JP2006010733A - Handicraft clay and molding material - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide handicraft clay superior in modeling and easy to be reduced in soil, a plant pot modeling material superior in modeling easy for reducing in soil, and a plant pot kit which even children can handle that contains the modeling material. <P>SOLUTION: This handicraft clay contains plant powder 5-20 wt.%, volcanic ash balloons 10-20 wt.%, talc 10-21 wt.%, pulp 5-11 wt.%, glue material 0.1-5 wt.%, and moisture 30-60 wt.%, and this plant powder is made into stalks cut into 1-5mm lengths. The modeling material contains this handicraft clay 1000, plant rough powder 200-800, polyvinyl alcohol 30-150 wt.parts, and carboxymethyl cellulose 1-10 wt.parts, and the plant rough powder is made into stalks cut into 5-30mm lengths. The plant pot kit includes this modeling material. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

本発明は、工作用粘土、該工作用粘土を含む原料から得られる成形用材、該成形用材を含む植木鉢作成用キットに関する。   The present invention relates to a work clay, a molding material obtained from a raw material containing the work clay, and a plant pot making kit including the molding material.

工作用粘土としては、パルプに糊剤を配合した紙粘土が一般に用いられている（例えば、特許文献１参照。）。更に、綿繊維を混入させることも試みられている（例えば、特許文献１参照。）。又、燃やして廃棄処分でき、しかも燃やした場合に有害物質が発生することのないようにと、くるみ殻粉末と、籾殻粉末と、竹粉末と、木粉末と、ケナフ粉末とから構成される群より選択された一種又は二種以上のものから構成される天然植物性粉末を配合することが開示されている（例えば、特許文献２参照。）。   As the clay for work, paper clay in which paste is mixed with pulp is generally used (for example, see Patent Document 1). Furthermore, attempts have been made to mix cotton fibers (see, for example, Patent Document 1). In addition, a group consisting of walnut husk powder, rice husk powder, bamboo powder, wood powder, and kenaf powder so that they can be burned and disposed of, and no harmful substances are generated when burned. It is disclosed that a natural vegetable powder composed of one or more selected ones is blended (see, for example, Patent Document 2).

パルプや天然植物性粉末を骨材として用いたこれらの従来の紙粘土は、ボソボソした性状で粘りに欠け、造形がやりにくい。   These conventional paper clays using pulp or natural vegetable powder as an aggregate are lumpy and lack stickiness and are difficult to shape.

又、使用後土に還そうとしても分解がおそく、大量に畑や野原に投棄することはできない。
特開平６−２０２５５６号公報 特開２００１−１３４１７１号公報 Moreover, even if it is tried to return to the soil after use, it will decompose slowly and cannot be dumped in large quantities in fields or fields.
JP-A-6-202556 JP 2001-134171 A

本発明の目的は、成形性にすぐれ土に容易に還元ができる工作用粘土を提供することにある。   An object of the present invention is to provide a clay for work that has excellent formability and can be easily reduced to soil.

本発明の目的は、成形性にすぐれ土に容易に還元ができる植木鉢用成形用材を提供することにある。   An object of the present invention is to provide a material for molding a flower pot that has excellent moldability and can be easily reduced to soil.

本発明の目的は、この成形用材を含み、児童でも取り扱える植木鉢作成用キットを提供することにある。   An object of the present invention is to provide a flowerpot making kit that includes this molding material and can be handled by children.

本発明の要旨とするところは、
粉体状植物 ５〜２０重量％
シラスバルーン １０〜２０重量％
タルク １０〜２１重量％
パルプ ５〜１１重量％
糊材 ０．１〜５重量％
水分 ３０〜６０重量％
を含む組成物が混練されて成り、
前記粉体状植物が１〜５ｍｍにカットされた茎であることを特徴とする工作用粘土であることにある。 The gist of the present invention is that
Powdery plant 5-20% by weight
Shirasu Balloon 10-20% by weight
Talc 10-21% by weight
Pulp 5-11% by weight
0.1-5% by weight of paste material
Moisture 30-60% by weight
A composition comprising kneaded,
The powdery plant is a work clay characterized by being a stem cut to 1 to 5 mm.

前記工作用粘土においては、前記糊材がポリビニルアルコールと該ポリビニルアルコールに対して０．０５〜５重量％の硼酸から成リ得る。   In the work clay, the paste material can be made of polyvinyl alcohol and 0.05 to 5% by weight of boric acid based on the polyvinyl alcohol.

前記工作用粘土は、さらに、組成物として液体肥料を含有し得る。   The work clay may further contain liquid fertilizer as a composition.

前記粉体状植物は、液体肥料を含有し得る。   The powdery plant may contain liquid fertilizer.

前記工作用粘土はリンゴ酢を含み得る。   The work clay may include cider vinegar.

又、本発明の要旨とするところは、
前記工作用粘土 １０００重量部
粗粉体状植物 ２００〜８００重量部
ポリビニルアルコール ３０〜１５０重量部
カルボキシメチルセルロース １〜１０重量部
を含み、
前記粗粉体状植物が５〜３０ｍｍにカットされた茎であることを特徴とする成形用材であることにある。 In addition, the gist of the present invention is that
1000 parts by weight of the clay for work
Coarse powdery plant 200-800 parts by weight
30-150 parts by weight of polyvinyl alcohol
1 to 10 parts by weight of carboxymethylcellulose,
The coarse powdery plant is a stalk cut to 5 to 30 mm.

前記粗粉体状植物は液体肥料を含有し得る。   The coarse powder plant may contain liquid fertilizer.

前記成形用材はリンゴ酢を含み得る。   The molding material may include apple vinegar.

又更に、本発明の要旨とするところは、前記成形用材が鉢状に成形されて成る植生用鉢であることにある。   Still further, the gist of the present invention resides in a vegetation pot formed by forming the molding material into a pot shape.

又、本発明の要旨とするところは、前記成形用材と、チップ化された植物と、鉢状の容器又は該容器の材料であるシート材とを含んで構成され、前記鉢状の容器又は前記シート材が生分解性である植木鉢作成用キットであることにある。   Further, the gist of the present invention includes the molding material, the chip plant, and a pot-shaped container or a sheet material that is a material of the container, and the pot-shaped container or the The sheet material is a kit for making a flower pot that is biodegradable.

前記植木鉢作成用キットにおいては、前記成形用材が液体肥料を含有し得る。   In the plant pot making kit, the molding material may contain liquid fertilizer.

前記植木鉢作成用キットは、前記成形用材及び前記チップ化された植物とを収納する箱を含み得、前記シート材が該箱を展開した展開盤であり得、該展開盤に前記容器を展開した展開板の輪郭形状に沿ったミシン目が形成され得、該展開板から前記容器が組み立てられ得る。   The plant pot making kit may include a box for storing the molding material and the chipped plant, and the sheet material may be a developing board in which the box is developed, and the container is developed in the developing board. A perforation along the profile of the development plate can be formed, and the container can be assembled from the development plate.

更に、本発明の要旨とするところは、
シラスバルーン、タルク、パルプ、ポリビニルアルコール及び硼酸を準備する工程、
少なくとも前記シラスバルーン、前記タルク、前記パルプ及び前記ポリビニルアルコールの一部を混合して混合物を得る工程、
１〜５ｍｍにカットされた茎から成る粉体状植物を準備する工程、
前記粉体状植物と前記液体肥料とを混合する工程、
混合された前記粉体状植物と前記液体肥料とを加圧タンク中で加圧して液体肥料を含有する粉体状植物を得る工程、
少なくとも前記混合物、前記液体肥料を含有する粉体状植物、前記ポリビニルアルコールの残部及び前記硼酸を混練する工程、
を含む工作用粘土の製造方法であることにある。 Further, the gist of the present invention is that
Preparing shirasu balloon, talc, pulp, polyvinyl alcohol and boric acid,
Mixing at least a part of the shirasu balloon, the talc, the pulp and the polyvinyl alcohol to obtain a mixture;
Preparing a powdery plant comprising stems cut to 1-5 mm,
Mixing the powdery plant and the liquid fertilizer,
Pressurizing the mixed powdery plant and the liquid fertilizer in a pressurized tank to obtain a powdered plant containing the liquid fertilizer;
Kneading at least the mixture, the powdery plant containing the liquid fertilizer, the remainder of the polyvinyl alcohol and the boric acid,
It is in the manufacturing method of the clay for work containing.

本発明によると、粘り気と成形性にすぐれ、紙、鉄、ガラス、プラスチックに対する付着性が良好で、工作時に手や衣服を汚さず、土に容易に還元できる工作用粘土が提供される。   According to the present invention, it is possible to provide a clay for work that is excellent in stickiness and formability, has good adhesion to paper, iron, glass, and plastic, and that can be easily reduced to the soil without soiling hands and clothes during work.

本発明によると、成形性にすぐれ土に容易に還元できる植木鉢用成形用材が提供される。   ADVANTAGE OF THE INVENTION According to this invention, the molding material for flowerpots which is excellent in a moldability and can be easily reduced to soil is provided.

本発明によると、この成形用材を含み、児童でも取り扱える植木鉢作成用キットが提供される。   According to the present invention, there is provided a flowerpot making kit that includes this molding material and can be handled by children.

本発明によると、葦等の茎性の植物の有効利用が出来る。   According to the present invention, it is possible to effectively use stem plants such as cocoons.

本発明の実施形態について説明する。本発明の工作用粘土は、骨材や充填材としての粉体状植物、シラスバルーン、タルク及びパルプと、糊材としてのポリビニルアルコールと、安定剤等の助剤とを組成物として含んで構成され、
粉体状植物 ５〜２０重量％
シラスバルーン １０〜２０重量％
タルク １０〜２１重量％
パルプ ５〜１１重量％
糊材 ０．１〜５重量％
水 ３０〜６０重量％
を含む組成物の混練物より成る。 An embodiment of the present invention will be described. The work clay of the present invention comprises a composition comprising powdery plants as aggregates and fillers, shirasu balloons, talc and pulp, polyvinyl alcohol as a paste, and an auxiliary agent such as a stabilizer. And
Powdery plant 5-20% by weight
Shirasu Balloon 10-20% by weight
Talc 10-21% by weight
Pulp 5-11% by weight
0.1-5% by weight of paste material
30-60% by weight of water
Comprising a kneaded composition.

この粉体状植物は、葦、ススキ、イグサ、麻、稲、麦類等の茎性の植物の茎が１〜５ｍｍにカットされたものである。   In this powdery plant, stems of stem plants such as straw, Japanese pampas grass, rush, hemp, rice, and wheat are cut to 1 to 5 mm.

この混練物は、例えば、シラスバルーン、タルク、パルプ、糊材を準備し、このなかのシラスバルーン、タルク、パルプ及び糊材の一部を適量の水とともに混合して混合物を得て、１〜５ｍｍにカットされた茎から成る粉体状植物と、この混合物と、糊材の残部と、助剤とを適量の水とともに混練して得られる。   This kneaded material is prepared, for example, by preparing shirasu balloon, talc, pulp, glue material, and mixing a part of shirasu balloon, talc, pulp and glue material together with an appropriate amount of water to obtain a mixture of 1 to 1 It is obtained by kneading a powdery plant composed of stems cut to 5 mm, this mixture, the remainder of the paste, and an auxiliary agent together with an appropriate amount of water.

糊材としてはポリビニルアルコールが好ましく用いられる。澱粉糊等の生分解性のものが用いられてもよい。糊材としてポリビニルアルコールを用いる場合は硼酸が助剤として用いられることが好ましい。硼酸はポリビニルアルコールの不溶化のためと工作用粘土の粘り気の増大のために添加される。硼酸の添加により、製品の外部からの湿気や水分に対する安定性が向上する。ポリビニルアルコールは、製品の粘り気と粘弾性が工作用に最適で好ましい。   Polyvinyl alcohol is preferably used as the paste material. Biodegradable materials such as starch paste may be used. When polyvinyl alcohol is used as the paste material, boric acid is preferably used as an auxiliary agent. Boric acid is added to insolubilize the polyvinyl alcohol and to increase the viscosity of the working clay. Addition of boric acid improves the stability against moisture and moisture from the outside of the product. Polyvinyl alcohol is preferable because the product has stickiness and viscoelasticity and is optimal for use in work.

パルプは再生パルプであってもよい。又、粉体状植物には液体肥料が含有されていてもよい。液体肥料は、チッソ成分、リン成分、カリ成分から選択される１種以上の成分を含むものであることが好ましい。チッソ成分、リン成分、カリ成分の全てが含まれることが更に好ましい。   The pulp may be recycled pulp. Moreover, liquid fertilizer may be contained in the powdery plant. The liquid fertilizer preferably contains one or more components selected from a nitrogen component, a phosphorus component, and a potash component. More preferably, all of the nitrogen component, phosphorus component, and potassium component are included.

粉体状植物に液体肥料を含有させるには、加圧タンクに収納された粉体状植物と液体肥料との混合物を加圧して、液体肥料を粉体状植物の茎の内部に浸透させることが好ましい。あるいは、液体肥料の液に粉体状植物を長時間浸漬して液体肥料を粉体状植物の茎の内部に浸透させることが好ましい。   To add liquid fertilizer to the powdered plant, pressurize the mixture of the powdered plant and the liquid fertilizer stored in the pressurized tank and allow the liquid fertilizer to penetrate into the stalk of the powdered plant. Is preferred. Alternatively, it is preferable to immerse the powdered plant in the liquid fertilizer liquid for a long time so that the liquid fertilizer penetrates into the stalk of the powdered plant.

植物の茎は、液体肥料を含有させてから粉体状に加工されてもよい。粉体状に加工されてから、液体肥料を含有させてもよい。   Plant stems may be processed into powder after containing liquid fertilizer. Liquid fertilizer may be contained after being processed into powder.

茎性の植物としては葦が混練時に他の原料とのなじみが良好で、均一な混合がなされ最も好ましい。   As a stem-like plant, koji is most preferable because it has good compatibility with other raw materials when kneaded and is uniformly mixed.

本発明の工作用粘土には、更に防腐剤が添加されていることが好ましい。防腐剤は、混練時に上述の原料とともに配合されることが好ましい。防腐剤としては有機酸をはじめ公知の防腐剤を用いることが出来る。なかでもリンゴ酢が不快臭を伴わず好ましい。防腐剤は全体に対して０．５〜２重量％添加されることが好ましい。   It is preferable that a preservative is further added to the work clay of the present invention. The preservative is preferably blended with the above-mentioned raw materials at the time of kneading. As the preservative, organic acids and known preservatives can be used. Of these, apple cider vinegar is preferable without an unpleasant odor. The preservative is preferably added in an amount of 0.5 to 2% by weight.

このようにして得られた本発明の工作用粘土は粘り気があり、成形時に棒状にして引っ張ると飴状に伸び、成形時の変形でボソボソと破壊されないので、工作時の成形がやりやすい。カット長が１ｍｍを下回ると、粘り気が不足する。カット長が５ｍｍを上回ると、茎の繊維が混練時に絡んできめこまかい均一な混練ができにくい。   The clay for work of the present invention thus obtained is sticky and stretches like a rod when pulled into a rod shape at the time of molding, and is not broken as a result of deformation at the time of molding. When the cut length is less than 1 mm, the stickiness is insufficient. When the cut length exceeds 5 mm, the stem fibers are entangled during kneading, and it is difficult to perform uniform kneading.

糊材としてポリビニルアルコールを用い、かつ組成物として液体肥料が添加された場合、工作用粘土の粘り気は更に向上する。液体肥料は上述のように粉体状植物に含有させて添加されてもよい。単独で添加されてもよい。液体肥料はポリビニルアルコールに対して０．０５〜１重量％添加されることが好ましい。液体肥料は、チッソ成分、リン成分、カリ成分から選択される１種以上の成分を含むものであることが好ましい。チッソ成分、リン成分、カリ成分の全てが含まれることが更に好ましい。   When polyvinyl alcohol is used as the paste material and liquid fertilizer is added as a composition, the clay of the work clay is further improved. The liquid fertilizer may be added to the powdery plant as described above. It may be added alone. The liquid fertilizer is preferably added in an amount of 0.05 to 1% by weight with respect to polyvinyl alcohol. The liquid fertilizer preferably contains one or more components selected from a nitrogen component, a phosphorus component, and a potash component. More preferably, all of the nitrogen component, phosphorus component, and potassium component are included.

茎性の植物、なかでも葦はパルプや綿繊維に比べて土中の分解が早いので、使用後に工作用粘土を畑や野原に投棄しても、容易に土に還元され好ましい。又、茎性の植物に肥料が含浸されたことにより、植物の育成や、土中での工作用粘土の分解が促進される。   Stem plants, especially cocoons, decompose more quickly in the soil than pulp and cotton fibers, so even if the working clay is dumped in fields or fields after use, it is easily reduced to the soil. Further, the impregnation of the stem-like plant with the fertilizer promotes the growth of the plant and the decomposition of the work clay in the soil.

本発明の工作用粘土は、紙、鉄、ガラス、プラスチックに手で押し付けたときの付着性が良好である。通常の紙粘土はこれらの素材からなる板に付着しにくい。   The work clay of the present invention has good adhesion when pressed against paper, iron, glass and plastic by hand. Ordinary paper clay is difficult to adhere to a plate made of these materials.

更に、本発明の工作用粘土は、手や衣服に付着しにくく、工作作業中に手や衣服が粘土で汚れる度合いが従来の紙粘土に比べ極めて少ない。例えば、本発明の工作用粘土は、一旦手で握ってからその粘土からその手をはなすと、握ったときの粘土と手の面との接触全面積中、その手の面に粘土が付着して残留している面積は、接触全面積の約２％にすぎない。従来の紙粘土は、同様に握ると、手の面に粘土が付着して残留している面積は、接触全面積の９５％に達する。   Furthermore, the work clay of the present invention hardly adheres to hands and clothes, and the degree of soiling of hands and clothes with clay during the work is extremely less than conventional paper clay. For example, when the clay for work of the present invention is once grasped with a hand and then released from the clay, the clay adheres to the surface of the hand in the entire contact area between the clay and the surface of the hand when grasped. The remaining area is only about 2% of the total contact area. When the conventional paper clay is gripped in the same manner, the area where the clay adheres to the surface of the hand and reaches 95% of the total contact area.

この特性は、本発明の工作用粘土に粉体状植物が所定量含有されていることや、所定量含まれるポリビニルアルコールが液体肥料により粘り気を生じたことや、ポリビニルアルコールに硼酸が添加されたことなどによる総合効果により得られたものと考えられる。   This characteristic is that the predetermined amount of powdery plant is contained in the work clay of the present invention, that the polyvinyl alcohol contained in the predetermined amount has become sticky by the liquid fertilizer, and boric acid is added to the polyvinyl alcohol. It is thought that it was obtained as a result of comprehensive effects.

又、本発明の工作用粘土は、組成比にもよるが、見かけ比重が約０．９５〜１．２と従来の紙粘土に比べ約３〜５割ほど小さく、このことも良好な粘り気の要因となっているものと思われる。   Moreover, although the work clay of the present invention depends on the composition ratio, the apparent specific gravity is about 0.95 to 1.2, which is about 30 to 50% smaller than that of the conventional paper clay. This seems to be a factor.

本発明の工作用粘土は、これをベース素材として更に粗粉体状植物、ポリビニルアルコール、カルボキシメチルセルロース、硼酸が配合されて成形用材を得ることが出来る。   The clay for work of the present invention can be used as a base material and further blended with coarse powdery plants, polyvinyl alcohol, carboxymethylcellulose and boric acid to obtain a molding material.

この成形用材は、工作用粘土１０００重量部に対して、
粗粉体状植物 ３００〜６５０重量部
ポリビニルアルコール ４０〜１５０重量部
カルボキシメチルセルロース １〜１０重量部
が配合され、更に、ポリビニルアルコールに対して硼酸が０．０５〜５重量％が配合され、これらが混練されて成るものである。 This molding material is based on 1000 parts by weight of clay for work.
Coarse powdery plant 300-650 parts by weight
40-150 parts by weight of polyvinyl alcohol
1 to 10 parts by weight of carboxymethyl cellulose is blended, and 0.05 to 5% by weight of boric acid is blended with polyvinyl alcohol, and these are kneaded.

粗粉体状植物は、茎性の植物の茎が５〜３０ｍｍにカットされたものである。   The coarse powdery plant is obtained by cutting a stem of a stem-like plant into 5 to 30 mm.

このようにして得られた成形用材は、植木鉢やポットのような鉢状に成形して乾燥させ鉢状成形体となし、この鉢状成形体に培土を充填して苗を植生することが出来る。この時、培土に粗粉体状植物と同様のチップ化された植物を混合することも出来る。植生された苗は所定期間育成後、培土及び鉢状成形体ごと土に植えることが出来、植えたあとそのまま苗を育成すると、チップ化された植物、培土及び鉢状成形体が土に自然に還元される。   The molding material thus obtained is formed into a pot shape such as a flower pot or pot and dried to form a pot-shaped molded body. The pot-shaped molded body can be filled with culture soil to plant seedlings. . At this time, a chip-like plant similar to the coarse powdery plant can be mixed with the culture medium. Planted seedlings can be planted in soil together with cultivated soil and pot-shaped molded bodies after growing for a predetermined period, and when planted as seedlings after planting, the planted plants, soil and pot-shaped molded bodies are naturally put into the soil. Reduced.

この鉢のように薄い周壁を有する鉢状成形体については、配合された粗粉体状植物の茎が５〜３０ｍｍにカットされたものであると、粗粉体状植物による補強効果により充分な強度の周壁が得られ好ましい。鉢状成形体には茎繊維が束状に存在するので、束状の茎繊維による補強効果が得られ、周壁の強度が大となる。カット長が５ｍｍを下回ると、強度が不足する。カット長が３０ｍｍを上回ると、成形作業がやりにくく均一な周壁ができにくい。   As for the pot-shaped molded body having a thin peripheral wall like this pot, if the stem of the blended coarse powdery plant is cut to 5 to 30 mm, the reinforcing effect by the coarse powdery plant is sufficient. A strong peripheral wall is obtained and preferable. Since the stem fibers are present in a bundle shape in the pot-shaped molded body, a reinforcing effect by the bundle-like stem fibers is obtained, and the strength of the peripheral wall is increased. If the cut length is less than 5 mm, the strength is insufficient. When the cut length exceeds 30 mm, it is difficult to perform the molding operation and it is difficult to form a uniform peripheral wall.

成形用材には液体肥料が含有されていてもよい。又、粗粉体状植物に液体肥料が含有されていてもよい。液体肥料は、チッソ成分、リン成分、カリ成分から選択される１種以上の成分を含むものであることが好ましい。チッソ成分、リン成分、カリ成分の全てが含まれることが更に好ましい。   The molding material may contain liquid fertilizer. Moreover, the liquid fertilizer may be contained in the coarse powdery plant. The liquid fertilizer preferably contains one or more components selected from a nitrogen component, a phosphorus component, and a potash component. More preferably, all of the nitrogen component, phosphorus component, and potassium component are included.

成形用材から鉢状成形体を作成する態様の一例を説明する。図１（ａ）に示すように、鉢状の型容器２の外周壁面及び外底面に成形用材４を所定の厚さに層状に塗付し、そのまま約１〜２日自然乾燥する。符号５は底穴である。これにより、図１（ｂ）に示すように鉢状成形体６が得られる。鉢状成形体６に型容器２がそのまま成形用材４の乾燥に伴って固着され、複合鉢１０が形成されていてもよい。この鉢状成形体６又は複合鉢１０に培土を充填して苗を植生し、植生された苗を所定期間育成後、培土及び複合鉢１０ごと土に植えることが出来る。植えたあとそのまま苗を育成すると、型容器２が生分解性であると、複合鉢１０が土に自然に還元される。   An example of the aspect which produces a pot-shaped molded object from the material for shaping | molding is demonstrated. As shown to Fig.1 (a), the molding material 4 is apply | coated to the outer peripheral wall surface and outer bottom face of the bowl-shaped type | mold container 2 to a predetermined thickness in layers, and is naturally dried as it is for about 1-2 days. Reference numeral 5 denotes a bottom hole. Thereby, as shown in FIG.1 (b), the pot-shaped molded object 6 is obtained. The mold container 2 may be fixed to the pot-shaped molded body 6 as it is as the molding material 4 is dried, and the composite bowl 10 may be formed. The pot-shaped molded body 6 or the composite pot 10 is filled with cultivated soil to plant seedlings. After the cultivated seedlings are grown for a predetermined period, the cultivated soil and the combined pots 10 can be planted in the soil. When seedlings are grown as they are after planting, if the mold container 2 is biodegradable, the composite pot 10 is naturally reduced to soil.

成形用材あるいは、粗粉体状植物に液体肥料が含有されていると、鉢状成形体６あるいは複合鉢１０が土に自然に還元される速度が増進され好ましい。   When the molding material or the coarse powdery plant contains liquid fertilizer, the rate at which the pot-shaped molded body 6 or the composite pot 10 is naturally reduced to the soil is increased, which is preferable.

成形用材から鉢状成形体６への成形は、通常の陶土の素地の成形の方法に準じて、例えば、轆轤成形や型プレス成形等により行なうことも出来るが、成形作業を型容器２を用いて児童により手作業で行なうことが出来る。更に、鉢状成形体６の成形から上述の苗の植生、地面への鉢状成形体６の植え込みに至る一貫の作業が、児童によりなされることにより、情操教育と自然環境保護意識の涵養を計ることが出来る。   Molding from the molding material into the pot-shaped molded body 6 can be performed by, for example, potting molding or mold press molding in accordance with a normal method of molding a clay body, but the molding operation is performed using the mold container 2. Can be done manually by children. Furthermore, the children are engaged in a consistent process from the formation of the pot-shaped molded body 6 to the vegetation of the seedlings described above and the implantation of the pot-shaped molded body 6 on the ground. Can be measured.

成形用材と、型容器２と、チップ化された植物とをセットにして所定の包装容器に収納して、供給することが出来る。   The molding material, the mold container 2 and the planted chips can be supplied as a set, housed in a predetermined packaging container.

この包装容器は紙箱であり得る。更に、この紙箱を展開して型容器２の材料として用いることが出来る。紙は生分解性であり、これにより資源を土に還元できて好ましい。この態様の一例を図２に示す。図２に示すように、梱包材２２に梱包された成形前の成形用材２０と、梱包材２２ａに梱包されたチップ化された植物２４と、約１５ｃｍの長さに切りそろえた葦の束６０を紐６２で括り梱包材２２ｂに梱包された葦見本６３とが、紙箱２６に収納されて植木鉢作成用キット３０を構成する。構成品の全てが土に還元される植木鉢作成用キット３０は、情操教育、自然環境保護教育にとって有用な教材となる。なお、植木鉢作成用キット３０には、付属品として成形作業に用いるポリエチレン製手袋３１が加えられてもよい。葦見本６３は葦を知らない児童への啓蒙のために加えられたものである。   The packaging container can be a paper box. Furthermore, this paper box can be developed and used as a material for the mold container 2. Paper is preferred because it is biodegradable, thereby reducing resources to the soil. An example of this aspect is shown in FIG. As shown in FIG. 2, a molding material 20 before molding packed in a packing material 22, a chip-like plant 24 packed in a packing material 22a, and a bundle 60 of cocoons cut to a length of about 15 cm. The scissors 63 packed in the packing material 22b with the string 62 are housed in the paper box 26 to constitute the plant pot making kit 30. The plant pot making kit 30 in which all the components are returned to the soil is a useful teaching material for emotional education and natural environment protection education. In addition, the polyethylene glove 31 used for a shaping | molding operation | work may be added to the plant pot creation kit 30 as an accessory. The book 63 is added for enlightenment of children who do not know fox.

紙箱２６は、図３に示す形状に展開されて展開盤３４となる。展開盤３４を折り目３２で折り、あるいは紙箱２６を折り目３２で開くことにより、組み立て展開自在とされている。又、展開盤３４にはミシン目４０、４１がそれぞれ形成されている。ミシン目４０に沿って展開盤３４をちぎり取ると、型容器２（図２）の側壁に相当する部分の略矩形又は略扇形の展開板４２が得られる。ミシン目４１に沿って展開盤３４をちぎり取ると、型容器２（図２）の底壁に相当する部分の略円形の展開板３５が得られる。   The paper box 26 is developed into the shape shown in FIG. The unfolding plate 34 is folded at the fold line 32 or the paper box 26 is opened at the fold line 32 so that the assembly can be unfolded. In addition, perforations 40 and 41 are formed on the development board 34, respectively. When the development board 34 is torn along the perforation 40, a substantially rectangular or substantially sector-shaped development plate 42 corresponding to the side wall of the mold container 2 (FIG. 2) is obtained. When the development board 34 is torn off along the perforation 41, a substantially circular development plate 35 corresponding to the bottom wall of the mold container 2 (FIG. 2) is obtained.

図４に示すように、展開板４２を筒状あるいはコーン状に組み立て、展開板３５を嵌め込み型容器２ａが得られる。展開板４２は長手方向の一端の縁に係合片５４が形成され、長手方向の他端部に係合片５４に係合する長穴５６が形成されている。又、展開板４２は一長縁部に長穴５０が形成されている。展開板３５の縁には長穴５０と係合する係合片５２が形成されている。展開板３５は筒状あるいはコーン状に組み立てた展開板４２の端部に接着剤で接着されてもよい。   As shown in FIG. 4, the development plate 42 is assembled in a cylindrical shape or a cone shape, and the development plate 35 is fitted into the container 2a. The development plate 42 has an engagement piece 54 formed at the edge of one end in the longitudinal direction, and an elongated hole 56 that engages with the engagement piece 54 at the other end in the longitudinal direction. Further, the developing plate 42 has a long hole 50 formed in one long edge portion. Engagement pieces 52 that engage with the long holes 50 are formed on the edge of the development plate 35. The development plate 35 may be adhered to the end of the development plate 42 assembled in a cylindrical shape or a cone shape with an adhesive.

粉体状植物 １．０ｋｇ
シラスバルーン １．５ｋｇ
タルク １．６ｋｇ
再生パルプ ０．８ｋｇ
ポリビニルアルコール ０．０３ｋｇ
硼酸 ０．５ｇｒ
を準備した。粉体状植物としては葦を平均２ｍｍの長さに切断したものを用いた。 Powdery plant 1.0kg
Shirasu Balloon 1.5kg
Talc 1.6kg
Recycled pulp 0.8kg
Polyvinyl alcohol 0.03kg
Boric acid 0.5gr
Prepared. As the powdery plant, one obtained by cutting cocoons into an average length of 2 mm was used.

シラスバルーン、タルク及び再生パルプの全量と、ポリビニルアルコールを１７重量倍の水に混合したものの半量を攪拌・混合し、混合物を得た。一方、粉体状植物全量と、液体肥料（住友化学工業株式会社製：商品名 住友尿素複合液肥２号。成分：窒素全量１０％、水溶性リン酸５％、水溶性加里８％）５０ｇｒとを混合して加圧タンク中で絶対圧０．５ＭＰａで加圧して液体肥料を葦の組織内に圧入し、タンクから取り出して乾燥した。   The whole amount of shirasu balloon, talc and recycled pulp and half of the mixture of polyvinyl alcohol in 17 weight times water were stirred and mixed to obtain a mixture. On the other hand, the total amount of powdery plants and liquid fertilizer (manufactured by Sumitomo Chemical Co., Ltd .: trade name Sumitomo urea complex liquid fertilizer No. 2; components: nitrogen total amount 10%, water-soluble phosphoric acid 5%, water-soluble potassium 8%) and 50 gr Were mixed and pressurized in an pressurized tank at an absolute pressure of 0.5 MPa, and the liquid fertilizer was pressed into the tissue of the cocoon, taken out of the tank and dried.

この液体肥料を含有させた粉体状植物全量と、混合物全量と、ポリビニルアルコールを１７重量倍の水に混合したものの残り半量と、水と硼酸とを混練装置にて混練し、水分率４０％、比重１．０５の工作用粘土を得た。   The total amount of the powdery plant containing the liquid fertilizer, the total amount of the mixture, the remaining half of the mixture of polyvinyl alcohol in 17 times by weight of water, water and boric acid are kneaded with a kneading apparatus, and the water content is 40%. A work clay with a specific gravity of 1.05 was obtained.

得られた工作用粘土（粘土Ａ）を３ｃｍ径の球体に成形し、両手で左右に引き千切るように引き伸ばしたところ３０ｃｍ以上の長さに引き伸ばすことができた。一方パルプと澱粉糊を主体とした通常の市販の紙粘土（粘土Ｂ）を同様にして引き伸ばしたところ５ｃｍ以下の長さで千切れてしまった。   The obtained work clay (clay A) was formed into a 3 cm diameter sphere and stretched to the left and right with both hands, and was able to be stretched to a length of 30 cm or more. On the other hand, when a normal commercial paper clay (clay B) mainly composed of pulp and starch paste was stretched in the same manner, it was broken into pieces with a length of 5 cm or less.

又、粘土Ａ、粘土Ｂにつき、それぞれ径１．５ｃｍの２０個の球体に成形し、垂直に立てたダンボール板の面に各球体それぞれを貼り付けた。粘土Ｂから成る球体は約３０分後に全ての球体が落下したが、粘土Ａから成る球体は２０個全てが６時間以上ダンボール板の面に付着したままで、落下することはなかった。   Further, each of clay A and clay B was formed into 20 spheres each having a diameter of 1.5 cm, and each sphere was attached to the surface of a corrugated cardboard standing upright. All of the spheres made of clay B dropped after about 30 minutes, but all 20 spheres made of clay A remained attached to the surface of the corrugated board for 6 hours or more and never dropped.

又、手で握れるほどの量の粘土Ａを手で強く握ったが、握ったのちの手のひらには、殆んど粘土の付着が認められなかった。粘土Ｂを同様に握ったのちの手のひらには、多くの粘土が付着していた。   Moreover, although the amount of clay A that could be grasped by hand was squeezed by hand, adhesion of clay was hardly recognized on the palm after grasping. A lot of clay had adhered to the palm after holding the clay B in the same manner.

又更に、この工作用粘土は粘土工作時の成形性が極めて良好であった。工作後のこの工作用粘土を土中に埋めたところ１年間で土に還元された。   Furthermore, this work clay had very good moldability during clay work. When this clay for work was buried in the soil, it was returned to the soil in one year.

更に、この工作用粘土１ｋｇに粗粉体状植物５００ｇｒ、ポリビニルアルコールを１７重量倍の水に混合した液１ｋｇ、カルボキシメチルセルロース５ｇｒ、硼酸２ｇｒ、液体肥料（住友化学工業株式会社製：商品名 住友尿素複合液肥２号）５０ｇｒ、リンゴ酢１０ｇｒ、を混練装置にて混練し、成形用材を得た。粗粉体状植物としては葦を平均１０ｍｍの長さに切断したものを用いた。   Furthermore, 1 kg of this clay for work, 1 kg of a coarse powdery plant mixed with 500 g of polyvinyl alcohol in 17 weight times water, 5 g of carboxymethylcellulose, 2 g of boric acid, liquid fertilizer (manufactured by Sumitomo Chemical Co., Ltd .: trade name Sumitomo Urea) Compound liquid fertilizer No. 2) 50 gr and apple vinegar 10 gr were kneaded with a kneader to obtain a molding material. As the coarse powdery plant, cocoons cut into an average length of 10 mm were used.

この成形用材は、成形性に優れ、植木鉢形に容易に成形できた。この成形用材を用いて成形された植木鉢に、畑土と、葦から成る粗粉体状植物とを１：２（容積比）で混合した配合土を入れてばらの苗を植生した。植生されたばらの成長は通常の土を用いて植生したばらに比べて良好であった。半年後にこのばらをこの植木鉢ごと土中に埋めたところばらはそのまま育ち、植木鉢はその後半年間で土に還元された。   This molding material was excellent in moldability and could be easily molded into a flower pot shape. In a flower pot molded using this molding material, a mixed soil in which field soil and coarse powdery plants made of straw were mixed at a ratio of 1: 2 (volume ratio) was added to plant rose seedlings. The growth of vegetation roses was better than that of vegetation using normal soil. Half a year later, when the roses were buried in the soil with the pots, the roses grew and the pots were reduced to the soil in the latter half of the year.

その他、本発明は、主旨を逸脱しない範囲で当業者の知識に基づき種々なる改良、修正、変更を加えた態様で実施できるものである。   In addition, the present invention can be carried out in a mode in which various improvements, modifications, and changes are added based on the knowledge of those skilled in the art without departing from the spirit of the present invention.

本発明の成形用材は、植木鉢形に工業的手段で成形して土に還る植木鉢として市販することも出来る。これにより、葦等の植物資源の有効活用に寄与することが出来る。   The molding material of the present invention can also be marketed as a flower pot that is molded into a flower pot shape by industrial means and returned to the soil. Thereby, it can contribute to effective utilization of plant resources, such as straw.

本発明において、成形用材から鉢状成形体を作成する態様の一例を説明する断面模式図であり、図１（ａ）は鉢状の型容器の外周壁面及び外底面に本発明の成形用材が層状に塗付された状態であり、図１（ｂ）はこれを乾燥させて得られる複合鉢の態様を示す。In this invention, it is a cross-sectional schematic diagram explaining an example of the aspect which produces a pot-shaped molded object from the molding material, Fig.1 (a) is the molding material of this invention on the outer peripheral wall surface and outer bottom face of a pot-shaped type | mold container. FIG. 1 (b) shows an embodiment of a composite bowl obtained by drying this. 本発明の植木鉢作成用キット３を示す斜視模式図である。It is a perspective schematic diagram which shows the kit 3 for flowerpot creation of this invention. 本発明において用いられる展開板を示す展開図である。It is an expanded view which shows the expansion | deployment board used in this invention. 本発明において複合鉢の製作に用いられる、型容器の態様を示す斜視組み立て模式図である。It is a perspective assembly schematic diagram which shows the aspect of the type | mold container used for manufacture of a composite bowl in this invention.

符号の説明Explanation of symbols

２、２ａ：型容器
４：成形用材
６：鉢状成形体
１０：複合鉢
２４：チップ化された植物
２６：紙箱
３０：植木鉢作成用キット
３４：展開盤
３５、４２：展開板
４０、４１：ミシン目 2, 2a: Mold container 4: Molding material 6: Pot-shaped molded body 10: Compound pot 24: Chip plant 26: Paper box 30: Flower pot making kit 34: Development board 35, 42: Development board 40, 41: Perforation

Claims (13)

粉体状植物 ５〜２０重量％
シラスバルーン １０〜２０重量％
タルク １０〜２１重量％
パルプ ５〜１１重量％
糊材 ０．１〜５重量％
水分 ３０〜６０重量％
を含む組成物が混練されて成り、
前記粉体状植物が１〜５ｍｍにカットされた茎であることを特徴とする工作用粘土。 Powdery plant 5-20% by weight
Shirasu Balloon 10-20% by weight
Talc 10-21% by weight
Pulp 5-11% by weight
0.1-5% by weight of paste material
Moisture 30-60% by weight
A composition comprising kneaded,
A working clay characterized in that the powdery plant is a stem cut to 1 to 5 mm. 前記糊材がポリビニルアルコールと該ポリビニルアルコールに対して０．０５〜５重量％の硼酸から成る請求項１に記載の工作用粘土。 2. The work clay according to claim 1, wherein the paste material comprises polyvinyl alcohol and 0.05 to 5% by weight boric acid based on the polyvinyl alcohol. さらに、組成物として液体肥料を含有する請求項１又は２に記載の工作用粘土。 Furthermore, the work clay of Claim 1 or 2 containing a liquid fertilizer as a composition. 前記粉体状植物が液体肥料を含有する請求項１乃至３のいずれかに記載の成形用材。 The molding material according to claim 1, wherein the powdery plant contains liquid fertilizer. リンゴ酢を含む請求項１乃至４のいずれかに記載の工作用粘土。 The clay for work according to any one of claims 1 to 4, comprising apple cider vinegar. 請求項１に記載の前記工作用粘土 １０００重量部
粗粉体状植物 ２００〜８００重量部
ポリビニルアルコール ３０〜１５０重量部
カルボキシメチルセルロース １〜１０重量部
を含み、
前記粗粉体状植物が５〜３０ｍｍにカットされた茎であることを特徴とする成形用材。 1000 parts by weight of the clay for work according to claim 1
Coarse powdery plant 200-800 parts by weight
30-150 parts by weight of polyvinyl alcohol
1 to 10 parts by weight of carboxymethylcellulose,
A molding material, wherein the coarse powdery plant is a stem cut to 5 to 30 mm. 前記粗粉体状植物が液体肥料を含有する請求項６に記載の成形用材。 The molding material according to claim 6, wherein the coarse powdery plant contains liquid fertilizer. リンゴ酢を含む請求項６又は７に記載の成形用材。 The molding material according to claim 6 or 7, comprising apple cider vinegar. 請求項６乃至８のいずれかに記載の前記成形用材が鉢状に成形されて成る植生用鉢。 A vegetation pot formed by forming the molding material according to any one of claims 6 to 8 into a pot shape. 請求項６乃至８のいずれかに記載の前記成形用材と、チップ化された植物と、鉢状の容器又は該容器の材料であるシート材とを含んで構成され、前記鉢状の容器又は前記シート材が生分解性である植木鉢作成用キット。 It is comprised including the said forming material in any one of Claim 6 thru | or 8, the chip-ized plant, and the pot-shaped container or the sheet material which is the material of this container, The said pot-shaped container or the said Kit for making flower pots with sheet material biodegradable. 前記成形用材が液体肥料を含有する請求項１０に記載の植木鉢作成用キット。 The plant pot making kit according to claim 10, wherein the molding material contains liquid fertilizer. 前記成形用材及び前記チップ化された植物とを収納する箱を含み、前記シート材が該箱を展開した展開盤であり、該展開盤に前記容器を展開した展開板の輪郭形状に沿ったミシン目が形成され、該展開板から前記容器が組み立てられる請求項１０又は１１に記載の植木鉢作成用キット。 A sewing machine including a box for storing the molding material and the chip-formed plant, wherein the sheet material is a development board in which the box is developed, and a sewing machine along a contour shape of a development board in which the container is developed on the development board The pot for making a flowerpot according to claim 10 or 11, wherein eyes are formed and the container is assembled from the development plate. シラスバルーン、タルク、パルプ、ポリビニルアルコール及び硼酸を準備する工程、
少なくとも前記シラスバルーン、前記タルク、前記パルプ及び前記ポリビニルアルコールの一部を混合して混合物を得る工程、
１〜５ｍｍにカットされた茎から成る粉体状植物を準備する工程、
前記粉体状植物と前記液体肥料とを混合する工程、
混合された前記粉体状植物と前記液体肥料とを加圧タンク中で加圧して液体肥料を含有する粉体状植物を得る工程、
少なくとも前記混合物、前記液体肥料を含有する粉体状植物、前記ポリビニルアルコールの残部及び前記硼酸を混練する工程、
を含む工作用粘土の製造方法。
Preparing shirasu balloon, talc, pulp, polyvinyl alcohol and boric acid,
Mixing at least a part of the shirasu balloon, the talc, the pulp and the polyvinyl alcohol to obtain a mixture;
Preparing a powdery plant comprising stems cut to 1-5 mm,
Mixing the powdery plant and the liquid fertilizer,
Pressurizing the mixed powdery plant and the liquid fertilizer in a pressurized tank to obtain a powdered plant containing the liquid fertilizer;
Kneading at least the mixture, the powdery plant containing the liquid fertilizer, the remainder of the polyvinyl alcohol and the boric acid,
A method for producing clay for work.

Images