JP2005220716A - Permeable concrete block, permeable paved road using permeable concrete block, and construction method for permeable paved road - Google Patents

Permeable concrete block, permeable paved road using permeable concrete block, and construction method for permeable paved road Download PDF

Info

Publication number
JP2005220716A
JP2005220716A JP2004061324A JP2004061324A JP2005220716A JP 2005220716 A JP2005220716 A JP 2005220716A JP 2004061324 A JP2004061324 A JP 2004061324A JP 2004061324 A JP2004061324 A JP 2004061324A JP 2005220716 A JP2005220716 A JP 2005220716A
Authority
JP
Japan
Prior art keywords
permeable
roadbed
concrete block
paved road
permeable concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2004061324A
Other languages
Japanese (ja)
Inventor
Kazutoshi Nasu
和俊 那須
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WAVE KK
Original Assignee
WAVE KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WAVE KK filed Critical WAVE KK
Priority to JP2004061324A priority Critical patent/JP2005220716A/en
Publication of JP2005220716A publication Critical patent/JP2005220716A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide permeable concrete blocks, a permeable paved road utilizing the water permeable concrete blocks and installation method for the water permeable paved road utilizing the permeability of recycled glass sand to the maximum degree which is utilized effectively and to the maximum amount by utilizing the glass sand recycled from a mixture of crushed earthenware, glass bottles or the like which are discharged from homes and factories and collected daily by autonomous bodies or traders. <P>SOLUTION: The permeable paved road 20 utilizing the water permeable concrete blocks is approximately composed of a subgrade 22, a lower subbase 24 including the recycled crushed stone, an upper subbase 26 with the recycled glass sand used as a sand cushion, and the permeable concrete blocks 10 in which the recycled glass sand is used as aggregate. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

本発明は、家庭や工場から排出されて各自治体や業者等で回収される、瀬戸物やガラスビン等を砕いた混合物を有効利用した、透水性コンクリートブロック及び透水性コンクリートブロックを利用した透水性舗装道路、透水性舗装道路敷設方法に関する。  The present invention is a water permeable concrete block and a water permeable paved road using a water permeable concrete block, which is effectively used as a mixture of crushed Seto and glass bottles, etc., discharged from homes and factories and collected by local governments and contractors. The present invention relates to a method for laying a permeable paved road.

従来、家庭や工場から排出されて各自治体や業者等で回収される瀬戸物やガラスビン等は、不純物を取り除かれ再生ガラス砂（ガラスカレット）としてガラス原料に再利用されている。  Conventionally, Seto, glass bottles, etc. discharged from homes and factories and collected by local governments, contractors, etc., are removed from impurities and recycled as glass raw materials as recycled glass sand (glass cullet).

また、特許文献１には、使用済みガラス容器等から得られるガラスカレットとエポキシ樹脂の混合物から道路舗装構造体を製造する方法が開示されている。  Patent Document 1 discloses a method for producing a road pavement structure from a mixture of glass cullet and epoxy resin obtained from a used glass container or the like.

特開２００２−２９４６１５    JP 2002-294615 A

しかしながら、この特許文献１で使用されるガラスカレットは、日々排出される瀬戸物やガラスビン等のごく一部であり、その利用量は限られたものとなっている。また、舗装道路構造体の再生ガラス砂を利用した下地層にはエポキシ樹脂が混合物されているため、透水性が担保されないという問題がある。  However, the glass cullet used in this Patent Document 1 is only a small part of the seto and glass bottles that are discharged every day, and its usage is limited. Moreover, since the epoxy resin is mixed with the ground layer using the recycled glass sand of a paved road structure, there exists a problem that water permeability is not ensured.

また、資源の有効利用と環境保全のために、建設現場や解体現場から日々排出されるコンクリート廃材塊やレンガ廃材を大量に再利用する方法が求められている。  In addition, in order to effectively use resources and preserve the environment, there is a need for a method of reusing a large amount of concrete waste lump and brick waste discharged daily from construction sites and demolition sites.

そこで本発明は、家庭や工場から排出されて各自治体や業者等で日々回収される、瀬戸物やガラスビン等を砕いた混合物から再生された再生ガラス砂を大量に有効利用すると共に、再生ガラス砂の透水性を最大限利用した、透水性コンクリートブロック及び透水性コンクリートブロックを利用した透水性舗装道路、透水性舗装道路敷設方法を提供することを目的とする。  Therefore, the present invention effectively uses a large amount of recycled glass sand that is discharged from homes and factories and collected daily by local governments and contractors, etc. An object of the present invention is to provide a water-permeable concrete block that uses water permeability to the maximum, a water-permeable paved road using the water-permeable concrete block, and a method for laying a water-permeable paved road.

上述の課題を解決し目的を達成するため、この発明に係わる透水性コンクリートブロックは、請求項１の記載によれば、コンクリートの骨材に再生ガラス砂を含むことを特徴とする。  In order to solve the above-described problems and achieve the object, a water-permeable concrete block according to the present invention is characterized in that recycled aggregate is included in concrete aggregate.

また、この発明に係わる透水性コンクリートブロックは、請求項２の記載によれば、前記再生ガラス砂は、陶器による茶褐色系の色を呈することを特徴とする。  According to a second aspect of the water-permeable concrete block according to the present invention, the recycled glass sand exhibits a brownish brown color due to earthenware.

また、この発明に係わる透水性コンクリートブロックは、請求項３の記載によれば、舗装道路に使用する透水性コンクリートブロックであって、コンクリートの骨材に通常の砂を使用した表層と、コンクリートの骨材に再生ガラス砂を混入した基層とからなることを特徴とする。  Further, the permeable concrete block according to the present invention is a permeable concrete block used for a paved road according to claim 3, wherein the surface layer using ordinary sand for the aggregate of the concrete, It consists of a base layer in which recycled glass sand is mixed into the aggregate.

また、この発明に係わる透水性コンクリートブロックは、請求項４の記載によれば、透水係数が０．０８ｃｍ／秒以上であることを特徴とする。  According to a fourth aspect of the present invention, the water permeable concrete block according to the present invention has a water permeability coefficient of 0.08 cm / second or more.

また、この発明に係わる透水性舗装道路は、請求項５の記載によれば、路床と、前記路床上に敷かれる砕石からなる下層路盤と、前記下層路盤上に敷かれるサンドクッションからなる上層路盤と、舗装路面を形成し、コンクリートの骨材に再生ガラス砂を含む透水性コンクリートブロックとからなることを特徴とする。  According to claim 5, the permeable paved road according to the present invention is an upper layer comprising a road bed, a lower road bed made of crushed stones laid on the road bed, and a sand cushion laid on the lower road bed. It is characterized by comprising a roadbed and a water-permeable concrete block that forms a paved road surface and contains recycled glass sand in a concrete aggregate.

また、この発明に係わる透水性舗装道路は、請求項６の記載によれば、路床と、前記路床上に敷かれる砕石からなる下層路盤と、前記下層路盤上に敷かれ、再生ガラス砂を含むサンドクッションからなる上層路盤と、舗装路面を形成し、コンクリートの骨材に再生ガラス砂を含む透水性コンクリートブロックとからなることを特徴とする。  According to a sixth aspect of the present invention, the permeable pavement according to the present invention is a roadbed, a lower roadbed made of crushed stones laid on the roadbed, and a recycled glass sand laid on the lower roadbed. It is characterized by comprising an upper layer roadbed comprising a sand cushion, and a water permeable concrete block that forms a paved road surface and contains recycled glass sand in a concrete aggregate.

また、この発明に係わる透水性舗装道路は、請求項７の記載によれば、前記下層路盤に再生砕石を含むことを特徴とする。  According to a seventh aspect of the present invention, the permeable paved road according to the present invention is characterized in that the lower roadbed includes recycled crushed stone.

また、この発明に係わる透水性舗装道路敷設方法は、請求項８の記載によれば、路床に砕石からなる下層路盤を敷設し、前記下層路盤上に再生ガラス砂を含むサンドクッションを上層路盤として敷設し、舗装上層路盤に路面を形成する透水性コンクリートブロックを敷設したことを特徴とする。  According to the eighth aspect of the present invention, the permeable pavement road laying method is such that a lower layer roadbed made of crushed stone is laid on the roadbed, and a sand cushion containing recycled glass sand is placed on the lower layer roadbed. It is characterized by laying a permeable concrete block that forms a road surface on a pavement upper layer roadbed.

この発明により、瀬戸物やガラスビン等から再生された再生ガラス砂を有効利用して、単位舗装面あたりの再生ガラス砂の使用量を増加させることできるので、再生ガラス砂の利用率の拡大を達成することができる。  According to the present invention, it is possible to effectively use recycled glass sand regenerated from a seto thing or a glass bottle to increase the amount of recycled glass sand used per unit pavement surface, thereby achieving an increase in the utilization rate of recycled glass sand. be able to.

また、この発明により、再生ガラス砂の透水性を最大限利用して、雨天等で舗装面にできる水溜り防止を達成した透水性コンクリートブロック及び透水性コンクリートブロックを利用した透水性舗装道路、透水性舗装道路敷設方法を提供することができる。  Further, according to the present invention, the water permeability of the recycled glass sand is maximized, and the water permeable concrete block which has achieved the prevention of water accumulation that can be formed on the pavement surface in rainy weather, the water permeable paved road using the water permeable concrete block, the water permeable A method for laying a pavement road can be provided.

さらに、この発明では、再生ガラス砂に瀬戸物等の陶器を使用することで、ガラスのみから再生された再生ガラス砂に多い緑色系を茶褐色系にすることができるので、ガラスから再生された再生ガラス砂から受けるイメージである手を傷つけるや危険であるといった印象をなくす効果がある。  Furthermore, in the present invention, the use of pottery such as Seto for regenerated glass sand allows the green color of the regenerated glass sand regenerated from only the glass to be brown, so that the regenerated glass regenerated from glass. It has the effect of eliminating the impression that it is dangerous or hurt the hand that is the image received from the sand.

また、この発明により、建設現場や解体現場から日々排出されるコンクリート廃材塊やレンガ廃材を大量に再利用することが可能となる。  In addition, according to the present invention, it is possible to reuse a large amount of concrete waste lump and brick waste discharged every day from the construction site and the demolition site.

＜第一の実施例＞
以下に本発明を図面に従って説明する。
本発明の第一の実施例を図１及び図２に従って説明する。図１は、本発明の透水性コンクリートブロック１０の実施例を示す断面図である。
本発明の透水性コンクリートブロック１０は、概略直方体の形状であり、基層１２と表層１４から概略構成されている。<First embodiment>
The present invention will be described below with reference to the drawings.
A first embodiment of the present invention will be described with reference to FIGS. FIG. 1 is a cross-sectional view showing an embodiment of a water-permeable concrete block 10 of the present invention.
The water-permeable concrete block 10 of the present invention has a substantially rectangular parallelepiped shape, and is generally composed of a base layer 12 and a surface layer 14.

基層１２のコンクリートは、骨材に再生ガラス砂が使用されている。この再生ガラス砂は、各自治体等で回収された瀬戸物やガラスビン等から不純物を取り除いて加工されたものである。  The concrete of the base layer 12 uses recycled glass sand as an aggregate. This recycled glass sand is processed by removing impurities from the Seto and glass bottles collected by local governments.

表層１４のコンクリートは、骨材に通常の砂が使用されているが、透水性が担保されるように粗骨材が混入されている。また、表層１４は舗装道路敷設後に路面となるので、表面の摩擦抵抗を大きくする加工や、彩色加工が施されている。  As for the concrete of the surface layer 14, although normal sand is used for the aggregate, coarse aggregate is mixed so that water permeability is ensured. Further, since the surface layer 14 becomes a road surface after laying a paved road, the surface layer 14 is subjected to processing for increasing the frictional resistance of the surface and coloring.

本発明の透水性コンクリートブロックを使用した路面舗装では、１平方メートル当たりに約４０ｋｇ（ワインビン約１００本分）の再生ガラス砂が使用されている。このように本発明の透水性コンクリートブロックは、瀬戸物やガラスビン等の資源の有効利用、省エネルギー及びリサイクルといった社会ニーズに応えた、環境に配慮した舗装材である。  In road pavement using the water-permeable concrete block of the present invention, about 40 kg (about 100 wine bottles) of recycled glass sand is used per square meter. As described above, the water-permeable concrete block of the present invention is an environment-friendly pavement material that meets social needs such as effective use of resources such as Seto and glass bottles, energy saving, and recycling.

本発明の透水性コンクリートブロックの透水係数は、定水位型透水試験機での計測で、平均０．０８９ｃｍ／秒となっている。透水係数の規格値は０．０１ｃｍ／秒であるので、本発明の透水性コンクリートブロックは非常に優れた透水性を有している。  The permeability coefficient of the water-permeable concrete block of the present invention is 0.089 cm / second on average as measured by a constant water level type permeability tester. Since the standard value of the water permeability coefficient is 0.01 cm / second, the water-permeable concrete block of the present invention has very good water permeability.

図２は、本発明で使用される再生ガラス砂の溶出試験結果である。この図中で＜で示される数値は、定量下限値未満を示している。この図２の通り、本発明で使用される再生ガラス砂は、その安全性が確認されている。  FIG. 2 is a dissolution test result of recycled glass sand used in the present invention. The numerical value indicated by <in this figure indicates less than the lower limit of quantification. As shown in FIG. 2, the safety of the recycled glass sand used in the present invention has been confirmed.

尚、第一の実施例における透水性コンクリートブロックにおいて、表層１４が施されていると説明したが、本発明の透水性コンクリートブロックはこの構成に限られるものではなく、基層１２のみで構成されてもよいことは言うまでもない。特に表層１４を設けられていない場合、本発明の再生ガラス砂には瀬戸物等の陶器が使用されているので、ガラスのみから再生された再生ガラス砂に多い緑色系を茶褐色系にすることができるので、ガラスから再生された再生ガラス砂から受けるイメージである手を傷つけるや危険であるといった印象をなくす効果がある。  In the permeable concrete block in the first embodiment, the surface layer 14 has been described. However, the permeable concrete block of the present invention is not limited to this configuration, and is configured only by the base layer 12. Needless to say. In particular, when the surface layer 14 is not provided, pottery such as Seto is used for the regenerated glass sand of the present invention, so that the green color that is often found in the regenerated glass sand regenerated only from glass can be changed to brown. Therefore, there is an effect of eliminating the impression that the hand, which is an image received from recycled glass sand reproduced from glass, is injured or dangerous.

また、第一の実施例における透水性コンクリートブロックの表層１４は、基層１２の片面のみに施されていると説明したが、本発明の透水性コンクリートブロックはこの構成に限られるものではなく、基層１２の両面に施されてもよいことは言うまでもない。  Moreover, although the surface layer 14 of the water-permeable concrete block in the first embodiment has been described as being applied only to one side of the base layer 12, the water-permeable concrete block of the present invention is not limited to this configuration. Needless to say, it may be applied to both sides of the twelve.

さらに、第一の実施例における透水性コンクリートブロックは、概略直方体の形状であると説明したが、本発明の透水性コンクリートブロックはこの構成に限られるものではなく、インターロッキングブロックとして形状加工されても良いことは言うまでもない。  Furthermore, although the water-permeable concrete block in the first embodiment has been described as having a substantially rectangular parallelepiped shape, the water-permeable concrete block of the present invention is not limited to this configuration, and is shaped as an interlocking block. It goes without saying that it is also good.

またさらに、第一の実施例における透水性コンクリートブロックの基層１２に骨材として使用される再生ガラス砂は、瀬戸物やガラスビン等から加工されたものであると説明したが、本発明で使用される再生ガラス砂はこれに限られるものではなく、磁器片等のガラス質を含むものであれば何を使用しても良いことは言うまでもない。  Furthermore, although the recycled glass sand used as the aggregate for the base layer 12 of the water-permeable concrete block in the first embodiment has been described as being processed from a seto or a glass bottle, it is used in the present invention. Needless to say, recycled glass sand is not limited to this, and any glass sand containing porcelain pieces or the like may be used.

さらにまた、第一の実施例における透水性コンクリートブロックの基層１２は、骨材に再生ガラス砂が使用されていると説明したが、本発明の透水性コンクリートブロックはこの構成に限られるものではなく、透水性が担保される範囲内で骨材に通常の砂を混入しても良いことは言うまでもない。  Furthermore, although the base layer 12 of the water-permeable concrete block in the first embodiment has been described as using recycled glass sand as an aggregate, the water-permeable concrete block of the present invention is not limited to this configuration. Needless to say, ordinary sand may be mixed into the aggregate within a range in which water permeability is ensured.

＜第二の実施例＞
本発明の第二の実施例を図３に従って説明する。図３は、本発明の透水性コンクリートブロックを利用した透水性舗装道路２０の実施例を示す斜視図である。<Second Example>
A second embodiment of the present invention will be described with reference to FIG. FIG. 3 is a perspective view showing an embodiment of the permeable paved road 20 using the permeable concrete block of the present invention.

本発明の透水性コンクリートブロックを利用した透水性舗装道路２０は、路床２２と、下層路盤２４と、上層路盤２６と、透水性コンクリートブロック１０とから概略構成されている。  The water-permeable paved road 20 using the water-permeable concrete block of the present invention is roughly composed of a road bed 22, a lower road bed 24, an upper road bed 26, and the water-permeable concrete block 10.

路床２２は、透水性舗装道路が施工される通常の路床であり、その施工のために道路舗装用重機等により平らにならされている。  The roadbed 22 is a normal roadbed on which a water-permeable paved road is constructed, and is flattened by a heavy machine for road paving for the construction.

路床２２上に敷設される下層路盤２４は、岩石破砕石や再生砕石等の透水性や排水性の高く、また、耐過重性の高い砕石で構成されている。尚、再生砕石には、建設現場や解体現場から排出されるコンクリート廃材塊やレンガ廃材を破砕機で細かく砕いて不純物を取り除いてから粒度調整されたものが使用されている。この再生砕石を利用することにより、コンクリート廃材塊やレンガ廃材を大量に再利用することが可能となる。  The lower roadbed 24 laid on the roadbed 22 is composed of crushed stones having high water permeability and drainage properties such as rock crushed stones and reclaimed crushed stones and having high overload resistance. In addition, the recycled crushed stone is used after the particle size is adjusted after finely pulverizing the concrete waste lump and brick waste discharged from the construction site and demolition site with a crusher to remove impurities. By using this recycled crushed stone, it becomes possible to reuse a large amount of concrete waste lump and brick waste.

下層路盤２４上に敷設される上層路盤２６は、本発明の透水性コンクリートブロックでも使用されている再生ガラス砂がサンドクッションとして使用されている。このサンドクッションは、透水性舗装道路の完成時に水平面を確保するための平面度の微調整にも利用されている。また、このサンドクッションに再生ガラス砂を使用することにより、高い透水性が担保されている。  Recycled glass sand, which is also used in the permeable concrete block of the present invention, is used as a sand cushion for the upper layer roadbed 26 laid on the lower layer roadbed 24. This sand cushion is also used for fine adjustment of flatness to secure a horizontal plane when a permeable paved road is completed. Moreover, high water permeability is ensured by using recycled glass sand for this sand cushion.

上層路盤２６上に敷設される透水性コンクリートブロック１０は、第一の実施例で説明した透水性コンクリートブロック１０が使用されている。尚、第二の実施例における透水性コンクリートブロックの形状は、インターロッキングブロックとして加工されている。このように、第二の実施例では、舗装道路の舗装面に本発明の透水性コンクリートブロック１０が利用されているので、雨天等で舗装面にできる水溜りを防止することができる。  As the permeable concrete block 10 laid on the upper layer roadbed 26, the permeable concrete block 10 described in the first embodiment is used. In addition, the shape of the water-permeable concrete block in a 2nd Example is processed as an interlocking block. As described above, in the second embodiment, the water-permeable concrete block 10 of the present invention is used on the paved surface of the paved road, so that it is possible to prevent water pools formed on the paved surface due to rain or the like.

さらに、この第二の実施例においては、上層路盤２６に再生ガラス砂が使用されているので、透水性や排水性を担保できるばかりでなく、単位舗装面あたりの再生ガラス砂の使用量を増加させることできるので、再生ガラス砂の利用率の拡大を達成することができる。  Furthermore, in this second embodiment, recycled glass sand is used for the upper layer base 26, so that not only water permeability and drainage can be ensured, but also the amount of recycled glass sand used per unit pavement surface is increased. Therefore, the utilization rate of recycled glass sand can be increased.

尚、第二の実施例における上層路盤２６は、サンドクッションとして再生ガラス砂が使用されていると説明したが、本発明の透水性コンクリートブロックを利用した透水性舗装道路はこの構成に限られるものではなく、透水性が担保される範囲内でサンドクッションに通常の砂を混入しても良いことは言うまでもない。  In addition, although the upper-layer roadbed 26 in the 2nd Example demonstrated that the recycled glass sand was used as a sand cushion, the water-permeable paved road using the water-permeable concrete block of this invention is restricted to this structure. However, it goes without saying that normal sand may be mixed in the sand cushion within a range in which water permeability is ensured.

また、第二の実施例における透水性舗装道路及び透水性舗装道路敷設方法は、路床に下層路盤及び上層路盤を敷設し、その上に透水性コンクリートブロックを敷設すると説明したが、本発明はこの構成に限られるものではなく、透水性舗装道路及び透水性舗装道路敷設方法において、本発明の透水性コンクリートブロックを利用すると共に下層路盤や上層路盤の一部に再生ガラス砂を使用するものであれば、その効果を達成できることは言うまでもない。  Further, the permeable pavement road and the permeable pavement road laying method in the second embodiment have been described as laying the lower layer roadbed and the upper layer roadbed on the roadbed and laying the permeable concrete block thereon, but the present invention Not limited to this configuration, in the permeable paved road and the permeable paved road laying method, the permeable concrete block of the present invention is used and recycled glass sand is used for a part of the lower roadbed and the upper roadbed. Needless to say, that effect can be achieved.

本発明の透水性コンクリートブロックを示す断面図である。It is sectional drawing which shows the water-permeable concrete block of this invention. 本発明で使用される再生ガラス砂の溶出試験結果である。It is an elution test result of the recycled glass sand used by this invention. 本発明の透水性コンクリートブロックを利用した透水性舗装道路を示す斜視図である。It is a perspective view which shows the water-permeable paved road using the water-permeable concrete block of this invention.

符号の説明Explanation of symbols

１０ 透水性コンクリートブロック
１２ 基層
１４ 表層
２０ 透水性コンクリートブロックを利用した透水性舗装道路
２２ 路床
２４ 下層路盤
２６ 上層路盤DESCRIPTION OF SYMBOLS 10 Water-permeable concrete block 12 Base layer 14 Surface layer 20 Water-permeable paved road 22 using water-permeable concrete block Subgrade 24 Lower roadbed 26 Upper roadbed

Claims (8)

舗装道路に使用する透水性コンクリートブロックであって、コンクリートの骨材に再生ガラス砂を含むことを特徴とする透水性コンクリートブロック。  A permeable concrete block for use on a paved road, wherein the aggregate of concrete includes recycled glass sand. 前記再生ガラス砂は、陶器による茶褐色系の色を呈することを特徴とする請求項１に記載の透水性コンクリートブロック。  The permeable concrete block according to claim 1, wherein the recycled glass sand exhibits a brownish brown color due to earthenware. 舗装道路に使用する透水性コンクリートブロックであって、
コンクリートの骨材に通常の砂を使用した表層と、
コンクリートの骨材に再生ガラス砂を混入した基層とからなることを特徴とする透水性コンクリートブロック。A permeable concrete block used on paved roads,
A surface layer using normal sand for concrete aggregate,
A permeable concrete block comprising a base layer in which recycled glass sand is mixed with concrete aggregate. 透水係数が０．０８ｃｍ／秒以上であることを特徴とする請求項１乃至請求項３に記載の透水性コンクリートブロック。  The water permeable concrete block according to claim 1, wherein the water permeability coefficient is 0.08 cm / second or more. 透水性コンクリートブロックを利用した透水性舗装道路であって、
路床と、
前記路床上に敷かれる砕石からなる下層路盤と、
前記下層路盤上に敷かれるサンドクッションからなる上層路盤と、
舗装路面を形成し、コンクリートの骨材に再生ガラス砂を含む透水性コンクリートブロックとからなることを特徴とする透水性舗装道路。It is a permeable paved road using permeable concrete blocks,
The roadbed,
A lower roadbed made of crushed stones laid on the roadbed;
An upper layer roadbed made of a sand cushion laid on the lower layer roadbed,
A permeable paved road characterized by comprising a permeable concrete block that forms a paved road surface and includes recycled glass sand in a concrete aggregate. 透水性コンクリートブロックを利用した透水性舗装道路であって、
路床と、
前記路床上に敷かれる砕石からなる下層路盤と、
前記下層路盤上に敷かれ、再生ガラス砂を含むサンドクッションからなる上層路盤と、
舗装路面を形成し、コンクリートの骨材に再生ガラス砂を含む透水性コンクリートブロックとからなることを特徴とする透水性舗装道路。It is a permeable paved road using permeable concrete blocks,
The roadbed,
A lower roadbed made of crushed stones laid on the roadbed;
An upper layer roadbed which is laid on the lower layer roadbed and comprises a sand cushion containing recycled glass sand;
A permeable paved road characterized by comprising a permeable concrete block that forms a paved road surface and includes recycled glass sand in a concrete aggregate. 前記下層路盤に再生砕石を含むことを特徴とする請求項５又は請求項６に記載の透水性舗装道路。  The permeable paved road according to claim 5 or 6, wherein the lower roadbed includes recycled crushed stone. 路床に砕石からなる下層路盤を敷設し、
前記下層路盤上に再生ガラス砂を含むサンドクッションを上層路盤として敷設し、
舗装上層路盤に路面を形成する透水性コンクリートブロックを敷設したことを特徴とする透水性舗装道路敷設方法。Laying the lower roadbed made of crushed stone on the roadbed,
Laying a sand cushion containing recycled glass sand on the lower roadbed as the upper roadbed,
A permeable pavement road laying method characterized by laying a permeable concrete block for forming a road surface on a pavement upper layer roadbed.
JP2004061324A 2004-02-05 2004-02-05 Permeable concrete block, permeable paved road using permeable concrete block, and construction method for permeable paved road Pending JP2005220716A (en)