JP2005194634A - Inorganic fiber mat - Google Patents

Inorganic fiber mat Download PDF

Info

Publication number
JP2005194634A
JP2005194634A JP2003434878A JP2003434878A JP2005194634A JP 2005194634 A JP2005194634 A JP 2005194634A JP 2003434878 A JP2003434878 A JP 2003434878A JP 2003434878 A JP2003434878 A JP 2003434878A JP 2005194634 A JP2005194634 A JP 2005194634A
Authority
JP
Japan
Prior art keywords
inorganic fiber
composition
fiber mat
parts
inorganic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2003434878A
Other languages
Japanese (ja)
Inventor
Manabu Iizuka
学 飯塚
Takao Uzawa
孝夫 鵜澤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Asahi Fiber Glass Co Ltd
Original Assignee
Asahi Fiber Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Fiber Glass Co Ltd filed Critical Asahi Fiber Glass Co Ltd
Priority to JP2003434878A priority Critical patent/JP2005194634A/en
Publication of JP2005194634A publication Critical patent/JP2005194634A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide an inorganic fiber mat generating a small amount of aldehydes without causing problems of corrosion on metals of an apparatus for production due to pH of a solution. <P>SOLUTION: The inorganic fiber mat is obtained by applying a binder consisting essentially of a phenol resin, forming and curing the binder. In the inorganic fiber mat, a composition for scavenging the aldehydes containing at least three components of a sulfite, an inorganic phosphate and an organic acid salt is converted into an aqueous solution at pH≤9.5 and applied to the inorganic fiber so as to afford 0.1-20 pts.mass expressed in terms of solid ratio based on 100 pts. mass of the applied binder. The amount of the released formaldehyde according to tests on the amount of the released formaldehyde based on a desiccator method of JIS-A5908 is ≤0.20 mg/liter. Urea is preferably further contained in the composition for scavenging the aldehydes. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

本発明は、建築用の断熱材、吸音材等として用いられる無機質繊維マットに関し、更に詳しくは、アルデヒド類の放出量が少ない無機質繊維マットに関する。   TECHNICAL FIELD The present invention relates to an inorganic fiber mat used as a heat insulating material for buildings, a sound absorbing material, and the like, and more particularly to an inorganic fiber mat that emits less aldehydes.

従来、グラスウール、ロックウール等の無機質繊維からなる無機質繊維マットは産業用や住宅用の断熱材や吸音材に広く用いられている。そして、この無機質繊維マットは一般に水溶性フェノール樹脂を主成分とする結合剤によって繊維同士が固定されマット状に成形されて製造されている。   Conventionally, inorganic fiber mats made of inorganic fibers such as glass wool and rock wool have been widely used for industrial and residential heat insulating materials and sound absorbing materials. In general, the inorganic fiber mat is manufactured by fixing the fibers to each other with a binder mainly composed of a water-soluble phenol resin and molding the fiber into a mat shape.

結合剤の主成分である水溶性フェノール樹脂には、架橋剤として一般的にホルムアルデヒド等のアルデヒド類が使用されている。そして、このアルデヒド類は、結合剤を加熱硬化するときに未反応のアルデヒド類、及び、水溶性フェノール樹脂に結合しているアルデヒド類の一部が無機質繊維マットの中に残留する。また、硬化した後も、結合剤の加水分解や縮合反応の進行によってもアルデヒド類が発生する。よって、これらのアルデヒド類が、製造後の無機質繊維マットの表面や側面から極微量放出されることになる。   Aldehydes such as formaldehyde are generally used as a crosslinking agent for the water-soluble phenol resin which is the main component of the binder. As for the aldehydes, unreacted aldehydes and a part of the aldehydes bonded to the water-soluble phenol resin remain in the inorganic fiber mat when the binder is heated and cured. In addition, even after curing, aldehydes are also generated by the hydrolysis of the binder and the progress of the condensation reaction. Therefore, a very small amount of these aldehydes is released from the surface and side surfaces of the inorganic fiber mat after production.

このアルデヒド類の外部への放出量は、住宅等への施工後には人体への影響が無い量である。しかし、無機質繊維マットは保管や輸送の効率を上げるために、製品は一定数量以上の無機質繊維マットをまとめて密封梱包される。更に多量の無機質繊維マットを圧縮して密封梱包する場合もある。このため、時間経過とともに、無機質繊維マットから極微量のアルデヒド類が放出されて包装内に蓄積される。この蓄積されたアルデヒド類は開封時に外部に放出するため、無機質繊維マットからのアルデヒド類の放出量は極力低いことが要求される。   The amount of aldehydes released to the outside is an amount that does not affect the human body after construction on a house or the like. However, in order to increase the efficiency of storage and transportation of inorganic fiber mats, products are sealed and packaged together with a certain number or more of inorganic fiber mats. Further, a large amount of inorganic fiber mat may be compressed and hermetically packed. For this reason, with the passage of time, a very small amount of aldehydes are released from the inorganic fiber mat and accumulated in the package. Since the accumulated aldehydes are released to the outside when opened, the amount of aldehydes released from the inorganic fiber mat is required to be as low as possible.

無機質繊維マットからのアルデヒド類の放出量を少なくする方法としては、水溶性フェノール樹脂中のアルデヒド類を低減する方法があり、その従来技術としては、水溶性フェノール樹脂を製造する際の反応温度、反応時間の最適化や、フェノール類とアルデヒド類の反応モル比の最適化によって、未反応のアルデヒド類を低減させる方法がある。   As a method of reducing the amount of aldehydes released from the inorganic fiber mat, there is a method of reducing aldehydes in the water-soluble phenol resin, and as its conventional technology, the reaction temperature when producing the water-soluble phenol resin, There are methods for reducing unreacted aldehydes by optimizing the reaction time and optimizing the reaction molar ratio of phenols and aldehydes.

また、他の方法として、無機質繊維マットを通風の良い場所に保管し、経時的にアルデヒド類を拡散させる方法等も知られている。   As another method, a method of storing an inorganic fiber mat in a well-ventilated place and diffusing aldehydes with time is also known.

更には、無機質繊維マットにホルムアルデヒドと反応してこれを捕集する、いわゆるアルデヒド類捕捉組成物を付着させることでアルデヒド類の放出量を低減させる方法も知られている。例えば、特許文献１には、ホルムアルデヒドに代表されるアルデヒド類捕捉組成物として、尿素、亜硫酸塩、及び無機性リン酸塩の３成分を少なくとも含んだ組成物、もしくは尿素、亜硫酸塩、及び有機酸塩の３成分を少なくとも含んだ組成物が開示されており、前記アルデヒド類捕捉組成物はホルムアルデヒドの捕捉効果、金属腐食の抑制効果に優れていることが記載されている。
特開２００２−３３１５０４号公報 Furthermore, a method for reducing the amount of aldehydes released by attaching a so-called aldehyde-capturing composition that reacts with and collects formaldehyde on an inorganic fiber mat is also known. For example, Patent Document 1 discloses a composition containing at least three components of urea, sulfite, and inorganic phosphate, or urea, sulfite, and an organic acid as an aldehyde capture composition represented by formaldehyde. A composition containing at least three salt components is disclosed, and it is described that the aldehyde capturing composition is excellent in formaldehyde capturing effect and metal corrosion suppressing effect.
JP 2002-331504 A

上記従来技術のうち、水溶性フェノール樹脂を製造する際の反応条件を最適化する方法においては、製造条件の許容範囲が狭くなることから製造コストの増大に繋がるという問題がある。また、反応モル比の最適化は、無機質繊維マットの製造工程において、熱分解により発生するフェノール樹脂中の低分子量体を排気中から除去処理する量の増加、あるいは結合剤の調合タンク及び送液配管中でのフェノール樹脂中の多核体の析出等のトラブルにも繋がることから容易でない。   Among the prior arts described above, the method for optimizing the reaction conditions for producing a water-soluble phenol resin has a problem that the manufacturing cost is increased because the allowable range of the manufacturing conditions is narrowed. In addition, the optimization of the reaction molar ratio can be achieved by increasing the amount of removal of low molecular weight substances in the phenol resin generated by thermal decomposition from the exhaust in the manufacturing process of the inorganic fiber mat, It is not easy because it leads to troubles such as precipitation of polynuclear substances in the phenolic resin in the piping.

また、通風、保管によって経時的にアルデヒド類を拡散させる方法では、無機質繊維マットはかさ密度が小さいので、大きな保管スペース及び長期の保管を必要とするため、経済的でないという問題がある。   Moreover, in the method of diffusing aldehydes with time by ventilation and storage, since the inorganic fiber mat has a small bulk density, it requires a large storage space and long-term storage, which is not economical.

一方、アルデヒド類捕捉組成物を用いる方法のうち、上記の特許文献１における、尿素、亜硫酸塩、及び無機性リン酸塩の３成分系では、アルデヒド類の捕捉効果が不充分である。また、尿素、亜硫酸塩、及び有機酸塩の３成分系では、アルデヒド類の捕捉効果は向上するものの、無機質繊維マットへ付与する際のアルデヒド類捕捉組成物を含んだ水溶液のｐＨが高くなるため、無機質繊維マット製造工程の際、金属部品の腐食の発生といったトラブルを発生しやすいという問題がある。また、ｐＨが高いと、廃液処理方法によっては処理コストが増大するという問題もある。   On the other hand, among the methods using an aldehyde capture composition, the three-component system of urea, sulfite, and inorganic phosphate in Patent Document 1 described above has an insufficient aldehyde capture effect. Moreover, in the three-component system of urea, sulfite, and organic acid salt, although the effect of capturing aldehydes is improved, the pH of the aqueous solution containing the aldehydes-trapping composition when applied to the inorganic fiber mat is increased. In addition, there is a problem that troubles such as corrosion of metal parts are likely to occur during the inorganic fiber mat manufacturing process. Moreover, when pH is high, there also exists a problem that processing cost increases depending on a waste-liquid processing method.

したがって、本発明の目的は、アルデヒド類の放出量が充分に低減でき、かつ、アルデヒド類捕捉組成物を付与する際の水溶液のｐＨを低くすることができる、無機質繊維マットを得ることにある。   Accordingly, an object of the present invention is to obtain an inorganic fiber mat that can sufficiently reduce the amount of aldehydes released and that can lower the pH of an aqueous solution when the aldehydes-trapping composition is applied.

上記目的を達成するため、本発明は、主成分がフェノール樹脂である結合剤を付着させて成形、硬化した無機質繊維マットにおいて、前記付着した結合剤１００質量部に対して、亜硫酸塩、無機性リン酸塩、有機酸塩の３成分を少なくとも含むアルデヒド類捕捉組成物をｐＨ９．５以下の水溶液として、固形分比率で０．１〜２０質量部となるように前記無機質繊維に付着させて得られ、ＪＩＳ−Ａ５９０８のデシケーター法に基づいたホルムアルデヒド放出量試験によるホルムアルデヒド放出量が０．２０ｍｇ／リットル以下であることを特徴とする。   In order to achieve the above object, the present invention provides an inorganic fiber mat molded and cured by attaching a binder whose main component is a phenol resin, with respect to 100 parts by mass of the attached binder, sulfite, inorganic Obtained by adhering an aldehyde capturing composition containing at least three components of phosphate and organic acid salt as an aqueous solution having a pH of 9.5 or less to the inorganic fiber so that the solid content ratio is 0.1 to 20 parts by mass. The formaldehyde emission amount by the formaldehyde emission amount test based on the desiccator method of JIS-A5908 is 0.20 mg / liter or less.

本発明の無機質繊維マットに、アルデヒド類捕捉組成物として所定量の亜硫酸塩、無機性リン酸塩、有機酸塩の３成分を含んだ組成物を用いることで、ｐＨを９．５以下の水溶液として組成物を使用することができ、さらには優れたアルデヒド類の放出量抑制効果の持った無機質繊維マットを得ることができる。   An aqueous solution having a pH of 9.5 or less by using a composition containing a predetermined amount of three components of sulfite, inorganic phosphate, and organic acid salt as the aldehyde capturing composition for the inorganic fiber mat of the present invention. In addition, an inorganic fiber mat having an excellent effect of suppressing the amount of aldehydes released can be obtained.

亜硫酸塩は優れたアルデヒド類捕捉効果を備えているが、金属類を腐食発錆してしまうという問題がある。特許文献１の組成のように、亜硫酸塩に無機性リン酸塩を加えることで溶液時のｐＨを低く抑えることが可能となるが、アルデヒド類の捕捉効果は充分に得られない。また、亜硫酸塩に有機酸塩を加えることでアルデヒド類捕捉効果は向上できるが、溶液時のｐＨが高くなってしまう。その為、アルデヒド類捕捉組成物として所定量の亜硫酸塩、無機性リン酸塩及び有機酸塩を含んだ３成分系とすることにより、充分なアルデヒド類捕捉効果を得ながら、製造装置の金属腐食の問題も解消することができる。   Although sulfite has an excellent aldehyde capturing effect, it has a problem of corroding and rusting metals. As in the composition of Patent Document 1, it is possible to keep pH at the time of solution low by adding inorganic phosphate to sulfite, but the effect of capturing aldehydes cannot be sufficiently obtained. Moreover, although an aldehyde capture | acquisition effect can be improved by adding organic acid salt to sulfite, pH at the time of a solution will become high. Therefore, by using a three-component system containing a predetermined amount of sulfite, inorganic phosphate, and organic acid salt as the aldehyde capture composition, the metal corrosion of the production equipment can be obtained while obtaining a sufficient aldehyde capture effect. This problem can also be solved.

本発明においては、アルデヒド類捕捉剤に含まれる亜硫酸塩、無機性リン酸塩及び有機酸塩の固形分比率をそれぞれ、亜硫酸塩が６０〜９４質量部、無機性リン酸塩が３〜２０質量部、有機酸塩が３〜２０質量部含まれる組成物とすることが好ましい。これによれば、前記組成物を、高いホルムアルデヒド抑制効果を備え、かつ、ｐＨがより中性域に近い水溶液として使用することができるので、より効果の高いアルデヒド類捕捉組成物として前記組成物を使用することができ、本発明に好適に使用することができる。   In the present invention, the solid content ratios of sulfite, inorganic phosphate and organic acid salt contained in the aldehyde scavenger are 60 to 94 parts by mass of sulfite and 3 to 20 mass of inorganic phosphate, respectively. It is preferable that the composition contains 3 to 20 parts by mass of organic acid salt. According to this, since the composition can be used as an aqueous solution having a high formaldehyde-suppressing effect and having a pH close to a neutral range, the composition is used as a more effective aldehyde capturing composition. Can be used preferably in the present invention.

更に、本発明においては、アルデヒド類捕捉組成物として亜硫酸塩、無機性リン酸塩、有機酸塩及び尿素の４成分を少なくとも含んだ組成物を用いることも好ましい。尿素は亜硫酸塩と同様にアルデヒド類の捕捉効果に優れていることが知られている。そして、尿素は亜硫酸塩に比べ安価に入手することができる為、尿素を含む４成分系とすることにより、より安価なアルデヒド類捕捉組成物を用いることができる。この場合、アルデヒド類捕捉組成物中の亜硫酸塩、無機性リン酸塩、有機酸塩及び尿素の固形分比率がそれぞれ、亜硫酸塩が２０〜８０質量部、無機性リン酸塩が５〜２０質量部、有機酸塩が５〜２０質量部及び尿素が１０〜７０質量部含まれる組成物であることが好ましい。これにより、高いホルムアルデヒド抑制効果を備え、かつ、ｐＨがより中性域に近い水溶液として使用することができるので、より効果の高いアルデヒド類捕捉組成物として前記捕捉組成物を使用することができる。   Furthermore, in the present invention, it is also preferable to use a composition containing at least four components of sulfite, inorganic phosphate, organic acid salt and urea as the aldehyde capturing composition. Urea is known to be excellent in the effect of capturing aldehydes, like sulfite. And since urea can be obtained at a lower cost than sulfite, a cheaper aldehyde capture composition can be used by using a four-component system containing urea. In this case, the solid content ratio of sulfite, inorganic phosphate, organic acid salt and urea in the aldehyde capture composition is 20 to 80 parts by mass of sulfite and 5 to 20 mass of inorganic phosphate, respectively. It is preferable that the composition contains 5 to 20 parts by mass of organic acid salt and 10 to 70 parts by mass of urea. Thereby, since it can be used as an aqueous solution having a high formaldehyde-suppressing effect and having a pH closer to the neutral range, the scavenging composition can be used as a more effective aldehyde scavenging composition.

また、前記無機質繊維が、グラスウール又はロックウールである事が好ましい。これによれば、グラスウール又はロックウールは産業用や住宅用の断熱材や吸音材に広く用いられるので本発明に特に好適に用いることができる。   Moreover, it is preferable that the said inorganic fiber is glass wool or rock wool. According to this, glass wool or rock wool can be used particularly suitably in the present invention because it is widely used for industrial and residential heat insulating materials and sound absorbing materials.

本発明では、無機質繊維マットからのアルデヒド類の放出量を低減できるので、特に密封梱包された無機質繊維マット包装体を開封したときのアルデヒド類の放出量を極力低くすることができる。よって、住宅等の建築用断熱材、吸音材等として好適に使用することができる。さらには、ｐＨ９．５以下の水溶液としてアルデヒド類捕捉組成物を使用することができるので、無機質繊維マット製造工程における装置金属部の腐食といった諸問題を効果的に解決、防止することができる。   In the present invention, since the amount of aldehydes released from the inorganic fiber mat can be reduced, the amount of aldehydes released particularly when the sealed inorganic fiber mat package is opened can be minimized. Therefore, it can be suitably used as a heat insulating material for buildings, a sound absorbing material, and the like. Furthermore, since the aldehyde capture composition can be used as an aqueous solution having a pH of 9.5 or less, various problems such as corrosion of the metal part of the apparatus in the inorganic fiber mat manufacturing process can be effectively solved and prevented.

まず、本発明の無機質繊維マットについて説明する。
本発明に用いられる無機質繊維は、特に限定されず、通常の断熱吸音材に使用されている、グラスウール、ロックウール等を用いることができる。また、無機質繊維の繊維化方法は、火焔法、吹き飛ばし法、遠心法（ロータリー法）など各種の方法を用いることができる。さらに、無機質繊維マットの密度も通常の断熱材や吸音材に使用されている密度でよく、好ましくは５〜１００ｋｇ／ｍ３の範囲である。 First, the inorganic fiber mat of the present invention will be described.
The inorganic fiber used for this invention is not specifically limited, Glass wool, rock wool, etc. which are used for the usual heat insulation sound-absorbing material can be used. Moreover, various methods, such as a flame method, a blowing method, and a centrifugal method (rotary method), can be used for the fiberization method of an inorganic fiber. Furthermore, the density of the inorganic fiber mat may be the density used in ordinary heat insulating materials and sound absorbing materials, and is preferably in the range of 5 to 100 kg / m 3 .

また、本発明において上記の無機質繊維に付与する結合剤は、通常のグラスウールやロックウールに使用されているフェノール樹脂を主成分とするものである。このフェノール樹脂は、フェノール類とアルデヒド類との縮合反応によって得られる樹脂であり、フェノール類としては、フェノール、クレゾール、キシレノール、レゾルシン及びこれらの変性物が例示でき、アルデヒド類としては、ホルムアルデヒドの他、アセトアルデヒド、フルフラール、パラホルムアルデヒドが例示できる。この場合、フェノール類の一部をメラミン、メチロール化メラミン、尿素、メチロール化尿素のアルデヒド類と縮合反応する物質に置き換えてもよい。また、水系の結合剤に使用する点から、上記フェノール樹脂は水溶性であることが好ましい。   In the present invention, the binder to be added to the inorganic fiber is mainly composed of a phenol resin used in ordinary glass wool or rock wool. This phenol resin is a resin obtained by a condensation reaction of phenols and aldehydes. Examples of phenols include phenol, cresol, xylenol, resorcin, and modified products thereof. Examples of aldehydes include formaldehyde and the like. , Acetaldehyde, furfural, and paraformaldehyde. In this case, a part of the phenols may be replaced with a substance that undergoes a condensation reaction with aldehydes of melamine, methylolated melamine, urea, or methylolated urea. Moreover, it is preferable that the said phenol resin is water-soluble from the point used for an aqueous binder.

更に、結合剤は、主成分のフェノール樹脂以外に尿素、メラミン、ｐＨ調整剤、硬化促進剤、シランカップリング剤、着色剤、防塵剤等の添加剤を必要により加えても良い。結合剤は上記の各成分を常法にしたがって混合し、水を加えて所定の濃度に調整される。   Further, the binder may be added with additives such as urea, melamine, pH adjuster, curing accelerator, silane coupling agent, colorant, dustproof agent and the like, if necessary, in addition to the main component phenol resin. The binder is prepared by mixing each of the above components according to a conventional method and adding water to a predetermined concentration.

次に、本発明に使用するアルデヒド類捕捉組成物について説明する。
本発明に用いるアルデヒド類捕捉組成物は、亜硫酸塩、無機性リン酸塩及び有機酸塩の少なくとも３成分を含んだ組成物であり、好ましくは、亜硫酸塩、無機性リン酸塩、有機酸塩及び尿素の少なくとも４成分を含んだ組成物である。 Next, the aldehyde capturing composition used in the present invention will be described.
The aldehyde capture composition used in the present invention is a composition containing at least three components of sulfite, inorganic phosphate and organic acid salt, preferably sulfite, inorganic phosphate and organic acid salt. And a composition containing at least four components of urea.

亜硫酸塩の好ましい具体例としては、亜硫酸ナトリウム、亜硫酸カリウムが例示でき、なかでも亜硫酸ナトリウムが好適である。   Preferable specific examples of the sulfite include sodium sulfite and potassium sulfite, and sodium sulfite is particularly preferable.

無機性リン酸塩の好ましい具体例としては、例えば、リン酸二水素カリウム、リン酸水素二カリウム、リン酸二水素ナトリウム、リン酸水素二ナトリウムが挙げられる。なかでも特にリン酸水素二カリウムが好適である。   Preferable specific examples of the inorganic phosphate include, for example, potassium dihydrogen phosphate, dipotassium hydrogen phosphate, sodium dihydrogen phosphate, and disodium hydrogen phosphate. Of these, dipotassium hydrogen phosphate is particularly preferred.

有機酸塩の好ましい具体例としては、グルコン酸、コハク酸、クエン酸、酒石酸、乳酸、リンゴ酸、タンニン酸、グリコール酸、セバシン酸等のアルカリ金属塩及びアンモニウム塩が挙げられるが、なかでも特にグルコン酸ナトリウムが好適である。   Specific examples of preferred organic acid salts include alkali metal salts such as gluconic acid, succinic acid, citric acid, tartaric acid, lactic acid, malic acid, tannic acid, glycolic acid, and sebacic acid, and ammonium salts. Sodium gluconate is preferred.

上記の亜硫酸塩、無機性リン酸塩及び有機酸塩の３成分の配合割合は、それぞれの固形分比率を、亜硫酸塩が６０〜９４質量部、無機性リン酸塩が３〜２０質量部、有機酸塩が３〜２０質量部とするのが好ましく、亜硫酸塩が８０〜９０質量部、無機リン酸塩が５〜１０質量部、有機酸塩が５〜１０質量部とすることがより好ましい。   The blending ratio of the above three components of sulfite, inorganic phosphate and organic acid salt is 60 to 94 parts by mass of sulfite, 3 to 20 parts by mass of inorganic phosphate, The organic acid salt is preferably 3 to 20 parts by mass, the sulfite is 80 to 90 parts by mass, the inorganic phosphate is 5 to 10 parts by mass, and the organic acid salt is more preferably 5 to 10 parts by mass. .

亜硫酸塩が６０質量部未満の場合、アルデヒド類の捕捉効果が充分発揮できなくなるので好ましくなく、９４質量部を超えるとアルデヒド類捕捉組成物のｐＨを９．５以下とすることが困難となるので好ましくない。   When the amount of sulfite is less than 60 parts by mass, the effect of capturing aldehydes cannot be sufficiently exerted, which is not preferable. When the amount exceeds 94 parts by mass, it is difficult to adjust the pH of the aldehydes capturing composition to 9.5 or less. It is not preferable.

無機性リン酸塩が３質量部未満の場合、アルデヒド類捕捉組成物のｐＨを９．５以下とする事が困難となるので好ましくなく、２０質量部を超えるとアルデヒド類の捕捉効果が充分に発揮できなくなるので好ましくない。   If the inorganic phosphate is less than 3 parts by mass, it is difficult to adjust the pH of the aldehyde capture composition to 9.5 or less, and if it exceeds 20 parts by mass, the aldehyde capture effect is sufficiently high. It is not preferable because it cannot be exhibited.

有機酸塩が３質量部未満の場合はアルデヒド類の捕捉効果が充分に発揮できなくなるので好ましくなく、２０質量部を超えるとアルデヒド類捕捉組成物のｐＨを９．５以下とすることが困難となるので好ましくない。   When the organic acid salt is less than 3 parts by mass, the effect of capturing aldehydes cannot be sufficiently exhibited, which is not preferable. When the amount exceeds 20 parts by mass, it is difficult to adjust the pH of the aldehydes capturing composition to 9.5 or less. This is not preferable.

また、本発明においては、上記の３成分に更に尿素を加え、亜硫酸塩、無機性リン酸塩、有機酸及び尿素の４成分を含んだアルデヒド類捕捉組成物とすることが好ましい。この場合、それぞれの固形分比率を亜硫酸塩が２０〜８０質量部、無機性リン酸塩が５〜２０質量部、有機酸塩が５〜２０質量部及び尿素が１０〜７０質量部とするのが好ましい。   Moreover, in this invention, it is preferable to add urea further to said 3 component, and to set it as the aldehyde capture | acquisition composition containing 4 components of a sulfite, an inorganic phosphate, an organic acid, and urea. In this case, the solid content ratio is 20 to 80 parts by mass of sulfite, 5 to 20 parts by mass of inorganic phosphate, 5 to 20 parts by mass of organic acid salt, and 10 to 70 parts by mass of urea. Is preferred.

亜硫酸塩が２０質量部未満の場合、アルデヒド類の捕捉効果が充分発揮できなくなるので好ましくなく、８０質量部を超えるとアルデヒド類捕捉組成物のｐＨを９．５以下とすることが困難となるので好ましくない。   When the amount of sulfite is less than 20 parts by mass, the effect of capturing aldehydes cannot be sufficiently exerted, which is not preferable. It is not preferable.

無機性リン酸塩が５質量部未満の場合、アルデヒド類捕捉組成物のｐＨを９．５以下とする事が困難となるので好ましくなく、２０質量部を超えるとアルデヒド類の捕捉効果が充分に発揮できなくなるので好ましくない。   If the inorganic phosphate is less than 5 parts by mass, it is difficult to adjust the pH of the aldehyde capture composition to 9.5 or less, and if it exceeds 20 parts by mass, the aldehyde capture effect is sufficiently high. It is not preferable because it cannot be exhibited.

有機酸塩が５質量部未満の場合はアルデヒド類の捕捉効果が充分に発揮できなくなるので好ましくなく、２０質量部を超えるとアルデヒド類捕捉組成物のｐＨを９．５以下とすることが困難となるので好ましくない。   When the organic acid salt is less than 5 parts by mass, the effect of capturing aldehydes cannot be sufficiently exhibited, which is not preferable. When the amount exceeds 20 parts by mass, it is difficult to adjust the pH of the aldehydes capturing composition to 9.5 or less. This is not preferable.

また、尿素が７０質量部を超えるとアルデヒド類の捕捉効果が充分に発揮できなくなるので好ましくない。   Moreover, when urea exceeds 70 mass parts, since the capture effect of aldehydes cannot fully be exhibited, it is unpreferable.

上記のアルデヒド類捕捉組成物は、無機質繊維の表面に均一に付与するために、水溶液として配合される。   Said aldehyde capture | acquisition composition is mix | blended as aqueous solution, in order to provide uniformly on the surface of an inorganic fiber.

この場合、上記の水溶液の濃度は５〜３５質量％が好ましく、１０〜３０質量％がより好ましい。３５質量％を超える高濃度であると、該組成物の固形分が全て溶解せずに固形物として残る場合や、一度溶解した固形分が再度結晶となって析出する場合があり、無機質繊維へ付与することが困難となったり、均一に付与することが困難になるので好ましくない。また、５質量％未満の低濃度であると、アルデヒド類の化学的に分解する効果を得るために付与量を増加する必要があり、後述する重合反応炉で余分な水分を飛ばすための熱量が必要となるため、経済上好ましくない。水溶液の温度は、特に限定されず常温でもよいが、凍結、固形分の析出等が生じない温度範囲であることが好ましい。   In this case, the concentration of the aqueous solution is preferably 5 to 35% by mass, and more preferably 10 to 30% by mass. When the concentration is higher than 35% by mass, the solid content of the composition may not be completely dissolved and may remain as a solid material, or the solid content once dissolved may be crystallized again to form an inorganic fiber. Since it becomes difficult to apply or it becomes difficult to apply uniformly, it is not preferable. Further, if the concentration is less than 5% by mass, it is necessary to increase the applied amount in order to obtain an effect of chemically decomposing aldehydes. This is not preferable because it is necessary. The temperature of the aqueous solution is not particularly limited and may be room temperature, but is preferably within a temperature range in which freezing, precipitation of solids, and the like do not occur.

水溶液のｐＨは、９．５以下である必要があり、好ましくは７．０〜９．５である。ｐＨを前記範囲内で調整することにより、無機質繊維へ付与する工程において、噴霧器等の金属部品及び装置の腐食が少なくし、さらには廃液処理を容易に実施することができる。   The pH of the aqueous solution needs to be 9.5 or less, preferably 7.0 to 9.5. By adjusting the pH within the above range, in the step of imparting to the inorganic fibers, the corrosion of metal parts such as a sprayer and the apparatus is reduced, and the waste liquid treatment can be easily performed.

本発明のアルデヒド類捕捉組成物が捕捉するアルデヒド類としては、ホルムアルデヒド、アセトアルデヒドなどが例示できる。   Examples of aldehydes captured by the aldehyde capture composition of the present invention include formaldehyde and acetaldehyde.

次に、本発明の無機質繊維マットの好ましい製造方法について図面を用いて説明する。 図１は、本発明の無機質繊維マットの製造方法のうち、結合剤を付与する工程の直後でアルデヒド類捕捉組成物を付与する方法の一例を示す概５略工程図である。   Next, the preferable manufacturing method of the inorganic fiber mat of this invention is demonstrated using drawing. FIG. 1 is a schematic five-step process diagram illustrating an example of a method for applying an aldehyde capturing composition immediately after a step of applying a binder in the method for producing an inorganic fiber mat of the present invention.

図１の製造方法では、繊維化装置１から紡出された無機質繊維３に、結合剤付与装置２によって結合剤が付与され、その直後に組成物付与装置９ａによってアルデヒド類捕捉組成物が付与される。次いで、結合剤とアルデヒド類捕捉組成物とが付与された無機質繊維３をコンベア４ａ上に堆積して、コンベア４ｂ上に搬送され、コンベア５によって所定厚さに圧縮成形されつつ、重合反応炉６に導入されて結合剤が加熱重合硬化され、無機質繊維マット７が形成される。以下、各工程について説明する。   In the manufacturing method of FIG. 1, a binder is applied to the inorganic fibers 3 spun from the fiberizing apparatus 1 by the binder applying apparatus 2, and immediately thereafter, an aldehyde capturing composition is applied by the composition applying apparatus 9a. The Next, the inorganic fibers 3 to which the binder and the aldehyde-capturing composition are applied are deposited on the conveyor 4a, conveyed onto the conveyor 4b, and compressed and molded to a predetermined thickness by the conveyor 5, while the polymerization reactor 6 And the binder is heated and polymerized and cured to form the inorganic fiber mat 7. Hereinafter, each step will be described.

まず、繊維化装置１によりグラスウール等の無機質繊維を紡出させる繊維化工程が行われる。ここで、繊維化装置１による繊維化の方法としては、従来公知の遠心法の他、火焔法、吹き飛ばし法等が例示でき、特に限定されない。また、繊維化装置１は、製造する無機質繊維マット７の密度、厚さ、及び巾方向の長さに応じて複数設けることも可能である。   First, a fiberizing process in which inorganic fibers such as glass wool are spun by the fiberizing apparatus 1 is performed. Here, examples of the fiberizing method by the fiberizing apparatus 1 include not only a conventionally known centrifugal method but also a flame method, a blowing method, and the like, and are not particularly limited. A plurality of fiberizing apparatuses 1 can be provided according to the density, thickness, and length in the width direction of the inorganic fiber mat 7 to be manufactured.

次いで、結合剤付与装置２によって、繊維化装置１から紡出された無機質繊維３に、主成分がフェノール樹脂である結合剤を付与する。結合剤の付与方法としては、従来公知のスプレー法等を用いることができる。   Next, a binder whose main component is a phenol resin is applied to the inorganic fibers 3 spun from the fiberizing apparatus 1 by the binder applying apparatus 2. As a method for applying the binder, a conventionally known spray method or the like can be used.

次に、上記の結合剤の付与工程の直後に、組成物付与装置９ａによって、アルデヒド類捕捉組成物が付与される。ここで、本発明において、結合剤の付与工程の直後とは、結合剤付与装置２と集綿のためのコンベア４ａとの間であることを意味する。ただし、組成物付与装置９ａから噴霧されるアルデヒド類捕捉組成物の一部が、コンベア４ａ上の無機質繊維３に直接付与されてもよい。   Next, immediately after the above-described binder application step, the composition application device 9a applies the aldehyde capturing composition. Here, in the present invention, “immediately after the binder application step” means between the binder application device 2 and the conveyor 4a for collecting cotton. However, a part of the aldehyde capturing composition sprayed from the composition application device 9a may be directly applied to the inorganic fibers 3 on the conveyor 4a.

コンベア４ａは、未硬化の結合剤が付着した無機質繊維３を有孔のコンベア上に積層する装置であり、繊維を均一に積層させるために、コンベア４ａは下面に図示しない吸引装置を有する有孔のコンベアとなっている。このため、組成物付与装置９ａ付近は、吸引装置からの下向きの吸引力が働いている。したがって、この位置に組成物付与装置９ａを設けることにより、下向きの吸引力を利用して少量でも効率よくアルデヒド類捕捉組成物を付与できる。   The conveyor 4a is a device for laminating the inorganic fibers 3 to which the uncured binder is attached on the perforated conveyor. In order to uniformly laminate the fibers, the conveyor 4a has a suction device (not shown) on the lower surface. It is a conveyor. For this reason, the downward suction force from the suction device works in the vicinity of the composition applying device 9a. Therefore, by providing the composition applying device 9a at this position, the aldehyde capturing composition can be efficiently applied even in a small amount by using the downward suction force.

また、無機質繊維３がコンベア４ａに堆積される途中であるので、繊維密度の低い状態で、個々の無機質繊維３へアルデヒド類捕捉組成物を付与しつつ堆積することができる。このため、無機質繊維マットの表面だけでなく、内部まで均一にアルデヒド類捕捉組成物が付与され、やはり効率的にアルデヒド類を化学的に分解できる。   Moreover, since the inorganic fiber 3 is in the middle of being deposited on the conveyor 4a, it can be deposited while applying an aldehyde capturing composition to each inorganic fiber 3 with a low fiber density. For this reason, an aldehyde capture | acquisition composition is uniformly provided not only to the surface of an inorganic fiber mat but to the inside, and also an aldehyde can be chemically decomposed | disassembled efficiently.

アルデヒド類捕捉組成物の無機質繊維への付着量としては、無機質繊維への結合剤の付着量（固形分として）１００質量部に対して、アルデヒド類捕捉組成物の付着量が固形分換算で０．１〜２０質量部となるような範囲とする。より好ましくは０．５〜１０質量部であり、特に好ましくは１〜５質量部が好適である。   The adhesion amount of the aldehyde capture composition to the inorganic fiber is 0 in terms of solid content with respect to the adhesion amount of the binder to the inorganic fiber (as solid content) of 100 parts by mass. .1 to 20 parts by mass. More preferably, it is 0.5-10 mass parts, Most preferably, 1-5 mass parts is suitable.

アルデヒド類捕捉組成物の付着量が０．１質量部未満となる付与量であるとアルデヒド類や臭気の放出を低減させる効果が充分に期待できない。また、２０質量部を超える付与量になると、アルデヒド類捕捉組成物が無機質繊維マットに固着しきれずに脱落したり、組成物に要するコストが高くなり経済的でない。   If the applied amount of the aldehyde capturing composition is less than 0.1 parts by mass, the effect of reducing the release of aldehydes and odors cannot be sufficiently expected. On the other hand, when the application amount exceeds 20 parts by mass, the aldehyde-capturing composition is not economically attached because it cannot be fixed to the inorganic fiber mat and falls off, or the cost required for the composition increases.

ここで、本発明における結合剤の付着量とは、強熱減量法又はＬＯＩ（Loss of Ignition ）と呼ばれる方法により測定される量であり、約５５０℃で結合剤付着後の無機質繊維マットの乾燥試料を強熱し、減量をすることにより失われる物質の重量を意味する。   Here, the attached amount of the binder in the present invention is an amount measured by an ignition loss method or a method called LOI (Loss of Ignition), and drying of the inorganic fiber mat after attaching the binder at about 550 ° C. It means the weight of material lost by igniting the sample and losing weight.

アルデヒド類捕捉組成物を付与する方法としては、特に、無機質繊維の表面に均一に付与するために、スプレー装置を用いて噴霧する方法が好ましい。   As a method for applying the aldehydes-trapping composition, a method of spraying using a spray device is particularly preferable in order to uniformly apply the surface to the inorganic fiber.

なお、本発明においては、水溶液の濃度と、スプレー装置の噴霧量の少なくともどちらか一方を調整することにより、従来の無機質繊維マットの製造する諸条件を変更することなく、無機質繊維３へのアルデヒド類捕捉組成物の付与量を所望の値に調整することができ、かつ、結合剤の量に対するアルデヒド類捕捉組成物の含有量を所望の値に調整することができる。   In the present invention, by adjusting at least one of the concentration of the aqueous solution and the spray amount of the spray device, the aldehyde to the inorganic fiber 3 can be changed without changing the conditions for producing the conventional inorganic fiber mat. It is possible to adjust the applied amount of the aldehyde capturing composition to a desired value, and to adjust the content of the aldehyde capturing composition relative to the amount of the binder to a desired value.

上記工程によって、結合剤及びアルデヒド類捕捉組成物が付与された無機質繊維３は、繊維化装置１の下方に配置されたコンベア４ａに堆積され、連続して、ライン方向に沿って設けられているコンベア４ｂに移動する。そして、コンベア４ｂ上に所定間隔で対向配置されたコンベア５によって、堆積した無機質繊維３は所定の厚さに圧縮されてマット状に成形される。   The inorganic fiber 3 to which the binder and the aldehyde capturing composition are applied by the above process is deposited on the conveyor 4a disposed below the fiberizing apparatus 1, and is continuously provided along the line direction. Move to conveyor 4b. Then, the deposited inorganic fibers 3 are compressed to a predetermined thickness and formed into a mat shape by the conveyor 5 disposed opposite to the conveyor 4b at a predetermined interval.

その後、コンベア４ｂの位置に配設された重合反応炉６に入り、無機質繊維３に付与された、主成分が水溶性フェノール樹脂である結合剤が重合反応炉６内で加熱重合硬化されて無機質繊維マット７を形成する。そして、形成された無機質繊維マット７は、コンベア４ｃの部分に設置された切断機８によって所定の製品寸法に切断された後、コンベア４ｄによって運ばれ、包装、梱包される。   After that, it enters the polymerization reaction furnace 6 disposed at the position of the conveyor 4b, and the binder, which is applied to the inorganic fibers 3 and whose main component is a water-soluble phenol resin, is heated and polymerized and cured in the polymerization reaction furnace 6 to be inorganic. A fiber mat 7 is formed. Then, the formed inorganic fiber mat 7 is cut into a predetermined product size by a cutting machine 8 installed in a portion of the conveyor 4c, and then conveyed by the conveyor 4d to be packed and packed.

なお、無機質繊維マット７は、そのままの形態で断熱材、吸音材等に用いることができるが、無機質繊維マットに表皮材を組み合わせてもよい。表皮材としては、紙、金属蒸着合成樹脂フィルム、合成樹脂フィルム、金属箔積層フィルム、不織布、織布あるいはこれらを組み合わせたもの(例えば、アルミ貼クラフト紙、アルミ貼ガラスクロス等)を用いることができる。   In addition, although the inorganic fiber mat 7 can be used for a heat insulating material, a sound absorbing material, etc. with the form as it is, you may combine a skin material with an inorganic fiber mat. As the skin material, it is possible to use paper, metal-deposited synthetic resin film, synthetic resin film, metal foil laminated film, non-woven fabric, woven fabric, or a combination thereof (for example, aluminum-coated kraft paper, aluminum-coated glass cloth, etc.) it can.

このようにして得られた本発明の無機質繊維マットは、アルデヒド類の放出量抑制効果に優れる。アルデヒド類の放出量としては、ＪＩＳ−Ａ５９０８のデシケーター法に基づいたホルムアルデヒド放出量試験によるホルムアルデヒド放出量が０．２０ｍｇ／リットル以下である。   The inorganic fiber mat of the present invention thus obtained is excellent in the effect of suppressing the release amount of aldehydes. As the amount of aldehydes released, the amount of formaldehyde released by the formaldehyde emission amount test based on the desiccator method of JIS-A5908 is 0.20 mg / liter or less.

上記ＪＩＳにおいては、ホルムアルデヒド放出量による区分としてＥ０、Ｅ１、Ｅ２の３段階に区分されており、それぞれホルムアルデヒド放出量が０．５ｍｇ／リットル以下の場合Ｅ０タイプ、０．５ｍｇ／リットル〜１．５ｍｇ／リットル以下の場合Ｅ１タイプ、１．５ｍｇ／リットル〜５．０ｍｇ／リットル以下の場合Ｅ２タイプに区分される。Ｅ０タイプが最も優れるタイプと規定される。したがって、本発明の好ましいホルムアルデヒド放出量である０．２０ｍｇ／リットル以下は、上記Ｅ０タイプの上限を大きく下回るので、極めて少ないホルムアルデヒド放出量である。 In the above JIS, the classification according to the amount of formaldehyde released is divided into three stages of E 0 , E 1 , E 2. When the amount of formaldehyde released is 0.5 mg / liter or less, E 0 type, 0.5 mg / liter ～1.5Mg / liter when E 1 type, are classified into the case where E 2 type below 1.5 mg / l ～5.0Mg / liter. E 0 type is defined as the most excellent type. Therefore, a is 0.20 mg / liter or less is preferably formaldehyde emission amount of the present invention, since substantially below the upper limit of the E 0 type, a very small formaldehyde emissions.

前記ホルムアルデヒド放出量の測定は、上記のＪＩＳ−Ａ５９０８に準拠して測定される。ここで、本発明の無機質繊維マットで測定するにあたっては、試験片の全表面積が１８００ｃｍ２となるように、厚みが１０〜１５０ｍｍの無機質繊維マットを適宜切断して、試験片のサイズ調整をおこなう。また、包装内に蓄積されたアルデヒド類が包装を開梱した瞬間に放散することから、無機質繊維マットの包装体を開封してから試験片を採取し、前記試験法に従い測定容器内に置いて、測定を開始するまでの時間を１０分以内とする。 The formaldehyde emission amount is measured according to the above JIS-A5908. Here, when measuring with the inorganic fiber mat of the present invention, the size of the test piece is adjusted by appropriately cutting the inorganic fiber mat having a thickness of 10 to 150 mm so that the total surface area of the test piece is 1800 cm 2. . In addition, since the aldehydes accumulated in the packaging are released at the moment when the packaging is unpacked, the test piece is collected after opening the package of the inorganic fiber mat and placed in the measurement container according to the above test method. The time until the measurement is started is within 10 minutes.

図２には、本発明の無機質繊維マットの製造方法のうち、無機質繊維を堆積させる工程と結合剤を重合硬化させる工程との間で組成物を付与する方法の実施形態が示されている。なお、以下の説明においては、前記実施形態と実質的に同一部分には同符号を付してその説明を省略する。   FIG. 2 shows an embodiment of a method for applying a composition between a step of depositing inorganic fibers and a step of polymerizing and curing a binder in the method for producing an inorganic fiber mat of the present invention. In the following description, parts that are substantially the same as those in the above embodiment are given the same reference numerals, and descriptions thereof are omitted.

図２の実施形態は、アルデヒド類捕捉組成物の付与装置が、無機質繊維３が堆積し終わったコンベア４ａ上と、それに連続して設けられている重合反応炉６に導入するためのコンベア４ｂ及びコンベア５との間の部分に設けられている点が、図１の実施形態と異なっている。   In the embodiment of FIG. 2, an apparatus for capturing an aldehyde capture composition includes a conveyor 4 b for introducing the inorganic fiber 3 onto the conveyor 4 a on which the inorganic fibers 3 have been deposited, and a polymerization reactor 6 provided continuously therewith. The point provided in the part between the conveyors 5 is different from the embodiment of FIG.

まず、図１と同様に、繊維化装置１から紡出された無機質繊維３に結合剤付与装置２によって結合剤が付与されてコンベア４ａ上に堆積し、次いで連続するコンベア４ｂ上に搬送される。   First, as in FIG. 1, a binder is applied to the inorganic fiber 3 spun from the fiberizing apparatus 1 by the binder applying apparatus 2 and deposited on the conveyor 4a, and then conveyed onto the continuous conveyor 4b. .

このとき、アルデヒド類捕捉組成物の付与は、無機質繊維３が堆積し終わったコンベア４ａ上からコンベア５の直前までの間に設けられた組成物付与装置９ｂと、コンベア４ａとコンベア４ｂの隙間に設けられた組成物付与装置９ｃによって、堆積された無機質繊維３の上下両面に対して行われる。   At this time, the application of the aldehyde capture composition is performed in the gap between the conveyor 4a and the conveyor 4b provided between the conveyor 4a where the inorganic fibers 3 have been deposited and immediately before the conveyor 5 and the conveyor 4a. This is performed on the upper and lower surfaces of the deposited inorganic fiber 3 by the provided composition applying device 9c.

そして、上記組成物の付与直後に、図１と同様にコンベア５によって所定厚さに圧縮成形されつつ、重合反応炉６に導入されて結合剤が加熱重合硬化され、無機質繊維マット７が形成される。そして、形成された無機質繊維マット７は、コンベア４ｃの部分に設置された切断機８によって所定の製品寸法に切断された後、包装、梱包される。   Then, immediately after the application of the composition, the binder is heated and polymerized and cured by being compressed and molded to a predetermined thickness by the conveyor 5 as in FIG. 1, and the inorganic fiber mat 7 is formed. The And the formed inorganic fiber mat 7 is cut | disconnected by the predetermined | prescribed product dimension with the cutting machine 8 installed in the part of the conveyor 4c, Then, it packs and packs.

このように、アルデヒド類捕捉組成物の付与を、無機質繊維３が堆積し終わったコンベア４ａと、それに連続して設けられている重合反応炉６に導入するためのコンベア４ｂ及びコンベア５との間の部分で上下両方向から行うことにより、アルデヒド類捕捉組成物を更に均一に付与でき、付着の効率をよくすることができる。   In this way, between the conveyor 4a and the conveyor 5 for introducing the aldehydes-trapping composition into the polymerization reactor 6 provided continuously to the conveyor 4a on which the inorganic fibers 3 have been deposited. By carrying out from both the upper and lower directions in this part, the aldehyde capturing composition can be applied more uniformly and the efficiency of adhesion can be improved.

なお、この実施形態においては、組成物付与装置は上下いずれかの１ヶ所に設けられていてもよいが、堆積された無機質繊維３の上下面全体にアルデヒド類捕捉組成物を付与するために、上下両方に設けられていることが好ましい。また、図１の実施形態と同様に、組成物付与装置は、堆積された無機質繊維３の巾方向の長さに応じて複数設けられていてもよい。   In this embodiment, the composition application device may be provided at any one of the top and bottom, but in order to apply the aldehyde capturing composition to the entire upper and lower surfaces of the deposited inorganic fibers 3, It is preferable to be provided on both upper and lower sides. Moreover, the composition provision apparatus may be provided with two or more according to the length of the width direction of the deposited inorganic fiber 3 similarly to embodiment of FIG.

なお、本発明の製造方法においては、アルデヒド類捕捉組成物を付与するタイミングは、無機質繊維に結合剤を付与する工程から結合剤を重合硬化させる工程の間であれば特に限定されないが、アルデヒド類捕捉組成物を無機質繊維に効率よく付着させて、無機質繊維マットからのアルデヒド類の放出の抑制効率を上げられる点から、図２に示した無機質繊維を堆積させる工程と結合剤を重合硬化させる工程との間で付与する方法が特に好ましい。   In the production method of the present invention, the timing of applying the aldehyde capturing composition is not particularly limited as long as it is between the step of applying the binder to the inorganic fiber and the step of polymerizing and curing the binder, but the aldehydes are not limited. The step of depositing the inorganic fiber shown in FIG. 2 and the step of polymerizing and curing the binder from the viewpoint that the trapping composition can be efficiently attached to the inorganic fiber to increase the suppression efficiency of the release of aldehydes from the inorganic fiber mat. Particularly preferred is a method of applying between the two.

また、図１及び図２の方法は、それらの何れかを単独で用いてもよいが、両者を併用してもよい。併用する場合は、両者の方法によるそれぞれのアルデヒド類捕捉組成物の付与量を適宜配分して、組成物の付与量を所望の値に調整することができる。   Moreover, although either of them may be used independently for the method of FIG.1 and FIG.2, you may use both together. When using together, the application amount of each aldehyde capture | acquisition composition by both methods can be distributed suitably, and the application amount of a composition can be adjusted to a desired value.

なお、アルデヒド類捕捉組成物を無機質繊維に付与するタイミングとして、上記の製造方法以外に、例えば、重合反応炉で結合剤が加熱硬化した直後にアルデヒド類捕捉組成物を無機質繊維マットへ付与してもよく、無機質繊維マットを取り付け作業する場所で該無機質繊維マットへ付与してもよく、上記の製造方法と併用してもよく、単独で用いてもよい。この場合、無機質繊維マットの結合剤が既に硬化しているために、アルデヒド類捕捉組成物が無機質繊維マットの内部へ充分に固着し難いものの、無機質繊維マットの表層部分への付与量を増加することにより、アルデヒド類の放出を低減させる効率が低下するのを防止できる。   In addition to the production method described above, the timing for applying the aldehyde capture composition to the inorganic fiber is, for example, by applying the aldehyde capture composition to the inorganic fiber mat immediately after the binder is heated and cured in the polymerization reaction furnace. Alternatively, it may be applied to the inorganic fiber mat at the place where the inorganic fiber mat is attached, may be used in combination with the above production method, or may be used alone. In this case, since the binder of the inorganic fiber mat is already cured, the aldehyde capturing composition is not sufficiently fixed to the inside of the inorganic fiber mat, but the amount applied to the surface layer portion of the inorganic fiber mat is increased. By this, it can prevent that the efficiency which reduces discharge | release of aldehydes falls.

以下、実施例を挙げて本発明を詳細に説明するが、本発明はこれら実施例に限定されるものではない。なお、部、％は、特にことわりの無い時は質量基準を表す。   EXAMPLES Hereinafter, although an Example is given and this invention is demonstrated in detail, this invention is not limited to these Examples. In addition, part and% represent a mass reference | standard when there is no notice in particular.

[アルデヒド類捕捉組成物の調製]
表１に示すような配合割合（質量部）で、実施例１〜８及び比較例１〜３のアルデヒド類捕捉組成物を、それぞれ３０％濃度の水溶液となるように調製した。それぞれの水溶液のｐＨを表２に示す。 [Preparation of aldehyde capture composition]
The aldehyde capture | acquisition composition of Examples 1-8 and Comparative Examples 1-3 was prepared so that it might become a 30% concentration aqueous solution by the mixture ratio (mass part) as shown in Table 1, respectively. The pH of each aqueous solution is shown in Table 2.

Figure 2005194634
Figure 2005194634

Figure 2005194634
Figure 2005194634

[無機質繊維マットの製造]
図１に示すような製造装置を用い、水溶性フェノール樹脂を主成分とする結合剤を付与する工程の直後に、スプレー装置を用いて、実施例１のアルデヒド類捕捉組成物を噴霧して、密度３２Ｋｇ／ｍ３、厚み５０ｍｍの無機質繊維マットを得た。このとき、無機質繊維マットの結合剤の付着量１００質量部に対して、該組成物の付着量が固形分比率で１．５質量部となるように水溶液を付与した。なお、無機質繊維としては、グラスウールを用いた。 [Manufacture of inorganic fiber mats]
Using the production apparatus as shown in FIG. 1, immediately after the step of applying the binder mainly composed of a water-soluble phenol resin, the spray device is used to spray the aldehyde capture composition of Example 1, An inorganic fiber mat having a density of 32 kg / m 3 and a thickness of 50 mm was obtained. At this time, the aqueous solution was applied so that the adhesion amount of the composition was 1.5 parts by mass with respect to 100 parts by mass of the binder adhesion amount of the inorganic fiber mat. Glass wool was used as the inorganic fiber.

そして、この無機質繊維マットを、長さ９１０ｍｍ、幅９１０ｍｍに切断加工し、この加工した無機質繊維マット１０枚をまとめて密閉包装した。実施例２〜８及び比較例１〜３のアルデヒド類捕捉組成物を用いる以外は実施例１と同様の条件で実施例２〜８及び比較例１〜３となる無機質繊維マットをそれぞれ得た。   The inorganic fiber mat was cut into a length of 910 mm and a width of 910 mm, and the 10 processed inorganic fiber mats were collectively sealed. Except using the aldehyde capture | acquisition composition of Examples 2-8 and Comparative Examples 1-3, the inorganic fiber mat used as Examples 2-8 and Comparative Examples 1-3 was obtained on the conditions similar to Example 1, respectively.

上記の実施例１〜８及び、比較例１〜３のアルデヒド類捕捉組成物を付着させた無機質繊維マットを、ＪＩＳ−Ａ５９０８のデシケーター法に基づいた、ホルムアルデヒド放出量試験をおこなった。測定結果をまとめて表３に示す。   The formaldehyde emission amount test based on the desiccator method of JIS-A5908 was performed on the inorganic fiber mats to which the aldehyde capture compositions of Examples 1 to 8 and Comparative Examples 1 to 3 were attached. The measurement results are summarized in Table 3.

Figure 2005194634
Figure 2005194634

表３より、本発明の実施例１〜８のアルデヒド類捕捉組成物を用いた無機質繊維マットは、ホルムアルデヒド放出量が０．２０ｍｇ／リットル以下であり、優れたホルムアルデヒドの捕捉効果得られていることがわかる。また、表２より、水溶液のｐＨは、いずれも９．５以下である。   From Table 3, the inorganic fiber mat using the aldehyde capture composition of Examples 1 to 8 of the present invention has a formaldehyde emission amount of 0.20 mg / liter or less, and an excellent formaldehyde capture effect is obtained. I understand. From Table 2, the pH of the aqueous solution is 9.5 or less.

一方、有機酸塩を含んでいない比較例１の組成であるアルデヒド類捕捉組成物を使用して作製した無機質繊維マットでは、捕捉剤をｐＨ９．５以下の水溶液として使用することがでるが、ホルムアルデヒドの放出量抑制効果は規定範囲の０．２０ｍｇ／リットルを超えてしまう。   On the other hand, in the inorganic fiber mat produced using the aldehyde capture composition which is the composition of Comparative Example 1 containing no organic acid salt, the capture agent can be used as an aqueous solution having a pH of 9.5 or less. The release amount suppression effect exceeds the specified range of 0.20 mg / liter.

また、無機性リン酸塩を含んでいない比較例２及び比較例３の組成であるアルデヒド類捕捉剤を使用して作製した無機質繊維マットでは、ホルムアルデヒドの放出量抑制効果については良好な結果が得られるが、いずれの組成物も水溶液とした際には、ｐＨが１０．０以上となってしまうことがわかる。   In addition, in the inorganic fiber mat produced using the aldehyde scavenger having the composition of Comparative Example 2 and Comparative Example 3 that does not contain inorganic phosphate, good results were obtained for the effect of suppressing the amount of formaldehyde released. However, it turns out that pH will be 10.0 or more when all compositions are made into aqueous solution.

本発明により得られる無機質繊維マットは、例えば建築用の断熱材、吸音材等として用いることができる。   The inorganic fiber mat obtained by the present invention can be used as, for example, a building heat insulating material, a sound absorbing material, and the like.

本発明の無機質繊維マットにおける、製造方法の一例を示す概略工程図である。It is a schematic process drawing which shows an example of the manufacturing method in the inorganic fiber mat of this invention. 本発明の無機質繊維マットにおける、製造方法の他の例を示す概略工程図である。It is a schematic process drawing which shows the other example of the manufacturing method in the inorganic fiber mat of this invention.

符号の説明Explanation of symbols

１： 繊維化装置
２： 結合剤付与装置
３： 無機質繊維
４ａ、４ｂ、４ｃ、４ｄ、５： コンベア
６： 重合反応炉
７： 無機質繊維マット
８： 切断機
９ａ、９ｂ、９ｃ： 組成物付与装置
1: Fiberizing device 2: Binder applying device 3: Inorganic fibers 4a, 4b, 4c, 4d, 5: Conveyor 6: Polymerization reactor 7: Inorganic fiber mat 8: Cutting machines 9a, 9b, 9c: Composition applying device

Claims (5)

主成分がフェノール樹脂である結合剤を付着させて成形、硬化した無機質繊維マットにおいて、前記付着した結合剤１００質量部に対して、亜硫酸塩、無機性リン酸塩、有機酸塩の３成分を少なくとも含むアルデヒド類捕捉組成物をｐＨ９．５以下の水溶液として、固形分比率で０．１〜２０質量部となるように前記無機質繊維に付着させて得られ、ＪＩＳ−Ａ５９０８のデシケーター法に基づいたホルムアルデヒド放出量試験によるホルムアルデヒド放出量が０．２０ｍｇ／リットル以下であることを特徴とする無機質繊維マット。   In an inorganic fiber mat molded and cured by attaching a binder whose main component is a phenol resin, three components of sulfite, inorganic phosphate, and organic acid salt are added to 100 parts by mass of the attached binder. At least the aldehyde-containing composition containing at least 9.5 is obtained as an aqueous solution having a pH of 9.5 or less, and is attached to the inorganic fiber so that the solid content ratio is 0.1 to 20 parts by mass. An inorganic fiber mat having a formaldehyde emission amount of 0.20 mg / liter or less by a formaldehyde emission amount test. 前記アルデヒド類捕捉組成物が、亜硫酸塩、無機性リン酸塩、有機酸塩、尿素の４成分を少なくとも含んでいる請求項１に記載の無機質繊維マット。   The inorganic fiber mat according to claim 1, wherein the aldehyde capturing composition contains at least four components of sulfite, inorganic phosphate, organic acid salt, and urea. 前記アルデヒド類捕捉組成物の組成が、固形分比率で亜硫酸塩６０〜９４部、無機性リン酸塩３〜２０部、有機酸塩３〜２０部である請求項１に記載の無機質繊維マット。   2. The inorganic fiber mat according to claim 1, wherein the composition of the aldehyde capturing composition is 60 to 94 parts of sulfite, 3 to 20 parts of inorganic phosphate, and 3 to 20 parts of organic acid salt in a solid content ratio. 前記アルデヒド類捕捉組成物の組成が、固形分比率で尿素１０〜７０部、亜硫酸塩２０〜８０部、無機性リン酸塩５〜２０部、有機酸塩５〜２０部である請求項２に記載の無機質繊維マット。   The composition of the aldehyde capturing composition is 10 to 70 parts of urea, 20 to 80 parts of sulfite, 5 to 20 parts of inorganic phosphate, and 5 to 20 parts of organic acid salt in a solid content ratio. The inorganic fiber mat described. 前記無機質繊維が、グラスウール又はロックウールである請求項１〜４のいずれか１つに記載の無機質繊維マット。
The inorganic fiber mat according to any one of claims 1 to 4, wherein the inorganic fiber is glass wool or rock wool.
JP2003434878A 2003-12-26 2003-12-26 Inorganic fiber mat Pending JP2005194634A (en)