relates to a polarizing plate in which a difference in elastic modulus between an absorption axis direction and a transmission axis direction is reduced, and a liquid crystal display device using the polarizing plate.
液晶表示装置は、低電圧・低消費電力で小型化・薄膜化が可能など様々な利点からパーソナルコンピューターや携帯機器のモニター、テレビ用途に広く利用されている。このような液晶表示装置は液晶セル内の液晶分子の配列状態により様々なモードが提案されているが、従来は液晶セルの下側基板から上側基板に向かって約９０°捩れた配列状態になるＴＮモードが主流であった。
一般に液晶表示装置は液晶セル、光学補償シート、偏光子から構成される。光学補償シートは画像着色を解消したり、視野角を拡大するために用いられており、延伸した複屈折フィルムや透明フィルムに液晶を塗布したフィルムが使用されている。例えば、特許文献１ではディスコティック液晶をトリアセチルセルロースフィルム上に塗布し配向させて固定化した光学補償シートをＴＮモードの液晶セルに適用し、視野角を広げる技術が開示されている。しかしながら、大画面で様々な角度から見ることが想定されるテレビ用途の液晶表示装置は視野角依存性に対する要求が厳しく、前述のような手法をもってしても要求を満足することはできていない。そのため、ＩＰＳ（In-Plane Switching）モード、ＯＣＢ（Optically Compensatory Bend）モード、ＶＡ（Vertically Aligned）モードなど、ＴＮモードとは異なる液晶表示装置が研究されている。特にＶＡモードはコントラストが高く、比較的製造の歩留まりが高いことからＴＶ用の液晶表示装置として着目されている。
Liquid crystal display devices are widely used in monitors for personal computers and portable devices, and for television applications because of their various advantages, such as low voltage and low power consumption, enabling miniaturization and thinning. Various modes have been proposed for such a liquid crystal display device depending on the alignment state of the liquid crystal molecules in the liquid crystal cell. Conventionally, the liquid crystal display device is in an alignment state twisted by about 90 ° from the lower substrate to the upper substrate of the liquid crystal cell. The TN mode was mainstream.
In general, a liquid crystal display device includes a liquid crystal cell, an optical compensation sheet, and a polarizer. The optical compensation sheet is used for eliminating image coloring or expanding the viewing angle, and a stretched birefringent film or a film obtained by applying a liquid crystal to a transparent film is used. For example, Patent Document 1 discloses a technique of applying an optical compensation sheet in which a discotic liquid crystal is applied on a triacetyl cellulose film, aligned, and fixed to a TN mode liquid crystal cell to widen the viewing angle. However, a television-use liquid crystal display device that is expected to be viewed from various angles on a large screen has a strict requirement for viewing angle dependency, and even with the above-described method, the requirement cannot be satisfied. Therefore, liquid crystal display devices different from the TN mode, such as an IPS (In-Plane Switching) mode, an OCB (Optically Compensatory Bend) mode, and a VA (Vertically Aligned) mode, have been studied. In particular, the VA mode is attracting attention as a liquid crystal display device for TV because of its high contrast and relatively high production yield.
ところで、セルロースアシレートフィルムは、他のポリマーフィルムと比較して、光学的等方性が高い（レターデーション値が低い）という特徴がある。従って、光学的等方性が要求される用途、例えば偏光板には、セルロースアシレートフィルムを用いることが普通である。
一方、液晶表示装置の光学補償シート（位相差フィルム）には、逆に光学的異方性（高いレターデーション値）が要求される。特にＶＡ用の光学補償シートでは３０乃至２００ｎｍの正面レターデーション（Ｒｅ）、７０乃至４００ｎｍの膜厚方向レターデーション（Ｒｔｈ）が必要とされる。従って、光学補償シートとしては、ポリカーボネートフィルムやポリスルホンフィルムのようなレターデーション値が高い合成ポリマーフィルムを用いることが普通であった。正面レターデーション値Ｒｅと膜厚方向レターデーション値Ｒｔｈとは、それぞれ下記式にしたがって算出される光学特性値である。
Ｒｅ＝（ｎｘ−ｎｙ）×ｄ
Ｒｔｈ＝｛（ｎｘ＋ｎｙ）／２−ｎｚ｝×ｄ
（式中、ｎｘはフィルム平面内のｘ方向の屈折率であり、ｎｙはフィルム平面内のｙ方向の屈折率であり、ｎｚはフィルム面と直交する方向の屈折率であり、ｄはフィルムの厚み（ｎｍ）である。）
以上のように光学材料の技術分野では、ポリマーフィルムに光学的異方性（高いレターデーション値）が要求される場合には合成ポリマーフィルムを使用し、光学的等方性（低いレターデーション値）が要求される場合にはセルロースアシレートフィルムを使用することが一般的な原則であった。
By the way, the cellulose acylate film is characterized by high optical isotropy (low retardation value) as compared with other polymer films. Therefore, it is common to use a cellulose acylate film for an application requiring optical isotropy, for example, a polarizing plate.
On the other hand, the optical compensation sheet (retardation film) of the liquid crystal display device is required to have optical anisotropy (high retardation value). In particular, an optical compensation sheet for VA requires a front retardation (Re) of 30 to 200 nm and a thickness direction retardation (Rth) of 70 to 400 nm. Therefore, it is common to use a synthetic polymer film having a high retardation value such as a polycarbonate film or a polysulfone film as the optical compensation sheet. The front retardation value Re and the film thickness direction retardation value Rth are optical characteristic values calculated according to the following equations, respectively.
Re = (nx−ny) × d
Rth = {(nx + ny) / 2−nz} × d
(Where nx is the refractive index in the x direction within the film plane, ny is the refractive index in the y direction within the film plane, nz is the refractive index in the direction perpendicular to the film plane, and d is the film refractive index) Thickness (nm).)
As described above, in the technical field of optical materials, when a polymer film requires optical anisotropy (high retardation value), a synthetic polymer film is used and optical isotropy (low retardation value) is used. It was a general principle to use cellulose acylate films when required.
特許文献２には、従来の一般的な原則を覆して、光学的異方性が要求される用途にも使用できる高いレターデーション値を有するセルロースアセテートフィルムが提案されている。この提案ではセルローストリアセテートで高いレターデーション値を実現するために、少なくとも２つの芳香環を有する芳香族化合物、中でも１，３，５−トリアジン環を有する化合物を添加し、延伸処理を行っている。一般にセルローストリアセテートは延伸しにくい高分子素材であり、複屈折率を大きくすることは困難であることが知られているが、添加剤を延伸処理で同時に配向させることにより複屈折率を大きくすることを可能にし、高いレターデーション値を実現している。このフィルムは偏光板の保護膜を兼ねることができるため、安価で薄膜な液晶表示装置を提供することができる利点がある。
特許文献３には炭素数２〜４のアシル基を置換基として有し、アセチル基の置換度をＡとし、プロピオニル基またはブチリル基の置換度をＢとしたとき、式２．０≦Ａ＋Ｂ≦３．０及び式Ａ＜２．４を同時に満たすセルロースエステルを含有する光学フィルムであって、更に、波長５９０ｎｍにおける遅相軸方向の屈折率Ｎｘ及び進相軸方向の屈折率Ｎｙが式０．０００５≦Ｎｘ−Ｎｙ≦０．００５０を満たすことを特徴とする光学フィルムが開示されている。
特許文献４にはＶＡモード液晶表示装置に用いられる偏光板において、該偏光板が、偏光子と光学的に二軸性の混合脂肪酸セルロースエステルフィルムとを有し、液晶セルと偏光子の間に該光学的に二軸性の混合脂肪酸セルロースエステルフィルムが配置されていることを特徴とする偏光板が開示されている。
Patent Document 3 has an acyl group having 2 to 4 carbon atoms as a substituent, where the substitution degree of acetyl group is A and the substitution degree of propionyl group or butyryl group is B, formula 2.0 ≦ A + B ≦ 3.0 and an optical film containing cellulose ester satisfying the formula A <2.4 at the same time, and the refractive index Nx in the slow axis direction and the refractive index Ny in the fast axis direction at a wavelength of 590 nm are expressed by the formula 0. An optical film characterized by satisfying 0005 ≦ Nx−Ny ≦ 0.0050 is disclosed.
In Patent Document 4, a polarizing plate used in a VA mode liquid crystal display device, the polarizing plate has a polarizer and an optically biaxial mixed fatty acid cellulose ester film, and the liquid crystal cell and the polarizer are interposed. A polarizing plate is disclosed in which the optically biaxial mixed fatty acid cellulose ester film is disposed.
上述の文献に開示されている方法は、安価でかつ薄い液晶表示装置が得られる点で有効である。しかしながら、近年、液晶表示装置はテレビへの使用が急速に進んでおり、より多様な使用環境を想定しての評価を行った場合、画面上に丸いムラが発生することが明らかになった。テレビはモニターよりもバックライトが明るく、ムラが見えやすいうえに、ムラの少ない面状が求められるため、このムラの発生は大きな問題とされる。
そのため、このようなムラを発生させない、光学補償機能を有する偏光板の開発が要望されている。
本発明の目的は、高い光学補償機能を有しつつ、ムラを生じさせないように改良した偏光板、および該偏光板を使用した視野角性能に優れる液晶表示装置を提供することである。
The method disclosed in the above-mentioned document is effective in that an inexpensive and thin liquid crystal display device can be obtained. However, in recent years, the use of liquid crystal display devices in televisions has been rapidly progressing, and it has been clarified that round unevenness occurs on the screen when an evaluation is performed assuming more various usage environments. Since a TV has a brighter backlight than a monitor, and it is easy to see unevenness, and a surface shape with less unevenness is required, this unevenness is a major problem.
Therefore, development of a polarizing plate having an optical compensation function that does not cause such unevenness is desired.
An object of the present invention is to provide a polarizing plate improved so as not to cause unevenness while having a high optical compensation function, and a liquid crystal display device having excellent viewing angle performance using the polarizing plate.
本発明者らが鋭意検討した結果、偏光板の吸収軸方向と透過軸方向の弾性率の差異を小さくすることで、上記目的を達成できることを見出し、本発明を完成するに至った。また、さらに、偏光板の透過軸方向の弾性率ＥTを高めた特定範囲とすることで、さらに上記目的を達成できる。
即ち、本発明は、下記構成の偏光板及び液晶表示装置であり、これにより本発明の上記目的が達成される。
As a result of intensive studies by the present inventors, it has been found that the above object can be achieved by reducing the difference in elastic modulus between the absorption axis direction and the transmission axis direction of the polarizing plate, and the present invention has been completed. Furthermore, the said objective can further be achieved by setting it as the specific range which raised the elasticity modulus ET of the transmission axis direction of a polarizing plate.
That is, the present invention is a polarizing plate and a liquid crystal display device having the following constitutions, thereby achieving the object of the present invention.
１）
偏光子の少なくとも一方に保護膜を貼り合わせた偏光板であって、２５℃６０％ＲＨ下における、該偏光板の吸収軸方向の弾性率ＥA及び透過軸方向の弾性率ＥTが、下記式（Ｉ）を満たすことを特徴とする偏光板。
式（Ｉ） ： ０．９≦ＥA／ＥT≦１．４
２）
前記透過軸方向の弾性率ＥTが下記式（II）を満たすことを特徴とする１）に記載の偏光板。
式（II） ： ２６４０ＭＰａ≦ＥT≦５４００ＭＰａ
３）
前記一方の保護膜の、式（III）で定義される正面レターデーション値Ｒｅ(λ)と式（IV）で定義される膜厚方向のレターデーション値Ｒｔｈ(λ)とが、下記式（Ｖ）及び（VI）を満たすことを特徴とする１）または２）に記載の偏光板。
式（III） ： Ｒｅ(λ)＝（ｎｘ−ｎｙ）×ｄ
式（IV） ： Ｒｔｈ(λ)＝｛（ｎｘ＋ｎｙ）／２−ｎｚ｝×ｄ
式（Ｖ） ： ２０ｎｍ≦Ｒｅ(590)≦２００ｎｍ
式（VI） ： ７０ｎｍ≦Ｒｔｈ(590)≦４００ｎｍ
［式中、Ｒｅ(λ)、Ｒｔｈ(λ)は波長λｎｍにおける測定値（単位：ｎｍ）である。またｎｘはフィルム面内の遅相軸方向の屈折率であり、ｎｙはフィルム面内の進相軸方向の屈折率であり、ｎｚはフィルムの厚み方向の屈折率であり、ｄはフィルムの厚さ（単位：ｎｍ）である。］
４）
前記一方の保護膜の正面レターデーション値Ｒｅと膜厚方向のレターデーション値Ｒｔｈとが下記式（VII）を満たすことを特徴とする１）乃至３）のいずれかに記載の偏光板。
式（VII） ： ０．１≦Ｒｅ(590)／Ｒｔｈ(590)≦０．８
５）
前記一方の保護膜が、セルロースの水酸基がアセチル基および炭素原子数が３以上のアシル基で置換されたセルロースの混合脂肪酸エステルであるセルロースアシレートを主たるポリマー成分とするセルロースアシレートフィルムであって、
該セルロースアシレートが、アセチル基の置換度Ａと、炭素原子数が３以上のアシル基の置換度Ｂとが下記式（VIII）、（IX）を満たすことを特徴とする１）乃至４）のいずれかに記載の偏光板。
式（VIII）： ２．０≦Ａ＋Ｂ≦３．０
式（IX） ： ０＜Ｂ
６）
前記炭素原子数が３以上のアシル基がブタノイル基であることを特徴とする５）に記載の偏光板。
７）
前記炭素原子数が３以上のアシル基がプロピオニル基であることを特徴とする５）に記載の偏光板。
８）
前記一方の保護膜が、セルロースを構成するグルコース単位の水酸基を炭素原子数が２以上のアシル基で置換して得られたセルロースアシレートからなるフィルムであって、セルロースを構成するグルコース単位の２位の水酸基のアシル基による置換度をＤＳ２、３位の水酸基のアシル基による置換度をＤＳ３、６位の水酸基のアシル基による置換度をＤＳ６としたときに、下記式（Ｘ）および（ＸI）を満たすセルロースアシレートフィルムであることを特徴とする１）乃至７）のいずれかに記載の偏光板。
式（Ｘ） ： ２．０≦ＤＳ２＋ＤＳ３＋ＤＳ６≦３．０
式（ＸI） ： ＤＳ６／（ＤＳ２＋ＤＳ３＋ＤＳ６）≧０．３１５
９）
前記アシル基がアセチル基であることを特徴とする８）に記載の偏光板。
１０）
前記一方の保護膜が、可塑剤、紫外線吸収剤、剥離促進剤、染料、及びマット剤のうち１種以上を含有していることを特徴とする１）乃至９）のいずれかに記載の偏光板。
１１）
前記一方の保護膜が、棒状化合物または円盤状化合物のレターデーション発現剤を１種以上含有していることを特徴とする１）乃至１０）のいずれかに記載の偏光板。
１２）
前記一方の保護膜の２５℃６０％ＲＨ下におけるＭＤ方向の弾性率ＥMFとＴＤ方向の弾性率ＥTFとが下記式（ＸII）を満たすことを特徴とする１）乃至１１）のいずれかに記載の偏光板。
式（ＸII）： ０．９≦ＥTF／ＥMF≦１．７
１３）
前記一方の保護膜の２５℃６０％ＲＨ下におけるＴＤ方向の弾性率ＥTFが下記式（ＸIII）を満たすことを特徴とする１）乃至１２）のいずれかに記載の偏光板。
式（ＸIII）： ２８４０ＭＰａ≦ＥTF≦４７１０ＭＰａ
１４）
前記一方の保護膜が、高分子フィルム上に光学異方性層を設けたものであることを特徴とする１）乃至１３）のいずれかに記載の偏光板。
１５）
前記一方の保護膜と反対側に配置される保護膜の表面にハードコート層、防眩層、反射防止層の少なくとも一層を設けたことを特徴とする１）乃至１４）のいずれかに記載の偏光板。
１６）
前記一方の保護膜が液晶セル側に配置されるよう、１）乃至１５）のいずれかに記載の偏光板を用いたことを特徴とする液晶表示装置。
1)
A polarizing plate in which a protective film is bonded to at least one of the polarizers, and an elastic modulus EA in the absorption axis direction and an elastic modulus ET in the transmission axis direction of the polarizing plate at 25 ° C. and 60% RH are expressed by the following formula ( A polarizing plate characterized by satisfying I).
Formula (I): 0.9 ≦ EA / ET ≦ 1.4
2)
The polarizing plate according to 1), wherein the elastic modulus ET in the transmission axis direction satisfies the following formula (II):
Formula (II): 2640 MPa ≦ ET ≦ 5400 MPa
3)
The front retardation value Re ( λ ) defined by the formula (III) and the retardation value Rth ( λ ) in the film thickness direction defined by the formula (IV) of the one protective film are expressed by the following formula (V ) And (VI). The polarizing plate according to 1) or 2).
Formula (III): Re ( λ ) = (nx−ny) × d
Formula (IV): Rth ( λ ) = {(nx + ny) / 2−nz} × d
Formula (V): 20 nm ≦ Re (590) ≦ 200 nm
Formula (VI): 70 nm ≦ Rth (590) ≦ 400 nm
[In the formula, Re ( λ ) and Rth ( λ ) are measured values (unit: nm) at a wavelength of λ nm. Further, nx is the refractive index in the slow axis direction in the film plane, ny is the refractive index in the fast axis direction in the film plane, nz is the refractive index in the thickness direction of the film, and d is the thickness of the film. (Unit: nm). ]
4)
The polarizing plate according to any one of 1) to 3), wherein the front retardation value Re and the retardation value Rth in the film thickness direction of the one protective film satisfy the following formula (VII).
Formula (VII): 0.1 ≦ Re (590) / Rth (590) ≦ 0.8
5)
The one protective film is a cellulose acylate film comprising, as a main polymer component, cellulose acylate which is a mixed fatty acid ester of cellulose in which a hydroxyl group of cellulose is substituted with an acetyl group and an acyl group having 3 or more carbon atoms. ,
The cellulose acylate is characterized in that the substitution degree A of the acetyl group and the substitution degree B of the acyl group having 3 or more carbon atoms satisfy the following formulas (VIII) and (IX): The polarizing plate in any one of.
Formula (VIII): 2.0 ≦ A + B ≦ 3.0
Formula (IX): 0 <B
6)
The polarizing plate according to 5), wherein the acyl group having 3 or more carbon atoms is a butanoyl group.
7)
The polarizing plate according to 5), wherein the acyl group having 3 or more carbon atoms is a propionyl group.
8)
The one protective film is a film made of cellulose acylate obtained by substituting the hydroxyl group of the glucose unit constituting cellulose with an acyl group having 2 or more carbon atoms, and comprising 2 glucose units constituting cellulose. When the substitution degree of the hydroxyl group at the position is DS2, the substitution degree of the hydroxyl group at the 3-position is DS3, and the substitution degree of the hydroxyl group at the 6-position is DS6, the following formulas (X) and (XI The polarizing plate according to any one of 1) to 7), which is a cellulose acylate film satisfying
Formula (X): 2.0 ≦ DS2 + DS3 + DS6 ≦ 3.0
Formula (XI): DS6 / (DS2 + DS3 + DS6) ≧ 0.315
9)
The polarizing plate according to 8), wherein the acyl group is an acetyl group.
10)
The polarized light according to any one of 1) to 9), wherein the one protective film contains at least one of a plasticizer, an ultraviolet absorber, a peeling accelerator, a dye, and a matting agent. Board.
11)
11. The polarizing plate according to any one of 1) to 10), wherein the one protective film contains at least one rod-like compound or discotic compound retardation enhancer.
12)
The elastic modulus EMF in the MD direction and the elastic modulus ETF in the TD direction satisfy the following formula (XII) at 25 ° C. and 60% RH of the one protective film, according to any one of 1) to 11) Polarizing plate.
Formula (XII): 0.9 ≦ ETF / EMF ≦ 1.7
13)
The polarizing plate according to any one of 1) to 12), wherein an elastic modulus ETF in a TD direction under 25 ° C. and 60% RH of the one protective film satisfies the following formula (XIII).
Formula (XIII): 2840 MPa ≦ ETF ≦ 4710 MPa
14)
The polarizing plate according to any one of 1) to 13), wherein the one protective film is a polymer film provided with an optically anisotropic layer.
15)
15. The method according to any one of 1) to 14), wherein at least one layer of a hard coat layer, an antiglare layer, and an antireflection layer is provided on the surface of the protective film disposed on the side opposite to the one protective film. Polarizer.
16)
A liquid crystal display device using the polarizing plate according to any one of 1) to 15) so that the one protective film is disposed on the liquid crystal cell side.
本発明の偏光板は、吸収軸方向と透過軸方向の弾性率の差異が小さく、視野角補償効果に優れる。
また、本発明の偏光板を使用することにより、ムラが少なく、表示性能に優れた液晶表示装置を作製することができる。
The polarizing plate of the present invention has a small difference in elastic modulus between the absorption axis direction and the transmission axis direction, and is excellent in viewing angle compensation effect.
In addition, by using the polarizing plate of the present invention, a liquid crystal display device with less unevenness and excellent display performance can be manufactured.
以下、本発明について更に詳細に説明する。なお、本明細書において、数値が物性値、特性値等を表す場合に、「（数値１）〜（数値２）」という記載は「（数値１）以上（数値２）以下」の意味を表す。また、本明細書において、「（メタ）アクリレート」との記載は、「アクリレート及びメタクリレートの少なくともいずれか」の意味を表す。「（メタ）アクリル酸」等も同様である。 Hereinafter, the present invention will be described in more detail. In the present specification, when a numerical value represents a physical property value, a characteristic value, etc., the description “(numerical value 1) to (numerical value 2)” means “(numerical value 1) or more and (numerical value 2) or less”. . Moreover, in this specification, description with "(meth) acrylate" represents the meaning of "at least one of an acrylate and a methacrylate." The same applies to “(meth) acrylic acid” and the like.
（セルロースアシレートフィルム）
まず、本発明において用いられるセルロースアシレートについて詳細に記載する。本発明においては異なる２種類以上のセルロースアシレートを混合して用いても良い。
前記のセルロースアシレートは、セルロースの水酸基をアセチル基および炭素原子数が３以上のアシル基で置換して得られたセルロースの混合脂肪酸エステルであって、セルロースの水酸基への置換度が下記式（VIII）及び（IX）を満足するセルロースアシレートである。
式（VIII）： ２．０≦Ａ＋Ｂ≦３．０
式（IX） ： ０＜Ｂ
ここで、式中Ａ及びＢはセルロースの水酸基に置換されているアシル基の置換度を表し、Ａはアセチル基の置換度、またＢは炭素原子数３以上のアシル基の置換度である。
セルロースを構成するβ−１，４結合しているグルコース単位は、２位、３位および６位に遊離の水酸基を有している。セルロースアシレートは、これらの水酸基の一部または全部をアシル基によりエステル化した重合体（ポリマー）である。アシル置換度は、２位、３位および６位のそれぞれについて、セルロースがエステル化している割合（１００％のエステル化は置換度１）を意味する。
本発明では、水酸基のＡとＢとの置換度の総和（Ａ＋Ｂ）は、上記式（VIII）に示すように、２．０〜３．０であり、好ましくは２．２〜２．９であり、特に好ましくは２．４０〜２．８５である。また、Ｂの置換度は上記式（IX）に示すように、０より大きいことが好ましく、０．６以上であることがさらに好ましい。
Ａ＋Ｂが２．０未満であると、親水性が強くなり環境湿度の影響を受けやすくなる。
さらにＢはその２８％以上が６位水酸基の置換基であるのが好ましいが、より好ましくは３０％以上が６位水酸基の置換基であり、３１％以上がさらに好ましく、特には３２％以上が６位水酸基の置換基であることが好ましい。
また更に、セルロースアシレートの６位のＡとＢの置換度の総和が０．７５以上であるのが好ましく、さらには０．８０以上が、特には０．８５以上が好ましい。これらのセルロースアシレートフィルムにより溶解性、濾過性の好ましいフィルム調製用の溶液が作製でき、非塩素系有機溶媒においても、良好な溶液の作製が可能となる。更に粘度が低くろ過性のよい溶液の作成が可能となる。
(Cellulose acylate film)
First, the cellulose acylate used in the present invention will be described in detail. In the present invention, two or more different cellulose acylates may be mixed and used.
The cellulose acylate is a mixed fatty acid ester of cellulose obtained by substituting the hydroxyl group of cellulose with an acetyl group and an acyl group having 3 or more carbon atoms, and the degree of substitution of the cellulose with a hydroxyl group is represented by the following formula ( Cellulose acylate satisfying VIII) and (IX).
Formula (VIII): 2.0 ≦ A + B ≦ 3.0
Formula (IX): 0 <B
Here, A and B in the formula represent the substitution degree of the acyl group substituted with the hydroxyl group of cellulose, A is the substitution degree of the acetyl group, and B is the substitution degree of the acyl group having 3 or more carbon atoms.
Glucose units having β-1,4 bonds constituting cellulose have free hydroxyl groups at the 2nd, 3rd and 6th positions. Cellulose acylate is a polymer obtained by esterifying some or all of these hydroxyl groups with acyl groups. The degree of acyl substitution means the proportion of cellulose esterified at each of the 2-position, 3-position and 6-position (100% esterification has a substitution degree of 1).
In the present invention, the total substitution degree (A + B) of hydroxyl groups A and B is 2.0 to 3.0, preferably 2.2 to 2.9, as shown in the above formula (VIII). And particularly preferably 2.40 to 2.85. Further, the substitution degree of B is preferably larger than 0, more preferably 0.6 or more, as shown in the above formula (IX).
When A + B is less than 2.0, the hydrophilicity becomes strong and it is easy to be affected by environmental humidity.
Further, 28% or more of B is preferably a 6-position hydroxyl group substituent, more preferably 30% or more is a 6-position hydroxyl group substituent, more preferably 31% or more, and particularly preferably 32% or more. A substituent at the 6-position hydroxyl group is preferred.
Furthermore, the total substitution degree of A and B at the 6-position of cellulose acylate is preferably 0.75 or more, more preferably 0.80 or more, and particularly preferably 0.85 or more. With these cellulose acylate films, a solution for preparing a film having preferable solubility and filterability can be produced, and a good solution can be produced even in a non-chlorine organic solvent. Furthermore, it becomes possible to produce a solution having a low viscosity and good filterability.
また、セルロースアシレートフィルムが偏光板の液晶セル側に配置される保護膜である場合、セルロースを構成するグルコース単位の２位の水酸基のアシル基による置換度をＤＳ２、３位の水酸基のアシル基による置換度をＤＳ３、６位の水酸基のアシル基による置換度をＤＳ６としたときに、下記式（Ｘ）および（ＸI）を満たすことが好ましい。
式（Ｘ） ： ２．０≦ＤＳ２＋ＤＳ３＋ＤＳ６≦３．０
式（ＸI） ： ＤＳ６／（ＤＳ２＋ＤＳ３＋ＤＳ６）≧０．３１５
上記式（Ｘ）および（ＸI）を満たすことにより、光学性能を好ましい範囲で調整することが容易となり、好ましい。
Further, when the cellulose acylate film is a protective film disposed on the liquid crystal cell side of the polarizing plate, the substitution degree of the hydroxyl group at the 2-position of the glucose unit constituting the cellulose by the acyl group is DS2, and the acyl group of the hydroxyl group at the 3-position It is preferable that the following formulas (X) and (XI) are satisfied, where DS is the substitution degree by DS3 and DS6 is the substitution degree by the acyl group of the hydroxyl group at the 6-position.
Formula (X): 2.0 ≦ DS2 + DS3 + DS6 ≦ 3.0
Formula (XI): DS6 / (DS2 + DS3 + DS6) ≧ 0.315
By satisfying the above formulas (X) and (XI), it is easy to adjust the optical performance within a preferable range, which is preferable.
前記炭素原子数３以上のアシル基としては、脂肪族基でも芳香族炭化水素基でもよく特に限定されない。それらは、例えばセルロースのアルキルカルボニルエステル、アルケニルカルボニルエステルあるいは芳香族カルボニルエステル、芳香族アルキルカルボニルエステルなどであり、それぞれさらに置換された基を有していてもよい。好ましい炭素原子数３以上のアシル基としては、プロピオニル、ブタノイル、ケプタノイル、ヘキサノイル、オクタノイル、デカノイル、ドデカノイル、トリデカノイル、テトラデカノイル、ヘキサデカノイル、オクタデカノイル、ｉｓｏ−ブタノイル、ｔ−ブタノイル、シクロヘキサンカルボニル、オレオイル、ベンゾイル、ナフチルカルボニル、シンナモイル基などを挙げることが出来る。これらの中でも、好ましくはプロピオニル、ブタノイル、ドデカノイル、オクタデカノイル、ｔ−ブタノイル、オレオイル、ベンゾイル、ナフチルカルボニル、シンナモイル基などである。特に好ましくはプロピオニル、ブタノイル基である。また、プロピオニル基の場合には置換度Ｂは１．３以上であるのが好ましい。 The acyl group having 3 or more carbon atoms may be an aliphatic group or an aromatic hydrocarbon group, and is not particularly limited. These are, for example, cellulose alkylcarbonyl esters, alkenylcarbonyl esters, aromatic carbonyl esters, aromatic alkylcarbonyl esters, and the like, each of which may further have a substituted group. Preferred acyl groups having 3 or more carbon atoms include propionyl, butanoyl, keptanoyl, hexanoyl, octanoyl, decanoyl, dodecanoyl, tridecanoyl, tetradecanoyl, hexadecanoyl, octadecanoyl, iso-butanoyl, t-butanoyl, cyclohexanecarbonyl Oleoyl, benzoyl, naphthylcarbonyl, cinnamoyl group and the like. Among these, propionyl, butanoyl, dodecanoyl, octadecanoyl, t-butanoyl, oleoyl, benzoyl, naphthylcarbonyl, cinnamoyl group and the like are preferable. Particularly preferred are propionyl and butanoyl groups. In the case of a propionyl group, the substitution degree B is preferably 1.3 or more.
前記混合脂肪酸セルロースアシレートとしては、具体的には、セルロースアセテートプロピオネート、セルロースアセテートブチレートが挙げられる。 Specific examples of the mixed fatty acid cellulose acylate include cellulose acetate propionate and cellulose acetate butyrate.
（セルロースアシレートの合成方法）
セルロースアシレートの合成方法の基本的な原理は、右田他、木材化学１８０〜１９０頁（共立出版、１９６８年）に記載されている。代表的な合成方法は、カルボン酸無水物−酢酸−硫酸触媒による液相酢化法である。
前記セルロースアシレートを得るには、具体的には、綿花リンタや木材パルプ等のセルロース原料を適当量の酢酸で前処理した後、予め冷却したカルボン酸化混液に投入してエステル化し、完全セルロースアシレート（２位、３位および６位のアシル置換度の合計が、ほぼ３．００）を合成する。上記カルボン酸化混液は、一般に溶媒としての酢酸、エステル化剤としての無水カルボン酸および触媒としての硫酸を含む。無水カルボン酸は、これと反応するセルロースおよび系内に存在する水分の合計よりも、化学量論的に過剰量で使用することが普通である。エステル化反応終了後に、系内に残存している過剰の無水カルボン酸の加水分解およびエステル化触媒の一部の中和のために、中和剤（例えば、カルシウム、マグネシウム、鉄、アルミニウムまたは亜鉛の炭酸塩、酢酸塩または酸化物）の水溶液を添加する。次に、得られた完全セルロースアシレートを少量の酢化反応触媒（一般には、残存する硫酸）の存在下で、５０〜９０℃に保つことによりケン化熟成し、所望のアシル置換度および重合度を有するセルロースアシレートまで変化させる。所望のセルロースアシレートが得られた時点で、系内に残存している触媒を前記のような中和剤を用いて完全に中和するか、あるいは中和することなく水または希硫酸中にセルロースアシレート溶液を投入（あるいは、セルロースアシレート溶液中に、水または希硫酸を投入）してセルロースアシレートを分離し、洗浄および安定化処理を行う等して、前記の特定のセルロースアシレートを得ることができる。
(Method for synthesizing cellulose acylate)
The basic principle of the cellulose acylate synthesis method is described in Mita et al., Wood chemistry, 180-190 (Kyoritsu Shuppan, 1968). A typical synthesis method is a liquid phase acetylation method using a carboxylic acid anhydride-acetic acid-sulfuric acid catalyst.
In order to obtain the cellulose acylate, specifically, a cellulose raw material such as cotton linter or wood pulp is pretreated with an appropriate amount of acetic acid, and then esterified by introducing it into a pre-cooled carboxylated mixed solution. Synthesize the rate (total of acyl substitutions at the 2nd, 3rd and 6th positions is approximately 3.00). The carboxylated mixed solution generally contains acetic acid as a solvent, carboxylic anhydride as an esterifying agent, and sulfuric acid as a catalyst. The carboxylic anhydride is usually used in a stoichiometric excess over the sum of the cellulose that reacts with it and the water present in the system. After completion of the esterification reaction, a neutralizing agent (for example, calcium, magnesium, iron, aluminum or zinc) is used for hydrolysis of excess carboxylic anhydride remaining in the system and neutralization of a part of the esterification catalyst. Of carbonate, acetate or oxide). Next, the obtained complete cellulose acylate is saponified and aged by maintaining it at 50 to 90 ° C. in the presence of a small amount of an acetylation reaction catalyst (generally, remaining sulfuric acid) to obtain the desired degree of acyl substitution and polymerization. The cellulose acylate having a degree is changed. When the desired cellulose acylate is obtained, the catalyst remaining in the system is completely neutralized with the neutralizing agent as described above, or in water or dilute sulfuric acid without neutralization. The cellulose acylate solution is added (or water or dilute sulfuric acid is added to the cellulose acylate solution), the cellulose acylate is separated, washed and stabilized, and the like. Can be obtained.
前記セルロースアシレートフィルムは、フィルムを構成するポリマー成分が実質的に上記の特定のセルロースアシレートからなることが好ましい。『実質的に』とは、ポリマー成分の５５質量％以上（好ましくは７０質量％以上、さらに好ましくは８０質量％以上）を意味する。
前記セルロースアシレートは、粒子状で使用することが好ましい。使用する粒子の９０質量％以上は、０．５〜５ｍｍの粒子径を有することが好ましい。また、使用する粒子の５０質量％以上が１〜４ｍｍの粒子径を有することが好ましい。セルロースアシレート粒子は、なるべく球形に近い形状を有することが好ましい。
本発明で好ましく用いられるセルロースアシレートの重合度は、粘度平均重合度で、好ましくは２００〜７００、より好ましくは２５０〜５５０、更に好ましくは２５０〜４００であり、特に好ましくは２５０〜３５０である。平均重合度は、宇田らの極限粘度法（宇田和夫、斉藤秀夫、繊維学会誌、第１８巻第１号、１０５〜１２０頁、１９６２年）により測定できる。更に特開平９−９５５３８号公報に詳細に記載されている。
In the cellulose acylate film, it is preferable that the polymer component constituting the film is substantially composed of the specific cellulose acylate. “Substantially” means 55% by mass or more (preferably 70% by mass or more, more preferably 80% by mass or more) of the polymer component.
The cellulose acylate is preferably used in the form of particles. 90% by mass or more of the particles to be used preferably have a particle diameter of 0.5 to 5 mm. Moreover, it is preferable that 50 mass% or more of the particle | grains to be used have a particle diameter of 1-4 mm. The cellulose acylate particles preferably have a shape as close to a sphere as possible.
The degree of polymerization of cellulose acylate preferably used in the present invention is a viscosity average degree of polymerization, preferably 200 to 700, more preferably 250 to 550, still more preferably 250 to 400, and particularly preferably 250 to 350. . The average degree of polymerization can be measured by Uda et al.'S intrinsic viscosity method (Kazuo Uda, Hideo Saito, Journal of Textile Society, Vol. 18, No. 1, pages 105-120, 1962). Further details are described in JP-A-9-95538.
低分子成分が除去されると、平均分子量（重合度）が高くなるが、粘度は通常のセルロースアシレートよりも低くなるため、前記セルロースアシレートとしては低分子成分を除去したものが有用である。低分子成分の少ないセルロースアシレートは、通常の方法で合成したセルロースアシレートから低分子成分を除去することにより得ることができる。低分子成分の除去は、セルロースアシレートを適当な有機溶媒で洗浄することにより実施できる。なお、低分子成分の少ないセルロースアシレートを製造する場合、酢化反応における硫酸触媒量を、セルロースアシレート１００質量部に対して０．５〜２５質量部に調整することが好ましい。硫酸触媒の量を上記範囲にすると、分子量分布の点でも好ましい（分子量分布の均一な）セルロースアシレートを合成することができる。セルロースアシレートの製造時に使用される際には、その含水率は２質量％以下であることが好ましく、さらに好ましくは１質量％以下であり、特には０．７質量％以下である。一般に、セルロースアシレートは、水を含有しており含水率２．５〜５質量％が知られている。本発明でこのセルロースアシレートの含水率にするためには、乾燥することが必要であり、その方法は目的とする含水率になれば特に限定されない。
前記セルロースアシレートの原料綿や合成方法は、発明協会公開技報公技番号２００１−１７４５号（２００１年３月１５日発行、発明協会）ｐ．７−１２に詳細に記載されている原料綿や合成方法を採用できる。
When the low molecular component is removed, the average molecular weight (polymerization degree) is increased, but the viscosity is lower than that of ordinary cellulose acylate. Therefore, the cellulose acylate from which the low molecular component is removed is useful. . Cellulose acylate having a small amount of low molecular components can be obtained by removing low molecular components from cellulose acylate synthesized by a usual method. The removal of the low molecular component can be carried out by washing the cellulose acylate with an appropriate organic solvent. In addition, when manufacturing a cellulose acylate with few low molecular components, it is preferable to adjust the sulfuric acid catalyst amount in an acetylation reaction to 0.5-25 mass parts with respect to 100 mass parts of cellulose acylates. When the amount of the sulfuric acid catalyst is in the above range, cellulose acylate that is preferable in terms of molecular weight distribution (uniform molecular weight distribution) can be synthesized. When used in the production of cellulose acylate, the water content is preferably 2% by mass or less, more preferably 1% by mass or less, and particularly 0.7% by mass or less. In general, cellulose acylate contains water and is known to have a water content of 2.5 to 5% by mass. In order to obtain the water content of the cellulose acylate in the present invention, it is necessary to dry it, and the method is not particularly limited as long as the desired water content is obtained.
The cellulose acylate raw material cotton and the synthesis method thereof are disclosed in JIII Journal of Technical Disclosure No. 2001-1745 (issued March 15, 2001, Invention Association) p. Raw material cotton and synthesis methods described in detail in 7-12 can be employed.
本発明に関するセルロースアシレートフィルムは、前記の特定のセルロースアシレートと必要に応じて添加剤とを有機溶媒に溶解させた溶液を用いてフィルム化することにより得ることができる。 The cellulose acylate film according to the present invention can be obtained by forming a film using a solution obtained by dissolving the specific cellulose acylate and, if necessary, an additive in an organic solvent.
（添加剤）
本発明において前記セルロースアシレート溶液に用いることができる添加剤としては、例えば、可塑剤、紫外線吸収剤、劣化防止剤、レターデーション（光学異方性）発現剤、レターデーション（光学異方性）減少剤、微粒子、染料、剥離促進剤、赤外吸収剤などを挙げることができる。本発明においては、レターデーション発現剤を用いるのが好ましい。また、可塑剤、紫外線吸収剤、染料及び剥離促進剤の少なくとも１種以上を用いるのが好ましい。
それらは固体でもよく油状物でもよい。すなわち、その融点や沸点において特に限定されるものではない。例えば２０℃以下と２０℃以上の紫外線吸収剤を混合して用いたり、同様に可塑剤を混合して用いることができ、例えば特開平２００１−１５１９０１号公報などに記載されている。
紫外線吸収剤としては、目的に応じ任意の種類のものを選択することができ、サリチル酸エステル系、ベンゾフェノン系、ベンゾトリアゾール系、ベンゾエート系、シアノアクリレート系、ニッケル錯塩系等の吸収剤を用いることができ、好ましくはベンゾフェノン系、ベンゾトリアゾール系、サリチル酸エステル系である。ベンゾフェノン系紫外線吸収剤の例として、２，４−ジヒドロキシベンゾフェノン、２−ヒドロキシ−４−アセトキシベンゾフェノン、２−ヒドロキシ−４−メトキシベンゾフェノン、２，２’−ジ−ヒドロキシ−４−メトキシベンゾフェノン、２，２’−ジ−ヒドロキシ−４，４’−メトキシベンゾフェノン、２−ヒドロキシ−４−ｎ−オクトキシベンゾフェノン、２−ヒドロキシ−４−ドデシルオキシベンゾフェノン、２−ヒドロキシ−４−（２−ヒドロキシ−３−メタクリロキシ）プロポキシベンゾフェノン等を挙げることができる。ベンゾトリアゾール系紫外線吸収剤としては、２（２’−ヒドロキシ−３’−ｔｅｒｔ−ブチル−５’−メチルフェニル）−５−クロルベンゾトリアゾール、２（２’−ヒドロキシ−５’−ｔｅｒｔ−ブチルフェニル）ベンゾトリアゾール、２（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−アミルフェニル）ベンゾトリアゾール、２（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェニル）−５−クロルベンゾトリアゾール、２（２’−ヒドロキシ−５’−ｔｅｒｔ−オクチルフェニル）ベンゾトリアゾール等を挙げることができる。サリチル酸エステル系としては、フェニルサリシレート、ｐ−オクチルフェニルサリシレート、ｐ−ｔｅｒｔ−ブチルフェニルサリシレート等を挙げることができる。これら例示した紫外線吸収剤の中でも、特に２−ヒドロキシ−４−メトキシベンゾフェノン、２，２’−ジ−ヒドロキシ−４，４’−メトキシベンゾフェノン、２（２’−ヒドロキシ−３’−ｔｅｒｔ−ブチル−５’−メチルフェニル）−５−クロルベンゾトリアゾール、２（２’−ヒドロキシ−５’−ｔｅｒｔ−ブチルフェニル）ベンゾトリアゾール、２（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−アミルフェニル）ベンゾトリアゾール、２（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェニル）−５−クロルベンゾトリアゾールが特に好ましい。
(Additive)
Examples of the additive that can be used in the cellulose acylate solution in the present invention include a plasticizer, an ultraviolet absorber, a deterioration preventing agent, a retardation (optical anisotropy) developing agent, and a retardation (optical anisotropy). Examples thereof include a reducing agent, fine particles, a dye, a peeling accelerator, and an infrared absorber. In the present invention, it is preferable to use a retardation developer. Moreover, it is preferable to use at least one of a plasticizer, an ultraviolet absorber, a dye and a peeling accelerator.
They may be solid or oily. That is, the melting point and boiling point are not particularly limited. For example, ultraviolet absorbers of 20 ° C. or lower and 20 ° C. or higher can be mixed and used, and plasticizers can also be mixed and used, for example, as described in JP-A No. 2001-151901.
As the ultraviolet absorber, any type can be selected according to the purpose, and a salicylic acid ester-based, benzophenone-based, benzotriazole-based, benzoate-based, cyanoacrylate-based, nickel complex-based absorber or the like is used. Preferred are benzophenone series, benzotriazole series, and salicylic acid ester series. Examples of benzophenone ultraviolet absorbers include 2,4-dihydroxybenzophenone, 2-hydroxy-4-acetoxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2,2′-di-hydroxy-4-methoxybenzophenone, 2, 2′-di-hydroxy-4,4′-methoxybenzophenone, 2-hydroxy-4-n-octoxybenzophenone, 2-hydroxy-4-dodecyloxybenzophenone, 2-hydroxy-4- (2-hydroxy-3- And methacryloxy) propoxybenzophenone. As a benzotriazole ultraviolet absorber, 2 (2′-hydroxy-3′-tert-butyl-5′-methylphenyl) -5-chlorobenzotriazole, 2 (2′-hydroxy-5′-tert-butylphenyl) ) Benzotriazole, 2 (2′-hydroxy-3 ′, 5′-di-tert-amylphenyl) benzotriazole, 2 (2′-hydroxy-3 ′, 5′-di-tert-butylphenyl) -5 Examples include chlorobenzotriazole, 2 (2′-hydroxy-5′-tert-octylphenyl) benzotriazole, and the like. Examples of salicylic acid esters include phenyl salicylate, p-octylphenyl salicylate, and p-tert-butylphenyl salicylate. Among these exemplified ultraviolet absorbers, in particular, 2-hydroxy-4-methoxybenzophenone, 2,2′-di-hydroxy-4,4′-methoxybenzophenone, 2 (2′-hydroxy-3′-tert-butyl- 5'-methylphenyl) -5-chlorobenzotriazole, 2 (2'-hydroxy-5'-tert-butylphenyl) benzotriazole, 2 (2'-hydroxy-3 ', 5'-di-tert-amylphenyl) ) Benzotriazole, 2 (2′-hydroxy-3 ′, 5′-di-tert-butylphenyl) -5-chlorobenzotriazole is particularly preferred.
紫外線吸収剤は、吸収波長の異なる複数の吸収剤を複合して用いることが、広い波長範囲で高い遮断効果を得ることができるので好ましい。液晶用紫外線吸収剤は、液晶の劣化防止の観点から、波長３７０ｎｍ以下の紫外線の吸収能に優れ、かつ、液晶表示性の観点から、波長４００ｎｍ以上の可視光の吸収が少ないものが好ましい。特に好ましい紫外線吸収剤は、先に上げたベンゾトリアゾール系化合物やベンゾフェノン系化合物、サリチル酸エステル系化合物である。中でも、ベンゾトリアゾール系化合物は、セルロースエステルに対する不要な着色が少ないことから、好ましい。 As the ultraviolet absorber, it is preferable to use a combination of a plurality of absorbers having different absorption wavelengths because a high blocking effect can be obtained in a wide wavelength range. From the viewpoint of preventing deterioration of the liquid crystal, the ultraviolet absorbent for liquid crystal is preferably excellent in the ability to absorb ultraviolet rays having a wavelength of 370 nm or less, and from the viewpoint of liquid crystal display properties, the absorption of visible light having a wavelength of 400 nm or more is small. Particularly preferred ultraviolet absorbers are the benzotriazole compounds, benzophenone compounds, and salicylic acid ester compounds mentioned above. Among these, a benzotriazole-based compound is preferable because unnecessary coloring with respect to the cellulose ester is small.
また、紫外線吸収剤については、特開昭６０−２３５８５２号、特開平３−１９９２０１号、同５−１９０７０７３号、同５−１９４７８９号、同５−２７１４７１号、同６−１０７８５４号、同６−１１８２３３号、同６−１４８４３０号、同７−１１０５６号、同７−１１０５５号、同７−１１０５６号、同８−２９６１９号、同８−２３９５０９号、特開２０００−２０４１７３号の各公報に記載の化合物も用いることができる。 As for the UV absorber, JP-A-60-235852, JP-A-3-199201, JP-A-51907073, JP-A-5-194789, JP-A-5-271471, JP-A-6-107854, JP-A-6-107854. 118233, 6-148430, 7-11056, 7-11055, 7-11056, 8-29619, 8-239509, JP-A-2000-204173 These compounds can also be used.
紫外線吸収剤の添加量は、セルロースアシレートに対し０．００１〜５質量％が好ましく、０．０１〜１質量％がより好ましい。添加量が０．００１質量％未満では添加効果を十分に発揮することができず、添加量が５質量％を超えると、フィルム表面へ紫外線吸収剤がブリードアウトする場合がある。 0.001-5 mass% is preferable with respect to a cellulose acylate, and, as for the addition amount of a ultraviolet absorber, 0.01-1 mass% is more preferable. If the addition amount is less than 0.001% by mass, the effect of addition cannot be sufficiently exhibited. If the addition amount exceeds 5% by mass, the ultraviolet absorber may bleed out to the film surface.
また、紫外線吸収剤はセルロースアシレート溶解時に同時に添加しても良いし、溶解後のドープに添加しても良い。特にスタティックミキサ等を用い、流延直前にドープに紫外線吸収剤溶液を添加する形態が、分光吸収特性を容易に調整することができ、好ましい。 Further, the ultraviolet absorber may be added simultaneously with the dissolution of cellulose acylate, or may be added to the dope after dissolution. In particular, a mode in which an ultraviolet absorbent solution is added to the dope immediately before casting using a static mixer or the like is preferable because the spectral absorption characteristics can be easily adjusted.
前記劣化防止剤は、セルローストリアセテート等が劣化、分解するのを防止することができる。劣化防止剤としては、ブチルアミン、ヒンダードアミン化合物（特開平８−３２５５３７号公報）、グアニジン化合物（特開平５−２７１４７１号公報）、ベンゾトリアゾール系ＵＶ吸収剤（特開平６−２３５８１９号公報）、ベンゾフェノン系ＵＶ吸収剤（特開平６−１１８２３３号公報）などの化合物がある。 The deterioration inhibitor can prevent cellulose triacetate and the like from deteriorating and decomposing. Examples of the deterioration preventing agent include butylamine, hindered amine compounds (JP-A-8-325537), guanidine compounds (JP-A-5-271471), benzotriazole-based UV absorbers (JP-A-6-235819), and benzophenone-based compounds. There are compounds such as UV absorbers (JP-A-6-118233).
可塑剤としては、リン酸エステル、カルボン酸エステルであることが好ましい。また、前記可塑剤が、トリフェニルフォスフェート（ＴＰＰ）、トリクレジルホスフェート（ＴＣＰ）、クレジルジフェニルホスフェート、オクチルジフェニルホスフェート、ビフェニルジフェニルホスフェート（ＢＤＰ）、トリオクチルホスフェート、トリブチルホスフェート、ジメチルフタレート（ＤＭＰ）、ジエチルフタレート（ＤＥＰ）、ジブチルフタレート（ＤＢＰ）、ジオクチルフタレート（ＤＯＰ）、ジフェニルフタレート（ＤＰＰ）、ジエチルヘキシルフタレート（ＤＥＨＰ）、Ｏ−アセチルクエン酸トリエチル（ＯＡＣＴＥ）、Ｏ−アセチルクエン酸トリブチル（ＯＡＣＴＢ）、クエン酸アセチルトリエチル、クエン酸アセチルトリブチル、オレイン酸ブチル、リシノール酸メチルアセチル、セバシン酸ジブチル、トリアセチン、トリブチリン、ブチルフタリルブチルグリコレート、エチルフタリルエチルグリコレート、メチルフタリルエチルグリコレート、ブチルフタリルブチルグリコレートから選ばれたものであることがより好ましい。さらに、前記可塑剤が、（ジ）ペンタエリスリトールエステル類、グリセロールエステル類、ジグリセロールエステル類であることが好ましい。
剥離促進剤としてはクエン酸のエチルエステル類が例として挙げられる。さらに赤外吸収剤としては例えば特開平２００１−１９４５２２号公報に記載されている。
The plasticizer is preferably a phosphate ester or a carboxylic acid ester. The plasticizer may be triphenyl phosphate (TPP), tricresyl phosphate (TCP), cresyl diphenyl phosphate, octyl diphenyl phosphate, biphenyl diphenyl phosphate (BDP), trioctyl phosphate, tributyl phosphate, dimethyl phthalate (DMP) ), Diethyl phthalate (DEP), dibutyl phthalate (DBP), dioctyl phthalate (DOP), diphenyl phthalate (DPP), diethyl hexyl phthalate (DEHP), triethyl O-acetylcitrate (OACTE), tributyl O-acetylcitrate ( OACTB), acetyl triethyl citrate, acetyl tributyl citrate, butyl oleate, methyl acetyl ricinoleate, dibutyl sebacate, tria Chin, tributyrin, butyl phthalyl butyl glycolate, ethyl phthalyl ethyl glycolate, methyl phthalyl ethyl glycolate, and more preferably one selected from butyl phthalyl butyl glycolate. Furthermore, the plasticizer is preferably (di) pentaerythritol esters, glycerol esters, diglycerol esters.
Examples of the peeling accelerator include citric acid ethyl esters. Further, infrared absorbers are described in, for example, JP-A-2001-194522.
また、本発明では、色相調整のための染料を添加してもよい。染料の含有量は、セルロースアシレートに対する質量割合で１０〜１０００ｐｐｍが好ましく、５０〜５００ｐｐｍが更に好ましい。この様に染料を含有させることにより、セルロースアシレートフイルムのライトパイピングが減少でき、黄色味を改良することができる。これらの化合物は、セルロースアシレート溶液の調製の際に、セルロースアシレートや溶媒と共に添加してもよいし、溶液調製中や調製後に添加してもよい。又インライン添加する紫外線吸収剤液に添加しても良い。 In the present invention, a dye for adjusting the hue may be added. The content of the dye is preferably 10 to 1000 ppm, more preferably 50 to 500 ppm in terms of a mass ratio with respect to cellulose acylate. By containing the dye in this way, light piping of the cellulose acylate film can be reduced and the yellowness can be improved. These compounds may be added together with cellulose acylate and a solvent during the preparation of the cellulose acylate solution, or may be added during or after the solution preparation. Moreover, you may add to the ultraviolet absorber liquid added in-line.
これらの添加剤を添加する時期はドープ作製工程において何れで添加しても良いが、ドープ調製工程の最後の調製工程に添加剤を添加し調製する工程を加えて行ってもよい。更にまた、各素材の添加量は機能が発現する限りにおいて特に限定されない。また、セルロースアシレートフィルムが多層である場合、各層の添加物の種類や添加量が異なってもよい。例えば特開２００１−１５１９０２号公報などに記載されているが、これらは従来から知られている技術である。これら添加剤の種類や添加量の選択によって、セルロースアシレートフィルムの動的粘弾性測定機（バイブロン：ＤＶＡ−２２５（アイティー計測制御（株）製）で測定するガラス転移点Ｔｇを７０〜１５０℃に、より好ましくは、ガラス転移点Ｔｇが８０〜１３５℃にすることが好ましい。すなわち、本発明に関するセルロースアシレートフィルムは、偏光板加工や液晶表示装置組立ての工程適性の点で、ガラス転移点Ｔｇを上記の範囲とすることが好ましい。
さらに添加剤については、発明協会公開技報公技番号２００１−１７４５号（２００１年３月１５日発行、発明協会）ｐ．１６以降に詳細に記載されているものを適宜用いることができる。
These additives may be added at any time in the dope preparation step, but may be added to the final preparation step of the dope preparation step by adding a preparation step. Furthermore, the amount of each material added is not particularly limited as long as the function is manifested. Moreover, when a cellulose acylate film is a multilayer, the kind and addition amount of the additive of each layer may differ. For example, it is described in Japanese Patent Application Laid-Open No. 2001-151902, but these are conventionally known techniques. The glass transition point Tg measured by a dynamic viscoelasticity measuring device for cellulose acylate film (Vibron: DVA-225 (manufactured by IT Measurement Control Co., Ltd.)) is adjusted to 70 to 150 depending on the selection of the type and amount of these additives. More preferably, the glass transition point Tg is 80 to 135 ° C. That is, the cellulose acylate film according to the present invention has a glass transition point from the viewpoint of process suitability for polarizing plate processing and liquid crystal display device assembly. The point Tg is preferably within the above range.
Furthermore, regarding the additive, the Japan Institute of Invention and Innovation Technical Bulletin No. 2001-1745 (issued on March 15, 2001, Japan Institute of Invention) p. Those described in detail after 16 can be used as appropriate.
（レターデーション発現剤）
本発明では光学異方性を大きく発現させ、好ましいレターデーション値を実現するため、レターデーション発現剤を用いるのが好ましい。
本発明において用いることができるレターデーション発現剤としては、棒状又は円盤状化合物からなるものを挙げることができる。
上記棒状又は円盤状化合物としては、少なくとも二つの芳香族環を有する化合物を用いることができる。
棒状化合物からなるレターデーション発現剤の添加量は、セルロースアシレートを含むポリマー成分１００質量部に対して０．１乃至３０質量部であることが好ましく、０．５乃至２０質量部であることがさらに好ましい。
円盤状のレターデーション発現剤は、前記セルロースアシレートを含むポリマー成分１００質量部に対して、０．０５乃至３０質量部の範囲で使用することが好ましく、０．１乃至２０質量部の範囲で使用することがより好ましく、０．２乃至１５質量部の範囲で使用することがさらに好ましく、０．５乃至１０質量部の範囲で使用することが最も好ましい。
円盤状化合物はＲｔｈレターデーション発現性において棒状化合物よりも優れているため、特に大きなＲｔｈレターデーションを必要とする場合には好ましく使用される。
二種類以上のレターデーション発現剤を併用してもよい。
棒状または円盤状化合物からなる前記レターデーション発現剤は、２５０乃至４００ｎｍの波長領域に最大吸収を有することが好ましく、可視領域に実質的に吸収を有していないことが好ましい。
(Retardation expression agent)
In the present invention, it is preferable to use a retardation enhancer in order to greatly develop optical anisotropy and realize a preferable retardation value.
Examples of the retardation enhancer that can be used in the present invention include those composed of rod-shaped or discotic compounds.
As the rod-like or discotic compound, a compound having at least two aromatic rings can be used.
The addition amount of the retardation developer composed of the rod-like compound is preferably 0.1 to 30 parts by mass, and preferably 0.5 to 20 parts by mass with respect to 100 parts by mass of the polymer component containing cellulose acylate. Further preferred.
The disc-shaped retardation developing agent is preferably used in a range of 0.05 to 30 parts by mass, and in a range of 0.1 to 20 parts by mass with respect to 100 parts by mass of the polymer component containing cellulose acylate. More preferably, it is used in the range of 0.2 to 15 parts by mass, and most preferably in the range of 0.5 to 10 parts by mass.
Since the discotic compound is superior to the rod-shaped compound in Rth retardation expression, it is preferably used when a particularly large Rth retardation is required.
Two or more retardation developing agents may be used in combination.
The retardation developer composed of a rod-like or discotic compound preferably has maximum absorption in the wavelength region of 250 to 400 nm, and preferably has substantially no absorption in the visible region.
円盤状化合物について説明する。円盤状化合物としては少なくとも二つの芳香族環を有する化合物を用いることができる。
本明細書において、「芳香族環」は、芳香族炭化水素環に加えて、芳香族性ヘテロ環を含む。
芳香族炭化水素環は、６員環（すなわち、ベンゼン環）であることが特に好ましい。
芳香族性ヘテロ環は一般に、不飽和ヘテロ環である。芳香族性ヘテロ環は、５員環、６員環または７員環であることが好ましく、５員環または６員環であることがさらに好ましい。芳香族性ヘテロ環は一般に、最多の二重結合を有する。ヘテロ原子としては、窒素原子、酸素原子および硫黄原子が好ましく、窒素原子が特に好ましい。芳香族性ヘテロ環の例には、フラン環、チオフェン環、ピロール環、オキサゾール環、イソオキサゾール環、チアゾール環、イソチアゾール環、イミダゾール環、ピラゾール環、フラザン環、トリアゾール環、ピラン環、ピリジン環、ピリダジン環、ピリミジン環、ピラジン環および１，３，５−トリアジン環が含まれる。
芳香族環としては、ベンゼン環、フラン環、チオフェン環、ピロール環、オキサゾール環、チアゾール環、イミダゾール環、トリアゾール環、ピリジン環、ピリミジン環、ピラジン環および１，３，５−トリアジン環が好ましく、特に１，３，５−トリアジン環が好ましく用いられる。具体的には例えば特開２００１−１６６１４４号公報に開示の化合物が円盤状化合物として好ましく用いられる。
The discotic compound will be described. As the discotic compound, a compound having at least two aromatic rings can be used.
In the present specification, the “aromatic ring” includes an aromatic hetero ring in addition to an aromatic hydrocarbon ring.
The aromatic hydrocarbon ring is particularly preferably a 6-membered ring (that is, a benzene ring).
The aromatic heterocycle is generally an unsaturated heterocycle. The aromatic heterocycle is preferably a 5-membered ring, 6-membered ring or 7-membered ring, more preferably a 5-membered ring or 6-membered ring. Aromatic heterocycles generally have the most double bonds. As the hetero atom, a nitrogen atom, an oxygen atom and a sulfur atom are preferable, and a nitrogen atom is particularly preferable. Examples of aromatic heterocycles include furan ring, thiophene ring, pyrrole ring, oxazole ring, isoxazole ring, thiazole ring, isothiazole ring, imidazole ring, pyrazole ring, furazane ring, triazole ring, pyran ring, pyridine ring , Pyridazine ring, pyrimidine ring, pyrazine ring and 1,3,5-triazine ring.
As the aromatic ring, benzene ring, furan ring, thiophene ring, pyrrole ring, oxazole ring, thiazole ring, imidazole ring, triazole ring, pyridine ring, pyrimidine ring, pyrazine ring and 1,3,5-triazine ring are preferable, In particular, a 1,3,5-triazine ring is preferably used. Specifically, for example, a compound disclosed in JP 2001-166144 A is preferably used as the discotic compound.
前記円盤状化合物が有する芳香族環の数は、２乃至２０であることが好ましく、２乃至１２であることがより好ましく、２乃至８であることがさらに好ましく、２乃至６であることが最も好ましい。
二つの芳香族環の結合関係は、（ａ）縮合環を形成する場合、（ｂ）単結合で直結する場合および（ｃ）連結基を介して結合する場合に分類できる（芳香族環のため、スピロ結合は形成できない）。結合関係は、（ａ）〜（ｃ）のいずれでもよい。
The number of aromatic rings contained in the discotic compound is preferably 2 to 20, more preferably 2 to 12, still more preferably 2 to 8, and most preferably 2 to 6. preferable.
The bond relationship between two aromatic rings can be classified into (a) a condensed ring, (b) a direct bond with a single bond, and (c) a bond through a linking group (for aromatic rings). , Spiro bonds cannot be formed). The connection relationship may be any of (a) to (c).
（ａ）の縮合環（二つ以上の芳香族環の縮合環）の例には、インデン環、ナフタレン環、アズレン環、フルオレン環、フェナントレン環、アントラセン環、アセナフチレン環、ビフェニレン環、ナフタセン環、ピレン環、インドール環、イソインドール環、ベンゾフラン環、ベンゾチオフェン環、インドリジン環、ベンゾオキサゾール環、ベンゾチアゾール環、ベンゾイミダゾール環、ベンゾトリアゾール環、プリン環、インダゾール環、クロメン環、キノリン環、イソキノリン環、キノリジン環、キナゾリン環、シンノリン環、キノキサリン環、フタラジン環、プテリジン環、カルバゾール環、アクリジン環、フェナントリジン環、キサンテン環、フェナジン環、フェノチアジン環、フェノキサチイン環、フェノキサジン環およびチアントレン環が含まれる。ナフタレン環、アズレン環、インドール環、ベンゾオキサゾール環、ベンゾチアゾール環、ベンゾイミダゾール環、ベンゾトリアゾール環およびキノリン環が好ましい。 Examples of the condensed ring (a condensed ring of two or more aromatic rings) include an indene ring, a naphthalene ring, an azulene ring, a fluorene ring, a phenanthrene ring, an anthracene ring, an acenaphthylene ring, a biphenylene ring, a naphthacene ring, Pyrene ring, indole ring, isoindole ring, benzofuran ring, benzothiophene ring, indolizine ring, benzoxazole ring, benzothiazole ring, benzimidazole ring, benzotriazole ring, purine ring, indazole ring, chromene ring, quinoline ring, isoquinoline Ring, quinolidine ring, quinazoline ring, cinnoline ring, quinoxaline ring, phthalazine ring, pteridine ring, carbazole ring, acridine ring, phenanthridine ring, xanthene ring, phenazine ring, phenothiazine ring, phenoxathiin ring, phenoxazine ring and thiant It includes emissions ring. Naphthalene ring, azulene ring, indole ring, benzoxazole ring, benzothiazole ring, benzimidazole ring, benzotriazole ring and quinoline ring are preferred.
（ｂ）の単結合は、二つの芳香族環の炭素原子間の結合であることが好ましい。二以上の単結合で二つの芳香族環を結合して、二つの芳香族環の間に脂肪族環または非芳香族性複素環を形成してもよい。 The single bond (b) is preferably a bond between carbon atoms of two aromatic rings. Two aromatic rings may be bonded with two or more single bonds to form an aliphatic ring or a non-aromatic heterocyclic ring between the two aromatic rings.
（ｃ）の連結基も、二つの芳香族環の炭素原子と結合することが好ましい。連結基は、アルキレン基、アルケニレン基、アルキニレン基、−ＣＯ−、−Ｏ−、−ＮＨ−、−Ｓ−またはそれらの組み合わせであることが好ましい。組み合わせからなる連結基の例を以下に示す。なお、以下の連結基の例の左右の関係は、逆になってもよい。
ｃ１：−ＣＯ−Ｏ−
ｃ２：−ＣＯ−ＮＨ−
ｃ３：−アルキレン−Ｏ−
ｃ４：−ＮＨ−ＣＯ−ＮＨ−
ｃ５：−ＮＨ−ＣＯ−Ｏ−
ｃ６：−Ｏ−ＣＯ−Ｏ−
ｃ７：−Ｏ−アルキレン−Ｏ−
ｃ８：−ＣＯ−アルケニレン−
ｃ９：−ＣＯ−アルケニレン−ＮＨ−
ｃ10：−ＣＯ−アルケニレン−Ｏ−
ｃ11：−アルキレン−ＣＯ−Ｏ−アルキレン−Ｏ−ＣＯ−アルキレン−
ｃ12：−Ｏ−アルキレン−ＣＯ−Ｏ−アルキレン−Ｏ−ＣＯ−アルキレン−Ｏ−
ｃ13：−Ｏ−ＣＯ−アルキレン−ＣＯ−Ｏ−
ｃ14：−ＮＨ−ＣＯ−アルケニレン−
ｃ15：−Ｏ−ＣＯ−アルケニレン−
The linking group in (c) is also preferably bonded to carbon atoms of two aromatic rings. The linking group is preferably an alkylene group, an alkenylene group, an alkynylene group, —CO—, —O—, —NH—, —S—, or a combination thereof. Examples of linking groups composed of combinations are shown below. In addition, the relationship between the left and right in the following examples of the linking group may be reversed.
c1: -CO-O-
c2: —CO—NH—
c3: -alkylene-O-
c4: —NH—CO—NH—
c5: —NH—CO—O—
c6: —O—CO—O—
c7: -O-alkylene-O-
c8: -CO-alkenylene-
c9: -CO-alkenylene-NH-
c10: -CO-alkenylene-O-
c11: -alkylene-CO-O-alkylene-O-CO-alkylene-
c12: -O-alkylene-CO-O-alkylene-O-CO-alkylene-O-
c13: -O-CO-alkylene-CO-O-
c14: -NH-CO-alkenylene-
c15: -O-CO-alkenylene-
芳香族環および連結基は、置換基を有していてもよい。
置換基の例には、ハロゲン原子（Ｆ、Ｃｌ、Ｂｒ、Ｉ）、ヒドロキシル基、カルボキシル基、シアノ基、アミノ基、ニトロ基、スルホ基、カルバモイル基、スルファモイル基、ウレイド基、アルキル基、アルケニル基、アルキニル基、脂肪族アシル基、脂肪族アシルオキシ基、アルコキシ基、アルコキシカルボニル基、アルコキシカルボニルアミノ基、アルキルチオ基、アルキルスルホニル基、脂肪族アミド基、脂肪族スルホンアミド基、脂肪族置換アミノ基、脂肪族置換カルバモイル基、脂肪族置換スルファモイル基、脂肪族置換ウレイド基および非芳香族性複素環基が含まれる。
The aromatic ring and the linking group may have a substituent.
Examples of substituents include halogen atoms (F, Cl, Br, I), hydroxyl groups, carboxyl groups, cyano groups, amino groups, nitro groups, sulfo groups, carbamoyl groups, sulfamoyl groups, ureido groups, alkyl groups, alkenyls. Group, alkynyl group, aliphatic acyl group, aliphatic acyloxy group, alkoxy group, alkoxycarbonyl group, alkoxycarbonylamino group, alkylthio group, alkylsulfonyl group, aliphatic amide group, aliphatic sulfonamido group, aliphatic substituted amino group An aliphatic substituted carbamoyl group, an aliphatic substituted sulfamoyl group, an aliphatic substituted ureido group, and a non-aromatic heterocyclic group.
アルキル基の炭素原子数は、１乃至８であることが好ましい。環状アルキル基よりも鎖状アルキル基の方が好ましく、直鎖状アルキル基が特に好ましい。アルキル基は、さらに置換基（例、ヒドロキシ基、カルボキシ基、アルコキシ基、アルキル置換アミノ基）を有していてもよい。アルキル基の（置換アルキル基を含む）例には、メチル基、エチル基、ｎ−ブチル基、ｎ−ヘキシル基、２−ヒドロキシエチル基、４−カルボキシブチル基、２−メトキシエチル基および２−ジエチルアミノエチル基が含まれる。
アルケニル基の炭素原子数は、２乃至８であることが好ましい。環状アルケニル基よりも鎖状アルケニル基の方が好ましく、直鎖状アルケニル基が特に好ましい。アルケニル基は、さらに置換基を有していてもよい。アルケニル基の例には、ビニル基、アリル基および１−ヘキセニル基が含まれる。
アルキニル基の炭素原子数は、２乃至８であることが好ましい。環状アルキケニル基よりも鎖状アルキニル基の方が好ましく、直鎖状アルキニル基が特に好ましい。アルキニル基は、さらに置換基を有していてもよい。アルキニル基の例には、エチニル基、１−ブチニル基および１−ヘキシニル基が含まれる。
The alkyl group preferably has 1 to 8 carbon atoms. A chain alkyl group is preferable to a cyclic alkyl group, and a linear alkyl group is particularly preferable. The alkyl group may further have a substituent (eg, hydroxy group, carboxy group, alkoxy group, alkyl-substituted amino group). Examples of alkyl groups (including substituted alkyl groups) include methyl, ethyl, n-butyl, n-hexyl, 2-hydroxyethyl, 4-carboxybutyl, 2-methoxyethyl, and 2- A diethylaminoethyl group is included.
The alkenyl group preferably has 2 to 8 carbon atoms. A chain alkenyl group is preferable to a cyclic alkenyl group, and a linear alkenyl group is particularly preferable. The alkenyl group may further have a substituent. Examples of the alkenyl group include a vinyl group, an allyl group, and a 1-hexenyl group.
The alkynyl group preferably has 2 to 8 carbon atoms. A chain alkynyl group is preferable to a cyclic alkynyl group, and a linear alkynyl group is particularly preferable. The alkynyl group may further have a substituent. Examples of the alkynyl group include ethynyl group, 1-butynyl group and 1-hexynyl group.
脂肪族アシル基の炭素原子数は、１乃至１０であることが好ましい。脂肪族アシル基の例には、アセチル基、プロパノイル基およびブタノイル基が含まれる。
脂肪族アシルオキシ基の炭素原子数は、１乃至１０であることが好ましい。脂肪族アシルオキシ基の例には、アセトキシ基が含まれる。
アルコキシ基の炭素原子数は、１乃至８であることが好ましい。アルコキシ基は、さらに置換基（例、アルコキシ基）を有していてもよい。アルコキシ基の（置換アルコキシ基を含む）例には、メトキシ基、エトキシ基、ブトキシ基およびメトキシエトキシ基が含まれる。
アルコキシカルボニル基の炭素原子数は、２乃至１０であることが好ましい。アルコキシカルボニル基の例には、メトキシカルボニル基およびエトキシカルボニル基が含まれる。
アルコキシカルボニルアミノ基の炭素原子数は、２乃至１０であることが好ましい。アルコキシカルボニルアミノ基の例には、メトキシカルボニルアミノ基およびエトキシカルボニルアミノ基が含まれる。
The aliphatic acyl group preferably has 1 to 10 carbon atoms. Examples of the aliphatic acyl group include an acetyl group, a propanoyl group, and a butanoyl group.
The aliphatic acyloxy group preferably has 1 to 10 carbon atoms. Examples of the aliphatic acyloxy group include an acetoxy group.
The number of carbon atoms of the alkoxy group is preferably 1 to 8. The alkoxy group may further have a substituent (eg, alkoxy group). Examples of the alkoxy group (including a substituted alkoxy group) include a methoxy group, an ethoxy group, a butoxy group, and a methoxyethoxy group.
The alkoxycarbonyl group preferably has 2 to 10 carbon atoms. Examples of the alkoxycarbonyl group include a methoxycarbonyl group and an ethoxycarbonyl group.
The number of carbon atoms of the alkoxycarbonylamino group is preferably 2 to 10. Examples of the alkoxycarbonylamino group include a methoxycarbonylamino group and an ethoxycarbonylamino group.
アルキルチオ基の炭素原子数は、１乃至１２であることが好ましい。アルキルチオ基の例には、メチルチオ基、エチルチオ基およびオクチルチオ基が含まれる。
アルキルスルホニル基の炭素原子数は、１乃至８であることが好ましい。アルキルスルホニル基の例には、メタンスルホニル基およびエタンスルホニル基が含まれる。
脂肪族アミド基の炭素原子数は、１乃至１０であることが好ましい。脂肪族アミド基の例には、アセトアミド基が含まれる。
脂肪族スルホンアミド基の炭素原子数は、１乃至８であることが好ましい。脂肪族スルホンアミド基の例には、メタンスルホンアミド基、ブタンスルホンアミド基およびｎ−オクタンスルホンアミド基が含まれる。
脂肪族置換アミノ基の炭素原子数は、１乃至１０であることが好ましい。脂肪族置換アミノ基の例には、ジメチルアミノ基、ジエチルアミノ基および２−カルボキシエチルアミノ基が含まれる。
脂肪族置換カルバモイル基の炭素原子数は、２乃至１０であることが好ましい。脂肪族置換カルバモイル基の例には、メチルカルバモイル基およびジエチルカルバモイル基が含まれる。
脂肪族置換スルファモイル基の炭素原子数は、１乃至８であることが好ましい。脂肪族置換スルファモイル基の例には、メチルスルファモイル基およびジエチルスルファモイル基が含まれる。
脂肪族置換ウレイド基の炭素原子数は、２乃至１０であることが好ましい。脂肪族置換ウレイド基の例には、メチルウレイド基が含まれる。
非芳香族性複素環基の例には、ピペリジノ基およびモルホリノ基が含まれる。
円盤状化合物からなるレターデーション発現剤の分子量は、３００乃至８００であることが好ましい
The alkylthio group preferably has 1 to 12 carbon atoms. Examples of the alkylthio group include a methylthio group, an ethylthio group, and an octylthio group.
The alkylsulfonyl group preferably has 1 to 8 carbon atoms. Examples of the alkylsulfonyl group include a methanesulfonyl group and an ethanesulfonyl group.
The aliphatic amide group preferably has 1 to 10 carbon atoms. Examples of the aliphatic amide group include an acetamide group.
The aliphatic sulfonamide group preferably has 1 to 8 carbon atoms. Examples of the aliphatic sulfonamido group include a methanesulfonamido group, a butanesulfonamido group, and an n-octanesulfonamido group.
The number of carbon atoms of the aliphatic substituted amino group is preferably 1 to 10. Examples of the aliphatic substituted amino group include a dimethylamino group, a diethylamino group, and a 2-carboxyethylamino group.
The aliphatic substituted carbamoyl group preferably has 2 to 10 carbon atoms. Examples of the aliphatic substituted carbamoyl group include a methylcarbamoyl group and a diethylcarbamoyl group.
The aliphatic substituted sulfamoyl group preferably has 1 to 8 carbon atoms. Examples of the aliphatic substituted sulfamoyl group include a methylsulfamoyl group and a diethylsulfamoyl group.
The number of carbon atoms in the aliphatic substituted ureido group is preferably 2 to 10. Examples of the aliphatic substituted ureido group include a methylureido group.
Examples of the non-aromatic heterocyclic group include a piperidino group and a morpholino group.
The molecular weight of the retardation developer composed of a discotic compound is preferably 300 to 800.
本発明では前述の円盤状化合物の他に、直線的な分子構造を有する棒状化合物も好ましく用いることができる。直線的な分子構造とは、熱力学的に最も安定な構造において棒状化合物の分子構造が直線的であることを意味する。熱力学的に最も安定な構造は、結晶構造解析または分子軌道計算によって求めることができる。例えば、分子軌道計算ソフト（例、WinMOPAC2000、富士通（株）製）を用いて分子軌道計算を行い、化合物の生成熱が最も小さくなるような分子の構造を求めることができる。分子構造が直線的であるとは、上記のように計算して求められる熱力学的に最も安定な構造において、分子構造で主鎖の構成する角度が１４０度以上であることを意味する。 In the present invention, in addition to the aforementioned discotic compound, a rod-shaped compound having a linear molecular structure can also be preferably used. The linear molecular structure means that the molecular structure of the rod-like compound is linear in the most thermodynamically stable structure. The most thermodynamically stable structure can be obtained by crystal structure analysis or molecular orbital calculation. For example, molecular orbital calculation can be performed using molecular orbital calculation software (eg, WinMOPAC2000, manufactured by Fujitsu Limited) to determine the molecular structure that minimizes the heat of formation of the compound. The molecular structure being linear means that in the thermodynamically most stable structure obtained by calculation as described above, the angle of the main chain constituting the molecular structure is 140 degrees or more.
棒状化合物としては、少なくとも二つの芳香族環を有するものが好ましく、少なくとも二つの芳香族環を有する棒状化合物としては、下記一般式（１）で表される化合物が好ましい。
一般式（１）：Ａｒ1−Ｌ1−Ａｒ2
上記一般式（１）において、Ａｒ1およびＡｒ2は、それぞれ独立に、芳香族基である。
本明細書において、芳香族基は、アリール基（芳香族性炭化水素基）、置換アリール基、芳香族性ヘテロ環基および置換芳香族性ヘテロ環基を含む。
アリール基および置換アリール基の方が、芳香族性ヘテロ環基および置換芳香族性ヘテロ環基よりも好ましい。芳香族性へテロ環基のヘテロ環は、一般には不飽和である。芳香族性ヘテロ環は、５員環、６員環または７員環であることが好ましく、５員環または６員環であることがさらに好ましい。芳香族性へテロ環は一般に最多の二重結合を有する。ヘテロ原子としては、窒素原子、酸素原子または硫黄原子が好ましく、窒素原子または硫黄原子がさらに好ましい。
芳香族基の芳香族環としては、ベンゼン環、フラン環、チオフェン環、ピロール環、オキサゾール環、チアゾール環、イミダゾール環、トリアゾール環、ピリジン環、ピリミジン環およびピラジン環が好ましく、ベンゼン環が特に好ましい。
As the rod-shaped compound, those having at least two aromatic rings are preferable, and as the rod-shaped compound having at least two aromatic rings, a compound represented by the following general formula (1) is preferable.
Formula (1): Ar 1 -L 1 -Ar 2
In the general formula (1), Ar 1 and Ar 2 are each independently an aromatic group.
In the present specification, the aromatic group includes an aryl group (aromatic hydrocarbon group), a substituted aryl group, an aromatic heterocyclic group, and a substituted aromatic heterocyclic group.
An aryl group and a substituted aryl group are more preferable than an aromatic heterocyclic group and a substituted aromatic heterocyclic group. The heterocycle of the aromatic heterocyclic group is generally unsaturated. The aromatic heterocycle is preferably a 5-membered ring, 6-membered ring or 7-membered ring, more preferably a 5-membered ring or 6-membered ring. Aromatic heterocycles generally have the most double bonds. As a hetero atom, a nitrogen atom, an oxygen atom or a sulfur atom is preferable, and a nitrogen atom or a sulfur atom is more preferable.
As the aromatic ring of the aromatic group, a benzene ring, a furan ring, a thiophene ring, a pyrrole ring, an oxazole ring, a thiazole ring, an imidazole ring, a triazole ring, a pyridine ring, a pyrimidine ring and a pyrazine ring are preferable, and a benzene ring is particularly preferable. .
置換アリール基および置換芳香族性ヘテロ環基の置換基の例には、ハロゲン原子（Ｆ、Ｃｌ、Ｂｒ、Ｉ）、ヒドロキシル基、カルボキシル基、シアノ基、アミノ基、アルキルアミノ基（例、メチルアミノ基、エチルアミノ基、ブチルアミノ基、ジメチルアミノ基）、ニトロ基、スルホ基、カルバモイル基、アルキルカルバモイル基（例、Ｎ−メチルカルバモイル基、Ｎ−エチルカルバモイル基、Ｎ，Ｎ−ジメチルカルバモイル基）、スルファモイル基、アルキルスルファモイル基（例、Ｎ−メチルスルファモイル基、Ｎ−エチルスルファモイル基、Ｎ，Ｎ−ジメチルスルファモイル基）、ウレイド基、アルキルウレイド基（例、Ｎ−メチルウレイド基、Ｎ，Ｎ−ジメチルウレイド基、Ｎ，Ｎ，Ｎ'−トリメチルウレイド基）、アルキル基（例、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘプチル基、オクチル基、イソプロピル基、ｓ−ブチル基、ｔ−アミル基、シクロヘキシル基、シクロペンチル基）、アルケニル基（例、ビニル基、アリル基、ヘキセニル基）、アルキニル基（例、エチニル基、ブチニル基）、アシル基（例、ホルミル基、アセチル基、ブチリル基、ヘキサノイル基、ラウリル基）、アシルオキシ基（例、アセトキシ基、ブチリルオキシ基、ヘキサノイルオキシ基、ラウリルオキシ基）、アルコキシ基（例、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペンチルオキシ基、ヘプチルオキシ基、オクチルオキシ基）、アリールオキシ基（例、フェノキシ基）、アルコキシカルボニル基（例、メトキシカルボニル基、エトキシカルボニル基、プロポキシカルボニル基、ブトキシカルボニル基、ペンチルオキシカルボニル基、ヘプチルオキシカルボニル基）、アリールオキシカルボニル基（例、フェノキシカルボニル基）、アルコキシカルボニルアミノ基（例、ブトキシカルボニルアミノ基、ヘキシルオキシカルボニルアミノ基）、アルキルチオ基（例、メチルチオ基、エチルチオ基、プロピルチオ基、ブチルチオ基、ペンチルチオ基、ヘプチルチオ基、オクチルチオ基）、アリールチオ基（例、フェニルチオ基）、アルキルスルホニル基（例、メチルスルホニル基、エチルスルホニル基、プロピルスルホニル基、ブチルスルホニル基、ペンチルスルホニル基、ヘプチルスルホニル基、オクチルスルホニル基）、アミド基（例、アセトアミド基、ブチルアミド基、ヘキシルアミド基、ラウリルアミド基）および非芳香族性複素環基（例、モルホリル基、ピラジニル基）が含まれる。 Examples of the substituent of the substituted aryl group and the substituted aromatic heterocyclic group include a halogen atom (F, Cl, Br, I), a hydroxyl group, a carboxyl group, a cyano group, an amino group, an alkylamino group (eg, methyl). Amino group, ethylamino group, butylamino group, dimethylamino group), nitro group, sulfo group, carbamoyl group, alkylcarbamoyl group (eg, N-methylcarbamoyl group, N-ethylcarbamoyl group, N, N-dimethylcarbamoyl group) ), Sulfamoyl group, alkylsulfamoyl group (eg, N-methylsulfamoyl group, N-ethylsulfamoyl group, N, N-dimethylsulfamoyl group), ureido group, alkylureido group (eg, N -Methylureido group, N, N-dimethylureido group, N, N, N'-trimethylureido group), alkyl group (eg, Methyl, ethyl, propyl, butyl, pentyl, heptyl, octyl, isopropyl, s-butyl, t-amyl, cyclohexyl, cyclopentyl), alkenyl (eg, vinyl, allyl) Group, hexenyl group), alkynyl group (eg, ethynyl group, butynyl group), acyl group (eg, formyl group, acetyl group, butyryl group, hexanoyl group, lauryl group), acyloxy group (eg, acetoxy group, butyryloxy group, Hexanoyloxy group, lauryloxy group), alkoxy group (eg, methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, heptyloxy group, octyloxy group), aryloxy group (eg, phenoxy group), Alkoxycarbonyl group (eg, methoxycarbonyl group, ethoxycarbonyl group, Ropoxycarbonyl group, butoxycarbonyl group, pentyloxycarbonyl group, heptyloxycarbonyl group), aryloxycarbonyl group (eg, phenoxycarbonyl group), alkoxycarbonylamino group (eg, butoxycarbonylamino group, hexyloxycarbonylamino group) , Alkylthio groups (eg, methylthio group, ethylthio group, propylthio group, butylthio group, pentylthio group, heptylthio group, octylthio group), arylthio groups (eg, phenylthio group), alkylsulfonyl groups (eg, methylsulfonyl group, ethylsulfonyl group) , Propylsulfonyl group, butylsulfonyl group, pentylsulfonyl group, heptylsulfonyl group, octylsulfonyl group), amide group (eg, acetamido group, butyramide group, hexylamide group, Uriruamido group) and a non-aromatic Hajime Tamaki (e.g., morpholyl groups include pyrazinyl group).
置換アリール基および置換芳香族性ヘテロ環基の置換基としては、ハロゲン原子、シアノ基、カルボキシル基、ヒドロキシル基、アミノ基、アルキル置換アミノ基、アシル基、アシルオキシ基、アミド基、アルコキシカルボニル基、アルコキシ基、アルキルチオ基およびアルキル基が好ましい。
アルキルアミノ基、アルコキシカルボニル基、アルコキシ基およびアルキルチオ基のアルキル部分とアルキル基とは、さらに置換基を有していてもよい。アルキル部分およびアルキル基の置換基の例には、ハロゲン原子、ヒドロキシル、カルボキシル、シアノ、アミノ、アルキルアミノ基、ニトロ、スルホ、カルバモイル、アルキルカルバモイル基、スルファモイル、アルキルスルファモイル基、ウレイド、アルキルウレイド基、アルケニル基、アルキニル基、アシル基、アシルオキシ基、アシルアミノ基、アルコキシ基、アリールオキシ基、アルコキシカルボニル基、アリールオキシカルボニル基、アルコキシカルボニルアミノ基、アルキルチオ基、アリールチオ基、アルキルスルホニル基、アミド基および非芳香族性複素環基が含まれる。アルキル部分およびアルキル基の置換基としては、ハロゲン原子、ヒドロキシル、アミノ、アルキルアミノ基、アシル基、アシルオキシ基、アシルアミノ基、アルコキシカルボニル基およびアルコキシ基が好ましい。
Examples of the substituent of the substituted aryl group and the substituted aromatic heterocyclic group include a halogen atom, a cyano group, a carboxyl group, a hydroxyl group, an amino group, an alkyl-substituted amino group, an acyl group, an acyloxy group, an amide group, an alkoxycarbonyl group, Alkoxy groups, alkylthio groups and alkyl groups are preferred.
The alkyl part and the alkyl group of the alkylamino group, alkoxycarbonyl group, alkoxy group and alkylthio group may further have a substituent. Examples of alkyl moieties and substituents of alkyl groups include halogen atom, hydroxyl, carboxyl, cyano, amino, alkylamino group, nitro, sulfo, carbamoyl, alkylcarbamoyl group, sulfamoyl, alkylsulfamoyl group, ureido, alkylureido Group, alkenyl group, alkynyl group, acyl group, acyloxy group, acylamino group, alkoxy group, aryloxy group, alkoxycarbonyl group, aryloxycarbonyl group, alkoxycarbonylamino group, alkylthio group, arylthio group, alkylsulfonyl group, amide group And non-aromatic heterocyclic groups. As the substituent for the alkyl moiety and the alkyl group, a halogen atom, hydroxyl, amino, alkylamino group, acyl group, acyloxy group, acylamino group, alkoxycarbonyl group and alkoxy group are preferable.
一般式（１）において、Ｌ1は、アルキレン基、アルケニレン基、アルキニレン基、−Ｏ−、−ＣＯ−およびそれらの組み合わせからなる基から選ばれる二価の連結基である。
アルキレン基は、環状構造を有していてもよい。環状アルキレン基としては、シクロヘキシレンが好ましく、１，４−シクロへキシレンが特に好ましい。鎖状アルキレン基としては、直鎖状アルキレン基の方が分岐を有するアルキレン基よりも好ましい。
アルキレン基の炭素原子数は、１乃至２０であることが好ましく、より好ましくは１乃至１５であり、さらに好ましくは１乃至１０であり、さらに好ましくは１乃至８であり、最も好ましくは１乃至６である。
In the general formula (1), L 1 is a divalent linking group selected from an alkylene group, an alkenylene group, an alkynylene group, —O—, —CO— and a combination thereof.
The alkylene group may have a cyclic structure. As the cyclic alkylene group, cyclohexylene is preferable, and 1,4-cyclohexylene is particularly preferable. As the chain alkylene group, a linear alkylene group is more preferable than a branched alkylene group.
The alkylene group preferably has 1 to 20 carbon atoms, more preferably 1 to 15, more preferably 1 to 10, still more preferably 1 to 8, and most preferably 1 to 6 carbon atoms. It is.
アルケニレン基およびアルキニレン基は、環状構造よりも鎖状構造を有することが好ましく、分岐を有する鎖状構造よりも直鎖状構造を有することがさらに好ましい。
アルケニレン基およびアルキニレン基の炭素原子数は、好ましくは２乃至１０であり、より好ましくは２乃至８であり、さらに好ましくは２乃至６であり、さらに好ましくは２乃至４であり、最も好ましくは２（ビニレンまたはエチニレン）である。
アリーレン基は、炭素原子数は６乃至２０であることが好ましく、より好ましくは６乃至１６であり、さらに好ましくは６乃至１２である。
The alkenylene group and alkynylene group preferably have a chain structure rather than a cyclic structure, and more preferably have a linear structure rather than a branched chain structure.
The number of carbon atoms of the alkenylene group and the alkynylene group is preferably 2 to 10, more preferably 2 to 8, further preferably 2 to 6, further preferably 2 to 4, and most preferably 2. (Vinylene or ethynylene).
The arylene group preferably has 6 to 20 carbon atoms, more preferably 6 to 16, and still more preferably 6 to 12.
一般式（１）の分子構造において、Ｌ1を挟んで、Ａｒ1とＡｒ2とが形成する角度は、１４０度以上であることが好ましい。
棒状化合物は、文献記載の方法により合成できる。文献としては、Mol. Cryst. Liq. Cryst., 53巻、229ページ（１９７９年）、同89巻、93ページ（１９８２年）、同145巻、111ページ（１９８７年）、同170巻、43ページ（１９８９年）、J. Am. Chem. Soc.,113巻、1349ページ（１９９１年）、同118巻、5346ページ（１９９６年）、同92巻、1582ページ（１９７０年）、J. Org. Chem.,40巻、420ページ（１９７５年）、Tetrahedron、48巻16号、3437ページ（１９９２年）を挙げることができる。
また、一般式（Ｉ）で表される棒状化合物を用いることがさらに好ましい。以下に一般式（Ｉ）で表される化合物について説明する。
In the molecular structure of the general formula (1), the angle formed by Ar 1 and Ar 2 across L 1 is preferably 140 degrees or more.
The rod-like compound can be synthesized by a method described in the literature. References include Mol. Cryst. Liq. Cryst., 53, 229 (1979), 89, 93 (1982), 145, 111 (1987), 170, 43 Page (1989), J. Am. Chem. Soc., 113, 1349 (1991), 118, 5346 (1996), 92, 1582 (1970), J. Org Chem., 40, 420 (1975), Tetrahedron, 48, 16, 3437 (1992).
Further, it is more preferable to use a rod-like compound represented by the general formula (I). The compound represented by general formula (I) is demonstrated below.
（式中、Ｒ1、Ｒ2、Ｒ3、Ｒ4、Ｒ5、Ｒ6、Ｒ7、Ｒ9およびＲ10はそれぞれ独立に水素原子または置換基を表し、Ｒ1、Ｒ2、Ｒ3、Ｒ4およびＲ5のうち少なくとも１つは電子供与性基を表す。Ｒ8は水素原子、炭素数１〜４のアルキル基、炭素数２〜６のアルキニル基、炭素数６〜１２のアリール基、炭素数１〜１２のアルコキシ基、炭素数６〜１２のアリールオキシ基、炭素数２〜１２のアルコキシカルボニル基、炭素数２〜１２のアシルアミノ基、シアノ基またはハロゲン原子を表す。） (In the formula, R 1 , R 2 , R 3 , R 4 , R 5 , R 6 , R 7 , R 9 and R 10 each independently represent a hydrogen atom or a substituent, and R 1 , R 2 , R 3 At least one .R 8 which represents an electron-donating group is a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, an alkynyl group having 2 to 6 carbon atoms, aryl having 6 to 12 carbon atoms of R 4 and R 5 A group, an alkoxy group having 1 to 12 carbon atoms, an aryloxy group having 6 to 12 carbon atoms, an alkoxycarbonyl group having 2 to 12 carbon atoms, an acylamino group having 2 to 12 carbon atoms, a cyano group, or a halogen atom.
一般式（Ｉ）中、Ｒ1、Ｒ2、Ｒ3、Ｒ4、Ｒ5、Ｒ6、Ｒ7、Ｒ9およびＲ10はそれぞれ独立に水素原子、または置換基を表し、置換基は後述の置換基Ｔが適用できる。
Ｒ1、Ｒ2、Ｒ3、Ｒ4およびＲ5のうち少なくとも１つは電子供与性基を表す。好ましくはＲ1、Ｒ3またはＲ5のうちの１つが電子供与性基であり、Ｒ3が電子供与性基であることがより好ましい。
電子供与性基とはHammetのσｐ値が０以下のものを表し、Cｈeｍ．Rev．，９１，１６５（１９９１）記載のHammetのσｐ値が０以下のものが好ましく適用でき、より好ましくは−０．８５〜０のものが用いられる。例えば、アルキル基、アルコキシ基、アミノ基、水酸基などが挙げられる。
電子供与性基として好ましくはアルキル基、アルコキシ基であり、より好ましくはアルコキシ基（好ましくは炭素数１〜１２、より好ましくは炭素数１〜８、更に好ましくは炭素数１〜６特に好ましくは炭素数１〜４である。）である。
In general formula (I), R 1 , R 2 , R 3 , R 4 , R 5 , R 6 , R 7 , R 9 and R 10 each independently represents a hydrogen atom or a substituent, and the substituent will be described later. The substituent T can be applied.
At least one of R 1 , R 2 , R 3 , R 4 and R 5 represents an electron donating group. Preferably, one of R 1 , R 3 or R 5 is an electron donating group, and R 3 is more preferably an electron donating group.
An electron donating group is one having a Hammet's σp value of 0 or less. Rev. 91, 165 (1991), those having Hammet's σp value of 0 or less are preferably applicable, and those having −0.85 to 0 are more preferably used. Examples thereof include an alkyl group, an alkoxy group, an amino group, and a hydroxyl group.
The electron donating group is preferably an alkyl group or an alkoxy group, more preferably an alkoxy group (preferably having 1 to 12 carbon atoms, more preferably 1 to 8 carbon atoms, still more preferably 1 to 6 carbon atoms, particularly preferably carbon). 1 to 4).
Ｒ1として好ましくは、水素原子または電子供与性基であり、より好ましくはアルキル基、アルコキシ基、アミノ基、水酸基であり、更に好ましくは、炭素数１〜４のアルキル基、炭素数１〜１２のアルコキシ基であり、特に好ましくはアルコキシ基（好ましくは炭素数１〜１２、より好ましくは炭素数１〜８、更に好ましくは炭素数１〜６、特に好ましくは炭素数１〜４）であり、最も好ましくはメトキシ基である。 R 1 is preferably a hydrogen atom or an electron donating group, more preferably an alkyl group, an alkoxy group, an amino group, or a hydroxyl group, and still more preferably an alkyl group having 1 to 4 carbon atoms or a carbon number 1 to 12 Particularly preferably an alkoxy group (preferably having 1 to 12 carbon atoms, more preferably 1 to 8 carbon atoms, still more preferably 1 to 6 carbon atoms, and particularly preferably 1 to 4 carbon atoms). Most preferred is a methoxy group.
Ｒ2として好ましくは、水素原子、アルキル基、アルコキシ基、アミノ基、水酸基であり、より好ましくは、水素原子、アルキル基、アルコキシ基であり、更に好ましくは水素原子、アルキル基（好ましくは炭素数１〜４、より好ましくはメチル基である。）、アルコキシ基（好ましくは炭素数１〜１２、より好ましくは炭素数１〜８、更に好ましくは炭素数１〜６、特に好ましくは炭素数１〜４）である。特に好ましくは水素原子、メチル基、メトキシ基である。 R 2 is preferably a hydrogen atom, an alkyl group, an alkoxy group, an amino group or a hydroxyl group, more preferably a hydrogen atom, an alkyl group or an alkoxy group, still more preferably a hydrogen atom or an alkyl group (preferably a carbon number). 1 to 4, more preferably a methyl group), an alkoxy group (preferably having 1 to 12 carbon atoms, more preferably 1 to 8 carbon atoms, still more preferably 1 to 6 carbon atoms, and particularly preferably 1 to carbon atoms). 4). Particularly preferred are a hydrogen atom, a methyl group and a methoxy group.
Ｒ3として好ましくは、水素原子または電子供与性基であり、より好ましくは水素原子、アルキル基、アルコキシ基、アミノ基、水酸基であり、更に好ましくは、アルキル基、アルコキシ基であり、特に好ましくはアルコキシ基（好ましくは炭素数１〜１２、より好ましくは炭素数１〜８、更に好ましくは炭素数１〜６、特に好ましくは炭素数１〜４）である。最も好ましくはｎ−プロポキシ基、エトキシ基、メトキシ基である。 R 3 is preferably a hydrogen atom or an electron donating group, more preferably a hydrogen atom, an alkyl group, an alkoxy group, an amino group, or a hydroxyl group, still more preferably an alkyl group or an alkoxy group, particularly preferably. An alkoxy group (preferably having 1 to 12 carbon atoms, more preferably 1 to 8 carbon atoms, still more preferably 1 to 6 carbon atoms, and particularly preferably 1 to 4 carbon atoms). Most preferred are n-propoxy group, ethoxy group and methoxy group.
Ｒ4として好ましくは、水素原子または電子供与性基であり、より好ましくは水素原子、アルキル基、アルコキシ基、アミノ基、水酸基であり、更に好ましくは、水素原子、炭素数１〜４のアルキル基、炭素数１〜１２のアルコキシ基（好ましくは炭素数１〜１２、より好ましくは炭素数１〜８、更に好ましくは炭素数１〜６、特に好ましくは炭素数１〜４）であり、特に好ましくは水素原子、炭素数１〜４のアルキル基、炭素数１〜４のアルコキシ基であり、最も好ましくは水素原子、メチル基、メトキシ基である。 R 4 is preferably a hydrogen atom or an electron donating group, more preferably a hydrogen atom, an alkyl group, an alkoxy group, an amino group, or a hydroxyl group, and still more preferably a hydrogen atom or an alkyl group having 1 to 4 carbon atoms. , An alkoxy group having 1 to 12 carbon atoms (preferably having 1 to 12 carbon atoms, more preferably 1 to 8 carbon atoms, still more preferably 1 to 6 carbon atoms, and particularly preferably 1 to 4 carbon atoms), particularly preferably. Is a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and most preferably a hydrogen atom, a methyl group, or a methoxy group.
Ｒ5として好ましくは、水素原子、アルキル基、アルコキシ基、アミノ基、水酸基であり、より好ましくは、水素原子、アルキル基、アルコキシ基であり、更に好ましくは水素原子、アルキル基（好ましくは炭素数１〜４より好ましくはメチル基である。）、アルコキシ基（好ましくは炭素数１〜１２、より好ましくは炭素数１〜８、更に好ましくは炭素数１〜６特に好ましくは炭素数１〜４）である。特に好ましくは水素原子、メチル基、メトキシ基である。 R 5 is preferably a hydrogen atom, an alkyl group, an alkoxy group, an amino group or a hydroxyl group, more preferably a hydrogen atom, an alkyl group or an alkoxy group, still more preferably a hydrogen atom or an alkyl group (preferably a carbon number). 1 to 4 is more preferably a methyl group), an alkoxy group (preferably having 1 to 12 carbon atoms, more preferably 1 to 8 carbon atoms, still more preferably 1 to 6 carbon atoms, and particularly preferably 1 to 4 carbon atoms). It is. Particularly preferred are a hydrogen atom, a methyl group and a methoxy group.
Ｒ6、Ｒ7、Ｒ9およびＲ10として好ましくは水素原子、炭素数1〜１２のアルキル基、炭素数1〜１２のアルコキシ基、ハロゲン原子であり、より好ましくは、水素原子、ハロゲン原子であり、更に好ましくは水素原子である。 R 6 , R 7 , R 9 and R 10 are preferably a hydrogen atom, an alkyl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, or a halogen atom, more preferably a hydrogen atom or a halogen atom. More preferably a hydrogen atom.
Ｒ8は水素原子、炭素数１〜４のアルキル基、炭素数２〜６のアルキニル基、炭素数６〜１２のアリール基、炭素数1〜１２のアルコキシ基、炭素数６〜１２のアリールオキシ基、炭素数２〜１２のアルコキシカルボニル基、炭素数２〜１２のアシルアミノ基、シアノ基またはハロゲン原子を表し、可能な場合には置換基を有してもよく、置換基としては後述の置換基Ｔが適用できる。
Ｒ8として好ましくは炭素数１〜４のアルキル基、炭素数２〜６のアルキニル基、炭素数６〜１２のアリール基、炭素数１〜１２のアルコキシ基、炭素数２〜１２のアリールオキシ基であり、より好ましくは、炭素数６〜１２のアリール基、炭素数１〜１２のアルコキシ基、炭素数６〜１２のアリールオキシ基であり、更に好ましくは炭素数１〜１２のアルコキシ基（好ましくは炭素数１〜１２、より好ましくは炭素数１〜８、更に好ましくは炭素数１〜６、特に好ましくは炭素数１〜４である。）であり、特に好ましくは、メトキシ基、エトキシ基、ｎ−プロポキシ基、ｉｓｏ−プロポキシ基、ｎ−ブトキシ基である。
R 8 is a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, an alkynyl group having 2 to 6 carbon atoms, an aryl group having 6 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, or an aryloxy group having 6 to 12 carbon atoms. Group, an alkoxycarbonyl group having 2 to 12 carbon atoms, an acylamino group having 2 to 12 carbon atoms, a cyano group, or a halogen atom, which may have a substituent if possible. The group T can be applied.
R 8 is preferably an alkyl group having 1 to 4 carbon atoms, an alkynyl group having 2 to 6 carbon atoms, an aryl group having 6 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, and an aryloxy group having 2 to 12 carbon atoms. And more preferably an aryl group having 6 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, and an aryloxy group having 6 to 12 carbon atoms, still more preferably an alkoxy group having 1 to 12 carbon atoms (preferably Is preferably 1 to 12 carbon atoms, more preferably 1 to 8 carbon atoms, still more preferably 1 to 6 carbon atoms, particularly preferably 1 to 4 carbon atoms, and particularly preferably a methoxy group, an ethoxy group, n-propoxy group, iso-propoxy group and n-butoxy group.
一般式（Ｉ）のうちより好ましくは下記一般式（Ｉ−Ａ）である。
一般式（Ｉ−Ａ）
Of the general formula (I), the following general formula (IA) is more preferable.
General formula (IA)
（式中、Ｒ11はアルキル基を表す。Ｒ1、Ｒ2、Ｒ4、Ｒ5、Ｒ6、Ｒ7、Ｒ9およびＲ10はそれぞれ独立に水素原子、または置換基を表す。Ｒ8は水素原子、炭素数１〜４のアルキル基、炭素数２〜６のアルキニル基、炭素数６〜１２のアリール基、炭素数1〜１２のアルコキシ基、炭素数６〜１２のアリールオキシ基、炭素数２〜１２のアルコキシカルボニル基、炭素数２〜１２のアシルアミノ基、シアノ基またはハロゲン原子を表す。）
一般式（Ｉ−Ａ）中、Ｒ1、Ｒ2、Ｒ4、Ｒ5、Ｒ6、Ｒ7、Ｒ8、Ｒ9およびＲ10はそれぞれ一般式（Ｉ）におけるそれらと同義であり、また好ましい範囲も同様である。
(Wherein R 11 represents an alkyl group. R 1 , R 2 , R 4 , R 5 , R 6 , R 7 , R 9 and R 10 each independently represents a hydrogen atom or a substituent. R 8 Is a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, an alkynyl group having 2 to 6 carbon atoms, an aryl group having 6 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, an aryloxy group having 6 to 12 carbon atoms, Represents an alkoxycarbonyl group having 2 to 12 carbon atoms, an acylamino group having 2 to 12 carbon atoms, a cyano group, or a halogen atom.)
In the general formula (IA), R 1 , R 2 , R 4 , R 5 , R 6 , R 7 , R 8 , R 9 and R 10 are respectively synonymous with those in the general formula (I), and The preferable range is also the same.
一般式（Ｉ−Ａ）中、Ｒ11は炭素数１〜１２のアルキル基を表し、Ｒ11で表されるアルキル基は直鎖でも分岐があってもよく、また更に置換基を有してもよいが、好ましくは炭素数１〜１２のアルキル基、より好ましくは炭素数１〜８アルキル基、更に好ましくは炭素数１〜６アルキル基、特に好ましくは炭素数１〜４のアルキル基（例えば、メチル基、エチル基、ｎ−プロピル基、ｉｓｏ−プロピル基、ｎ−ブチル基、ｉｓｏ−ブチル基、ｔｅｒｔ−ブチル基などが挙げられる）を表す。 In General Formula (IA), R 11 represents an alkyl group having 1 to 12 carbon atoms, and the alkyl group represented by R 11 may be linear or branched, and further has a substituent. However, preferably an alkyl group having 1 to 12 carbon atoms, more preferably an alkyl group having 1 to 8 carbon atoms, still more preferably an alkyl group having 1 to 6 carbon atoms, and particularly preferably an alkyl group having 1 to 4 carbon atoms (for example, , Methyl group, ethyl group, n-propyl group, iso-propyl group, n-butyl group, iso-butyl group, tert-butyl group and the like.
一般式（Ｉ）のうちより好ましくは下記一般式（Ｉ−Ｂ）である。
一般式（Ｉ−Ｂ）
Of the general formula (I), the following general formula (IB) is more preferable.
General formula (IB)
（式中、Ｒ1、Ｒ2、Ｒ4、Ｒ5、Ｒ6、Ｒ7、Ｒ9およびＲ10はそれぞれ独立に水素原子、または置換基を表す。Ｒ11は炭素数１〜１２のアルキル基を表す。Ｘは炭素数１〜４のアルキル基、炭素数２〜６のアルキニル基、炭素数６〜１２のアリール基、炭素数1〜１２のアルコキシ基、炭素数６〜１２のアリールオキシ基、炭素数２〜１２のアルコキシカルボニル基、炭素数２〜１２のアシルアミノ基、シアノ基またはハロゲン原子を表す。） (Wherein R 1 , R 2 , R 4 , R 5 , R 6 , R 7 , R 9 and R 10 each independently represents a hydrogen atom or a substituent. R 11 is an alkyl having 1 to 12 carbon atoms. X represents an alkyl group having 1 to 4 carbon atoms, an alkynyl group having 2 to 6 carbon atoms, an aryl group having 6 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, or an aryloxy group having 6 to 12 carbon atoms. A group, an alkoxycarbonyl group having 2 to 12 carbon atoms, an acylamino group having 2 to 12 carbon atoms, a cyano group, or a halogen atom.)
一般式（Ｉ−Ｂ）中、Ｒ1、Ｒ2、Ｒ4、Ｒ5、Ｒ6、Ｒ7、Ｒ9、およびＲ10は一般式（Ｉ）におけるそれらと同義であり、また好ましい範囲も同様である。
一般式（Ｉ−Ｂ）中、Ｒ11は一般式（Ｉ−Ａ）におけるそれらと同義であり、また好ましい範囲も同様である。
In the general formula (IB), R 1 , R 2 , R 4 , R 5 , R 6 , R 7 , R 9 , and R 10 have the same meanings as those in the general formula (I), and preferred ranges are also included. It is the same.
In general formula (IB), R < 11 > is synonymous with those in general formula (IA), and the preferred range is also the same.
一般式（Ｉ−Ｂ）中、Ｘは炭素数１〜４のアルキル基、炭素数２〜６のアルキニル基、炭素数６〜１２のアリール基、炭素数１〜１２のアルコキシ基、炭素数６〜１２のアリールオキシ基、炭素数２〜１２のアルコキシカルボニル基、炭素数２〜１２のアシルアミノ基、シアノ基またはハロゲン原子を表す。
Ｒ1、Ｒ2、Ｒ4、およびＲ5がすべて水素原子の場合にはＸとして好ましくはアルキル基、アルキニル基、アリール基、アルコキシ基、アリールオキシ基であり、より好ましくは、アリール基、アルコキシ基、アリールオキシ基であり、更に好ましくはアルコキシ基（好ましくは炭素数１〜１２、より好ましくは炭素数１〜８、更に好ましくは炭素数１〜６、特に好ましくは炭素数１〜４である。）であり、特に好ましくは、メトキシ基、メトキシ基、ｎ−プロポキシ基、ｉｓｏ−プロポキシ基、ｎ−ブトキシ基である。
In general formula (IB), X is an alkyl group having 1 to 4 carbon atoms, an alkynyl group having 2 to 6 carbon atoms, an aryl group having 6 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, or 6 carbon atoms. Represents an aryloxy group having 12 to 12 carbon atoms, an alkoxycarbonyl group having 2 to 12 carbon atoms, an acylamino group having 2 to 12 carbon atoms, a cyano group, or a halogen atom.
When all of R 1 , R 2 , R 4 and R 5 are hydrogen atoms, X is preferably an alkyl group, alkynyl group, aryl group, alkoxy group or aryloxy group, more preferably an aryl group, alkoxy group Group, aryloxy group, more preferably alkoxy group (preferably having 1 to 12 carbon atoms, more preferably 1 to 8 carbon atoms, still more preferably 1 to 6 carbon atoms, particularly preferably 1 to 4 carbon atoms). And particularly preferably a methoxy group, a methoxy group, an n-propoxy group, an iso-propoxy group or an n-butoxy group.
Ｒ1、Ｒ2、Ｒ4、およびＲ5のうち少なくとも１つが置換基の場合にはＸとして好ましくはアルキニル基、アリール基、アルコキシカルボニル基、シアノ基、であり、より好ましくはアリール基（好ましくは炭素数６〜１２）、シアノ基、アルコキシカルボニル基（好ましくは炭素数２〜１２）であり、更に好ましくはアリール基（好ましくは炭素数６〜１２のアリール基であり、より好ましくはフェニル基、p−シアノフェニル基、ｐ−メトキシフェニルである。）、アルコキシカルボニル基（好ましくは炭素２〜１２、より好ましくは炭素数２〜６、更に好ましくは炭素数２〜４、特に好ましくはメトキシカルボニル、エトキシカルボニル、ｎ−プロポキシカルボニルである。）、シアノ基であり、特に好ましくは、フェニル基、メトキシカルボニル基、エトキシカルボニル基、ｎ−プロポキシカルボニル基、シアノ基である。 When at least one of R 1 , R 2 , R 4 and R 5 is a substituent, X is preferably an alkynyl group, an aryl group, an alkoxycarbonyl group or a cyano group, more preferably an aryl group (preferably Is a cyano group or an alkoxycarbonyl group (preferably a carbon number of 2 to 12), more preferably an aryl group (preferably an aryl group of 6 to 12 carbon atoms, more preferably a phenyl group). , P-cyanophenyl group and p-methoxyphenyl group), an alkoxycarbonyl group (preferably having 2 to 12 carbon atoms, more preferably 2 to 6 carbon atoms, still more preferably 2 to 4 carbon atoms, and particularly preferably methoxycarbonyl group). , Ethoxycarbonyl, n-propoxycarbonyl), cyano group, particularly preferably phenyl group, methoxy group. Group, an ethoxycarbonyl group, n- propoxycarbonyl group, a cyano group.
一般式（Ｉ）のうち更に好ましくは下記一般式（Ｉ−Ｃ）である。
一般式（Ｉ−Ｃ）
Of the general formula (I), the following general formula (IC) is more preferable.
General formula (IC)
式中、Ｒ1、Ｒ2、Ｒ4、Ｒ5、Ｒ11およびＸは一般式（Ｉ−Ｂ）におけるそれらと同義であり、また好ましい範囲も同様である。 In the formula, R 1 , R 2 , R 4 , R 5 , R 11 and X have the same meanings as those in formula (IB), and preferred ranges are also the same.
一般式（Ｉ）で表される化合物の中でより好ましいのは下記一般式（Ｉ−Ｄ）で表される化合物である。
一般式（Ｉ−Ｄ）
Among the compounds represented by the general formula (I), a compound represented by the following general formula (ID) is more preferable.
Formula (ID)
（式中、Ｒ2、Ｒ4およびＲ5は一般式（Ｉ−Ｃ）におけるそれらと同義であり、また好ましい範囲も同様である。Ｒ21、Ｒ22はそれぞれ独立に炭素数１〜４のアルキル基である。Ｘ1は炭素数６〜１２のアリール基、炭素数２〜１２のアルコキシカルボニル基、又はシアノ基である。） (Wherein R 2 , R 4 and R 5 have the same meanings as those in formula (IC), and preferred ranges are also the same. R 21 and R 22 each independently has 1 to 4 carbon atoms. X 1 is an aryl group having 6 to 12 carbon atoms, an alkoxycarbonyl group having 2 to 12 carbon atoms, or a cyano group.
Ｒ21は炭素数１〜４のアルキル基を表し、好ましくは炭素数１〜３のアルキル基であり、より好ましくはエチル基、メチル基である。
Ｒ22は炭素数１〜４のアルキル基を表し、好ましくは炭素数１〜３のアルキル基であり、より好ましくはエチル基、メチル基であり、更に好ましくはメチル基である。
R 21 represents an alkyl group having 1 to 4 carbon atoms, preferably an alkyl group having 1 to 3 carbon atoms, and more preferably an ethyl group or a methyl group.
R 22 represents an alkyl group having 1 to 4 carbon atoms, preferably an alkyl group having 1 to 3 carbon atoms, more preferably an ethyl group or a methyl group, and still more preferably a methyl group.
Ｘ1は炭素数６〜１２のアリール基、炭素２〜１２アルコキシカルボニル基、又はシアノ基であり、好ましくは炭素数６〜１０のアリール基、炭素数２〜６アルコキシカルボニル基、シアノ基であり、より好ましくはフェニル基、p−シアノフェニル基、ｐ−メトキシフェニル基、メトキシカルボニル、エトキシカルボニル、ｎ−プロポキシカルボニル、シアノ基であり、更に好ましくは、フェニル基、メトキシカルボニル基、エトキシカルボニル基、ｎ−プロポキシカルボニル基、シアノ基である。 X 1 is an aryl group having 6 to 12 carbon atoms, an alkoxycarbonyl group having 2 to 12 carbon atoms, or a cyano group, preferably an aryl group having 6 to 10 carbon atoms, an alkoxycarbonyl group having 2 to 6 carbon atoms, or a cyano group. More preferably a phenyl group, a p-cyanophenyl group, a p-methoxyphenyl group, a methoxycarbonyl, an ethoxycarbonyl, an n-propoxycarbonyl, a cyano group, and still more preferably a phenyl group, a methoxycarbonyl group, an ethoxycarbonyl group, n-propoxycarbonyl group and cyano group.
一般式（Ｉ）のうち最も好ましくは下記一般式（Ｉ−Ｅ）である。
一般式（Ｉ−Ｅ）
Of the general formula (I), the following general formula (IE) is most preferable.
Formula (IE)
（式中、Ｒ2、Ｒ4およびＲ5は一般式（Ｉ−Ｄ）におけるそれらと同義であり、また好ましい範囲も同様だが、いずれか１つは−ＯＲ13で表される基である（Ｒ13は炭素数１〜４のアルキル基である。）。Ｒ21、Ｒ22、およびＸ1は一般式（Ｉ−Ｄ）におけるそれらと同義であり、また好ましい範囲も同様である。） (Wherein R 2 , R 4 and R 5 have the same meanings as those in formula (ID) and preferred ranges are also the same, but one of them is a group represented by —OR 13 ( R 13 is an alkyl group having 1 to 4 carbon atoms.) R 21 , R 22 and X 1 have the same meanings as those in formula (ID), and preferred ranges are also the same.)
一般式（Ｉ−Ｅ）中、Ｒ2、Ｒ4およびＲ5は一般式（Ｉ−Ｄ）におけるそれらと同義であり、また好ましい範囲も同様だが、いずれか１つは−ＯＲ13で表される基であり（Ｒ13は炭素数１〜４のアルキル基である。）、好ましくはＲ4、およびＲ5が−ＯＲ13で表される基であり、より好ましくはＲ4が−ＯＲ13で表される基である。
Ｒ13は炭素数１〜４のアルキル基を表し、好ましくは炭素数１〜３のアルキル基であり、より好ましくはエチル基、メチル基であり、更に好ましくはメチル基である。
In the general formula (IE), R 2 , R 4 and R 5 have the same meanings as those in the general formula (ID), and preferred ranges are also the same, but any one of them is represented by —OR 13. (R 13 is an alkyl group having 1 to 4 carbon atoms), preferably R 4 and R 5 are groups represented by —OR 13 , more preferably R 4 is —OR 13. It is group represented by these.
R 13 represents an alkyl group having 1 to 4 carbon atoms, preferably an alkyl group having 1 to 3 carbon atoms, more preferably an ethyl group or a methyl group, and still more preferably a methyl group.
以下に前述の置換基Ｔについて説明する。
置換基Ｔとしては例えばアルキル基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１２、特に好ましくは炭素数１〜８であり、例えばメチル、エチル、ｉｓｏ−プロピル、ｔｅｒｔ−ブチル、ｎ−オクチル、ｎ−デシル、ｎ−ヘキサデシル、シクロプロピル、シクロペンチル、シクロヘキシルなどが挙げられる。）、アルケニル基（好ましくは炭素数２〜２０、より好ましくは炭素数２〜１２、特に好ましくは炭素数２〜８であり、例えばビニル、アリル、２−ブテニル、３−ペンテニルなどが挙げられる。）、アルキニル基（好ましくは炭素数２〜２０、より好ましくは炭素数２〜１２、特に好ましくは炭素数２〜８であり、例えばプロパルギル、３−ペンチニルなどが挙げられる。）、アリール基（好ましくは炭素数６〜３０、より好ましくは炭素数６〜２０、特に好ましくは炭素数６〜１２であり、例えばフェニル、ｐ−メチルフェニル、ナフチルなどが挙げられる。）、置換又は未置換のアミノ基（好ましくは炭素数０〜２０、より好ましくは炭素数０〜１０、特に好ましくは炭素数０〜６であり、例えばアミノ、メチルアミノ、ジメチルアミノ、ジエチルアミノ、ジベンジルアミノなどが挙げられる。）、アルコキシ基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１２、特に好ましくは炭素数１〜８であり、例えばメトキシ、エトキシ、ブトキシなどが挙げられる。）、アリールオキシ基（好ましくは炭素数６〜２０、より好ましくは炭素数６〜１６、特に好ましくは炭素数６〜１２であり、例えばフェニルオキシ、２−ナフチルオキシなどが挙げられる。）、アシル基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１６、特に好ましくは炭素数１〜１２であり、例えばアセチル、ベンゾイル、ホルミル、ピバロイルなどが挙げられる。）、アルコキシカルボニル基（好ましくは炭素数２〜２０、より好ましくは炭素数２〜１６、特に好ましくは炭素数２〜１２であり、例えばメトキシカルボニル、エトキシカルボニルなどが挙げられる。）、アリールオキシカルボニル基（好ましくは炭素数７〜２０、より好ましくは炭素数７〜１６、特に好ましくは炭素数７〜１０であり、例えばフェニルオキシカルボニルなどが挙げられる。）、アシルオキシ基（好ましくは炭素数２〜２０、より好ましくは炭素数２〜１６、特に好ましくは炭素数２〜１０であり、例えばアセトキシ、ベンゾイルオキシなどが挙げられる。）、アシルアミノ基（好ましくは炭素数２〜２０、より好ましくは炭素数２〜１６、特に好ましくは炭素数２〜１０であり、例えばアセチルアミノ、ベンゾイルアミノなどが挙げられる。）、アルコキシカルボニルアミノ基（好ましくは炭素数２〜２０、より好ましくは炭素数２〜１６、特に好ましくは炭素数２〜１２であり、例えばメトキシカルボニルアミノなどが挙げられる。）、アリールオキシカルボニルアミノ基（好ましくは炭素数７〜２０、より好ましくは炭素数７〜１６、特に好ましくは炭素数７〜１２であり、例えばフェニルオキシカルボニルアミノなどが挙げられる。）、スルホニルアミノ基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１６、特に好ましくは炭素数１〜１２であり、例えばメタンスルホニルアミノ、ベンゼンスルホニルアミノなどが挙げられる。）、スルファモイル基（好ましくは炭素数０〜２０、より好ましくは炭素数０〜１６、特に好ましくは炭素数０〜１２であり、例えばスルファモイル、メチルスルファモイル、ジメチルスルファモイル、フェニルスルファモイルなどが挙げられる。）、カルバモイル基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１６、特に好ましくは炭素数１〜１２であり、例えばカルバモイル、メチルカルバモイル、ジエチルカルバモイル、フェニルカルバモイルなどが挙げられる。）、アルキルチオ基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１６、特に好ましくは炭素数１〜１２であり、例えばメチルチオ、エチルチオなどが挙げられる。）、アリールチオ基（好ましくは炭素数６〜２０、より好ましくは炭素数６〜１６、特に好ましくは炭素数６〜１２であり、例えばフェニルチオなどが挙げられる。）、スルホニル基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１６、特に好ましくは炭素数１〜１２であり、例えばメシル、トシルなどが挙げられる。）、スルフィニル基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１６、特に好ましくは炭素数１〜１２であり、例えばメタンスルフィニル、ベンゼンスルフィニルなどが挙げられる。）、ウレイド基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１６、特に好ましくは炭素数１〜１２であり、例えばウレイド、メチルウレイド、フェニルウレイドなどが挙げられる。）、リン酸アミド基（好ましくは炭素数１〜２０、より好ましくは炭素数１〜１６、特に好ましくは炭素数１〜１２であり、例えばジエチルリン酸アミド、フェニルリン酸アミドなどが挙げられる。）、ヒドロキシ基、メルカプト基、ハロゲン原子（例えばフッ素原子、塩素原子、臭素原子、ヨウ素原子）、シアノ基、スルホ基、カルボキシル基、ニトロ基、ヒドロキサム酸基、スルフィノ基、ヒドラジノ基、イミノ基、ヘテロ環基（好ましくは炭素数１〜３０、より好ましくは１〜１２であり、ヘテロ原子としては、例えば窒素原子、酸素原子、硫黄原子、具体的には例えばイミダゾリル、ピリジル、キノリル、フリル、ピペリジル、モルホリノ、ベンゾオキサゾリル、ベンズイミダゾリル、ベンズチアゾリルなどが挙げられる。）、シリル基（好ましくは、炭素数３〜４０、より好ましくは炭素数３〜３０、特に好ましくは、炭素数３〜２４であり、例えば、トリメチルシリル、トリフェニルシリルなどが挙げられる）などが挙げられる。これらの置換基は更に置換されてもよい。
The aforementioned substituent T will be described below.
Examples of the substituent T include an alkyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 12 carbon atoms, and particularly preferably 1 to 8 carbon atoms such as methyl, ethyl, iso-propyl, tert-butyl, and n-octyl, n-decyl, n-hexadecyl, cyclopropyl, cyclopentyl, cyclohexyl, etc.), an alkenyl group (preferably having 2 to 20 carbon atoms, more preferably 2 to 12 carbon atoms, and particularly preferably carbon number). 2 to 8, for example, vinyl, allyl, 2-butenyl, 3-pentenyl, etc.), an alkynyl group (preferably having 2 to 20 carbon atoms, more preferably 2 to 12 carbon atoms, and particularly preferably carbon number). 2-8, for example, propargyl, 3-pentynyl, etc.), aryl groups (preferably having 6-30 carbon atoms) More preferably, it has 6 to 20 carbon atoms, particularly preferably 6 to 12 carbon atoms, and examples thereof include phenyl, p-methylphenyl, naphthyl and the like, and a substituted or unsubstituted amino group (preferably having 0 to 0 carbon atoms). 20, more preferably 0 to 10 carbon atoms, particularly preferably 0 to 6 carbon atoms, such as amino, methylamino, dimethylamino, diethylamino, dibenzylamino, etc.), an alkoxy group (preferably having a carbon number) 1 to 20, more preferably 1 to 12 carbon atoms, particularly preferably 1 to 8 carbon atoms, such as methoxy, ethoxy, butoxy, etc.), an aryloxy group (preferably 6 to 20 carbon atoms, more Preferably it has 6 to 16 carbon atoms, particularly preferably 6 to 12 carbon atoms, such as phenyloxy, 2-naphthyloxy and the like. An acyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms, and examples thereof include acetyl, benzoyl, formyl, and pivaloyl). An alkoxycarbonyl group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 12 carbon atoms, such as methoxycarbonyl, ethoxycarbonyl, etc.), an aryloxycarbonyl group ( Preferably it has 7 to 20 carbon atoms, more preferably 7 to 16 carbon atoms, particularly preferably 7 to 10 carbon atoms, and examples thereof include phenyloxycarbonyl, etc.), an acyloxy group (preferably 2 to 20 carbon atoms, More preferably, it has 2 to 16 carbon atoms, particularly preferably 2 to 10 carbon atoms. Nzoyloxy and the like. ), An acylamino group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 10 carbon atoms, and examples thereof include acetylamino and benzoylamino), alkoxycarbonylamino group (Preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 12 carbon atoms, such as methoxycarbonylamino), aryloxycarbonylamino group (preferably having carbon number) 7 to 20, more preferably 7 to 16 carbon atoms, particularly preferably 7 to 12 carbon atoms, such as phenyloxycarbonylamino, and the like, and sulfonylamino groups (preferably 1 to 20 carbon atoms, more preferably Has 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms. And sulfamoyl group (preferably having 0 to 20 carbon atoms, more preferably 0 to 16 carbon atoms, particularly preferably 0 to 12 carbon atoms, such as sulfamoyl and methylsulfamoyl). , Dimethylsulfamoyl, phenylsulfamoyl, etc.), a carbamoyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms, such as carbamoyl). , Methylcarbamoyl, diethylcarbamoyl, phenylcarbamoyl, etc.), an alkylthio group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms, such as methylthio, Ethylthio etc.), arylthio group (preferably Has 6 to 20 carbon atoms, more preferably 6 to 16 carbon atoms, particularly preferably 6 to 12 carbon atoms, such as phenylthio, and a sulfonyl group (preferably 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms, such as mesyl, tosyl, etc.), sulfinyl group (preferably 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably Has 1 to 12 carbon atoms, such as methanesulfinyl, benzenesulfinyl, etc.), ureido group (preferably 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms). For example, ureido, methylureido, phenylureido, etc.), phosphoric acid amide group (preferably having 1 to 20 carbon atoms) More preferably, it is C1-C16, Most preferably, it is C1-C12, for example, diethyl phosphoric acid amide, phenylphosphoric acid amide etc. are mentioned. ), Hydroxy group, mercapto group, halogen atom (eg fluorine atom, chlorine atom, bromine atom, iodine atom), cyano group, sulfo group, carboxyl group, nitro group, hydroxamic acid group, sulfino group, hydrazino group, imino group, Heterocyclic group (preferably having 1 to 30 carbon atoms, more preferably 1 to 12 carbon atoms, and examples of the hetero atom include a nitrogen atom, an oxygen atom, a sulfur atom, specifically, for example, imidazolyl, pyridyl, quinolyl, furyl, piperidyl , Morpholino, benzoxazolyl, benzimidazolyl, benzthiazolyl, etc.), silyl group (preferably having 3 to 40 carbon atoms, more preferably 3 to 30 carbon atoms, and particularly preferably 3 to 24 carbon atoms). For example, trimethylsilyl, triphenylsilyl, etc.) . These substituents may be further substituted.
また、置換基が二つ以上ある場合は、同じでも異なってもよい。また、可能な場合には互いに連結して環を形成してもよい。 Moreover, when there are two or more substituents, they may be the same or different. If possible, they may be linked together to form a ring.
以下に一般式（Ｉ）で表される化合物に関して具体例をあげて詳細に説明するが、本発明は以下の具体例によって何ら限定されることはない。 Hereinafter, the compound represented by formula (I) will be described in detail with specific examples, but the present invention is not limited to the following specific examples.
本発明一般式（Ｉ）で表される化合物は置換安息香酸とフェノール誘導体の一般的なエステル反応によって合成でき、エステル結合形成反応であればどのような反応を用いてもよい。例えば、置換安息香酸を酸ハロゲン化物に官能基変換した後、フェノールと縮合する方法、縮合剤あるいは触媒を用いて置換安息香酸とフェノール誘導体を脱水縮合する方法などがあげられる。
製造プロセス等を考慮すると置換安息香酸を酸ハロゲン化物に官能基変換した後、フェノールと縮合する方法が好ましい。
The compound represented by the general formula (I) of the present invention can be synthesized by a general ester reaction of a substituted benzoic acid and a phenol derivative, and any reaction may be used as long as it is an ester bond forming reaction. Examples thereof include a method of converting a substituted benzoic acid to an acid halide and then condensing with phenol, a method of dehydrating the substituted benzoic acid and a phenol derivative using a condensing agent or a catalyst, and the like.
In view of the production process and the like, a method in which the substituted benzoic acid is functionally converted to an acid halide and then condensed with phenol is preferable.
反応溶媒として炭化水素系溶媒（好ましくはトルエン、キシレンが挙げられる。）、エーテル系溶媒（好ましくはジメチルエーテル、テトラヒドロフラン、ジオキサンなどが挙げられる）、ケトン系溶媒、エステル系溶媒、アセトニトリル、ジメチルホルムアミド、ジメチルアセトアミドなどを用いることができる。これらの溶媒は単独でも数種を混合して用いてもよく、反応溶媒として好ましくはトルエン、アセトニトリル、ジメチルホルムアミド、ジメチルアセトアミドである。 Reaction solvents include hydrocarbon solvents (preferably toluene and xylene), ether solvents (preferably dimethyl ether, tetrahydrofuran, dioxane, etc.), ketone solvents, ester solvents, acetonitrile, dimethylformamide, dimethyl Acetamide or the like can be used. These solvents may be used alone or in admixture of several kinds, and preferred reaction solvents are toluene, acetonitrile, dimethylformamide and dimethylacetamide.
反応温度としては、好ましくは０〜１５０℃、より好ましくは０〜１００℃、更に好ましくは０〜９０℃であり、特に好ましくは２０℃〜９０℃である。
本反応には塩基を用いないのが好ましく、塩基を用いる場合には有機塩基、無機塩基のどちらでもよく、好ましくは有機塩基であり、ピリジン、３級アルキルアミン（好ましくはトリエチルアミン、エチルジイソプルピルアミンなどが挙げられる）である。
The reaction temperature is preferably 0 to 150 ° C, more preferably 0 to 100 ° C, still more preferably 0 to 90 ° C, and particularly preferably 20 ° C to 90 ° C.
In this reaction, it is preferable not to use a base. When a base is used, either an organic base or an inorganic base may be used, preferably an organic base such as pyridine, tertiary alkylamine (preferably triethylamine, ethyldiisopropyl). Pyramine and the like).
溶液の紫外線吸収スペクトルにおいて最大吸収波長（λmax）が２５０ｎｍより短波長である棒状化合物を、二種類以上併用してもよい。 Two or more rod-shaped compounds whose maximum absorption wavelength (λmax) is shorter than 250 nm in the ultraviolet absorption spectrum of the solution may be used in combination.
［マット剤微粒子］
本発明に関するセルロースアシレートフィルムには、マット剤として微粒子を加えることが好ましい。本発明に使用される微粒子としては、二酸化珪素、二酸化チタン、酸化アルミニウム、酸化ジルコニウム、炭酸カルシウム、炭酸カルシウム、タルク、クレイ、焼成カオリン、焼成珪酸カルシウム、水和ケイ酸カルシウム、ケイ酸アルミニウム、ケイ酸マグネシウム及びリン酸カルシウムを挙げることができる。微粒子はケイ素を含むものが濁度が低くなる点で好ましく、特に二酸化珪素が好ましい。二酸化珪素の微粒子は、１次平均粒子径が２０ｎｍ以下であり、かつ見かけ比重が７０ｇ／リットル以上であるものが好ましい。１次粒子の平均径が５〜１６ｎｍと小さいものがフィルムのヘイズを下げることができより好ましい。見かけ比重は９０〜２００ｇ／リットル以上が好ましく、１００〜２００ｇ／リットル以上がさらに好ましい。見かけ比重が大きい程、高濃度の分散液を作ることが可能になり、ヘイズ、凝集物が良化するため好ましい。
前記二酸化珪素微粒子を用いる場合の使用量は、セルロースアシレートを含むポリマー成分１００質量部に対して０．０１〜０．３質量部とするのが好ましい。
[Matting agent fine particles]
It is preferable to add fine particles as a matting agent to the cellulose acylate film according to the present invention. The fine particles used in the present invention include silicon dioxide, titanium dioxide, aluminum oxide, zirconium oxide, calcium carbonate, calcium carbonate, talc, clay, calcined kaolin, calcined calcium silicate, hydrated calcium silicate, aluminum silicate, silica Mention may be made of magnesium and calcium phosphates. Fine particles containing silicon are preferable in terms of low turbidity, and silicon dioxide is particularly preferable. The fine particles of silicon dioxide preferably have a primary average particle diameter of 20 nm or less and an apparent specific gravity of 70 g / liter or more. Those having an average primary particle size as small as 5 to 16 nm are more preferred because they can reduce the haze of the film. The apparent specific gravity is preferably 90 to 200 g / liter or more, and more preferably 100 to 200 g / liter or more. A larger apparent specific gravity is preferable because a high-concentration dispersion can be produced, and haze and aggregates are improved.
The amount of silicon dioxide fine particles used is preferably 0.01 to 0.3 parts by mass with respect to 100 parts by mass of the polymer component containing cellulose acylate.
これらの微粒子は、通常平均粒子径が０．１〜３．０μｍの２次粒子を形成し、これらの微粒子はフィルム中では、１次粒子の凝集体として存在し、フィルム表面に０．１〜３．０μｍの凹凸を形成させる。２次平均粒子径は０．２μｍ以上１．５μｍ以下が好ましく、０．４μｍ以上１．２μｍ以下がさらに好ましく、０．６μｍ以上１．１μｍ以下が最も好ましい。１．５μｍよりも大きいとヘイズが強くなり、０．２μｍよりも小さいときしみ防止効果が小さくなる。
１次、２次粒子径はフィルム中の粒子を走査型電子顕微鏡で観察し、粒子に外接する円の直径をもって粒径とする。また、場所を変えて粒子２００個を観察し、その平均値をもって平均粒子径とする。
These fine particles usually form secondary particles having an average particle diameter of 0.1 to 3.0 μm, and these fine particles are present as aggregates of primary particles in the film, and 0.1 to 0.1 μm on the film surface. An unevenness of 3.0 μm is formed. The secondary average particle size is preferably from 0.2 μm to 1.5 μm, more preferably from 0.4 μm to 1.2 μm, and most preferably from 0.6 μm to 1.1 μm. When it is larger than 1.5 μm, the haze becomes strong, and when it is smaller than 0.2 μm, the effect of preventing stain is reduced.
The primary and secondary particle diameters are determined by observing the particles in the film with a scanning electron microscope and using the diameter of a circle circumscribing the particles as the particle diameter. Also, 200 particles are observed at different locations, and the average value is taken as the average particle diameter.
二酸化珪素の微粒子は、例えば、アエロジルＲ９７２、Ｒ９７２Ｖ、Ｒ９７４、Ｒ８１２、２００、２００Ｖ、３００、Ｒ２０２、ＯＸ５０、ＴＴ６００（以上日本アエロジル（株）製）などの市販品を使用することができる。酸化ジルコニウムの微粒子は、例えば、アエロジルＲ９７６及びＲ８１１（以上日本アエロジル（株）製）の商品名で市販されており、使用することができる。 As fine particles of silicon dioxide, for example, commercially available products such as Aerosil R972, R972V, R974, R812, 200, 200V, 300, R202, OX50, TT600 (above Nippon Aerosil Co., Ltd.) can be used. Zirconium oxide fine particles are commercially available, for example, under the trade names Aerosil R976 and R811 (manufactured by Nippon Aerosil Co., Ltd.) and can be used.
これらの中でアエロジル２００Ｖ、アエロジルＲ９７２Ｖが１次平均粒子径が２０ｎｍ以下であり、かつ見かけ比重が７０ｇ／リットル以上である二酸化珪素の微粒子であり、光学フィルムの濁度を低く保ちながら、摩擦係数をさげる効果が大きいため特に好ましい。 Among these, Aerosil 200V and Aerosil R972V are fine particles of silicon dioxide having a primary average particle diameter of 20 nm or less and an apparent specific gravity of 70 g / liter or more, and the coefficient of friction is maintained while keeping the turbidity of the optical film low. It is particularly preferable because it has a great effect of reducing the effect.
本発明において２次平均粒子径の小さな粒子を有するセルロースアシレートフィルムを得るために、微粒子の分散液を調製する際にいくつかの手法が考えられる。例えば、溶剤と微粒子を撹拌混合した微粒子分散液をあらかじめ作成し、この微粒子分散液を別途用意した少量のセルロースアシレート溶液に加えて撹拌溶解し、さらにメインのセルロースアシレートドープ液と混合する方法がある。この方法は二酸化珪素微粒子の分散性がよく、二酸化珪素微粒子が更に再凝集しにくい点で好ましい調製方法である。ほかにも、溶剤に少量のセルロースエステルを加え、撹拌溶解した後、これに微粒子を加えて分散機で分散を行いこれを微粒子添加液とし、この微粒子添加液をインラインミキサーでドープ液と十分混合する方法もある。本発明はこれらの方法に限定されないが、二酸化珪素微粒子を溶剤などと混合して分散するときの二酸化珪素の濃度は５〜３０質量％が好ましく、１０〜２５質量％が更に好ましく、１５〜２０質量％が最も好ましい。分散濃度が高い方が添加量に対する液濁度は低くなり、ヘイズ、凝集物が良化するため好ましい。最終的なセルロースアシレートのドープ溶液中でのマット剤の添加量は１ｍ2あたり０．０１〜１．０ｇが好ましく、０．０３〜０．３ｇが更に好ましく、０．０８〜０．１６ｇが最も好ましい。 In order to obtain a cellulose acylate film having particles having a small secondary average particle size in the present invention, several methods are conceivable when preparing a fine particle dispersion. For example, a method of preparing a fine particle dispersion in which a solvent and fine particles are mixed with stirring in advance, adding this fine particle dispersion to a small amount of cellulose acylate solution separately prepared, stirring and dissolving, and further mixing with the main cellulose acylate dope solution There is. This method is a preferable preparation method in that the dispersibility of the silicon dioxide fine particles is good and the silicon dioxide fine particles are more difficult to reaggregate. In addition, after adding a small amount of cellulose ester to the solvent and dissolving with stirring, add the fine particles to this and disperse with a disperser to make this fine particle additive solution, and mix this fine particle additive solution with the dope solution using an inline mixer There is also a way to do it. The present invention is not limited to these methods, but the concentration of silicon dioxide when the silicon dioxide fine particles are mixed and dispersed with a solvent or the like is preferably 5 to 30% by mass, more preferably 10 to 25% by mass, and 15 to 20%. Mass% is most preferred. A higher dispersion concentration is preferable because the liquid turbidity with respect to the added amount is lowered, and haze and aggregates are improved. The addition amount of the matting agent in the final cellulose acylate dope solution is preferably 0.01 to 1.0 g, more preferably 0.03 to 0.3 g, and 0.08 to 0.16 g per 1 m 2. Most preferred.
使用される溶剤は低級アルコール類としては、好ましくはメチルアルコール、エチルアルコール、プロピルアルコール、イソプロピルアルコール、ブチルアルコール等が挙げられる。低級アルコール以外の溶媒としては特に限定されないが、セルロースエステルの製膜時に用いられる溶剤を用いることが好ましい。 The solvent used is preferably lower alcohols such as methyl alcohol, ethyl alcohol, propyl alcohol, isopropyl alcohol, butyl alcohol and the like. Although it does not specifically limit as solvents other than a lower alcohol, It is preferable to use the solvent used at the time of film forming of a cellulose ester.
次に、本発明に関するセルロースアシレートが溶解される前記有機溶媒について記述する。
本発明においては、有機溶媒として、塩素系有機溶媒を主溶媒とする塩素系溶媒と塩素系有機溶媒を含まない非塩素系溶媒とのいずれをも用いることができる。
（塩素系溶媒）
本発明に関するセルロースアシレートの溶液を作製するに際しては、主溶媒として塩素系有機溶媒が好ましく用いられる。本発明においては、セルロースアシレートが溶解し流延，製膜できる範囲において、その目的が達成できる限りはその塩素系有機溶媒の種類は特に限定されない。これらの塩素系有機溶媒は、好ましくはジクロロメタン、クロロホルムである。特にジクロロメタンが好ましい。また、塩素系有機溶媒以外の有機溶媒を混合することも特に問題ない。その場合は、ジクロロメタンは有機溶媒全体量中少なくとも５０質量％使用することが必要である。本発明で塩素系有機溶剤と併用される他の有機溶媒について以下に記す。すなわち、好ましい他の有機溶媒としては、炭素原子数が３〜１２のエステル、ケトン、エーテル、アルコール、炭化水素などから選ばれる溶媒が好ましい。エステル、ケトン、エーテルおよびアルコールは、環状構造を有していてもよい。エステル、ケトンおよびエーテルの官能基（すなわち、−Ｏ−、−ＣＯ−および−ＣＯＯ−）のいずれかを二つ以上有する化合物も溶媒として用いることができ、たとえばアルコール性水酸基のような他の官能基を同時に有していてもよい。二種類以上の官能基を有する溶媒の場合、その炭素原子数はいずれかの官能基を有する化合物の規定範囲内であればよい。炭素原子数が３〜１２のエステル類の例には、エチルホルメート、プロピルホルメート、ペンチルホルメート、メチルアセテート、エチルアセテートおよびペンチルアセテート等が挙げられる。炭素原子数が３〜１２のケトン類の例には、アセトン、メチルエチルケトン、ジエチルケトン、ジイソブチルケトン、シクロペンタノン、シクロヘキサノンおよびメチルシクロヘキサノン等が挙げられる。炭素原子数が３〜１２のエーテル類の例には、ジイソプロピルエーテル、ジメトキシメタン、ジメトキシエタン、１，４−ジオキサン、１，３−ジオキソラン、テトラヒドロフラン、アニソールおよびフェネトール等が挙げられる。二種類以上の官能基を有する有機溶媒の例には、２−エトキシエチルアセテート、２−メトキシエタノールおよび２−ブトキシエタノール等が挙げられる。
Next, the organic solvent in which the cellulose acylate according to the present invention is dissolved will be described.
In the present invention, as the organic solvent, any of a chlorinated solvent containing a chlorinated organic solvent as a main solvent and a non-chlorinated solvent not containing a chlorinated organic solvent can be used.
(Chlorine solvent)
In preparing the cellulose acylate solution according to the present invention, a chlorinated organic solvent is preferably used as the main solvent. In the present invention, the type of the chlorinated organic solvent is not particularly limited as long as the object can be achieved within a range where the cellulose acylate can be dissolved, cast and formed. These chlorinated organic solvents are preferably dichloromethane and chloroform. Particularly preferred is dichloromethane. In addition, there is no particular problem in mixing an organic solvent other than the chlorinated organic solvent. In that case, it is necessary to use at least 50% by mass of dichloromethane in the total amount of the organic solvent. Other organic solvents used in combination with the chlorinated organic solvent in the present invention will be described below. That is, as another preferable organic solvent, a solvent selected from esters, ketones, ethers, alcohols, hydrocarbons and the like having 3 to 12 carbon atoms is preferable. Esters, ketones, ethers and alcohols may have a cyclic structure. A compound having two or more functional groups of esters, ketones and ethers (that is, —O—, —CO— and —COO—) can also be used as a solvent. For example, other functional groups such as alcoholic hydroxyl groups can be used. You may have group simultaneously. In the case of a solvent having two or more types of functional groups, the number of carbon atoms may be within the specified range of the compound having any functional group. Examples of esters having 3 to 12 carbon atoms include ethyl formate, propyl formate, pentyl formate, methyl acetate, ethyl acetate and pentyl acetate. Examples of ketones having 3 to 12 carbon atoms include acetone, methyl ethyl ketone, diethyl ketone, diisobutyl ketone, cyclopentanone, cyclohexanone and methylcyclohexanone. Examples of ethers having 3 to 12 carbon atoms include diisopropyl ether, dimethoxymethane, dimethoxyethane, 1,4-dioxane, 1,3-dioxolane, tetrahydrofuran, anisole and phenetole. Examples of the organic solvent having two or more kinds of functional groups include 2-ethoxyethyl acetate, 2-methoxyethanol and 2-butoxyethanol.
また塩素系有機溶媒と併用されるアルコールとしては、好ましくは直鎖であっても分枝を有していても環状であってもよく、その中でも飽和脂肪族炭化水素であることが好ましい。アルコールの水酸基は、第一級〜第三級のいずれであってもよい。アルコールの例には、メタノール、エタノール、１−プロパノール、２−プロパノール、１−ブタノール、２−ブタノール、ｔ−ブタノール、１−ペンタノール、２−メチル−２−ブタノールおよびシクロヘキサノールが含まれる。なおアルコールとしては、フッ素系アルコールも用いられる。例えば、２−フルオロエタノール、２，２，２−トリフルオロエタノール、２，２，３，３−テトラフルオロ−１−プロパノールなども挙げられる。さらに炭化水素は、直鎖であっても分岐を有していても環状であってもよい。芳香族炭化水素と脂肪族炭化水素のいずれも用いることができる。脂肪族炭化水素は、飽和であっても不飽和であってもよい。炭化水素の例には、シクロヘキサン、ヘキサン、ベンゼン、トルエンおよびキシレンが含まれる。
塩素系有機溶媒と他の有機溶媒との組合せ例としては以下の組成を挙げることができるが、これらに限定されるものではない。
The alcohol used in combination with the chlorinated organic solvent may be linear, branched or cyclic, and among them, saturated aliphatic hydrocarbon is preferable. The hydroxyl group of the alcohol may be any of primary to tertiary. Examples of the alcohol include methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, t-butanol, 1-pentanol, 2-methyl-2-butanol and cyclohexanol. As the alcohol, fluorine-based alcohol is also used. Examples thereof include 2-fluoroethanol, 2,2,2-trifluoroethanol, 2,2,3,3-tetrafluoro-1-propanol and the like. Furthermore, the hydrocarbon may be linear, branched or cyclic. Either aromatic hydrocarbons or aliphatic hydrocarbons can be used. The aliphatic hydrocarbon may be saturated or unsaturated. Examples of hydrocarbons include cyclohexane, hexane, benzene, toluene and xylene.
Examples of combinations of chlorinated organic solvents and other organic solvents include the following compositions, but are not limited thereto.
・ジクロロメタン／メタノール／エタノール／ブタノール（８０／１０／５／５、質量部）、
・ジクロロメタン／アセトン／メタノール／プロパノール（８０／１０／５／５、質量部）、
・ジクロロメタン／メタノール／ブタノール／シクロヘキサン（８０／１０／５／５、質量部）、
・ジクロロメタン／メチルエチルケトン／メタノール／ブタノール（８０／１０／５／５、質量部）、
・ジクロロメタン／アセトン／メチルエチルケトン／エタノール／イソプロパノール（７５／８／５／５／７、質量部）
・ジクロロメタン／シクロペンタノン／メタノール／イソプロパノール（８０／７／５／８、質量部）
・ジクロロメタン／酢酸メチル／ブタノール（８０／１０／１０、質量部）、
・ジクロロメタン／シクロヘキサノン／メタノール／ヘキサン（７０／２０／５／５、質量部）、
・ジクロロメタン／メチルエチルケトン／アセトン／メタノール／エタノール（５０／２０／２０／５／５、質量部）、
・ジクロロメタン／１、３ジオキソラン／メタノール／エタノール（７０／２０／５／５、質量部）、
・ジクロロメタン／ジオキサン／アセトン／メタノール／エタノール（６０／２０／１０／５／５、質量部）、
・ジクロロメタン／アセトン／シクロペンタノン／エタノール／イソブタノール／シクロヘキサン（６５／１０／１０／５／５／５、質量部）、
・ジクロロメタン／メチルエチルケトン／アセトン／メタノール／エタノール（７０／１０／１０／５／５、質量部）、
・ジクロロメタン／アセトン／酢酸エチル／エタノール／ブタノール／ヘキサン（６５／１０／１０／５／５／５、質量部）、
・ジクロロメタン／アセト酢酸メチル／メタノール／エタノール（６５／２０／１０／５、質量部）、
・ジクロロメタン／シクロペンタノン／エタノール／ブタノール（６５／２０／１０／５、質量部）、
などを挙げることができる。
Dichloromethane / methanol / ethanol / butanol (80/10/5/5, parts by mass),
Dichloromethane / acetone / methanol / propanol (80/10/5/5, parts by mass),
Dichloromethane / methanol / butanol / cyclohexane (80/10/5/5, parts by mass),
Dichloromethane / methyl ethyl ketone / methanol / butanol (80/10/5/5, parts by mass),
・ Dichloromethane / acetone / methyl ethyl ketone / ethanol / isopropanol (75/8/5/5/7, parts by mass)
・ Dichloromethane / cyclopentanone / methanol / isopropanol (80/7/5/8, part by mass)
Dichloromethane / methyl acetate / butanol (80/10/10, parts by mass),
Dichloromethane / cyclohexanone / methanol / hexane (70/20/5/5, parts by mass)
Dichloromethane / methyl ethyl ketone / acetone / methanol / ethanol (50/20/20/5/5, parts by mass),
Dichloromethane / 1, 3 dioxolane / methanol / ethanol (70/20/5/5, parts by mass),
Dichloromethane / dioxane / acetone / methanol / ethanol (60/20/10/5/5, parts by mass),
Dichloromethane / acetone / cyclopentanone / ethanol / isobutanol / cyclohexane (65/10/10/5/5/5, parts by mass)
Dichloromethane / methyl ethyl ketone / acetone / methanol / ethanol (70/10/10/5/5, parts by mass),
Dichloromethane / acetone / ethyl acetate / ethanol / butanol / hexane (65/10/10/5/5/5, parts by mass),
Dichloromethane / methyl acetoacetate / methanol / ethanol (65/20/10/5, parts by mass),
Dichloromethane / cyclopentanone / ethanol / butanol (65/20/10/5, parts by mass),
And so on.
（非塩素系溶媒）
次に、本発明に関するセルロースアシレートの溶液を作製するに際して好ましく用いられる非塩素系有機溶媒について記載する。本発明においては、セルロースアシレートが溶解し流延，製膜できる範囲において、その目的が達成できる限りは非塩素系有機溶媒は特に限定されない。本発明で用いられる非塩素系有機溶媒は、炭素原子数が３〜１２のエステル、ケトン、エーテルから選ばれる溶媒が好ましい。エステル、ケトンおよび、エーテルは、環状構造を有していてもよい。エステル、ケトンおよびエーテルの官能基（すなわち、−Ｏ−、−ＣＯ−および−ＣＯＯ−）のいずれかを２つ以上有する化合物も、主溶媒として用いることができ、たとえばアルコール性水酸基のような他の官能基を有していてもよい。２種類以上の官能基を有する主溶媒の場合、その炭素原子数はいずれかの官能基を有する化合物の規定範囲内であればよい。炭素原子数が３〜１２のエステル類の例には、エチルホルメート、プロピルホルメート、ペンチルホルメート、メチルアセテート、エチルアセテートおよびペンチルアセテートが挙げられる。炭素原子数が３〜１２のケトン類の例には、アセトン、メチルエチルケトン、ジエチルケトン、ジイソブチルケトン、シクロペンタノン、シクロヘキサノンおよびメチルシクロヘキサノンが挙げられる。炭素原子数が３〜１２のエーテル類の例には、ジイソプロピルエーテル、ジメトキシメタン、ジメトキシエタン、１，４−ジオキサン、１，３−ジオキソラン、テトラヒドロフラン、アニソールおよびフェネトールが挙げられる。二種類以上の官能基を有する有機溶媒の例には、２−エトキシエチルアセテート、２−メトキシエタノールおよび２−ブトキシエタノールが挙げられる。
(Non-chlorine solvent)
Next, a non-chlorine organic solvent that is preferably used in preparing a cellulose acylate solution according to the present invention will be described. In the present invention, the non-chlorine organic solvent is not particularly limited as long as the object can be achieved as long as the cellulose acylate can be dissolved and cast and formed into a film. The non-chlorine organic solvent used in the present invention is preferably a solvent selected from esters, ketones and ethers having 3 to 12 carbon atoms. Esters, ketones and ethers may have a cyclic structure. A compound having two or more functional groups of esters, ketones and ethers (that is, —O—, —CO—, and —COO—) can also be used as a main solvent, such as an alcoholic hydroxyl group. It may have a functional group of In the case of the main solvent having two or more kinds of functional groups, the number of carbon atoms may be within the specified range of the compound having any functional group. Examples of esters having 3 to 12 carbon atoms include ethyl formate, propyl formate, pentyl formate, methyl acetate, ethyl acetate and pentyl acetate. Examples of ketones having 3 to 12 carbon atoms include acetone, methyl ethyl ketone, diethyl ketone, diisobutyl ketone, cyclopentanone, cyclohexanone and methylcyclohexanone. Examples of ethers having 3 to 12 carbon atoms include diisopropyl ether, dimethoxymethane, dimethoxyethane, 1,4-dioxane, 1,3-dioxolane, tetrahydrofuran, anisole and phenetole. Examples of the organic solvent having two or more kinds of functional groups include 2-ethoxyethyl acetate, 2-methoxyethanol and 2-butoxyethanol.
以上のセルロースアシレートに用いられる非塩素系有機溶媒については、前述のいろいろな観点から選定されるが、好ましくは以下のとおりである。すなわち、非塩素系溶媒としては、前記非塩素系有機溶媒を主溶媒とする混合溶媒が好ましく、互いに異なる３種類以上の溶媒の混合溶媒であって、第１の溶媒が酢酸メチル、酢酸エチル、蟻酸メチル、蟻酸エチル、アセトン、ジオキソラン、ジオキサンから選ばれる少なくとも一種あるいは或いはそれらの混合液であり、第２の溶媒が炭素原子数が４〜７のケトン類またはアセト酢酸エステルから選ばれ、第３の溶媒として炭素数が１〜１０のアルコールまたは炭化水素、より好ましくは炭素数１〜８のアルコールから選ばれる、混合溶媒である。なお第１の溶媒が、２種以上の溶媒の混合液である場合は、第２の溶媒がなくてもよい。第１の溶媒は、さらに好ましくは酢酸メチル、アセトン、蟻酸メチル、蟻酸エチルあるいはこれらの混合物であり、第２の溶媒は、メチルエチルケトン、シクロペンタノン、シクロヘキサノン、アセチル酢酸メチルが好ましく、これらの混合溶媒であってもよい。 The non-chlorine organic solvent used in the above cellulose acylate is selected from the various viewpoints described above, and is preferably as follows. That is, the non-chlorine solvent is preferably a mixed solvent containing the non-chlorine organic solvent as a main solvent, and is a mixed solvent of three or more different solvents, wherein the first solvent is methyl acetate, ethyl acetate, At least one selected from methyl formate, ethyl formate, acetone, dioxolane, and dioxane, or a mixture thereof; the second solvent is selected from ketones having 4 to 7 carbon atoms or acetoacetate; The solvent is a mixed solvent selected from alcohols or hydrocarbons having 1 to 10 carbon atoms, more preferably alcohols having 1 to 8 carbon atoms. Note that when the first solvent is a mixed liquid of two or more kinds of solvents, the second solvent may be omitted. The first solvent is more preferably methyl acetate, acetone, methyl formate, ethyl formate, or a mixture thereof, and the second solvent is preferably methyl ethyl ketone, cyclopentanone, cyclohexanone, methyl acetyl acetate, or a mixed solvent thereof. It may be.
第３の溶媒であるアルコールは、直鎖であっても分枝を有していても環状であってもよく、その中でも飽和脂肪族炭化水素であることが好ましい。アルコールの水酸基は、第一級〜第三級のいずれであってもよい。アルコールの例には、メタノール、エタノール、１−プロパノール、２−プロパノール、１−ブタノール、２−ブタノール、ｔ−ブタノール、１−ペンタノール、２−メチル−２−ブタノールおよびシクロヘキサノールが含まれる。なおアルコールとしては、フッ素系アルコールも用いられる。例えば、２−フルオロエタノール、２，２，２−トリフルオロエタノール、２，２，３，３−テトラフルオロ−１−プロパノールなども挙げられる。さらに炭化水素は、直鎖であっても分岐を有していても環状であってもよい。芳香族炭化水素と脂肪族炭化水素のいずれも用いることができる。脂肪族炭化水素は、飽和であっても不飽和であってもよい。炭化水素の例には、シクロヘキサン、ヘキサン、ベンゼン、トルエンおよびキシレンが含まれる。これらの第３の溶媒であるアルコールおよび炭化水素は単独でもよいし２種類以上の混合物でもよく特に限定されない。第３の溶媒としては、好ましい具体的化合物は、アルコールとしてはメタノール、エタノール、１−プロパノール、２−プロパノール、１−ブタノール、２−ブタノール、およびシクロヘキサノール、シクロヘキサン、ヘキサンを挙げることができ、特にはメタノール、エタノール、１−プロパノール、２−プロパノール、１−ブタノールである。 The alcohol as the third solvent may be linear, branched or cyclic, and is preferably a saturated aliphatic hydrocarbon. The hydroxyl group of the alcohol may be any of primary to tertiary. Examples of the alcohol include methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, t-butanol, 1-pentanol, 2-methyl-2-butanol and cyclohexanol. As the alcohol, fluorine-based alcohol is also used. Examples thereof include 2-fluoroethanol, 2,2,2-trifluoroethanol, 2,2,3,3-tetrafluoro-1-propanol and the like. Furthermore, the hydrocarbon may be linear, branched or cyclic. Either aromatic hydrocarbons or aliphatic hydrocarbons can be used. The aliphatic hydrocarbon may be saturated or unsaturated. Examples of hydrocarbons include cyclohexane, hexane, benzene, toluene and xylene. These alcohols and hydrocarbons as the third solvent may be used alone or in combination of two or more, and are not particularly limited. As the third solvent, preferred specific compounds include alcohol, methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, and cyclohexanol, cyclohexane, hexane, Are methanol, ethanol, 1-propanol, 2-propanol, 1-butanol.
以上の３種類の混合溶媒の混合割合は、混合溶媒全体量中、第１の溶媒が２０〜９５質量％、第２の溶媒が２〜６０質量％さらに第３の溶媒が２〜３０質量％の比率で含まれることが好ましく、さらに第１の溶媒が３０〜９０質量％であり、第２の溶媒が３〜５０質量％、さらに第３のアルコールが３〜２５質量％含まれることが好ましい。また特に第１の溶媒が３０〜９０質量％であり、第２の溶媒が３〜３０質量％、第３の溶媒がアルコールであり３〜１５質量％含まれることが好ましい。以上の本発明で用いられる非塩素系有機溶媒は、さらに詳細には発明協会公開技報公技番号２００１−１７４５号（２００１年３月１５日発行、発明協会）ｐ．１２−１６に詳細に記載されている。本発明の好ましい非塩素系有機溶媒の組合せは以下挙げることができるが、これらに限定されるものではない。 The mixing ratio of the above three types of mixed solvents is 20 to 95% by mass for the first solvent, 2 to 60% by mass for the second solvent, and 2 to 30% by mass for the third solvent in the total amount of the mixed solvent. The first solvent is preferably 30 to 90% by mass, the second solvent is 3 to 50% by mass, and the third alcohol is preferably 3 to 25% by mass. . In particular, it is preferable that the first solvent is 30 to 90% by mass, the second solvent is 3 to 30% by mass, and the third solvent is alcohol and 3 to 15% by mass. The non-chlorine-based organic solvent used in the present invention described above is more specifically described in JIII Journal of Technical Disclosure No. 2001-1745 (issued March 15, 2001, Invention Association) p. 12-16. Preferred combinations of non-chlorine organic solvents of the present invention can include the following, but are not limited thereto.
・酢酸メチル／アセトン／メタノール／エタノール／ブタノール（７５／１０／５／５／５、質量部）、
・酢酸メチル／アセトン／メタノール／エタノール／プロパノール（７５／１０／５／５／５、質量部）、
・酢酸メチル／アセトン／メタノール／ブタノール／シクロヘキサン（７５／１０／５／５／５、質量部）、
・酢酸メチル／アセトン／エタノール／ブタノール（８１／８／７／４、質量部）
・酢酸メチル／アセトン／エタノール／ブタノール（８２／１０／４／４、質量部）
・酢酸メチル／アセトン／エタノール／ブタノール（８０／１０／４／６、質量部）
・酢酸メチル／メチルエチルケトン／メタノール／ブタノール（８０／１０／５／５、質量部）、
・酢酸メチル／アセトン／メチルエチルケトン／エタノール／イソプロパノール（７５／８／５／５／７、質量部）、
・酢酸メチル／シクロペンタノン／メタノール／イソプロパノール（８０／７／５／８、質量部）、
・酢酸メチル／アセトン／ブタノール（８５／１０／５、質量部）、
・酢酸メチル／シクロペンタノン／アセトン／メタノール／ブタノール（６０／１５／１４／５／６、質量部）、
・酢酸メチル／シクロヘキサノン／メタノール／ヘキサン（７０／２０／５／５、質量部）、
・酢酸メチル／メチルエチルケトン／アセトン／メタノール／エタノール（５０／２０／２０／５／５、質量部）、
・酢酸メチル／１、３−ジオキソラン／メタノール／エタノール（７０／２０／５／５、質量部）、
・酢酸メチル／ジオキサン／アセトン／メタノール／エタノール（６０／２０／１０／５／５、質量部）、
・酢酸メチル／アセトン／シクロペンタノン／エタノール／イソブタノール／シクロヘキサン（６５／１０／１０／５／５／５、質量部）、
-Methyl acetate / acetone / methanol / ethanol / butanol (75/10/5/5/5, parts by mass),
-Methyl acetate / acetone / methanol / ethanol / propanol (75/10/5/5/5, parts by mass),
Methyl acetate / acetone / methanol / butanol / cyclohexane (75/10/5/5/5, parts by mass),
・ Methyl acetate / acetone / ethanol / butanol (81/8/7/4, parts by mass)
・ Methyl acetate / acetone / ethanol / butanol (82/10/4/4, parts by mass)
・ Methyl acetate / acetone / ethanol / butanol (80/10/4/6, part by mass)
Methyl acetate / methyl ethyl ketone / methanol / butanol (80/10/5/5, parts by mass),
-Methyl acetate / acetone / methyl ethyl ketone / ethanol / isopropanol (75/8/5/5/7, parts by mass)
Methyl acetate / cyclopentanone / methanol / isopropanol (80/7/5/8, parts by mass),
Methyl acetate / acetone / butanol (85/10/5, parts by mass),
Methyl acetate / cyclopentanone / acetone / methanol / butanol (60/15/14/5/6, parts by mass),
-Methyl acetate / cyclohexanone / methanol / hexane (70/20/5/5, parts by mass)
Methyl acetate / methyl ethyl ketone / acetone / methanol / ethanol (50/20/20/5/5, parts by mass),
Methyl acetate / 1,3-dioxolane / methanol / ethanol (70/20/5/5, parts by mass),
Methyl acetate / dioxane / acetone / methanol / ethanol (60/20/10/5/5, parts by mass),
Methyl acetate / acetone / cyclopentanone / ethanol / isobutanol / cyclohexane (65/10/10/5/5/5, parts by mass),
・ギ酸メチル／メチルエチルケトン／アセトン／メタノール／エタノール（５０／２０／２０／５／５、質量部）、
・ギ酸メチル／アセトン／酢酸エチル／エタノール／ブタノール／ヘキサン（６５／１０／１０／５／５／５、質量部）、
・アセトン／アセト酢酸メチル／メタノール／エタノール（６５／２０／１０／５、質量部）、
・アセトン／シクロペンタノン／エタノール／ブタノール（６５／２０／１０／５、質量部）、
・アセトン／１，３−ジオキソラン／エタノール／ブタノール（６５／２０／１０／５、質量部）、
・１、３−ジオキソラン／シクロヘキサノン／メチルエチルケトン／メタノール／ブタノール（５５／２０／１０／５／５／５、質量部）
などをあげることができる。
更に下記の方法で調整したセルロースアシレート溶液を用いることもできる。
・酢酸メチル／アセトン／エタノール／ブタノール（８１／８／７／４、質量部）でセルロースアシレート溶液を作製しろ過・濃縮後に２質量部のブタノールを追加添加する方法
・酢酸メチル／アセトン／エタノール／ブタノール（８４／１０／４／２、質量部）でセルロースアシレート溶液を作製しろ過・濃縮後に４質量部のブタノールを追加添加する方法
・酢酸メチル／アセトン／エタノール（８４／１０／６、質量部）でセルロースアシレート溶液を作製しろ過・濃縮後に５質量部のブタノールを追加添加する方法
本発明に用いるドープには、上記本発明の非塩素系有機溶媒以外に、ジクロロメタンを本発明の全有機溶媒量の１０質量％以下含有させてもよい。
Methyl formate / methyl ethyl ketone / acetone / methanol / ethanol (50/20/20/5/5, parts by mass),
-Methyl formate / acetone / ethyl acetate / ethanol / butanol / hexane (65/10/10/5/5/5, parts by mass)
Acetone / methyl acetoacetate / methanol / ethanol (65/20/10/5, parts by mass)
Acetone / cyclopentanone / ethanol / butanol (65/20/10/5, parts by mass)
Acetone / 1,3-dioxolane / ethanol / butanol (65/20/10/5, parts by mass)
1,3-dioxolane / cyclohexanone / methyl ethyl ketone / methanol / butanol (55/20/10/5/5/5, parts by mass)
Etc.
Further, a cellulose acylate solution prepared by the following method can also be used.
A method of preparing a cellulose acylate solution with methyl acetate / acetone / ethanol / butanol (81/8/7/4, parts by mass), adding 2 parts by weight of butanol after filtration and concentration, and methyl acetate / acetone / ethanol / Butanol (84/10/4/2, parts by mass) A method for adding a cellulose acylate solution after filtration and concentration, and adding 4 parts by mass of butanol after addition. Methyl acetate / acetone / ethanol (84/10/6, In addition to the above non-chlorine organic solvent of the present invention, dichloromethane is added to the dope used in the present invention. You may make it contain 10 mass% or less of the total amount of organic solvents.
（セルロースアシレート溶液特性）
セルロースアシレートの溶液は、前記有機溶媒にセルロースアシレートを１０〜３０質量％の濃度で溶解させた溶液であるのが製膜流延適性の点で好ましく、より好ましくは１３〜２７質量％であり、特に好ましくは１５〜２５質量％である。これらの濃度にセルロースアシレートを実施する方法は、溶解する段階で所定の濃度になるように実施してもよく、また予め低濃度溶液（例えば９〜１４質量％）として作製した後に後述する濃縮工程で所定の高濃度溶液に調整してもよい。さらに、予め高濃度のセルロースアシレート溶液とした後に、種々の添加物を添加することで所定の低濃度のセルロースアシレート溶液としてもよく、いずれの方法でも本発明に関するセルロースアシレート溶液濃度になるように実施されれば特に問題ない。
(Characteristics of cellulose acylate solution)
The cellulose acylate solution is preferably a solution obtained by dissolving cellulose acylate in the organic solvent at a concentration of 10 to 30% by mass from the viewpoint of film forming casting suitability, and more preferably 13 to 27% by mass. It is particularly preferably 15 to 25% by mass. The method for carrying out the cellulose acylate at these concentrations may be carried out so as to obtain a predetermined concentration at the stage of dissolution, or it is prepared as a low-concentration solution (for example, 9 to 14% by mass) and then concentrated as described later You may adjust to a predetermined high concentration solution by a process. Furthermore, after making a cellulose acylate solution with a high concentration in advance, various additives may be added to obtain a predetermined cellulose acylate solution with a low concentration, and any method makes the cellulose acylate solution concentration of the present invention. If implemented, there is no particular problem.
次に、本発明ではセルロースアシレート溶液を同一組成の有機溶媒で０．１〜５質量％にした希釈溶液中のセルロースアシレートの会合体分子量が１５万〜１５００万であることが、剥ぎ取り性を良くする点で好ましい。さらに好ましくは、会合分子量が１８万〜９００万である。この会合分子量は静的光散乱法で求めることができる。その際に同時に求められる慣性自乗半径は１０〜２００ｎｍになるように溶解することが好ましい。さらに好ましい慣性自乗半径は２０〜２００ｎｍである。更にまた、第２ビリアル係数が−２×１０-4〜＋４×１０-4となるように溶解することが好ましく、より好ましくは第２ビリアル係数が−２×１０-4〜＋２×１０-4である。 Next, in the present invention, it is stripped that the aggregate molecular weight of cellulose acylate in a diluted solution in which the cellulose acylate solution is 0.1 to 5% by mass with an organic solvent having the same composition is 150,000 to 15 million. It is preferable in terms of improving the properties. More preferably, the associated molecular weight is 180,000 to 9 million. This associated molecular weight can be determined by a static light scattering method. In that case, it is preferable to dissolve so that the inertial square radius required at the same time is 10 to 200 nm. A more preferable inertial square radius is 20 to 200 nm. Furthermore, it is preferable to dissolve so that the second virial coefficient is −2 × 10 −4 to + 4 × 10 −4, and more preferably, the second virial coefficient is −2 × 10 −4 to + 2 × 10 −4. It is.
ここで、本発明での会合分子量、さらに慣性自乗半径および第２ビリアル係数の定義について述べる。これらは下記方法に従って、静的光散乱法を用いて測定する。測定は装置の都合上希薄領域で測定するが、これらの測定値は本発明の高濃度域でのドープの挙動を反映するものである。
まず、セルロースアシレートをドープに使用する溶剤に溶かし、０．１質量％、０．２質量％、０．３質量％、０．４質量％の溶液を調製する。なお、秤量は吸湿を防ぐためセルロースアシレートは１２０℃で２時間乾燥したものを用い、２５℃，１０％ＲＨで行う。溶解方法は、ドープ溶解時に採用した方法（常温溶解法、冷却溶解法、高温溶解法）に従って実施する。続いてこれらの溶液、および溶剤を０．２μｍのテフロン製フィルターで濾過する。そして、ろ過した溶液を静的光散乱を、光散乱測定装置（大塚電子（株）製ＤＬＳ−７００）を用い、２５℃に於いて３０度から１４０度まで１０度間隔で測定する。得られたデータをＢＥＲＲＹプロット法にて解析する。なお、この解析に必要な屈折率はアッベ屈折系で求めた溶剤の値を用い、屈折率の濃度勾配（ｄｎ／ｄｃ）は、示差屈折計（大塚電子（株）製ＤＲＭ−１０２１）を用い、光散乱測定に用いた溶剤、溶液を用いて測定する。
Here, the definition of the association molecular weight, the inertial square radius, and the second virial coefficient in the present invention will be described. These are measured using the static light scattering method according to the following method. Although the measurement is performed in a dilute region for the convenience of the apparatus, these measured values reflect the behavior of the dope in the high concentration region of the present invention.
First, cellulose acylate is dissolved in a solvent used for the dope to prepare 0.1 mass%, 0.2 mass%, 0.3 mass%, and 0.4 mass% solutions. In order to prevent moisture absorption, the cellulose acylate is dried at 120 ° C. for 2 hours and is measured at 25 ° C. and 10% RH. The dissolution method is carried out according to the method employed at the time of dope dissolution (room temperature dissolution method, cooling dissolution method, high temperature dissolution method). Subsequently, these solutions and the solvent are filtered through a 0.2 μm Teflon filter. Then, the static light scattering of the filtered solution is measured at an interval of 10 ° from 30 ° to 140 ° at 25 ° C. using a light scattering measuring device (DLS-700 manufactured by Otsuka Electronics Co., Ltd.). The obtained data is analyzed by the BERRY plot method. In addition, the refractive index required for this analysis uses the value of the solvent calculated | required with the Abbe refractive system, and the refractive index concentration gradient (dn / dc) uses the differential refractometer (Otsuka Electronics Co., Ltd. DRM-1021). Measure using the solvent and solution used for light scattering measurement.
（ドープ調製）
次にセルロースアシレート溶液（ドープ）の調製について述べる。セルロースアシレートの溶解方法は特に限定されず、室温でもよくさらには冷却溶解法あるいは高温溶解方法、さらにはこれらの組み合わせで実施される。これらに関しては、例えば特開平５−１６３３０１号、特開昭６１−１０６６２８号、特開昭５８−１２７７３７号、特開平９−９５５４４号、特開平１０−９５８５４号、特開平１０−４５９５０号、特開２０００−５３７８４号、特開平１１−３２２９４６号、さらに特開平１１−３２２９４７号、特開平２−２７６８３０号、特開２０００−２７３２３９号、特開平１１−７１４６３号、特開平０４−２５９５１１号、特開２０００−２７３１８４号、特開平１１−３２３０１７号、特開平１１−３０２３８８号各公報などにセルロースアシレート溶液の調製法が記載されている。以上記載したこれらのセルロースアシレートの有機溶媒への溶解方法は、本発明においても適宜本発明の範囲であればこれらの技術を適用できるものである。これらの詳細は、特に非塩素系溶媒系については発明協会公開技報公技番号２００１−１７４５号（２００１年３月１５日発行、発明協会）ｐ．２２−２５に詳細に記載されている方法で実施される。さらに本発明に関するセルロースアシレートのドープ溶液は、溶液濃縮，ろ過が通常実施され、同様に発明協会公開技報公技番号２００１−１７４５号（２００１年３月１５日発行、発明協会）ｐ．２５に詳細に記載されている。なお、高温度で溶解する場合は、使用する有機溶媒の沸点以上の場合がほとんどであり、その場合は加圧状態で用いられる。
(Dope preparation)
Next, preparation of a cellulose acylate solution (dope) will be described. The method for dissolving cellulose acylate is not particularly limited, and may be room temperature, and further, a cooling dissolution method or a high temperature dissolution method, and further a combination thereof. With respect to these, for example, JP-A-5-163301, JP-A-61-106628, JP-A-58-127737, JP-A-9-95544, JP-A-10-95854, JP-A-10-45950, JP 2000-53784, JP 11-322946, JP 11-322947, JP 2-276830, JP 2000-273239, JP 11-71463, JP 04-259511, Special JP-A-2000-273184, JP-A-11-323017, JP-A-11-302388, etc. describe methods for preparing a cellulose acylate solution. The above-described method for dissolving cellulose acylate in an organic solvent is applicable to the present invention as long as it is within the scope of the present invention. For details of these, particularly for non-chlorine-based solvent systems, the Japan Society for Invention and Innovation Publication No. 2001-1745 (issued March 15, 2001, Japan Society for Invention) p. It is carried out in the manner described in detail in 22-25. Further, the cellulose acylate dope solution according to the present invention is usually subjected to solution concentration and filtration. Similarly, the Japan Society for Invention and Innovation Technical Report No. 2001-1745 (issued March 15, 2001, Invention Association) p. 25 in detail. In addition, when it melt | dissolves at high temperature, it is the case where it is more than the boiling point of the organic solvent to be used, and in that case, it uses in a pressurized state.
セルロースアシレート溶液は、その溶液の粘度と動的貯蔵弾性率が以下に述べる範囲であることが、流延しやすく好ましい。試料溶液１ｍＬをレオメーター（ＣＬＳ ５００）に直径 ４ｃｍ／２°のSteel Cone（共にTA Instruments社製）を用いて測定する。測定条件はOscillation Step/Temperature Rampで ４０℃〜−１０℃の範囲を２℃／分で可変して測定し、４０℃の静的非ニュートン粘度 ｎ*（Ｐａ・ｓ）および−５℃の貯蔵弾性率Ｇ’（Ｐａ）を求める。尚、試料溶液は予め測定開始温度にて液温一定となるまで保温した後に測定を開始する。本発明では、４０℃での粘度が１〜４００Ｐａ・ｓであり、１５℃での動的貯蔵弾性率が５００Ｐａ以上であるのが好ましく、より好ましくは４０℃での粘度が１０〜２００Ｐａ・ｓで、１５℃での動的貯蔵弾性率が１００〜１００万である。さらには低温での動的貯蔵弾性率が大きいほど好ましく、例えば流延支持体が−５℃の場合は動的貯蔵弾性率が−５℃で１万〜１００万Ｐａであることが好ましく、支持体が−５０℃の場合は−５０℃での動的貯蔵弾性率が１万〜５００万Ｐａが好ましい。 It is preferable that the cellulose acylate solution has a viscosity and a dynamic storage elastic modulus within the ranges described below because it is easy to cast. 1 mL of the sample solution is measured with a rheometer (CLS 500) using a Steel Cone having a diameter of 4 cm / 2 ° (both manufactured by TA Instruments). Measurement conditions were measured by varying at 2 ° C. / min range of 40 ℃ ~-10 ℃ in Oscillation Step / Temperature Ramp, static non-Newtonian viscosity of 40 ℃ n * (Pa · s ) and storage of -5 ° C. The elastic modulus G ′ (Pa) is obtained. The sample solution is preliminarily kept at the measurement start temperature until the liquid temperature becomes constant, and then the measurement is started. In the present invention, the viscosity at 40 ° C. is 1 to 400 Pa · s, the dynamic storage elastic modulus at 15 ° C. is preferably 500 Pa or more, and more preferably the viscosity at 40 ° C. is 10 to 200 Pa · s. Thus, the dynamic storage elastic modulus at 15 ° C. is 1,000 to 1,000,000. Furthermore, it is preferable that the dynamic storage elastic modulus at low temperature is larger. For example, when the casting support is −5 ° C., the dynamic storage elastic modulus is preferably 10,000 to 1,000,000 Pa at −5 ° C. When the body is at −50 ° C., the dynamic storage elastic modulus at −50 ° C. is preferably 10,000 to 5 million Pa.
本発明においては、前述の特定のセルロースアシレートを用いているので、高濃度のドープが得られるのが特徴であり、濃縮という手段に頼らずとも高濃度でしかも安定性の優れたセルロースアシレート溶液が得られる。更に溶解し易くするために低い濃度で溶解してから、濃縮手段を用いて濃縮してもよい。濃縮の方法としては、特に限定するものはないが、例えば、低濃度溶液を筒体とその内部の周方向に回転する回転羽根外周の回転軌跡との間に導くとともに、溶液との間に温度差を与えて溶媒を蒸発させながら高濃度溶液を得る方法（例えば、特開平４−２５９５１１号公報等）、加熱した低濃度溶液をノズルから容器内に吹き込み、溶液をノズルから容器内壁に当たるまでの間で溶媒をフラッシュ蒸発させるとともに、溶媒蒸気を容器から抜き出し、高濃度溶液を容器底から抜き出す方法（例えば、米国特許第２，５４１，０１２号、米国特許第２，８５８，２２９号、米国特許第４，４１４，３４１号、米国特許第４，５０４，３５５号各明細書等などに記載の方法）等で実施できる。 In the present invention, since the above-mentioned specific cellulose acylate is used, it is characterized in that a high concentration dope is obtained, and a cellulose acylate having a high concentration and excellent stability without relying on a means of concentration. A solution is obtained. Furthermore, in order to make it easy to melt | dissolve, after making it melt | dissolve at a low density | concentration, you may concentrate using a concentration means. The concentration method is not particularly limited. For example, the low-concentration solution is guided between the cylindrical body and the rotation trajectory of the outer periphery of the rotating blade rotating in the circumferential direction, and the temperature between the solution and the solution. A method of obtaining a high-concentration solution while evaporating the solvent by giving a difference (for example, JP-A-4-259511), a heated low-concentration solution is blown into the container from the nozzle, and the solution is applied from the nozzle to the inner wall of the container In which the solvent is flash evaporated and the solvent vapor is withdrawn from the container and the concentrated solution is withdrawn from the bottom of the container (eg, US Pat. No. 2,541,012, US Pat. No. 2,858,229, US Pat. No. 4,414,341, US Pat. No. 4,504,355, etc.).
溶液は流延に先だって金網やネルなどの適当な濾材を用いて、未溶解物やゴミ、不純物などの異物を濾過除去しておくのが好ましい。セルロースアシレート溶液の濾過には絶対濾過精度が０．１〜１００μｍのフィルタを用いることが好ましく、さらには絶対濾過精度が０．５〜２５μｍであるフィルタを用いることが好ましい。フィルタの厚さは、０．１〜１０ｍｍが好ましく、更には０．２〜２ｍｍが好ましい。その場合、ろ過圧力は１．６ＭＰａ 以下が好ましく、より好ましくは１．２ＭＰａ以下、更には１．０ＭＰａ以下、特に０．２ＭＰａ以下で濾過することが好ましい。濾材としては、ガラス繊維、セルロース繊維、濾紙、四フッ化エチレン樹脂などのフッ素樹脂等の従来公知である材料を好ましく用いることができ、特にセラミックス、金属等が好ましく用いられる。セルロースアシレート溶液の製膜直前の粘度は、製膜の際に流延可能な範囲であればよく、通常１０Ｐａ・ｓ〜２０００Ｐａ・ｓの範囲に調製されることが好ましく、３０Ｐａ・ｓ〜１０００Ｐａ・ｓがより好ましく、４０Ｐａ・ｓ〜５００Ｐａ・ｓが更に好ましい。なお、この時の温度はその流延時の温度であれば特に限定されないが、好ましくは−５〜＋７０℃であり、より好ましくは−５〜＋５５℃である。 Prior to casting, it is preferable to filter off foreign matters such as undissolved matter, dust, and impurities using a suitable filter medium such as a wire mesh or flannel. For the filtration of the cellulose acylate solution, it is preferable to use a filter having an absolute filtration accuracy of 0.1 to 100 μm, and it is more preferable to use a filter having an absolute filtration accuracy of 0.5 to 25 μm. The thickness of the filter is preferably 0.1 to 10 mm, and more preferably 0.2 to 2 mm. In that case, the filtration pressure is 1.6 MPa. The following is preferable, more preferably 1.2 MPa or less, further 1.0 MPa or less, and particularly preferably 0.2 MPa or less. As the filter medium, conventionally known materials such as glass fibers, cellulose fibers, filter paper, fluororesins such as tetrafluoroethylene resin can be preferably used, and ceramics, metals and the like are particularly preferably used. The viscosity of the cellulose acylate solution immediately before film formation may be in a range that can be cast during film formation, and is usually preferably adjusted in the range of 10 Pa · s to 2000 Pa · s, and preferably 30 Pa · s to 1000 Pa. · S is more preferable, and 40 Pa · s to 500 Pa · s is more preferable. The temperature at this time is not particularly limited as long as it is the temperature at the time of casting, but is preferably −5 to + 70 ° C., more preferably −5 to + 55 ° C.
（製膜）
本発明に関するセルロースアシレートフィルムは、前記セルロースアシレート溶液を用いて製膜を行うことにより得ることができる。製膜方法及び設備は、従来セルローストリアセテートフィルム製造に供する溶液流延製膜方法及び溶液流延製膜装置が用いられる。溶解機（釜）から調製されたドープ（セルロースアシレート溶液）を貯蔵釜で一旦貯蔵し、ドープに含まれている泡を脱泡して最終調製をする。ドープをドープ排出口から、例えば回転数によって高精度に定量送液できる加圧型定量ギヤポンプを通して加圧型ダイに送り、ドープを加圧型ダイの口金（スリット）からエンドレスに走行している流延部の金属支持体の上に均一に流延され、金属支持体がほぼ一周した剥離点で、生乾きのドープ膜（ウェブとも呼ぶ）を金属支持体から剥離する。得られるウェブの両端をクリップで挟み、幅保持しながらテンターで搬送して乾燥し、続いて乾燥装置のロール群で搬送し乾燥を終了して巻き取り機で所定の長さに巻き取る。テンターとロール群の乾燥装置との組み合わせはその目的により変わる。電子ディスプレイ用機能性保護膜に用いる溶液流延製膜方法においては、溶液流延製膜装置の他に、下引層、帯電防止層、ハレーション防止層、保護層等のフィルムへの表面加工のために、塗布装置が付加されることが多い。以下に各製造工程について簡単に述べるが、これらに限定されるものではない。
(Film formation)
The cellulose acylate film according to the present invention can be obtained by forming a film using the cellulose acylate solution. As the film forming method and equipment, a solution casting film forming method and a solution casting film forming apparatus conventionally used for producing a cellulose triacetate film are used. The dope (cellulose acylate solution) prepared from the dissolving machine (kettle) is temporarily stored in a storage kettle, and the foam contained in the dope is defoamed for final preparation. The dope is sent from the dope discharge port to the pressure die through a pressure metering gear pump capable of delivering a constant amount of liquid with high accuracy, for example, by the number of rotations. The dry-dried dope film (also referred to as web) is peeled off from the metal support at a peeling point that is uniformly cast on the metal support and substantially rounds the metal support. Both ends of the obtained web are sandwiched between clips, transported by a tenter while keeping the width, dried, then transported by a roll group of a drying device, dried, and wound up to a predetermined length by a winder. The combination of the tenter and the roll group dryer varies depending on the purpose. In the solution casting film forming method used for the functional protective film for electronic displays, in addition to the solution casting film forming apparatus, surface processing on films such as an undercoat layer, an antistatic layer, an antihalation layer, a protective layer, etc. Therefore, a coating device is often added. Although each manufacturing process is described briefly below, it is not limited to these.
まず、調製したセルロースアシレート溶液（ドープ）は、ソルベントキャスト法によりセルロースアシレートフィルムを作製する際に、ドープをドラムまたはバンド上に流延し、溶媒を蒸発させてフィルムを形成する。流延前のドープは、固形分量が５〜４０質量％となるように濃度を調整することが好ましい。ドラムまたはバンドの表面は、鏡面状態に仕上げておくことが好ましい。ドープは、表面温度が３０℃以下のドラムまたはバンド上に流延することが好ましく用いられ、特には−１０〜２０℃の金属支持体温度であることが好ましい。さらに特開２０００−３０１５５５号、特開２０００−３０１５５８号、特開平０７−０３２３９１号、特開平０３−１９３３１６号、特開平０５−０８６２１２号、特開昭６２−０３７１１３号、特開平０２−２７６６０７号、特開昭５５−０１４２０１号、特開平０２−１１１５１１号、および特開平０２−２０８６５０号の各公報に記載の方法を本発明では用いることができる。 First, the prepared cellulose acylate solution (dope) is casted on a drum or band when a cellulose acylate film is produced by a solvent cast method, and the solvent is evaporated to form a film. It is preferable to adjust the concentration of the dope before casting so that the solid content is 5 to 40% by mass. The surface of the drum or band is preferably finished in a mirror state. The dope is preferably cast on a drum or band having a surface temperature of 30 ° C. or lower, and particularly preferably a metal support temperature of −10 to 20 ° C. Further, JP 2000-301555, JP 2000-301558, JP 07-032391, JP 03-193316, JP 05-086212, JP 62-037113, JP 02-276607. The methods described in JP-A Nos. 55-014201, 02-111511, and 02-208650 can be used in the present invention.
（重層流延）
セルロースアシレート溶液を、金属支持体としての平滑なバンド上或いはドラム上に単層液として流延してもよいし、２層以上の複数のセルロースアシレート液を流延してもよい。複数のセルロースアシレート溶液を流延する場合、金属支持体の進行方向に間隔を置いて設けた複数の流延口からセルロースアシレートを含む溶液をそれぞれ流延させて積層させながらフィルムを作製してもよく、例えば特開昭６１−１５８４１４号、特開平１−１２２４１９号、および特開平１１−１９８２８５号の各公報などに記載の方法が適応できる。また、２つの流延口からセルロースアシレート溶液を流延することによってフィルム化することでもよく、例えば特公昭６０−２７５６２号、特開昭６１−９４７２４号、特開昭６１−９４７２４５号、特開昭６１−１０４８１３号、特開昭６１−１５８４１３号、および特開平６−１３４９３３号の各公報に記載の方法で実施できる。また、特開昭５６−１６２６１７号公報に記載の高粘度セルロースアシレート溶液の流れを低粘度のセルロースアシレート溶液で包み込み、その高、低粘度のセルロースアシレート溶液を同時に押出すセルロースアシレートフィルム流延方法でもよい。更に又、特開昭６１−９４７２４号および特開昭６１−９４７２５号の各公報に記載の外側の溶液が内側の溶液よりも貧溶媒であるアルコール成分を多く含有させることも好ましい態様である。或いはまた２個の流延口を用いて、第一の流延口により金属支持体に成型したフィルムを剥離し、金属支持体面に接していた側に第二の流延を行なうことでより、フィルムを作製することでもよく、例えば特公昭４４−２０２３５号公報に記載されている方法である。流延するセルロースアシレート溶液は同一の溶液でもよいし、異なるセルロースアシレート溶液でもよく特に限定されない。複数のセルロースアシレート層に機能を持たせるために、その機能に応じたセルロースアシレート溶液を、それぞれの流延口から押出せばよい。さらにセルロースアシレート溶液は、他の機能層（例えば、接着層、染料層、帯電防止層、アンチハレーション層、ＵＶ吸収層、偏光層など）を同時に流延することも実施しうる。
(Multilayer casting)
The cellulose acylate solution may be cast as a single layer liquid on a smooth band or drum as a metal support, or a plurality of cellulose acylate liquids of two or more layers may be cast. When casting a plurality of cellulose acylate solutions, produce a film while casting and laminating a solution containing cellulose acylate from a plurality of casting openings provided at intervals in the traveling direction of the metal support. For example, the methods described in JP-A-61-158414, JP-A-1-122419, and JP-A-11-198285 can be applied. Alternatively, a film may be formed by casting a cellulose acylate solution from two casting ports. For example, JP-B-60-27562, JP-A-61-94724, JP-A-61-947245, It can be carried out by the methods described in JP-A Nos. 61-104813, 61-158413, and 6-134933. Further, a cellulose acylate film in which a flow of a high-viscosity cellulose acylate solution described in JP-A-56-162617 is wrapped with a low-viscosity cellulose acylate solution, and the high- and low-viscosity cellulose acylate solutions are simultaneously extruded. A casting method may be used. Furthermore, it is also a preferable aspect that the outer solution described in JP-A-61-94724 and JP-A-61-94725 contains a larger amount of an alcohol component which is a poor solvent than the inner solution. Alternatively, by using two casting ports, peeling the film formed on the metal support by the first casting port, and performing the second casting on the side that was in contact with the metal support surface, A film may be produced, for example, a method described in Japanese Patent Publication No. 44-20235. The cellulose acylate solution to be cast may be the same solution or different cellulose acylate solutions, and is not particularly limited. In order to give a function to a plurality of cellulose acylate layers, a cellulose acylate solution corresponding to the function may be extruded from each casting port. Furthermore, the cellulose acylate solution can be cast by simultaneously casting other functional layers (for example, an adhesive layer, a dye layer, an antistatic layer, an antihalation layer, a UV absorbing layer, a polarizing layer).
従来の単層液では、必要なフィルム厚さにするためには高濃度で高粘度のセルロースアシレート溶液を押出すことが必要であり、その場合セルロースアシレート溶液の安定性が悪くて固形物が発生し、ブツ故障となったり、平面性が不良であったりして問題となることが多かった。この解決として、複数のセルロースアシレート溶液を流延口から流延することにより、高粘度の溶液を同時に金属支持体上に押出すことができ、平面性も良化し優れた面状のフィルムが作製できるばかりでなく、濃厚なセルロースアシレート溶液を用いることで乾燥負荷の低減化が達成でき、フィルムの生産スピードを高めることができる。共流延の場合、内側と外側の厚さは特に限定されないが、好ましくは外側が全膜厚の１〜５０％であることが好ましく、より好ましくは２〜３０％の厚さである。ここで、３層以上の共流延の場合は金属支持体に接した層と空気側に接した層のトータル膜厚を外側の厚さと定義する。共流延の場合、前述の可塑剤、紫外線吸収剤、マット剤等の添加物濃度が異なるセルロースアシレート溶液を共流延して、積層構造のセルロースアシレートフィルムを作製することもできる。例えば、スキン層／コア層／スキン層といった構成のセルロースアシレートフィルムを作ることができる。例えば、マット剤は、スキン層に多く、又はスキン層のみに入れることができる。可塑剤、紫外線吸収剤はスキン層よりもコア層に多くいれることができ、コア層のみにいれてもよい。又、コア層とスキン層で可塑剤、紫外線吸収剤の種類を変更することもでき、例えばスキン層に低揮発性の可塑剤及び紫外線吸収剤の少なくともいずれかを含ませ、コア層に可塑性に優れた可塑剤、或いは紫外線吸収性に優れた紫外線吸収剤を添加することもできる。また、剥離促進剤を金属支持体側のスキン層のみ含有させることも好ましい態様である。また、冷却ドラム法で金属支持体を冷却して溶液をゲル化させるために、スキン層に貧溶媒であるアルコールをコア層より多く添加することも好ましい。スキン層とコア層のＴｇが異なっていても良く、スキン層のＴｇよりコア層のＴｇが低いことが好ましい。又、流延時のセルロースアシレートを含む溶液の粘度もスキン層とコア層で異なっていても良く、スキン層の粘度がコア層の粘度よりも小さいことが好ましいが、コア層の粘度がスキン層の粘度より小さくてもよい。 In the conventional single-layer liquid, it is necessary to extrude a high-concentration and high-viscosity cellulose acylate solution in order to obtain the required film thickness. In many cases, this causes a problem such as a fault or flatness. As a solution to this, by casting a plurality of cellulose acylate solutions from a casting port, a highly viscous solution can be extruded onto a metal support at the same time. Not only can it be produced, but also the use of a concentrated cellulose acylate solution can reduce the drying load and increase the film production speed. In the case of co-casting, the inner and outer thicknesses are not particularly limited, but preferably the outer side is preferably 1 to 50% of the total film thickness, and more preferably 2 to 30%. Here, in the case of co-casting with three or more layers, the total thickness of the layer in contact with the metal support and the layer in contact with the air side is defined as the outer thickness. In the case of co-casting, a cellulose acylate film having a laminated structure can be produced by co-casting cellulose acylate solutions having different additive concentrations such as the above-mentioned plasticizer, ultraviolet absorber and matting agent. For example, a cellulose acylate film having a structure of skin layer / core layer / skin layer can be produced. For example, the matting agent can be contained in the skin layer in a large amount or only in the skin layer. The plasticizer and the ultraviolet absorber can be contained in the core layer more than the skin layer, and may be contained only in the core layer. It is also possible to change the type of plasticizer and ultraviolet absorber between the core layer and the skin layer. For example, the skin layer contains at least one of a low-volatile plasticizer and an ultraviolet absorber, and the core layer is made plastic. It is also possible to add an excellent plasticizer or an ultraviolet absorber excellent in ultraviolet absorption. Moreover, it is also a preferable aspect to contain a peeling accelerator only in the skin layer on the metal support side. It is also preferable to add more alcohol, which is a poor solvent, to the skin layer than the core layer in order to cool the metal support by the cooling drum method to gel the solution. The Tg of the skin layer and the core layer may be different, and the Tg of the core layer is preferably lower than the Tg of the skin layer. Further, the viscosity of the solution containing cellulose acylate during casting may be different between the skin layer and the core layer, and the viscosity of the skin layer is preferably smaller than the viscosity of the core layer. It may be smaller than the viscosity.
（流延）
溶液の流延方法としては、調製されたドープを加圧ダイから金属支持体上に均一に押し出す方法、一旦金属支持体上に流延されたドープをブレードで膜厚を調節するドクターブレードによる方法、或いは逆回転するロールで調節するリバースロールコーターによる方法等があるが、加圧ダイによる方法が好ましい。加圧ダイにはコートハンガータイプやＴダイタイプ等があるがいずれも好ましく用いることができる。また、ここで挙げた方法以外にも従来知られているセルローストリアセテート溶液を流延製膜する種々の方法で実施でき、用いる溶媒の沸点等の違いを考慮して各条件を設定することによりそれぞれの公報に記載の内容と同様の効果が得られる。本発明に関するセルロースアシレートフィルムを製造するのに使用されるエンドレスに走行する金属支持体としては、表面がクロムメッキによって鏡面仕上げされたドラムや表面研磨によって鏡面仕上げされたステンレスベルト（バンドといってもよい）が用いられる。本発明に関するセルロースアシレートフィルムの製造に用いられる加圧ダイは、金属支持体の上方に１基或いは２基以上の設置でもよい。好ましくは１基又は２基である。２基以上設置する場合には流延するドープ量をそれぞれのダイに種々な割合にわけてもよく、複数の精密定量ギヤアポンプからそれぞれの割合でダイにドープを送液してもよい。流延に用いられるセルロースアシレート溶液の温度は、−１０〜５５℃が好ましくより好ましくは２５〜５０℃である。その場合、工程のすべてが同一でもよく、あるいは工程の各所で異なっていてもよい。異なる場合は、流延直前で所望の温度であればよい。
(Casting)
As a solution casting method, a method in which the prepared dope is uniformly extruded from a pressure die onto a metal support, and a method using a doctor blade in which the dope once cast on the metal support is adjusted with a blade is used. Alternatively, there is a method using a reverse roll coater that adjusts with a reverse rotating roll, and a method using a pressure die is preferable. The pressure die includes a coat hanger type and a T die type, and any of them can be preferably used. In addition to the methods listed here, it can be carried out by various methods of casting a cellulose triacetate solution known in the art, and by setting each condition in consideration of differences in the boiling point of the solvent used, etc. The same effects as those described in the above publication can be obtained. The endlessly running metal support used for producing the cellulose acylate film according to the present invention includes a drum whose surface is mirror-finished by chrome plating and a stainless steel belt whose surface is mirror-finished by surface polishing (referred to as a band). May be used). One or two or more pressure dies used for producing the cellulose acylate film according to the present invention may be installed above the metal support. Preferably 1 or 2 groups. When two or more units are installed, the amount of dope to be cast may be divided into various ratios for each die, or the dope may be fed to the dies from each of a plurality of precision quantitative gear pumps. The temperature of the cellulose acylate solution used for casting is preferably −10 to 55 ° C., more preferably 25 to 50 ° C. In that case, all of the steps may be the same or may be different at different points in the step. If they are different, it may be a desired temperature just before casting.
（乾燥）
セルロースアシレートフィルムの製造に係わる金属支持体上におけるドープの乾燥は、一般的には金属支持体（ドラム或いはベルト）の表面側、つまり金属支持体上にあるウェブの表面から熱風を当てる方法、ドラム或いはベルトの裏面から熱風を当てる方法、温度コントロールした液体をベルトやドラムのドープ流延面の反対側である裏面から接触させて、伝熱によりドラム或いはベルトを加熱し表面温度をコントロールする液体伝熱方法などがあるが、裏面液体伝熱方式が好ましい。流延される前の金属支持体の表面温度はドープに用いられている溶媒の沸点以下であれば何度でもよい。しかし乾燥を促進するためには、また金属支持体上での流動性を失わせるためには、使用される溶媒の内の最も沸点の低い溶媒の沸点より１〜１０℃低い温度に設定することが好ましい。尚、流延ドープを冷却して乾燥することなく剥ぎ取る場合はこの限りではない。
(Dry)
The drying of the dope on the metal support involved in the production of the cellulose acylate film is generally performed by applying hot air from the surface side of the metal support (drum or belt), that is, the surface of the web on the metal support, A method of applying hot air from the back of the drum or belt, contacting the temperature-controlled liquid from the back of the belt or drum opposite the dope casting surface, and heating the drum or belt by heat transfer to control the surface temperature Although there is a heat transfer method, the back surface liquid heat transfer method is preferable. The surface temperature of the metal support before casting may be any number as long as it is not higher than the boiling point of the solvent used for the dope. However, in order to promote drying and to lose fluidity on the metal support, the temperature should be set to 1 to 10 ° C. lower than the boiling point of the lowest boiling solvent used. Is preferred. This is not the case when the cast dope is cooled and peeled off without drying.
（延伸処理）
本発明に関するセルロースアシレートフィルムは、延伸処理によりレターデーションを調整することができる。更には、積極的に幅方向に延伸する方法もあり、例えば、特開昭６２−１１５０３５号、特開平４−１５２１２５号、特開平４−２８４２１１号、特開平４−２９８３１０号、および特開平１１−４８２７１号の各公報などに記載されている。これは、セルロースアシレートフィルムの面内レターデーション値を高い値とするために、製造したフィルムを延伸する。
フィルムの延伸は、常温または加熱条件下で実施する。加熱温度は、フィルムのガラス転移温度以下であることが好ましい。フィルムの延伸は、縦あるいは横だけの一軸延伸でもよく同時あるいは逐次２軸延伸でもよい。延伸は１〜２００％の延伸が行われる。好ましくは１〜１００％の延伸が、特に好ましくは１から５０％延伸を行う。光学フィルムの複屈折は幅方向の屈折率が長さ方向の屈折率よりも大きくなることが好ましい。従って幅方向により多く延伸することが好ましい。また、延伸処理は製膜工程の途中で行ってもよいし、製膜して巻き取った原反を延伸処理しても良い。前者の場合には残留溶剤量を含んだ状態で延伸を行っても良く、残留溶剤量が２乃至３０％で好ましく延伸することができる。
(Extension process)
The retardation of the cellulose acylate film according to the present invention can be adjusted by stretching. Furthermore, there is also a method of positively stretching in the width direction. -48271, and the like. This stretches the produced film in order to increase the in-plane retardation value of the cellulose acylate film.
The film is stretched at room temperature or under heating conditions. The heating temperature is preferably not higher than the glass transition temperature of the film. The stretching of the film may be uniaxial stretching only in the longitudinal or lateral direction, or may be simultaneous or sequential biaxial stretching. Stretching is performed by 1 to 200%. The stretching is preferably 1 to 100%, particularly preferably 1 to 50%. The birefringence of the optical film is preferably such that the refractive index in the width direction is larger than the refractive index in the length direction. Therefore, it is preferable to stretch more in the width direction. In addition, the stretching process may be performed in the middle of the film forming process, or the raw film that has been formed and wound may be stretched. In the former case, the stretching may be performed in a state including the residual solvent amount, and the stretching can be preferably performed at a residual solvent amount of 2 to 30%.
乾燥後得られる本発明に関するセルロースアシレートフィルムの膜厚は、使用目的によって異なり、通常５から５００μｍの範囲であることが好ましく、更に２０〜３００μｍの範囲が好ましく、特に３０〜１５０μｍの範囲が好ましい。また、光学用として特にＶＡ液晶表示装置用としては４０〜１１０μｍであることが好ましい。フィルム厚さの調製は、所望の厚さになるように、ドープ中に含まれる固形分濃度、ダイの口金のスリット間隙、ダイからの押し出し圧力、金属支持体速度等を調節すればよい。以上のようにして得られたセルロースアシレートフィルムの幅は０．５〜３ｍが好ましく、より好ましくは０．６〜２．５ｍ、さらに好ましくは０．８〜２．２ｍである。長さは１ロールあたり１００〜１００００ｍで巻き取るのが好ましく、より好ましくは５００〜７０００ｍであり、さらに好ましくは１０００〜６０００ｍである。巻き取る際、少なくとも片端にナーリングを付与するのが好ましく、幅は３ｍｍ〜５０ｍｍが好ましく、より好ましくは５ｍｍ〜３０ｍｍ、高さは０．５〜５００μｍが好ましく、より好ましくは１〜２００μｍである。これは片押しであっても両押しであっても良い。
全幅のＲｅ(590)値のばらつきが±５ｎｍであることが好ましく、±３ｎｍであることが更に好ましい。また、Ｒｔｈ(590)値のバラツキは±１０ｎｍが好ましく、±５ｎｍであることが更に好ましい。また、長さ方向のＲｅ値、及びＲｔｈ値のバラツキも幅方向のバラツキの範囲内であることが好ましい。
The film thickness of the cellulose acylate film relating to the present invention obtained after drying varies depending on the purpose of use and is usually preferably in the range of 5 to 500 μm, more preferably in the range of 20 to 300 μm, particularly preferably in the range of 30 to 150 μm. . Moreover, it is preferable that it is 40-110 micrometers for optical uses, especially for VA liquid crystal display devices. The film thickness may be adjusted by adjusting the solid content concentration contained in the dope, the slit gap of the die base, the extrusion pressure from the die, the metal support speed, and the like so as to obtain a desired thickness. The width of the cellulose acylate film obtained as described above is preferably 0.5 to 3 m, more preferably 0.6 to 2.5 m, still more preferably 0.8 to 2.2 m. The length is preferably 100 to 10,000 m per roll, more preferably 500 to 7000 m, and still more preferably 1000 to 6000 m. When winding, knurling is preferably applied to at least one end, the width is preferably 3 mm to 50 mm, more preferably 5 mm to 30 mm, and the height is preferably 0.5 to 500 μm, more preferably 1 to 200 μm. This may be a single push or a double push.
The variation in the Re (590) value of the full width is preferably ± 5 nm, and more preferably ± 3 nm. Further, the variation of the Rth (590) value is preferably ± 10 nm, and more preferably ± 5 nm. Further, it is preferable that the variation in the Re value and the Rth value in the length direction is also within the range of the variation in the width direction.
（セルロースアシレートフィルムの光学特性）
本発明に関するセルロースアシレートフィルムの光学特性は、
式（III） ：Ｒｅ(λ)＝（ｎｘ−ｎｙ）×ｄ、
式（IV） ：Ｒｔｈ(λ)＝｛（ｎｘ＋ｎｙ）／２−ｎｚ｝×ｄ
で表されるＲｅレターデション値、Ｒｔｈレターデーション値がそれぞれ、以下の式（Ｖ）、（VI）を満たすことが、液晶表示装置、特にＶＡモード液晶表示装置の視野角を広くするために好ましい。特に、セルロースアシレートフィルムが偏光板の液晶セル側の保護膜に用いられる場合、好ましい。
式（Ｖ） ：２０ｎｍ≦Ｒｅ(590)≦２００ｎｍ、
式（VI） ：７０ｎｍ≦Ｒｔｈ(590)≦４００ｎｍ
［式中、Ｒｅ(λ)は波長λｎｍにおける正面レターデーション値（単位：ｎｍ）、Ｒｔｈ(λ)は波長λｎｍにおける膜厚方向のレターデーション値（単位：ｎｍ）である。またｎｘはフィルム面内の遅相軸方向の屈折率であり、ｎｙはフィルム面内の進相軸方向の屈折率であり、ｎｚはフィルムの厚み方向の屈折率であり、ｄはフィルムの厚さ（単位：ｎｍ）である。］
Ｒｅ(λ)はＫＯＢＲＡ ２１ＡＤＨ（王子計測機器（株）製）において波長λｎｍの光をフィルム法線方向に入射させて測定した。また、Ｒｔｈ(λ)は前記Ｒｅ(λ)、面内の遅相軸を傾斜軸としてフィルム法線方向に対して＋４０°傾斜した方向から波長λｎｍの光を入射させて測定したレターデーション値、および面内の遅相軸を傾斜軸としてフィルム法線方向に対して−４０°傾斜した方向から波長λｎｍの光を入射させて測定したレターデーション値の計３つの方向で測定したレターデーション値を基に、平均屈折率の仮定値１．４８および膜厚を入力し算出した。
また、本発明ではＲｅ／Ｒｔｈ比を好ましくは０．１乃至０．８に調節する。さらに好ましくは、０．２５乃至０．６に調節する。これらの調整は添加剤の種類、添加量および延伸倍率により行うことが出来る。
(Optical properties of cellulose acylate film)
The optical properties of the cellulose acylate film according to the present invention are:
Formula (III): Re ( λ ) = (nx−ny) × d,
Formula (IV): Rth ( λ ) = {(nx + ny) / 2−nz} × d
In order to widen the viewing angle of a liquid crystal display device, particularly a VA mode liquid crystal display device, it is preferable that the Re retardation value and Rth retardation value represented by the following formulas (V) and (VI) respectively be satisfied: . In particular, it is preferable when a cellulose acylate film is used for the protective film on the liquid crystal cell side of the polarizing plate.
Formula (V): 20 nm ≦ Re (590) ≦ 200 nm,
Formula (VI): 70 nm ≦ Rth (590) ≦ 400 nm
[Wherein, Re ( λ ) is a front retardation value (unit: nm) at a wavelength λnm, and Rth ( λ ) is a retardation value (unit: nm) in a film thickness direction at a wavelength λnm. Further, nx is the refractive index in the slow axis direction in the film plane, ny is the refractive index in the fast axis direction in the film plane, nz is the refractive index in the thickness direction of the film, and d is the thickness of the film. (Unit: nm). ]
Re (λ) was measured with KOBRA 21ADH (manufactured by Oji Scientific Instruments) by making light having a wavelength of λ nm incident in the normal direction of the film. Rth (λ) is Re (λ), a retardation value measured by making light having a wavelength λ nm incident from a direction inclined by + 40 ° with respect to the film normal direction with the in-plane slow axis as the tilt axis, And retardation values measured in three directions, including retardation values measured by making light of wavelength λ nm incident from a direction inclined by −40 ° with respect to the film normal direction with the in-plane slow axis as the tilt axis. Based on this, an assumed average refractive index of 1.48 and a film thickness were input and calculated.
In the present invention, the Re / Rth ratio is preferably adjusted to 0.1 to 0.8. More preferably, it is adjusted to 0.25 to 0.6. These adjustments can be made according to the type of additive, the amount added, and the draw ratio.
本発明に関するセルロースアシレートフィルムをＶＡモードに使用する場合、セルの両側に１枚ずつ合計２枚使用する形態（２枚型）と、セルの上下のいずれか一方の側にのみ使用する形態（１枚型）の２通りがある。
２枚型の場合、Ｒｅは２０乃至１００ｎｍが好ましく、３０乃至７０ｎｍがさらに好ましい。Ｒｔｈについては７０乃至３００ｎｍが好ましく、１００乃至２００ｎｍがさらに好ましい。
１枚型の場合、Ｒｅは３０乃至１５０ｎｍが好ましく、４０乃至１００ｎｍがさらに好ましい。Ｒｔｈについては１００乃至３００ｎｍが好ましく、１５０乃至２５０ｎｍがさらに好ましい。
When the cellulose acylate film according to the present invention is used in the VA mode, a mode in which a total of two sheets are used on each side of the cell (two-sheet type) and a mode in which only one of the upper and lower sides of the cell is used ( There are two types, one sheet type).
In the case of the two-sheet type, Re is preferably 20 to 100 nm, and more preferably 30 to 70 nm. Rth is preferably 70 to 300 nm, more preferably 100 to 200 nm.
In the case of a single sheet type, Re is preferably 30 to 150 nm, and more preferably 40 to 100 nm. Rth is preferably from 100 to 300 nm, more preferably from 150 to 250 nm.
本発明に関するセルロースアシレートフィルムのフィルム面内の遅相軸角度のバラつきは、ロールフィルムの基準方向に対して−２度から＋２度の範囲にあることが好ましく、−１度から＋１度の範囲にあることがさらに好ましく、−０．５度から＋０．５度の範囲にあることが最も好ましい。ここで、基準方向とは、セルロースアシレートフィルムを縦延伸する場合はロールフィルムの長手方向であり、横延伸する場合はロールフィルムの幅方向である。 The variation of the slow axis angle in the film plane of the cellulose acylate film according to the present invention is preferably in the range of -2 to +2 degrees with respect to the reference direction of the roll film, and in the range of -1 to +1 degrees. More preferably, it is in the range of -0.5 degree to +0.5 degree. Here, the reference direction is the longitudinal direction of the roll film when the cellulose acylate film is longitudinally stretched, and the width direction of the roll film when laterally stretched.
また、本発明に関するセルロースアシレートフィルムは、２５℃１０％ＲＨにおけるＲｅ値と２５℃８０％ＲＨにおけるＲｅ値との差ΔＲｅ（＝Ｒｅ１０％ＲＨ−Ｒｅ８０％ＲＨ）が０〜１０ｎｍであり、２５℃１０％ＲＨにおけるＲｔｈ値と２５℃８０％ＲＨにおけるＲｔｈ値との差ΔＲｔｈ（＝Ｒｔｈ１０％ＲＨ−Ｒｔｈ８０％ＲＨ）が０〜３０ｎｍであるのが、液晶表示装置の経時による色味変化を少なくする上で好ましい。
また、本発明に関するセルロースアシレートフィルムは、２５℃８０％ＲＨにおける平衡含水率が３．２％以下であるのが、液晶表示装置の経時による色味変化を少なくする上で好ましい。
含水率の測定法は、本発明に関するセルロースアシレートフィルム試料７ｍｍ×３５ｍｍを水分測定器、試料乾燥装置（ＣＡ−０３、ＶＡ−０５、共に三菱化学（株））にてカールフィッシャー法で測定する。水分量（ｇ）を試料質量（ｇ）で除して算出する。
In the cellulose acylate film according to the present invention, the difference ΔRe (= Re10% RH−Re80% RH) between the Re value at 25 ° C. and 10% RH and the Re value at 25 ° C. and 80% RH is 0 to 10 nm. The difference ΔRth (= Rth10% RH−Rth80% RH) between the Rth value at 10 ° C. at 10 ° C. and the Rth value at 80% RH at 25 ° C. is 0 to 30 nm, so that the change in the color tone of the liquid crystal display device with time This is preferable.
In addition, the cellulose acylate film according to the present invention preferably has an equilibrium water content of not more than 3.2% at 25 ° C. and 80% RH in order to reduce the color change with time of the liquid crystal display device.
The moisture content is measured by measuring a cellulose acylate film sample 7 mm × 35 mm according to the present invention by a Karl Fischer method using a moisture measuring device and a sample drying apparatus (CA-03, VA-05, both Mitsubishi Chemical Corporation). . It is calculated by dividing the amount of water (g) by the sample mass (g).
また、本発明に関するセルロースアシレートフィルムは、６０℃、９５％ＲＨ、２４ｈｒの透湿度（膜厚８０μｍ換算）が、４００ｇ／ｍ2・２４ｈｒ以上１８００ｇ／ｍ2・２４ｈｒ以下であるのが、液晶表示装置の経時による色味変化を少なくする上で好ましい。
セルロースアシレートフィルムの膜厚が厚ければ透湿度は小さくなり、膜厚が薄ければ透湿度は大きくなる。そこでどのような膜厚のサンプルでも基準を８０μｍに設け換算する必要がある。膜厚の換算は、（８０μｍ換算の透湿度＝実測の透湿度×実測の膜厚μｍ／８０μｍ）として求める。
透湿度の測定法は、「高分子の物性II」（高分子実験講座４ 共立出版）の２８５頁〜２９４頁：蒸気透過量の測定（質量法、温度計法、蒸気圧法、吸着量法）に記載の方法を適用することができる。
ガラス転移温度の測定は、本発明に関するセルロースアシレートフィルム試料（未延伸）５ｍｍ×３０ｍｍを、２５℃６０％ＲＨで２時間以上調湿した後に動的粘弾性測定装置（バイブロン：ＤＶＡ−２２５（アイティー計測制御（株）製））で、つかみ間距離２０ｍｍ、昇温速度２℃／分、測定温度範囲３０℃〜２００℃、周波数１Ｈｚで測定し、縦軸に対数軸で貯蔵弾性率、横軸に線形軸で温度（℃）をとった時に、貯蔵弾性率が固体領域からガラス転移領域へ移行する際に見受けられる貯蔵弾性率の急激な減少を固体領域で直線１を引き、ガラス転移領域で直線２を引いたときの直線１と直線２の交点を、昇温時に貯蔵弾性率が急激に減少しフィルムが軟化し始める温度であり、ガラス転移領域に移行し始める温度であるため、ガラス転移温度Ｔｇ（動的粘弾性）とした。
また、本発明に関するセルロースアシレートフィルムは、ヘイズが０．０１〜２％であるのが、好ましい。ここで、ヘイズは、以下のようにして測定できる。
ヘイズの測定は、本発明に関するセルロースアシレートフィルム試料４０ｍｍ×８０ｍｍを、２５℃，６０％ＲＨでヘイズメーター（ＨＧＭ−２ＤＰ、スガ試験機）でＪＩＳ Ｋ−６７１４に従って測定する。
また、本発明に関するセルロースアシレートフィルムは、８０℃、９０％ＲＨの条件下に４８時間静置した場合の質量変化が、０〜５％であるのが、好ましい。
また、本発明に関するセルロースアシレートフィルムは、６０℃、９５％ＲＨの条件下に２４時間静置した場合の寸度変化および９０℃、５％ＲＨの条件下に２４時間静置した場合の寸度変化が、いずれも０〜５％であるのが、好ましい。
光弾性係数が、５０×１０-13ｃｍ2／ｄｙｎｅ以下であるのが、液晶表示装置の経時による色味変化を少なくする上で好ましい。
具体的な測定方法としては、セルロースアシレートフィルム試料１０ｍｍ×１００ｍｍの長軸方向に対して引っ張り応力をかけ、その際のレターデーションをエリプソメーター（Ｍ１５０、日本分光（株））で測定し、応力に対するレターデーションの変化量から光弾性係数を算出する。
The cellulose acylate film according to the present invention is liquid crystal having a moisture permeability of 60 ° C., 95% RH, 24 hr (film thickness 80 μm conversion) of 400 g / m 2 · 24 hr to 1800 g / m 2 · 24 hr. This is preferable for reducing the change in color of the display device over time.
If the film thickness of the cellulose acylate film is thick, the moisture permeability becomes small, and if the film thickness is thin, the moisture permeability becomes large. Therefore, it is necessary to convert the sample of any film thickness to a standard of 80 μm. Conversion of the film thickness is obtained as (water vapor permeability in terms of 80 μm = measured water vapor permeability × measured film thickness μm / 80 μm).
The measurement method of moisture permeability is “Polymer Properties II” (Polymer Experiment Course 4, Kyoritsu Shuppan), pages 285-294: Measurement of vapor permeation (mass method, thermometer method, vapor pressure method, adsorption amount method) The method described in can be applied.
The glass transition temperature was measured by adjusting a cellulose acylate film sample (unstretched) 5 mm × 30 mm according to the present invention at 25 ° C. and 60% RH for 2 hours or more, and then measuring the dynamic viscoelasticity (Vibron: DVA-225 ( Measured by a distance between grips of 20 mm, a temperature increase rate of 2 ° C./min, a measurement temperature range of 30 ° C. to 200 ° C., a frequency of 1 Hz, a logarithmic axis and a storage elastic modulus on the logarithmic axis, When the temperature (° C) is taken as the linear axis on the horizontal axis, the straight line 1 is drawn in the solid region to draw the straight line 1 in the solid region, and the storage elastic modulus shifts from the solid region to the glass transition region. When the straight line 2 is drawn in the region, the intersection of the straight line 1 and the straight line 2 is a temperature at which the storage elastic modulus suddenly decreases and the film starts to soften when the temperature rises, and the temperature starts to move to the glass transition region. Glass Was the transition temperature Tg (dynamic viscoelasticity).
In addition, the cellulose acylate film according to the present invention preferably has a haze of 0.01 to 2%. Here, the haze can be measured as follows.
The haze is measured by measuring a cellulose acylate film sample 40 mm × 80 mm according to the present invention at 25 ° C. and 60% RH with a haze meter (HGM-2DP, Suga Test Instruments) according to JIS K-6714.
The cellulose acylate film according to the present invention preferably has a mass change of 0 to 5% when left for 48 hours under conditions of 80 ° C. and 90% RH.
In addition, the cellulose acylate film according to the present invention has a dimensional change when left for 24 hours under conditions of 60 ° C. and 95% RH, and a size when left for 24 hours under conditions of 90 ° C. and 5% RH. The degree of change is preferably 0 to 5%.
It is preferable that the photoelastic coefficient is 50 × 10 −13 cm 2 / dyne or less in order to reduce the color change with time of the liquid crystal display device.
As a specific measuring method, a tensile stress is applied to the major axis direction of a 10 mm × 100 mm cellulose acylate film sample, and the retardation at that time is measured with an ellipsometer (M150, JASCO Corporation). The photoelastic coefficient is calculated from the amount of change in retardation with respect to.
また、保護フィルムの弾性率は、２８４０ＭＰａ乃至４７１０ＭＰａであることが好ましく、さらに好ましくは２０６０ＭＰａ乃至４４１０ＭＰａである。ＭＤ方向（フィルム進行方向）、ＴＤ方向（フィルム幅方向）の弾性率をＥMF、ＥTFとした場合、０．９≦ＥTF／ＥMF≦１．８であることが好ましく、０．９５≦ＥTF／ＥMF≦１．８であることがさらに好ましい。
なお、保護フィルムの弾性率は、試料幅１０ｍｍ、長さ１００ｍｍに切り出し、２５℃６０％雰囲気下でチャック間距離５０ｍｍにし、３０ｍｍ／分で引っ張り試験を行い求める。
The elastic modulus of the protective film is preferably 2840 MPa to 4710 MPa, more preferably 2060 MPa to 4410 MPa. When the elastic modulus in the MD direction (film traveling direction) and TD direction (film width direction) is EMF and ETF, it is preferably 0.9 ≦ ETF / EMF ≦ 1.8, and 0.95 ≦ ETF / EMF. More preferably, ≦ 1.8.
The elastic modulus of the protective film is obtained by cutting the sample to a width of 10 mm and a length of 100 mm, setting the distance between chucks to 50 mm in an atmosphere of 25 ° C. and 60%, and performing a tensile test at 30 mm / min.
（光学異方性層）
さらに、保護フィルムは、高分子フィルム上に光学異方性層を設けたものであっても良い。光学異方性層は、透明なポリマーフィルム上に配向層と光学異方性層をこの順に有したものが好ましい。
(Optically anisotropic layer)
Further, the protective film may be a polymer film provided with an optically anisotropic layer. The optically anisotropic layer preferably has an alignment layer and an optically anisotropic layer in this order on a transparent polymer film.
配向層は、有機化合物（好ましくはポリマー）のラビング処理、無機化合物の斜方蒸着、マイクログループを有する層の形成のような手段で設けることができる。さらに電場の付与、磁場の付与あるいは光照射により配向機能が生じる配向層も知られているが、ポリマーのラビング処理により形成する配向層が特に好ましい。ラビング処理はポリマー層の表面を紙や布で一定方向に数回こすることにより好ましく実施される。偏光子の吸収軸方向とラビング方向は実質的に平行であることが好ましい。配向層に使用するポリマーの種類は、ポリイミド、ポリビニルアルコール、特開平９−１５２５０９号公報に記載された重合性基を有するポリマー等を好ましく使用することができる。配向層の厚さは０．０１〜５μｍであることが好ましく、０．０５〜２μｍであることがさらに好ましい。 The alignment layer can be provided by means such as a rubbing treatment of an organic compound (preferably a polymer), oblique deposition of an inorganic compound, or formation of a layer having a microgroup. Furthermore, an alignment layer in which an alignment function is generated by application of an electric field, application of a magnetic field or light irradiation is also known, but an alignment layer formed by a rubbing treatment of a polymer is particularly preferable. The rubbing treatment is preferably performed by rubbing the surface of the polymer layer several times in a certain direction with paper or cloth. It is preferable that the absorption axis direction and the rubbing direction of the polarizer are substantially parallel. As the polymer used for the alignment layer, polyimide, polyvinyl alcohol, a polymer having a polymerizable group described in JP-A-9-152509, and the like can be preferably used. The thickness of the alignment layer is preferably 0.01 to 5 μm, and more preferably 0.05 to 2 μm.
光学異方性層は液晶性化合物を含有していることが好ましい。本発明に使用される液晶性化合物はディスコティック化合物（ディスコティック液晶）を有していることが特に好ましい。ディスコティック液晶分子は、下記のトリフェニレン誘導体のように円盤状のコア部を有し、そこから放射状に側鎖が伸びた構造を有している。また、経時安定性を付与するため、熱、光等で反応する基をさらに導入することも好ましく行われる。上記ディスコティック液晶の好ましい例は特開平８−５０２０６号公報に記載されている。 The optically anisotropic layer preferably contains a liquid crystalline compound. The liquid crystal compound used in the present invention particularly preferably has a discotic compound (discotic liquid crystal). The discotic liquid crystal molecule has a disk-like core portion like the following triphenylene derivative, and has a structure in which side chains extend radially therefrom. In order to impart stability over time, it is also preferable to further introduce a group that reacts with heat, light or the like. Preferred examples of the discotic liquid crystal are described in JP-A-8-50206.
ディスコティック液晶分子は、配向層付近ではラビング方向にプレチルト角を持ってほぼフィルム平面に平行に配向しており、反対の空気面側ではディスコティック液晶分子が面に垂直に近い形で立って配向している。ディスコティック液晶層全体としては、ハイブリッド配向を取っており、この層構造によってＴＮモードのＴＦＴ−ＬＣＤの視野角拡大を実現することができる。 The discotic liquid crystal molecules are aligned almost parallel to the film plane with a pretilt angle in the rubbing direction in the vicinity of the alignment layer, and the discotic liquid crystal molecules are oriented so that they are perpendicular to the plane on the opposite air side. is doing. The discotic liquid crystal layer as a whole has a hybrid alignment, and this layer structure can realize a wide viewing angle of a TN mode TFT-LCD.
上記光学異方性層は、一般にディスコティック化合物及び他の化合物（更に、例えば重合性モノマー、光重合開始剤）を溶剤に溶解した溶液を配向層上に塗布し、乾燥し、次いでディスコティックネマチック相形成温度まで加熱した後、ＵＶ光の照射等により重合させ、さらに冷却することにより得られる。本発明に用いるディスコティック液晶性化合物のディスコティックネマティック液晶相−固相転移温度としては、７０〜３００℃が好ましく、特に７０〜１７０℃が好ましい。 The optically anisotropic layer is generally a discotic compound and another compound (for example, a polymerizable monomer, a photopolymerization initiator) dissolved in a solvent, coated on the alignment layer, dried, and then discotic nematic. After heating to the phase formation temperature, it is obtained by polymerization by irradiation with UV light or the like and further cooling. The discotic nematic liquid crystal phase-solid phase transition temperature of the discotic liquid crystalline compound used in the present invention is preferably 70 to 300 ° C, particularly preferably 70 to 170 ° C.
また、上記光学異方性層に添加するディスコティック化合物以外の化合物としては、ディスコティック化合物と相溶性を有し、液晶性ディスコティック化合物に好ましい傾斜角の変化を与えられるか、あるいは配向を阻害しない限り、どのような化合物も使用することができる。これらの中で、重合性モノマー（例、ビニル基、ビニルオキシ基、アクリロイル基及びメタクリロイル基を有する化合物）、含フッ素トリアジン化合物等の空気界面側の配向制御用添加剤が、セルロースアセテート、セルロースアセテートプロピオネート、ヒドロキシプロピルセルロース及びセルロースアセテートブチレート等のポリマーを挙げることができる。これらの化合物は、ディスコティック化合物に対して一般に０．１〜５０質量％、好ましくは０．１〜３０質量％の添加量にて使用される。
光学異方性層の厚さは、０．１〜１０μｍであることが好ましく、０．５〜５μｍであることがさらに好ましい。
In addition to the discotic compound added to the optically anisotropic layer, the compound has compatibility with the discotic compound and can give a preferable change in tilt angle to the liquid crystalline discotic compound or inhibit the alignment. Any compound can be used as long as it is not. Among these, additives for controlling the orientation on the air interface side such as polymerizable monomers (eg, compounds having vinyl group, vinyloxy group, acryloyl group and methacryloyl group), fluorine-containing triazine compounds, cellulose acetate, cellulose acetate Mention may be made of polymers such as pionate, hydroxypropylcellulose and cellulose acetate butyrate. These compounds are generally used in an amount of 0.1 to 50% by mass, preferably 0.1 to 30% by mass, based on the discotic compound.
The thickness of the optically anisotropic layer is preferably 0.1 to 10 μm, and more preferably 0.5 to 5 μm.
（偏光板）
次に、本発明の偏光板について説明する。
本発明の偏光板は、上述の本発明の光学用セルロースアシレートフィルムを少なくとも１枚、偏光子の保護膜として用いたものである。
偏光板は、通常、偏光子およびその両側に配置された二枚の透明保護膜からなる。そして、本発明では、少なくとも一方の保護膜として、本発明に関するセルロースアシレートフィルムを用いる。他方の保護膜は、本発明に関するセルロースアシレートフィルムを用いても、通常のセルロースアセテートフィルムを用いてもよい。本発明では、偏光板の吸収軸方向と透過軸方向の弾性率を調整することにより、液晶表示装置として使用した際のムラを低減させている。
(Polarizer)
Next, the polarizing plate of the present invention will be described.
The polarizing plate of the present invention uses at least one optical cellulose acylate film of the present invention described above as a protective film for a polarizer.
The polarizing plate is usually composed of a polarizer and two transparent protective films disposed on both sides thereof. In the present invention, the cellulose acylate film according to the present invention is used as at least one protective film. The other protective film may be a cellulose acylate film according to the present invention or a normal cellulose acetate film. In the present invention, unevenness when used as a liquid crystal display device is reduced by adjusting the elastic modulus in the absorption axis direction and the transmission axis direction of the polarizing plate.
偏光板を液晶表示装置に使用した場合の丸いムラの発生原因に関して本発明者らが鋭意検討した結果、以下の原因であることがわかった。
偏光板を液晶セルに貼り付け、液晶表示装置とし、バックライトを点灯すると、バックライトによる熱がかかり、偏光板が収縮しやすい状況になる。このとき、吸収軸方向、あるいは透過軸方向の弾性率が著しく異なると、偏光板の収縮も吸収軸、透過軸で異なってしまう（弾性率が小さいと収縮が大きい）。偏光板は、液晶セルの表裏で吸収軸が直交するように貼り付けるため、前述の収縮が起こると、セルの表裏で収縮が強い方向が異なり、セルに不均一な力がかかることになる。それにより上記の丸いムラが生じると考えられる。
As a result of intensive studies by the present inventors on the cause of the occurrence of round unevenness when the polarizing plate is used in a liquid crystal display device, it has been found that the cause is as follows.
When a polarizing plate is attached to a liquid crystal cell to form a liquid crystal display device and the backlight is turned on, heat from the backlight is applied and the polarizing plate is likely to contract. At this time, if the elastic modulus in the absorption axis direction or the transmission axis direction is significantly different, the contraction of the polarizing plate also differs between the absorption axis and the transmission axis (the smaller the elastic modulus, the greater the contraction). Since the polarizing plate is attached so that the absorption axes are orthogonal to each other on the front and back of the liquid crystal cell, when the above-described shrinkage occurs, the direction in which the shrinkage is strong differs on the front and back of the cell, and an uneven force is applied to the cell. This is considered to cause the above-mentioned round unevenness.
よって、本発明の偏光板は、２５℃６０％ＲＨ下において、偏光板の吸収軸方向の弾性率ＥAと、偏光板透過軸方向の弾性率ＥTが下記式（Ｉ）を満たすことが好ましい。
式（Ｉ） ： ０．９≦ＥA／ＥT≦１．４
上記式（Ｉ）を満たすことにより、液晶セルに貼り付けた後に偏光板の吸収軸方向、透過軸方向に生じる力のバランスがとれ、吸収軸あるいは透過軸方向のみが大きく収縮することを防止することができる。その結果、液晶セルとしてのアンバランスを防ぐことができ、液晶表示装置のムラを抑制することができる。
また、ＥA／ＥTは、さらに好ましくは０．９５乃至１．４であり、０．９５乃至１．３８が特に好ましい。
Therefore, in the polarizing plate of the present invention, the elastic modulus EA in the absorption axis direction and the elastic modulus ET in the polarizing plate transmission axis direction preferably satisfy the following formula (I) at 25 ° C. and 60% RH.
Formula (I): 0.9 ≦ EA / ET ≦ 1.4
By satisfying the above formula (I), the force generated in the absorption axis direction and the transmission axis direction of the polarizing plate is balanced after being attached to the liquid crystal cell, and only the absorption axis or the transmission axis direction is prevented from being greatly contracted. be able to. As a result, imbalance as a liquid crystal cell can be prevented, and unevenness of the liquid crystal display device can be suppressed.
Further, EA / ET is more preferably 0.95 to 1.4, and particularly preferably 0.95 to 1.38.
さらに、このような偏光板を作製するための方法としては、偏光子の吸収軸方向は偏光子作製過程で延伸され弾性率が大きくなるため、偏光板の保護フィルムのＴＤ方向（貼り合わせ時に偏光子の吸収軸方向と直行する方向）の弾性率をＭＤ方向よりも大きくすること、偏光子の延伸時に何らかの工夫をして吸収軸方向の弾性率が大きくならないようにする（例えば延伸倍率の低下）こと、などの方法が考えられる。
偏光板の弾性率は、２５℃６０％ＲＨ下における偏光板の透過軸方向の弾性率ＥTが、２６４０ＭＰａ乃至５４００ＭＰａであることが好ましく、さらに好ましくは２６４０ＭＰａ乃至４８００ＭＰａであり、２６４０ＭＰａ乃至４４００ＭＰａであることが特に好ましい。弾性率が小さいと、液晶セルに貼り付け後の偏光板の収縮が大きすぎるため適切でなく、また、弾性率が大きすぎると、偏光板をセルに貼り付けしにくい等の不都合がある。
なお、偏光板の弾性率は、試料幅１０ｍｍ、長さ１００ｍｍに切り出し、２５℃６０％雰囲気下でチャック間距離５０ｍｍにし、３０ｍｍ／分で引っ張り試験を行い求める。
Furthermore, as a method for producing such a polarizing plate, the absorption axis direction of the polarizer is stretched in the process of producing the polarizer and the elastic modulus is increased, so that the TD direction of the protective film of the polarizing plate (polarized when bonded) The elastic modulus in the direction perpendicular to the absorption axis direction of the optical element is made larger than that in the MD direction, and some measures are taken when stretching the polarizer so that the elastic modulus in the absorption axis direction does not increase (for example, reduction in the stretching ratio) ) Can be considered.
As for the elastic modulus of the polarizing plate, the elastic modulus ET in the transmission axis direction of the polarizing plate at 25 ° C. and 60% RH is preferably 2640 MPa to 5400 MPa, more preferably 2640 MPa to 4800 MPa, and 2640 MPa to 4400 MPa. Is particularly preferred. If the elastic modulus is low, the contraction of the polarizing plate after being attached to the liquid crystal cell is too large, which is not appropriate. If the elastic modulus is too high, the polarizing plate is difficult to attach to the cell.
The elastic modulus of the polarizing plate is obtained by cutting the sample into a width of 10 mm and a length of 100 mm, setting the distance between chucks to 50 mm in an atmosphere of 25 ° C. and 60%, and performing a tensile test at 30 mm / min.
偏光板の偏光子には、ヨウ素系偏光子、二色性染料を用いる染料系偏光子やポリエン系偏光子がある。ヨウ素系偏光子および染料系偏光子は、一般にポリビニルアルコール系フィルムを用いて製造する。本発明に関するセルロースアシレートフィルムを偏光板保護膜として用いる場合、偏光板の作製方法は特に限定されず、一般的な方法で作製することができる。例えば、得られたセルロースアシレートフィルムをアルカリ処理し、ポリビニルアルコールフィルムを沃素溶液中に浸漬延伸して作製した偏光子の両面に完全ケン化ポリビニルアルコール水溶液を用いて貼り合わせる方法がある。アルカリ処理の代わりに特開平６−９４９１５号公報、特開平６−１１８２３２号公報に記載されているような易接着加工を施してもよい。保護膜処理面と偏光子を貼り合わせるのに使用される接着剤としては、例えば、ポリビニルアルコール、ポリビニルブチラール等のポリビニルアルコール系接着剤や、ブチルアクリレート等のビニル系ラテックス等が挙げられる。偏光板は偏光子及びその両面を保護する保護膜で構成されており、更に該偏光板の一方の面にプロテクトフィルムを、反対面にセパレートフィルムを貼合して構成してもよい。プロテクトフィルム及びセパレートフィルムは偏光板出荷時、製品検査時等において偏光板を保護する目的で用いられる。この場合、プロテクトフィルムは、偏光板の表面を保護する目的で貼合され、偏光板を液晶セルへ貼合する面の反対面側に用いられる。又、セパレートフィルムは液晶セルへ貼合する接着層をカバーする目的で用いられ、偏光板を液晶セルへ貼合する面側に用いられる。
本発明に関するセルロスアシレートフィルムの偏光子への貼り合せ方は、偏光子の透過軸と本発明に関するセルロースアシレートフィルムの遅相軸を一致させるように貼り合せることが好ましい。
なお、偏光板クロスニコル下で作製した偏光板は、本発明に関するセルロースアシレートフィルムの遅相軸と偏光子の吸収軸（透過軸と直交する軸）との直交精度が１°より大きいと、偏光板クロスニコル下での偏光度性能が低下して光抜けが生じ、液晶セルと組み合わせた場合に、十分な黒レベルやコントラストが得られない為、本発明に関するセルロースアシレートフィルムの主屈折率ｎｘの方向と偏光板の透過軸の方向とは、そのずれが１°以内、好ましくは０．５°以内であることが好ましい。
Polarizers for polarizing plates include iodine-based polarizers, dye-based polarizers using dichroic dyes, and polyene-based polarizers. The iodine polarizer and the dye polarizer are generally produced using a polyvinyl alcohol film. When the cellulose acylate film according to the present invention is used as a polarizing plate protective film, the production method of the polarizing plate is not particularly limited, and can be produced by a general method. For example, there is a method in which the obtained cellulose acylate film is treated with an alkali and bonded to both sides of a polarizer produced by immersing and stretching a polyvinyl alcohol film in an iodine solution using a completely saponified polyvinyl alcohol aqueous solution. Instead of alkali treatment, easy adhesion processing as described in JP-A-6-94915 and JP-A-6-118232 may be performed. Examples of the adhesive used to bond the protective film-treated surface and the polarizer include polyvinyl alcohol adhesives such as polyvinyl alcohol and polyvinyl butyral, vinyl latexes such as butyl acrylate, and the like. The polarizing plate is composed of a polarizer and a protective film that protects both surfaces of the polarizer, and a protective film may be bonded to one surface of the polarizing plate and a separate film may be bonded to the opposite surface. The protective film and the separate film are used for the purpose of protecting the polarizing plate at the time of shipping the polarizing plate and at the time of product inspection. In this case, the protect film is bonded for the purpose of protecting the surface of the polarizing plate, and is used on the side opposite to the surface where the polarizing plate is bonded to the liquid crystal cell. Moreover, a separate film is used in order to cover the contact bonding layer bonded to a liquid crystal cell, and is used for the surface side which bonds a polarizing plate to a liquid crystal cell.
The cellulosic acylate film relating to the present invention is preferably bonded to the polarizer so that the transmission axis of the polarizer coincides with the slow axis of the cellulose acylate film relating to the present invention.
In addition, the polarizing plate produced under polarizing plate crossed Nicol, when the accuracy of orthogonality between the slow axis of the cellulose acylate film according to the present invention and the absorption axis of the polarizer (axis orthogonal to the transmission axis) is greater than 1 °, Polarization degree performance under a polarizing plate crossed Nicole is reduced, light leakage occurs, and when combined with a liquid crystal cell, a sufficient black level and contrast cannot be obtained, so the main refractive index of the cellulose acylate film according to the present invention The deviation between the direction of nx and the direction of the transmission axis of the polarizing plate is preferably within 1 °, preferably within 0.5 °.
（表面処理）
本発明に関するセルロースアシレートフィルムは、場合により表面処理を行うことによって、セルロースアシレートフィルムと各機能層（例えば、下塗層およびバック層）との接着の向上を達成することができる。表面処理としては、例えばグロー放電処理、紫外線照射処理、コロナ処理、火炎処理、酸またはアルカリ処理を用いることができる。ここでいうグロー放電処理とは、１０-3〜２０Ｔｏｒｒの低圧ガス下でおこる低温プラズマでもよく、更にまた大気圧下でのプラズマ処理も好ましい。プラズマ励起性気体とは上記のような条件においてプラズマ励起される気体をいい、アルゴン、ヘリウム、ネオン、クリプトン、キセノン、窒素、二酸化炭素、テトラフルオロメタンの様なフロン類及びそれらの混合物などがあげられる。これらについては、詳細が発明協会公開技報公技番号２００１−１７４５号（２００１年３月１５日発行、発明協会）ｐ．３０−３２に詳細に記載されている。なお、近年注目されている大気圧でのプラズマ処理は、例えば１０〜１０００Ｋｅｖ下で２０〜５００Ｋｇｙの照射エネルギーが用いられ、より好ましくは３０〜５００Ｋｅｖ下で２０〜３００Ｋｇｙの照射エネルギーが用いられる。これらの中でも特に好ましくは、アルカリ鹸化処理でありセルロースアシレートフィルムの表面処理としては極めて有効である。
(surface treatment)
The cellulose acylate film according to the present invention can achieve improved adhesion between the cellulose acylate film and each functional layer (for example, the undercoat layer and the back layer) by optionally performing a surface treatment. As the surface treatment, for example, glow discharge treatment, ultraviolet irradiation treatment, corona treatment, flame treatment, acid or alkali treatment can be used. The glow discharge treatment here may be low-temperature plasma that occurs in a low-pressure gas of 10 −3 to 20 Torr, and plasma treatment under atmospheric pressure is also preferable. A plasma-excitable gas is a gas that is plasma-excited under the above conditions, and includes chlorofluorocarbons such as argon, helium, neon, krypton, xenon, nitrogen, carbon dioxide, tetrafluoromethane, and mixtures thereof. It is done. Regarding these, the details are disclosed in the Invention Association Public Technical Bulletin No. 2001-1745 (issued March 15, 2001, Invention Association) p. 30-32. Note that, in the plasma treatment at atmospheric pressure which has been attracting attention in recent years, for example, irradiation energy of 20 to 500 Kgy is used under 10 to 1000 Kev, and more preferably irradiation energy of 20 to 300 Kgy is used under 30 to 500 Kev. Among these, an alkali saponification treatment is particularly preferable, and it is extremely effective as a surface treatment of a cellulose acylate film.
アルカリ鹸化処理は、セルロースアシレートフィルムを鹸化液の槽に直接浸漬する方法または鹸化液をセルロースアシレートフィルム塗布する方法で実施することが好ましい。塗布方法としては、ディップコーティング法、カーテンコーティング法、エクストルージョンコーティング法、バーコーティング法およびＥ型塗布法を挙げることができる。アルカリ鹸化処理塗布液の溶媒は、鹸化液をセルロースアシレートフィルムに対して塗布するために、濡れ性が良く、また鹸化液溶媒によってセルロースアシレートフィルム表面に凹凸を形成させずに、面状を良好なまま保つ溶媒を選択することが好ましい。具体的には、アルコール系溶媒が好ましく、イソプロピルアルコールが特に好ましい。また、界面活性剤の水溶液を溶媒として使用することもできる。アルカリ鹸化塗布液のアルカリは、上記溶媒に溶解するアルカリが好ましく、ＫＯＨ、ＮａＯＨがさらに好ましい。鹸化塗布液のｐＨは１０以上が好ましく、１２以上がさらに好ましい。アルカリ鹸化時の反応条件は、室温で１秒以上５分以下が好ましく、５秒以上５分以下がさらに好ましく、２０秒以上３分以下が特に好ましい。アルカリ鹸化反応後、鹸化液塗布面を水洗あるいは酸で洗浄したあと水洗することが好ましい。 The alkali saponification treatment is preferably carried out by a method in which the cellulose acylate film is directly immersed in a saponification solution tank or a method in which the saponification solution is applied to the cellulose acylate film. Examples of the coating method include a dip coating method, a curtain coating method, an extrusion coating method, a bar coating method, and an E-type coating method. The solvent of the alkali saponification coating solution has good wettability in order to apply the saponification solution to the cellulose acylate film, and the surface of the cellulose acylate film surface is not formed by the saponification solution solvent. It is preferred to select a solvent that remains good. Specifically, an alcohol solvent is preferable, and isopropyl alcohol is particularly preferable. An aqueous solution of a surfactant can also be used as a solvent. The alkali of the alkali saponification coating solution is preferably an alkali that dissolves in the above solvent, and more preferably KOH or NaOH. The pH of the saponification coating solution is preferably 10 or more, more preferably 12 or more. The reaction conditions during alkali saponification are preferably 1 second to 5 minutes at room temperature, more preferably 5 seconds to 5 minutes, and particularly preferably 20 seconds to 3 minutes. After the alkali saponification reaction, it is preferable to wash the surface on which the saponification solution is applied with water or with an acid and then with water.
また、本発明の偏光板は、偏光板の他方の側の保護膜の表面にハードコート層、防眩層、反射防止層の少なくとも一層を設けたものであるのが好ましい。すなわち、偏光板の液晶表示装置への使用時において液晶セルと反対側に配置される保護膜（ＴＡＣ２）には反射防止層などの機能性膜を設けることが好ましく、かかる機能性膜としてハードコート層、防眩層、反射防止層の少なくとも一層を設けるのが好ましい。なお、各層はそれぞれ別個の層として設ける必要はなく、例えば、防眩層を、反射防止層やハードコート層にその機能を持たせることにより反射防止層を反射防止層及び防眩層として機能させることにより設けても良い。（図１） In the polarizing plate of the present invention, it is preferable that at least one layer of a hard coat layer, an antiglare layer and an antireflection layer is provided on the surface of the protective film on the other side of the polarizing plate. That is, when the polarizing plate is used for a liquid crystal display device, it is preferable to provide a functional film such as an antireflection layer on the protective film (TAC2) disposed on the side opposite to the liquid crystal cell. It is preferable to provide at least one of a layer, an antiglare layer, and an antireflection layer. Each layer does not need to be provided as a separate layer. For example, the antiglare layer functions as an antireflection layer and an antiglare layer by providing the antireflection layer and the hard coat layer with the function. May be provided. (Figure 1)
（反射防止層）
本発明では、保護膜上に少なくとも光散乱層と低屈折率層がこの順で積層されてなる反射防止層又は保護膜上に中屈折率層、高屈折率層、低屈折率層がこの順で積層した反射防止層が好適に用いられる。以下にそれらの好ましい例を記載する。
(Antireflection layer)
In the present invention, at least the light scattering layer and the low refractive index layer are laminated in this order on the protective film, or the intermediate refractive index layer, the high refractive index layer, and the low refractive index layer are arranged in this order on the protective film. The antireflection layer laminated with is preferably used. Preferred examples thereof are described below.
保護膜上に光散乱層と低屈折率層を設けた反射防止層の好ましい例について述べる。
光散乱層には、マット粒子が分散されているのが好ましく、光散乱層のマット粒子以外の部分の素材の屈折率は１．５０〜２．００の範囲にあることが好ましく、低屈折率層の屈折率は１．２０〜１．４９の範囲にあることが好ましい。本発明において光散乱層は、防眩性とハードコート性を兼ね備えており、１層でもよいし、複数層、例えば２層〜４層で構成されていてもよい。
A preferred example of an antireflection layer in which a light scattering layer and a low refractive index layer are provided on a protective film will be described.
In the light scattering layer, mat particles are preferably dispersed, and the refractive index of the material other than the mat particles in the light scattering layer is preferably in the range of 1.50 to 2.00, and the low refractive index The refractive index of the layer is preferably in the range of 1.20 to 1.49. In the present invention, the light scattering layer has both antiglare properties and hard coat properties, and may be a single layer or a plurality of layers, for example, 2 to 4 layers.
反射防止層は、その表面凹凸形状として、中心線平均粗さＲａが０．０８〜０．４０μｍ、１０点平均粗さＲｚがＲａの１０倍以下、平均山谷距離Ｓｍが１〜１００μｍ、凹凸最深部からの凸部高さの標準偏差が０．５μｍ以下、中心線を基準とした平均山谷距離Ｓｍの標準偏差が２０μｍ以下、傾斜角０〜５度の面が１０％以上となるように設計することで、十分な防眩性と目視での均一なマット感が達成され、好ましい。また、Ｃ光源下での反射光の色味がａ*値−２〜２、ｂ*値−３〜３、３８０ｎｍ〜７８０ｎｍの範囲内での反射率の最小値と最大値の比０．５〜０．９９であることで、反射光の色味がニュートラルとなり、好ましい。またＣ光源下での透過光のｂ*値が０〜３とすることで、表示装置に適用した際の白表示の黄色味が低減され、好ましい。また、面光源上と本発明の反射防止フィルムの間に１２０μｍ×４０μｍの格子を挿入してフィルム上で輝度分布を測定した際の輝度分布の標準偏差が２０以下であると、高精細パネルに本発明のフィルムを適用したときのギラツキが低減され、好ましい。 The antireflection layer has an uneven surface shape with a center line average roughness Ra of 0.08 to 0.40 μm, a 10-point average roughness Rz of 10 times or less of Ra, an average mountain valley distance Sm of 1 to 100 μm, and an uneven depth. Designed so that the standard deviation of the height of the convex part from the part is 0.5 μm or less, the standard deviation of the average mountain valley distance Sm with respect to the center line is 20 μm or less, and the surface with the inclination angle of 0 to 5 degrees is 10% or more. By doing so, sufficient anti-glare properties and a visually uniform matte feeling are achieved, which is preferable. Further, the ratio of the minimum value and the maximum value of the reflectance within the range of a * value −2 to 2, b * value −3 to 3, and 380 nm to 780 nm under the light source C is 0.5. By being -0.99, the color of reflected light becomes neutral, which is preferable. Moreover, it is preferable that the b * value of the transmitted light under the C light source is 0 to 3 because the yellow color of white display when applied to a display device is reduced. In addition, when a 120 μm × 40 μm grid is inserted between the surface light source and the antireflection film of the present invention and the luminance distribution is measured on the film, the standard deviation of the luminance distribution is 20 or less. The glare when applying the film of the present invention is reduced, which is preferable.
本発明で用いることができる反射防止層は、その光学特性として、鏡面反射率２．５％以下、透過率９０％以上、６０度光沢度７０％以下とすることで、外光の反射を抑制でき、視認性が向上するため好ましい。特に鏡面反射率は１％以下がより好ましく、０.５％以下であることが最も好ましい。ヘイズ２０％〜５０％、内部ヘイズ／全ヘイズ値の比が０．３〜１、光散乱層までのヘイズ値から低屈折率層を形成後のヘイズ値の低下が１５％以内、くし幅０．５ｍｍにおける透過像鮮明度２０％〜５０％、垂直透過光／垂直から２度傾斜方向の透過率比が１．５〜５．０とすることで、高精細ＬＣＤパネル上でのギラツキ防止、文字等のボケの低減が達成され、好ましい。 The antireflective layer that can be used in the present invention suppresses reflection of external light by setting its optical characteristics to a specular reflectance of 2.5% or less, a transmittance of 90% or more, and a 60 degree gloss of 70% or less. This is preferable because visibility is improved. In particular, the specular reflectance is more preferably 1% or less, and most preferably 0.5% or less. Haze 20% to 50%, ratio of internal haze / total haze value 0.3 to 1, haze value after formation of low refractive index layer from haze value up to light scattering layer within 15%, comb width 0 .Transmission image sharpness at 5 mm to 20% to 50%, vertical transmission light / transmittance ratio of 2 degrees from vertical to 1.5 to 5.0, preventing glare on a high-definition LCD panel, Reduction of blurring of characters and the like is achieved, which is preferable.
（低屈折率層）
本発明で用いることができる低屈折率層の屈折率は、好ましくは１．２０〜１．４９であり、更に好ましくは１．３０〜１．４４の範囲にある。さらに、低屈折率層は下記式を満たすことが低反射率化の点で好ましい。
（ｍ／４）λ×０．７＜ｎ１ｄ１＜（ｍ／４）λ×１．３
式中、ｍは正の奇数であり、ｎ１は低屈折率層の屈折率であり、そして、ｄ１は低屈折率層の膜厚（ｎｍ）である。また、λは波長であり、５００〜５５０ｎｍの範囲の値である。
(Low refractive index layer)
The refractive index of the low refractive index layer that can be used in the present invention is preferably 1.20 to 1.49, more preferably 1.30 to 1.44. Further, the low refractive index layer preferably satisfies the following formula from the viewpoint of reducing the reflectance.
(M / 4) λ × 0.7 <n1d1 <(m / 4) λ × 1.3
In the formula, m is a positive odd number, n1 is the refractive index of the low refractive index layer, and d1 is the film thickness (nm) of the low refractive index layer. Further, λ is a wavelength, which is a value in the range of 500 to 550 nm.
低屈折率層を形成する素材について以下に説明する。
低屈折率層は、低屈折率バインダーとして、含フッ素ポリマーを含むことが好ましい。フッ素ポリマーとしては動摩擦係数０．０３〜０．２０、水に対する接触角９０〜１２０°、純水の滑落角が７０°以下の熱または電離放射線により架橋する含フッ素ポリマーが好ましい。本発明の偏光板を画像表示装置に装着した時、市販の接着テープとの剥離力が低いほどシールやメモを貼り付けた後に剥がれ易くなり好ましく、引張り試験機で測定した場合に５００ｇｆ以下が好ましく、３００ｇｆ以下がより好ましく、１００ｇｆ以下が最も好ましい。また、微小硬度計で測定した表面硬度が高いほど、傷がつき難く、０．３ＧＰａ以上が好ましく、０．５ＧＰａ以上がより好ましい。
The material for forming the low refractive index layer will be described below.
The low refractive index layer preferably contains a fluorine-containing polymer as a low refractive index binder. The fluorine polymer is preferably a fluorine-containing polymer that is crosslinked by heat or ionizing radiation having a coefficient of dynamic friction of 0.03 to 0.20, a contact angle with water of 90 to 120 °, and a sliding angle of pure water of 70 ° or less. When the polarizing plate of the present invention is mounted on an image display device, the lower the peel strength from a commercially available adhesive tape, the easier it is to peel off after sticking a sticker or memo, preferably 500 gf or less when measured with a tensile tester. 300 gf or less is more preferable, and 100 gf or less is most preferable. Further, the higher the surface hardness measured with a microhardness meter, the harder it is to scratch, preferably 0.3 GPa or more, more preferably 0.5 GPa or more.
低屈折率層に用いられる含フッ素ポリマーとしてはパーフルオロアルキル基含有シラン化合物（例えば（ヘプタデカフルオロ−１，１，２，２−テトラヒドロデシル）トリエトキシシラン）の加水分解に引き続く脱水縮合物の他、含フッ素モノマー単位と架橋反応性付与のための構成単位を構成成分とする含フッ素共重合体が挙げられる。 Examples of the fluorine-containing polymer used in the low refractive index layer include dehydration condensates subsequent to hydrolysis of perfluoroalkyl group-containing silane compounds (for example, (heptadecafluoro-1,1,2,2-tetrahydrodecyl) triethoxysilane). In addition, a fluorine-containing copolymer having a fluorine-containing monomer unit and a structural unit for imparting crosslinking reactivity as constituent components can be mentioned.
含フッ素モノマーの具体例としては、例えばフルオロオレフィン類（例えばフルオロエチレン、ビニリデンフルオライド、テトラフルオロエチレン、パーフルオロオクチルエチレン、ヘキサフルオロプロピレン、パーフルオロ−２，２−ジメチル−１，３−ジオキソール等）、（メタ）アクリル酸の部分または完全フッ素化アルキルエステル誘導体類（例えばビスコート６ＦＭ（大阪有機化学製）やＭ−２０２０（ダイキン製）等）、完全または部分フッ素化ビニルエーテル類等が挙げられるが、好ましくはパーフルオロオレフィン類であり、屈折率、溶解性、透明性、入手性等の観点から特に好ましくはヘキサフルオロプロピレンである。 Specific examples of the fluorine-containing monomer include fluoroolefins (for example, fluoroethylene, vinylidene fluoride, tetrafluoroethylene, perfluorooctylethylene, hexafluoropropylene, perfluoro-2,2-dimethyl-1,3-dioxole, etc. ), A part of (meth) acrylic acid or a fully fluorinated alkyl ester derivative (for example, Biscoat 6FM (manufactured by Osaka Organic Chemicals) or M-2020 (manufactured by Daikin)), a complete or partially fluorinated vinyl ether, and the like. Perfluoroolefins are preferred, and hexafluoropropylene is particularly preferred from the viewpoints of refractive index, solubility, transparency, availability, and the like.
架橋反応性付与のための構成単位としては、グリシジル（メタ）アクリレート、グリシジルビニルエーテルのように分子内にあらかじめ自己架橋性官能基を有するモノマーの重合によって得られる構成単位、カルボキシル基やヒドロキシ基、アミノ基、スルホ基等を有するモノマー（例えば（メタ）アクリル酸、メチロール（メタ）アクリレート、ヒドロキシアルキル（メタ）アクリレート、アリルアクリレート、ヒドロキシエチルビニルエーテル、ヒドロキシブチルビニルエーテル、マレイン酸、クロトン酸等）の重合によって得られる構成単位、これらの構成単位に高分子反応によって（メタ）アクリルロイル基等の架橋反応性基を導入した構成単位（例えばヒドロキシ基に対してアクリル酸クロリドを作用させる等の手法で導入できる）が挙げられる。 As structural units for imparting crosslinking reactivity, structural units obtained by polymerization of monomers having a self-crosslinkable functional group in the molecule in advance such as glycidyl (meth) acrylate and glycidyl vinyl ether, carboxyl groups, hydroxy groups, amino acids Polymerization of monomers having a group, a sulfo group, etc. (eg (meth) acrylic acid, methylol (meth) acrylate, hydroxyalkyl (meth) acrylate, allyl acrylate, hydroxyethyl vinyl ether, hydroxybutyl vinyl ether, maleic acid, crotonic acid, etc.) The resulting structural unit, a structural unit in which a crosslinking reactive group such as a (meth) acryloyl group is introduced into these structural units by a polymer reaction (for example, an acrylic acid chloride is allowed to act on a hydroxy group). And the like.
また上記含フッ素モノマー単位、架橋反応性付与のための構成単位以外に溶剤への溶解性、皮膜の透明性等の観点から適宜フッ素原子を含有しないモノマーを共重合することもできる。併用可能なモノマー単位には特に限定はなく、例えばオレフィン類（エチレン、プロピレン、イソプレン、塩化ビニル、塩化ビニリデン等）、アクリル酸エステル類（アクリル酸メチル、アクリル酸メチル、アクリル酸エチル、アクリル酸２−エチルヘキシル）、メタクリル酸エステル類（メタクリル酸メチル、メタクリル酸エチル、メタクリル酸ブチル、エチレングリコールジメタクリレート等）、スチレン誘導体（スチレン、ジビニルベンゼン、ビニルトルエン、α−メチルスチレン等）、ビニルエーテル類（メチルビニルエーテル、エチルビニルエーテル、シクロヘキシルビニルエーテル等）、ビニルエステル類（酢酸ビニル、プロピオン酸ビニル、桂皮酸ビニル等）、アクリルアミド類（Ｎ−ｔｅｒｔ−ブチルアクリルアミド、Ｎ−シクロヘキシルアクリルアミド等）、メタクリルアミド類、アクリロ二トリル誘導体等を挙げることができる。 In addition to the above-mentioned fluorine-containing monomer units and structural units for imparting crosslinking reactivity, monomers not containing fluorine atoms can be copolymerized as appropriate from the viewpoints of solubility in solvents and film transparency. There are no particular limitations on the monomer units that can be used in combination. For example, olefins (ethylene, propylene, isoprene, vinyl chloride, vinylidene chloride, etc.), acrylic esters (methyl acrylate, methyl acrylate, ethyl acrylate, acrylic acid 2) -Ethylhexyl), methacrylates (methyl methacrylate, ethyl methacrylate, butyl methacrylate, ethylene glycol dimethacrylate, etc.), styrene derivatives (styrene, divinylbenzene, vinyl toluene, α-methylstyrene, etc.), vinyl ethers (methyl) Vinyl ether, ethyl vinyl ether, cyclohexyl vinyl ether, etc.), vinyl esters (vinyl acetate, vinyl propionate, vinyl cinnamate etc.), acrylamides (N-tert-butylacrylamide, N- Black hexyl acrylamide), methacrylamides, and acrylonitrile derivatives.
上記のポリマーに対しては特開平１０−２５３８８号および特開平１０−１４７７３９号各公報に記載のごとく適宜硬化剤を併用しても良い。 As described in JP-A-10-25388 and JP-A-10-147739, a curing agent may be appropriately used in combination with the above polymer.
（光散乱層）
光散乱層は、表面散乱および内部散乱の少なくともいずれかによる光拡散性と、フィルムの耐擦傷性を向上するためのハードコート性をフィルムに付与する目的で形成される。従って、ハードコート性を付与するためのバインダー、光拡散性を付与するためのマット粒子、および必要に応じて高屈折率化、架橋収縮防止、高強度化のための無機フィラーを含んで形成される。また、このような光散乱層を設けることにより、該光散乱層が防眩層としても機能し、偏光板が防眩層を有することになる。
(Light scattering layer)
The light scattering layer is formed for the purpose of imparting to the film a light diffusibility due to at least one of surface scattering and internal scattering and a hard coat property for improving the scratch resistance of the film. Therefore, it is formed to contain a binder for imparting hard coat properties, matte particles for imparting light diffusibility, and inorganic fillers for increasing the refractive index, preventing cross-linking shrinkage, and increasing the strength as necessary. The Further, by providing such a light scattering layer, the light scattering layer also functions as an antiglare layer, and the polarizing plate has an antiglare layer.
光散乱層の膜厚は、ハードコート性を付与する目的で、１〜１０μｍが好ましく、１．２〜６μｍがより好ましい。薄すぎるとハード性が不足し、厚すぎるとカールや脆性が悪化して加工適性が不足となる。 The thickness of the light scattering layer is preferably 1 to 10 μm and more preferably 1.2 to 6 μm for the purpose of imparting hard coat properties. If it is too thin, the hard property will be insufficient, and if it is too thick, curling and brittleness will deteriorate and the workability will be insufficient.
光散乱層のバインダーとしては、飽和炭化水素鎖またはポリエーテル鎖を主鎖として有するポリマーであることが好ましく、飽和炭化水素鎖を主鎖として有するポリマーであることがさらに好ましい。また、バインダーポリマーは架橋構造を有することが好ましい。飽和炭化水素鎖を主鎖として有するバインダーポリマーとしては、エチレン性不飽和モノマーの重合体が好ましい。飽和炭化水素鎖を主鎖として有し、かつ架橋構造を有するバインダーポリマーとしては、二個以上のエチレン性不飽和基を有するモノマーの（共）重合体が好ましい。バインダーポリマーを高屈折率にするには、このモノマーの構造中に芳香族環や、フッ素以外のハロゲン原子、硫黄原子、リン原子、及び窒素原子から選ばれた少なくとも１種の原子を含むものを選択することもできる。 The binder of the light scattering layer is preferably a polymer having a saturated hydrocarbon chain or a polyether chain as the main chain, and more preferably a polymer having a saturated hydrocarbon chain as the main chain. The binder polymer preferably has a crosslinked structure. As the binder polymer having a saturated hydrocarbon chain as a main chain, a polymer of an ethylenically unsaturated monomer is preferable. As the binder polymer having a saturated hydrocarbon chain as the main chain and having a crosslinked structure, a (co) polymer of monomers having two or more ethylenically unsaturated groups is preferable. In order to make the binder polymer have a high refractive index, the monomer structure contains an aromatic ring, at least one atom selected from halogen atoms other than fluorine, sulfur atoms, phosphorus atoms, and nitrogen atoms. You can also choose.
二個以上のエチレン性不飽和基を有するモノマーとしては、多価アルコールと（メタ）アクリル酸とのエステル（例、エチレングリコールジ（メタ）アクリレート、ブタンジオールジ（メタ）アクリレート、ヘキサンジオールジ（メタ）アクリレート、１，４−シクロヘキサンジアクリレート、ペンタエリスリトールテトラ（メタ）アクリレート）、ペンタエリスリトールトリ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、トリメチロールエタントリ（メタ）アクリレート、ジペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールペンタ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、ペンタエリスリトールヘキサ（メタ）アクリレート、１，２，３−シクロヘキサンテトラメタクリレート、ポリウレタンポリアクリレート、ポリエステルポリアクリレート）、上記のエチレンオキサイド変性体、ビニルベンゼンおよびその誘導体（例、１，４−ジビニルベンゼン、４−ビニル安息香酸−２−アクリロイルエチルエステル、１，４−ジビニルシクロヘキサノン）、ビニルスルホン（例、ジビニルスルホン）、アクリルアミド（例、メチレンビスアクリルアミド）およびメタクリルアミドが挙げられる。上記モノマーは２種以上併用してもよい。 Examples of the monomer having two or more ethylenically unsaturated groups include esters of polyhydric alcohol and (meth) acrylic acid (eg, ethylene glycol di (meth) acrylate, butanediol di (meth) acrylate, hexanediol di ( (Meth) acrylate, 1,4-cyclohexanediacrylate, pentaerythritol tetra (meth) acrylate), pentaerythritol tri (meth) acrylate, trimethylolpropane tri (meth) acrylate, trimethylolethane tri (meth) acrylate, dipentaerythritol Tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, pentaerythritol hexa (meth) acrylate, 1,2,3-si Rhohexanetetramethacrylate, polyurethane polyacrylate, polyester polyacrylate), modified ethylene oxide, vinylbenzene and derivatives thereof (eg, 1,4-divinylbenzene, 4-vinylbenzoic acid-2-acryloylethyl ester, 1, 4-divinylcyclohexanone), vinyl sulfone (eg, divinyl sulfone), acrylamide (eg, methylenebisacrylamide) and methacrylamide. Two or more of these monomers may be used in combination.
高屈折率モノマーの具体例としては、ビス（４−メタクリロイルチオフェニル）スルフィド、ビニルナフタレン、ビニルフェニルスルフィド、４−メタクリロキシフェニル−４'−メトキシフェニルチオエーテル等が挙げられる。これらのモノマーも２種以上併用してもよい。 Specific examples of the high refractive index monomer include bis (4-methacryloylthiophenyl) sulfide, vinyl naphthalene, vinyl phenyl sulfide, 4-methacryloxyphenyl-4′-methoxyphenyl thioether, and the like. Two or more of these monomers may be used in combination.
これらのエチレン性不飽和基を有するモノマーの重合は、光ラジカル開始剤あるいは熱ラジカル開始剤の存在下、電離放射線の照射または加熱により行うことができる。
従って、エチレン性不飽和基を有するモノマー、光ラジカル開始剤あるいは熱ラジカル開始剤、マット粒子および無機フィラーを含有する塗液を調製し、該塗液を保護膜上に塗布後電離放射線または熱による重合反応により硬化して反射防止膜を形成することができる。これらの光ラジカル開始剤等は公知のものを使用することができる。
Polymerization of the monomer having an ethylenically unsaturated group can be performed by irradiation with ionizing radiation or heating in the presence of a photo radical initiator or a thermal radical initiator.
Therefore, a coating liquid containing a monomer having an ethylenically unsaturated group, a photo radical initiator or a thermal radical initiator, mat particles, and an inorganic filler is prepared, and the coating liquid is applied onto a protective film and then ionizing radiation or heat. It can be cured by a polymerization reaction to form an antireflection film. As these photo radical initiators, known ones can be used.
ポリエーテルを主鎖として有するポリマーは、多官能エポシキシ化合物の開環重合体が好ましい。多官能エポシキ化合物の開環重合は、光酸発生剤あるいは熱酸発生剤の存在下、電離放射線の照射または加熱により行うことができる。
従って、多官能エポシキシ化合物、光酸発生剤あるいは熱酸発生剤、マット粒子および無機フィラーを含有する塗液を調製し、該塗液を保護膜上に塗布後電離放射線または熱による重合反応により硬化して反射防止膜を形成することができる。
The polymer having a polyether as the main chain is preferably a ring-opening polymer of a polyfunctional epoxy compound. The ring-opening polymerization of the polyfunctional epoxy compound can be performed by irradiation with ionizing radiation or heating in the presence of a photoacid generator or a thermal acid generator.
Therefore, a coating solution containing a polyfunctional epoxy compound, a photoacid generator or a thermal acid generator, matte particles and an inorganic filler is prepared, and the coating solution is applied on a protective film and then cured by ionizing radiation or heat polymerization reaction. Thus, an antireflection film can be formed.
二個以上のエチレン性不飽和基を有するモノマーの代わりにまたはそれに加えて、架橋性官能基を有するモノマーを用いてポリマー中に架橋性官能基を導入し、この架橋性官能基の反応により、架橋構造をバインダーポリマーに導入してもよい。
架橋性官能基の例には、イソシアナート基、エポキシ基、アジリジン基、オキサゾリン基、アルデヒド基、カルボニル基、ヒドラジン基、カルボキシル基、メチロール基および活性メチレン基が含まれる。ビニルスルホン酸、酸無水物、シアノアクリレート誘導体、メラミン、エーテル化メチロール、エステルおよびウレタン、テトラメトキシシランのような金属アルコキシドも、架橋構造を導入するためのモノマーとして利用できる。ブロックイソシアナート基のように、分解反応の結果として架橋性を示す官能基を用いてもよい。すなわち、本発明において架橋性官能基は、すぐには反応を示すものではなくとも、分解した結果反応性を示すものであってもよい。
これら架橋性官能基を有するバインダーポリマーは塗布後、加熱することによって架橋構造を形成することができる。
Instead of or in addition to a monomer having two or more ethylenically unsaturated groups, a monomer having a crosslinkable functional group is used to introduce a crosslinkable functional group into the polymer, and by reaction of this crosslinkable functional group, A crosslinked structure may be introduced into the binder polymer.
Examples of the crosslinkable functional group include isocyanate group, epoxy group, aziridine group, oxazoline group, aldehyde group, carbonyl group, hydrazine group, carboxyl group, methylol group and active methylene group. Vinylsulfonic acid, acid anhydride, cyanoacrylate derivative, melamine, etherified methylol, ester and urethane, and metal alkoxide such as tetramethoxysilane can also be used as a monomer for introducing a crosslinked structure. A functional group that exhibits crosslinkability as a result of the decomposition reaction, such as a block isocyanate group, may be used. That is, in the present invention, the crosslinkable functional group may not react immediately but may exhibit reactivity as a result of decomposition.
These binder polymers having a crosslinkable functional group can form a crosslinked structure by heating after coating.
光散乱層には、防眩性付与の目的で、フィラー粒子より大きく、平均粒径が１〜１０μｍ、好ましくは１．５〜７．０μｍのマット粒子、例えば無機化合物の粒子または樹脂粒子が含有される。
上記マット粒子の具体例としては、例えばシリカ粒子、ＴｉＯ2粒子等の無機化合物の粒子；アクリル粒子、架橋アクリル粒子、ポリスチレン粒子、架橋スチレン粒子、メラミン樹脂粒子、ベンゾグアナミン樹脂粒子等の樹脂粒子が好ましく挙げられる。なかでも架橋スチレン粒子、架橋アクリル粒子、架橋アクリルスチレン粒子、シリカ粒子が好ましい。マット粒子の形状は、球状あるいは不定形のいずれも使用できる。
For the purpose of imparting antiglare properties, the light scattering layer contains matte particles having an average particle size of 1 to 10 μm, preferably 1.5 to 7.0 μm, such as inorganic compound particles or resin particles, for the purpose of imparting antiglare properties. Is done.
As specific examples of the mat particles, inorganic particles such as silica particles and TiO 2 particles; resin particles such as acrylic particles, cross-linked acrylic particles, polystyrene particles, cross-linked styrene particles, melamine resin particles, and benzoguanamine resin particles are preferable. Can be mentioned. Of these, crosslinked styrene particles, crosslinked acrylic particles, crosslinked acrylic styrene particles, and silica particles are preferable. The shape of the mat particles can be either spherical or irregular.
また、粒子径の異なる２種以上のマット粒子を併用して用いてもよい。より大きな粒子径のマット粒子で防眩性を付与し、より小さな粒子径のマット粒子で別の光学特性を付与することが可能である。 Two or more kinds of mat particles having different particle diameters may be used in combination. It is possible to impart anti-glare properties with mat particles having a larger particle size and to impart other optical characteristics with mat particles having a smaller particle size.
さらに、上記マット粒子の粒子径分布としては単分散であることが最も好ましく、各粒子の粒子径は、それぞれ同一に近ければ近いほど良い。例えば平均粒子径よりも２０％以上粒子径が大きな粒子を粗大粒子と規定した場合には、この粗大粒子の割合は全粒子数の１％以下であることが好ましく、より好ましくは０．１％以下であり、さらに好ましくは０．０１％以下である。このような粒子径分布を持つマット粒子は通常の合成反応後に、分級によって得られ、分級の回数を上げることやその程度を強くすることにより、より好ましい分布のマット剤を得ることができる。 Furthermore, the particle size distribution of the mat particles is most preferably monodisperse, and the particle sizes of the particles are preferably closer to each other. For example, when a particle having a particle size of 20% or more than the average particle size is defined as a coarse particle, the proportion of the coarse particle is preferably 1% or less, more preferably 0.1% of the total number of particles. Or less, more preferably 0.01% or less. Matt particles having such a particle size distribution are obtained by classification after a normal synthesis reaction, and a matting agent having a more preferable distribution can be obtained by increasing the number of classifications or increasing the degree of classification.
上記マット粒子は、形成された光散乱層のマット粒子量が好ましくは１０〜１０００ｍｇ／ｍ2、より好ましくは１００〜７００ｍｇ／ｍ2となるように光散乱層に含有される。
マット粒子の粒度分布はコールターカウンター法により測定し、測定された分布を粒子数分布に換算する。
The mat particles are contained in the light scattering layer so that the amount of mat particles in the formed light scattering layer is preferably 10 to 1000 mg / m 2 , more preferably 100 to 700 mg / m 2 .
The particle size distribution of the mat particles is measured by a Coulter counter method, and the measured distribution is converted into a particle number distribution.
光散乱層には、層の屈折率を高めるために、上記のマット粒子に加えて、チタン、ジルコニウム、アルミニウム、インジウム、亜鉛、錫、アンチモンのうちより選ばれる少なくとも１種の金属の酸化物からなり、平均粒径が０．２μｍ以下、好ましくは０．１μｍ以下、より好ましくは０．０６μｍ以下である無機フィラーが含有されることが好ましい。
また逆に、マット粒子との屈折率差を大きくするために、高屈折率マット粒子を用いた光散乱層では層の屈折率を低目に保つためにケイ素の酸化物を用いることも好ましい。好ましい粒径は前述の無機フィラーと同じである。
光散乱層に用いられる無機フィラーの具体例としては、ＴｉＯ2、ＺｒＯ2、Ａｌ2Ｏ3、Ｉｎ2Ｏ3、ＺｎＯ、ＳｎＯ2、Ｓｂ2Ｏ3、ＩＴＯとＳｉＯ2等が挙げられる。ＴｉＯ2およびＺｒＯ2が高屈折率化の点で特に好ましい。該無機フィラーは表面をシランカップリング処理又はチタンカップリング処理されることも好ましく、フィラー表面にバインダー種と反応できる官能基を有する表面処理剤が好ましく用いられる。
これらの無機フィラーの添加量は、光散乱層の全質量の１０〜９０％であることが好ましく、より好ましくは２０〜８０％であり、特に好ましくは３０〜７５％である。
なお、このようなフィラーは、粒径が光の波長よりも十分小さいために散乱が生じず、バインダーポリマーに該フィラーが分散した分散体は光学的に均一な物質として振舞う。
The light scattering layer is made of an oxide of at least one metal selected from titanium, zirconium, aluminum, indium, zinc, tin, and antimony, in addition to the above mat particles, in order to increase the refractive index of the layer. Thus, it is preferable that an inorganic filler having an average particle size of 0.2 μm or less, preferably 0.1 μm or less, more preferably 0.06 μm or less is contained.
Conversely, in order to increase the refractive index difference from the mat particles, it is also preferable to use a silicon oxide in order to keep the refractive index of the layer low in the light scattering layer using the high refractive index mat particles. The preferred particle size is the same as that of the aforementioned inorganic filler.
Specific examples of the inorganic filler to be used in the light scattering layer, TiO 2, ZrO 2, Al 2 O 3, In 2 O 3, ZnO, SnO 2, Sb 2 O 3, ITO and SiO 2 and the like. TiO 2 and ZrO 2 are particularly preferable from the viewpoint of increasing the refractive index. The surface of the inorganic filler is preferably subjected to a silane coupling treatment or a titanium coupling treatment, and a surface treatment agent having a functional group capable of reacting with a binder species on the filler surface is preferably used.
The amount of these inorganic fillers added is preferably 10 to 90% of the total mass of the light scattering layer, more preferably 20 to 80%, and particularly preferably 30 to 75%.
In addition, since such a filler has a particle size sufficiently smaller than the wavelength of light, scattering does not occur, and a dispersion in which the filler is dispersed in a binder polymer behaves as an optically uniform substance.
光散乱層のバインダーおよび無機フィラーの混合物のバルクの屈折率は、１．５０〜２．００であることが好ましく、より好ましくは１．５１〜１．８０である。屈折率を上記範囲とするには、バインダー及び無機フィラーの種類及び量割合を適宜選択すればよい。どのように選択するかは、予め実験的に容易に知ることができる。 The bulk refractive index of the mixture of binder and inorganic filler in the light scattering layer is preferably 1.50 to 2.00, more preferably 1.51 to 1.80. In order to make the refractive index within the above range, the kind and amount ratio of the binder and the inorganic filler may be appropriately selected. How to select can be easily known experimentally in advance.
光散乱層は、特に塗布ムラ、乾燥ムラ、点欠陥等の面状均一性を確保するために、フッ素系、シリコーン系の何れかの界面活性剤、あるいはその両者を光散乱層形成用の塗布組成物中に含有する。特にフッ素系の界面活性剤は、より少ない添加量において、本発明の反射防止フィルムの塗布ムラ、乾燥ムラ、点欠陥等の面状故障を改良する効果が現れるため、好ましく用いられる。面状均一性を高めつつ、高速塗布適性を持たせることにより生産性を高めることが目的である。 In order to ensure surface uniformity such as uneven coating, uneven drying, point defects, etc., the light scattering layer should be coated with either a fluorine-based surfactant or a silicone-based surfactant, or both for forming the light scattering layer. Contained in the composition. In particular, a fluorine-based surfactant is preferably used because an effect of improving surface defects such as coating unevenness, drying unevenness, and point defects of the antireflection film of the present invention appears in a smaller addition amount. The purpose is to increase productivity by giving high-speed coating suitability while improving surface uniformity.
次に保護膜上に中屈折率層、高屈折率層、低屈折率層がこの順で積層された反射防止層について述べる。
保護膜上に少なくとも中屈折率層、高屈折率層、低屈折率層（最外層）の順序の層構成から成る反射防止層は、以下の関係を満足する屈折率を有する様に設計される。
高屈折率層の屈折率＞中屈折率層の屈折率＞保護膜の屈折率＞低屈折率層の屈折率
また、保護膜と中屈折率層の間に、ハードコート層を設けてもよい。更には、中屈折率ハードコート層、高屈折率層及び低屈折率層からなってもよい。
例えば、特開平８−１２２５０４号公報、同８−１１０４０１号公報、同１０−３００９０２号公報、特開２００２−２４３９０６号公報、特開２０００−１１１７０６号公報等に記載の反射防止層が挙げられる。
また、各層に他の機能を付与させてもよく、例えば、防汚性の低屈折率層、帯電防止性の高屈折率層としたもの（例、特開平１０−２０６６０３号公報、特開２００２−２４３９０６号公報等）等が挙げられる。
反射防止層のヘイズは、５％以下あることが好ましく、３％以下がさらに好ましい。また、膜の強度は、ＪＩＳ Ｋ５４００に従う鉛筆硬度試験でＨ以上であることが好ましく、２Ｈ以上であることがさらに好ましく、３Ｈ以上であることが最も好ましい。
Next, an antireflection layer in which a middle refractive index layer, a high refractive index layer, and a low refractive index layer are laminated in this order on the protective film will be described.
The antireflection layer comprising at least a middle refractive index layer, a high refractive index layer, and a low refractive index layer (outermost layer) in order on the protective film is designed to have a refractive index satisfying the following relationship. .
High refractive index layer refractive index> Medium refractive index layer refractive index> Protective film refractive index> Low refractive index layer refractive index A hard coat layer may be provided between the protective film and the medium refractive index layer. . Further, it may comprise a medium refractive index hard coat layer, a high refractive index layer and a low refractive index layer.
Examples thereof include antireflection layers described in JP-A-8-122504, JP-A-8-110401, JP-A-10-300902, JP-A-2002-243906, JP-A-2000-11706, and the like.
Other functions may be imparted to each layer, for example, an antifouling low refractive index layer or an antistatic high refractive index layer (eg, JP-A-10-206603, JP-A-2002). -243906 publication etc.) etc. are mentioned.
The haze of the antireflection layer is preferably 5% or less, more preferably 3% or less. The strength of the film is preferably H or more, more preferably 2H or more, and most preferably 3H or more in a pencil hardness test according to JIS K5400.
（高屈折率層および中屈折率層）
反射防止膜の高い屈折率を有する層は、平均粒径１００ｎｍ以下の高屈折率の無機化合物微粒子及びマトリックスバインダーを少なくとも含有する硬化膜から成る。
高屈折率の無機化合物微粒子としては、屈折率１．６５以上の無機化合物が挙げられ、好ましくは屈折率１．９以上のものが挙げられる。例えば、Ｔｉ、Ｚｎ、Ｓｂ、Ｓｎ、Ｚｒ、Ｃｅ、Ｔａ、Ｌａ、Ｉｎ等の酸化物、これらの金属原子を含む複合酸化物等が挙げられる。
このような微粒子とするには、粒子表面が表面処理剤で処理されること（例えば、シランカップリング剤等：特開平１１−２９５５０３号公報、同１１−１５３７０３号公報、特開２０００−９９０８号公報、アニオン性化合物或は有機金属カップリング剤：特開２００１−３１０４３２号公報等）、高屈折率粒子をコアとしたコアシェル構造とすること（特開２００１−１６６１０４号公報等）、特定の分散剤併用（例、特開平１１−１５３７０３号公報、米国特許第６２１０８５８号明細書、特開２００２−２７７６０９号公報等）等挙げられる。
マトリックスを形成する材料としては、従来公知の熱可塑性樹脂、硬化性樹脂皮膜等が挙げられる。
更に好ましい材料としては、ラジカル重合性及びカチオン重合性の少なくともいずれかの重合性基を２個以上有する多官能性化合物含有組成物、加水分解性基を含有する有機金属化合物を含有する組成物、及びその部分縮合体を含有する組成物から選ばれる少なくとも１種の組成物が挙げられる。
例えば、特開２０００−４７００４号公報、同２００１−３１５２４２号公報、同２００１−３１８７１号公報、同２００１−２９６４０１号公報等に記載の化合物が挙げられる。
(High refractive index layer and medium refractive index layer)
The layer having a high refractive index of the antireflection film is composed of a cured film containing at least an inorganic compound fine particle having a high refractive index having an average particle diameter of 100 nm or less and a matrix binder.
Examples of the high refractive index inorganic compound fine particles include inorganic compounds having a refractive index of 1.65 or more, preferably those having a refractive index of 1.9 or more. Examples thereof include oxides such as Ti, Zn, Sb, Sn, Zr, Ce, Ta, La, and In, and composite oxides containing these metal atoms.
In order to obtain such fine particles, the surface of the particles is treated with a surface treatment agent (for example, silane coupling agents, etc .: JP-A Nos. 11-295503, 11-153703, 2000-9908). Gazette, anionic compound or organometallic coupling agent: JP 2001-310432 A, a core-shell structure with high refractive index particles as a core (JP 2001-166104 A, etc.), specific dispersion (For example, JP-A-11-153703, US Pat. No. 6,210,858, JP-A-2002-277609, etc.) and the like.
Examples of the material forming the matrix include conventionally known thermoplastic resins and curable resin films.
More preferable materials include a polyfunctional compound-containing composition having at least two polymerizable groups of at least one of radically polymerizable and cationically polymerizable, a composition containing an organometallic compound containing a hydrolyzable group, And at least one composition selected from compositions containing a partial condensate thereof.
Examples thereof include compounds described in JP-A Nos. 2000-47004, 2001-315242, 2001-31871, and 2001-296401.
また、金属アルコキドの加水分解縮合物から得られるコロイド状金属酸化物と金属アルコキシド組成物から得られる硬化性膜も好ましい。例えば、特開２００１−２９３８１８号公報等に記載されている。
高屈折率層の屈折率は、１．７０〜２．２０であることが好ましい。高屈折率層の厚さは、５ｎｍ〜１０μｍであることが好ましく、１０ｎｍ〜１μｍであることがさらに好ましい。
中屈折率層の屈折率は、低屈折率層の屈折率と高屈折率層の屈折率との間の値となるように調整する。中屈折率層の屈折率は、１．５０〜１．７０であることが好ましい。また、厚さは５ｎｍ〜１０μｍであることが好ましく、１０ｎｍ〜１μｍであることがさらに好ましい。
A curable film obtained from a colloidal metal oxide obtained from a hydrolyzed condensate of metal alkoxide and a metal alkoxide composition is also preferred. For example, it describes in Unexamined-Japanese-Patent No. 2001-293818.
The refractive index of the high refractive index layer is preferably 1.70 to 2.20. The thickness of the high refractive index layer is preferably 5 nm to 10 μm, and more preferably 10 nm to 1 μm.
The refractive index of the middle refractive index layer is adjusted to be a value between the refractive index of the low refractive index layer and the refractive index of the high refractive index layer. The refractive index of the middle refractive index layer is preferably 1.50 to 1.70. The thickness is preferably 5 nm to 10 μm, and more preferably 10 nm to 1 μm.
（低屈折率層）
低屈折率層は、高屈折率層の上に順次積層して成る。低屈折率層の屈折率は１．２０〜１．５５であることが好ましい。より好ましくは１．３０〜１．５０である。
低屈折率層は、耐擦傷性、防汚性を有する最外層として構築することが好ましい。耐擦傷性を大きく向上させる手段として表面への滑り性付与が有効で、従来公知のシリコーンの導入、フッ素の導入等から成る薄膜層の手段を適用できる。
また、含フッ素化合物はフッ素原子を３５〜８０質量％の範囲で含む架橋性若しくは重合性の官能基を含む化合物が好ましい。
例えば、特開平９−２２２５０３号公報明細書段落番号［００１８］〜［００２６］、同１１−３８２０２号公報明細書段落番号［００１９］〜［００３０］、特開２００１-４０２８４号公報明細書段落番号［００２７］〜［００２８］、特開２０００−２８４１０２号公報等に記載の化合物が挙げられる。
含フッ素化合物の屈折率は１．３５〜１．５０であることが好ましい。より好ましくは１．３６〜１．４７である。
シリコーン化合物としてはポリシロキサン構造を有する化合物であり、高分子鎖中に硬化性官能基あるいは重合性官能基を含有して、膜中で橋かけ構造を有するものが好ましい。例えば、反応性シリコーン（例、サイラプレーン（チッソ（株）製等）、両末端にシラノール基含有のポリシロキサン（特開平１１−２５８４０３号公報等）等が挙げられる。
架橋又は重合性基を有する含フッ素ポリマー及びシロキサンポリマーの少なくともいずれかの架橋又は重合反応は、重合開始剤、増感剤等を含有する最外層を形成するための塗布組成物を塗布と同時または塗布後に光照射や加熱することにより低屈折率層を形成することが好ましい。
又、シランカップリング剤等の有機金属化合物と特定のフッ素含有炭化水素基含有のシランカップリング剤とを触媒共存下に縮合反応で硬化するゾルゲル硬化膜も好ましい。
例えば、ポリフルオロアルキル基含有シラン化合物またはその部分加水分解縮合物（特開昭５８−１４２９５８号公報、同５８−１４７４８３号公報、同５８−１４７４８４号公報、特開平９−１５７５８２号公報、同１１−１０６７０４号公報記載等記載の化合物）、フッ素含有長鎖基であるポリ「パーフルオロアルキルエーテル」基を含有するシリル化合物（特開２０００−１１７９０２号公報、同２００１−４８５９０号公報、同２００２−５３８０４号公報記載の化合物等）等が挙げられる。
低屈折率層は、上記以外の添加剤として充填剤（例えば、二酸化珪素（シリカ）、含フッ素粒子（フッ化マグネシウム，フッ化カルシウム，フッ化バリウム）等の一次粒子平均径が１〜１５０ｎｍの低屈折率無機化合物、特開平１１−３８２０号公報の段落番号［００２０］〜［００３８］に記載の有機微粒子等）、シランカップリング剤、滑り剤、界面活性剤等を含有することができる。
低屈折率層が最外層の下層に位置する場合、低屈折率層は気相法（真空蒸着法、スパッタリング法、イオンプレーティング法、プラズマＣＶＤ法等）により形成されても良い。安価に製造できる点で、塗布法が好ましい。
低屈折率層の膜厚は、３０〜２００ｎｍであることが好ましく、５０〜１５０ｎｍであることがさらに好ましく、６０〜１２０ｎｍであることが最も好ましい。
(Low refractive index layer)
The low refractive index layer is formed by sequentially laminating on the high refractive index layer. The refractive index of the low refractive index layer is preferably 1.20 to 1.55. More preferably, it is 1.30-1.50.
The low refractive index layer is preferably constructed as an outermost layer having scratch resistance and antifouling properties. As means for greatly improving the scratch resistance, it is effective to impart slipperiness to the surface, and conventionally known thin film layer means such as introduction of silicone or introduction of fluorine can be applied.
The fluorine-containing compound is preferably a compound containing a crosslinkable or polymerizable functional group containing fluorine atoms in the range of 35 to 80% by mass.
For example, paragraph numbers [0018] to [0026] of Japanese Patent Application Laid-Open No. 9-222503, paragraph numbers [0019] to [0030] of Japanese Patent Application Laid-Open No. 11-38202, and paragraph numbers of Japanese Patent Application Laid-Open No. 2001-40284. [0027] to [0028], compounds described in JP-A No. 2000-284102, and the like.
The refractive index of the fluorine-containing compound is preferably 1.35 to 1.50. More preferably, it is 1.36-1.47.
The silicone compound is a compound having a polysiloxane structure, preferably containing a curable functional group or a polymerizable functional group in the polymer chain and having a crosslinked structure in the film. For example, reactive silicone (eg, Silaplane (manufactured by Chisso Corporation), silanol group-containing polysiloxane (Japanese Patent Laid-Open No. 11-258403, etc.) and the like can be mentioned.
The crosslinking or polymerization reaction of at least one of the fluorine-containing polymer having a crosslinking or polymerizable group and the siloxane polymer is performed simultaneously with the application of the coating composition for forming the outermost layer containing a polymerization initiator, a sensitizer, or the like. It is preferable to form the low refractive index layer by light irradiation or heating after coating.
Also preferred is a sol-gel cured film in which an organometallic compound such as a silane coupling agent and a specific fluorine-containing hydrocarbon group-containing silane coupling agent are cured by a condensation reaction in the presence of a catalyst.
For example, a polyfluoroalkyl group-containing silane compound or a partially hydrolyzed condensate thereof (Japanese Patent Laid-Open Nos. 58-142958, 58-147483, 58-147484, Japanese Patent Laid-Open Nos. 9-157582, 11) -106704), silyl compounds containing a poly "perfluoroalkyl ether" group which is a fluorine-containing long chain group (Japanese Patent Application Laid-Open Nos. 2000-117902, 2001-48590, 2002) 53804), and the like.
The low refractive index layer has an average primary particle diameter of 1 to 150 nm such as a filler (for example, silicon dioxide (silica), fluorine-containing particles (magnesium fluoride, calcium fluoride, barium fluoride)) as an additive other than the above. Low refractive index inorganic compounds, organic fine particles described in paragraphs [0020] to [0038] of JP-A-11-3820, etc.), silane coupling agents, slip agents, surfactants, and the like can be contained.
When the low refractive index layer is located below the outermost layer, the low refractive index layer may be formed by a vapor phase method (vacuum deposition method, sputtering method, ion plating method, plasma CVD method, etc.). The coating method is preferable because it can be manufactured at a low cost.
The film thickness of the low refractive index layer is preferably 30 to 200 nm, more preferably 50 to 150 nm, and most preferably 60 to 120 nm.
（ハードコート層）
ハードコート層は、反射防止層を設けた保護膜に物理強度を付与するために、保護膜の表面に設ける。特に、透明支持体と前記高屈折率層の間に設けることが好ましい。ハードコート層は、光及び／又は熱の硬化性化合物の架橋反応、又は、重合反応により形成されることが好ましい。硬化性化合物における硬化性官能基としては、光重合性官能基が好ましい。又加水分解性官能基含有の有機金属化合物や有機アルコキシシリル化合物も好ましい。
これらの化合物の具体例としては、高屈折率層で例示したと同様のものが挙げられる。ハードコート層の具体的な構成組成物としては、例えば、特開２００２−１４４９１３号公報、同２０００−９９０８号公報、国際公開第００／４６６１７号パンフレット等記載のものが挙げられる。
高屈折率層はハードコート層を兼ねることができる。このような場合、高屈折率層で記載した手法を用いて微粒子を微細に分散してハードコート層に含有させて形成することが好ましい。
ハードコート層は、平均粒径０．２〜１０μｍの粒子を含有させて防眩機能（アンチグレア機能）を付与した防眩層を兼ねることもできる。
ハードコート層の膜厚は、用途により適切に設計することができる。ハードコート層の膜厚は、０．２〜１０μｍであることが好ましく、より好ましくは０．５〜７μｍである。
ハードコート層の強度は、ＪＩＳ Ｋ５４００に従う鉛筆硬度試験で、Ｈ以上であることが好ましく、２Ｈ以上であることがさらに好ましく、３Ｈ以上であることが最も好ましい。又、ＪＩＳ Ｋ５４００に従うテーバー試験で、試験前後の試験片の摩耗量が少ないほど好ましい。
(Hard coat layer)
The hard coat layer is provided on the surface of the protective film in order to impart physical strength to the protective film provided with the antireflection layer. In particular, it is preferably provided between the transparent support and the high refractive index layer. The hard coat layer is preferably formed by a crosslinking reaction or a polymerization reaction of a light and / or heat curable compound. The curable functional group in the curable compound is preferably a photopolymerizable functional group. Also, hydrolyzable functional group-containing organometallic compounds and organoalkoxysilyl compounds are preferred.
Specific examples of these compounds are the same as those exemplified for the high refractive index layer. Specific examples of the constituent composition of the hard coat layer include those described in JP-A Nos. 2002-144913, 2000-9908, and WO 00/46617.
The high refractive index layer can also serve as a hard coat layer. In such a case, it is preferable to form fine particles dispersed in the hard coat layer using the method described for the high refractive index layer.
The hard coat layer can also serve as an antiglare layer containing particles having an average particle size of 0.2 to 10 μm and imparted with an antiglare function (antiglare function).
The film thickness of the hard coat layer can be appropriately designed depending on the application. The film thickness of the hard coat layer is preferably 0.2 to 10 μm, more preferably 0.5 to 7 μm.
The strength of the hard coat layer is preferably H or higher, more preferably 2H or higher, and most preferably 3H or higher in a pencil hardness test according to JIS K5400. Further, in the Taber test according to JIS K5400, the smaller the wear amount of the test piece before and after the test, the better.
（反射防止層の他の層）
さらに、前方散乱層、プライマー層、帯電防止層、下塗り層や保護層等を設けてもよい。
(Other layers of antireflection layer)
Further, a forward scattering layer, a primer layer, an antistatic layer, an undercoat layer, a protective layer, and the like may be provided.
（帯電防止層）
帯電防止層を設ける場合には体積抵抗率が１０-8（Ωｃｍ-3）以下の導電性を付与することが好ましい。吸湿性物質や水溶性無機塩、ある種の界面活性剤、カチオンポリマー、アニオンポリマー、コロイダルシリカ等の使用により１０-8（Ωｃｍ-3）の体積抵抗率の付与は可能であるが、温湿度依存性が大きく、低湿では十分な導電性を確保できない問題がある。そのため、導電性層素材としては金属酸化物が好ましい。金属酸化物には着色しているものがあるが、これらの金属酸化物を導電性層素材として用いるとフィルム全体が着色してしまい好ましくない。着色のない金属酸化物を形成する金属としてＺｎ，Ｔｉ，Ｓｎ，Ａｌ，Ｉｎ，Ｓｉ，Ｍｇ，Ｂａ，Ｍｏ，Ｗ，又はＶをあげることができ、これらを主成分とした金属酸化物を用いることが好ましい。具体的な例としては、ＺｎＯ，ＴｉＯ2，ＳｎＯ2，Ａｌ2Ｏ3，Ｉｎ2Ｏ3，ＳｉＯ2，ＭｇＯ，ＢａＯ，ＭｏＯ3，ＷＯ3，Ｖ2Ｏ5等、あるいはこれらの複合酸化物がよく、特にＺｎＯ，ＴｉＯ2，及びＳｎＯ2が好ましい。異種原子を含む例としては、例えばＺｎＯに対してはＡｌ，Ｉｎ等の添加物、ＳｎＯ2に対してはＳｂ，Ｎｂ，ハロゲン元素等の添加、またＴｉＯ2に対してはＮｂ，Ｔａ等の添加が効果的である。更にまた、特公昭５９−６２３５号公報に記載の如く、他の結晶性金属粒子あるいは繊維状物（例えば酸化チタン）に上記の金属酸化物を付着させた素材を使用しても良い。尚、体積抵抗値と表面抵抗値は別の物性値であり単純に比較することはできないが、体積抵抗値で１０-8（Ωｃｍ-3）以下の導電性を確保するためには、該導電層が概ね１０-10（Ω／□）以下の表面抵抗値を有していればよく更に好ましくは１０-8（Ω／□）である。導電層の表面抵抗値は帯電防止層を最表層としたときの値として測定されることが必要であり、本特許に記載の積層フィルムを形成する途中の段階で測定することができる。
(Antistatic layer)
In the case of providing an antistatic layer, it is preferable to impart conductivity with a volume resistivity of 10 −8 (Ωcm −3 ) or less. The use of hygroscopic substances, water-soluble inorganic salts, certain surfactants, cationic polymers, anionic polymers, colloidal silica, etc. can give a volume resistivity of 10 −8 (Ωcm −3 ). There is a problem that dependency is large, and sufficient conductivity cannot be secured at low humidity. Therefore, a metal oxide is preferable as the conductive layer material. Some metal oxides are colored, but using these metal oxides as the conductive layer material is not preferable because the entire film is colored. Zn, Ti, Sn, Al, In, Si, Mg, Ba, Mo, W, or V can be given as the metal that forms a metal oxide without coloring, and a metal oxide containing these as main components is used. It is preferable. Specific examples include ZnO, TiO 2 , SnO 2 , Al 2 O 3 , In 2 O 3 , SiO 2 , MgO, BaO, MoO 3 , WO 3 , V 2 O 5 , or complex oxides thereof. In particular, ZnO, TiO 2 and SnO 2 are preferable. Examples of containing different atoms include, for example, additives such as Al and In for ZnO, addition of Sb, Nb and halogen elements for SnO 2 , and Nb and Ta for TiO 2 . Addition is effective. Furthermore, as described in Japanese Examined Patent Publication No. 59-6235, a material in which the above metal oxide is attached to other crystalline metal particles or fibrous materials (for example, titanium oxide) may be used. The volume resistance value and the surface resistance value are different physical properties and cannot be simply compared. However, in order to secure a conductivity of 10 −8 (Ωcm −3 ) or less in volume resistance, It is sufficient that the layer has a surface resistance value of approximately 10 −10 (Ω / □) or less, and more preferably 10 −8 (Ω / □). The surface resistance value of the conductive layer needs to be measured as a value when the antistatic layer is the outermost layer, and can be measured in the middle of forming the laminated film described in this patent.
（液晶表示装置）
本発明の液晶表示装置は、本発明の偏光板を用いた液晶表示装置（第１形態）、本発明の偏光板のいずれかをセル上下に２枚用いたＶＡモード、ＯＣＢモードおよびＴＮモード液晶表示装置（第２形態）、及び本発明の偏光板のいずれか１枚をバックライト側に用いたＶＡモード液晶表示装置（第３形態）である。
すなわち、本発明の偏光板は、液晶表示装置に有利に用いられる。本発明の偏光板は、様々な表示モードの液晶セルに用いることができる。ＴＮ（Twisted Nematic）、ＩＰＳ（In-Plane Switching）、ＦＬＣ（Ferroelectric Liquid Crystal）、ＡＦＬＣ（Anti-ferroelectric Liquid Crystal）、ＯＣＢ（Optically Compensatory Bend）、ＳＴＮ（Supper Twisted Nematic）、ＶＡ（Vertically Aligned）およびＨＡＮ（Hybrid Aligned Nematic）のような様々な表示モードが提案されている。このうち、ＶＡモードまたはＯＣＢモードに好ましく用いることができる。
(Liquid crystal display device)
The liquid crystal display device of the present invention includes a liquid crystal display device using the polarizing plate of the present invention (first form), a VA mode, OCB mode and TN mode liquid crystal using any one of the polarizing plates of the present invention above and below the cell. It is a VA mode liquid crystal display device (third embodiment) using any one of the display device (second embodiment) and the polarizing plate of the present invention on the backlight side.
That is, the polarizing plate of the present invention is advantageously used for a liquid crystal display device. The polarizing plate of the present invention can be used for liquid crystal cells in various display modes. TN (Twisted Nematic), IPS (In-Plane Switching), FLC (Ferroelectric Liquid Crystal), AFLC (Anti-ferroelectric Liquid Crystal), OCB (Optically Compensatory Bend), STN (Supper Twisted Nematic), VA (Vertically Aligned) and Various display modes such as HAN (Hybrid Aligned Nematic) have been proposed. Among these, it can use preferably for VA mode or OCB mode.
ＶＡモードの液晶セルでは、電圧無印加時に棒状液晶性分子が実質的に垂直に配向している。
ＶＡモードの液晶セルには、（１）棒状液晶性分子を電圧無印加時に実質的に垂直に配向させ、電圧印加時に実質的に水平に配向させる狭義のＶＡモードの液晶セル（特開平２−１７６６２５号公報記載）に加えて、（２）視野角拡大のため、ＶＡモードをマルチドメイン化した（ＭＶＡモードの）液晶セル（ＳＩＤ９７、Digest of tech. Papers（予稿集）２８（１９９７）８４５記載）、（３）棒状液晶性分子を電圧無印加時に実質的に垂直配向させ、電圧印加時にねじれマルチドメイン配向させるモード（ｎ−ＡＳＭモード、ＣＰＡモード）の液晶セル（日本液晶討論会の予稿集５８〜５９（１９９８）記載）および（４）ＳＵＲＶＡＩＶＡＬモードの液晶セル（ＬＣＤインターナショナル９８で発表）が含まれる。
ＶＡモードの液晶表示装置としては、液晶セル（ＶＡモードセル）およびその両側に配置された二枚の偏光板（ＴＡＣ１、偏光子及びＴＡＣ２からなる偏光板）からなるものが挙げられる（図２）。液晶セルは、二枚の電極基板の間に液晶を担持している。
本発明の透過型液晶表示装置の別の態様では、液晶セルと偏光子との間に配置される偏光板の保護膜として、本発明に関するセルロースアシレートフィルムが用いられる。一方の偏光板の（液晶セルと偏光子との間の）保護膜のみに上記のセルロースアシレートフィルムを用いてもよいし、あるいは双方の偏光板の（液晶セルと偏光子との間の）二枚の保護膜に、上記のセルロースアシレートフィルムを用いてもよい。液晶セルへの貼り合わせは、本発明に関するセルロースアシレートフィルム（ＴＡＣ１）をＶＡセル側にすることが好ましい。一方の偏光板の（液晶セルと偏光子との間の）保護膜のみに上記のセルロースアシレートフィルムを用いた場合、これが、上側偏光板（観察側）、下側偏光板（バックライト側）のどちら側でもよく、機能的には何ら問題がない。ただし、上側偏光板として使用すると機能性膜を観察側（上側）に設ける必要性があり生産得率が下がる可能性があるため、下側偏光板として使用する場合が高いと考えられ、より好ましい実施形態であると考えられる。
そして、光源側及び観察者側の両方を本発明の偏光板で形成したものが第２形態の液晶表示装置であり、光源側のみを本発明の偏光板で形成したものが第３形態の液晶表示装置である。
保護膜（ＴＡＣ２）は、通常のセルレートアシレートフィルムでも良く、本発明に関するセルロースアシレートフィルムより薄いことが好ましい。たとえば、４０〜８０μｍが好ましく、市販のＫＣ４ＵＸ２Ｍ（コニカオプト（株）製４０μｍ）、ＫＣ５ＵＸ（コニカオプト（株）製６０μｍ）、ＴＤ８０（富士写真フイルム（株）製８０μｍ）等が挙げられるが、これらに限定されない。
In a VA mode liquid crystal cell, rod-like liquid crystalline molecules are aligned substantially vertically when no voltage is applied.
The VA mode liquid crystal cell includes (1) a narrowly defined VA mode liquid crystal cell in which rod-like liquid crystalline molecules are aligned substantially vertically when no voltage is applied, and substantially horizontally when a voltage is applied (Japanese Patent Laid-Open No. Hei 2-). 176625) (2) Liquid crystal cell (SID97, Digest of tech. Papers (Preliminary Proceed) 28 (1997) 845 in which the VA mode is converted into a multi-domain (MVA mode) for widening the viewing angle ), (3) Liquid crystal cells (n-ASM mode, CPA mode) in which rod-like liquid crystalline molecules are aligned substantially vertically when no voltage is applied and twisted multi-domain alignment is applied when a voltage is applied 58-59 (1998)) and (4) SURVAIVAL mode liquid crystal cells (announced at LCD International 98).
Examples of the VA mode liquid crystal display device include a liquid crystal cell (VA mode cell) and two polarizing plates (polarizing plates made of TAC1, polarizer and TAC2) arranged on both sides thereof (FIG. 2). . The liquid crystal cell carries a liquid crystal between two electrode substrates.
In another aspect of the transmissive liquid crystal display device of the present invention, a cellulose acylate film according to the present invention is used as a protective film for a polarizing plate disposed between a liquid crystal cell and a polarizer. The above cellulose acylate film may be used only for the protective film (between the liquid crystal cell and the polarizer) of one polarizing plate, or both polarizing plates (between the liquid crystal cell and the polarizer). The cellulose acylate film may be used for the two protective films. For bonding to the liquid crystal cell, the cellulose acylate film (TAC1) according to the present invention is preferably on the VA cell side. When the above cellulose acylate film is used only for the protective film (between the liquid crystal cell and the polarizer) of one polarizing plate, this is the upper polarizing plate (observation side) and the lower polarizing plate (backlight side). Either side can be used and there is no functional problem. However, when used as an upper polarizing plate, it is necessary to provide a functional film on the observation side (upper side) and the production yield may be lowered. It is considered an embodiment.
And what formed both the light source side and the observer side with the polarizing plate of this invention is a liquid crystal display device of 2nd form, and what formed only the light source side with the polarizing plate of this invention is liquid crystal of 3rd form. It is a display device.
The protective film (TAC2) may be a normal cell rate acylate film, and is preferably thinner than the cellulose acylate film according to the present invention. For example, 40-80 μm is preferable, and examples thereof include commercially available KC4UX2M (40 μm manufactured by Konica Capt Corp.), KC5UX (60 μm manufactured by Konica Capt Corp.), TD80 (80 μm manufactured by Fuji Photo Film Co., Ltd.), and the like. It is not limited to.
以下、本発明を実施例に基づき具体的に説明するが、本発明は実施例に限定されない。 EXAMPLES Hereinafter, although this invention is demonstrated concretely based on an Example, this invention is not limited to an Example.
［実施例１：セルロースアシレートフィルムの製膜（フィルム１〜２２）］
（１）セルロースアシレート
表１に記載のアシル基の種類、置換度の異なるセルロースアシレートを調製した。これは、触媒として硫酸（セルロース１００質量部に対し７．８質量部）を添加し、アシル置換基の原料となるカルボン酸を添加し４０℃でアシル化反応を行った。この時、カルボン酸の種類、量を調整することでアシル基の種類、置換度を調整した。またアシル化後の４０℃で熟成を行った。さらにこのセルロースアシレートの低分子量成分をアセトンで洗浄し除去した。なお、表中ＣＡＢとは、セルロースアセテートブチレート（アシル基がアセチル基とブチリル基からなるセルロースエステル誘導体）の略称であり、ＣＡＰとは、セルロースアセテートプロピオネート（アシル基がアセチル基とプロピオニル基からなるセルロースエステル誘導体）の略称であり、ＣＴＡとは、セルローストリアセテート（アシル基がアセチル基のみからなるセルロースエステル誘導体）を意味する。
（２）溶解
表１に記載のセルロースアシレート、可塑剤（ＴＰＰ：トリフェニルフォスフェート、ＢＤＰ：ビフェニルジフェニルフォスフェート）、下記紫外線吸収剤、下記レターデーション発現剤１、２を次の混合溶剤、ジクロロメタン／メタノール（８７／１３質量部）に綿の質量濃度が１５質量％となるように攪拌しながら投入して加熱攪拌し溶解させた。このとき、同時にセルロースアシレート１００質量部に対して微粒子であるマット剤（ＡＥＲＯＳＩＬ Ｒ９７２、日本エアロジル（株）製）０．０５質量部を投入し、加熱しながら攪拌させた。表１の添加剤量は綿質量１００に対する添加剤の質量である。
[Example 1: Film formation of cellulose acylate film (films 1 to 22)]
(1) Cellulose acylate Cellulose acylates having different types of acyl groups and different degrees of substitution described in Table 1 were prepared. This was carried out by adding sulfuric acid (7.8 parts by mass with respect to 100 parts by mass of cellulose) as a catalyst, adding carboxylic acid as a raw material for the acyl substituent, and carrying out an acylation reaction at 40 ° C. At this time, the kind and substitution degree of the acyl group were adjusted by adjusting the kind and amount of the carboxylic acid. Moreover, it age | cure | ripened at 40 degreeC after acylation. Further, the low molecular weight component of the cellulose acylate was removed by washing with acetone. In the table, CAB is an abbreviation for cellulose acetate butyrate (cellulose ester derivative whose acyl group is composed of acetyl group and butyryl group), and CAP is cellulose acetate propionate (acyl group is acetyl group and propionyl group). CTA means cellulose triacetate (a cellulose ester derivative whose acyl group is composed only of an acetyl group).
(2) Dissolution Cellulose acylate described in Table 1, plasticizer (TPP: triphenyl phosphate, BDP: biphenyl diphenyl phosphate), the following ultraviolet absorber, the following retardation developing agents 1 and 2, the following mixed solvent: The mixture was added to dichloromethane / methanol (87/13 parts by mass) with stirring so that the mass concentration of cotton was 15% by mass, and heated to stir to dissolve. At the same time, 0.05 parts by mass of a matting agent (AEROSIL R972, manufactured by Nippon Aerosil Co., Ltd.) as fine particles was added to 100 parts by mass of cellulose acylate and stirred while heating. The additive amount in Table 1 is the mass of the additive with respect to 100 mass of cotton.
紫外線吸収剤 UV absorber
レターデーション発現剤１ Retardation developer 1
レターデーション発現剤２ Retardation developer 2
（流延）
上述のドープをバンド流延機を用いて流延した。残留溶剤量が２５から３５質量％でバンドから剥ぎ取ったフィルムを、延伸温度が約Ｔｇ−５〜Ｔｇ＋５℃の範囲の条件で、テンターを用いて０％〜３０％の延伸倍率（表１参照）で幅方向に延伸して、セルロースアシレートフィルムを製膜した。表１に、テンターの延伸倍率を示してある。
作製したセルロースアシレートフィルム（光学補償シート）について、複屈折測定装置（ＫＯＢＲＡ ２１ＡＤＨ、王子計測機器（株）製）を用いて、２５℃６０％ＲＨで波長５９０ｎｍにおけるＲｅレターデーション値およびＲｔｈレターデーション値を測定した。
また、フィルムの弾性率を、ＭＤ方向、ＴＤ方向に対して、試料幅１０ｍｍ、長さ１００ｍｍに切り出し、２５℃６０％雰囲気下でチャック間距離５０ｍｍにし、３０ｍｍ／分で引っ張り試験を行い求めた。結果を表２に示す。
(Casting)
The above dope was cast using a band casting machine. A film peeled off from the band with a residual solvent amount of 25 to 35% by mass was stretched at a stretching ratio of 0% to 30% using a tenter under the condition where the stretching temperature was in the range of about Tg-5 to Tg + 5 ° C. (see Table 1). ) In the width direction to form a cellulose acylate film. Table 1 shows the stretch ratio of the tenter.
About the produced cellulose acylate film (optical compensation sheet), Re retardation value and Rth retardation at a wavelength of 590 nm at 25 ° C. and 60% RH using a birefringence measuring device (KOBRA 21ADH, manufactured by Oji Scientific Instruments) The value was measured.
Further, the elastic modulus of the film was cut into a sample width of 10 mm and a length of 100 mm with respect to the MD direction and the TD direction, a distance between chucks of 50 mm in an atmosphere of 25 ° C. and 60%, and a tensile test was performed at 30 mm / min. . The results are shown in Table 2.
本実施例で得られたフィルムのヘイズは、全て０．１〜０．９、マット剤の２次平均粒子径が１．０μｍ以下であり、８０℃９０％ＲＨの条件下に４８時間静置した場合の質量変化は０〜３％であった。さらに、どのサンプルも光弾性係数は５０×１０-13ｃｍ2／ｄｙｎｅ以下であった。 The hazes of the films obtained in this example are all 0.1 to 0.9, the secondary average particle size of the matting agent is 1.0 μm or less, and left for 48 hours under conditions of 80 ° C. and 90% RH. The mass change was 0-3%. Further, all the samples had a photoelastic coefficient of 50 × 10 −13 cm 2 / dyne or less.
［実施例２：反射防止機能付き保護膜（フィルム２３）の作製］
（光散乱層用塗布液の調製）
ペンタエリスリトールトリアクリレート、ペンタエリスリトールテトラアクリレートの混合物（ＰＥＴＡ、日本化薬（株）製）５０ｇをトルエン３８．５ｇで希釈した。更に、重合開始剤（イルガキュア１８４、チバ・スペシャルティ・ケミカルズ（株）製）を２ｇ添加し、混合攪拌した。 この溶液を塗布、紫外線硬化して得られた塗膜の屈折率は１．５１であった。
さらにこの溶液にポリトロン分散機にて１００００ｒｐｍで２０分分散した平均粒径３．５μｍの架橋ポリスチレン粒子（屈折率１．６０、ＳＸ−３５０、綜研化学（株）製）の３０％トルエン分散液を１．７ｇおよび平均粒径３．５μｍの架橋アクリル−スチレン粒子（屈折率１．５５、綜研化学（株）製）の３０％トルエン分散液を１３．３ｇ加え、最後に、フッ素系表面改質剤（ＦＰ−１）０．７５ｇ、シランカップリング剤（ＫＢＭ−５１０３、信越化学工業（株）製）を１０ｇを加え、完成液とした。
上記混合液を孔径３０μｍのポリプロピレン製フィルターでろ過して光散乱層の塗布液を調製した。
[Example 2: Production of protective film with antireflection function (film 23)]
(Preparation of coating solution for light scattering layer)
50 g of a mixture of pentaerythritol triacrylate and pentaerythritol tetraacrylate (PETA, Nippon Kayaku Co., Ltd.) was diluted with 38.5 g of toluene. Further, 2 g of a polymerization initiator (Irgacure 184, manufactured by Ciba Specialty Chemicals Co., Ltd.) was added and mixed and stirred. The refractive index of the coating film obtained by applying this solution and curing with ultraviolet rays was 1.51.
Further, a 30% toluene dispersion of crosslinked polystyrene particles having an average particle size of 3.5 μm (refractive index: 1.60, SX-350, manufactured by Soken Chemical Co., Ltd.) dispersed in this solution for 20 minutes at 10,000 rpm with a Polytron disperser. Add 13.3 g of 30% toluene dispersion of 1.7 g and crosslinked acrylic-styrene particles having an average particle size of 3.5 μm (refractive index 1.55, manufactured by Soken Chemical Co., Ltd.), and finally, fluorine-based surface modification 0.75 g of agent (FP-1) and 10 g of silane coupling agent (KBM-5103, manufactured by Shin-Etsu Chemical Co., Ltd.) were added to obtain a finished solution.
The liquid mixture was filtered through a polypropylene filter having a pore size of 30 μm to prepare a coating solution for the light scattering layer.
（低屈折率層用塗布液の調製）
まず初めに、次のようにしてゾル液ａを調製した。攪拌機、還流冷却器を備えた反応器、メチルエチルケトン１２０部、アクリロイルオキシプロピルトリメトキシシラン（ＫＢＭ５１０３、信越化学工業（株）製）１００部、ジイソプロポキシアルミニウムエチルアセトアセテート３部を加え混合したのち、イオン交換水３０部を加え、６０℃で４時間反応させたのち、室温まで冷却し、ゾル液ａを得た。質量平均分子量は１６００であり、オリゴマー成分以上の成分のうち、分子量が１０００〜２００００の成分は１００％であった。また、ガスクロマトグラフィー分析から、原料のアクリロイルオキシプロピルトリメトキシシランは全く残存していなかった。
屈折率１．４２の熱架橋性含フッ素ポリマー（ＪＮ−７２２８、固形分濃度６％、ＪＳＲ（株）製）１３ｇ、シリカゾル（シリカ、ＭＥＫ−ＳＴの粒子サイズ違い、平均粒径４５ｎｍ、固形分濃度３０％、日産化学（株）製）１．３ｇ、上記ゾル液ａ０．６ｇおよびメチルエチルケトン５ｇ、シクロヘキサノン０．６ｇを添加、攪拌の後、孔径１μｍのポリプロピレン製フィルターでろ過して、低屈折率層用塗布液を調製した。
(Preparation of coating solution for low refractive index layer)
First, sol solution a was prepared as follows. A stirrer, a reactor equipped with a reflux condenser, 120 parts of methyl ethyl ketone, 100 parts of acryloyloxypropyltrimethoxysilane (KBM5103, manufactured by Shin-Etsu Chemical Co., Ltd.), 3 parts of diisopropoxyaluminum ethyl acetoacetate were added and mixed. After adding 30 parts of ion-exchanged water and reacting at 60 ° C. for 4 hours, it was cooled to room temperature to obtain a sol solution a. The mass average molecular weight was 1600, and among the components higher than the oligomer component, the component having a molecular weight of 1000 to 20000 was 100%. Further, from the gas chromatography analysis, the raw material acryloyloxypropyltrimethoxysilane did not remain at all.
Thermally crosslinkable fluorine-containing polymer having a refractive index of 1.42 (JN-7228, solid content concentration 6%, manufactured by JSR Corporation) 13 g, silica sol (silica, MEK-ST particle size difference, average particle size 45 nm, solid content 30% concentration, manufactured by Nissan Chemical Co., Ltd.) 1.3 g, the above sol a0.6 g, methyl ethyl ketone 5 g, and cyclohexanone 0.6 g were added. A layer coating solution was prepared.
（反射防止層付き透明保護膜の作製）
８０μｍの厚さのトリアセチルセルロースフィルム（フジタックＴＤ８０Ｕ、富士写真フイルム（株）製）をロール形態で巻き出して、上記の機能層（光散乱層）用塗布液を線数１８０本／インチ、深度４０μｍのグラビアパターンを有する直径５０ｍｍのマイクログラビアロールとドクターブレードを用いて、グラビアロール回転数３０ｒｐｍ、搬送速度３０ｍ／分の条件で塗布し、６０℃で１５０秒乾燥の後、さらに窒素パージ下で１６０Ｗ／ｃｍの空冷メタルハライドランプ（アイグラフィックス（株）製）を用いて、照度４００ｍＷ／ｃｍ2、照射量２５０ｍＪ／ｃｍ2の紫外線を照射して塗布層を硬化させ、厚さ６μｍの機能層を形成し、巻き取った。
該機能層（光散乱層）を塗設したトリアセチルセルロースフィルムを再び巻き出してその光散乱層側に、該調製した低屈折率層用塗布液を線数１８０本／インチ、深度４０μｍのグラビアパターンを有する直径５０ｍｍのマイクログラビアロールとドクターブレードを用いて、グラビアロール回転数３０ｒｐｍ、搬送速度１５ｍ／分の条件で塗布し、１２０℃で１５０秒乾燥の後、更に１４０℃で８分乾燥させてから窒素パージ下で２４０Ｗ／ｃｍの空冷メタルハライドランプ（アイグラフィックス（株）製）を用いて、照度４００ｍＷ／ｃｍ2、照射量９００ｍＪ／ｃｍ2の紫外線を照射し、厚さ１００ｎｍの低屈折率層を形成し、巻き取り、反射防止機能付き保護膜（フィルム２３）を作製した。
(Preparation of transparent protective film with antireflection layer)
An 80 μm-thick triacetylcellulose film (Fujitac TD80U, manufactured by Fuji Photo Film Co., Ltd.) is unwound in a roll form, and the above functional layer (light scattering layer) coating solution has a line number of 180 lines / inch, depth Using a microgravure roll with a diameter of 50 mm and a doctor blade having a gravure pattern of 40 μm, coating was performed under the conditions of a gravure roll rotation speed of 30 rpm and a conveyance speed of 30 m / min, drying at 60 ° C. for 150 seconds, and further under nitrogen purge Using a 160 W / cm air-cooled metal halide lamp (manufactured by Eye Graphics Co., Ltd.), the coating layer is cured by irradiating ultraviolet rays with an illuminance of 400 mW / cm 2 and an irradiation amount of 250 mJ / cm 2 , and a functional layer having a thickness of 6 μm And wound up.
The triacetyl cellulose film coated with the functional layer (light scattering layer) is unwound again, and the prepared coating liquid for the low refractive index layer is gravure with a line number of 180 lines / inch and a depth of 40 μm on the light scattering layer side. Using a micro gravure roll with a diameter of 50 mm and a doctor blade having a pattern, it is applied under the conditions of a gravure roll rotation speed of 30 rpm and a conveyance speed of 15 m / min, dried at 120 ° C. for 150 seconds, and further dried at 140 ° C. for 8 minutes. Then, using a 240 W / cm air-cooled metal halide lamp (manufactured by Eye Graphics Co., Ltd.) under a nitrogen purge, ultraviolet rays with an illuminance of 400 mW / cm 2 and an irradiation amount of 900 mJ / cm 2 were irradiated, and a low refraction with a thickness of 100 nm A rate layer was formed, wound, and a protective film with antireflection function (film 23) was produced.
［実施例３：反射防止機能付き保護膜（フィルム２４）の作製］
（ハードコート層用塗布液の調製）
トリメチロールプロパントリアクリレート（ＴＭＰＴＡ、日本化薬（株）製）７５０．０質量部に、質量平均分子量３０００のポリ（グリシジルメタクリレート）２７０．０質量部、メチルエチルケトン７３０．０ｇ、シクロヘキサノン５００．０ｇ及び光重合開始剤（イルガキュア１８４、日本チバガイギー（株）製）５０．０ｇを添加して攪拌した。孔径０．４μｍのポリプロピレン製フィルターで濾過してハードコート層用の塗布液を調製した。
[Example 3: Production of protective film with antireflection function (film 24)]
(Preparation of coating solution for hard coat layer)
750.0 parts by mass of trimethylolpropane triacrylate (TMPTA, Nippon Kayaku Co., Ltd.), 270.0 parts by mass of poly (glycidyl methacrylate) having a mass average molecular weight of 3000, 730.0 g of methyl ethyl ketone, 500.0 g of cyclohexanone and light A polymerization initiator (Irgacure 184, manufactured by Nippon Ciba-Geigy Co., Ltd.) 50.0 g was added and stirred. The solution was filtered through a polypropylene filter having a pore size of 0.4 μm to prepare a coating solution for a hard coat layer.
（二酸化チタン微粒子分散液の調製）
二酸化チタン微粒子としては、コバルトを含有し、かつ水酸化アルミニウムと水酸化ジルコニウムを用いて表面処理を施した二酸化チタン微粒子（ＭＰＴ−１２９、石原産業（株）製）を使用した。
この粒子２５７．１ｇに、下記分散剤３８．６ｇ、およびシクロヘキサノン７０４．３ｇを添加してダイノミルにより分散し、質量平均径７０ｎｍの二酸化チタン分散液を調製した。
(Preparation of titanium dioxide fine particle dispersion)
As the titanium dioxide fine particles, titanium dioxide fine particles (MPT-129, manufactured by Ishihara Sangyo Co., Ltd.) containing cobalt and surface-treated with aluminum hydroxide and zirconium hydroxide were used.
The following dispersant (38.6 g) and cyclohexanone (704.3 g) were added to 257.1 g of the particles and dispersed by dynomill to prepare a titanium dioxide dispersion having a mass average diameter of 70 nm.
（中屈折率層用塗布液の調製）
上記の二酸化チタン分散液８８．９ｇに、ジペンタエリスリトールペンタアクリレートとジペンタエリスリトールヘキサアクリレートの混合物（ＤＰＨＡ）５８．４ｇ、光重合開始剤（イルガキュア９０７）３．１ｇ、光増感剤（カヤキュアーＤＥＴＸ、日本化薬（株）製）１．１ｇ、メチルエチルケトン４８２．４ｇおよびシクロヘキサノン１８６９．８ｇを添加して攪拌した。十分に攪拌ののち、孔径０．４μｍのポリプロピレン製フィルターで濾過して中屈折率層用塗布液を調製した。
(Preparation of coating solution for medium refractive index layer)
To 88.9 g of the above titanium dioxide dispersion, 58.4 g of a mixture of dipentaerythritol pentaacrylate and dipentaerythritol hexaacrylate (DPHA), 3.1 g of a photopolymerization initiator (Irgacure 907), a photosensitizer (Kayacure DETX) 1.1 g of Nippon Kayaku Co., Ltd.), 482.4 g of methyl ethyl ketone and 1869.8 g of cyclohexanone were added and stirred. After sufficiently stirring, the solution was filtered through a polypropylene filter having a pore diameter of 0.4 μm to prepare a coating solution for a medium refractive index layer.
（高屈折率層用塗布液の調製）
上記の二酸化チタン分散液５８６．８ｇに、ジペンタエリスリトールペンタアクリレートとジペンタエリスリトールヘキサアクリレートの混合物（ＤＰＨＡ、日本化薬（株）製）４７．９ｇ、光重合開始剤（イルガキュア９０７、日本チバガイギー（株）製）４．０ｇ、光増感剤（カヤキュア−ＤＥＴＸ、日本化薬（株）製）１．３ｇ、メチルエチルケトン４５５．８ｇ、およびシクロヘキサノン１４２７．８ｇを添加して攪拌した。孔径０．４μｍのポリプロピレン製フィルターで濾過して高屈折率層用の塗布液を調製した。
(Preparation of coating solution for high refractive index layer)
To 56.8 g of the above titanium dioxide dispersion, 47.9 g of a mixture of dipentaerythritol pentaacrylate and dipentaerythritol hexaacrylate (DPHA, manufactured by Nippon Kayaku Co., Ltd.), photopolymerization initiator (Irgacure 907, Nippon Ciba Geigy ( Co., Ltd.) 4.0 g, photosensitizer (Kayacure-DETX, Nippon Kayaku Co., Ltd.) 1.3 g, methyl ethyl ketone 455.8 g, and cyclohexanone 1427.8 g were added and stirred. The solution was filtered through a polypropylene filter having a pore diameter of 0.4 μm to prepare a coating solution for a high refractive index layer.
（低屈折率層用塗布液の調製）
下記共重合体（Ｐ−１）をメチルイソブチルケトンに７質量％の濃度になるように溶解し、末端メタクリレート基含有シリコーン樹脂Ｘ−２２−１６４Ｃ（信越化学（株）製）を固形分に対して３％、光ラジカル発生剤イルガキュア９０７（商品名）を固形分に対して５質量％添加し、低屈折率層用塗布液を調製した。
(Preparation of coating solution for low refractive index layer)
The following copolymer (P-1) is dissolved in methyl isobutyl ketone to a concentration of 7% by mass, and a terminal methacrylate group-containing silicone resin X-22-164C (manufactured by Shin-Etsu Chemical Co., Ltd.) is added to the solid content. 3% of the photoradical generator Irgacure 907 (trade name) was added in an amount of 5% by mass based on the solid content to prepare a coating solution for a low refractive index layer.
共重合体（Ｐ−１）
（反射防止層付透明保護膜の作製）
膜厚８０μｍのトリアセチルセルロースフィルム（フジタックＴＤ８０Ｕ、富士写真フイルム（株）製）上に、ハードコート層用塗布液をグラビアコーターを用いて塗布した。１００℃で乾燥した後、酸素濃度が１．０体積％以下の雰囲気になるように窒素パージしながら１６０Ｗ／ｃｍの空冷メタルハライドランプ（アイグラフィックス（株）製）を用いて、照度４００ｍＷ／ｃｍ2、照射量３００ｍＪ／ｃｍ2の紫外線を照射して塗布層を硬化させ、厚さ８μｍのハードコート層を形成した。
ハードコート層の上に、中屈折率層用塗布液、高屈折率層用塗布液、低屈折率層用塗布液を３つの塗布ステーションを有するグラビアコーターを用いて連続して塗布した。
(Production of transparent protective film with antireflection layer)
A hard coat layer coating solution was applied onto a triacetyl cellulose film (Fujitac TD80U, manufactured by Fuji Photo Film Co., Ltd.) having a thickness of 80 μm using a gravure coater. After drying at 100 ° C., an irradiance of 400 mW / cm using an air-cooled metal halide lamp (manufactured by Eye Graphics Co., Ltd.) of 160 W / cm while purging with nitrogen so that the oxygen concentration becomes 1.0 vol% or less. 2. The coating layer was cured by irradiating ultraviolet rays with an irradiation amount of 300 mJ / cm 2 to form a hard coat layer having a thickness of 8 μm.
On the hard coat layer, a medium refractive index layer coating solution, a high refractive index layer coating solution, and a low refractive index layer coating solution were successively applied using a gravure coater having three coating stations.
中屈折率層の乾燥条件は１００℃、２分間とし、紫外線硬化条件は酸素濃度が１．０体積％以下の雰囲気になるように窒素パージしながら１８０Ｗ／ｃｍ2の空冷メタルハライドランプ（アイグラフィックス（株）製）を用いて、照度４００ｍＷ／ｃｍ2、照射量４００ｍＪ／ｃｍ2の照射量とした。硬化後の中屈折率層は屈折率１．６３０、膜厚６７ｎｍであった。 The medium refractive index layer is dried at 100 ° C. for 2 minutes, and the ultraviolet curing condition is 180 W / cm 2 air-cooled metal halide lamp (eye graphics) while purging with nitrogen so that the oxygen concentration becomes 1.0 vol% or less. The irradiance was 400 mW / cm 2 and the irradiation amount was 400 mJ / cm 2 . The medium refractive index layer after curing had a refractive index of 1.630 and a film thickness of 67 nm.
高屈折率層および低屈折率層の乾燥条件はいずれも９０℃、１分の後、１００℃、１分とし、紫外線硬化条件は酸素濃度が１．０体積％以下の雰囲気になるように窒素パージしながら２４０Ｗ／ｃｍ2の空冷メタルハライドランプ（アイグラフィックス（株）製）を用いて、照度６００ｍＷ／ｃｍ2、照射量６００ｍＪ／ｃｍ2の照射量とした。
硬化後の高屈折率層は屈折率１．９０５、膜厚１０７ｎｍ、低屈折率層は屈折率１．４４０、膜厚８５ｎｍであった。このようにして、反射防止層付き透明保護膜（フィルム２４）を作製した。
The drying conditions of the high refractive index layer and the low refractive index layer are both 90 ° C., 1 minute, 100 ° C., 1 minute, and the ultraviolet curing condition is nitrogen so that the oxygen concentration is 1.0 volume% or less. While purging, a 240 W / cm 2 air-cooled metal halide lamp (manufactured by Eye Graphics Co., Ltd.) was used to obtain an irradiation amount of 600 mW / cm 2 and an irradiation amount of 600 mJ / cm 2 .
The cured high refractive index layer had a refractive index of 1.905 and a film thickness of 107 nm, and the low refractive index layer had a refractive index of 1.440 and a film thickness of 85 nm. Thus, the transparent protective film (film 24) with an antireflection layer was produced.
［実施例４］
（偏光板の作製）
厚さ７５μｍのポリビニルアルコール（ＰＶＡ）フィルムを、ヨウ素濃度０．０５質量％のヨウ素水溶液中に３０℃で６０秒浸漬して染色し、次いでホウ酸濃度４質量％濃度のホウ酸水溶液中に６０秒浸漬している間に元の長さの５倍に縦延伸した後、５０℃で４分間乾燥させて、厚さ２５μｍの偏光子１を得た。
また、延伸倍率を４倍にし、膜厚を３０μｍにすること以外は偏光子１と同様にして、偏光子２を得た。
表２に示す実施例１から３で作製した保護膜および市販のセルロースアシレートを１．５モル／リットルで５５℃の水酸化ナトリウム水溶液中に浸漬した後、水で十分に水酸化ナトリウムを洗い流した。その後、０．００５モル／リットルで３５℃の希硫酸水溶液に１分間浸漬した後、水に浸漬し希硫酸水溶液を十分に洗い流した。最後に試料を１２０℃で十分に乾燥させた。
前記のように鹸化処理を行った実施例１から３で作製した保護膜および市販のセルロースアシレートを表２に示す組合せで前記の偏光子を挟むようにポリビニルアルコール系接着剤を用いて貼り合せ偏光板１〜２７を得た。
ここで市販のセルロースアシレートフィルムとしてはフジタックＴＦ８０Ｕ、フジタックＴＤ８０Ｕ（それぞれ富士写真フイルム（株）製）、およびＫＣ８０ＵＶＳＦＤ（それぞれコニカオプト（株）製）を用いた。
このとき、偏光子および偏光子両側の保護膜はロール形態で作製されているため各ロールフィルムの長手方向が平行となっており連続的に貼り合わされる。また、セル側に配置される保護膜においては偏光子の透過軸と実施例１で作製したセルロースアシレートフィルムの遅相軸とは平行になっている。
上記で作製した偏光板のセル側の面にはアクリル系の粘着材、さらにその粘着材の上にセパレートフィルムを貼り付けた。セルと反対側の面にはプロテクトフィルムを貼り付けた。
[Example 4]
(Preparation of polarizing plate)
A polyvinyl alcohol (PVA) film having a thickness of 75 μm is dyed by immersing it in an aqueous iodine solution having an iodine concentration of 0.05% by mass at 30 ° C. for 60 seconds, and then in an aqueous boric acid solution having a boric acid concentration of 4% by mass. The film was longitudinally stretched 5 times the original length while being immersed for 2 seconds, and then dried at 50 ° C. for 4 minutes to obtain a polarizer 1 having a thickness of 25 μm.
Further, a polarizer 2 was obtained in the same manner as the polarizer 1 except that the draw ratio was 4 times and the film thickness was 30 μm.
After immersing the protective film prepared in Examples 1 to 3 shown in Table 2 and a commercially available cellulose acylate in an aqueous sodium hydroxide solution at 55 ° C. at 1.5 mol / liter, the sodium hydroxide was thoroughly washed away with water. It was. Then, after being immersed in a diluted sulfuric acid aqueous solution at 0.005 mol / liter at 35 ° C. for 1 minute, it was immersed in water to sufficiently wash away the diluted sulfuric acid aqueous solution. Finally, the sample was thoroughly dried at 120 ° C.
The protective film prepared in Examples 1 to 3 subjected to the saponification treatment as described above and a commercially available cellulose acylate were bonded using a polyvinyl alcohol adhesive so as to sandwich the polarizer in the combination shown in Table 2. Polarizing plates 1 to 27 were obtained.
Here, as a commercially available cellulose acylate film, Fujitac TF80U, Fujitac TD80U (manufactured by Fuji Photo Film Co., Ltd.) and KC80UVSFD (each manufactured by Konica Capto Co., Ltd.) were used.
At this time, since the polarizer and the protective films on both sides of the polarizer are manufactured in a roll form, the longitudinal directions of the roll films are parallel to each other and are continuously bonded. In the protective film disposed on the cell side, the transmission axis of the polarizer and the slow axis of the cellulose acylate film produced in Example 1 are parallel.
An acrylic adhesive material was attached to the cell side surface of the polarizing plate prepared above, and a separate film was attached on the adhesive material. A protective film was attached to the surface opposite to the cell.
［実施例５］
分光光度計（日本分光（株）製）を用いて、３８０〜７８０ｎｍの波長領域において、入射角５°における分光反射率を機能性膜側から測定し、４５０〜６５０ｎｍの積分球平均反射率を求めたところ、反射防止層付き透明保護膜であるフィルム２３を使用した偏光板４、１２では２．３％、反射防止層付き透明保護膜であるフィルム２４を使用した偏光板７、１３では０．４％であった。ここで反射防止層付き透明保護膜上のプロテクトフィルムは剥がして反射率測定を行った。
[Example 5]
Using a spectrophotometer (manufactured by JASCO Corporation), the spectral reflectance at an incident angle of 5 ° is measured from the functional film side in the wavelength region of 380 to 780 nm, and the integrating sphere average reflectance of 450 to 650 nm is obtained. As a result, it was 2.3% for the polarizing plates 4 and 12 using the film 23 which is a transparent protective film with an antireflection layer, and 0 for the
［実施例６］
（偏光板の弾性率の測定）
実施例４で作製した偏光板１〜３、５、６、８〜１１、１４〜２７、および市販の偏光板を、偏光板の吸収軸、透過軸に対して、試料幅１０ｍｍ、長さ１００ｍｍに切り出し、２５℃６０％雰囲気下でチャック間距離５０ｍｍにし、３０ｍｍ／分で引っ張り試験を行い求めた。結果を表２に示す。
[Example 6]
(Measurement of elastic modulus of polarizing plate)
The polarizing plates 1 to 3, 5, 6, 8 to 11, 14 to 27, and the commercially available polarizing plates produced in Example 4 are 10 mm in sample width and 100 mm in length with respect to the absorption axis and transmission axis of the polarizing plate. The distance between chucks was 50 mm in an atmosphere of 25 ° C. and 60%, and a tensile test was performed at 30 mm / min. The results are shown in Table 2.
［実施例７］
（パネルへの実装）
ＶＡパネルへの実装（２枚型）
ＶＡモードの液晶ＴＶ（ＬＣ−２０Ｃ５−Ｓ、シャープ（株）社製）の表裏の偏光板および位相差板を剥し、表と裏側に実施例４で作製した偏光板１〜３、５、６、８〜１０を貼り付けた。この際、視認側の偏光板の吸収軸をパネル水平方向に、バックライト側の偏光板の吸収軸をパネル鉛直方向となり、粘着材面が液晶セル側となるように配置した。
プロテクトフィルムを剥した後、測定機（ＥＺ−Ｃｏｎｔｒａｓｔ １６０Ｄ、ＥＬＤＩＭ社製）を用いて、黒表示（Ｌ１）から白表示（Ｌ８）までの８段階で視野角（コントラスト比が１０以上で黒側の階調反転のない範囲）を測定した。いずれの偏光板を使用した場合も、良好な視野角特性が得られた。
[Example 7]
(Mounting on the panel)
Mounting on VA panel (2 sheets type)
Polarizing plates 1-3, 5, and 6 prepared in Example 4 on the front and back sides of the VA mode liquid crystal TV (LC-20C5-S, manufactured by Sharp Corporation) were peeled off. 8-10 were pasted. In this case, the absorption axis of the polarizing plate on the viewing side is in the horizontal direction of the panel, the absorption axis of the polarizing plate on the backlight side is in the vertical direction of the panel, and the adhesive material surface is on the liquid crystal cell side.
After removing the protective film, using a measuring instrument (EZ-Contrast 160D, manufactured by ELDIM), the viewing angle (contrast ratio is 10 or more and black side) in 8 steps from black display (L1) to white display (L8) Range without gradation inversion). When any polarizing plate was used, good viewing angle characteristics were obtained.
ＶＡパネルへの実装（１枚型）
ＶＡモードの液晶ＴＶ（ＬＣ−２０Ｃ５−Ｓ、シャープ（株）社製）の表裏の偏光板および位相差板を剥し、表側に視野角補償板のない市販の偏光板（ＨＬＣ２−５６１８、サンリッツ（株）製）を、裏側に実施例４で作製した偏光板１１、１４〜２３を貼り付けた。この際、視認側の偏光板の吸収軸をパネル水平方向に、バックライト側の偏光板の吸収軸をパネル鉛直方向となり、粘着材面が液晶セル側となるように配置した。
プロテクトフィルムを剥した後、測定機（ＥＺ−Ｃｏｎｔｒａｓｔ １６０Ｄ、ＥＬＤＩＭ社製）を用いて、黒表示（Ｌ１）から白表示（Ｌ８）までの８段階で視野角（コントラスト比が１０以上で黒側の階調反転のない範囲）を測定した。いずれの偏光板を使用した場合も、良好な視野角特性が得られた。
Mounting on VA panel (single-sheet type)
VA mode liquid crystal TV (LC-20C5-S, manufactured by Sharp Corporation) is peeled off the front and back polarizing plates and retardation plates, and commercially available polarizing plates (HLC2-5618, Sanritz (No. The polarizing plate 11, 14-23 produced in Example 4 was affixed on the back side. In this case, the absorption axis of the polarizing plate on the viewing side is in the horizontal direction of the panel, the absorption axis of the polarizing plate on the backlight side is in the vertical direction of the panel, and the adhesive material surface is on the liquid crystal cell side.
After removing the protective film, using a measuring instrument (EZ-Contrast 160D, manufactured by ELDIM), the viewing angle (contrast ratio is 10 or more and black side) in 8 steps from black display (L1) to white display (L8) Range without gradation inversion). When any polarizing plate was used, good viewing angle characteristics were obtained.
（ムラの評価）
上記で作製した、実施例４で作製した偏光板を用いた液晶パネルについて、ムラの評価を行った。
偏光板を貼り合せた液晶パネルを使用し、液晶ＴＶを組み立て、バックライトを連続で２４時間点灯させた。
そのときに観察されるムラについて、下記のように評価した。結果を表２に示す。
◎ ：ムラはほとんど観察されない
○ ：うっすらと丸いムラが観察されるがほとんど気にならない
× ：画面上に大きな丸いムラがハッキリと観察される
(Evaluation of unevenness)
The liquid crystal panel using the polarizing plate produced in Example 4 produced above was evaluated for unevenness.
Using a liquid crystal panel with a polarizing plate attached, a liquid crystal TV was assembled, and the backlight was continuously lit for 24 hours.
The unevenness observed at that time was evaluated as follows. The results are shown in Table 2.
◎: Unevenness is hardly observed ○: Slightly rounded unevenness is observed but hardly noticeable ×: Large round unevenness is clearly observed on the screen
［比較例１］
実施例４で作製した偏光板２４〜２７について、実施例７と同様に、パネルへの実装（２枚型）を行った。また、市販の偏光板も同様に実装した。
プロテクトフィルムを剥した後、測定機（ＥＺ−Ｃｏｎｔｒａｓｔ １６０Ｄ、ＥＬＤＩＭ社製）を用いて、黒表示（Ｌ１）から白表示（Ｌ８）までの８段階で視野角（コントラスト比が１０以上で黒側の階調反転のない範囲）を測定しが、いずれの偏光板を使用した場合も、視野角特性が悪く、本発明の偏光板を使用した場合よりも劣っていた。
また、ムラの評価も同様に行ったが、ハッキリとムラが観察され、本発明の偏光板に劣るものであった。
[Comparative Example 1]
The polarizing plates 24 to 27 produced in Example 4 were mounted on a panel (two-sheet type) in the same manner as in Example 7. A commercially available polarizing plate was also mounted in the same manner.
After removing the protective film, using a measuring instrument (EZ-Contrast 160D, manufactured by ELDIM), the viewing angle (contrast ratio is 10 or more and black side) in 8 steps from black display (L1) to white display (L8) However, the viewing angle characteristics were poor when using any of the polarizing plates, which was inferior to when using the polarizing plate of the present invention.
Further, the unevenness was evaluated in the same manner, but clear and unevenness was observed, which was inferior to the polarizing plate of the present invention.
１，１１，２１ 偏光子
２，１２．２２ ＴＡＣ１：本発明に関するセルロースアシレートフィルム（一方の保護膜：図２では液晶セル側に配置される）
３，１３，２３ ＴＡＣ２：他方の側の保護膜
４ 機能性膜
５ 偏光板
３０ ＶＡモードセル
1,11,21 Polarizer 2,12.22 TAC1: Cellulose acylate film according to the present invention (one protective film: disposed on the liquid crystal cell side in FIG. 2)
3, 13, 23 TAC2: Protective film 4 on the other side 4 Functional film 5 Polarizing plate 30 VA mode cell
Claims (16)
式（Ｉ） ： ０．９≦ＥA／ＥT≦１．４ A polarizing plate in which a protective film is bonded to at least one of the polarizers, and an elastic modulus EA in the absorption axis direction and an elastic modulus ET in the transmission axis direction of the polarizing plate at 25 ° C. and 60% RH are expressed by the following formula ( A polarizing plate characterized by satisfying I).
Formula (I): 0.9 ≦ EA / ET ≦ 1.4
式（II） ： ２６４０ＭＰａ≦ＥT≦５４００ＭＰａ The polarizing plate according to claim 1, wherein the elastic modulus ET in the transmission axis direction satisfies the following formula (II).
Formula (II): 2640 MPa ≦ ET ≦ 5400 MPa
式（III） ： Ｒｅ(λ)＝（ｎｘ−ｎｙ）×ｄ
式（IV） ： Ｒｔｈ(λ)＝｛（ｎｘ＋ｎｙ）／２−ｎｚ｝×ｄ
式（Ｖ） ： ２０ｎｍ≦Ｒｅ(590)≦２００ｎｍ
式（VI） ： ７０ｎｍ≦Ｒｔｈ(590)≦４００ｎｍ
［式中、Ｒｅ(λ)、Ｒｔｈ(λ)は波長λｎｍにおける測定値（単位：ｎｍ）である。またｎｘはフィルム面内の遅相軸方向の屈折率であり、ｎｙはフィルム面内の進相軸方向の屈折率であり、ｎｚはフィルムの厚み方向の屈折率であり、ｄはフィルムの厚さ（単位：ｎｍ）である。］ The front retardation value Re ( λ ) defined by the formula (III) and the retardation value Rth ( λ ) in the film thickness direction defined by the formula (IV) of the one protective film are expressed by the following formula (V ) And (VI) are satisfied, The polarizing plate according to claim 1 or 2.
Formula (III): Re ( λ ) = (nx−ny) × d
Formula (IV): Rth ( λ ) = {(nx + ny) / 2−nz} × d
Formula (V): 20 nm ≦ Re (590) ≦ 200 nm
Formula (VI): 70 nm ≦ Rth (590) ≦ 400 nm
[In the formula, Re ( λ ) and Rth ( λ ) are measured values (unit: nm) at a wavelength of λ nm. Further, nx is the refractive index in the slow axis direction in the film plane, ny is the refractive index in the fast axis direction in the film plane, nz is the refractive index in the thickness direction of the film, and d is the thickness of the film. (Unit: nm). ]
式（VII） ： ０．１≦Ｒｅ(590)／Ｒｔｈ(590)≦０．８ The polarizing plate according to any one of claims 1 to 3, wherein the front retardation value Re and the retardation value Rth in the film thickness direction of the one protective film satisfy the following formula (VII).
Formula (VII): 0.1 ≦ Re (590) / Rth (590) ≦ 0.8
該セルロースアシレートが、アセチル基の置換度Ａと、炭素原子数が３以上のアシル基の置換度Ｂとが下記式（VIII）、（IX）を満たすことを特徴とする請求項１乃至４のいずれかに記載の偏光板。
式（VIII）： ２．０≦Ａ＋Ｂ≦３．０
式（IX） ： ０＜Ｂ The one protective film is a cellulose acylate film comprising, as a main polymer component, cellulose acylate which is a mixed fatty acid ester of cellulose in which a hydroxyl group of cellulose is substituted with an acetyl group and an acyl group having 3 or more carbon atoms. ,
5. The cellulose acylate according to claim 1, wherein the substitution degree A of the acetyl group and the substitution degree B of the acyl group having 3 or more carbon atoms satisfy the following formulas (VIII) and (IX): The polarizing plate in any one of.
Formula (VIII): 2.0 ≦ A + B ≦ 3.0
Formula (IX): 0 <B
式（Ｘ） ： ２．０≦ＤＳ２＋ＤＳ３＋ＤＳ６≦３．０
式（ＸI） ： ＤＳ６／（ＤＳ２＋ＤＳ３＋ＤＳ６）≧０．３１５ The one protective film is a film made of cellulose acylate obtained by substituting the hydroxyl group of the glucose unit constituting cellulose with an acyl group having 2 or more carbon atoms, and comprising 2 glucose units constituting cellulose. When the substitution degree of the hydroxyl group at the position is DS2, the substitution degree of the hydroxyl group at the 3-position is DS3, and the substitution degree of the hydroxyl group at the 6-position is DS6, the following formulas (X) and (XI The polarizing plate according to claim 1, wherein the polarizing plate is a cellulose acylate film satisfying
Formula (X): 2.0 ≦ DS2 + DS3 + DS6 ≦ 3.0
Formula (XI): DS6 / (DS2 + DS3 + DS6) ≧ 0.315
式（ＸII）： ０．９≦ＥTF／ＥMF≦１．７ 12. The elastic modulus EMF in the MD direction and the elastic modulus ETF in the TD direction satisfy the following formula (XII) at 25 ° C. and 60% RH of the one protective film. Polarizing plate.
Formula (XII): 0.9 ≦ ETF / EMF ≦ 1.7
式（ＸIII）： ２８４０ＭＰａ≦ＥTF≦４７１０ＭＰａ 13. The polarizing plate according to claim 1, wherein an elastic modulus ETF in a TD direction at 25 ° C. and 60% RH of the one protective film satisfies the following formula (XIII).
Formula (XIII): 2840 MPa ≦ ETF ≦ 4710 MPa