JP2006001942A - Pest control material - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a pest control material sufficiently attracting pest insects for a long term and having excellent pest control effect. <P>SOLUTION: The invention relates to the pest control material comprising the pest control material obtained by supporting the pest controlling ingredients on a fiber base colored by an azo dye, the pest control material obtained by supporting the pest controlling ingredients on a fiber base composed of polyester fiber or polyolefin fiber colored by the azo dye, the pest control material obtained by supporting the pest controlling ingredients on a fiber base colored by azo dyes having color tone which attracts the insect pest, and the pest control material obtained by supporting the pest controlling ingredients on a fiber base colored by a yellow or a blue azo dyes. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

本発明は害虫防除材に関するものである。   The present invention relates to a pest control material.

従来より、害虫を誘引する色調を有する粘着リボン等を用いて害虫を誘引、捕殺する害虫防除方法が知られている（植物防疫第３６巻第１０号第３８〜４１頁、１９８２年）。また、昆虫成長制御剤を担持させた害虫誘引色を呈する基材を用いて害虫を不妊化し、害虫密度の低下を図る方法も提案されている（特開平５−２３６８５６号公報）。   Conventionally, there is known a pest control method for attracting and killing pests using an adhesive ribbon having a color tone that attracts pests (Plant Protection Vol. 36, No. 10, pages 38-41, 1982). In addition, a method has been proposed in which a pest is sterilized by using a base material exhibiting a pest-attracting color carrying an insect growth control agent to reduce the pest density (Japanese Patent Laid-Open No. 5-236856).

特開平５−２３６８５６号公報JP-A-5-236856

しかしながら、実用場面においては温度、湿度、光照射等の変化する種々の条件下において常に害虫を充分に誘引すると共に、長期間にわたって誘引効力を維持する必要があり、環境条件の変化に左右されない害虫防除材の開発が望まれていた。   However, in practical use, it is necessary to always attract pests sufficiently under various conditions such as temperature, humidity, light irradiation, etc., and to maintain the attracting effect for a long period of time, and is not affected by changes in environmental conditions. Development of a control material was desired.

本発明は、以下の発明を含む。
［発明１］
アゾ系色素により着色された繊維基材に、防虫活性成分が保持されてなることを特徴とする害虫防除材。
［発明２］
繊維基材がポリエステル繊維又はポリオレフィン繊維の繊維基材であることを特徴とする発明１記載の害虫防除材。
［発明３］
アゾ系色素が害虫を誘引する色調を有する色素であることを特徴とする発明１又は発明２記載の害虫防除材。
［発明４］
アゾ系色素が黄色又は青色アゾ系色素であることを特徴とする発明１又は発明２記載の害虫防除材。 The present invention includes the following inventions.
[Invention 1]
A pest control material characterized in that an insect repellent active ingredient is held on a fiber substrate colored with an azo dye.
[Invention 2]
The pest control material according to invention 1, wherein the fiber substrate is a fiber substrate of polyester fiber or polyolefin fiber.
[Invention 3]
The pest control material according to invention 1 or 2, wherein the azo dye is a dye having a color tone that attracts pests.
[Invention 4]
The pest control material according to invention 1 or 2, wherein the azo dye is a yellow or blue azo dye.

本発明の害虫防除材は、長期間にわたって害虫を充分に誘引することから、優れた害虫防除効力を有するものである。   The pest control material of the present invention has an excellent pest control effect because it sufficiently attracts pests over a long period of time.

本発明は、上述の課題を解決するものであり、基材に害虫誘引色を着けるに際してアゾ系色素を用いるものである。即ち、本発明は、アゾ系色素、例えばアゾ系黄色色素により害虫誘引色を呈する基材に、防虫活性成分が保持されてなる害虫防除材、およびアゾ系色素により害虫誘引色を呈する基材により害虫を誘引する方法を提供するものである。   The present invention solves the above-described problems, and uses an azo dye when applying a pest attracting color to a substrate. That is, the present invention relates to a pest control material in which an insecticidal active ingredient is retained on a substrate exhibiting a pest-attracting color by an azo dye, for example, an azo yellow dye, and a substrate exhibiting a pest-attracting color by an azo dye. It provides a method for attracting pests.

そもそも、色素は化学構造上、ニトロ系、ニトロソ系、アゾ系、スチルベン系、カルボニウム系、キノリン系、メチン系、チアゾール系、キノンイミン系、ラクトン系、アミノケトン系、ヒドロキシケトン系、アントラキノン系、インジゴ系、チオインジゴ系、フタロシアニン系等の多種の系統に分類されるが、本発明において用いられるアゾ系色素とは、その化学構造中にアゾ基
−Ｎ＝Ｎ−
を有する色素全般を意味するものである。 In the first place, the dye has chemical structure, nitro, nitroso, azo, stilbene, carbonium, quinoline, methine, thiazole, quinoneimine, lactone, aminoketone, hydroxyketone, anthraquinone, indigo The azo dye used in the present invention is an azo group —N═N— in the chemical structure, but is classified into various systems such as thioindigo and phthalocyanine.
It means all dyes having

アゾ系色素には、モノアゾ系染料、ジスアゾ系染料、トリスアゾ系染料、ポリアゾ系染料、アゾイック系染料、溶性アゾ系顔料、アゾレーキ顔料、不溶性アゾ系顔料、縮合アゾ系顔料等がある。
アゾ系染料としては、例えばスミノールミリングイエローＯ、ブリリアントスカーレット３Ｒ、アミニルブルーＥ−２ＧＬ、スミノールミリングシアニン５Ｒエクストラ（以上、住友化学工業製）等のアゾ系酸性染料、スミカロンイエローＳＥ−５Ｇ、スミカロンイエローＳＥ−３ＧＬ、スミカロンオレンジＳＥ−Ｂ、スミカロンイエローブラウン２ＲＬ−Ｓ、スミカロンレッドＥ−ＦＢＬ、スミカロンルビンＳＥ−ＧＬ（以上、住友化学工業製）等のアゾ系分散染料、スミフィックスブリリアントイエローＨ−３Ｇ、スミフィックススカーレットＨ−２Ｇ、スミフィックスターコイスブルーＨ−ＧＦ、スミフィックスブリリアントブルーＲ（以上、住友化学工業製）等のアゾ系反応染料、ダイレクトファーストイエローＧＣ、ダイレクトファーストオレンジＳ、ダイレクトファーストスカーレット
４ＢＳ、スミライトスープラレッド４ＢＬ、ダイレクトスカイブルー５Ｂ、スミライトスープラブルーＢＲＲ、ダイレクトコッパーブルーＢＢＳ（以上、住友化学工業製）等のアゾ系直接染料、スミアクリルレッドＦ−ＧＴＬ（住友化学工業製）等のアゾ系カチオン染料、アゾ系硫化染料、アゾ系油溶染料、ビスアゾ系直接染料、Benzopurpurine、Chrysophenine 、Nippon、Sumilight （以上、住友化学工業製）等のトリスアゾ系直接染料、アゾイック系分散染料などが挙げられる。
アゾ系顔料としては、例えばアセト酢酸アニリド系アゾ顔料、ピラゾロン系アゾ顔料、β−ナフトール系アゾ顔料、β−オキシナフトエ酸系アゾ顔料、β−オキシナフトエ酸アニリド系アゾ顔料等の溶性アゾ系顔料およびアゾレーキ顔料、アセト酢酸アニリド系モノアゾ顔料、アセト酢酸アニリド系ビスアゾ顔料、ピラゾロン系モノアゾ顔料、ピラゾロン系ビスアゾ顔料、β−ナフトール系アゾ顔料、β−オキシナフトエ酸アニリド系モノアゾ顔料、β−オキシナフトエ酸アニリド系ビスアゾ顔料等の不溶性アゾ系顔料、アセト酢酸アニリド系アゾ顔料、β−オキシナフトエ酸アニリド系アゾ顔料等の縮合アゾ系顔料、ベンズイミダゾロン系顔料、難溶性金属塩モノアゾ顔料などが挙げられる。 Examples of the azo dye include a monoazo dye, a disazo dye, a trisazo dye, a polyazo dye, an azoic dye, a soluble azo pigment, an azo lake pigment, an insoluble azo pigment, and a condensed azo pigment.
Examples of the azo dye include azo acid dyes such as Suminol Milling Yellow O, Brilliant Scarlet 3R, Aminyl Blue E-2GL, Suminol Milling Cyanine 5R Extra (manufactured by Sumitomo Chemical Co., Ltd.), Sumikaron Yellow SE-5G, Azo-based disperse dyes such as Sumicaron Yellow SE-3GL, Sumicaron Orange SE-B, Sumicaron Yellow Brown 2RL-S, Sumicaron Red E-FBL, Sumicaron Rubin SE-GL (manufactured by Sumitomo Chemical Co., Ltd.), Azo-based reactive dyes such as Sumifix Brilliant Yellow H-3G, Sumifix Scarlet H-2G, Sumifix Turquoise Blue H-GF, Sumifix Brilliant Blue R (Sumitomo Chemical Industries), Direct First Yellow GC, Direct Yellow AST Orange S, Direct First Scarlet 4BS, Sumilite Supra Red 4BL, Direct Sky Blue 5B, Sumilite Supra Blue BRR, Direct Copper Blue BBS (above, manufactured by Sumitomo Chemical Co., Ltd.) and other azo-based direct dyes, Sumiacryl Red F-GTL Trisazo direct dyes such as azo cationic dyes (manufactured by Sumitomo Chemical Co., Ltd.), azo sulfur dyes, azo oil-soluble dyes, bisazo direct dyes, Benzopurpurine, Chrysophenine, Nippon, Sumilight (manufactured by Sumitomo Chemical Co., Ltd.) And azoic disperse dyes.
Examples of the azo pigment include soluble azo pigments such as acetoacetanilide azo pigments, pyrazolone azo pigments, β-naphthol azo pigments, β-oxynaphthoic acid azo pigments, β-oxynaphthoic acid anilide azo pigments, and the like. And azo lake pigments, acetoacetanilide monoazo pigments, acetoacetanilide bisazo pigments, pyrazolone monoazo pigments, pyrazolone bisazo pigments, β-naphthol azo pigments, β-oxynaphthoic acid anilide monoazo pigments, β-oxynaphthoic acid Examples include insoluble azo pigments such as anilide bisazo pigments, condensed azo pigments such as acetoacetanilide azo pigments, β-oxynaphthoic acid anilide azo pigments, benzimidazolone pigments, and poorly soluble metal salt monoazo pigments. .

本発明において用いられるアゾ系色素の具体名としては、ファーストイエローＧ、ファーストイエロー１０Ｇ、ジスアゾイエローＡＡＡ、ジスアゾイエローＡＡＭＸ、ジスアゾイエローＡＡＯＴ、ジスアゾイエローＡＡＯＡ、ジスアゾイエローＡＡＰＴ、ジスアゾイエローＨ１０Ｇ、ジスアゾイエローＨＲ、クロモフタルイエローＧＲ、ファーストイエローＦＧＬ、ファーストイエロー１０ＧＸ、タートラジンレーキ、メチンイエロー、サンセットイエローレーキ、ベンズイミダゾロンイエロー、ジニトロアニリンオレンジ、ピラゾロンオレンジ、ジアニシジンオレンジ、ペルシアンオレンジレーキ、ベンズイミダゾロンイエローＨ２Ｇ、ベンズイミダゾロンイエローＨＬ、パラレッド、ナフトールレッドＦＲＲ、ナフトールレッド４Ｒ、ナフトールカーミンＦＢ、ナフトールレッドＭ、レーキレッド４Ｒ、ナフトールレッドＢＳ、ナフトールレッドＲＮ、ブリリアントスカーレットＧ、ナフトールレッド、クロモフタルスカーレット、ベンズイミダゾロンカーミン、ハンザイエロー１０Ｇ、ハンザイエロー５Ｇ、ハンザイエロー３Ｇ、ハンザイエローＧ、ハンザイエローＧＲ、ハンザイエローＡ、ハンザイエローＲＮ、ピグメントイエローＬ、ベンジジンイエロー、ベンジジンイエローＧ、ベンジジンイエローＧＲ、パーマネントイエローＮＣＧ、バルカンファーストイエロー５Ｇ、バルカンファーストイエローＲ、パーマネントイエローＦＧＬ、パーマネントイエローＨＲ、パーマネントイエローＨ１０Ｇ（以上、標準名）、ファーストイエローＧ、ファーストイエロー１０Ｇ（以上、日本ピグメント製）、ジスアゾイエローＬ３Ｇ−Ｇ、ジスアゾイエロー３ＧＲ、ジスアゾイエロー３Ｒ、ジスアゾイエロー５Ｇ、ジスアゾオレンジＬＧ、ファーストスカーレットＧＲ−Ｗ、レーキボルドー１０Ｂ−Ｏ（以上、住化カラー製）、スミカプリントイエローＳＴ−Ｏ、スミカプリントイエローＧＦＮ、スミカファーストイエローＧＢＦＮ、スミカコートイエロー２ＲＮ、スミトーンファーストイエローＨＲＴ、スミトーンオレンジＧ、ペルシャオレンジＧＲ、スミカコートカーミンＢ、スミトーンスカーレットＡ−５８４８、ファーストスカーレット２Ｇ−Ｗ、スミトーンファーストスカーレットＡＳＧ、スミトーンレッドＰＺ、スミカプリントレッドＫＦ、スミカプリントレッド３ＢＦ、スミトーンイエローＧＢ、レーキファーストグリーンイエロー５Ｇ（以上、住友化学工業製）、パーマネントレッドＦＲＲ、パーマネントオレンジＨＬ、ノボパームイエローＨ２Ｇ、ハンザブリリアントイエロー１０ＧＸ、パーマネントイエローＧＲ、パーマネントイエローＨ１０Ｇ（以上、ヘキスト製）、クロモフタルイエロー２Ｇ、クロモフタルイエローＧＲ、クロモフタルイエロー３Ｇ（以上、チバガイギー製）、ジスアゾイエローＦＧ−１７００（以上、東洋インキ製）等が挙げられる。   Specific names of the azo dyes used in the present invention include First Yellow G, First Yellow 10G, Disazo Yellow AAA, Disazo Yellow AAMX, Disazo Yellow AAOT, Disazo Yellow AAOA, Disazo Yellow AAPT, Disazo Yellow H10G, Disazo Yellow HR, Chromophthal Yellow GR, First Yellow FGL, First Yellow 10GX, Tartrazine Lake, Metin Yellow, Sunset Yellow Lake, Benzimidazolone Yellow, Dinitroaniline Orange, Pyrazolone Orange, Dianisidine Orange, Persian Orange Lake, Benzimidazolone Yellow H2G , Benzimidazolone Yellow HL, Para Red, Naphthol Red FRR, Naphthol Red 4R, Na Tall Carmine FB, Naphthol Red M, Lake Red 4R, Naphthol Red BS, Naphthol Red RN, Brilliant Scarlet G, Naphthol Red, Chromophthal Scarlet, Benzimidazolone Carmine, Hansa Yellow 10G, Hansa Yellow 5G, Hansa Yellow 3G, Hansa Yellow G, Hansa Yellow GR, Hansa Yellow A, Hansa Yellow RN, Pigment Yellow L, Benzidine Yellow, Benzidine Yellow G, Benzidine Yellow GR, Permanent Yellow NCG, Vulcan First Yellow 5G, Vulcan First Yellow R, Permanent Yellow FGL, Permanent Yellow HR , Permanent yellow H10G (above, standard name), first yellow G, first yellow 10G Above, made by Nippon Pigment), Disazo Yellow L3G-G, Disazo Yellow 3GR, Disazo Yellow 3R, Disazo Yellow 5G, Disazo Orange LG, First Scarlet GR-W, Lake Bordeaux 10B-O (above, Sumika Color), Sumika Print Yellow ST-O, Sumika Print Yellow GFN, Sumika First Yellow GBFN, Sumika Coat Yellow 2RN, Sumitone First Yellow HRT, Sumitone Orange G, Persia Orange GR, Sumika Coat Carmine B, Sumitone Scarlet A-5848, First Scarlet 2G-W, Sumitone First Scarlet ASG, Sumitone Red PZ, Sumika Print Red KF, Sumika Print Red 3BF, Sumitone Yellow GB, Rake First Green Yellow 5G (above, manufactured by Sumitomo Chemical), Permanent Red FRR, Permanent Orange HL, Novo Palm Yellow H2G, Hansa Brilliant Yellow 10GX, Permanent Yellow GR, Permanent Yellow H10G (above, made by Hoechst), Chromophthal Yellow 2G, Examples thereof include chromophthal yellow GR, chromophthal yellow 3G (above, manufactured by Ciba Geigy), disazo yellow FG-1700 (above, manufactured by Toyo Ink), and the like.

本発明において用いられるアゾ系色素の中ても、アゾ系顔料の使用が好ましく、特に、ジスアゾ顔料、不溶性アゾ系顔料、縮合アゾ系顔料が好ましい。
また、害虫を誘引する色調という点から、一般に黄色または青色アゾ系色素が用いられる。
黄色アゾ系色素としては、マンセル表色系における表示法においてマンセルヒューがＹＲ、ＹまたはＧＹで表される色素、さらには 2.5ＹＲ〜 7.5ＧＹで表される色素が挙げられる。また、マンセルバリューが通常４以上、好ましくは５以上の色素が用いられ、マンセルクロマは通常６以上の色素が用いられる。
ＣＩＥ−１９３１表色系（Commision Internationale del'Eclariage-1931 表色系）による色調表示における明るさの刺激度は、通常１０以上、好ましくは２５以上であり、主波長は通常 500〜600nm 、好ましくは 550〜600nm であり、刺激純度は通常５０％以上、好ましくは７０％以上である。
青色アゾ系色素としては、マンセル表色系における表示法においてマンセルヒューがＢＧ、ＢまたはＰＢで表される色素、さらには 2.5ＢＧ〜 7.5ＰＢで表される色素が挙げられる。また、マンセルバリューが通常４以上、好ましくは５以上の色素が用いられ、マンセルクロマは通常６以上の色素が用いられる。
アゾ系色素は、一種単独で使用しても、二種以上を混合して使用してもよく、その使用量は、基材に塗布して使用する場合またはシート状物等の薄片に使用する場合、一般に本発明の害虫防除材１ｍ² 当たり 0.01 〜 100ｇ程度、好ましくは 0.1〜 20 ｇ程度である。 Among the azo dyes used in the present invention, azo pigments are preferably used, and disazo pigments, insoluble azo pigments, and condensed azo pigments are particularly preferable.
Also, yellow or blue azo dyes are generally used from the viewpoint of the color tone that attracts pests.
Examples of the yellow azo dye include dyes in which Munsell Hue is represented by YR, Y, or GY in the display method in the Munsell color system, and further, dyes represented by 2.5YR to 7.5GY. A Munsell value is usually 4 or more, preferably 5 or more, and Munsell chroma is usually 6 or more.
The degree of brightness stimulation in the color tone display by the CIE-1931 color system (Commision Internationale del'Eclariage-1931 color system) is usually 10 or more, preferably 25 or more, and the dominant wavelength is usually 500 to 600 nm, preferably The stimulation purity is usually 50% or more, preferably 70% or more.
Examples of blue azo dyes include dyes in which Munsell Hue is represented by BG, B, or PB in the display method in the Munsell color system, and further, dyes represented by 2.5 BG to 7.5 PB. A Munsell value is usually 4 or more, preferably 5 or more, and Munsell chroma is usually 6 or more.
The azo dyes may be used alone or in combination of two or more, and the amount used is applied to a substrate or used for a flake such as a sheet-like material. In general, the amount is about 0.01 to 100 g, preferably about 0.1 to 20 g, per 1 m ² of the pest control material of the present invention.

本発明において用いられる防虫活性成分は、誘引した害虫を薬殺する殺虫活性成分、例えばピレスロイド化合物、有機リン化合物、カーバメート化合物等であってもよいし、誘引した害虫を不妊化して次世代の害虫密度を減少させるための昆虫成長制御活性成分、例えば幼若ホルモン活性化合物、キチン合成阻害化合物等であってもよい。   The insecticidal active ingredient used in the present invention may be an insecticidal active ingredient that kills the attracted pest, such as a pyrethroid compound, an organophosphorus compound, a carbamate compound, etc., and the next-generation pest density by sterilizing the attracted pest It may be an insect growth control active ingredient for reducing the amount of, for example, a juvenile hormone active compound, a chitin synthesis inhibiting compound and the like.

以下に、防虫活性成分の具体例のいくつかを示す。
（１） α−シアノ−３−フェノキシベンジル ２−（４−クロロフェニル）−３−メチルブチラート
（２） （Ｓ）−α−シアノ−３−フェノキシベンジル （Ｓ）−２−（４−クロロフェニル）−３−メチルブチラート
（３） α−シアノ−３−フェノキシベンジル ２，２，３，３−テトラメチルシクロプロパンカルボキシラート
（４） α−シアノ−３−フェノキシベンジル ３−（２，２−ジクロロビニル）−２，２−ジメチルシクロプロパンカルボキシラート
（５） α−シアノ−３−フェノキシベンジル クリサンテマート
（６） ３−フェノキシベンジル クリサンテマート
（７） ３−フェノキシベンジル （１Ｒ）−クリサンテマート
（８） α−シアノ−３−フェノキシベンジル ２−（４−tert−ブチルフェニル）−３−メチルブチラート
（９） α−シアノ−３−フェノキシベンジル ２−（３，４−メチレンジオキシフェニル）−３−メチルブチラート
（１０） （Ｓ）−α−シアノ−３−フェノキシベンジル （１Ｒ，３Ｒ）−３−（２，２−ジブロモビニル）−２，２−ジメチルシクロプロパンカルボキシラート Below, some specific examples of the insect repellent active ingredient are shown.
(1) α-cyano-3-phenoxybenzyl 2- (4-chlorophenyl) -3-methylbutyrate (2) (S) -α-cyano-3-phenoxybenzyl (S) -2- (4-chlorophenyl) -3-methylbutyrate (3) α-cyano-3-phenoxybenzyl 2,2,3,3-tetramethylcyclopropanecarboxylate (4) α-cyano-3-phenoxybenzyl 3- (2,2-dichloro) Vinyl) -2,2-dimethylcyclopropanecarboxylate (5) α-cyano-3-phenoxybenzyl chrysanthemate (6) 3-phenoxybenzyl chrysanthemate (7) 3-phenoxybenzyl (1R) -chrysanthemate (8) α-Cyano-3-phenoxybenzyl 2- (4-tert-butylphenyl) -3-methylbutyrate (9 α-cyano-3-phenoxybenzyl 2- (3,4-methylenedioxyphenyl) -3-methylbutyrate (10) (S) -α-cyano-3-phenoxybenzyl (1R, 3R) -3- ( 2,2-Dibromovinyl) -2,2-dimethylcyclopropanecarboxylate

（１１） α−シアノ−３−フェノキシベンジル ２−クロロ−４−（トリフルオロメチル）アニリノ−３−メチルブチラート
（１２） α−シアノ−４−フルオロ−３−フェノキシベンジル ３−（２，２−ジクロロビニル）−２，２−ジメチルシクロプロパンカルボキシラート
（１３） シアノ−（５−フェノキシ−２−ピリジル）メチル ３−（２，２−ジクロロビニル）−２，２−ジメチルシクロプロパンカルボキシラート
（１４） α−シアノ−３−フェノキシベンジル ２，２−ジメチル−３−（１，２，２，２−テトラブロモエチル）シクロプロパンカルボキシラート
（１５） α−シアノ−３−フェノキシベンジル １−（４−エトキシフェニル）−２，２−ジクロロシクロプロパンカルボキシラート
（１６） α−シアノ−３−フェノキシベンジル ３−〔２−クロロ−２−（トリフルオロメチル）ビニル〕−２，２−ジメチルシクロプロパンカルボキシラート
（１７） α−シアノ−３−フェノキシベンジル ２−（４−ジフルオロメトキシフェニル）−３−メチルブチラート
（１８） ３−フェノキシベンジル ３−（２，２−ジクロロビニル）−２，２−ジメチルシクロプロパンカルボキシラート
（１９） ２−メチル−３−フェニルベンジル （１Ｒ，トランス）−３−〔２−クロロ−２−（トリフルオロメチル）ビニル〕−２，２−ジメチルシクロプロパンカルボキシラート
（２０） ２，３，５，６−テトラフルオロ−４−メチルベンジル （１Ｒ，トランス）−３−〔２−クロロ−２−（トリフルオロメチル）ビニル〕−２，２−ジメチルシクロプロパンカルボキシラート (11) α-cyano-3-phenoxybenzyl 2-chloro-4- (trifluoromethyl) anilino-3-methylbutyrate (12) α-cyano-4-fluoro-3-phenoxybenzyl 3- (2,2 -Dichlorovinyl) -2,2-dimethylcyclopropanecarboxylate (13) cyano- (5-phenoxy-2-pyridyl) methyl 3- (2,2-dichlorovinyl) -2,2-dimethylcyclopropanecarboxylate ( 14) α-Cyano-3-phenoxybenzyl 2,2-dimethyl-3- (1,2,2,2-tetrabromoethyl) cyclopropanecarboxylate (15) α-cyano-3-phenoxybenzyl 1- (4 -Ethoxyphenyl) -2,2-dichlorocyclopropanecarboxylate (16) α-cyano-3-phenoxybe Zyl 3- [2-chloro-2- (trifluoromethyl) vinyl] -2,2-dimethylcyclopropanecarboxylate (17) α-cyano-3-phenoxybenzyl 2- (4-difluoromethoxyphenyl) -3- Methyl butyrate (18) 3-phenoxybenzyl 3- (2,2-dichlorovinyl) -2,2-dimethylcyclopropanecarboxylate (19) 2-methyl-3-phenylbenzyl (1R, trans) -3- [ 2-Chloro-2- (trifluoromethyl) vinyl] -2,2-dimethylcyclopropanecarboxylate (20) 2,3,5,6-tetrafluoro-4-methylbenzyl (1R, trans) -3- [ 2-Chloro-2- (trifluoromethyl) vinyl] -2,2-dimethylcyclopropanecarboxylate

（２１） ３，４，５，６−テトラヒドロフタルイミドメチル クリサンテマート
（２２） ３，４，５，６−テトラヒドロフタルイミドメチル （１Ｒ）−クリサンテマート
（２３） ３−アリル−２−メチル−４−オキソシクロペント−２−エンイルクリサンテマート
（２４） ３−アリル−２−メチル−４−オキソシクロペント−２−エンイル（１Ｒ）−クリサンテマート
（２５） ２−メチル−４−オキソ−３−（２−プロピニル）シクロペント−２−エンイル クリサンテマート
（２６） （Ｓ）−２−メチル−４−オキソ−３−（２−プロピニル）シクロペント−２−エンイル （１Ｒ）−クリサンテマート
（２７） １−エチニル−２−メチル−２−ペンテニル クリサンテマート
（２８） １−エチニル−２−メチル−２−ペンテニル （１Ｒ）−クリサンテマート
（２９） ５−ベンジル−３−フリルメチル クリサンテマート
（３０） ５−ベンジル−３−フリルメチル （１Ｒ）−クリサンテマート (21) 3,4,5,6-tetrahydrophthalimidomethyl chrysanthemate (22) 3,4,5,6-tetrahydrophthalimidomethyl (1R) -chrysanthemate (23) 3-allyl-2-methyl-4 -Oxocyclopent-2-enylchrysanthemate (24) 3-allyl-2-methyl-4-oxocyclopent-2-eneyl (1R) -chrysanthemate (25) 2-methyl-4-oxo- 3- (2-propynyl) cyclopent-2-enyl chrysanthemate (26) (S) -2-methyl-4-oxo-3- (2-propynyl) cyclopent-2-enyl (1R) -chrysanthemate ( 27) 1-ethynyl-2-methyl-2-pentenyl chrysanthemate (28) 1-ethynyl-2-methyl-2-pentenyl (1R - chestnut Sante Mart (29) 5-benzyl-3-furylmethyl chestnut Santé Mart (30) 5-benzyl-3-furylmethyl (1R) - Chestnut Sante Mart

（３１） Ｏ，Ｏ−ジメチル Ｓ−〔１，２−ジ（エトキシカルボニル）エチル〕 ホスホロジチオエート
（３２） Ｏ，Ｏ−ジメチル Ｏ−（４−シアノフェニル） ホスホロチオエート
（３３） Ｏ，Ｏ−ジメチル Ｓ−（α−エトキシカルボニルベンジル） ホスホロジチオエート
（３４） Ｏ，Ｏ−ジメチル Ｏ−（２−イソプロピル−４−メチル−６−ピリミジニル） ホスホロチオエート
（３５） Ｏ，Ｏ−ジメチル Ｏ−〔３−メチル−４−（メチルチオ）フェニル〕 ホスホロチオエート
（３６） Ｏ−（４−ブロモ−２，５−ジクロロフェニル） Ｏ，Ｏ−ジエチル ホスホロチオエート
（３７） ２−メトキシ−４Ｈ−１，３，２−ベンゾオキサホスホリン−２−スルフィド
（３８） Ｏ，Ｏ−ジメチル Ｏ−（２，４，５−トリクロロフェニル） ホスホロチオエート
（３９） Ｏ，Ｏ−ジメチル Ｏ−（３，５，６−トリクロロ−２−ピリジル） ホスホロチオエート
（４０） Ｏ，Ｏ−ジエチル Ｏ−（３，５，６−トリクロロ−２−ピリジル） ホスホロチオエート (31) O, O-dimethyl S- [1,2-di (ethoxycarbonyl) ethyl] phosphorodithioate (32) O, O-dimethyl O- (4-cyanophenyl) phosphorothioate (33) O, O- Dimethyl S- (α-ethoxycarbonylbenzyl) phosphorodithioate (34) O, O-dimethyl O- (2-isopropyl-4-methyl-6-pyrimidinyl) phosphorothioate (35) O, O-dimethyl O- [3 -Methyl-4- (methylthio) phenyl] phosphorothioate (36) O- (4-bromo-2,5-dichlorophenyl) O, O-diethyl phosphorothioate (37) 2-methoxy-4H-1,3,2-benzoxa Phosphorin-2-sulfide (38) O, O-dimethyl O- (2,4,5-trichlorophenyl) e Horochioeto (39) O, O-dimethyl O-(3,5,6-trichloro-2-pyridyl) phosphorothioate (40) O, O-diethyl O-(3,5,6-trichloro-2-pyridyl) phosphorothioate

（４１） Ｏ，Ｏ−ジメチル Ｏ−（４−ブロモ−２，５−ジクロロフェニル） ホスホロチオエート
（４２） ジメチル ２，２−ジクロロビニルホスフェート
（４３） Ｏ，Ｓ−ジメチル Ｎ−アセチルホスホロアミドチオエート
（４４） Ｏ−（２，４−ジクロロフェニル） Ｏ−エチル Ｓ−プロピル ホスホロジチオエート
（４５） Ｏ，Ｏ−ジメチル Ｓ−（５−メトキシ−１，３，４−チアジアゾリン−２−オン−３−イルメチル） ホスホロチオエート
（４６） ジメチル ２，２，２−トリクロロ−１−ヒドロキシエチルホスホネート
（４７） Ｏ，Ｏ−ジメチル Ｓ−（Ｎ−メチルカルバモイルメチル） ホスホロジチオエート
（４８） Ｏ−エチル Ｏ−（５−メチル−２−ニトロフェニル） sec−ブチルホスホロアミドチオエート
（４９） Ｏ，Ｏ−ジメチル Ｏ−〔３−メチル−４−（メチルスルフィニル）フェニル〕 ホスホロチオエート
（５０） Ｏ，Ｏ−ジメチル Ｏ−（３−メチル−４−ニトロフェニル） ホスホロチオエート (41) O, O-dimethyl O- (4-bromo-2,5-dichlorophenyl) phosphorothioate (42) dimethyl 2,2-dichlorovinyl phosphate (43) O, S-dimethyl N-acetyl phosphoramidothioate ( 44) O- (2,4-Dichlorophenyl) O-ethyl S-propyl phosphorodithioate (45) O, O-dimethyl S- (5-methoxy-1,3,4-thiadiazolin-2-one-3- Ylmethyl) phosphorothioate (46) dimethyl 2,2,2-trichloro-1-hydroxyethylphosphonate (47) O, O-dimethyl S- (N-methylcarbamoylmethyl) phosphorodithioate (48) O-ethyl O- ( 5-methyl-2-nitrophenyl) sec-butyl phosphoramidothioate (49) O, O Dimethyl O- [3-methyl-4- (methylsulfinyl) phenyl] phosphorothioate (50) O, O- dimethyl O- (3-methyl-4-nitrophenyl) phosphorothioate

（５１） Ｏ，Ｏ−ジメチル Ｏ−（２−ジエチルアミノ−６−メチルピリミジン−４−イル） ホスホロチオエート
（５２） Ｏ，Ｏ−ジエチル Ｏ−（５−フェニル−３−イソキサゾール） ホスホロチオエート
（５３） Ｏ，Ｏ−ジエチル Ｏ−（３−オキソ−２−フェニル−２Ｈ−ピリダジン−６−イル） ホスホロチオエート
（５４） Ｏ，Ｏ−ジメチル Ｓ−（２−エチルチオ）エチル ホスホロジチオエート
（５５） Ｏ，Ｏ−ジメチル Ｓ−（２−イソプロピルチオ）エチル ホスホロジチオエート
（５６） Ｏ，Ｏ−ジメチル Ｓ−フタルイミドメチル ホスホロジチオエート
（５７） ２−クロロ−１−（２，４，５−トリクロロフェニル）ビニル ジメチルホスフェート
（５８） ２−クロロ−１−（２，４−ジクロロフェニル）ビニル ジメチルホスフェート
（５９） Ｏ，Ｏ−ジプロピル Ｏ−〔４−（メチルチオ）フェニル〕 ホスホロチオエート
（６０） Ｏ−エチル Ｏ−（４−ニトロフェニル） ベンゼンホスホノチオエート (51) O, O-dimethyl O- (2-diethylamino-6-methylpyrimidin-4-yl) phosphorothioate (52) O, O-diethyl O- (5-phenyl-3-isoxazole) phosphorothioate (53) O, O-diethyl O- (3-oxo-2-phenyl-2H-pyridazin-6-yl) phosphorothioate (54) O, O-dimethyl S- (2-ethylthio) ethyl phosphorodithioate (55) O, O- Dimethyl S- (2-isopropylthio) ethyl phosphorodithioate (56) O, O-dimethyl S-phthalimidomethyl phosphorodithioate
(57) 2-chloro-1- (2,4,5-trichlorophenyl) vinyl dimethyl phosphate (58) 2-chloro-1- (2,4-dichlorophenyl) vinyl dimethyl phosphate (59) O, O-dipropyl O -[4- (Methylthio) phenyl] phosphorothioate (60) O-ethyl O- (4-nitrophenyl) benzenephosphonothioate

（６１） Ｏ−エチル Ｏ−（２，４−ジクロロフェニル） ベンゼンホスホノチオエート
（６２） １−ナフチル Ｎ−メチルカーバメート
（６３） ２−イソプロポキシフェニル Ｎ−メチルカーバメート
（６４） ３−メチルフェニル Ｎ−メチルカーバメート
（６５） ２−ｓｅｃ−ブチルフェニル Ｎ−メチルカーバメート
（６６） ３，４−ジメチルフェニル Ｎ−メチルカーバメート
（６７） ３，５−ジメチルフェニル Ｎ−メチルカーバメート
（６８） ２−ジメチルアミノ−５，６−ジメチルピリジン−４−イル Ｎ，Ｎ−ジメチルカーバメート
（６９） ２−（エチルチオメチル）フェニル Ｎ−メチルカーバメート
（７０） Ｓ−メチル Ｎ−〔（メチルカルバモイル）オキシ〕チオアセトイミデート (61) O-ethyl O- (2,4-dichlorophenyl) benzenephosphonothioate (62) 1-naphthyl N-methyl carbamate (63) 2-isopropoxyphenyl N-methyl carbamate (64) 3-methylphenyl N- Methyl carbamate (65) 2-sec-butylphenyl N-methyl carbamate (66) 3,4-dimethylphenyl N-methyl carbamate (67) 3,5-dimethylphenyl N-methyl carbamate (68) 2-dimethylamino-5 , 6-Dimethylpyridin-4-yl N, N-dimethylcarbamate (69) 2- (ethylthiomethyl) phenyl N-methylcarbamate (70) S-methyl N-[(methylcarbamoyl) oxy] thioacetimidate

（７１） ２−イソプロピルフェニル Ｎ−メチルカーバメート
（７２） ２，３−ジヒドロ−２，２−ジメチル−７−ベンゾフラニル Ｎ−ジブチルアミノチオ−Ｎ−メチルカーバメート
（７３） エチル ２−（４−フェノキシフェノキシ）エチルカーバメート
（７４） Ｓ−４−フェノキシブチル ジメチルチオカーバメート
（７５） エチル Ｎ−〔２，３−ジヒドロ−２，２−ジメチルベンゾフラン−７−イルオキシカルボニル（メチル）アミノチオ〕−Ｎ−イソプロピル−β−アラニナート
（７６） ４−フェノキシフェニル ２−（２−ピリジルオキシ）プロピル エーテル
（７７） イソプロピル １１−メトキシ−３，７，１１−トリメチル−２，４−ドデカジエノエート
（７８） ４−クロロ−２−（２−クロロ−２−メチルプロピル）−５−（６−ヨード−３−ピリジルメトキシ）ピリダジン−３（２Ｈ）−オン
（７９） １−（４−クロロフェニル）−３−（２，６−ジフルオロベンゾイル）ウレア
（８０） １−〔３，５−ジクロロ−２，４−ジフルオロフェニル）−３−（２，６−ジフルオロベンゾイル）ウレア (71) 2-isopropylphenyl N-methylcarbamate (72) 2,3-dihydro-2,2-dimethyl-7-benzofuranyl N-dibutylaminothio-N-methylcarbamate (73) ethyl 2- (4-phenoxyphenoxy ) Ethyl carbamate (74) S-4-phenoxybutyl dimethylthiocarbamate (75) Ethyl N- [2,3-dihydro-2,2-dimethylbenzofuran-7-yloxycarbonyl (methyl) aminothio] -N-isopropyl- β-alaninate (76) 4-phenoxyphenyl 2- (2-pyridyloxy) propyl ether (77) isopropyl 11-methoxy-3,7,11-trimethyl-2,4-dodecadienoate (78) 4-chloro -2- (2-chloro-2-methylpropyl) -5 6-iodo-3-pyridylmethoxy) pyridazin-3 (2H) -one (79) 1- (4-chlorophenyl) -3- (2,6-difluorobenzoyl) urea (80) 1- [3,5-dichloro -2,4-difluorophenyl) -3- (2,6-difluorobenzoyl) urea

（８１） １−〔３，５−ジクロロ−４−（３−クロロ−５−トリフルオロメチルピリジン−２−イルオキシ）フェニル〕−３−（２，６−ジフルオロベンゾイル）ウレア
（８２） １−（４−トリフルオロメトキシフェニル）−３−（２−クロロベンゾイル）ウレア
（８３） １−〔４−（２−クロロ−４−トリフルオロメチルフェノキシ）−２−フルオロフェニル〕−３−（２，６−ジフルオロベンゾイル）ウレア
（８４） １−〔α−（４−クロロ−α−シクロプロピルベンジリデンアミノオキシ）−ｐ−トリル〕−３−（２，６−ジフルオロベンゾイル）ウレア
（８５） １−〔３，５−ジクロロ−４−（１，１，２，２−テトラフルオロエトキシ）フェニル〕−３−（２，６−ジフルオロベンゾイル）ウレア
（８６） １−（２−フルオロ−４−トリフルオロメチルフェニル）−３−（２，６−ジフルオロベンゾイル）ウレア
（８７） ２−tert−ブチルイミノ−３−イソプロピル−５−フェニル−３，４，５，６−テトラヒドロ−２Ｈ−１，３，５−チアジアジン−４−オン
（８８） ３−メチル−１，５−ビス（２，４−キシリル）−１，３，５−トリアザペンタ−１，４−ジエン
（８９） １，１−ビス（クロロフェニル）−２，２，２−トリクロロエタノール
（９０） ４−クロロフェニル ４−クロロベンゼンスルホナート (81) 1- [3,5-Dichloro-4- (3-chloro-5-trifluoromethylpyridin-2-yloxy) phenyl] -3- (2,6-difluorobenzoyl) urea (82) 1- ( 4-trifluoromethoxyphenyl) -3- (2-chlorobenzoyl) urea (83) 1- [4- (2-chloro-4-trifluoromethylphenoxy) -2-fluorophenyl] -3- (2,6 -Difluorobenzoyl) urea (84) 1- [α- (4-chloro-α-cyclopropylbenzylideneaminooxy) -p-tolyl] -3- (2,6-difluorobenzoyl) urea (85) 1- [3 , 5-Dichloro-4- (1,1,2,2-tetrafluoroethoxy) phenyl] -3- (2,6-difluorobenzoyl) urea (86) 1- (2-fluoro- 4-trifluoromethylphenyl) -3- (2,6-difluorobenzoyl) urea (87) 2-tert-butylimino-3-isopropyl-5-phenyl-3,4,5,6-tetrahydro-2H-1, 3,5-thiadiazin-4-one (88) 3-methyl-1,5-bis (2,4-xylyl) -1,3,5-triazapenta-1,4-diene (89) 1,1-bis (Chlorophenyl) -2,2,2-trichloroethanol (90) 4-chlorophenyl 4-chlorobenzenesulfonate

（９１） ２，４，５，４’−テトラクロロジフェニルスルホン
（９２） ２−（４−tert−ブチルフェノキシ）シクロヘキシル ２−プロピル スルフィド
（９３） １，３−ビス（カルバモイルチオ）−２−（Ｎ，Ｎ−ジメチルアミノ）プロパン塩酸塩
（９４） １−〔（６−クロロ−３−ピリジニル）メチル〕−Ｎ−ニトロ−２−イミダゾリジンイミン
本発明において用いられる防虫活性成分は、一種単独で使用しても、二種以上を混合して使用してもよく、その混合割合は任意に選択できる。防虫活性成分の使用量は、該活性成分の種類、防除対象害虫の種類等により異なるが、通常、本発明の害虫防除材１ｍ² 当たり 0.01 〜 100ｇ程度、好ましくは0.05〜 20 ｇ程度である。 (91) 2,4,5,4′-tetrachlorodiphenylsulfone (92) 2- (4-tert-butylphenoxy) cyclohexyl 2-propyl sulfide (93) 1,3-bis (carbamoylthio) -2- ( N, N-dimethylamino) propane hydrochloride (94) 1-[(6-chloro-3-pyridinyl) methyl] -N-nitro-2-imidazolidineimine The insecticidal active ingredient used in the present invention is a single type. Even if it uses, 2 or more types may be mixed and used, The mixing ratio can be selected arbitrarily. The amount of the insecticidal active ingredient used varies depending on the type of the active ingredient, the type of the insect pest to be controlled, etc., but is usually about 0.01 to 100 g, preferably about 0.05 to 20 g per 1 m ² of the insect controlling material of the present invention.

本発明において、アゾ系色素により着色されて用いられる基材としては、例えば、上質紙、中級紙、下級紙、中性紙、グラビア紙、上更紙、更紙、包装紙、コーティド紙、ケント紙、クラフト紙、再生紙、新聞紙、パラフィン紙、ハトロン紙、合成紙、加工紙、グラシン紙、耐油紙、クレイアート紙、マニラ紙、段ボール紙、トレーシング紙、エンボス紙、濾紙、和紙、板紙、インディア紙、印画紙、パルプシート等の紙製基材、ナイロン繊維（例えばナイロン−６、ナイロン−６６）、ビニロン繊維、アセテート繊維（例えばアセテート、トリアセテート）、ポリエステル繊維（例えばポリエチレンテレフタレート、ポリヒドロキシブチレート、ポリ乳酸）、アクリル繊維（例えばポリメタクリル酸メチル、ポリアクリロニトリル）、ポリオレフィン繊維（例えば低密度ポリエチレン、高密度ポリエチレン、塩素化ポリエチレン、ポリプロピレン）、フェノール繊維（例えばベークライト）、ポリウレタン繊維、ポリウレア繊維、ビニル繊維（例えばポリスチレン、ポリ酢酸ビニル）、アラミド繊維（例えばデュポン社ケブラー、エンカ社トワロン、帝人社テクノーラ）、キュプラ繊維（例えば旭化成社ベンベルグ）、ノボロイド繊維、ビニリデン繊維（例えばポリ塩化ビニリデン）、ポリスルホン繊維、ポリカーボネート繊維、ポリアセタール繊維、ポリクラール繊維、ポリノジック繊維、木綿繊維、羊毛繊維、セルロース繊維、絹繊維、麻繊維、レーヨン繊維等の繊維の織布、不織布、混紡などの繊維基材が挙げられる。
また、基材として樹脂製フィルムを用いることもでき、樹脂製フィルムの材質としては、例えば、低密度ポリエチレン、高密度ポリエチレン、塩素化ポリエチレン、ポリプロピレン等のポリオレフィン樹脂、ポリクロロエチレン、ポリ塩化プロピレン等のハロゲン化ポリオレフィン樹脂、ポリアクリロニトリル、ポリメタクリル酸メチル、ビニロン、ポリアクリル酸、ポリヒドロキシエチルメタクリレート等のアクリル樹脂、ポリエチレンテレフタレート等のポリエステル樹脂、ナイロン−６、ナイロン−１１、ナイロン−６６等のナイロン樹脂、ベークライト等のフェノール樹脂、ポリウレタン、ポリウレア等のウレタン樹脂やウレア樹脂、ポリスチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリ酢酸ビニル、アクリロニトリル−ポリスチレン−ブタジエン共重合体、ポリ塩化ビニル−酢酸ビニル共重合体、塩素化塩化ビニルポリマー、ポリビニルアルコール、ポリビニルアルコール部分鹸化物、ポリビニルエーテル、ポリビニルピロリドン等のビニル樹脂、アセテート、トリアセテート等のアセテート樹脂、デュポン社ケブラー、エンカ社トワロン等のアラミド樹脂、ノボロイド樹脂、ポリスルホン樹脂、ポリカーボネート等のカーボネート樹脂、カルボキシメチルセルロース、カルボキシメチルセルロースナトリウム塩、ヒドロキシプロピルメチルセルロース、ニトロセルロース、酢酸セルロース、メチルセルロース、エチルセルロース、ヒドロキシプロピルセルロース等のセルロース系樹脂、リグニン、リグニンスルホン酸ナトリウム、リグニンスルホン酸アンモニウム等のリグニン系樹脂、ケトン−ホルマリン樹脂、フェノキシ樹脂、ポリブタジエン、ポリイソブチレン、ポリイソプレン等の合成ゴム樹脂、シリコ−ン樹脂、ポリフッ化ビニリデン、ポリトリフルオロエチレン等のフッ素樹脂、ポリイミド樹脂、ポリエチレンオキシド、ポリフェニレンオキシド、ポリエチレングリコール、ポリプロピレングリコール、ポリ（オキシエチレン−オキシプロピレン）コポリマー等の酸化オレフィン樹脂、エポキシ樹脂、メラミン樹脂、ポリアミノ酸、無水マレイン酸−エチレン共重合体、無水マレイン酸−スチレン共重合体等のマレイン酸樹脂などが挙げられる。中でも、ポリプロピレン、ポリアクリロニトリル、ポリメタクリル酸メチル、ポリエチレンテレフタレート等のポリエステル樹脂、ナイロン−６、ナイロン−１１、ナイロン−６６等のナイロン樹脂、ポリアミド樹脂、ポリ塩化ビニル、ポリ塩化ビニリデン、塩化ビニル−プロピレン共重合体などの材質が好ましい。 In the present invention, examples of the base material that is colored with an azo dye include high-quality paper, intermediate paper, lower paper, neutral paper, gravure paper, upper renewal paper, renewal paper, wrapping paper, coated paper, and Kent paper. Craft paper, recycled paper, newspaper, paraffin paper, hatron paper, synthetic paper, processed paper, glassine paper, oil-resistant paper, clay art paper, Manila paper, corrugated paper, tracing paper, embossed paper, filter paper, Japanese paper, paperboard, Paper substrates such as India paper, photographic paper, pulp sheet, nylon fibers (for example, nylon-6, nylon-66), vinylon fibers, acetate fibers (for example, acetate, triacetate), polyester fibers (for example, polyethylene terephthalate, polyhydroxybutyrate) Rate, polylactic acid), acrylic fibers (eg polymethyl methacrylate, polyacrylonitrile), poly Refin fibers (eg low density polyethylene, high density polyethylene, chlorinated polyethylene, polypropylene), phenol fibers (eg bakelite), polyurethane fibers, polyurea fibers, vinyl fibers (eg polystyrene, polyvinyl acetate), aramid fibers (eg DuPont Kevlar) , Enka Co., Ltd. Twaron, Teijin Technole), Cupra fiber (eg Asahi Kasei Bemberg), Novoloid fiber, Vinylidene fiber (eg Polyvinylidene chloride), Polysulfone fiber, Polycarbonate fiber, Polyacetal fiber, Polyclar fiber, Polynosic fiber, Cotton fiber, Wool Examples thereof include fiber base materials such as fibers, cellulose fibers, silk fibers, hemp fibers, rayon fibers, and the like, woven fabrics, nonwoven fabrics, and blends.
In addition, a resin film can be used as the substrate. Examples of the resin film material include polyolefin resins such as low density polyethylene, high density polyethylene, chlorinated polyethylene, and polypropylene, polychlorethylene, polypropylene chloride, and the like. Halogenated polyolefin resin, polyacrylonitrile, polymethyl methacrylate, vinylon, acrylic resin such as polyacrylic acid, polyhydroxyethyl methacrylate, polyester resin such as polyethylene terephthalate, nylon such as nylon-6, nylon-11, nylon-66, etc. Resin, phenol resin such as bakelite, urethane resin such as polyurethane and polyurea, urea resin, polystyrene, polyvinyl chloride, polyvinylidene chloride, polyvinyl acetate, acrylonitrile-poly Tylene-butadiene copolymer, polyvinyl chloride-vinyl acetate copolymer, chlorinated vinyl chloride polymer, polyvinyl alcohol, polyvinyl alcohol partially saponified product, polyvinyl ether, polyvinyl pyrrolidone and other vinyl resins, acetate, triacetate and other acetate resins, Aramid resins such as DuPont Kevlar and Enka Twaron, Novoloid resins, Polysulfone resins, Carbonates such as polycarbonate, Carboxymethylcellulose, Sodium carboxymethylcellulose, Hydroxypropylmethylcellulose, Nitrocellulose, Cellulose acetate, Methylcellulose, Ethylcellulose, Hydroxypropylcellulose, etc. Cellulosic resin, lignin, sodium lignin sulfonate, ammonium lignin sulfonate Lignin resins such as ketone-formalin resin, phenoxy resin, synthetic rubber resin such as polybutadiene, polyisobutylene, polyisoprene, fluorine resin such as silicone resin, polyvinylidene fluoride, polytrifluoroethylene, polyimide resin, polyethylene oxide , Olefin oxide resin such as polyphenylene oxide, polyethylene glycol, polypropylene glycol, poly (oxyethylene-oxypropylene) copolymer, epoxy resin, melamine resin, polyamino acid, maleic anhydride-ethylene copolymer, maleic anhydride-styrene copolymer Examples thereof include maleic acid resins such as coalescence. Among them, polyester resins such as polypropylene, polyacrylonitrile, polymethyl methacrylate, polyethylene terephthalate, nylon resins such as nylon-6, nylon-11, nylon-66, polyamide resin, polyvinyl chloride, polyvinylidene chloride, vinyl-propylene chloride A material such as a copolymer is preferred.

これらの基材の大きさや形は特に制限されず、例えば、厚さ 0.0005 〜10mm、好ましくは 0.001〜２mmの基材を用い、害虫から保護したい植物の周囲にテープ状物として張り巡らしたり、暖簾状物、簾状物、カーテン状物、蚊帳状物、ついたて状物またはネット状物として設置したりする。   The size and shape of these base materials are not particularly limited. For example, a base material having a thickness of 0.0005 to 10 mm, preferably 0.001 to 2 mm, is used as a tape around a plant to be protected from pests. It can be installed as a shape, bowl, curtain, mosquito net, vertical or net.

防虫活性成分を基材に保持させるに際しては、該活性成分に必要によりバインダー、可塑剤、溶剤、界面活性剤、安定化剤、香料、撥水剤、フィラー、粘着剤等を添加して保持させる。
用いられるバインダーとしては、例えば、ベントナイト、モンモリロナイト、水ガラス、コロイダルシリカ等の無機バインダー、澱粉、デキストリン、カゼイン、ゼラチン、にかわ、寒天、コラーゲン、トラガントガム、ペクチン、アラビアガム、コーンスターチ、天然ゴム、パルプ液等の天然有機バインダー、カルボキシメチルセルロース、アセチルセルロース、カルボキシメチルセルロースナトリウム、ベンジルセルロース、酪酸セルロース、ヒドロキシプロピルメチルセルロース、ニトロセルロース、酢酸セルロース、メチルセルロース、エチルセルロース、ヒドロキシプロピルセルロースなどのセルロース系バインダー、リグニン、リグニンスルホン酸ナトリウム、リグニンスルホン酸アンモニウムなどのリグニン系バインダー等の半合成バインダー、高密度ポリエチレン、低密度ポリエチレン、ポリプロピレンなどのポリオレフィン、ポリクロロエチレン、ポリ塩化プロピレンなどのハロゲン化ポリオレフィン、ポリアクリロニトリル、ポリメタクリル酸メチル、ポリアクリル酸、ポリヒドロキシエチルメタクリレートなどのアクリル系高分子、ポリスチレン、アクリロニトリル−ポリスチレン−ブタジエン共重合体、ポリ塩化ビニル、ポリ酢酸ビニル、塩化ビニル−酢酸ビニル共重合体、ポリビニルアルコール、ポリビニルアルコール部分鹸化物、ポリビニルエーテル、ポリビニルピロリドンなどのビニル系高分子、ポリ塩化ビニリデン、ケトン−ホルマリン樹脂、フェノキシ樹脂、ポリブタジエン、ポリイソブチレン、ポリイソプレンなどの合成ゴム、シリコーン樹脂、ポリフッ化ビニリデン、ポリトリフルオロエチレンなどのフッ素樹脂、ポリアセタールなどのアセタール樹脂、ナイロン−６、ナイロン−６６、ポリエチレンテレフタレートなどのポリエステル樹脂、ポリアミド樹脂、ポリイミド樹脂、ポリエチレンオキシド、ポリフェニレンオキシド、ポリエチレングリコール、ポリプロピレングリコール、ポリオキシエチレンポリオキシプロピレン共重合体などの酸化オレフィン、ポリカーボネートなどのカーボネート樹脂、ポリサルホン樹脂、ポリウレタン、ポリウレタン尿素などのウレタン樹脂、エポキシ樹脂、フェノール樹脂、メラミン樹脂、尿素樹脂、ポリアミノ酸、無水マレイン酸−エチレン共重合体、無水マレイン酸−スチレン共重合体などのマレイン酸樹脂等の合成樹脂系バインダー、キャンデリラワックス、カルナバロウワックス、ライスワックス、木ロウ、ホホバ油、蜜ロウ、ラノリン、鯨ロウ、牛脂、オゾケライト、セレシンなどの天然ワックス、パラフィンワックス、マイクロクリスタリンワックスなどの石油ワックス、モンタンワックス、ポリエチレンワックス、フィッシャートロプシュワックス、サゾールワックス、硬化ひまし油、１２−ヒドロキシステアリン酸、ステアリン酸、ステアリルアルコール、ラウロン、ステアロン、ミリスチン酸イソプロピル、グリセリン脂肪酸エステル、グリコール脂肪酸エステル、ソルビタン脂肪酸エステルなどの合成ワックス等のワックスなどおよびその混合物が挙げられる。 When holding the insect repellent active ingredient on the base material, a binder, a plasticizer, a solvent, a surfactant, a stabilizer, a fragrance, a water repellent, a filler, an adhesive, etc. are added to the active ingredient as necessary. .
Examples of the binder used include inorganic binders such as bentonite, montmorillonite, water glass, colloidal silica, starch, dextrin, casein, gelatin, glue, agar, collagen, tragacanth gum, pectin, gum arabic, corn starch, natural rubber, pulp liquid Natural organic binders such as carboxymethylcellulose, acetylcellulose, sodium carboxymethylcellulose, benzylcellulose, cellulose butyrate, hydroxypropylmethylcellulose, nitrocellulose, cellulose acetate, methylcellulose, ethylcellulose, hydroxypropylcellulose and other cellulose binders, lignin, ligninsulfonic acid Lignin binders such as sodium and ammonium lignin sulfonate Synthetic binders, polyolefins such as high-density polyethylene, low-density polyethylene, and polypropylene, halogenated polyolefins such as polychlorethylene and polypropylene chloride, and acrylic-based polymers such as polyacrylonitrile, polymethyl methacrylate, polyacrylic acid, and polyhydroxyethyl methacrylate Molecules, polystyrene, acrylonitrile-polystyrene-butadiene copolymer, polyvinyl chloride, polyvinyl acetate, vinyl chloride-vinyl acetate copolymer, polyvinyl alcohol, polyvinyl alcohol, partially saponified polyvinyl alcohol, polyvinyl ether, polyvinyl pyrrolidone, and other vinyl polymers , Synthetic rubber such as polyvinylidene chloride, ketone-formalin resin, phenoxy resin, polybutadiene, polyisobutylene, polyisoprene, silicone resin , Fluororesin such as polyvinylidene fluoride and polytrifluoroethylene, acetal resin such as polyacetal, polyester resin such as nylon-6, nylon-66, polyethylene terephthalate, polyamide resin, polyimide resin, polyethylene oxide, polyphenylene oxide, polyethylene glycol, Olefin oxides such as polypropylene glycol and polyoxyethylene polyoxypropylene copolymers, carbonate resins such as polycarbonate, urethane resins such as polysulfone resins, polyurethane and polyurethane urea, epoxy resins, phenol resins, melamine resins, urea resins, polyamino acids, Synthetic resin binders such as maleic acid resins such as maleic anhydride-ethylene copolymer, maleic anhydride-styrene copolymer, Candelilla wax, carnauba wax, rice wax, wood wax, jojoba oil, beeswax, lanolin, whale wax, beef tallow, ozokerite, ceresin and other natural waxes, paraffin wax, microcrystalline wax and other petroleum waxes, montan wax, polyethylene wax , Fischer-Tropsch wax, Sazol wax, hydrogenated castor oil, 12-hydroxystearic acid, stearic acid, stearyl alcohol, laurone, stearone, isopropyl myristate, glycerin fatty acid ester, glycol fatty acid ester, sorbitan fatty acid ester, etc. And mixtures thereof.

これらのバインダーの中でも、半合成バインダーまたは合成樹脂系バインダーの使用が好ましい。バインダーは使用される基材に応じて選択され、加熱溶融物、水溶液、有機溶剤溶液、水中または油中のエマルジョンまたはサスペンジョン等種々の形態で使用できる。ポリオレフィン、ポリエステル、ポリアミド等のフィルム基材に対しては、塩素化ポリオレフィン、マレイン酸樹脂、環化ゴム、ニトロセルロース、ポリアミド、ポリウレタン樹脂、塩化ビニル−酢酸ビニル共重合体などのバインダーの使用が好ましい。バインダーの使用量は特に制限されないが、一般に防虫活性成分１重量部に対して０．１〜５０重量部、好ましくは１〜５０重量部である。   Among these binders, use of a semi-synthetic binder or a synthetic resin binder is preferable. The binder is selected according to the substrate to be used, and can be used in various forms such as a heated melt, an aqueous solution, an organic solvent solution, an emulsion in water or oil, or a suspension. For film base materials such as polyolefin, polyester and polyamide, the use of binders such as chlorinated polyolefin, maleic acid resin, cyclized rubber, nitrocellulose, polyamide, polyurethane resin, vinyl chloride-vinyl acetate copolymer is preferable. . Although the usage-amount of a binder is not restrict | limited in particular, Generally it is 0.1-50 weight part with respect to 1 weight part of insect-control active ingredients, Preferably it is 1-50 weight part.

用いられる可塑剤としては、例えば、リン酸トリブチル、リン酸フェニルクレジル、リン酸トリフェニル、リン酸トリクレジルなどのリン酸エステル系可塑剤、フタル酸ジメチル、フタル酸ジエチル、フタル酸ジブチル、フタル酸ジイソブチル、フタル酸ジオクチル、フタル酸ブチルベンジル、フタル酸ジ−２−エチルヘキシル、フタル酸ジイソデシルなどのフタル酸エステル系可塑剤、オレイン酸ブチル、グリセリンモノオレイン酸エステル、アジピン酸ジブチル、アジピン酸ジヘキシル、アジピン酸ジイソオクチル、セバシン酸ジブチル、ジエチレングリコールジベンゾエート、トリエチレングリコールジ−２−エチルブチラート、アセチルリシノール酸メチル、ブチルフタリルブチルグリコレートなどのその他のエステル系可塑剤、塩素化パラフィン、ジノリルナフタレン等およびその混合物が挙げられる。
可塑剤の使用量は特に制限されないが、一般に本発明の害虫防除材全重量の０．５〜２０重量％程度である。 Examples of the plasticizer used include phosphate ester plasticizers such as tributyl phosphate, phenyl cresyl phosphate, triphenyl phosphate, and tricresyl phosphate, dimethyl phthalate, diethyl phthalate, dibutyl phthalate, and phthalic acid. Phthalate plasticizers such as diisobutyl, dioctyl phthalate, butyl benzyl phthalate, di-2-ethylhexyl phthalate, diisodecyl phthalate, butyl oleate, glycerol monooleate, dibutyl adipate, dihexyl adipate, adipine Other ester plasticizers and salts such as diisooctyl acid, dibutyl sebacate, diethylene glycol dibenzoate, triethylene glycol di-2-ethylbutyrate, methyl acetylricinoleate, butylphthalyl butyl glycolate Paraffin include Ginori Le naphthalene and mixtures thereof.
The amount of the plasticizer used is not particularly limited, but is generally about 0.5 to 20% by weight of the total weight of the pest control material of the present invention.

用いられる溶剤としては、例えば、ペンタン、ヘキサン、ヘプタン、デカン、ウンデカン、ドデカン、テトラデカン、オクタデカン、シクロヘキサンなどの飽和脂肪族または脂環式炭化水素、１−ウンデセン、１−ヘンエイコセンなどの不飽和脂肪族炭化水素、セレクロールＳ４５、セレクロールＳ５０（以上、ゼネカ社製溶剤）などのハロゲン化炭化水素、トルエン、キシレン、エチルベンゼン、ジエチルベンゼン、トリエチルベンゼン、メチルナフタレン、エチルナフタレン、フェニルキシリルエタンなどの芳香族炭化水素、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノンなどのケトン、メタノール、エタノール、イソプロパノール、ブタノール、グリセリンなどのアルコール、オレイン酸、カプリル酸、エナント酸などの脂肪酸、酢酸メチル、酢酸エチル、酢酸イソプロピル、酢酸イソブチル、吉草酸エチル、オレイン酸メチル、ラウリン酸メチル、フタル酸ジメチル、パルミチン酸エチル、コハク酸ジオクチルなどのエステル、エチレングリコール、ジエチレングリコール、テトラエチレングリコール、エチレングリコールモノメチルエーテル、２−エトキシエタノール、２−ブトキシエタノールなどのグリコール誘導体、Ｎ，Ｎ−ジメチルホルムアミド、Ｎ，Ｎ−ジエチルホルムアミドなどの酸アミド、Ｎ−メチルピロリドン、Ｎ−オクチルピロリドン、ひまし油、大豆油、オリーブ油、菜種油、アマニ油等およびその混合物が挙げられる。
溶剤の使用量は特に制限されないが、一般に防虫活性成分１重量部に対して０．２〜５０重量部、好ましくは１〜５０重量部である。 Examples of the solvent used include saturated aliphatics such as pentane, hexane, heptane, decane, undecane, dodecane, tetradecane, octadecane, and cyclohexane, and unsaturated aliphatics such as alicyclic hydrocarbons, 1-undecene, and 1-henecocene. Halogenated hydrocarbons such as hydrocarbons, Selechlor S45, Selechlor S50 (Seneca solvent), aromatics such as toluene, xylene, ethylbenzene, diethylbenzene, triethylbenzene, methylnaphthalene, ethylnaphthalene, phenylxylylethane Hydrocarbon, acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone and other ketones, methanol, ethanol, isopropanol, butanol, glycerin and other alcohols, oleic acid, caprylic acid, Fatty acids such as Nanto acid, methyl acetate, ethyl acetate, isopropyl acetate, isobutyl acetate, ethyl valerate, methyl oleate, methyl laurate, dimethyl phthalate, ethyl palmitate, dioctyl succinate, ethylene glycol, diethylene glycol, Glycol derivatives such as tetraethylene glycol, ethylene glycol monomethyl ether, 2-ethoxyethanol, 2-butoxyethanol, acid amides such as N, N-dimethylformamide, N, N-diethylformamide, N-methylpyrrolidone, N-octylpyrrolidone , Castor oil, soybean oil, olive oil, rapeseed oil, linseed oil and the like and mixtures thereof.
Although the usage-amount of a solvent is not restrict | limited in particular, Generally it is 0.2-50 weight part with respect to 1 weight part of insect repellent active ingredients, Preferably it is 1-50 weight part.

用いられる界面活性剤としては、例えば、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルアリールエーテル、ポリオキシエチレンラノリンアルコール、ポリオキシエチレンアルキルフェノールホルマリン縮合物、ポリオキシエチレンソルビタン脂肪酸エステル、ポリオキシエチレングリセリルモノ脂肪酸エステル、ポリオキシプロピレングリコールモノ脂肪酸エステル、ポリオキシエチレンソルビトール脂肪酸エステル、ポリオキシエチレンひまし油誘導体、ポリオキシエチレン脂肪酸エステル、高級脂肪酸グリセリンエステル、ソルビタン脂肪酸エステル、ショ糖脂肪酸エステル、ポリオキシエチレンポリオキシプロピレン共重合体、ポリオキシエチレン脂肪酸アミド、アルキロールアミド、ポリオキシエチレンアルキルアミン等のノニオン系界面活性剤、ドデシルアミン塩酸塩などのアルキルアミン塩酸塩、アルキル四級アンモニウム塩、ドデシルトリメチルアンモニウム塩などのアルキルトリメチルアンモニウム塩、アルキルジメチルベンジルアンモニウム塩、アルキルピリジニウム塩、アルキルイソキノリニウム塩、ジアルキルモルホリニウム塩、塩化ベンゼトニウム、ポリアルキルビニルピリジニウム塩などのカチオン系界面活性剤、パルミチン酸ナトリウムなどの脂肪酸ナトリウム、ポリオキシエチレンラウリルエーテルカルボン酸ナトリウムなどのエーテルカルボン酸ナトリウム、ラウロイルサルコシンナトリウム、Ｎ−ラウロイルグルタミン酸ナトリウムなどの高級脂肪酸のアミノ酸縮合物、高級アルキルスルホン酸塩、ラウリン酸エステルスルホン酸塩などの高級脂肪酸エステルスルホン酸塩、ジオクチルスルホサクシネートなどのジアルキルスルホコハク酸、オレイン酸アミドスルホン酸塩などの高級脂肪酸アミドスルホン酸、ドデシルベンゼンスルホン酸塩、ジイソプロピルナフタレンスルホン酸塩などのアルキルアリールスルホン酸塩、アルキルアリールスルホン酸塩のホルマリン縮合物、ペンタデカン−２−サルフェートなどの高級アルコール硫酸エステル塩、ポリオキシエチレンドデシルエーテル硫酸ナトリウムなどのポリオキシエチレンアルキルエーテル硫酸エステル塩、ジポリオキシエチレンドデシルエーテルリン酸エステルなどのポリオキシエチレンアルキルリン酸エステル、スチレン−マレイン酸共重合体、アルキルビニルエーテル−マレイン酸共重合体等のアニオン系界面活性剤、Ｎ−ラウリルアラニン、Ｎ，Ｎ，Ｎ−トリメチルアミノプロピオン酸、Ｎ，Ｎ，Ｎ−トリヒドロキシエチルアミノプロピオン酸、Ｎ−ヘキシル−Ｎ，Ｎ−ジメチルアミノ酢酸、１−（２−カルボキシエチル）ピリジニウムベタイン、レシチン等の両性界面活性剤などおよびその混合物が挙げられる。
界面活性剤の使用量は特に制限されないが、一般に防虫活性成分１重量部に対して０．０１〜５重量部である。 Examples of the surfactant used include polyoxyethylene alkyl ether, polyoxyethylene alkyl aryl ether, polyoxyethylene lanolin alcohol, polyoxyethylene alkylphenol formalin condensate, polyoxyethylene sorbitan fatty acid ester, polyoxyethylene glyceryl mono fatty acid Ester, polyoxypropylene glycol mono fatty acid ester, polyoxyethylene sorbitol fatty acid ester, polyoxyethylene castor oil derivative, polyoxyethylene fatty acid ester, higher fatty acid glycerin ester, sorbitan fatty acid ester, sucrose fatty acid ester, polyoxyethylene polyoxypropylene Polymer, polyoxyethylene fatty acid amide, alkylolamide, polyoxyethylene alcohol Nonionic surfactants such as ruamine, alkylamine hydrochlorides such as dodecylamine hydrochloride, alkyltrimethylammonium salts such as alkyl quaternary ammonium salts and dodecyltrimethylammonium salts, alkyldimethylbenzylammonium salts, alkylpyridinium salts, alkyl isocyanates Cationic surfactants such as norinium salt, dialkylmorpholinium salt, benzethonium chloride, polyalkylvinylpyridinium salt, sodium fatty acid such as sodium palmitate, sodium ether carboxylate such as sodium polyoxyethylene lauryl ether carboxylate, lauroyl Amino acid condensates of higher fatty acids such as sodium sarcosine, sodium N-lauroyl glutamate, higher alkyl sulfonates, lauric acid esters Higher fatty acid ester sulfonates such as sulfonates, dialkylsulfosuccinic acids such as dioctylsulfosuccinate, higher fatty acid amide sulfonic acids such as oleic acid amide sulfonate, alkyls such as dodecylbenzene sulfonate and diisopropylnaphthalene sulfonate Aryl sulfonates, formalin condensates of alkyl aryl sulfonates, higher alcohol sulfates such as pentadecane-2-sulfate, polyoxyethylene alkyl ether sulfates such as sodium polyoxyethylene dodecyl ether sulfate, dipolyoxyethylene Polyoxyethylene alkyl phosphate ester such as dodecyl ether phosphate ester, styrene-maleic acid copolymer, alkyl vinyl ether-maleic acid copolymer, etc. Nionic surfactant, N-laurylalanine, N, N, N-trimethylaminopropionic acid, N, N, N-trihydroxyethylaminopropionic acid, N-hexyl-N, N-dimethylaminoacetic acid, 1- ( 2-Carboxyethyl) pyridinium betaine, amphoteric surfactants such as lecithin, and mixtures thereof.
Although the usage-amount of surfactant is not specifically limited, Generally it is 0.01-5 weight part with respect to 1 weight part of insect repellent active ingredients.

用いられる安定化剤としては、例えば、フェノール系酸化防止剤、アミン系酸化防止剤、リン系酸化防止剤、イオウ系酸化防止剤などの酸化防止剤、ベンゾトリアゾール系紫外線吸収剤、ベンゾフェノン系紫外線吸収剤、ベンゾエート系紫外線吸収剤、シアノアクリレート系紫外線吸収剤、サリチル酸系紫外線吸収剤、ヒンダードアミン系系紫外線吸収剤などの紫外線吸収剤、有機ニッケル系化合物などのクエンチャー、イソプロピルアシッドホスフェート、流動パラフィン、エポキシ化大豆油、エポキシ化菜種油、エポキシ化アマニ油等およびその混合物が挙げられる。
安定化剤の使用量は特に制限されないが、一般に防虫活性成分１重量部に対して０．０５〜２重量部、好ましくは０．０５〜０．５重量部である。 Examples of the stabilizer used include antioxidants such as phenolic antioxidants, amine antioxidants, phosphorus antioxidants, sulfur antioxidants, benzotriazole ultraviolet absorbers, and benzophenone ultraviolet absorbers. , UV absorbers such as benzoate UV absorbers, cyanoacrylate UV absorbers, salicylic acid UV absorbers, hindered amine UV absorbers, quenchers such as organic nickel compounds, isopropyl acid phosphate, liquid paraffin, epoxy Epoxidized soybean oil, epoxidized rapeseed oil, epoxidized linseed oil and the like and mixtures thereof.
Although the usage-amount of a stabilizer is not restrict | limited in particular, Generally it is 0.05-2 weight part with respect to 1 weight part of insect-control active ingredients, Preferably it is 0.05-0.5 weight part.

用いられる香料としては、例えば、アセト酢酸エチル、アントラニル酸メチル、イソ吉草酸イソアミル、エナント酸エチル、桂皮酸エチル、酪酸イソアミルなどのエステル、カプロン酸、桂皮酸などの有機酸、桂皮アルコール、ゲラニオール、シトラール、デシルアルコールなどのアルコール、バニリン、ピペロナール、ペリルアルデヒドなどのアルデヒド、マルニトール、メチルβナフチルケトンなどのケトン、メントール等が挙げられる。   Examples of the fragrance used include esters such as ethyl acetoacetate, methyl anthranilate, isoamyl isovalerate, ethyl enanthate, ethyl cinnamate, and isoamyl butyrate, organic acids such as caproic acid and cinnamic acid, cinnamon alcohol, geraniol, Examples thereof include alcohols such as citral and decyl alcohol, aldehydes such as vanillin, piperonal and perylaldehyde, ketones such as malnitol and methyl β-naphthyl ketone, and menthol.

用いられる撥水剤としては、例えば、シリコーンオイル、メチルスチレンシリコーンオイル、オレフィン変性シリコーンオイル、ポリエーテル変性シリコーンオイル、アルコール変性シリコーンオイル、フッ素変性シリコーンオイル、メルカプト変性シリコーンオイル、エポキシ変性シリコーンオイル、高級脂肪酸変性シリコーンオイルなどのシリコーン系撥水剤、テックスガードＴＧ−６２０（ダイキン工業製）などのフッ素系撥水剤等が挙げられる。   Examples of the water repellent used include silicone oil, methylstyrene silicone oil, olefin-modified silicone oil, polyether-modified silicone oil, alcohol-modified silicone oil, fluorine-modified silicone oil, mercapto-modified silicone oil, epoxy-modified silicone oil, and higher grades. Examples thereof include silicone water repellents such as fatty acid-modified silicone oil and fluorine water repellents such as Texguard TG-620 (manufactured by Daikin Industries).

用いられるフィラーとしては、例えば、カオリンクレー、モンモリロナイトクレー、ろう石、酸性白土、活性白土、アタパルジャイトクレー、パイロフィライト、ベントナイト、セリサイト、けいそう土、タルク、酸化チタン、炭酸カルシウム、軽石、ケイ砂、ひる石、ゼオライトなどの鉱物質フィラー、湿式法シリカ、乾式法シリカ、湿式法シリカの焼成品などのホワイトカーボン、小麦粉、ショ糖、デキストリン、木粉、澱粉、糠、ふすま、籾殻、大豆粉、カルナバロウ、油脂などの動植物性フィラー、硫酸アンモニウム、尿素、塩化アンモニウム、硫酸ナトリウム、炭酸ナトリウム、塩化カリウム、リン酸カリウム、硝酸アンモニウム等およびその混合物が挙げられる。   Examples of fillers used include kaolin clay, montmorillonite clay, wax stone, acid clay, activated clay, attapulgite clay, pyrophyllite, bentonite, sericite, diatomaceous earth, talc, titanium oxide, calcium carbonate, pumice, silica Mineral fillers such as sand, vermiculite, zeolite, etc., white carbon such as wet-process silica, dry-process silica, and fired product of wet-process silica, wheat flour, sucrose, dextrin, wood powder, starch, straw, bran, rice husk, soybean Examples include animal and plant fillers such as powder, carnauba wax, oils and fats, ammonium sulfate, urea, ammonium chloride, sodium sulfate, sodium carbonate, potassium chloride, potassium phosphate, ammonium nitrate, and mixtures thereof.

用いられる粘着剤としては、例えば、天然ゴム系樹脂、エチレン−酢酸ビニル共重合体、スチレン−ブタジエン共重合体、スチレン−イソプレン共重合体、シリコーン系共重合体、アクリル酸エステル共重合体、メタクリル酸エステル共重合体、ポリアクリル酸、ポリアクリルアミド、ポリビニルピロリドン、マレイン酸およびその無水物の共重合体、ポリエチレンイミン、メラミン樹脂、尿素樹脂、アクリル酸エステルまたはメタクリル酸エステル−カルボキシル基、ヒドロキシ基、アミド基、ジアルキルアミノ基またはエポキシ基含有モノマー−ビニル基含有モノマー共重合体などが挙げられる。   Examples of the adhesive used include natural rubber resins, ethylene-vinyl acetate copolymers, styrene-butadiene copolymers, styrene-isoprene copolymers, silicone copolymers, acrylic ester copolymers, methacrylic esters, Acid ester copolymer, polyacrylic acid, polyacrylamide, polyvinylpyrrolidone, maleic acid and its anhydride copolymer, polyethyleneimine, melamine resin, urea resin, acrylate ester or methacrylate ester-carboxyl group, hydroxy group, Examples thereof include amide group, dialkylamino group or epoxy group-containing monomer-vinyl group-containing monomer copolymer.

本発明の害虫防除材は通常以下のようにして製造される。 防虫活性成分およびアゾ系色素、さらに必要により、バインダー、可塑剤、溶剤、界面活性剤、安定化剤、香料、撥水剤、フィラー、粘着剤等をプロペラミキサー、タービンミキサー、デゾルバー等の攪拌機、Ｔ．Ｋ．ホモミキサー（特殊機化工業）等の高速回転高剪断型攪拌機、コロイドミルなどで混合して得た液状物を、塗布、印刷、噴霧、含浸等により基材に保持させる。該液状物を基材に塗布する場合、一般にその粘度は平版インキとして使用するには 500〜 3000 ポイズ、凸版インキとして使用するには 100〜 1000 ポイズ、フレキソインキとして使用するには 0.5〜３ポイズ、グラビアインキとして使用するには 0.1〜３ポイズ、スクリーンインキとして使用するには５〜１５ポイズ程度が好ましい。該液状物を保持させる方法としては、ロールコーター、プレードコーター、エアナイフコーター、キャストコーター、ナイフコーター等のコーティング機によるコーティング法、活版輪転機、銅版輪転機または樹脂版輪転機による凸版印刷法、グラビア印刷機、ロートグラビア印刷機または彫刻凹版印刷機によるグラビア印刷法、オフセット印刷機によるオフセット印刷法、タイプ平版印刷機、シルクスクリーン、ドラム型スクリーン印刷機またはスクリーン捺染機による平版印刷法、浸漬機によるディッピング法、噴霧器によるスプレー法、静電噴霧器による静電スプレー法などが挙げられ、特にグラビア印刷法が便利である。
該液状物を基材に保持させた後は、必要により乾燥、加熱、スリット等の操作を行う。 The pest control material of the present invention is usually produced as follows. Insect repellent active ingredients and azo dyes, and if necessary, binders, plasticizers, solvents, surfactants, stabilizers, fragrances, water repellents, fillers, adhesives, etc., agitator such as a propeller mixer, turbine mixer, resolver, T. T. K. A liquid material obtained by mixing with a high-speed rotating high shear type stirrer such as a homomixer (Special Machine Industries) or a colloid mill is held on the substrate by coating, printing, spraying, impregnation or the like. When the liquid is applied to a substrate, the viscosity is generally 500 to 3000 poise for use as a lithographic ink, 100 to 1000 poise for use as a relief printing ink, and 0.5 to 3 poise for use as a flexographic ink. For use as a gravure ink, 0.1 to 3 poise is preferred, and for use as a screen ink, about 5 to 15 poise is preferred. Examples of the method for retaining the liquid material include a coating method using a coating machine such as a roll coater, a plate coater, an air knife coater, a cast coater, and a knife coater, a letterpress printing machine, a letterpress printing method using a copper printing press or a resin printing press, and a gravure. Gravure printing method using printing machine, rotogravure printing machine or engraving intaglio printing machine, offset printing method using offset printing machine, type lithographic printing machine, lithographic printing method using silk screen, drum type screen printing machine or screen printing machine, dipping machine Examples include a dipping method, a spray method using a sprayer, and an electrostatic spray method using an electrostatic sprayer, and a gravure printing method is particularly convenient.
After the liquid is held on the substrate, operations such as drying, heating, and slitting are performed as necessary.

このようにして製造される本発明の害虫防除材は、例えば、作物の一部または全体をシート状物またはネット状物として覆ったり、囲ったり、また、テープ状物として張り巡らせたり、さらには作物の畝間についたて状物を設置したり、温室出入り口に暖簾状物または簾状物を設置したりすることにより用いられる。
本発明の害虫防除材は、防虫活性成分量に換算して、通常１ヘクタール当たり１〜５０００ｇ、好ましくは１０〜５００ｇ程度使用されるが、防虫活性成分の種類、施用方法、害虫の種類、被害の程度等の条件により適宜変更される。 The pest control material of the present invention produced in this way is, for example, covering or enclosing a part or the whole of a crop as a sheet or net, or stretching it around as a tape, It is used by installing a vertical object between crops, or installing a warm or a rice cake at the entrance of a greenhouse.
The pest control material of the present invention is usually used in an amount of 1 to 5000 g, preferably about 10 to 500 g per hectare, in terms of the amount of the insect repellent active ingredient, but the type of insect repellent active ingredient, method of application, pest type, damage It is appropriately changed depending on conditions such as the degree.

本発明の害虫防除材は、主に農作物加害害虫の防除に有効であり、その具体例としては、オンシツコナジラミ（Trialeurodes vaporariorum ）、タバココナジラミ（Bemisia tabaci）、フタテンヒメヨコバイ（Arboridia apicalis）、アブラムシ類等の半翅目害虫、ミナミキイロアザミウマ（Thrips palmi）、チャノキイロアザミウマ（Acirtothrips dorsalis ）、ヒラズハナアザミウマ（Frankliniella intonsa ）等のアザミウマ目害虫、コナガ（Plutella xylostella ）、イチモンジセセリ（Parnara guttata ）等の鱗翅目害虫、ウリミバエ（Dacus cucubitae ）、キノコバエ類（Mycetophilidae）、マメハモグリバエ（Liriomyza trifolii）、タマネギバエ（Delia antiqua ）等の双翅目害虫などが挙げられる。これらの農作物加害害虫は、黄色〜青色に誘引され、特にオンシツコナジラミ、タバココナジラミ、フタテンヒメヨコバイ、チャノキイロアザミウマ、ヒラズハナアザミウマ、イチモンジセセリ、ウリミバエおよびマメハモグリバエは黄色によく誘引され、コナガは黄色〜緑色に、ミナミキイロアザミウマは青色に、タマネギバエは薄青色または黄色によく誘引される。   The pest control material of the present invention is mainly effective for controlling crop pests, and specific examples thereof include Trialeurodes vaporariorum, Bemisia tabaci, Arboridia apicalis, and aphids Hemiptera pests, such as Thrips palmi, Thrips palmi (Acirtothrips dorsalis), Thrips thrips (Frankliniella intonsa), Plutella xylostella , Diptera pests such as Dacus cucubitae, Mycetophilidae, Liriomyza trifolii, and Delia antiqua. These crop pests are attracted to yellow-blue, especially on whitefly, tobacco whitefly, phanten whitefly, teatrothrips, thrips, thrips, yellowflies and legumes are often attracted to yellow. Southern thrips are often attracted to blue and onion flies are light blue or yellow.

次に、本発明の害虫防除材について製造例および試験例を挙げてより具体的に説明するが、本発明は以下の例のみに限定されるものではない。
尚、以下の例において、部は重量部を表わすものである。製造例１ ジスアゾイエロー１０部、ニトロセルロース１０部、フタル酸ジエチル２部およびトルエン７０部を高速高剪断型攪拌機で混合し、フェニトロチオン（有機リン系殺虫化合物）１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、上質紙の両面にグラビア印刷機により塗布し、フェニトロチオンを３ｇ／ｍ² 含有する害虫防除材（１）を得た。 Next, the pest control material of the present invention will be described more specifically with reference to production examples and test examples, but the present invention is not limited to the following examples.
In the following examples, parts represent parts by weight. Production Example 1 10 parts of disazo yellow, 10 parts of nitrocellulose, 2 parts of diethyl phthalate and 70 parts of toluene were mixed with a high-speed high shear type stirrer, and 10 parts of fenitrothion (organophosphorus insecticidal compound) were added and further mixed to obtain an ink. A composition was obtained. The obtained ink composition was applied to both surfaces of a high-quality paper by a gravure printing machine to obtain a pest control material (1) containing 3 g / m ^{2 of} fenitrothion.

製造例２
ジスアゾイエロー１０部、ニトロセルロース１０部、フタル酸ジエチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、フェニトロチオン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、上質紙の両面にグラビア印刷機により塗布し、フェニトロチオンを５ｇ／ｍ² 含有する害虫防除材（２）を得た。 Production Example 2
Mix 10 parts of disazo yellow, 10 parts of nitrocellulose, 2 parts of diethyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol with a high-speed high shear type stirrer, add 10 parts of fenitrothion, and mix further to form an ink composition. I got a thing. The obtained ink composition was applied to both surfaces of a high-quality paper by a gravure printing machine to obtain a pest control material (2) containing 5 g / m ^{2 of} fenitrothion.

製造例３
ファーストイエロー１０Ｇ １０部、ポリアミド樹脂１０部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、エスフェンバレレート（ピレスロイド系殺虫化合物）５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、エスフェンバレレートを１ｇ／ｍ² 含有する害虫防除材（３）を得た。 Production Example 3
10 parts of Fast Yellow 10G, 10 parts of polyamide resin, 2 parts of dibutyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol are mixed with a high-speed high shear type stirrer, and 5 parts of esfenvalerate (pyrethroid insecticide) And further mixing to obtain an ink composition. The obtained ink composition was applied to both sides of a Kent paper by a gravure printing machine to obtain a pest control material (3) containing 1 g / m ^{2 of} esfenvalerate.

製造例４
ジスアゾイエロー１０部、ポリアミド樹脂１０部、アジピン酸ジブチル２部、トルエン７０部およびフェニルキシリルエタン４部を高速高剪断型攪拌機で混合し、エスフェンバレレート１部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、エスフェンバレレートを０．２ｇ／ｍ² 含有する害虫防除材（４）を得た。 Production Example 4
Mix 10 parts of disazo yellow, 10 parts of polyamide resin, 2 parts of dibutyl adipate, 70 parts of toluene and 4 parts of phenylxylylethane with a high-speed, high-shear stirrer, add 1 part of esfenvalerate, and mix further to form an ink composition. I got a thing. The obtained ink composition was applied to both sides of a Kent paper with a gravure printing machine to obtain a pest control material (4) containing 0.2 g / m ^{2 of} esfenvalerate.

製造例５
ファーストイエロー１０Ｇ １０部、塩化ビニル−酢酸ビニル共重合体樹脂１０部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、フェンプロパトリン（ピレスロイド系殺虫化合物）５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、上質紙の両面にグラビア印刷機により塗布し、フェンプロパトリンを２ｇ／ｍ² 含有する害虫防除材（５）を得た。 Production Example 5
10 parts of Fast Yellow 10G, 10 parts of vinyl chloride-vinyl acetate copolymer resin, 2 parts of dibutyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol were mixed with a high-speed high shear type stirrer, and fenpropatoline ( 5 parts of pyrethroid insecticidal compound) were added and further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a high-quality paper by a gravure printing machine to obtain a pest control material (5) containing 2 g / m ^{2 of} fenpropatoline.

製造例６
ジスアゾイエロー１０部、ポリウレタン樹脂１０部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部、イソプロパノール３０部およびフェニルキシリルエタン２部を高速高剪断型攪拌機で混合し、フェンプロパトリン１部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、上質紙の両面にグラビア印刷機により塗布し、フェンプロパトリンを０．１ｇ／ｍ² 含有する害虫防除材（６）を得た。 Production Example 6
10 parts of disazo yellow, 10 parts of polyurethane resin, 2 parts of dibutyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate, 30 parts of isopropanol and 2 parts of phenylxylylethane are mixed with a high-speed high shear type stirrer, and 1 part of fenpropatoline And further mixing to obtain an ink composition. The obtained ink composition was applied to both surfaces of a high-quality paper by a gravure printing machine to obtain a pest control material (6) containing 0.1 g / m ^{2 of} fenpropatoline.

製造例７
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジエチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン（幼若ホルモン活性化合物）３０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを３ｇ／ｍ² 含有する害虫防除材（７）を得た。 Production Example 7
10 parts of disazo yellow, 5 parts of nitrocellulose, 5 parts of polyamide resin, 2 parts of diethyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol were mixed with a high speed high shear type stirrer, and pyriproxyfen (juvenile hormone) 30 parts of active compound) was added and further mixed to obtain an ink composition. The obtained ink composition was apply | coated to both surfaces of Kent paper with the gravure printing machine, and the insect pest control material (7) containing 3 g / m < ² > of pyriproxyfen was obtained.

製造例８
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジエチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン２０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、上質紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを２ｇ／ｍ² 含有する害虫防除材（８）を得た。 Production Example 8
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, diethyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high speed high shear type stirrer, and 20 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both surfaces of a high-quality paper by a gravure printing machine to obtain a pest control material (8) containing 2 g / m ^{2 of} pyriproxyfen.

製造例９
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジエチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（９）を得た。 Production Example 9
Mix 10 parts of disazo yellow, 5 parts of nitrocellulose, 5 parts of polyamide resin, 2 parts of diethyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol with a high speed high shear type stirrer and add 10 parts of pyriproxyfen. Were further mixed to obtain an ink composition. The obtained ink composition was apply | coated to both surfaces of Kent paper with the gravure printing machine, and the pest control material (9) containing 1 g / m < ² > of pyriproxyfen was obtained.

製造例１０
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジエチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（１０）を得た。 Production Example 10
Mix 10 parts of disazo yellow, 5 parts of nitrocellulose, 5 parts of polyamide resin, 2 parts of diethyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol with a high speed high shear type stirrer and add 5 parts of pyriproxyfen. Were further mixed to obtain an ink composition. The obtained ink composition was apply | coated to both surfaces of Kent paper with the gravure printing machine, and the insect pest control material (10) containing 0.5 g / m < ² > of pyriproxyfen was obtained.

製造例１１
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジエチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．１ｇ／ｍ² 含有する害虫防除材（１１）を得た。 Production Example 11
Mix 10 parts of disazo yellow, 5 parts of nitrocellulose, 5 parts of polyamide resin, 2 parts of diethyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol with a high speed high shear type stirrer and add 1 part of pyriproxyfen. Were further mixed to obtain an ink composition. The obtained ink composition was apply | coated to both surfaces of Kent paper with the gravure printing machine, and the insect pest control material (11) containing 0.1 g / m < ² > of pyriproxyfen was obtained.

製造例１２
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジエチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン０．１部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．０１ｇ／ｍ² 含有する害虫防除材（１２）を得た。 Production Example 12
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, diethyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high speed high shear type stirrer, and pyriproxyfen 0.1 part And further mixing to obtain an ink composition. The obtained ink composition was applied to both sides of a Kent paper by a gravure printing machine to obtain a pest control material (12) containing 0.01 g / m ^{2 of} pyriproxyfen.

製造例１３
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジエチル２部、トルエン７０部、酢酸エチル１５部、イソプロパノール３０部およびフェニルキシリルエタン５部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（１３）を得た。 Production Example 13
10 parts of disazo yellow, 5 parts of nitrocellulose, 5 parts of polyamide resin, 2 parts of diethyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate, 30 parts of isopropanol and 5 parts of phenylxylylethane were mixed with a high-speed high shear type stirrer. 5 parts of pyriproxyfen were added and further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a Kent paper with a gravure printing machine to obtain a pest control material (13) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例１４
ジスアゾイエロー１０部、塩化ビニル−酢酸ビニル共重合体樹脂１０部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（１４）を得た。 Production Example 14
Mix 10 parts of disazo yellow, 10 parts of vinyl chloride-vinyl acetate copolymer resin, 2 parts of dibutyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol with a high speed high shear type stirrer, and 5 parts of pyriproxyfen And further mixing to obtain an ink composition. The obtained ink composition was applied to both sides of a Kent paper with a gravure printing machine to obtain a pest control material (14) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例１５
ジスアゾイエロー１０部、ニトロセルロース５部、ポリウレタン樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（１５）を得た。 Production Example 15
Disazo yellow 10 parts, nitrocellulose 5 parts, polyurethane resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high speed high shear type stirrer and 5 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both surfaces of Kent paper by a gravure printing machine to obtain a pest control material (15) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例１６
ジスアゾイエロー１０部、ニトロセルロース８部、ポリアミド樹脂２部、アジピン酸ジブチル２部、トルエン７０部、酢酸エチル１５部、イソプロパノール３０部およびフェニルキシリルエタン１０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（１６）を得た。 Production Example 16
10 parts of disazo yellow, 8 parts of nitrocellulose, 2 parts of polyamide resin, 2 parts of dibutyl adipate, 70 parts of toluene, 15 parts of ethyl acetate, 30 parts of isopropanol and 10 parts of phenylxylylethane were mixed with a high-speed high shear type stirrer. 5 parts of pyriproxyfen were added and further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a Kent paper by a gravure printing machine to obtain a pest control material (16) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例１７
ジスアゾイエロー１０部、ニトロセルロース８部、ポリアミド樹脂２部、アジピン酸ジブチル２部、トルエン７０部、酢酸エチル１５部、イソプロパノール３０部およびフェニルキシリルエタン１部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（１７）を得た。 Production Example 17
10 parts of disazo yellow, 8 parts of nitrocellulose, 2 parts of polyamide resin, 2 parts of dibutyl adipate, 70 parts of toluene, 15 parts of ethyl acetate, 30 parts of isopropanol and 1 part of phenylxylylethane were mixed with a high-speed high shear type stirrer. 5 parts of pyriproxyfen were added and further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a Kent paper by a gravure printing machine to obtain a pest control material (17) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例１８
ジスアゾイエロー１０部、ニトロセルロース８部、ポリアミド樹脂２部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（１８）を得た。 Production Example 18
Disazo Yellow 10 parts, Nitrocellulose 8 parts, Polyamide resin 2 parts, Dibutyl phthalate 2 parts, Toluene 70 parts, Ethyl acetate 15 parts and Isopropanol 30 parts are mixed with a high speed high shear type stirrer, and Pyriproxyfen 10 parts are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a Kent paper by a gravure printing machine to obtain a pest control material (18) containing 1 g / m ^{2 of} pyriproxyfen.

製造例１９
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（１９）を得た。 Production Example 19
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a Kent paper with a gravure printing machine to obtain a pest control material (19) containing 1 g / m ^{2 of} pyriproxyfen.

製造例２０
ジスアゾイエロー１０部、ニトロセルロース２部、ポリアミド樹脂８部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２０）を得た。 Production Example 20
Disazo Yellow 10 parts, Nitrocellulose 2 parts, Polyamide resin 8 parts, Dibutyl phthalate 2 parts, Toluene 70 parts, Ethyl acetate 15 parts and Isopropanol 30 parts are mixed with a high speed high shear type stirrer, and Pyriproxyfen 10 parts are added. Were further mixed to obtain an ink composition. The obtained ink composition was apply | coated to both surfaces of Kent paper with the gravure printing machine, and the pest control material (20) containing 1 g / m < ² > of pyriproxyfen was obtained.

製造例２１
ジスアゾイエロー２０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、上質紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２１）を得た。 Production Example 21
Mix 20 parts of disazo yellow, 5 parts of nitrocellulose, 5 parts of polyamide resin, 2 parts of dibutyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol with a high speed high shear type stirrer and add 10 parts of pyriproxyfen. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both surfaces of a high-quality paper by a gravure printing machine to obtain a pest control material (21) containing 1 g / m ^{2 of} pyriproxyfen.

製造例２２
ジスアゾイエロー５部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、上質紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２２）を得た。 Production Example 22
Disazo Yellow 5 parts, Nitrocellulose 5 parts, Polyamide resin 5 parts, Dibutyl phthalate 2 parts, Toluene 70 parts, Ethyl acetate 15 parts and Isopropanol 30 parts are mixed with a high speed high shear type stirrer, and Pyriproxyfen 10 parts are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both surfaces of a high-quality paper by a gravure printing machine to obtain a pest control material (22) containing 1 g / m ^{2 of} pyriproxyfen.

製造例２３
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２３）を得た。 Production Example 23
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was apply | coated to both surfaces of Kent paper with the gravure printing machine, and the pest control material (23) containing 1 g / m < ² > of pyriproxyfen was obtained.

製造例２４
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、コート紙の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２４）を得た。 Production Example 24
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of the coated paper by a gravure printing machine to obtain a pest control material (24) containing 1 g / m ^{2 of} pyriproxyfen.

製造例２５
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、木綿布の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２５）を得た。 Production Example 25
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a cotton cloth with a gravure printing machine to obtain a pest control material (25) containing 1 g / m ^{2 of} pyriproxyfen.

製造例２６
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ポリエステル布の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２６）を得た。 Production Example 26
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a polyester cloth by a gravure printing machine to obtain a pest control material (26) containing 1 g / m ^{2 of} pyriproxyfen.

製造例２７
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ポリプロピレン製不織布の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２７）を得た。 Production Example 27
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was apply | coated to both surfaces of the nonwoven fabric made from a polypropylene with the gravure printing machine, and the pest control material (27) containing 1 g / m < ² > of pyriproxyfen was obtained.

製造例２８
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ポリエステル製不織布の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２８）を得た。 Production Example 28
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a polyester nonwoven fabric by a gravure printing machine to obtain a pest control material (28) containing 1 g / m ^{2 of} pyriproxyfen.

製造例２９
ジスアゾイエロー１０部、塩化ビニル−酢酸ビニル共重合体樹脂１０部、フタル酸ジエチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ケント紙の両面にプレードコーターにより塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（２９）を得た。 Production Example 29
10 parts of disazo yellow, 10 parts of vinyl chloride-vinyl acetate copolymer resin, 2 parts of diethyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 30 parts of isopropanol were mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen And further mixing to obtain an ink composition. The obtained ink composition was applied to both sides of the Kent paper with a plate coater to obtain a pest control material (29) containing 1 g / m ^{2 of} pyriproxyfen.

製造例３０
ジスアゾイエロー１０部、ポリウレタン樹脂１０部、アジピン酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、木綿布の両面にスプレーコーティングにより塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（３０）を得た。 Production Example 30
Disazo yellow 10 parts, polyurethane resin 10 parts, dibutyl adipate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high speed high shear type stirrer, and 10 parts of pyriproxyfen are further mixed. An ink composition was obtained. The obtained ink composition was applied to both sides of a cotton cloth by spray coating to obtain a pest control material (30) containing 1 g / m ^{2 of} pyriproxyfen.

製造例３１
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ポリプロピレン製不織布の両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．１ｇ／ｍ² 含有する害虫防除材（３１）を得た。 Production Example 31
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was apply | coated to both surfaces of the nonwoven fabric made from a polypropylene with the gravure printing machine, and the pest control material (31) containing 0.1 g / m < ² > of pyriproxyfen was obtained.

製造例３２
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ポリプロピレン製不織布の両面にグラビア印刷機により塗布し、ピリプロキシフェンを１０ｇ／ｍ² 含有する害虫防除材（３２）を得た。 Production Example 32
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a polypropylene nonwoven fabric by a gravure printing machine to obtain a pest control material (32) containing 10 g / m ^{2 of} pyriproxyfen.

製造例３３
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ポリプロピレン製不織布の両面にグラビア印刷機により塗布し、ピリプロキシフェンを２０ｇ／ｍ² 含有する害虫防除材（３３）を得た。 Production Example 33
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a polypropylene nonwoven fabric by a gravure printing machine to obtain a pest control material (33) containing 20 g / m ^{2 of} pyriproxyfen.

製造例３４
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ポリプロピレン製不織布の片面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（３４）を得た。 Production Example 34
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to one side of a polypropylene nonwoven fabric by a gravure printing machine to obtain a pest control material (34) containing 1 g / m ^{2 of} pyriproxyfen.

製造例３５
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、フタル酸ジブチル２部、トルエン７０部、酢酸エチル１５部およびイソプロパノール３０部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、ポリプロピレン製不織布の片面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（３５）を得た。 Production Example 35
Disazo yellow 10 parts, nitrocellulose 5 parts, polyamide resin 5 parts, dibutyl phthalate 2 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 30 parts are mixed with a high-speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to one side of a polypropylene nonwoven fabric by a gravure printing machine to obtain a pest control material (35) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例３６
ジスアゾイエロー１０部、ニトロセルロース２０部、フタル酸ジブチル５部、トルエン７０部、酢酸エチル１５部およびイソプロパノール５部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、厚さ５０μｍのポリエチレンフィルムの両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（３６）を得た。 Production Example 36
Disazo yellow 10 parts, nitrocellulose 20 parts, dibutyl phthalate 5 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 5 parts are mixed with a high speed high shear type stirrer, and 5 parts of pyriproxyfen are further mixed. An ink composition was obtained. The obtained ink composition was applied to both sides of a 50 μm-thick polyethylene film by a gravure printing machine to obtain a pest control material (36) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例３７
製造例３６において、厚さ５０μｍのポリエチレンフィルムにかえて厚さ３０μｍのポリプロピレンフィルムを用いる以外は全て製造例３６と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（３７）を得た。 Production Example 37
A pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 36 except that a polypropylene film with a thickness of 30 μm was used instead of a polyethylene film with a thickness of 50 μm in Production Example 36 (37 )

製造例３８
製造例３６において、厚さ５０μｍのポリエチレンフィルムにかえて厚さ３０μｍのコロナ処理ポリプロピレンフィルムを用いる以外は全て製造例３６と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（３８）を得た。 Production Example 38
A pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 36 except that, in Production Example 36, a 30 μm thick corona-treated polypropylene film is used instead of the 50 μm thick polyethylene film. (38) was obtained.

製造例３９
製造例３６において、厚さ５０μｍのポリエチレンフィルムにかえて厚さ５０μｍのポリスチレンフィルムを用いる以外は全て製造例３６と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（３９）を得た。 Production Example 39
In Production Example 36, except that a 50 μm thick polystyrene film was used instead of the 50 μm thick polyethylene film, a pest control material containing 0.5 g / m ^{2 of} pyriproxyfen (39 )

製造例４０
製造例３６において、厚さ５０μｍのポリエチレンフィルムにかえて厚さ１０μｍのポリエチレンテレフタレートフィルムを用いる以外は全て製造例３６と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４０）を得た。 Production Example 40
In Production Example 36, a pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 36 except that a polyethylene terephthalate film having a thickness of 10 μm is used instead of a polyethylene film having a thickness of 50 μm. 40) was obtained.

製造例４１
製造例３６において、厚さ５０μｍのポリエチレンフィルムにかえて厚さ２０μｍのポリ塩化ビニリデンフィルムを用いる以外は全て製造例３６と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４１）を得た。 Production Example 41
A pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 36 except that a polyvinylidene chloride film having a thickness of 20 μm is used instead of the polyethylene film having a thickness of 50 μm in Production Example 36. (41) was obtained.

製造例４２
製造例３６において、厚さ５０μｍのポリエチレンフィルムにかえて厚さ３０μｍのポリアクリロニトリルフィルムを用いる以外は全て製造例３６と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４２）を得た。
Production Example 42
In Production Example 36, a pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 36 except that a polyacrylonitrile film having a thickness of 30 μm is used instead of a polyethylene film having a thickness of 50 μm. 42) was obtained.

製造例４３
製造例３６において、厚さ５０μｍのポリエチレンフィルムにかえて厚さ３０μｍのナイロン６フィルムを用いる以外は全て製造例３６と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４３）を得た。 Production Example 43
In Production Example 36, a pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 36 except that a nylon 6 film having a thickness of 30 μm was used instead of a polyethylene film having a thickness of 50 μm. 43) was obtained.

製造例４４
製造例３６において、厚さ５０μｍのポリエチレンフィルムにかえて厚さ５μｍのポリエチレンテレフタレートフィルムを用いる以外は全て製造例３６と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４４）を得た。 Production Example 44
A pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 36 except that a polyethylene terephthalate film having a thickness of 5 μm was used instead of the polyethylene film having a thickness of 50 μm in Production Example 36. 44) was obtained.

製造例４５
製造例４０において、ジスアゾイエロー１０部にかえてファーストイエローＧ１０部を用いる以外は全て製造例４０と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４５）を得た。 Production Example 45
In Production Example 40, except that 10 parts of First Yellow G was used instead of 10 parts of Disazo Yellow, a pest control material (45) containing 0.5 g / m ^{2 of} pyriproxyfen was obtained in the same manner as in Production Example 40. .

製造例４６
製造例４０において、ジスアゾイエロー１０部にかえてパーマネントイエローＨＲ１０部を用いる以外は全て製造例４０と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４６）を得た。 Production Example 46
In Production Example 40, except that 10 parts of permanent yellow HR was used instead of 10 parts of disazo yellow, a pest control material (46) containing 0.5 g / m ^{2 of} pyriproxyfen was obtained in the same manner as in Production Example 40. .

製造例４７
製造例４０において、ジスアゾイエロー１０部にかえてジスアゾイエロー２０部を用いる以外は全て製造例４０と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４７）を得た。 Production Example 47
In Production Example 40, except that 20 parts of Disazo Yellow was used instead of 10 parts of Disazo Yellow, a pest control material (47) containing 0.5 g / m ^{2 of} pyriproxyfen was obtained in the same manner as in Production Example 40. .

製造例４８
ファーストイエローＧ１０部、ポリアミド樹脂２０部、フタル酸ジブチル５部、トルエン７０部、酢酸エチル１５部およびイソプロパノール５部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、厚さ３０μｍのコロナ処理ポリプロピレンフィルムの両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４８）を得た。 Production Example 48
First yellow G 10 parts, polyamide resin 20 parts, dibutyl phthalate 5 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 5 parts are mixed with a high speed high shear type stirrer, and 5 parts of pyriproxyfen are added and further mixed. An ink composition was obtained. The obtained ink composition was applied to both surfaces of a corona-treated polypropylene film having a thickness of 30 μm by a gravure printing machine to obtain a pest control material (48) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例４９
製造例４８において、ポリアミド樹脂２０部にかえてポリウレタン樹脂２０部を用いる以外は全て製造例４８と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（４９）を得た。 Production Example 49
In Production Example 48, except that 20 parts of polyurethane resin was used instead of 20 parts of polyamide resin, a pest control material (49) containing 0.5 g / m ^{2 of} pyriproxyfen was obtained in the same manner as in Production Example 48. .

製造例５０
製造例４８において、ポリアミド樹脂２０部にかえて塩化ビニル−酢酸ビニル共重合体２０部を用いる以外は全て製造例４８と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（５０）を得た。 Production Example 50
A pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 48 except that, in Production Example 48, 20 parts of vinyl chloride-vinyl acetate copolymer is used instead of 20 parts of polyamide resin. (50) was obtained.

製造例５１
製造例４８において、ポリアミド樹脂２０部にかえてポリアミド樹脂１０部とニトロセルロース１０部とを用いる以外は全て製造例４８と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（５１）を得た。 Production Example 51
In Production Example 48, except that 10 parts of polyamide resin and 10 parts of nitrocellulose are used in place of 20 parts of polyamide resin, the same pesticide containing 0.5 g / m ^{2 of} pyriproxyfen is used in the same manner as in Production Example 48. (51) was obtained.

製造例５２
ジスアゾイエロー１０部、ニトロセルロース１０部、ポリアミド樹脂１０部、フタル酸ジブチル５部、トルエン７０部、酢酸エチル１５部およびイソプロパノール５部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、厚さ３０μｍのコロナ処理ポリプロピレンフィルムの両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（５２）を得た。 Production Example 52
Mix 10 parts of disazo yellow, 10 parts of nitrocellulose, 10 parts of polyamide resin, 5 parts of dibutyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 5 parts of isopropanol, and add 10 parts of pyriproxyfen. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both surfaces of a 30 μm-thick corona-treated polypropylene film by a gravure printing machine to obtain a pest control material (52) containing 1 g / m ^{2 of} pyriproxyfen.

製造例５３
製造例５２において、ピリプロキシフェン１０部にかえてピリプロキシフェン２０部を用いる以外は全て製造例５２と同様にして、ピリプロキシフェンを２ｇ／ｍ² 含有する害虫防除材（５３）を得た。 Production Example 53
In Production Example 52, a pest control material (53) containing 2 g / m ^{2 of} pyriproxyfen was obtained in the same manner as in Production Example 52 except that 20 parts of pyriproxyfen was used instead of 10 parts of pyriproxyfen. .

製造例５４
製造例５２において、ピリプロキシフェン１０部にかえてピリプロキシフェン１部を用いる以外は全て製造例５２と同様にして、ピリプロキシフェンを０．１ｇ／ｍ² 含有する害虫防除材（５４）を得た。 Production Example 54
In Production Example 52, except that 1 part of pyriproxyfen was used in place of 10 parts of pyriproxyfen, a pest control material (54) containing 0.1 g / m ^{2 of} pyriproxyfen was used in the same manner as in Production Example 52. Obtained.

製造例５５
製造例５２において、ピリプロキシフェン１０部にかえてピリプロキシフェン０．１部を用いる以外は全て製造例５２と同様にして、ピリプロキシフェンを０．０１ｇ／ｍ² 含有する害虫防除材（５５）を得た。 Production Example 55
In Production Example 52, except that 0.1 part of pyriproxyfen is used in place of 10 parts of pyriproxyfen, a pest control material containing 55 g / m ^{2 of} pyriproxyfen (55) )

製造例５６
製造例５２において、ピリプロキシフェン１０部にかえてピリプロキシフェン０．０１部を用いる以外は全て製造例５２と同様にして、ピリプロキシフェンを０．００１ｇ／ｍ² 含有する害虫防除材（５６）を得た。 Production Example 56
In Production Example 52, except that 0.01 part of pyriproxyfen is used instead of 10 parts of pyriproxyfen, the pest control material containing 0.001 g / m ^{2 of} pyriproxyfen (56) )

製造例５７
ジスアゾイエロー１０部、ニトロセルロース２０部、ポリアミド樹脂２０部、フタル酸ジブチル５部、トルエン７０部、酢酸エチル１５部およびイソプロパノール５部を高速高剪断型攪拌機で混合し、ピリプロキシフェン４０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、厚さ３０μｍのコロナ処理ポリプロピレンフィルムの両面にグラビア印刷機により塗布し、ピリプロキシフェンを４ｇ／ｍ² 含有する害虫防除材（５７）を得た。 Production Example 57
Disazo Yellow 10 parts, Nitrocellulose 20 parts, Polyamide resin 20 parts, Dibutyl phthalate 5 parts, Toluene 70 parts, Ethyl acetate 15 parts and Isopropanol 5 parts are mixed with a high speed high shear type stirrer, and Pyriproxyfen 40 parts are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both surfaces of a 30 μm-thick corona-treated polypropylene film by a gravure printing machine to obtain a pest control material (57) containing 4 g / m ^{2 of} pyriproxyfen.

製造例５８
ファーストイエローＧ１０部、ニトロセルロース５部、ポリアミド樹脂１５部、フタル酸ジブチル５部、トルエン７０部、酢酸エチル１５部およびイソプロパノール５部を高速高剪断型攪拌機で混合し、ピリプロキシフェン１０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、厚さ３０μｍのコロナ処理ポリプロピレンフィルムの両面にグラビア印刷機により塗布し、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（５８）を得た。 Production Example 58
First yellow G 10 parts, nitrocellulose 5 parts, polyamide resin 15 parts, dibutyl phthalate 5 parts, toluene 70 parts, ethyl acetate 15 parts and isopropanol 5 parts are mixed with a high speed high shear type stirrer, and 10 parts of pyriproxyfen are added. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a 30 μm-thick corona-treated polypropylene film by a gravure printing machine to obtain a pest control material (58) containing 1 g / m ^{2 of} pyriproxyfen.

製造例５９
製造例５８において、ニトロセルロース５部とポリアミド樹脂１５部とにかえてニトロセルロース１５部とポリアミド樹脂５部とを用いる以外は全て製造例５８と同様にして、ピリプロキシフェンを１ｇ／ｍ² 含有する害虫防除材（５９）を得た。 Production Example 59
In Production Example 58, except for using 15 parts of nitrocellulose and 5 parts of polyamide resin in place of 5 parts of nitrocellulose and 15 parts of polyamide resin, all contained 1 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 58 A pest control material (59) was obtained.

製造例６０
ジスアゾイエロー１０部、ニトロセルロース５部、ポリアミド樹脂５部、ポリウレタン樹脂１０部、フタル酸ジブチル５部、トルエン７０部、酢酸エチル１５部およびイソプロパノール５部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、厚さ３０μｍのコロナ処理ポリプロピレンフィルムの両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（６０）を得た。 Production Example 60
Mix 10 parts of disazo yellow, 5 parts of nitrocellulose, 5 parts of polyamide resin, 10 parts of polyurethane resin, 5 parts of dibutyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 5 parts of isopropanol with a high speed high shear type stirrer. 5 parts of phen was added and further mixed to obtain an ink composition. The obtained ink composition was applied to both surfaces of a 30 μm-thick corona-treated polypropylene film by a gravure printing machine to obtain a pest control material (60) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例６１
ジスアゾイエロー１０部、ニトロセルロース１０部、ポリアミド樹脂１０部、フタル酸ジブチル５部、トルエン７０部、酢酸エチル１５部およびイソプロパノール５部を高速高剪断型攪拌機で混合し、ピリプロキシフェン５部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、厚さ１０μｍのポリエチレンテレフタレートフィルムの両面にグラビア印刷機により塗布し、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（６１）を得た。 Production Example 61
Mix 10 parts of disazo yellow, 10 parts of nitrocellulose, 10 parts of polyamide resin, 5 parts of dibutyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 5 parts of isopropanol with a high-speed high shear stirrer, and add 5 parts of pyriproxyfen. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a 10 μm-thick polyethylene terephthalate film by a gravure printing machine to obtain a pest control material (61) containing 0.5 g / m ^{2 of} pyriproxyfen.

製造例６２
製造例６１において、厚さ１０μｍのポリエチレンテレフタレートフィルムにかえて厚さ２０μｍのポリ塩化ビニリデンフィルムを用いる以外は全て製造例６１と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（６２）を得た。 Production Example 62
Pest control containing pyriproxyfen in an amount of 0.5 g / m ^{2 in the same} manner as in Production Example 61 except that a polyvinylidene chloride film having a thickness of 20 μm was used instead of a polyethylene terephthalate film having a thickness of 10 μm. Material (62) was obtained.

製造例６３
製造例６１において、厚さ１０μｍのポリエチレンテレフタレートフィルムにかえて厚さ３０μｍのナイロン６フィルムを用いる以外は全て製造例６１と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（６３）を得た。 Production Example 63
A pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 61 except that, in Production Example 61, a nylon 6 film having a thickness of 30 μm is used instead of a polyethylene terephthalate film having a thickness of 10 μm. (63) was obtained.

製造例６４
製造例６１において、厚さ１０μｍのポリエチレンテレフタレートフィルムにかえて厚さ５μｍのポリエチレンテレフタレートフィルムを用いる以外は全て製造例６１と同様にして、ピリプロキシフェンを０．５ｇ／ｍ² 含有する害虫防除材（６４）を得た。 Production Example 64
A pest control material containing 0.5 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 61 except that a polyethylene terephthalate film having a thickness of 5 μm is used instead of the polyethylene terephthalate film having a thickness of 10 μm in Production Example 61. (64) was obtained.

製造例６５
ジスアゾイエロー１０部、ニトロセルロース１０部、ポリアミド樹脂１０部、フタル酸ジブチル５部、トルエン７０部、酢酸エチル１５部およびイソプロパノール５部を高速高剪断型攪拌機で混合し、ピリプロキシフェン２０部を加えてさらに混合してインキ組成物を得た。得られたインキ組成物を、厚さ５０μｍのポリエチレンフィルムの両面にグラビア印刷機により塗布し、ピリプロキシフェンを２ｇ／ｍ² 含有する害虫防除材（６５）を得た。 Production Example 65
Mix 10 parts of disazo yellow, 10 parts of nitrocellulose, 10 parts of polyamide resin, 5 parts of dibutyl phthalate, 70 parts of toluene, 15 parts of ethyl acetate and 5 parts of isopropanol, and add 20 parts of pyriproxyfen. Were further mixed to obtain an ink composition. The obtained ink composition was applied to both sides of a 50 μm-thick polyethylene film by a gravure printing machine to obtain a pest control material (65) containing 2 g / m ^{2 of} pyriproxyfen.

製造例６６
製造例６５において、厚さ３０μｍのポリエチレンフィルムにかえて厚さ１０μｍのポリエチレンテレフタレートフィルムを用いる以外は全て製造例６５と同様にして、ピリプロキシフェンを２ｇ／ｍ² 含有する害虫防除材（６６）を得た。 Production Example 66
A pest control material containing 2 g / m ^{2 of} pyriproxyfen in the same manner as in Production Example 65 except that in Example 65, a polyethylene terephthalate film having a thickness of 10 μm was used instead of the polyethylene film having a thickness of 30 μm (66) Got.

次に、後述の試験例において比較試験用として使用する害虫防除材の製造例を比較製造例として示す。
比較製造例
ピリプロキシフェン５部と綿実油９５部とを攪拌、混合して得た溶液を黄色ケント紙（カドミウムイエローにより着色済）にグラビア印刷機により塗布し、ピリプロキシフェンを２ｇ／ｍ² 含有する比較用害虫防除材を得た。 Next, a production example of a pest control material used for a comparative test in a test example described later will be shown as a comparative production example.
Comparative Production Example A solution obtained by stirring and mixing 5 parts of pyriproxyfen and 95 parts of cottonseed oil was applied to yellow Kent paper (colored with cadmium yellow) by a gravure printing machine, and contained 2 g / m ^{2 of} pyriproxyfen. A comparative pest control material was obtained.

次に、試験例を示す。
試験例１
網室内にキャベツ幼苗１０株を５株ずつ２列（株間２０cm、列間３０cm）に配置した。また、幅１０cm、長さ１ｍのテープ状に裁断した本発明の害虫防除材と比較用害虫防除材とをキャベツ幼苗の列間の地上３０cmの位置に設置した。このとき、テープ状物の長辺が地面と平行に、短辺が地面と垂直になるように設置した。次に、網室内に２００頭のタバココナジラミ成虫を放飼し、経時的にキャベツ１葉当たりのタバココナジラミの幼虫数を調査した。
結果を表１に示す。 Next, test examples are shown.
Test example 1
Ten cabbage seedlings of 5 strains were placed in two rows (20 cm between strains, 30 cm between rows) in the net room. Further, the pest control material of the present invention and a comparative pest control material cut into a tape shape having a width of 10 cm and a length of 1 m were placed at a position 30 cm above the row of cabbage seedlings. At this time, the tape-like object was installed so that the long side was parallel to the ground and the short side was perpendicular to the ground. Next, 200 tobacco whitefly adults were released in the net chamber, and the number of tobacco whitefly larvae per cabbage leaf was investigated over time.
The results are shown in Table 1.

上表の結果に見られるように、同量の活性成分（ピリプロキシフェン）を使用したにもかかわらず、本発明の害虫防除材の方が長期間にわたってより高い防除効果を示した。

As can be seen from the results in the above table, the pest control material of the present invention showed a higher control effect over a long period of time despite the use of the same amount of active ingredient (pyriproxyfen).

試験例２
温室内に幅５cmのテープ状に裁断した本発明の害虫防除材をトマト畝に沿って地上 1.5ｍの位置に水平に設置し、設置５日後に５００頭のタバココナジラミ成虫を放飼し、経時的にトマトに寄生しているタバココナジラミの成虫数を調査してトマト１０葉当たりの成虫数の平均値を求めた。
結果を表２に示す。 Test example 2
A pest control material of the present invention cut into a tape of 5 cm in width in a greenhouse is placed horizontally at a position of 1.5 m above the tomato basket and 500 adult tobacco whiteflies are released 5 days after installation. The average number of adult insects per 10 tomato leaves was determined by investigating the number of adult whitefly whitefly parasitic on tomatoes.
The results are shown in Table 2.

上表の結果に見られるように、本発明の害虫防除材は極めて長期間にわたり害虫を防除し得るものである。

As can be seen from the results in the above table, the pest control material of the present invention can control pests for a very long time.

本発明の害虫防除材は、長期間にわたって害虫を防除することから、有用である。
The pest control material of the present invention is useful because it controls pests over a long period of time.

Claims (4)

アゾ系色素により着色された繊維基材に、防虫活性成分が保持されてなることを特徴とする害虫防除材。 A pest control material characterized in that an insect repellent active ingredient is held on a fiber substrate colored with an azo dye. 繊維基材がポリエステル繊維又はポリオレフィン繊維の繊維基材であることを特徴とする請求項１記載の害虫防除材。 The pest control material according to claim 1, wherein the fiber substrate is a fiber substrate of polyester fiber or polyolefin fiber. アゾ系色素が害虫を誘引する色調を有する色素であることを特徴とする請求項１又は請求項２記載の害虫防除材。 The pest control material according to claim 1 or 2, wherein the azo dye is a dye having a color tone that attracts pests. アゾ系色素が黄色又は青色アゾ系色素であることを特徴とする請求項１又は請求項２記載の害虫防除材。
The pest control material according to claim 1 or 2, wherein the azo dye is a yellow or blue azo dye.