JP2005068767A - Void form - Google Patents
Void form Download PDFInfo
- Publication number
- JP2005068767A JP2005068767A JP2003298961A JP2003298961A JP2005068767A JP 2005068767 A JP2005068767 A JP 2005068767A JP 2003298961 A JP2003298961 A JP 2003298961A JP 2003298961 A JP2003298961 A JP 2003298961A JP 2005068767 A JP2005068767 A JP 2005068767A
- Authority
- JP
- Japan
- Prior art keywords
- void
- sound insulation
- sound
- insulation layer
- cylindrical body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、ホイド型枠、詳しくは、コンクリートスラブの層内に中空ボイドを具備させるための筒体でなるボイド型枠に関する。 The present invention relates to a void formwork, and more particularly to a void formwork formed of a cylinder for providing a hollow void in a layer of a concrete slab.
ボイド型枠は、集合住宅や高層建物などのスラブを軽量化して大スパン化することに有益な建築資材であり、そのボイド型枠として金属製又は発泡スチロール製の筒体を用いることが知られていて、一般的には筒体として円筒形又は矩形筒形のものが汎用されている。また、このボイド型枠を層内に具備させたコンクリートスラブは、ボイド型枠の設置箇所でのコンクリート層の層厚が薄くなっているために、その設置箇所で音波が共振することによって床衝撃音の遮音性能のレベルが低下し、たとえば壁掛け電話のベル音などが間仕切り壁を介して固体音として伝播しやすくなるということが云われている。そこで、床衝撃音の遮音性能を改善すること意図して、ボイド型枠を形成している筒体の形状を種々変更したり、ボイド型枠の使用によってスラブの軽量化が図られることを勘案してそのスラブを厚くするという試みもなされている。 Void formwork is a building material that is useful for reducing the weight and lengthening of slabs such as apartment buildings and high-rise buildings, and it is known to use a metal or polystyrene foam cylinder as the void formwork. In general, cylindrical or rectangular cylinders are widely used as cylinders. In addition, in concrete slabs with this void formwork in the layer, since the layer thickness of the concrete layer at the place where the void formwork is installed is thin, the sound wave resonates at that place and the floor impact It is said that the level of sound insulation performance is reduced, and for example, the bell sound of a wall-mounted telephone is easily propagated as a solid sound through a partition wall. Therefore, with the intention of improving the sound insulation performance of floor impact sound, it is possible to reduce the weight of the slab by variously changing the shape of the cylinder forming the void formwork and using the void formwork. Attempts have also been made to thicken the slab.
一方、従来例として、円筒形の筒体をボイド型枠とすることが公知である(特許文献1参照)。 On the other hand, as a conventional example, it is known to use a cylindrical tubular body as a void type frame (see Patent Document 1).
しかしながら、ボイド型枠を形成している筒体の形状を特殊な形状に置き換えたりスラブを厚くしたりすることによって床衝撃音の遮音性能を改善するという試みは、それ自体が床衝撃音の遮音性能の改善に一定の効果を発揮するものであるとしても、筒体の製作に高度な技術が必要になってそれだけコスト高になったり、スラブが厚くなることによって室内天井高さを高く保つことが困難になったりするという問題点を有している。 However, attempts to improve the sound insulation performance of floor impact sound by replacing the shape of the cylinder forming the void formwork with a special shape or thickening the slab itself Even if it has a certain effect on improving the performance, it requires a high level of technology to manufacture the cylinder, which increases the cost and keeps the indoor ceiling height high by increasing the thickness of the slab. Has the problem of becoming difficult.
本発明は以上の問題に鑑みてなされたものであり、ボイド型枠を形成している筒体の形状を変更することなく、また、スラブを厚くしたりすることなく、床衝撃音の遮音性能を改善することのできるボイド型枠を提供することを目的とする。 The present invention has been made in view of the above problems, and does not change the shape of the cylinder forming the void mold frame, and does not increase the thickness of the slab, so that the sound insulation performance of floor impact sound is achieved. An object of the present invention is to provide a void formwork that can improve the above.
本発明に係るボイド型枠は、コンクリートスラブの層内に中空ボイドを具備させるための筒体でなるボイド型枠において、上記筒体の外周面又は内周面に、パーライト、ガラスビーズ又はアルミナバブルから選ばれる1種又は複数種の粉粒体でなる遮音層を形成してある、という点に特徴を有している。 The void form according to the present invention is a void form made of a cylinder for providing a hollow void in a layer of a concrete slab, and pearlite, glass beads or alumina bubbles are formed on the outer peripheral surface or inner peripheral surface of the cylinder. It has the characteristic that the sound-insulation layer which consists of 1 type or multiple types of granular material chosen from these is formed.
この発明によれば、パーライト、ガラスビーズ又はアルミナバブルから選ばれる1種又は複数種の粉粒体でなる遮音層が、音波を乱反射して干渉させたり、音波を吸収したり、吸収して取り込んだ音波をその層内で乱反射して干渉させたりする作用を発揮することにより、また、遮音層を形成している粉粒体が音波との摩擦によって音響エネルギーを吸収したりする作用を発揮することによって優れた床衝撃音の遮音性能を発揮する。また、上掲の各種の粉粒体の中からパーライトを選択したボイド型枠では、パーライトが気密性の小気泡の集合体であって砂の1/10〜1/20の重さであるために軽量性に優れ、耐火性や耐薬品性にも優れているため、スラブに加わる強度上の負担が小さく抑えられるだけでなく、初期の消音作用が長期に亘って持続するという特筆すべき作用を発揮する。 According to the present invention, the sound insulation layer made of one or more kinds of powders selected from pearlite, glass beads, or alumina bubbles reflects and interferes with sound waves, or absorbs or absorbs sound waves. By exhibiting the action of causing irregular reflection of the sound wave in the layer and causing interference, the granular material forming the sound insulation layer also exhibits the action of absorbing acoustic energy by friction with the sound wave. By doing so, it exhibits excellent sound insulation performance for floor impact sound. In addition, in the void mold form in which pearlite is selected from the various powders and particles described above, pearlite is an aggregate of airtight small bubbles and weighs 1/10 to 1/20 of sand. It is notable for its light weight, fire resistance, and chemical resistance, which not only keeps the load on the strength of the slab small, but also keeps the initial silencing effect for a long time. Demonstrate.
この発明では、上記筒体の正面視形状が、正円形状、長円形状、多角形状及び湾曲部を備えた形状から選ばれるいずれかであってもよい。 In this invention, the front view shape of the cylinder may be any one selected from a perfect circle shape, an oval shape, a polygonal shape, and a shape having a curved portion.
この発明では、遮音層を形成している粉粒体の直径が0.2〜4mmである、という構成を採用することが可能であり、それによると、直径が0.2〜4mmの上記粉粒体が現況下で市場に流通していることから、低コストでの入手が容易であるという利点がある。 In this invention, it is possible to employ a configuration in which the diameter of the granular material forming the sound insulation layer is 0.2 to 4 mm. According to this, the powder having a diameter of 0.2 to 4 mm is adopted. Since the granule is distributed in the market under the present situation, there is an advantage that it is easy to obtain at low cost.
本発明では、遮音層の層厚が0.5〜5mmであることが望ましい。これは、層厚が0.5〜5mmの遮音層は、塗布、吹付け、その他の汎用的な手段によってそれほどの熟練を要することなく容易に形成することができるからである。 In the present invention, it is desirable that the sound insulation layer has a thickness of 0.5 to 5 mm. This is because a sound insulation layer having a layer thickness of 0.5 to 5 mm can be easily formed by applying, spraying, and other general means without requiring much skill.
本発明では、上記筒体に上記遮音層が接着剤で接合されている、という構成を採用することができ、これによれば、0.5〜5mmの層厚の遮音層を塗布、吹付け、その他の汎用的な手段によってそれほどの熟練を要することなく容易に形成することができる。また、遮音層を形成している粉粒体が剥がれ落ちるという事態が抑制される。 In this invention, the structure that the said sound insulation layer is joined to the said cylinder with the adhesive agent can be employ | adopted, According to this, the sound insulation layer with a layer thickness of 0.5-5 mm is apply | coated and sprayed. It can be easily formed by other general-purpose means without requiring much skill. Moreover, the situation where the granular material which forms the sound-insulation layer peels off is suppressed.
本発明では、上記筒体の外周面に形成された上記遮音層が、不織布などの柔軟な素材でなる保護シートで覆われていることが望ましい。これによれば、コンクリートスラブの施工中に作業者がボイド型枠の上を通行した場合や、ボイド型枠の上に他の資材が一時的に載置されたような場合に、遮音層を形成している粉粒体の脱落などが保護シートにより抑制される。 In the present invention, it is desirable that the sound insulation layer formed on the outer peripheral surface of the cylindrical body is covered with a protective sheet made of a flexible material such as a nonwoven fabric. According to this, when the worker passes over the void formwork during the construction of the concrete slab, or when other materials are temporarily placed on the void formwork, the sound insulation layer is provided. Dropping off of the formed granular material is suppressed by the protective sheet.
本発明に係る他のボイド型枠は、コンクリートスラブの層内に中空ボイドを具備させるための筒体でなるボイド型枠において、上記筒体が合成樹脂発泡体でなり、その合成樹脂発泡体が、パーライト、ガラスビーズ又はアルミナバブルから選ばれる1種又は複数種の粉粒体を、体積比で30%以下含んでいる、いうものである。これによると、筒体の内周面や外周面に遮音層を形成する必要がなく、合成樹脂材料を発泡させて筒体を製作するだけで床衝撃音の遮音性に優れたボイド型枠が得られる。 Another void mold according to the present invention is a void mold formed of a cylinder for providing a hollow void in a layer of a concrete slab. The cylinder is a synthetic resin foam, and the synthetic resin foam is In other words, it contains 30% or less by volume of one or more powders selected from perlite, glass beads, or alumina bubbles. According to this, it is not necessary to form a sound insulation layer on the inner peripheral surface or outer peripheral surface of the cylinder, and a void form frame having excellent sound insulation of floor impact sound can be obtained simply by producing a cylinder by foaming a synthetic resin material. can get.
以上のように、本発明によれば、ボイド型枠を形成している筒体の外周面又は内周面に保持させた遮音層によって床衝撃音の遮音性能が発揮されるので、ボイド型枠を形成している筒体の形状を変更したりスラブを厚くしたりすることなく、遮音性能に優れたコンクリートスラブを製作することが可能になるという効果がある。 As described above, according to the present invention, the sound insulation performance of the floor impact sound is exhibited by the sound insulation layer held on the outer peripheral surface or the inner peripheral surface of the cylindrical body forming the void mold frame. There is an effect that it is possible to manufacture a concrete slab having excellent sound insulation performance without changing the shape of the cylinder forming the slab or increasing the thickness of the slab.
また、筒体を合成樹脂発泡体で形成し、その合成樹脂発泡体が、上掲の粉粒体を、体積比で30%以下含んでいるというものでは、合成樹脂材料を発泡させて筒体を製作するだけで床衝撃音の遮音性に優れたボイド型枠が得られるという効果がある。 Further, in the case where the cylindrical body is formed of a synthetic resin foam, and the synthetic resin foam contains 30% or less of the above-mentioned powder particles by volume, the synthetic resin material is foamed to form the cylindrical body It is possible to obtain a void form having excellent sound insulation of floor impact sound simply by manufacturing.
図1は本発明に係るボイド型枠の様々な実施形態の正面視形状を示した説明図、図2はボイド型枠の好ましい輪郭形状を例示した説明図、図3はボイド型枠を用いたコンクリートスラブの施工事例を示した説明図である。 FIG. 1 is an explanatory view showing the shape of a front view of various embodiments of a void form according to the present invention, FIG. 2 is an explanatory view illustrating a preferred contour shape of the void form, and FIG. 3 is using a void form. It is explanatory drawing which showed the construction example of concrete slab.
図1(A)〜(F)において、1はボイド型枠の骨材としての金属(板金)製又は合成樹脂発泡体でなる筒体であり、それらの筒体の正面視形状は、(A)が正円形状、(B)が長円形状、(C)が矩形、(D)が波形の湾曲部12を有する形状、(E)が5角形状、(F)が正円形状に、それぞれ形成されている。このうち、(A)〜(E)の筒体1には、その内周面に遮音層3が形成され、(F)の筒体1には、その外周面に遮音層3が形成されている。
1 (A) to (F), reference numeral 1 denotes a cylinder made of metal (sheet metal) or a synthetic resin foam as an aggregate of a void form frame. ) Is an oval shape, (B) is an oval shape, (C) is a rectangle, (D) is a shape having a corrugated
図1(A)〜(F)のそれぞれのボイド型枠において、遮音層3は、パーライト、ガラスビーズ又はアルミナバブルから選ばれる1種又は複数種の粉粒体でなる。パーライトは気密性の小気泡の集合体であり、ガラスビーズやアルミナバブルも同様に気密性の小気泡の集合体である。したがって、これらの素材を用いて形成した上記遮音層3は、音波を乱反射して干渉させたり、音波を吸収したり、吸収して取り込んだ音波をその層内で乱反射して干渉させたりする作用を顕著に発揮する。また、遮音層3を形成している粉粒体が音波との摩擦によって音響エネルギーを吸収したりする作用をも発揮する。そして、このよな作用によって、当該ボイド型枠を層内に具備させたコンクリートスラブは優れた床衝撃音の遮音性能を発揮する。特に、上掲の各種の粉粒体の中からパーライトを選択して形成した遮音層3を有するボイド型枠では、パーライトが砂の1/10〜1/20の重さであるために軽量性に優れ、耐火性や耐薬品性にも優れているため、スラブに加わる強度上の負担が小さく抑えられるだけでなく、筒体1の形状を特殊な形状に変更したりスラブを厚くしたりしなくても、初期の消音作用が長期に亘って持続する。特に、図1(D)のように、波形の湾曲部12を有する形状の筒体1の内周面に遮音層3を形成したものでは、筒体1の形状により音波が乱反射して干渉するので、そのような音波干渉作用と遮音層3による消音作用とが相乗してきわめて高い消音作用が発揮される。したがって、そのようなボイド型枠を用いたスラブは床衝撃音の遮音作用に特に優れている。また、図2(A)のように、筒体1の外面に環状又は螺旋状の凸部15を具備させてボイド型枠の側面視での輪郭線を波形に形成したり、同図(B)のように、筒体1の内面に環状又は螺旋状の凸部15を具備させてボイド型枠の側面視での輪郭線を波形に形成したりすることも可能であり、そのようにすることにより、音波の乱反射による干渉作用が助長された高い消音作用が発揮される。
In each of the void molds shown in FIGS. 1A to 1F, the
遮音層3の形成箇所は、筒体1の内周面であっても外周面であっても、さらには内周面と外周面の両方であってもよく、いずれを選んでも、上記したような消音機能が発揮される。また、筒体1の形状は図1(A)〜(E)に掲げたものに限定されない。
The formation location of the
ところで、遮音層3を形成している粉粒体を、パーライト、ガラスビーズ又はアルミナバブルから選択する場合、それらの粉粒体は、直径が0.2〜4mmのものであれば現況下で市場に汎用的に流通している。そのため、この範囲の直径を有する粉粒体を用いることが、安価に入手することが容易である点で望ましい。しかし、入手が可能であることを前提とすれば、直径が上記範囲外の粉粒体を用いることを排除するものではない。
By the way, when the granular material forming the
また、遮音層3の層厚は0.5〜5mmであることが望ましい。これは、層厚が0.5〜5mmの遮音層3は、筒体1の外周面や内周面に、塗布、吹付け、その他の汎用的な手段によってそれほどの熟練を要することなく容易に形成することができることによる。
The layer thickness of the
遮音層3を筒体1の外周面や内周面に保持させる手段として、遮音層3を筒体1に接着剤で接合するという手段を採用することができる。そして、筒体1に遮音層3を接着剤で接合するようにすると、0.5〜5mmの層厚の遮音層を塗布、吹付け、その他の汎用的な手段によってそれほどの熟練を要することなく容易に形成することができるだけでなく、遮音層3を形成している粉粒体が筒体1から剥がれ落ちるという事態が起こりにくくなる。
As a means for holding the sound
図1(F)に例示したように、筒体1の外周面に遮音層3を形成したボイド型枠では、その遮音層3を、不織布などの柔軟な素材でなる保護シート(不図示)で覆っておくことが望まれる。保護シートには、不織布のほか、布、紙、ネットなどを用いることも可能である。通常、ボイド型枠は、コンクリートスラブの施工中に作業者がその上を通行する場合や、その上に他の資材を一時的に載置するような場合が起こり得る。そのような場合でも、遮音層3を保護シートで覆っておくと、遮音層3を形成している粉粒体の脱落などが保護シートにより抑制されるという利点がある。
As illustrated in FIG. 1 (F), in the void form frame in which the
図3のように、本発明に係るボイド型枠10は、コンクリートスラブ20の層内に埋入されてそのスラブ20に中空ボイド30を具備させることに役立つ。そして、このような中空ボイド30を備えたコンクリートスラブ20では、ボイド型枠10の遮音層3が、音波を乱反射して干渉させたり、音波を吸収したり、吸収して取り込んだ音波をその層内で乱反射して干渉させたりする作用を顕著に発揮し、また、遮音層3を形成している粉粒体が音波との摩擦によって音響エネルギーを吸収したりする作用をも発揮する。
As shown in FIG. 3, the
本発明に係るボイド型枠10では、その遮音層3としてパーライトの粉粒体を用いることが特に好ましい。パーライトは、天然火山ガラスである真珠岩や松脂岩を所定の粒度に粉砕して急速に加熱、膨張させることによって得られる気密性小気泡の集合体であり、たとえば、SiO2 75.0%、Al2 O3 14.0%、Fe2 O3 0.9%、CaO0.1%:K2 O4.2%、Na2 03.5%の組成を持つ。この組成のパーライトは、単位容積質量が砂の1/10〜1/20という軽量性を持ち、1200℃でも溶融しないという耐火性を備え、熱伝導率が0.036〜0.05kcal/m・h・℃で断熱性に優れ、ガラス質であるために耐薬品性に優れ、PH値が7を示す中性であって化学的に安定した性質を示す。
In the
本発明に係るボイド型枠は、筒体が発泡スチロール成形体などの合成樹脂発泡体で成形することも可能であり、その場合には、その合成樹脂発泡体が、パーライト、ガラスビーズ又はアルミナバブルから選ばれる1種又は複数種の粉粒体を、体積比で30%以下含んでいるものであってもよい。この構造のボイド型枠によると、筒体の内周面や外周面に遮音層を形成する必要がなく、合成樹脂材料を発泡させて筒体を製作するだけで床衝撃音の遮音性に優れたボイド型枠が得られる。なお、粉粒体の含有量が30%を越えると、合成樹脂発泡体でる筒体が脆くなって満足のいく強度が得られなくなるおそれがある。 In the void form according to the present invention, the cylindrical body can be molded from a synthetic resin foam such as a polystyrene foam molded body. In that case, the synthetic resin foam is made of pearlite, glass beads, or alumina bubbles. It may contain 30% or less of the selected one or more powders by volume. According to the void formwork of this structure, it is not necessary to form a sound insulation layer on the inner and outer peripheral surfaces of the cylinder, and it is excellent in sound insulation of floor impact sound just by producing a cylinder by foaming a synthetic resin material Void formwork is obtained. In addition, when the content of the granular material exceeds 30%, the cylindrical body made of the synthetic resin foam may become brittle and a satisfactory strength may not be obtained.
本発明に係るボイド型枠を採用したコンクリートスラブは、床衝撃音遮断性能が500〜1000Hzの中高音域で顕著に発揮され、そのような共振防止の具体的作用としては、波形ボイド(図1(D)のもの)の場合と同様に、10〜15dB程度に抑えられることを確認している。 The concrete slab adopting the void form according to the present invention exhibits floor impact sound blocking performance remarkably in the middle to high frequency range of 500 to 1000 Hz. As a specific action for preventing such resonance, a corrugated void (FIG. 1) As in the case of (D), it is confirmed that it can be suppressed to about 10 to 15 dB.
1 筒体
3 遮音層
10 ボイド型枠
20 コンクリートスラブ
30 中空ボイド
DESCRIPTION OF SYMBOLS 1
Claims (7)
上記筒体の外周面又は内周面に、パーライト、ガラスビーズ又はアルミナバブルから選ばれる1種又は複数種の粉粒体でなる遮音層を形成してあることを特徴とするボイド型枠。 In the void formwork consisting of a cylinder for providing a hollow void in the concrete slab layer,
A void type frame comprising a sound insulation layer made of one or more kinds of powders selected from pearlite, glass beads, or alumina bubbles formed on an outer peripheral surface or an inner peripheral surface of the cylindrical body.
上記筒体が合成樹脂発泡体でなり、その合成樹脂発泡体が、パーライト、ガラスビーズ又はアルミナバブルから選ばれる1種又は複数種の粉粒体を、体積比で30%以下含んでいることを特徴とするボイド型枠。
In the void formwork consisting of a cylinder for providing a hollow void in the concrete slab layer,
The cylindrical body is made of a synthetic resin foam, and the synthetic resin foam contains 30% or less by volume ratio of one or more powders selected from pearlite, glass beads, or alumina bubbles. Characteristic void formwork.