JP2005242389A - Photosensitive resin composition - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a photosensitive resin composition having good light transmittance and excellent in film properties, heat resistance, adhesiveness, image forming properties, etc. <P>SOLUTION: The photosensitive resin composition contains (A) a polyamide acid having recurring units represented by formula (I) and (B) an acryl compound having an amino group. In the formula, R<SP>1</SP>represents formula (a); and R<SP>2</SP>represents a specified divalent organic group. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

本発明は感光性樹脂組成物に関する。   The present invention relates to a photosensitive resin composition.

近年、半導体工業にあっては、従来より無機材料を用いて行われていた層間絶縁材料として、主にポリイミド樹脂等のような耐熱性に優れた有機物が、その特性を活かして使用されてきている。   In recent years, in the semiconductor industry, organic materials having excellent heat resistance such as polyimide resins have been used as interlayer insulating materials that have been conventionally used with inorganic materials, taking advantage of their properties. Yes.

ところで、半導体集積回路やプリント基板上の回路パターン形成は、基材表面へのレジスト材の造膜、所定箇所への露光、エッチング等により不要箇所の除去、基板表面の洗浄作業等の煩雑で多岐に亘る工程を経てパターン形成が行われることから、露光、現像によるパターン形成後も必要な部分のレジストを絶縁材料としてそのまま残して用いることができる耐熱感光材料の開発が望まれている。これらの材料として、例えば感光性ポリイミド、環化ポリブタジエン等をベースポリマとした耐熱感光材料が提案されており、特に感光性ポリイミドは、その耐熱性が優れていることや不純物の排除が容易であること等の点から特に注目されている。このような感光性ポリイミドとしては、例えば、特公昭４９−１７３７４号公報には、ポリイミド前駆体と重クロム酸塩からなる系が最初に提案されたが、この材料は、実用的な光感度を有するとともに膜形成能が高いなどの長所を有する反面、保存安定性に欠け、またポリイミド中にクロムイオンが残存することなどの欠点があり、実用には至らなかった。また他の例として、特公昭５５−３０２０７号公報には、ポリアミド酸（ポリイミド前駆体）に感光基をエステル結合で導入した感光性ポリイミド前駆体が提案されているが、この材料は、感光基を導入する際に脱塩酸反応を含むため、最終的に塩化物が残存する問題がある。   By the way, circuit pattern formation on a semiconductor integrated circuit or a printed circuit board is complicated and diverse, such as film formation of a resist material on the surface of a substrate, exposure to a predetermined location, removal of unnecessary portions by etching, etc., cleaning work of the substrate surface, etc. Therefore, it is desired to develop a heat-resistant photosensitive material that can be used by leaving a necessary portion of resist as an insulating material even after pattern formation by exposure and development. As these materials, for example, heat-resistant photosensitive materials based on, for example, photosensitive polyimide and cyclized polybutadiene have been proposed. In particular, photosensitive polyimide has excellent heat resistance and can easily eliminate impurities. In particular, it is attracting attention from such points. As such photosensitive polyimide, for example, Japanese Patent Publication No. 49-17374 first proposed a system comprising a polyimide precursor and dichromate, but this material has practical light sensitivity. In addition to having advantages such as having a high film forming ability, it lacks storage stability and has disadvantages such as remaining chromium ions in the polyimide, and thus has not been put to practical use. As another example, Japanese Patent Publication No. 55-30207 proposes a photosensitive polyimide precursor in which a photosensitive group is introduced into a polyamic acid (polyimide precursor) by an ester bond. Since the dehydrochlorination reaction is included in the introduction of the chloride, there is a problem that chloride remains finally.

このような問題を回避するために、例えば、特開昭５４−１０９８２８号公報には、ポリイミド前駆体に感光基を有する化合物を混合する方法、また、特開昭５６−２４３４３号公報、特開昭６０−１００１４３号公報等により、ポリイミド前駆体中の官能基と感光基を有する化合物の官能基とを反応させて感光性を付与させる方法が提案されている。しかしながら、これらの感光性ポリイミド前駆体は耐熱性、機械特性に優れる芳香族系モノマーを基本骨格に用いており、そのポリイミド前駆体自体の吸収のため、紫外領域での透光性が低く、露光部における光化学反応を十分効果的に行うことができず、低感度であったり、パターンの形状が悪化するという問題があった。特に、最近では、半導体の高集積化に伴い、加工ルールが益々小さくなる傾向にある。そのため、従来の平行光線を用いるコンタクト／プロキシミテイ露光機から、ミラープロジェクションと呼ばれる１：１投影露光機、さらにステッパと呼ばれる縮小投影露光機が用いられるようになってきている。ステッパは超高圧水銀灯の高出力発振線、エキシマレーザのような単色光を利用するものである。これまでステッパとしては超高圧水銀灯のｇ−lineと呼ばれる可視光（波長：４３５nm）を使ったｇ線ステッパが主流であった。しかし、さらなる加工ルール微細化の要求がある。すでに光の回析限界に近い所で加工を行っているので、より微細な加工を行うには使用するステッパの波長を短くすることが必須である。そのために、ｇ線ステッパ（波長：４３５nm）からｉ線ステッパ（波長：３６５nm）に移行しつつある。しかしながら、コンタクト／プロキシミテイ露光機、ミラープロジェクション投影露光機、ｇ線ステッパ用に設計された従来の感光性ポリイミドのベースポリマは、先に述べた理由により透明性が低く、特にｉ線（波長：３６５nm）での透過率はほとんどないため、ｉ線ステッパではまともなパターンが得られない。また、半導体素子の高密度実装方式であるＬＯＣ（リードオンチップ）に対応して表面保護用ポリイミド膜はさらに厚膜のものが求められているが、厚膜の場合には、光透過性が低い問題はさらに深刻になる。このため、ｉ線ステッパ用に設計された、即ちｉ線透過率の高い感光性ポリイミドが強く求められている。   In order to avoid such a problem, for example, Japanese Patent Laid-Open No. 54-109828 discloses a method of mixing a polyimide precursor with a compound having a photosensitive group, and Japanese Patent Laid-Open No. 56-24343, Japanese Patent Laid-Open No. Japanese Laid-Open Patent Publication No. 60-1000014 proposes a method of imparting photosensitivity by reacting a functional group in a polyimide precursor with a functional group of a compound having a photosensitive group. However, these photosensitive polyimide precursors use aromatic monomers with excellent heat resistance and mechanical properties as the basic skeleton, and because of the absorption of the polyimide precursor itself, the translucency in the ultraviolet region is low, and exposure The photochemical reaction in the area cannot be performed sufficiently effectively, and there is a problem that the sensitivity is low and the shape of the pattern is deteriorated. In particular, recently, with the high integration of semiconductors, the processing rules tend to become smaller. For this reason, a 1: 1 projection exposure machine called a mirror projection and a reduced projection exposure machine called a stepper have been used from a conventional contact / proximity exposure machine using parallel rays. The stepper utilizes a monochromatic light such as an excimer laser or a high-power oscillation line of an ultra-high pressure mercury lamp. Until now, g-line steppers using visible light (wavelength: 435 nm) called g-line of ultra-high pressure mercury lamps have been the mainstream as steppers. However, there is a demand for further refinement of processing rules. Since processing is already performed near the diffraction limit of light, it is essential to shorten the wavelength of the stepper used in order to perform finer processing. Therefore, a transition from a g-line stepper (wavelength: 435 nm) to an i-line stepper (wavelength: 365 nm) is being made. However, conventional photosensitive polyimide base polymers designed for contact / proximity exposure machines, mirror projection projection exposure machines, and g-line steppers have low transparency, especially i-line (wavelength: wavelength) for the reasons described above. Since there is almost no transmittance at 365 nm), a decent pattern cannot be obtained with an i-line stepper. In addition, a thicker surface protective polyimide film is required in response to LOC (Lead On Chip), which is a high-density mounting method for semiconductor elements, but in the case of a thick film, light transmittance is required. Low problems become more serious. For this reason, there is a strong demand for photosensitive polyimides designed for i-line steppers, that is, having high i-line transmittance.

本発明は、上記のような問題点に鑑みなされたものであり、露光に使用する光を十分に透過し、ｉ線ステッパでの像形成性および膜特性、耐熱性、接着性等に優れた感光性樹脂組成物及びｉ線ステッパ用感光性樹脂組成物を提供することを目的とするものである。   The present invention has been made in view of the above-described problems, and sufficiently transmits light used for exposure, and is excellent in image forming properties and film characteristics, heat resistance, adhesiveness, etc. with an i-line stepper. An object of the present invention is to provide a photosensitive resin composition and a photosensitive resin composition for an i-line stepper.

本発明は、（Ａ）一般式（Ｉ）   The present invention relates to (A) the general formula (I)

（式中、Ｒ¹は

(Where R ¹ is

を表し、Ｒ²は、 R ² is

及び

as well as

からなる群より選択される２価の有機基を表す）
で示される繰り返し単位；並びに
一般式（Ｉ′） Represents a divalent organic group selected from the group consisting of
As well as the general formula (I ′)

（式中、Ｒ¹は前記のとおりであり、Ｒ²′は

(Wherein R ¹ is as defined above, and R ² ′ is

（式中、Ｒ⁵及びＲ⁶は、同一でも異なっていてもよく、二価の炭化水素基を表し、Ｒ⁷及びＲ⁸は、同一でも異なっていてもよく、一価の炭化水素基を表し、ｔは１以上の整数である）で表される）
で示される繰り返し単位
を有するポリアミド酸；
並びに
（Ｂ）アミノ基を有するアクリル化合物
を含む感光性樹脂組成物に関する。 (In the formula, R ⁵ and R ⁶ may be the same or different and each represents a divalent hydrocarbon group; R ⁷ and R ⁸ may be the same or different and represent a monovalent hydrocarbon group; And t is an integer of 1 or more)
A polyamic acid having a repeating unit represented by:
And (B) a photosensitive resin composition containing an acrylic compound having an amino group.

本発明は、また（Ａ）一般式（Ｉ″）   The present invention also provides (A) the general formula (I ″)

（式中、Ｒ¹は (Where R ¹ is

を表し、Ｒ²″は、２価の芳香族有機基を表す）
で示される繰り返し単位；並びに
一般式（Ｉ′） R ² ″ represents a divalent aromatic organic group)
As well as the general formula (I ′)

（式中、Ｒ¹は前記のとおりであり、Ｒ²′は (Wherein R ¹ is as defined above, and R ² ′ is

（式中、Ｒ⁵及びＲ⁶は、同一でも異なっていてもよく、二価の炭化水素基を表し、Ｒ⁷及びＲ⁸は、同一でも異なっていてもよく、一価の炭化水素基を表し、ｔは１以上の整数である）で表される）
で示される繰り返し単位
を有するポリアミド酸；
並びに
（Ｂ）アミノ基を有するアクリル化合物
を含む感光性樹脂組成物に関する。 (In the formula, R ⁵ and R ⁶ may be the same or different and each represents a divalent hydrocarbon group; R ⁷ and R ⁸ may be the same or different and represent a monovalent hydrocarbon group; And t is an integer of 1 or more)
A polyamic acid having a repeating unit represented by:
And (B) a photosensitive resin composition containing an acrylic compound having an amino group.

本発明の感光性樹脂組成物及びｉ線ステッパ用感光性樹脂組成物は、光透過性が良好なポリアミド酸を使用しているため、像形成性に優れ、特にｉ線によるパターン化に適している。また、これらから得られるポリイミドは、膜の機械特性、耐熱性、接着性等に優れたものである。   Since the photosensitive resin composition of the present invention and the photosensitive resin composition for i-line stepper use a polyamic acid having good light transmittance, it is excellent in image forming property and particularly suitable for patterning by i-line. Yes. Moreover, the polyimide obtained from these is excellent in the mechanical characteristics, heat resistance, adhesiveness, etc. of the film.

本発明における（Ａ）ポリアミド酸は、例えば、オキシジフタル酸又はオキシジフタル酸無水物と必要に応じて用いられる他のテトラカルボン酸二無水物とから成る酸成分とジアミンとを有機溶媒中で開環重付加反応することにより得られる。   The polyamic acid (A) in the present invention includes, for example, an acid component composed of oxydiphthalic acid or oxydiphthalic anhydride and another tetracarboxylic dianhydride used as necessary, and a diamine in an organic solvent. Obtained by addition reaction.

上記の必要に応じて用いられる他のテトラカルボン酸二無水物としては、例えば、ピロメリット酸二無水物、３，３′，４，４′−ベンゾフェノンテトラカルボン酸二無水物、３，３′，４，４′−ビフェニルテトラカルボン酸二無水物、１，２，５，６−ナフタレンテトラカルボン酸二無水物、２，３，６，７−ナフタレンテトラカルボン酸二無水物、２，３，５，６−ピリジンテトラカルボン酸二無水物、１，４，５，８−ナフタレンテトラカルボン酸二無水物、３，４，９，１０−ペリレンテトラカルボン酸二無水物、スルホニルジフタル酸無水物、ｍ−ターフェニル−３，３′，４，４′−テトラカルボン酸二無水物、ｐ−ターフェニル−３，３′，４，４′−テトラカルボン酸二無水物、１，１，１，３，３，３−ヘキサフルオロ−２，２−ビス（２，３−又は３，４−ジカルボキシフェニル）プロパン二無水物、２，２−ビス（２，３−又は３，４−ジカルボキシフェニル）プロパン二無水物、２，２−ビス｛４，（２，３−又は３，４−ジカルボキシフェノキシ）フェニル｝プロパン二無水物、１，１，１，３，３，３−ヘキサフルオロ−２，２−ビス｛４−（２，３−又は３，４−ジカルボキシフェノキシ）フェニル｝プロパン二無水物、下記一般式（II）   Examples of other tetracarboxylic dianhydrides used as necessary include pyromellitic dianhydride, 3,3 ', 4,4'-benzophenone tetracarboxylic dianhydride, 3,3' , 4,4'-biphenyltetracarboxylic dianhydride, 1,2,5,6-naphthalenetetracarboxylic dianhydride, 2,3,6,7-naphthalenetetracarboxylic dianhydride, 2,3 5,6-pyridinetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 3,4,9,10-perylenetetracarboxylic dianhydride, sulfonyldiphthalic anhydride M-terphenyl-3,3 ', 4,4'-tetracarboxylic dianhydride, p-terphenyl-3,3', 4,4'-tetracarboxylic dianhydride, 1,1,1 , 3,3,3-Hexafluoro 2,2-bis (2,3- or 3,4-dicarboxyphenyl) propane dianhydride, 2,2-bis (2,3- or 3,4-dicarboxyphenyl) propane dianhydride, 2, 2-bis {4, (2,3- or 3,4-dicarboxyphenoxy) phenyl} propane dianhydride, 1,1,1,3,3,3-hexafluoro-2,2-bis {4- (2,3- or 3,4-dicarboxyphenoxy) phenyl} propane dianhydride, the following general formula (II)

（Ｒ³及びＲ⁴は一価の炭化水素基を表し、それぞれ同一でも異なっていてもよく、ｓは１以上の整数である）で示されるテトラカルボン酸無水物等の芳香族テトラカルボン酸無水物などが挙げられ、これらは単独で又は二種以上を組み合わせて用いられる。 (R ³ and R ⁴ each represent a monovalent hydrocarbon group, which may be the same or different, and s is an integer of 1 or more) and an aromatic tetracarboxylic acid anhydride such as tetracarboxylic acid anhydride The thing etc. are mentioned, These are used individually or in combination of 2 or more types.

これらのテトラカルボン酸二無水物は、必須成分のオキシジフタル酸無水物の他に必要に応じて用いられるが、その使用量は得られるポリアミド酸の透光性が低下しない量であることが好ましく、酸成分全体の８０mol％以下の量で使用することが好ましい。   These tetracarboxylic dianhydrides are used as necessary in addition to the essential component oxydiphthalic anhydride, but the amount used is preferably an amount that does not decrease the translucency of the resulting polyamic acid, It is preferably used in an amount of 80 mol% or less of the total acid component.

上記のジアミンとしては、特に制限はないが、４，４′−ジアミノジフェニルエーテル、２，４′−ジアミノジフェニルエーテル、３，４′−ジアミノジフェニルエーテル、３，３′−ジアミノジフェニルエーテル、４，４′−ジアミノジフェニルスルフォン、３，３′−ジアミノジフェニルスルフォン及びメタフェニレンジアミンが好ましく、これらは単独で又は二種以上を組み合わせて用いられる。   The diamine is not particularly limited, but is 4,4'-diaminodiphenyl ether, 2,4'-diaminodiphenyl ether, 3,4'-diaminodiphenyl ether, 3,3'-diaminodiphenyl ether, 4,4'-diamino. Diphenyl sulfone, 3,3′-diaminodiphenyl sulfone and metaphenylenediamine are preferred, and these are used alone or in combination of two or more.

これらのジアミン以外にも、得られるポリイミド前駆体の透光性が低下しない程度に、例えばＰ−フェニレンジアミン、Ｐ−キシリレンジアミン、１，５−ジアミノナフタレン、３，３′−ジメチルベンジジン、３，３′−ジメトキシベンジジン、４，４′−（又は３，４′−，３，３′−，２，４′−，２，２′−）ジアミノジフェニルメタン、２，２′−ジアミノジフェニルエーテル、３，４′−（又は２，４′−，２，２′−）ジアミノジフェニルスルホン、４，４′−（又は３，４′−，３，３′−，２，４′−，２，２′−）ジアミノジフェニルスルフイド、４，４′−ベンゾフェノンジアミン、ビス｛４−（４′−アミノフェノキシ）フェニル｝スルホン、１，１，１，３，３，３−ヘキサフルオロ−２，２−ビス（４−アミノフェニル）プロパン、２，２−ビス｛４−（４′−アミノフェノキシ）フェニル｝プロパン、３，３′−ジメチル−４，４′−ジアミノジフェニルメタン、３，３′，５，５′−テトラメチル−４，４′−ジアミノジフェニルメタン、ビス｛４−（３′−アミノフェノキシ）フェニル｝スルホン、２，２−ビス（４−アミノフェニル）プロパン、下記一般式（III）   In addition to these diamines, P-phenylenediamine, P-xylylenediamine, 1,5-diaminonaphthalene, 3,3′-dimethylbenzidine, 3 , 3'-dimethoxybenzidine, 4,4 '-(or 3,4'-, 3,3 '-, 2,4'-, 2,2 '-) diaminodiphenylmethane, 2,2'-diaminodiphenyl ether, 3, , 4 '-(or 2,4'-, 2,2 '-) diaminodiphenylsulfone, 4,4'-(or 3,4 '-, 3,3'-, 2,4 '-, 2,2 '-) Diaminodiphenylsulfide, 4,4'-benzophenonediamine, bis {4- (4'-aminophenoxy) phenyl} sulfone, 1,1,1,3,3,3-hexafluoro-2,2 -Bis (4-amino Enyl) propane, 2,2-bis {4- (4'-aminophenoxy) phenyl} propane, 3,3'-dimethyl-4,4'-diaminodiphenylmethane, 3,3 ', 5,5'-tetramethyl -4,4'-diaminodiphenylmethane, bis {4- (3'-aminophenoxy) phenyl} sulfone, 2,2-bis (4-aminophenyl) propane, the following general formula (III)

（式中、Ｒ⁵及びＲ⁶は、同一でも異なっていてもよく、二価の炭化水素基を表し、Ｒ⁷及びＲ⁸は、同一でも異なっていてもよく、一価の炭化水素基を表し、ｔは１以上の整数である）で示されるジアミノポリシロキサン等の脂肪族ジアミンを用いてもよい。 (In the formula, R ⁵ and R ⁶ may be the same or different and each represents a divalent hydrocarbon group; R ⁷ and R ⁸ may be the same or different and represent a monovalent hydrocarbon group; And an aliphatic diamine such as diaminopolysiloxane represented by the formula: t is an integer of 1 or more.

また、３，３′−ヒドロキシベンジジン、３，４′−ジアミノ−３′，４−ジヒドロキシビフェニル、３，３′−ジヒドロキシ−４，４′−ジアミノジフェニルオキシド、３，３′−ジヒドロキシ−４，４′−ジアミノジフェニルスルホン、２，２−ビス（３−アミノ−４−ヒドロキシフェニル）プロパン、１，１，１，３，３，３−ヘキサフルオロ−２，２−ビス−（３−アミノ−４−ヒドロキシフェニル）プロパン、ビス−（３−ヒドロキシ−４−アミノフェニル）メタン、３，３′−ジヒドロキシ−４，４′−ジアミノベンゾフェノン、１，１−ビス（３−ヒドロキシ−４−アミノフェニル）エタン、２，２−ビス−（３−ヒドロキシ−４−アミノフェニル）プロパン、１，１，１，３，３，３−ヘキサフルオロ−２，２−ビス−（３−ヒドロキシ−４−アミノフェニル）プロパン、１，３−ジアミノ−４−ヒドロキシベンゼン、１，３−ジアミノ−５−ヒドロキシベンゼン、１，３−ジアミノ−４，６−ジヒドロキシベンゼン、１，４−ジアミノ−２−ヒドロキシベンゼン、１，４−ジアミノ−２，５−ジヒドロキシベンゼン等のヒドロキシル基含有ジアミンも用いることができる。これらは、単独で又は二種以上を組み合わせて用いられる。   3,3'-hydroxybenzidine, 3,4'-diamino-3 ', 4-dihydroxybiphenyl, 3,3'-dihydroxy-4,4'-diaminodiphenyl oxide, 3,3'-dihydroxy-4, 4'-diaminodiphenylsulfone, 2,2-bis (3-amino-4-hydroxyphenyl) propane, 1,1,1,3,3,3-hexafluoro-2,2-bis- (3-amino- 4-hydroxyphenyl) propane, bis- (3-hydroxy-4-aminophenyl) methane, 3,3'-dihydroxy-4,4'-diaminobenzophenone, 1,1-bis (3-hydroxy-4-aminophenyl) ) Ethane, 2,2-bis- (3-hydroxy-4-aminophenyl) propane, 1,1,1,3,3,3-hexafluoro-2,2-bis- (3 Hydroxy-4-aminophenyl) propane, 1,3-diamino-4-hydroxybenzene, 1,3-diamino-5-hydroxybenzene, 1,3-diamino-4,6-dihydroxybenzene, 1,4-diamino- Hydroxyl group-containing diamines such as 2-hydroxybenzene and 1,4-diamino-2,5-dihydroxybenzene can also be used. These may be used alone or in combination of two or more.

上記反応に用いる有機溶媒としては、生成するポリイミド前駆体を完全に溶解する極性溶媒が一般に好ましく、例えば、Ｎ−メチル−２−ピロリドン、Ｎ，Ｎ−ジメチルアセトアミド、Ｎ，Ｎ−ジメチルホルムアミド、ジメチルスルホキシド、テトラメチル尿素、ヘキサメチルリン酸トリアミド、γ−ブチロラクトン等が挙げられる。   As the organic solvent used in the above reaction, a polar solvent that completely dissolves the resulting polyimide precursor is generally preferable. For example, N-methyl-2-pyrrolidone, N, N-dimethylacetamide, N, N-dimethylformamide, dimethyl Examples include sulfoxide, tetramethylurea, hexamethylphosphoric triamide, and γ-butyrolactone.

その他、この極性溶媒以外に、ケトン類、エステル類、ラクトン類、エーテル類、ハロゲン化炭化水素類、炭化水素類、例えば、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン、酢酸メチル、酢酸エチル、酢酸ブチル、シュウ酸ジエチル、マロン酸ジエチル、ジエチルエーテル、エチレングリコールジメチルエーテル、ジエチレングリコールジメチルエーテル、テトラヒドロフラン、ジクロロメタン、１，２−ジクロロエタン、１，４−ジクロロブタン、トリクロロエタン、クロロベンゼン、ｏ−ジクロロベンゼン、ヘキサン、ヘプタン、オクタン、ベンゼン、トルエン、キシレン等も使用することができる。これらの有機溶媒は、単独又は二種以上を組み合わせて用いられる。   Other than this polar solvent, ketones, esters, lactones, ethers, halogenated hydrocarbons, hydrocarbons such as acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, methyl acetate, ethyl acetate, butyl acetate , Diethyl oxalate, diethyl malonate, diethyl ether, ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, tetrahydrofuran, dichloromethane, 1,2-dichloroethane, 1,4-dichlorobutane, trichloroethane, chlorobenzene, o-dichlorobenzene, hexane, heptane, octane Benzene, toluene, xylene and the like can also be used. These organic solvents are used alone or in combination of two or more.

本発明で用いられる（Ｂ）アミノ基を有するアクリル化合物は、例えば、Ｎ，Ｎ−ジメチルアミノエチルメタクリレート、Ｎ，Ｎ−ジエチルアミノエチルメタクリレート、Ｎ，Ｎ−ジメチルアミノプロピルメタクリレート、Ｎ，Ｎ−ジエチルアミノプロピルメタクリレート、Ｎ，Ｎ−ジメチルアミノエチルアクリレート、Ｎ，Ｎ−ジエチルアミノエチルアクリレート、Ｎ，Ｎ−ジメチルアミノプロピルアクリレート、Ｎ，Ｎ−ジエチルアミノプロピルアクリレート、Ｎ，Ｎ−ジメチルアミノエチルアクリルアミド、Ｎ，Ｎ−ジメチルアミノエチルアクリルアミド等が挙げられる。これらは、単独で又は２種類以上を組み合わせて用いられる。   Examples of the acrylic compound having an amino group (B) used in the present invention include N, N-dimethylaminoethyl methacrylate, N, N-diethylaminoethyl methacrylate, N, N-dimethylaminopropyl methacrylate, and N, N-diethylaminopropyl. Methacrylate, N, N-dimethylaminoethyl acrylate, N, N-diethylaminoethyl acrylate, N, N-dimethylaminopropyl acrylate, N, N-diethylaminopropyl acrylate, N, N-dimethylaminoethyl acrylamide, N, N-dimethyl Aminoethyl acrylamide etc. are mentioned. These may be used alone or in combination of two or more.

（Ｂ）アミノ基を有するアクリル化合物の使用量は、光感度、耐熱性フィルム強度等の点から（Ａ）一般式（Ｉ）で示される繰り返し単位を含むポリアミド酸に対して１〜２００重量％とすることが好ましく、５〜５０重量％とすることがより好ましい。   (B) The usage-amount of the acrylic compound which has an amino group is 1-200 weight% with respect to the polyamic acid containing the repeating unit shown to (A) general formula (I) from points, such as photosensitivity and heat resistant film strength. It is preferable to set it as 5 to 50 weight%.

本発明の感光性樹脂組成物は、必要に応じて次のような（Ｃ）光開始剤を含有してもよい。（Ｃ）光開始剤としては、例えば、ミヒラーズケトン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、２−ｔ−ブチルアントラキノン、２−エチルアントラキノン、４，４′−ビス（ジエチルアミノ）ベンゾフェノン、アセトフェノン、ベンゾフェノン、チオキサントン、２，２−ジメトキシ−２−フェニルアセトフェノン、１−ヒドロキシシクロヘキシルフェニルケトン、２−メチル−〔４−（メチルチオ）フェニル〕−２−モルフォリノ−１−プロパノン、ベンジル、ジフェニルジスルフィド、フェナンスレンキノン、２−イソプロピルチオキサントン、リボフラビンテトラブチレート、２，６−ビス（ｐ−ジエチルアミノベンザル）−４−メチル−４−アザシクロヘキサノン、Ｎ−エチル−Ｎ−（ｐ−クロロフェニル）グリシン、Ｎ−エチル−Ｎ−（ｐ−クロロフェニル）グリシン、Ｎ−フェニルジエタノールアミン、２−（ｏ−エトキシカルボニル）オキシイミノ−１，３−ジフェニルプロパンジオン、１−フェニル−２−（ｏ−エトキシカルボニル）オキシイミノプロパン−１−オン、３，３′，４，４′−テトラ（ｔ−ブチルパーオキシカルボニル）ベンゾフェノン、３，３′−カルボニルビス（７−ジエチルアミノクマリン）、ビス（シクロペンタジエニル）−ビス〔２，６−ジフルオロ−３−（ピリ−１−イル）フェニル〕チタン等が挙げられる。これらは、単独で又は２種類以上を組み合わせて用いられる。   The photosensitive resin composition of this invention may contain the following (C) photoinitiators as needed. (C) As photoinitiators, for example, Michler's ketone, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, 2-t-butylanthraquinone, 2-ethylanthraquinone, 4,4'-bis (diethylamino) benzophenone, acetophenone, Benzophenone, thioxanthone, 2,2-dimethoxy-2-phenylacetophenone, 1-hydroxycyclohexyl phenyl ketone, 2-methyl- [4- (methylthio) phenyl] -2-morpholino-1-propanone, benzyl, diphenyl disulfide, phenance Lenquinone, 2-isopropylthioxanthone, riboflavin tetrabutyrate, 2,6-bis (p-diethylaminobenzal) -4-methyl-4-azacyclohexanone, N-ethyl N- (p-chlorophenyl) glycine, N-ethyl-N- (p-chlorophenyl) glycine, N-phenyldiethanolamine, 2- (o-ethoxycarbonyl) oxyimino-1,3-diphenylpropanedione, 1-phenyl-2 -(O-ethoxycarbonyl) oxyiminopropan-1-one, 3,3 ', 4,4'-tetra (t-butylperoxycarbonyl) benzophenone, 3,3'-carbonylbis (7-diethylaminocoumarin), And bis (cyclopentadienyl) -bis [2,6-difluoro-3- (pyridin-1-yl) phenyl] titanium. These may be used alone or in combination of two or more.

これらの（Ｃ）光開始剤を使用する場合、その使用量は、光感度、フィルム強度等の点から、（Ａ）一般式（Ｉ）で示される繰り返し単位を有するポリアミド酸に対して０．０１から３０重量％とすることが好ましく、０．０５から１０重量％とすることがより好ましい。   In the case of using these (C) photoinitiators, the amount used is 0. 0 with respect to the polyamic acid having a repeating unit represented by (A) general formula (I) from the viewpoint of photosensitivity, film strength and the like. The content is preferably from 01 to 30% by weight, and more preferably from 0.05 to 10% by weight.

本発明の感光性樹脂組成物は、必要に応じて次のような（Ｄ）付加重合性化合物を含有してもよい。（Ｄ）付加重合性化合物としては、例えば、ジエチレングリコールジアクリレート、トリエチレングリコールジアクリレート、テトラエチレングリコールジアクリレート、ジエチレングリコールジメタクリレート、トリエチレングリコールジメタクリレート、テトラエチレングリコールジメタクリレート、トリメチロールプロパンジアクリレート、トリメチロールプロパントリアクリレート、トリメチロールプロパンジメタクリレート、トリメチロールプロパントリメタクリレート、１，４−ブタンジオールジアクリレート、１，６−ヘキサンジオールジアクリレート、１，４−ブタンジオールジメタクリレート、１，６−ヘキサンジオールメタクリレート、ペンタエリスリトールトリアクリレート、ペンタエリスリトールテトラアクリレート、ペンタエリスリトールトリメタクリレート、ペンタエリスリトールテトラメタクリレート、スチレン、ジビニルベンゼン、４−ビニルトルエン、４−ビニルピリジン、Ｎ−ビニルピロリドン、２−ヒドロキシエチルアクリレート、２−ヒドロキシエチルメタクリレート、１，３−アクリロイルオキシ−２−ヒドロキシプロパン、１，３−メタクリロイルオキシ−２−ヒドロキシプロパン、メチレンビスアクリルアミド、Ｎ，Ｎ−ジメチルアクリルアミド、Ｎ−メチロールアクリルアミド等が挙げられる。これらは、単独で又は２種類以上を組み合わせて用いられる。   The photosensitive resin composition of this invention may contain the following (D) addition polymerizable compound as needed. (D) As the addition polymerizable compound, for example, diethylene glycol diacrylate, triethylene glycol diacrylate, tetraethylene glycol diacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, trimethylolpropane diacrylate, Trimethylolpropane triacrylate, trimethylolpropane dimethacrylate, trimethylolpropane trimethacrylate, 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, 1,4-butanediol dimethacrylate, 1,6-hexane Diol methacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate , Pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, styrene, divinylbenzene, 4-vinyltoluene, 4-vinylpyridine, N-vinylpyrrolidone, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 1,3-acryloyloxy- Examples include 2-hydroxypropane, 1,3-methacryloyloxy-2-hydroxypropane, methylenebisacrylamide, N, N-dimethylacrylamide, N-methylolacrylamide and the like. These may be used alone or in combination of two or more.

（Ｄ）付加重合性化合物を使用する場合、その使用量は、現像液への溶解性も含んだ感光特性、フィルム強度等の点から一般式（Ｉ）で示される繰り返し単位を有するポリアミド酸に対して１〜２００重量％とすることが好ましい。   (D) When an addition polymerizable compound is used, the amount used thereof is a polyamic acid having a repeating unit represented by the general formula (I) in terms of photosensitive properties including solubility in a developer, film strength, and the like. It is preferable to set it as 1 to 200 weight% with respect to it.

本発明の感光性樹脂組成物は、必要に応じて次のような（Ｅ）アジド化合物を含有してもよい。（Ｅ）アジド化合物としては、例えば、   The photosensitive resin composition of this invention may contain the following (E) azide compounds as needed. (E) As an azide compound, for example,

等が挙げられる。これらは、単独で又は２種類以上を組み合わせて用いられる。 Etc. These may be used alone or in combination of two or more.

これらの（Ｅ）アジド化合物を使用する場合、その使用量は、光感度、フィルム強度等の点から、（Ａ）一般式（Ｉ）で示される繰り返し単位を有するポリアミド酸に対して０．０１〜３０重量％とすることが好ましく、０．０５〜１０重量％とすることがより好ましい。   When these (E) azide compounds are used, the amount used is 0.01 to the polyamic acid having a repeating unit represented by (A) the general formula (I) from the viewpoint of photosensitivity, film strength and the like. It is preferable to set it as -30 weight%, and it is more preferable to set it as 0.05-10 weight%.

本発明の感光性樹脂組成物は、保存時の安定性を高めるためにｐ−メトキシフェノール、ハイドロキノン、ピロガロール、フェノチアジン、ニトロソアミン類等のラジカル重合禁止剤またはラジカル重合抑制剤を含有してもよい。   The photosensitive resin composition of the present invention may contain a radical polymerization inhibitor or a radical polymerization inhibitor such as p-methoxyphenol, hydroquinone, pyrogallol, phenothiazine, and nitrosamines in order to enhance the stability during storage.

本発明の感光性樹脂組成物は、浸漬法、スプレー法、スクリーン印刷法、回転塗布法等によってシリコンウエーハ、金属基板、ガラス基板、セラミック基板等の基材上に塗布され、溶剤の大部分を加熱乾燥することにより粘着性のない塗膜とすることが出来る。   The photosensitive resin composition of the present invention is applied on a substrate such as a silicon wafer, a metal substrate, a glass substrate, or a ceramic substrate by a dipping method, a spray method, a screen printing method, a spin coating method, etc. A coating film having no tackiness can be obtained by heating and drying.

この塗膜上に、所望のパターンが描かれたマスクを通して活性光線または化学線を照射する。本発明の材料は、ｉ線ステッパ用に設計されたものであるが、照射する活性光線または化学線としてｉ線ステッパ以外に、超高圧水銀灯を用いるコンタクト／プロキシミティ露光機、ミラープロジェクション露光機、ｇ線ステッパ、その他の紫外・可視光源や、Ｘ線、電子線も用いることができる。照射後未照射部を適当な現像液で溶解除去することにより所望のレリーフパターンを得る。   The coating film is irradiated with actinic rays or actinic radiation through a mask on which a desired pattern is drawn. The material of the present invention is designed for an i-line stepper, but in addition to the i-line stepper as an actinic ray or actinic ray to be irradiated, a contact / proximity exposure machine that uses an ultra-high pressure mercury lamp, a mirror projection exposure machine, A g-line stepper, other ultraviolet / visible light sources, X-rays, and electron beams can also be used. A desired relief pattern is obtained by dissolving and removing the unirradiated portion with an appropriate developer after irradiation.

現像液としては、Ｎ，Ｎ−ジメチルホルムアミド、Ｎ，Ｎ−ジメチルアセトアミド、Ｎ−メチル−２−ピロリドンなどの良溶媒やこれらと低級アルコールや水または芳香族炭化水素などの貧溶媒との混合溶媒、あるいは水酸化テトラメチルアンモニウム水溶液やトリエタノールアミン水溶液などの塩基性溶液が用いられる。現像後は必要に応じて水または貧溶媒でリンスを行い、１００℃前後で乾燥しパターンを安定なものとする。このレリーフパターンを、耐熱性のあるものとするために２００〜５００℃、好ましくは３００〜４００℃の温度で数十分から数時間加熱することによりパターン化された高耐熱性ポリイミドが形成される。   As a developing solution, a good solvent such as N, N-dimethylformamide, N, N-dimethylacetamide, N-methyl-2-pyrrolidone, and a mixed solvent of these with a poor solvent such as a lower alcohol, water, or an aromatic hydrocarbon Alternatively, a basic solution such as an aqueous tetramethylammonium hydroxide solution or an aqueous triethanolamine solution is used. After development, if necessary, rinse with water or a poor solvent, and dry at around 100 ° C. to stabilize the pattern. In order to make this relief pattern heat resistant, a patterned high heat resistant polyimide is formed by heating at a temperature of 200 to 500 ° C., preferably 300 to 400 ° C. for several tens of minutes to several hours. .

このようにして本発明の感光性樹脂組成物は半導体用バッファーコート膜、多層配線板の層間絶縁膜などに変換しうるものである。   Thus, the photosensitive resin composition of the present invention can be converted into a semiconductor buffer coat film, an interlayer insulating film of a multilayer wiring board, and the like.

以下に本発明を実施例により詳細に説明する。   Hereinafter, the present invention will be described in detail with reference to examples.

合成例１
撹拌機、温度計及び窒素導入管を備えた１００mlのフラスコに３，４′−ジアミノジフェニルエーテル９．８９１７ｇ、１，３−ビス（３−アミノプロピル）−１，１，３，３−テトラメチルジシロキサン０．６４６２ｇ、水２．２４８４ｇ、キシレン１４．６０ｇ及びＮ−メチル−２−ピロリドン５８．３８ｇを加え、窒素流通下、室温で撹拌溶解した後、この溶液にオキシジフタル酸無水物１６．４５３４ｇを添加し、５時間撹拌し粘稠なポリアミド酸（ポリイミド前駆体）の溶液を得た。さらに、この溶液を７０℃で加熱し粘度を８００Pa・s｛８０ポイズ｝に調節した。このポリマ溶液をＰ−１と呼ぶ。 Synthesis example 1
In a 100 ml flask equipped with a stirrer, a thermometer and a nitrogen introduction tube, 9.817 g of 3,4'-diaminodiphenyl ether, 1,3-bis (3-aminopropyl) -1,1,3,3-tetramethyldi After adding 0.6462 g of siloxane, 2.2484 g of water, 14.60 g of xylene and 58.38 g of N-methyl-2-pyrrolidone, stirring and dissolving at room temperature under nitrogen flow, 16.4534 g of oxydiphthalic anhydride was added to this solution. The mixture was added and stirred for 5 hours to obtain a viscous polyamic acid (polyimide precursor) solution. Further, this solution was heated at 70 ° C. to adjust the viscosity to 800 Pa · s {80 poise}. This polymer solution is referred to as P-1.

合成例２
撹拌機、温度計及び窒素導入管を備えた５００mlのフラスコに２，４′−ジアミノジフェニルエーテル４９．４５８３ｇ、１，３−ビス（３−アミノプロピル）−１，１，３，３−テトラメチルジシロキサン３．２３０８ｇ、キシレン７２．１０ｇ及びＮ−メチル−２−ピロリドン２８８．４２ｇを加え、窒素流通下、室温で撹拌溶解した後、この溶液にオキシジフタル酸無水物８０．６５４１ｇを添加し、５時間撹拌し粘稠なポリアミド酸（ポリイミド前駆体）の溶液を得た。さらに、この溶液を７０℃で加熱し粘度を８００Pa・s｛８０ポイズ｝に調節した。このポリマ溶液をＰ−２と呼ぶ。 Synthesis example 2
In a 500 ml flask equipped with a stirrer, a thermometer and a nitrogen inlet tube, 49.4583 g of 2,4'-diaminodiphenyl ether, 1,3-bis (3-aminopropyl) -1,1,3,3-tetramethyldi After adding 3.2308 g of siloxane, 72.10 g of xylene and 288.42 g of N-methyl-2-pyrrolidone, stirring and dissolving at room temperature under nitrogen flow, 80.541 g of oxydiphthalic anhydride was added to this solution for 5 hours. A viscous polyamic acid (polyimide precursor) solution was obtained by stirring. Further, this solution was heated at 70 ° C. to adjust the viscosity to 800 Pa · s {80 poise}. This polymer solution is called P-2.

合成例３
撹拌機、温度計及び窒素導入管を備えた５００mlのフラスコに３，３′−ジアミノジフェニルスルフォン５７．０８５５ｇ、１，３−ビス（３−アミノプロピル）−１，１，３，３−テトラメチルジシロキサン３．００７１ｇ、キシレン７３．０９ｇ及びＮ−メチル−２−ピロリドン２９２．３５ｇを加え、窒素流通下、室温で撹拌溶解した後、この溶液にオキシジフタル酸無水物７５．０７０３ｇを添加し、５時間撹拌し粘稠なポリアミド酸（ポリイミド前駆体）の溶液を得た。さらに、この溶液を７０℃で加熱し粘度を８００Pa・s｛８０ポイズ｝に調節した。このポリマ溶液をＰ−３と呼ぶ。 Synthesis example 3
57.0855 g of 3,3'-diaminodiphenylsulfone, 1,3-bis (3-aminopropyl) -1,1,3,3-tetramethyl in a 500 ml flask equipped with a stirrer, thermometer and nitrogen inlet tube After adding 3.0071 g of disiloxane, 73.09 g of xylene and 292.35 g of N-methyl-2-pyrrolidone, stirring and dissolving at room temperature under nitrogen flow, 75.0703 g of oxydiphthalic anhydride was added to this solution, and 5 The mixture was stirred for a time to obtain a viscous polyamic acid (polyimide precursor) solution. Further, this solution was heated at 70 ° C. to adjust the viscosity to 800 Pa · s {80 poise}. This polymer solution is called P-3.

合成例４
撹拌機、温度計及び窒素導入管を備えた５００mlのフラスコに４，４′−ジアミノジフェニルスルフォン５７．０８５５ｇ、１，３−ビス（３−アミノプロピル）−１，１，３，３−テトラメチルジシロキサン３．００７１ｇ、キシレン７３．０９ｇ及びＮ−メチル−２−ピロリドン２９２．３５ｇを加え、窒素流通下、室温で撹拌溶解した後、この溶液にオキシジフタル酸無水物７５．０７０３ｇを添加し、５時間撹拌し粘稠なポリアミド酸（ポリイミド前駆体）の溶液を得た。さらに、この溶液を７０℃で加熱し粘度を８００Pa・s｛８０ポイズ｝に調節した。このポリマ溶液をＰ−４と呼ぶ。 Synthesis example 4
In a 500 ml flask equipped with a stirrer, a thermometer and a nitrogen introduction tube, 57.0855 g of 4,4'-diaminodiphenylsulfone, 1,3-bis (3-aminopropyl) -1,1,3,3-tetramethyl After adding 3.0071 g of disiloxane, 73.09 g of xylene and 292.35 g of N-methyl-2-pyrrolidone, stirring and dissolving at room temperature under nitrogen flow, 75.0703 g of oxydiphthalic anhydride was added to this solution, and 5 The mixture was stirred for a time to obtain a viscous polyamic acid (polyimide precursor) solution. Further, this solution was heated at 70 ° C. to adjust the viscosity to 800 Pa · s {80 poise}. This polymer solution is called P-4.

合成例５
撹拌機、温度計及び窒素導入管を備えた１００mlのフラスコにメタフェニレンジアミン６．３６９７ｇ、１，３−ビス（３−アミノプロピル）−１，１，３，３−テトラメチルジシロキサン０．７７０４ｇ、水２．６８０８ｇ、キシレン１４．４７ｇ及びＮ−メチル−２−ピロリドン５７．８８ｇを加え、窒素流通下、室温で撹拌溶解した後、この溶液にオキシジフタル酸無水物１９．６１７６ｇを添加し、５時間撹拌し粘稠なポリアミド酸（ポリイミド前駆体）の溶液を得た。さらに、この溶液を７０℃で加熱し粘度を８００Pa・s｛８０ポイズ｝に調節した。このポリマ溶液をＰ−５と呼ぶ。 Synthesis example 5
In a 100 ml flask equipped with a stirrer, a thermometer and a nitrogen introducing tube, 6.397 g of metaphenylenediamine, 0.7704 g of 1,3-bis (3-aminopropyl) -1,1,3,3-tetramethyldisiloxane After adding 2.6808 g of water, 14.47 g of xylene and 57.88 g of N-methyl-2-pyrrolidone, stirring and dissolving at room temperature under nitrogen flow, 19.6176 g of oxydiphthalic anhydride was added to this solution. The mixture was stirred for a time to obtain a viscous polyamic acid (polyimide precursor) solution. Further, this solution was heated at 70 ° C. to adjust the viscosity to 800 Pa · s {80 poise}. This polymer solution is called P-5.

合成例６
撹拌機、温度計及び窒素導入管を備えた２００mlのフラスコに４，４′−ジアミノジフェニルエーテル１９．５９３１ｇ、１，３−ビス（３−アミノプロピル）−１，１，３，３−テトラメチルジシロキサン１．２７９９ｇ、水４．４５３６ｇ、γ−ブチロラクトン２９．２６ｇ及びＮ−メチル−２−ピロリドン１１７．０２ｇを加え、窒素流通下、室温で撹拌溶解した後、この溶液にオキシジフタル酸無水物３３．２２９５ｇを添加し、５時間撹拌し粘稠なポリアミド酸（ポリイミド前駆体）の溶液を得た。さらに、この溶液を７０℃で加熱し粘度を８００Pa・s｛８０ポイズ｝に調節した。このポリマ溶液をＰ−６と呼ぶ。 Synthesis Example 6
In a 200 ml flask equipped with a stirrer, a thermometer and a nitrogen introducing tube, 19.5931 g of 4,4'-diaminodiphenyl ether, 1,3-bis (3-aminopropyl) -1,1,3,3-tetramethyldi 1.2799 g of siloxane, 4.4536 g of water, 29.26 g of γ-butyrolactone and 117.02 g of N-methyl-2-pyrrolidone were added, and the mixture was stirred and dissolved at room temperature under a nitrogen stream. 2295 g was added and stirred for 5 hours to obtain a viscous polyamic acid (polyimide precursor) solution. Further, this solution was heated at 70 ° C. to adjust the viscosity to 800 Pa · s {80 poise}. This polymer solution is referred to as P-6.

合成例７
撹拌機、温度計及び窒素導入管を備えた１００mlのフラスコに４，４′−ジアミノジフェニルエーテル１１．９８４１ｇ、１，３−ビス（３−アミノプロピル）−１，１，３，３−テトラメチルジシロキサン０．７８２９ｇ、水２．７２４０ｇ、キシレン１４．４８ｇ及びＮ−メチル−２−ピロリドン５７．９３ｇを加え、窒素流通下、室温で撹拌溶解した後、この溶液にピロメリット酸二無水物１４．０１６１ｇを添加し、５時間撹拌し粘稠なポリアミド酸（ポリイミド前駆体）の溶液を得た。さらに、この溶液を７０℃で加熱し粘度を８００Pa・s｛８０ポイズ｝に調節した。このポリマ溶液をＰ−７と呼ぶ。 Synthesis example 7
In a 100 ml flask equipped with a stirrer, a thermometer and a nitrogen introduction tube, 11.9841 g of 4,4'-diaminodiphenyl ether, 1,3-bis (3-aminopropyl) -1,1,3,3-tetramethyldi After adding 0.7829 g of siloxane, 2.7240 g of water, 14.48 g of xylene and 57.93 g of N-methyl-2-pyrrolidone, stirring and dissolving at room temperature under nitrogen flow, pyromellitic dianhydride 14. 0161 g was added and stirred for 5 hours to obtain a viscous polyamic acid (polyimide precursor) solution. Further, this solution was heated at 70 ° C. to adjust the viscosity to 800 Pa · s {80 poise}. This polymer solution is called P-7.

合成例８
撹拌機、温度計及び窒素導入管を備えた１００mlのフラスコに４，４′−ジアミノジフェニルエーテル１０．０８１９ｇ、１，３−ビス（３−アミノプロピル）−１，１，３，３−テトラメチルジシロキサン０．６５８６ｇ、水２．２９１６ｇ、キシレン１４．４１ｇ及びＮ−メチル−２−ピロリドン９０．０５ｇを加え、窒素流通下、室温で撹拌溶解した後、この溶液にビフェニルテトラカルボン酸二無水物１５．９０４９ｇを添加し、５時間撹拌し粘稠なポリアミド酸（ポリイミド前駆体）の溶液を得た。さらに、この溶液を７０℃で加熱し粘度を８００Pa・s｛８０ポイズ｝に調節した、このポリマ溶液をＰ−８と呼ぶ。 Synthesis example 8
10.0819 g of 4,4'-diaminodiphenyl ether, 1,3-bis (3-aminopropyl) -1,1,3,3-tetramethyldiethyl in a 100 ml flask equipped with a stirrer, thermometer and nitrogen inlet tube 0.6586 g of siloxane, 2.2916 g of water, 14.41 g of xylene and 90.05 g of N-methyl-2-pyrrolidone were added and stirred and dissolved at room temperature under a nitrogen stream, and then biphenyltetracarboxylic dianhydride 15 was added to this solution. 9049 g was added and stirred for 5 hours to obtain a viscous polyamic acid (polyimide precursor) solution. Furthermore, this polymer solution which heated this solution at 70 degreeC and adjusted the viscosity to 800 Pa * s {80 poise} is called P-8.

合成例１〜８で得られたポリアミド酸（ポリイミド前駆体）の溶液Ｐ−１〜Ｐ−８の塗膜状態での、３６５nmにおける透過率を表１に示した。ポリアミド酸の透過率は、ガラス基板上にポリアミド酸（ポリイミド前駆体）の樹脂溶液をスピンコートし、８５℃で３分、さらに１０５℃で３分乾燥して得られた塗膜を、分光光度計を用いて測定した。   Table 1 shows the transmittance at 365 nm in the coating state of the solutions P-1 to P-8 of the polyamic acid (polyimide precursor) obtained in Synthesis Examples 1 to 8. The transmittance of the polyamic acid was determined by spectrophotometrically measuring the coating film obtained by spin-coating a polyamic acid (polyimide precursor) resin solution on a glass substrate and drying at 85 ° C. for 3 minutes and further at 105 ° C. for 3 minutes. Measured using a meter.

実施例１〜６
合成例１〜６で得られたポリアミド酸（ポリイミド前駆体）の溶液Ｐ−１〜Ｐ−６の各々１０ｇに対して、表２に示したように、ＭＤＡＰ、ＣＡ、ＥＡＢ及びＰＤＯを所定量ずつ加え、撹拌混合して実施例１〜６に供する均一な感光性樹脂組成物溶液を得た。 Examples 1-6
As shown in Table 2, predetermined amounts of MDAP, CA, EAB, and PDO are added to 10 g of each of the polyamic acid (polyimide precursor) solutions P-1 to P-6 obtained in Synthesis Examples 1 to 6. Then, the mixture was stirred and mixed to obtain a uniform photosensitive resin composition solution used in Examples 1 to 6.

比較例１及び２合成例７及び８で得られたポリアミド酸（ポリイミド前駆体）の溶液Ｐ−７及びＰ−８各々１０ｇに対して、表２に示したようにＭＤＡＰ、ＣＡ、ＥＡＢ及びＰＤＯを所定量ずつ加え、撹拌混合して比較例１及び２に供する均一な感光性樹脂組成物溶液を得た。   Comparative Examples 1 and 2 As shown in Table 2, MDAP, CA, EAB, and PDO were used for 10 g each of the polyamic acid (polyimide precursor) solutions P-7 and P-8 obtained in Synthesis Examples 7 and 8. Were added in predetermined amounts and mixed by stirring to obtain a uniform photosensitive resin composition solution used in Comparative Examples 1 and 2.

これらの各溶液をフィルタ濾過し、それぞれシリコンウエハ上に滴下スピンコートした。次にホットプレートを用いて１００℃、１５０秒加熱し２０μmの塗膜を形成した後、パターンマスクし、ｉ線ステッパ（ｉ−lineステッパ）で露光した。これを、さらに１１０℃、５０秒間、加熱し、Ｎ−メチル−２−ピロリドン／水（重量比７５／２５）混合溶液を用いてパドル現像した。これを、１００℃で３０分、２００℃で３０分、窒素雰囲気下３５０℃で６０分加熱してポリイミドのレリーフパターンを得た。   Each of these solutions was filtered and dropped onto a silicon wafer. Next, a 20 μm coating film was formed by heating at 100 ° C. for 150 seconds using a hot plate, and then patterned and exposed with an i-line stepper. This was further heated at 110 ° C. for 50 seconds and subjected to paddle development using a mixed solution of N-methyl-2-pyrrolidone / water (weight ratio 75/25). This was heated at 100 ° C. for 30 minutes, 200 ° C. for 30 minutes, and under a nitrogen atmosphere at 350 ° C. for 60 minutes to obtain a relief pattern of polyimide.

これらの評価結果を表３に示した。尚、解像度、現像残膜率及び接着性は、以下の方法により評価した。   The evaluation results are shown in Table 3. In addition, the resolution, the developing residual film rate, and the adhesiveness were evaluated by the following methods.

解像度は、スルホールテストパターンを用いて、現像可能なスルホールの最小の大きさとして評価した。   The resolution was evaluated as the smallest developable through hole size using the through hole test pattern.

現像残膜率は、現像前及び現像後の膜厚を測定し、（現像後の膜厚／現像前の膜厚）×１００（％）で求めた。膜厚はスローン社製膜厚計Dektak−３０３０を用いて測定した。   The development residual film ratio was obtained by measuring the film thickness before and after development and (film thickness after development / film thickness before development) × 100 (%). The film thickness was measured using a Throne film thickness meter Dektak-3030.

接着性は、感光性樹脂組成物をシリコンウエハ上に塗布し、１００℃で３０分、２００℃で３０分、窒素雰囲気下３５０℃で６０分加熱して得た塗膜（膜厚：５μm）について、プレッシャクッカー試験（条件：１２１℃、２気圧、１００時間）を行った後の碁盤目試験で評価した。   Adhesiveness was obtained by coating a photosensitive resin composition on a silicon wafer and heating it at 100 ° C. for 30 minutes, 200 ° C. for 30 minutes, and nitrogen atmosphere at 350 ° C. for 60 minutes (film thickness: 5 μm). Was evaluated by a cross-cut test after a pressure cooker test (conditions: 121 ° C., 2 atm, 100 hours).

碁盤目試験は、カッタナイフで１mmで１００個のます目ができるように碁盤目状の傷をつけ、これをＪＩＳに規定された（ＪＩＳ Ｋ５４００）セロハン粘着テープで剥離し、１００個のます目に対する残存したます目の個数で表す方法である。   In the cross cut test, a grid cut is made with a cutter knife so that 100 squares can be made with 1 mm, and this is peeled with cellophane adhesive tape specified by JIS (JIS K5400). This is a method of expressing the number of remaining meshes with respect to.

Claims (5)

（Ａ）一般式（Ｉ）

（式中、Ｒ¹は

を表し、Ｒ²は、

及び

からなる群より選択される２価の有機基を表す）
で示される繰り返し単位；並びに
一般式（Ｉ′）

（式中、Ｒ¹は前記のとおりであり、Ｒ²′は

（式中、Ｒ⁵及びＲ⁶は、同一でも異なっていてもよく、二価の炭化水素基を表し、Ｒ⁷及びＲ⁸は、同一でも異なっていてもよく、一価の炭化水素基を表し、ｔは１以上の整数である）で表される）
で示される繰り返し単位
を有するポリアミド酸；
並びに
（Ｂ）アミノ基を有するアクリル化合物
を含む感光性樹脂組成物。 (A) General formula (I)

(Where R ¹ is

R ² is

as well as

Represents a divalent organic group selected from the group consisting of
As well as the general formula (I ′)

(Wherein R ¹ is as defined above, and R ² ′ is

(In the formula, R ⁵ and R ⁶ may be the same or different and each represents a divalent hydrocarbon group; R ⁷ and R ⁸ may be the same or different and represent a monovalent hydrocarbon group; And t is an integer of 1 or more)
A polyamic acid having a repeating unit represented by:
And (B) a photosensitive resin composition containing an acrylic compound having an amino group. 一般式（Ｉ）において、Ｒ²が

である、請求項１記載の感光性樹脂組成物。 In general formula (I), R ² is

The photosensitive resin composition of Claim 1 which is. 一般式（Ｉ）において、Ｒ²が

である、請求項１記載の感光性樹脂組成物。 In general formula (I), R ² is

The photosensitive resin composition of Claim 1 which is. 一般式（Ｉ）において、Ｒ²が

である、請求項１記載の感光性樹脂組成物。 In general formula (I), R ² is

The photosensitive resin composition of Claim 1 which is. 一般式（Ｉ）において、Ｒ²が

である、請求項１記載の感光性樹脂組成物。 In general formula (I), R ² is

The photosensitive resin composition of Claim 1 which is.